Coated glass substrate or glass ceramic substrate with resistant multi-functional surface properties, method for production thereof and use thereof

0001The present invention relates to a coated glass or glass ceramic substrate with stable, ie permanently present, multifunctional surface properties, a method for its production and its use.

Prior Art Background

0002Due to its special properties, in particular the excellent mechanical strength, optical properties and resistance to chemicals, glass is one of the most used materials worldwide and is also relatively inexpensive to produce. Glasses are used almost everywhere in construction, electronics, transportation, daily necessities, laboratory applications, scientific equipment and the like. For such diverse fields of application, the glass properties used are also very different. For example, building glass should have high mechanical strength. Glass used in medical or public areas should have antimicrobial properties. Window glass or glass in display devices should exhibit high transparency and high anti-reflective properties. For so-called touch screens, shop windows or exhibition areas made of glass, it is expedient if these have anti-fingerprint or so-called easy-to-clean properties. In many cases, it is not strictly necessary to develop new lenses to meet each of the requirements mentioned above. The desired functions are usually only properties of the glass surface, so that over time many surface treatments and coating processes have been developed to give new functions to the well-known glass products.

0003For example, numerous publications from the prior art have become known for antimicrobial (AM) glass surfaces:<ul id="ul_0001" list-style="none"><li id="ul_0001_0001">So describe the documents<de-docref CY="US" DNUM="20070172661" KI="A1">U.S. 2007/0172661 A1</de-docref>, <de-docref CY="JP" DNUM="2011133800" KI="A">JP 2011-133800A</de-docref> and the<de-docref CY="US" DNUM="20120034435" KI="A1">US 2012/0034435 A1</de-docref> various ways of imparting antimicrobial properties to the glass surface, for example through silver-alkaline ion exchange technology. According to this prior art, an ion exchange takes place between silver ions and the alkali ions in the glass, usually sodium ions, so that the silver ions diffuse into the glass surface and are present at a depth of several hundred nanometers to several tens of micrometers. Silver ions have a well-known cytotoxic effect on microorganisms, ranging from inhibition of their growth to cell death.</li></ul>

0004Antimicrobial glass surfaces can also be manufactured using other technologies. In principle, all types of known antimicrobial agents, in particular metals such as silver or copper, metal compounds such as silver salts, or nanoparticles of complex organic compounds can be deposited on glass surfaces as antimicrobial coatings. Antimicrobial glass surfaces can also be manufactured using thermal annealing processes.

0005For example, describes the<de-docref CY="US" DNUM="20080145625" KI="A1">U.S. 2008/0145625 A1</de-docref> describe a method for producing a glass substrate with a sol-gel layer, wherein a silver-containing antimicrobial sol-gel layer can be used.

0006the<de-docref CY="US" DNUM="20140017462" KI="A1">US 2014/0017462 A1</de-docref> describes a transparent and antimicrobial cover glass containing nanoparticles of Cu or Cu₂O on the surface of the glass, as well as methods of making these glass objects.

0007the<de-docref CY="US" DNUM="20090162695" KI="A1">U.S. 2009/0162695 A1</de-docref> describes a method for preparing a substrate having antimicrobial properties comprising depositing a mixed layer on a substrate by vacuum sputtering, the mixed layer comprising at least one antimicrobial agent and one binder.

0008the<de-docref CY="WO" DNUM="2007108514" KI="A1">WO 2007/108514 A1</de-docref> describes a glass plate with an antibacterial film.

0009the<de-docref CY="US" DNUM="6921546" KI="B2">U.S. 6,921,546 B2</de-docref> describes a glass or a glass-like substrate with an antimicrobial effect. The antimicrobial substrate is prepared by providing a metal ion precursor comprising at least one source of antimicrobial metal ions dissolved or otherwise dispersed in a support material; depositing the precursor on at least one surface of the substrate; drying the substrate at a temperature of about 20°C to about 105°C, devolatilizing the metal ion precursor, and heating the resulting substrate at a temperature of about 600°C to about 650°C for 2 to 5 minutes to exchange or otherwise introduce antimicrobial metal ions from the precursor to the glass or glass-like substrate.

0010the<de-docref CY="WO" DNUM="2007147842" KI="A2">WO 2007/147842 A2</de-docref> describes a method for producing a substrate with antimicrobial properties, wherein a metal layer comprising an inorganic antimicrobial agent is applied and the agent diffuses into at least one area of ​​the substrate which is subjected to a thermal treatment. Alternatively, the substrate can first be coated with an underlayer, with diffusion then occurring in the underlayer.

0011the<de-docref CY="US" DNUM="20120219792" KI="A1">US 2012/0219792 A1</de-docref> describes a glass substrate as a cover glass for a display, which not only has excellent strength and antibacterial properties, but also high transparency and high visible transmittance. The method includes chemically tempering the glass substrate in at least a KNO₃-containing molten salt, cleaning the glass substrate, forming a silver film on the surface of the cleaned glass substrate, subjecting the glass substrate having the silver film formed thereon to heat treatment to diffuse the silver ions from the glass substrate surface inside, and washing and removing of the silver left on the surface and not diffused from the glass substrate.

0012To add anti-reflective (AR) properties to a glass surface, an AR coating is the traditional choice. AR coating is a type of optical coating that is applied to the surface to reduce reflection, thereby improving light transmission at a specific wavelength range. IR, visible or UV frequencies are often selected.

0013The simplest interference AR coating consists of a single quarter-wave layer of transparent material whose index of refraction is the square root of the index of refraction of the substrate. This theoretically gives zero reflection at the center of the wavelength and reduces the reflection for wavelengths in a broad band around the center. For example, multilayer AR coatings consist of transparent thin film structures with alternating layers of opposite refractive indices. The layer thicknesses are chosen to produce destructive interference in the rays reflected from the interfaces and constructive interference in the corresponding transmitted rays. AR coatings are used in a wide variety of applications where light passes through an optical surface and low loss or low reflection is desired.

0014According to the interference mechanism in AR coatings, in principle any known coating can be used as an anti-reflection coating as long as its refractive index is suitable. The coating can be applied by liquid phase coating such as by printing technology, spray technology or a sol-gel process. The anti-reflective coating may also be applied by CVD coating such as PECVD, PICVD, low pressure CVD, or atmospheric pressure chemical vapor deposition. The antireflective coating can also be applied with a PVD coating, which can be, for example, sputtering, thermal evaporation, laser beam, electron beam or arc evaporation.

0015Numerous proposals for antireflective coatings have become known from the prior art:<ul id="ul_0002" list-style="none"><li id="ul_0002_0001">That's how she describes it<de-docref CY="US" DNUM="5847876" KI="A">U.S. 5,847,876</de-docref> an antireflective layer deposited on a glass substrate comprising a first layer of high refractive index, preferably of Al₂O₃, and a second layer of low refractive index, preferably of MgF₂, describes.</li></ul>

0016the<de-docref CY="EP" DNUM="2103965" KI="A1">EP 2 103 965 A1</de-docref> describes an antireflective layer applied to a glass or plastic substrate. The first high refractive index layer comprises an oxide of at least one of tin, gallium or cerium and indium oxide; the second layer is composed of a metal such as silver and palladium; the third layer corresponds to the first layer with a high refractive index and the fourth and uppermost layer has a low refractive index and consists of silicon dioxide, magnesium fluoride or potassium fluoride. The layers are each applied by sputtering.

0017the<de-docref CY="US" DNUM="20110052815" KI="A1">US 2011/0052815 A1</de-docref> describes a composition for producing an AR coating comprising a condensate obtainable by the condensation of silicon compounds of the general formula R_nSiX_4-n, wherein the X groups are the same or different and represent hydrolyzable groups or hydroxyl groups, the R groups are the same or different and represent non-hydrolyzable groups, and n is 0, 1, 2 or 3, the composition being at least one polymeric rheology control agent, and at least one solvent having a boiling point of at least 150°C. This document also describes the methods of making and using the present composition. In particular, the composition can be applied to the substrates by screen printing processes.

0018the<de-docref CY="CN" DNUM="102923969" KI="A">CN 102923969A</de-docref> describes a dual function in the form of anti-reflective and oleophobic coated glass and its manufacturing process. The film structure of the coated glass is as follows: a glass substrate, a base film, a buffer film and a surface film, the base film containing a silicon compound, the buffer film containing a silicon fluoride compound and the surface film containing a fluorosilicon compound. The films are mainly applied by spraying techniques.

0019the<de-docref CY="CN" DNUM="103013189" KI="A">CN 103013189A</de-docref> describes an antireflective glass coating liquid prepared by silica sols applied to the surface of the glass by a roll coating method, dip coating or spraying method, and annealing treatment is performed at temperatures not higher than 100°C.

0020the<de-docref CY="WO" DNUM="2008099061" KI="A1">WO 2008/099061 A1</de-docref> describes a method for coating an optical product, including an AR coating applied by chemical vapor deposition (CVD).

0021An Anti-Fingerprint (AF) surface, sometimes referred to as an Easy-To-Clean (ETC) or amphiphobic surface, ensures that dirt or contamination as a result of fingerprints is largely invisible and therefore the surface in use is too appears clean without cleaning. The AF surface must be resistant to water, salts, and grease derived from user's use, such as fingerprint residue, applied to the surface. The wetting properties of an AF surface must be both hydrophobic and oleophobic.

0022The majority of known AF coatings are essentially based on organofluorine compounds with a high water contact angle. In some cases, specially designed structures are created on the glass surface to further increase the contact angle with oil or water.

0023The following documents, for example, have become known from the prior art on AF surfaces of glass objects:<ul id="ul_0003" list-style="none"><li id="ul_0003_0001">That's how she describes it<de-docref CY="DE" DNUM="19848591" KI="A1">DE 198 48 591 A1</de-docref> to produce a protective layer of this type, the use of organofluorine compounds of the formula R_f-V in the form of a liquid system comprising the organofluorine compound in a carrier liquid, wherein R_f in the formula represents an aliphatic hydrocarbon residue which is partially or fully fluorinated and is straight-chain, branched or cyclic. The hydrocarbon radical can also be interrupted by one or more oxygen, nitrogen or sulfur atoms. V represents a polar or dipolar group selected from -COOR, -COR, -COF, -CH₂OR, -OCOR, -CONR₂, -CN, -CONH-NO₂, -CON=C(NH₂)₂, -CH=NOR, -NRCONR₂, -NO₂COR, NO_w, -SO₃R, -OSO₂R, -OH, -SH, =B, -OP(OH)₂, -OPO(OH)₂, - OP(ONH₄)₂, -OPO(ONH₄)₂, -CO-CH=CH₂, in which R in a group V can be the same or different and is hydrogen, a phenyl radical, a straight-chain or branched alkyl or alkyl ether radical having up to 12, preferably up to 8 carbon atoms, and is partially or fully fluorinated or chlorofluorinated, and w is 2 or 3 or represents -R_v-V-. In the formula -R_v-V-, V is the polar or dipolar group mentioned above and R_v represents a straight-chain or branched alkylene radical having up to 12, preferably up to 8, carbon atoms, which may be partially or fully fluorinated or chlorofluorinated.</li></ul>

0024the<de-docref CY="EP" DNUM="0844265" KI="A1">EP 0 844 265 A1</de-docref> describes a silicon-containing organic fluoropolymer for coating substrate surfaces, for example metal, glass and plastic materials, to provide a surface with sufficient and long-lasting antifouling properties, sufficient weather resistance, lubricity, non-stick properties, water repellency and resistance to oily soiling and fingerprints. Also disclosed is a treatment solution for a surface treatment process comprising a silicon-containing organic fluoropolymer, a fluorine-containing organic solvent, and a silane compound.

0025the<de-docref CY="US" DNUM="20100279068" KI="A1">US 2010/0279068 A1</de-docref> describes a method for providing hydrophobic and oleophobic glass surfaces. The process consists of heating a glass article to temperatures near the glass softening point and pressing a structured mold into the glass article to impart surface texture.

0026the<de-docref CY="US" DNUM="20100285272" KI="A1">US 2010/0285272 A1</de-docref> describes a glass substrate having at least one finished surface that is hydrophobic and oleophobic, has nonstick properties, is fingerprint resistant, has durability, and is transparent. The surface has at least one type of topological feature that, with a special geometry, prevents the decrease in contact angle and adhesion of water and oil drops. For example, for the application of an AF coating, the glass surface can be sand blown and the coating applied thereto by means of physical or chemical vapor deposition.

0027the<de-docref CY="US" DNUM="20090197048" KI="A1">U.S. 2009/0197048 A1</de-docref> describes an AF or Easy-To-Clean coating on a glass cover that is present as an outer coating with fluorine end groups such as perfluorocarbon residues or a perfluorocarbon-containing residue, making the glass cover hydrophobic and oleophobic and thereby preventing wetting of the glass surface with water and oils is minimized. Below the AF coating there may be an AR coating made of silica, fused silica, fluorine-doped silica, fluorine-doped fused silica, MgF₂, HfO₂, TiO₂, ZrO₂, Y₂O₃ or Gd₂O₃ is constructed. A pattern can also be created or a structure applied or introduced onto the glass surface before the AF coating, using an etching, lithography or particle coating process. The glass cover can be etched after ion exchange and before AF plating.

0028Tempering or toughening of glass is also a known surface treatment. The principle of thermal as well as chemical hardening or chemical toughening of glass is to form a compressive stress layer under the glass surface with a depth of about several 10 µm. This layer of compressive stress results in the tempered glass having increased strength. This is attributed to surface defects being compressed by the compressive stress forces. Otherwise, expansion of these defects could lead to a crack.

0029Chemical toughening or hardening is a long-established technology. Glass is typically immersed in a bath containing molten potassium nitrate at a temperature around 400°C. This causes the sodium ions in the glass surface to be replaced by potassium ions from the bath solution. The potassium ions are larger than the sodium ions, with the sodium ions migrating from the glass into the potassium nitrate melt and the potassium ions cramming into the voids left by the smaller sodium ions. This exchange of ions causes the surface of the glass to build up a stress and the interior of the glass tries to compensate for the stress. The surface compressive stress of a chemically toughened glass can reach more than 600 MPa.

0030There are numerous prior art documents describing chemical hardening or tempering:<ul id="ul_0004" list-style="none"><li id="ul_0004_0001">So reveals the<de-docref CY="US" DNUM="3778335" KI="A">US 3,778,335A</de-docref> Glass compositions of sodium aluminosilicate glass having a surface compressive stress layer that increases strength in a glass article, such as chemical toughening of glass.</li></ul>

0031the<de-docref CY="US" DNUM="20130202715" KI="A1">U.S. 2013/0202715 A1</de-docref> describes an aluminosilicate glass for a touch screen and the chemical toughening of the glass.

0032It has been shown in the prior art that for each property, such as antimicrobial, antireflective, antifingerprint property as well as increased glass strength, there are many different approaches to imparting this to a glass surface. However, in some cases the combination of several of these properties is desirable.

0033The cover glass of a touch screen, smartphone or tablet PC is a typical example where many functions should be integrated together. The devices are very thin and must have high mechanical strength, so tempered glass is necessary. At the same time, a surface with anti-reflective properties means that energy can be saved because the display module can work with lower brightness if the reflection at the glass-air interface is reduced. Furthermore, a very large amount of bacteria can be present on such screens, so an antimicrobial surface could protect the health of the user. After all, such screens are touched a lot every day, so the anti-fingerprint feature would also be very useful.

0034Display window glass or window glass used in exhibitions, such as picture glazing in museums, or in shops is another typical example. High mechanical strength is an obvious requirement for such glasses. The anti-reflective surface in these windows could lead to the best effects. Conventional glass reflects around 8% of the light that falls on it. The anti-reflective coating reduces reflection and thus allows an undistorted view. These panes are also frequently touched by visitors, especially children, for example when particularly beautiful objects are exhibited behind glass, for example in museums. Therefore, an antimicrobial surface could also be beneficial from a public health perspective and the provision of anti-fingerprint surfaces could reduce the frequency with which these discs need to be cleaned.

0035While there is a high demand and need for such combinations of properties, no such technology or article that integrates all of these properties onto the same glass surface currently exists. This is probably due to the fact that it is relatively difficult to provide the desired property profiles in combination, since each of these properties and functions has a number of implementation pathways and difficulties of its own. Furthermore, any features imparted to the glass surface must be durable enough to meet current industry quality standards, and the process should also be amenable to mass production.

0036In order to actually incorporate all of the properties of interest into the glass surface, there are therefore only two options: to develop a treatment process that imparts many properties in one step, or to develop a multi-step process that adds a function in each step, but with the one from a previous one The functions obtained in step 1 should still be present after the subsequent treatment. However, neither of these two possibilities can be implemented in a simple manner.

0037Some very limited functional combinations are already known from the prior art:<ul id="ul_0005" list-style="none"><li id="ul_0005_0001">That's how she describes it<de-docref CY="WO" DNUM="2012163946" KI="A1">WO 2012/163 946 A1</de-docref> a substrate element for coating with an easy-to-clean coating, comprising a substrate and an anti-reflective coating applied to the substrate, wherein the top layer of the anti-reflective coating is an adhesion promoter layer capable of having an easy-to -Clean coating to interact. It is also mentioned in this document that the anti-reflective coated glass substrate can be thermally hardened without appreciably affecting the coating, so that an AR function, AF function and the thermal hardening of glass are combined.</li></ul>

0038the<de-docref CY="DE" DNUM="102007009785" KI="B4">DE 10 2007 009 785 B4</de-docref> discloses a sol-gel coated glass article that is chemically toughened after coating to provide a combination of an AR coating and chemically toughened glass.

0039the<de-docref CY="CN" DNUM="102923966" KI="A">CN 102 923 966 A</de-docref> describes an antimicrobial and antireflective sol-gel coating. A metal compound with antimicrobial activity is doped to the coating, the metal being selected from the group consisting of silver, copper, cadmium, zinc, iron, tin, cobalt, cerium, antimony, selenium, chromium, magnesium and nickel. It is also mentioned that the thermal treatment of the coating can be carried out together in one step with the thermal annealing of the glass substrate, whereby antimicrobial and antireflective functions can be imparted to the glass and the glass is thermally strengthened.

0040the<de-docref CY="US" DNUM="20120034435" KI="A1">US 2012/0 034 435 A1</de-docref> describes a chemically strengthened glass with antimicrobial properties and a method for producing this glass. In particular, a chemically strengthened glass with antimicrobial properties is disclosed that has a low surface energy coating on the glass that does not impair the antimicrobial properties of the glass. Therefore, a combination of antimicrobial and anti-fingerprint features as well as chemically strengthened glass is provided.

0041Finally describes the<de-docref CY="US" DNUM="20140017462" KI="A1">US 2014/0017462 A1</de-docref> a transparent cover glass for applications such as touch screen devices that has antimicrobial properties. The antimicrobial glasses contain nanoparticles of Cu or Cu₂O on the surface of the glass. The antimicrobial glasses may further have a fluorosilane coating or other coating on the surface to provide an easy-to-clean surface. Therefore, antimicrobial and anti-fingerprint functions are imparted to the glass.

0042The following documents have become known as further prior art:<ul id="ul_0006" list-style="none"><li id="ul_0006_0001">the<de-docref CY="WO" DNUM="2014124348" KI="A1">WO 2014/124 348 A1</de-docref> describes antimicrobial glass articles that exhibit improved resistance to discoloration when exposed to harsh conditions. The antimicrobial glass articles comprise a glass substrate having a low concentration of non-bridging oxygen atoms, a compressive stress layer, and an antimicrobial silver-containing region, each extending inwardly from the surface of the glass substrate to a specified depth. The glass articles are therefore hardened, for example chemically toughened. An additional layer can be applied to the surface of the glass substrate after creating the compressive stress layer and the antimicrobial silver-containing region.</li></ul>

0043the<de-docref CY="US" DNUM="20140322547" KI="A1">US 2014/0 322 547 A1</de-docref> discloses a coated article comprising a glass or glass-ceramic substrate and an antimicrobial coating disposed on at least a portion of a surface of the glass or glass-ceramic substrate, the antimicrobial coating comprising an at least partially cured siloxane having organic side chains, wherein at least a portion of the organic side chains comprise protonated amine substituents or amine substituents having at least one hydrogen.

0044Furthermore, the<de-docref CY="EP" DNUM="1123906" KI="B1">EP 1 123 906 B1</de-docref> and the<de-docref CY="US" DNUM="6391462" KI="B1">U.S. 6,391,462 B1</de-docref> on low-e-coated glasses, in particular heat-reflecting layer systems for glass substrates, consisting of at least one anti-reflective layer consisting of one or more individual layers, at least one electrically highly conductive functional layer in the form of a very thin metallic silver layer and one applied at least to one side of the functional layer blocker layer. Glasses of this type are used in thermal insulation glazing that is not intended to transmit any NIR radiation.

0045The known prior art, in which multifunctional glass surfaces are described, does not take into account that the layers should be designed for chemical toughening. Furthermore, the anti-fingerprint (AF) coatings, if any, are generally not sufficiently durable, so that the desired improvement in properties is only temporary at best. Also, a film or layer(s) applied to the glass surface can block ion exchange if the film or layer is applied to the glass surface prior to chemical toughening. In the case of chemically toughened glass, subsequent heating of the glass can lead to a relaxation of the compressive stresses that have built up, especially if the temperature is above 200°C. Many coating technologies require heating during film formation or post-processing, which limits the coating of the tempered substrates. However, chemical toughening is an important feature in certain applications because thin glass, particularly used for touch screen cover glasses in consumer and home electronics, is the only way to increase the strength of the glass. This plays a special role, for example, in mobile phones, smartphones, tablet PCs, notebooks, televisions, ATM machines, ticket machines or control or monitoring displays in any devices or in a motor vehicle.

0046Thin glasses cannot be thermally toughened due to their small thickness. Furthermore, it has not yet been investigated which combinations with anti-fingerprint (AF) coatings are possible at all and whether an AF coating is compatible with other functions, such as an antimicrobial (AM) function, and whether these do not adversely affect each other or even block. Another important point is that the multiple functions imparted to the glass surface should have sufficient durability to be useful in practice.

0047The object of the present invention is therefore to overcome the disadvantages of the prior art and to provide a glass or glass-ceramic substrate which combines several of the properties or functionalities described, the properties being intended to be permanent. It should also be possible to provide additional properties or functionalities. Furthermore, a method is to be made available that enables the production of the glass or glass-ceramic substrate according to the invention in a simple manner.

Description of the invention

0048The object described above is achieved according to the invention by a coated glass or glass ceramic substrate with stable, multifunctional surface properties, comprising<ul id="ul_0007" list-style="dash"><li id="ul_0007_0001">- a combination of antimicrobial, antireflective and antifingerprint properties,<br />or</li><li id="ul_0007_0002">- a combination of antimicrobial and antireflective properties,</li></ul>wherein the glass or glass-ceramic substrate is coated with an anti-reflective coating and an ion exchange has been carried out through the anti-reflective coating present on the glass or glass-ceramic substrate, the ions exchanged being antimicrobially active metal ions and ions which cause chemical tempering of the glass or glass-ceramic substrate , represent;<br />and wherein the coated glass or glass ceramic substrate according to the standard JIS Z 2801 or ISO 22196 has an antimicrobial effectiveness of > 99% against E. coli and S. aureus.

0049The coated glass or glass ceramic substrates with stable, multifunctional surface properties according to the present invention are used in many ways, for example as cover glasses for any form of touch screen, for example in entertainment and household electronics, in particular in mobile phones, smartphones, tablet PCs, notebook PCs, televisions, ATM machines and the like. Other fields of application are in hospitals, museums, shops, in construction and transport, at ticket offices, control displays of devices or motor vehicles, advertising boards and the like, wherever antimicrobial properties, low light reflection, and possibly also easy cleaning and high mechanical strength are appropriate and are required.

0050To date, there is no such technology or a coated glass or glass-ceramic substrate that combines all of these properties or functions in one and the same glass surface. This is not easy to achieve, since each individual function is incorporated into the glass surface in a completely different way, and each of these functions and thus each of the manufacturing processes used has its own requirements.

0051There are several ways in which the various functions can be implemented in or on a glass or glass-ceramic surface. According to the invention, the antimicrobial function is achieved by ion exchange, with one or more antimicrobial metal ions in an antimicrobially effective amount, preferably selected from silver, copper, cadmium, zinc, iron, tin, cobalt, cerium, antimony -, selenium, chromium, magnesium and/or nickel ions are present. No coating, for example in the form of a single layer of metal salts with an antimicrobial effect, is applied to the glass or glass ceramic surface or to the glass or glass ceramic surface with an antireflective coating. The anti-reflective coating and also the anti-fingerprint function are preferably each applied to the glass or glass-ceramic substrate by providing a coating of one or more layers. The anti-fingerprint function or coating is usually the top layer on the glass or glass-ceramic substrate to perform its function. Chemical toughening, if desired, is performed by ion exchange with the glass or glass-ceramic substrate and anti-reflective coating thereon.

0052Surprisingly, it has now been found that the combinations of properties according to the invention do not adversely affect one another. In particular, it is unexpected that the antimicrobial properties can be obtained according to the invention without adversely affecting other functionalities of the coated glass or glass-ceramic surface. The antimicrobial functionality is also not adversely affected when an anti-fingerprint coating is applied to the coated glass or glass-ceramic surface. This is particularly the case when the AF coating is applied, preferably based on a liquid phase coating.

0053The invention further relates to a method for producing a coated glass or glass ceramic substrate with stable, multifunctional surface properties, comprising the following steps:<ul id="ul_0008" list-style="dash"><li id="ul_0008_0001">- Application of an anti-reflective coating to a glass or glass-ceramic substrate;</li><li id="ul_0008_0002">- performing one of the 2 following ion exchange processes on the anti-reflective coated glass or glass-ceramic substrate in a salt bath, whereby the ion exchange is performed through the anti-reflective coating present on the glass or glass-ceramic:<ul id="ul_0009" list-style="none"><li id="ul_0009_0001">(1) wherein the salt bath contains a mixture of potassium, rubidium and/or cesium salt with one or more metal salts with an antimicrobial effect, preferably selected from the group consisting of silver, copper, cadmium, zinc, iron, tin, cobalt, cerium, antimony, selenium, chromium, magnesium and/or nickel salts to impart antimicrobial properties to the glass or glass-ceramic substrate while chemically toughening it;<br />or</li><li id="ul_0009_0002">(2) wherein in a first step the first salt bath contains potassium, rubidium and/or cesium salt and in a second step the second salt bath contains a mixture of potassium, rubidium and/or cesium salt with one or more metal salts having an antimicrobial effect , preferably selected from the group consisting of silver, copper, cadmium, zinc, iron, tin, cobalt, cerium, antimony, selenium, chromium, magnesium and/or nickel salts, to impart antimicrobial properties to the glass or glass-ceramic substrate and to chemically toughen it.</li></ul></li></ul>

0054After the ion exchange, the method can have the further step:<ul id="ul_0010" list-style="dash"><li id="ul_0010_0001">- Application of an anti-fingerprint coating to the anti-reflective coated glass or glass-ceramic surface obtained.</li></ul>

0055In the present description, the term “antireflective” is also referred to as “AR”, the term “antimicrobial” is also referred to as “AM” and the term “antifingerprint” is also referred to as “AF”.

0056According to the invention, an antireflective (AR) coating is therefore first provided, which is preferably based on sol-gel technology and is suitable for ion exchange and thus chemical prestressing of the glass or glass-ceramic surface.

0057The top layer of the AR coating, in particular sol-gel AR coating, is preferably an adhesion promoter layer in order to be able to apply a permanent AF coating thereon. The glass or glass ceramic surface provided with the AR coating can then be antimicrobially equipped and chemically tempered in the same step according to the method according to the invention (ion exchange method (1)) or the chemical tempering and imparting of antimicrobial properties can be carried out in two consecutive steps (ion exchange method (2)). An anti-fingerprint coating can then optionally be applied, whereby the glass or glass-ceramic surface has anti-microbial (AM), anti-reflective (AR) and anti-fingerprint (AF) properties and can be chemically tempered at the same time.

0058The anti-fingerprint coating is only applied when it is appropriate for the particular application, for example in touchscreen applications.

0059Thus, according to the invention, glass or glass ceramic substrates with a durable, multifunctional surface and various combinations of properties are made available.

0060The individual properties or functions with which the glass or glass-ceramic substrate is equipped are explained in detail below:

Anti-reflective (AR) coating

0061The AR-coated substrate, which is produced in the first method step of the method according to the invention, comprises a carrier material made of glass or glass-ceramic and an anti-reflective coating.

0062According to one embodiment, the antireflective coating consists of one or at least two layers. One layer or the top layer of the at least two layers is preferably an adhesion promoter layer that can interact with an anti-fingerprint or easy-to-clean coating to be applied thereto, resulting in long-term stability of the anti-fingerprint coating. The adhesion promoter layer is a layer that provides improved adhesion between the underlying and overlying layers. This interacts with an applied anti-fingerprint coating in such a way that the long-term stability of the anti-fingerprint coating is increased due to a chemical, in particular a covalent bond, between the adhesion promoter layer of the substrate according to the invention and an anti-fingerprint coating applied thereto.

0063The function of the antireflective layer(s) is (are) more surprising by the ion exchange process carried out to obtain the antimicrobial properties (e.g. ion exchange of sodium ions for silver ions) and by the ion exchange process carried out for chemical tempering (e.g. ion exchange of sodium ions for potassium ions). way not adversely affected. Conversely, it was also found that the ion exchange for both the chemical toughening and the antimicrobial finish does not negatively affect either the antireflective coating or the function of any adhesion promoter layer that may be present.

0064The adhesion promoter layer, which preferably represents the top layer of the antireflective coating, preferably has a low refractive index.

0065When the antireflective coating is a single layer, preferably in the form of an adhesion promoter layer, the refractive index is preferably in the range of 1.22 to 1.44, more preferably in the range of 1.28 to 1.44. In the case of an AR coating which is composed of several layers and in which the top layer preferably represents an adhesion promoter layer, the refractive index range of the top layer is preferably in the range from 1.22 to 1.70, more preferably in the range from 1.28 to 1.60, most preferably in the range of 1.28 to 1.56.

0066The antireflective coating is preferably constructed in such a way that it represents an incomplete antireflective coating and an optically complete antireflective coating is present only after an AF coating has been applied. However, the optical contribution of the AF coating is usually small because it is very thin. In some cases, the AF coating can therefore also be optically inactive.

0067The antireflective coating can also be constructed in such a way that an incomplete antireflective coating is present and a complete antireflective coating is only present when an adhesion promoter layer and optionally an AF coating are present.

0068According to a further embodiment, the antireflective coating consists of three or more layers with alternating medium, high and low refractive indices. In this case, too, the uppermost layer is preferably an adhesion promoter layer and preferably has a low refractive index.

0069According to a further embodiment, the anti-reflective coating consists of two or more layers with alternating low and high refractive indices. In this case, too, the uppermost layer is preferably an adhesion promoter layer and preferably has a low refractive index.

0070At least one layer of the antireflective coating, particularly preferably the top or adhesion promoter layer, can be divided into sublayers, with one or more intermediate layers being present. The one or more intermediate layers then preferably have practically the same refractive index as the sublayers.

0071The adhesion promoter layer is particularly advantageous and unfolds its function to a particular extent when it is a mixed oxide. According to a preferred embodiment of the invention, the adhesion promoter layer is therefore a mixed oxide layer, more preferably a silicon mixed oxide layer, in particular a silicon oxide layer mixed with an oxide of at least one of the elements aluminum, tin, magnesium, phosphorus, cerium, zirconium, titanium, cesium, barium, strontium, Niobium, zinc, boron, hafnium and/or magnesium fluoride, preferably at least one oxide of the element aluminum.

0072For the purposes of this invention, silicon oxide is also understood to mean any silicon oxide between silicon mono- and silicon dioxide. For the purposes of the invention, silicon is understood to mean metal and semimetal. Mixed silicon oxide is a mixture of a silicon oxide with an oxide of at least one other element, which can be homogeneous or non-homogeneous, stoichiometric or non-stoichiometric.

0073The adhesion promoter layer preferably has a thickness greater than 1 nm, more preferably greater than 10 nm, particularly preferably greater than 20 nm.

0074In principle, any coating can be used as an antireflective coating, preferably including an adhesion promoter layer. An anti-reflective coating can be applied by printing technology, spray technology or vapor deposition technology, preferably a liquid phase coating, more preferably a sol-gel coating. The antireflective coating, preferably comprising or consisting of the adhesion promoter layer, can be applied by CVD technology, for example by means of PECVD, PICVD, low-pressure CVD or vapor deposition at atmospheric pressure (AVD, atomic vapor deposition; ALD atomic layer deposition). The antireflective coating can also be applied by PVD technology such as sputtering, thermal evaporation, laser beam or electron beam or arc evaporation. Alternatively, the adhesion promoter layer can be deposited by flame pyrolysis technology. The adhesion promoter layer and the other layers of the antireflective coating can alternatively be produced by combinations of different processes.

0075A sol-gel coating process to produce an anti-reflective coating is described below as an example:<ul id="ul_0011" list-style="none"><li id="ul_0011_0001">First, the surface to be coated is preferably cleaned. Cleaning glass or glass-ceramic substrates with liquids is a widespread process. A large number of cleaning liquids are used here, such as demineralized water or aqueous systems such as dilute alkali solutions (pH > 9) and acids, detergent solutions or non-aqueous solvents such as alcohols or ketones.</li></ul>

0076The glass or glass-ceramic substrate can be activated prior to coating. Activation methods include, for example, oxidation, corona discharge, flame treatment, UV treatment, plasma activation and/or mechanical methods such as roughening, sandblasting and also plasma treatments or other treatments of the substrate surface for activation with an acid and/or alkali.

0077A preferred sol-gel process uses the reaction of metal-organic starting materials in the dissolved state to form the layers. As a result of a controlled hydrolysis and condensation reaction of the organometallic starting materials, a metal oxide network structure is built up, ie a structure in which the metal atoms are connected to each other through oxygen atoms, simultaneously with elimination of the reaction products, such as alcohol and water. The hydrolysis reaction can be accelerated by adding catalysts.

0078The inorganic sol-gel material from which the sol-gel layers are produced is preferably a condensate, in particular comprising one or more hydrolyzable and condensable or condensed silanes and/or metal alkoxides, preferably of Si, Ti, Zr, Al, Nb, Hf, Ge, B, Sn and/or Zn. The groups crosslinked in the sol-gel process by inorganic hydrolysis and/or condensation can preferably be, for example, the following functional groups: TiR₄, ZrR₄, SiR₄, AlR₃, TiR₃(OR), TiR₂(OR)₂, ZrR₂(OR)₂, ZrR₃(OR), SiR₃(OR), SiR₂(OR)₂, TiR(OR)₃, ZrR(OR)₃, AlR₂(OR), AlR(OR)₂, Ti(OR)₄, Zr(OR)₄, Al(OR)₃, Si(OR)₄, SiR(OR)₃ and/or Si₂(OR)₆. The group OR can be, for example: alkoxy, such as preferably methoxy, ethoxy, n-propoxy, isopropoxy, butoxy, isopropoxyethoxy, methoxypropoxy, phenoxy, acetoxy, propionyloxy, ethanolamine, diethanolamine, triethanolamine, methacryloxypropyl, acrylate, methyl acrylate, acetylacetone, ethyl acetoacetate, ethoxy acetate , methoxy acetate, methoxy ethoxy acetate and/or methoxy ethoxy ethoxy acetate. The radical R can be, for example: Cl, Br, F, methyl, ethyl, phenyl, n-propyl, butyl, allyl, vinyl, glycidylpropyl, methacryloyloxypropyl, aminopropyl and/or fluorooctyl.

0079A common feature of all sol-gel reactions is that the molecularly disperse precursors undergo hydrolysis-condensation and polymerization reactions to form particulate disperse or colloidal systems. Depending on the conditions selected, the "primary particles" initially formed may continue to grow, may combine to form clusters, or may form more linear chains. The resulting entities give rise to microstructures that arise as a result of solvent removal. Ideally, the material may be fully thermally consolidated, but in reality a degree of porosity often remains, in some cases significant residual porosity. The chemical conditions during sol formation have a critical impact on the properties of sol-gel coatings, as described in P. Löbmann, "Sol-gel coatings", advanced training course 2003 "Surface finishing of glass", Metallurgical Association of the German Glass Industry.

0080The Si starting materials have been studied very closely up to now. In this regard, reference is made to C. Brinker, G. Scherer, "Sol-Gel-Science - The Physics and Chemistry of Sol-Gel Processing (Academic Press, Boston 1990), R. Iller, The Chemistry of Silica (Wiley, New York, 1979). The Si starting materials that are most commonly used are silicon alkoxides with the formula Si(OR)₄, which hydrolyze when water is added. Linear aggregates are preferentially formed under acidic conditions. Under basic conditions, the silicon alkoxides react to form more highly crosslinked "globular" particles. The sol-gel coatings contain pre-condensed particles and clusters.

0081In order to prepare a silicon oxide dipping solution for the glass or glass-ceramic substrate according to the present invention, the dipping solution is preferably prepared as follows:<ul id="ul_0012" list-style="none"><li id="ul_0012_0001">The starting silicon compound(s) is(are) dissolved in an organic solvent. The solvents used can be any organic solvent which dissolves the silicon starting compound(s) and is capable of dissolving a sufficient amount of water necessary for the hydrolysis of the silicon starting compounds. Suitable solvents are, for example, toluene, cyclohexane or acetone, but especially C_1-6-alcohols. Examples of these are methanol, ethanol, propanol, butanol, pentanol, hexanol or isomers thereof. It is advantageous to use lower alcohols, particularly methanol and ethanol, because they are easy to handle and have relatively low vapor pressures.</li></ul>

0082The silicon starting compound used is in particular a C_1-4-alkyl esters of a silicic acid, ie methyl, ethyl, propyl or butyl silicic acid. Methyl silicate is preferred.

0083The concentration of the silicon starting compound in the organic solvent is usually 0.05 to 1 mol/liter. For the hydrolysis of the silicon starting compound, in the example described, this solution is mixed with 0.05 to 12% by weight of water, preferably distilled water, and with 0.01 to 7% by weight of an acid catalyst. For this purpose, preferably organic acids are added, such as acetic acid, methoxyacetic acid, polyether carboxylic acids (e.g ethoxyethoxyacetic acid), citric acid, para-toluenesulfonic acid, lactic acid, methacrylic acid or acrylic acid or mineral acids such as HNO₃, HCl or H₂SO₄.

0084The pH of the solution should preferably be about. If the solution is not sufficiently acidic (pH > 3), there is a risk that the polycondensates/clusters will become too large.

0085In another embodiment, the solution can be prepared in two steps. The first step is as described above. This solution is then allowed to stand (ripen). The maturation time is achieved by diluting the matured solution with further solvent and/or by terminating the maturation by shifting the pH of the solution into the strongly acidic range. Shifting to a pH range of 1.5 to 2.5 is preferred. Shifting the pH to the strongly acidic range is preferably achieved by adding an inorganic acid, more preferably by adding hydrochloric acid, nitric acid, sulfuric acid or phosphoric acid, or any organic acid such as oxalic acid or the like. The strong acid is preferably added in an organic solvent, more preferably in the solvent in which the starting silicon compound is already dissolved. It is also possible here to add the acid in a sufficient quantity together with the solvent, more preferably again in alcoholic solution, so that the dilution of the starting solution and the termination of the aging process take place in one step.

0086The sol-gel coatings include pre-condensed particles and clusters that can have various structures. These structures can be determined using scattered light experiments. Using the process parameters, such as temperature, addition rate, stirring speed, but especially the pH value, it is possible for these structures to be created in the sols. It has been found that the use of small silicon oxide polycondensates/clusters with a diameter of ≦20 nm, preferably ≦4 nm, more preferably in the range 1 to 2 nm, makes it possible to produce dip layers that are more densely packed than conventional silicon oxide layers. This leads, for example, to an improvement in the chemical resistance of the layer.

0087A further improvement in the chemical resistance and the function as an adhesion promoter layer is achieved by adding small amounts of an admixture or several additives to the solution, which are distributed homogeneously in the solution and also in the later layer and form a mixed oxide. Suitable additives are hydrolyzable or dissociating inorganic salts, optionally containing water of crystallization, selected from the salts of tin, aluminum, phosphorus, boron, cerium, zirconium, titanium, cesium, barium, strontium, niobium and/or magnesium. Examples include SnCl₄, SnCl₂, AlCl₃, Al(NO₃)₃, Mg(NO₃)₂, MgCl₂, MgSO₄, TiCl₄, ZrCl₄, CeCl₃, Ce(NO₃)₃ and the same. These inorganic salts can be used both in aqueous form and with water of crystallization.

0088According to a further embodiment according to the invention, the additive or additives used can be selected from one or more metal alkoxides of tin, aluminum, phosphorus, boron, cerium, zirconium, titanium, cesium, barium, strontium, niobium and/or magnesium, preferably titanium, zirconium, aluminum or niobium. Also suitable are phosphoric acid esters such as methyl or ethyl phosphorus ester, phosphorus halides such as chlorides and bromides, boric acid esters such as ethyl, methyl, butyl or propyl ester, boric acid anhydride, BBr₃, BCL₃, magnesium methylate or ethylate and the like.

0089According to a further embodiment according to the invention, the additives can also be selected as inorganic fluorides, eg MgF₂, CaF₂ etc., which are preferably in the form of nanoparticles &lt;200 nm.

0090The additives are particularly preferably used when the antireflective coating or parts of the antireflective coating are present as a sol-gel coating in the form of an adhesion promoter layer.

0091These one or more additives are used, for example, in a concentration of about 0.5 to 20% by weight, calculated as oxide (or fluoride), based on the silicon content of the solution, calculated as SiO₂, admitted. The additive or additives can also be used in combination.

0092If the immersion solution is to be stored or otherwise used over a longer period of time, it can be advantageous if this solution is stabilized by adding one or more complexing agents. These complexing agents should be soluble in the dipping solution and can match the solvent of the dipping solution.

0093Complexing agents that can be used include, for example, ethyl acetoacetate, 2,3-pentanedione (acetylacetone), 3,5-heptanedione, 4,6-nonanedione, 3-methyl-2,4-pentanedione, 2-methylacetylacetone, triethanolamine, diethylamine, ethanolamine, 1,3-propanediol, 1,5-pentanediol, carboxylic acids such as acetic acid, propionic acid, ethoxyacetic acid, methoxyacetic acid, polyether carboxylic acids (eg, ethoxyethoxyacetic acid), citric acid, lactic acid, methylacrylic acid and acrylic acid, and the like.

0094The molar ratio of complexing agent to semimetal oxide precursor and/or metal oxide precursor may range from 0.1 to 5.

0095In a preferred embodiment, the glass or glass-ceramic material is fed during sol-gel coating at a target speed of about 50-1500 mm/min, preferably 200-1000 mm/min, more preferably about 300-1000 mm/min. pulled out of the solution, the moisture content of the ambient air being between about 4 g/m³ and about 12 g/m³, more preferably at about 8 g/m³ lies.

0096The dip-coated layer can be dried after application to obtain higher mechanical strength. The drying can be carried out in a very wide temperature range, for example in a high-temperature oven. Typically, drying times are a few minutes at temperatures in the range of 100 - 200°C.

0097The formation of the applied layer takes place in a high-temperature step, during which the organic components of the gel are preferably burned out. Finally, in order to form the mixed oxide layer, preferably silicon mixed oxide layer, which can act as an adhesion promoter layer, for example, this is below the softening point of the glass or glass-ceramic material, preferably at temperatures of less than 550° C., more preferably between 350 and 500° C., even more preferably between 400 and 500°C. It is also possible to use temperatures higher than 550°C, but the duration should then preferably be selected to be short so that the glass substrate (depending on the thickness of the glass substrate) does not deform. However, such temperatures do not generally lead to a further improvement in the adhesive strength of the layer.

Antimicrobial (AM) property and chemical toughening by ion exchange

0098Antimicrobial properties are imparted to the coated glass or glass-ceramic surface using an ion exchange process. For this purpose, one or more antimicrobial salts, in particular one or more antimicrobial metal salts, are introduced into the substrate and probably also the layer(s) present thereon in an antimicrobially effective amount, the metal preferably being selected from the group consisting of of silver, copper, cadmium, zinc, iron, tin, cobalt, cerium, antimony, selenium, chromium, magnesium and/or nickel. Particularly preferred are silver salts, especially silver nitrate, silver chloride, silver fluoride, silver bromide, silver oxide, silver sulfate, silver carbonate, silver cyanide, silver tetrafluoroborate, silver sulfide, silver acetate, silver lactate, silver benzoate, silver cyclohexanebutyrate, silver diethyldithiocarbamate, silver trifluoromethanesulfonate, and mixtures thereof. AgCl-/AgNO are particularly preferred₃- and/or ZnCl- and/or ZnNO₃-containing mixtures. According to the invention, the antimicrobial properties are imparted by an ion exchange in a salt or melt bath, the ion exchange being carried out with the glass or the glass ceramic and the antireflective coating present thereon. Ion exchange to provide the glass or glass-ceramic substrate with antimicrobial properties is performed like ion exchange for chemical toughening.

0099The glass or glass-ceramic substrate of the present invention is also chemically toughened so as to have higher mechanical strength and scratch resistance than without chemical toughening. The chemical toughening in the context of the present invention is also carried out by an ion exchange, as is known in the prior art, but according to the invention the ion exchange is carried out through the antireflective coating present on the glass or the glass-ceramic. The ion exchange of smaller alkali metal ions, e.g Sodium and/or lithium ions, from the glass by larger alkali metal ions, such as potassium, rubidium and/or cesium ions, leads to a compressive stress layer that prevents mechanical damage, such as scratching or abrasion, and thus the glass or glass-ceramic more resistant to damage.

0100The chemical toughening is carried out, for example, by immersion in a potassium-containing, preferably potassium nitrate-containing, molten salt. There is also the possibility of using an aqueous potassium silicate solution, paste or dispersion, as for example in<de-docref CY="WO" DNUM="2011120656" KI="A">WO 2011/120656</de-docref> described in detail. Chemical toughening can be characterized by depth of ion exchanged layer (DoL) and compressive strength (CS).

0101If the glass or glass-ceramic surface has antimicrobial properties and is to be chemically toughened at the same time, the glass or glass-ceramic substrate is treated, for example, in two consecutive steps, i.e. the glass or glass-ceramic can be chemically toughened in a first step and antimicrobially finished in a second step .

0102In the context of the present invention, however, it has proven to be particularly advantageous if both treatments are carried out simultaneously in one step (process variant (1)) or if two steps are carried out, with the first step being chemically prestressed and the second step being antimicrobially finished . In the second step, a mixture of antimicrobial compound(s) and alkali metal salt(s) suitable for chemical tempering is preferably used in a salt bath (process variant (2)). The ion exchange in the first step then takes place, for example, in a potassium nitrate salt bath and the second step takes place, for example, with a mixture of potassium salt(s) and silver salt(s), for example a mixture of KNO₃ and AgNO₃.

0103If only one step is carried out or the first ion exchange step is carried out for chemical toughening, the ion exchange process is preferably carried out in a salt bath at a temperature between 350 and 500°C for a period of preferably 0.5 to 48 hours. If aluminum silicate and boroaluminosilicate glasses or glass ceramics based thereon are used as substrates, the temperature is preferably 400 to 450° C. and the duration between 1 and 8 hours. If soda-lime glass or a glass ceramic based thereon is used, the temperatures are preferably 390 to 480° C. for a period of between 2 and 24 hours. Borosilicate glasses or glass ceramics based thereon are treated, for example, at temperatures between 440 and 500° C. for a period of between 4 and 48 hours.

0104If the chemical prestressing and antimicrobial finishing is carried out in a single ion exchange step (variant (1)), the concentration of the one or more antimicrobial metal salts in the salt bath, for example in the form of one or more silver salts, is preferably 0.01 to 2% by weight. %, more preferably 0.01 to 0.5% by weight. When the antimicrobial ion exchange step is the second step (variant (2)) performed after the chemical toughening, the ion exchange process is performed at a temperature between 400 and 500°C for a duration between 0.25 and 2 hours. The concentration of the one or more antimicrobial metal salts in the second salt bath, for example in the form of one or more silver salts, is also preferably 0.01 to 2% by weight, more preferably 0.01 to 0.5% by weight.

0105It was surprisingly found that after carrying out the ion exchange process, whether in one or two steps, the desired antimicrobial properties and at the same time corresponding properties of a chemically toughened glass or glass-ceramic substrate are obtained. For example, it was found for aluminosilicate and boroaluminosilicate glasses and the glass ceramics based on them that the compressive stress of the surface CS (compressive stress) is ≥ 600 MPa and the depth of the compressive stress layer DoL (depth of ion exchanged layer) is ≥ 20 µm. For soda-lime glasses and the glass ceramics based thereon, it was found that the compressive stress of the surface CS is ≧100 MPa, preferably ≧200 MPa, more preferably ≧300 MPa, and the depth of the surface compressive stress DoL is ≧5 μm. These values ​​are in the same range as for glasses or glass-ceramics that have only been chemically toughened by ion exchange without providing them with antimicrobial properties at the same time.

0106Furthermore, it was found that the glass or glass ceramic substrates produced with the method according to the invention have an antimicrobial effectiveness >99% against E. coli and S.aureus, more preferably >99.9%, particularly preferably >99.99%. The method for measuring the antimicrobial effectiveness is based on the standard JIS Z 2801 or ISO 22196. The values ​​for antimicrobial effectiveness are also in the same range as for glasses or glass ceramics that are only antimicrobially equipped.

0107The glass and/or glass-ceramic substrates according to the present invention also have an antimicrobial effect against other bacteria such as K.pneumoniae and P.aeruginosa. It is known that silver ion, for example, has an antimicrobial effect against about 650 species of bacteria and other microorganisms including viruses, bacteria, fungi, algae and the like, so the antimicrobial substrates of the present invention can fully exhibit these properties.

Anti-fingerprint (AF) coating

0108According to one embodiment of the present invention, the ion-exchanged, anti-reflectively coated glass and/or glass-ceramic substrate can be provided with an AF coating, which is also referred to as an easy-to-clean coating or an amphiphobic coating.

0109An AF coating exhibits hydrophobic and oleophobic, ie, amphiphobic, properties such that wetting of the surface by water and oils is minimized. The wetting characteristics of a surface with an AF coating must therefore be such that the surface is both hydrophobic, i.e. the contact angle between surface and water is preferably greater than 90°, and oleophobic, i.e. the contact angle between surface and oil is preferably greater than 50 °.

0110The AF coating can be a surface layer comprising a silane containing alkyl and/or fluoroalkyl groups such as 3,3,3-trifluoropropyltrimethoxysilane or pentyltriethoxysilane.

0111The AF coating can also be a fluorine-based surface layer based on compounds with hydrocarbon groups, where the CH bonds have been partially or preferably substantially all replaced by CF bonds. Such compounds are preferably perfluorocarbons having, for example, the formula (R_f)_nSiX_4-n have, where R_f a c_1- to C₂₂-alkylperfluorohydrocarbon or -alkylperfluoropolyether, preferably C_1- to C₁₀-alkylperfluorohydrocarbon or -alkylperfluoropolyether, n is an integer from 1 to 3, X is a hydrolysable group such as halogen or an alkoxy group -OR, in which R represents, for example, a linear or branched hydrocarbon having 1 to 6 carbon atoms. In this case, the hydrolyzable group X can, for example, react with a terminal OH group of the coating of the glass substrate and thus bind to it by forming a covalent bond. Perfluorocarbons are advantageously used to reduce the surface energy of the surface due to the low polarity of the terminal fluorine surface bonds.

0112The AF coating may also be derived, for example, from a monolayer of fluorine-terminated molecular chain, a fluoropolymer coating, or from previously fluorine-terminated or treated silica soot particles.

0113AF coatings are for example in the<de-docref CY="DE" DNUM="19848591">DE19848591</de-docref>, <de-docref CY="EP" DNUM="0844265" KI="A">EP 0 844 265</de-docref>, <de-docref CY="US" DNUM="20100279068" KI="A">US2010/0279068</de-docref>, <de-docref CY="US" DNUM="20100285272" KI="A">US2010/0285272</de-docref>, <de-docref CY="US" DNUM="2009/0197048">U.S. 2009/0197048</de-docref> and the<de-docref CY="WO" DNUM="2012163947" KI="A1">WO 2012/163947 A1</de-docref> described, the disclosure of which is incorporated herein by reference into the present invention. Known AF coatings are, for example, products based on perfluoropolyether under the name “Fluorolink® PFPE”, such as “Fluorolink® S10”, from Solvay Solexis or also “Optool^TM DSX” or “Optool^TM AES4-E” from Daikin Industries LTD, “Hymocer® EKG 6000N” from ETC Products GmbH or fluorosilane under the designation “FSD”, such as “FSD 2500” or “FSD 4500” from Cytonix LLC or Easy Clean Coating” ECC" products such as "ECC 3000" or "ECC 4000" from 3M Deutschland GmbH. These are liquid applied layers. AF coatings, for example as nano-layer systems, which are applied by means of physical vapor deposition, are offered by Cotec GmbH under the name “DURALON UltraTec”, for example.

0114The coating may be applied to the surface by dipping, vapor coating, spraying, roller or knife application, thermal vacuum deposition or sputtering, preferably by liquid phase methods such as spraying, dip coating, printing, roller coating, spin coating or other suitable methods procedures are applied. Dipping or spraying are particularly preferred. After the coating has been applied, it is preferably cured at a suitable temperature for a suitable length of time.

0115The water contact angle of the AF coating is preferably >90°, more preferably >100°, particularly preferably >110°.

0116In the context of the present invention, it was found that the coating applied to the glass or glass-ceramic substrate in the form of the AF coating has no adverse effect on the release of the antimicrobial ions from the glass or glass-ceramic surface and therefore has no adverse effect on the antimicrobial Effectiveness of the resulting antimicrobial glass and / or glass ceramic surface affects.

0117According to the invention, it was also found that the application of an AF layer to an AR coating regularly leads to an improvement in the abrasion resistance of the entire coating system.

antiglare property

0118In addition or as an alternative to one of the properties described, the glass or glass ceramic substrate according to the invention can also have anti-glare properties.

0119An antiglare surface describes a surface that can physically convert light radiation into a diffuse reflection instead of a specular reflection. An anti-glare surface is useful in situations where high transmission through a surface is not as important, but rather low reflectivity is required. The anti-glare function can be present within the scope of the present invention, for example combined with the AM, AR, AF properties and, if appropriate, chemical toughening in a glass or glass-ceramic surface.

0120There are several ways to make a glass surface matt: e.g. B. the embossing of structures during hot forming or etching of the glass surface by acid. The surface can subsequently be coated with one or more AR layers. Small particles can also be included in an AR coating, other than the top layer of the AR coating, or a texture or pattern can be incorporated or applied to the surface to enhance surface light diffusion. Furthermore, the properties described can also already be combined with one another in an anti-glare glass substrate, such as Xensation Cover AG, sold by Schott AG, with multifunctionalities such as AM, AR, optional AF and, if necessary, chemical prestressing.

0121An anti-glare coating can therefore be produced, for example, by embossing a sol-gel layer or adding nanoparticles to the sol-gel solution, so that the roughness is increased and is preferably in the range from 5 nm to 5 μm.

0122An anti-glare surface, which is obtained for example in the form of a matt and/or etched and/or structured surface, converts the specular reflection into a hazy reflection. This so-called scattering of the reflected light blurs reflected images so that different shapes and reflected light sources do not distract from what is shown behind the glass or glass-ceramic. The scattering of the light does not reduce the overall reflection or the absorption of the incident light on the glass or glass-ceramic surface or in the glass or glass-ceramic substrate. Rather, the light is not only directed, but scattered in all spatial directions. The total amount of light remains the same.

0123Etched surfaces have the following advantages: The diffuse scattering of bright reflected light allows for better viewing of transmitted images and text. Textured surfaces are also sometimes used as an alternative to anti-reflective coatings. The shine of directly reflected light sources is reduced. Due to its structure, the surface shows reduced coefficients of static friction in contact with a large number of substances and surfaces. The associated better haptics make them particularly attractive for use in touch display applications. The reduced, effective contact area between such a structured surface and other touching surfaces leads to a purely mechanically caused "anti-fingerprint" functionality. This, too, often motivates use in touch display applications. However, dirt that has found its way into the structures of the surface is more difficult to remove than a correspondingly smooth surface.

0124In one embodiment of the present invention, the antireflective layer can be used, for example, in combination with an antiglare layer. The anti-reflective layer and an AF layer applied thereto inherit the roughness of the anti-glare layer while maintaining the AF and anti-reflective properties.

The glass or glass-ceramic substrate

0125Any glass or glass-ceramic composition in which the desired ion exchange, e.g. sodium to potassium ion for chemical toughening and e.g. sodium to silver ion for antimicrobial imparting to the glass or glass-ceramic, can be carried out can be used in accordance with the present invention. The glass or glass-ceramic material that is provided with the AR coating is any ion-exchangeable glass or ion-exchangeable glass-ceramic. The glass is preferably selected from: silicate glass, phosphate glass, borosilicate glass, aluminosilicate glass, boroaluminosilicate glass, tin phosphate glass, boron phosphate glass, titanate glass, barium glass, preferably silicate glass containing alkali metals and even more preferably silicate glass containing sodium.

0126The glass is, for example, an alkali aluminosilicate glass with the following composition:<de-tables num="0000"><table frame="none"><tgroup cols="2" colsep="0" rowsep="0"><colspec colname="col1" colsep="0" rowsep="0" colnum="1" colwidth="136.28583999999998mm" /><colspec colname="col2" colsep="0" rowsep="0" colnum="2" colwidth="33.71416mm" /><thead><row rowsep="0"><entry align="left" colname="col1" valign="top" colsep="0" rowsep="0"><b>composition</b></entry><entry align="left" colname="col2" valign="top" colsep="0" rowsep="0"><b>wt%</b></entry></row></thead><tbody><row rowsep="0"><entry align="left" colname="col1" valign="top" colsep="0" rowsep="0">SiO₂</entry><entry align="left" colname="col2" valign="top" colsep="0" rowsep="0">40 - 75</entry></row><row rowsep="0"><entry align="left" colname="col1" valign="top" colsep="0" rowsep="0">Al₂O₃</entry><entry align="left" colname="col2" valign="top" colsep="0" rowsep="0">10 - 30</entry></row><row rowsep="0"><entry align="left" colname="col1" valign="top" colsep="0" rowsep="0">B₂O₃</entry><entry align="left" colname="col2" valign="top" colsep="0" rowsep="0">0 - 20</entry></row><row rowsep="0"><entry align="left" colname="col1" valign="top" colsep="0" rowsep="0">Sum of Li₂O + Na₂O+K₂O</entry><entry align="left" colname="col2" valign="top" colsep="0" rowsep="0">4 - 30</entry></row><row rowsep="0"><entry align="left" colname="col1" valign="top" colsep="0" rowsep="0">Sum of MgO + CaO + SrO + BaO + ZnO</entry><entry align="left" colname="col2" valign="top" colsep="0" rowsep="0">0 - 15</entry></row><row rowsep="0"><entry align="left" colname="col1" valign="top" colsep="0" rowsep="0">Sum of TiO₂ + ZrO₂</entry><entry align="left" colname="col2" valign="top" colsep="0" rowsep="0">0 - 15</entry></row><row rowsep="0"><entry align="left" colname="col1" valign="top" colsep="0" rowsep="0">P₂O₅</entry><entry align="left" colname="col2" valign="top" colsep="0" rowsep="0">0 - 10</entry></row></tbody></tgroup></table></de-tables>

0127The glass material is, for example, a borosilicate glass with the following composition:<de-tables num="0000"><table frame="none"><tgroup cols="2" colsep="0" rowsep="0"><colspec colname="col1" colsep="0" rowsep="0" colnum="1" colwidth="137.77238608695652mm" /><colspec colname="col2" colsep="0" rowsep="0" colnum="2" colwidth="32.22761391304348mm" /><thead><row rowsep="0"><entry align="left" colname="col1" valign="top" colsep="0" rowsep="0"><b>composition</b></entry><entry align="left" colname="col2" valign="top" colsep="0" rowsep="0"><b>wt%</b></entry></row></thead><tbody><row rowsep="0"><entry align="left" colname="col1" valign="top" colsep="0" rowsep="0">SiO₂</entry><entry align="left" colname="col2" valign="top" colsep="0" rowsep="0">60 - 85</entry></row><row rowsep="0"><entry align="left" colname="col1" valign="top" colsep="0" rowsep="0">Al₂O₃</entry><entry align="left" colname="col2" valign="top" colsep="0" rowsep="0">1 - 10</entry></row><row rowsep="0"><entry align="left" colname="col1" valign="top" colsep="0" rowsep="0">B₂O₃</entry><entry align="left" colname="col2" valign="top" colsep="0" rowsep="0">5 - 20</entry></row><row rowsep="0"><entry align="left" colname="col1" valign="top" colsep="0" rowsep="0">Sum of Li₂O + Na₂O+K₂O</entry><entry align="left" colname="col2" valign="top" colsep="0" rowsep="0">2 - 16</entry></row><row rowsep="0"><entry align="left" colname="col1" valign="top" colsep="0" rowsep="0">Sum of MgO + CaO + SrO + BaO + ZnO</entry><entry align="left" colname="col2" valign="top" colsep="0" rowsep="0">0 - 15</entry></row><row rowsep="0"><entry align="left" colname="col1" valign="top" colsep="0" rowsep="0">Sum of TiO₂ + ZrO₂</entry><entry align="left" colname="col2" valign="top" colsep="0" rowsep="0">0 - 5</entry></row><row rowsep="0"><entry align="left" colname="col1" valign="top" colsep="0" rowsep="0">P₂O₅</entry><entry align="left" colname="col2" valign="top" colsep="0" rowsep="0">0 - 2</entry></row></tbody></tgroup></table></de-tables>

0128The glass material is, for example, a soda-lime glass with the following composition:<de-tables num="0000"><table frame="none"><tgroup cols="2" colsep="0" rowsep="0"><colspec colname="col1" colsep="0" rowsep="0" colnum="1" colwidth="139.25893217391302mm" /><colspec colname="col2" colsep="0" rowsep="0" colnum="2" colwidth="30.741067826086955mm" /><thead><row rowsep="0"><entry align="left" colname="col1" valign="top" colsep="0" rowsep="0"><b>composition</b></entry><entry align="left" colname="col2" valign="top" colsep="0" rowsep="0"><b>wt%</b></entry></row></thead><tbody><row rowsep="0"><entry align="left" colname="col1" valign="top" colsep="0" rowsep="0">SiO₂</entry><entry align="left" colname="col2" valign="top" colsep="0" rowsep="0">40 - 80</entry></row><row rowsep="0"><entry align="left" colname="col1" valign="top" colsep="0" rowsep="0">Al₂O₃</entry><entry align="left" colname="col2" valign="top" colsep="0" rowsep="0">0 - 6</entry></row><row rowsep="0"><entry align="left" colname="col1" valign="top" colsep="0" rowsep="0">B₂O₃</entry><entry align="left" colname="col2" valign="top" colsep="0" rowsep="0">0 - 5</entry></row><row rowsep="0"><entry align="left" colname="col1" valign="top" colsep="0" rowsep="0">Sum of Li₂O + Na₂O+K₂O</entry><entry align="left" colname="col2" valign="top" colsep="0" rowsep="0">5 - 30</entry></row><row rowsep="0"><entry align="left" colname="col1" valign="top" colsep="0" rowsep="0">Sum of MgO + CaO + SrO + BaO + ZnO</entry><entry align="left" colname="col2" valign="top" colsep="0" rowsep="0">5 - 30</entry></row><row rowsep="0"><entry align="left" colname="col1" valign="top" colsep="0" rowsep="0">Sum of TiO₂ + ZrO₂</entry><entry align="left" colname="col2" valign="top" colsep="0" rowsep="0">0 - 7</entry></row><row rowsep="0"><entry align="left" colname="col1" valign="top" colsep="0" rowsep="0">P₂O₅</entry><entry align="left" colname="col2" valign="top" colsep="0" rowsep="0">0 - 2</entry></row></tbody></tgroup></table></de-tables>

0129The glass material is, for example, a low-alkali aluminosilicate glass having the following composition:<de-tables num="0000"><table frame="none"><tgroup cols="2" colsep="0" rowsep="0"><colspec colname="col1" colsep="0" rowsep="0" colnum="1" colwidth="137.77238608695652mm" /><colspec colname="col2" colsep="0" rowsep="0" colnum="2" colwidth="32.22761391304348mm" /><thead><row rowsep="0"><entry align="left" colname="col1" valign="top" colsep="0" rowsep="0"><b>composition</b></entry><entry align="left" colname="col2" valign="top" colsep="0" rowsep="0"><b>wt%</b></entry></row></thead><tbody><row rowsep="0"><entry align="left" colname="col1" valign="top" colsep="0" rowsep="0">SiO₂</entry><entry align="left" colname="col2" valign="top" colsep="0" rowsep="0">50 - 75</entry></row><row rowsep="0"><entry align="left" colname="col1" valign="top" colsep="0" rowsep="0">Al₂O₃</entry><entry align="left" colname="col2" valign="top" colsep="0" rowsep="0">7 - 25</entry></row><row rowsep="0"><entry align="left" colname="col1" valign="top" colsep="0" rowsep="0">B₂O₃</entry><entry align="left" colname="col2" valign="top" colsep="0" rowsep="0">0 -20</entry></row><row rowsep="0"><entry align="left" colname="col1" valign="top" colsep="0" rowsep="0">Sum of Li₂O + Na₂O+K₂O</entry><entry align="left" colname="col2" valign="top" colsep="0" rowsep="0">1 - 4</entry></row><row rowsep="0"><entry align="left" colname="col1" valign="top" colsep="0" rowsep="0">Sum of MgO + CaO + SrO + BaO + ZnO</entry><entry align="left" colname="col2" valign="top" colsep="0" rowsep="0">5 - 25</entry></row><row rowsep="0"><entry align="left" colname="col1" valign="top" colsep="0" rowsep="0">Sum of TiO₂ + ZrO₂</entry><entry align="left" colname="col2" valign="top" colsep="0" rowsep="0">0 - 10</entry></row><row rowsep="0"><entry align="left" colname="col1" valign="top" colsep="0" rowsep="0">P₂O₅</entry><entry align="left" colname="col2" valign="top" colsep="0" rowsep="0">0 - 5</entry></row></tbody></tgroup></table></de-tables>

0130The glass material is preferably a lead glass with the following composition:<de-tables num="0000"><table frame="none"><tgroup cols="2" colsep="0" rowsep="0"><colspec colname="col1" colsep="0" rowsep="0" colnum="1" colwidth="112.50110260869565mm" /><colspec colname="col2" colsep="0" rowsep="0" colnum="2" colwidth="57.49889739130435mm" /><thead><row rowsep="0"><entry align="left" colname="col1" valign="top" colsep="0" rowsep="0"><b>composition</b></entry><entry align="left" colname="col2" valign="top" colsep="0" rowsep="0"><b>wt%</b></entry></row></thead><tbody><row rowsep="0"><entry align="left" colname="col1" valign="top" colsep="0" rowsep="0">PbO</entry><entry align="left" colname="col2" valign="top" colsep="0" rowsep="0">20 - 80</entry></row><row rowsep="0"><entry align="left" colname="col1" valign="top" colsep="0" rowsep="0">SiO₂</entry><entry align="left" colname="col2" valign="top" colsep="0" rowsep="0">20 - 60</entry></row><row rowsep="0"><entry align="left" colname="col1" valign="top" colsep="0" rowsep="0">K₂O</entry><entry align="left" colname="col2" valign="top" colsep="0" rowsep="0">0 - 10</entry></row><row rowsep="0"><entry align="left" colname="col1" valign="top" colsep="0" rowsep="0">N / A₂O</entry><entry align="left" colname="col2" valign="top" colsep="0" rowsep="0">1 - 10</entry></row><row rowsep="0"><entry align="left" colname="col1" valign="top" colsep="0" rowsep="0">BaO</entry><entry align="left" colname="col2" valign="top" colsep="0" rowsep="0">0 - 20</entry></row><row rowsep="0"><entry align="left" colname="col1" valign="top" colsep="0" rowsep="0">SrO</entry><entry align="left" colname="col2" valign="top" colsep="0" rowsep="0">0 - 20</entry></row><row rowsep="0"><entry align="left" colname="col1" valign="top" colsep="0" rowsep="0">Al₂O₃</entry><entry align="left" colname="col2" valign="top" colsep="0" rowsep="0">0 - 10</entry></row><row rowsep="0"><entry align="left" colname="col1" valign="top" colsep="0" rowsep="0">CaO</entry><entry align="left" colname="col2" valign="top" colsep="0" rowsep="0">0 - 10</entry></row><row rowsep="0"><entry align="left" colname="col1" valign="top" colsep="0" rowsep="0">f₂O₃</entry><entry align="left" colname="col2" valign="top" colsep="0" rowsep="0">0 - 1</entry></row><row rowsep="0"><entry align="left" colname="col1" valign="top" colsep="0" rowsep="0">Sb₂O₃</entry><entry align="left" colname="col2" valign="top" colsep="0" rowsep="0">0 - 1</entry></row><row rowsep="0"><entry align="left" colname="col1" valign="top" colsep="0" rowsep="0">ZnO</entry><entry align="left" colname="col2" valign="top" colsep="0" rowsep="0">0 - 20</entry></row><row rowsep="0"><entry align="left" colname="col1" valign="top" colsep="0" rowsep="0">B₂O₃</entry><entry align="left" colname="col2" valign="top" colsep="0" rowsep="0">0 - 20</entry></row><row rowsep="0"><entry align="left" colname="col1" valign="top" colsep="0" rowsep="0">ZrO₂</entry><entry align="left" colname="col2" valign="top" colsep="0" rowsep="0">0 - 10</entry></row></tbody></tgroup></table></de-tables>

0131The glass material is preferably a glass with the following composition:<de-tables num="0000"><table frame="none"><tgroup cols="2" colsep="0" rowsep="0"><colspec colname="col1" colsep="0" rowsep="0" colnum="1" colwidth="111.01455652173912mm" /><colspec colname="col2" colsep="0" rowsep="0" colnum="2" colwidth="58.98544347826087mm" /><thead><row rowsep="0"><entry align="left" colname="col1" valign="top" colsep="0" rowsep="0"><b>composition</b></entry><entry align="left" colname="col2" valign="top" colsep="0" rowsep="0"><b>wt%</b></entry></row></thead><tbody><row rowsep="0"><entry align="left" colname="col1" valign="top" colsep="0" rowsep="0">SiO₂</entry><entry align="left" colname="col2" valign="top" colsep="0" rowsep="0">10 - 90</entry></row><row rowsep="0"><entry align="left" colname="col1" valign="top" colsep="0" rowsep="0">Al₂O₃</entry><entry align="left" colname="col2" valign="top" colsep="0" rowsep="0">0 - 40</entry></row><row rowsep="0"><entry align="left" colname="col1" valign="top" colsep="0" rowsep="0">B₂O₃</entry><entry align="left" colname="col2" valign="top" colsep="0" rowsep="0">0 - 80</entry></row><row rowsep="0"><entry align="left" colname="col1" valign="top" colsep="0" rowsep="0">N / A₂O</entry><entry align="left" colname="col2" valign="top" colsep="0" rowsep="0">1 - 30</entry></row><row rowsep="0"><entry align="left" colname="col1" valign="top" colsep="0" rowsep="0">K₂O</entry><entry align="left" colname="col2" valign="top" colsep="0" rowsep="0">0 - 30</entry></row><row rowsep="0"><entry align="left" colname="col1" valign="top" colsep="0" rowsep="0">CoO</entry><entry align="left" colname="col2" valign="top" colsep="0" rowsep="0">0 - 20</entry></row><row rowsep="0"><entry align="left" colname="col1" valign="top" colsep="0" rowsep="0">not ok</entry><entry align="left" colname="col2" valign="top" colsep="0" rowsep="0">0 - 20</entry></row><row rowsep="0"><entry align="left" colname="col1" valign="top" colsep="0" rowsep="0">no₂O₃</entry><entry align="left" colname="col2" valign="top" colsep="0" rowsep="0">0 - 20</entry></row><row rowsep="0"><entry align="left" colname="col1" valign="top" colsep="0" rowsep="0">MnO</entry><entry align="left" colname="col2" valign="top" colsep="0" rowsep="0">0 - 20</entry></row><row rowsep="0"><entry align="left" colname="col1" valign="top" colsep="0" rowsep="0">CaO</entry><entry align="left" colname="col2" valign="top" colsep="0" rowsep="0">0 - 40</entry></row><row rowsep="0"><entry align="left" colname="col1" valign="top" colsep="0" rowsep="0">BaO</entry><entry align="left" colname="col2" valign="top" colsep="0" rowsep="0">0 - 60</entry></row><row rowsep="0"><entry align="left" colname="col1" valign="top" colsep="0" rowsep="0">ZnO</entry><entry align="left" colname="col2" valign="top" colsep="0" rowsep="0">0 - 40</entry></row><row rowsep="0"><entry align="left" colname="col1" valign="top" colsep="0" rowsep="0">ZrO₂</entry><entry align="left" colname="col2" valign="top" colsep="0" rowsep="0">0 - 10</entry></row><row rowsep="0"><entry align="left" colname="col1" valign="top" colsep="0" rowsep="0">MnO₂</entry><entry align="left" colname="col2" valign="top" colsep="0" rowsep="0">0 - 10</entry></row><row rowsep="0"><entry align="left" colname="col1" valign="top" colsep="0" rowsep="0">CeO</entry><entry align="left" colname="col2" valign="top" colsep="0" rowsep="0">0 - 3</entry></row><row rowsep="0"><entry align="left" colname="col1" valign="top" colsep="0" rowsep="0">SnO₂</entry><entry align="left" colname="col2" valign="top" colsep="0" rowsep="0">0 - 2</entry></row><row rowsep="0"><entry align="left" colname="col1" valign="top" colsep="0" rowsep="0">Sb₂O₃</entry><entry align="left" colname="col2" valign="top" colsep="0" rowsep="0">0 - 2</entry></row><row rowsep="0"><entry align="left" colname="col1" valign="top" colsep="0" rowsep="0">TiO₂</entry><entry align="left" colname="col2" valign="top" colsep="0" rowsep="0">0 - 40</entry></row><row rowsep="0"><entry align="left" colname="col1" valign="top" colsep="0" rowsep="0">P₂O₅</entry><entry align="left" colname="col2" valign="top" colsep="0" rowsep="0">0 - 70</entry></row><row rowsep="0"><entry align="left" colname="col1" valign="top" colsep="0" rowsep="0">MgO</entry><entry align="left" colname="col2" valign="top" colsep="0" rowsep="0">0 - 40</entry></row><row rowsep="0"><entry align="left" colname="col1" valign="top" colsep="0" rowsep="0">SrO</entry><entry align="left" colname="col2" valign="top" colsep="0" rowsep="0">0 - 60</entry></row><row rowsep="0"><entry align="left" colname="col1" valign="top" colsep="0" rowsep="0">Li₂O</entry><entry align="left" colname="col2" valign="top" colsep="0" rowsep="0">0 - 30</entry></row><row rowsep="0"><entry align="left" colname="col1" valign="top" colsep="0" rowsep="0">Li₂O + Na₂O+K₂O</entry><entry align="left" colname="col2" valign="top" colsep="0" rowsep="0">1 - 30</entry></row><row rowsep="0"><entry align="left" colname="col1" valign="top" colsep="0" rowsep="0">SiO₂ + B₂O₃ + p₂O₅</entry><entry align="left" colname="col2" valign="top" colsep="0" rowsep="0">10 - 90</entry></row><row rowsep="0"><entry align="left" colname="col1" valign="top" colsep="0" rowsep="0">Nd₂O₅</entry><entry align="left" colname="col2" valign="top" colsep="0" rowsep="0">0 - 20</entry></row><row rowsep="0"><entry align="left" colname="col1" valign="top" colsep="0" rowsep="0">V₂O₅</entry><entry align="left" colname="col2" valign="top" colsep="0" rowsep="0">0 - 50</entry></row><row rowsep="0"><entry align="left" colname="col1" valign="top" colsep="0" rowsep="0">Bi₂O₃</entry><entry align="left" colname="col2" valign="top" colsep="0" rowsep="0">0 - 50</entry></row><row rowsep="0"><entry align="left" colname="col1" valign="top" colsep="0" rowsep="0">SO₃</entry><entry align="left" colname="col2" valign="top" colsep="0" rowsep="0">0 - 50</entry></row><row rowsep="0"><entry align="left" colname="col1" valign="top" colsep="0" rowsep="0">SnO</entry><entry align="left" colname="col2" valign="top" colsep="0" rowsep="0">0 - 70</entry></row></tbody></tgroup></table></de-tables><br />wherein the content of SiO₂ + p₂O₅ + B₂O₃ is 10 - 90% by weight.

0132The glass material is preferably a lithium aluminum silicate glass with the following composition:<de-tables num="0000"><table frame="none"><tgroup cols="2" colsep="0" rowsep="0"><colspec colname="col1" colsep="0" rowsep="0" colnum="1" colwidth="124.39347130434783mm" /><colspec colname="col2" colsep="0" rowsep="0" colnum="2" colwidth="45.60652869565217mm" /><thead><row rowsep="0"><entry align="left" colname="col1" valign="top" colsep="0" rowsep="0"><b>composition</b></entry><entry align="left" colname="col2" valign="top" colsep="0" rowsep="0"><b>wt%</b></entry></row></thead><tbody><row rowsep="0"><entry align="left" colname="col1" valign="top" colsep="0" rowsep="0">SiO₂</entry><entry align="left" colname="col2" valign="top" colsep="0" rowsep="0">55 - 69</entry></row><row rowsep="0"><entry align="left" colname="col1" valign="top" colsep="0" rowsep="0">Al₂O₃</entry><entry align="left" colname="col2" valign="top" colsep="0" rowsep="0">19 - 25</entry></row><row rowsep="0"><entry align="left" colname="col1" valign="top" colsep="0" rowsep="0">Li₂O</entry><entry align="left" colname="col2" valign="top" colsep="0" rowsep="0">3 - 5</entry></row><row rowsep="0"><entry align="left" colname="col1" valign="top" colsep="0" rowsep="0">Sum of Na₂O+K₂O</entry><entry align="left" colname="col2" valign="top" colsep="0" rowsep="0">0,5 - 15</entry></row><row rowsep="0"><entry align="left" colname="col1" valign="top" colsep="0" rowsep="0">Sum of MgO + CaO + SrO + BaO</entry><entry align="left" colname="col2" valign="top" colsep="0" rowsep="0">0 - 5</entry></row><row rowsep="0"><entry align="left" colname="col1" valign="top" colsep="0" rowsep="0">ZnO</entry><entry align="left" colname="col2" valign="top" colsep="0" rowsep="0">0 - 4</entry></row><row rowsep="0"><entry align="left" colname="col1" valign="top" colsep="0" rowsep="0">TiO₂</entry><entry align="left" colname="col2" valign="top" colsep="0" rowsep="0">0 - 5</entry></row><row rowsep="0"><entry align="left" colname="col1" valign="top" colsep="0" rowsep="0">ZrO₂</entry><entry align="left" colname="col2" valign="top" colsep="0" rowsep="0">0 - 3</entry></row><row rowsep="0"><entry align="left" colname="col1" valign="top" colsep="0" rowsep="0">Sum of TiO₂ + ZrO₂ + SnO₂</entry><entry align="left" colname="col2" valign="top" colsep="0" rowsep="0">2 - 6</entry></row><row rowsep="0"><entry align="left" colname="col1" valign="top" colsep="0" rowsep="0">P₂O₅</entry><entry align="left" colname="col2" valign="top" colsep="0" rowsep="0">0 - 8</entry></row><row rowsep="0"><entry align="left" colname="col1" valign="top" colsep="0" rowsep="0">f</entry><entry align="left" colname="col2" valign="top" colsep="0" rowsep="0">0 - 1</entry></row><row rowsep="0"><entry align="left" colname="col1" valign="top" colsep="0" rowsep="0">B₂O₃</entry><entry align="left" colname="col2" valign="top" colsep="0" rowsep="0">0 - 2</entry></row></tbody></tgroup></table></de-tables>

0133The above glass compositions can optionally contain additions of coloring oxides such as Nd₂O₃, Fe₂O₃, CoO, NiO, V₂O₅, MnO₂, TiO₂, CuO, CeO₂, Cr₂O₃, rare earth oxides in contents of 0 - 5% by weight or for "black glass" from 0 - 15% by weight, as well as refining agents such as As₂O₃, Sb₂O₃, SnO₂, SO₃, Cl, F, CeO₂, contained in contents of 0 - 2% by weight.

0134The components of the glass compositions each add up to 100% by weight.

0135The glasses can be produced, for example, by means of a drawing process, such as an updraw or downdraw process, overflow fusion, by float technology, or from cast or rolled glass. Particularly in the case of a casting or rolling process or a floated glass, it may be that the necessary optical quality of the surface is achieved via a polishing technology, which is required for a display cover lens, for example.

0136In a further aspect of the present invention, the substrate can also be a glass-ceramic obtained by converting the glass using a thermal treatment. Glass-ceramic is a type of crystallized glass. The glass may be fully or partially crystallized, for example only the upper part of the surface and/or a lower part of the surface may be crystallized. The glass-ceramic material has properties different from glass and properties different from ceramics. Glass-ceramic has an amorphous phase and one or more crystalline phases produced by "crystallization control" as opposed to spontaneous crystallization, which is undesirable in a glass product. Glass-ceramic typically has 30-90% vol. of crystalline phase and can thus be used to produce a range of materials with interesting mechanical properties.

0137The glass ceramic used according to the invention can be produced, for example, using the following method: During the glass manufacturing process, the raw materials are first melted at a high temperature higher than 1000°C, 1200°C, 1300°C, 1400°C, 1500°C, 1550°C, 1600°C or 1650°C to form glass wherein the glass melt is formed after homogenization, and then nucleation and crystallization are performed at a predetermined temperature after cooling to obtain a glass-ceramic article having a homogeneous structure with fine grains. The resulting glass ceramic usually has no pores.

0138Typically, crystallization agents suitable for crystallization (nucleation) can be used, such as TiO₂, ZrO₂, HfO₂ or other known components, the total amount of the crystallization agents being at most 5% by weight, preferably at most 3% by weight and more preferably at most 2% by weight, based on the total amount of the glass composition.

0139The glass ceramic can be, for example, a silicate, aluminosilicate, or fluorosilicate glass ceramic. In the glass-ceramic, the predominant crystal phase may be selected from the group consisting of lithium disilicate, enstatite, wollastonite, filled β-quartz, β-spodumene, cordierite, mullite, potassium richterite, canasite, spinel solid solution and quartz.

0140The glass-ceramic according to the present invention is preferably transparent. As already described for the glass, this can have a multifunctional surface comprising, according to one embodiment of the invention, permanent antimicrobial, antireflective, antifingerprint properties, optionally together with chemical toughening, or according to a further embodiment of the invention, antimicrobial and antireflective functions, the substrate being chemically toughened is.

0141The glass ceramic preferably has a crystalline phase of at least 30% by volume.

0142The thickness of the glass ceramic is preferably less than 20 mm, more preferably less than 15 mm, less than 10 mm, less than 5 mm, less than 3 mm, less than 1 mm, less than 0.7 mm, less than 0.5 mm or less than 0.1mm.

0143In one embodiment, the substrate is a glass ceramic made from a ceramized aluminosilicate glass or lithium aluminosilicate glass.

0144A glass ceramic or a ceramizable glass with the following composition of the starting glass (in % by weight) is preferably used:<de-tables num="0000"><table frame="none"><tgroup cols="2" colsep="0" rowsep="0"><colspec colname="col1" colsep="0" rowsep="0" colnum="1" colwidth="115.7051145631068mm" /><colspec colname="col2" colsep="0" rowsep="0" colnum="2" colwidth="54.29488543689321mm" /><tbody><row rowsep="0"><entry align="left" colname="col1" valign="top" colsep="0" rowsep="0">Li₂O</entry><entry align="left" colname="col2" valign="top" colsep="0" rowsep="0">3,2 - 5,0</entry></row><row rowsep="0"><entry align="left" colname="col1" valign="top" colsep="0" rowsep="0">N / A₂O</entry><entry align="left" colname="col2" valign="top" colsep="0" rowsep="0">0 - 1,5</entry></row><row rowsep="0"><entry align="left" colname="col1" valign="top" colsep="0" rowsep="0">K₂O</entry><entry align="left" colname="col2" valign="top" colsep="0" rowsep="0">0 - 1,5</entry></row><row rowsep="0"><entry align="left" colname="col1" valign="top" colsep="0" rowsep="0">sum well₂O+K₂O</entry><entry align="left" colname="col2" valign="top" colsep="0" rowsep="0">0,2 - 2,0</entry></row><row rowsep="0"><entry align="left" colname="col1" valign="top" colsep="0" rowsep="0">MgO</entry><entry align="left" colname="col2" valign="top" colsep="0" rowsep="0">0,1 - 2,2</entry></row><row rowsep="0"><entry align="left" colname="col1" valign="top" colsep="0" rowsep="0">CaO</entry><entry align="left" colname="col2" valign="top" colsep="0" rowsep="0">0 - 1,5</entry></row><row rowsep="0"><entry align="left" colname="col1" valign="top" colsep="0" rowsep="0">SrO</entry><entry align="left" colname="col2" valign="top" colsep="0" rowsep="0">0 - 1,5</entry></row><row rowsep="0"><entry align="left" colname="col1" valign="top" colsep="0" rowsep="0">BaO</entry><entry align="left" colname="col2" valign="top" colsep="0" rowsep="0">0 - 2,5</entry></row><row rowsep="0"><entry align="left" colname="col1" valign="top" colsep="0" rowsep="0">ZnO</entry><entry align="left" colname="col2" valign="top" colsep="0" rowsep="0">0 - 1,5</entry></row><row rowsep="0"><entry align="left" colname="col1" valign="top" colsep="0" rowsep="0">Al₂O₃</entry><entry align="left" colname="col2" valign="top" colsep="0" rowsep="0">19 - 25</entry></row><row rowsep="0"><entry align="left" colname="col1" valign="top" colsep="0" rowsep="0">SiO₂</entry><entry align="left" colname="col2" valign="top" colsep="0" rowsep="0">55 - 69</entry></row><row rowsep="0"><entry align="left" colname="col1" valign="top" colsep="0" rowsep="0">TiO₂</entry><entry align="left" colname="col2" valign="top" colsep="0" rowsep="0">1,0 - 5,0</entry></row><row rowsep="0"><entry align="left" colname="col1" valign="top" colsep="0" rowsep="0">ZrO₂</entry><entry align="left" colname="col2" valign="top" colsep="0" rowsep="0">1,0 - 2,5</entry></row><row rowsep="0"><entry align="left" colname="col1" valign="top" colsep="0" rowsep="0">SnO₂</entry><entry align="left" colname="col2" valign="top" colsep="0" rowsep="0">0 - 1,0</entry></row><row rowsep="0"><entry align="left" colname="col1" valign="top" colsep="0" rowsep="0">Total TiO₂+ ZrO₂ + SnO₂</entry><entry align="left" colname="col2" valign="top" colsep="0" rowsep="0">2,5 - 5,0</entry></row><row rowsep="0"><entry align="left" colname="col1" valign="top" colsep="0" rowsep="0">P₂O₅</entry><entry align="left" colname="col2" valign="top" colsep="0" rowsep="0">0 - 3,0.</entry></row></tbody></tgroup></table></de-tables>

0145In another embodiment, a glass ceramic or a ceramizable glass with the following composition of the starting glass is preferably used (in % by weight):<de-tables num="0000"><table frame="none"><tgroup cols="2" colsep="0" rowsep="0"><colspec colname="col1" colsep="0" rowsep="0" colnum="1" colwidth="102.42722718446602mm" /><colspec colname="col2" colsep="0" rowsep="0" colnum="2" colwidth="67.57277281553398mm" /><tbody><row rowsep="0"><entry align="left" colname="col1" valign="top" colsep="0" rowsep="0">Li₂O</entry><entry align="left" colname="col2" valign="top" colsep="0" rowsep="0">3 - 5</entry></row><row rowsep="0"><entry align="left" colname="col1" valign="top" colsep="0" rowsep="0">N / A₂O</entry><entry align="left" colname="col2" valign="top" colsep="0" rowsep="0">0 - 1,5</entry></row><row rowsep="0"><entry align="left" colname="col1" valign="top" colsep="0" rowsep="0">K₂O</entry><entry align="left" colname="col2" valign="top" colsep="0" rowsep="0">0 - 1,5</entry></row><row rowsep="0"><entry align="left" colname="col1" valign="top" colsep="0" rowsep="0">sum well₂O+K₂O</entry><entry align="left" colname="col2" valign="top" colsep="0" rowsep="0">0,2 - 2</entry></row><row rowsep="0"><entry align="left" colname="col1" valign="top" colsep="0" rowsep="0">MgO</entry><entry align="left" colname="col2" valign="top" colsep="0" rowsep="0">0,1 - 2,5</entry></row><row rowsep="0"><entry align="left" colname="col1" valign="top" colsep="0" rowsep="0">CaO</entry><entry align="left" colname="col2" valign="top" colsep="0" rowsep="0">0-2</entry></row><row rowsep="0"><entry align="left" colname="col1" valign="top" colsep="0" rowsep="0">SrO</entry><entry align="left" colname="col2" valign="top" colsep="0" rowsep="0">0 - 2</entry></row><row rowsep="0"><entry align="left" colname="col1" valign="top" colsep="0" rowsep="0">BaO</entry><entry align="left" colname="col2" valign="top" colsep="0" rowsep="0">0 - 3</entry></row><row rowsep="0"><entry align="left" colname="col1" valign="top" colsep="0" rowsep="0">ZnO</entry><entry align="left" colname="col2" valign="top" colsep="0" rowsep="0">0 - 1,5</entry></row><row rowsep="0"><entry align="left" colname="col1" valign="top" colsep="0" rowsep="0">Al₂O₃</entry><entry align="left" colname="col2" valign="top" colsep="0" rowsep="0">15 - 25</entry></row><row rowsep="0"><entry align="left" colname="col1" valign="top" colsep="0" rowsep="0">SiO₂</entry><entry align="left" colname="col2" valign="top" colsep="0" rowsep="0">50 - 75</entry></row><row rowsep="0"><entry align="left" colname="col1" valign="top" colsep="0" rowsep="0">TiO₂</entry><entry align="left" colname="col2" valign="top" colsep="0" rowsep="0">1 -5</entry></row><row rowsep="0"><entry align="left" colname="col1" valign="top" colsep="0" rowsep="0">ZrO₂</entry><entry align="left" colname="col2" valign="top" colsep="0" rowsep="0">1 - 2,5</entry></row><row rowsep="0"><entry align="left" colname="col1" valign="top" colsep="0" rowsep="0">SnO₂</entry><entry align="left" colname="col2" valign="top" colsep="0" rowsep="0">0 - 1,0</entry></row><row rowsep="0"><entry align="left" colname="col1" valign="top" colsep="0" rowsep="0">Total TiO₂+ ZrO₂ + SnO₂</entry><entry align="left" colname="col2" valign="top" colsep="0" rowsep="0">2,5 - 5</entry></row><row rowsep="0"><entry align="left" colname="col1" valign="top" colsep="0" rowsep="0">P₂O₅</entry><entry align="left" colname="col2" valign="top" colsep="0" rowsep="0">0 - 3,0.</entry></row></tbody></tgroup></table></de-tables>

0146In a further embodiment, a glass ceramic or a ceramizable glass with the following composition of the starting glass is preferably used (in % by weight):<de-tables num="0000"><table frame="none"><tgroup cols="2" colsep="0" rowsep="0"><colspec colname="col1" colsep="0" rowsep="0" colnum="1" colwidth="122.54570841121495mm" /><colspec colname="col2" colsep="0" rowsep="0" colnum="2" colwidth="47.45429158878505mm" /><tbody><row rowsep="0"><entry align="left" colname="col1" valign="top" colsep="0" rowsep="0">Li₂O</entry><entry align="left" colname="col2" valign="top" colsep="0" rowsep="0">3 - 4,5</entry></row><row rowsep="0"><entry align="left" colname="col1" valign="top" colsep="0" rowsep="0">N / A₂O</entry><entry align="left" colname="col2" valign="top" colsep="0" rowsep="0">0 - 1,5</entry></row><row rowsep="0"><entry align="left" colname="col1" valign="top" colsep="0" rowsep="0">K₂O</entry><entry align="left" colname="col2" valign="top" colsep="0" rowsep="0">0 - 1,5</entry></row><row rowsep="0"><entry align="left" colname="col1" valign="top" colsep="0" rowsep="0">sum well₂O+K₂O</entry><entry align="left" colname="col2" valign="top" colsep="0" rowsep="0">0,2 - 2</entry></row><row rowsep="0"><entry align="left" colname="col1" valign="top" colsep="0" rowsep="0">MgO</entry><entry align="left" colname="col2" valign="top" colsep="0" rowsep="0">0 - 2</entry></row><row rowsep="0"><entry align="left" colname="col1" valign="top" colsep="0" rowsep="0">CaO</entry><entry align="left" colname="col2" valign="top" colsep="0" rowsep="0">0 - 1,5</entry></row><row rowsep="0"><entry align="left" colname="col1" valign="top" colsep="0" rowsep="0">SrO</entry><entry align="left" colname="col2" valign="top" colsep="0" rowsep="0">0 - 1,5</entry></row><row rowsep="0"><entry align="left" colname="col1" valign="top" colsep="0" rowsep="0">BaO</entry><entry align="left" colname="col2" valign="top" colsep="0" rowsep="0">0 - 2,5</entry></row><row rowsep="0"><entry align="left" colname="col1" valign="top" colsep="0" rowsep="0">ZnO</entry><entry align="left" colname="col2" valign="top" colsep="0" rowsep="0">0 - 2,5</entry></row><row rowsep="0"><entry align="left" colname="col1" valign="top" colsep="0" rowsep="0">B₂O₃</entry><entry align="left" colname="col2" valign="top" colsep="0" rowsep="0">0 - 1</entry></row><row rowsep="0"><entry align="left" colname="col1" valign="top" colsep="0" rowsep="0">Al₂O₃</entry><entry align="left" colname="col2" valign="top" colsep="0" rowsep="0">19 - 25</entry></row><row rowsep="0"><entry align="left" colname="col1" valign="top" colsep="0" rowsep="0">SiO₂</entry><entry align="left" colname="col2" valign="top" colsep="0" rowsep="0">55 - 69</entry></row><row rowsep="0"><entry align="left" colname="col1" valign="top" colsep="0" rowsep="0">TiO₂</entry><entry align="left" colname="col2" valign="top" colsep="0" rowsep="0">1,4 - 2,7</entry></row><row rowsep="0"><entry align="left" colname="col1" valign="top" colsep="0" rowsep="0">ZrO₂</entry><entry align="left" colname="col2" valign="top" colsep="0" rowsep="0">1,3 - 2,5</entry></row><row rowsep="0"><entry align="left" colname="col1" valign="top" colsep="0" rowsep="0">SnO₂</entry><entry align="left" colname="col2" valign="top" colsep="0" rowsep="0">0 - 0,4</entry></row><row rowsep="0"><entry align="left" colname="col1" valign="top" colsep="0" rowsep="0">Total TiO₂ + SnO₂</entry><entry align="left" colname="col2" valign="top" colsep="0" rowsep="0">less than 2.7</entry></row><row rowsep="0"><entry align="left" colname="col1" valign="top" colsep="0" rowsep="0">P₂O₅</entry><entry align="left" colname="col2" valign="top" colsep="0" rowsep="0">0 - 3</entry></row><row rowsep="0"><entry align="left" colname="col1" valign="top" colsep="0" rowsep="0">Total ZrO₂+ 0.87 (TiO₂ + SnO₂)</entry><entry align="left" colname="col2" valign="top" colsep="0" rowsep="0">3,6 - 4,3.</entry></row></tbody></tgroup></table></de-tables>

0147The glass ceramic preferably contains high quartz mixed crystals or keatite mixed crystals as the predominant crystal phase. The crystallite size is preferably less than 70 nm, particularly preferably less than or equal to 50 nm, very particularly preferably less than or equal to 10 nm.

0148The surface of the glass or glass-ceramic substrate may be polished, textured, or patterned, such as by acid/alkaline etching, depending on the surface properties required to meet desired application requirements, such as good tactile properties.

0149The glass or glass ceramic substrates according to the invention are used wherever the combination of properties in the form of antireflection behavior, antimicrobial properties and optionally increased strength and scratch resistance and optionally anti-fingerprint properties are appropriate and necessary.

0150The glass or glass ceramic substrates according to the invention with multifunctional properties can be used, for example, for all types of display applications, such as display applications with touch screen function as single, dual or multi-touch displays, 3D displays or flexible displays. The substrates according to the invention for avoiding disruptive or contrast-reducing reflections can also be used, for example, as substrates for all types of interactive input elements, which are designed in particular with a touch function, preferably with a resistive, capacitive, optical, touch that acts by means of infrared or surface acoustic waves. Technology. It is precisely in this area that the provision of antimicrobial properties is particularly advantageous, since one or more users repeatedly come into direct contact with the substrate. The chemically toughened substrate has higher strength and is more scratch-resistant and is therefore particularly advantageous in this area.

0151Systems that work with light coupling, such as infrared or optical touch technologies, are sensitive to the presence of dirt and deposits on the touch surface, since additional reflections can occur due to deposits. Therefore, it is useful if an additional AF coating is provided in this area on the substrate.

0152Other applications for avoiding disruptive or contrast-reducing reflections with permanent antimicrobial properties and possibly anti-fingerprint properties at the same time are, for example, panes indoors and outdoors, such as shop windows, glazing of pictures, showcases, counters or refrigerated cabinets, decorative glass elements, especially in stressed areas with higher Risk of contamination, such as kitchens, bathrooms or laboratories or covers of solar modules.

0153Areas of application are also in the household, in particular in kitchens, bathrooms, components on/in the refrigerator, components in/on the cooker, in particular on hobs and the like.

0154It may be advantageous if, in addition to AR and AM properties, long-term stable AF properties are present at the same time. In particular, decorative elements that have printing on the back of the glass or glass ceramic or have a reflective coating benefit from an AF coating. These elements, which are used, for example, as stove front panes or in other kitchen appliances, repeatedly come into contact with fingerprints or greasy substances during use. In these cases, the surface very quickly looks unsightly and unhygienic. The AF coating improves the visual appearance and is easier to clean. The simultaneous provision of antimicrobial properties protects the user from germs when the substrates are touched.

0155The glass or glass-ceramic substrates of the invention can also be used to advantage in the medical field, such as hospitals, doctor's offices or pharmacies, and more generally in the pharmaceutical field, where it is essential that the appearance of germs already on the existing surfaces, such as shelves, Containers, discs and the like is prevented.

0156The glass or glass ceramic substrates according to the invention are also used in glazing of all kinds, in particular indoor and outdoor panes, such as shop windows, glazing of pictures, showcases, counters, windows, such as protective windows, in particular fire protection windows, motor vehicle windows, train windows, aircraft windows, insulating glass doors for cupboards , display or advertising boards, picture frames, architectural glass, for example for use in an exhibition, generally for the protection of any work of art or objects on display.

0157Preferred embodiments of the present invention are described in detail below with reference to the drawings, without restricting the present invention thereto. Show in detail:<ul id="ul_0013" list-style="none"><li id="ul_0013_0001"><figref>1</figref> a schematic representation of an inventive embodiment of the method of the present invention;</li><li id="ul_0013_0002"><figref>2</figref> a schematic representation of an embodiment according to the invention of a glass or glass-ceramic substrate with an antireflective coating in the form of 3 layers;</li><li id="ul_0013_0003"><figref>3</figref> a schematic representation of an embodiment according to the invention of a glass or glass-ceramic substrate with an antireflective coating in the form of 4 layers;</li><li id="ul_0013_0004"><figref>4</figref> a schematic representation of an embodiment according to the invention of a glass or glass-ceramic substrate with an antireflective coating in the form of a single layer, which in the present case represents an adhesion promoter layer;</li><li id="ul_0013_0005"><figref>5</figref> the representation of the comparison of the different transmissions (in %), plotted against the wavelength (in nm) of the untreated glass substrate, the antireflective coated glass substrate before the ion exchange and the glass substrate produced according to the invention according to Example 1;</li><li id="ul_0013_0006"><figref>6</figref> a representation for comparison of the different transmissions (in %), plotted against the wavelength (in nm) of the untreated glass substrate and of the glass substrate produced according to Example 2 according to the invention.</li><li id="ul_0013_0007"><figref>7</figref> a representation for comparing the reflections (in %), plotted against the wavelength (in nm), of the glass substrate produced according to example 3 before and after the ion exchange;</li><li id="ul_0013_0008"><figref>8</figref> a representation for comparing the reflections (in %), plotted against the wavelength (in nm), of the glass substrate produced according to Example 4 before and after the ion exchange;</li><li id="ul_0013_0009"><figref>9</figref> a representation for comparing the different transmissions (in %), plotted against the wavelength (in nm) of the untreated glass substrate and the glass substrate produced according to the invention according to example 5; and</li><li id="ul_0013_0010"><figref>10</figref> a representation to compare the different transmissions (in %), plotted against the wavelength (in nm) of the untreated glass substrate and the glass substrate produced according to the invention according to Example 6.</li></ul>

0158In<figref>1</figref> Illustrated is a schematic representation of an embodiment of the method of the present invention according to the present invention. In this case, a glass or glass-ceramic substrate 2 is first provided. An antireflective coating is applied to its surface 20, which is optionally cleaned first. Depending on the embodiment, the coating can also be applied to both surfaces (not shown) of the glass or glass-ceramic substrate 2 . The anti-reflective coating can be any coating with anti-reflective properties. For example, this can be made up of one layer, at least 2 layers with an alternating high and low refractive index, or at least 3 layers with an alternating medium, high and low refractive index. In the exemplary embodiment shown, the antireflective coating consists of a single layer 5 (<figref>4</figref>) or at least 2 layers 3 and 4(<figref>2</figref> and<figref>3</figref>) constructed with high and low refractive index, wherein the outer or top layer 31, 41, 5 of the stack of layers has a low refractive index. According to a preferred embodiment, the layer 31, 41, 5 can be an adhesion promoter layer. The adhesion promoter layer is preferably a mixed oxide layer, preferably a silicon mixed oxide layer.

0159Subsequently, the glass or glass ceramic substrate 2 present with the antireflective coating is then subjected to an ion exchange. For this purpose, according to one of the variants according to the invention, it is antimicrobially finished and chemically prestressed. Metal salts with an antimicrobial effect are, for example, silver, copper, cadmium, zinc, iron, tin, cobalt, cerium, antimony, selenium, chromium, magnesium and/or nickel salts. Any compounds suitable for this purpose can be used for chemical prestressing. Conventionally, potassium, rubidium and/or cesium salts are used. If the glass or glass-ceramic substrate 2 is to be antimicrobially equipped and chemically tempered, this can be carried out in one or two steps. If this is to be carried out in one step, the metal salts suitable for chemical toughening and the metal salts with an antimicrobial effect are mixed together in a salt bath and the glass or glass-ceramic substrate 2 is immersed in the salt bath. If this is to be carried out in two steps, chemical prestressing is preferably carried out in a first salt bath in the first step and the antimicrobial finish is only provided in a second salt bath in the second step. It is particularly advantageous if the second salt bath contains a mixture of potassium, rubidium and/or cesium salt with one or more metal salts with an antimicrobial effect. The ion exchange takes place through the anti-reflective coating so that it covers the entire substrate with the layer or layers present thereon (this is indicated by the bracket in<figref>1</figref> expressed).

0160Following the ion exchange process or processes, an anti-fingerprint coating 6 can be applied to the coated, antimicrobially finished and chemically toughened glass or glass-ceramic substrate 2 .<figref>2</figref> shows a schematic representation of an embodiment according to the invention of a glass or glass ceramic substrate 2 with an antireflective coating in the form of 3 layers. Layer 33 has a medium refractive index (M layer), layer 32 has a high refractive index (T layer), and layer 31 has a low refractive index (S layer). The layer 31 can be an adhesion promoter layer. Before the anti-reflective coating is applied, it can be expedient to clean the surface 20 of the substrate 2 . In the example shown, the glass or glass ceramic substrate 2 has antimicrobial properties and is chemically prestressed.

0161The production of such an antireflective coating is explained in detail below in the examples.

0162<figref>3</figref> FIG. 12 illustrates a schematic representation of a further embodiment of a glass or glass-ceramic substrate 2 according to the invention with an anti-reflective coating in the form of 4 layers (41, 42, 43, 44). The 4 layers alternately have a high and a low refractive index and together form the anti-reflective coating. The top layer 41 is preferably an adhesion promoter layer. In the example shown, the glass or glass ceramic substrate 2 with the coating 4 has antimicrobial properties and is chemically prestressed.

0163<figref>4</figref> 1 shows a schematic representation of a further embodiment of a glass or glass-ceramic substrate 2 according to the invention with an anti-reflective coating which is present in the form of a single layer 5. FIG. This is preferably an adhesion promoter layer. In the example shown, the glass or glass ceramic substrate 2 has antimicrobial properties with the individual layer 5 and is chemically prestressed. The production of such a substrate is described in the examples.

0164the<figref>5</figref> until<figref>10</figref> are explained in detail in the examples.

0165The advantages of the present invention are very complex:<ul id="ul_0014" list-style="none"><li id="ul_0014_0001">The present invention offers a special combination of properties that are simultaneously and permanently integrated in a glass or glass-ceramic substrate. The glass or glass-ceramic substrates with durable multifunctional surface properties of the invention comprise a combination of antimicrobial, antireflective and antifingerprint functions with the substrate being chemically toughened, or a combination of antimicrobial and antireflective functions with the substrate being chemically toughened. The subject matter of the invention is also a method for producing such substrates.</li></ul>

0166The present invention provides combinations of properties that are not previously known in this way from the prior art, with each individual property or function not being adversely affected by another property or function, but rather these complement each other advantageously and each property to the full scope is available.

0167It was found that with simultaneous antimicrobial finishing and chemical prestressing, values ​​for the compressive stress of the surface CS (compressive stress) and depth of the compressive stress layer DoL (depth of ion exchanged layer) are obtained that are in the same range as for glasses or glass ceramics, which have only been chemically pre-stressed by ion exchange, without providing them with an antimicrobial treatment at the same time.

0168The presence of an AF coating has no adverse effect on the release of the antimicrobial ions from the glass or glass-ceramic surface, so that the antimicrobial properties can develop to their full extent unhindered. Applying an AF layer to an AR coating also leads to an improvement in the abrasion resistance of the entire coating system.

0169The glass or glass-ceramic substrates according to the invention are used wherever the combination of properties in the form of high strength, anti-reflection behavior and anti-microbial properties and optionally anti-fingerprint properties are useful and necessary. The glass or glass-ceramic substrates disclosed in the present invention can be used, for example, as cover glasses for any form of touch screen of electronic devices and many devices in the home or industrial field, such as mobile phones, smart phones, tablet PCs, notebook PCs, televisions, ATM machines, ticket machines and can also be control, information and/or operation panels or windows of any shape and size, which are used, for example, in automobiles, hospitals, museums, shops, housing and transport, etc.

0170The substrates according to the invention are advantageously used in applications in which many functions are integrated together, such as touch screens of smartphones or tablet PCs. For this purpose, the substrates according to the invention are chemically toughened, have an AR and AF coating and have antimicrobial properties: The glass substrate according to the invention is chemically toughened in this case, so that the very thin glass substrates that are used in touch screens have sufficiently high mechanical strength. In addition to avoiding disruptive or contrast-reducing reflections, the AR coating makes it possible to save energy, since the display module can be operated with lower brightness due to a reduction in reflections at the glass-air interface. The antimicrobial finish on the glass surface protects the user, who is constantly in direct contact with the glass surface, from bacteria that are on the surface. Finally, the anti-fingerprint properties of the glass surface are very useful because the appearance of the glass improves and the screen is easier to clean. In particular, the functions described can be provided with a long service life.

0171The glass or glass-ceramic substrates provided according to the invention therefore impart all functions to the surface in a durable manner in such a way that common industrial quality standards are met. The method according to the invention is also suitable for mass production.

0172The present invention is explained in more detail below on the basis of examples, without being restricted thereto.

examples

example 1

Glass substrate: soda lime float glass

0173A carefully cleaned 100 x 200 mm soda lime float glass was coated with an anti-reflective coating composed of a three-layer structure according to FIG<figref>2</figref> shown. The antireflective coating consisted of three layers and had the following structure: glass substrate (2) + M layer (33) + T layer (32) + S layer (31). The S layer (31) was also an adhesion promoter layer. The three layers were applied to the glass by dip coating.

0174The solutions for the three layers were prepared as follows:

S layer:

preliminary solution

0175A mixture of 60 mL of TEOS and 125 mL of ethanol was stirred for 15 minutes. Then 30 ml of distilled water and 12 ml of 1N nitric acid were added. After stirring for 10 minutes, the solution was diluted with 675 mL of ethanol.<br />(This pre-solution was used for the M layer.)

Mixed oxide solution:

0176In order to achieve the adhesion promoter layer properties, after 24 hours 10.9 g Al(NO₃)₃·9H₂O dissolved in 95 mL of ethanol and 5 mL of acetylacetonate added to the pre-solution.

T layer:

017768 ml of titanium n-butoxide, 918 ml of ethanol (absolute), 5 ml of acetylacetone and 9 ml of ethyl butyl acetate were mixed together and stirred for 2 hours.

M layer:

0178The coating solutions for preparing the M layer having an intermediate refractive index were prepared by mixing the S pre-solution and T solution. The M layer solution comprised a mixture of S and T solutions in the ratio of 75:25 wt% of the oxides.

0179The individual layers of example 1 were applied by separate dipping steps. The glass material was immersed in the dipping solution. Then this was done at a rate of 6mm/sec. extracted, the moisture content of the ambient atmosphere between 5 g / m³ and 12 gsm³, preferably 8 g/m³ was. The solvent was then evaporated at 90-100°C. Thereafter, the coated layer was cured at a temperature of 450°C for 20 minutes.

0180The sample provided with the AR coating using the sol-gel method was then placed in a KNO₃- Salt bath containing 0.01 wt% AgNO₃ contained, immersed and treated at 430°C for one hour.

0181Then, the ion-exchanged AR-coated sample was coated with an AF coating on one side by a liquid pressure technique. The AF coating solutions are products based on polyfluoropolyethers known under the trade name “Fluorolink® PFPE” such as “Fluorolink® S10” from Solvay Solexis or “Optool DSX™” or “Optool™ AES4-E” from Daikin Industries LTD.

0182The glass substrate thus produced according to example 1 has an AR coating, is chemically toughened, has antimicrobial properties and has an AF coating.

0183For comparison purposes, the measured transmissions of the uncoated soda-lime substrate, the AR-coated substrate before ion exchange and the glass substrate produced according to Example 1 are in<figref>5</figref> shown.

0184<figref>5</figref> shows a clear increase in the transmission of the glass substrate according to the invention, which was obtained despite the different functionalities of the glass surface.

0185The compressive stress (CS) of the glass substrate obtained according to Example 1 was 332 MPa and the DoL (depth of ion exchanged layer) was 5.3 μm.

0186The antimicrobial efficacy of the glass substrate of Example 1 on its AF-coated surface was >99.9% against both E.coli and S.aureus.

0187The water contact angle of the AF-coated surface of the glass substrate of Example 1 was 112°C. The resistance of the glass substrate was examined in the neutral salt spray test. After the glass substrate was exposed to water and sodium chloride at 35°C for 10 weeks, the measured water contact angle was still 105°C. This proves that the durability of the coating applied to the glass substrate is very high.

example 2

Glass substrate: aluminosilicate glass

0188A carefully cleaned aluminosilicate glass as a glass material with a size of 100 x 60 x 0.5 mm was provided with an anti-reflective coating having a single-layer structure as in<figref>4</figref> shown. The single AR layer was also an adhesion promoter layer.

0189The single layer solution was prepared as follows:<ul id="ul_0015" list-style="none"><li id="ul_0015_0001">100 ml of TEOS was mixed with 200 ml of ethyl alcohol and 15 ml of 0.1N HCl. The mixture was stirred at 40°C for 3 hours. Then the solution was diluted with 300 ml of ethyl alcohol and 16 g of Al(NO₃)₃·9H₂O was also added and stirring continued for another half hour. After aging the solution at room temperature for 24 hours, the solution was used as dip coating.</li></ul>

0190The substrate glass was coated on both sides with the above solution by a dip coating method. The rate of withdrawal of the substrate from the liquid was 9 mm/min. The fresh coating was preheated at 200°C for 2 minutes and then the coated glass substrate was cured at 450°C for 1 hour. Then, the coated glass substrate was immersed in a salt bath for the ion exchange process, which was carried out at a temperature of 430°C for 4 hours. The molten salt in the salt bath was KNO₃ mixed with 0.02 wt% AgNO₃.

0191After ion exchange, the glass substrate was cleaned and an AF coating was applied using a conventional spray deposition method.

0192The glass substrate thus produced according to Example 2 has an AR coating, is chemically toughened, has antimicrobial properties and has an AF coating.

0193The transmission of the untreated glass substrate compared to the glass substrate from example 2 is in<figref>6</figref> shown.

0194<figref>6</figref> shows the high transmission of the glass substrate produced according to Example 2 compared to the untreated glass substrate.

0195The compressive stress (CS) of the glass substrate obtained in Example 2 was 840 MPa, and the DoL was 35 µm.

0196The antimicrobial efficacy of Example 2 on its AF-coated surface was >99.9% against E.coli and 99.5% against S.aureus.

0197The water contact angle on the AF coated surface of Example 1 was 115°C.

Example 3

Glass substrate: a glass having the following composition:

<de-tables num="0000"><table frame="none"><tgroup cols="2" colsep="0" rowsep="0"><colspec colname="col1" colsep="0" rowsep="0" colnum="1" colwidth="101.7428mm" /><colspec colname="col2" colsep="0" rowsep="0" colnum="2" colwidth="68.2572mm" /><thead><row rowsep="0"><entry align="left" colname="col1" valign="top" colsep="0" rowsep="0"><b>composition</b></entry><entry align="left" colname="col2" valign="top" colsep="0" rowsep="0"><b>wt%</b></entry></row></thead><tbody><row rowsep="0"><entry align="left" colname="col1" valign="top" colsep="0" rowsep="0">SiO₂</entry><entry align="left" colname="col2" valign="top" colsep="0" rowsep="0">58,1</entry></row><row rowsep="0"><entry align="left" colname="col1" valign="top" colsep="0" rowsep="0">Al₂O₃</entry><entry align="left" colname="col2" valign="top" colsep="0" rowsep="0">19,7</entry></row><row rowsep="0"><entry align="left" colname="col1" valign="top" colsep="0" rowsep="0">N / A₂O</entry><entry align="left" colname="col2" valign="top" colsep="0" rowsep="0">8,2</entry></row><row rowsep="0"><entry align="left" colname="col1" valign="top" colsep="0" rowsep="0">K₂O</entry><entry align="left" colname="col2" valign="top" colsep="0" rowsep="0">2,5</entry></row><row rowsep="0"><entry align="left" colname="col1" valign="top" colsep="0" rowsep="0">MgO</entry><entry align="left" colname="col2" valign="top" colsep="0" rowsep="0">1,9</entry></row><row rowsep="0"><entry align="left" colname="col1" valign="top" colsep="0" rowsep="0">B₂O₃</entry><entry align="left" colname="col2" valign="top" colsep="0" rowsep="0">9,6</entry></row></tbody></tgroup></table></de-tables>

0198A carefully cleaned glass with the above composition was used as the glass material with a size of 100×200×3 mm, which was coated with an antireflective coating consisting of three layers according to<figref>2</figref>, has been coated. The antireflective coating consisted of three layers and had the following structure: glass substrate (2) + M layer (33) + T layer (32) + S layer (31). The S layer was also an adhesion promoter layer. The three layers were applied to the glass using a dip coating technique.

0199The solutions for the three layers were prepared as follows:

S layer:

preliminary solution:

0200A mixture of 60 mL of TEOS and 125 mL of ethanol was stirred for 15 minutes. Then 30 ml of distilled water and 12 ml of 1N nitric acid were added. After stirring for 10 minutes, the solution was diluted with 750 mL of ethanol. (This pre-solution was used for the M layer.)

Mixed oxide solution:

0201In order to achieve the adhesion promoter layer properties, after 24 hours 10.9 g Al(NO₃)₃·9H₂O dissolved in 95 mL of ethanol and 5 mL of acetylacetonate added to the pre-solution.

T layer:

0202109 g amorphous TiO₂powder was added to the solvent mixture of 802 g ethanol and 89 g 1,5-pentanediol. The synthesis of TiO₂-Powder was as follows: 1 mole of titanium tetraethylate was reacted with 1 mole of acetylacetone and then with 5 moles of H₂O hydrolyzed. After removing the solvent, the powder was dried at 125° C. for 5 hours. The amorphous powder contained TiO₂ of about 58% by weight.

M layer:

0203The coating solutions for preparing the M layer having an intermediate refractive index were prepared by mixing the S pre-solution and T solution. The M layer solution may comprise a mixture of S and T solution in a 65:35 weight ratio of oxides.

0204Then, the glass substrate was immersed in a salt bath to perform the ion exchange process at a temperature of 420°C for 6 hours. The molten salt in the salt bath was KNO₃, mixed with 0.02 wt% AgNO₃.

0205After performing the ion exchange, the sample was cleaned and an AF coating was applied by a conventional thermal vacuum deposition technique.

0206The glass substrate thus produced according to example 3 has an AR coating, is chemically toughened, has antimicrobial properties and has an AF coating.

0207The compressive stress (CS) of the glass substrate of Example 3 was 712 MPa and the DoL was 30 µm.

0208The antimicrobial efficacy of the glass substrate of Example 3 on its AF-coated surface was >99% against both E.coli and S.aureus.

0209The water contact angle on the AF coated surface of Example 3 was 115°C.

0210The reflections of the glass substrate of Example 3 before and after ion exchange are in<figref>7</figref> shown.<figref>7</figref> shows that the reflection of the glass substrate of Example 3 is in fact not adversely affected by the ion exchange.

Example 4:

Glass substrate: soda-lime glass having the following composition:

<de-tables num="0000"><table frame="none"><tgroup cols="2" colsep="0" rowsep="0"><colspec colname="col1" colsep="0" rowsep="0" colnum="1" colwidth="108.7924mm" /><colspec colname="col2" colsep="0" rowsep="0" colnum="2" colwidth="61.2076mm" /><thead><row rowsep="0"><entry align="left" colname="col1" valign="top" colsep="0" rowsep="0"><b>composition</b></entry><entry align="left" colname="col2" valign="top" colsep="0" rowsep="0"><b>wt%</b></entry></row></thead><tbody><row rowsep="0"><entry align="left" colname="col1" valign="top" colsep="0" rowsep="0">SiO₂</entry><entry align="left" colname="col2" valign="top" colsep="0" rowsep="0">70</entry></row><row rowsep="0"><entry align="left" colname="col1" valign="top" colsep="0" rowsep="0">TiO₂</entry><entry align="left" colname="col2" valign="top" colsep="0" rowsep="0">0,3</entry></row><row rowsep="0"><entry align="left" colname="col1" valign="top" colsep="0" rowsep="0">N / A₂O</entry><entry align="left" colname="col2" valign="top" colsep="0" rowsep="0">8,36</entry></row><row rowsep="0"><entry align="left" colname="col1" valign="top" colsep="0" rowsep="0">K₂O</entry><entry align="left" colname="col2" valign="top" colsep="0" rowsep="0">8,46</entry></row><row rowsep="0"><entry align="left" colname="col1" valign="top" colsep="0" rowsep="0">CaO</entry><entry align="left" colname="col2" valign="top" colsep="0" rowsep="0">5,74</entry></row><row rowsep="0"><entry align="left" colname="col1" valign="top" colsep="0" rowsep="0">ZnO</entry><entry align="left" colname="col2" valign="top" colsep="0" rowsep="0">4,53</entry></row><row rowsep="0"><entry align="left" colname="col1" valign="top" colsep="0" rowsep="0">BaO</entry><entry align="left" colname="col2" valign="top" colsep="0" rowsep="0">2,11</entry></row><row rowsep="0"><entry align="left" colname="col1" valign="top" colsep="0" rowsep="0">Sb₂O₃</entry><entry align="left" colname="col2" valign="top" colsep="0" rowsep="0">0,5</entry></row></tbody></tgroup></table></de-tables>

0211A carefully cleaned soda-lime glass substrate of the above composition measuring 100 x 200 mm was provided with an anti-reflective coating consisting of three layers according to<figref>2</figref> was built. The antireflective layer had the following structure: glass substrate (2) + M layer (33) + T layer (32) + S layer (31). The S layer (31) was also an adhesion promoter layer. The three layers were applied to the glass by dip coating.

0212The solutions for the three layers were prepared as follows:

S layer:

0213A mixture of 45 mL of TMOS and 125 mL of ethanol was stirred for 15 minutes. Then 38 ml of distilled water and 1.7 g of 37% HCl were added. After stirring for 10 minutes, the solution was diluted with 675 mL of ethanol. Then 10 g of SnCl4·6H₂O dissolved in 95 mL of ethanol and 5 mL of acetylacetone added to the solution.

T layer:

021470 ml of titanium n-butoxide, 920 ml of ethanol (absolute), 5 ml of acetylacetone and 10 ml of ethyl butyl acetate were mixed together and stirred for 2 hours.

M layer:

0215The M layer was prepared as described in Example 3.

0216The glass substrate was cut into a pure KNO₃- Immersed in a salt bath for chemical toughening at a temperature of 420°C for 8 hours. Then, the glass substrate was ion-exchanged in another silver-containing salt bath at a temperature of 430°C for 0.5 hour. The molten salt in the second salt bath was KNO₃ mixed with 0.1 wt% AgNO₃.

0217After the ion exchange, the sample was cleaned and an AF coating was applied by a liquid pressure technology.

0218The glass substrate thus produced according to Example 4 has an AR coating, is chemically toughened, has antimicrobial properties and has an AF coating.

0219The compressive stress (CS) of the glass substrate of Example 4 was 339 MPa and the DoL was 14 µm.

0220The antimicrobial efficacy of the glass substrate of Example 4 on its AF-coated surface was >99.9% against both E.coli and S.aureus.

0221The water contact angle on the AF-coated surface of the glass substrate of Example 4 was 113°C.

0222The reflections of the glass substrate, produced according to example 4, before and after the ion exchange, carried out in 2 steps, are in<figref>8</figref> shown.<figref>8</figref> shows that the reflections of the glass substrate according to Example 4 before and after the ion exchange practically do not differ, so that the antireflective coating was not adversely affected by the tempering and antimicrobial finishing.

Example 5:

Glass substrate: borosilicate glass without antimony

<de-tables num="0000"><table frame="all"><tgroup cols="2" colsep="1" rowsep="1"><colspec colname="col1" colsep="1" rowsep="1" colnum="1" colwidth="85mm" /><colspec colname="col2" colsep="1" rowsep="1" colnum="2" colwidth="85mm" /><thead><row rowsep="1"><entry align="center" colname="col1" valign="bottom" colsep="1" rowsep="1"><b>oxide</b></entry><entry align="center" colname="col2" valign="top" colsep="1" rowsep="1"><b>Proportion [% by weight]</b></entry></row></thead><tbody><row rowsep="1"><entry align="center" colname="col1" valign="top" colsep="1" rowsep="1">SiO₂</entry><entry align="center" colname="col2" valign="top" colsep="1" rowsep="1">65</entry></row><row rowsep="1"><entry align="center" colname="col1" valign="top" colsep="1" rowsep="1">B₂O₃</entry><entry align="center" colname="col2" valign="top" colsep="1" rowsep="1">7</entry></row><row rowsep="1"><entry align="center" colname="col1" valign="top" colsep="1" rowsep="1">Al₂O₃</entry><entry align="center" colname="col2" valign="top" colsep="1" rowsep="1">3</entry></row><row rowsep="1"><entry align="center" colname="col1" valign="top" colsep="1" rowsep="1">N / A₂O</entry><entry align="center" colname="col2" valign="top" colsep="1" rowsep="1">9</entry></row><row rowsep="1"><entry align="center" colname="col1" valign="top" colsep="1" rowsep="1">K₂O</entry><entry align="center" colname="col2" valign="top" colsep="1" rowsep="1">8</entry></row><row rowsep="1"><entry align="center" colname="col1" valign="top" colsep="1" rowsep="1">ZnO</entry><entry align="center" colname="col2" valign="top" colsep="1" rowsep="1">5</entry></row><row rowsep="1"><entry align="center" colname="col1" valign="top" colsep="1" rowsep="1">TiO₂</entry><entry align="center" colname="col2" valign="top" colsep="1" rowsep="1">2</entry></row><row rowsep="1"><entry align="center" colname="col1" valign="top" colsep="1" rowsep="1">CaO</entry><entry align="center" colname="col2" valign="top" colsep="1" rowsep="1">1</entry></row></tbody></tgroup></table></de-tables>

0223A carefully cleaned glass substrate having the above composition with a size of 135 x 70 x 0.7 mm was coated with an anti-reflective coating composed of a three-layer structure as in<figref>2</figref> shown. The antireflective coating consisted of three layers and had the following structure: glass substrate (2) + S layer (33) + T layer (32) + S layer (31). The S layer (31) was a primer layer. The three layers were applied to the glass by dip coating technology.

0224The solutions for the three layers were prepared as follows:

S layer:

022560 ml of TEOS was mixed with 120 ml of ethanol and 10 ml of 0.1N HCl and stirred at 40°C for 3 hours. Then 9.5 g of Al(NO₃)₃, 270 ml of ethanol and 50 ml of ethylacetone were added and stirred for a further 30 minutes.

T layer:

022630 ml of titanium oxide isopropoxide was mixed with 36 ml of acetic acid and stirred for 1 hour. Then 400 ml of ethanol was added and stirred for 1 hour. Finally 100 ml of acetylacetone was added into the solution and stirred for 1 hour.

0227The glass substrate was immersed in a salt bath for an ion exchange process at a temperature of 410°C for 3 hours. The molten salt in the salt bath was KNO₃ mixed with 0.5 wt% AgNO₃.

0228After the ion exchange was completed, the glass substrate was cleaned and an AF coating applied by conventional commercial spray deposition technology.

0229The glass substrate thus produced according to Example 5 has an AR coating, is chemically toughened, has antimicrobial properties and has an AF coating.

0230The compressive stress (CS) of the glass substrate prepared according to Example 4 was 407 MPa and the DoL was 14 µm.

0231The antimicrobial effectiveness of the glass substrate according to Example 5 on its AF-coated surface was >99.9% against both E.coli and S.aureus.

0232The water contact angle on the AF-coated surface of the glass substrate of Example 5 was 114°C.

0233The transmission of the same but untreated glass substrate compared to the glass substrate produced according to Example 5 is in<figref>9</figref> shown.

0234<figref>9</figref> shows that the transmission of the glass substrate according to Example 5 is significantly higher and has a maximum at a wavelength in the range between 450 and 500 nm in contrast to an untreated glass substrate.

Example 6:

Glass substrate: borosilicate glass with the following composition:

<de-tables num="0000"><table frame="none"><tgroup cols="2" colsep="0" rowsep="0"><colspec colname="col1" colsep="0" rowsep="0" colnum="1" colwidth="99.24606666666666mm" /><colspec colname="col2" colsep="0" rowsep="0" colnum="2" colwidth="70.75393333333334mm" /><thead><row rowsep="0"><entry align="left" colname="col1" valign="top" colsep="0" rowsep="0"><b>composition</b></entry><entry align="left" colname="col2" valign="top" colsep="0" rowsep="0"><b>wt%</b></entry></row></thead><tbody><row rowsep="0"><entry align="left" colname="col1" valign="top" colsep="0" rowsep="0">SiO₂</entry><entry align="left" colname="col2" valign="top" colsep="0" rowsep="0">80,8</entry></row><row rowsep="0"><entry align="left" colname="col1" valign="top" colsep="0" rowsep="0">Al₂O₃</entry><entry align="left" colname="col2" valign="top" colsep="0" rowsep="0">2,4</entry></row><row rowsep="0"><entry align="left" colname="col1" valign="top" colsep="0" rowsep="0">B₂O₃</entry><entry align="left" colname="col2" valign="top" colsep="0" rowsep="0">12,7</entry></row><row rowsep="0"><entry align="left" colname="col1" valign="top" colsep="0" rowsep="0">N / A₂O</entry><entry align="left" colname="col2" valign="top" colsep="0" rowsep="0">3,5</entry></row><row rowsep="0"><entry align="left" colname="col1" valign="top" colsep="0" rowsep="0">K₂O</entry><entry align="left" colname="col2" valign="top" colsep="0" rowsep="0">0,6</entry></row></tbody></tgroup></table></de-tables>

0235A carefully cleaned borosilicate glass of the above composition measuring 100 × 200 mm was provided with an anti-reflective coating comprising a single layer according to<figref>4</figref> exhibited The single AR layer was a primer layer.

0236The solution for the single layer was prepared as follows:

023756 g of 30% aqueous SiO₂-Solution stabilized with NH₄OH, where the SiO₂ had an average particle size of 8 nm, was mixed with 120 ml of ethanol and 10 ml of 0.1 N HCl and stirred at 40° C. for 3 hours. Then 9.5 g of Al(NO₃)₃, 270 ml of ethanol and 50 ml of ethylacetone were added and stirred for a further 30 minutes.

0238The borosilicate glass substrate was coated on both sides with the above solution in a dip coating process. The fresh coating was first preheated at 200°C for 2 minutes, then the coated glass substrate was cured at 450°C for 1 hour.

0239Then, the coated glass substrate was immersed in a salt bath to perform an ion exchange process at a temperature of 450°C for 4 hours. The molten salt in the salt bath was KNO₃, mixed with 0.5 wt% AgNO₃.

0240After the ion exchange was completed, the sample was cleaned and an AF coating was applied by a liquid pressure method.

0241The glass substrate thus produced according to Example 6 has an AR coating, is chemically toughened, has antimicrobial properties and has an AF coating.

0242The compressive stress (CS) of the glass substrate prepared according to Example 6 was 213 MPa and the DoL was 12 μm.

0243The antimicrobial efficacy of the glass substrate of Example 6 on its AF-coated surface was >99% against both E.coli and S.aureus.

0244The water contact angle on the AF-coated surface of the glass substrate of Example 6 was 112°C.

0245The transmission of the untreated glass substrate compared to the glass substrate produced according to example 6 is in<figref>10</figref> shown.<figref>10</figref> shows that the transmission of the glass substrate that was produced according to Example 6 is significantly higher than that of the same untreated glass substrate.

Reference List

<dl tsize="14"><dt>2</dt><dd>Glass or glass ceramic substrate</dd><dt>20</dt><dd>Surface of the glass or glass-ceramic substrate</dd><dt>3</dt><dd>Low refractive index layer of anti-reflective coating</dd><dt>4</dt><dd>High refractive index layer of anti-reflective coating</dd><dt>5</dt><dd>anti-reflective coating in the form of a single layer</dd><dt>31</dt><dd>Low refractive index layer of anti-reflective coating</dd><dt>32</dt><dd>High refractive index layer of anti-reflective coating</dd><dt>33</dt><dd>Medium refractive index layer of anti-reflective coating</dd><dt>41, 42, 43, 44</dt><dd>Alternating high and low refractive index layers of the anti-reflective coating</dd></dl>