Solid polymer electrolyte composite membrane comprising laser micromachined porous support

CROSS-REFERENCE TO RELATED APPLICATIONS

0001The present application claims the benefit under 35 U.S.C. 119(e) of U.S. Provisional Patent Application Ser. No.60/613,765, filed Sep. 28, 2004, the disclosure of which is incorporated herein by reference.

BACKGROUND OF THE INVENTION

0002The present invention relates generally to solid polymer electrolyte membranes of the type suitable for use in electrochemical devices and relates more particularly to a novel such membrane.

0003Electrochemical devices of the type comprising a solid polymer electrolyte membrane (PEM) sandwiched between a pair of electrodes are well-known, such electrochemical devices finding applications as, for example, fuel cells, electrolyzers, sensors, gas concentrators, gas compressors, supercapacitors, ultracapacitors and industrial electrochemical process units.

0004A common type of solid polymer electrolyte membrane consists of a homogeneous perfluorosulfonic acid (PFSA) polymer, said PFSA polymer being formed by the copolymerization of tetrafluoroethylene and perfluorovinylether sulfonic acid. See e.g., U.S. Pat. No. 3,282,875, inventors Connolly et al., issued Nov. 1, 1966; U.S. Pat. No. 4,470,889, inventors Ezzell et al., issued Sep. 11, 1984; U.S. Pat. No. 4,478,695, inventors Ezzell et al., issued Oct. 23, 1984; U.S. Pat. No. 6,492,431, inventor Cisar, issued Dec. 10, 2002, all of which are incorporated herein by reference. A commercial embodiment of a perfluorosulfonic acid polymer PEM is available from DuPont (Wilmington, Del.) as NAFION® PFSA polymer.

0005Although PFSA PEMs function in a generally satisfactory manner in electrochemical devices, there nonetheless remains room for improvement in certain properties of PFSA PEMs. For example, one common difficulty associated with PFSA PEMs is a lack of mechanical strength, resulting in a tendency for the PFSA PEMs to tear, especially when being handled (such as during assembly of an electrochemical cell) or in stressed areas where compression is applied thereto (such as in peripheral areas of PEMs sealed under pressure to other electrochemical cell components). Such a lack of mechanical strength also often leads to electrical shorting, which results in premature failures during cell operation as the typical porous electrodes in contact with the PEM have a tendency to penetrate the softened PEM. This problem of shorting is even greater when the membrane is made thin (e.g., less than 25 microns) in order to decrease membrane resistance.

0006Because the tendency to tear and to short is greatest when the PFSA PEMs are wet (especially at elevated temperatures) and because the PFSA PEMs must be wet in order to function properly, one approach to this problem has been to assemble electrochemical cells with dry PEMs and then to subject the PEMs to a humidification process. This approach, however, has its own shortcomings. One such shortcoming is that the dry assembly requires special moisture-free facilities, such as a “dry room.” Another such shortcoming is that the humidification process is time-consuming. Still another such shortcoming is that the humidification process typically results in the PEM swelling in a non-uniform manner, thereby creating stress in some areas of the PEM, as well as in other components of the cell that are in contact with the PEM, and introducing irregularities in the contact pressure applied over the entire active surface area of the PEM. (When the contact pressure is not uniform over the entire active surface area of the PEM, the performance of the electrochemical cell is adversely affected.) As can readily be appreciated, such irregularities are amplified where humidification is applied to a plurality of PEM-containing fuel cells arranged in a stack.

0007Moreover, if the PEM is subjected to variable conditions of humidity (e.g., alternating wet and dry intervals during periods of use and non-use, respectively), the membrane will undergo additional dimensional changes as it swells when wet and shrinks when dry. Such dimensional changes cause further stress to the PEM and to the other cell components, all of which are tightly packed together. If sufficiently great, such stress results in damage to the PEM and/or to the cell components in contact therewith. Pinholes/microcracks have a tendency to form along the edges where one side of the membrane is heavily compressed by the fixture while the other side can still partially swell.

0008One approach that has been taken to address the aforementioned problem of low mechanical strength of PFSA PEMs has been to cross-link the membrane polymer. Such cross-linking reduces the swelling of the membrane when wet which, in turn, reduces the deterioration of the mechanical strength of the membrane when wet. Unfortunately, however, such cross-linking tends to make the membrane undesirably brittle under dry conditions.

0009Another approach to this problem is disclosed in U.S. Pat. No. 6,635,384, inventors Bahar et al., which issued Oct. 21, 2003, and which is incorporated herein by reference. In the aforementioned '384 patent, there is described a composite membrane that comprises a microporous sheet, said microporous sheet preferably being an expanded polytetrafluoroethylene (ePTFE) membrane, said ePTFE membrane preferably being formed by stretching a sheet of polytetrafluoroethylene (PTFE) until pores are formed therein. The structure defining the pores of the microporous sheet is then at least partially covered with a functional material selected from (i) inorganic particulate; (ii) metal; and (iii) an organic polymer. In addition, the pores of the sheet are then at least partially filled with polymer electrolyte selected from (i) polymer compositions that contain metal salts; (ii) polymeric gels that contain electrolyte; and (iii) ion exchange resins, such as PFSA.

0010One disadvantage that has been noted by the present inventors regarding the foregoing composite membrane is that the pores of the expanded polytetrafluoroethylene (ePTFE) sheet tend to follow a tortuous pathway between opposing surfaces of the ePTFE sheet, as opposed to following a direct or straight pathway between opposing surfaces. As a result of these tortuous pathways, protons conducted through the pores (by means of the polymer electrolyte that is disposed within the pores) have to travel considerably longer pathways through the membrane than merely the thickness of the membrane. Such longer pathways result in a reduction in the conductivity of the membrane and an increase in the resistivity of the membrane.

0011Another disadvantage that has been noted by the present inventors regarding the foregoing composite membrane is that a microporous sheet of ePTFE possesses only slightly better mechanical strength than a PFSA PEM. Consequently, the foregoing composite membrane is not significantly stronger than a PFSA PEM and is subject to the same types of shortcomings discussed above in connection with PFSA PEMs.

0012Still another disadvantage that has been noted by the present inventors regarding the foregoing composite membrane is that the stretching process that is used to expand the PTFE sheet to create the desired pores tends to result in a fairly uniform yet random distribution of pores throughout the sheet and cannot be tailored to control the positioning or concentration of pores in particular regions of the sheet. This is unfortunate because certain regions of the membrane, such as the membrane active area edges/corners or the membrane contact area with the current collector, are typically subjected to greater stresses than other regions. Consequently, pores in these regions of high stress undesirably diminish membrane strength in those regions where membrane strength is needed most.

SUMMARY OF THE INVENTION

0013It is an object of the present invention to provide a novel solid polymer electrolyte membrane of the type that is suitable for use in electrochemical devices, such as, but not limited to, fuel cells, electrolyzers, sensors, gas concentrators, gas compressors, supercapacitors, ultracapacitors and industrial electrochemical process units.

0014It is another object of the present invention to provide a solid polymer electrolyte membrane of the type described above that overcomes at least some of the drawbacks discussed above in connection with existing solid polymer electrolyte membranes.

0015Therefore, according to one aspect of the invention, there is provided a solid polymer electrolyte composite membrane, said solid polymer electrolyte composite membrane comprising (a) a rigid, non-electrically-conductive support, said rigid, non-electrically-conductive support having opposing top and bottom surfaces and a plurality of pores extending from said top surface to said bottom surface; and (b) a solid polymer electrolyte at least partially filling at least some of said pores.

0016According to another aspect of the invention, there is provided a solid polymer electrolyte composite membrane, said solid polymer electrolyte composite membrane comprising (a) a non-electrically-conductive support, said non-electrically-conductive support having opposing top and bottom surfaces and a plurality of pores extending directly from said top surface to said bottom surface; and (b) a first solid polymer electrolyte at least partially filling at least some of said pores.

0017In a preferred embodiment, the non-electrically-conductive support is a polyimide membrane having a thickness of about 5 μm to 50 μm. A plurality of cylindrical pores are formed in the support by laser micromachining. The pores have a diameter of about 5 μm to 200 μm and are arranged in a defined pattern, such as in a uniform hexangular pattern or in a pattern in which fewer pores are located in areas of higher membrane stress and more pores are located in areas of lower membrane stress. A solid polymer electrolyte, such as PFSA polymer, fills the pores. Additional solid polymer electrolyte, which may be the same as or different than that filling the pores, may be applied to one or both of the top and bottom surfaces of the solid polymer electrolyte filling the pores.

0018The present invention is also directed to a method of preparing a solid polymer electrolyte composite membrane and to the membrane prepared by said method. According to one aspect of the invention, such a method comprises the steps of (a) providing a non-electrically-conductive support; (b) lasing a plurality of pores through said non-electrically-conductive support; and (c) at least partially filling at least some of said pores with a first solid polymer electrolyte.

0019In a preferred embodiment, the lasing step comprises providing a beam of laser light capable of forming pores in said non-electrically-conductive support, then passing said beam of laser light through a mask having a pattern of openings, and then focusing the laser light transmitted through the pattern of openings in said mask onto a surface of said non-electrically-conductive support, whereby a plurality of pores are formed in said non-electrically-conductive support that correspond to said pattern of openings. Preferably, the laser light used is laser light from an excimer laser.

0020The present invention is also directed to membrane electrode assemblies incorporating the above-described composite composite membranes and to electrochemical devices incorporating the above-described composite membranes, such electrochemical devices including, but not being limited to, fuel cells, electrolyzers, gas concentrators, gas compressors, sensors, supercapacitors, ultracapacitors, and industrial electrochemical process units.

0021For purposes of the present specification and claims, it is to be understood that certain relational terms used herein, such as “above,” “below,” “top,” “bottom,” “over,” “under,” “in front of,” or “behind,” when used to denote the relative positions of two or more components of an electrochemical device are used to denote such relative positions in a particular orientation and that, in a different orientation, the relationship of said components may be reversed or otherwise altered.

0022Additional objects, as well as features and advantages, of the present invention will be set forth in part in the description which follows, and in part will be obvious from the description or may be learned by practice of the invention. In the description, reference is made to the accompanying drawings which form a part thereof and in which is shown by way of illustration various embodiments for practicing the invention. The embodiments will be described in sufficient detail to enable those skilled in the art to practice the invention, and it is to be understood that other embodiments may be utilized and that structural changes may be made without departing from the scope of the invention. The following detailed description is, therefore, not to be taken in a limiting sense, and the scope of the present invention is best defined by the appended claims.

BRIEF DESCRIPTION OF THE DRAWINGS

0023The accompanying drawings, which are hereby incorporated into and constitute apart of this specification, illustrate various embodiments of the invention and, together with the description, serve to explain the principles of the invention. In the drawings wherein like reference numerals represent like parts:

0024<figref idref="DRAWINGS">FIG. 1</figref> is a schematic section view of a first embodiment of a solid polymer electrolyte composite membrane constructed according to the teachings of the present invention;

0025FIGS. <b>2</b>(<i>a</i>) and <b>2</b>(<i>b</i>) are top and perspective views, respectively, of the non-electrically-conductive support shown in <figref idref="DRAWINGS">FIG. 1</figref>;

0026<figref idref="DRAWINGS">FIG. 3</figref> is a fragmentary top view of a non-electrically-conductive support that may be used as an alternative to the non-electrically-conductive support of FIGS. <b>2</b>(<i>a</i>) and <b>2</b>(<i>b</i>);

0027<figref idref="DRAWINGS">FIG. 4</figref> is a schematic depiction of the laser micromachining technique of near-field imaging;

0028<figref idref="DRAWINGS">FIG. 5</figref> is a schematic section view of a second embodiment of a solid polymer electrolyte composite membrane constructed according to the teachings of the present invention;

0029<figref idref="DRAWINGS">FIG. 6</figref> is a graphic depiction comparing the performance of a fuel cell containing the composite membrane of the present invention to a fuel cell containing a conventional PFSA membrane; and

0030<figref idref="DRAWINGS">FIG. 7</figref> is a graphic depiction comparing the performance of an electrolysis cell containing the composite membrane of the present invention to a fuel cell containing a conventional PFSA membrane.

DETAILED DESCRIPTION OF PREFERRED EMBODIMENTS

0031Referring now to <figref idref="DRAWINGS">FIG. 1</figref>, there is shown a schematic section view of a first embodiment of a solid polymer electrolyte composite membrane constructed according to the teachings of the present invention, said solid polymer electrolyte composite membrane being represented generally by reference numeral <b>11</b>.

0032Composite membrane <b>11</b> comprises a non-electrically-conductive support <b>13</b> and a solid polymer electrolyte <b>15</b>, support <b>13</b> being impregnated with solid polymer electrolyte <b>15</b>.

0033Referring now to FIGS. <b>2</b>(<i>a</i>) and <b>2</b>(<i>b</i>), support <b>13</b> can be seen to be a generally sheet-like, unitary structure, preferably of high mechanical strength, having a top surface <b>17</b> and a bottom surface <b>19</b>. The thickness of support <b>13</b> may vary, depending upon the type of use to which membrane <b>11</b> is put and the types of pressures typically encountered by support <b>13</b> in such a use. For example, where membrane <b>11</b> is used in an electrolyzer, support <b>13</b> preferably has a thickness suitable for withstanding pressures of 2000-5000 psi. For most applications, support <b>13</b> has a thickness of about 5 μm to 50 μm, preferably about 7.5 μm to 15 μm.

0034As noted above, support <b>13</b> is preferably a rigid member; in addition, support <b>13</b> is preferably chemically resistant to acid and water hydrolysis at elevated temperatures. Examples of materials that may be used to make support <b>13</b> include, but are not limited to, perfluorinated polymers, polyvinylidene fluoride, poly(tetrafluoroethylene), polybenzimidazole, polyphenylenesulfide, polysulfone, polyethersulfone, polyesters, polyparaphenylene, polyquinoxaline, polyarylketone, polybenzazole, polyaramid, poly(etherether-ketone), liquid crystal polymers, polyimide and polyetherimide. A comparison of the mechanical strength of some of the above-listed polymers to conventional PEM materials is provided below in TABLE I. <tables id="TABLE-US-00001" num="1"><table frame="none" colsep="0" rowsep="0"><tgroup align="left" colsep="0" rowsep="0" cols="2"><colspec colname="1" colwidth="133PT" align="left" /><colspec colname="2" colwidth="84PT" align="center" /><thead><row><entry namest="1" nameend="2" align="center">TABLE I</entry></row><row><entry /></row><row><entry namest="1" nameend="2" align="center" rowsep="1" /></row><row><entry>Material, condition</entry><entry>Young's Modulus (Mpa)</entry></row><row><entry namest="1" nameend="2" align="center" rowsep="1" /></row></thead><tbody valign="top"><row><entry /></row></tbody></tgroup><tgroup align="left" colsep="0" rowsep="0" cols="2"><colspec colname="1" colwidth="133PT" align="left" /><colspec colname="2" colwidth="84PT" align="char" char="." /><tbody valign="top"><row><entry>Nafion ® 112 PFSA membrane, dry 20° C.</entry><entry>300</entry></row><row><entry>Nafion ® 112 PFSA membrane, wet 80° C.</entry><entry>70</entry></row><row><entry>Poly(tetrafluoroethylene) (PTFE)</entry><entry>400</entry></row><row><entry>Polybenzimidazole (PBI)</entry><entry>5900</entry></row><row><entry>Polyphenylenesulfide (PPS)</entry><entry>3300</entry></row><row><entry>Polysulfone (PS)</entry><entry>2600</entry></row><row><entry>Poly(etherether-ketone) (PEEK)</entry><entry>2700</entry></row><row><entry>Polyimide (PI)</entry><entry>2900</entry></row><row><entry namest="1" nameend="2" align="center" rowsep="1" /></row></tbody></tgroup></table></tables>

0035As can be seen, PBI, PPS, PS, PEEK and PI are substantially stronger than PFSA and PTFE and, therefore, are preferred as materials for use in making support <b>13</b>.

0036Kapton® polyimide (DuPont, Wilmington, Del.), which has a high strength, good hydrolysis stability and excellent thermal properties, is a particularly desirable material for use in making support <b>13</b>. Ultra-thin membranes of Kapton® polyimide (8.5 μm and 17 μm) are commercially available and may be used to make support <b>13</b>. VECTRA® liquid crystal polymers (Goodfellow, Cambridgeshire, UK) also have superb mechanical, chemical and thermal stability and may be used to make support <b>13</b>.

0037Although the polymers discussed above as suitable for use in making support <b>13</b> are non-ionic, ionomers may alternatively be used. Examples of suitable cationic ionomers include carboxylated, sulfonated or phosphorylated derivatives of the polymers discussed above. Examples of suitable anionic ionomers include amino, imimo, ammonium, sulfonium and phosphonium derivatives of the polymers discussed above.

0038A plurality of pores <b>21</b>, preferably cylindrical in shape, extend in a direct, i.e. straight-line, fashion from top surface <b>17</b> to bottom surface <b>19</b> of support <b>13</b>. It should be stressed that the base shape of the pore can be chosen from any two-dimensional geometric shape distributed in either regular or irregular fashion. As will be discussed further below, pores <b>21</b> are made by laser micromachining and preferably each have a diameter of about 5 μm to 200 μm, with pores <b>21</b> constituting about 20% to 95%, more preferably about 40% to 70%, of support <b>13</b>.

0039The conductance of a membrane including such a porous support can be easily estimated as: <maths id="MATH-US-00001" num="1"><math overflow="scroll"><mrow><mfrac><mn>1</mn><mi>G</mi></mfrac><mo>=</mo><mrow><mfrac><mi>Ts</mi><mrow><mi>σ</mi><mo>*</mo><mi>A</mi><mo>*</mo><mi>X</mi></mrow></mfrac><mo>+</mo><mfrac><mrow><mo>(</mo><mrow><mi>T</mi><mo>-</mo><mi>Ts</mi></mrow><mo>)</mo></mrow><mrow><mi>σ</mi><mo>*</mo><mi>A</mi></mrow></mfrac></mrow></mrow></math></maths><br /> where G is the ionic conductance of the composite membrane, o is the ionic conductivity of the solid polymer electrolyte, A is the geometric area of the composite membrane, X is the percentage of pores in the support, T is the thickness of the composite membrane and T_sis the thickness of the support.

0040As can be seen from the above equation, the conductance of the composite membrane is inversely proportional to the percentage of pores in the support. Thus, a support with 50% pores results in a composite membrane with conductance equivalent to a homogenous membrane twice as thick. To maximize the conductance of the supported membrane without a sacrifice in mechanical properties, a support with 50% pores may be fabricated.

0041In the present embodiment, pores <b>21</b> are arranged in a uniform hexangular pattern over the entirety of support <b>13</b>, such pores <b>21</b> having, for example, a diameter of about 25 μm and a center-to-center spacing of about 40 μm. It is to be understood, however, that the present invention is not limited to the above-described pattern of pores and may encompass a variety of different patterns of pores. For example, as can be seen in <figref idref="DRAWINGS">FIG. 3</figref>, there is shown a fragmentary top view of a support <b>13</b>′ having a plurality of pores <b>21</b>′ that are arranged so that a lesser concentration of pores <b>21</b>′ may be found in areas of higher membrane stress (e.g., at the membrane edge <b>23</b> or in local “hot spots” <b>25</b>) and a greater concentration of pores <b>21</b>′ may be found elsewhere.

0042Pores <b>21</b> (and <b>21</b>′) are made by lasing support <b>13</b> with suitable laser light. Although either gas lasers or solid state lasers may be used to create pores <b>21</b>, gas lasers are preferred. Within the class of gas lasers, excimer lasers are preferred over CO₂lasers. This is because excimer lasers produce laser light having a much shorter wavelength than that produced by CO₂lasers (˜0.3 μm for an excimer laser vs. ˜10 μm for a CO₂laser). Consequently, because of their shorter wavelengths, excimer lasers directly excite the covalent bonds of the support and decompose the support without creating as extreme high-temperature conditions as is the case with CO₂lasers. Additionally, due to their shorter wavelengths, excimer lasers can create significantly smaller pores than can CO₂lasers.

0043Where a CO₂laser is used to micromachine pores into the support, the whole laser beam is focused onto an area of the support until the irradiated area is ablated. Where an excimer laser is used, the relatively uniform beam intensity produced thereby provides an alternative approach to pore formation: near-field imaging. In near-field imaging, which is schematically depicted in <figref idref="DRAWINGS">FIG. 4</figref>, a mask having a pattern is placed in the path of the beam emitted by the excimer laser. The light transmitted through the pattern of the mask is then focused by an imaging lens onto the support, resulting in the mask pattern being projected onto the support, with a corresponding pattern of pores being formed in the support. As can readily be appreciated, near-field imaging enables various alternative patterns to be projected onto the support simply by using differently patterned masks.

0044Referring back to <figref idref="DRAWINGS">FIG. 1</figref>, solid polymer electrolyte <b>15</b> can be seen to fill pores <b>21</b> and to cover thinly top surface <b>17</b> and bottom surface <b>19</b> of support <b>13</b>. Examples of suitable materials for use as solid polymer electrolyte <b>15</b> include (i) polymer compositions that contain metal salts; (ii) polymeric gels that contain electrolytes; and (iii) ion exchange resins. In general, if proton conductivity is required, a carboxylated, sulfonated or phosphorylated polymer is preferably used as solid polymer electrolyte <b>15</b>. If hydroxyl ions are needed, a polymer containing amino, imimo, ammonium, sulfonium, and phosphonium groups is preferably used as solid polymer electrolyte <b>15</b>. To enhance the ionic conductivity of membrane <b>11</b>, inorganic ionically-conductive materials, such as metal oxide (e.g., TiO₂), silicon oxide, metal phosphates (e.g., zirconium phosphate) or heteropolyacids, may be impregnated into the solid polymer electrolyte <b>15</b>.

0045A preferred material for use as solid polymer electrolyte <b>15</b> is a perfluorosulfonic acid (PFSA) membrane, such as is commercially available from DuPont (Wilmington, Del.) as NAFION® PFSA polymer. Of the aforementioned NAFION® PFSA polymers, particularly preferred are those having an equivalent weight of 200 to 2000, even more preferably those having an equivalent weight of 500 to 1200, the optimal equivalent weight depending on the use to which membrane <b>11</b> is applied.

0046Various techniques may be used to couple solid polymer electrolyte <b>15</b> to support <b>13</b>. One such technique involves providing the solid polymer electrolyte in the form of a solution/dispersion (e.g., Nafion® 1100 in water or isopropanol) and then coating support <b>13</b> with said solution/dispersion. Examples of suitable coating techniques include gravure coating, immersion (dip) coating, metering rod (Meyer bar) coating, slot die coating, rotary screen and air knife coating. The optimal coating technique for any particular case will depend on factors, such as instrument complexity, thickness accuracy, operation efficiency, initial investment, and the like. After the solution/dispersion is coated onto the support, the coated support is heated at about 50° C. to 100° C., preferably 80° C., for about 5 minutes to evaporate the solvent. If desired, one or more additional coatings may thereafter be applied. Said one or more additional coatings either may be of the same solution/dispersion previously applied in order to build up the thickness of the solid polymer electrolyte or may be different from the initial solution/dispersion in order to obtain a composite membrane with a multilayer electrolyte structure having desired propeties. (An example of a composite membrane possessing such a multilayer structure is shown in <figref idref="DRAWINGS">FIG. 5</figref>, said composite membrane <b>51</b> comprising a support <b>13</b>, a first solid polymer electrolyte <b>53</b> and a second polymer electrolyte <b>55</b>.) After coating and drying each applied layer or after coating and drying all applied layers, the layer or layers are preferably cured by heating at a temperature greater than the glass transition temperature of the ionomer (e.g., 100° C. to 400°<b>0</b> C., preferably 160° C. for 15 minutes). Such curing, which serves to sinter or anneal the ionomer, further enhances the mechanical properties of the membrane.

0047If desired, mask coating technology may be used to create a composite membrane wherein the solid polymer electrolyte is confined to certain patches or regions.

0048As an alternative to coating, the solid polymer electrolyte may be applied by spraying the polymer electrolyte solution/dispersion onto support <b>13</b>. Conventional spraying techniques may be used for this purpose. Such spraying is preferably performed at 80° C. and does not require a subsequent solvent evaporation step. Micro-spraying may be used to create solid polymer electrolyte patches on the support, such patches, if desired, being far smaller than those capable of being produced by masked coating techniques.

0049Still another technique for incorporating the solid polymer electrolyte <b>15</b> into support <b>13</b> involves a membrane extrusion technique. Such a technique comprises providing the solid polymer electrolyte in the form of a thin membrane, stacking the thin ionomer membrane on the top and/or bottom surfaces of support <b>13</b>, and then pressing the stack together at an elevated temperature, preferably above the melting point or glass transition temperature of the ionomer.

0050The total thickness of membrane <b>11</b> is preferably about 5 to 300 μm, more preferably 10 to 75 μm, with the thickness of the membrane being governed by application requirements. Generally, a water electrolyzer requires a thicker membrane due to its high differential pressure while an ultra-thin membrane is suitable for super capacitors since no dynamic pressure is involved for their operation.

0051Membrane and electrode assemblies (MEAs) comprising the composite membrane of the present invention can be fabricated by pressing a precast Pt-supported on carbon/ionomer ink onto each side of the composite membrane. The foregoing method is typically referred to as the decal transfer method.

0052One of the advantages of the composite membrane of the present invention is that catalyst ink can be directly coated or sprayed onto the top and bottom surfaces of the membrane. This direct coating of the catalyst ink is not practical for conventional ionomer membranes since such membranes change dimension when contacted with the ink. Since the composite membrane of the present invention has excellent dimensional stability when contacted with swelling agents, such as water or alcohols, the catalyst ink can be directly applied to the membrane.

0053Another approach that may be used to fabricate an MEA using the composite membrane of the present invention involves a technique called “catalyst on diffusion media.” The diffusion medium of this technique is a porous electrically-conductive material, which is typically in the form of a thin sheet. Optionally, a microporous layer prepared from carbon black and a polymer binder may be applied to the diffusion medium. The catalyst is then sprayed onto the diffusion medium to form a diffusion electrode. A catalyst-loaded diffusion electrode is then pressed onto each side of the composite membrane to form a full MEA.

0054The following examples are provided for illustrative purposes only and are in no way intended to limit the scope of the present invention:

EXAMPLE 1

0055A plurality of pores were formed in a piece of 8 μm thick Kapton® polyimide film (DuPont, Wilmington, Del.) using an excimer laser and near-field imaging. The diameter of each pore was 30 μm, and the distance between the centers of the pores was 40 μm. Nafion® PFSA solution, with an equivalent weight of 1100, was coated onto the porous film, and the product was then heated to dry off the solvent from the coated PFSA solution and to cure the PFSA polymer. The resultant composite membrane had a thickness of approximately 32 μm. The mechanical strength of said composite membrane was then compared to that of Nafion® 112 PFSA film and found to be approximately 100 times stronger than Nafion® 112 PFSA film at elevated temperatures.

EXAMPLE 2

0056A composite membrane identical to that of Example 1 was prepared. A catalyst in the form of a carbon black supported platinum was sprayed onto plastic thin films to form catalyst decals. The catalyst decals were then hot pressed against opposing surfaces of the composite membrane to form an MEA. The MEA was then sandwiched between two pieces of teflonated porous carbon paper and assembled into a functional PEM fuel cell as described in U.S. Pat. No. 4,215,183, inventor MacLoed, which issued Jul. 29, 1980, the disclosure of which is incorporated herein by reference.

0057The foregoing PEM fuel cell was then tested at 80° C., with the anode saturator temperature controlled at 90° C. and the cathode saturator temperature controlled at 65° C.

0058As can be seen in <figref idref="DRAWINGS">FIG. 6</figref>, the performance of the subject fuel cell was similar to a fuel cell containing a Nafion® 112 PFSA membrane having a thickness of 50 μm.

EXAMPLE 3

0059A composite membrane identical to that of Example 1 was prepared. A pure Pt black catalyst serving as a cathode catalyst and a Pt/Ir mixture serving as an anode catalyst were pressed onto opposing surfaces of the composite membrane to form an MEA. The MEA was sandwiched between porous titanium metal meshes or sinters and assembled into an electrolysis cell as described in U.S. Pat. No. 6,500,319, inventors LaConti et al., which issued Dec. 31, 2002, the disclosure of which is incorporated herein by reference. The resulting electrolysis cell was operated at 80° C. under ambient pressure and its performance compared to a similar electrolysis cell containing a Nafion® 112 membrane. As can be seen in <figref idref="DRAWINGS">FIG. 7</figref>, the performance of the two electrolysis cells was similar.

0060The embodiments of the present invention recited herein are intended to be merely exemplary and those skilled in the art will be able to make numerous variations and modifications to it without departing from the spirit of the present invention. All such variations and modifications are intended to be within the scope of the present invention as defined by the claims appended hereto.