Small pore molecular sieve supported copper catalysts durable against lean/rich aging for the reduction of nitrogen oxides
13 claims: 2 independent, 11 dependent
- 1A chemical process for treating exhaust gas from a vehicular internal combustion engine with a lean/rich cycle using a selective catalytic reduction (SCR) catalyst, which chemical process comprising generating NH 3 nitrogenous reductant over a NO X adsorber catalyst (NAC) during periodic rich regeneration events, exposing the SCR catalyst in a NAC+(downstream)SCR catalyst system to at least one reactant including nitrogen oxides and reducing the nitrogen oxides with the NH 3 nitrogenous reductant generated over the NAC during the periodic rich regeneration events, wherein the SCR catalyst comprises copper and a small pore molecular sieve having a maximum ring size of eight tetrahedral atoms and wherein additional nitrogenous reductant is metered into a flowing exhaust gas only when the SCR catalyst is at above 100°C.
Independent claims2
75 paragraphs in 5 sections, as filed
FIELD OF THE INVENTION
0001The present invention relates to small pore molecular sieve supported copper catalysts that are durable after being exposed to a reducing atmosphere, particularly after high temperature exposure.
BACKGROUND OF THE INVENTION
0002Selective catalytic reduction (SCR) of NO<sub>X</sub> by nitrogenous compounds, such as ammonia or urea, has developed for numerous applications including for treating industrial stationary applications, thermal power plants, gas turbines, coal-fired power plants, plant and refinery heaters and boilers in the chemical processing industry, furnaces, coke ovens, municipal waste plants and incinerators, and a number of vehicular (mobile) applications, e.g., for treating diesel exhaust gas.
0003Several chemical reactions occur in an NH<sub>3</sub> SCR system, all of which represent desirable reactions that reduce NO<sub>X</sub> to nitrogen. The dominant reaction is represented by reaction (1). 4NO + 4NH<sub>3</sub> + O<sub>2</sub> → 4N<sub>2</sub> + 6H<sub>2</sub>O (1)
0004Competing, non-selective reactions with oxygen can produce secondary emissions or may unproductively consume ammonia. One such non-selective reaction is the complete oxidation of ammonia, shown in reaction (2). 4NH<sub>3</sub> + 5O<sub>2</sub> → 4NO + 6H<sub>2</sub>O (2) Also, side reactions may lead to undesirable products such as N<sub>2</sub>O, as represented by reaction (3). 4NH<sub>3</sub> + 4NO + 3O<sub>2</sub> → 4N<sub>2</sub>O + 6H<sub>2</sub>O (3)
0005Catalysts for SCR of NO<sub>X</sub> with NH<sub>3</sub> may include, for example, aluminosilicate molecular sieves. One application is to control NO<sub>X</sub> emissions from vehicular diesel engines, with the reductant obtainable from an ammonia precursor such as urea or by injecting ammonia <i>per se</i>. To promote the catalytic activity, transition metals may be incorporated into the aluminosilicate molecular sieves. The most commonly tested transition metal molecular sieves are Cu/ZSM-5, Cu/Beta, Fe/ZSM-5 and Fe/Beta because they have a relatively wide temperature activity window. In general, however, Cu-based molecular sieve catalysts show better low temperature NO<sub>X</sub> reduction activity than Fe-based molecular sieve catalysts.
0006In use, ZSM-5 and Beta molecular sieves have a number of drawbacks. They are susceptible to dealumination during high temperature hydrothermal ageing resulting in a loss of acidity, especially with Cu/Beta and Cu/ZSM-5 catalysts. Both beta- and ZSM-5-based catalysts are also affected by hydrocarbons which become adsorbed on the catalysts at relatively low temperatures and are oxidized as the temperature of the catalytic system is raised, generating a significant exotherm, which can thermally damage the catalyst. This problem is particularly acute in vehicular diesel applications where significant quantities of hydrocarbon can be adsorbed on the catalyst during cold-start; and Beta and ZSM-5 molecular sieves are also prone to coking by hydrocarbons.
0007In general, Cu-based molecular sieve catalysts are less thermally durable, and produce higher levels of N<sub>2</sub>O than Fe-based molecular sieve catalysts. However, they have a desirable advantage in that they slip less ammonia in use compared with a corresponding Fe-molecular sieve catalyst.
0008<patcit id="pcit0001" dnum="WO2008132452A"><text>WO 2008/132452</text></patcit> discloses a method of converting nitrogen oxides in a gas to nitrogen by contacting the nitrogen oxides with a nitrogenous reducing agent in the presence of a zeolite catalyst containing at least one transition metal, wherein the zeolite is a small pore zeolite containing a maximum ring size of eight tetrahedral atoms, wherein the at least one transition metal is selected from the group consisting of Cr, Mn, Fe, Co, Ce, Ni, Cu, Zn, Ga, Mo, Ru, Rh, Pd, Ag, In, Sn, Re, Ir and Pt.
0009<patcit id="pcit0002" dnum="WO2008118434A1"><text>WO 2008/118434 A1</text></patcit> discloses a hydrothermally stable microporous crystalline material comprising a molecular sieve or zeolite having an 8-ring pore opening structure, such as SAPO-34 or aluminosilicate zeolite, able to retain a specific percentage of its surface area and micropore volume after treatment with heat and moisture, such as at least 80% of its surface area and micropore volume after exposure to temperatures of up to 900°C in the presence of up to 10 volume percent water vapour for a time ranging from 1 to 16 hours. Methods of using the disclosed crystalline material, such as in the SCR of NOx in exhaust gas are also disclosed, as are methods of making such materials.
0010<patcit id="pcit0003" dnum="WO2008106518A"><text>WO 2008/106518</text></patcit> discloses a combination of a fiber matrix wall flow filter and a hydrophobic chabazite molecular sieve as a SCR catalyst on the fiber matrix wall flow filter. The filter purportedly achieves improved flexibility in system configuration and lower fuel costs for active regeneration. Such active regeneration would likely encompass exposure to lean atmospheric conditions. The reference, however, does not contemplate subjecting the filter to reducing conditions. The reference also fails to disclose or appreciate maintaining the durability of a catalyst after being exposed to such a reducing atmosphere.
0011<patcit id="pcit0004" dnum="US2007269353A1"><text>US 2007/269353 A1</text></patcit> discloses am emissions treatment system for an exhaust stream, having a NOx storage reduction (NSR) catalyst with a NOx sorbent at a concentration of at least 0.1 g/in<sup>3</sup> and a platinum group metal component dispersed on a refractory metal oxide support; and an SCR catalyst disposed downstream of the NSR catalyst.
0012<nplcit id="ncit0001" npl-type="s"><text>T. Ishihara et al. published a paper entitled "Copper ion-exchanged SAPO-34 as a thermostable catalyst for selective reduction of NO with C3H6" in Journal of Catalysis, 169, pages 93-102</text></nplcit>.
SUMMARY OF THE INVENTION
0013A chemical process for treating exhaust gas from a vehicular internal combustion engine with a lean/rich cycle using a selective catalytic reduction (SCR) catalyst, which chemical process comprising generating NH<sub>3</sub> nitrogenous reductant over a NO<sub>x</sub> adsorber catalyst (NAC) during periodic rich regeneration events, exposing the SCR catalyst in a NAC+(downstream)SCR catalyst system to at least one reactant including nitrogen oxides and reducing the nitrogen oxides with the NH<sub>3</sub> nitrogenous reductant generated over the NAC during the periodic rich regeneration events, wherein the SCR catalyst comprises copper and a small pore molecular sieve having a maximum ring size of eight tetrahedral atoms and wherein additional nitrogenous reductant is metered into a flowing exhaust gas only when the SCR catalyst is at above 100°C. Preferably, the catalyst is a copper promoted small pore molecular sieve, i.e., a small pore molecular sieve loaded with copper. The small pore molecular sieve can be selected from the group of Framework Type Codes consisting of CHA, LEV, ERI and DDR.
0014In order that the invention may be more fully understood, reference is made to the following drawing by way of illustration only, in which: <ul id="ul0001" list-style="none" compact="compact"><li><figref idref="f0001">Figure 1</figref> is a graph illustrating NO<sub>X</sub> conversion of medium pore and large pore molecular sieve supported copper catalysts after lean hydrothermal aging and lean/rich cycle aging;</li><li><figref idref="f0002">Figure 2</figref> is a graph illustrating NO<sub>X</sub> conversion of Fe/molecular sieve catalysts after lean hydrothermal aging and lean/rich cycle aging;</li><li><figref idref="f0003">Figure 3</figref> is a graph illustrating NO<sub>X</sub> conversion of small pore molecular sieve supported copper catalysts according to embodiments of the invention and a comparative Cu/Beta catalyst after lean hydrothermal aging and lean/rich cycle aging; and</li><li><figref idref="f0004">Figure 4</figref> is a graph illustrating NO<sub>X</sub> conversion efficiency over a NAC and combined NAC+SCR systems with different SCR catalysts according to embodiments of the invention and comparative examples.</li></ul>
DETAILED DESCRIPTION OF THE INVENTION
0015A method of treating NO<sub>X</sub> in an exhaust gas of a lean burn internal combustion engine is to store the NO<sub>X</sub> from a lean gas in a basic material and then to release the NO<sub>X</sub> from the basic material and reduce it periodically using a rich gas. The combination of a basic material (such as an alkali metal, alkaline earth metal or a rare earth metal), and a precious metal (such as platinum), and possibly also a reduction catalyst component (such as rhodium) is typically referred to as a NO<sub>X</sub> adsorber catalyst (NAC), a lean NO<sub>X</sub> trap (LNT), or a NO<sub>X</sub> storage/reduction catalyst (NSRC). As used herein, NO<sub>X</sub> storage/reduction catalyst, NO<sub>X</sub> trap, and NO<sub>X</sub> adsorber catalyst (or their acronyms) may be used interchangeably.
0016Under certain conditions, during the periodically rich regeneration events, NH<sub>3</sub> may be generated over a NO<sub>X</sub> adsorber catalyst. The addition of a SCR catalyst downstream of the NO<sub>X</sub> adsorber catalyst may improve the overall system NO<sub>X</sub> reduction efficiency. In the combined system, the SCR catalyst is capable of storing the released NH<sub>3</sub> from the NAC catalyst during rich regeneration events and utilizes the stored NH<sub>3</sub> to selectively reduce some or all of the NO<sub>X</sub> that slips through the NAC catalyst during the normal lean operation conditions. As used herein, such combined systems may be shown as a combination of their respective acronyms, e.g., NAC+SCR or LNT+SCR.
0017The combined NAC+SCR system imposes additional requirements on the SCR catalyst component. Namely, besides having good activity and excellent thermal stability, the SCR catalyst has to be stable against lean/rich excursions. Such lean/rich excursions not only may occur during the regular NAC regeneration events, but also may happen during the NAC desulfation events. During the NAC desulfation events, the SCR catalyst may be exposed to temperatures much higher than it would be exposed to during the regular NO<sub>X</sub> regeneration events. Therefore, a good SCR catalyst that is suitable for the NAC+SCR systems needs to be durable after being exposed to a reducing atmosphere at high temperature.
0018Catalysts are often unstable when exposed to a reducing atmosphere, more particularly a high temperature reducing atmosphere. For example, copper catalysts are unstable during repeated lean/rich high temperature excursions, e.g., as is often encountered in vehicle exhaust gas or an exhaust gas treatment system. The reducing atmosphere occurs in the rich phase of a lean/rich excursion cycle. The reducing atmosphere conditions, however, can occur in a variety of environments including but not limited to environments typical for the regeneration or the desulfation of a NO<sub>X</sub> adsorber catalyst, and for the active regeneration of a catalysed soot filter, etc. Thus, as used herein, a reducing atmosphere is net reducing, for example, an exhaust gas having a lambda value of less than 1 (e.g., derived from an air/fuel ratio less than stoichiometric). Contrastingly, a non-reducing atmosphere is net oxidizing, e.g., having a lambda value greater than 1 (e.g., derived from an air/fuel ratio greater than stoichiometric).
0019Without wishing to be bound to a particular theory, it was believed prior to discovery of the present invention that molecular sieve supported copper catalysts would not maintain stability or activity when exposed to a reducing atmosphere (especially a reducing atmosphere encountered in a repeated lean/rich cycle excursions) because when exposed to the reducing atmosphere, the copper catalysts lost their activity. This loss of activity was suspected to be due to copper migration, sintering, and/or reduced copper dispersion. Surprisingly, we discovered in the present invention that small pore molecular sieve-supported copper catalysts maintained their catalytic activity even though the medium and large pore molecular sieve supported copper catalysts could not. It is believed that small pore molecular sieves provide a restriction on the copper from migrating out of the framework, sintering, losing copper dispersion, and beneficially resulting in an improved stability and activity of the catalyst. The medium and large pore molecular sieves, however, do not maintain their stability and activity when exposed to a reducing atmosphere possibly because of the effects of copper migration, sintering, and/or reduced copper dispersion.
0020According to the present invention, a chemical process for treating exhaust gas from a vehicular internal combustion engine with a lean/rich cycle using a selective catalytic reduction (SCR) catalyst comprises generating NH<sub>3</sub> nitrogenous reductant over a NO<sub>x</sub> adsorber catalyst (NAC) during periodic rich regeneration events, exposing the SCR catalyst in a NAC+(downstream)SCR catalyst system to at least one reactant including nitrogen oxides and reducing the nitrogen oxides with the NH<sub>3</sub> nitrogenous reductant generated over the NAC during the periodic rich regeneration events, wherein the SCR catalyst comprises copper and a small pore molecular sieve having a maximum ring size of eight tetrahedral atoms and wherein additional nitrogenous reductant is metered into a flowing exhaust gas only when the SCR catalyst is at above 100°C.
0021The chemical process according to the invention is exhaust gas treatment which is selective catalytic reduction using nitrogenous reductants, specifically in combination with a NO<sub>X</sub> adsorber catalyst, i.e. NAC+(downstream)SCR.
0022The SCR catalyst can be a SCR catalysed soot filter wherein the SCR catalyst comprises a copper promoted small pore zeolite sieve as described here.
0023Selective catalytic reduction may include (1) using ammonia or a nitrogenous reductant. Other reactants may include nitrogen oxides and oxygen.
0024The catalyst comprises a transition metal, preferably copper, and a small pore molecular sieve having a maximum ring size of eight tetrahedral atoms. As is used herein "molecular sieve" is understood to mean a metastable material containing tiny pores of a precise and uniform size that may be used as an adsorbent for gases or liquids. The molecules which are small enough to pass through the pores are adsorbed while the larger molecules are not. The molecular sieve framework may be defined as is generally acceptable by the International Zeolite Association framework type codes (at http://www.iza-online.org/). These molecular sieves are described in more detail below.
0025Molecular sieves are typically defined by the member rings as follows: large pore rings are 12-member rings or larger; medium pore rings are 10-member rings; and small pore rings are 8-member rings or smaller. The catalyst in the present invention is a small pore ring having a maximum ring size of eight tetrahedral atoms.
0026Most catalysts are supported on medium pore (10-ring, such as ZSM-5) or large pore (12-ring, such as Beta) molecular sieves. A molecular sieve supported copper SCR catalyst, for example, may exhibit wide temperature windows under NO only conditions. These catalysts, however, are not stable against repeated lean/rich high temperature aging as is demonstrated in <figref idref="f0001">Figure 1</figref>. In <figref idref="f0001">Figure 1</figref>, a Cu/Beta catalyst (large pore) and a Cu/ZSM-5 catalyst (medium pore) are shown under hydrothermal aging conditions and lean/rich aging conditions. As is evidenced by the dotted lines representing the lean/rich aging conditions, these types of catalysts are not suitable when exposed to repeated reducing conditions. In particular, these catalysts are not suitable for NAC+SCR applications.
0027Molecular sieve supported iron SCR catalysts, although not as active as molecular sieve supported copper catalysts at low temperatures (e.g. <350°C), are stable against repeated lean/rich high temperature aging as shown in <figref idref="f0002">Figure 2</figref>. In <figref idref="f0002">Figure 2</figref>, Fe/Ferrierite, Fe/ZSM-5, and Fe/Beta are shown after hydrothermal aging and lean/rich aging conditions. Accordingly, molecular sieve supported iron catalysts have been the technology of choice due to their excellent stability against cycled lean/rich aging, e.g., as is encountered in NAC+SCR applications.
0028Small pore molecular sieve supported Cu catalysts have been demonstrated to exhibit improved NH<sub>3</sub>-SCR activity and excellent thermal stability. According to one aspect of the invention, it was found that this type of catalyst also tolerates repeated lean/rich high temperature aging. <figref idref="f0003">Figure 3</figref> compares a series of small pore molecular sieve supported Cu catalysts (Cu/SAPO-34, Cu/Nu-3, and Cu/SSZ-13, respectively) against a comparative large pore catalyst (Cu/Beta) after 700°C/2 hours hydrothermal aging and 600°C/12 hours cycled lean/rich aging, respectively. As is evident in <figref idref="f0003">Figure 3</figref>, the catalysts with small pore molecular sieve are very stable against lean/rich aging. In particular, the Cu/SAPO-34 catalyst exhibited exceptionally good low temperature activity and showed no activity degradation after cycled lean/rich aging, i.e., repeated exposure to a reducing atmosphere.
0029The catalysts in embodiments of the present invention show a much wider temperature window of high NO<sub>X</sub> conversion. The temperature range of improved conversion efficiency may range from about 150 to 650 °C, more particularly from 200 to 500°C, more particularly from 200 to 450°C, or most significantly from about 200 to 400°C. In these temperature ranges, conversion efficiencies after exposure to a reducing atmosphere, and even after exposure to a reducing atmosphere and to high temperatures (e.g., up to 850 °C), may range from greater than 55% to 100%, more preferably greater than 90% efficiency, and even more preferably greater than 95% efficiency. In particular, combined NAC+SCR systems show a much wider temperature window of high NO<sub>X</sub> conversion compared to either NAC catalysts alone or NAC+SCR systems using a Fe/molecular sieve SCR catalyst. See <figref idref="f0004">Figure 4</figref>. For example at about 250°C and about 300°C, the NO<sub>X</sub> conversion efficiencies for systems subjected to lean/rich aging are as follows: <tables id="tabl0001" num="0001"><table frame="all"><tgroup cols="3"><colspec colnum="1" colname="col1" colwidth="56mm" /><colspec colnum="2" colname="col2" colwidth="44mm" /><colspec colnum="3" colname="col3" colwidth="44mm" /><thead><row><entry valign="top">System (undergone lean/rich aging)</entry><entry valign="top">NO<sub>X</sub> Conversion % at 250°C</entry><entry valign="top">NO<sub>X</sub> Conversion % at 300°C</entry></row></thead><tbody><row><entry>NAC alone</entry><entry align="center">73</entry><entry align="center">92</entry></row><row><entry>NAC + Fe/Beta SCR catalyst</entry><entry align="center">87</entry><entry align="center">90</entry></row><row><entry>NAC + Cu/SSZ-13 SCR catalyst</entry><entry align="center">93</entry><entry align="center">97</entry></row><row><entry>NAC + Cu/SAPO-34 SCR catalyst</entry><entry align="center">97</entry><entry align="center">96</entry></row></tbody></tgroup></table></tables>
0030As is evident from these results, the use of the NAC + Cu/small pore molecular sieve catalyst shows dramatic improvement in conversion efficiencies. These improvements are to the final NO<sub>X</sub> emissions. Thus, an improvement from about 87% NO<sub>X</sub> conversion (about 13% NO<sub>X</sub> remaining) to about 97% NO<sub>X</sub> conversion (about 3% NO<sub>X</sub> remaining) is about a 433% improvement in efficiency, based on the percent NO<sub>X</sub> remaining.
0031The catalyst has an initial activity and the catalyst has a final activity after the at least one period of exposure to the reducing atmosphere. In certain embodiments, catalyst activity is NOx conversion efficiency. Accordingly, the initial activity is NOx conversion efficiency of a catalyst that has not been exposed to a reducing atmosphere and the final activity is NOx conversion efficiency of the catalyst after exposure to a reducing atmosphere. The initial activity may include a baseline aging under hydrothermal conditions. Hydrothermal conditions may include aging at 700°C for 2 hours with 5% H<sub>2</sub>O in air.
0032According to the invention, the chemical process undergoes at least one period of exposure to a reducing atmosphere during rich conditions in a lean/rich aging cycle, e.g. a cycled lean/rich aging at 600°C for 12 hours. A lean cycle may last from 15 seconds to several tens of minutes, and a rich cycle may last from less than 1 second to several minutes. In a NAC-SCR system , the rich cycle may range, for example, from 1 to 60 continuous seconds, from 1 to 15 continuous seconds, or from 5 to 15 continuous seconds. Additionally, localized reducing atmosphere may occur during catalysed soot filter regeneration. In a coated soot filter application (e.g., a SCR/DPF (diesel particulate filter), the rich cycle may range, for example, from 30 seconds to 60 minutes of continuous exposure, from 5 minutes to 30 minutes of continuous exposure, or from 10 minutes to 30 minutes of continuous exposure. For example, the lean portion of the cycle may consist of exposure to 200 ppm NO, 10% O<sub>2</sub>, 5% H<sub>2</sub>O, 5% CO<sub>2</sub> in N<sub>2</sub>, and the rich portion of the cycle may consist of exposure to 200 ppm NO, 5000 ppm C<sub>3</sub>H<sub>6</sub>, 1.3% H<sub>2</sub>, 4% CO, 1% O<sub>2</sub>, 5% H<sub>2</sub>O, 5% CO<sub>2</sub> in N<sub>2</sub>. The reducing atmosphere may be a high temperature reducing atmosphere. A high temperature reducing atmosphere may occur at a temperature from about 150°C to 850°C or more particularly from about 450°C to 850°C.
0033The final activity is within about 30%, more preferably within about 10%, more preferably within about 5%, even more preferably within about 3% of the initial activity at a catalytic operating temperature. Preferably, the catalytic operating temperature is between about 150 and about 650 °C and more preferably between about 200 and about 500°C. While the activity of the catalyst is preferably measured within a temperature range of 200 and 500°C, portions of the chemical process can operate at any temperature, for example, a wider temperature range including higher temperatures. For example, catalyst activity will still be maintained in the temperature range of 200 and 500°C even after the catalyst has been exposed to higher temperatures, e.g. up to 850 °C. As used herein, when the final activity is given as a percentage of the initial activity, it is given as an average of percentages over the temperature range provided; in other words, if a final activity is said to be within 30% of the initial activity at a temperature between 200 and 500°C, it need not be less than 30% at every temperatures tested in that range, but would merely average less than 30% over the temperatures tested. Moreover, while activity is identified as NO<sub>X</sub> conversion in the examples of this application, the activity could be some other measure of catalyst activity depending on the chemical process, as is known in the art. The data showing catalyst activity and the percentage of initial activity to final activity is evidenced in the following tables (See also <figref idref="f0003">Figure 3</figref>). A negative number means that the activity after exposure to the reducing conditions actually improved relative to the initial activity (and therefore would certainly be "within" a certain positive percentage of the initial activity):
0034For the embodiment using Cu/Nu-3 the following data was obtained: <tables id="tabl0002" num="0002"><table frame="all"><tgroup cols="5"><colspec colnum="1" colname="col1" colwidth="15mm" /><colspec colnum="2" colname="col2" colwidth="20mm" /><colspec colnum="3" colname="col3" colwidth="15mm" /><colspec colnum="4" colname="col4" colwidth="20mm" /><colspec colnum="5" colname="col5" colwidth="10mm" /><thead><row><entry align="center" valign="top"><b>TEMP</b></entry><entry align="center" valign="top"><b>HT Aging</b></entry><entry align="center" valign="top"><b>TEMP</b></entry><entry align="center" valign="top"><b>LR Aging</b></entry><entry align="center" valign="top">%</entry></row></thead><tbody><row><entry align="center"><b>150</b></entry><entry align="center"><b>9</b></entry><entry align="center"><b>150</b></entry><entry align="center"><b>9</b></entry><entry align="center">-2%</entry></row><row><entry align="center"><b>200</b></entry><entry align="center"><b>50</b></entry><entry align="center"><b>198</b></entry><entry align="center"><b>52</b></entry><entry align="center">-2%</entry></row><row><entry align="center"><b>250</b></entry><entry align="center"><b>76</b></entry><entry align="center"><b>250</b></entry><entry align="center"><b>75</b></entry><entry align="center">1%</entry></row><row><entry align="center"><b>350</b></entry><entry align="center"><b>72</b></entry><entry align="center"><b>350</b></entry><entry align="center"><b>69</b></entry><entry align="center">4%</entry></row><row><entry align="center"><b>450</b></entry><entry align="center"><b>62</b></entry><entry align="center"><b>450</b></entry><entry align="center"><b>58</b></entry><entry align="center">6%</entry></row><row><entry align="center"><b>550</b></entry><entry align="center"><b>45</b></entry><entry align="center"><b>550</b></entry><entry align="center"><b>43</b></entry><entry align="center">3%</entry></row><row><entry align="center"><b>650</b></entry><entry align="center"><b>27</b></entry><entry align="center"><b>650</b></entry><entry align="center"><b>26</b></entry><entry align="center">2%</entry></row></tbody></tgroup></table></tables>
0035Thus, the lean/rich aging % NO<sub>X</sub> reduction was within about 6% of the hydrothermal aging % NO<sub>X</sub> reduction. Accordingly, the catalyst remained stable and had good activity following repeated exposure to reducing conditions throughout the temperature ranging from about 150 to about 650°C.
0036For the embodiment using Cu/SSZ-13 the following data was obtained: <tables id="tabl0003" num="0003"><table frame="all"><tgroup cols="5"><colspec colnum="1" colname="col1" colwidth="15mm" /><colspec colnum="2" colname="col2" colwidth="20mm" /><colspec colnum="3" colname="col3" colwidth="15mm" /><colspec colnum="4" colname="col4" colwidth="20mm" /><colspec colnum="5" colname="col5" colwidth="14mm" /><thead><row><entry align="center" valign="top"><b>TEMP</b></entry><entry align="center" valign="top"><b>HT Aging</b></entry><entry align="center" valign="top"><b>TEMP</b></entry><entry align="center" valign="top"><b>LR Aging</b></entry><entry align="center" valign="top"><b>%</b></entry></row></thead><tbody><row><entry align="center"><b>164</b></entry><entry align="center"><b>61</b></entry><entry align="center"><b>160</b></entry><entry align="center"><b>19</b></entry><entry align="center">68%</entry></row><row><entry align="center"><b>218</b></entry><entry align="center"><b>100</b></entry><entry align="center"><b>216</b></entry><entry align="center"><b>71</b></entry><entry align="center">29%</entry></row><row><entry align="center"><b>269</b></entry><entry align="center"><b>100</b></entry><entry align="center"><b>269</b></entry><entry align="center"><b>97</b></entry><entry align="center">3%</entry></row><row><entry align="center"><b>373</b></entry><entry align="center"><b>97</b></entry><entry align="center"><b>372</b></entry><entry align="center"><b>86</b></entry><entry align="center">12%</entry></row><row><entry align="center"><b>473</b></entry><entry align="center"><b>86</b></entry><entry align="center"><b>474</b></entry><entry align="center"><b>68</b></entry><entry align="center">20%</entry></row><row><entry align="center"><b>572</b></entry><entry align="center"><b>64</b></entry><entry align="center"><b>573</b></entry><entry align="center"><b>41</b></entry><entry align="center">36%</entry></row><row><entry align="center"><b>668</b></entry><entry align="center"><b>22</b></entry><entry align="center"><b>669</b></entry><entry align="center"><b>-7</b></entry><entry align="center">134%</entry></row></tbody></tgroup></table></tables>
0037Thus, the lean/rich aging % NO<sub>X</sub> reduction was within about 30% of the hydrothermal aging % NO<sub>X</sub> reduction throughout the temperature ranging from about 200 to about 500°C.
0038For the embodiment using Cu/SAPO34 the following data was obtained: <tables id="tabl0004" num="0004"><table frame="all"><tgroup cols="5"><colspec colnum="1" colname="col1" colwidth="15mm" /><colspec colnum="2" colname="col2" colwidth="20mm" /><colspec colnum="3" colname="col3" colwidth="15mm" /><colspec colnum="4" colname="col4" colwidth="20mm" /><colspec colnum="5" colname="col5" colwidth="15mm" /><thead><row><entry align="center" valign="top"><b>TEMP</b></entry><entry align="center" valign="top"><b>HT Aging</b></entry><entry align="center" valign="top"><b>TEMP</b></entry><entry align="center" valign="top"><b>LR Aging</b></entry><entry align="center" valign="top"><b>%</b></entry></row></thead><tbody><row><entry align="center"><b>156</b></entry><entry align="center"><b>33</b></entry><entry align="center"><b>156</b></entry><entry align="center"><b>47</b></entry><entry align="center">-41%</entry></row><row><entry align="center"><b>211</b></entry><entry align="center"><b>95</b></entry><entry align="center"><b>212</b></entry><entry align="center"><b>97</b></entry><entry align="center">-3%</entry></row><row><entry align="center"><b>264</b></entry><entry align="center"><b>99</b></entry><entry align="center"><b>265</b></entry><entry align="center"><b>99</b></entry><entry align="center">0.04%</entry></row></tbody></tgroup></table></tables><tables id="tabl0005" num="0005"><table frame="all"><tgroup cols="5"><colspec colnum="1" colname="col1" colwidth="15mm" /><colspec colnum="2" colname="col2" colwidth="20mm" /><colspec colnum="3" colname="col3" colwidth="15mm" /><colspec colnum="4" colname="col4" colwidth="20mm" /><colspec colnum="5" colname="col5" colwidth="15mm" /><thead><row><entry align="center" valign="top"><b>TEMP</b></entry><entry align="center" valign="top"><b>HT Aging</b></entry><entry align="center" valign="top"><b>TEMP</b></entry><entry align="center" valign="top"><b>LR Aging</b></entry><entry align="center" valign="top"><b>%</b></entry></row></thead><tbody><row><entry align="center"><b>366</b></entry><entry align="center"><b>89</b></entry><entry align="center"><b>366</b></entry><entry align="center"><b>89</b></entry><entry align="center">-0.01%</entry></row><row><entry align="center"><b>464</b></entry><entry align="center"><b>86</b></entry><entry align="center"><b>465</b></entry><entry align="center"><b>83</b></entry><entry align="center">3%</entry></row><row><entry align="center"><b>561</b></entry><entry align="center"><b>70</b></entry><entry align="center"><b>564</b></entry><entry align="center"><b>62</b></entry><entry align="center">11%</entry></row><row><entry align="center"><b>658</b></entry><entry align="center"><b>34</b></entry><entry align="center"><b>662</b></entry><entry align="center"><b>26</b></entry><entry align="center">22%</entry></row></tbody></tgroup></table></tables>
0039Thus, the lean/rich aging % NO<sub>X</sub> reduction was within about 3% of the hydrothermal aging % NO<sub>X</sub> reduction throughout the temperature ranging from about 200 to about 500°C, and within about 10% at temperatures ranging from about 200 to 560°C.
0040As a comparative example a Cu/Beta, large pore molecular sieve catalyst, was compared: <tables id="tabl0006" num="0006"><table frame="all"><tgroup cols="5"><colspec colnum="1" colname="col1" colwidth="15mm" /><colspec colnum="2" colname="col2" colwidth="20mm" /><colspec colnum="3" colname="col3" colwidth="15mm" /><colspec colnum="4" colname="col4" colwidth="20mm" /><colspec colnum="5" colname="col5" colwidth="12mm" /><thead><row><entry align="center" valign="top"><b>TEMP</b></entry><entry align="center" valign="top"><b>HT Aging</b></entry><entry align="center" valign="top"><b>TEMP</b></entry><entry align="center" valign="top"><b>LR Aging</b></entry><entry align="center" valign="top"><b>%</b></entry></row></thead><tbody><row><entry align="center"><b>150</b></entry><entry align="center"><b>21</b></entry><entry align="center"><b>152</b></entry><entry align="center"><b>9</b></entry><entry align="center">57%</entry></row><row><entry align="center"><b>200</b></entry><entry align="center"><b>72</b></entry><entry align="center"><b>199</b></entry><entry align="center"><b>24</b></entry><entry align="center">67%</entry></row><row><entry align="center"><b>250</b></entry><entry align="center"><b>93</b></entry><entry align="center"><b>250</b></entry><entry align="center"><b>30</b></entry><entry align="center">67%</entry></row><row><entry align="center"><b>350</b></entry><entry align="center"><b>93</b></entry><entry align="center"><b>351</b></entry><entry align="center"><b>26</b></entry><entry align="center">72%</entry></row><row><entry align="center"><b>450</b></entry><entry align="center"><b>82</b></entry><entry align="center"><b>450</b></entry><entry align="center"><b>37</b></entry><entry align="center">56%</entry></row><row><entry align="center"><b>550</b></entry><entry align="center"><b>82</b></entry><entry align="center"><b>550</b></entry><entry align="center"><b>54</b></entry><entry align="center">35%</entry></row><row><entry align="center"><b>650</b></entry><entry align="center"><b>64</b></entry><entry align="center"><b>650</b></entry><entry align="center"><b>49</b></entry><entry align="center">24%</entry></row></tbody></tgroup></table></tables>
0041The Cu/Beta comparative example showed poor activity following lean/rich cycled aging. Thus, exposure to a reducing atmosphere for the copper molecular sieve catalysts causes poor stability and activity as was contemplated prior to discovery of the present invention.
0042The catalyst for use in the present invention comprises copper and a small pore molecular sieve having a maximum ring size of eight tetrahedral atoms and can be selected from the group of Framework Type Codes consisting of CHA, LEV, ERI and DDR. The catalyst has an initial activity, and the catalyst has a final activity after the at least one period of exposure to the reducing atmosphere. The final activity is within 10% of the initial activity at a temperature between 250 and 350°C. In a preferred embodiment, the catalyst has a final activity that is within 3% of the initial activity at a temperature between 250 and 350°C.
0043In an embodiment of the invention, the catalysts have been combined with a NAC (NO<sub>X</sub> adsorber catalyst) and tested as NAC+SCR systems. <figref idref="f0004">Figure 4</figref> compares the NO<sub>X</sub> reduction efficiency over a NAC alone and NAC+SCR systems with different SCR small pore molecular sieve catalysts (Cu/SAPO-34, and Cu/SSZ-13), and a comparative example of a Fe/beta catalyst. Combining an Fe/molecular sieve SCR with a NAC catalyst has been shown to improve the system NO<sub>X</sub> conversion compared to NAC alone. Remarkably, however, the other two systems with a small pore molecular sieve comprising copper, i.e., Cu/SAPO-34 or Cu/SSZ-13, also exhibited further improved NO<sub>X</sub> removal efficiency. This is especially evident at low temperatures (200-350°C). These results clearly suggest that small pore molecular sieve supported Cu catalysts offers new potential to further improve the performance of NAC+SCR systems.
0044In addition to NAC+SCR applications, the small pore molecular sieve supported Cu catalysts offer significant performance advantages for other applications that may be exposed to a high temperature reducing atmosphere. For example, a small pore molecular sieve supported Cu catalyst may be used in a reducing atmosphere which occurs during active regeneration of a SCR/DPF (diesel particulate filter). Small pore molecular sieve supported Cu catalysts provide excellent thermal durability and exceptional stability against reducing conditions, e.g., rich aging that occurs in exhaust gas treatment systems.
0045It will be appreciated that by defining the molecular sieve by their Framework Type Codes we intend to include the "Type Material" and any and all isotypic framework materials. (The "Type Material" is the species first used to establish the framework type). Reference is made to Table 1, which lists a range of illustrative molecular sieve materials for use in the present invention. For the avoidance of doubt, unless otherwise made clear, reference herein to a molecular sieve by name, e.g. "chabazite", is to the molecular sieve material <i>per se</i> (in this example the naturally occurring type material chabazite) and not to any other material designated by the Framework Type Code to which the individual molecular sieve may belong, e.g. some other isotypic framework material. Use of a FTC herein is intended to refer to the Type Material and all isotypic framework materials defined by that FTC.
0046The distinction between molecular sieve type materials, such as naturally occurring (i.e. mineral) chabazite, and isotypes within the same Framework Type Code is not merely arbitrary, but reflects differences in the properties between the materials, which may in turn lead to differences in activity in the method of the present invention. It will be appreciated, e.g. from Table 1 hereinbelow, that by "MeAPSO" and "MeAlPO" we intend zeotypes substituted with one or more metals. Suitable substituent metals include one or more of, without limitation, As, B, Be, Co, Fe, Ga, Ge, Li, Mg, Mn, Zn and Zr.
0047In a particular embodiment, the small pore molecular sieve catalysts for use in the present invention can be selected from the group consisting of aluminosilicate molecular sieves, metal-substituted aluminosilicate molecular sieves and aluminophosphate molecular sieves. Aluminophosphate molecular sieves with application in the present invention include aluminophosphate (A1PO) molecular sieves, metal substituted (MeAlPO) molecular sieves, silico-aluminophosphate (SAPO) molecular sieves and metal substituted silico-aluminophosphate (MeAPSO) molecular sieves.
0048In one embodiment, the small pore molecular sieve is selected from the group of Framework Type Codes consisting of: ACO, AEI, AEN, AFN, AFT, AFX, ANA, APC, APD, ATT, CDO, CHA, DDR, DFT, EAB, EDI, EPI, ERI, GIS, GOO, IHW, ITE, ITW, LEV, KFI, MER, MON, NSI, OWE, PAU, PHI, RHO, RTH, SAT, SAV, SIV, THO, TSC, UEI, UFI, VNI, YUG and ZON.
0049In an embodiment, the small pore molecular sieve containing a maximum ring size of eight tetrahedral atoms is selected from the group of Framework Type Codes consisting of CHA, LEV, ERI, and DDR. In a preferred embodiment, the small pore molecular sieve comprises a CHA Framework Type Code selected from SAPO-34 or SSZ-13. In another embodiment, the small pore molecular sieve comprises a LEV Framework Type Code Nu-3. Additionally, the small pore molecular sieve may comprise an AEI Framework Type Code SAPO-18, an ERI Framework Type Code ZSM-34, and/or a DDR Framework Type Code sigma-1. The small pore molecular sieve may also include disordered molecular sieves, such as an intergrown or mixed phase AEI/CHA, AEI/SAV, etc.
0050Molecular sieves with application in the present invention can include those that have been treated to improve hydrothermal stability. Illustrative methods of improving hydrothermal stability include: <ol id="ol0001" compact="compact"><li>(i) Dealumination by: steaming and acid extraction using an acid or complexing agent e.g. (EDTA - ethylenediaminetetracetic acid); treatment with acid and/or complexing agent; treatment with a gaseous stream of SiCl<sub>4</sub> (replaces Al in the molecular sieve framework with Si);</li><li>(ii) Cation exchange - use of multi-valent cations such as La; and</li><li>(iii) Use of phosphorous containing compounds (see e.g. <patcit id="pcit0005" dnum="US5958818A"><text>U.S. Patent No. 5,958,818</text></patcit>). Illustrative examples of suitable small pore molecular sieves are set out in Table 1.</li></ol><tables id="tabl0007" num="0007"><table frame="all"><title><b>Table 1: Small Pore Molecular Sieve</b></title><tgroup cols="5"><colspec colnum="1" colname="col1" colwidth="43mm" /><colspec colnum="2" colname="col2" colwidth="49mm" /><colspec colnum="3" colname="col3" colwidth="28mm" /><colspec colnum="4" colname="col4" colwidth="25mm" /><colspec colnum="5" colname="col5" colwidth="21mm" /><thead><row><entry align="center" valign="top"><b>Molecular Sieve Framework Type (by Framework Type Code)</b></entry><entry align="center" valign="top"><b>Type material</b>* <b>and illustrative isotypic framework structures</b></entry><entry align="center" valign="top"><b>Dimensionality</b></entry><entry align="center" valign="top"><b>Pore size (Å)</b></entry><entry align="center" valign="top"><b>Additional info</b></entry></row></thead><tbody><row><entry align="center">ACO</entry><entry align="center">*ACP-1</entry><entry align="center">3D</entry><entry align="center">3.5 x 2.8, 3.5 x 3.5</entry><entry align="center">Ring sizes-8, 4</entry></row><row><entry align="center">AEI</entry><entry align="center">*AlPO-18</entry><entry align="center">3D</entry><entry align="center">3.8 x 3.8</entry><entry align="center">Ring sizes-8, 6, 4</entry></row><row><entry align="center" /><entry align="center">[Co-Al-P-O]-AEI</entry><entry align="center" /><entry align="center" /><entry align="center" /></row><row><entry align="center" /><entry align="center">SAPO-18</entry><entry align="center" /><entry align="center" /><entry align="center" /></row><row><entry align="center" /><entry align="center">SIZ-8</entry><entry align="center" /><entry align="center" /><entry align="center" /></row><row><entry align="center" /><entry align="center">SSZ-39</entry><entry align="center" /><entry align="center" /><entry align="center" /></row><row><entry align="center">AEN</entry><entry align="center">*AlPO-EN3</entry><entry align="center">2D</entry><entry align="center">4.3 x 3.1, 2.7 x 5.0</entry><entry align="center">Ring sizes - 8, 6, 4</entry></row><row><entry align="center" /><entry align="center">AlPO-53(A)</entry><entry align="center" /><entry align="center" /><entry align="center" /></row><row><entry align="center" /><entry align="center">AlPO-53(B)</entry><entry align="center" /><entry align="center" /><entry align="center" /></row><row><entry align="center" /><entry align="center">[Ga-P-O]-AEN</entry><entry align="center" /><entry align="center" /><entry align="center" /></row><row><entry align="center" /><entry align="center">CFSAPO-1A</entry><entry align="center" /><entry align="center" /><entry align="center" /></row><row><entry align="center" /><entry align="center">CoIST-2</entry><entry align="center" /><entry align="center" /><entry align="center" /></row><row><entry align="center" /><entry align="center">IST-2</entry><entry align="center" /><entry align="center" /><entry align="center" /></row><row><entry align="center" /><entry align="center">JDF-2</entry><entry align="center" /><entry align="center" /><entry align="center" /></row><row><entry align="center" /><entry align="center">MCS-1</entry><entry align="center" /><entry align="center" /><entry align="center" /></row><row><entry align="center" /><entry align="center">MnAPO-14</entry><entry align="center" /><entry align="center" /><entry align="center" /></row><row><entry align="center" /><entry align="center">Mu-10</entry><entry align="center" /><entry align="center" /><entry align="center" /></row><row><entry align="center" /><entry align="center">UiO-12-500</entry><entry align="center" /><entry align="center" /><entry align="center" /></row><row><entry align="center" /><entry align="center">UiO-12-as</entry><entry align="center" /><entry align="center" /><entry align="center" /></row><row><entry align="center">AFN</entry><entry align="center">*AlPO-14</entry><entry align="center">3D</entry><entry align="center">1.9 x 4.6, 2.1 x 4.9, 3.3 x 4.0</entry><entry align="center">Ring sizes - 8, 6, 4</entry></row><row><entry align="center" /><entry align="center">|(C<sub>3</sub>N<sub>2</sub>H<sub>12</sub>)-|[Mn-Al-P-O]-AFN</entry><entry align="center" /><entry align="center" /><entry align="center" /></row><row><entry align="center" /><entry align="center">GaPO-14</entry><entry align="center" /><entry align="center" /><entry align="center" /></row><row><entry align="center">AFT</entry><entry align="center">*AlPO-52</entry><entry align="center">3D</entry><entry align="center">3.8 x 3.2, 3.8 x 3.6</entry><entry align="center">Ring sizes-8, 6, 4</entry></row><row><entry align="center">AFX</entry><entry align="center">*SAPO-56</entry><entry align="center">3D</entry><entry align="center">3.4 x 3.6</entry><entry align="center">Ring sizes-8, 6, 4</entry></row><row><entry align="center" /><entry align="center">MAPSO-56, M=Co, Mn, Zr</entry><entry align="center" /><entry align="center" /><entry align="center" /></row><row><entry align="center" /><entry align="center">SSZ-16</entry><entry align="center" /><entry align="center" /><entry align="center" /></row><row><entry align="center">ANA</entry><entry align="center">*Analcime</entry><entry align="center">3D</entry><entry align="center">4.2 x 1.6</entry><entry align="center">Ring sizes-8, 6, 4</entry></row><row><entry align="center" /><entry align="center">AlPO<sub>4</sub>-pollucite</entry><entry align="center" /><entry align="center" /><entry align="center" /></row><row><entry align="center" /><entry align="center">AlPO-24</entry><entry align="center" /><entry align="center" /><entry align="center" /></row><row><entry align="center" /><entry align="center">Ammonioleucite</entry><entry align="center" /><entry align="center" /><entry align="center" /></row><row><entry align="center" /><entry align="center">[Al-Co-P-O]-ANA</entry><entry align="center" /><entry align="center" /><entry align="center" /></row><row><entry align="center" /><entry align="center">[Al-Si-P-O]-ANA</entry><entry align="center" /><entry align="center" /><entry align="center" /></row><row><entry align="center" /><entry align="center">|Cs-|[Al-Ge-O]-ANA</entry><entry align="center" /><entry align="center" /><entry align="center" /></row><row><entry align="center" /><entry align="center">|Cs-|[Be-Si-O]-ANA</entry><entry align="center" /><entry align="center" /><entry align="center" /></row><row><entry align="center" /><entry align="center">|Cs<sub>16</sub>|[Cu<sub>8</sub>Si<sub>40</sub>O<sub>96</sub>]-ANA</entry><entry align="center" /><entry align="center" /><entry align="center" /></row><row><entry align="center" /><entry align="center">|Cs-Fe|[Si-O]-ANA</entry><entry align="center" /><entry align="center" /><entry align="center" /></row><row><entry align="center" /><entry align="center">|Cs-Na-(H<sub>2</sub>O)|[Ga-Si-O]-ANA</entry><entry align="center" /><entry align="center" /><entry align="center" /></row><row><entry align="center" /><entry align="center">[Ga-Ge-O]-ANA</entry><entry align="center" /><entry align="center" /><entry align="center" /></row><row><entry align="center" /><entry align="center">|K-|[B-Si-O]-ANA</entry><entry align="center" /><entry align="center" /><entry align="center" /></row><row><entry align="center" /><entry align="center">|K-|[Be-B-P-O]-ANA</entry><entry align="center" /><entry align="center" /><entry align="center" /></row><row><entry align="center" /><entry align="center">|Li-|[Li-Zn-Si-O]-ANA</entry><entry align="center" /><entry align="center" /><entry align="center" /></row><row><entry align="center" /><entry align="center">|Li-Na|[Al-Si-O]-ANA</entry><entry align="center" /><entry align="center" /><entry align="center" /></row><row><entry align="center" /><entry align="center">|Na-|[Be-B-P-O]-ANA</entry><entry align="center" /><entry align="center" /><entry align="center" /></row><row><entry align="center" /><entry align="center">|(NH<sub>4</sub>)-|[Be-B-P-O]-ANA</entry><entry align="center" /><entry align="center" /><entry align="center" /></row><row><entry align="center" /><entry align="center">|(NH<sub>4</sub>)-|[Zn-Ga-PO]-ANA</entry><entry align="center" /><entry align="center" /><entry align="center" /></row><row><entry align="center" /><entry align="center">[Zn-As-O]-ANA</entry><entry align="center" /><entry align="center" /><entry align="center" /></row><row><entry align="center" /><entry align="center">Ca-D</entry><entry align="center" /><entry align="center" /><entry align="center" /></row><row><entry align="center" /><entry align="center">Hsianghualite</entry><entry align="center" /><entry align="center" /><entry align="center" /></row><row><entry align="center" /><entry align="center">Leucite</entry><entry align="center" /><entry align="center" /><entry align="center" /></row><row><entry align="center" /><entry align="center">Na-B</entry><entry align="center" /><entry align="center" /><entry align="center" /></row><row><entry align="center" /><entry align="center">Pollucite</entry><entry align="center" /><entry align="center" /><entry align="center" /></row><row><entry align="center" /><entry align="center">Wairakite</entry><entry align="center" /><entry align="center" /><entry align="center" /></row><row><entry align="center">APC</entry><entry align="center">*AlPO-C</entry><entry align="center">2D</entry><entry align="center">3.7 x 3.4, 4.7 x 2.0</entry><entry align="center">Ring sizes-8,6,4</entry></row><row><entry align="center" /><entry align="center">AlPO-H3</entry><entry align="center" /><entry align="center" /><entry align="center" /></row><row><entry align="center" /><entry align="center">CoAPO-H3</entry><entry align="center" /><entry align="center" /><entry align="center" /></row><row><entry align="center">APD</entry><entry align="center">*AlPO-D</entry><entry align="center">2D</entry><entry align="center">6.0 x 2.3, 5.8 x 1.3</entry><entry align="center">Ring sizes-8,6,4</entry></row><row><entry align="center" /><entry align="center">APO-CJ3</entry><entry align="center" /><entry align="center" /><entry align="center" /></row><row><entry align="center">ATT</entry><entry align="center">*AlPO-12-TAMU</entry><entry align="center">2D</entry><entry align="center">4.6 x 4.2, 3.8 x 3.8</entry><entry align="center">Ring sizes-8, 6, 4</entry></row><row><entry align="center" /><entry align="center">AlPO-33</entry><entry align="center" /><entry align="center" /><entry align="center" /></row><row><entry align="center" /><entry align="center">RMA-3</entry><entry align="center" /><entry align="center" /><entry align="center" /></row><row><entry align="center">CDO</entry><entry align="center">*CDS-1</entry><entry align="center">2D</entry><entry align="center">4.7 x 3.1, 4.2 x 2.5</entry><entry align="center">Ring sizes-8,5</entry></row><row><entry align="center" /><entry align="center">MCM-65</entry><entry align="center" /><entry align="center" /><entry align="center" /></row><row><entry align="center" /><entry align="center">UZM-25</entry><entry align="center" /><entry align="center" /><entry align="center" /></row><row><entry align="center">CHA</entry><entry align="center">*Chabazite</entry><entry align="center">3D</entry><entry align="center">3.8 x 3.8</entry><entry align="center">Ring sizes-8, 6, 4</entry></row><row><entry align="center" /><entry align="center">AlPO-34</entry><entry align="center" /><entry align="center" /><entry align="center" /></row><row><entry align="center" /><entry align="center">[Al-As-O]-CHA</entry><entry align="center" /><entry align="center" /><entry align="center" /></row><row><entry align="center" /><entry align="center">[Al-Co-P-O]-CHA</entry><entry align="center" /><entry align="center" /><entry align="center" /></row><row><entry align="center" /><entry align="center">|Co|[Be-P-O]-CHA</entry><entry align="center" /><entry align="center" /><entry align="center" /></row><row><entry align="center" /><entry align="center">|CO<sub>3</sub>(C<sub>6</sub>N<sub>4</sub>H<sub>24</sub>)<sub>3</sub> (H<sub>2</sub>O)<sub>9</sub>|[Be<sub>18</sub>P<sub>18</sub>O<sub>72</sub>]-CHA</entry><entry align="center" /><entry align="center" /><entry align="center" /></row><row><entry align="center" /><entry align="center">[Co-Al-P-O]-CHA</entry><entry align="center" /><entry align="center" /><entry align="center" /></row><row><entry align="center" /><entry align="center">|Li-Na| [Al-Si-O]-CHA</entry><entry align="center" /><entry align="center" /><entry align="center" /></row><row><entry align="center" /><entry align="center">[Mg-Al-P-O]-CHA</entry><entry align="center" /><entry align="center" /><entry align="center" /></row><row><entry align="center" /><entry align="center">[Si-O]-CHA</entry><entry align="center" /><entry align="center" /><entry align="center" /></row><row><entry align="center" /><entry align="center">[Zn-Al-P-O]-CHA</entry><entry align="center" /><entry align="center" /><entry align="center" /></row><row><entry align="center" /><entry align="center">[Zn-As-O]-CHA</entry><entry align="center" /><entry align="center" /><entry align="center" /></row><row><entry align="center" /><entry align="center">CoAPO-44</entry><entry align="center" /><entry align="center" /><entry align="center" /></row><row><entry align="center" /><entry align="center">CoAPO-47</entry><entry align="center" /><entry align="center" /><entry align="center" /></row><row><entry align="center" /><entry align="center">DAF-5</entry><entry align="center" /><entry align="center" /><entry align="center" /></row><row><entry align="center" /><entry align="center">GaPO-34</entry><entry align="center" /><entry align="center" /><entry align="center" /></row><row><entry align="center" /><entry align="center">K-Chabazite</entry><entry align="center" /><entry align="center" /><entry align="center" /></row><row><entry align="center" /><entry align="center">Linde D</entry><entry align="center" /><entry align="center" /><entry align="center" /></row><row><entry align="center" /><entry align="center">Linde R</entry><entry align="center" /><entry align="center" /><entry align="center" /></row><row><entry align="center" /><entry align="center">LZ-218</entry><entry align="center" /><entry align="center" /><entry align="center" /></row><row><entry align="center" /><entry align="center">MeAPO-47</entry><entry align="center" /><entry align="center" /><entry align="center" /></row><row><entry align="center" /><entry align="center">MeAPSO-47</entry><entry align="center" /><entry align="center" /><entry align="center" /></row><row><entry align="center" /><entry align="center">(Ni(deta)<sub>2</sub>)-UT-6</entry><entry align="center" /><entry align="center" /><entry align="center" /></row><row><entry align="center" /><entry align="center">Phi</entry><entry align="center" /><entry align="center" /><entry align="center" /></row><row><entry align="center" /><entry align="center">SAPO-34</entry><entry align="center" /><entry align="center" /><entry align="center" /></row><row><entry align="center" /><entry align="center">SAPO-47</entry><entry align="center" /><entry align="center" /><entry align="center" /></row><row><entry align="center" /><entry align="center">SSZ-13</entry><entry align="center" /><entry align="center" /><entry align="center" /></row><row><entry align="center" /><entry align="center">UiO-21</entry><entry align="center" /><entry align="center" /><entry align="center" /></row><row><entry align="center" /><entry align="center">Willhendersonite</entry><entry align="center" /><entry align="center" /><entry align="center" /></row><row><entry align="center" /><entry align="center">ZK-14</entry><entry align="center" /><entry align="center" /><entry align="center" /></row><row><entry align="center" /><entry align="center">ZYT-6</entry><entry align="center" /><entry align="center" /><entry align="center" /></row><row><entry align="center">DDR</entry><entry align="center">*Deca-dodecasil 3R</entry><entry align="center">2D</entry><entry align="center">4.4 x 3.6</entry><entry align="center">Ring sizes-8, 6, 5, 4</entry></row><row><entry align="center" /><entry align="center">[B-Si-O]-DDR</entry><entry align="center" /><entry align="center" /><entry align="center" /></row><row><entry align="center" /><entry align="center">Sigma-1</entry><entry align="center" /><entry align="center" /><entry align="center" /></row><row><entry align="center" /><entry align="center">ZSM-58</entry><entry align="center" /><entry align="center" /><entry align="center" /></row><row><entry align="center">DFT</entry><entry align="center">*DAF-2</entry><entry align="center">3D</entry><entry align="center">4.1 x 4.1, 4.7 x 1.8</entry><entry align="center">Ring sizes-8, 6, 4</entry></row><row><entry align="center" /><entry align="center">ACP-3, [Co-Al-P-O]-DFT</entry><entry align="center" /><entry align="center" /><entry align="center" /></row><row><entry align="center" /><entry align="center">[Fe-Zn-P-O]-DFT</entry><entry align="center" /><entry align="center" /><entry align="center" /></row><row><entry align="center" /><entry align="center">[Zn-Co-P-O]-DFT</entry><entry align="center" /><entry align="center" /><entry align="center" /></row><row><entry align="center" /><entry align="center">UCSB-3GaGe</entry><entry align="center" /><entry align="center" /><entry align="center" /></row><row><entry align="center" /><entry align="center">UCSB-3ZnAs</entry><entry align="center" /><entry align="center" /><entry align="center" /></row><row><entry align="center" /><entry align="center">UiO-20, [Mg-P-O]-DFT</entry><entry align="center" /><entry align="center" /><entry align="center" /></row><row><entry align="center">EAB</entry><entry align="center">*TMA-E</entry><entry align="center">2D</entry><entry align="center">5.1 x 3.7</entry><entry align="center">Ring sizes-8, 6, 4</entry></row><row><entry align="center" /><entry align="center">Bellbergite</entry><entry align="center" /><entry align="center" /><entry align="center" /></row><row><entry align="center">EDI</entry><entry align="center">*Edingtonite</entry><entry align="center">3D</entry><entry align="center">2.8 x 3.8, 3.1 x 2.0</entry><entry align="center">Ring sizes-8, 4</entry></row><row><entry align="center" /><entry align="center">|(C<sub>3</sub>H<sub>12</sub>N<sub>2</sub>)<sub>2.51</sub>| [Zn<sub>5</sub>P<sub>5</sub>O<sub>20</sub>]-EDI</entry><entry align="center" /><entry align="center" /><entry align="center" /></row><row><entry align="center" /><entry align="center">[Co-Al-P-O]-EDI</entry><entry align="center" /><entry align="center" /><entry align="center" /></row><row><entry align="center" /><entry align="center">[Co-Ga-P-O]-EDI</entry><entry align="center" /><entry align="center" /><entry align="center" /></row><row><entry align="center" /><entry align="center">|Li-|[Al-Si-O]-EDI</entry><entry align="center" /><entry align="center" /><entry align="center" /></row><row><entry align="center" /><entry align="center">|Rb<sub>7</sub> Na (H<sub>2</sub>O)<sub>3</sub> [Ga<sub>8</sub>Si<sub>12</sub>0<sub>40</sub>]-EDI</entry><entry align="center" /><entry align="center" /><entry align="center" /></row><row><entry align="center" /><entry align="center">[Zn-As-O]-EDI</entry><entry align="center" /><entry align="center" /><entry align="center" /></row><row><entry align="center" /><entry align="center">K-F</entry><entry align="center" /><entry align="center" /><entry align="center" /></row><row><entry align="center" /><entry align="center">Linde F</entry><entry align="center" /><entry align="center" /><entry align="center" /></row><row><entry align="center" /><entry align="center">Zeolite N</entry><entry align="center" /><entry align="center" /><entry align="center" /></row><row><entry align="center">EPI</entry><entry align="center">*Epistilbite</entry><entry align="center">2D</entry><entry align="center">4.5 x 3.7, 3.6 x 3.6</entry><entry align="center">Ring sizes - 8, 4</entry></row><row><entry align="center">ERI</entry><entry align="center">*Erionite</entry><entry align="center">3D</entry><entry align="center">3.6 x 5.1</entry><entry align="center">Ring sizes - 8, 6, 4</entry></row><row><entry align="center" /><entry align="center">AlPO-17</entry><entry align="center" /><entry align="center" /><entry align="center" /></row><row><entry align="center" /><entry align="center">Linde T</entry><entry align="center" /><entry align="center" /><entry align="center" /></row><row><entry align="center" /><entry align="center">LZ-220</entry><entry align="center" /><entry align="center" /><entry align="center" /></row><row><entry align="center" /><entry align="center">SAPO-17</entry><entry align="center" /><entry align="center" /><entry align="center" /></row><row><entry align="center" /><entry align="center">ZSM-34</entry><entry align="center" /><entry align="center" /><entry align="center" /></row><row><entry align="center">GIS</entry><entry align="center">*Gismondine</entry><entry align="center">3D</entry><entry align="center">4.5 x 3.1, 4.8 x 2.8</entry><entry align="center">Ring sizes - 8, 4</entry></row><row><entry align="center" /><entry align="center">Amicite</entry><entry align="center" /><entry align="center" /><entry align="center" /></row><row><entry align="center" /><entry align="center">[Al-Co-P-O]-GIS</entry><entry align="center" /><entry align="center" /><entry align="center" /></row><row><entry align="center" /><entry align="center">[Al-Ge-O]-GIS</entry><entry align="center" /><entry align="center" /><entry align="center" /></row><row><entry align="center" /><entry align="center">[Al-P-O]-GIS</entry><entry align="center" /><entry align="center" /><entry align="center" /></row><row><entry align="center" /><entry align="center">[Be-P-O]-GIS</entry><entry align="center" /><entry align="center" /><entry align="center" /></row><row><entry align="center" /><entry align="center">|(C<sub>3</sub>H<sub>12</sub>N<sub>2</sub>)<sub>4</sub>| [Be<sub>8</sub>P<sub>8</sub>O<sub>32</sub>]-GIS</entry><entry align="center" /><entry align="center" /><entry align="center" /></row><row><entry align="center" /><entry align="center">|(C<sub>3</sub>H<sub>12</sub>N<sub>2</sub>)<sub>4</sub>| [Zn<sub>8</sub>P<sub>8</sub>O<sub>32</sub>]-GIS</entry><entry align="center" /><entry align="center" /><entry align="center" /></row><row><entry align="center" /><entry align="center">[Co-Al-P-O]-GIS</entry><entry align="center" /><entry align="center" /><entry align="center" /></row><row><entry align="center" /><entry align="center">[Co-Ga-P-O]-GIS</entry><entry align="center" /><entry align="center" /><entry align="center" /></row><row><entry align="center" /><entry align="center">[Co-P-O]-GIS</entry><entry align="center" /><entry align="center" /><entry align="center" /></row><row><entry align="center" /><entry align="center">|Cs<sub>4</sub>|[Zn<sub>4</sub>B<sub>4</sub>P<sub>8</sub>O<sub>32</sub>]-GIS</entry><entry align="center" /><entry align="center" /><entry align="center" /></row><row><entry align="center" /><entry align="center">[Ga-Si-O]-GIS</entry><entry align="center" /><entry align="center" /><entry align="center" /></row><row><entry align="center" /><entry align="center">[Mg-Al-P-O]-GIS</entry><entry align="center" /><entry align="center" /><entry align="center" /></row><row><entry align="center" /><entry align="center">|(NH<sub>4</sub>)<sub>4</sub>|[Zn<sub>4</sub>B<sub>4</sub>P<sub>8</sub>O<sub>32</sub>]-GIS</entry><entry align="center" /><entry align="center" /><entry align="center" /></row><row><entry align="center" /><entry align="center">|Rb<sub>4</sub>|[Zn<sub>4</sub>B<sub>4</sub>P<sub>8</sub>O<sub>32</sub>]-GIS</entry><entry align="center" /><entry align="center" /><entry align="center" /></row><row><entry align="center" /><entry align="center">[Zn-Al-As-O]-GIS</entry><entry align="center" /><entry align="center" /><entry align="center" /></row><row><entry align="center" /><entry align="center">[Zn-Co-B-P-O]-GIS</entry><entry align="center" /><entry align="center" /><entry align="center" /></row><row><entry align="center" /><entry align="center">[Zn-Ga-As-O]-GIS</entry><entry align="center" /><entry align="center" /><entry align="center" /></row><row><entry align="center" /><entry align="center">[Zn-Ga-P-O]-GIS</entry><entry align="center" /><entry align="center" /><entry align="center" /></row><row><entry align="center" /><entry align="center">Garronite</entry><entry align="center" /><entry align="center" /><entry align="center" /></row><row><entry align="center" /><entry align="center">Gobbinsite</entry><entry align="center" /><entry align="center" /><entry align="center" /></row><row><entry align="center" /><entry align="center">MAPO-43</entry><entry align="center" /><entry align="center" /><entry align="center" /></row><row><entry align="center" /><entry align="center">MAPSO-43</entry><entry align="center" /><entry align="center" /><entry align="center" /></row><row><entry align="center" /><entry align="center">Na-P1</entry><entry align="center" /><entry align="center" /><entry align="center" /></row><row><entry align="center" /><entry align="center">Na-P2</entry><entry align="center" /><entry align="center" /><entry align="center" /></row><row><entry align="center" /><entry align="center">SAPO-43</entry><entry align="center" /><entry align="center" /><entry align="center" /></row><row><entry align="center" /><entry align="center">TMA-gismondine</entry><entry align="center" /><entry align="center" /><entry align="center" /></row><row><entry align="center">GOO</entry><entry align="center">*Goosecreekite</entry><entry align="center">3D</entry><entry align="center">2.8 x 4.0, 2.7 x 4.1, 4.7 x 2.9</entry><entry align="center">Ring sizes - 8, 6, 4</entry></row><row><entry align="center">IHW</entry><entry align="center">*ITQ-32</entry><entry align="center">2D</entry><entry align="center">3.5 x 4.3</entry><entry align="center">Ring sizes - 8, 6, 5, 4</entry></row><row><entry align="center">ITE</entry><entry align="center">*ITQ-3</entry><entry align="center">2D</entry><entry align="center">4.3 x 3.8, 2.7 x 5.8</entry><entry align="center">Ring sizes - 8, 6, 5, 4</entry></row><row><entry align="center" /><entry align="center">Mu-14</entry><entry align="center" /><entry align="center" /><entry align="center" /></row><row><entry align="center" /><entry align="center">SSZ-36</entry><entry align="center" /><entry align="center" /><entry align="center" /></row><row><entry align="center">ITW</entry><entry align="center">*ITQ-12</entry><entry align="center">2D</entry><entry align="center">5.4 x 2.4, 3.9 x 4.2</entry><entry align="center">Ring sizes - 8, 6, 5, 4</entry></row><row><entry align="center">LEV</entry><entry align="center">*Levyne</entry><entry align="center">2D</entry><entry align="center">3.6 x 4.8</entry><entry align="center">Ring sizes - 8, 6, 4</entry></row><row><entry align="center" /><entry align="center">AlPO-35</entry><entry align="center" /><entry align="center" /><entry align="center" /></row><row><entry align="center" /><entry align="center">CoDAF-4</entry><entry align="center" /><entry align="center" /><entry align="center" /></row><row><entry align="center" /><entry align="center">LZ-132</entry><entry align="center" /><entry align="center" /><entry align="center" /></row><row><entry align="center" /><entry align="center">NU-3</entry><entry align="center" /><entry align="center" /><entry align="center" /></row><row><entry align="center" /><entry align="center">RUB-1 [B-Si-O]-LEV</entry><entry align="center" /><entry align="center" /><entry align="center" /></row><row><entry align="center" /><entry align="center">SAPO-35</entry><entry align="center" /><entry align="center" /><entry align="center" /></row><row><entry align="center" /><entry align="center">ZK-20</entry><entry align="center" /><entry align="center" /><entry align="center" /></row><row><entry align="center" /><entry align="center">ZnAPO-35</entry><entry align="center" /><entry align="center" /><entry align="center" /></row><row><entry align="center">KFI</entry><entry align="center">ZK-5</entry><entry align="center">3D</entry><entry align="center">3.9 x 3.9</entry><entry align="center">Ring sizes - 8, 6, 4</entry></row><row><entry align="center" /><entry align="center">|18-crown-6|[Al-Si-O]-UFI</entry><entry align="center" /><entry align="center" /><entry align="center" /></row><row><entry align="center" /><entry align="center">[Zn-Ga-As-O]-KFI</entry><entry align="center" /><entry align="center" /><entry align="center" /></row><row><entry align="center" /><entry align="center">(Cs,K)-ZK-5</entry><entry align="center" /><entry align="center" /><entry align="center" /></row><row><entry align="center" /><entry align="center">P</entry><entry align="center" /><entry align="center" /><entry align="center" /></row><row><entry align="center" /><entry align="center">Q</entry><entry align="center" /><entry align="center" /><entry align="center" /></row><row><entry align="center">MER</entry><entry align="center">*Merlinoite</entry><entry align="center">3D</entry><entry align="center">3.5 x 3.1, 3.6 x 2.7, 5.1 x 3.4, 3.3 x 3.3</entry><entry align="center">Ring sizes-8, 4</entry></row><row><entry align="center" /><entry align="center">[Al-Co-P-O]-MER</entry><entry align="center" /><entry align="center" /><entry align="center" /></row><row><entry align="center" /><entry align="center">|Ba-|[Al-Si-O]-MER</entry><entry align="center" /><entry align="center" /><entry align="center" /></row><row><entry align="center" /><entry align="center">|Ba-Cl-|[Al-Si-O]-MER</entry><entry align="center" /><entry align="center" /><entry align="center" /></row><row><entry align="center" /><entry align="center">[Ga-Al-Si-O]-MER</entry><entry align="center" /><entry align="center" /><entry align="center" /></row><row><entry align="center" /><entry align="center">|K-|[Al-Si-O]-MER</entry><entry align="center" /><entry align="center" /><entry align="center" /></row><row><entry align="center" /><entry align="center">|NH<sub>4</sub>-|[Be-P-O]-MER</entry><entry align="center" /><entry align="center" /><entry align="center" /></row><row><entry align="center" /><entry align="center">K-M</entry><entry align="center" /><entry align="center" /><entry align="center" /></row><row><entry align="center" /><entry align="center">Linde W</entry><entry align="center" /><entry align="center" /><entry align="center" /></row><row><entry align="center" /><entry align="center">Zeolite W</entry><entry align="center" /><entry align="center" /><entry align="center" /></row><row><entry align="center">MON</entry><entry align="center">*Montesommaite</entry><entry align="center">2D</entry><entry align="center">4.4 x 3.2, 3.6 x 3.6</entry><entry align="center">Ring sizes - 8, 5, 4</entry></row><row><entry align="center" /><entry align="center">[Al-Ge-O]-MON</entry><entry align="center" /><entry align="center" /><entry align="center" /></row><row><entry align="center">NSI</entry><entry align="center">*Nu-6(2)</entry><entry align="center">2D</entry><entry align="center">2.6 x 4.5, 2.4 x 4.8</entry><entry align="center">Ring sizes - 8, 6, 5</entry></row><row><entry align="center" /><entry align="center">EU-20</entry><entry align="center" /><entry align="center" /><entry align="center" /></row><row><entry align="center">OWE</entry><entry align="center">*UiO-28</entry><entry align="center">2D</entry><entry align="center">4.0 x 3.5, 4.8 x 3.2</entry><entry align="center">Ring sizes - 8, 6, 4</entry></row><row><entry align="center" /><entry align="center">ACP-2</entry><entry align="center" /><entry align="center" /><entry align="center" /></row><row><entry align="center">PAU</entry><entry align="center">*Paulingite</entry><entry align="center">3D</entry><entry align="center">3.6 x 3.6</entry><entry align="center">Ring sizes - 8, 6, 4</entry></row><row><entry align="center" /><entry align="center">[Ga-Si-O]-PAU</entry><entry align="center" /><entry align="center" /><entry align="center" /></row><row><entry align="center" /><entry align="center">ECR-18</entry><entry align="center" /><entry align="center" /><entry align="center" /></row><row><entry align="center">PHI</entry><entry align="center">*Phillipsite</entry><entry align="center">3D</entry><entry align="center">3.8 x 3.8, 3.0 x 4.3, 3.3 x 3.2</entry><entry align="center">Ring sizes - 8, 4</entry></row><row><entry align="center" /><entry align="center">[Al-Co-P-O]-PHI</entry><entry align="center" /><entry align="center" /><entry align="center" /></row><row><entry align="center" /><entry align="center">DAF-8</entry><entry align="center" /><entry align="center" /><entry align="center" /></row><row><entry align="center" /><entry align="center">Harmotome</entry><entry align="center" /><entry align="center" /><entry align="center" /></row><row><entry align="center" /><entry align="center">Wellsite</entry><entry align="center" /><entry align="center" /><entry align="center" /></row><row><entry align="center" /><entry align="center">ZK-19</entry><entry align="center" /><entry align="center" /><entry align="center" /></row><row><entry align="center">RHO</entry><entry align="center">*Rho</entry><entry align="center">3D</entry><entry align="center">3.6 x 3.6</entry><entry align="center">Ring sizes - 8, 6, 4</entry></row><row><entry align="center" /><entry align="center">[Be-As-O]-RHO</entry><entry align="center" /><entry align="center" /><entry align="center" /></row><row><entry align="center" /><entry align="center">[Be-P-O]-RHO</entry><entry align="center" /><entry align="center" /><entry align="center" /></row><row><entry align="center" /><entry align="center">[Co-Al-P-O]-RHO</entry><entry align="center" /><entry align="center" /><entry align="center" /></row><row><entry align="center" /><entry align="center">|H-|[Al-Si-O]-RHO</entry><entry align="center" /><entry align="center" /><entry align="center" /></row><row><entry align="center" /><entry align="center">[Mg-Al-P-O]-RHO</entry><entry align="center" /><entry align="center" /><entry align="center" /></row><row><entry align="center" /><entry align="center">[Mn-Al-P-O]-RHO</entry><entry align="center" /><entry align="center" /><entry align="center" /></row><row><entry align="center" /><entry align="center">|Na<sub>16</sub> Cs<sub>8</sub>| [Al<sub>24</sub>Ge<sub>24</sub>O<sub>96</sub>]-RHO</entry><entry align="center" /><entry align="center" /><entry align="center" /></row><row><entry align="center" /><entry align="center">|NH<sub>4</sub>-[Al-Si-O]-RHO</entry><entry align="center" /><entry align="center" /><entry align="center" /></row><row><entry align="center" /><entry align="center">|Rb-|[Be-As-O]-RHO</entry><entry align="center" /><entry align="center" /><entry align="center" /></row><row><entry align="center" /><entry align="center">Gallosilicate ECR-10</entry><entry align="center" /><entry align="center" /><entry align="center" /></row><row><entry align="center" /><entry align="center">LZ-214</entry><entry align="center" /><entry align="center" /><entry align="center" /></row><row><entry align="center" /><entry align="center">Pahasapaite</entry><entry align="center" /><entry align="center" /><entry align="center" /></row><row><entry align="center">RTH</entry><entry align="center">*RUB-13</entry><entry align="center">2D</entry><entry align="center">4.1 x 3.8, 5.6 x 2.5</entry><entry align="center">Ring sizes - 8, 6, 5, 4</entry></row><row><entry align="center" /><entry align="center">SSZ-36</entry><entry align="center" /><entry align="center" /><entry align="center" /></row><row><entry align="center" /><entry align="center">SSZ-50</entry><entry align="center" /><entry align="center" /><entry align="center" /></row><row><entry align="center">SAT</entry><entry align="center">*STA-2</entry><entry align="center">3D</entry><entry align="center">5.5 x 3.0</entry><entry align="center">Ring sizes - 8, 6, 4</entry></row><row><entry align="center">SAV</entry><entry align="center">*Mg-STA-7</entry><entry align="center">3D</entry><entry align="center">3.8 x 3.8, 3.9 x 3.9</entry><entry align="center">Ring sizes - 8, 6, 4</entry></row><row><entry align="center" /><entry align="center">Co-STA-7</entry><entry align="center" /><entry align="center" /><entry align="center" /></row><row><entry align="center" /><entry align="center">Zn-STA-7</entry><entry align="center" /><entry align="center" /><entry align="center" /></row><row><entry align="center">SBN</entry><entry align="center">*UCSB-9</entry><entry align="center">3D</entry><entry align="center">TBC</entry><entry align="center">Ring sizes - 8, 4, 3</entry></row><row><entry align="center" /><entry align="center">SU-46</entry><entry align="center" /><entry align="center" /><entry align="center" /></row><row><entry align="center">SIV</entry><entry align="center">*SIZ-7</entry><entry align="center">3D</entry><entry align="center">3.5 x 3.9, 3.7 x 3.8, 3.8 x 3.9</entry><entry align="center">Ring sizes - 8, 4</entry></row><row><entry align="center">THO</entry><entry align="center">*Thomsonite</entry><entry align="center">3D</entry><entry align="center">2.3 x 3.9, 4.0 x 2.2, 3.0 x 2.2</entry><entry align="center">Ring sizes - 8, 4</entry></row><row><entry align="center" /><entry align="center">[Al-Co-P-O]-THO</entry><entry align="center" /><entry align="center" /><entry align="center" /></row><row><entry align="center" /><entry align="center">[Ga-Co-P-O]-THO</entry><entry align="center" /><entry align="center" /><entry align="center" /></row><row><entry align="center" /><entry align="center">|Rb<sub>20</sub>|[Ga<sub>20</sub>Ge<sub>20</sub>O<sub>80</sub>-THO</entry><entry align="center" /><entry align="center" /><entry align="center" /></row><row><entry align="center" /><entry align="center">[Zn-Al-As-O]-THO</entry><entry align="center" /><entry align="center" /><entry align="center" /></row><row><entry align="center" /><entry align="center">[Zn-P-O]-THO</entry><entry align="center" /><entry align="center" /><entry align="center" /></row><row><entry align="center" /><entry align="center">[Ga-Si-O]-THO)</entry><entry align="center" /><entry align="center" /><entry align="center" /></row><row><entry align="center" /><entry align="center">[Zn-Co-P-O]-THO</entry><entry align="center" /><entry align="center" /><entry align="center" /></row><row><entry align="center">TSC</entry><entry align="center">*Tschörtnerite</entry><entry align="center">3D</entry><entry align="center">4.2 x 4.2, 5.6 x 3.1</entry><entry align="center">Ring sizes - 8, 6, 4</entry></row><row><entry align="center">UEI</entry><entry align="center">*Mu-18</entry><entry align="center">2D</entry><entry align="center">3.5 x 4.6, 3.6 x 2.5</entry><entry align="center">Ring sizes - 8, 6, 4</entry></row><row><entry align="center">UFI</entry><entry align="center">*UZM-5</entry><entry align="center">2D</entry><entry align="center">3.6 x 4.4, 3.2 x 3.2 (cage)</entry><entry align="center">Ring sizes - 8, 6, 4</entry></row><row><entry align="center">VNI</entry><entry align="center">*VPI-9</entry><entry align="center">3D</entry><entry align="center">3.5 x 3.6, 3.1 x 4.0</entry><entry align="center">Ring sizes - 8, 5, 4, 3</entry></row><row><entry align="center">YUG</entry><entry align="center">*Yugawaralite</entry><entry align="center">2D</entry><entry align="center">2.8 x 3.6, 3.1 x 5.0</entry><entry align="center">Ring sizes - 8, 5, 4</entry></row><row><entry align="center" /><entry align="center">Sr-Q</entry><entry align="center" /><entry align="center" /><entry align="center" /></row><row><entry align="center">ZON</entry><entry align="center">*ZAPO-M1</entry><entry align="center">2D</entry><entry align="center">2.5 x 5.1, 3.7 x 4.4</entry><entry align="center">Ring sizes - 8, 6, 4</entry></row><row><entry align="center" /><entry align="center">GaPO-DAB-2</entry><entry align="center" /><entry align="center" /><entry align="center" /></row><row><entry align="center" /><entry align="center">UiO-7</entry><entry align="center" /><entry align="center" /><entry align="center" /></row></tbody></tgroup></table></tables>
0051Small pore molecular sieves with particular application for exposure to reducing conditions are set out in Table 2. <tables id="tabl0008" num="0008"><table frame="all"><title><b>Table 2: Preferred Small Pore Molecular Sieves.</b></title><tgroup cols="2"><colspec colnum="1" colname="col1" colwidth="34mm" /><colspec colnum="2" colname="col2" colwidth="40mm" /><thead><row><entry align="center" valign="top"><b>Structure</b></entry><entry align="center" valign="top"><b>Molecular Sieve</b></entry></row></thead><tbody><row><entry align="center">CHA</entry><entry align="center">SAPO-34</entry></row><row><entry align="center" /><entry align="center">AlPO-34</entry></row><row><entry align="center" /><entry align="center">SSZ-13</entry></row><row><entry align="center">LEV</entry><entry align="center">Levynite</entry></row><row><entry align="center" /><entry align="center">Nu-3</entry></row><row><entry align="center" /><entry align="center">LZ-132</entry></row><row><entry align="center" /><entry align="center">SAPO-35</entry></row><row><entry align="center" /><entry align="center">ZK-20</entry></row><row><entry align="center">ERI</entry><entry align="center">Erionite</entry></row><row><entry align="center" /><entry align="center">ZSM-34</entry></row><row><entry align="center" /><entry align="center">Linde type T</entry></row><row><entry align="center">DDR</entry><entry align="center">Deca-dodecasil 3R</entry></row><row><entry align="center" /><entry align="center">Sigma-1</entry></row><row><entry align="center">KFI</entry><entry align="center">ZK-5</entry></row><row><entry align="center" /><entry align="center">18-crown-6</entry></row><row><entry align="center" /><entry align="center">[Zn-Ga-As-O]-KFI</entry></row><row><entry align="center">EAB</entry><entry align="center">TMA-E</entry></row><row><entry align="center">PAU</entry><entry align="center">ECR-18</entry></row><row><entry align="center">MER</entry><entry align="center">Merlinoite</entry></row><row><entry align="center">AEI</entry><entry align="center">SSZ-39</entry></row><row><entry align="center" /><entry align="center">SAPO-18</entry></row><row><entry align="center">GOO</entry><entry align="center">Goosecreekite</entry></row><row><entry align="center">YUG</entry><entry align="center">Yugawaralite</entry></row><row><entry align="center">GIS</entry><entry align="center">P1</entry></row><row><entry align="center">VNI</entry><entry align="center">VPI-9</entry></row></tbody></tgroup></table></tables>
0052Molecular sieves for use in the present application include natural and synthetic molecular sieves, preferably synthetic molecular sieves because the molecular sieves can have a more uniform: silica-to-alumina ratio (SAR), crystallite size, crystallite morphology, and the absence of impurities (e.g. alkaline earth metals). Small pore aluminosilicate molecular sieves may have a silica-to-alumina ratio (SAR) of from 2 to 300, optionally 4 to 200, and preferably 8 to 150. It will be appreciated that higher SAR ratios are preferred to improve thermal stability but this may negatively affect transition metal exchange.
0053The at least one reactant may contact the catalyst at a gas hourly space velocity of from 5,000 hr<sup>-1</sup> to 500,000 hr<sup>-1</sup>, optionally from 10,000 hr<sup>-1</sup> to 200,000 hr<sup>-1</sup>.
0054Small pore molecular sieves for use in the invention may have three-dimensional dimensionality, i.e. a pore structure which is interconnected in all three crystallographic dimensions, or two-dimensional dimensionality. In one embodiment, the small pore molecular sieves for use in the present invention consist of molecular sieves having three-dimensional dimensionality. In another embodiment, the small pore molecular sieves for use in the present invention consist of molecular sieves having two-dimensional dimensionality.
0055In certain embodiments, the small pore molecular sieve comprises, consists essentially of, or consists of a disordered framework selected from the group consisting of ABC-6, AEI/CHA, AEI/SAV, AEN/UEI, AFS/BPH, BEC/ISV, beta, faujasite, ITE/RTH, KFI/SAV, lovdarite, montesommaite, MTT/TON, pentasils, SBS/SBT, SSF/STF, SSZ-33, and ZSM-48. In a preferred embodiment, one or more of the small pore molecular sieves may comprise a CHA Framework Type Code selected from SAPO-34, AlPO-34, SAPO-47, ZYT-6, CAL-1, SAPO-40, SSZ-62 or SSZ-13 and/or an AEI Framework Type Code of selected from AlPO-18, SAPO-18, SIZ-8, or SSZ-39. In one embodiment, the mixed phase composition is an AEI/CHA-mixed phase composition. The ratio of each framework type in the molecular sieve is not particularly limited. For example, the ratio of AEI/CHA may range from about 5/95 to about 95/5, preferably about 60/40 to 40/60. In an exemplary embodiment, the ratio of AEI/CHA may range from about 5/95 to about 40/60. It is envisioned that a disordered molecular sieve, such as AEI/CHA, will be used as the support for one or more transition metals, such as Cr, Mn, Fe, Co, Ce, Ni, Cu, Zn, Ga, Mo, Ru, Rh, Pd, Ag, In, Sn, Re, Ir, Pt, and mixtures thereof, preferably Cr, Mn, Fe, Co, Ce, Ni, Cu, Rh, Pd, Pt, and mixtures thereof, more preferably Fe and/or Cu, and most preferably copper.
0056The total of the copper metal that can be included in the molecular sieve can be from 0.01 to 20 wt%, based on the total weight of the catalyst. In one embodiment, the total of the copper that can be included can be from 0.1 to 10 wt%. In a particular embodiment, the total of copper that can be included is from 0.5 to 5 wt%. The copper may be included in the molecular sieve by any feasible method. For example, it can be added after the molecular sieve has been synthesized, e.g. by incipient wetness or exchange process; or can be added during molecular sieve synthesis.
0057A preferred two dimensional small pore molecular sieve for use in the present invention consists of Cu/LEV, such as Cu/Nu-3, whereas a preferred copper-containing three dimensional small pore molecular sieve/aluminophosphate molecular sieve for use in the present invention consists of Cu/CHA, such as Cu/SAPO-34 or Cu/SSZ-13.
0058The molecular sieve catalysts for use in the present invention can be coated on a suitable substrate monolith or can be formed as extruded-type catalysts, but are preferably used in a catalyst coating. In one embodiment, the molecular sieve catalyst is coated on a flow-through monolith substrate (i.e. a honeycomb monolithic catalyst support structure with many small, parallel channels running axially through the entire part) or filter monolith substrate such as a wall-flow filter etc. The molecular sieve catalyst for use in the present invention can be coated, e.g. as a washcoat component, on a suitable monolith substrate, such as a metal or ceramic flow through monolith substrate or a filtering substrate, such as a wall-flow filter or sintered metal or partial filter (such as is disclosed in <patcit id="pcit0006" dnum="WO0180978A"><text>WO 01/80978</text></patcit> or <patcit id="pcit0007" dnum="EP1057519A"><text>EP 1057519</text></patcit>, the latter document describing a substrate comprising convoluted flow paths that at least slows the passage of soot therethrough). Alternatively, the molecular sieves for use in the present invention can be synthesized directly onto the substrate. Alternatively, the molecular sieve catalysts according to the invention can be formed into an extruded-type flow through catalyst.
0059Washcoat compositions containing the molecular sieves for use in the present invention for coating onto the monolith substrate for manufacturing extruded type substrate monoliths can comprise a binder selected from the group consisting of alumina, silica, (non-molecular sieve) silica-alumina, naturally occurring clays, TiO<sub>2</sub>, ZrO<sub>2</sub>, and SnO<sub>2</sub>.
0060In one embodiment, the nitrogen oxides are reduced with the reducing agent at a temperature of at least 100°C. In another embodiment, the at least one reactant are reduced with the reducing agent at a temperature from about 150°C to 750°C. In a particular embodiment, the temperature range is from 175 to 550°C, or more particularly from 175 to 400°C.
0061For a reactant including nitrogen oxides, the reduction of nitrogen oxides may be carried out in the presence of oxygen or in the absence of oxygen. The source of nitrogenous reductant can be ammonia <i>per se</i>, hydrazine or any suitable ammonia precursor (such as urea ((NH<sub>2</sub>)<sub>2</sub>CO)), ammonium carbonate, ammonium carbamate, ammonium hydrogen carbonate or ammonium formate.
0062The process of the present invention is performed on a gas derived from a mobile internal combustion engine, in particular a vehicular internal combustion engine with a lean/rich cycle, such as a diesel engine, a gasoline engine, or an engine powered by liquid petroleum gas or natural gas.
0063For a reactant including nitrogen oxides, the nitrogenous reductant may be metered into the flowing exhaust gas only when it is determined that the molecular sieves catalyst is capable of catalysing NO<sub>X</sub> reduction at or above a desired efficiency, such as at above 100°C, above 150°C or above 175°C. The determination by the control means can be assisted by one or more suitable sensor inputs indicative of a condition of the engine selected from the group consisting of: exhaust gas temperature, catalyst bed temperature, accelerator position, mass flow of exhaust gas in the system, manifold vacuum, ignition timing, engine speed, lambda value of the exhaust gas, the quantity of fuel injected in the engine, the position of the exhaust gas recirculation (EGR) valve and thereby the amount of EGR and boost pressure.
0064Metering may be controlled in response to the quantity of nitrogen oxides in the exhaust gas determined either directly (using a suitable NO<sub>X</sub> sensor) or indirectly, such as using pre-correlated look-up tables or maps - stored in the control means - correlating any one or more of the abovementioned inputs indicative of a condition of the engine with predicted NO<sub>X</sub> content of the exhaust gas.
EXAMPLES
0065Although the invention is illustrated and described herein with reference to specific embodiments, the invention is not intended to be limited to the details shown. Rather, various modifications may be made in the details within the scope and range of equivalents of the claims and without departing from the invention.
1. Steady State SCR Evaluation
0066Steady-state selective catalytic reduction (SCR) activity tests were conducted in a quartz reactor of 24 inches in length, and uniformly heated by two tube furnace units of 12 inches length. Experiments were performed at a gas hourly space velocity of 30,000 hr<sup>-1</sup> utilizing catalyst dimensions of 1 inch diameter x 1 inch length. All gas lines directly connected to the reactor were maintained at 130 °C by heating tape to prevent gas species adsorption on the walls of the gas line. Water vapour was provided by a water bomb, which was constantly maintained at 70°C.
0067Prior to reaching the catalyst bed, the feed gas was heated and mixed upstream in the reactor via an inert thermal mass. The temperature of the gas stream was monitored at the catalyst inlet, centre of the catalyst bed, and at the outlet by k-type thermocouples. Reacted feed gas was analysed by a FTIR downstream from the catalyst bed at a sampling rate of 1.25 s<sup>-1</sup>. The composition of the inlet feed gas could be determined by sampling from a bypass valve located upstream of the reactor.
0068Steady-state SCR experiments were initially performed on catalyst samples that had been hydrothermally (HT) aged at 700°C for 2 hours in the presence of air containing 4.5% H<sub>2</sub>O. All steady state experiments were conducted using a feed gas of NO and NH<sub>3</sub> containing 350 ppm of NO, with an ammonia-to-NO (ANR) ratio of 1 (i.e., 350 ppm of NH<sub>3</sub>). The remainder of the feed gas composition was as follows: 14% O<sub>2</sub>, 4.6% H<sub>2</sub>O, 5% CO<sub>2</sub>, balance N<sub>2</sub>. The steady-state NO<sub>X</sub> conversion was determined at catalyst bed temperatures of 150°C, 200°C, 250°C, 350°C, 450°C, 550°C, and 650°C.
0069Catalysts were then aged under lean-rich cycling conditions at 600°C for 12 h. The lean portion of the cycle consisted of exposure to 200 ppm NO, 10% O<sub>2</sub>, 5% H<sub>2</sub>O, 5% CO<sub>2</sub> in N<sub>2</sub> for 5 seconds at a space velocity of 30,000 h<sup>-1</sup>. The rich portion of the cycle consisted of exposure to 200 ppm NO, 5000 ppm C<sub>3</sub>H<sub>6</sub>, 1.3% H<sub>2</sub>, 4% CO, 1%O<sub>2</sub>, 5% H<sub>2</sub>O, 5% CO<sub>2</sub> in N<sub>2</sub> for 15 seconds. After the aging, steady-state SCR experiments were performed as described above.
0070In <figref idref="f0003">Figure 3</figref>, the NO<sub>X</sub> conversion efficiency is shown for embodiments of the present invention and a comparative example. Cu/SAPO-34, Cu/Nu-3 and Cu/SSZ-13, small pore molecular sieve catalysts according to embodiments of the invention, are shown after having undergone the above described hydrothermal aging treatment and lean/rich aging treatment, respectively. A comparative example showing Cu/Beta, a large pore molecular sieve catalyst, is also shown after both hydrothermal aging and lean/rich aging. As is evident, the small pore molecular sieve catalysts demonstrated enhanced NO<sub>X</sub> conversion efficiencies especially in the temperature window of 200 to 500°C.
2. NAC+SCR Experiments
0071NO<sub>X</sub> adsorber catalyst (NAC) and SCR cores were initially hydrothermally aged at 750°C for 16 hours in a 4.5% H<sub>2</sub>O in air gas mixture. Samples were then mounted in the same reactor setup described above with the NAC catalyst mounted directly in front of the SCR catalyst. The catalysts were aged at 600°C for 12 hours under the lean-rich aging conditions described above (5 seconds lean/15 seconds rich).
0072The catalysts were then cooled to 450°C under lean-rich cycling (60 seconds lean/5 seconds rich, same gas compositions). At 450°C, 25 lean-rich cycles were completed (60 seconds lean/5 seconds rich) with the last five cycles used to determine an average cycle NO<sub>X</sub> conversion for the catalyst. After the 25<sup>th</sup> cycle, the catalyst was held under the lean gas composition for 5 minutes. The catalyst was then cooled and evaluated at 400°C, 350°C, 300°C, 250°C, 200°C, and 175°C following the aforementioned cycle procedure.
0073In <figref idref="f0004">Figure 4</figref>, the NO<sub>X</sub> conversion efficiency is shown for embodiments of the present invention and two comparative examples. NAC+Cu/SAPO-34 and NAC+ Cu/SSZ-13, small pore molecular sieve catalysts according to embodiments of the invention are shown after having undergone the above described lean/rich aging treatment. A comparative example showing NAC alone and NAC+Fe/Beta, a large pore molecular sieve catalyst, is also shown after lean/rich aging. As is evident, the small pore molecular sieve catalysts demonstrate enhanced NO<sub>X</sub> conversion efficiencies comparable to and/or better than NAC alone or NAC+Fe/Beta, especially in the temperature window of 250 to 450°C.
Contents5
4 sheets
Sheet 1 Sheet 2 Sheet 3 Sheet 4
Every citation, both ways
| Document | Relation | Office | Cited during |
|---|---|---|---|
| KR20250069742A | Cited by | Republic of Korea | Applicant |
| US17035809P | Cites | United States of America | Filed by opponent |
| US2004076565A1 | Cites | United States of America | Filed by opponent |
| WO2006008625A1 | Cites | World Intellectual Property Organization (WIPO) | Filed by opponent |
| WO2008106518A2 | Cites | World Intellectual Property Organization (WIPO) | Filed by opponent |
| WO2008106519A1 | Cites | World Intellectual Property Organization (WIPO) | Filed by opponent |
| WO2008106519A1 | Cites | World Intellectual Property Organization (WIPO) | Filed by opponent |
| WO2008118434A1 | Cites | World Intellectual Property Organization (WIPO) | Filed by opponent |
| WO2008132452A2 | Cites | World Intellectual Property Organization (WIPO) | Filed by opponent |
| WO2008132452A2 | Cites | World Intellectual Property Organization (WIPO) | Filed by opponent |
| US2008202107A1 | Cites | United States of America | Filed by opponent |
| JP2009185621A | Cites | Japan | Filed by opponent |
| US2009196812A1 | Cites | United States of America | Filed by opponent |
| WO2010114873A2 | Cites | World Intellectual Property Organization (WIPO) | Filed by opponent |
| WO2010121257A1 | Cites | World Intellectual Property Organization (WIPO) | Filed by opponent |
| US31283210P | Cites | United States of America | Filed by opponent |
| US7062904B1 | Cites | United States of America | Filed by opponent |
| WO2008118434A1 | Cites | World Intellectual Property Organization (WIPO) | – |
| WO2008132452A2 | Cites | World Intellectual Property Organization (WIPO) | – |
| GB2361653A | Cites | United Kingdom | – |
| US2004076565A1 | Cites | United States of America | – |
| US2007269353A1 | Cites | United States of America | – |
| TATSUMI ISHIHARA ET AL: "Copper Ion-Exchanged SAPO-34 as a Thermostable Catalyst for Selective Reduction of NO with C3H6", JOURNAL OF CATALYSIS, ACADEMIC PRESS, DULUTH, MN, US, vol. 169, 1 January 1997 (1997-01-01), pages 93-102, XP002463595, ISSN: 0021-9517, DOI: 10.1006/JCAT.1997.1681 | Non-patent | – | – |
| MICHAEL BECKMANN: "Beschreibung unterschiedlicher Techniken und deren Entwicklungspotentiale zur Minderung von Stickstoffoxiden im Abgas von Abfallver-brennungsanlagen;", UMWELTBUNDESAMT, vol. 71, 2011, pages 52 - 54, XP055519911 | Non-patent | – | Filed by opponent |
75 members in 11 offices
Members75
| Document | Office | Kind | |
|---|---|---|---|
| GB201006381D0 | United Kingdom | D0 | |
| GB2469581A | United Kingdom | A | |
| US2010267548A1 | United States of America | A1 | |
| WO2010121257A1 | World Intellectual Property Organization (WIPO) | A1 | |
| DE102010027883A1 | Germany | A1 | |
| US7998443B2 | United States of America | B2 | |
| WO2011112949A1 | World Intellectual Property Organization (WIPO) | A1 | |
| US2011281720A1 | United States of America | A1 | |
| GB201119664D0 | United Kingdom | D0 | |
| KR20120006053A | Republic of Korea | A | |
| GB2482094A | United Kingdom | A | |
| US8101147B2 | United States of America | B2 | |
| EP2419209A1 | European Patent Office (EPO) | A1 | |
| US2012093702A1 | United States of America | A1 | |
| US8182777B2 | United States of America | B2 | |
| US2012184429A1 | United States of America | A1 | |
| US2012189518A1 | United States of America | A1 | |
| US2012213673A1 | United States of America | A1 | |
| JP2012523958A | Japan | A | |
| KR20120121925A | Republic of Korea | A | |
| CN102802791A | China | A | |
| US8347614B2 | United States of America | B2 | |
| CN102869427A | China | A | |
| EP2555853A1 | European Patent Office (EPO) | A1 | |
| US2013095012A1 | United States of America | A1 | |
| RU2011146545A | Russian Federation | A | |
| JP2013522011A | Japan | A | |
| KR101294098B1 | Republic of Korea | B1 | |
| US8518355B2 | United States of America | B2 | |
| US2013323146A1 | United States of America | A1 | |
| GB201320065D0 | United Kingdom | D0 | |
| EP2698192A1 | European Patent Office (EPO) | A1 | |
| EP2698193A1 | European Patent Office (EPO) | A1 | |
| GB201402348D0 | United Kingdom | D0 | |
| EP2555853A4 | European Patent Office (EPO) | A4 | |
| GB2507006A | United Kingdom | A | |
| RU2012143404A | Russian Federation | A | |
| GB2482094B | United Kingdom | B | |
| GB2507902A | United Kingdom | A | |
| US8753598B2 | United States of America | B2 | |
| US8809217B2 | United States of America | B2 | |
| US2014248203A1 | United States of America | A1 | |
| GB2507006B | United Kingdom | B | |
| US8932973B2 | United States of America | B2 | |
| GB2507902B | United Kingdom | B | |
| RU2546666C2 | Russian Federation | C2 | |
| US2015141237A1 | United States of America | A1 | |
| JP5767206B2 | Japan | B2 | |
| JP2015164729A | Japan | A | |
| US9199195B2 | United States of America | B2 | |
| US2016038876A1 | United States of America | A1 | |
| JP5882238B2 | Japan | B2 | |
| EP2995367A1 | European Patent Office (EPO) | A1 | |
| BRPI1015166A2 | Brazil | A2 | |
| CN105749747A | China | A | |
| CN105833717A | China | A | |
| RU2593989C2 | Russian Federation | C2 | |
| BR112012021655A2 | Brazil | A2 | |
| CN102869427B | China | B | |
| US9802156B2 | United States of America | B2 | |
| KR101809040B1 | Republic of Korea | B1 | |
| EP2995367B1This record | European Patent Office (EPO) | B1 | |
| KR20170141263A | Republic of Korea | A | |
| DK2995367T3 | Denmark | T3 | |
| JP6363554B2 | Japan | B2 | |
| JP2019000848A | Japan | A | |
| EP3456413A2 | European Patent Office (EPO) | A2 | |
| EP3456413A3 | European Patent Office (EPO) | A3 | |
| US10532349B2 | United States of America | B2 | |
| KR20200007089A | Republic of Korea | A | |
| JP2020116573A | Japan | A | |
| KR102180723B1 | Republic of Korea | B1 | |
| JP6931628B2 | Japan | B2 | |
| EP4112168A1 | European Patent Office (EPO) | A1 | |
| EP4112168B1 | European Patent Office (EPO) | B1 |
103 legal events, as 11 offices reported them to INPADOC
Over the term
Point at a mark for the eventEvents
| Event | Code | Office | |
|---|---|---|---|
| Patent revokedRevoked27W | 27W | EP | |
| Gb: patent revoked under art. 102 of the ep convention designating the uk as contracting stateRevokedGBPR | GBPR | EP | |
| Patent ceasedCeasedPL | PL | CH | |
| Patent revokedRevokedORIGINAL CODE: 0009271RDAG | RDAG | EP | |
| Information on the status of an ep patent application or granted ep patentGrantedSTATUS: PATENT REVOKEDSTAA | STAA | EP | |
| Appeal procedure closedAppealORIGINAL CODE: EPIDOSNNOA9OAPBU | APBU | EP | |
| Epo's revocation decision now finalR064 | R064 | DE | |
| Patent revoked by epoRevokedR103 | R103 | DE | |
| Annual fee paid to national office [announced via postgrant information from national office to epo]GrantedPGFP | PGFP | EP | |
| Annual fee paid to national office [announced via postgrant information from national office to epo]GrantedPGFP | PGFP | EP | |
| Opt-out of the competence of the unified patent court (upc) registeredP01 | P01 | EP | |
| Annual fee paid to national office [announced via postgrant information from national office to epo]GrantedPGFP | PGFP | EP | |
| Annual fee paid to national office [announced via postgrant information from national office to epo]GrantedPGFP | PGFP | EP | |
| Annual fee paid to national office [announced via postgrant information from national office to epo]GrantedPGFP | PGFP | EP | |
| Annual fee paid to national office [announced via postgrant information from national office to epo]GrantedPGFP | PGFP | EP | |
| Annual fee paid to national office [announced via postgrant information from national office to epo]GrantedPGFP | PGFP | EP | |
| Opposition withdrawnWithdrawnORIGINAL CODE: 0009264PLBP | PLBP | EP | |
| Date of receipt of statement of grounds of appeal recordedAppealORIGINAL CODE: EPIDOSNNOA3OAPBQ | APBQ | EP | |
| Appeal reference modifiedAppealORIGINAL CODE: EPIDOSCREFNOAPAH | APAH | EP | |
| Appeal reference recordedAppealORIGINAL CODE: EPIDOSNREFNOAPBM | APBM | EP | |
| Date of receipt of notice of appeal recordedAppealORIGINAL CODE: EPIDOSNNOA2OAPBP | APBP | EP | |
| Communication despatched that patent is revokedRevokedORIGINAL CODE: EPIDOSNREV1RDAF | RDAF | EP | |
| Opposition filed (corrected)OppositionR26 | R26 | EP | |
| Opposition data, opponent's data or that of the opponent's representative modifiedOppositionORIGINAL CODE: 0009299OPPOPLAB | PLAB | EP | |
| Lapsed in a contracting state [announced via postgrant information from national office to epo]LapsedPG25 | PG25 | EP | |
| Lapsed in a contracting state [announced via postgrant information from national office to epo]LapsedPG25 | PG25 | EP | |
| Lapsed in a contracting state [announced via postgrant information from national office to epo]LapsedPG25 | PG25 | EP | |
| Lapsed in a contracting state [announced via postgrant information from national office to epo]LapsedPG25 | PG25 | EP | |
| Lapsed in a contracting state [announced via postgrant information from national office to epo]LapsedPG25 | PG25 | EP | |
| Change of representativeR082 | R082 | DE | |
| Lapsed in a contracting state [announced via postgrant information from national office to epo]LapsedPG25 | PG25 | EP | |
| Reply of patent proprietor to notice(s) of opposition receivedOppositionORIGINAL CODE: EPIDOSNOBS3PLBB | PLBB | EP | |
| Lapsed in a contracting state [announced via postgrant information from national office to epo]LapsedPG25 | PG25 | EP | |
| Lapsed in a contracting state [announced via postgrant information from national office to epo]LapsedPG25 | PG25 | EP | |
| Information related to reply of patent proprietor to notice(s) of opposition deletedOppositionORIGINAL CODE: EPIDOSDOBS3PLAS | PLAS | EP | |
| Reply of patent proprietor to notice(s) of opposition receivedOppositionORIGINAL CODE: EPIDOSNOBS3PLBB | PLBB | EP | |
| Lapsed in a contracting state [announced via postgrant information from national office to epo]LapsedPG25 | PG25 | EP | |
| Patent lapsedLapsedMM4A | MM4A | IE | |
| Lapsed because of non-payment of the annual feeLapsedMM | MM | BE | |
| Lapsed in a contracting state [announced via postgrant information from national office to epo]LapsedPG25 | PG25 | EP | |
| Opposition filedOpposition26 | 26 | EP | |
| Opposition filedOpposition26 | 26 | EP | |
| Notice of opposition and request to file observation + time limit sentOppositionORIGINAL CODE: EPIDOSNOBS2PLAX | PLAX | EP | |
| Opposition filedOppositionORIGINAL CODE: 0009260PLBI | PLBI | EP | |
| Opposition filedOppositionORIGINAL CODE: 0009260PLBI | PLBI | EP | |
| Opposition filed against patentOppositionR026 | R026 | DE | |
| Lapsed in a contracting state [announced via postgrant information from national office to epo]LapsedPG25 | PG25 | EP | |
| Lapsed in a contracting state [announced via postgrant information from national office to epo]LapsedPG25 | PG25 | EP | |
| Lapsed in a contracting state [announced via postgrant information from national office to epo]LapsedPG25 | PG25 | EP | |
| Lapsed in a contracting state [announced via postgrant information from national office to epo]LapsedPG25 | PG25 | EP | |
| Lapsed in a contracting state [announced via postgrant information from national office to epo]LapsedPG25 | PG25 | EP | |
| Lapsed in a contracting state [announced via postgrant information from national office to epo]LapsedPG25 | PG25 | EP | |
| Lapsed in a contracting state [announced via postgrant information from national office to epo]LapsedPG25 | PG25 | EP | |
| Lapsed in a contracting state [announced via postgrant information from national office to epo]LapsedPG25 | PG25 | EP | |
| Lapsed in a contracting state [announced via postgrant information from national office to epo]LapsedPG25 | PG25 | EP | |
| Lapsed in a contracting state [announced via postgrant information from national office to epo]LapsedPG25 | PG25 | EP | |
| Lapsed in a contracting state [announced via postgrant information from national office to epo]LapsedPG25 | PG25 | EP | |
| Lapsed in a contracting state [announced via postgrant information from national office to epo]LapsedPG25 | PG25 | EP | |
| Lapsed in a contracting state [announced via postgrant information from national office to epo]LapsedPG25 | PG25 | EP | |
| Lapsed in a contracting state [announced via postgrant information from national office to epo]LapsedPG25 | PG25 | EP | |
| Deletion acc. to par. 5 (withdrawal of the translation of the ep patent)MK05 | MK05 | AT | |
| Invalidated european patentMG4D | MG4D | LT | |
| Lapsed in a contracting state [announced via postgrant information from national office to epo]LapsedPG25 | PG25 | EP | |
| Lapsed in a contracting state [announced via postgrant information from national office to epo]LapsedPG25 | PG25 | EP | |
| Lapsed in a contracting state [announced via postgrant information from national office to epo]LapsedPG25 | PG25 | EP | |
| Lapsed in a contracting state [announced via postgrant information from national office to epo]LapsedPG25 | PG25 | EP | |
| Fee paymentPLFP | PLFP | FR | |
| Ep patent with danish claimsT3 | T3 | DK | |
| Translation for ep filed (entry of ep into country)FP | FP | NL | |
| New agentNV | NV | CH | |
| Dpma publication of mentioned ep patent grantGrantedR096 | R096 | DE | |
| Reference to at number (ep patent validated in austria)REF | REF | AT | |
| European patents granted designating irelandGrantedFG4D | FG4D | IE | |
| European patent takes effect as a national patent in ch/liEP | EP | CH | |
| Divisional application: reference to earlier applicationAC | AC | EP | |
| Designated contracting statesAK | AK | EP | |
| European patent grantedGrantedFG4D | FG4D | GB | |
| (expected) grantORIGINAL CODE: 0009210GRAA | GRAA | EP | |
| Information on the status of an ep patent application or granted ep patentGrantedSTATUS: THE PATENT HAS BEEN GRANTEDSTAA | STAA | EP | |
| Grant fee paidORIGINAL CODE: EPIDOSNIGR3GRAS | GRAS | EP | |
| Intention to grant announcedINTG | INTG | EP | |
| Despatch of communication of intention to grant a patentORIGINAL CODE: EPIDOSNIGR1GRAP | GRAP | EP | |
| Information on the status of an ep patent application or granted ep patentGrantedSTATUS: GRANT OF PATENT IS INTENDEDSTAA | STAA | EP | |
| Information provided on ipc code assigned before grantRIC1 | RIC1 | EP | |
| Information provided on ipc code assigned before grantRIC1 | RIC1 | EP | |
| Information provided on ipc code assigned before grantRIC1 | RIC1 | EP | |
| Information provided on ipc code assigned before grantRIC1 | RIC1 | EP | |
| Information provided on ipc code assigned before grantRIC1 | RIC1 | EP | |
| Information provided on ipc code assigned before grantRIC1 | RIC1 | EP | |
| Information provided on ipc code assigned before grantRIC1 | RIC1 | EP | |
| Information provided on ipc code assigned before grantRIC1 | RIC1 | EP | |
| Information provided on ipc code assigned before grantRIC1 | RIC1 | EP | |
| Information provided on ipc code assigned before grantRIC1 | RIC1 | EP | |
| Information provided on ipc code assigned before grantRIC1 | RIC1 | EP | |
| Information provided on ipc code assigned before grantRIC1 | RIC1 | EP | |
| Information provided on ipc code assigned before grantRIC1 | RIC1 | EP | |
| Amendment of ipc main classPREVIOUS MAIN CLASS: B01D0053940000R079 | R079 | DE | |
| Information on the status of an ep patent application or granted ep patentGrantedSTATUS: EXAMINATION IS IN PROGRESSSTAA | STAA | EP | |
| First examination report despatched17Q | 17Q | EP | |
| Request for examination filed17P | 17P | EP |
Numbers
- Publication
- 2995367
- Application
- 151898467
Titles3
- German
- KLEINPORIGE MOLEKULARSIEBGESTÜTZTE KUPFERKATALYSATOREN MIT BESTÄNDIGKEIT GEGEN MAGERE/REICHE ALTERUNG ZUR REDUKTION VON STICKSTOFFOXIDEN
- English
- SMALL PORE MOLECULAR SIEVE SUPPORTED COPPER CATALYSTS DURABLE AGAINST LEAN/RICH AGING FOR THE REDUCTION OF NITROGEN OXIDES
- French
- CATALYSEURS DURABLES A BASE DE CUIVRE SUPPORTES PAR UN TAMIS MOLECULAIRE A PETITS PORES CONTRE LE VIEILLISSEMENT PAUVRE/RICHE POUR LA REDUCTION D'OXYDES D'AZOTE
Classification
- CPC, 30
- B01D53/8628
- B01D53/9418
- B01J23/72
- B01J29/76
- B01J29/763
- B01J29/85
- B01J35/56
- B01J35/30
- B01D2251/2062
- B01D2251/208
- B01D2255/20761
- B01D2255/50
- B01D2258/012
- B01D2258/018
- B01D2258/0291
- B01J29/072
- B01J29/46
- B01J29/56
- B01J29/7615
- B01J29/7676
- B01J29/83
- B01J37/0009
- B01J37/0246
- B01J37/16
- B01J2229/42
- B01D2255/9202
- B01D2253/1122
- Y02A50/20
- Y02T10/12
- B01J35/617
- IPC, 15
- B01J37 02
- B01J37 16
- B01J29 072
- B01J29 56
- B01J29 76
- B01J29 46
- B01D53 86
- B01D53 94
- B01J29 83
- B01J35 00
- B01J35 04
- B01J37 00
- B01J29 85
- B01J35 30
- B01J35 56
Designated states36
- Contracting states, 36
- Austria
- Belgium
- Bulgaria
- Switzerland
- Cyprus
- Czechia
- Germany
- Denmark
- Estonia
- Spain
- Finland
- France
- United Kingdom
- Greece
- Croatia
- Hungary
- Ireland
- Iceland
- Italy
- Liechtenstein
- Lithuania
- Luxembourg
- Latvia
- Monaco
and 12 moreShow fewer
- North Macedonia
- Malta
- Netherlands (Kingdom of the)
- Norway
- Poland
- Portugal
- Romania
- Sweden
- Slovenia
- Slovakia
- San Marino
- Türkiye