High performance, durable, low-e glass and method of making same

2089421 HIGH PERFORMANCE, DURABLE, LOW-E GLASS AND M~THOD OF MAKING SAME FIELD OF THE INVENTION This invention relates to sputter-coated glasses and methods for making them. More particularly, this invention relates to sputter-coated glasses exhibiting high visible light transmittance and excellent infrared energy reflecting characteristics useful as architectural glasses, and certain unique methods for making them.

BACKGROUND OF THE INVENTION For architectural flat glass, such as is made by the "float" process, two of the more prominent techniques for creating solar management coatings on these glasses are the pyrolytic process and the magnetron sputter-coating process. Drawbacks heretofore experienced in the sputtercoating process have been that the coatings can often be easily rubbed off (i.e. lack "durability"~ and that the polysealant used in forming multi-paned architectural windows often attacks the coating. This, in turn, breaks down the seal between the panes, allowing detrimental condensation to accumulate between them. On the other hand, sputter coatings have had the historic advantage of being able to achieve low emissivity values and high visible light transmittance properties, as compared to most pyrolytic coatings. These latter two properties are perhaps among the most important to achieve in certain architectural glasses.

The terms "emissivity" and "transmittance" are well understood in the art and are used herein according to their well known meaning. Thus, for example, the term "transmittance" herein means solar transmittance, which is 2089421 made up of visible light transmittance, infrared energy transmittance, and ultraviolet light transmittance. Total solar energy transmittance is then usually characterized as a weighted average of these other values. With respect to these transmittances, visible transmittance, as reported herein, is characterized by the standard Illuminant C technique at 380-720nm; infrared is 800-2100nm;

ultraviolet is 300-400nm; and total solar is 300-2100nm.

For purposes of emissivity, however, a particular infrared range (i.e. 2,500-40,000nm) is employed, as discussed below.

Visible transmittance can be measured using known, conventional techniques. For example, by using a spectrophotometer, such as a Beckman 5240 (Beckman Sci.

Inst. Corp.), a spectral curve of transmission at each wavelength is obtained. Visible transmission is then calculated using ASTM E-308 "Method for Computing the Colors of Objects by Using the CIE System" (Annual Book of ASTM Standards, Vol. 14.02). A lesser number of wavelength points may be employed than prescribed, if desired.

Another technique for measuring visible transmittance is to employ a spectrometer such as a commercially available Spectragard spectrophotometer manufactured by Pacific Scientific Corporation. This device measures and reports visible transmittance directly.

"Emissivity" (E) is a measure, or characteristic of both absorption and reflectance of light at given wavelengths.

It is usually represented by the formula:

E~ Reflectancefjtm For architectural purposes, emissivity values become quite important in the so-called "mid range", sometimes also called the "far range", of the infrared spectrum, i.e. about 2500-40,000nm.

The term "emissivity", as used herein, is thus used to refer to emissivity values measured in this infrared range as specified by the 1991 2089g21 Proposed ASTM Standard for measuring infrared energy to calculate emittance, as proposed by the Primary Glass Manufacturers' Council and entitled "lest Method for Measuring and Calculating Emittance of Architectural Flat S Glass Products Using Radiometric Measurements". This Standard, and its provisions, are incorporated herein by reference. In this Standard, emissivity is broken into two components, hemispherical emissivity (Eh) and normal emissivity (En).

The actual accumulation of data for measurement of such emissivity values is conventional and may be done by using, for example, a Beckman Model 4260 spectrophotometer with "VW" attachment (Beckman Scientific Inst.

Corp.). This spectrophotometer measures reflectance versus wavelength, and from this, emissivity is calculated using the aforesaid 1991 Proposed ASTM Standard which has been incorporated herein by reference.

Another term employed herein is "sheet resistance". Sheet resistance (~s) is a well known term in the art and is used herein in accordance with its well known meaning. Generally speaking, this term refers to the resistance in ohms for any square of a layer system on a glass substrate to an electric current passed through the layer system. Sheet resistance is an indication of how well the layer is reflecting infrared energy, and is thus often used along with emissivity as a measure of this characteristic, so important in many architectural glasses.

"Sheet resistance" is conveniently measured by using a 4point probe ohmmeter, such as a dispensable 4-point resistivity probe with a Magnetron Instruments Corp. head, Model M-800 produced by Signatone Corp. of Santa Clara, California.

As stated above, for many architectural purposes it is desirable to have as low an emissivity and Rs value as 3~ feasible, such that the glass window is reflecting 2089~21 substantial amounts of the infrared energy impinging on the glass. Generally speaking, "low-E" (i.e. low emissivity) glasses are considered to be those glasses which have a hemispherical emissivity (Eh) of less than about 0.16 and a normal emissivity (En) of less than about 0.12. Preferably, Eh is about 0.13 or less, and En is about 0.10 or less. At the same time, sheet resistance (Rs) is, therefore, preferablY less than about 10.5 ohms/5quare- Such glasses~ to be commercially acceptable, usually are required to transmit as much visible light as possible, often about 76% or more using the Illuminant C technique for measuring transmittance in glasses of about 2mm-6mm thick. Visible transmittance, in this respect, should more preferably be at least about 78% or greater for glasses between about 2mm-6mm thick. Even more preferably, visible transmittance should be about 80% or greater, and still most preferably, greater than about 80%.

The technique of creating architectural glass by magnetron sputter-coating multiple layers of metal and/or metal oxides or nitrides onto float glass sheets is well known and a large number of permutations and combinations of known metals (e.g.

Ag, Au, etc.), oxides and nitrides have been attempted and reported. Such techniques may employ either planar or tubular targets, or a combination of both, in multi-target zones to achieve their desired results. Exemplary of preferred apparatus for use in this invention, and known in the art, is a magnetron sputtercoater sold by Airco Corporation. This commercially available device is disclosed in U.S.

Patent Nos. 4,356,073 and 4,422,916, respectively. The disclosures of these patents are incorporated herein by reference.

In particular, it has been known to use the aforesaid Airco sputter-coater to produce architectural glasses having a layering system, sequentially from the glass (e.g. standard float glass) outwardly, as follows:

208~92~ Si3N4/Ni:Cr/Ag/Ni:cr/si3N4 in which it has been found in practice that the Ni:Cr alloy is 80/20 by weight Ni/Cr, respectively (i.e. nichrome), and wherein the two nichrome layers are reported as being 7 thick, the Ag layer is specified as being only about 70 thic~ [except that it is stated that the silver may be about looA thick], and the Si3N4 layers are relatively thicker (e.g. 320A for the undercoat and about 4S0~ for the overcoat). In reality, because of its thinness (i.e. about 70A), the silver (Ag) layer has been found, in practice, to actually be rather semi-continuous in nature.

Figure 1 (explained more fully below) schematically illustrates a typical Airco sputter-coater as referenced above, used to produce this known Airco product.

With reference to Figure 1, Zones 1, 2, 4 and 5 are made up of silicon (Si) tubular targets ("t") and sputtering is conducted in a 100% N2 atmosphere. Zone 3 typically employs planar targets "P" and is used to create the three intermediate layers, i.e.

Ni:Cr/Ag/Ni:Cr. A 100~ argon atmosphere is employed. It was believed, and heretofore has historically been believed in the sputter-coating art, that N2 adversely affects silver during sputter-coating, and thus care was used to keep Zone 3 substantially free of N2.

While this coating achieved good "durability" (i.e. the coating was scratch resistant, wear resistant and chemically stable) and thus achieved an important measure of this characteristic as compared to pyrolytic coatings, its other characteristics, in practice, have been found to fall short of the levels of infrared reflectance and visible transmittance characteristics normally desired for low-E architectural glasses. For example, for glass at about 3mm thick, visible transmittance (Ill. C~ is usually only about 76~, Eh is about 0.20-0.22, and En is about 0.140.17. Both of these emissivity values are rather high. In addition, sheet resistance (Rs) measures a relatively high 20~9421 15.8 ohms/5q (the more acceptable value being about 10.5 or less). Thus, while durability was significantly improved and while these coatings also proved to be compatible with conventional sealants (thus overcoming this problem in the multi-pane window art which normally required "edge deletion", and is now no longer required), solar management qualities were less than optimal for many modern architectural purposes.

In addition to this Airco layer system, other coatings containing silver and/or Ni:Cr as layers for infrared reflectance and other light management purposes have been reported in the patent and scientific literature.

See, ~or example, the Fabry-Perot filters and other prior art coatings and techniques disclosed in U.S.

Patent Nos.

3,682,528 and 4,799,745 (and the prior art discussed and/or cited therein). See also the dielectric, metal sandwiches created in numerous patents including, for example, U.S.

Patent Nos. 4,179,181; 3,698,946; 3,978,273; 3,901,997; and 3,889,026 just to name a few. While such other coatings have been known or reported, it is believed that prior to our invention, none of these prior art disclosures teach or have achieved the ability to employ the highly productive sputter-coating process and, at the same time, achieve an architectural glass which not only approaches or equals the durability of pyrolytic coatings, but which also achieves excellent solar management qualities as well.

It is to be further stated that while the basic Airco apparatus and basic method of operation have been found to be quite acceptable, its productivity was found lacking. The reason for this lowered productivity is related to the assumption, which we have found to be inapplicable to our invention, that silver had to be isolated from N2 gas during sputtering.

-- 2089~2~.

In view of the above, it is apparent that there exists a need in the art for a sputter-coated layer system which approaches or equals the durability of pyrolytic coatings, but which also achieves optimal solar management characteristics, thereby overcoming the problem normally attendant the pyrolytic method. As used herein, the terms "durable" or "durability" are used in accordance with their well known meanings in the art, and reflect, in this respect, a mechanical and chemical resistance to deterioration approaching or equalling that achieved by the pyrolytic process. It is also apparent from the above that there exists a need in the art for a coating created by magnetron sputter-coating which improves upon the transmittance, emissivity and, preferably, also the sheet resistance of those coatings obtained under the Airco process as above-described, as well as improving upon the productivity of this known process.

It is a purpose of this invention to fulfill the above needs, as well as other needs in the art which will become more apparent to the skilled artisan once given the following disclosure.

SUMMARY OF THE I~V~N'1'10N Generally speaking, this invention fulfills the above-described needs in the art by providing a sputtercoated glass article comprising a glass substrate havingthereon, from the glass outwardly, a layer system comprising: an undercoat layer of Si3N4, a first layer of nickel or nickel alloy, a layer of silver, a second layer of nickel or nickel alloy, and an overcoat layer of Si3N4, and wherein when the glass substrate has a thickness of about 2mm-6mm, the coated glass preferably has a visible transmittance of at least about 78% (Ill. C), a normal emissivity (En) of less than about 0.12, and a hemispherical emissivity (Eh) of less than about 0.16.

20~2~ In certain particularly preferred embodiments the layer systems are "durable" and visible transmittance, as aforesaid, is at least about 80% or greater, and most preferably, is greater than 80%. In still further preferred embodiments, the emissivity values are about 0.13 or less for Eh and about 0.10 or less for En.

Most preferred are Eh's of about 0.12-0.13 and En's of about 0.09-0.10. In these embodiments the preferred range for sheet resistance is preferably 10.5 ohms/5q or less, and most preferably, about 9-10 ohms/Sq.

In certain further preferred embodiments of this invention the layer system consists of the above five layers and no others. In other preferred embodiments the layer system may be augmented by other known coatings which do not interfere or disturb the essential qualities of the coatings of this invention. In certain instances, these additional layers may actually enhance the essential qualities of the coatings. One such other layer system as contemplated by this invention, for example, consists essentially of a seven-layer system created by severing the silver layer into two silver layers with a nickel-based (e.g. nickel-chrome) layer in between, such that the layer system from the glass outwardly now consists essentially of:

Si3N4/Ni:Cr/Ag/Ni:Cr/Ag/Ni:Cr/Si3N4 This seven-layered system is believed to exhibit, in general, somewhat higher durability and scratch resistance characteristics as compared to the above-described fivelayered system, as well as an even higher infrared reflectance.

Further layers could, at times, include optional overcoats for further scratch resistance, or undercoats for adhesive purposes and the like. However, in the practice of this invention, the most preferred systems are the five and seven-layer systems set forth above.

208942~ It has been found in the practice of this invention that, in the preferred embodiments, and in order to achieve the desired optimal emissivity and transmittance characteristics desired, the thicknesses of the various layers are reasonably important to obtaining the desired ultimate results. In this respect, and in comparison to the known Airco five-layer system described above, it has been found important to employ an increased thickness of silver beyond the Airco prescribed 70~, on the order of about 20%-30% more, to insure, when the silver is a single layer, a substantially continuous silver layer and in all instances, to insure proper infrared reflectance properties. Thus, for this invention, rather than employing the prescribed Airco 70A silver layer, a total thickness of silver of about go-losA and preferably about 95-lOSA is employed.

For the five-layered system of this invention, e.g. having a single Ag layer, about 95A is preferred for its thickness. In those embodiments where the silver layer is severed into two layers with a nickel-based layer between them, the total thickness of both should be about 90-105A, and preferably each should be about 50A. In this respect, it is to be noted that at 50A the silver layers become somewhat discontinuous. Despite this condition, which is a problem in the Airco system, no adverse affects arise therefrom in the practice of this invention.

The nickel-based layers employed are preferably the same Ni:Cr (80/20~ nichrome employed in the Airco system. However, instead of using Airco's prescribed loA (or greater) thickness, the Ni:Cr layers are usually kept below about 7~ (e.g. about 6A or less, or a decrease of about 15-20%).

In a like manner to the total silver layer(s) employed, each of the Si3N4 layers of this invention are increased over those of the Airco system. In the preferred 20894~ ~ embodiments the increase is on the same order of magnitude as the silver increase, e.g. about 20~ or greater. Thus, in the preferred embodiments, instead of using an undercoat and overcoat of Si3N4, each in a thickness of about 320A and 450A, respectively, as Airco prescribes (the undercoat being somewhat thinner than the overcoat), in the practice of this invention an undercoat thickness of Si3N4 of at least about 400A and an overcoat thickness of at least about 540A is preferred. Most preferred is an undercoat of about 400A-425A and an overcoat of about 540~-575A. The purpose of these layers of Si3N4 is primarily for antireflection, color control, chemical resistance, scratch resistance and wear resistance.

Multi-pane windows are popular for architectural use. The layer systems of this invention have been found to be quite compatible with the conventional sealants used in making these windows, and thus overcomes this problem in the art (as above-described) to the same degree that the Airco layer system overcame this problem. Thus, in the preferred embodiments of this invention, "edge deletion" is not required.

Flying directly in the face of beliefs heretofore held in the art is the finding of this invention that, for certain preferred layer systems contemplated herein, it is not only unnecessary to isolate the silver from N2 during sputtering, but it is advantageous to conduct both silver and nickel-based sputtering together in such an environment. No substantial loss of Ag performance, in this respect, has been found to occur. This, in turn, has led to the unexpected finding that if the nickel-based layer contains chromium and that chromium is converted into a nitride during sputtering, enhancement of transmittance properties surprisingly occurs. Thus, in certain preferred embodiments of this invention, the Ni-based target is a Ni:Cr alloy and the Cr during sputtering is converted (at 2089~21 least in part3 to a nitride of Cr in the same sputter zone with the silver. This, as stated, has been found to enhance visible transmittance significantly in the ultima'e product. In addition, by producing this nitride in the same zone that silver sputter occurs, expense is decreased and productivity is ircreased.

Improved productivity and decreased costs, compared to the Airco process, are experienced in this way:

In the Airco process (and others), sputtering of Si is difficult and slow because power to the targets (e.g. the tubular targets in the Airco process~ must be increased, usually to the limit of the equipment, because the atmosphere used is 100% N2. Under the assumption that silver must not be sputtered in an N2-containing environment, and if one wished to convert the Cr to a nitride, the Ni:Cr targets would have to be put in separate zones, thus creating additional expense. The alternative would be to sputter these targets in the same N2-containing zones as the Si, but this would slow production by decreasing the number of Si targets available for use. The finding that, in the practice of this invention, it is both advantageous to create a nitride of chromium and that Nz does not adversely affect silver during sputtering, eliminates the need for the above expensive and antiproductive alternatives because the two Ni:Cr targets maynow be in the same zone as the silver target and sputtering can now be conducted in an Ar/N2 atmosphere, as opposed to a pure argon atmosphere, as heretofore believed necessary.

In this respect, in preferred embodiments the atmosphere employed is 50/50 by volume Ar/N2, although it can range widely between 0%-75% Ar and 100~-25% N2.

The Airco process teaches, as aforesaid, to sputter Si in a 100% N2 environment. While this is currently one way of conducting this phase of Si sputtering according to this invention, it has also been found that 11 208942~ under certain circumstances (e.g. small unit, low volume production), argon may be added to the N2 during Si sputtering to improve, in a known way, the rate of sputtering of Si, while still forming an acceptable amount of Si3N4.

In view of the above, this invention further fulfills the above-described needs in the art by providing a novel method for making the above-described articles which includes sputter-coating the Ni:Cr/Ag/Ni:Cr targets in the same zone while employing an atmosphere containing sufficient N2 to create a nitride of the Cr. Preferably, such an atmosphere contains by volume about 0~-75~ Ar and about 100%-25% N2. Most preferably, the volume is about 50% N2 and 50% Ar. In certain embodiments the undercoat and overcoat layer sputtering is conducted in a 100~ N2 atmosphere, while in other embodiments argon, in amounts of about 3%-50% by volume may be used with the N2 to increase productivity.

This invention will now be described with respect to certain embodiments thereof, along with reference to the accompanying illustrations, wherein:

IN THE DRAWINGS Figure 1 is a schematic illustration of the Airco apparatus which may be employed in the practice of this invention (and which is employed differently in the practice of the prior art as described above).

Figure 2 is a partial side sectional view of the prior art Airco layer system.

Figure 3 is a partial side sectional view of one embodiment of this invention.

Figure 4 is a partial side sectional view of another embodiment of this invention.

~ 2089421 DETAILED DESCRIPTION OF EMBODIMENTS OF THE INVENTION Referring to Figure l there is illustrated a conventional magnetron sputter coater such as the Airco device referenced above. In the practice of this invention five Zones 1-5 are preferably employed. (Layers are sequentially applied to the glass G as it progresses in the direction of arrow A.) Zone l contains six tubular targets t16 of silicon (Si) (e.g.

Si doped with 3-5% by weight Al for conductivity~. Zone 2 contains six more tubular targets t7 12 of the same material. In a similar fashion, Zones 4 and 5 each contain six more tubular targets t19 24 and tz5 30, respectively, of the same material.

Middle Zone 3 is preferably formed of either three planar targets P1~ (i.e. numbered 31, 16, and 33, respectively) for making a five-layered system such as shown in Figure 3 or five-six targets (i.e. of the tubular or planar type) for making a seven-layered system such as shown in Figure 4. The three-planar target system as shown can, of course, also be used to make the prior art Airco layered system illustrated in Figure 2. The target arrangement for the seven-layered system of Figure 4 in Zone 3 is a matter of choice within the level of the skilled artisan and is not shown for convenience. Assuming the availability of six target locations as in Zones 1-2 and 4-5, as is typical of such a device, one technique to employ, given the relative thinness of the three nickelbased (e.g. nichrome) layers required, is to employ targets (31) and (33) [i.e. P1 and P3~ as nickel-based targets and in place of target (16) ti.e. P2] employ a sequence of targets between P1 and P3 wherein tl3 is silver, t~4 is nickel-based, and either t15 or t~6 is silver.

In operation, the Zones l-5 are separated by appropriate curtains "C" as are the ends, thereby to be able to establish in each zone a given, controlled atmosphere, all by conventional apparatus well known in the .

20~42:~ sputter coating art. As explained above, it was heretofore believed that when silver was employed as a target in a sputter-coating operation, it was important to maintain its zone (i.e.

Zone 3) substantially free of N2 as possible.

Thus, in the known process for producing the prior art system of Figure 2, 100% argon gas was specified as the atmosphere to be used. It was also believed that sputtering of Si should take place in 100% N2, and thus this atmosphere was specified.

Using, then, this apparatus and atmospheres and by controlling speed and electrical power to the sputtering operation, accordingly, the known Airco process produced a layer system such as that illustrated in Figure 2. In this Figure 2 there is shown a glass substrate "G". Such a glass substrate was preferably a sheet of glass of about 2mm-6mm thick, usually made by the known float process and of a typical soda-lime-silica composition employed historically in this process. In Zones 1-2 a first undercoat layer 111 consisting essentially of Si3N4 was formed. Its nominal thickness was about 325A. Zones 1-2 were conducted in substantially 100% N2. Next, Zone 3 was employed, using a substantially 100% argon atmosphere to first produce a relatively thick (e.g. 7~ or greater) layer 113 of 80/20 nichrome, followed by a relatively thin (e.g. about 70A) rather discontinuous silver layer 115 whose discontinuity is illustrated by voids 117. In this same Zone 3 there was then applied to the silver another, relatively thick (e.g. 7~ or greater) 80/20 nichrome layer 119. A topcoat 121 of Si3N4 was then formed in Zones 4-5 of a thickness somewhat greater than that of undercoat 111 (e.g. about 450A thick). The less than desirable solar management qualities of this glass are mentioned above and an example thereof is reported below under the designation "Standard [Std.] Airco".

14 20~9~2 1 Figure 3 illustrates two embodiments of our invention which may be formed using the apparatus of Figure 1. As illustrated, there are five layers formed on float glass (2mm-6mm thick) substrate G. First layer 211 is Si3N4 and is formed in Zones 1-2 employing a substantially 100% N2 atmosphere. Optionally, under certain conditions (e.g.

where sizes are smaller), some argon may be introduced, for example, into Zone 2 to increase the sputtering of Si.

Next, layers 213 (213'), 215, and 219 (219') are formed in Zone 3.

In one embodiment of this invention the atmosphere employed in Zone 3 is substantially 100% argon.

In this embodiment target P1 (31) is preferably 80/20 nichrome, but may be nickel or other nickel-based alloy as desired. In order to obtain improved solar management characteristics and thus overcome the problems attendant the product of Figure 2, layer 213, which is a substantially pure metallic layer, is kept to a thickness of less than about 7A.

This is done by reducing the power to target P1 (31) compared to that employed in producing the product of Figure 2 by about 20% or more. Then, as a further improvement over the product of Figure 2, silver layer 215 produced from target P2 (16) is thickened (e.g. to about 90-105~ compared to that of layer llS, rendering layer 215 substantially continuous. This is accomplished conveniently by increasing the power to target P2 by about 20%-33% or more compare to that used for producing layer 115.

Next, another substantially pure metallic 80/20 nichrome ~or other nickel-based) layer 219 is formed in the same way as layer 213 was formed and having the same thickness thereof. This is then followed by producing in Zones 4 and 5 an overcoat layer 221 of Si3N4 in a similar way as was used to form undercoat layer 211. Layer 221 is usually somewhat thicker than layer 211, in this respect.

- 20~421 (e.g. about 540~ compared to about 400~ for layer 211~.

While at times the thicknesses of the Si3N4 undercoat and overcoat layers (e.g. 211 and 221, or 311 and 321 described below) of this invention may be the same as those in the Airco product (e.g. 111 and 121), in the preferred embodiments of this invention, each is thickened in comparison to those of the Airco product. This is accomplished by increasing the power in the sputter coater, Zones 1-2 and 4-5, approximately 20% or more to achieve these higher thicknesses. The resulting layering system has a durability approximately the same as the layer system of the product of Figure 2, with a bit less scratch resistance, but exhibits markedly superior emissivity, transmittance, and sheet resistance properties to this produce of Figure 2 (i.e. transmittances approach the 80% level and emissivity and Rs values are significantly lower).

In another, particularly preferred embodiment exemplified ~y Figure 3, a unique method is employed, using preferably the apparatus of Figure 1 and even better solar management properties are achieved. In this unique method the same basic steps are followed as described with respect to the first embodiment, except that, by flying directly in the face of heretofore held beliefs to the contrary, N2 gas is employed with argon in Zone 3 and a nickel-chromium alloy is employed as either, and preferably both, targets P1 (31) and P3 (33), such that the chromium metal is deposited as a nitride thereof in the Ni:Cr layer(s) [i.e.

as either or both layers 213' and/or 219']. In this respect, the argon to N2 ratio may vary according to need, but, generally speaking, a ratio of ~%-75% by volume of Ar to 100%-25% N2, and preferably 50%-50% Ar to N2 has been found to achieve enhanced characteristics (e.g.

transmittance and Rs) over even the first embodiment of this invention described above. In the preferred forms of this embodiment the thicknesses are maintained the same as those 20~9~21.

of the first embodi~ent. Typical power levels are reported below.

The layer system exemplified in Figure 4 may be produced as above-described either by forming the nickelbased layers as substantially pure metallic layers, or byemploying an N2-containing argon environment and employing a nickel-chromium alloy as one or more of the targets, as above-described, achieving improved results through the creation of a nitride of chromium in one or more (and preferably all) of the Ni:Cr layers. In this embodiment, furthermore, the single silver layer 215 of Figure 3 is split into two silver layers with a nickel-based layer therebetween. Thus, the embodiment of Figure 4 may be produced, using the appropriate number of targets (not shown) in Zone 3, by creating in Zones 1-2 an undercoat layer 311 of Si3N4 and in Zones 4-5 an overcoat layer 321 of Si3N4. The same thicknesses for layers 311 and 321 as used for layers 211 and 221, respectively, are preferred.

Figure 4 differs primarily from Figure 3 in that in Zone 3 there is first produced the nickel-based (i.e.

preferably 80/20 nichrome) metallic layer 313 or its nitride replacement 313' having a thickness of less than about 7A. Thereafter, a first layer of silver 315A of about 50A thick is formed, followed by another nickel-based metallic layer 314 or its nitride replacement 314' of less than about 7~ in thickness. A second layer of silver 315B having a thickness of about 50A is then formed, followed by another nickel-based metallic layer 319 or its nitride replacement 319' having a thickness of less than about 7A.

In this respect, it is to be noted that the total thickness of the combined silver layers is preferably between about 90-105A. The system is finished with overcoat 321 of Si3N4 as aforesaid.

20~9~1 As is to be expected, when in the embodiment of Figure 4 the silver layers 315A, B are each only about 50 thick, discontinuities represented by voids 317 will occur, as they do in the embodiment of Fig. 2, voids 117. Such discontinuities, while a significant detriment in Fig. 2, are not in the practice of the embodiment in Fig. 4.

The seven-layer system of Figure 4 is more durable than the prior two embodiments of Figure 3, and while it exhibits a lower transmittance than these embodiments (i.e. just slightly above the minimal 76% level), its emissivity and Rs values are better than those of the embodiments of Figure 3. The exact reasons for this are not known, but it is believed that the severance of silver into two layers, coupled with the use of an intermediate Ni-based (e.g.

Ni:Cr) layer, is believed to be substantially responsible for this. In this respect, it is believed that the intermediate Ni-based layer is a significant, functional layer which significantly helps to achieve greater durability, particularly if it is in the form of an alloy of Ni:Cr (e.g. 80/20 nichrome) wherein the chromium has been converted to a nitride thereof.

This invention will now be described with respect to certain examples as follows:

20~94~1 EXAMPLES A typical standard ("STD") Airco system exemplified by Figure 2 and the two embodiments exemplified by Figure 3 were produced using the apparatus of Figure 1.

The first embodiment of this invention is referred to as Type "A" and the second (i.e. where a nitride is formed in both layers 213' and 219') is referred to as Type "B". The targets employed were Airco tubular aluminum doped Si targets for t1 12 and t19 30- Targets P1 (31) and P3 (33) were by weight 80% Ni and 20% Cr. Target P2 (16) was silver (Ag). The glass employed was a conventional soda-limesilica float glass produced by Guardian Industries Corp.

having a thickness of 3mm (i.e. 0.123 inches). The line speed used was 345 inches/min. The pressure in Zones 1-2 and 4-5 was maintained at 2.5 x 10-3 Torr. A 100~ N2 atmosphere was employed in these zones. In Zone 3 a pressure of 2.0 x 10-3 Torr was maintained. For the "STD" Airco system and Type "A" of this invention a 100% argon atmosphere was employed. For Type "B" a 50%/50% argon/N2 atmosphere was used. The electrical supply for each target was as follows:

19 208942~.

TABLE 1 (Types A & B, Zones 1-2 & 4-53 TARGET NO. VOLTS (V) AMPS (A) POWER ~KW) 1 470 124 58.0 2 481 115 55.5 3 431 21 8.9 4 446 123 55.0 446 124 55.5 6 449 124 55.5 7 440 123 54.1 8 449 130 58.2 9 429 123 52.7 420 123 51.5 11 479 30 14.3 15 12 450 112 50.4 19 425 136 57.5 444 135 60.0 21 453 129 50.6 22 426 130 55.0 20 23 415 104 43.1 24 441 135 59.5 458 35 16.1 26 477 138 65.6 27 455 133 60.5 25 28 478 137 58.6 29 447 86 38.2 429 86 36.8 TABLE 2 (Type "A", Zone 3) 30 TARGET NO. VOLTS (V) AMPS (A) POWER (KW) 31 390 2.6 1.0 16 447 22.8 10.2 33 392 2.6 1.0 - 20~9~2~.

TABLE 3 (Type "B", Zone 3) TARGET NO. VOLTS (V) AMPS (A) POWER (KW) 31 403 5.0 2.0 5 16 446 32 14.2 33 400 5.1 2.0 Power, Amps, and Volts must be greater for same film thickness when nitride is produced.

TABLE 4 (STD, Zones 1-5) TARGET NO. - AMPS (A) POWER (XW) 1 80 2 80 3 80 4 ZONE 1 80 6 80 7 80 8 80 9 ZONE 2 80 11 80 25 12 80 _ 31 3.81.5 16 ZONE 3 18.48.1 33 3.81.5 _ _ _ _ _ _ _ _ _ _ _ _ _ 19 135 105 21 125 22 ZONE 4 125 35 23 105 2~ 25 2089~2~ TABLE 4 Cont'd.

(STD, Zones 1-5~ TARGET NO. AMPS (A) POWER fKW) 125 26 120 27 ZONE 5 50 28 110 29 110 TABLE 5 (Comparative Results) GLASS SIDE FILM SIDE (RG) (RF) LAYER SYSTEM VISIBLE TRANSMITTANCE REFLECTANCE REFLECTANCE Type A Y(%)78.75 8.42 4.08 Ill. C x .3097 .2610 .2449 2~ OBS. y .3192 .2722 .2427 a~ - 1.69 - 1.64 + 1.64 b + 1.03 - 11.57 - 14.68 Type B Y 79.57 7.56 3.75 Ill. C x .3089 .2641 .2559 2 G OBS. y .3190 .2709 .2441 a* - 1.98 - 0.40 + 3.77 b + 0.84 - 11.19 - 13.45 STD Y 76.45 8.26 5.09 Ill. C x .3078 .2626 .2723 2 G OBS. y .3163 .2801 .2857 a* - 1.19 - 3.25 - 1.76 b - 0.30 - 9.88 - 6.95 2089~21 TABLE 6 (Comparative Results) LAYER SYSTEM E ~ R _ (ohms/Sq) Type "A" 0.10 0.13 10.0 Type "B" 0.10 0.13 9.4 STD 0.16 0.20 15.8 As two other examples of this invention and in demonstration of the affect thickness of layer, particularly that of a Ni-based layer, can have upon transmittance and infrared energy reflectance, two type "B" glasses were made employing substantially identical conditions in Zones 1 and 2, and again in Zones 4 and 5 wherein, in a 100% N2 atmosphere the undercoat and overcoat Si3N4 layers were formed. The targets in Zones 1, 2, 4 and 5 were Al-doped Si Targets, P1 (31) and P3 (33) were 80/20 nichrome and P2 (16) was silver. The only difference was that in Zone 3 different power levels were employed, as reported in the following table. The glass was a 3mm thick float glass of the soda-lime-silica type.

TABLE 7 (Zone 3, 50/50 Ar/N2 Atmos.~ TARGET (KW) TRANSMITTANCE (Ill. C) P1(31) P2(16) P3(33) Rs Eh Y% a b Glass No. 1 1.5 15.0 1.5 8.3 o.ll 80.97 -1.88 +1.13 Glass No. 2 2.0 14.0 2.0 9.1 0.12 80.02 -1.71 +0.70 23 20~94~1.

As can be seen, by slightly increasing the thickness of the tw~ Ni:Cr (nitride) layers and slightly decreasing the thickness of the silver layer, infrared reflectance and transmittance values were decreased. Both of these glasses, however, are acceptable for commercial use in multi-pane architectural windows.

Further examples of type "A" glass were formed employing different power levels in the various zones, as reported below. The glass thickness was 3mm and was the same standard float glass used in Table 7 above.

24 - 2~)89~2~.

TAB~E 8 TRANSMITTANCE GLASS ( Ill . C) N0. TARGET N0. AMPS KW R_ ~_ Y% a b 11-12,19-30 85 9.6 0.13 77.11 -2.28 -1.53 4 35 31 2.9 1.1 16 10.2 33 2.9 1.1 21-3,5-12 85 10.3 0.14 78.02 -2.38 -1.56 19-30 85 4 35 31 2.6 1.0 16 10.2 33 2.6 1.0 3 " " " 10.0 0.13 77.84 -2.45 -1.66 16 10.4 4 " " " 9.8 0.13 79.41 -2.13 -0.30 19-30 105 51-3,5-12 90 " 9.8 0.13 79.20 -2.10 -0. ~0 19-30 90 4 40 6 " " " 9.8 0.13 79.48 -1.95 +0.17 19 -30 115 71-3,5-12 95 19-30 115 4 40 31,16,33 " 9.7 0.12 79.61 -1.89 +0.05 8 " " 9.7 0.13 79.78 -1.81 +0.31 19-30 120 4 40 31,16,33 " 9.8 0.13 79.95 -1.80 +0.15 101-3,5-10,12 105 9.8 0.13 79.48 -1.68 +0.66 19 -30 1~ 5 4 95 2~89~ TABLE 8 Cont'd.

TRANSMITTANCE GLASS (Ill. C) NO.TARGET NO. AMPS KW R_ ~h-- Y% a b 11 30 ..

11 " " " 9.7 0. 12 79.66 -1.74 +0.62 121-2,5-10,12 107 10.1 0. 13 79.76 -1.61 +0.68 3,4 47 11 32 19-30 125 31,33 1.0 16 10.2 -- 13*" " " 9.9 0.13 79.60 -1.62 +0.64 This glass has been found to be particularly preferred for commercial multi-pane window use.

Once given the above disclosure many other features, modifications and improvements will become 20 apparent to the skilled artisan.

Such other features, modifications and improvements are therefore considered to be a part of this invention, the scope of which is to be determined by the following claims:

26