In-line coated biaxially orientated polypropylene based antistatic multilayer films

FIELD OF THE INVENTION

0001The present invention relates to the field of plastic fabrication and uses. More specifically, the present invention relates to in-line coated or multilayered polyolefin films that exhibit improved surface properties such as excellent antistatic, cold-seal adhesion, slipperness, wetting tension, printability and adhesion to different lamination glues.

BACKGROUND OF INVENTION (STATE OF THE ART)

0002It is known that many thermoplastic polymer packaging materials, such as films, sheets, coatings, foams, and the like, exhibiting suitable flexibility and mechanical strength have a wide range of application areas in food and non-food industry such as food packaging, agriculture, industrial wrapping applications, medicine, pharmacy, electrical and electronical material industry, and the like.

0003The several goals of these materials, especially packaging films, including biaxially oriented polyolefin films, are: (1) to have required surface properties such as antistatic, wetting tension, adequate adhesion and slipperness during their exploitation in various conditions, (2) to ensure that the films retain their optical (haze, gloss, opacity, etc.) and thermal properties (heat-sealability, etc.) (3) to ensure that the films retain their tensile and mechanical properties needed for the specified applications.

0004Currently, antistatic films are produced by adding additives in masterbatch form into the film during extrusion or by coating the film offline after production with various types of organic antistatic additives such as ethoxylated amines, polyimines, and the like, containing positive charged ions in their molecules, to prepare the conventional film-forming thermoplastic polymers, such as polyolefins, flexible poly(vinyl chloride), styrene polymers, polyesters, functional copolymers of α-olefins, and the like.

0005There are a number of available patent publications related to in-line coated thermoplastic films, antistatic polyolefin thin films, white cavitated heat-sealable or non heat-sealable biaxially oriented polypropylene films containing various types of organic and inorganic additives, such as polyethylene glycol and its stearyl ether, fatty acid monoester of polyhydric alcohol, monoglyceride of fatty acid, alcohol esters and amides or metal salts of either saturated or unsaturated monocarboxylic fatty acids, low and high molecular weight amine and imine compounds, inorganic fillers and pigments, silica and organic antiblocking agents, and the like. Fatty acid esters, ethoxylated alkylamines, diethanolamides and ethoxylated alcohol are conventional non-ionic antistatic agents predominantly used in polyolefin film compositions.

0006More specifically, thermoplastic resin film laminate with antistatic property, such as disclosed in <patcit id="pcit0001" dnum="US4605591A"><text>US Pat. 4605591</text></patcit>, relate to a polyester film and a layer of polyester resin composition provided on at least one surface of the film, said composition comprising (A) a water insoluble polyester copolymer of mixture of the aliphatic or alicyclic dicarboxylic acids and its metal sulfonate derivatives (sulphophthalic acid and its isostructural analogues) with aliphatic glycols with C_2-8 and and alicyclic glycols with C_2-8 and (B) inorganic inert particles such as calcium carbonate fine, kaolin, bentonite, zeolite and the like (the weight ratio of (A)/(B) = 100/0.5-3.0); taking transparency and slipperiness into consideration, this patent invention preferred use of natural and synthetic silicic acids. The composition also contained one or more ingredients selected from the group consisting of a water soluble silicone, a polyfunctional reactive compound, a poly(ethylene glycol) and its derivative (0.1-15 wt. %) and a antistatic agent. This film laminate preferably produced by in-line coating method.

0007Though this invention recommended the possibility of production film laminate using other non-polar thermoplastic polymers, especially polyolefins, but this method is not applicable to polyolefins (polyethylene, polypropylene and copolymers of α-olefins) that surface of films of said polymers is strong hydrophobic and formation of thin coatings from polar monomer system in their surface is not possible without preliminary surface treatments (corona, plasma, flame and chemical treatments). Polyester laminate film according to this invention is a melt extruded, unoriented or uniaxially oriented and non-mono or multilayered film and the resulting laminate is further uniaxially or biaxially oriented.

0008In <patcit id="pcit0002" dnum="EP0505861A2"><text>EP Pat. 0505861 A2</text></patcit>, there is disclosed a laminated film comprising from 3-300 µm polyester film and at least one 0.01-5.0 µm coating layer on one or both surface of said polyester film. Coating thin film contained (a) polymer having cationic nitrogen atom in main chain thereof, (b) a binder polymer selected from the group consisting of polyesters, polyacrylated, polyurethanes, chlorine-containing polymers and mixtures thereof, (c) a material selected from the group consisting of particles, lubricants and mixtures thereof, and (d) a crosslinker selected from the group consisting of melamine or epoxy crosslinking agents and their mixtures. Said coating film formed by an in-line coating method. This laminated film is mono- or biaxially oriented which is excellent in an antistatic property, adhesion and slipperness. <patcit id="pcit0003" dnum="EP0172269A2"><text>EP Pat. 0172269 A2</text></patcit> is disclosed a copolyester thermoplastic resin film laminate comprising (A) a water insoluble polyester copolymer which contained a mixtured dicarboxylic acid component with metal sulfonate group and a glycol component and (B) inert particles; the weight ratio of (A)/(B) = 100/0.5-3.0. Composition of film contained a water soluble silicone, a polyfunctional reactive compound, a poly(ethylene glycol) and its derivative and phosphoric acid derivatives as the antistatic agents. Copolyester laminate film preferably produced by in-line coating. According to <patcit id="pcit0004" dnum="EP0362568A2"><text>EP Pat. 0362568A2</text></patcit>, the antistatic polyester film is useful in various applications including magnetic recording media, graphic arts, display, packing materials, building materials and so on. Several patent publications related to improve adhesion between surface of basic polymeric film and the surface of coating by using various polymeric compositions for coating solutions. Such coatings include compositions based on poly(ethylene imine) (<patcit id="pcit0005" dnum="US5156904A"><text>US Pat. 5156904</text></patcit>), acrylic or methacrylic thermosets (<patcit id="pcit0006" dnum="US4571363A"><text>US Pat. 4571363</text></patcit>), crosslinked styrene-maleic anhydride copolymer (<patcit id="pcit0007" dnum="US4410600A"><text>US Pat. 4410600</text></patcit>), vinylidene chloride copolymer (<patcit id="pcit0008" dnum="US2698240A"><text>US Pat. 2698240</text></patcit>), water dispersible copolyesters (<patcit id="pcit0009" dnum="US5156904A"><text>US Pat. 5156904</text></patcit>) and like polymeric coatings. Among said coatings, poly(ethylene imine) is most used an coating ingredient between various ionomeric and non-ionomeric thermoplastic films such as polyester or cellophane/polyethylene (<patcit id="pcit0010" dnum="US28554A"><text>US Pat. Reissue No. 28554</text></patcit>), polypropylene/other polymers (<patcit id="pcit0011" dnum="US4139643A"><text>US Pat. 4139643</text></patcit>), and like polymer systems. Oriented polymeric films, preferably polyethylene terephthalate, coated with poly(ethylene imine) and/or polyamido-poly(ethylene imine) are disclosed in <patcit id="pcit0012" dnum="US5156904A"><text>US Pat. 5156904</text></patcit> and <patcit id="pcit0013" dnum="US5453326A"><text>US Pat. 5453326</text></patcit>, respectively, in which the poly(ethylene imine) is coated by in-line method i.e., during the film manufacturing process the polymeric film is formed before heat setting the film. In-line coated film, when used to make a laminate with other polymers such as polyethylene or ionomer type polymers, showed no signs of delamination between the basic polymeric film and the extrusion coated polymer after 2 hours in water at 121°C at 0.1 N/mm² (<patcit id="pcit0014" dnum="US5156904A"><text>US Pat. 5156904</text></patcit> and <patcit id="pcit0015" dnum="EP0458147A2"><text>EP Pat. 0458147A2</text></patcit>). Oriented polyethylene terephthalate film is in-line coated with polyamido-poly(ethylene imine) to improve the antistatic properties of film and its utilization for other packaging applications (<patcit id="pcit0016" dnum="US5453326A"><text>US Pat. 5453326</text></patcit>). In-line poly(ethylene imine) coated film used to make a laminate with other non-ionomer or ionomer type of polymers such as polyethylene or polyester, preferable polyethylene terephthalate (<patcit id="pcit0017" dnum="EP0458147A2"><text>EP Pat. 0458147A2</text></patcit>). However, above mentioned patent inventions related to preparation of laminated film only using monolayer polymer matrix film and a group of polymeric antistatic agents containing complexes of cationic nitrogen-containing polymer, preferably water-soluble poly(ethylene imine), with HCl or HBr acids. But it is well known that using inorganic acidic components in poly(ethylene imine) complexes exhibit some difficulties in processing such as corrosion of metallic parts of the machinery and environmental problems since these components evaporate during film forming process.

0009It is well known that many acrylic and methacrylic polymers [<nplcit id="ncit0001" npl-type="b"><text>Maltzer Y. L. Water-soluble polymer, Noves Data Co.: New Jersey, USA, 1981</text></nplcit>] and copolymers of maleic anhydride and its isostructural analogues (citraconic and itaconic anhydrides, amides, esters and imides) [<nplcit id="ncit0002" npl-type="b"><text>Triverdi B. C., Culberton B.M. Maleic anhydride, Plenum Press: New York, 1982</text></nplcit>; <nplcit id="ncit0003" npl-type="b"><text>Rzaev Z. M. O. Polymers and copolymers of maleic anhydride, Elm: Baku, 1984</text></nplcit>; <nplcit id="ncit0004" npl-type="s"><text>Rzaev Z. M. O. Prog. Polym. Sci., 2000;25:163</text></nplcit>; <nplcit id="ncit0005" npl-type="s"><text>Rzaev Z. M. O. et al. Eur. Polym. J. 2002;38:2143</text></nplcit>] widely used as the effective ingredient in the water-soluble or dispersed film-forming compositions which are also useful for the producing the surface coatings on various thermoplastic polymers, preferably on polar polymer systems using in-line coating processing. For example, <patcit id="pcit0018" dnum="US4410600A"><text>US Pat. 4410600</text></patcit> is disclosed a biaxially oriented aromatic polyester film coated by an in-line method with a crosslinked functional poly(styrene-co-maleic anhydride) copolymer before heat setting; the coated said copolymer film still requires corona treatment prior to extrusion coating by a converter. Number of publications relating to the use of said water-soluble functional polymer film-forming systems for coating of polyolefin film surface is significantly limited with the use of (meth)acrylic type of polymer compositions while for the anhydride-containing copolymers and their various compositions, any publication, including patent publications, almost are absenced.

0010Several Japan patent publications also related to coated thermoplastic polymers, preferably polyester type polymers, in which antistatic layer coated on at least the single surface of basic films. Used antistatic resin prepared by copolymerization of a component having a side chain polyalkylene oxide with a component having a quaternary ammonium group. Coated antistatic layer is stretched at least of uniaxially (<patcit id="pcit0019" dnum="JP2003136641A"><text>JP Pat. 2003-136641</text></patcit>). <patcit id="pcit0020" dnum="JP2002012858A"><text>JP Pat. 2002-012858</text></patcit> is disclosed a method to improve an antistatic properties of a thermoplastic film by using antistatic agent exhibiting an excellent antistatic behavior under low humidity, capable of providing an antistatic film excellent in color tone, and provide a coat-type antistatic film, as well as a method of preparing the coat-type antistatic film by an in-line coating method. Antistatic agent comprised (1) a compound including a sulfonic acid or its salt in the molecule and (2) a polymer including a cationic group. Subject of other patent (<patcit id="pcit0021" dnum="JP2001026088A"><text>JP Pat. 2001-026088</text></patcit>) is to improve adhesiveness, printability and other characteristics by providing an easy wettable coating film layer on the single surface of a polyester film and setting the wetting tension of the other surface of the polyester film to a specific value (45 mN/m or more). As a method for forming the coating film layer, an in-line coating method wherein a coating agent is applied to the polyester film before orientation/crystallization is completed and the coated film is stretched at least unidirectionally to be formed coated film preferable 0.001-1.0 µm. Patent invention (<patcit id="pcit0022" dnum="JP2004345298A"><text>JP Pat. 2004-345298</text></patcit>) is disclosed a polyester film for heat-shrinkable packaging which is excellent in solvent bonding properties and has enough solvent bonding properties even if an antistatic coating film is applied by an in-line coated method. <patcit id="pcit0023" dnum="JP5320391B"><text>JP Pat. 5320391</text></patcit> is related to the easily coated polyester improved in electrostatic property and characterized by disposing a primer layer comprising a composition containing (1) an easily adhesive polyester resin, (2) an antistatic agent having a sulfonic acid group and/or its metal salt group in the molecule and (3) an acidic compound having a least one free carboxylic group or phenolic hydroxyl group on at least one side of a polyester film, and the method for producing the film by an in-line coating method. Purpose of <patcit id="pcit0024" dnum="JP6293875B"><text>JP 6293875</text></patcit> invention is to obtain a coating agent having excellent slip properties and blocking resistance to a copolyester film and exhibiting adhesiveness to various coating materials by compounding a water soluble copolyester and acrylic resin. This invention provides a polyester film coated with the coating agent dispersed in water and manufacturing method of this film by an in-line technique. <patcit id="pcit0025" dnum="JP6099559B"><text>JP Pat. 6099559</text></patcit> disclosed a polyester film useful as a base film such as film-processed product like a magnetic recording medium, an X-ray photographic film, a telephone card, a diazo microfilm, etc., having excellent adhesive properties, blocking resistance and smoothness. This polyester based film is comprised a coating layer formed of water dispersive or soluble acrylic resin, fine inorganic particles (size of 0.2 µm). Coating layer of this film is prepared by an in-line coating method. Tsunashima et al. (Toray Ind.) (<patcit id="pcit0026" dnum="JP11198228B"><text>JP Pat. 11198228</text></patcit>) developed the in-line coating method for the water soluble coating materials or the like having good productivity and quality such as without thickness irregularities during a film making process, and also allowing to form a simultaneously biaxially oriented film with orientation speed of 10 ± 4 %/min or more in both the longitudinal direction and lateral direction. Obtained by this method oriented film includes a coating material layer having a thickness 0.005-05 µm on the film surface.

0011However, these patent inventions predominantly comprised polyester type basic polymers and adhesive polyester or acrylic resin, and films prepared are not mono or multilayered. All the methods including developed in said patents are not applicable to hydrophobic polyolefin films, especially to polypropylene mono or multilayered and biaxially oriented films. On the other hand, any patent information about polypropylene and acrylic composition based film laminates having a combination of useful properties such as excellent antistatic, antiblocking, physico-mechanical properties and other important parameters is only limited by proposal informations without detailed experimental and prototype technological results.

0012As evident from the above described patent publications, there is relatively small publications describing polyolefin based, in particular, polyolefin based in-line surface coated films. All of the patent publications suffer from one or more of the following properties, such as film compositions are not mono or multilayered, not biaxially oriented polypropylene based, not heat sealable or neither cavitated nor colored with having combination of excellent properties of antistatic behavior with antiblocking, slipping, improved wetting tension, cold seal and adhesive adhesion capability, and like, to be retained on prolonged time periods.

BRIEF DESCRIPTION OF THE DRAWINGS

0013<ul id="ul0001" list-style="none"><li><figref idref="f0001">FIG. <b>1</b></figref> is a schematic representation of the formation of self-assembled hyperbranched positive charges macrocomplexes as an effective antistatic agents.</li><li><figref idref="f0002">FIG. <b>2</b></figref> is a general scheme for the production and processing technology of the disclosed films with revised and improved in-line chemical coated unit.</li></ul>

SUMMARY OF THE INVENTION

0014It is an object of the present invention to design and prepare a multilayered structure, preferable A/B/C/D/E structure having at least a thin antistatic coated skin (A) layer, two inner (B) and (D) layers, a basic core (C) layer and an outer (E) layer for biaxially oriented polyolefin based, preferably polypropylene based films exhibiting advantageous properties such as antistatic, antiblocking, slipperness, cavitated, non-heat sealable or heat-sealable and improved wetting tension properties, as compared with known and commercial polypropylene based films with similar compositions. To improve antistatic properties of films, composition of (A) skin coated layer contains a mixture of crosslinkable copolymers maleic anhydride and its isostructural analogues and ionic antistatic agent on the base of the complexed binary systems such as linear or branched poly(ethylene imine) (PEIs)/ oligo(acrylic acid) and (meth)acrylic copolymers or PEIs/water soluble copolymers of maleic anhydride [poly(MA-co-comonomer)] with different comonomers, preferable with ethylene, propylene, N-isopropylacrylamide, N-vinyl-2-pyrrolidone and like comonomers (<figref idref="f0001">Fig. 1</figref>), polypropylene homopolymer, donor-acceptor or hydrogen bonding interaction in used combination of binary systems in composition of said layer providing significantly increase of positive charge in primary, secondary and tertiary amine groups, and therefore exhibiting excellent antistatic properties. It is known fact that the hydrolyzed anhydride containing copolymers with strong hydrogen bonding structure easily form assembled macrocomplexes with PEI through -COO-. ⁺NH- noncovalent interaction between free carboxylic groups of acidic unit and PEI amine groups (<nplcit id="ncit0006" npl-type="s"><text>Rzaev Z. M. O. et al. J Appl. Polym. Sci. 2007;102:5841</text></nplcit>) Two inner (B) and (D) layers of said mono or multilayered structure is comprised 100 % of polypropylene or the mixture of polypropylene with poly(ethylene-co-propylene) copolymer or poly (ehylene-co-propylene-co-butylene) terpolymer or polypropylene, TiO₂ white masterbatch for producing a sold white BOPP film, slip/antistatic masterbatch and CaCO₃ masterbatch for producing a white cavitated BOPP film. (C) core layer with similar composition as in (B) and (D) layers is comprised of polypropylene or slip/non-ionic antistatic masterbatch and CaCO₃ or TiO₂ white masterbatch. Outer layer (E) is comprised of polypropylene or poly(ethylene-co-propylene) <patcit id="pcit0027" dnum="US6979495B"><text>US Patent No. 6,979,495</text></patcit> discloses a biaxially oriented multi-layer film which comprises a core layer comprising: a syndiotactic propylene homopolymer; and at least one additional layer adjacent to the core layer comprising a polymer which is an ethylene or propylene homopolymer, ethylene copolymer or terpolymer containing comononers of propylene and/or butane-1. copolymer or poly(ehylene-co-propylene-co-butylene) terpolymer, silica and organic antiblocking masterbatches, and slip/non-ionic antistatic masterbatch. Outer layer (E) can be treated with corona discharge, plasma or flame methods or can be nontreated depending on final usage of the film. Compositions and layer component compositions for various types of polypropylene based film with coated surface layer of the present invention were presented below with examples and in the Tables.

0015Further multilayered films that are based on polypropylene are known from <patcit id="pcit0028" dnum="WO9907553A"><text>WO 99/07553</text></patcit> and <patcit id="pcit0029" dnum="TR200002164A2"><text>TR 2000 02164 A2</text></patcit>.

0016The present invention is an surface coated antistatic film that is a multilayered, biaxially oriented and made from polyolefin based, preferably polypropylene and poly(ethylene-co-propylene-co-butylene) terpolymers [poly(E-co-P-co-B)s] with different content of E- and B-units. Thin surface coating with thickness around 0.05-2.0 µm made (a) from a mixture of polyethylene glycol (PEG) crosslinked copolymers maleic anhydride and its isostructural analogues and ionic antistatic agent on the base of the complexed binary systems such as linear or branched poly(ethylene imine) (PEIs)/ oligo(acrylic acid) and (meth)acrylic copolymers or PEIs/water soluble copolymers of maleic anhydride (poly(MA-co-comonomer) with different comonomer, preferable with ethylene, propylene, N-isopropylacrylamide, N-vinyl-2-pyrrolidone and like comonomers and (b) from one of the conventional acrylic adhesive compositions (Rogers Int. Inc., Greenville, SC, USA) that modified with said polymer/polymer binary complexed system as an antistatic agent. The invented surface coated antistatic multilayer films are produced by a improved technology of production, processing and in-line coating. The present invention is useful for the food packaging and agricultural applications as well as for other general packaging and nonconventional special applications.

0017The following examples of the present invention for preparation of multilayered and surface coated antistatic polypropylene based films having different compositions, properties are illustrated.

EXAMPLE 1 - disclosing a product outside the scope of protection of the present invention for better understanding of the field

0018A first example of a in-line surface coated multilayer film (A/B/C/D/E) having excellent antistatic properties comprises: (A) 0.1 µm surface corona treated and in-line coated onto surface of 0.9 µm skin layer containing 90 % by weight of propylene homopolymer, 10 % by weight of mixture of acrylic matrix polymer and ionic antistatic agent on the base of the complexed binary systems such as linear or branched poly(ethylene imine)s PEIs [LPEI or (BPEI)/oligo(acrylic acid)], (B) 2.0 µm inner layer containing 100 % by weight of polypropylene, (C) 22.0 µm core layer containing 100 % by weight of polypropylene, (D) 2.0 µm inner layer containing 100 % by weight of polypropylene, (E) 1.0 µm surface corona treated outer layer containing 98,5 % by weight of polypropylene. Before biaxially stretching and in-line coated, skin layer (A) has twice corona or flame treatments in order to provide the better adhesion between polypropylene based matrix polymer surface and acrylic based in-line coated system. Outer layer (E) is also corona or flame treated for further printing and labelling purposes. The film prepared by using the flat tenter twin-screw extrusion system with excellent mixing and simultaneous or sequential stretching capacity, supplied with a chilled corona and an improved in-line coating system for the effective surface modification/hydrophilization of films, three or four satellite co-extruders, flat die, chill roll, water vaporization and recycling lines.

EXAMPLE 2 - disclosing a product outside the scope of protection of the present invention for better understanding of the field

0019A second example of a in-line surface coated multilayer film (A/B/C/D/E) having excellent antistatic properties comprises: (A) 0.1 µm surface corona treated and in-line coated onto surface of 0.9 µm skin layer containing 90 % by weight of propylene homopolymer or poly(ehylene-co-propylene-co-butylene) terpolymer, 10 % by weight of mixture of acrylic matrix polymer and ionic antistatic agent on the base of the complexed binary systems such as linear or branched poly(ethylene imine)s PEIs [LPEI or (BPEI)/oligo(acrylic acid)], (B) 3.0 µm inner layer containing 85 % by weight of polypropylene, 15 % by weight of TiO₂ white pigment, (C) 30 µm core layer containing 85 % by weight of polypropylene homopolymer, 15 % by weight of CaCO₃ cavitating masterbatch, (D) 3.0 µm inner layer containing 95 % by weight of polypropylene, 5 % by weight of TiO₂ white pigment and (E) 1.0 µm surface corona treated outer layer containing 100 % by weight of polypropylene or poly(ethylene-co-propylene-co-butylene) terpolymer. Before biaxially stretching and in-line coated, skin layer (A) has twice corona or flame treatments in order to provide the better adhesion between polypropylene based matrix polymer surface and acrylic based in-line coated system. Outer layer (E) as also corona or flame treatment for further printing and labelling proposes. The film prepared by using the flat tenter twin-screw extrusion system with excellent mixing and simultaneous or sequential stretching capacity, supplied with a chilled corona and an improved in-line coating system for the effective surface modification/hydrophilization of films, three or four satellite co-extruders, flat die, chill roll, water vaporization and recycling lines.

EXAMPLE 3

0020A third example of a in-line surface coated multilayer film comprises the same thickness structure and composition as in Example 1 with the following changes: the in-line coated skin layer (A) having 1.0 µm thickness comprises 10 % by weight of mixture of crosslinkable copolymers maleic anhydride and ionic antistatic agent on the base of the complexed binary systems such as linear or branched poly(ethylene imine) (LPEI or BPEI/oligo(acrylic acid) having average molecular weight (Mn) which is equal to or greater than 480 g/mol or 2000 g/mol, respectively.

EXAMPLE 4 - disclosing a product outside the scope of protection of the present invention for better understanding of the field

0021A fourth example of a in-line surface coated multilayer film comprises the same thickness structure and composition as in Example 1 with the following changes: the in-line coated skin layer (A) comprises 10 % by weight of mixture of PEIs/water soluble copolymers of maleic anhydride with equivalent amine/carboxylic acid unit ratio having average molecular weight (Mn) which is equal to or greater than 10000 g/mol.

EXAMPLE 5 - disclosing a product outside the scope of protection of the present invention for better understanding of the field

0022A fifth example of a in-line surface coated multilayer film comprises the same thickness structure and composition as in Example 1 with the following changes: the in-line coated skin layer (A) having 1.0 µm thickness comprises 10 % by weight of a mixture of PEIs/(meth)acrylic copolymer with equivalent amine/carboxylic acid unit ratio having average molecular weight (Mw) which is equal to or greater than 1500 g/mol.

EXAMPLE 6 - disclosing a product outside the scope of protection of the present invention for better understanding of the field

0023A sixth example of a in-line surface coated multilayer film comprises the same thickness structure and composition as in Example 1 with the following changes: (A) 0.1 µm surface corona treated and in-line coated onto surface of 0.9 µm skin layer containing 90 % by weight of propylene homopolymer, 10 % by weight of mixture of acrylic matrix polymer and ionic antistatic agent on the base of the complexed binary systems such as linear or branched poly(ethylene imine)s PEIs [LPEI or (BPEI)/oligo(acrylic acid)], the core layer (C) having 24 µm thickness comprises 85 % by weight of propylene homopolymer and 15 % by weight of TiO₂ white pigment. E) 1.0 µm surface corona treated outer layer containing 100 % by weight of polypropylene or poly(ethylene-co-propylene-co-butylene) terpolymer.

COMPARATIVE EXAMPLE

0024A comparative example of a in-line coated multilayer film (A/B/C/D/E) having excellent antistatic properties comprises: (A) 1,0 µm skin layer containing 98,5 % by weight of propylene homopolymer and 1,5 % by weight of polypropylene based antiblocking masterbatch (containing 5 % silica based inorganic additive) (B) 2.0 µm inner layer containing 100 % by weight of polypropylene, (C) 22.0 µm core layer containing 98 % by weight of polypropylene and 2 % by weight of polypropylene based antistatic masterbatch (containing 15 % ethoxylated amine additive), (D) 2.0 µm inner layer containing 100 % by weight of polypropylene, (E) 1.0 µm surface corona treated outer layer containing 97,5 % by weight of polypropylene and 2,5 % by weight of polypropylene based antiblocking masterbatch (containing 5 % silica based inorganic additive). Before biaxially stretching and in-line coated, skin layer (A) has twice corona or flame treatments in order to provide the better adhesion between polypropylene based matrix polymer surface and acrylic based in-line coated system. Outer layer (E) is also corona or flame treated for further printing and labeling purposes. The film prepared by using the flat tenter twin-screw extrusion system with excellent mixing and simultaneous or sequential stretching capacity, supplied with a chilled corona and three or four satellite co-extruders, flat die, chill roll, water vaporization and recycling lines. <tables id="tabl0001" num="0001"><table frame="all"><title>TABLE 1</title><tgroup cols="8"><colspec colnum="1" colname="col1" colwidth="44mm" /><colspec colnum="2" colname="col2" colwidth="17mm" /><colspec colnum="3" colname="col3" colwidth="17mm" /><colspec colnum="4" colname="col4" colwidth="17mm" /><colspec colnum="5" colname="col5" colwidth="17mm" /><colspec colnum="6" colname="col6" colwidth="17mm" /><colspec colnum="7" colname="col7" colwidth="17mm" /><colspec colnum="8" colname="col8" colwidth="24mm" /><thead><row><entry namest="col1" nameend="col8" align="center" valign="middle">Compositions for inline coated films</entry></row><row><entry morerows="1" align="center" valign="middle">Individual Components</entry><entry align="center" valign="middle">Ex-1</entry><entry align="center" valign="middle">Ex-2</entry><entry align="center" valign="middle">Ex-3</entry><entry align="center" valign="middle">Ex-4</entry><entry align="center" valign="middle">Ex-5</entry><entry align="center" valign="middle">Ex-6</entry><entry align="center" valign="middle">Comparative film</entry></row><row><entry align="center" valign="middle">Content (wt. %)</entry><entry align="center" valign="middle">Content (wt. %)</entry><entry align="center" valign="middle">Content (wt. %)</entry><entry align="center" valign="middle">Content (wt. %)</entry><entry align="center" valign="middle">Content (wt. %)</entry><entry align="center" valign="middle">Content (wt. %)</entry><entry align="center" valign="middle">Content (wt. %)</entry></row></thead><tbody><row><entry valign="middle">Isotactic polypropylene (homopolymer)</entry><entry align="center" valign="middle">99,635</entry><entry align="center" valign="middle">85,334</entry><entry align="center" valign="middle">99,635</entry><entry align="center" valign="middle">99,635</entry><entry align="center" valign="middle">99,635</entry><entry align="center" valign="middle">84,926</entry><entry align="center" valign="middle">99,745</entry></row><row><entry valign="middle">Poly[propylene-coethylene(1.2-5.4%)-co-1-butene(2.8-14.6%)]</entry><entry align="center" valign="middle">0,000</entry><entry align="center" valign="middle">5,000</entry><entry align="center" valign="middle">0,000</entry><entry align="center" valign="middle">0,000</entry><entry align="center" valign="middle">0,000</entry><entry align="center" valign="middle">6,333</entry><entry align="center" valign="middle">0,000</entry></row><row><entry valign="middle">Calcium carbonate -cavitating agent</entry><entry align="center" valign="middle">0,000</entry><entry align="center" valign="middle">8,289</entry><entry align="center" valign="middle">0,000</entry><entry align="center" valign="middle">0,000</entry><entry align="center" valign="middle">0,000</entry><entry align="center" valign="middle">0,000</entry><entry align="center" valign="middle">0,000</entry></row><row><entry valign="middle">Titanium dioxide -white pigment</entry><entry align="center" valign="middle">0,000</entry><entry align="center" valign="middle">1,105</entry><entry align="center" valign="middle">0,000</entry><entry align="center" valign="middle">0,000</entry><entry align="center" valign="middle">0,000</entry><entry align="center" valign="middle">8,400</entry><entry align="center" valign="middle">0,000</entry></row><row><entry valign="middle">Tetrakis methane -antioxidant</entry><entry align="center" valign="middle">0,004</entry><entry align="center" valign="middle">0,004</entry><entry align="center" valign="middle">0,004</entry><entry align="center" valign="middle">0,004</entry><entry align="center" valign="middle">0,004</entry><entry align="center" valign="middle">0,004</entry><entry align="center" valign="middle">0,004</entry></row><row><entry valign="middle">Aryl phosphide -stabilizer</entry><entry align="center" valign="middle">0,004</entry><entry align="center" valign="middle">0,004</entry><entry align="center" valign="middle">0,004</entry><entry align="center" valign="middle">0,004</entry><entry align="center" valign="middle">0,004</entry><entry align="center" valign="middle">0,004</entry><entry align="center" valign="middle">0,004</entry></row><row><entry valign="middle">Silica based Antiblocking agent</entry><entry align="center" valign="middle">0,000</entry><entry align="center" valign="middle">0,000</entry><entry align="center" valign="middle">0,000</entry><entry align="center" valign="middle">0,000</entry><entry align="center" valign="middle">0,000</entry><entry align="center" valign="middle">0,000</entry><entry align="center" valign="middle">0,007</entry></row><row><entry valign="middle">Ethoxylated amine based additive</entry><entry align="center" valign="middle">0,000</entry><entry align="center" valign="middle">0,000</entry><entry align="center" valign="middle">0,000</entry><entry align="center" valign="middle">0,000</entry><entry align="center" valign="middle">0,000</entry><entry align="center" valign="middle">0,000</entry><entry align="center" valign="middle">0,240</entry></row><row><entry valign="middle">Coating Material 1</entry><entry align="center" valign="middle">0,357</entry><entry align="center" valign="middle">0,263</entry><entry align="center" valign="middle">0,000</entry><entry align="center" valign="middle">0,000</entry><entry align="center" valign="middle">0,000</entry><entry align="center" valign="middle">0,333</entry><entry align="center" valign="middle">0,000</entry></row><row><entry valign="middle">Coating Material 2</entry><entry align="center" valign="middle">0,000</entry><entry align="center" valign="middle">0,000</entry><entry align="center" valign="middle">0,357</entry><entry align="center" valign="middle">0,000</entry><entry align="center" valign="middle">0,000</entry><entry align="center" valign="middle">0,000</entry><entry align="center" valign="middle">0,000</entry></row><row><entry valign="middle">Coating Material 3</entry><entry align="center" valign="middle">0,000</entry><entry align="center" valign="middle">0,000</entry><entry align="center" valign="middle">0,000</entry><entry align="center" valign="middle">0,357</entry><entry align="center" valign="middle">0,000</entry><entry align="center" valign="middle">0,000</entry><entry align="center" valign="middle">0,000</entry></row><row><entry valign="middle">Coating Material 4</entry><entry align="center" valign="middle">0,000</entry><entry align="center" valign="middle">0,000</entry><entry align="center" valign="middle">0,000</entry><entry align="center" valign="middle">0,000</entry><entry align="center" valign="middle">0,357</entry><entry align="center" valign="middle">0,000</entry><entry align="center" valign="middle">0,000</entry></row><row rowsep="0"><entry namest="col1" nameend="col8" align="left" valign="middle">Coating Material 1: Mixture of acrylic matrix polymer and ionic antistatic agent on the base of the complexed binary systems such as linear or branched poly(ethylene imine)s PEIs [LPEI or (BPEI)/oligo(acrylic acid)]</entry></row><row rowsep="0"><entry namest="col1" nameend="col8" align="left" valign="middle">Coating Material 2: mixture of crosslinkable copolymers maleic anhydride and ionic antistatic agent on the base of the complexed binary systems such as linear or branched poly(ethylene imine) (LPEI or BPEI/oligo(acrylic acid) having average molecular weight (<i>M</i>_n) which is equal to or greater than 480 g/mol or 2000 g/mol, respectively.</entry></row><row rowsep="0"><entry namest="col1" nameend="col8" align="left" valign="middle">Coating Material 3: mixture of PEIs/water soluble copolymers of maleic anhydride with equivalent amine/carboxylic acid unit ratio having average molecular weight (<i>M</i>_n) which is equal to or greater than 10000 g/mol.</entry></row><row><entry namest="col1" nameend="col8" align="left" valign="middle">Coating Material 4: mixture of PEIs/(meth)acrylic copolymer with equivalent amine/carboxylic acid unit ratio having average molecular weight (<i>M</i>_w) which is equal to or greater than 1500 g/mol.</entry></row></tbody></tgroup></table></tables><tables id="tabl0002" num="0002"><table frame="all"><title>TABLE 2</title><tgroup cols="8"><colspec colnum="1" colname="col1" colwidth="16mm" /><colspec colnum="2" colname="col2" colwidth="32mm" /><colspec colnum="3" colname="col3" colwidth="32mm" /><colspec colnum="4" colname="col4" colwidth="32mm" /><colspec colnum="5" colname="col5" colwidth="32mm" /><colspec colnum="6" colname="col6" colwidth="32mm" /><colspec colnum="7" colname="col7" colwidth="32mm" /><colspec colnum="8" colname="col8" colwidth="36mm" /><thead><row><entry namest="col1" nameend="col8" align="center" valign="middle">Layer component compositions for various types multilayer BOPP films</entry></row><row rowsep="0"><entry morerows="2" rowsep="1" align="center" valign="middle"><b>Layers</b></entry><entry align="center" valign="middle"><b>EXAMPLE -1</b></entry><entry align="center" valign="middle"><b>EXAMPLE-2</b></entry><entry align="center" valign="middle"><b>EXAMPLE-3</b></entry><entry align="center" valign="middle"><b>EXAMPLE-4</b></entry><entry align="center" valign="middle"><b>EXAMPLE - 5</b></entry><entry align="center" valign="middle"><b>EXAMPLE-6</b></entry><entry align="center" valign="middle"><b>COMPARATIVE FILM</b></entry></row><row><entry rowsep="0" align="center" valign="middle"><b>(28 µm)</b></entry><entry rowsep="0" align="center" valign="middle"><b>(38 µm)</b></entry><entry rowsep="0" align="center" valign="middle"><b>(28 µm)</b></entry><entry rowsep="0" align="center" valign="middle"><b>(28 µm)</b></entry><entry rowsep="0" align="center" valign="middle"><b>(28 µm)</b></entry><entry rowsep="0" align="center" valign="middle"><b>(30 µm)</b></entry><entry rowsep="0" align="center" valign="middle"><b>(28 µm)</b></entry></row><row><entry align="center" valign="middle"><b>In-line coated non-heat sealable BOPP film</b></entry><entry align="center" valign="middle"><b>In-line coated cavitated opaque BOPP film</b></entry><entry align="center" valign="middle"><b>In-line coated non-heat sealable BOPP film</b></entry><entry align="center" valign="middle"><b>In-line coated non-heat sealable BOPP film</b></entry><entry align="center" valign="middle"><b>In-line coated non-heat sealable BOPP film</b></entry><entry align="center" valign="middle"><b>White heat sealable BOPP film</b></entry><entry align="center" valign="middle"><b>Non-heat sealable BOPP film</b></entry></row></thead><tbody><row rowsep="0"><entry morerows="2" rowsep="1" valign="middle">Skin layer</entry><entry valign="middle">Homopolymer 90 %</entry><entry valign="middle">Terpolymer 90 %</entry><entry valign="middle">Homopolymer 90 %</entry><entry valign="middle">Homopolymer 90 %</entry><entry valign="middle">Homopolymer 90 %</entry><entry valign="middle">Terpolymer 90 %</entry><entry valign="middle">Homopolymer 98,5 %</entry></row><row rowsep="0"><entry valign="middle">Coating Material 1 10 %</entry><entry valign="middle">Coating Material 1 10 %</entry><entry valign="middle">Coating Material 2 10 %</entry><entry valign="middle">Coating Material 3 10 %</entry><entry valign="middle">Coating Material 4 10 %</entry><entry valign="middle">Coating Material 1 10 %</entry><entry valign="middle">Antiblocking masterbatch 1,5 %</entry></row><row><entry valign="middle">(Thickness: 1 µm)</entry><entry valign="middle">(Thickness: 1 µm)</entry><entry valign="middle">(Thickness: 1 µm)</entry><entry valign="middle">(Thickness:) 1 µm)</entry><entry valign="middle">(Thickness: 1 µm)</entry><entry valign="middle">(Thickness: 1 µm)</entry><entry valign="middle">(Thickness: 1 µm)</entry></row><row rowsep="0"><entry morerows="2" rowsep="1" valign="middle">Inner layer</entry><entry valign="middle" /><entry valign="middle">Homopolymer 85 %</entry><entry valign="middle" /><entry valign="middle" /><entry valign="middle" /><entry valign="middle" /><entry valign="middle" /></row><row rowsep="0"><entry valign="middle">Homopolymer 100 %</entry><entry valign="middle">White (TiO₂) Masterbatch15 %</entry><entry valign="middle">Homopolymer 100 %</entry><entry valign="middle">Homopolymer 100 %</entry><entry valign="middle">Homopolymer 100 %</entry><entry valign="middle">Homopolymer 100 %</entry><entry valign="middle">Homopolymer 100 %</entry></row><row><entry valign="middle">(Thickness: 2 µm)</entry><entry valign="middle">(Thickness: 3 µm)</entry><entry valign="middle">(Thickness: 2 µm)</entry><entry valign="middle">(Thickness: 2 µm)</entry><entry valign="middle">(Thickness: 2 µm)</entry><entry valign="middle">(Thickness: 2 µm)</entry><entry valign="middle">(Thickness: 2 µm)</entry></row><row rowsep="0"><entry morerows="2" rowsep="1" valign="middle">Core layer</entry><entry valign="middle">Homopolymer 100 %</entry><entry valign="middle">Homopolymer 85 %</entry><entry valign="middle">Homopolymer 100 %</entry><entry valign="middle">Homopolymer 100 %</entry><entry valign="middle">Homopolymer 100 %</entry><entry valign="middle">Homopolymer 85 %</entry><entry valign="middle">Homopolymer 98 %</entry></row><row rowsep="0"><entry valign="middle">(Thickness: 22.0 µm)</entry><entry valign="middle">Cavitation(CaCO₃) Masterbatch 15 %</entry><entry valign="middle">(Thickness: 22.0 µm)</entry><entry valign="middle">(Thickness: 22.0 µm)</entry><entry valign="middle">(Thickness : 22.0 µm)</entry><entry valign="middle">White (TiO₂) Masterbatch 15%</entry><entry valign="middle">Antistatic masterbatch 2 %</entry></row><row><entry valign="middle" /><entry valign="middle">(Thickness: 30 µm)</entry><entry valign="middle" /><entry valign="middle" /><entry valign="middle" /><entry valign="middle">(Thickness: 24.0 µm)</entry><entry valign="middle">(Thickness: 22.0 µm)</entry></row><row rowsep="0"><entry morerows="2" rowsep="1" valign="middle">Inner layer</entry><entry valign="middle" /><entry valign="middle">Homopolymer 95 %</entry><entry valign="middle" /><entry valign="middle" /><entry valign="middle" /><entry valign="middle" /><entry valign="middle" /></row><row rowsep="0"><entry valign="middle">Homopolymer 100 %</entry><entry valign="middle">White (TiO₂) Masterbatch 5 %</entry><entry valign="middle">Homopolymer 100 %</entry><entry valign="middle">Homopolymer 100 %</entry><entry valign="middle">Homopolymer 100 %</entry><entry valign="middle">Homopolymer 100 %</entry><entry valign="middle">Homopolymer 100 %</entry></row><row><entry valign="middle">(Thickness: 2 µm)</entry><entry valign="middle">(Thickness: 3 µm)</entry><entry valign="middle">(Thickness: 2 µm)</entry><entry valign="middle">(Thickness: 2 µm)</entry><entry valign="middle">(Thickness: 2 µm)</entry><entry valign="middle">(Thickness: 2 µm)</entry><entry valign="middle">(Thickness: 2 µm)</entry></row><row rowsep="0"><entry morerows="2" rowsep="1" valign="middle">Outer layer</entry><entry valign="middle">Homopolymer 100 %</entry><entry valign="middle">Terpolymer 100 %</entry><entry valign="middle">Homopolymer 100 %</entry><entry valign="middle">Homopolymer 100 %</entry><entry valign="middle">Homopolymer 100 %</entry><entry valign="middle">Terpolymer 100 %</entry><entry valign="middle">Homopolymer 97,5 %</entry></row><row rowsep="0"><entry valign="middle">(Thickness: 1 µm)</entry><entry valign="middle">(Thickness: 1 µm)</entry><entry valign="middle">(Thickness: 1 µm)</entry><entry valign="middle">(Thickness: 1 µm)</entry><entry valign="middle">(Thickness: 1 µm)</entry><entry valign="middle">(Thickness: 1 µm)</entry><entry valign="middle">Antiblocking masterbatch 2,5 % (Thickness: 1 µm)</entry></row><row><entry valign="middle">Surface treatment: Corona or Flame Treatment</entry><entry valign="middle">Surface treatment: Corona or Flame Treatment</entry><entry valign="middle">Surface treatment: Corona or Flame Treatment</entry><entry valign="middle">Surface treatment: Corona or Flame Treatment</entry><entry valign="middle">Surface treatment: Corona or Flame Treatment</entry><entry valign="middle">Surface treatment: Corona or Rame Treatment</entry><entry valign="middle">Surface treatment: Corona or Flame Treatment</entry></row></tbody></tgroup></table></tables>

0025The surface skin layer thickness of maleic based antistatic in-line coated film developed in this invention is equal to or greater than 0.8 µm thick, the thickness of coating which is inline coated is equal to or lower than 0.5 µm as in the examples 1 to 6.

0026An aspect of the present disclosure is the possibility of production of the films in the form of mono-oriented and biaxially oriented polyolefin, preferably polypropylene based mono or multilayered films having at least of one surface coated with antistatic adhesive layer by using a combination of <ol id="ol0001" ol-style=""><li>a) a flat tenter twin-screw extrusion system with excellent mixing and simultaneous or sequential stretching capacity, one main extruder with three or four satellite co-extruders, flat die, chill roll and water bath, machine direction and transverse direction orientation units, recycling line, corona and/or flame treatment units, winding unit.</li><li>b) an in-line coater system supplied with tension rollers, gravure roller, double chilled corona units and water vaporization line for the effective surface modification/hydrophilization and to significantly improve antistatic and wetting tension properties of films.</li></ol>

0027Flat tenter extrusion film line is the one which produce conventional biaxially oriented polypropylene films with an industrially acceptable properties. However, this technology does not allow to produce films having improved and long-lasting slipperness, antistatic, wetting tension, optical properties and the like. With the use of conventional migratory additive containing masterbatches mentioned properties confronts to change upon aging and exploitation periods.

0028According to present disclosure, improved version of in-line coating system developed and integrated into standard flat tenter biaxially oriented polypropylene processing and manufacturing line with realizing the following important changes in in-line coating processing; <ol id="ol0002" ol-style=""><li>1) Taking into consideration that polypropylene surfaces are hydrophobic with intrinsic lower wetting tension values (29-31 dynes/cm) compared with polyester surfaces with intrinsically higher wetting tension levels (40-42 dynes/cm) which are widely used in in-line coating technology, double chilled corona units are adopted into the in-line coating system to be sure that wetting tension level of polypropylene film surface is adequate enough to enable water based coatings to be adhered on the surface.</li><li>2) In the standard BOPP production process, the tension between MDO and TDO is precisely controlled to avoid film breaks and non-quality production. While the in-line coating unit between them leads to tension increase and unprecise tension control. So the new bearing system of the last MDO rolls changed and a new control system is supplied into the system in order to achieve the precise tension control.</li><li>3) It is well known that polypropylene structures have lower heat resistance properties compared with polyester structures. Hence, corona treatment systems in BOPP film manufacturing processes, the heat generated during electrical corona discharge unit should be compensated by cooling rollers. Since the corona power used in in-line coating system is high which is about 30-40 kW, the corona rolls adopted to in-line coating system are cooled by additional refrigeration system in order to avoid overheating of the film.</li><li>4) It is also well known that one of the most important parameter in in-line coating system is to get a homogeneous and even coating thickness distribution of the coating all along the web since coated MDO stretched film have to be TDO stretched between 1:8 to 1:10, the thickness of coatings has to be controlled in a very sensitive controlling unit. Therefore, new coating thickness controlling unit using ®-gauge or X-ray system is mounted into in-line coating system.</li><li>5) The gravure pattern for polyester and polypropylene are different for each substrate. For the film of the present invention, different cell angle, line (cell number/in2) and cell volume depending on the composition and concentration of the coating material are used in in-line coating process.</li><li>6) The drier, in this case the TDO preheating section, must have enough thermal capacity in order to dry and remove the water from coated film. To achieve the desired drying temperature of 180-190 °C (with in-line coating) instead of 160 - 170 °C (for standard production without coating), the thermal capacity of the TDO preheating section is increased.</li></ol>

0029According to the present disclosure, the developed technological aspects of producing and processing the said films are: <ol id="ol0003" ol-style=""><li>a) mono or multilayered biaxially oriented polypropylene film technology,</li><li>b) a flat tenter twin-screw extrusion system with excellent mixing and simultaneous or sequential stretching capacity, one main extruder with three or four satellite co-extruders, flat die, chill roll and water bath, machine direction and transverse direction orientation units, recycling line, corona and/or flame treatment units, winding unit</li><li>c) an in-line coater system supplied with tension rollers, gravure roller, double chilled corona units and water vaporization line for the effective surface modification/hydrophilization and to significantly improve antistatic and wetting tension properties of films.</li></ol>

0030Alternatively the (E) outer layer of biaxially oriented films prepared may be treated in a known manner such as plasma or flame or more preferably, by electrical corona discharge. General scheme for the technology of production and improved processing of films are represented in <figref idref="f0002">Fig.2</figref>.

0031Another aspect of the present invention is to use new systems of functional copolymers using as a basic polymers, i.e., water-soluble anhydride-containing copolymers and their PEI macrocomplexes in the compositions of surface coatings and polymeric antistatic agents; linear and branched PEIs have the following average characteristics: average molecular weight <i>M</i>_n = 425 g/mol, viscosity η = 200 cP at 25 °C and density <i>d</i> = 1.07 g/cm³ (for linear PEI) and <i>M</i>_n = 1800, <i>M</i>_w = 2000 g/mol and density <i>d</i> = 1.08 g/cm³ (for branched PEI). Used anhydride-containing copolymers and (meth)acrylic acid homo- and copolymers easily crosslinked by poly(ethylene glycol) (PEG) in the aqueous medium at 85-110 °C without any catalyst and at room temperature in the presence of carbamide type water-soluble catalyst (as in <nplcit id="ncit0007" npl-type="s"><text>Devrim Y., Rzaev Z. M. O. et al. Macromol. Chem. Phys. 2007;208:175</text></nplcit>). Physical state of used PEGs are changed from liquid to powder crystalline; having the different molecular weights (<i>M</i>_n = 200, 420, 950 and 8000 g/mol) are used as a crosslinker, intermolecular linkages of which also improved antistatic properties of films. Both the said crosslinkable copolymer systems and hyperbranched copolymer/PEIs macrocomplexes (<figref idref="f0001">Fig. 1</figref>) exhibit better film-forming properties and excellent antistatic activity, respectively. The conventional acrylic adhesives can also be integrated to be used in the in-line surface coating process.

0032It is further object of the present invention to widen the field of application of said coated films useful for the conventional applications including food and non-food industry such as food packaging, agriculture, industrial wrapping applications, medicine, pharmacy, electrical and electronical material industry, and the like.

0033Some important properties of films prepared according to the present invention are summarized in Table 3. <tables id="tabl0003" num="0003"><table frame="all"><title>TABLE 3</title><tgroup cols="11"><colspec colnum="1" colname="col1" colwidth="17mm" /><colspec colnum="2" colname="col2" colwidth="25mm" /><colspec colnum="3" colname="col3" colwidth="16mm" /><colspec colnum="4" colname="col4" colwidth="13mm" /><colspec colnum="5" colname="col5" colwidth="24mm" /><colspec colnum="6" colname="col6" colwidth="24mm" /><colspec colnum="7" colname="col7" colwidth="24mm" /><colspec colnum="8" colname="col8" colwidth="24mm" /><colspec colnum="9" colname="col9" colwidth="24mm" /><colspec colnum="10" colname="col10" colwidth="24mm" /><colspec colnum="11" colname="col11" colwidth="29mm" /><thead><row><entry namest="col1" nameend="col11" align="center" valign="middle">Physical and Mechanical Characteristics and surface properties of multilayer BOPP films</entry></row><row><entry align="center" valign="middle"><b>Test Method</b></entry><entry align="center" valign="middle"><b>Parameters</b></entry><entry namest="col3" nameend="col4" align="center" valign="middle"><b>UNIT</b></entry><entry align="center" valign="middle"><b>EXAMPLE-1 (28 µm) In-line coated non-heat sealable BOPP film</b></entry><entry align="center" valign="middle"><b>EXAMPLE-2 (38 µm) In-line coated cavitated opaque BOPP film</b></entry><entry align="center" valign="middle"><b>EXAMPLE-3 (28 µm) In-line coated non-heat sealable BOPP film</b></entry><entry align="center" valign="middle"><b>EXAMPLE-4 (28 µm) In-line coated non-heat sealable BOPP film</b></entry><entry align="center" valign="middle"><b>EXAMPLE-5 (28 µm) In-line coated non-heat sealable BOPP film</b></entry><entry align="center" valign="middle"><b>EXAMPLE-6 (30 µm) White heat sealable BOPP film</b></entry><entry align="center" valign="middle"><b>COMPARATIVE FILM (28 µm) Non-heat sealable BOPP film</b></entry></row></thead><tbody><row><entry align="center" valign="middle">ASTM D 374</entry><entry valign="middle">Thickness</entry><entry namest="col3" nameend="col4" align="center" valign="middle">µm</entry><entry align="center" valign="middle">28</entry><entry align="center" valign="middle">38</entry><entry align="center" valign="middle">28</entry><entry align="center" valign="middle">28</entry><entry align="center" valign="middle">28</entry><entry align="center" valign="middle">30</entry><entry align="center" valign="middle">28</entry></row><row><entry align="center" valign="middle">ASTM D 4321</entry><entry valign="middle">Yield</entry><entry namest="col3" nameend="col4" align="center" valign="middle">m²/kg</entry><entry align="center" valign="middle">39,2</entry><entry align="center" valign="middle">39,3</entry><entry align="center" valign="middle">39,2</entry><entry align="center" valign="middle">39,2</entry><entry align="center" valign="middle">39,2</entry><entry align="center" valign="middle">34</entry><entry align="center" valign="middle">39,2</entry></row><row><entry align="center" valign="middle">ASTM D 1505</entry><entry valign="middle">Density</entry><entry namest="col3" nameend="col4" align="center" valign="middle">g/cm³</entry><entry align="center" valign="middle">0,91</entry><entry align="center" valign="middle">0,67</entry><entry align="center" valign="middle">0,91</entry><entry align="center" valign="middle">0,91</entry><entry align="center" valign="middle">0,91</entry><entry align="center" valign="middle">0,98</entry><entry align="center" valign="middle">0,91</entry></row></tbody></tgroup><tgroup cols="11"><colspec colnum="1" colname="col1" colwidth="17mm" /><colspec colnum="2" colname="col2" colwidth="25mm" /><colspec colnum="3" colname="col3" colwidth="16mm" /><colspec colnum="4" colname="col4" colwidth="13mm" /><colspec colnum="5" colname="col5" colwidth="24mm" /><colspec colnum="6" colname="col6" colwidth="24mm" /><colspec colnum="7" colname="col7" colwidth="24mm" /><colspec colnum="8" colname="col8" colwidth="24mm" /><colspec colnum="9" colname="col9" colwidth="24mm" /><colspec colnum="10" colname="col10" colwidth="24mm" /><colspec colnum="11" colname="col11" colwidth="29mm" /><thead><row><entry namest="col1" nameend="col10" align="center" valign="middle">SURFACE &amp; OPTICAL PROPERTIES</entry><entry align="center" valign="middle" /></row></thead><tbody><row><entry align="center" valign="middle">ASTM D 2578</entry><entry valign="middle">Wetting Tension</entry><entry namest="col3" nameend="col4" align="center" valign="middle">dynes/cm</entry><entry align="center" valign="middle">42</entry><entry align="center" valign="middle">42</entry><entry align="center" valign="middle">42</entry><entry align="center" valign="middle">42</entry><entry align="center" valign="middle">42</entry><entry align="center" valign="middle">42</entry><entry align="center" valign="middle">38</entry></row><row><entry align="center" valign="middle">ASTM D 257</entry><entry valign="middle">Static decay time</entry><entry namest="col3" nameend="col4" align="center" valign="middle">seconds</entry><entry align="center" valign="middle">0*</entry><entry align="center" valign="middle">0*</entry><entry align="center" valign="middle">0*</entry><entry align="center" valign="middle">0*</entry><entry align="center" valign="middle">0*</entry><entry align="center" valign="middle">0*</entry><entry align="center" valign="middle">195**</entry></row><row><entry align="center" valign="middle">ASTM D 1003</entry><entry valign="middle">Haze</entry><entry namest="col3" nameend="col4" align="center" valign="middle">%</entry><entry align="center" valign="middle">0,4</entry><entry align="center" valign="middle">-</entry><entry align="center" valign="middle">0,4</entry><entry align="center" valign="middle">0,4</entry><entry align="center" valign="middle">0,4</entry><entry align="center" valign="middle">-</entry><entry align="center" valign="middle">1,6</entry></row><row><entry align="center" valign="middle">ASTM D 2457</entry><entry valign="middle">Gloss</entry><entry namest="col3" nameend="col4" align="center" valign="middle">%</entry><entry align="center" valign="middle">100</entry><entry align="center" valign="middle">90</entry><entry align="center" valign="middle">100</entry><entry align="center" valign="middle">100</entry><entry align="center" valign="middle">100</entry><entry align="center" valign="middle">55</entry><entry align="center" valign="middle">85</entry></row><row><entry align="center" valign="middle">DIN 53146</entry><entry valign="middle">Opacity</entry><entry namest="col3" nameend="col4" align="center" valign="middle">%</entry><entry align="center" valign="middle">-</entry><entry align="center" valign="middle">75</entry><entry align="center" valign="middle">-</entry><entry align="center" valign="middle">-</entry><entry align="center" valign="middle">-</entry><entry align="center" valign="middle">65</entry><entry align="center" valign="middle">-</entry></row><row><entry align="center" valign="middle">ASTM D 1746</entry><entry valign="middle">Light Transmission</entry><entry namest="col3" nameend="col4" align="center" valign="middle">%</entry><entry align="center" valign="middle">-</entry><entry align="center" valign="middle">30</entry><entry align="center" valign="middle">-</entry><entry align="center" valign="middle">-</entry><entry align="center" valign="middle">-</entry><entry align="center" valign="middle">35</entry><entry align="center" valign="middle">-</entry></row></tbody></tgroup><tgroup cols="11"><colspec colnum="1" colname="col1" colwidth="17mm" /><colspec colnum="2" colname="col2" colwidth="25mm" /><colspec colnum="3" colname="col3" colwidth="16mm" /><colspec colnum="4" colname="col4" colwidth="13mm" /><colspec colnum="5" colname="col5" colwidth="24mm" /><colspec colnum="6" colname="col6" colwidth="24mm" /><colspec colnum="7" colname="col7" colwidth="24mm" /><colspec colnum="8" colname="col8" colwidth="24mm" /><colspec colnum="9" colname="col9" colwidth="24mm" /><colspec colnum="10" colname="col10" colwidth="24mm" /><colspec colnum="11" colname="col11" colwidth="29mm" /><thead><row><entry namest="col1" nameend="col10" align="center" valign="middle">MECHANICAL &amp; THERMAL PROPERTIES</entry><entry align="center" valign="middle" /></row></thead><tbody><row><entry morerows="1" align="center" valign="middle">ASTM D 882</entry><entry morerows="1" valign="middle">Tensile Strength</entry><entry morerows="1" align="center" valign="middle">N/mm²</entry><entry align="center" valign="middle">MD</entry><entry align="center" valign="middle">165</entry><entry align="center" valign="middle">79</entry><entry align="center" valign="middle">173</entry><entry align="center" valign="middle">169</entry><entry align="center" valign="middle">172</entry><entry align="center" valign="middle">148</entry><entry align="center" valign="middle">166</entry></row><row><entry align="center" valign="middle">TD</entry><entry align="center" valign="middle">298</entry><entry align="center" valign="middle">137</entry><entry align="center" valign="middle">287</entry><entry align="center" valign="middle">293</entry><entry align="center" valign="middle">305</entry><entry align="center" valign="middle">227</entry><entry align="center" valign="middle">306</entry></row><row><entry morerows="1" align="center" valign="middle">ASTM D 882</entry><entry morerows="1" valign="middle">Elongation at Break</entry><entry morerows="1" align="center" valign="middle">%</entry><entry align="center" valign="middle">MD</entry><entry align="center" valign="middle">155</entry><entry align="center" valign="middle">98</entry><entry align="center" valign="middle">167</entry><entry align="center" valign="middle">162</entry><entry align="center" valign="middle">174</entry><entry align="center" valign="middle">166</entry><entry align="center" valign="middle">159</entry></row><row><entry align="center" valign="middle">TD</entry><entry align="center" valign="middle">58</entry><entry align="center" valign="middle">40</entry><entry align="center" valign="middle">62</entry><entry align="center" valign="middle">59</entry><entry align="center" valign="middle">55</entry><entry align="center" valign="middle">63</entry><entry align="center" valign="middle">59</entry></row><row><entry morerows="1" align="center" valign="middle">ASTM D 2732</entry><entry morerows="1" valign="middle">Thermal Shrinkage</entry><entry morerows="1" align="center" valign="middle">%</entry><entry align="center" valign="middle">MD</entry><entry align="center" valign="middle">4</entry><entry align="center" valign="middle">3</entry><entry align="center" valign="middle">4</entry><entry align="center" valign="middle">4</entry><entry align="center" valign="middle">4</entry><entry align="center" valign="middle">3</entry><entry align="center" valign="middle">4</entry></row><row><entry align="center" valign="middle">TD</entry><entry align="center" valign="middle">2</entry><entry align="center" valign="middle">1</entry><entry align="center" valign="middle">2</entry><entry align="center" valign="middle">2</entry><entry align="center" valign="middle">2</entry><entry align="center" valign="middle">2</entry><entry align="center" valign="middle">2</entry></row><row><entry align="center" valign="middle">ASTM F 88</entry><entry valign="middle">Heat seal range</entry><entry align="center" valign="middle">° C</entry><entry align="center" valign="middle">-</entry><entry align="center" valign="middle">-</entry><entry align="center" valign="middle">-</entry><entry align="center" valign="middle">-</entry><entry align="center" valign="middle">-</entry><entry align="center" valign="middle">-</entry><entry align="center" valign="middle">105-145</entry><entry align="center" valign="middle">-</entry></row><row rowsep="0"><entry namest="col1" nameend="col11" align="left" valign="middle">* 0 means electrostatic charging on coated film surface immediately discharged and no static build up on the surface. Same values are taken after production and after 10 days aging time.</entry></row><row><entry namest="col1" nameend="col11" align="left" valign="middle">** comparative film includes migratory antistatic agent and this value is taken after 10 days aging time.</entry></row></tbody></tgroup></table></tables>

0034The examples and the comparative film have tested regarding the wetting tension and adhesion quality towards water based and UV based inks since both ink systems are widely used in industry and standard BOPP films suffers to have adequate adhesion towards these ink systems. <tables id="tabl0004" num="0004"><table frame="all"><tgroup cols="5"><colspec colnum="1" colname="col1" colwidth="32mm" /><colspec colnum="2" colname="col2" colwidth="26mm" /><colspec colnum="3" colname="col3" colwidth="17mm" /><colspec colnum="4" colname="col4" colwidth="26mm" /><colspec colnum="5" colname="col5" colwidth="21mm" /><thead><row rowsep="0"><entry namest="col1" nameend="col5" align="center" valign="middle"><b>Table - 4</b></entry></row><row><entry namest="col1" nameend="col5" align="center" valign="middle"><b>Ink Adhesion Test Results (Ink adhesion: 1-5, with "5" being best adhesion)</b></entry></row><row><entry morerows="1" align="center" valign="middle"><b>Film Type</b></entry><entry namest="col2" nameend="col3" align="center" valign="middle"><b>WB FLEXO INK</b></entry><entry namest="col4" nameend="col5" align="center" valign="middle"><b>UV FLEXO INK</b></entry></row><row><entry align="center" valign="middle">Immediately</entry><entry align="center" valign="middle">24 hours</entry><entry align="center" valign="middle">Immediately</entry><entry align="center" valign="middle">24 hours</entry></row></thead><tbody><row><entry valign="middle">Example - 1, 2 and 6</entry><entry align="center" valign="middle">5</entry><entry align="center" valign="middle">5</entry><entry align="center" valign="middle">1</entry><entry align="center" valign="middle">1</entry></row><row><entry valign="middle">Example - 3</entry><entry align="center" valign="middle">4</entry><entry align="center" valign="middle">5</entry><entry align="center" valign="middle">1</entry><entry align="center" valign="middle">2</entry></row><row><entry valign="middle">Example - 4</entry><entry align="center" valign="middle">4</entry><entry align="center" valign="middle">5</entry><entry align="center" valign="middle">1</entry><entry align="center" valign="middle">1</entry></row><row><entry valign="middle">Example - 5</entry><entry align="center" valign="middle">4</entry><entry align="center" valign="middle">5</entry><entry align="center" valign="middle">1</entry><entry align="center" valign="middle">1</entry></row><row><entry valign="middle">Comparative Film</entry><entry align="center" valign="middle">2</entry><entry align="center" valign="middle">3</entry><entry align="center" valign="middle">0</entry><entry align="center" valign="middle">0</entry></row></tbody></tgroup><tgroup cols="5"><colspec colnum="1" colname="col1" colwidth="32mm" /><colspec colnum="2" colname="col2" colwidth="26mm" /><colspec colnum="3" colname="col3" colwidth="17mm" /><colspec colnum="4" colname="col4" colwidth="26mm" /><colspec colnum="5" colname="col5" colwidth="21mm" /><thead><row><entry morerows="1" align="center" valign="middle"><b>Film Type</b></entry><entry namest="col2" nameend="col3" align="center" valign="middle"><b>UV OFFSET INK</b></entry><entry namest="col4" nameend="col5" align="center" valign="middle"><b>UV LETTERPRESS INK</b></entry></row><row><entry align="center" valign="middle">Immediately</entry><entry align="center" valign="middle">24 hours</entry><entry align="center" valign="middle">Immediately</entry><entry align="center" valign="middle">24 hours</entry></row></thead><tbody><row><entry valign="middle">Example - 1, 2 and 6</entry><entry align="center" valign="middle">4</entry><entry align="center" valign="middle">4,5</entry><entry align="center" valign="middle">3</entry><entry align="center" valign="middle">3,5</entry></row><row><entry valign="middle">Example - 3</entry><entry align="center" valign="middle">3</entry><entry align="center" valign="middle">4</entry><entry align="center" valign="middle">2</entry><entry align="center" valign="middle">2,5</entry></row><row><entry valign="middle">Example - 4</entry><entry align="center" valign="middle">4</entry><entry align="center" valign="middle">4</entry><entry align="center" valign="middle">3</entry><entry align="center" valign="middle">3</entry></row><row><entry valign="middle">Example - 5</entry><entry align="center" valign="middle">3</entry><entry align="center" valign="middle">3,5</entry><entry align="center" valign="middle">2</entry><entry align="center" valign="middle">3</entry></row><row><entry valign="middle">Comparative Film</entry><entry align="center" valign="middle">1</entry><entry align="center" valign="middle">3</entry><entry align="center" valign="middle">1</entry><entry align="center" valign="middle">1,5</entry></row></tbody></tgroup></table></tables>

0035Another aspect of the present invention is to use the various combinations of the organic and inorganic additives to make possibility of producing different types of polypropylene based mono or multilayer biaxially oriented and surface coated films such as transparent non-heat sealable, transparent non-heat sealable for labels, white cavitated non-heat sealable, white cavitated heat sealable, and the like using above described improved version of production and processing technology mono or multilayered and surface coated antistatic thin films including chemical surface modification of films by in-line coated method.

0036Advantages of maleic based antistatic films disclosed in this present invention and their manufacturing and processing technology are: <ol id="ol0004" ol-style=""><li>(1) assembled structure of macrocomplexes with higher degree of positive charges in macromolecules is provided excellent antistatic properties during the long exploitation time with combination of other important properties of films such as slipperness, antiblocking, improved wetting tension, adhesion to cold seal and to different lamination adhesive types, etc.,</li><li>(2) all the disclosed functional polymer components in the surface coated compositions related to class of water-soluble bioengineering polymer systems, and therefore, production and processing technology of films is green-chemical technology,</li><li>(3) improved technology of coated processing allows to apply this method to manufacture of a wide range of polyolefin based mono or multilayer biaxially oriented films and their laminates with various polar thermoplastics and thermosets,</li><li>(4) possibility to widen the field of conventional applications. The disclosed films are also useful for the special application as a new generation of antibacterial and antifogging films due to high positively charged surface of films.</li></ol>

0037The maleic based antistatic in-line coated film developed in this invention may be antibacterial or anti- fogging or antimicrobial or degradable or biodegradable or low SIT or their combination.

0038The developed maleic based antistatic in-line coated film may be mono layer biaxially oriented polypropylene (BOPP) based film comprising: a single layer with a polypropylene or the mixture of polypropylene with poly (ethylene-co-propylene) copolymer or poly(ethylene-co-propylene-co-butylene) terpolymer and in-line surface coated thin antistatic layer.