A polyurethane ballast layer, the method for preparing the same and the use thereof

Abstract

one. Way including providing a ballast layer with a filler of polyurethane, spraying the first reaction system on the surface of the ballast layer with a filler of polyurethane to form a polyurethane outer protective layer, moreover, this first reaction system contains: 1a) one or more polyisocyanates, having the general formula R (NCO), in which R is selected from the group consisting of an aliphatic alkyl group, containing 2-18 carbon atoms, aromatic alkyl group, containing 6-15 carbon atoms, and an aryl alkyl group, containing 8-15 carbon atoms, and n is an integer from 2 to 4; 1b) one or more polyether polyols and / or amino-terminated polyethers, having an average molecular weight greater than 200 and functionality from 2 to 6; 1c) one or more chain extension agents; and 1d) from 0 to 0.5 wt.% of one or more blowing agents per 100 wt.% 1b) and 1c); in which the tensile strength of the polyurethane outer protective layer is from 4 to 20 MPa. 2. The method according to claim 1, in which the density of the polyurethane external protective layer is from 0.6 to 1.5 g / cm, the shore hardness of the polyurethane external protective layer is from 10 to 90 on a scale A, and the elongation at the time of rupture of the polyurethane external protective layer layer is from 100 to 550%. 3. The method according to claim 1, wherein the ballast layer with a filler of polyurethane contains ballast and polyurethane foam filling the space among the ballast, wherein the polyurethane foam contains a reaction product of a second reaction system containing reaction components: 2a) one or more polyisocyanates having the general formula R (NCO ) in which

Term

No projected expiry on record.

  1. Priority
  2. Filed
  3. Published
  4. Today

34 claims: 27 independent, 7 dependent

  1. 1
    A process comprising 1. Способ, включающий
  2. 2
    providing a ballast layer of polyurethane filler 2. обеспечение балластного слоя с наполнителем из полиуретана,
  3. 3
    Spray on the first surface of the reaction system with a ballast layer of polyurethane to form a polyurethane-filled outer protective layer, wherein the first reaction system comprising:3. распыление первой реакционной системы на поверхность балластного слоя с наполнителем из полиуретана для образования полиуретанового внешнего защитного слоя, причем эта первая реакционная система содержит:
  4. 4
    1a) one or more polyisocyanates having R (NCO general formula)nWherein R is selected from the group consisting of an aliphatic alkyl group having 2-18 carbon atoms, an aromatic alkyl group having 6-15 carbon atoms and aryl alkyl groups containing 8-15 carbon atoms and n is an integer from 2 to 4;4. 1а) один или более полиизоцианатов, имеющих общую формулу R(NCO)n, в которой R выбирается из группы, состоящей из алифатической алкильной группы, содержащей 2-18 атомов углерода, ароматической алкильной группы, содержащей 6-15 атомов углерода, и арилированной алкильной группы, содержащей 8-15 атомов углерода, а n представляет собой целое число от 2 до 4;
  5. 5
    1b) one or more polyether polyols and / or polyether having terminal amino groups, having an average molecular weight greater than 200 and a functionality of from 2 to 6;5. 1b) один или более простых полиэфирполиолов и/или простых полиэфиров с концевыми аминогруппами, имеющих среднюю молекулярную массу больше 200 и функциональность от 2 до 6;
  6. 6
    1c) one or more chain extension agents;and 6. 1с) один или более агентов удлинения цепи;и
  7. 7
    . 7. 1d) from 0 to 0.5 wt% of one or more blowing agents, based on 100 wt% 1b) and 1c).;7. 1d) от 0 до 0,5 мас.% одного или более вспенивающих агентов в расчете на 100 мас.% 1b) и 1с);
  8. 8
    wherein the tensile strength of the polyurethane outer protective layer is from 4 to 20 MPa. 8. в котором прочность на растяжение полиуретанового внешнего защитного слоя составляет от 4 до 20 МПа.
  9. 11
    2a) one or more polyisocyanates having R (NCO general formula)nWherein R is selected from the group consisting of an aliphatic alkyl group having from 2 to 18 carbon atoms, an aromatic alkyl group containing from 6 to 15 carbon atoms and aryl alkyl groups containing from 8 to 15 carbon atoms, and n represents an integer from 2 to 4;11. 2а) один или более полиизоцианатов, имеющих общую формулу R(NCO)n, в которой R выбирается из группы, состоящей из алифатической алкильной группы, содержащей от 2 до 18 атомов углерода, ароматической алкильной группы, содержащей от 6 до 15 атомов углерода, и арилированной алкильной группы, содержащей от 8 до 15 атомов углерода, а n представляет собой целое число от 2 до 4;
  10. 12
    2b) one or more polyols selected from the group consisting of polyether polyol, polyester polyol, polycarbonate polyols, and polycaprolactone politetragidrofuranpoliola;12. 2b) один или более полиолов, выбранных из группы, состоящей из простого полиэфирполиола, сложного полиэфирполиола, поликарбонатполиола, поликапролактонполиола и политетрагидрофуранполиола;
  11. 13
    2c) one or more chain extension agents;and 13. 2с) один или более агентов удлинения цепи;и
  12. 14
    2d) from 0.3 to 4.5 wt% of one or more blowing agents, based on 100 wt% 2b) and 2)..;14. 2d) от 0,3 до 4,5 мас.% одного или более вспенивающих агентов в расчете на 100 мас.% 2b) и 2 с);
  13. 15
    The polyurethane foam in which the elongation at break amounts to 120 to 400%. 15. в котором удлинение пенополиуретана к моменту разрыва составляет от 120 до 400%.
  14. 17
    5. Ballast airbag railway track comprising a ballast bed of a polyurethane filler and a polyurethane outer protective layer, wherein the polyurethane outer protective layer comprises the reaction product of the first reaction system, the reaction system is first sprayed onto the surface of the ballast bed filled with polyurethane, and wherein the first reaction The reaction system comprises the following components:5. Балластная подушка железнодорожного пути, содержащая балластный слой с наполнителем из полиуретана и полиуретановый внешний защитный слой, где полиуретановый внешний защитный слой содержит продукт реакции первой реакционной системы, причем первая реакционная система распылена на поверхность балластного слоя с наполнителем из полиуретана, и причем первая реакционная система содержит следующие компоненты реакции:
  15. 18
    1a) one or more polyisocyanates having R (NCO general formula)nWherein R is selected from the group consisting of an aliphatic alkyl group having from 2 to 18 carbon atoms, an aromatic alkyl group containing from 6 to 15 carbon atoms and aryl alkyl groups containing from 8 to 15 carbon atoms, and n represents an integer from 2 to 4;18. 1а) один или более полиизоцианатов, имеющих общую формулу R(NCO)n, в которой R выбирается из группы, состоящей из алифатической алкильной группы, содержащей от 2 до 18 атомов углерода, ароматической алкильной группы, содержащей от 6 до 15 атомов углерода, и арилированной алкильной группы, содержащей от 8 до 15 атомов углерода, а n представляет собой целое число от 2 до 4;
  16. 19
    1b) one or more polyether polyols and / or polyether having terminal amino groups, having an average molecular weight greater than 200 and a functionality of from 2 to 6;19. 1b) один или более простых полиэфирполиолов и/или простых полиэфиров с концевыми аминогруппами, имеющих среднюю молекулярную массу больше 200 и функциональность от 2 до 6;
  17. 20
    1c) one or more chain extension agents;and 20. 1с) один или более агентов удлинения цепи;и
  18. 21
    . 21. 1d) from 0 to 0.5 wt% of one or more blowing agents, based on 100 wt% 1b) and 1c).;21. 1d) от 0 до 0,5 мас.% одного или более вспенивающих агентов в расчете на 100 мас.% 1b) и 1с);
  19. 22
    22 wherein the tensile strength of the polyurethane outer protective layer is from 4 to 20 MPa. 22. в котором прочность на растяжение полиуретанового внешнего защитного слоя составляет от 4 до 20 МПа.
  20. 25
    2a) one or more polyisocyanates having R (NCO general formula)nWherein R is selected from the group consisting of an aliphatic alkyl group having from 2 to 18 carbon atoms, an aromatic alkyl group containing from 6 to 15 carbon atoms and aryl alkyl groups containing from 8 to 15 carbon atoms, and n represents an integer from 2 to 4;25. 2а) один или более полиизоцианатов, имеющих общую формулу R(NCO)n, в которой R выбирается из группы, состоящей из алифатической алкильной группы, содержащей от 2 до 18 атомов углерода, ароматической алкильной группы, содержащей от 6 до 15 атомов углерода, и арилированной алкильной группы, содержащей от 8 до 15 атомов углерода, а n представляет собой целое число от 2 до 4;
  21. 26
    2b) one or more polyols selected from the group consisting of polyether polyol, polyester polyol, polycarbonate polyols, and polycaprolactone politetragidrofuranpoliola;26. 2b) один или более полиолов, выбранных из группы, состоящей из простого полиэфирполиола, сложного полиэфирполиола, поликарбонатполиола, поликапролактонполиола и политетрагидрофуранполиола;
  22. 27
    2c) one or more chain extension agents;and 27. 2с) один или более агентов удлинения цепи;и
  23. 28
    2d) from 0.3 to 4.5 wt% of one or more blowing agents, based on 100 wt% 2b) and 2c)..;28. 2d) от 0,3 до 4,5 мас.% одного или более вспенивающих агентов в расчете на 100 мас.% 2b) и 2с);
  24. 29
    The polyurethane foam in which the elongation at break amounts to 120 to 400%. 29. в котором удлинение пенополиуретана к моменту разрыва составляет от 120 до 400%.
  25. 32
    10. A method for construction of railway track ballast cushion as defined in claim 5, which comprises 10. Способ сооружения балластной подушки железнодорожного пути, определенной в п.5, который включает
  26. 33
    The provision of railway track subgrade and 33. обеспечение земляного полотна железнодорожного пути, и
  27. 34
    The imposition of a ballast layer of polyurethane filler and polyurethane outer protective layer on the roadbed of railway track. 34. наложение балластного слоя с наполнителем из полиуретана и полиуретанового внешнего защитного слоя на земляное полотно железнодорожного пути.
Independent claims27