Electrochromic device and assembly incorporating the same

Abstract

one. A method of manufacturing electrochromic windows, comprising: providing a first glass substrate; applying layers of an electrochromic device to a first substrate, including at least counter electrode layers (PE), ion conductor (IP) and electrochromic material (ECM); forming a pattern of layers of an electrochromic device (ECM) and cutting the first glass substrate with layers of an electrochromic device deposited on it so so that a plurality of substrates with ECM are formed; providing a plurality of second glass substrates; laminating or combining a plurality of substrates with ECM with a plurality of second glass substrates, respectively; providing a plurality of third glass substrates; forming a plurality of glass packets (SP), respectively containing the first and second substrates in a substantially parallel arrangement at a distance from the third glass substrates. 2. The method according to p. 1, while many of the second substrates are subjected to thermal hardening. The method according to p. 2, the ECU layers being sprayed. 4. The method according to p. 3, while spraying is carried out using an ion beam. 5. The method according to p. 2, while the ECU layers face the second substrates when assembled in double-glazed windows. 6. The method according to p. 2, the ECU layers facing the third substrates when assembling in double-glazed windows. 7. The method according to p. 2, further comprising providing the first and second transparent conductive coatings (SPP) on opposite sides of the layers of the electrochromic device. The method according to p. 7, wherein each said IFR includes a silver layer located between the ITO layers, and furthermore, including NiCr or Cu layers between the silver layer and the ITO layers are provided. Spo

Term

No projected expiry on record.

  1. Priority
  2. Filed
  3. Published
  4. Today

39 claims: 39 independent, 0 dependent

  1. 1
    A method of manufacturing an electrochromic window comprising:1. Способ изготовления электрохромных окон, содержащий:
  2. 2
    The provision of the first glass substrate;2. обеспечение первой стеклянной подложки;
  3. 3
    coating the first substrate layer electrochromic device including at least a counter electrode layer (TE), ion conductor (IP) and the electrochromic material (EHM);3. нанесение на первую подложку слоев электрохромного устройства, включая по меньшей мере слои противоэлектрода (ПЭ), ионного проводника (ИП) и электрохромного материала (ЭХМ);
  4. 4
    patterning layers of electrochromic devices (echo) and cutting the first glass substrate coated with a layer of electrochromic devices, so that a plurality of substrates with an echo;4. формирование рисунка слоев электрохромного устройства (ЭХУ) и разрезание первой стеклянной подложки с нанесенными на нее слоями электрохромного устройства так, чтобы образовалось множество подложек с ЭХУ;
  5. 5
    providing a plurality of second glass substrates;5. обеспечение множества вторых стеклянных подложек;
  6. 6
    lamination or connection of a plurality of substrates with the echo from the plurality of second glass substrates, respectively;6. ламинирование или соединение множества подложек с ЭХУ с множеством вторых стеклянных подложек соответственно;
  7. 7
    providing a plurality of third glass substrates;7. обеспечение множества третьих стеклянных подложек;
  8. 8
    forming a plurality of insulating glass units (PO), respectively comprising first and second substrates in a substantially parallel arrangement at a distance from the third glass substrates. 8. формирование множества стеклопакетов (СП), соответственно содержающих первую и вторую подложки в практически параллельном расположении на расстоянии от третьих стеклянных подложек.
  9. 9
    2. The method of claim. 1, wherein the plurality of second substrates subjected to thermal hardening. 2. Способ по п. 1, при этом множество вторых подложек подвергнуты термической закалке.
  10. 10
    3. The method of claim. 2, wherein the layers are applied by spraying echo. 3. Способ по п. 2, при этом слои ЭХУ нанесены напылением.
  11. 11
    4. The method of claim. 3, wherein the spraying is carried out using an ion beam. 4. Способ по п. 3, при этом напыление осуществляют с помощью ионного пучка.
  12. 12
    5. The method of claim. 2, wherein the facing layers to the second echo in the assembly of substrates in double glazing. 5. Способ по п. 2, при этом слои ЭХУ обращены ко вторым подложкам при сборке в стеклопакеты.
  13. 13
    6. The method of claim. 2, with the layers facing the third echo when assembling the substrates in double glazing. 6. Способ по п. 2, при этом слои ЭХУ обращены к третьим подложкам при сборке в стеклопакеты.
  14. 14
    7. The method of claim. 2, further comprising providing the first and second transparent conductive coatings (RFP) on opposite sides of the layers of the electrochromic device. 7. Способ по п. 2, дополнительно содержащий обеспечение первого и второго прозрачных проводящих покрытий (ППП) на противоположных сторонах слоев электрохромного устройства.
  15. 15
    8. The method of claim. 7, wherein each said PPP includes silver layer sandwiched between layers of ITO, and thus also provided comprising Cu or NiCr layers between the silver layer and the layers of ITO. 8. Способ по п. 7, при этом каждое упомянутое ППП включает в себя слой серебра, расположенный между слоями ITO, и при этом, кроме того, предусмотрены включающие NiCr или Cu слои между слоем серебра и слоями ITO.
  16. 16
    9. A method according to claim. 8, the surface resistance of each said RFP is approximately 5 ohms / square. 9. Способ по п. 8, при этом поверхностное сопротивление каждого упомянутого ППП составляет примерно 5 Ом/квадрат.
  17. 17
    10. The method of claim. 2, wherein the IP layer includes LiPON. 10. Способ по п. 2, при этом слой ИП включает в себя LiPON.
  18. 18
    11. The method of claim. 2, wherein the layer comprises WO EHMx. 11. Способ по п. 2, при этом слой ЭХМ содержит WOx.
  19. 19
    12. The method of claim. 11 wherein the WOx It is a sub-stoichiometric. 12. Способ по п. 11, при этом WOx является субстехиометрическим.
  20. 20
    13. The method of claim. 12 wherein 2,6 <x <3. 13. Способ по п. 12, при этом 2,6<x<3.
  21. 21
    14. The method of claim. 11 wherein the polyethylene layer, IP layer and / or the EHM doped layer (s) of magnesium (Mg). 14. Способ по п. 11, при этом слой ПЭ, слой ИП и/или слой ЭХМ легирован(ы) магнием (Mg).
  22. 22
    15. The method of claim. 14, further comprising providing one or more low emissivity coatings, low emissivity coatings and provide data on the internal surfaces of the second substrate, on one or both surfaces of the first substrate and / or on the inner surfaces of the third glass substrates. 15. Способ по п. 14, дополнительно содержащий обеспечение одного или более низкоэмиссионных покрытий, причем данные низкоэмиссионные покрытия обеспечивают на внутренних поверхностях вторых подложек, на одной или обеих поверхностях первой подложки и/или на внутренних поверхностях третьих стеклянных подложек.
  23. 23
    16. The method of claim. 15, further comprising providing a UV blocking coatings on inner surfaces of second substrates. 16. Способ по п. 15, дополнительно содержащий обеспечение блокирующих УФ покрытий на внутренних поверхностях вторых подложек.
  24. 24
    17. The method of claim. 2, the plurality of substrates are laminated with an echo or connected to a plurality of second substrates by respective glass layers on the polymer base. 17. Способ по п. 2, при этом множество подложек с ЭХУ ламинируют или соединяют с множеством вторых стеклянных подложек посредством соответствующих слоев на полимерной основе.
  25. 25
    18. A method of manufacturing an electrochromic unit (EHB), comprising:18. Способ изготовления электрохромного блока (ЭХБ), содержающий:
  26. 26
    The provision of the first, second and third glass substrates, wherein the second substrate is thermally hardened, and the first substrate is not subjected to thermal quenching;26. обеспечение первой, второй и третьей стеклянных подложек, при этом вторая подложка подвергнута термической закалке, а первая подложка не подвергнута термической закалке;
  27. 27
    The deposition sputtering multiple layers of the electrochromic device (echo), directly or indirectly, to the first substrate, wherein the given set of layers comprises a first echo transparent conductive coating (PPP), a counterelectrode layer (PE), an ion conductor layer (IP) layer and EHM second RFP;27. осаждение напылением множества слоев электрохромного устройства (ЭХУ), непосредственно или опосредованно, на первую подложку, причем данное множество слоев ЭХУ содержит первое прозрачное проводящее покрытие (ППП), слой противоэлектрода (ПЭ), слой ионного проводника (ИП), слой ЭХМ и второе ППП;
  28. 28
    The compound or laminating the first and second substrates with each other;and 28. ламинирование или соединение первой и второй подложек друг с другом;и
  29. 29
    providing a second and third substrates in a substantially parallel arrangement at a distance from each other, 29. обеспечение второй и третьей подложек в практически параллельном расположении на расстоянии друг от друга,
  30. 30
    with PE layers and EHM, both are able to change their color when the EHB is in working condition. 30. при этом слои ПЭ и ЭХМ оба способны изменять свой цвет, когда ЭХБ находится в рабочем состоянии.
  31. 31
    19. A method of manufacturing an electrochromic unit (EHB), comprising:19. Способ изготовления электрохромного блока (ЭХБ), содержающий:
  32. 32
    The deposition sputtering multiple layers of the electrochromic device (echo), directly or indirectly, to the first substrate, wherein this device comprises a plurality of layers in order of proximity to the first substrate, the first transparent conductive coating (PPP), a cathode layer, an electrolyte layer, anode tinctable the anode layer and the second RFP;and 32. осаждение напылением множества слоев электрохромного устройства (ЭХУ), непосредственно или опосредованно, на первую подложку, причем данное множество слоев устройства содержит, в порядке удаления от первой подложки, первое прозрачное проводящее покрытие (ППП), слой катода, слой электролита, анодно окрашивающийся слой анода и второе ППП;и
  33. 33
    The connection of the first substrate with a plurality of deposited layers coated on her device to a second substrate such that the first and second substrates are in substantially parallel arrangement at a distance from each other. 33. соединение первой подложки с множеством осажденных на нее напылением слоев устройства со второй подложкой так, что первая и вторая подложки находятся в практически параллельном расположении на расстоянии друг от друга.
  34. 34
    20. The method of claim. 19 wherein the first and / or second sets PPP represent dielectric layers based on silver. 20. Способ по п. 19, при этом первое и/или второе ППП представляют собой комплекты диэлектрических слоев на основе серебра.
  35. 35
    21. The method of claim. 19 wherein the electrolyte layer comprises LiPON. 21. Способ по п. 19, при этом слой электролита содержит LiPON.
  36. 36
    22. The method of claim. 19 wherein the cathode layer, an electrolyte layer and / or anode layer of the dye doped anode (s), magnesium (Mg). 22. Способ по п. 19, при этом слой катода, слой электролита и/или анодно окрашивающийся слой анода легирован(ы) магнием (Mg).
  37. 37
    23. The method of claim. 19 wherein the cathode comprises a layer of substoichiometric WOx. 23. Способ по п. 19, при этом слой катода содержит субстехиометрический WOx.
  38. 38
    24. The method of claim. 19 wherein the cathode comprises a layer of substoichiometric WOxAnd 2,6 <x <3. 24. Способ по п. 19, при этом слой катода содержит субстехиометрический WOx, и 2,6<x<3.
  39. 39
    25. The method of claim. 19, wherein the PE layers and EHM, both are able to change their color when the EHB is in working condition. 25. Способ по п. 19, при этом слои ПЭ и ЭХМ оба способны изменять свой цвет, когда ЭХБ находится в рабочем состоянии.
Independent claims39