System and method for electrically conductive membrane separation

CROSS-REFERENCE TO RELATED APPLICATIONS

0001The present application claims the benefit of U.S. Provisional Application No. 63/213,085, filed Jun. 21, 2021, the contents of which are herein incorporated by reference in its entirety.

TECHNICAL FIELD

0002This invention relates generally to the field of electrically conductive membrane separation, and more specifically to a new and useful system and method for electrically conductive membrane-based ionic separation.

BACKGROUND

0003As battery technology has become an integral part of today's society, the need for recycling of batteries, battery components, and critical battery materials is rapidly increasing. Of particular importance, are lithium (Li), cobalt (Co), manganese (Mn), and nickel (Ni). Current methods typically include grinding the important battery components (e.g., the anode and the cathode) down into a “black mass”, leaching the black mass by exposing it to strong acids (e.g., H₂SO₄and HCl), adding neutralizing agents (e.g., sodium compounds, such as sodium carbonate and sodium hydroxide), and precipitating out the valuable materials. Solvent extraction and thermal crystallization are also common process stages to enable further separation and purification of critical materials.

0004Although these methods are useful, they are suboptimal with respect to capital cost, operating cost, and environmental impact. Additionally, using chemical precipitation techniques ends up invariably contaminating the black mass such that extraction of lithium becomes difficult due to residual sodium and other chemicals. Thus, there is a need in the field of hydrometallurgical battery recycling to create a new and useful system and method for low-cost and environmentally sustainable critical materials extraction that minimizes chemical precipitation, thermal crystallization, and solvent exchange. This invention provides such a new and useful system and method.

SUMMARY

0005An aspect of the present disclosure is a system for electrically conductive membrane separation comprising: a membrane filter comprising a nanoporous structure; an electrical contact in contact with the membrane filter; and a counter electrode above a top surface of the membrane electrode. The membrane filter, via the electrical contact, and the counter electrode are configured to generate an electric field between the membrane filter and the counter electrode, to hold the membrane filter at a constant electric potential, or to flow constant current into the membrane filter. The membrane filter is configured to separate a component from a mixture solution into a permeate solution.

0006In some aspects, the system may be used in a hydrometallurgical separation process. In an aspect, mixture solution comprises a black mass leachate. For example, the component of the mixture solution may be selected from the group consisting of Co, Ni, Al, Mn, Fe, Li, Cu, Ag, Zn, ions thereof, or mixtures thereof. The mixture solution comprises an acid and may have a pH less than 4.0. In some examples, the acid is H₂SO₄. The system may be configured to recycle up to 50% of the acid. In some aspects, Li is the component separated in the permeate solution. In an aspect, the components not in the permeate solution exit the system in a retentate solution. The system may be configured to recycle the retentate solution. In other aspects, the retentate solution may pass through another membrane filter for separation of one or more additional components of the mixture solution. In an aspect of the disclosure, the membrane filter comprises silicon. The membrane filter may have pore sizes ranging from 1 nm to 500 nm, 1 nm to 1,000 nm, or 500 nm to 1,000 nm.

0007The system may contain a membrane filter in a cross-flow or dead-end configuration. In some examples, a flow-through configuration may be used with electro-extraction, where components aren't rejected at the membrane surface (i.e. everything flows through), but target components are selectively immobilized within the membrane filter pores via electrochemical reduction or oxidation. The system may further include a pressure cell configured to house the membrane filter and counter electrode. The pressure cell may further include an opening configured to receive the electrical contact. The pressure cell may be operable to operate at pressures up to 3000 psi. In various aspects, the system may include modules for size filtration, charge filtration, electro-filtration, electro-extraction, or combinations thereof. In an aspect, the system may be configured for electro-filtration and the electric field is applied between the membrane filter and the counter electrode. In this aspect, the membrane filter may have pore sizes of 1 nm to 10 nm, 1 nm to 100 nm, 10 nm to 50 nm, or 50 nm to 100 nm and the system may be configured to operate at a pressure greater than 700 psi. In another aspect, the system may be configured for electro-extraction and the membrane filter is held at a constant electric potential or has a constant current driven through the membrane filter. For example, the pore walls may deliver an electric current to components (e.g. ions) within close proximity in the mixture solution, resulting in the ions being reduced. In this aspect, the membrane filter may have pore sizes of 50 nm to 100 nm, 100 nm to 500 nm, or 500 nm to 1,000 nm and the system may be configured to operate at a pressure less than 500 psi. In an aspect, the system may be configured for size and charge selective filtration.

0008In some aspects of the present disclosure, the system is a cross-flow configuration. In various aspects, the system may include modules for size filtration, charge filtration, electro-filtration, electro-extraction, or combinations thereof. The system may be configured for electro-filtration and the electric field is applied between the membrane and counter electrode. In an aspect, the system is configured for size and charge selective filtration.

0009The electric field is adjustable to select for the desired component. For example, 0.1 V to 5 V may be applied to the electrical contact and counter electrode to generate the electric field, the constant electric potential, or the constant current in the membrane filter.

0010Further aspects of the present disclosure include a method for electrically conductive membrane separation from a mixture solution comprising: generating an electric field above or within a membrane filter, holding the membrane filter at a constant electric potential, or flowing constant current into the membrane filter; feeding a mixture solution through the membrane nanofiltration system; and separating a component from the mixture solution into a permeate solution. For example, holding the membrane filter at a constant electric potential or flowing constant current into the membrane filter may include driving/running an electrochemically reducing or oxidizing current through the membrane filter.

0011The method may further include: providing a membrane nanofiltration system comprising: a membrane filter comprising a nanoporous structure; an electrical contact in contact with the membrane filter; and a counter electrode above a top surface of the membrane electrode.

0012In some aspects, the mixture solution comprises a black mass leachate. The component of the mixture solution to be separated may be selected from the group consisting of ions of Co, Ni, Al, Mn, Fe, Li, Cu, Ag, Zn, ions thereof, or mixtures thereof. The mixture solution may include an acid and the mixture solution may have a pH less than 4.0. For example, the acid is H₂SO₄. In some aspects, the method further includes recycling up to 50% of the acid. In an aspect, Li is the component in the permeate solution.

0013In various aspects, the method may further include removing a retentate solution comprising the components not in the permeate solution. The electric field may be configured to separate components with lower charges into the permeate solution and components with higher charges into the retentate solution. For example, the permeate solution may include components with an ionic charge of 1+ or lower and the retentate solution may include components with an ionic charge of 2+ or greater. In some aspects, the method may further include recycling the retentate solution back to the leaching process. In additional aspects, the method may further include separating a second component from the recycled mixture solution. In yet further aspects, the method may further include passing the retentate solution through the one or more additional membrane filters to separate one or more additional components of the mixture solution.

0014In some aspects, the membrane filter comprises silicon and may have pore sizes ranging from 1 nm to 500 nm or 500 nm to 1,000 nm. The system may be a flow-through, dead-end configuration, and/or a cross-flow configuration. The component may be separated from the mixture solution via electro-filtration and the electric field is above the membrane filter and/or the component (or additional components) may be separated from the mixture solution via electro-extraction and electrochemically oxidizing/reducing current is conducted through the membrane filter such that the membrane filter is held at a constant electric potential or has a constant current driven through the membrane filter . In other or additional aspects, the component may be separated from the mixture solution via size and charge selective filtration and the electric field is 0 V/m.

0015In some aspects, the method may further include adjusting the electric field to select for the desired component. For example, 0.1 V to 5 V may be applied to the electrical contact connected to the membrane filter and the counter electrode to generate the electric field, electric potential, or current in the membrane filter.

0016In an aspect, one or more components of the mixture not in the permeate solution may be retained within the pores of the membrane filter by electrochemical oxidation or reduction, chemical or physical affinity, adsorption, or absorption. The method may further include reversing the polarity of the electric potential or direction of the current and passing a pure draw solution through the membrane filter. In some aspects, the pure draw solution comprises water or sulfuric acid. In some aspects, the method further includes leaching the one or more components retained in the membrane filter into a pure product stream comprising the pure draw solution and the one or more components. The pure draw solution may have a volume that is 1% to 50% of the mixture solution volume, generating a concentrated solution of the one or more components.

0017In some aspects, the method may further comprise precipitating the component from the permeate solution, the retentate solution, the pure product stream, or the pure draw solution.

0018Another aspect of the present disclosure is a method for electrically conductive membrane separation from a mixture solution comprising: holding a membrane filter at a constant electric potential or driving a constant current through the membrane filter; feeding a mixture solution through the membrane filter; and separating a component from the mixture solution into a permeate solution.

0019Yet another aspect of the present disclosure is a method for electrically conductive membrane separation from a mixture solution comprising: generating an electric field orthogonal or perpendicular to a membrane filter; feeding a mixture solution through the membrane; and separating a component from the mixture solution into a permeate solution.

0020An even further aspect of the present disclosure is a method for electrically conductive membrane separation from a mixture solution comprising: applying an electric field orthogonal or perpendicular to a membrane filter; feeding a mixture solution through the membrane; and separating a component from the mixture solution into a permeate solution.

0021In an aspect, the solution comprises a monovalent ion component and polyvalent ion component, and the monovalent ion component and polyvalent ion component are filtered differently based on their charge. In another aspect, the solution comprises a first polyvalent ion component and second polyvalent ion component, and the first and second polyvalent ion components comprise different charges. In this aspect, the first polyvalent ion component and second polyvalent ion component are filtered differently based on their charge.

0022In some aspects, the method further includes isolating the monovalent ion component and/or isolating the polyvalent ion component.

BRIEF DESCRIPTION OF THE FIGURES

0023<figref idref="DRAWINGS">FIG. <b>1</b>A</figref> is a schematic of one example system implementing size and charge selective filtration in a dead-end configuration.

0024<figref idref="DRAWINGS">FIG. <b>1</b>B</figref> is a schematic of one example system implementing size and charge selective filtration in a cross-flow configuration.

0025<figref idref="DRAWINGS">FIG. <b>2</b>A</figref> is a schematic of one example system implementing electro-filtration in a dead-end configuration.

0026<figref idref="DRAWINGS">FIG. <b>2</b>B</figref> is a schematic of one example system implementing electro-filtration in a cross-flow configuration.

0027<figref idref="DRAWINGS">FIG. <b>3</b>A</figref> is a schematic of one example system implementing a first step in electro-extraction in a flow-through configuration.

0028<figref idref="DRAWINGS">FIG. <b>3</b>B</figref> is a schematic of one example system implementing a second step in electro-extraction in a flow-through configuration.

0029<figref idref="DRAWINGS">FIG. <b>4</b>A</figref> is one example membrane filtration system with an electrified membrane filter in a pressure cell.

0030<figref idref="DRAWINGS">FIG. <b>4</b>B</figref> is one example membrane filtration system with an electrified membrane filter in a pressure cell.

0031<figref idref="DRAWINGS">FIG. <b>4</b>C</figref> shows how a ring terminal connects to a counter electrode, in one example.

0032<figref idref="DRAWINGS">FIG. <b>4</b>D</figref> shows the distance between the counter electrode and the membrane filter, in one example.

0033<figref idref="DRAWINGS">FIG. <b>4</b>E</figref> shows a cross-section of a bottom portion of a pressure cell in an example membrane filtration system.

0034<figref idref="DRAWINGS">FIG. <b>4</b>F</figref> shows an example spring-loaded electrical contact in an example membrane filtration system.

0035<figref idref="DRAWINGS">FIG. <b>4</b>G</figref>, <figref idref="DRAWINGS">FIG. <b>4</b>H</figref>, and <figref idref="DRAWINGS">FIG. <b>41</b></figref> show portions of an example membrane filtration system being assembled or disassembled.

0036<figref idref="DRAWINGS">FIG. <b>5</b>A</figref>, <figref idref="DRAWINGS">FIG. <b>5</b>B</figref>, <figref idref="DRAWINGS">FIG. <b>5</b>C</figref>, <figref idref="DRAWINGS">FIG. <b>5</b>D</figref>, <figref idref="DRAWINGS">FIG. <b>5</b>E</figref>, and <figref idref="DRAWINGS">FIG. <b>5</b>F</figref> show portions of an example membrane filtration system with an electrified membrane filter in a stainless-steel pressure cell.

0037<figref idref="DRAWINGS">FIG. <b>5</b>G</figref> shows an example membrane filtration system with an electrified membrane filter in a polycarbonate pressure cell.

0038<figref idref="DRAWINGS">FIG. <b>5</b>H</figref> shows testing of the example membrane filtration system of <figref idref="DRAWINGS">FIGS. <b>5</b>A-<b>5</b>F</figref>.

0039<figref idref="DRAWINGS">FIG. <b>6</b>A</figref> is an exploded view of an example membrane module.

0040<figref idref="DRAWINGS">FIG. <b>6</b>B</figref> is an example membrane module with three membrane filter plates.

0041<figref idref="DRAWINGS">FIG. <b>6</b>C</figref> and <figref idref="DRAWINGS">FIG. <b>6</b>D</figref> show feed solution pumped into a manifold and distributed across several membrane filters in parallel and then collected into another manifold before being routed out of the module.

0042<figref idref="DRAWINGS">FIG. <b>6</b>E</figref> and <figref idref="DRAWINGS">FIG. <b>6</b>F</figref> show permeate passing through a membrane filter into channels and traveling outward toward a circumferential groove that collects into a common drain.

0043<figref idref="DRAWINGS">FIG. <b>7</b>A</figref> shows the top side of an example membrane filter plate.

0044<figref idref="DRAWINGS">FIG. <b>7</b>B</figref> shows the bottom side of an example membrane filter plate.

0045<figref idref="DRAWINGS">FIG. <b>7</b>C</figref> is a side view of an example membrane filter plate.

0046<figref idref="DRAWINGS">FIG. <b>8</b></figref> is a flowchart representation of an example method.

0047<figref idref="DRAWINGS">FIG. <b>9</b>A</figref> is a flowchart representation of an alternative example method for electro-filtration.

0048<figref idref="DRAWINGS">FIG. <b>9</b>B</figref> is a flowchart representation of an alternative example method for electro-extraction.

0049<figref idref="DRAWINGS">FIG. <b>10</b></figref> is a process flowchart of another example method.

0050<figref idref="DRAWINGS">FIG. <b>11</b></figref> is a process flowchart of an additional example method.

0051<figref idref="DRAWINGS">FIG. <b>12</b></figref> shows the difference in the transport of an ionic species through an example membrane filter when the membrane is electrified (1 V) and not electrified (0 V).

DETAILED DESCRIPTION

0052The following description of the embodiments of the invention is not intended to limit the invention to these embodiments but rather to enable a person skilled in the art to make and use this invention.

Overview

0053A system and method for a nanofiltration method includes: a membrane filter, comprising a nanoporous structure; and one or more electrodes configured to apply an electric potential to the membrane filter, or drive an electric current into the membrane filter. For example, the system may include an electrical contact in contact with the membrane filter and a counter electrode, and the system may be configured to generate an electric field between the membrane filter and the counter electrode, to hold the membrane filter at a constant electric potential, or to flow constant current into the membrane filter. In an example, the system may be operable to separate a component from a mixture solution when the mixture solution has a pH of 5.0 or less. For example, the system may be operable at a pH of 2 to 5, less than 5, less than 4, less than 3, less than 2, or less than 1. In some examples, the membrane filter may further include a coating, comprising a functional coating within and around the porous structure of the membrane filter. In an embodiment, the system and method further includes feeding a mixture solution through the membrane filter, thereby separating a desired component (i.e. compound/compounds/ion) from the mixture solution. The component separated from the mixture solution may be selected from Co, Ni, Al, Mn, Fe, Li, Cu, Ag, Zn, ions thereof, or mixtures thereof. Non-limiting examples of ions include Co²⁺, Co³⁺, Ni²⁺, Al³⁺, Mn²⁺, Fe²⁺, Fe³⁺, Li+, Cu²⁺, Ag⁺, Zn²⁺, and combinations and variations thereof. The system and method function to build and employ a membrane filtration system uniquely able to separate nanoscale compounds at a low pH, using size, charge, and/or compound/membrane interactions. The system and method may enable multiple variants of separation, wherein in a first method of separation, the mixture is separated by driving it through the membrane system under high pressure (e.g., via a hydraulic pressurization of the feed mixture solution) with small pore sizes in the membrane filter (e.g. less than 100 nm). The system and method may also enable different forms of separation, wherein components are separated by diffusion through, or across, the membrane, driven by a concentration gradient (or other type of gradient). In an embodiment, the system and method may perform separation using electro-filtration, using high pressure and small pore size in an electrified membrane to separate a desired compound/compounds/ion from the mixture solution. In another embodiment, the system and method may perform separation using electroplating, using low pressure and large pore size in an electrified membrane to separate a desired compound/compounds/ion from the mixture solution.

0054The system and method may be generally applicable to any field of nanoscale (or larger) separation and/or extraction.

0055The system and method may be applicable for the extraction of small charged ions, elements, and compounds from a mixture, wherein the system and method may be particularly useful for molecular (i.e., nanometer scale) extraction at lower pH (i.e., less than pH 5.0). The system and method may further enable nanoscale extraction at pH less than 2.0 or less than 1.0. The system and method may also be applicable for atomic scale (i.e., order of angstroms) extraction (e.g., element or ion extraction), wherein the system and method may be particularly useful for atomic extractions at low pH (i.e., less than pH 5.0) or very low pH (i.e., less than pH 2.0 or 1.0). In various examples, the system may be operable at a pH ranging from 0 to 5, 0 to 4, 0 to 3, 0 to 1, 0.5 to 5, 0.5 to 4, 0.5 to 3, 0.5 to 2, 0.5 to 1, 0.1 to 5, 0.1 to 4, 0.5 to 3, 0.1 to 2, 0.1 to 1, 1 to 5, 1 to 4, 1 to 3, 1 to 2, 2 to 4, or 2 to 5. In some examples, the system may be operable at a pH of 2 to 5, less than 5, less than 4, less than 3, less than 2, or less than 1. This compound extraction can be particularly useful in the field of hydrometallurgy wherein small compounds and elements may be filtered and/or extracted without the requirement for chemical precipitation, chemical pH neutralization techniques, liquid-liquid extraction (solvent exchange), thermal distillation, or thermal crystallization.

0056The system and method may be particularly applicable for material extraction from a battery leachate solution (e.g., as applied to battery recycling). That is, the system and method may be applicable for extraction of typical battery compounds (e.g., lithium carbonate, lithium hydroxide, cobalt sulfate, nickel sulfate, manganese oxide) from a battery or battery leachate solution (e.g., black mass leachate). In some examples, major black mass components may include but are not limited to Al, Co, Cu, Fe, Li, Ni, Ag, Zn, Mn, graphite, F, P, and ions thereof.

0057The system and method may provide a number of potential benefits. The system and method are not limited to always providing such benefits, and are presented only as exemplary representations for how the system and method may be put to use. The list of benefits is not intended to be exhaustive and other benefits may additionally or alternatively exist.

0058Some benefits of the system and method include a reduced system complexity and/or a reduced number of process stages/footprint due to being able to recover multiple components of a mixture solution without further difficult processing steps and/or the ability to recycle one or more components of the system. This may lead to reduced capital and operating cost and reduced usage of chemicals and heat.

0059One potential benefit of the system and method is that the system and method enable membrane separation in acidic conditions.

0060Additionally, the system and method may provide the potential benefit of being used for multiple forms of membrane separation. For example, in some implementations, the system and method may enable utilization of membrane separation to separate by molecular/atomic/ionic size, charge, and/or membrane interaction.

0061As part of battery recycling implementation, the system and method may enable separation and extraction of valuable metals with exceptionally high selectivity and/or yield. This potentially provides a significant benefit over current chemical precipitation/solvent extraction/thermal crystallization techniques that end up contaminating battery mixtures and requiring high capital and operational cost, thereby limiting extraction.

0062As part of a battery recycling implementation, the system and method may further provide the potential benefit of a means for lithium extraction. Using current means of battery recycling, the battery mixtures typically become too contaminated for most extraction techniques to be applied at a reasonable cost of resources and time. Specifically, for battery chemistries such as lithium-iron-phosphate, wherein lithium is the only high-value material, recycling is particularly challenging from an economics standpoint. The system and method may be especially beneficial in such cases.

System

0063A system for a low pH capable nanofiltration, includes a membrane filter comprising a porous structure with pore sizes ranging from the order of 1 nanometer to the order of 1,000 nanometers. In an embodiment, the system includes at least one electrode operable to drive an electric current into the membrane filter, or hold the filter at a constant electric potential. For example, the system may be configured to generate an electric field between the membrane filter and the counter electrode, to hold the membrane filter at a constant electric potential, or to flow constant current into the membrane filter. In other embodiments, the membrane filter may include a coating, comprising a functional coating within and around the porous structure of the membrane filter. The system functions as a membrane particularly suited for filtration of nanometer or atomic scale compounds at low pH (i.e., below pH 5.0), or very low pH (i.e., below pH 2.0). In various examples, the system is operable at a pH ranging from 0 to 5, 0 to 4, 0 to 3, 0 to 1, 0.5 to 5, 0.5 to 4, 0.5 to 3, 0.5 to 2, 0.5 to 1, 0.1 to 5, 0.1 to 4, 0.5 to 3, 0.1 to 2, 0.1 to 1, 1 to 5, 1 to 4, 1 to 3, 1 to 2, 2 to 5, less than 5, less than 4, less than 3, less than 2, or less than 1. In other examples, the system may operate at a neutral pH ranging from 6 to 8 or operate at a basic pH ranging from 8 to 14. In at least one example, the system may be used with mixture solutions comprising sulfuric acid. In some embodiments, the system may be operable to recycle at least a portion of the sulfuric acid. As shown in <figref idref="DRAWINGS">FIGS. <b>1</b>A-<b>3</b>B</figref>, the system and/or membrane filter may have multiple variations and may be implemented to separate by size, charge, and/or through membrane/compound interaction(s) (e.g., membrane sorption, electrochemical reduction and/or oxidation, or substrate binding). <figref idref="DRAWINGS">FIGS. <b>4</b>A-<b>6</b>C</figref> show example membrane nanofiltration systems.

0064The system may be particularly useful for filtration of battery metals and chemicals from a battery leachate solution (e.g., as part of a method for battery recycling). For example, the system may be implemented for lithium (Li) extraction from battery solution (e.g., black mass leachate solution). As desired, the system may be implemented for filtration of other battery metals or chemicals, such as: cobalt (Co), manganese (Mn), and nickel (Ni). Additionally or alternatively, the system may be implemented for filtration of other chemicals or minerals in use today, or used in future batteries.

0065The system may include a membrane filter. The membrane filter functions as the primary filtration body, wherein the membrane filter comprises a porous body. That is, the membrane filter comprises a porous structure, such that fluids may flow through the membrane filter wherein, dependent on implementation, certain compounds (or elements/ions) within the fluid selectively pass through the membrane filter at differing rates.

0066As a porous body, the membrane filter may be implemented with any desired porosity. For general filtration purposes the membrane filter may be implemented such that it has a desired porosity between 1% to 5%, 5% to 10%, 10% to 20%, 20% to 30%, 30% to 40%, or 40% to 50%. Alternatively, the membrane filter may have a porosity less than or greater than the suggested range. For example, in an industrial high flow, high throughput implementation, the membrane filter may comprise a thick column (e.g., 20 μm to 1 cm thickness) with a high porosity (e.g., 70% porosity).

0067Pores within and through the membrane filter may vary dependent on implementation. Unless stated otherwise, as used herein, for simplicity of explanation, pores within the membrane filter are described as relatively cylindrical and pore size refers to the approximate diameter of the pore. In actuality, pores within the membrane filter may have any shape, and the pore size refers to the size of some generic non-charged globular molecule or spherical non-charged particle that may travel through the pore at a reasonable rate. In some variations, particularly for larger molecule filtration (e.g., polymers), the pore shape may be controlled to match the shape of a complex shaped molecule. In these variations, discussion of pore sizes may be ignored and the relative permeability of molecules will be discussed instead.

0068The membrane filter may generally have pores of approximately nanometer length or larger. In some examples, the pores may extend through the membrane filter such that there is a path for at least one component of a mixture solution to pass through the pores in the membrane filter from a top side to a bottom side. In various embodiments, the membrane filter pore size may be approximately between 1 nm to 10 nm, 1 nm to 100 nm, 10 nm to 50 nm, 10 nm to 100 nm, 50 nm to 100 nm, or 00 nm to 500 nm, or 500 nm to 1,000 nm. In some examples, the pore size of the membrane filter may be 1 nm to 10 nm, 10 nm to 20 nm, 20 nm to 30 nm, 30 nm to 40 nm, 40 nm to 50 nm, 50 nm to 60 nm, 60 nm to 70 nm, 70 nm to 80 nm, 80 nm to 90 nm, or 90 nm to 100 nm. In some embodiments, the pore size may be considered to be small if it is less than 100 nm, less than 50 nm, or less than 10 nm. In other examples, the pore size may be approximately between 100 nm to 150 nm, 150 nm to 200 nm, 200 nm to 250 nm, 250 nm to 300 nm, 300 nm to 350 nm, 350 nm to 400 nm, 400 nm to 450 nm, 450 nm to 500 nm, 500 nm to 550 nm, 550 nm to 600 nm, 600 nm to 650 nm, 650 nm to 700 nm, 700 nm to 750 nm, 750 nm to 800 nm, 800 nm to 850 nm, 850 nm to 900 nm, 900 nm to 950 nm, or 950 nm to 1,000 nm. In some embodiments, the pore size may be considered to be large if it is greater than 100 nm. Alternatively, the membrane filter pore sizes may be larger or smaller (e.g., 1 Å, 1 μm, 10 μm, etc.). Dependent on implementation, the variance and distribution of the membrane filter pore size may be controlled.

0069As is common in many filtration implementations, the pore sizes may be relatively similar. That is the pore size may have a low variance. For example, the pore size variance may be approximately 1% of the pore size. Generally, the pore size variance may be in any range. For example, in one implementation the pore size variance is approximately 1% to 5% of the pore size; in another implementation the pore size variance is approximately 5% to 10% of the pore size; in another implementation the pore size variance is approximately 10% to 20% of the pore size; in another implementation the pore size variance is approximately 20% to 30% of the pore size; in another implementation the pore size variance is approximately 30% to 40% of the pore size; in another implementation the pore size variance is approximately 40% to 50% of the pore size; in another implementation the pore size variance is approximately 50% to 60% of the pore size; in another implementation the pore size variance is approximately 60% to 70% of the pore size; in another implementation the pore size variance is approximately 70% to 80% of the pore size; in another implementation the pore size variance is approximately 80% to 90% of the pore size; in another implementation the pore size variance is approximately 90% to 100% of the pore size, etc.

0070The membrane filter thickness may vary, wherein the thickness may be chosen to meet a particular filtration implementation. For typical implementations, the membrane filter may commonly have a thickness in the range of 10 μm to 50 μm, 50 μm to 100 μm, 100 μm to 150 μm, 150 μm to 200 μm, 200 μm to 250 μm, 250 μm to 300 μm, 300 μm to 350 μm, 350 μm to 400 μm, 400 μm to 450 μm, 450 μm to 500 μm, 500 μm to 1000 μm, or 1000 μm to 10,000 μm. In at least one example, the membrane filter may have a thickness of 280 μm. Alternatively, the membrane filter thickness may be less. For example, in one implementation, the membrane filter thickness is approximately 1 μm thick. Generally, the membrane filter thickness is only limited by mechanical constraints (e.g., the membrane should be sufficiently thick such that it doesn't break or buckle while filtering) and the membrane pore size (i.e., the membrane thickness must be sufficiently large to incorporate a desired pore size, or pore size range) and porosity. In the case where the membrane is thin, it may be supported by a mechanically stable thick layer with larger pore size. In this embodiment, the thin membrane and the thick supporting layer may be monolithic (part of a continuous piece of material). In some embodiments, the membrane filter may be a flat disc, with a diameter of 1 in to 1.5 in, 1.5 in to 2 in, 2 in to 2.5 in, 2.5 in to 3 in, 3 in to 3.5 in, or 3.5 in to 4 in. In at least one example, the membrane filter may have a diameter of 2 inches. In at least one example, the membrane filter may have a diameter of 0.4 meters.

0071The membrane filter may be composed of an inorganic element or compound (or compounds). In some embodiments, the membrane filter is composed of a conductive material. In one variation, the inorganic compound membrane filter comprises a body composed primarily of silicon. In one example, the silicon body comprises a monolithic piece of silicon, or alternatively nanoporous silicon. For example, membrane filter may be a silicon wafer that has been modified to have pores ranging from 1 nm to 500 nm, or 1 nm to 1,000 nm. Alternatively, the silicon body may include multiple pieces (e.g., layers of silicon).

0072In an alternative variation, the membrane filter is composed of an organic compound (or compounds). In one variation, the organic compound membrane filter comprises a body composed of a polymer. Examples of the polymer material may include: polyamide, polysulfone, polycarbonate, PTFE, and/or polyimide. In some variations, the membrane filter may comprise multiple layers of the same polymer, or a composite of multiple layers of different polymers. In this variation, the polymeric membrane could be made electrically conductive via functionalization of the membrane with electrically conductive materials.

0073As per the intended system implementation, the membrane filter may be enabled for one or more types of filtration. Dependent on implementation, the membrane filter may be structured such that it may filter based on size, charge, electrochemical reduction and oxidation potentials, and/or through membrane/compound interaction(s). In some examples, the system may be configured for size and charge selective filtration, electro-filtration, or electro-extraction. Additionally or alternatively, the membrane filter may be enabled for filtration based on hydrophobicity, chirality, solubility, redox potential, coordination number and/or some other molecule/compound property.

0074In some variations, the membrane filter may comprise a structure to enable size filtration. In these variations, the membrane filter may comprise pore size “tuned” to allow one or more type(s) of compounds/molecules/atoms/ions to permeate, while retaining all other species. That is, the membrane filter is constructed with a desired porosity and desired pore size to enable filtration and/or separation of compounds/molecules/atoms/ions dependent on the effective size of those entities. For example, for a black mass leachate solution, Li may pass through the membrane filter, wherein Co, Ni, and Mn are retained. This size exclusion may not be based only atomic mass/size, but may also be based on additional coordination effects (e.g., hydration and ionic charge), which can result in different effective sizes for the filtered compounds.

0075In some variations, the membrane filter may comprise a structure that enables filtration by electrical charge. In these variations, the membrane filter may be composed of material that can carry charge or is conductive (e.g., silicon). That is, the membrane filter is constructed with a desired conductivity, or range of conductivities to enable filtration and/or separation of compounds/molecules/ions dependent on an effective charge. In some examples, the membrane filter may have a resistivity ranging from 100 ohm.cm to 0.001 ohm.cm, 100 ohm.cm to 50 ohm.cm, 50 ohm.cm to 10 ohm.cm, 10 ohm.cm to 1 ohm.cm, 1 ohm.cm to 0.1 ohm.cm, 0.1 ohm.cm to 0.01 ohm.cm, or 0.01 ohm.cm to 0.001 ohm.cm. For charge separation, the system may further include a current source, or sources, and may include a current sink, or sinks; wherein a desired current or currents is driven through or formed above the membrane filter, or a constant electric potential is applied to the membrane filter.

0076The membrane filter may be implemented with different directional flows. In addition to flows directly through the membrane, the membrane filter may be used with flows parallel to the membrane surface and/or in a direction askew to the membrane. The system may be configured in a flow-through configuration, dead-end configuration, or a cross-flow configuration. In a flow-through or dead-end configuration, the mixture solution may be fed downward through the top side of the membrane filter (e.g. perpendicular to the membrane filter) and the permeate solution is collected below the membrane filter. <figref idref="DRAWINGS">FIGS. <b>1</b>A, <b>2</b>A, and <b>3</b>A</figref> show example dead-end/flow-through configurations. In a cross-flow configuration, the mixture solution may be fed across the top side of the membrane filter (e.g parallel to the membrane filter) such that the permeate solution is collected below the membrane filter and the retentate solution remains above the membrane filter. <figref idref="DRAWINGS">FIGS. <b>1</b>B and <b>2</b>B</figref> show example cross-flow configurations. In some embodiments, the separation may be operated in a continuous mode and/or allow for recycling of one or more components of the mixture solution.

0077The system may use size filtration, electro-filtration, electro-extraction, or combinations thereof to separate at least one component from the mixture solution. In some embodiments, such as in electro-filtration as seen in <figref idref="DRAWINGS">FIGS. <b>2</b>A and <b>2</b>B</figref>, an electrical contact may be placed such that it makes electrical contact with the membrane filter and a counter electrode may be placed above the surface of the membrane filter. In an example, the electrified membrane filter may be a cathode and the counter electrode may be an anode. When a voltage is applied between the electrified membrane filter and the counter electrode, an electric field is generated above the top surface of the membrane filter such that the electric field prevents higher charged components (compounds/molecules/atoms/ions) from passing through the pores while components (compounds/molecules/atoms/ions) with lower charge may pass through the pores. In other words, the electric field is configured to separate components with lower charges into the permeate solution and components with higher charges into the retentate solution. In other examples, the electric field may act to “pull” ions through the membrane, where higher charges would be more likely to be pulled through into the permeate solution. In some embodiments, the permeate solution comprises components with an ionic charge of 1+ or lower and the retentate solution comprises components with an ionic charge of 2+ or greater. For example, for a black mass leachate solution, the electric field may allow Li to pass through the membrane filter, while Co, Ni, Mn, etc. are retained above the membrane filter. In some embodiments, the separation of one component and the retention of other components in the mixture solution may also be based on additional coordination effects (e.g., size, polarity, hydration), which can result in different effective permeabilities for the filtered compounds.

0078Referring to <figref idref="DRAWINGS">FIG. <b>2</b>A</figref>, in some embodiments, the system may be configured for electro-filtration in a dead-end configuration. <figref idref="DRAWINGS">FIG. <b>2</b>A</figref> shows a feed solution (i.e. mixture solution) entering the membrane filter from the top side and passing through the electric field between the top surface of the electrified membrane filter and the counter electrode. MX represents an ion dissolved in an aqueous solution, with ionic charge x. The components with lower charges (represented generically as M+) pass through the pores of the membrane filter as the permeate solution while components with higher charges (represented generically as M²⁺ and M³⁺) are retained in the electric field above the membrane filter. In some examples, uncharged components may pass through the pores into the permeate solution or may be retained above the membrane filter due to size selection of the pore size. In some embodiments, the strength of the electric field may be adjusted to select for different charged components.

0079Referring back to <figref idref="DRAWINGS">FIG. <b>2</b>B</figref>, in some embodiments, the system may be configured for electro-filtration in a cross-flow configuration. <figref idref="DRAWINGS">FIG. <b>2</b>B</figref> shows a feed solution (i.e. mixture solution) flowing across the top of the membrane filter and passing through the electric field between the top surface of the electrified membrane filter and the counter electrode. The components with lower charges (represented generically as M⁺) pass through the pores of the membrane filter as the permeate solution while components with higher charges (represented generically as M²⁺ and M³⁺) are retained in the electric field above the membrane filter and exit as a retentate solution. In some examples, uncharged components may pass through the pores into the permeate solution or may be retained above the membrane filter due to size selection of the pore size. In some embodiments, the strength of the electric field may be adjusted to select for different charged components.

0080In some embodiments, the membrane filter may have small pores when used for electro-filtration with the electric field at the surface of the membrane filter. For example, the membrane filter may have pore sizes of 1 nm to 10 nm, 10 nm to 20 nm, 20 nm to 30 nm, 30 nm to 40 nm, 40 nm to 50 nm, 50 nm to 60 nm, 60 nm to 70 nm, 70 nm to 80 nm, 80 nm to 90 nm, or 90 nm to 100 nm when used with electro-filtration.

0081In other embodiments, such as in electro-extraction (e.g. electroplating) as seen in <figref idref="DRAWINGS">FIGS. <b>3</b>A and <b>3</b>B</figref>, an electrical contact may be placed on the membrane filter and a counter electrode may be placed above the membrane filter to hold the membrane filter at a constant electric potential or to flow constant current into the membrane filter such that the pore walls within the membrane filter are charged to attract and electrochemically reduce or oxidize certain components (compounds/molecules/atoms/ions), fixing them to the pore wall while letting other components pass through. In some embodiments, for electro-extraction, the membrane filter is held at a constant electric potential or has a constant current driven through the membrane filter. In some examples, the potential and/or current may fluctuate. Therefore, as used herein, a “constant” electric potential or “constant” current may be controlled to be within a threshold of a set parameter (e.g. ±10% of the desired constant electrical potential or constant current). The electro-extraction may be used in a constant-flow system or a batch pressure cell.

0082The specific component(s) may be fixed within the pores of the membrane filter, either at the pore wall surface or absorbed within the membrane material. The initial feed solution (mixture solution) may then be replaced with pure solution (e.g., water or sulfuric acid), into which the specific component(s) of interest is released. In this example, the polarity of the electric field may be reversed to aid in releasing the components retained in the membrane filter. In this example, the total volume of the pure solution passed through the membrane may be much less (1-50%) of the volume of the mixture solution from which the component was extracted, resulting in a more concentrated solution of the target component. In another example, a mixture solution may flow across the membrane filter, where multiple components travel freely through the membrane but only one (or multiple specified) component(s) of the mixture solution is/are retained by the membrane filter. Then, a pure solution is passed through (optionally with a reversed polarity electric field) and the specified retained component(s) are released into it. The components retained within the membrane filter and/or passing through the membrane filter may be selected from Li, Co, Ni, Al, Mn, Fe, Cu, Al, Ag, Zn, etc. In one example, as seen in <figref idref="DRAWINGS">FIG. <b>3</b>A</figref>, a feed solution (e.g. a battery leachate solution) may pass through the membrane filter where some components (compounds/molecules/atoms/ions) such as Co, Ni, Al, Mn, Fe, Cu, Al, Ag, Zn, etc. may be retained within the pores of the membrane filter while other components such as Li may pass through the pores. In some embodiments, as seen in <figref idref="DRAWINGS">FIG. <b>3</b>B</figref>, the polarity of the electric field may be reversed and a pure draw solution (e.g. water) may be passed through the system to extract the components (compounds/molecules/atoms/ions) trapped in the pores of the membrane filter and exit the system as a pure product stream. In some examples, an acid flush may be needed to achieve 100% or close to 100% deplating.

0083In some embodiments, the membrane filter may have larger pores when used for electro-extraction with the electric field inside the membrane filter. For example, the membrane filter may have pore sizes of 100 nm to 150 nm, 150 nm to 200 nm, 200 nm to 300 nm, 300 nm to 400 nm, 400 nm to 500 nm, or 500 nm to 1,000 nm when used with electro-extraction.

0084In some embodiments, the system may be configured for recycling of acids and other materials used in the system. Batteries ground into black mass are usually dissolved in acids such as sulfuric or hydrochloric acid to form a leachate solution. Typically, low-value materials in the leachate solution such as Fe and Al that were not wanted were precipitated, which also required heat and the addition of neutralizing chemicals (sodium hydroxide and sodium bicarbonate) such that sulfuric acid couldn't be recovered. The present system and process does not require heat, precipitation, or the addition of other chemicals, allowing at least a portion of the sulfuric acid to be recovered and recycled for further use in the leaching system/process. For example, up to 10%, up to 20%, up to 30%, up to 40%, or up to 50% of the sulfuric acid may be recovered and recycled back into the system/process. Thus, the system allows for continuous reuse of sulfuric acid.

0085In additional embodiments, the process may be run multiple times and the electric field may be adjusted to select for different components. For example, the retentate solution and/or permeate solution may be recycled back as the mixture solution or into the mixture solution such that a second component can be separated. In other embodiments, multiple electro-filtration and/or electro-extraction modules may be combined in series to extract a series of components.

0086<figref idref="DRAWINGS">FIGS. <b>4</b>A-<b>4</b>I</figref> show an embodiment of a system that may be used for electro-filtration or electro-extraction. The system <b>100</b> may include a pressure cell <b>102</b> that is operable to enable electrification of the membrane filter <b>104</b> and introduce an electric field <b>101</b> at the membrane filter <b>104</b> surface. In an embodiment, the pressure cell <b>102</b> may include the membrane filter <b>104</b>, a counter electrode <b>106</b>, and an electrical contact <b>134</b>. In various embodiments, the system may further include a porous support piece <b>108</b>, an inlet pressure port <b>110</b>, an O-ring <b>112</b>, a housing <b>114</b>, an insulated wire (i.e. counter electrode lead) <b>116</b>, a plastic shim <b>118</b>, a shim <b>120</b>, a clamp <b>122</b>, an endcap <b>124</b>, a spout <b>126</b>, a plastic rod <b>128</b>, centering spacers <b>130</b>, and/or quick disconnect terminals <b>132</b>.

0087In some embodiments, the counter electrode <b>106</b> may be comprised of a conductive mesh with a large porosity to let all compounds/ions through. In at least one example, the counter electrode <b>106</b> is a platinum mesh. <figref idref="DRAWINGS">FIGS. <b>4</b>B-<b>4</b>D</figref> further show that the counter electrode <b>106</b> may be supported by a rod <b>128</b> running the length of the pressure cell <b>102</b> housing <b>114</b>. In some embodiments, the rod <b>128</b> may be supported by at least one centering spacer <b>130</b>. In some examples, the rod <b>128</b> comprises a plastic material and the centering spacers <b>130</b> comprise a plastic material or PTFE. The two centering spacers <b>130</b> may be press-fit into the pressure cell <b>102</b>. <figref idref="DRAWINGS">FIG. <b>4</b>G</figref> shows how the rod <b>128</b>, counter electrode <b>106</b>, insulated wire <b>116</b>, and related elements may be removed through the bottom of the pressure cell when needed for cleaning, modification, or replacement. <figref idref="DRAWINGS">FIG. <b>4</b>H</figref> shows how the counter electrode <b>106</b> may be re-installed through the bottom of the pressure cell <b>102</b>, the membrane filter <b>104</b> and porous support piece <b>108</b> installed, and the clamp <b>122</b> clamped on the bottom of the pressure cell <b>102</b>. <figref idref="DRAWINGS">FIG. <b>41</b></figref> shows how the insulated wire <b>116</b> is connected to the lid pass-through <b>146</b> using the quick connect/disconnect terminal <b>132</b>

0088The insulated wire <b>116</b> may be an electrical lead connected to the counter electrode <b>106</b>. As seen in <figref idref="DRAWINGS">FIG. <b>4</b>B</figref>, the insulated wire <b>116</b> may have quick disconnect terminals <b>132</b>. In one example, they may be ¼ quick disconnect terminals <b>132</b>. The insulated wire <b>116</b> may be an epoxied wire, such as a PTFE insulated wire. In some examples, as seen in <figref idref="DRAWINGS">FIG. <b>4</b>C</figref>, the insulated wire <b>116</b> may connect to the counter electrode <b>106</b> via a gold-plated ring terminal <b>138</b>. The ring terminal <b>138</b> may be held in place using one or more washers <b>140</b> and a mounting screw <b>142</b>. Referring to <figref idref="DRAWINGS">FIG. <b>4</b>D</figref>, the distance <b>144</b> between the counter electrode <b>106</b> and the membrane filter <b>104</b> may be controlled by the number of washers <b>140</b> added below the mounting screw <b>142</b>. The distance <b>144</b> between the counter electrode <b>106</b> and the membrane filter <b>104</b> may range from 0.1 mm to 10 mm. In some non-limiting examples, the distance <b>144</b> may be 0.1 mm to 0.5 mm, 0.5 mm to 1 mm, 0.5 mm to 1.5 mm, 1.25 mm, 2.5 mm, 3.75 mm, or 5 mm. In some embodiments, the washers <b>140</b> may be PTFE washers and the mounting screw <b>142</b> may be a PEEK mounting screw. Other materials known in the art are contemplated for the ring terminal <b>138</b>, washers <b>140</b>, and screw <b>142</b>. In some examples, the washers <b>140</b> and screw <b>142</b> may be made of non-conducting materials.

0089In an embodiment, the electrical contact <b>134</b> is a spring-loaded electrical contact. For example, the electrical contact <b>134</b> may be a pogo pin. As seen in <figref idref="DRAWINGS">FIG. <b>4</b>F</figref>, the wiring/lead <b>138</b> for the electrical contact <b>134</b> sits inside an insulating plastic tube and passes through a Swagelok fitting. The housing <b>114</b> may further include an opening <b>136</b> operable to receive the electrical contact <b>134</b>. The electrical contact <b>134</b> may contact the membrane filter <b>104</b> on the top side of the membrane filter <b>104</b>. <figref idref="DRAWINGS">FIGS. <b>5</b>A-<b>5</b>F</figref> show an example system with the electrical contact <b>134</b> inserted through the opening <b>136</b> in the side of housing <b>114</b> the pressure cell <b>102</b>.

0090In an embodiment, the pressure cell <b>102</b> is made of stainless steel, such as seen in <figref idref="DRAWINGS">FIGS. <b>5</b>A-<b>5</b>F</figref>, for example. In some embodiments, the pressure cell <b>102</b> is made of polycarbonate, Teflon, PFA, or other chemically-resistant materials. <figref idref="DRAWINGS">FIG. <b>5</b>G</figref> shows an example polycarbonate pressure cell <b>102</b>. The pressure cell includes an inlet pressure port <b>110</b>, a relief valve <b>111</b> (60 psi), a counter electrode lead <b>116</b>, a counter electrode <b>106</b>, a membrane filter <b>104</b>, and a porous support piece <b>108</b>.

0091In various examples, the pressure cell may operate under pressures ranging from 0 psi to 50 psi, 50 psi to 100 psi, 100 psi to 200 psi, 200 psi to 300 psi, 300 psi to 400 psi, 400 psi to 500 psi, 500 psi to 1000 psi, 1000 psi to 1500 psi, 1500 psi to 2000 psi, 2000 psi to 2500 psi, or 2500 psi to 3000 psi. The system may be operable at pressures up to 3000 psi whether the system is electrified not non-electrified. In some examples, a low pressure condition may refer to pressures less than 500 psi. In other examples, a high pressure condition may refer to pressures greater than 500 psi. The stainless steel pressure cell may be operated under both low and high pressure conditions and the polycarbonate or Teflon pressure cell may be operated under low pressure conditions. In an example, a stainless steel pressure cell may be coated internally with a chemically-resistant polymer to enable operation at high pressure with low pH solutions (pH&lt;2). In an example, the stainless steel pressure cell may be operable to withstand pressures up to 3000 psi. In an embodiment, a system with small pore sizes (e.g. 1 nm to 100 nm) may be used with high pressures, while a system with larger pore sizes (e.g. 100 nm to 1,000 nm) may be used with low pressures. In at least one example, system with a membrane filter with a pore size of 10 nm may operate at pressures greater than 700 psi.

0092In various embodiments, the system may further include a pump operable to pump the mixed solution, permeate solution, and/or retentate solution through the system at the desired pressures.

0093In some embodiments, the housing of the pressure cell may have a polymeric or other electrically-insulating coating. This may prevent conduction of the electrical current throughout the pressure cell and allow it to be contained at the membrane filter or between the membrane filter and the counter electrode.

0094Additionally or alternatively, the application of an electric current to the membrane may not act to pull a specific ion through the membrane, but may instead act to enhance the ionic separation selectivity of the membrane, allowing for greater specificity in the separation of target materials. In this embodiment, transport through the membrane may be driven by either a concentration gradient or pressure-driven flow. As part of charge separation, the membrane filter may enable separation of multiple compounds/elements within the solution, wherein molecules/ions of different magnitudes of charge may be positionally separated in the solution as the entire sample solution, or a portion of the sample solution travels through the membrane filter.

0095In some variations, the membrane filter may comprise a structure that enables filtration by interaction of the membrane with molecules/compounds/ions in solution. In these variations, the membrane filter may be composed of material that enables interaction with a particular molecule(s)/ion(s)/atom(s), type of molecule(s). In some variations, this may comprise binding sites, wherein a substrate may bind the membrane to enable/disable passage across the membrane.

0096Additionally or alternatively, the membrane filter may comprise a semi-permeable membrane that allows passage of certain types of molecules/ions while preventing other types of molecules/ions to pass. For example, in one implementation the membrane filter may comprise a semipermeable membrane that allows passage of polar molecule and prevents passage of non-polar molecules. In other variations, the membrane filter may allow unique interactions with certain molecule(s) or types of molecules. For example, a silicon-based membrane filter may enable unique interactions with lithium ions, enabling their passage, while blocking other ions and other molecules from passing through the membrane filter. In this example, properties of the silicon membrane filter may be leveraged to enable sorption of the Li by the membrane filter followed by desorption to enable release of the Li. In this example, a coating may be applied within the pores of the membrane and at the membrane surface that allows, or improves, the selective oxidation or reduction of Li, Ni, Co, Al, Fe, Cu, Mn, or other components via a current applied to the conductive silicon membrane.

0097In some variations, the system may comprise multiple membrane filters. Multiple membrane filters may function to provide enhanced filtration of a specific type, multiple types of filtration, and/or provide other filtration utility.

0098In one example, multiple membrane filters constructed for size filtration may be stacked upon each other to improve size filtration. In one implementation of this example, multiple membrane filters of decreasing or increasing pore sizes may be stacked in a row to enable filtration of multiple compounds of different sizes. These stacked multiple filters may be used in this manner to create a molecular size gradient within the solution or to filter/separate out multiple compounds/ions.

0099<figref idref="DRAWINGS">FIG. <b>6</b>A</figref> shows an embodiment of a system having multiple membrane filters in a membrane module. In some embodiments, the membrane module <b>210</b> may include a top plate <b>202</b>, one or more membrane plates <b>204</b> operable to support a membrane filter <b>206</b>, and a base plate <b>208</b>. In some examples, the base plate may also be operable to support a membrane filter <b>206</b>. Multiple membrane support plates <b>204</b> may be stacked between the top plate <b>202</b> and the base plate <b>208</b> to form a stacked membrane module <b>210</b>. The membrane module <b>210</b> may include 1, 2, 3, 4, 5, 6, 7, 8, 9, 10, 10 to 50, 50 to 100, or numerous (>100) membrane plates <b>204</b> and/or may include 1, 2, 3, 4, 5, 6, 7, 8, 9, 10, 10 to 50, 50 to 100, or numerous (>100) membrane filters <b>206</b>. <figref idref="DRAWINGS">FIG. <b>6</b>B</figref> shows an example membrane module <b>210</b> with <b>3</b> membrane plates and <b>4</b> membranes. The membrane module <b>210</b> may have ports <b>212</b>, <b>214</b>, <b>224</b> for the feed, retentate, and permeate lines. <figref idref="DRAWINGS">FIGS. <b>6</b>C and <b>6</b>D</figref> show the flow of the mixed solution/concentrate pumped into a manifold/port <b>212</b> and distributed across several membrane filters <b>206</b> in parallel then collected into another manifold/port <b>214</b> before exiting the module. <figref idref="DRAWINGS">FIGS. <b>6</b>E and <b>6</b>F</figref> show the flow of permeate passing through the membrane filters <b>206</b>, into channels <b>216</b>, and traveling outward toward a circumferential groove <b>218</b> that collects into a common drain.

0100<figref idref="DRAWINGS">FIGS. <b>7</b>A-<b>7</b>C</figref> show views of an example membrane support plate <b>204</b>. <figref idref="DRAWINGS">FIG. <b>7</b>G</figref> shows the top side of the membrane support plate <b>204</b>. In some embodiments, the membrane support plate <b>204</b> may include a smooth surface <b>220</b> or flat isotopically microporous surface for supporting the membrane filter <b>206</b>, a face seal <b>222</b> around the retentate manifold/port <b>214</b>, channel <b>216</b> permeate holes, a plate drain manifold/port <b>224</b>, a face seal <b>226</b> for permeate, a secondary seal <b>228</b> for retentate on a cylindrical boss, a face seal <b>230</b> around the feed manifold/port <b>212</b>, one or more PTFE pins <b>232</b> for locating the membrane filter <b>204</b> location, and a plate separation groove <b>234</b>. <figref idref="DRAWINGS">FIG. <b>7</b>B</figref> shows the bottom side of the membrane support plate <b>204</b>. In some embodiments, the membrane support plate <b>204</b> may further include a smooth surface <b>236</b> for face seals, a circumferential permeate collection groove <b>218</b>, a cross-flow outlet <b>238</b>, one or more clearance holes <b>240</b> operable to receive the one or more PTFE pins <b>232</b>, a cylindrical bore <b>242</b> for the secondary seal <b>228</b>, a primary face seal <b>244</b> for the membrane filter <b>204</b>, a cross-flow inlet <b>246</b>, and clearance holes <b>248</b> operable to receive a threaded rod <b>250</b>.

0101In some embodiments, the height of the membrane support plates <b>204</b> may range from 0.5 inches to 1 inch. For example, the height of the membrane support plates <b>204</b> may range from 0.5 inches to 0.6 inches, 0.6 inches to 0.7 inches, 0.7 inches to 0.8 inches, 0.8 inches to 0.9 inches, or 0.9 inches to 1 inch. In at least one example, the membrane support plate <b>204</b> may have a height of 0.875 inches. In some embodiments, the height of the top plate <b>202</b> may range from 0.5 inches to 1 inch. For example, the height of the top plate <b>202</b> may range from 0.5 inches to 0.6 inches, 0.6 inches to 0.7 inches, 0.7 inches to 0.8 inches, 0.8 inches to 0.9 inches, or 0.9 inches to 1 inch. In at least one example, the top plate <b>202</b> may have a height of about 0.875 inches. In some embodiments, the height of the base plate <b>208</b> may range from 0.5 inches to 1 inch. For example, the height of the base plate <b>208</b> may range from 0.5 inches to 0.6 inches, 0.6 inches to 0.7 inches, 0.7 inches to 0.8 inches, 0.8 inches to 0.9 inches, or 0.9 inches to 1 inch. In at least one example, the base plate <b>208</b> may have a height of about 0.875 inches. A membrane support module <b>210</b> may have a height ranging from 1.5 inches to 10 inches, depending on the number of membrane support plates <b>204</b> included in the membrane support module <b>210</b>. In one example, a membrane support module <b>210</b> may have a height of about 4 inches when it includes 3 membrane support plates <b>204</b> and <b>4</b> membrane filters <b>206</b>. The permeate, retentate, and feed manifolds/ports may be sized to accommodate the desired total flow rate through the system. In some embodiments, the size of the manifold may be increased with the more membrane support plates <b>204</b> in a membrane module <b>210</b> or a higher flow per membrane filter <b>206</b>. In some examples, the manifold may be up to 0.5-1.0 meters in diameter and the height would increase with the number of membranes needed.

0102Analogous to multiple filters with the same, or changing, pore size, other types of membrane filters (e.g., charge/electric current, or membrane binding/coating) may be implemented in the same manner. In another example, multiple membrane filters constructed to conduct electricity are positioned in a series. A voltage may then be passed through the membranes such that multiple, differently charged components are separated such that the majority fraction of each component is spatially separated by the membrane filters.

0103Additionally or alternatively, the system may include multiple filters of differing type. For example, one system may include one, or more, membrane filters that filter by size and one, or more, membrane filters that interact with the desired compound(s)/ion(s). In one implementation for Li filtering, the system may include a silicon membrane filter that adsorbs and desorbs Li and another membrane filter that filters by pore size.

0104In some variations the system may include a coating, wherein the coating comprises a functional coating within and around the porous structure and on the surface of the membrane filter. The specific type of coating may be dependent on the system implementation. The coating may function to improve membrane filtration. Additionally, or alternatively, the coating may improve the durability of the membrane filter (e.g., provide the porous structure with increased structural support).

0105In some variations, the coating may improve membrane filtration. For example, in an implementation to separate Li from a black mass leachate solution using a membrane interaction electro-extraction process, the coating may comprise a compound, or compounds, that catalyze the reduction of Li (or other targeted material) below the reduction potential of water (to avoid hydrogen and oxygen formation). The coating may catalyze a sorption/desorption reaction (which may be a Redox reaction). That is, the coating may catalyze a reaction such that the desired compound and the membrane sorb or desorb from the membrane material surface or bulk. For example, the coating may promote Li absorption by the membrane when the membrane is tuned to a specific charge/polarity and then release of the lithium from the membrane once the charge/polarity is removed or switched. Examples of coating compounds may include: vanadium oxide, titanium oxide, aluminum oxide, and other oxides. These compounds may be applied to the membrane surface and pores by a process such as atomic layer deposition.

0106In some variations, the coating may comprise a structural coating that improves the structural integrity of the membrane filter. This may be in addition to or an alternative to the functional aspects of the coating discussed previously. The structural coating may include a compound, or compounds, that conformally layer the membrane filter, particularly the porous structure to provide additional structural support and/or durability. Additionally or alternatively, the structural coating may prevent degradation of the porous structure of the membrane filter. Examples of structural coatings may include non-reactable metals and metal alloys (e.g., aluminum, titanium). In variations, wherein the coating may provide a functional aspect, the metallic coating may be metallic oxide (e.g. aluminum oxide, titanium oxide).

0107In variations where the system includes a coating, the coating may be implemented in any desired method. For nanoscale deposition in the pore structure, atomic layer deposition may be implemented. Alternatively, solution-based electrochemical deposition may be implemented. Nanoscale scale deposition may enable deposition of the coating into and onto the porous structure of the membrane filter.

Method

0108As shown in <figref idref="DRAWINGS">FIG. <b>8</b></figref>, a method <b>300</b> for material extraction from a mixture via membrane filtration includes: preparing a membrane nanofiltration system <b>302</b>; obtaining a mixture solution <b>304</b>, where the mixture solution comprises a solution that includes a desired component for separation; and feeding the mixture solution through a membrane nanofiltration system <b>306</b>, thereby separating the desired component (e.g. compound(s)/ion(s)) from unwanted components (e.g. compounds) within the mixture solution. The method functions to separate the desired component from other, “undesired” components. The method may implement the material extraction process by leveraging properties of the membrane filtration system to separate by size, charge, membrane/compound interaction, electrochemical oxidation or reduction, sorption, and/or any combination thereof. Additionally or alternatively, the method may leverage other separation properties, such as compound shape(s), polarity, magnetization, conductivity, and/or any other properties or combination of properties.

0109In some variations, the method functions by feeding all or a portion of the mixture solution through a membrane nanofiltration system (e.g., via pressure-driven flow), whereby the mixture solution is actively filtered such that the desired compound is uniquely blocked passage by the membrane nanofiltration system while other compounds within the mixture are enabled to pass through the membrane nanofiltration system. Alternatively, the desired compound may uniquely pass through the membrane nanofiltration system while other compounds within the mixture are prevented, or hindered, from passing through the nanofiltration system.

0110In some other variations, the method may function by initially saturating the membrane nanofiltration system with the mixture and then driving the mixture, either passively or actively out of the membrane nanofiltration system. Thus, in these variations, the method may further include saturating the membrane nanofiltration system with the mixture solution. Dependent on implementation, the desired compound may be either separated out of the membrane nanofiltration system, such that undesired compounds remain behind within (or blocked by) the membrane nanofiltration system; or undesired compounds may be filtered out of the membrane nanofiltration system, leaving behind the desired compound.

0111In other variations, the method may function by generating an electric field at the membrane filter to enable the membrane nanofiltration system to separate components from the mixture solution by charge, as shown in FIGA. <b>9</b>A and <b>9</b>B. In an embodiment, the method <b>400</b> of <figref idref="DRAWINGS">FIG. <b>9</b>A</figref> may include: preparing a membrane nanofiltration system <b>402</b>; obtaining a mixture solution <b>404</b>; generating an electric field at the membrane filter <b>406</b>; and feeding the mixture solution through the membrane nanofiltration system <b>408</b>. In another embodiment, the method <b>450</b> of <figref idref="DRAWINGS">FIG. <b>9</b>B</figref> may include: preparing a membrane nanofiltration system <b>452</b>; obtaining a mixture solution <b>454</b>; driving electrochemically reducing current into the membrane filter <b>456</b>; feeding the mixture solution through the membrane nanofiltration system <b>458</b>; feeding a pure draw solution through the membrane filter <b>460</b>; reversing the current for electrochemical oxidation <b>462</b>; and collecting a component of the mixture solution in the pure solution <b>464</b>.

0112The method may be implemented with the system as described above. Additionally or alternatively, the method may be implemented with any general membrane filtration system, particularly for the extraction of desired materials in a hydrometallurgical process.

0113Block <b>402</b> or <b>452</b>, which includes preparing a membrane nanofiltration system, functions to enable the desired type of filtration, or filtrations, with the membrane nanofiltration system. Preparing a membrane nanofiltration system <b>402</b> or <b>452</b> may be dependent on the mixture, desired compound(s) to filter, and desired method of filtration. In some variations, the membrane filter may have been obtained prepared, and so the method may not require block <b>402</b> or <b>452</b>.

0114In some variations, preparing a membrane nanofiltration system <b>402</b> or <b>452</b> may comprise constructing the membrane nanofiltration system. This may comprise creating the appropriate set of membrane filter, or filters, of the desired size, shape, thickness. Dependent on the type of filtration, constructing the membrane nanofiltration system may additionally include setting the membrane pore size, pore density, charge capacity, conductivity, functional coating chemistry, setting binding sites, etc. In some examples, the membrane filter may be prepared as described in U.S. Pat. Nos. 10,128,341, 10,943,982, or U.S. Pat. No. 11,004,943, the contents of each of which are incorporated herein in their entirety.

0115Although any general step for constructing the membrane nanofiltration system may be implemented, herein an example for constructing a single body Si-membrane, membrane nanofiltration system is presented. Constructing the Si-membrane may comprise: obtaining a silicon feedstock (e.g., silicon wafers); depositing metal particles onto the silicon surface (e.g., by using sputtering film deposition); and shaping the silicon feedstock into the Si-membrane (e.g., by chemically etching the silicon feedstock through deposition of the silicon wafers in a chemical etch bath for a period of time).

0116In some variations, preparing a membrane nanofiltration system <b>400</b> may include treating the membrane nanofiltration system. Treating the membrane nanofiltration system may function to improve the functionality. For example, for improved Li/Na separation through a silicon membrane, treating the membrane nanofiltration system may include applying a functional coating. The functional coating may function as a catalyst to electrochemically reduce Lithium to Lithium metal. Lithium reduction or oxidation may be mediated by a voltage applied to the conductive membrane. Once reduced, lithium may diffuse into the silicon lattice, allowing the membrane to act as a reversible lithium sponge. Applying the coating may comprise using atomic layer deposition to apply the coating on nanoscale pore structure, or using an electrochemical deposition technique. Example coatings may include vanadium oxide, titanium oxide, aluminum oxide, and other oxides.

0117Block <b>404</b> or <b>454</b>, which includes obtaining a mixture solution, functions in obtaining a source material for filtration, wherein the mixture solution includes some desired compound(s) that can be extracted from the mixture and wherein the mixture solution is in the suitable form to use with the membrane nanofiltration system. In some variations, the obtaining a mixture solution <b>404</b> or <b>454</b> may comprise simply acquiring the mixture (e.g., purchasing, receiving, etc.). In other variations, obtaining a mixture may comprise converting a lithium-ion battery to black mass, and leaching that black mass with a strong acid (H<b>2</b>SO<b>4</b> or HCI). An example mixture solution may include black mass components including but not limited to 1-5 wt. % Al, 3-33 wt. % Co, 1-3 wt. % Cu, 0.1-0.3 wt. % Fe, 3.5-4 wt. % Li, 3-11 wt. % Mn, about 35 wt. % graphite, 2-4 wt. % F, and 0.5-1 wt. % P.

0118For use with the membrane nanofiltration system, the mixture solution may be in the form such that it can be filtered. Dependent on the type of membrane nanofiltration system this may vary. Generally, the mixture may be in some liquid form. In variations where this is not the case, obtaining a mixture solution <b>404</b> or <b>454</b> may further include converting the mixture solution to a usable form. This will include having the mixture at the appropriate pH and appropriate concentration. The mixture is preferably sufficiently diluted such that it can flow through the membrane nanofiltration system. This may vary significantly dependent on the type of filtration, and mixture content. In one example, approximately 1 kg of black mass powder may be dissolved in approximately 110 kg of sulfuric acid. In another example, approximately 1 kg of black mass powder may be dissolved in approximately 10-20 kg of sulfuric acid. In another example, approximately 1 kg of black mass powder may be dissolved in approximately 20-50 kg of sulfuric acid. In another example, approximately 1 kg of black mass powder may be dissolved in approximately 50-100 kg of sulfuric acid.

0119Although the pH may vary for each specific implementation, the method may be particularly applicable for use with relatively neutral or low pH (e.g., pH-1-10). In various examples, the pH of the mixture solution may range from 0 to 5, 0 to 4, 0 to 3, 0 to 1, 0.5 to 5, 0.5 to 4, 0.5 to 3, 0.5 to 2, 0.5 to 1, 0.1 to 5, 0.1 to 4, 0.5 to 3, 0.1 to 2, 0.1 to 1, 1 to 5, 1 to 4, 1 to 3, or 1 to 2. For some variations, the pH may be very acidic. In one acidic example, the pH is approximately 2.0, less than 2.0, or between pH 1.0 and pH 2.0. In another acidic example, the pH is approximately 1.0. In another acidic example the pH is less than 1.0. In one pH&lt;1.0 (e.g., pH −0.1) implementation, the system may be initially implemented with concentrated (98%) sulfuric acid. In some examples, the method may include recycling some of the sulfuric acid. Dependent on desired outcome, the system may be maintained at that pH, or the pH may be raised during activity (e.g., pH may rise to pH −1.0). In other examples, the system may operate at a neutral pH ranging from 6 to 8 or operate at a basic pH ranging from 8 to 14.

0120Generally, for hydrometallurgical implementations, obtaining a mixture solution <b>404</b> or <b>454</b> may include digesting solid compounds thereby creating a liquid mixture for filtration. For example, for a battery recycling implementation, obtaining a mixture solution <b>404</b> or <b>454</b> may include converting the battery into “black mass”. This may include: physically pulling apart battery components, grinding the anode and cathode, digesting the ground components using acid, adding neutralizing components, etc.

0121Block <b>406</b> in <figref idref="DRAWINGS">FIG. <b>9</b>A</figref> includes generating an electric field at a membrane filter in the membrane nanofiltration system. The electric field may be generated orthogonal or perpendicular to the membrane filter. For charge filtration implementations (e.g. electro-filtration), generating an electric field <b>406</b> may include generating electric field between the membrane filter and the counter electrode (e.g., through an applying a voltage at the membrane filter via an electrical contact and a counter electrode). A voltage applied to the membrane filter and the counter electrode generates an electric field between them. This electric field may act as a driving force for separating a component from the mixture solution. The electric field strength and/or polarity may be increased, decreased, or even change direction during filtration. For electro-extraction in <figref idref="DRAWINGS">FIG. <b>9</b>B</figref>, driving electrochemically reducing current into the membrane filter <b>456</b> may include electrification of the membrane filter (e.g. the membrane filter is held at a constant electric potential or has a constant current driven through the membrane filter). In some examples, the membrane filter may be held at a constant electric potential or a constant current may flow into the membrane filter. The electrified membrane filter may allow target components to be selectively immobilized within the membrane filter pores via electrochemical reduction or oxidation.

0122A voltage of 0.1 V to 5 V may be applied to the electrical contact and the counter electrode. In some examples, a voltage of 0.1 V, 0.5 V, 1 V, 1.5 V, 2 V, 2.5 V, 3 V, 3.5 V, 4 V, 4.5 V, or 5 V may be applied to the electrodes to generate the electric field.

0123In some examples the electric field may be above the top surface of the membrane filter such that the components of the mixture solution have to pass through the electric field before reaching the membrane filter. In this example of electro-filtration (<figref idref="DRAWINGS">FIG. <b>9</b>A</figref>), some components with higher charges may be retained in the electric filed while other components with lower charges may be capable of passing through the electric field and entering the pores of the membrane filter. In some examples, the membrane filter may be held at a constant potential with little current to apply the electric field.

0124In other examples, the membrane filter may be charged for an electro-extraction configuration (<figref idref="DRAWINGS">FIG. <b>9</b>B</figref>). In this configuration, some components may adhere to and be retained within the charged membrane filter while other components may pass through the pores of the membrane filter. In some embodiments, in the electro-extraction configuration, a consistent flow of current at a specific potential may to reduce target component ions.

0125In other examples, charge may not be applied and the membrane filter may be used to separate components by size or other features of the components without the use of the electric field.

0126Block <b>408</b> or <b>458</b>, which includes feeding the mixture through the membrane nanofiltration system, functions to implement filtration/separation of the mixture. Block <b>408</b> or <b>458</b> implementation may be highly dependent on the mixture content, desired compound(s) for filtration, and the type of membrane nanofiltration system that is used. Driving the mixture through the membrane nanofiltration system <b>408</b> may comprise either passive (e.g., simple diffusion, or directed diffusion, such as by a concentration gradient) or active driving (e.g., pumps generating flow). In active driving variations, driving the mixture may comprise setting a flow rate (e.g., solution [volume] flow rate or a material [mass] flow rate). In a solution flow rate variation, the solution flow rate through the membrane may be between 0.1-200 [L/(m²hr)]. In some implementations, the solution flow rate may be lower or greater. In a material flow rate variation, the material flow rate may be between 1.0-1000 [g/(m²hr)]. In some variations, the material flow rate may be lower or greater.

0127In some variations, feeding the mixture may include multiple stages. Feeding the mixture solution may be used in combination with the electric field to control the separation of components from the mixture solution. In one example implementation, wherein the Lithium (Li) is filtered through a silicon (Si) based membrane nanofiltration system, an initial driving charge force is initiated to enable Li to pass through the pores in the Si membrane filter while simultaneously attracting other components of the mixture solution to the surface of the Si membrane filter. Once the permeate solution with Li has passed through, the feed will be switched to a pure draw solution (water or sulfuric acid) and the polarity of the membrane filter may change, thus releasing the other components. The components may then diffuse off of the membrane filter and be collected by a pure draw solution (water, pure acid, or dilute acid), or another flow (e.g., a pump) may drive the components out to be collected. In other embodiments, Li may be the component to be retained by the membrane filter and the other components may pass through the membrane filter.

0128For active filtration type implementations of the method, feeding the mixture solution may include uni-directional flows, wherein the mixture solution is driven through or across the membrane filter. This may not generally be the case for saturation filtration. For saturation filtration, passive forces (e.g., simple or directed diffusion) may be more commonly implemented such as concentration gradients, pH gradients, charge gradients. Generally, active filtration and saturation filtration may incorporate uni-directional, multi-directional, or non-biased diffusion as desired.

0129In some variations, the mixture solution is not fed through the membrane filter but is instead fed along or only partially against it. That is, the mixture solution may be fed parallel, adjacent to the membrane, or partially askew, such that the mixture is fed against and along the membrane filter. In these “cross-flow” variations, components of the mixture that are capable of crossing the membrane may do so, while the mixture solution itself, containing components that cannot pass the membrane, continue out. Cross-flow variations may implement passive and/or active transport. For purely passive implementations, the membrane nanofiltration system may be pre-saturated with solution, and a counter-flow of draw solution on the permeate side of the membrane may be used to sustain a concentration gradient.

0130Generally, feeding the mixture <b>408</b> or <b>458</b> may include any type of driving forces as desired and applicable to the implementation. As mentioned previously, feeding the mixture <b>408</b> or <b>458</b> may be, at least somewhat, filtration type of dependent. For certain types of filtration, some preferred methods for feeding the mixture solution <b>408</b> or <b>458</b> may exist. For example, feeding the mixture solution <b>408</b> or <b>458</b> may include generating pH or concentration gradient drive, or pressure driven flows. For membrane interaction (e.g., selective absorption, adsorption, or ion exchange) filtration, feeding the mixture solution <b>408</b> or <b>458</b> may include chemically driving the flows. In one implementation, for Li interaction with a Si membrane, a Redox reaction may be initiated to drive the flow by improving Li-Si interaction, whereby Li is reduced at the pore wall and absorbed into the bulk Si lattice.

0131For variations that require the filtration membrane to first be saturated with liquid prior to the separation process, the method may include saturating the membrane nanofiltration system with the mixture. Saturating the membrane nanofiltration system with the mixture functions to set up the saturation filtration process. Saturating the membrane nanofiltration system with the mixture solution, may include allowing the membrane nanofiltration system sit in the mixture or pure solvent (water or pure acid solution) for some allotted time. In another example, pure solvent (water or pure acid solution) is actively driven through the membrane (e.g., via pressure-driven flow) until the membrane is saturated. In another example, in the case where the small pore size within the membrane prevents direct saturation with aqueous solutions due to surface tension, a sequential approach may be used whereby low surface tension organic solvents or supercritical CO<b>2</b> are used to first saturate the pore structure and are then replaced with pure aqueous solvent. Dependent on implementation, the mixture solution may be heated, mixed, or agitated in some way to improve saturation. An example is the saturation of the membrane with water vapor at temperatures above the boiling point of water, possibly driven into the membrane under pressure, followed by a lowering of temperature to promote precipitation of pure water within the pore structure of the membrane. In some variations, where the membrane nanofiltration system reacts with compounds within the mixture, a charge may be run through the solution to also facilitate membrane saturation.

0132<figref idref="DRAWINGS">FIG. <b>9</b>B</figref> further includes feeding a pure draw solution through the membrane filter <b>460</b>; reversing the current driven into the membrane filter for electrochemical oxidation <b>462</b>; and collecting a component of the mixture solution in the pure draw solution <b>464</b>. For example, one or more components retained in the membrane filter may be leached into a pure product stream by the pure draw stream after the current is reversed. In some examples, the pure draw solution includes but is not limited to water or sulfuric acid. The pure draw solution may have a volume that is 1% to 5%, 5% to 10%, 10% to 20%, 20% to 30%, 30% to 40%, or 40% to 50% of the mixture solution volume. This reduced volume of pure draw solution may result in generating a concentrated pure product stream (e.g. a concentration solution of one or more components of the mixture solution).

0133<figref idref="DRAWINGS">FIG. <b>10</b></figref> shows an example multi-step process <b>500</b> for hydrometallurgical separation from a mixture solution via membrane nanofiltration that includes recycling. The process <b>500</b> may utilize multiple membrane filtration modules in various combinations. The membrane filtration modules may utilize electro-filtration, electro-extraction, or combinations thereof.

0134In this process <b>500</b>, ground battery powder may be combined with sulfuric acid to obtain the mixture solution <b>502</b>. The mixture solution is then filtered through a mesh for coarse filtration <b>504</b> to remove any solids from the mixture solution. The mixture solution may then enter a concentration loop <b>506</b>, where the mixture solution may enter an electro-filtration module <b>508</b> that contains a lithium permeable membrane. The permeate solution from the electro-filtration module <b>508</b> contains lithium that has passed through the membrane filter. The permeate solution may then be mixed with precipitation reagents to precipitate lithium carbonate or lithium hydroxide <b>510</b>. At least a portion of sulfuric acid remaining after precipitation may be recycled back <b>511</b> to the beginning of the process.

0135The remaining mixture solution not passing through the membrane filter in the electro-filtration module enters one or more electro-extraction module(s) <b>512</b> to remove other components of the remaining mixture solution. The electro-extraction module(s) <b>512</b> remove any metals that may plate/adhere to the membrane filter by collecting a second permeate solution <b>514</b> containing non-plated/non-adhered metals. The components in the second permeate solution may then be purified. Plated metals on the membrane filter may be periodically removed into a draw solution (water or sulfuric acid) <b>516</b> after reversing the polarity of the electric field, possibly at a concentration as high as their saturation point in solution. For example, the electro-extraction module(s) may remove any metals that plate below the potential of cobalt and nickel (iron, copper, etc.). In another example, a cascade of electro-extraction modules may be used to separate the mixture into multiple pure draw solutions, where the first contains lower-value Fe, Mn, and Cu, the second contains Co and Ni, and the third contains Li and Al. A pure stream of Li may then be separated via electro-filtration.

0136The retentate solution (containing the components not removed in the electro-extraction module(s)) may then pass through an additional electro-extraction module <b>518</b> configured to remove remaining components from the retentate solution. For example, the additional electro-extraction module may be configured to remove cobalt and nickel and exit the additional electro-extraction module in a third permeate solution <b>520</b>. Similar to the other electro-extraction module(s), a draw solution may be passed through <b>522</b> the electro-extraction module after reversing the polarity of the electric field to periodically remove plated metals. The permeate solution <b>520</b> exiting the additional electro-extraction module may then be mixed <b>524</b> with precipitation reagents to precipitate out <b>526</b> the components in the second permeate solution. For example, cobalt sulfate and nickel sulfate may be precipitated out of the solution. Sulfuric acid remaining after the precipitation may be recycled back <b>528</b> to the start of the process. Any remaining mixture solution may exit the system as waste <b>530</b>.

0137<figref idref="DRAWINGS">FIG. <b>11</b></figref> shows an example process <b>600</b> for electrically conductive membrane filter separation from a mixture solution via membrane nanofiltration that includes recycling. In this process <b>600</b>, ground battery powder may be combined with sulfuric acid to obtain the mixture solution <b>602</b>. The mixture solution is then filtered through a mesh for coarse filtration <b>604</b> to remove any solids from the mixture solution. The mixture solution may then enter an electro-extraction module <b>612</b>. The permeate solution of the electro-extraction module <b>612</b> contains a component (e.g. desired metal to be extracted) that has passed through the membrane filter. The permeate solution <b>516</b> may be a pure solution of the extracted metal, near saturation. The permeate solution may then be mixed <b>617</b> with precipitation reagents to precipitate a pure solid product <b>610</b>. At least a portion of sulfuric acid remaining after precipitation may be recycled back <b>611</b> to the beginning of the process. Plated metals on the membrane filter may be periodically removed into a draw solution (water or sulfuric acid) <b>614</b> after reversing the polarity of the electric field. Any remaining mixture solution may be recycled back to the beginning of the process <b>513</b>.

Definitions

0138As used herein, the term “about” is used to provide flexibility to a numerical range endpoint by providing that a given value may be “a little above” or “a little below” the endpoint. For example, the endpoint may be within 10%, 8%, 5%, 3%, 2%, or 1% of the listed value. Further, for the sake of convenience and brevity, a numerical range of “about 50 mg/mL to about 80 mg/mL” should also be understood to provide support for the range of “50 mg/mL to 80 mg/mL” The endpoint may also be based on the variability allowed by an appropriate regulatory body, such as the FDA, USP, etc.

0139As used herein, “comprises,” “comprising,” “containing,” and “having” and the like can have the meaning ascribed to them in U.S. Patent Law and can mean “includes,” “including,” and the like, and are generally interpreted to be open ended terms. The terms “consisting of” or “consists of” are closed terms, and include only the components, structures, steps, or the like specifically listed in conjunction with such terms, as well as that which is in accordance with U.S. Patent law. “Consisting essentially of” or “consists essentially of” have the meaning generally ascribed to them by U.S. Patent law. In particular, such terms are generally closed terms, with the exception of allowing inclusion of additional items, materials, components, steps, or elements, that do not materially affect the basic and novel characteristics or function of the item(s) used in connection therewith. For example, trace elements present in a composition, but not affecting the composition's nature or characteristics would be permissible if present under the “consisting essentially of” language, even though not expressly recited in a list of items following such terminology. In this specification when using an open ended term, like “comprising” or “including,” it is understood that direct support should be afforded also to “consisting essentially of” language as well as “consisting of” language as if stated explicitly and vice versa.

0140As used herein, first, second, third, etc. are used to characterize and distinguish various elements, components, regions, layers and/or sections. These elements, components, regions, layers and/or sections should not be limited by these terms. Use of numerical terms may be used to distinguish one element, component, region, layer and/or section from another element, component, region, layer and/or section. Use of such numerical terms does not imply a sequence or order unless clearly indicated by the context. Such numerical references may be used interchangeably without departing from the teaching of the embodiments and variations herein.

0141As used herein, the terms “membrane filter” and “wafer” may be used interchangeably to mean a nanoporous filter as described herein.

0142As used herein, the terms “battery leachate solution,” “black mass leachate,” “mixture solution” and “feed solution” may be used interchangeably to refer to the solution entering the membrane filtration system.

0143As used herein, the terms “compound” and “component” are used to refer to any type of material, without any loss of generality of the material in question. That is, compound may refer to any element, ion, molecule, complex structure(s), or combinations thereof (e.g. metal oxides, metal sulfides).

EXAMPLES

0144An example system with a silicon membrane filter in a pressure cell was tested for validation of electrical current passing into the membrane filter from the electrical contact. <figref idref="DRAWINGS">FIG. <b>5</b>H</figref> shows the pogo pin was inserted through a port in the pressure cell to form an electrical contact with the interior surface of the silicon membrane, mounted in the cell and a meter probe was placed on the unpolished back side of the silicon membrane. It was assumed that contact resistance on the unpolished side was low. The membrane filter was compressed into the pogo pin down to the O-ring. Resistance was measured at 23-130 Ohms for a 0.4′ max compression pin and at 1103-1771 Ohms for a 0.25′ max compression pin.

0145In another example, the resistance of the electrical contact was about 1000 Ohms. The pressure cell was pressurized to 700 psi and held the pressure for 45 minutes without significant leakage or cracking of the wafer. The pressurization was repeated with the same wafer and then 3 more times with different wafers. The pressure was held for about 5 minutes for the repeat tests.

0146<figref idref="DRAWINGS">FIG. <b>12</b></figref> shows results from an example electrified filtration. Water was placed in a filtration cell with a silicon membrane filter with a pore size of about 100 nm and a low pressure (50 psi). Once a liquid bridge was formed on both sides of the membrane, the pressure was turned off and MgSO₄was added on one side of the membrane to evaluate diffusive transport in a no-flow condition. The diffusion of MgSO₄across the membrane was then measured. <figref idref="DRAWINGS">FIG. <b>12</b></figref> shows the difference in the flow through of MgSO₄through the membrane via conductivity measurement over time, when the membrane is electrified (1 V) and not electrified (0 V). The diffusion based (non-pressurized flow) filtration experiment with MgSO₄showed a significantly reduced ability of salt to flow through the membrane once an electric field was applied.

0147As a person skilled in the art will recognize from the previous detailed description and from the figures and claims, modifications and changes can be made to the embodiments of the invention without departing from the scope of this invention as defined in the following claims.