Multi color-shifting devices

Field of the Invention

0001This invention relates generally to thin film color shifting devices and more particularly to a multilayer color-shifting device having a non-conforming dielectric spacer layer having a varying thickness.

Background of the Invention

0002Security devices are being used more and more to protect currency and other valuable documents such as passports, drivers' licenses, green cards, identity cards and the like. These security devices are also used to protect commercial products such as pharmaceuticals, cosmetics, cigarettes, liquor, electronic media, wearing apparel, toys and spare parts for automobiles and aircraft from counterfeiting. In fact, it is estimated that counterfeit articles now comprise between 5% and 7% of world trade. Holograms attached to such articles have been the traditional method to foil counterfeiters.

0003Color shifting pigments and colorants have been used in numerous applications, ranging from automobile paints to anti-counterfeiting inks for security documents and currency. Such pigments and colorants exhibit the property of changing color upon variation of the angle of incident light, or as the viewing angle of the observer is shifted. The primary method used to achieve such color shifting colorants is to disperse small flakes, which are typically composed of multiple layers of thin films having particular optical characteristics, throughout a medium such as paint or ink that may then be subsequently applied to the surface of an object.

0004<patcit id="pcit0001" dnum="US6761959B"><text>U.S. Pat. No. 6,761,959</text></patcit> discloses a security article having Chromagram™ thereon. The Chromagram™ provides both color shifting and holographic effects to the viewer. In the '959 patent an organic substrate stamped with a holographic grating or pattern is coated with a color shifting multilayer film.

0005United States patent <patcit id="pcit0002" dnum="US7630109B"><text>7,630,109 in the name of Phillips et al</text></patcit>, assigned to JDS Uniphase Corp., discloses a more complex type of Chromagram™ wherein patterning is shown. In some regions, holographic effects are shown, and in other regions only color shifting effects are visible. In Phillips '109 patent a multilayer thin film filter is disclosed an organic dielectric layer serving as a spacer layer in a Fabry-Perot structure. The dielectric has embossed regions of varying thicknesses wherein the thickness within a region is substantially uniform. Each different region of a different thickness produces a different color shift. The size of one of the embossed adjacent regions is such that the color of said one region is uniform and cannot be seen by a human eye as different in color from the uniform color of an adjacent region thereto, and wherein the color within a region can be seen with magnification of at least 10:1. Phillips' teaches a Fabry-Perot device with a variable thickness dielectric layer by embossing the dielectric material to various thicknesses. Since the dielectric in regions a, b, and c as shown in <figref idref="f0001">Fig. 1</figref> of the '109 patent are purposefully embossed with different thicknesses, light reflecting back to the viewer after impinging upon the reflector will be three different distinct colors. However due to the small size of the regions a, b, and c, the eye will tend to integrate and if the pixel or region defined by (a) through (d) inclusive can be seen; only a single color will be perceived. With sufficient magnification, the individual regions (a), (b), and (c) will be seen and different colors will be perceived.

0006Another United States patent application which discloses diffraction gratings with color shifting coatings but deviates from the teaching of <patcit id="pcit0003" dnum="US7054042B"><text>Phillips et al, is U.S. patent 7,054,042</text></patcit>. United States Patent '042 appears to deviate from the teaching of Phillips in that a decoupling layer is taught as way in which to separate the diffraction grating effects from the color shifting effects. Holmes suggests placing a decoupling layer between the relief structure and the thin film reflection filter, which is described to be a thin film reflection filter.

0007In all of these aforementioned security structures, conventional application of the coating is suggested, for example by vacuum deposition to yield conforming layers.

0008The prior art teaches first stamping a substrate, and subsequently applying the coating layers required to create the desired patterns of reflective and color shifting coatings.

0009This invention deviates from the prior art teaching by using conforming coatings with non-conforming coatings on substrates having structures thereon. In preferred embodiments the structures stamped or formed upon the substrate layer are so small, for their effects to be seen, magnification is required, however in other less preferred embodiments the structures may be large enough that they can be seen without magnification when coated. By way of example logos and other readable discernible indicia are provided on these substrates and are highlighted by providing thin film coatings that contrast particular regions.

0010This invention provides a thin film structure that is coated on a substrate wherein the dielectric spacer layer has a varying thickness. The provision of a dielectric layer with a varying thickness has been disclosed not only by <patcit id="pcit0004" dnum="US7630109B"><text>Phillips in 7,630,109</text></patcit> but also much earlier in <patcit id="pcit0005" dnum="US587789A"><text>U.S. Pat. No. 5,877,89 in the name of Shaw et al.</text></patcit> Shaw et al disclose applying heat variably to create a dielectric layer of varying thickness.

0011In contrast to the prior art which uses a stamped substrate as a spacer layer coated on one side with a reflector and on another side with an absorbing layer, an embodiment of this invention uses non-conforming dielectric layer coated on a same side of a microstructured substrate as a reflective layer and absorbing layer. Therefore the Fabry-Perot structure is supported by the substrate. This provides numerous advantages. One advantage is that the coating can be removed from the substrate if coated with a release layer. Furthermore this coating can be made into shaped flakes if carefully removed from the substrate.

0012The Fabry-Perot structure of this invention provides different color shifting regions adjacent to one another which preferably differ in their color from one another by at least a delta E value of 10.

0013It is an object of this invention to provide a device, which exhibits different color shifting regions, visible with magnification, wherein adjacent color shifting regions provide a color shift between two distinct different colors due to the dielectric spacer layer having a varying thickness.

0014It is an object of this invention to provide a substrate having relief structures across its surface so that a cross section thereof has a varying thickness, and to mirror that varying thickness by applying a non-conforming layer filling depressions, valleys and troughs with a dielectric material so as to provide a Fabry-Perot structure having a spacer layer which provides color shift differences corresponding to the thickness of the substrate.

0015It is an object of this invention to provide at least one conforming layer and a non- conforming layer to fabricate a Fabry-Perot color-shifting filter, and wherein a substrate supporting the Fabry-Perot filter is purposefully embossed with a predetermined pattern to provide encoding that will form color-shifting indicia within the filter.

0016It is a further object of this invention to provide a flake having a non-conforming dielectric layer with at least one conforming layer and another conforming or non-conforming layer, wherein the flake is a color shifting device.

Summary of the Invention

0017In accordance with the invention, there is provided a color shifting security device comprising: a first absorbing or reflecting layer having a microstructured surface; a second absorbing or reflecting layer; and a dielectric non-conforming layer disposed between the first absorbing or reflecting layer and the second absorbing or reflecting layer having a surface contacting and complementary with the microstructured surface, wherein at least one of the first and second layers is an absorbing layer, and wherein a cross section of the dielectric non-conforming layer has a varying thickness such that at least one region is substantially thicker than a thinner adjacent region of said layer, and wherein a visible color difference is seen when viewing the filter through the one region and the adjacent region from a same location simultaneously when light is incident upon the filter.

0018In a preferred embodiment of the invention the first absorbing or reflecting layer, or the second absorbing or reflecting layer, has a substantially uniform thickness, which varies by no more than 20%, and/or the difference in thickness of cross-section of the dielectric non conforming layer is more than 1/8 wavelengths of visible light and less than 8 quarter wavelengths of visible light.

0019In a particular embodiment the regions of the device corresponding to particular microstructures form visible indicia that can be seen with magnification, and wherein the height or depth of some of the microstructures are at least 50nm.

0020Optionally, at least some of the particular microstructures form valleys, which in cross-section form flat-bottomed valleys.

0021Optionally, peaks of the particular microstructures in cross-section are flat-topped structures.

0022Optionally, the color shifting security device comprises a substrate supporting the first absorbing or reflecting layer, wherein the substrate has microstructures corresponding to the microstructured surface of the first absorbing or reflecting layer.

0023Optionally, the microstructures define a logo or discernible indicia.

0024In accordance with this invention, a security device is provided comprising: <ul id="ul0001" list-style="none" compact="compact"><li>a Fabry-Perot cavity having: a first layer having a microstructured upper surface, a second layer, and a deposited dielectric non-conforming layer having an upper surface and a lower surface disposed between the microstructured upper surface of the first and second layer, wherein the lower surface of the dielectric layer conforms to the microstructured upper surface of the first layer, and where the upper surface of the dielectric layer does not conform to the microstructured surface of the first layer, wherein a cross section of the dielectric layer has a varying thickness such that at least one region is substantially thicker than an adjacent region, wherein the first and second layers are absorber layers, or one of the first and second layers is a reflector layer and the other of the first and second layers is an absorber layer.</li></ul>

0025In accordance with this invention a color shifting security device is provided, which exhibits two different colors from a same viewing location comprising: <ul id="ul0002" list-style="none" compact="compact"><li>one or more deposited layers forming a microstructure, wherein at least one of the layers is a reflecting or absorbing layer;</li><li>an infill non-conforming dielectric material filling in grooves within the microstructure to form a planar surface over a continuous region of the microstructure; and an absorbing or reflective cover layer covering at least a part of the continuous region, wherein the one or more deposited layers or the cover layer is an absorber layer.</li></ul>

0026In accordance with another aspect of the invention a method is provided of fabricating a security device comprising: <ul id="ul0003" list-style="none" compact="compact"><li>providing a microstructured substrate;</li><li>coating the microstructured substrate with a first reflective or absorbing coating which conforms to the microstructure substrate;</li><li>coating the reflective or absorbing coating with a non-conforming dielectric leveling coating which at least partially fills voids within the microstructured coating; and,</li><li>coating the non-conforming dielectric leveling coating with a second absorbing coating or a reflective coating, wherein one of the first and second coatings are an absorbing coating.</li></ul>

0027In a particular embodiment the aforementioned color shifting structure is a flake.

0028In accordance with another aspect of the invention, there is provided a color shifting security device as defined herein, wherein the first absorbing or reflecting layer, the second absorbing or reflecting layer and the dielectric non-conforming layer, together form a Fabry-Perot cavity, and wherein the non-conforming layer is formed of a deposited non-conforming material.

0029Optionally, the Fabry-Perot cavity forms a flake after being removed from a substrate.

0030Optionally, the color shifting security device, further comprises a substrate, wherein the substrate and layers thereon form a foil.

0031Optionally, the first and second absorbing or reflecting layers are conforming deposited layers.

0032Optionally, the second conforming deposited layer is a reflector layer, and the color shifting security device further comprises: <ul id="ul0004" list-style="none" compact="compact"><li>a second non-conforming dielectric layer contacting the reflector layer having an absorbing layer over the second non-conforming dielectric layer, thereby forming a two-sided color shifting device, and</li><li>wherein the dielectric non-conforming layer and the second dielectric non-conforming layer both have a varying thickness in cross-section.</li></ul>

0033Optionally, the dielectric non-conforming layer contacts the second absorbing or reflecting layer.

0034Optionally, the dielectric non-conforming layer is a discontinuous layer having gaps between regions of different thickness of dielectric material.

0035Optionally, the dielectric non-conforming layer fills in grooves within the microstructured surface to form a planar surface over a continuous region of the microstructured surface; and wherein the second absorbing or reflective layer covers at least a part of the continuous region.

0036According to another aspect of the invention, there is provided a color shifting security device, which exhibits two different colors from a same viewing location comprising: <ul id="ul0005" list-style="none" compact="compact"><li>a first absorbing or reflecting deposited layer having a microstructured surface; an infill non-conforming dielectric material able to fill in grooves within the microstructured surface to form a non-conforming dielectric layer having a planar surface over a continuous region of the microstructured surface, and regions of different thicknesses able to provide two different color shifting regions;</li><li>a second absorbing or reflecting deposited cover layer covering at least a part of the continuous region;</li></ul> and wherein one of the first and second absorbing or reflecting layers is an absorber layer.

0037Optionally, the color shifting security device further comprises a substrate supporting the first absorbing or reflecting layer, wherein the substrate has microstructures corresponding to the microstructured surface of the first absorbing or reflecting layer.

0038Optionally, the microstructures have selectively chosen depths, such as in cross-section flat-bottomed valleys, or protuberances in the form of upstanding features, such as in cross-section flat-topped structures.

0039Optionally, microstructures have a number of distinct levels or depths.

0040Optionally, the microstructures define a logo or discernible indicia.

0041Optionally, the grooves are of two different depths.

0042Optionally, the first absorbing or reflecting layer, the second absorbing or reflecting layer, and the dielectric non-conforming layer, together form a Fabry-Perot cavity.

0043Optionally, the Fabry-Perot cavity forms a flake.

0044Optionally, the first absorbing or reflecting layer, or the second absorbing or reflecting layer, has a substantially uniform thickness, which varies by no more than 20%.

0045Optionally, a difference in thickness of a cross-section of the dielectric non-conforming layer is more than 1/8 wavelengths of visible light and less than 8 quarter wavelengths of visible light.

0046Optionally, the color shifting security device further comprises a second dielectric layer.

0047Optionally, the second dielectric layer conforms to the microstructured surface.

0048Optionally, the second dielectric layer is disposed between the first absorbing or reflecting deposited layer having a microstructured surface and the non-conforming dielectric layer.

0049Optionally, the non-conforming dielectric layer includes a first material that conforms to the microstructured surface and a second non-conforming material that fills in grooves within the first material.

0050Optionally, the non-conforming dielectric layer is a discontinuous layer having gaps between regions of different thickness of dielectric material.

Brief Description of the Drawings

0051Exemplary embodiments of the invention will now be described in conjunction with the drawings in which: <ul id="ul0006" list-style="none" compact="compact"><li><figref idref="f0001">Fig. 1</figref> is cross-sectional view of a prior art three-layer Fabry-Perot cavity.</li><li><figref idref="f0002">Fig. 2a</figref> is cross-sectional view a prior art substrate having frames in relief as upstanding walls extending from the substrate surface and an upstanding logo.</li><li><figref idref="f0002">Fig. 2b</figref> is an isometric view of the prior art structure of <figref idref="f0002">Fig. 2a</figref>.</li><li><figref idref="f0002">Fig. 2c</figref> is a plan view of the prior art structure shown in <figref idref="f0002">Fig. 2b</figref>.</li><li><figref idref="f0003">Fig. 3a</figref> is a cross-sectional view of a prior art substrate having grooved frames and a grooved logo.</li><li><figref idref="f0003">Fig. 3b</figref> is an isometric view of the prior art structure of <figref idref="f0003">Fig. 3a</figref>.</li><li><figref idref="f0003">Fig. 3c</figref> is a plan view of the prior art structure shown <figref idref="f0003">Fig. 3b</figref>.</li><li><figref idref="f0004">Fig. 4a</figref> is a cross-sectional view of a prior art substrate having grooved frames and a grooved grating across its surface.</li><li><figref idref="f0004">Fig. 4b</figref> is an isometric view of the prior art structure of <figref idref="f0004">Fig 4a</figref>.</li><li><figref idref="f0004">Fig 4c</figref> is a plan view of the prior art structure shown in <figref idref="f0004">Fig. 4b</figref>.</li><li><figref idref="f0005">Fig. 4d</figref> is a cross-sectional view of a substrate having a squared array of peaks and valleys.</li><li><figref idref="f0005">Fig. 4e</figref> is an isometric view of the prior art structure of <figref idref="f0005">Fig. 4d</figref>.</li><li><figref idref="f0005">Fig. 4f</figref> is a plan view of the prior art structure shown in <figref idref="f0005">Fig. 4d</figref>.</li><li><figref idref="f0006">Fig. 5a</figref> is a prior art cross-section of a microstructured foil wherein symbols are a same depth and wherein the coating is a uniform thickness.</li><li><figref idref="f0006">Fig. 5b</figref> is a prior art cross-section of a microstructured foil wherein symbols are a same depth and wherein the coating is a non-uniform thickness.</li><li><figref idref="f0007">Fig. 6</figref> is a prior art microstructured substrate having grooves therein coated with three conforming layers forming a Fabry-Perot color shifting coating.</li><li><figref idref="f0008">Fig. 7</figref> is a cross-sectional view of a microstructured structure having a conforming reflector layer, a non-conforming dielectric layer and an absorber layer together forming a Fabry Perot structure in accordance with this invention wherein two different alternating color shifting regions are provided due to the difference in thickness of the non-conforming dielectric layer.</li><li><figref idref="f0009">Fig. 8</figref> is a cross-sectional view of a microstructured structure having a conforming reflector layer, a non-conforming dielectric layer and an absorber layer together forming a Fabry Perot structure in accordance with this invention wherein three different alternating color shifting regions are provided due to the difference in thickness of the non-conforming dielectric layer.</li><li><figref idref="f0010">Fig. 9</figref> is a cross-sectional view of an embodiment of the invention wherein a Fabry- Perot structure in the form of a microstructured foil has a conforming dielectric layer adjacent to a non-conforming dielectric layer.</li><li><figref idref="f0011">Fig. 10</figref> is a cross-sectional view of an embodiment of the invention wherein a conforming and non-conforming dielectric layers are used and wherein an upper surface of the two dielectrics are at a same level such that a deposited absorber layer thereover is planar.</li><li><figref idref="f0012">Fig. 11</figref> is a cross-sectional view of a microstructured substrate having a release coat for forming flakes in accordance with this invention.</li><li><figref idref="f0013">Fig. 12</figref> is a cross-sectional view of a coating for forming a shaped flake in accordance with this invention wherein conforming and non-conforming layers are used and wherein a reflective layer is a central layer such that the flake is color shifting when viewed from either side.</li><li><figref idref="f0014">Fig. 13</figref> is cross-sectional view of an alternative embodiment wherein a reflector layer is not required and is replaced with an additional absorber layer wherein color shifting is seen from both sides.</li></ul>

Detailed Description

0052The invention is related to the use of thin dielectric non-conforming layers on microstructured surfaces allowing for the manufacturing of devices having micro areas of different color shifting. The different colors are obtained by thin film interference when the thickness of the dielectric layer varies in different regions. Different color shifting refers to a different range of colors; for example due to the thickness of the spacer layer in different regions of the device, one region may shift from orange to brown and another region may shift from gold to green.

0053Conforming deposited layers are obtained when the species in the vapor phase condenses as a solid. This is the case of most of the metals and their compounds; when oxides, nitrides, carbides, fluorides, combinations, etc. are deposited by standard vacuum physical vapor deposition, sputtering and evaporation, or by chemical vapor deposition.

0054Once the species in the vapor phase condenses on a substrate, there is not enough mobility of the condensed species in the form of mobile atoms, radicals or molecules. Therefore the condensed species will be fixed on the surface of the substrate following the original roughness of the substrate.

0055In contrast, a non-conforming layer will act similar to a layer of water resting upon a surface, filling any roughness of the surface to create a planar surface independently of the roughness of the surface. When water is solidified, for example by freezing in optimal conditions when the layer is not disturbed during the freezing process, the solid layer will present the smoothness of the original water liquid layer. Water will fill in any voids and will yield a planar upper surface.

0056Although the illustrative example of water allows one to envisage how a non- conforming layer behaves, other materials, in particular some selected monomers exhibiting similar behaviour, provide the smoothing or planarizing properties in the liquid state and can be solidified by a post polymerization stage by ultra-violet (UV) or electron radiation. Selected light transmissive monomers having preferred properties such as a suitable refractive index can be used as a spacer layer in a Fabry-Perot filter.

0057To deposit monomers they are heated within a container so as to produce a vapor. When the vapor makes contact with a cooler surface in proximity it condenses upon the cooler surface. Therefore, non-conforming layers are obtained when a monomer in the gas phase is brought into contact with a cooled substrate whereby the gas phase condenses forming a liquid layer. In accordance with this invention, the liquid layer supported by the substrate is subsequently cured, producing the polymerization of the liquid monomer into a solid layer.

0058The monomer can be evaporated by heating it in a reservoir with an aperture or nozzle used to build the desired pressure of the monomer vapor before it expands in the vacuum chamber. If the vapor pressure of the monomer is not high enough to produce a gas stream directed at the substrate, an inert gas can be introduced into the liquid monomer. In an alternative embodiment, the liquid monomer can be directly sprayed in a hot reservoir to be instantaneously evaporated to achieve flash evaporation. Care must be taken to ensure that the temperature of the reservoir is low enough to avoid degradation of the monomer or its thermal polymerization.

0059Although evaporation is the preferred method of depositing the dielectric monomer, printing, painting, extrusion, spin-off, or the use of a doctoring-blade, may be considered; however, often these technologies have the tendency to form layers that are too thick to create interference for visible wavelengths of light. Various monomers and/or oligomers can be used as non-conforming layers in this invention. By way of example, the non-confirming layer can be formed using any of the following materials: epoxy acrylates, urethane acrylates, polyester acrylates, polyether acrylates, amine modified polyether acrylates, acrylic acrylates and miscellaneous acrylate oligomers.

0060This invention provides a method for fabricating one or more thin-film Fabric-Perot interference devices upon a microstructured substrate that will exhibit a color change when irradiated with visible light when the angle of incidence or viewing angle changes.

0061Referring now to prior art <figref idref="f0001">Fig. 1</figref> a three-layer Fabry-Perot cavity is shown. The substrate 100 has deposited thereon a conforming layer 101a of a highly reflective material such as Al. Deposited on the aluminum layer 101a is a dielectric conforming layer 102a. A conforming absorber layer 103 a is subsequently deposited on the dielectric layer 102a. Using conventional vacuum coating techniques results in a thin film optically variable filter upon a substrate wherein each layer has a substantially uniform thickness. Notably, since the surface of the substrate is flat, each layer will be a uniform thickness whether conforming layers or nonconforming layers are deposited, providing a same optical effect when applied to a planar surface such as that in <figref idref="f0001">Fig. 1</figref>. However, the optical effects obtained for conforming or non-conforming layers will be different when the substrate has a microstructured surface. Non-conforming layers will fill in voids where conforming layers simply conform to the microstructured surface so that they are substantially uniform in thickness.

0062In operation, a thin-film Fabry-Perot filter functions as a color changing element; as the angle of light incident upon the cavity is varied between the light source and the viewer, the color varies as a function of the path length through the dielectric layer varying with the change in angle.

0063Turning now to <figref idref="f0002">Fig. 2a</figref> a substrate is shown in cross-section where microstructures 201 pointing upward from the substrate are shown, and wherein the height of the upstanding structures is uniform. A three dimensional perspective isometric view is shown in <figref idref="f0002">Fig. 2b</figref> and a top view is shown in <figref idref="f0002">Fig. 2c</figref>.

0064<figref idref="f0003">Figs. 3a through 3c</figref> illustrate an embodiment wherein the microstructures within the substrate 300 are in the form of grooves 301 of varying depth within the substrate.

0065<figref idref="f0004">Figs 4a through 4c</figref> show a substrate 400 wherein a grating formed of grooves 401 of a first depth are bound by deeper framing grooves 402 within the substrate.

0066<figref idref="f0006">Fig. 5a and 5b</figref> show a cross section of a substrate coated with a coating material where the layer has been grown atom by atom by conventional vacuum coating processes as evaporation and sputtering. The layer conforms to the substrate following the original microstructure of the surface. If for example a 3 layer <i>RID</i>/A is coated, the same color by thin film interference will be seen everywhere in the substrate since the thickness of the dielectric is constant as shown in <figref idref="f0007">Fig. 6</figref>.

0067Referring now to prior art <figref idref="f0007">Fig. 6</figref> a substrate 600 having embossed grooves 612 and 614 of varying depth shows a reflector layer 601 of a first uniform thickness, a dielectric layer 602 of a second uniform thickness, and an absorber layer 603 of a third uniform thickness coated over the substrate 600 wherein of the layers are conforming layers.

0068A first embodiment of the invention is shown in <figref idref="f0008">Fig. 7</figref> wherein the same substrate as shown in <figref idref="f0007">Fig. 6</figref> is used however one of the coating layers in <figref idref="f0008">Fig. 7</figref> is non-conforming providing a functionally differing device from <figref idref="f0007">Fig. 6</figref>. Turning now to <figref idref="f0008">Fig. 7</figref> a substrate 700 is shown having a conforming reflector layer 701 of uniform thickness coated directly thereon. Upon the reflector layer is a non-conforming coating of dielectric material, which fills in the grooves within the reflector coated substrate and has an upper substantially planar layer. As a result the dielectric layer 702 has a varying thickness, in cross-section, as shown. Two different thicknesses result when the dielectric layer is coated over substrate 700 due to the two different depths within the microstructured substrate 700. The two different depths of the dielectric spacer layer provide two different color shifting regions, where the color shifts from a different first color, to a different second color in the regions of different thickness. For a perceivable color difference to be seen in the two regions of different thickness, a thickness difference in the spacer or dielectric layer, is required. As can be seen in <figref idref="f0008">Fig. 7</figref> the thickness difference in the spacer layer is considerably larger than the combined thickness of the adjacent two layers 703 and 701. An absorber layer 703 having a substantially uniform thickness is shown over the dielectric layer 702. The absorber layer 703 could be a conforming layer or a non-conforming layer since it is a planar layer applied onto a planar surface. However, preferably, a conforming absorber layer is used, typical of conventional color-shifting filters. The thickness of the dielectric layer can be selectively controlled by providing microstructures having selectively chosen depths or protuberances in the form of upstanding features, as the dielectric layer essentially fills in voids resulting in a varying of its thickness. In <figref idref="f0008">Fig. 7</figref> color shifting regions 706 having a first color shifting range of colors and color shifting regions 708 have a second color shifting range of colors. Typical thickness ranges for the absorber layer would be 20 Angstroms to 150 Angstroms depending upon which metal was selected. The reflectivity of the reflector layer is preferably at least 20% to provide an adequate visual effect from the device and the dielectric spacer layer could vary be as much as 800 nm.

0069When a non-conforming or conforming dielectric is applied to a single level macrostructure surface such as that of <figref idref="f0001">Fig. 1</figref>, two different colors will be produced by thin film interference corresponding to the different thickness of the planarizing dielectric layer as the angle of incidence increases. Notice that the reflector and absorber layers applied are conforming layers. Since a dielectric polymeric layer tends to have an index of refraction in between 1.5 and 1.7, the thin-film interference will produce colors that shift from high to low wavelengths as the angle of illumination increases.

0070Advantageously, a release layer can be applied in between the substrate and the deposited layers with the intention to strip off the multilayer to make micro multi-color shifting microstructured pigment flakes. The release layer can also be used to transfer the multilayer to another object. If the device is intended to make thread, yam, or foils it may not require the use of release layers. Such flakes are typically less than 100 mm or equal thereto, across a longest length. The difference shown in the figures between the two dielectric thicknesses are exaggerated. The aspect ratio for the microstructured character is 100-500nm of depth for a line width that is typically 1-5um.

0071The microstructure within the substrate can represent symbols, logos, grating, frames, peaks/valleys, etc. as shown in <figref idref="f0002 f0003">Figs 2a through 3c</figref>. Advantageously the color shifting coating provides a way in which these features, such as logos, etc., can be enhanced.

0072Turning now to <figref idref="f0009">Fig. 8</figref> a second embodiment of the invention is shown wherein grooves in substrate 800 are of two different depths. When the non-conforming dielectric layer 802 is deposited over the conforming reflector layer 801 and an absorbing layer 803 is applied thereover, the resulting structure is a Fabry-Perot color-shifting filter having three distinct ranges of color shifting. The non-conforming layer provides a planarizing smoothing effect upon which layer 803 is deposited conforming to this planarized layer. As the number of distinct levels or depths within the microstructure increases the number of ranges of color shifting increases accordingly.

0073<figref idref="f0010">Fig. 9</figref> illustrates an embodiment of the invention wherein a microstructured substrate 900 is coated with a conforming reflector layer 901 and where conforming and non-conforming dielectric layers 902a and 902b respectively are used adjacent to one another in a same device. A planar absorber layer 903 is coated over the non-conforming dielectric layer 902b. This planar layer 903 could be a conforming or a non-conforming layer since it is being applied to a planar surface. In this device three different color ranges are seen due to the three thicknesses of the combined dielectric layers. As mentioned previously, generally non-conforming polymeric dielectric layers have a lower refractive index than standard inorganic oxides layers.

0074By using a judiciously selected combination of a high refractive index inorganic dielectric with a lower refractive index polymer dielectric further control the color shifting properties can be attained.

0075<figref idref="f0010">Fig. 9</figref> exemplifies a microstructured foil.

0076Turning now to the device of <figref idref="f0011">Fig. 10</figref> shown in cross section, the microstructure substrate 1000 is shown coated with a reflector layer 1001, which is coated with a conforming first dielectric layer 1002a. A second non-confirming polymeric layer 1002b is coated and only fills in trenches or grooves within the coated substrate 1001. Absorber layer 1003 is coated as a top layer forming together with the other coated layers a color-shifting filter. In practice this could be achieved by eliminating the top of the polymeric dielectric of <figref idref="f0010">Fig. 9</figref>, for example by ion bombarding under vacuum until reaching suitable level of the inorganic oxide layer prior to the deposition of the absorber layer.

0077An alternative embodiment of the invention described heretofore is shown in <figref idref="f0012">Fig. 11</figref>. In this instance a substrate 1100 having protuberances or upstanding structures is shown. This embodiment lends itself more to applying a release layer than the previously described structures. If a release layer is applied, it is first applied prior to depositing the reflector layer 1101, so that the reflector layer and subsequent deposited layer can together be released from the substrate. The organic non-conforming dielectric layer 1102 is deposited to a level lower than the higher areas that will be used as braking points to produce the shaped flakes. Only the thin layers corresponding to the reflector 1101 and absorber 1103 will be in the top of these areas.

0078After separating the multilayer from the substrate and forming shaped flakes, these flakes will have different properties when viewed from different sides. When viewed from the side having a reflector layer, the flakes will simply be reflective. However on the opposite side, a viewer with magnification would see the logos or symbols with a color shifting exhibited surrounded by a background of a different color. From the reflective side logos may be discernible however the color will correspond to that of the reflector layer.

0079In an alternative embodiment if the absorber layer is not applied, the top of the higher areas have a thin metal layer exposed surrounded by a dielectric layer. In this instance, the top areas can be used as seed point to grow preferentially other layers, for example one can perform electroplating using the exposed metallic layer as electrodes. Such devices can be used for other applications such as for sensors where micro exposed metallic layers are necessary.

0080An embodiment similar to that shown in <figref idref="f0012">Fig. 11</figref> is shown in <figref idref="f0013">Fig. 12</figref> however the multilayer Fabry-Perot filter is formed of a five-layer structure with layers A/D/R/D/A. Since the reflector layer 1201 is shown as a central layer, color shifting will be seen from both sides of this flake after it is released from the substrate 1200. Upon the substrate is a release layer, not shown and a first absorber layer 1203a. Upon the first absorber layer is a first non-conforming dielectric layer 1202a. The reflector layer 1201 is shown deposited upon the first dielectric layer 1202a. A second non-conforming dielectric layer 1202b is deposited over the reflector layer 1201 and a conforming 2nd absorber layer 1203b is deposited over the second non-conforming dielectric layer 1202b. After releasing the multilayer, the shaped flakes when broken along the breaking lines, exhibit on side 1 the Symbol 2 with a non-shifting color corresponding to Absorber /Reflector and symbol 1 corresponding to a color shifting (CS4) from the multilayer Absorber/Dielectric/Reflector surrounded by another color shifting background (CS3).

0081When viewed on side 2 the flake will show a color-shifting (CS2) symbol 2 with a background of a different color (CS 1). Symbol 1 will not be seen due to the presence of the opaque reflector layer. Since these flakes are small and below resolution that can be seen with an unaided eye, magnification would be required to see these aforementioned features.

0082The embodiment shown in <figref idref="f0014">Fig. 13</figref> differs to the embodiment shown in <figref idref="f0012">Fig. 11</figref> in the optical design used to create the thin-film interference. In <figref idref="f0014">Fig. 13</figref> a microstructured substrate 1300 is shown having a first conforming absorber layer 1301 instead of a reflector layer. A non conforming dielectric layer 1302 is coated over layer 1301 and a conforming 2nd absorber layer 1303 is coated over the dielectric layer. Thin film interference is obtained by this three-layer Absorber/Dielectric/ Absorber design. Such optical designs are semi transparent. If coated on a substrate with the features up shown in a previous embodiment with logos with a single height, the shaped flakes will show the symbols with a different color than their background in both sides. If the symbols have more than one height in cross-section, different areas of the logo will show different colors.

0083In all instances, the variation in the thickness of the dielectric layer is much greater than the thickness of each of the two layers adjacent the dielectric layer.

0084By depositing a non-conforming dielectric spacer layer in a Fabry-Perot structure, this invention allows for the fabrication of filters which have a varying thickness spacer layer and wherein the thickness can be precisely controlled. This allows for a single layer be it either continuous or segmented to provide different color shifting in different regions across the filter as function of the spacer layer thickness. Either flakes or foil can be made. Typically the nonconforming dielectric layer is coated over a conforming layer and covered with a conforming layer, however the dielectric layer could be coated over a non-conforming layer or may be covered with a non-conforming layer.