Compositions for porous materials

0001The present invention relates to the use of phosphonates / phosphinates in aqueous formulations as carriers for improving the absorption of the compounds present in said formulations, into porous wettable materials, such as paper, wood, masonite and plaster.

0002More particularly, the present invention relates to the use of low molecular weight phosphonates and/or phosphinates, soluble in aqueous formulations in order to improve impregnation capacity as shown by the substantial absence of any blooming phenomena.

0003Even more particularly, the present invention relates to the use of phosphonates and/or phosphinates in the application of aqueous solutions onto ligneous materials.

0004Compositions comprising phosphonates and phosphinates for applications onto substrates of plant origin are known in the art. <patcit id="pcit0001" dnum="US6423251B"><text>US patent 6,423,251</text></patcit> describes a composition for ligneous materials which may be in solid, aqueous or aqueous emulsion form, based on the condensation products between urea and boron oxyacids, and optionally containing carbonization catalytic agents (carbonization auxiliaries). Said catalytic agents may be acidic compounds such as boric, sulphuric or phosphoric acids, and salts thereof. Furthermore, other phosphorous compounds are indicated as being suitable for use as "carbonization auxiliaries" such as for example, phosphoric acid salts with nitrogen containing compounds and organo-phosphor compounds such as for example phosphoric esters. In the patent, it is affirmed that in order to have good penetration into wood, the composition must be applied hot and that it is necessary to operate under pressure or vacuum, or using glycol, polyol or ethylene oxide type surfactants. This patent solves the problem of the absorption of aqueous compositions based on urea - boron oxyacid condensation products into wood through the use of particular composition application procedures, as indicated above. <patcit id="pcit0002" dnum="US6114340A"><text>US patent 6,114,340</text></patcit> describes fungicidal compositions, particularly usable for phytopathogenic fungi, including a fungicidal compound together with a second compound, capable of increasing the activity of the first compound, said second compound being selected from among the following: phosphinates, diphosphinates, phosphonates and diphosphonates. Such phosphorus compounds contain three aliphatic C₆-C₂₀ chains within the molecule, and hence possess high molecular weights. Furthermore, said phosphinates/phosphonates are insoluble in water, but are emulsionable. In the examples, the use of such compositions for spraying wheat fields inoculated with a pathogenic fungus is described. Hence the patent does not refer to applications onto wood.

0005<patcit id="pcit0003" dnum="WO9304585A"><text>WO 9304585</text></patcit> describes a herbicidal composition which comprises a phosphonate or phosphinate.

0006The need was felt for the availability of water soluble compounds for use as carriers in order to improve the absorption of aqueous compositions, preferably aqueous solutions, into porous wettable materials, such as paper, wood, masonite, plaster, preferably wood, so as to obtain the following combination of properties: <ul id="ul0001" list-style="bullet" compact="compact"><li>the application of the aqueous formulation at room temperature;</li><li>improved substrate impregnation capacity, thus avoiding the addition of solvents and surfactants, even when the dry percentage is high and there are additives, such as for example biocides, present;</li><li>applicability using simple impregnation techniques, such as for example spraying or application by brushing;</li><li>improved environmental impact.</li></ul>

0007A class of compounds overcoming the above mentioned drawbacks has now been surprisingly and unexpectedly found by the Applicant.

0008The use of water soluble neutral esters of acids of phosphorous of general formula (I) as carriers for the improved absorption of aqueous compositions, preferably aqueous solutions, into porous wettable materials such as paper, wood, masonite, plaster, preferably wood, constitutes a subject of the present invention: <chemistry id="chem0001" num="0001"><img file="EP1580320B1_D0001.tif" /></chemistry> wherein: <ul id="ul0002" list-style="none" compact="compact"><li>R₁ and R₃, being identical or different, are linear or branched C₁-C₄ alkyls, preferably C₁ -C₃;</li><li>R₂ is linear or branched C₁-C₄ alkyl or oxyalkyl, preferably C₁-C₃;</li><li>R₃ and R₂, when R₂ is oxyalkyl taken together may form a ring having 5 to 6 atoms, including 2 or 3 carbon atoms.</li></ul>

0009Preferably, R₂ is oxyalkyl.

0010The compounds of formula (I) which may be cited are diethylethylphosphonate, dimethylmethylphosphonate and cyclic phosphonates.

0011The quantities of the compounds of formula (I) in the aqueous formulations varies, as a percentage by weight over the total, from 0.1 % to 15%, preferably from 1% to 10%, even more preferably from 1% to 8%.

0012Application of the aqueous formulations of the invention is achieved through the impregnation of said substrates while operating within a temperature interval of from 5°C to 80°C, preferably at a temperature of less than 40°C.

0013Application may be performed using even simple impregnation methods, such as for example application by spraying, by roller or by brushing.

0014The Applicant has surprisingly and unexpectedly found that the aqueous formulations containing compounds of formula (I) allow the carrying of both ionic and non-ionic additives, and also polymeric additives, such as for example urea formaldehyde condensates, into porous substrates. Furthermore, the presence of solvents and surfactants is not required in the formulations.

0015The additives which may be carried using the compounds of formula (I) are for example the following: <ol id="ol0001" compact="compact"><li>A) flame retardants, such as for example ethylenediamine monophosphate, guanidine phosphate, triethylphosphate, guanylurea phosphate, trihydroxyethyl isocyanurate phosphates, melamine pentaerythritol phosphate, urea phosphate, neutral phosphates of polyethylene oxides, diethyl-N,N-bis(2-hydroxyethyl)amino-methylphosphonate, neutral phosphates of oligomeric alcohols, dicyandiamide phosphate, condensation products between melamine, urea formaldehyde and phosphoric acid described in <patcit id="pcit0004" dnum="US3832316A"><text>USP 3.832.316</text></patcit>; mono- and di-ammonium phosphate; ammonium polyphosphates; mono- and di-melamine phosphate; melamine polyphosphate; glucose and phosphoric acid based condensates (<patcit id="pcit0005" dnum="US2719179A"><text>USP 2.719.179</text></patcit>) commercially known by the brand Budit®; glucose phosphoric acid and formaldehyde based condensates; dextrin and phosphoric acid based condensates; guanidine, formaldehyde phosphoric acid condensation products described in <patcit id="pcit0006" dnum="US4219456A"><text>USP 4.219.456</text></patcit>; the product of the condensation between formaldehyde, urea, dicyandiamide and phosphoric acid described in <patcit id="pcit0007" dnum="US3887511A"><text>USP 3.887.511</text></patcit>, the condensate may be obtained through the reaction of the above mentioned substances using the following amounts: <ul id="ul0003" list-style="bullet" compact="compact"><li>from 1 to 10 moles of urea;</li><li>from 1 to 11 moles of dicyandiamide;</li><li>from 1.2 to 3 moles of formaldehyde for each mole of urea + dicyandiamide;</li><li>from 0.5 to 2 moles of phosphoric acid for each mole of urea + dicyandiamide;</li></ul> the condensation compound is prepared by adding a urea and dicyandiamide mixture to an aqueous solution of formaldehyde, at a temperature of between 60°C and 90°C, whilst keeping the temperature constant until the solution becomes clear; the temperature is then lowered to less than 50°C and phosphoric acid is added whilst stirring; the quantity of flame retardants, as a percentage by weight, varies from 1% to 35%, preferably from 5% to 25%, with the total percentage sum of the components present being equal to 100;</li><li>B) biocide additives, for example boron based salts, preferably selected from sodium borate, borax pentahydrate, borax decahydrate (Na₂B₄O₇x10H₂O), sodium octaborate tetrahydrate, boric acid or mixtures thereof. The quantities of biocide additives are generally from 0.5% to 23%, preferably from 1% to 10%, in reference to the total weight of the composition.</li></ol>

0016Other additives which may be carried using the compounds of formula (I) include the following: colorants, pigments, gelling agents, waxes, proteins, surfactants, silanes, siloxanes, cellulose, halogens, additives for improving the mechanical or aesthetic characteristics of porous items such as for example vinyl latexes.

0017The useable aqueous formulations are in the form of aqueous solutions or dispersions, preferably aqueous solutions. In the case of aqueous dispersions then preferably emulsions are used if it is possible to obtain them with the components of the formulation.

0018The preferred aqueous compositions of the present invention include: <ul id="ul0004" list-style="bullet" compact="compact"><li>diethylethylphosphonate, dimethylmethylphosphonate as compounds of formula (I), with the quantities as a percentage by weight of the total being from 1% to 8%; <ol id="ol0002" compact="compact"><li>A) phosphates selected from guanidine phosphates, guanidine urea phosphate and urea phosphate; condensation products between formaldehyde, urea, dicyandiamide and phosphoric acid described in <patcit id="pcit0008" dnum="US3887511A"><text>USP 3,887,511</text></patcit>. The condensate may be obtained through the reaction of the above indicated substances using the following amounts: <ul id="ul0005" list-style="bullet" compact="compact"><li>from 1 to 10 moles of urea;</li><li>from 1 to 11 moles of dicyandiamide;</li><li>from 1.2 to 3 moles of formaldehyde for each mole of urea + dicyandiamide;</li><li>from 0.5 to 2 moles of phosphoric acid for each mole of urea + dicyandiamide; the condensation compound is prepared by adding a urea and dicyandiamide mixture to an aqueous solution of formaldehyde, at a temperature of between 60°C and 90°C, whilst keeping the temperature constant until the solution becomes clear; the temperature is then lowered to less than 50°C and phosphoric acid is added whilst stirring; condensation products between melamine, urea formaldehyde and phosphoric acid described in <patcit id="pcit0009" dnum="US3832316A"><text>USP 3,832,316</text></patcit>; with the percentage by weight of component A) being from 5% to 25%;</li></ul></li><li>B) biocides, preferably borax decahydrate (Na₂B₄O₇.10H₂O), boric acid or mixtures thereof; in quantities as percentages by weight from 1% to 10%;</li></ol></li></ul>

0019The percentage by weight of the various components is in reference to the total weight of the composition; with the total sum of the components present being equal to 100%.

0020The percentage dry weight of the aqueous compositions according to the present invention is from 3% a 50%, preferably from 10% to 40%.

0021It has been surprisingly and unexpectedly found by the Applicant that using the above indicated quantities of the compounds of formula (I) it is possible to achieve the absorption into the substrate of aqueous formulations, even oligomeric or polymeric in nature, having a high dry content. For example, it is possible to mention to the condensation products belonging to a) such as neutral polyethylene oxide phosphates, neutral phosphates of oligomeric alcohols, condensation products between melamine, urea formaldehyde and phosphoric acid described in <patcit id="pcit0010" dnum="US3832316A"><text>USP 3.832.316</text></patcit>; or the condensation product between formaldehyde, urea, dicyandiamide and phosphoric acid described in <patcit id="pcit0011" dnum="US3887511A"><text>USP 3.887.511</text></patcit>. The condensate may be obtained through the reaction of the above indicated substances using the following amounts: <ul id="ul0006" list-style="bullet" compact="compact"><li>from 1 to 10 moles of urea;</li><li>from 1 to 11 moles of dicyandiamide;</li><li>from 1.2 to 3 moles of formaldehyde for each mole of urea + dicyandiamide;</li><li>from 0.5 to 2 moles of phosphoric acid for each mole of urea + dicyandiamide;</li></ul> the condensation compounds are prepared by adding a urea and dicyandiamide mixture to an aqueous solution of formaldehyde, at a temperature of between 60°C and 90°C, whilst keeping the temperature constant until the solution becomes clear; the temperature is then lowered to less than 50°C and phosphoric acid is added whilst stirring.

0022The aqueous formulations of the invention may also have high dry content, generally even greater than 40%, preferably even up to 50% by weight of the formulation.

0023The Applicant has found that aqueous formulations marketed for applications to the above mentioned porous supports leave unabsorbed residues, and that it is possible to avoid such drawbacks by the addition of the compounds of formula (I). This way the unabsorbed residues are made to completely penetrate the porous material without leaving any deposits. Hence, the presence of compounds of formula (I) in the aqueous compositions containing the additives to be carried, allows the improvement of absorption, even when the additive would only be partially absorbed or not absorbed into the porous substrate as it is.

0024Use of the compounds of formula (I) according to the present invention has particular importance for applications involved in the restoration of wooden materials, where the following requirements must also be taken into consideration: <ul id="ul0007" list-style="bullet" compact="compact"><li>the treatment of the item must not alter its outward appearance;</li><li>the composition must have good biocide effectiveness and good resistance to fire;</li><li>the neutrality of the composition.</li></ul>

0025Application of the compositions onto porous materials is simple and may even be performed using conventional impregnation methods such as for example by immersion at atmospheric pressure or by using repeated cycles including depressurisation, immersion and pressurisation stages. Preferably the composition is applied onto the surface to be treated by using, as already mentioned, techniques such as application by brushing, by roller or by spraying, which are simpler and less costly than those indicated above.

0026Independently from the technique of application, following evaporation of the aqueous solvent, the ligneous material treated with the composition of the present invention shows essentially no blooming due to the surface crystallisation of salts.

0027Using the compounds of formula (I) it is possible to apply overall quantities of additives varying from 200 g/m² to 2,000 g/m², preferably between 300 g/m² and 1,000 g/m² onto substrates, without detecting any blooming phenomena on the treated surface.

0028Depending on the porosity of the material to be treated and also using a simple application technique, such as that of brushing, absorption of the required quantity of composition is already obtained after just a few applications, even in the case of applications onto smooth, low porosity, unseasoned wood.

0029The following examples are given herein by way of non-limiting illustration of the present invention.

EXAMPLES

0030In the following examples, dry components have been calculated as % by weight of all components, excluding water, over the composition total.

EXAMPLE 1

0031Preparation of an aqueous solution containing boric acid, borax, diethyl ethylphosphonate and neutral condensation products between formaldehyde, urea, dicyandiamide and phosphoric acid.

0032Into a mixer with a nominal volume of 500 ml, fitted with a mechanical turbine stirrer, were introduced in order: <ul id="ul0008" list-style="bullet" compact="compact"><li>71 g of an aqueous solution containing 15% by weight of boric acid, 20% by weight of borax decahydrate;</li><li>71 ml of water;</li><li>143 g of a condensate in aqueous solution, containing urea dicyandiamide and phosphoric acid, prepared according to <patcit id="pcit0012" dnum="US3887511A"><text>USP 3,887,511</text></patcit> (example 7), having the following characteristics: <ul id="ul0009" list-style="bullet" compact="compact"><li>the urea, dicyandiamide, formaldehyde, phosphoric acid molar ratio was 1.0/1.5/2.0/0.8,</li><li>dry content = 57%,</li><li>pH of approx. 7;</li></ul></li><li>15 g of diethyl ethylphosphonate.</li></ul> The dry content was 41 % by weight. After a few minutes stirring at 1500 r/min the composition was clear and colourless and remained stable for many days.

EXAMPLE 1a

Application of the composition of example 1 onto wood

0033A white pine board having dimensions 80 x 15.5 cm and a thickness of 2 cm was impregnated by brushing using 1,000 g/m² of composition on average.

0034The product was rapidly absorbed. Following application, it was noted that the appearance of the treated surface was indistinguishable from that of the untreated wood.

EXAMPLE 2 (Comparison)

0035Preparation of a composition like that of example 1 but omitting diethyl ethylphosphonate.

0036Into a mixer with a nominal volume of 500 ml, fitted with a mechanical turbine stirrer, were introduced in order: <ul id="ul0010" list-style="bullet" compact="compact"><li>71 g of an aqueous solution containing 15% by weight of boric acid, 20% by weight of borax decahydrate;</li><li>71 ml of water;</li><li>143 g of a condensate in aqueous solution, containing urea dicyandiamide and phosphoric acid, prepared according to <patcit id="pcit0013" dnum="US3887511A"><text>USP 3,887,511</text></patcit> (example 7), having the following characteristics:</li></ul><ul id="ul0011" list-style="bullet" compact="compact"><li>the urea, dicyandiamide, formaldehyde, phosphoric acid molar ratio was 1.0/1.5/2.0/0.8;</li><li>dry content = 57%;</li><li>pH of approx. 7.</li></ul>

EXAMPLE 2a (Comparison)

0037Application of the composition of comparative example 2 onto wood.

0038Example 1a was repeated but with the use of the composition of example 2. Following application of the composition and evaporation of the aqueous solvent, the presence of evident quantities of solid residues was observed on the surface of the wood.

EXAMPLE 3

0039Preparation of an aqueous solution as in example 1 but containing dimethyl methylphosphonate instead of diethyl ethylphosphonate.

0040Into a mixer with a nominal volume of 500 ml, fitted with a mechanical turbine stirrer, were introduced in order: <ul id="ul0012" list-style="bullet" compact="compact"><li>71 g of an aqueous solution containing 15% by weight of 15% boric acid and 20% by weight of borax decahydrate;</li><li>71 ml of water;</li><li>100 g of a condensate in aqueous solution, containing urea dicyandiamide and phosphoric acid, prepared according to <patcit id="pcit0014" dnum="US3887511A"><text>USP 3,887,511</text></patcit> (example 7), having the following characteristics: <ul id="ul0013" list-style="none" compact="compact"><li>the urea, dicyandiamide, formaldehyde, phosphoric acid molar ratio was 1.0/1.5/2.0/0.8;</li><li>dry content = 57%;</li><li>pH of approx. 7;</li></ul></li><li>15 g of dimethyl methylphosphonate.</li></ul> The dry content was 37.6% by weight. After a few minutes stirring at 1,500 r/min the composition was clear and colourless and remained stable for many days.

EXAMPLE 3a

0041Application of the composition of example 3 onto wood.

0042Example 1a was repeated but with the use of the composition of example 3.

0043The product was rapidly absorbed. After application, it was noted that the appearance of the treated surface was indistinguishable from that of the untreated wood.

EXAMPLE 4 (Comparison)

0044Preparation of an aqueous solution like that of example 3 but omitting dimethyl methylphosphonate.

0045Into a mixer with a nominal volume of 500 ml, fitted with a mechanical turbine stirrer, were introduced in order: <ul id="ul0014" list-style="bullet" compact="compact"><li>71 g of an aqueous solution containing 15% by weight of 15% boric acid and 20% by weight of borax decahydrate;</li><li>71 ml of water;</li><li>100 g of a condensate in aqueous solution, containing urea dicyandiamide and phosphoric acid, prepared according to <patcit id="pcit0015" dnum="US3887511A"><text>USP 3,887,511</text></patcit> (example 7), having the following characteristics: <ul id="ul0015" list-style="none" compact="compact"><li>the urea, dicyandiamide, formaldehyde, phosphoric acid molar ratio was 1.0/1.5/2.0/0.8;</li><li>dry content = 57%;</li><li>pH of approx. 7.</li></ul></li></ul>

EXAMPLE 4a (Comparison)

0046Application of the composition of comparison example 4 onto wood.

0047Example 1a was repeated but with the use of the composition of example 4. Following application of the composition and evaporation of the aqueous solvent, the presence of evident quantities of solid residues was observed on the surface of the wood.

EXAMPLE 5

0048Preparation of an aqueous solution containing boric acid, borax and diethyl ethylphosphonate.

0049Into a mixer with a nominal volume of 500 ml, fitted with a mechanical turbine stirrer, were introduced in order: <ul id="ul0016" list-style="bullet" compact="compact"><li>71 g of an aqueous solution containing 15% by weight of boric acid, 20% by weight of borax decahydrate;</li><li>15 g of diethyl ethylphosphonate;</li><li>114 g of water.</li></ul> The dry content was 20% by weight. After a few minutes stirring at 1,500 r/min the composition was clear and colourless and remained stable for many days.

EXAMPLE 5a

0050A white pine board having dimensions 80 x 15.5 cm and a thickness of 2 cm was impregnated by brushing using 2.000 g/m² of composition on average.

0051The product was rapidly absorbed. The same results as for example 1a were obtained.

EXAMPLE 6 (Comparison)

0052Preparation of an aqueous solution like in example 5 but omitting diethyl ethylphosphonate Into a mixer with a nominal volume of 500 ml, fitted with a mechanical turbine stirrer, were introduced in order: <ul id="ul0017" list-style="bullet" compact="compact"><li>71 g of an aqueous solution containing 15% by weight of 15% boric acid and 20% by weight of borax decahydrate;</li><li>114 g of water.</li></ul> After a few minutes stirring at 1,500 r/min the composition was clear and colourless.

EXAMPLE 6a (Comparison)

0053Example 5a was repeated but with the use of the composition of example 6. Following application of the composition and evaporation of the aqueous solvent, the presence of evident quantities of solid residues (borates) was observed on the surface of the wood.

EXAMPLE 7

0054Preparation of a composition containing boric acid, borax, urea phosphate and diethyl ethylphosphonate

0055Into a mixer with a nominal volume of 250 ml, fitted with a mechanical turbine stirrer, were introduced in order: <ul id="ul0018" list-style="bullet" compact="compact"><li>25 g of urea phosphate;</li><li>150 ml of water;</li><li>15 g of boric acid;</li><li>15 g of diethyl ethylphosphonate;</li></ul> The dry content was 26.8% by weight. The pH was adjusted to neutrality using borax decahydrate. After a few minutes stirring at 1,500 r/min the composition was clear and colourless and remained stable for many days.

EXAMPLE 7a

0056Example 5a was repeated but with the use of the composition of example 7.

0057The product is rapidly absorbed. The same results as for example 1a were obtained.

EXAMPLE 8 (Comparison)

0058Preparation of an aqueous solution like in example 7 but omitting diethyl ethylphosphonate.

0059Into a mixer with a nominal volume of 250 ml, fitted with a mechanical turbine stirrer, were introduced in order: <ul id="ul0019" list-style="bullet" compact="compact"><li>25 g of urea phosphate;</li><li>150 ml of water;</li><li>15 g of boric acid.</li></ul> The pH is adjusted to neutrality using borax decahydrate. After a few minutes stirring at 1,500 r/min the composition was clear and colourless.

EXAMPLE 8a (Comparison)

0060Example 5a was repeated but with the use of the composition of example 8. Following application of the composition and evaporation of the aqueous solvent, the presence of evident quantities of solid residues was observed on the surface of the wood.

EXAMPLE 9

0061Preparation of an aqueous solution containing diethyl ethylphosphonate and a glucose and phosphoric acid based condensate

0062Into a mixer with a nominal volume of 500 ml, fitted with a mechanical turbine stirrer, were introduced in order: <ul id="ul0020" list-style="bullet" compact="compact"><li>113 g of water;</li><li>36 g of Budit® 380 (Budenheim, glucose and phosphoric acid based condensate having the following mean composition by weight: 68% H₃PO₄, 13% glucose, 19% water);</li><li>15 g of diethyl ethylphosphonate.</li></ul> The dry content was 26.8% by weight. After a few minutes stirring at 1,500 r/min the composition was clear and colourless.

EXAMPLE 9a

0063Example 1a was repeated but with the use of the composition of example 9.

0064The product was rapidly absorbed. The same results as for example 1a were obtained.

EXAMPLE 10 (Comparison)

0065Preparation of an aqueous solution like in example 9 but omitting diethyl phosphonate.

0066Into a mixer with a nominal volume of 500 ml, fitted with a mechanical turbine stirrer, were introduced in order: <ul id="ul0021" list-style="bullet" compact="compact"><li>113 g of water;</li><li>36 g of Budit® 380 (Budenheim, glucose and phosphoric acid based condensate having the following mean composition by weight: 68% H₃PO₄, 13% glucose, 19% water).</li></ul> After a few minutes stirring at 1,500 r/min the composition was clear and colourless.

EXAMPLE 10a (Comparison)

0067Example 1a was repeated but with the use of the composition of comparison example 10.

0068Following application of the composition and evaporation of the aqueous solvent, significant quantities of sticky and hygroscopic solid residues were observed on the surface of the wood.

EXAMPLE 11

0069Preparation of an aqueous solution containing guanidine urea phosphate and diethyl ethylphosphonate

0070Into a mixer with a nominal volume of 500 ml, fitted with a mechanical turbine stirrer, were introduced in order: <ul id="ul0022" list-style="bullet" compact="compact"><li>7.5 g of guanidine urea phosphate;</li><li>100 g of water;</li><li>5.0 g of diethyl ethylphosphonate.</li></ul> The dry content is 11.2% by weight.

0071The pH is adjusted to neutrality using aqueous KOH. After a few minutes stirring at 1,500 r/min the composition was clear and colourless and remained stable for many days.

EXAMPLE 11a

0072A white pine board having dimensions 80 x 15.5 cm and a thickness of 2 cm was impregnated by brushing using 500 g/m² of composition on average.

0073The product was rapidly absorbed. After the application, it was noted that the appearance of the treated surface was indistinguishable from that of the untreated wood.

EXAMPLE 12 (Comparison)

0074Preparation of an aqueous solution like in example 11 but omitting diethylethylphosphonate Into a mixer with a nominal volume of 500 ml, fitted with a mechanical turbine stirrer, were introduced in order: <ul id="ul0023" list-style="bullet" compact="compact"><li>7.5 g of guanidine urea phosphate;</li><li>100 g of water.</li></ul> The pH is adjusted to neutrality using aqueous KOH. After a few minutes stirring at 1,500 r/min the composition was clear and colourless.

EXAMPLE 12a (Comparison)

0075Example 11a was repeated but with the use of the composition of comparison example 12. After the application of the composition and evaporation of the aqueous solvent, evident amounts of solid residues were observed on the surface of the wood.

EXAMPLE 13

0076Preparation of an aqueous solution containing diguanidine phosphate, borlc acid, diethyl ethylphosphonate, alkyltrialkoxysilane and phosphoric acid.

0077Into a mixer with a nominal volume of 500 ml, fitted with a mechanical turbine stirrer, were introduced in order: <ul id="ul0024" list-style="bullet" compact="compact"><li>60.9 g of diguanidine phosphate;</li><li>13.5 g of boric acid;</li><li>3.6 g of phosphoric acid (75%)</li></ul> The composition was heated until all guanidine was fully solubilized. It was then cooled down and the following ingredients were introduced: <ul id="ul0025" list-style="bullet" compact="compact"><li>192 g of water</li><li>15 g of diethyl ethylphosphonate</li><li>15 g of octyl trietoxysilane</li></ul>

0078The dry content was 33.1 % by weight. After a few minutes stirring at 1,500 r/min the composition was clear and colourless and remained stable for many days.

EXAMPLE 13a

0079A white pine board having dimensions 80 x 15.5 cm and a thickness of 2 cm was impregnated by brushing using 500 g/m² of composition on average.

0080The product was rapidly absorbed. After the application, it was noted that the appearance of the treated surface was indistinguishable from that of the untreated wood.

EXAMPLE 14 (Comparison)

0081Preparation of an aqueous solution like in example 13 but omitting diethylethylphosphonate.

0082Into a mixer with a nominal volume of 500 ml, fitted with a mechanical turbine stirrer, were introduced in order: <ul id="ul0026" list-style="bullet" compact="compact"><li>60.9 g of diguanidine phosphate;</li><li>13.5 g of boric acid;</li><li>3.6 g of phosphoric acid (75%)</li></ul> The composition was heated until all guanidine was fully solubilized. It was then cooled down and the following ingredients were introduced: <ul id="ul0027" list-style="bullet" compact="compact"><li>207 g of water</li><li>15 g of octyl trietoxysilane</li></ul>

0083The dry content was 28.1 % by weight.

EXAMPLE 14a (Comparison)

0084Example 13a was repeated but with the use of the composition of comparison example 14. After the application of the composition and evaporation of the aqueous solvent, evident amounts of solid residues were observed on the surface of the wood.

EXAMPLE 15

0085Preparation of an aqueous solution containing boric acid, borax, diethyl ethylphosphonate, halogenides and cellulose.

0086Into a mixer with a nominal volume of 500 ml, fitted with a mechanical turbine stirrer, were introduced in order: <ul id="ul0028" list-style="bullet" compact="compact"><li>148.8 g of an aqueous solution containing 15% by weight of boric acid, 20% by weight of borax decahydrate;</li><li>2.1 g of ammonium bromide;</li><li>68 g of water;</li><li>0.9 g of low molecular weight cellulose (viscosity Brookfield, 25°C, 15 mPa · s)</li></ul>

0087The composition is heated until cellulose is fully solubilized; then, after cooling down, 15 g of diethyl ethylphosphonate were introduced.

0088After a few minutes stirring at 1,500 r/min the composition was clear and colourless and remained stable for many days.

EXAMPLE 16 (Comparison)

0089Preparation of an aqueous solution like in example 15 but omitting diethylethylphosphonate.

0090Into a mixer with a nominal volume of 500 ml, fitted with a mechanical turbine stirrer, were introduced in order: <ul id="ul0029" list-style="bullet" compact="compact"><li>148.8 g of an aqueous solution containing 15% by weight of boric acid, 20% by weight of borax decahydrate;</li><li>2.1 g of ammonium bromide;</li><li>68 g of water;</li><li>0.9 g of low molecular weight cellulose (viscosity Brookfield, 25°C, 15 mPa · s)</li></ul>

0091After a few minutes stirring at 1,500 r/min, the composition was heated until cellulose was fully solubilized. The solution was clear and colourless and remained stable for many days.

EXAMPLE 16a (Comparison)

0092Example 15a was repeated but with the use of the composition of comparison example 14. After the application of the composition and evaporation of the aqueous solvent, evident amounts of solid residues were observed on the surface of the wood.