Heat conducting material having an electromagnetic shielding effect and an enclosure including the same

BACKGROUND OF THE INVENTION

1. Field of the Invention

0001The present disclosure relates to a heat conductor and a device including the heat conductor, and particularly to a heat conductor in a rubber composition for shielding electromagnetic waves and to a device including the heat conductor.

2. Description of the Related Art

0002In recent years, electronic devices have been miniaturized and achieved greater functionality in many fields of, for example, households, offices, industries, and health care. The electromagnetic waves radiated from, for example, enclosures of electronic devices sometimes enter other electronic devices and cause the other electronic devices to malfunction.

0003As such, electronic devices malfunction due to electromagnetic waves from the outside. Thus, to prevent such malfunction, for example, the electronic devices are covered with electromagnetic wave shielding materials so that electromagnetic waves do not enter the electronic devices.

0004Conventional examples of the electromagnetic wave shielding materials include metal plates such as aluminum plates, metal-fiber wire meshes made of, for example, stainless-steel, plating films, and materials each having a surface treated to be conductive. These materials are separately used according to the application or the cost. Furthermore, the examples of the electromagnetic wave shielding materials also include a rubber material containing carbon for the conductivity. This rubber material produces advantages of low cost, durability, and adding the sealability to a part to which the rubber material is attached (Japanese Patent No. <patcit id="pcit0001" dnum="JP4759852B"><text>4759852</text></patcit> hereinafter referred to as Patent Literature (PTL) 1).

0005Since the electromagnetic wave shielding materials including this rubber material are used in a compressed state for a long period of time, they require not only sufficient conductivity but also excellent compression restorability as mechanical properties, that is, a low compression set. However, an electromagnetic wave shielding material containing a smaller amount of a filler for maintaining the rubber properties exhibits insufficient electromagnetic shielding effect. Thus, the electromagnetic wave shielding materials including this rubber material require the compatibility between the rubber properties and the electromagnetic shielding effect.

0006For example, PTL 1 suggests that a rubber material containing a plasticizer, graphite fillers, and a reinforcing agent satisfies the compatibility between the rubber properties and the electromagnetic shielding effect.

0007<patcit id="pcit0002" dnum="WO2013099089A"><text>WO2013/099089</text></patcit> discloses a heat conducting material in a form of a sheet containing a resin component and a plurality of flake graphite fillers each having a basal plane, wherein an acute angle is created between the basal plane of each of the flake graphite fillers and a planar direction of the sheet and has an average of 1° to 30°.

SUMMARY OF THE INVENTION

0008The electromagnetic wave shielding materials including the rubber materials containing fillers linearly improve the electromagnetic shielding effect almost in proportion to the amount of the fillers. In other words, as the amount of the fillers increases, the electromagnetic shielding effect of the electromagnetic wave shielding materials is increased.

0009However, the increased amount of the fillers reduces the moldability of the electromagnetic wave shielding materials. As a result, the electromagnetic wave shielding materials are hardened, and the rubber elasticity decreases.

0010As described in PTL 1, a composition in which graphite fillers are dispersed into a matrix of a thermoplastic resin has limitations in improvement in the electromagnetic shielding effect.

0011Thus, the present disclosure aims at providing a heat conductor containing graphite fillers, having electromagnetic wave properties, and having superior elasticity.

0012One non-limiting and exemplary embodiment provides a heat conductor including: a first layer containing a first resin component and a plurality of flake graphite fillers each having a basal plane; and a second layer containing a second resin component and the plurality of flake graphite fillers, wherein the heat conductor is a laminate including the first layer and the second layer, an average of first angles in the first layer is 35 degrees or smaller, each of the first angles being an acute angle between the basal plane of a corresponding one of the flake graphite fillers and a laminated surface of the laminate, and an average of second angles in the second layer ranges from 55 degrees to 90 degrees, each of the second angles being an acute angle between the basal plane of a corresponding one of the flake graphite fillers and the laminated surface of the laminate.

BRIEF DESCRIPTION OF DRAWINGS

0013<ul id="ul0001" list-style="none" compact="compact"><li><figref idref="f0001">FIG. 1</figref> is a cross-section view of a structure of a heat conductor according to an embodiment;</li><li><figref idref="f0001">FIG. 2</figref> is an oblique perspective view illustrating a flake graphite filler according to the embodiment; and</li><li><figref idref="f0002">FIG. 3</figref> is a cross-section view of another structure of a heat conductor according to the embodiment.</li></ul>

DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENT

0014An embodiment will be described hereinafter.

0015<figref idref="f0001">FIG. 1</figref> is a cross-section view of a structure of heat conductor 3 according to an embodiment. As illustrated in <figref idref="f0001">FIG. 1</figref>, flake graphite fillers 1 are oriented to two directions for respective layers in matrix resin 2 of heat conductor 3. Heat conductor 3 has a double-layered structure. Here, "flake" means a thin strip or a curved plate.

<Definition of orientation angle θ>

0016The definition of orientation angle θ will be described hereinafter with reference to <figref idref="f0001">FIG. 1</figref>. Sheet surfaces abbreviated as S and indicated by dotted lines are arbitrary and parallel to the line indicating the laminated surface of heat conductor 3 (laminate). Each of the dotted lines and a line indicating a surface of flake graphite filler 1 form orientation angle θ. The surface of flake graphite filler 1 is indicated by basal plane B, and orientation angle θ may be defined as an angle between basal plane B and the laminated surface of heat conductor 3. <figref idref="f0001">FIG. 1</figref> is a cross-section view of heat conductor 3. Since flake graphite fillers 1 are uniformly distributed in heat conductor 3, the same holds true for the other cross-sections of heat conductor 3.

0017Orientation angle θ is calculated in the following manner. A cross-section of heat conductor 3 as illustrated in <figref idref="f0001">FIG. 1</figref> is observed. Next, orientation angles θ of more than 20 flake graphite fillers 1 in the cross-section are measured and averaged. The average is defined as orientation angle θ. In other words, orientation angle θ is defined as an average of the angles of all flake graphite fillers 1. The same also holds for the following angles θ.

0018Here, orientation angle θ is an acute angle between the intersecting lines. Thus, orientation angle θ ranges from 0 degree to 90 degrees.

0019The angles between surfaces vary depending on each of the cross-sections. Here, orientation angle θ is defined by averaging orientation angles θ in a cross-section.

<Heat conductor>

0020In <figref idref="f0001">FIG. 1</figref>, flake graphite fillers 1 are horizontally oriented in upper layer 31 (first layer). Orientation angle θ (first angle) of flake graphite fillers 1 in upper layer 31 is 35 degrees or smaller. Such arrangement ensures the electric conductivity, and enables heat conductor 3 to exhibit the electromagnetic shielding effect as a whole. Orientation angle θ suitably falls within 30 degrees.

0021Setting orientation angle θ in upper layer 31 higher than 1 degree can adequately secure the number of contact points of flake graphite fillers 1, thus resulting in heat conductor 3 having higher thermal conductivity. Furthermore, setting orientation angle 0 of flake graphite fillers 1 within 35 degrees enable flake graphite fillers 1 to be oriented enough to increase the thermal conductivity in a surface direction of heat conductor 3. In contrast, the thermal conductivity in a thickness direction of heat conductor 3 is suppressed. Thus, orientation angle θ needs to be set within 35 degrees to ensure the thermal conductivity.

0022Flake graphite fillers 1 are vertically oriented in lower layer 32 (second layer) of heat conductor 3. Orientation angle θ (second angle) in lower layer 32 ranges from 55 degrees to 90 degrees. Thus, heat conductor 3 has a compression set as a whole.

0023Here, flake graphite fillers 1 hardly spread across the boundary between upper layer 31 and lower layer 32 of heat conductor 3. The boundary is clearly separated at the interface between these layers. Here, upper and lower surfaces of upper layer 31 and lower layer 32 are parallel to the laminated surface of heat conductor 3 (laminate).

<Flake graphite filler 1>

0024<figref idref="f0001">FIG. 2</figref> schematically illustrates flake graphite filler 1.

<Longer length "a">

0025As illustrated in <figref idref="f0001">FIG. 2</figref>, longer length "a" indicates the maximum length of flake graphite filler 1 in an arrow direction of "a" on basal plane B of flake graphite filler 1. Flake graphite fillers 1 may have a lower orientation degree in heat conductor 3 when longer length "a" is smaller than or equal to 5 µm on average in preparing heat conductor 3. When longer length "a" is larger than or equal to 300 µm on average, the dispersibility may decrease.

<Shorter length "b">

0026Shorter length "b" indicates the maximum length of flake graphite filler 1 perpendicular to longer length "a" on basal plane B.

<Thickness "c">

0027Thickness "c" indicates the maximum thickness of flake graphite filler 1 in a direction vertical to basal plane B as illustrated in <figref idref="f0001">FIG. 2</figref>.

<a/c>

0028The ratio (a/c) of longer length "a" to thickness "c" of flake graphite filler 1 is suitably 30 or higher on average. When a/c is smaller than 30 on average, the number of contact points between flake graphite fillers 1 is reduced, and the thermal conductivity decreases.

<a/b>

0029Furthermore, when shorter length "b" indicates the maximum length of flake graphite filler 1 perpendicular to longer length "a" on basal plane B, an average ratio (a/b) of longer length "a" to shorter length "b" suitably ranges from 1 to 30. When the average ratio of a/b exceeds 30, the shape of flake graphite fillers 1 in heat conductor 3 cannot be maintained.

0030Flake graphite fillers 1 having such a shape have suitable contacts in-between, and the thermal conductivity increases. However, the shape of flake graphite filler 1 described above is an example, and not necessarily limited to this.

0031When flake graphite fillers have such a unique shape and are oriented in one direction, it is highly possible that flake graphite fillers 1 may be in contact with each other. Furthermore, the contact areas of flake graphite fillers may increase. Thus, the conductive path can be efficiently formed, and the electromagnetic shielding effect can be increased.

<Heat conductor 3>

0032When orientation angle θ between basal plane B and the surface direction of heat conductor 3 is set within 35 degrees on average, higher electromagnetic shielding effect can be observed.

0033When orientation angle θ is set from 55 degrees to 90 degrees on average, flake graphite fillers 1 function as a spring in the rubber composition, and becomes a rubber molded product having a compression set.

0034The rubber molded product exhibiting the higher electromagnetic shielding effect and having a better compression set can be obtained by laminating layers oriented in two directions, as upper layer 31 and lower layer 32 of heat conductor 3 in <figref idref="f0001">FIG. 1</figref>.

0035Flake graphite fillers 1 in each of upper layer 31 and lower layer 32 are set to account for more than 50% to 80% of heat conductor 3 by mass. The layers with such content exhibit the high electromagnetic shielding effect and have a compression set.

0036When flake graphite fillers 1 in upper layer 31 account for 50% or lower of heat conductor 3 by mass, the amount of flake graphite fillers 1 for electromagnetic shielding is insufficient, and the electromagnetic shielding effect may decrease. When flake graphite fillers 1 in upper layer 31 account for 80% or higher of heat conductor 3 by mass, the amount of flake graphite fillers 1 in the resulting polymer is excessive, and the polymer becomes very brittle.

0037When flake graphite fillers 1 in lower layer 32 account for 50% or lower of heat conductor 3 by mass, the amount of flake graphite fillers 1 that produce restoring force against compression is insufficient, and the compression set becomes poor. When flake graphite fillers 1 in lower layer 32 account for 80% or higher of heat conductor 3 by mass, the resulting polymer becomes very brittle as upper layer 31.

0038The two layers in heat conductor 3 may be any as long as the proportion of upper layer 31 to lower layer 32 in thickness ranges from 40% to 60%. When the proportion of upper layer 31 falls below 40% or exceeds 60%, the electromagnetic shielding effect and the compression properties becomes unbalanced and incompatible.

0039Such properties can be exhibited when upper layer 31 and lower layer 32 are laminated (compressed) with the same surface area. Upper layer 31 may be larger than lower layer 32 in the other portions to dissipate heat.

0040For example, <figref idref="f0002">FIG. 3</figref> is a cross-section view of such a case. Heat conductor 3 is disposed between lid 50 and main unit 51. Upper layer 31 is larger than lower layer 32, and the edge portion of upper layer 31 is connected to heat dissipator 52.

0041Since upper layer 31 protrudes in the portion other than the laminated (compressed) portion, the heat can be dissipated into heat dissipator 52.

0042The thicknesses of upper layer 31 and lower layer 32 are changed depending on the respective positions. However, each of upper layer 31 and lower layer 32 requires a thickness of at least 1 mm to fulfill their functions.

0043Although the ratio of upper layer 31 to lower layer 32 in thickness is suitably 1:1, the quotient of upper layer 31 may range from 0.5 to 2.

0044Heat conductor 3 is suitable as a shielding material to prevent malfunction of an electronic device caused by the electromagnetic waves from the outside, that is, electromagnetic interference (EMI).

<Method for preparing flake graphite fillers 1>

0045The constituent elements of heat conductor 3 according to the embodiment will be more specifically described hereinafter.

0046Flake graphite fillers whose longer length "a" ranges from 5 µm to 300 µm and a/c ratio is 30 or higher on average can be obtained by, for example, milling a graphite film. Alternatively, natural graphite may be processed into flakes whose longer length "a" ranges from 5 µm to 300 µm and a/c ratio is 30 or higher on average. Flake graphite fillers 1 of one kind may be solely used, or flake graphite fillers 1 obtained by mixing multiple kinds may be used as long as longer length "a" and the a/c ratio satisfy the above conditions.

0047The graphite film can be obtained by graphitizing a polymer film through sintering it at a temperature of 2,400°C or higher and suitably 2,600°C to 3,000°C in an inert gas atmosphere. The graphite film may be sintered in a single step or in two or more steps by changing the respective temperatures. Suitable examples of the inert gas include nitrogen or argon due to the low cost. Suitable examples of the sintering time include a period from 2 hours to 6 hours.

0048The thickness of the polymer film to be graphitized may be selected as appropriate in accordance with thickness "c" of flake graphite fillers 1. Examples of the thickness include 400 µm or smaller and suitably ranging from 10 µm to 200 µm. When a comparatively thick polymer film is graphitized as a starting material and the resulting graphite film is milled, the graphite layers exfoliate. Thus, thinner flake graphite fillers can be obtained.

0049If the polymer film has a thickness larger than 400 µm, heat is less likely to be evenly applied to the film, thus reducing the crystallinity of the graphite. If the polymer film has a thickness smaller than 10 µm, the film is broken by the heat treatment.

0050Examples of suitable materials of the polymer film include polyimide, polyamide-imide, polyoxadiazole, polybenzothiazole, polybenzobisthiazole, polybenzoxazole, polybenzobisthiazole, polyphenyleneisophthalamide, poly(m-phenylene benzimidazole), poly(phenylenebenzobisimidazole), polythiazole, and polyparaphenylene vinylene. These materials are, for example, formed into films.

0051The preparation method is not particularly limited to the above. These materials may be used singly or in a combination of two or more. For example, two or more different kinds of the films may be graphitized, milled, and then mixed; or two or more different kinds of the materials that are conjugated or alloyed in advance may be formed into films and then graphitized. Particularly, graphite having superior properties can be obtained from polyimide films.

0052The obtained graphite film is milled into flake graphite fillers. Suitable examples of the milling method include making graphite fillers to collide against one another or physically collide against a hard material serving as a medium. Examples of the method also include ball milling, nanomizing, and jet milling.

0053The thickness of the graphite film to be milled may be selected as appropriate in accordance with thickness "c" of desired flake graphite fillers.

0054In processing natural graphite, the natural graphite is suitably pretreated by having it immersed in sulfuric acid and then heated, thereby causing the graphite layers to expand. After such pretreatment, shear force is applied to the expanded graphite, thereby accelerating exfoliation of the layers. As a result, flake graphite fillers having a higher a/c ratio can be easily obtained.

<Matrix resin 2>

0055Example components of matrix resin 2 include various thermoplastic resins and elastomers. Alternatively, a mixture of a thermoplastic resin having no rubber elasticity and an elastic elastomer may be used as matrix resin 2. Particularly, the elastic elastomer is suitably used as matrix resin 2.

0056Examples of the thermoplastic resin include: styrene polymers such as styrene-acrylonitrile copolymer, styrene-maleic anhydride copolymer, and (meth)acrylic acid ester-styrene copolymer; rubber toughened polymers such as acrylonitrile butadiene styrene (ABS) and acrylonitrile-Ethylene-Styrene (AES) resins; olefin polymers such as polyethylene, polypropylene, ethylene-vinyl acetate copolymer, ethylene-vinyl alcohol copolymer, and chlorinated polyethylene; vinyl chloride polymers such as polyvinyl chloride, ethylene-vinyl chloride polymer, and polyvinylidene chloride; (meth)acrylic acid ester polymers such as polymethyl methacrylate; imide polymers such as polyamide, polyimide, polyamide-imide, and polyether-imide; polyester polymers such as polyethylene terephthalate and polybutylene terephthalate; polyacetal; polycarbonate; polyarylate; polyphenylene ether; polyphenylene sulfide; fluororesins such as polytetrafluoroethylene and polyvinylidene fluoride; ketone polymers such as polyetherketone and polyether ether ketone; sulfone polymers such as polysulfone and polyethersulfone; urethane polymers; and polyvinyl acetate. These materials may be used singly or in a combination of two or more. Furthermore, some of these materials may be alloyed.

0057Examples of the elastomer include chloroprene rubber, isoprene rubber, natural rubber, styrene-butadiene rubber, butadiene rubber, butyl rubber, ethylene propylene rubber, ethylene propylene diene monomer (M-class) (EPDM) rubber, nitrile rubber, urethane rubber, acrylic rubber, silicone rubber, fluorine rubber, and hydrogenated nitrile rubber. These materials may be used singly or in a combination of two or more.

<Additives>

0058Heat conductor 3 of the embodiment may include various additives, in addition to flake graphite fillers 1 and matrix resin 2. Various additives are used, particularly when heat conductor 3 is a rubber composition including an elastomer. Examples of the additives for the rubber composition include a crosslinker for crosslinking the rubber components, a carbon black (e.g., Ketjen black, acetylene black) for improving the mechanical strength of the rubber components, and a plasticizer to be used in moderate amount for adjusting rubber hardness. In addition, the other additives including a vulcanizing agent such as stearic acid, an antidegradant, oil, a lubricant, and inorganic fillers (e.g., silica fillers, alumina fillers) can be added to the anisotropic heat conductive compositions as appropriate. Furthermore, the examples of the additives include a flame retardant.

0059Examples of the crosslinker include a sulfur crosslinker (vulcanizing agent) and a peroxide. The crosslinker is suitably added to the anisotropic heat conductive compositions in moderate amount. When a silicone rubber is used in matrix resin 2, a curing agent for curing silicone (e.g., tertiary amines) is suitably added. Moreover, curing accelerators including zinc oxide and active zinc oxide may be added to the anisotropic heat conductive compositions in moderate amount.

0060Examples of the flame retardant include an organic flame retardant, an inorganic flame retardant, and a reactive flame retardant. The retardants may be used singly or at least two of the retardants may be combined. Examples of the organic flame retardant include: halogen flame retardants such as a brominated epoxy compound, a brominated alkyltriazine compound, a brominated bisphenol epoxy resin, a brominated bisphenol phenoxy resin, a brominated bisphenol polycarbonate resin, a brominated polystyrene resin, a brominated crosslinked polystyrene resin, a brominated bisphenol cyanurate resin, a brominated polyphenylene ether, a decabromodiphenyl oxide, tetrabromobisphenol A, and an oligomer thereof, phosphoric acid esters such as trimethyl phosphate, triethyl phosphate, tripropyl phosphate, tributyl phosphate, tripentyl phosphate, trihexyl phosphate, tricyclohexyl phosphate, triphenyl phosphate, tricresyl phosphate, trixylenyl phosphate, cresyl diphenyl phosphate, dicresyl phenyl phosphate, dimethyl ethyl phosphate, methyl dibutyl phosphate, ethyl dipropyl phosphate, and hydroxyphenyl diphenyl phosphate compounds obtained by denaturing these phosphoric acid esters by various substituents; various condensed phosphoric acid ester compounds; phosphorous flame retardants such as phosphazene derivatives including phosphorus and nitrogen; and polytetrafluoroethylene. The retardants may be used singly or at least two of the retardants may be combined.

0061Examples of the inorganic flame retardant include aluminum hydroxide, antimony oxide, magnesium hydroxide, zinc borate, a zirconium compound, a molybdenum compound, zinc stannate, guanidine salt, a silicone compound, and a phosphazene compound. The retardants may be used singly or at least two of the retardants may be combined.

0062Examples of the reactive flame retardant include tetrabromobisphenol A, dibromophenol glycidyl ether, brominated aromatic triazine, tribromophenol, tetrabromophthalate, tetrachlorophthalic anhydride, dibromoneopentyl glycol, poly(pentabromobenzyl polyacrylate), chlorendic acid (HET acid), chlorendic anhydride (HET anhydride), brominated phenol glycidyl ether, and dibromocresyl glycidyl ether. The retardants may be used singly or at least two of the retardants may be combined.

0063The amount of the additives is suitably 30% or lower of the total amount of heat conductor 3 by mass. This is because the moderate amount of the additives maintains the quantitative balance between flake graphite fillers 1 and matrix resin 2, thus enabling heat conductor 3 to easily maintain satisfactory heat conductivity and to easily secure the moldability and the strength.

<Method of preparing heat conductor 3>

0064First, heat conductor 3 is prepared. The preparation method may be any as long as the components of matrix resin 2, flake graphite fillers 1, and the additives if necessary that are to be included in the anisotropic heat conductive composition are blended and kneaded in an appropriate order.

0065However, when the elastomer (rubber component) is used as a resin component, it is suitable that materials except the rubber crosslinking agent are first kneaded and then, the agent is added to avoid progression of the crosslinking of the rubber by the heat generated during the kneading.

0066The raw materials are kneaded in, for example, roll milling. In the roll milling, the anisotropic heat conductive compositions pass through a gap between a pair of rollers to form heat conductors. As the anisotropic heat conductive compositions are sandwiched between the rollers and pass through the gap therebetween, shear force produced by the rotating rollers is applied to the compositions, and the compositions are elongated in a direction parallel to the rotating direction of the rollers. Along with the elongation of matrix resin 2, flake graphite fillers 1 dispersed in the anisotropic heat conductive composition become oriented in the same direction.

0067As a result, basal planes B of flake graphite fillers 1 are successfully oriented in the surface direction of heat conductor 3. Increasing the degree of orientation of flake graphite fillers 1 requires heat conductor 3 to pass through the rollers multiple times. Moreover, when heat conductor 3 sticks onto one of the rollers when coming out from the rollers, heat conductor 3 is suitably separated from that roller, reversed, and then passes through the rollers again.

0068Before kneading the anisotropic heat conductive composition in the roll milling, the raw materials may be pre-kneaded by known kneaders, for example, a twin screw extruder, a single screw extruder, a twin or single screw feeder capable of applying heat, a feeder ruder, a Banbury mixer, and a roll mill.

0069Next, the anisotropic heat conductive composition is molded into heat conductor 3 with an intended thickness. The manner of molding heat conductor 3 is not particularly limited, as long as the thickness of heat conductor 3 can be adjusted. Here, calendaring can produce a sufficient pressure to heat conductor 3 in the thickness direction. Furthermore, such a process enables basal planes B of flake graphite fillers 1 to be oriented in the surface direction of heat conductor 3. Thus, the calendaring is suited to molding heat conductor 3.

0070In the calendaring, the anisotropic heat conductive composition is continuously fed to at least a pair of rollers to form heat conductors 3. Then, heat conductors 3 are wound up by a wind-up roll. Thus, the calendaring is suited to continuous production. The thickness of heat conductor 3 can be made more precise by hot rolling and then cold rolling the anisotropic heat conductive compositions in a preliminary process.

0071Alternatively, the anisotropic heat conductive compositions may be extruded after it is sufficiently kneaded by an internal batch mixer such as a Banbury mixer. In the extrusion, a anisotropic heat conductive compositions are continuously pushed out of a metal nozzle or a die that matches with the shape of heat conductor 3, thereby to form heat conductor 3. During the extrusion, shear force is applied to the anisotropic heat conductive composition in the extrusion direction, thus causing basal planes B of flake graphite fillers 1 to be oriented in the surface direction of heat conductor 3. Extruded heat conductor 3 may further be pressed between calendar rolls.

0072When the anisotropic heat conductive composition includes a rubber component, it is heated as necessary to promote the crosslinking (vulcanization) by the crosslinker, thereby to obtain heat conductor 3 with excellent flexibility and strength. Thereafter, heat conductor 3 is cut in a direction perpendicular to its plane and rotated 90 degrees, thereby to obtain heat conductor 3 in which flake graphite fillers 1 are oriented in the thickness direction.

0073When heat conductor 3 in <figref idref="f0001">FIG. 1</figref> is prepared, upper layer 31 in <figref idref="f0001">FIG. 1</figref> is first prepared in the above methods. Here, crosslinking the rubber component is stopped during the reaction.

0074Then, lower layer 32 of heat conductor 3 in which flake graphite fillers 1 are vertically oriented is laminated on upper layer 31. Finally, lower layer 32 and upper layer 31 are heated to produce heat conductor 3 (<figref idref="f0001">FIG. 1</figref>) having different two orientation directions of flake graphite fillers 1.

< Examples>

<<Examples 1 and 2>>

(i) Preparing flake graphite fillers 1

0075A polyimide film (Kapton film manufactured by Du Pont-Toray Co., Ltd.) 25 µm in thickness was heat treated for 4 hours at 2,600°C in an argon gas atmosphere, thereby to obtain a graphite film. The obtained graphite film was then milled by a jet mill for 15 minutes. The number of rotations by the classifier during the milling was 7,000. As a result, flake graphite fillers 1 each having the following shape were obtained. The longer length "a" was 17 µm on average.

(ii) Preparation of heat conductor 3

0076Obtained flake graphite fillers 1, EPDM (Esprene manufactured by Sumitomo Chemical Co., Ltd.), a peroxide serving as a crosslinker, and stearic acid were mixed together. The resultant mixture was sufficiently kneaded by a two-roll mixer with 8-inch diameter rollers to prepare heat conductor 3; meanwhile, flake graphite fillers 1 in the anisotropic heat conductive composition were oriented in the surface direction.

0077Table 1 shows the obtained anisotropic heat conductive compositions. The anisotropic heat conductive compositions were further heated at 170°C for five minutes to accelerate the vulcanization. Then, the anisotropic heat conductive compositions oriented in the horizontal and thickness directions were bonded together and heated at 170°C for five minutes to form heat conductors 3. Table 1 also shows the evaluation results.

<<Comparative examples 1 and 2>>

0078The anisotropic heat conductive compositions were prepared and molded according to the conditions in Table 1, as Examples 1 and 2. In each of Examples 1 to 6, heat conductor 3 includes two layers, that is, upper layer 31 in which flake graphite fillers 1 are oriented within 35 degrees with respect to a horizontal (surface) direction of heat conductor 3 and lower layer 32 in which flake graphite fillers 1 are oriented within a range from 55 degrees to 80 degrees with respect to the same. Heat conductor 3 in each of comparative examples 1 and 2 is a single layer. Upper layer 31 and lower layer 32 each have a thickness of 2 mm. <tables id="tabl0001" num="0001"><table frame="all"><title>[Table 1]</title><tgroup cols="9"><colspec colnum="1" colname="col1" colwidth="50mm" /><colspec colnum="2" colname="col2" colwidth="14mm" /><colspec colnum="3" colname="col3" colwidth="14mm" /><colspec colnum="4" colname="col4" colwidth="14mm" /><colspec colnum="5" colname="col5" colwidth="14mm" /><colspec colnum="6" colname="col6" colwidth="14mm" /><colspec colnum="7" colname="col7" colwidth="14mm" /><colspec colnum="8" colname="col8" colwidth="18mm" /><colspec colnum="9" colname="col9" colwidth="18mm" /><thead><row><entry morerows="1" align="center" valign="middle" /><entry namest="col2" nameend="col7" align="center" valign="middle">EXAMPLE</entry><entry namest="col8" nameend="col9" align="center" valign="middle">COMPARATIVE EXAMPLE</entry></row><row><entry align="center" valign="middle">1</entry><entry align="center" valign="middle">2</entry><entry align="center" valign="middle">3</entry><entry align="center" valign="middle">4</entry><entry align="center" valign="middle">5</entry><entry align="center" valign="middle">6</entry><entry align="center" valign="middle">1</entry><entry align="center" valign="middle">2</entry></row></thead><tbody><row><entry align="center" valign="middle">AMOUNT OF GRAPHITE</entry><entry align="center" valign="middle">60</entry><entry align="center" valign="middle">70</entry><entry align="center" valign="middle">60</entry><entry align="center" valign="middle">70</entry><entry align="center" valign="middle">60</entry><entry align="center" valign="middle">60</entry><entry align="center" valign="middle">70</entry><entry align="center" valign="middle">70</entry></row><row><entry align="center" valign="middle">ORIENTATION DEGREE (°) (UPPER LAYER 31/LOWER LAYER 32)</entry><entry align="center" valign="middle">10/80</entry><entry align="center" valign="middle">10/80</entry><entry align="center" valign="middle">30/60</entry><entry align="center" valign="middle">30/60</entry><entry align="center" valign="middle">35/80</entry><entry align="center" valign="middle">10/55</entry><entry align="center" valign="middle">10 (SINGLE LAYER)</entry><entry align="center" valign="middle">80 (SINGLE LAYER)</entry></row><row><entry align="center" valign="middle">SHIELDING EFFECT (DB)</entry><entry align="center" valign="middle">34</entry><entry align="center" valign="middle">50</entry><entry align="center" valign="middle">30</entry><entry align="center" valign="middle">50</entry><entry align="center" valign="middle">27</entry><entry align="center" valign="middle">30</entry><entry align="center" valign="middle">60</entry><entry align="center" valign="middle">20</entry></row><row><entry align="center" valign="middle">COMPRESSION SET (%)</entry><entry align="center" valign="middle">20</entry><entry align="center" valign="middle">23</entry><entry align="center" valign="middle">22</entry><entry align="center" valign="middle">25</entry><entry align="center" valign="middle">20</entry><entry align="center" valign="middle">27</entry><entry align="center" valign="middle">40</entry><entry align="center" valign="middle">13</entry></row><row><entry align="center" valign="middle">ACCEPTABILITY</entry><entry align="center" valign="middle">✔+</entry><entry align="center" valign="middle">✔+</entry><entry align="center" valign="middle">✔+</entry><entry align="center" valign="middle">✔+</entry><entry align="center" valign="middle">✔</entry><entry align="center" valign="middle">✔</entry><entry align="center" valign="middle">×</entry><entry align="center" valign="middle">×</entry></row></tbody></tgroup><tgroup cols="9" rowsep="0"><colspec colnum="1" colname="col1" colwidth="50mm" /><colspec colnum="2" colname="col2" colwidth="14mm" /><colspec colnum="3" colname="col3" colwidth="14mm" /><colspec colnum="4" colname="col4" colwidth="14mm" /><colspec colnum="5" colname="col5" colwidth="14mm" /><colspec colnum="6" colname="col6" colwidth="14mm" /><colspec colnum="7" colname="col7" colwidth="14mm" /><colspec colnum="8" colname="col8" colwidth="18mm" /><colspec colnum="9" colname="col9" colwidth="18mm" /><tbody><row><entry namest="col1" nameend="col9" align="justify">× FAIL ✔ ACCEPTABLE ✔+ EXCELLENT</entry></row></tbody></tgroup></table></tables>

<Evaluation of properties>

(1) Shielding effect

0079The shielding effect of obtained heat conductors 3 was measured by a waveguide method. The samples of 1 mm in thickness were measured in a frequency range from 18 GHz to 25 GHz, and evaluated at a frequency of 20 GHz. Heat conductors 3 of 25 dB or higher were accepted as exhibiting the shielding effect. Heat conductors 3 lower than 25 dB do not exhibit the shielding effect. Thus, the electromagnetic waves radiated from other electronic devices enter the current device and cause the device to malfunction.

(2) Compression set

0080The compression set was measured at 70°C after 100 hours in accordance with JIS K6262. Heat conductors 3 having a compression set within 30% were accepted. When heat conductors 3 having a compression set exceeding 30% are used as gaskets or others, the restoring force and the shielding effect are lost.

(3) Acceptability

0081Since heat conductor 3 in Example 5 marginally satisfies the criterion on the shielding effect, it was marked √. Since heat conductor 3 in Example 6 marginally satisfies the criterion on the compression set, it was marked √. Since heat conductors 3 in Examples 1 to 4 sufficiently satisfy the criteria, they were marked √+.

<Study of results>

0082Table 1 indicates that heat conductor 3 in which flake graphite fillers 1 are horizontally oriented in Comparative example 1 exhibited the higher shielding effect. However, heat conductor 3 of Comparative example 1 exhibited a poor compression set. Conversely, heat conductor 3 in which flake graphite fillers 1 are vertically oriented in Comparative example 2 exhibited a better compression set. However, heat conductor 3 of Comparative example 2 exhibited the poor shielding effect.

0083In contrast, heat conductors 3 including upper layer 31 and lower layer 32 according to Examples 1 to 6 each exhibited the higher shielding effect and a better compression set.

0084Specifically, heat conductors 3 including (i) upper layer 31 in which flake graphite fillers 1 are oriented within a range from 10 degrees to 35 degrees and (ii) lower layer 32 in which flake graphite fillers 1 are oriented within a range from 55 degrees to 80 degrees with respect to the horizontal (surface) direction according to Examples 1 to 6 satisfy both of the properties.

0085According to Table 1, as orientation angle θ in upper layer 31 is smaller, the electromagnetic shielding effect is increased. Conversely, as orientation angle θ in lower layer 32 is larger, a better compression set is obtained.

0086Thus, heat conductor 3 having a structure of two layers, that is, upper layer 31 in which flake graphite fillers 1 are oriented within the range from 10 degrees to 35 degrees and lower layer 32 in which flake graphite fillers 1 are oriented within the range from 55 degrees to 80 degrees satisfy both of the properties.

0087Lower layer 32 in which flake graphite fillers 1 are oriented within the range from 55 degrees to 80 degrees and even up to 90 degrees exhibits a compression set, because higher orientation angle θ results in a better compression set. Furthermore, orientation angle θ of flake graphite fillers 1 in upper layer 31 is suitably closer to 0 degree or 1 degree or higher. When orientation angle θ in upper layer 31 is set to 0 degree, the graphite particles are excessively aligned, and the thermal conductivity decreases.

0088Preparing heat conductors 3 each obtained by laminating the respective layers succeeded in having the two properties of the electromagnetic shielding effect and a compression set.

<Note>

0089Although the dimensions of flake graphite fillers 1 are averaged in the Specification, when the number of flake graphite fillers 1 is less and at least one of flake graphite fillers 1 satisfies the dimensions defined above, the present disclosure holds.

0090Heat conductor 3 having the two layers may have more than two layers. In other words, heat conductor 3 may be any as long as it has at least two kinds of layers.

0091Although one or more aspects of the present invention have been described and illustrated in detail, it is clearly understood that the same is by way of example only and is not to be taken by way of limitation, the scope of the present invention being limited only by the terms of the appended claims.

INDUSTRIAL APPLICABILITY

0092The electromagnetic shielding effect and having a compression set are compatible in the heat conductor according to the present disclosure. Thus, the heat conductor is suitable for sealants. The expectation based on such properties is that the heat conductor is applicable to fiber-reinforced components, heat dissipating components, phase change components, photoluminescent pattern components, gas barrier components, conductive components, insulating components, components of low linear expansion coefficients, and methods for manufacturing these components.

REFERENCE SIGNS LIST

0093<dl id="dl0001" compact="compact"><dt>1</dt><dd>Flake graphite filler</dd><dt>2</dt><dd>Matrix resin</dd><dt>3</dt><dd>Heat conductor</dd><dt>31</dt><dd>Upper layer</dd><dt>32</dt><dd>Lower layer</dd><dt>50</dt><dd>Lid</dd><dt>51</dt><dd>Main unit</dd><dt>52</dt><dd>Heat dissipator</dd><dt>B</dt><dd>Basal plane</dd><dt>S</dt><dd>Sheet surface</dd><dt>θ</dt><dd>Orientation angle</dd><dt>"a"</dt><dd>Longer length</dd><dt>"b"</dt><dd>Shorter length</dd><dt>"c"</dt><dd>Thickness</dd></dl>