Negative active material for non-aqueous electrolyte battery, method of preparing same, and non-aqueous electrolyte battery comprising same

BACKGROUND OF THE INVENTION

1. Field of the Invention

0001The present invention relates to a negative active material for a non-aqueous electrolyte battery, a method of preparing the same, and a non-aqueous electrolyte battery comprising the same, and more particularly to a negative active material of a non-aqueous battery with effective stability, a method of preparing the same, and a non-aqueous battery comprising the same.

2. Description of the Related Art

0002Rechargeable lithium batteries, which are attractive as power sources for portable electronics, use organic electrolyte, and exhibit twice the discharge capacity of conventional batteries with alkaline aqueous solution electrolyte as well as having a higher energy density.

0003Positive active materials of rechargeable lithium batteries use lithium and transition metal-included oxides having a structure being capable of intercalating lithium, such as LiCoO₂, LiMn₂O₄, and LiNi_1-xCo_xO₂ (0 < x < 1).

0004Negative active materials use carbonaceous materials which may intercalate and deintercalate lithium, such as graphite, e.g., artificial graphite, natural graphite, natural graphite, or hard carbon. A lower discharge voltage to lithium, i.e., -0.2 V of graphite, renders a higher discharge voltage of 3.6 V which provides advantages in energy density, and good reversibility guarantees long cycle life. Owing to these advantages, graphite is widely used as the negative active material. However, graphite has a low density per unit volume of the electrode (nominal density of 2.2 g/cc), which decreases capacity, and graphite easily and undesirably reacts with organic electrolytes at high discharge voltages, causing fires or explosion.

0005These shortcomings are addressed by developing oxide active materials. Amorphous tin oxides studied by FUJI FILM CO. exhibit a high capacity of 800 mAh/g, but initial irreversible capacity reached approximately 50%. In addition, the discharge voltage of 0.5 V or more and an inherently smooth voltage profile cause difficulty in the use of such materials as negative active materials. In addition, a significant amount of reduction from tin oxide to tin metal occurs, which negates the use of such materials as negative active materials.

0006Various oxide negative active materials have been taught, e.g., in Japanese Patent Laid-Open No. 2002-216753 (SUMITOMO METAL IND., LTD.) (Li_aMg_bVO_c (0.05 ≤ a ≤ 3, 0.12 ≤ b ≤ 2, 2 ≤ 2c-a-2b ≤ 5)), and in Abstract # 3B05 of The 43^rd Battery Symposium in Japan.

0007However, studies on oxides used as negative active materials exhibiting satisfactory battery performances are still required.

SUMMARY OF THE INVENTION

0008It is an aspect of the present invention to provide a negative active material of a non-aqueous battery that fails to have a side reaction with an organic electrolyte and that exhibits good safety characteristics.

0009It is another aspect to provide a negative active material of a non-aqueous battery having high energy density per unit volume and exhibiting a high capacity.

0010It is still another aspect to provide a method of preparing the negative active material of a non-aqueous electrolyte battery.

0011It is still another aspect to provide a non-aqueous electrolyte battery including the negative active material.

0012These and/or other aspects may be achieved by a negative active material of a non-aqueous battery, represented by formula 1:         Li_xM_yV_zO_2+d     (1) where 0.1 ≤ x ≤ 2.5, 0 < y ≤ 0.5, 0.5 ≤ z ≤ 1.5,0 ≤ d ≤ 0.5; and M is at least one element selected from the group consisting of Al, Cr, Mo, Ti, W and Zr.

0013The negative active material preferably has a tapping density of 1 to 5g/cc, or a void volume ranging from 1 X 10^-3cc/g to 0.8cc/g per weight of a particle of the negative active material with a size of 0.1 to 10µm. Alternatively, the negative active material has a full width at half-maximum of an X-ray diffraction peak at a (003) plane of 0.5 or less, and a full width at half-maximum of an X-ray diffraction peak at a (104) plane of 0.5 or less.

0014To achieve these and/or other aspects, the present invention provides a method of preparing the negative active material of a non-aqueous electrolyte battery. In this method, vanadium sources, lithium sources and metal sources are mixed, and the mixture is heat-treated at a temperature between approximately 500°C and 1400°C under a reductive atmosphere.

0015The present invention further includes a non-aqueous battery including a positive electrode, a negative electrode, and a non-aqueous electrolyte. The positive electrode includes a positive active material which may intercalate and deintercalate lithium ions, and the negative electrode includes the negative active material.

0016Additional aspects and/or advantages of the invention will be set forth in part in the description which follows and, in part, will be obvious from the description, or may be learned by practice of the invention.

BRIEF DESCRIPTION OF THE DRAWINGS

0017These and/or other aspects and advantages of the invention will become apparent and more readily appreciated from the following description of the embodiments, taken in conjunction with the accompanying drawings of which: <ul id="ul0001" list-style="none" compact="compact"><li>FIG. 1A is a drawing illustrating a LiVO₂ structure;</li><li>FIG. 1B is a drawing illustrating a change in a LiVO₂ structure if at least 1 mole of lithium is intercalated into the LiVO₂;</li><li>FIG. 2 is a schematic diagram showing an embodiment of a non-aqueous electrolyte battery of the present invention;</li><li>FIG. 3 is a graph showing charge and discharge characteristics of the cells according to Examples 1 to 3 of the present invention and Comparative Example 1;</li><li>FIG. 4 is a graph showing charge and discharge characteristics of the cells according to Examples 4 to 6 of the present invention and Comparative Example 1;</li><li>FIG. 5 is a graph showing constant current charge and discharge characteristics and constant voltage charge and discharge characteristics of the cells according to Examples 4 and 7 of the present invention;</li><li>FIG. 6 is a graph showing constant current charge and discharge characteristics and constant voltage charge and discharge characteristics of the cells according to Examples 8 and 9 of the present invention;</li><li>FIG. 7 is a graph illustrating rate characteristics after the cell according to Example 8 of the present invention is constant voltage and constant current charged at a 0.2 C rate and a 1C rate;</li><li>FIG. 8 is a graph illustrating K-edge energies of the negative active materials according to Examples 4 and 6;</li><li>FIG. 9 is a graph illustrating K-edge energies of V₂O₃, V₂O₄, and V₂O₆ vanadium oxides;</li><li>FIG. 10 is a graph illustrating vanadium oxidation numbers converted from K-edge energies shown in FIGS. 7 and 8;</li><li>FIG. 11 is a graph illustrating charge and discharge characteristics of the negative active material according to Example 13 of the present invention;</li><li>FIG. 12 is a graph showing the cycle life characteristic of the negative active material according to Example 13 of the present invention; [and]</li><li>FIG. 13 is a graph showing charge and discharge characteristics of the negative active material according to Example 16 of the present invention;</li><li>FIG. 14 is a graph showing a particle diameter of the negative active material according to Example 19 of the present invention;</li><li>FIG. 15 is a SEM photograph of the negative active material according to Example 19 of the present invention;</li><li>FIG. 16 is a SEM photograph of the negative active material according to Example 20 of the present invention;</li><li>FIG. 17 is void volumes of the negative active materials according to Examples 24 to 25 of the present invention; and</li><li>FIG. 18 is a graph showing an X-ray diffraction pattern of the negative active material according to Examples 24 to 27 of the present invention.</li></ul>

DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS

0018Reference will now be made in detail to the embodiments of the present invention, examples of which are illustrated in the accompanying drawings, wherein like reference numerals refer to the like elements throughout. The embodiments are described below to explain the present invention by referring to the figures.

0019The present invention relates to a negative active material of a non-aqueous electrolyte battery. The negative active material exhibits a higher density than the conventional graphite active material, increasing its energy density per unit volume. In addition, the negative active material has low reactivity with organic electrolytes and provides effective safety. The negative active material of the present invention is represented by formula 1, and has a layer structure:         Li_xM_yV_zO_2+d     (1) where 0.1 ≤ x ≤ 2.5, 0 &lt; y ≤ 0.5, 0.5 ≤ z ≤ 1.5, 0 ≤ d ≤ 0.5; and M is at least one element selected from the group consisting of Al, Cr, Mo, Ti, W, and Zr, and is preferably Mo or W.

0020The present invention synthesizes the negative active material by substituting Co with one metal, V, and another metal, Mo, W, Ti, Cr, or Zr in LiCoO₂, which exhibits a discharge voltage substantially corresponding to graphite. The negative active material represented by formula 1 may provide a capacity per unit volume of 1000 mAh/cc or more.

0021LiCoO₂ or LiNiO₂ of an R-3M structure has an interlayer structure comprising oxygen, lithium, and a transition metal, and the lithium layer is partially intercalated or deintercalated such that they are used as rocking chair type active materials. The R-3M structure indicates layer structures which include one layer alternated with lithium and oxygen, and another layer alternated with a transition metal and oxygen.

0022For example, a structure of LiVO₂ is shown in FIG. 1A. If at least one mole of lithium is intercalated into the LiVO₂ structure shown in FIG. 1A, the structure is reversibly changed into the structure shown in FIG. 1B (this particular change in structure occurs in LiNiO₂). Such a change in structure (reversible intercalation and deintercalation of lithium shown in FIGS. 1A and 1 B) appears in a Li-rich compound by partially substituting a transition metal (V) with Li and with various transition metals such as Ti, Mo, Cr, or Al.

0023That is, V metal ions (substituted with Li and another metal) and Li ions are presented between oxygen ions which are presented in a hexagonal, closed packing form. In particular, V metal ions (substituted with Li and another metal) are presented at an octahedral site of oxygen ions in one layer, and Li ions are present at an octahedral site in the lower layer. When lithium is intercalated into the structure to convert Li₂NiO₂, a V metal ion layer (substituted Li with another metal) and an oxygen ion layer are present in turn. In addition, the oxygen layer and V metal ion layer (substituted with Li and another metal) are presented in turn between the two lithium layers.

0024The present invention increases the lattice constant, i.e., the distance between the axes, by partially substituting V with another metal and Li so that intercalation and deintercalation of lithium smoothly occurs at low voltages. Accordingly, as shown in FIG. 1B, the width of the lithium layer facilitates smooth and active intercalation and deintercalation of lithium. Such smooth intercalation and deintercalation of lithium indicates an increase in lithium diffusion, thus improving cycle life and high-rate characteristics.

0025The present inventors studied changes in lattice structure to prepare the inventive active material represented by formula 1 in which intercalation and deintercalation of lithium smoothly and actively occurs at low voltages. The compound represented by formula 1 has an average oxidation state of vanadium of +1 to +4, and preferably +1 to +3. That is, the redox reaction occurs at +1 to +4, which indicates a redox voltage to lithium metal of 1 V or less. Thus, the redox reaction of the compound occurs at lower voltages than in the general vanadium oxide, which has a redox voltage to lithium metal of 2 V or more, and in which the redox reaction occurs at +3 to +4, or +4 to +5. Accordingly, it is expected that the negative active material represented by formula 1 has a high discharge voltage.

0026In formula 1, if x, y, z and d are outside these ranges, if the structure is modified, the redox reaction occurs at +3 to +4, or +4 to +5, which indicates a 1.0 V or of higher average potential to the lithium metal, thus decreasing the discharge voltage. Use of a compound with a value of × of less than 0.1 is taught Solid State Ionics, 139, 57∼65, 2001 and Journal of Power Source, 81∼82, 651∼655, 1999. The compound is a vanadium negative active material without Li. The active material has a different crystalline structure from the inventive active material and has an average discharge potential of 1 V or more, which disqualifies it for use for a negative electrode.

0027Use of a compound with x, y, z, and d out of these ranges is taught in Electrochem. Communications 5 (2003), 261-266. The compound of Li₂Ag_0.5V₂O₅ also has a different crystalline structure from the inventive active material, and has a potential of 3 to 1 V, which is a voltage corresponding to a positive electrode rather than a negative electrode.

0028The negative active material of the present invention has a distance ratio between axes (axial ratio of c/a) of 2.5 to 6.5, and preferably 3.0 to 6.2, before lithium intercalation. If the distance ratio is outside this range, it is difficult to intercalate and deintercalate lithium and the voltage in which intercalation and deintercalation occur increases by 0.6 V or more. Furthermore, a hysteresis phenomenon occurs in which a difference between the voltage of intercalation and the voltage of deintercalation is due to the participation of oxygen in the reaction.

0029The negative active material of the present invention has a distance ratio between axes of 3.5 to 7.0, and preferably 4.0 to 7.0 after lithium intercalation.

0030The negative active material of the present invention has a change in volume of the crystal lattice of 30% or less, and preferably 27% to 0%, according to lithium intercalation and deintercalation. If the change in volume is more than 30%, cracking occurs, causing a short-cut, separation of the active material from the current collector, and agglomeration, so that the internal resistance increases, the capacity decreases and the cycle life deteriorates.

0031Generally, the charging of the battery is performed by constant-current and constant-voltage charging, obtaining capacity. Unfortunately, a metal or a composite of a metal and graphite active material which has recently been studied as a higher capacity active material are unable to constant-voltage charge because intercalation and deintercalation mechanisms in metal are different from such mechanisms in graphite. If the constant-voltage charge is applied to the metal or the composite, the structure of the active material is broken, causing severe deterioration, or the extraction of lithium occurs, causing problems associated with reversibility and safety. These shortcomings make it difficult to use the metal or the composite active material in a battery, even though they have high capacity.

0032However, the negative active material of the present invention may be constant current/ constant voltage charged so that it is useful for a battery.

0033The negative active material of the present invention has a nominal energy density per unit volume of 4.2 g/cc and an experimental energy density of about 3.0 g/cc. Furthermore, it has a nominal capacity per unit volume of 1200 mAh or more, and a theoretical capacity of 900 mAh/cc. On the other hand, the conventional graphite active material has a nominal energy density per unit volume of 2.0 g/cc, an energy density of substantially 1.6 g/cc, and a capacity by volume of substantially 570 mAh/cc. Thus, the negative active material of the present invention has an energy density that is twice the energy density of the conventional graphite active material.

0034A negative electrode using the negative active material of the present invention preferably has a density of 1 to 5g/cc and more preferably 1.2 to 4.5g/cc. Increased density renders loading of a large amount of active material so that it can provide a high-capacity battery, but too high a density obtained from severe pressure causes an extreme reduction in voids of the electrode which results in decreased electrolyte immersion, thereby deteriorating high-rate characteristics. Therefore, more than 5g/cc of density deteriorates the high-rate characteristics and less than 1 g/cc of density decreases capacity.

0035The negative active material of the present invention preferably has a tapping density of 1 to 5g/cc, and more preferably 1.2 to 4.5g/cc. When the tapping density is out of these ranges, it is difficult to form a high-density electrode.

0036The negative active material of the present invention preferably has an average diameter of 1 to 100µm, and more preferably 5 to 80µm. An average diameter of less than 1µm causes a side-reaction between the negative active material and the electrolyte, and more than 100µm decreases packing density in electrode preparation.

0037The negative active material of the present invention preferably has a void volume of 1X10^-3 to 0.5cc/g per weight of the particle having a size of 0.1 to 10µm, more preferably 0.01 to 0.5cc/g, and most preferably 0.1 to 0.3cc/g. The void volume is measured by the mercury injection process. If the void volume is less than 1 X 10-3cc/g, the high-rate characteristics deteriorate, if the void volume is more than 0.5cc/g, the capacity per weight decreases.

0038The negative active material of the present invention preferably has a specific surface area (BET) of 0.01 to 10m²/g, and more preferably 0.01 to 5m²/g. The specific surface area is determined from the nitrogen absorption BET process. If the specific surface area is less than 0.01m²/g, the high-rate characteristics deteriorate. If the specific surface area is more than 10m2/g, the side-reaction between the electrolyte and the negative active material occurs.

0039The negative active material of the present invention has a full width at half-maximum of an X-ray diffraction peak at (003) plane of 0.5 or less, and more preferably 0.3 or less, and that at (103) plane of 0.5 or less, and more preferably 0.4 or less. If the full width at half-maximum is more than 0.5, the structure is unstable, decreasing initial capacity and causing fading enlarged capacity loss as the cycles repeat.

0040The negative active material of the present invention has an X-ray diffraction intensity ratio of the (003) plane to (104) plane (I(003)/I(104)) of between 0.3 to 2, and more preferably 0.5 to 1.5.

0041The negative active material of the present invention has of 2.8 A &lt; lattice constant of a axis &lt; 2.9Å, and 14Å &lt; lattice constant of c axis &lt; 15Å. When the lattice constant is out of these ranges, the layer structure is distorted so that the capacity decreases.

0042The negative active material of the present invention is used in a negative electrode for a rechargeable lithium battery including a positive electrode and an electrolyte. The negative electrode employs only the inventive negative active material, or a mixture of the inventive negative active material and a carbonaceous negative active material at a weight ratio of 1 to 99 : 99 to 1, and preferably 10 to 90 : 90 to 10.

0043The negative active material of the present invention has lower reactivity with organic electrolytes, and thus has effective stability compared to the conventional carbonaceous material.

0044Preparation of a negative active material of the present invention will be illustrated more specifically below.

0045A vanadium source, a lithium source, and a metal source are mixed without a solvent. The mixing ratio therebetween may be suitably controlled if a desired product is a compound represented by formula 1. The vanadium source may be VO, V₂O₃, V₂O₄, V₂O₅, V₄O₇, VOSO₄.nH₂O, or NH₄VO₃, and the lithium source may be lithium carbonate, lithium hydroxide, lithium nitrate, or lithium acetate. The metal source may be oxides or hydroxides that include Al, Cr, Mo, Ti, W, and Zr, and examples thereof are Al(OH)₃, Al₂O₃, Cr₂O₃, MoO₃, TiO₂, WO₃, and ZrO₂.

0046The mixture is heat-treated at approximately 500°C to 1400°C, and preferably at 900 to 1200°C, under a reductive atmosphere to prepare the inventive negative active material represented by formula 1. If the heat-treatment temperature is outside such a range, impurities (e. g., Li₃VO₄) may be formed, resulting in a decrease in capacity and in a deterioration of the cycle life characteristic.

0047The reductive atmosphere is a nitrogen atmosphere, an argon atmosphere, a N₂/H₂ gas mixture atmosphere, a CO/CO₂ gas mixture atmosphere, or a helium atmosphere. The oxygen partial pressure of the reductive atmosphere is preferably less than 2X10^-1 atmospheres. A higher oxygen partial pressure than 2X10^-1 atmospheres produces an oxidative atmosphere which oxidizes metal oxide to prepare an undesired oxygen-rich product, or prepares a mixture of a desired product and an undesired product.

0048A positive electrode of a non-aqueous electrolyte battery, including the negative electrode with the negative active material, includes a positive active material which may intercalate and deintercalate lithium. Exemplary thereof are at least one selected from compounds represented by formulas 2 to 13:         Li_xMn_1-yM_yA₂     (2)         Li_xMn_1-yM_yO_2-zX_z     (3)         Li_xMn₂O_4-zX_z     (4)         Li_xCo_1-yM_yA₂     (5)         Li_xCO_1-yM_yO_2-zX_z     (6)         Li_xNi_1-yM_yA₂     (7)         Li_xNi_1-yM_yO_2-zX_z     (8)         Li_xNi_1-yCo_yO_2-zX_z     (9)         Li_xNi_1-y-zCo_yM_zA_α     (10)         Li_xNi_1-y-zCo_yM_zO_2-αX_α     (11)         Li_xNi_1-y-zMn_yM_zA_α     (12)         Li_xNi_1-y-zMn_yM_zO_2-αX_α     (13) wherein, 0.90 ≤ x ≤1.1; 0 ≤y ≤0.5; 0 ≤z≤0.5; 0 ≤ α ≤ 2; M is at least one element selected from the group consisting of Al, Ni, Co, Mn, Cr, Fe, Mg, Sr, V, and rare earth elements; A is selected from the group consisting of O, F, S, and P; and X is selected from F, S, and P.

0049The negative electrode and the positive electrode are produced by respectively mixing an active material, a conductive agent, and a binder in a solvent to prepare an active material composition and coating the composition on a current collector. The electrode preparation is well known in the related art; thus, the detailed description of electrode preparation will not be taught in the application.

0050The conductive agent includes any conventional conductive agent used for an active material composition as long as the conductive agent is chemically inert and has electrical conductivity. Examples thereof are one or a mixture selected from natural graphite; artificial graphite; carbon black; acetylene black; ketjen black; carbon fiber; a metal fiber such as copper, nickel, aluminum, and silver; and polyphenylene derivatives (Japanese Patent Laid-Open No. Sho 59-20971).

0051The binder may be polyvinyl alcohol, carboxymethylcellulose, hydroxylpropylenecellulose, diacetylenecellulose, polyvinylchloride, polyvinylpyrrolidone, polytetrafluoroethylene, polyvinylidene fluoride, polyethylene, or polypropylene.

0052The solvent may be N-methyl pyrrolidone.

0053A non-aqueous electrolyte includes an organic solvent and a lithium salt. The organic solvent includes at least one carbonate, ester, ether or ketone. If a mixed solvent is used, the mixing ratio may be suitably controlled according to desired battery characteristics, as may be understood by one skilled in the related art. The carbonate may be, but is not limited to, at least one dimethyl carbonate, diethyl carbonate, dipropyl carbonate, methylpropyl carbonate, ethylpropyl carbonate, methylethyl carbonate, ethylene carbonate, propylene carbonate, butylenes or carbonate. The ester may be, but is not limited to, γ-butyrolactone, decanolide, valerolactone, mevalonolactone, caprolactone, n-methyl acetate, n-ethyl acetate, or n-propyl acetate. The ether may be, but is not limited to, dibutyl ether. The ketone may be, but is not limited to, polymethylvinyl ketone.

0054Alternatively, the non-aqueous organic solvent may further include aromatic organic solvents. Examples of the aromatic organic solvents are benzene, fluorobenzene, tolune, fluorotoluene, trifluorotoluene, and xylene.

0055The lithium salts may be at least one selected from LiPF₆, LiBF₄, LiSbF₆, LiAsF₆, LiCF₃SO₃, LiN(CF₃SO₂)₃, Li(CF₃SO₂)₂N, LiC₄F₉SO₃, LiClO₄, LiAlO₄, LiAlCl₄, LiN(C_xF_2x+,SO₂)(where x and y are natural numbers), LiCl, and Lil. The lithium salts are dissolved in an organic solvent to act as a lithium-ion supporting source, which helps to allow the operation of the battery and facilitate the transfer of lithium ions. The concentration of the lithium salt is generally approximately 0.1 to 2.0 M in the electrolyte.

0056An embodiment of a non-aqueous electrolyte battery of the present invention is illustrated in FIG. 2. The rechargeable lithium battery includes a positive electrode 3; a negative electrode 2; a separator 4 interposed between the positive electrode 3 and the negative electrode 2; an electrolyte in which the positive electrode 2, the negative electrode 3, and the separator 4 are immersed; a cylindrical battery case 5; and a sealing portion 6. The configuration of the rechargeable lithium battery is not limited to the structure shown in FIG. 1, as it can be readily modified into a prismatic, or pouch type battery as is well understood in the related art.

0057The following examples illustrate the present invention in further detail, but it is understood that the present invention is not limited by these examples.

Example 1

0058Li₂CO₃, V₂O₄ and MoO₃ were mixed at the mole ratio of Li:V:Mo of 1.1:0.89:0.01 without solvent. The mixture was heat-treated at 1100°C under a nitrogen atmosphere to provide a Li_1.1V_0.89Mo_0.01O₂ negative active material. The negative active material had a diffraction pattern of a single phase of an R-3M crystal structure.

005980 wt% of the negative active material, 10 wt% of a graphite conductive agent and 10 wt% of a polytetrafluoroethylene binder were mixed in an N-methyl pyrrolidone solvent to prepare a negative active material slurry. The slurry was coated on a Cu-foil current collector to produce a negative electrode. The density of the active mass (a mixture of the active material, the conductive agent and the binder) was 1.6 g/cc.

0060The charge and discharge characteristics of the negative active material exhibited a high initial reversible capacity of 800 mAh/cc and better cycle life characteristics than the conventional graphite active material.

Example 2

0061A negative electrode was produced by the same procedure as in Example 1, except that the mole ratio of Li:V:Mo was changed to 1.1:0.87:0.03 to prepare a Li_1.1V_0.87Mo_0.03O₂ negative active material.

Example 3

0062A negative electrode was produced by the same procedure as in Example 1, except that the mole ratio of Li:V:Mo was changed to 1.1:0.85:0.05 to prepare a Li_1.1V_0.85M_0.05O₂ negative active material.

Comparative Example 1

0063A negative electrode was produced by the same procedure as in Example 1, except that Li₂CO₃ and V₂O₄ were mixed at the mole ratio of Li:V of 1.1:0.9 without solvent to prepare a Li_1.1V_0.9O₂ negative active material.

Comparative Example 2

0064Li₂CO₃ and V₂O₄ were mixed at the mole ratio of Li:V of 1.1:0.9 without solvent, and the mixture was heat-treated at 1200°C under a nitrogen atmosphere to prepare a Li_1.1V_0.9O₂ negative active material. Using the negative active material, a negative electrode was produced by the same procedure as in Comparative Example 1.

Comparative Example 3

0065Li₂CO₃ and V₂O₄ were mixed at the mole ratio of Li:V of 1.1:0.9 without solvent, and the mixture was heat-treated at 1100°C under a nitrogen atmosphere to prepare a Li_1.1V_0.9O₂ negative active material. Using the negative active material, a negative electrode was produced by the same procedure as in Comparative Example 1.

Charge and discharge characteristics

0066Using the negative electrodes according to Examples 1 to 3 and Comparative Example 1, and lithium metal counter electrodes, half-cells were fabricated by the general procedure. The cells were constant-charged at a 0.2 C rate from 0 to 2 V. The charge and discharge characteristics are shown in FIG. 3. As shown in FIG. 3, the negative active material according to Examples 1 to 3 wherein Mo is substituted for predetermined amounts of vanadium exhibited higher capacity than the negative active material without Mo according to Comparative Example 1.

Example 4

0067A negative electrode was produced by the same procedure as in Example 1, except that Li₂CO₃, V₂O₃ and TiO₂ were mixed at the mole ratio of Li:V:Ti of 1.1:0.89:0.01 to prepare a Li_1.1V_0.89Ti_0.01O₂ negative active material.

Example 5

0068A negative electrode was produced by the same procedure as in Example 4, except that the mole ratio of Li:V:Ti was changed to 1.1:0.87:0.03 to prepare a Li_1.1V_0.87Ti_0.03O₂ negative active material.

Example 6

0069A negative electrode was produced by the same procedure as in Example 4, except that the mole ratio of Li:V:Ti was changed to 1.1:0.85:0.05 to prepare a Li_1.1V_0.85Ti_0.05O₂ negative active material.

Charge and discharge characteristics

0070Using the negative electrodes according to Examples 4 to 6 and lithium metal counter electrodes, half-cells were fabricated by the general procedure. The cells were constant-charged at a 0.2 C rate between 0 to 2 V, and the charge and discharge characteristics are shown in FIG. 4. FIG. 4 indicates that the negative active material according to Examples 4 to 6, made by substituting Ti for predetermined amounts of vanadium, exhibited a higher capacity than the negative active material without Ti according to Comparative Example 1.

Example 7

0071A negative electrode was produced by the same procedure as in Example 4, except that the density of the active mass was changed to 2.4 g/cc.

Charge and discharge characteristics

0072Using the negative electrode according to Example 7 and a lithium metal counter electrode, a half-cell was fabricated by the general procedure. Cells according to Examples 7 and 4 were constant-current charged at a 0.2 C rate between 0 to 2 V, and the cells were 0.01 V constant-voltage charged at a 1/50 C rate. The charge and discharge characteristics are shown in FIG. 5. It is evident from FIG. 5 that the cells according to Examples 4 and 7 may both be constant-current charged and constant-voltage charged even though the negative electrode of Example 7 had an increased active mass density compared to the negative electrode of Example 4.

Example 8

0073A negative electrode was produced by the same procedure as in Example 4 except that the Li_1.1V_0.89Ti_0.01O₂ negative active material was mixed with a graphite conductive agent in the weight ratio of 5:5, and 90 wt% of the mixture was mixed with 10 w% of a binder.

Example 9

0074A negative electrode was produced by the same procedure as in Example 8 except that the density of the active mass was changed to 2.4 g/cc.

Cycle life characteristics

0075Using the negative electrodes according to Examples 8 and 9 and lithium metal counter electrodes, half-cells were fabricated by the general procedure. The half-cells were constant-current charged at 0.2 C between 0 to 2 V, and the cells were constant-current and 0.01 constant-voltage charged at a 1/50 C rate. The cycle life characteristics are presented in FIG. 6. FIG. 6 indicates that the cells according to Examples 8 and 9 may both be constant-current and constant-voltage charged even though the density of the active mass of Example 9 increased compared to the density of the active mass of Example 8.

Charge and discharge characteristics at various rates

0076The cell according to Example 8 was constant-current and constant-voltage charged at a 0.2 C rate and a 1 C rate for 5 cycles, respectively. The results as shown in FIG. 7 demonstrate that the capacity at 0.2 C corresponded to 95.5% of the capacity at 1 C, indicating virtually no deterioration at high rates. The conventional graphite negative active material has a capacity at 0.2 C that corresponds to 80 to 95% of the capacity at 1 C.

Determination of oxidation number

0077To determine the oxidation number of negative active materials according to Examples 4 to 6 according to the addition of Ti, the K-edge energies were measured using XANES. The results are presented in FIG. 8. For reference, the K-edge energy of V₂O₃ is also presented in FIG. 8. In addition, the K-edge energy of vanadium oxides, V₂O₃, V₂O₄, and V₂O₅ are shown in FIG. 9. The K-edge energies shown in FIGS. 8 and 9 were converted into vanadium oxidation numbers. The results are presented in FIG. 10 and Table 1. The K-edge energies and vanadium oxidation numbers according to Comparative Examples 1 to 3 are also presented in Table 1. FIG. 10 and Table 1 indicate that the oxidation numbers according to Examples 4 to 6 were 1.0 to 2.5, and the K-edge energies were 1.4 to 4.9 eV. <tables id="tabl0001" num="0001"><table frame="all"><title>Table 1</title><tgroup cols="4" colsep="1" rowsep="1"><colspec colnum="1" colname="col1" colwidth="39.37mm" /><colspec colnum="2" colname="col2" colwidth="39.37mm" /><colspec colnum="3" colname="col3" colwidth="39.37mm" /><colspec colnum="4" colname="col4" colwidth="39.37mm" /><thead valign="top"><row><entry namest="col1" nameend="col1" align="center">Compound</entry><entry namest="col2" nameend="col2" align="center">1/2 height of K-edge, keV</entry><entry namest="col3" nameend="col3" align="center">Energy position of K-edge respective to V₂O₃</entry><entry namest="col4" nameend="col4" align="center">V oxidation state</entry></row></thead><tbody valign="top"><row><entry namest="col1" nameend="col1" align="center">V₂O₃</entry><entry namest="col2" nameend="col2" align="center">5.4860 ± 0.0003</entry><entry namest="col3" nameend="col3" align="center">-</entry><entry namest="col4" nameend="col4" align="center">3</entry></row><row><entry namest="col1" nameend="col1" align="center">Comparative Example 1 (Li_1.1V_0.9O₂, from V₂O₄)</entry><entry namest="col2" nameend="col2" align="center">5.4840 ± 0.0003</entry><entry namest="col3" nameend="col3" align="center">2.0 eV</entry><entry namest="col4" nameend="col4" align="center">2.3</entry></row><row><entry namest="col1" nameend="col1" align="center">Comparative Example 2 (Li_1.1V_0.9O₂, from V₂O₄, 1200°C)</entry><entry namest="col2" nameend="col2" align="center">5.4841 ± 0.0003</entry><entry namest="col3" nameend="col3" align="center">1.9 eV</entry><entry namest="col4" nameend="col4" align="center">2.3</entry></row><row><entry namest="col1" nameend="col1" align="center">Comparative Example 3 (Li_1.1V_0.9O₂, from V₂O₃, 1100°C)</entry><entry namest="col2" nameend="col2" align="center">5.4849 ±0.0003</entry><entry namest="col3" nameend="col3" align="center">1.1 eV</entry><entry namest="col4" nameend="col4" align="center">2.6</entry></row><row><entry namest="col1" nameend="col1" align="center">Example 4 (Li_1.1V_0.89Ti_0.01O₂, from V₂O₄, 1100°C)</entry><entry namest="col2" nameend="col2" align="center">5.4846 ±0.0004</entry><entry namest="col3" nameend="col3" align="center">1.4 eV</entry><entry namest="col4" nameend="col4" align="center">2.5</entry></row><row><entry namest="col1" nameend="col1" align="center">Example 5 (Li_1.1V_0.87 Ti_0.03O₂, from V₂O₄, 1100°C)</entry><entry namest="col2" nameend="col2" align="center">5.4829±0.0003</entry><entry namest="col3" nameend="col3" align="center">3.1 eV</entry><entry namest="col4" nameend="col4" align="center">1.8</entry></row><row rowsep="1"><entry namest="col1" nameend="col1" align="center">Example 6 (Li_1.1V_0.85 Ti_0.05O₂, from V₂O₄, 1100°C)</entry><entry namest="col2" nameend="col2" align="center">5.4811±0.0003</entry><entry namest="col3" nameend="col3" align="center">4.9 eV</entry><entry namest="col4" nameend="col4" align="center">1.0</entry></row></tbody></tgroup></table></tables>

Example 10

0078V₂O₃, LiCO₃, and WO₃ were mixed at the mole ratio of Li:V:W of 1.08:0.85:0.05 without solvent. The mixture was heat-treated at 1000°C under a nitrogen atmosphere to prepare a L_1.08V_0.85W_0.05O₂ negative active material. Using the negative active material, a negative electrode was produced by the same procedure as in Example 1.

0079The charge and discharge characteristics of the negative electrode indicated a high initial reversible capacity of 700 mAh/cc and an effective cycle life characteristic, which correspond to the results according to Example 1.

Example 11

0080V₂O₃, LiCO₃, and MoO₃ were mixed at the mole ratio of Li:V:Mo of 1.08 : 0.85:0.05 without solvent. The mixture was heat-treated at 1100°C under a nitrogen atmosphere to prepare a Li_1.08V_0.85Mo_0.05O₂ negative active material. Using the negative active material, a negative electrode was produced by the same procedure as in Example 1.

0081The charge and discharge characteristics of the negative electrode indicated a high initial reversible capacity of 900 mAh/cc (∼ 300 mAh/g) and a good cycle life characteristic.

Example 12

0082V₂O₄, LiCO₃, and MoO₃ were mixed at the mole ratio of Li:V:Mo of 1.08:0.9:0.02 without solvent. The mixture was heat-treated at 900°C under a nitrogen atmosphere to prepare a Li_1.08V_0.9Mo_0.02O₂ negative active material. The negative active material had a single diffraction pattern of an R-3M crystalline structure. Using the negative active material, a negative electrode was produced by the same procedure as in Example 1.

0083The charge and discharge characteristics of the negative electrode indicated reversible capacity and cycle life characteristics corresponding to Example 1.

Example 13

0084V₂O₅, LiCO₃, and MoO₃ were mixed at the mole ratio of Li:V:Mo of 1.08:0.9:0.02 without solvent. The mixture was heat-treated at 1000°C under a nitrogen atmosphere to prepare a Li_1.08V_0.9Mo_0.02O₂ negative active material. Using the negative active material, a negative electrode was produced by the same procedure as in Example 1.

0085The charge and discharge characteristics of the negative electrode indicated reversible capacity and cycle life characteristics corresponding to Example 1.

0086The charge and discharge characteristics of the cell using the negative active material according to Example 13 are shown in FIG. 11, and the cycle life characteristic is shown in FIG. 12. FIGS. 11 and 12 indicate that the cell using the negative active material according to Example 13 exhibited effective charge and discharge and cycle life characteristics.

Example 14

0087V₂O₃, LiCO₃, and TiO₂ were mixed at the mole ratio of Li:V:Ti of 1.08:0.9:0.02 without solvent. The mixture was heat-treated at 900°C under a nitrogen atmosphere to prepare a Li_1.08V_0.9Ti_0.02O₂ negative active material. The negative active material had a single diffraction pattern of an R-3M crystalline structure.

008880 wt% of the negative active material, 10 wt% of a graphite conductive agent, and 10 wt% of a polytetrafluoroethylene binder were mixed in an N-methyl pyrrolidone solvent to prepare a negative active material slurry. The slurry was coated on a Cu-foil current collector to produce a negative electrode.

0089The charge and discharge characteristics of the negative electrode indicated a high initial reversible capacity of 800 mAh/cc and an effective cycle life characteristic.

Example 15

0090V₂O₃, LiCO₃, and TiO₂ were mixed at the mole ratio of Li:V:Ti of 1.08:0.85:0.05 without solvent. The mixture was heat-treated at 1000°C under a nitrogen atmosphere to prepare a Li_1.08V_0.85Ti_0.05O₂ negative active material. Using the negative active material, a negative electrode was produced by the same procedure as in Example 1.

0091A charge and discharge test of the negative electrode indicated a high initial reversible capacity of 700 mAh/cc and an effective cycle life characteristic.

Example 16

0092V₂O₃, LiCO₃, and TiO₂ were mixed at the mole ratio of Li:V:Ti of 1.08:0.85:0.03 without solvent. The mixture was heat-treated at 1100°C under a nitrogen atmosphere to prepare a Li_1.08V_0.85Ti_0.03O₂ negative active material. Using the negative active material, a negative electrode was produced by the same procedure as in Example 1.

0093The charge and discharge characteristic of the negative electrode indicated a high initial reversible capacity of 900mAh/cc (∼ 300 mAh/g) and an effective cycle life characteristic.

Example 17

0094V₂O₄, LiCO₃ and TiO₂ were mixed at the mole ratio of Li:V:Ti of 1.08:0.9:0.02 without solvent. The mixture was heat-treated at 900°C under a nitrogen atmosphere to prepare a Li_1.08V_0.9Ti_0.02O₂ negative active material. The negative active material had a single diffraction pattern of an R-3M crystalline structure. Using the negative active material, a negative electrode was produced by the same procedure as in Example 1.

0095The charge and discharge characteristics of the negative electrode indicated reversible capacity and cycle life characteristics corresponding to Example 1.

Example 18

0096V₂O₅, LiCO₃, and TiO₂ were mixed at the mole ratio of Li:V:Ti of 1.08:0.9:0.02 without solvent. The mixture was heat-treated at 1000°C under a nitrogen atmosphere to prepare a Li_1.08V_0.9Ti_0.2O₂ negative active material. Using the negative active material, a negative electrode was produced by the same procedure as in Example 1.

0097The charge and discharge characteristics of the negative electrode indicated reversible capacity and cycle life characteristics corresponding to Example 1.

0098The charge and discharge characteristics of the cell using the negative active material according to Example 16 are shown in FIG. 13. It is evident from FIG. 13 that the cell using the negative active material according to Example 16 exhibited effective charge and discharge and cycle life characteristics.

Example 19

0099V₂O₃, Li₂CO₃, and MoO₃ were mixed at the mole ratio of Li:V:Mo of 1.08:0.9:0.02 without solvent. The mixture was heat-treated at 1000□ for 10 hours under a nitrogen atmosphere and then cooled to room temperature. The obtained material was sieved to obtain a Li_1.08V_0.9Mo_0.02O₂ negative active material.

0100The average diameter of the negative active material according to Example 19 was measured and the result is presented in FIG. 14. As shown in FIG. 14, the average diameter (D50) was about 35µm.

Example 20

0101V₂O₃, Li₂CO₃, and MoO₃ were mixed at the mole ratio of Li:V:Mo of 1.08:0.9:0.02 without solvent. The mixture was heat-treated at 1000□ for 10 hours under a nitrogen atmosphere, and then cooled to room temperature. The obtained material was sieved to obtain a Li_1.08V_0.9Mo_0.02O₂ negative active material with an average diameter (D50) of 80µm.

Example 21

0102V₂O₄, Li₂CO₃, and WO₃ were mixed at the mole ratio of Li:V:W of 1.08:0.85:0.05 without solvent. The mixture was heat-treated at 1000□ for 10 hours under a nitrogen atmosphere, and then cooled to room temperature. The obtained material was sieved to obtain a Li_1.08V_0.9Mo_0.02O₂ negative active material with an average diameter (D50) of 25µm.

Example 22

0103V₂O₄, Li₂CO₃, and WO₃ were mixed at the mole ratio of Li:V:W of 1.08:0.85:0.05 without solvent. The mixture was heat-treated at 1000□ for 10 hours under a nitrogen atmosphere, and then cooled to room temperature. The obtained material was sieved to obtain a Li_1.08V_0.9Vo_0.02Mo_0.02O₂ negative active material with an average diameter (D50) of 80µm.

Example 23

0104V₂O₃, Li₂CO₃, and MoO₃ were mixed at the mole ratio of Li:V:W of 1:0.95:0.05 without solvent. The mixture was heat-treated at 1000□ for 10 hours under a nitrogen atmosphere and then cooled to room temperature. The obtained material was sieved to obtain a Li_1.08V_0.9Mo_0.02O₂ negative active material with an average diameter (D50) of 120µm.

Comparative Example 4

0105V₂O₃, Li₂CO₃, and MoO₃ were mixed at the mole ratio of Li:V:W of 3:0.85:0.05 without solvent. The mixture was heat-treated at 1000□ for 10 hours under a nitrogen atmosphere and then cooled to room temperature. The obtained material was sieved to obtain a Li_1.08V_0.9MO_0.02O₂ negative active material with an average diameter (D50) of 30µm.

Comparative Example 5

0106V₂O₃, Li₂CO₃, and WO₃ were mixed at the mole ratio of Li:V:W of 1.1:0.05:0.85 without solvent. The mixture was heat-treated at 800□ for 10 hours under a nitrogen atmosphere and then cooled to room temperature. The obtained material was sieved to obtain a Li_1.08V_0.9Mo_0.02O₂ negative active material with an average diameter (D50) of 30µm.

< SEM photograph>

0107The SEM photographs of the negative active materials according to Examples 19 and 20 are shown in FIGS. 15 and 16, respectively. As shown in FIGS. 15 and 16, the negative active materials according to Examples 19 and 20 have an elliptical-like type.

< Tapping density measurement>

0108Tapping densities of the negative active materials according to Examples 19 and 20 were measured by the following procedure with an MT-1000 (available from SEISHIN CO.), and the results are shown in Table 2.

0109The negative active material was slowly charged into a 100ml mass cylinder of which weight was previously measured, with a spoon through a 200mm mesh until a volume of the negative active material reached 100ml. A weight of the negative active material charged into the mass cylinder was then obtained by subtraction of the original weight of the mass cylinder (Mo) from the weight of the mass cylinder with the negative active material (M).

0110Thereafter, the negative active material charged mass cylinder was covered with a rubber plate and was dropped 500 times from a height of 18mm, and a volume (V) of the packed negative active material was measured.

0111Using the weight of M and the volume of V, tapping densities were determined by the following mathematical formula 1.<maths id="math0001" num=""><math display="block"><mrow><mtext>Mathematical formula 1</mtext><mspace linebreak="newline" /><mtext> D = (M-Mo)/V</mtext></mrow></math><img file="EP1511101A2_D0001.tif" /></maths><dl id="dl0001"><dt>D:</dt><dd>Tapping density (g/cc)</dd><dt>Mo:</dt><dd>Weight of mass cylinder (g)</dd><dt>M:</dt><dd>Weight of mass cylinder with negative active material (g)</dd><dt>V:</dt><dd>Volume of negative active material after being dropped 500 times</dd></dl>

0112The results are present in Table 2.

<Battery performances measurements>

0113Electrochemical performance tests (capacity and cycle life) were performed on the negative active materials according to Examples 19 to 23, and Comparative Examples 4 and 5. The negative active material/ a graphite conductive agent/ a polyvinyldiene fluoride binder were weighed at a weight ratio of 45 : 45 : 10, and they were dissolved in an N-methyl-2-pyrrolidone solvent to prepare a slurry. The slurry was coated on a Cu foil to produce a negative electrode in the form of a thin plate (thickness of 40 to 50µm including the thickness of the Cu foil) and dried in an oven at 135□ for 3 hours or more followed by pressing. Using the negative electrode and a lithium metal counter electrode, a 2015 coin-type half-cell was fabricated. The cell was charged and discharged at 0.2C↔0.2C (one cycle) at 0.01V to 2.0V, 0.2C↔0.2C (one cycle) at 0.01V to 1.0V, and 1C↔1C (50 cycles) at 0.01V to 1.0V, then the initial capacity, initial discharge capacity per weight, initial discharge capacity per volume, initial efficiency, and cycle-life characteristics (capacity retention) were measured. The results are shown in Table 2. The cycle-life characteristics were percentage values obtained from dividing the discharge capacity after 50 cycles by initial discharge capacity. <tables id="tabl0002" num="0002"><table frame="all"><title>Table 2</title><tgroup cols="9" colsep="1" rowsep="1"><colspec colnum="1" colname="col1" colwidth="17.50mm" /><colspec colnum="2" colname="col2" colwidth="17.50mm" /><colspec colnum="3" colname="col3" colwidth="17.50mm" /><colspec colnum="4" colname="col4" colwidth="17.50mm" /><colspec colnum="5" colname="col5" colwidth="17.50mm" /><colspec colnum="6" colname="col6" colwidth="17.50mm" /><colspec colnum="7" colname="col7" colwidth="17.50mm" /><colspec colnum="8" colname="col8" colwidth="17.50mm" /><colspec colnum="9" colname="col9" colwidth="17.50mm" /><thead valign="top"><row><entry namest="col1" nameend="col1" /><entry namest="col2" nameend="col2" align="center">Average diameter (µm)</entry><entry namest="col3" nameend="col3" align="center">Tapping density (g/cc)</entry><entry namest="col4" nameend="col4" align="center">Density of electrode (g/cc)</entry><entry namest="col5" nameend="col5" align="center">Initial charge capacity (mAh/g)</entry><entry namest="col6" nameend="col6" align="center">Initial discharge capacity (mAh/g)</entry><entry namest="col7" nameend="col7" align="center">Initial discharge capacity (mAh/cc)</entry><entry namest="col8" nameend="col8" align="center">Initial efficiency (%)</entry><entry namest="col9" nameend="col9" align="center">Cycle-life characteristics (%)</entry></row></thead><tbody valign="top"><row><entry namest="col1" nameend="col1" align="left">Example 19</entry><entry namest="col2" nameend="col2" align="center">35</entry><entry namest="col3" nameend="col3" align="center">2.2</entry><entry namest="col4" nameend="col4" align="char" char=".">2.4</entry><entry namest="col5" nameend="col5" align="center">350</entry><entry namest="col6" nameend="col6" align="center">316</entry><entry namest="col7" nameend="col7" align="center">758.4</entry><entry namest="col8" nameend="col8" align="center">90</entry><entry namest="col9" nameend="col9" align="center">85</entry></row><row><entry namest="col1" nameend="col1" align="left">Example 20</entry><entry namest="col2" nameend="col2" align="center">80</entry><entry namest="col3" nameend="col3" align="center">2</entry><entry namest="col4" nameend="col4" align="char" char=".">2.2</entry><entry namest="col5" nameend="col5" align="center">362</entry><entry namest="col6" nameend="col6" align="center">322</entry><entry namest="col7" nameend="col7" align="center">708.4</entry><entry namest="col8" nameend="col8" align="center">89</entry><entry namest="col9" nameend="col9" align="center">83</entry></row><row><entry namest="col1" nameend="col1" align="left">Example 21</entry><entry namest="col2" nameend="col2" align="center">25</entry><entry namest="col3" nameend="col3" align="center">2.1</entry><entry namest="col4" nameend="col4" align="char" char=".">2.6</entry><entry namest="col5" nameend="col5" align="center">377</entry><entry namest="col6" nameend="col6" align="center">338</entry><entry namest="col7" nameend="col7" align="center">878.8</entry><entry namest="col8" nameend="col8" align="center">90</entry><entry namest="col9" nameend="col9" align="center">79</entry></row><row><entry namest="col1" nameend="col1" align="left">Example 22</entry><entry namest="col2" nameend="col2" align="center">80</entry><entry namest="col3" nameend="col3" align="center">2</entry><entry namest="col4" nameend="col4" align="char" char=".">2.3</entry><entry namest="col5" nameend="col5" align="center">364</entry><entry namest="col6" nameend="col6" align="center">325</entry><entry namest="col7" nameend="col7" align="center">747.5</entry><entry namest="col8" nameend="col8" align="center">89</entry><entry namest="col9" nameend="col9" align="center">80</entry></row><row><entry namest="col1" nameend="col1" align="left">Example 23</entry><entry namest="col2" nameend="col2" align="center">120</entry><entry namest="col3" nameend="col3" align="center">1.1</entry><entry namest="col4" nameend="col4" align="char" char=".">1.5</entry><entry namest="col5" nameend="col5" align="center">318</entry><entry namest="col6" nameend="col6" align="center">250</entry><entry namest="col7" nameend="col7" align="center">375</entry><entry namest="col8" nameend="col8" align="center">79</entry><entry namest="col9" nameend="col9" align="center">68</entry></row><row><entry namest="col1" nameend="col1" align="left">Comparative Example 4</entry><entry namest="col2" nameend="col2" align="center">30</entry><entry namest="col3" nameend="col3" align="center">1.5</entry><entry namest="col4" nameend="col4" align="char" char=".">1.9</entry><entry namest="col5" nameend="col5" align="center">362</entry><entry namest="col6" nameend="col6" align="center">204</entry><entry namest="col7" nameend="col7" align="center">387.6</entry><entry namest="col8" nameend="col8" align="center">56</entry><entry namest="col9" nameend="col9" align="center">-</entry></row><row rowsep="1"><entry namest="col1" nameend="col1" align="left">Comparative Example 5</entry><entry namest="col2" nameend="col2" align="center">30</entry><entry namest="col3" nameend="col3" align="center">1.8</entry><entry namest="col4" nameend="col4" align="char" char=".">1.7</entry><entry namest="col5" nameend="col5" align="center">401</entry><entry namest="col6" nameend="col6" align="center">183</entry><entry namest="col7" nameend="col7" align="center">311.1</entry><entry namest="col8" nameend="col8" align="center">46</entry><entry namest="col9" nameend="col9" align="center">-</entry></row></tbody></tgroup></table></tables>

0114As shown in Table 2, the negative active materials according to Examples 19 to 22 have tapping densities of 23 to 2.2g/cc, an average diameter of 25 to 80µm, and higher density of the electrode. In addition, the cells with the negative active material according to Examples 19 to 22 exhibited better initial charge capacity per weight, discharge capacity, discharge capacity per volume, and initial efficiency than Comparative Examples 4 and 5. Example 23 using the negative active material having a larger diameter than other materials according to Examples 19 to 22 exhibits a slightly reduced charge and discharge capacity, but a desirable initial efficiency and cycle life characteristics.

0115The cells according to Comparative Examples 4 and 5 have a similar average diameter and charged density with those according to Examples 1 to 4, but the inherent physical properties of the active materials according to Comparative Examples 2 and 3 deteriorates the charge and discharge efficiency and cycle life characteristics

Example 24

0116V₂O₃, Li₂CO₃, and MoO₃ were mixed at the mole ratio of Li:V:Mo of 1.08:0.9:0.02 without solvent. The mixture was heat-treated at 900□ for 10 hours under a nitrogen atmosphere and then cooled to room temperature to prepare a Li_1.08V_0.9Mo_0.02O₂ negative active material.

Example 25

0117V₂O₃, Li₂CO₃, and WO₃ were mixed at the mole ratio of Li:V:W of 1.12:0.85:0.05 without solvent. The mixture was heat-treated at 1000□ for 10 hours under a nitrogen atmosphere, and then cooled to room temperature to prepare a Li_1.12V_0.85Mo_0.05O₂ negative active material.

Example 26

0118V₂O₃, Li₂CO₃, and MoO₃ were mixed at the mole ratio of Li:V:Mo of 1.1:0.85:0.05 without solvent. The mixture was heat-treated at 1100□ for 10 hours under a nitrogen atmosphere, and then cooled to room temperature to prepare a Li_1.1V_0.85Mo_0.05O₂ negative active material.

Example 27

0119V₂O₃, Li₂CO₃, and MoO₃ were mixed at the mole ratio of Li:V:Mo of 1.08:0.9:0.02 without solvent. The mixture was heat-treated at 900□ for 10 hours under a nitrogen atmosphere, and then cooled to room temperature to prepare a Li_1.08V_0.9Mo_0.02O₂ negative active material.

Comparative Example 6

0120V₂O₃, Li₂CO₃ and MoO₃ were mixed at the mole ratio of Li:V:Mo of 1:0.95:0.05 without solvent. The mixture was heat-treated at 1000□ for 10 hours under a nitrogen atmosphere, and then cooled to room temperature to prepare a Li_1.0V_0.95Mo_0.05O₂ negative active material.

Comparative Example 7

0121V₂O₃, Li₂CO₃ and MoO₃ were mixed at the mole ratio of Li:V:Mo of 3:0.85:0.05 without solvent. The mixture was heat-treated at 1000□ for 10 hours under a nitrogen atmosphere, and then cooled to room temperature to prepare a Li₃V_0.85Mo_0.05O₂ negative active material.

Comparative Example 8

0122V₂O₃, Li₂CO₃ and WO₃ were mixed at the mole ratio of Li:V:Mo of 1.1:0.05:0.85 without solvent. The mixture was heat-treated at 400□ for 10 hours under a nitrogen atmosphere, and then cooled to room temperature to prepare a Li_1.1V_0.05W_0.85O₂ negative active material.

< Void Volume>

0123The void volumes of the negative active materials according to Examples 24 to 25 were measured and the results are shown in FIG. 17. As shown in FIG. 17, the negative active materials according to Examples 24 to 25 have the void volume of 1 X 10^-3cc/g to 0.33cc/g per weight of the particle having a size of 0.1 to 10 µm.

<Battery performances measurements>

0124Electrochemical performance tests (capacity and cycle life) were performed on the negative active materials according to Examples 24 to 27, and Comparative Examples 6 to 8. The negative active material/ a graphite conductive agent/ a polyvinylidene fluoride binder were weighed at a weight ratio of 45 : 45 : 10, and they were dissolved in an N-methyl-2-pyrrolidone solvent to prepare a slurry. The slurry was coated on a Cu foil to produce a negative electrode in the form of a thin plate (thickness of 40 to 50µm including the thickness of a Cu foil) and dried in an oven at 135□ for 3 hours or more followed by pressing. Using the negative electrode and a lithium metal counter electrode, a 2015 coin-type half-cell was fabricated. The cell was charged and discharged at 0.2C↔0.2C (one cycle) at 0.01V to 2.0V, 0.2C↔0.2C (one cycle) at 0.01V to 1.0V, and 1 C↔1 C (50 cycles) at 0.01V to 1.0V, then the initial capacity, initial discharge capacity per weight, initial discharge capacity per volume, initial efficiency and the cycle-life characteristics (capacity retention) were measured. The results are shown in Table 3. The cycle-life characteristics were percentage values obtained from dividing the discharge capacity after 50 cycles by initial discharge capacity. In Table 3, the void volume is an average value of the void volume for a particle with a size of 0.1 to 10µm. <tables id="tabl0003" num="0003"><table frame="all"><title>Table 3</title><tgroup cols="7" colsep="1" rowsep="1"><colspec colnum="1" colname="col1" colwidth="22.50mm" /><colspec colnum="2" colname="col2" colwidth="22.50mm" /><colspec colnum="3" colname="col3" colwidth="22.50mm" /><colspec colnum="4" colname="col4" colwidth="22.50mm" /><colspec colnum="5" colname="col5" colwidth="22.50mm" /><colspec colnum="6" colname="col6" colwidth="22.50mm" /><colspec colnum="7" colname="col7" colwidth="22.50mm" /><thead valign="top"><row><entry namest="col1" nameend="col1" /><entry namest="col2" nameend="col2" align="center">Void volume (cc/g) (0.1-10µm)</entry><entry namest="col3" nameend="col3" align="center">BET (m²/g)</entry><entry namest="col4" nameend="col4" align="center">Initial charge capacity (mAh/g)</entry><entry namest="col5" nameend="col5" align="center">Initial discharge capacity (mAh/g)</entry><entry namest="col6" nameend="col6" align="center">Initial efficiency (%)</entry><entry namest="col7" nameend="col7" align="center">Cycle life (%)</entry></row></thead><tbody valign="top"><row><entry namest="col1" nameend="col1" align="center">Example 24</entry><entry namest="col2" nameend="col2" align="center">0.2</entry><entry namest="col3" nameend="col3" align="center">3</entry><entry namest="col4" nameend="col4" align="center">355</entry><entry namest="col5" nameend="col5" align="center">318</entry><entry namest="col6" nameend="col6" align="center">90</entry><entry namest="col7" nameend="col7" align="center">86</entry></row><row><entry namest="col1" nameend="col1" align="center">Example 25</entry><entry namest="col2" nameend="col2" align="center">0.2</entry><entry namest="col3" nameend="col3" align="center">4</entry><entry namest="col4" nameend="col4" align="center">369</entry><entry namest="col5" nameend="col5" align="center">320</entry><entry namest="col6" nameend="col6" align="center">87</entry><entry namest="col7" nameend="col7" align="center">87</entry></row><row><entry namest="col1" nameend="col1" align="center">Example 26</entry><entry namest="col2" nameend="col2" align="center">0.3</entry><entry namest="col3" nameend="col3" align="center">2.1</entry><entry namest="col4" nameend="col4" align="center">371</entry><entry namest="col5" nameend="col5" align="center">338</entry><entry namest="col6" nameend="col6" align="center">91</entry><entry namest="col7" nameend="col7" align="center">78</entry></row><row><entry namest="col1" nameend="col1" align="center">Example 27</entry><entry namest="col2" nameend="col2" align="center">0.32</entry><entry namest="col3" nameend="col3" align="center">3.6</entry><entry namest="col4" nameend="col4" align="center">362</entry><entry namest="col5" nameend="col5" align="center">327</entry><entry namest="col6" nameend="col6" align="center">90</entry><entry namest="col7" nameend="col7" align="center">82</entry></row><row><entry namest="col1" nameend="col1" align="center">Comparative Example 6</entry><entry namest="col2" nameend="col2" align="center">11</entry><entry namest="col3" nameend="col3" align="center">12</entry><entry namest="col4" nameend="col4" align="center">302</entry><entry namest="col5" nameend="col5" align="center">236</entry><entry namest="col6" nameend="col6" align="center">78</entry><entry namest="col7" nameend="col7" align="center">63</entry></row><row><entry namest="col1" nameend="col1" align="center">Comparative Example 7</entry><entry namest="col2" nameend="col2" align="center">13</entry><entry namest="col3" nameend="col3" align="center">15</entry><entry namest="col4" nameend="col4" align="center">359</entry><entry namest="col5" nameend="col5" align="center">259</entry><entry namest="col6" nameend="col6" align="center">72</entry><entry namest="col7" nameend="col7" align="center">58</entry></row><row rowsep="1"><entry namest="col1" nameend="col1" align="center">Comparative Example 8</entry><entry namest="col2" nameend="col2" align="center">12</entry><entry namest="col3" nameend="col3" align="center">13</entry><entry namest="col4" nameend="col4" align="center">405</entry><entry namest="col5" nameend="col5" align="center">196</entry><entry namest="col6" nameend="col6" align="center">48</entry><entry namest="col7" nameend="col7" align="center">39</entry></row></tbody></tgroup></table></tables>

0125As shown in Table 3, the cells using negative active materials according to Examples 24 to 27 exhibited corresponding initial charge capacity and initial discharge capacity those according to Comparative Examples 6 to 8, but had higher initial efficiency and cycle life characteristics.

< X-ray diffraction>

0126The structures of the negative active materials according to Examples 24 to 26 were measured by a powdery method at a rotating speed of 0.02°/1 second with an X-ray irradiation. The results are shown in FIG. 18. It is evident from FIG. 18 that the negative active materials all have similar X-ray diffraction patterns.

0127The lattice constant, a full width at half-maximum at a (003) and a (104) plane, and the intensity ratio of I(003)/(104) were measured on the negative active materials according to Examples 24 to 27, and Comparative Examples 5 to 7. The results are shown in Table 4. <tables id="tabl0004" num="0004"><table frame="all"><title>Table 4</title><tgroup cols="8" colsep="1" rowsep="1"><colspec colnum="1" colname="col1" colwidth="19.68mm" /><colspec colnum="2" colname="col2" colwidth="19.68mm" /><colspec colnum="3" colname="col3" colwidth="19.68mm" /><colspec colnum="4" colname="col4" colwidth="19.68mm" /><colspec colnum="5" colname="col5" colwidth="19.68mm" /><colspec colnum="6" colname="col6" colwidth="19.68mm" /><colspec colnum="7" colname="col7" colwidth="19.68mm" /><colspec colnum="8" colname="col8" colwidth="19.68mm" /><thead valign="top"><row><entry namest="col1" nameend="col1" rowsep="0" /><entry namest="col2" nameend="col3" align="center">Lattice constant</entry><entry namest="col4" nameend="col5" align="center">(003)</entry><entry namest="col6" nameend="col7" align="center">(104)</entry><entry namest="col8" nameend="col8" align="center">Intensity ratio</entry></row><row><entry namest="col1" nameend="col1" /><entry namest="col2" nameend="col2" align="center">A(□)</entry><entry namest="col3" nameend="col3" align="center">c(□)</entry><entry namest="col4" nameend="col4" align="center">2θ</entry><entry namest="col5" nameend="col5" align="center">Full width at half maximum</entry><entry namest="col6" nameend="col6" align="center">2θ</entry><entry namest="col7" nameend="col7" align="center">Full width at half maximum</entry><entry namest="col8" nameend="col8" align="center">I(003)/I(104)</entry></row></thead><tbody valign="top"><row><entry namest="col1" nameend="col1" align="center">Example 24</entry><entry namest="col2" nameend="col2" align="center">2.8556</entry><entry namest="col3" nameend="col3" align="center">14.695</entry><entry namest="col4" nameend="col4" align="char" char=".">18.11</entry><entry namest="col5" nameend="col5" align="char" char=".">0.169</entry><entry namest="col6" nameend="col6" align="char" char=".">44.12</entry><entry namest="col7" nameend="col7" align="char" char=".">0.228</entry><entry namest="col8" nameend="col8" align="char" char=".">0.801</entry></row><row><entry namest="col1" nameend="col1" align="center">Example 25</entry><entry namest="col2" nameend="col2" align="center">2.8583</entry><entry namest="col3" nameend="col3" align="center">14.688</entry><entry namest="col4" nameend="col4" align="char" char=".">18.11</entry><entry namest="col5" nameend="col5" align="char" char=".">0.159</entry><entry namest="col6" nameend="col6" align="char" char=".">44.08</entry><entry namest="col7" nameend="col7" align="char" char=".">0.24</entry><entry namest="col8" nameend="col8" align="char" char=".">0.959</entry></row><row><entry namest="col1" nameend="col1" align="center">Example 26</entry><entry namest="col2" nameend="col2" align="center">2.8631</entry><entry namest="col3" nameend="col3" align="center">14.703</entry><entry namest="col4" nameend="col4" align="char" char=".">18.09</entry><entry namest="col5" nameend="col5" align="char" char=".">0.16</entry><entry namest="col6" nameend="col6" align="char" char=".">44.1</entry><entry namest="col7" nameend="col7" align="char" char=".">0.22</entry><entry namest="col8" nameend="col8" align="char" char=".">1.052</entry></row><row><entry namest="col1" nameend="col1" align="center">Example 27</entry><entry namest="col2" nameend="col2" align="center">2.8697</entry><entry namest="col3" nameend="col3" align="center">14.711</entry><entry namest="col4" nameend="col4" align="char" char=".">18.1</entry><entry namest="col5" nameend="col5" align="char" char=".">0.169</entry><entry namest="col6" nameend="col6" align="char" char=".">44.15</entry><entry namest="col7" nameend="col7" align="char" char=".">0.219</entry><entry namest="col8" nameend="col8" align="char" char=".">1.16</entry></row><row><entry namest="col1" nameend="col1" align="center">Comparative Example 6</entry><entry namest="col2" nameend="col2" align="center">-</entry><entry namest="col3" nameend="col3" align="center">-</entry><entry namest="col4" nameend="col4" align="char" char=".">18.708</entry><entry namest="col5" nameend="col5" align="char" char=".">0.515</entry><entry namest="col6" nameend="col6" align="char" char=".">44.12</entry><entry namest="col7" nameend="col7" align="char" char=".">0.508</entry><entry namest="col8" nameend="col8" align="char" char=".">1.021</entry></row><row><entry namest="col1" nameend="col1" align="center">Comparative Example 7</entry><entry namest="col2" nameend="col2" align="center">-</entry><entry namest="col3" nameend="col3" align="center">-</entry><entry namest="col4" nameend="col4" align="char" char=".">18.71</entry><entry namest="col5" nameend="col5" align="char" char=".">0.427</entry><entry namest="col6" nameend="col6" align="char" char=".">44.09</entry><entry namest="col7" nameend="col7" align="char" char=".">0.51</entry><entry namest="col8" nameend="col8" align="char" char=".">0.05</entry></row><row rowsep="1"><entry namest="col1" nameend="col1" align="center">Comparative Example 8</entry><entry namest="col2" nameend="col2" align="center">-</entry><entry namest="col3" nameend="col3" align="center">-</entry><entry namest="col4" nameend="col4" align="char" char=".">18.71</entry><entry namest="col5" nameend="col5" align="char" char=".">0.398</entry><entry namest="col6" nameend="col6" align="char" char=".">44.1</entry><entry namest="col7" nameend="col7" align="char" char=".">0.525</entry><entry namest="col8" nameend="col8" align="char" char=".">0.1</entry></row></tbody></tgroup></table></tables>

0128It is shown from Table 4 that the negative active materials according to Examples 24 to 27 exhibited a full width at half-maximum at a (003) of 0.16 to 0.169, that at a (104) plane of 0.219 to 0.24, and intensity ratio of 0.801 to 1.16. In addition, the negative active materials according to Examples 24 to 27 exhibited lattice constant of a-axis of 2.8556A to 2.8697A, and lattice constants of c-axis of 14.695A to 14.711A. Whereas, the negative active materials according to Comparative Examples 6 to 8 exhibited a full width at half-maximum at a (003) plane of 0.398 to 0.515, that at a (104) plane of 0.51 to 0.508, and an intensity ratio of 0.05 to 1.021.

0129The vanadium-based oxide negative active material of the present invention provides a higher energy density per unit volume and improves safety such as with respect to fires or explosion.

0130Although a few embodiments of the present invention have been shown and described, it would be appreciated by those skilled in the art that changes may be made in these embodiments without departing from the principles and spirit of the invention, the scope of which is defined in the claims and their equivalents.