Method for producing a composition for the removal of phosphates from solutions

TECHNICAL FIELD OF THE INVENTION

0001The invention relates generally to compositions and methods for removing phosphates, nitrates and heavy metals from aqueous solutions using one or more crystalline compositions comprised of multiple calcium silicate crystalline structures and amorphous structures

BACKGROUND OF THE INVENTION

0002The increasing accumulation of phosphorus, nitrogen and heavy metals discharged into the environment from agricultural, storm water run-off, wastewater treatment discharge and other sources is one of the most significant environmental challenges facing the planet. Phosphorus is also used in fertilizers, and given that phosphate mines are depleting and may be fully depleted within next 100 years, world food supplies will certainly be impacted.

0003Elevated phosphorus levels in surface waters leads to eutrophication, which is detrimental to aquatic life. To control eutrophication, the EPA recommends that total phosphates should not exceed 0.05 mg/L (as phosphorus) in a stream at a point where it enters a lake or reservoir, and total phosphorus should not exceed 0.1 mg/L in streams that do not discharge directly into lakes or reservoirs. To date, phosphorus removal has been accomplished with flocculation/precipitation methods that use metal salts such as ferric chloride, aluminum sulfate (alum) and calcium hydroxide (lime). In many cases, these methods require the use of polymers to enhance the precipitation and ultimate solids removal. Various methods have been detailed that utilize naturally occurring and synthesized forms of xonotlite and/or tobermorite to remove phosphorus. These materials are restricted by pH of the solution, as increasing pH causes bicarbonate ions to convert to carbonate ions, reducing the efficiency of removal. Another method of phosphorus removal is the chemical formation of struvite (ammonium magnesium phosphate hexahydrate). This process requires the introduction of a magnesium source, typically magnesium hydroxide, and is dependent on a high ammonia level as the ammonium source.

0004Nitrates are also of concern as increased levels in surface water and groundwater lead to undesirable levels in drinking water supplies. The current drinking water nitrate limit is 10 mg/L as nitrogen. Nitrate removal has most often been accomplished via microbiological denitrification. This process requires the availability of denitrifying bacteria in a reduced oxygen environment. The bacteria metabolize the nitrate resulting in reduction to nitrite and ultimately nitrogen gas.

0005Discharges of metal ions into water sources can render water non-potable as well as having adverse affects on aquatic life. In-stream water quality standards as well as National Drinking Water Standards for metals are very low. Metal ions have most often been removed from water and wastewater by flocculation/precipitation as metal hydroxides. This is typically accomplished by the addition of an alkali such as calcium hydroxide or sodium hydroxide. Typically a polymer is required to enhance flocculation and aid in solids removal. Metal ion removal is also accomplished by the use of cation exchange resins. This process typically requires a relatively clean water source that is free of suspended solids and oils and greases.

0006In this regard, <patcit id="pcit0001" dnum="JP2012050975A"><text>JP 2012-50975 A</text></patcit> discloses a phosphorus recovery material and the production thereof. Moreover, <patcit id="pcit0002" dnum="JP2009285636A"><text>JP 2009 285636 A</text></patcit> discloses a phosphorus material, a production method for such material, and a phosphorus recovery method.

0007Accordingly, there is a need for compositions and methods for making the same that are highly efficient at removing phosphate from aqueous solutions such as water and wastewater. It is especially preferable that the foregoing compositions are able to provide sufficient alkalinity necessary for effective phosphate removal without requiring additional pH adjustment. It is even more preferable that the foregoing compositions can be manipulated in ways to adsorb various cations and anions given that the aqueous solutions contemplated in connection with the present invention have differing contaminant profiles.

0008It is also highly preferred that the foregoing compositions are safe for use in removing contaminants from potable water sources and in food processing applications. It is also preferred that the foregoing compositions can recover phosphate in a form that can be used as a fertilizer.

BRIEF SUMMARY OF THE INVENTION

0009The present invention relates to a method for preparing a composition for removing phosphates from aqueous solutions using one or more compositions comprised of multiple calcium silicate crystalline structures and amorphous structures. Compositions in accordance with the present disclosure remove phosphates from surface waters, and in some cases can yield a high quality, slow-release fertilizer (5-35-0).

0010It is an object of the present invention to provide methods for preparing compositions for highly efficient removal of phosphate from aqueous solutions such as water and wastewater. It is also an object of the present invention to provide methods for preparing compositions that are able to provide sufficient alkalinity necessary for effective phosphate removal without requiring additional pH adjustment. It is also an object of the present invention to provide methods for preparing compositions that are safe for use in removing contaminants from potable water sources and in food processing applications. It is also an object of the present invention to provide methods for preparing compositions that can recover phosphate in a form that can be used as a fertilizer.

0011Aqueous solutions contemplated for applications of the invention include agricultural run-off, retention ponds, animal farm run-off, animal park run-off, streams, lakes, canals, reservoirs, residential and commercial storm-water run-off, wastewater treatment plant discharge, food processing discharge, industrial wastewater discharge, residential wastewater discharge, meat processing residuals, toilet water, and aquarium water.

0012Compositions in accordance with the present disclosure may be utilized in a variety of applications. In one embodiment, a composition is contacted with an aqueous solution containing phosphates and/or other contaminants in a reaction chamber that is designed to speed the rate of contact using centrifugal force. In a related embodiment, the reactor uses a Taylor vortex system operated under laminar flow conditions.

0013In another embodiment a composition is contacted with an aqueous solution containing phosphates and/or other contaminants by way of a dry feed or slurry mix into the final DAF or process stream (e.g., wastewater final treatment (municipal or food processors)). In another embodiment, a composition is contacted with an aqueous solution containing phosphates and/or other contaminants by way of an AdEdge™ Filtration System (e.g., high concentration nutrient removal).

0014In another embodiment, a composition is contacted with an aqueous solution containing phosphates and/or other contaminants by way of a portion injector (e.g., for use with a urinal or toilet).

0015In another embodiment, a composition is contacted with an aqueous solution containing phosphates and/or other contaminants by way of dry or slurry broadcast or crop dusting (e.g., on the ground or on a surface water body).

0016In another embodiment, a composition is contacted with an aqueous solution containing phosphates and/or other contaminants by way of a buried barrier (e.g., a sheet comprising the composition buried below the surface of an animal farm or park or used to capture aquarium filtrate for removing phosphates).

BRIEF SUMMARY OF THE SEVERAL VIEWS OF THE DRAWINGS

0017<ul id="ul0001" list-style="none" compact="compact"><li><figref idref="f0001">Figure 1</figref> is a phosphorus adsorption isotherm for a first composition (Composition A) in accordance with the disclosure.</li><li><figref idref="f0001">Figure 2</figref> is a phosphorus adsorption isotherm for a second composition (Composition B) in accordance with the disclosure.</li><li><figref idref="f0002">Figure 3</figref> is a phosphorus adsorption isotherm comparing Composition B to other phosphorus removal methods.</li><li><figref idref="f0002">Figure 4</figref> is a nitrate adsorption isotherm for Composition B.</li><li><figref idref="f0003">Figure 5</figref> demonstrates the affinity of Composition B for a variety of heavy metals.</li><li><figref idref="f0003">Figure 6</figref> demonstrates the efficiency of Composition B on the removal of arsenic from water as compared to other currently available media.</li><li><figref idref="f0004">Figure 7</figref> is a graph showing phosphorus removal from surface water samples obtained from a phosphorus mining operation utilizing Composition B.</li><li><figref idref="f0004">Figure 8</figref> is an EDS spectrum of Composition B.</li><li><figref idref="f0005">Figure 9</figref> shows the XRD spectrum of Composition B.</li><li><figref idref="f0006">Figure 10</figref> shows how the spatial orientation of the atoms within the calcium silicate molecules may be altered resulting in changes in bond lengths and or bond angles.</li><li><figref idref="f0007">Figure 11</figref> shows the effect of the addition of calcium ions to Composition B's efficiency in removing phosphorus from solution.</li><li><figref idref="f0007">Figure 12</figref> is a phosphorus adsorption isotherm for a third composition (Composition C) in accordance with the disclosure.</li></ul>

DETAILED DESCRIPTION OF THE INVENTION

0018The present invention relates to a method of producing a composition capable of removing phosphates according to claim 1. Preferable embodiments can be derived from the features of the dependent claims. The foregoing composition may be interchangeably referred to as a "hydrothermal residue". The method comprises the step (c) of heating the composition/hydrothermal residue at a temperature and for a time sufficient to increase the efficiency/effectiveness of the resultant composition at removing phosphates from a solution.

0019The alkali is selected from the group consisting of magnesium hydroxide, potassium hydroxide and sodium hydroxide. In some embodiments, the alkali may be in the form of a liquid alkali that comprises an alkali solute and the solvent. In some embodiments, the solvent is water. In other non-claimed embodiments the solvent is a liquid into which the calcium oxide, silicon dioxide and alkali are at least partially miscible, e.g., other polar protic solvents such as acetic acid, t-butanol, ethanol, formic acid, isopropanol, methanol and nitromethane. Mixtures of polar protic solvents are also acceptable.

0020In some embodiments, the molar ratios of the calcium oxide, silicon dioxide and liquid alkali is 2.7: 2.5: 1 respectively and the foregoing molar ratio may be varied independently by ±1%, ±2%, ±3%, ±4%, ±5%, ±6%, ±7%, ±8%, ±9% or ±10%. For example, the molar ratio of the calcium oxide : the silicon dioxide : the alkali in the slurry in one embodiment ranges from 2.43-2.97: 1.12-1.38: 0.9-1.1.

0021In particular embodiments, the slurry may additionally comprise a higher molar ratio of calcium oxide in order to achieve higher alkalinity. In some embodiments, the molar ratio of calcium oxide, silicon dioxide, and alkali is 2.7: 1.25: 1. In related embodiments the foregoing molar ratio may be varied independently by as much as by ±1%, ±2%, ±3%, ±4%, ±5%, ±6%, ±7%, ±8%, ±9% or ±10%.

0022The present invention also relates to methods of producing a composition capable of removing phosphates from a solution comprising (a) forming a slurry comprising calcium oxide, silicon dioxide, an alkali, a solvent and a metal halide salt; and (b) subjecting the slurry to a hydrothermal process under sufficient pressure and for sufficient time to form the composition. The foregoing composition may be interchangeably referred to as a "hydrothermal residue". The method comprises an additional step (c) of heating the composition/hydrothermal residue at a temperature and for a time sufficient to increase the efficiency/effectiveness of the resultant composition at removing phosphates, nitrates and/or heavy metals from a solution.

0023In related embodiments, the metal halide salt is selected from the group consisting of aluminum chloride, ferric chloride, lanthanum chloride, and magnesium chloride. In some embodiments, the molar ratio of the calcium oxide : the silicon dioxide : the alkali : metal halide salt is 54:25:20:5.5. In related embodiments, the foregoing molar ratios may be varied independently by ±1%, ±2%, ±3%, ±4%, ±5%, ±6%, ±7%, ±8%, ±9% or ±10%. For example, the molar ratio of the calcium oxide : the silicon dioxide : the alkali : the metal halide salt in one embodiment ranges from 48.6-59.4 : 22.5-27.5 : 18-22 : 4.95-6.05.

0024In some embodiments, the slurry may additionally comprise one or more amorphous compounds. In other embodiments, the calcium ion concentration and/or pH of the slurry may be increased by adding or more calcium salts and/or soluble alkaline earth salts.

0025In some embodiments, the hydrothermal process is carried out under at least about 93.08, 96.53, 99.97, 103.42, 106.87, 110.32 or 113.76 kPa (13.5, 14, 14.5, 15, 15.5, 16 or 16.5 psi) of pressure. In related embodiments, the slurry is subjected to the hydrothermal process for at least 1, 2, 3, 4, 5 or as many as 6 hours. The hydrothermal process may involve, for example, a sealed or covered reaction vessel heated at 121 °C (± 10%) such that the equivalent of the temperature generated by the foregoing range of steam pressures is achieved. In these embodiments, the reaction vessel may consist of a heated "jacketed" ball mill and or a sealed pressure pot or covered reaction vessel.

0026The "activation" step (i.e., step (c)), the composition/hydrothermal residue is heated for at least 27 minutes as low as 540 °C to as high as 660 °C. In related embodiments, the composition/hydrothermal residue is heated for at least 28, 29, 30, 31, 32 or 33 minutes up to 12 hours. The activation step may be accomplished by using, for example, a muffle furnace, electric kiln, or a gas kiln.

0027Disclosed but not claimed are compositions produced by the foregoing methods. Compositions in accordance with the present invention may also be characterized by methods of chemical analyses known in the art, for example, scanning electron microscopy (SEM) used in conjunction with energy dispersive spectrometry (EDS) or x-ray crystallography/diffraction (XRD). In one embodiment, a composition in accordance with the present invention has the EDS spectrum shown in <figref idref="f0004">Figure 8</figref>. In another embodiment, a composition in accordance with the present invention has the XRD spectrum shown in <figref idref="f0005">Figure 9</figref>.

0028The composition as shown in <figref idref="f0005">Figure 9</figref> comprises two different crystalline structures of calcium silicate (Ca₂SiO₄). XRD spectrum data for Composition B also indicated that in addition to the two separate Ca₂SiO₄ structures, the following crystal structures were also present: Ca(OH)₂, NaCl, SiO₂ and CaCO₃. The XRD spectrum data was obtained using Cu-Kα radiation.

0029Specific crystalline structure may be altered through composition variation and/or temperature and/or pressure variations. Spatial orientation of the atoms within the calcium silicate molecules may be altered resulting in changes in bond lengths and or bond angles as shown in <figref idref="f0006">Figure 10</figref>.

0030After being removed from a heat source, the resultant crystalline composition may be applied to a variety of aqueous solutions. For example, in one embodiment the crystalline composition may be contacted with an aqueous solution in a Taylor vortex system operated under laminar flow conditions when levels of nitrates, heavy metals and/or other contaminants are very low. In a system arranged in this manner, the reactor fluid dynamics are such that the unique vortex effect causes several layers of donut shaped levels of water spinning vertically through the donut hole and horizontally along the circumference of the reactor. Centrifugal force causes the crystalline composition and any other solutes to concentrate along the inner face of the reactor, increasing contact exposure and significantly reducing reaction time and improving adsorption efficiency.

0031In another embodiment, the crystalline composition can be applied to contaminated surface water. Water is pumped from a contaminated pond, lake or canal into a smaller tank or other receptacle. Algae and debris are removed or returned back to the source. The crystalline composition is then injected into the effluent flowing in a pipe and mixed using a mixing means, causing phosphates, nitrates, and heavy metals to be adsorbed onto the crystalline composition, which then are filtered by way of, e.g., a collection screen. Cleaned water is then discharged back into the source or into another body of water.

0032In another embodiment, the crystalline composition can be spread over lakes and ponds, for example by way of a barge, to adsorb and bind to nutrients to lower nutrient levels. The crystalline composition can also be mixed in soils to adsorb nutrients which will significantly reduce rainwater runoff problems. The crystalline composition may also be buried in a layer below the surface as a barrier which will prevent nutrients from entering ground water and aquifers. Multiple (i.e., staged) applications may be necessary to ensure that the pH is maintained to avoid harming marine and aquatic life.

0033In another embodiment, the crystalline composition may be used to treat wastewater by adding the composition directly into a mixed liquor or final DAF. After adsorption, the crystalline composition is flocculated out, processed and disposed of or sold as an edible by-product

0034In another embodiment, the crystalline composition may be used in an aquarium.

0035In another embodiment, the crystalline composition s may be dispensed into a toilet coincident with flushing.

0036In another embodiment, the crystalline composition may be used as an inorganic polymer flocculant. In still other embodiments, the crystalline composition comprises another inorganic or organic polymer.

Examples

0037The Examples are provided for the purpose of illustration only, and the invention is not limited to these Examples.

Example 1

0038100 mL of a 1 M solution of sodium hydroxide was added to a mixture comprising 15 g of calcium oxide and 15 g of silicon dioxide at room temperature. The resultant slurry was hydrothermally reacted in an autoclave for six hours under 103.42 kPa (15 psi) of steam pressure. The remaining solids were heated in a muffle furnace at 600 °C for thirty minutes.

0039<figref idref="f0001">Figure 1</figref> shows a phosphorus adsorption isotherm for the resultant composition ("Composition A").

Example 2

0040200 mL of a 1 M solution of sodium hydroxide was added to a mixture comprising 30 g of calcium oxide, 15 g of silicon dioxide, and 15 g of ferric chloride hexahydrate at room temperature. The resultant slurry was hydrothermally reacted in an autoclave for one to six hours under 103.42 kPa (15 psi) of steam pressure. The remaining solids were heated in a muffle furnace at 600 °C for thirty minutes.

0041<figref idref="f0001">Figure 2</figref> shows a phosphorus adsorption isotherm for the resultant composition ("Composition B").

0042<figref idref="f0002">Figure 3</figref> is a phosphorus adsorption isotherm comparing Composition B to other phosphorus removal methods.

0043<figref idref="f0002">Figure 4</figref> is a nitrate adsorption isotherm for Composition B.

0044<figref idref="f0003">Figure 5</figref> demonstrates the affinity of Composition B for a variety of heavy metals.

0045<figref idref="f0003">Figure 6</figref> demonstrates the efficiency of Composition B on the removal of arsenic from water as compared to other currently available media.

0046<figref idref="f0004">Figure 7</figref> is a graph showing phosphorus removal from surface water samples obtained from a phosphorus mining operation utilizing Composition B.

0047<figref idref="f0004">Figure 8</figref> is an EDS graph of Composition B.

0048<figref idref="f0005">Figure 9</figref> shows the XRD spectrum of Composition B.

0049<figref idref="f0007">Figure 11</figref> shows the effect of the addition of calcium ions to Composition B's efficiency in removing phosphorus from solution. ◆ shows the effect of the addition of calcium oxide. ■ shows the effect of the addition of calcium hydroxide.

Example 3

0050200 mL of a 1 M solution of sodium hydroxide was added to a mixture comprising 30 g of calcium oxide and 15 g of silicon dioxide at room temperature. The resultant slurry was hydrothermally reacted in an autoclave for 3 hours under 103.42 kPa (15 psi) of steam pressure. The remaining solids were heated in a muffle furnace at 600 °C for 12 hours.

0051<figref idref="f0007">Figure 12</figref> shows a phosphorus adsorption isotherm for the resultant composition ("Composition C").

Example 4

0052A more in-depth investigation into the properties and uses of Compositions A, B and C was conducted. Exemplary chemical and physical properties are detailed in Table 1. <tables id="tabl0001" num="0001"><table frame="all"><title>TABLE 1</title><tgroup cols="4"><colspec colnum="1" colname="col1" colwidth="76mm" /><colspec colnum="2" colname="col2" colwidth="14mm" /><colspec colnum="3" colname="col3" colwidth="14mm" /><colspec colnum="4" colname="col4" colwidth="14mm" /><thead><row><entry align="center" valign="middle">Composition</entry><entry align="center" valign="middle">A</entry><entry align="center" valign="middle">B</entry><entry align="center" valign="middle">C</entry></row></thead><tbody><row><entry align="center" valign="middle">pH 1 % solution (10g/L) S.U.</entry><entry align="center" valign="middle">12.21</entry><entry align="center" valign="middle">12.42</entry><entry align="center" valign="middle">12.60</entry></row><row><entry align="center" valign="middle">Alkalinity 1 % solution (10g/L) mg/L as CaCO₃</entry><entry align="center" valign="middle">1560</entry><entry align="center" valign="middle">1570</entry><entry align="center" valign="middle">2400</entry></row><row><entry align="center" valign="middle">Total Hardness 1 % solution (10g/L) mg/L as CaCO₃</entry><entry align="center" valign="middle">540</entry><entry align="center" valign="middle">1948</entry><entry align="center" valign="middle">2340</entry></row><row><entry align="center" valign="middle">Density g/cc</entry><entry align="center" valign="middle">0.34</entry><entry align="center" valign="middle">0.35</entry><entry align="center" valign="middle">0.38</entry></row></tbody></tgroup></table></tables>

0053EDS and XRD analysis performed on Composition B indicates that the material is composed of both crystalline and amorphous structures <i>(see</i><figref idref="f0004">Figures 8</figref> and <figref idref="f0005">9</figref>). The calcium silicate (Ca₂SiO₄) portion of the material exists as two separate crystal structures. These crystals of calcium silicate exist as two separate molecular structures. The XRD data is presented below. Relative intensity is expressed as a percentage, i.e., peak height in counts per second (cps) as a percentage of the most intense peak height. The interplanar spacing (d) and full width half maximum (FWHM) are presented as well. <tables id="tabl0002" num="0002"><table frame="all"><title>TABLE 2</title><tgroup cols="5"><colspec colnum="1" colname="col1" colwidth="28mm" /><colspec colnum="2" colname="col2" colwidth="17mm" /><colspec colnum="3" colname="col3" colwidth="31mm" /><colspec colnum="4" colname="col4" colwidth="24mm" /><colspec colnum="5" colname="col5" colwidth="31mm" /><thead><row><entry align="center"><b>Bragg angle 2Θ</b></entry><entry align="center"><b>d (Å)</b></entry><entry align="center"><b>Peak height (cps)</b></entry><entry align="center"><b>FWHM (deg)</b></entry><entry align="center" valign="top"><b>Relative intensity</b></entry></row></thead><tbody><row><entry align="center" valign="bottom">18.1063</entry><entry align="center" valign="bottom">4.89532</entry><entry align="center" valign="bottom">208.315</entry><entry align="center" valign="bottom">0.3151</entry><entry align="center" valign="bottom">28.67409</entry></row><row><entry align="center" valign="bottom">19.8817</entry><entry align="center" valign="bottom">4.46199</entry><entry align="center" valign="bottom">33.0368</entry><entry align="center" valign="bottom">0.2928</entry><entry align="center" valign="bottom">4.547442</entry></row><row><entry align="center" valign="bottom">20.8849</entry><entry align="center" valign="bottom">4.24989</entry><entry align="center" valign="bottom">73.0344</entry><entry align="center" valign="bottom">0.2043</entry><entry align="center" valign="bottom">10.05302</entry></row><row><entry align="center" valign="bottom">23.1636</entry><entry align="center" valign="bottom">3.8367</entry><entry align="center" valign="bottom">33.4842</entry><entry align="center" valign="bottom">0.4701</entry><entry align="center" valign="bottom">4.609025</entry></row><row><entry align="center" valign="bottom">26.6747</entry><entry align="center" valign="bottom">3.33912</entry><entry align="center" valign="bottom">464.332</entry><entry align="center" valign="bottom">0.1996</entry><entry align="center" valign="bottom">63.91426</entry></row><row><entry align="center" valign="bottom">27.4448</entry><entry align="center" valign="bottom">3.24714</entry><entry align="center" valign="bottom">64.8835</entry><entry align="center" valign="bottom">0.204</entry><entry align="center" valign="bottom">8.931069</entry></row><row><entry align="center" valign="bottom">28.7186</entry><entry align="center" valign="bottom">3.10595</entry><entry align="center" valign="bottom">70.1845</entry><entry align="center" valign="bottom">0.3103</entry><entry align="center" valign="bottom">9.66074</entry></row><row><entry align="center" valign="bottom">29.3996</entry><entry align="center" valign="bottom">3.03554</entry><entry align="center" valign="bottom">336.784</entry><entry align="center" valign="bottom">0.2447</entry><entry align="center" valign="bottom">46.35756</entry></row><row><entry align="center" valign="bottom">31.6566</entry><entry align="center" valign="bottom">2.82407</entry><entry align="center" valign="bottom">726.492</entry><entry align="center" valign="bottom">0.1889</entry><entry align="center" valign="bottom">100</entry></row><row><entry align="center" valign="bottom">34.2154</entry><entry align="center" valign="bottom">2.6185</entry><entry align="center" valign="bottom">267.297</entry><entry align="center" valign="bottom">0.3404</entry><entry align="center" valign="bottom">36.79283</entry></row><row><entry align="center" valign="bottom">36.037</entry><entry align="center" valign="bottom">2.49021</entry><entry align="center" valign="bottom">15.1368</entry><entry align="center" valign="bottom">0.3934</entry><entry align="center" valign="bottom">2.083547</entry></row><row><entry align="center" valign="bottom">39.4625</entry><entry align="center" valign="bottom">2.28158</entry><entry align="center" valign="bottom">109.214</entry><entry align="center" valign="bottom">0.2585</entry><entry align="center" valign="bottom">15.03306</entry></row><row><entry align="center" valign="bottom">41.2618</entry><entry align="center" valign="bottom">2.18615</entry><entry align="center" valign="bottom">59.116</entry><entry align="center" valign="bottom">0.2535</entry><entry align="center" valign="bottom">8.137185</entry></row><row><entry align="center" valign="bottom">43.3281</entry><entry align="center" valign="bottom">2.08656</entry><entry align="center" valign="bottom">16.46</entry><entry align="center" valign="bottom">0.5181</entry><entry align="center" valign="bottom">2.265682</entry></row><row><entry align="center" valign="bottom">45.4881</entry><entry align="center" valign="bottom">1.99237</entry><entry align="center" valign="bottom">408.821</entry><entry align="center" valign="bottom">0.1885</entry><entry align="center" valign="bottom">56.2733</entry></row><row><entry align="center" valign="bottom">47.2604</entry><entry align="center" valign="bottom">1.92171</entry><entry align="center" valign="bottom">107.694</entry><entry align="center" valign="bottom">0.32692</entry><entry align="center" valign="bottom">14.82384</entry></row><row><entry align="center" valign="bottom">47.4848</entry><entry align="center" valign="bottom">1.91314</entry><entry align="center" valign="bottom">85.011</entry><entry align="center" valign="bottom">0.3536</entry><entry align="center" valign="bottom">11.70157</entry></row><row><entry align="center" valign="bottom">48.6166</entry><entry align="center" valign="bottom">1.87122</entry><entry align="center" valign="bottom">39.2806</entry><entry align="center" valign="bottom">0.3704</entry><entry align="center" valign="bottom">5.406887</entry></row><row><entry align="center" valign="bottom">50.137</entry><entry align="center" valign="bottom">1.81798</entry><entry align="center" valign="bottom">65.8726</entry><entry align="center" valign="bottom">0.1421</entry><entry align="center" valign="bottom">9.067216</entry></row><row><entry align="center" valign="bottom">50.8006</entry><entry align="center" valign="bottom">1.79578</entry><entry align="center" valign="bottom">97.7427</entry><entry align="center" valign="bottom">0.3137</entry><entry align="center" valign="bottom">13.45406</entry></row><row><entry align="center" valign="bottom">54.3658</entry><entry align="center" valign="bottom">1.68613</entry><entry align="center" valign="bottom">49.5907</entry><entry align="center" valign="bottom">0.7577</entry><entry align="center" valign="bottom">6.826049</entry></row><row><entry align="center" valign="bottom">56.523</entry><entry align="center" valign="bottom">1.62679</entry><entry align="center" valign="bottom">118.673</entry><entry align="center" valign="bottom">0.2074</entry><entry align="center" valign="bottom">16.33507</entry></row><row><entry align="center" valign="bottom">59.9928</entry><entry align="center" valign="bottom">1.54073</entry><entry align="center" valign="bottom">43.6149</entry><entry align="center" valign="bottom">0.1637</entry><entry align="center" valign="bottom">6.003494</entry></row><row><entry align="center" valign="bottom">62.7463</entry><entry align="center" valign="bottom">1.47958</entry><entry align="center" valign="bottom">7.63492</entry><entry align="center" valign="bottom">0.9419</entry><entry align="center" valign="bottom">1.05093</entry></row><row><entry align="center" valign="bottom">64.2216</entry><entry align="center" valign="bottom">1.4491</entry><entry align="center" valign="bottom">20.5574</entry><entry align="center" valign="bottom">0.5663</entry><entry align="center" valign="bottom">2.82968</entry></row><row><entry align="center" valign="bottom">66.2656</entry><entry align="center" valign="bottom">1.40927</entry><entry align="center" valign="bottom">47.7325</entry><entry align="center" valign="bottom">0.2037</entry><entry align="center" valign="bottom">6.570272</entry></row><row><entry align="center" valign="bottom">68.2524</entry><entry align="center" valign="bottom">1.37301</entry><entry align="center" valign="bottom">34.818</entry><entry align="center" valign="bottom">0.348</entry><entry align="center" valign="bottom">4.79262</entry></row><row><entry align="center" valign="bottom">75.3313</entry><entry align="center" valign="bottom">1.26058</entry><entry align="center" valign="bottom">95.0097</entry><entry align="center" valign="bottom">0.2118</entry><entry align="center" valign="bottom">13.07787</entry></row><row><entry align="center" valign="bottom">81.4414</entry><entry align="center" valign="bottom">1.18074</entry><entry align="center" valign="bottom">12.4564</entry><entry align="center" valign="bottom">0.545</entry><entry align="center" valign="bottom">1.714596</entry></row><row><entry align="center" valign="bottom">84.0006</entry><entry align="center" valign="bottom">1.15116</entry><entry align="center" valign="bottom">67.5945</entry><entry align="center" valign="bottom">0.2521</entry><entry align="center" valign="bottom">9.304232</entry></row><row><entry align="center" valign="bottom">84.7205</entry><entry align="center" valign="bottom">1.14321</entry><entry align="center" valign="bottom">25.5075</entry><entry align="center" valign="bottom">0.3976</entry><entry align="center" valign="bottom">3.51105</entry></row><row><entry align="center" valign="bottom">107.4102</entry><entry align="center" valign="bottom">0.95571</entry><entry align="center" valign="bottom">6.85162</entry><entry align="center" valign="bottom">0.8705</entry><entry align="center" valign="bottom">0.94311</entry></row><row><entry align="center" valign="bottom">110.036</entry><entry align="center" valign="bottom">0.94013</entry><entry align="center" valign="bottom">30.6148</entry><entry align="center" valign="bottom">0.2791</entry><entry align="center" valign="bottom">4.214059</entry></row></tbody></tgroup></table></tables>

0054Both Composition A and Composition B were evaluated for their ability and efficiency in adsorbing ortho-phosphate ion (PO₄^-2). Adsorption isotherms were prepared with data obtained from laboratory experiments <i>(see</i><figref idref="f0001">Figures 1 and 2</figref>). Both materials exhibited excellent phosphate removal efficiency with adsorption ratios around 160-170 mg/g (i.e., mg P per g of Composition A and B). Phosphate adsorption comparisons showing Composition B versus various other typical adsorbents are detailed in <figref idref="f0002">Figure 3</figref>. Kinetic rates for the phosphate adsorption reaction are very fast - in the order of minutes for most situations. The phosphorus removal achieved on the phosphate mining operation surface water was achieved after one hour (<i>see</i><figref idref="f0004">Figure 7</figref>). This particular sample showed adsorption efficiency approaching 280 mg/g.

0055The optimal pH range for most efficient adsorption is 9.0-12.5 S.U. and, in most applications, this pH range is achieved by addition of the composition. The additional calcium provided by the calcium hydroxide Ca(OH)₂ offsets the potentially adverse effect of calcium carbonate CaCO₃ formation at higher pH.

0056It is believed that the presence of ferric chloride hexahydrate (FeCl₃·6H₂O) in the slurry of Composition B provides compositions in accordance with the present disclosure with good efficiency for nitrate (NO₃^-) adsorption. Adsorption isotherms were prepared with data obtained from laboratory experiments <i>(see</i><figref idref="f0002">Figure 4</figref>). Adsorption ratios of around 50 mg/g (i.e., mg N per g Composition B) were attained. The optimal pH for the most efficient adsorption of nitrate is around 6.0 S.U. Due to the high alkalinity of Composition B, pH adjustment over the reaction period is required.

0057Composition B demonstrates the ability to adsorb heavy metal ions. Removal efficiencies of 93 - 98% were achieved for chromium (Cr), copper (Cu), lead (Pb), manganese (Mn), and cadmium (Cd) <i>(see</i><figref idref="f0003">Figure 5</figref>). Specific removal efficiencies are set forth in Table 2. <tables id="tabl0003" num="0003"><table frame="all"><title>TABLE 3</title><tgroup cols="4"><colspec colnum="1" colname="col1" colwidth="14mm" /><colspec colnum="2" colname="col2" colwidth="41mm" /><colspec colnum="3" colname="col3" colwidth="78mm" /><colspec colnum="4" colname="col4" colwidth="23mm" /><thead><row><entry align="center" valign="top">Metal</entry><entry align="center" valign="top">Initial Concentration µg/L</entry><entry align="center" valign="top">Concentration After Application of Composition B µg/L</entry><entry align="center" valign="top">% Removal</entry></row></thead><tbody><row><entry align="center">Cr</entry><entry align="center">4000</entry><entry align="center">74</entry><entry align="center">98.15</entry></row><row><entry align="center">Cu</entry><entry align="center">4000</entry><entry align="center">80</entry><entry align="center">98.00</entry></row><row><entry align="center">Pb</entry><entry align="center">4000</entry><entry align="center">259</entry><entry align="center">93.53</entry></row><row><entry align="center">Mn</entry><entry align="center">4000</entry><entry align="center">89</entry><entry align="center">97.78</entry></row><row><entry align="center">Cd</entry><entry align="center">4000</entry><entry align="center">114</entry><entry align="center">97.15</entry></row></tbody></tgroup></table></tables>

0058Composition B was also evaluated for its ability to adsorb arsenic (As). Composition B was compared against the commonly used media GFO plus and E33. The comparisons were made using standard downflow packed column tests (<i>see</i><figref idref="f0003">Figure 6</figref>). Removal efficiencies are set forth in Table 3. The optimal pH range for most efficient adsorption is 9.0-12.5 S.U. <tables id="tabl0004" num="0004"><table frame="all"><title>TABLE 4</title><tgroup cols="4"><colspec colnum="1" colname="col1" colwidth="25mm" /><colspec colnum="2" colname="col2" colwidth="40mm" /><colspec colnum="3" colname="col3" colwidth="54mm" /><colspec colnum="4" colname="col4" colwidth="22mm" /><thead><row><entry align="center" valign="middle">Media</entry><entry align="center" valign="middle">Initial Concentration µg/L</entry><entry align="center" valign="middle">Concentration After Treatment µg/L</entry><entry align="center" valign="middle">% Removal</entry></row></thead><tbody><row><entry align="center" valign="middle">E33</entry><entry align="center" valign="middle">2000</entry><entry align="center" valign="middle">373</entry><entry align="center" valign="middle">81.35</entry></row><row><entry align="center" valign="middle">GFO+</entry><entry align="center" valign="middle">2000</entry><entry align="center" valign="middle">14.1</entry><entry align="center" valign="middle">99.30</entry></row><row><entry align="center" valign="middle">Composition B</entry><entry align="center" valign="middle">2000</entry><entry align="center" valign="middle">13.6</entry><entry align="center" valign="middle">99.32</entry></row></tbody></tgroup></table></tables>

Example 5

Adsorbed Phosphate and Nitrate Recovery for Fertilizer Use

0059Crystals that have adsorbed both phosphate and nitrate are easily removed from an aqueous solution via filtration or gravity settling. Drying these crystals may be accomplished by either oven drying or simple air drying. Based on laboratory isotherms the fertilizer value of saturated crystals derived from Composition B is 5-35-0, which represents 5% nitrogen (N), 35% phosphorus as P₂O₅, and 0% potassium (K). In some instances, the fertilizer value may increase as the treatment of surface water from a phosphate mining operation demonstrates (57% phosphorus as P₂O₅). <i>See,</i> e.g., <figref idref="f0007">Figure 11</figref>.