Phosphor and light-emitting device
Abstract
A luminescent material which is featured in that it exhibits an emission peak at a wavelength ranging from 490 to 580 nm as it is excited by light having a wavelength ranging from 250 to 500 nm and that it has a composition represented by the following general formula (2): (M1-xRx)a2AlSib2Oc2Nd2 (2) (In the general formula (2), M is at least one metallic element excluding Si and Al, R is a luminescence center element, and x, a2, b2, c2 and d2 satisfy the following relationships: 0<x≤1,0.93<a2<1.3,4.0<b2<5.80.6<c2<1,6<d2<11).
Term
0.5 yearsto projected expiry
Projected expiry 9 March 2027, counted from filing; an application has no term until it is granted.
- Priority
- Filed
- Published
- Today
- Projected expiry
8 claims: 3 independent, 5 dependent
- 1A luminescent material which is featured in that it exhibits a light emission peak in a wavelength ranging from 490 to 580 nm when excited with light having a wavelength ranging from 250 to 500 nm and that it has a composition represented by the following general formula (2):(M 1-x R x ) a2 AlSi b2 O c2 N d2 (2) (In the general formula (2), M is at least one metallic element excluding Si and Al;R is a luminescence center element;and x, a2, b2, c2 and d2 satisfy following relationships: 0 < x ≤ 1 , 0.93 < a 2 < 1.3 , 4.0 < b 2 < 5.8 0.6 < c 2 < 1 , 6 < d 2 < 11 ) .
- 2A luminescent material which is featured in that it exhibits a light emission peak in a wavelength ranging from 490 to 580 nm when excited with light having a wavelength ranging from 250 to 500 nm and that it has a composition represented by the following general formula (2):(M 1-x R x ) a2 AlSi b2 O c2 N d2 (2) (In the general formula (2), M is at least one metallic element excluding Si and Al;R is a luminescence center element;and x, a2, b2, c2 and d2 satisfy following relationships: 0 < x ≤ 1 , 0.94 < a 2 < 1.1 , 4.1 < b 2 < 4.7 0.7 < c 2 < 0.85 , 7 < d 2 < 9 ) .
- 8A light-emitting device characterized by comprising:a light-emitting element which exhibits light having a wavelength ranging from 250 to 500 nm;and a luminescent material layer disposed on the light-emitting element;wherein the luminescent material layer comprises the luminescent material defined by claim 1.
Independent claims3
284 paragraphs, as filed
Technical Field
0001This invention relates to a luminescent material to be employed in a light-emitting device and to a light-emitting device.
Background Art
0002LED lamps utilizing light-emitting diodes are now employed in various kinds of display devices such as portable devices, PC peripherals, OA equipment, various kinds of switches, light sources for backlights, and display panels. A high-load LED is known to become hot when energized, thus increasing the temperature of the luminescent material to about 100 to 200°C and, due to this rise in temperature, the emission intensity of the luminescent material deteriorates. It is desirable that the luminescent material barely deteriorates even when caused to rise in temperature.
0003As the luminescent material which is capable of green emission as it is excited by blue light and which is designed to be employed in the aforementioned LED lamp, there is known an Eu-activated β-sialon luminescent material. This luminescent material is known to exhibit excellent emission efficiency as it is excited with light having a wavelength of 450 nm. Namely, when this luminescent material is excited with light having a wavelength of 450 nm, it exhibits an absorption coefficient of 65%, an internal quantum efficiency of 53% and an emission efficiency of 35%.
0004It should be noted, with regard to the development of a flat panel display device, that although much vigorous effort has been made in the development of a plasma display panel (PDP) and liquid crystal display (LCD), a field-emission-type display is expected to be more advantageous than the PDP and the LCD in that it is capable of providing a clearer image.
0005This field-emission-type display has a screen in which red, green and blue luminescent materials are arrayed and with a cathode which is disposed to face the screen at smaller intervals than those of the CRT. The cathode is provided with a plurality of electron sources as an emitter element, enabling the electron sources to emit an electron in conformity with a potential difference between the electron sources and the gate electrodes disposed near the electron sources. The electron thus emitted is accelerated by an anode voltage (accelerating voltage) of the luminescent materials side and enabled to impinge against the luminescent materials, thereby enabling the luminescent materials to emit light.
0006As the luminescent materials to be employed in the field-emission-type display constructed as described above, it is required that the luminescent materials are capable of exhibiting a sufficiently high luminous efficiency, so that even when the luminescent materials are saturated with electric charge as excited by a high current density, they are still capable of exhibiting a sufficiently high luminous efficiency. The conventional sulfide luminescent materials (ZnS:Cu, ZnS:Ag) which have been employed as a luminescent material for CRT may be a prospective candidate as meeting the aforementioned requirements. It is however reported that the sulfide luminescent materials such as ZnS are subject to decomposition under the conditions where a low energy cathode-ray display screen is excited. The decomposed matters thus generated may badly degrade a heat filament which is designed to emit electron beam. In particular, ZnS-based blue luminescent materials that have been conventionally employed are more liable to suffer from luminance deterioration as compared with red luminescent materials and green luminescent materials, thereby raising the problem that the display color of a color picture plane changes with time.
Disclosure of Invention
0007An object of the present invention is to provide a luminescent material which is excellent in temperature characteristics.
0008A luminescent material according to one aspect of the present invention is featured in that it exhibits a light emission peak in a wavelength ranging from 490 to 580 nm when excited with light having a wavelength ranging from 250 to 500 nm and that it has a composition represented by the following general formula (2): (M<sub>1-x</sub>R<sub>x</sub>)<sub>a2</sub>AlSi<sub>b2</sub>O<sub>c2</sub>N<sub>d2</sub> (2) (In the general formula (2), M is at least one metallic element excluding Si and Al; R is a luminescence center element; and x, a2, b2, c2 and d2 satisfy following relationships: <maths id="math0001"><math display="block"><mn mathvariant="normal">0</mn><mo mathvariant="normal"><</mo><mi mathvariant="normal">x</mi><mo mathvariant="normal">≤</mo><mn mathvariant="normal">1</mn><mo mathvariant="normal">,</mo><mspace width="2em" /><mn mathvariant="normal">0.93</mn><mo><</mo><mi mathvariant="normal">a</mi><mo></mo><mn mathvariant="normal">2</mn><mo mathvariant="normal"><</mo><mn mathvariant="normal">1.3</mn><mo mathvariant="normal">,</mo><mspace width="1em" /><mn mathvariant="normal">4.0</mn><mo mathvariant="normal"><</mo><mi mathvariant="normal">b</mi><mo></mo><mn mathvariant="normal">2</mn><mo mathvariant="normal"><</mo><mn mathvariant="normal">5.8</mn></math><img file="EP2003183A1_D0001.tif" /></maths><maths id="math0002"><math display="block"><mrow><mn mathvariant="normal">0.6</mn><mo mathvariant="normal"><</mo><mi mathvariant="normal">c</mi><mo></mo><mn mathvariant="normal">2</mn><mo mathvariant="normal"><</mo><mn mathvariant="normal">1</mn><mo mathvariant="normal">,</mo><mspace width="2em" /><mn mathvariant="normal">6</mn><mo mathvariant="normal"><</mo><mi mathvariant="normal">d</mi><mo></mo><mn mathvariant="normal">2</mn><mo mathvariant="normal"><</mo><mn mathvariant="normal">11</mn><mo mathvariant="normal">)</mo></mrow><mn mathvariant="normal">.</mn></math><img file="EP2003183A1_D0002.tif" /></maths>
0009A luminescent material according to another aspect of the present invention is featured in that it exhibits a light emission peak in a wavelength ranging from 490 to 580 nm when excited with light having a wavelength ranging from 250 to 500 nm and that it has a composition represented by the following general formula (2) : (M<sub>1-x</sub>R<sub>x</sub>)<sub>a2</sub>AlSi<sub>b2</sub>O<sub>c2</sub>N<sub>d2</sub> (2) (In the general formula (2), M is at least one metallic element excluding Si and A1; R is a luminescence center element; and x, a2, b2, c2 and d2 satisfy following relationships: <maths id="math0003"><math display="block"><mn mathvariant="normal">0</mn><mo mathvariant="normal"><</mo><mi mathvariant="normal">x</mi><mo mathvariant="normal">≤</mo><mn mathvariant="normal">1</mn><mo mathvariant="normal">,</mo><mspace width="2em" /><mn mathvariant="normal">0.94</mn><mo><</mo><mi mathvariant="normal">a</mi><mo></mo><mn mathvariant="normal">2</mn><mo mathvariant="normal"><</mo><mn mathvariant="normal">1.1</mn><mo mathvariant="normal">,</mo><mspace width="1em" /><mn mathvariant="normal">4.1</mn><mo mathvariant="normal"><</mo><mi mathvariant="normal">b</mi><mo></mo><mn mathvariant="normal">2</mn><mo mathvariant="normal"><</mo><mn>4.7</mn></math><img file="EP2003183A1_D0003.tif" /></maths><maths id="math0004"><math display="block"><mrow><mn mathvariant="normal">0.7</mn><mo mathvariant="normal"><</mo><mi mathvariant="normal">c</mi><mo></mo><mn mathvariant="normal">2</mn><mo mathvariant="normal"><</mo><mn mathvariant="normal">0.85</mn><mo mathvariant="normal">,</mo><mspace width="5em" /><mn mathvariant="normal">7</mn><mo mathvariant="normal"><</mo><mi mathvariant="normal">d</mi><mo></mo><mn mathvariant="normal">2</mn><mo mathvariant="normal"><</mo><mn mathvariant="normal">9</mn><mo mathvariant="normal">)</mo></mrow><mn mathvariant="normal">.</mn></math><img file="EP2003183A1_D0004.tif" /></maths>
Brief Description of Drawings
0010<ul id="ul0001" list-style="none" compact="compact"><li><figref idref="f0001">FIG. 1</figref> is an XRD profile of a luminescent material according to one embodiment;</li><li><figref idref="f0001">FIG. 2</figref> is a cross-sectional view schematically illustrating the structure of a light-emitting device according to one embodiment;</li><li><figref idref="f0002">FIG. 3</figref> are emission spectra obtained as the luminescent materials of Reference Examples 1-4 were excited by light having a wavelength of 457 nm;</li><li><figref idref="f0002">FIG. 4</figref> are emission spectra obtained as the luminescent materials of Reference Examples 5-8 were excited by light having a wavelength of 457 nm;</li><li><figref idref="f0003">FIG. 5</figref> are XRD profiles of the luminescent materials of Reference Examples 1-4, 7 and 8;</li><li><figref idref="f0003">FIG. 6</figref> are emission spectra obtained as the luminescent materials of Reference Examples 9-11 were excited by light having a wavelength of 457 nm;</li><li><figref idref="f0004">FIG. 7</figref> are emission spectra obtained as the luminescent materials of Reference Examples 12-16 were excited by light having a wavelength of 457 nm;</li><li><figref idref="f0004">FIG. 8</figref> are emission spectra obtained as the luminescent materials of Reference Examples 17-20 were excited by light having a wavelength of 457 nm;</li><li><figref idref="f0005">FIG. 9</figref> are emission spectra obtained as the luminescent materials of Reference Examples 21-23 were excited by light having a wavelength of 457 nm;</li><li><figref idref="f0005">FIG. 10</figref> are emission spectra obtained as the luminescent materials of Reference Examples 24-26 were excited by light having a wavelength of 457 nm;</li><li><figref idref="f0006">FIG. 11</figref> are emission spectra obtained as the luminescent materials of Reference Examples 27-29 were excited by light having a wavelength of 457 nm;</li><li><figref idref="f0006">FIG. 12</figref> is an emission spectrum obtained as the luminescent material of Reference Example 30 was excited by light having a wavelength of 457 nm;</li><li><figref idref="f0007">FIG. 13</figref> are emission spectra obtained as the luminescent materials of Examples 1-4 were excited by light having a wavelength of 457 nm;</li><li><figref idref="f0007">FIG. 14</figref> is an emission spectrum obtained as the luminescent material of Example 5 was excited by light having a wavelength of 461 nm;</li><li><figref idref="f0008">FIG. 15</figref> are emission spectra obtained as the luminescent materials of Examples 6 and 7 were excited by light having a wavelength of 461 nm;</li><li><figref idref="f0008">FIG. 16</figref> are emission spectra obtained as the luminescent materials of Examples 8-11 were excited by light having a wavelength of 461 nm;</li><li><figref idref="f0009">FIG. 17</figref> are emission spectra obtained as the luminescent materials of Examples 12-14;</li><li><figref idref="f0009">FIG. 18</figref> are emission spectra obtained as the luminescent materials of Reference Examples 31-34 were excited by light having a wavelength of 457 nm;</li><li><figref idref="f0010">FIG. 19</figref> are emission spectra obtained as the luminescent materials of Reference Examples 35-38 were excited by light having a wavelength of 457 nm;</li><li><figref idref="f0010">FIG. 20</figref> is an emission spectrum obtained as the luminescent material of Reference Example 39 was excited by light having a wavelength of 457 nm;</li><li><figref idref="f0011">FIG. 21</figref> are XRD profiles of the luminescent materials of Comparative Examples 3-5, Reference Example 20 and Example 2;</li><li><figref idref="f0011">FIG. 22</figref> are emission spectra obtained as the luminescent materials of Comparative Examples 3-5, Reference Example 20 and Example 2 were excited by light having a wavelength of 390 nm;</li><li><figref idref="f0012">FIG. 23</figref> is a graph illustrating the temperature characteristics, relative to emission intensity, of the luminescent materials of Reference Examples 20 and 39 and Comparative Examples 1 and 2 as they were excited by light having a wavelength of 461 nm; and</li><li><figref idref="f0012">FIG. 24</figref> is a graph illustrating the temperature characteristics, relative to emission intensity, of the luminescent materials of Examples 1 and Comparative Example 6 as they were excited by light having a wavelength of 461 nm.</li></ul>
Best Mode for Carrying Out the Invention
0011Next, various embodiments of the present invention will be explained.
0012It has been found out by the present inventors that it is possible to obtain a luminescent material which is excellent in temperature characteristics through the addition of a luminescence center element to a sialon-based compound having a specific composition. This sialon-based compound in this specification can be represented by the following composition formula (A). MAlSiON (A)
0013In this composition formula (A), M is at least one metallic element excluding Si and Al. More specifically, the metallic element may be selected from alkaline earth metals such as Mg, Ca, Sr, Ba, etc.; rare earth elements such as Y, Gd, La, Lu, Sc, etc.; and alkaline metals such as Li, Na, K, etc. Further, B, Ga, In, Ge, etc., may be included in the aforementioned composition as the metallic element M.
0014In the creation of the luminescent material according to this embodiment, at least part of the metallic element M in the sialon-based compound is replaced by a luminescence center element and the constituent elements of the composition are respectively regulated to a predetermined range. The luminescent material according to this embodiment can be considered as represented by the following composition formula (B) wherein the constituent elements thereof are respectively regulated to a predetermined range. (M<sub>1-x</sub>R<sub>x</sub>)<sub>a</sub>AlSi<sub>b</sub>O<sub>c</sub>N<sub>d</sub> (B)
0015As the luminescence center element R, it can be selected, for example, from Eu, Ce, Mn, Tb, Yb, Dy, Sm, Tm, Pr, Nd, Pm, Ho, Er, Gd, Cr, Sn, Cu, Zn, Ga, Ge, As, Ag, Cd, In, Sb, Au, Hg, Tl, Pb, Bi and Fe. In view of the variability of emission wavelength, etc., it is more preferable to employ at least one selected from Eu and Mn.
0016It is desirable that the luminescence center element R is substituted for at least 0.1 mole % of the metallic element M. If the amount of substitution is less than 0.1 mole %, it may become difficult to obtain sufficient light-emitting effects. Although the luminescence center element R may be employed to substitute all of the metallic element M, as long as the amount of substitution is limited to less than 50 mole %, it is possible to suppress most effectively the deterioration (concentration quenching) of emission efficiency.
0017A luminescent material according to one embodiment is featured in that it exhibits an emission peak at a wavelength ranging from 490 to 580 nm as it is excited by light having a wavelength ranging from 250 to 500 nm and that it has a composition represented by the following general formula (2): (M<sub>1-x</sub>R<sub>x</sub>)<sub>a2</sub>AlSi<sub>b2</sub>O<sub>c2</sub>N<sub>d2</sub> (2)
0018(In the general formula (2), M is at least one metallic element excluding Si and Al; R is a luminescence center element; and x, a2, b2, c2 and d2 satisfy following relationships): <maths id="math0005"><math display="block"><mn mathvariant="normal">0</mn><mo mathvariant="normal"><</mo><mi mathvariant="normal">x</mi><mo mathvariant="normal">≤</mo><mn mathvariant="normal">1</mn><mo mathvariant="normal">,</mo><mspace width="2em" /><mn mathvariant="normal">0.93</mn><mo><</mo><mi mathvariant="normal">a</mi><mo></mo><mn mathvariant="normal">2</mn><mo mathvariant="normal"><</mo><mn mathvariant="normal">1.3</mn><mo mathvariant="normal">,</mo><mspace width="1em" /><mn mathvariant="normal">4.0</mn><mo mathvariant="normal"><</mo><mi mathvariant="normal">b</mi><mo></mo><mn mathvariant="normal">2</mn><mo mathvariant="normal"><</mo><mn mathvariant="normal">5.8</mn></math><img file="EP2003183A1_D0005.tif" /></maths><maths id="math0006"><math display="block"><mrow><mn>0.6</mn><mo><</mo><mi mathvariant="normal">c</mi><mo></mo><mn mathvariant="normal">2</mn><mo mathvariant="normal"><</mo><mn mathvariant="normal">1</mn><mo mathvariant="normal">,</mo><mspace width="5em" /><mn mathvariant="normal">6</mn><mo mathvariant="normal"><</mo><mi mathvariant="normal">d</mi><mo></mo><mn mathvariant="normal">2</mn><mo mathvariant="normal"><</mo><mn mathvariant="normal">11</mn><mo mathvariant="normal">)</mo></mrow><mn mathvariant="normal">.</mn></math><img file="EP2003183A1_D0006.tif" /></maths>
0019The luminescent material having the composition represented by the aforementioned general formula (2) may be classified as emitting a light zone ranging in color from green to yellowish green when excited with light having a wavelength ranging from 250 to 500 nm.
0020When an alkaline earth metal element is included, as the metallic element M, in the aforementioned general formula (2), the luminescent material to be obtained is enabled to exhibit an X-ray diffraction profile as schematically shown in <figref idref="f0001">FIG. 1</figref> for example in the X-ray diffraction where CuKα characteristic X-rays (wavelength: 1.54056Å) is employed. As shown in <figref idref="f0001">FIG. 1</figref>, the luminescent material having the composition represented by the aforementioned general formula (2) contains one component concurrently indicating diffraction peaks at diffraction angles (2θ) of 11.81-11.85, 15.34-15.38, 20.40-20.47 and 23.74-23.86°.
0021Since this luminescent material is formulated to have a composition wherein the contents of constituent elements thereof are respectively confined to a specific range, this luminescent material is enabled to exhibit excellent temperature characteristics.
0022The luminescent material according to this embodiment can be synthesized using, as starting materials, the carbonates, nitrides or oxides of the metallic element M; carbides of cyanamide; the nitrides, oxides or carbide of Al or Si; and the oxides, nitrides or carbonates of the luminescence center element R. More specifically, if it is desired to obtain a luminescent material containing Eu as a luminescence center element R, SrCO<sub>3</sub>, AlN, Si<sub>3</sub>N<sub>4</sub> and Eu<sub>2</sub>O<sub>3</sub> can be employed as starting materials. More specifically, these starting materials are weighed and mixed together so as to obtain a mixed powder having a desired composition, which is then sintered to obtain the aimed luminescent material. In the step of mixing these starting materials, it is possible to employ a ball mill in which these starting materials are mixed together with, for example, dehydrated isopropanol (IPA) for 2 to 72 hours. It is also possible to employ, other than the aforementioned IPA, other organic solvent such as ethanol or an aqueous solution. The mixing of these starting materials may be performed by either dry mixing in a mortar or wet mixing methods.
0023The IPA is then volatilized and removed by room temperature drying or heat-drying using a mantle heater. Thereafter, the resultant mixture is allowed to dry overnight in air atmosphere at a temperature ranging from 0 to 40°C and then ground in a mortar and charged in a carbon crucible. The drying of the mixture may be performed using a hot plate as desired. Further, as the material of the crucible, it may be boron nitride, silicon nitride, silicon carbide, aluminum nitride, sialon, aluminum oxide, molybdenum or tungsten.
0024The mixture in the crucible is then subjected to sintering for a predetermined period of time to obtain a luminescent material having a predetermined composition. The pressure in the sintering step should preferably be higher than atmospheric pressure. In order to suppress the decomposition of silicon nitride at high temperatures, the pressure in this sintering step should preferably be 5 atm or more. As for the sintering temperature, it should preferably be confined within the range of 1500 to 2000°C, more preferably the range of 1800 to 2000°C. If the sintering temperature is lower than 1500°C, it may become difficult to create the sialon. On the other hand, if the sintering temperature is higher than 2000°C, the materials or products may sublime. Further, since AlN employed as a raw material is vulnerable to oxidation, the sintering should preferably be performed in a nitrogen atmosphere. Alternatively, the sintering may be performed in a mixed gas atmosphere consisting of nitrogen and hydrogen.
0025The powder that has been sintered is optionally subjected to post treatments such as washing to obtain a luminescent material according to one embodiment. The washing can be performed by washing with pure water or by acid washing for example. It should be noted that, as for the conventional nitride luminescent material, there is also known CaAlSiN<sub>3</sub>:Eu, which can be synthesized using Ca<sub>3</sub>N<sub>2</sub>, etc., as raw materials. Since this raw material is anaerobic, the weighing and mixing of raw materials on the occasion of the synthesis of luminescent material are required to be performed in an environment which is sealed off from air atmosphere, e.g., in a glove box. Whereas, in the case of synthesizing a luminescent material according to this embodiment however, the weighing and mixing of raw materials can be performed in air atmosphere. The reason for this can be ascribed to the fact that the reactivity in air atmosphere of the raw materials of luminescent material according to this embodiment is lower than that of the aforementioned Ca<sub>3</sub>N<sub>2</sub>. Therefore, the luminescent material according to this embodiment can be manufactured in a very simple process, thereby making it possible to remarkably reduce the manufacturing cost.
0026The luminescent material according to this embodiment can be applied to the manufacture of a white LED. More specifically, it is possible to obtain white light by suitably combining plural kinds of luminescent materials. For example, plural kinds of luminescent materials respectively emitting red, yellow (or green) or blue light as they are irradiated with ultraviolet rays can be combined to obtain white light. Alternatively, it is also possible to combine plural kinds of luminescent materials respectively emitting yellow or red light (a luminescent material which is capable of emitting red light may be omitted if required) as they are irradiated with blue light.
0027In the light-emitting device shown in <figref idref="f0001">FIG. 2</figref>, a resin stem 200 comprises a lead 201 and a lead 202 both forming a lead frame, and a resin part 203 which is formed integral with these leads 201 and 202. This resin part 203 is provided with a recess 205 having an upper opening which is made larger in width than that of the bottom thereof and with a reflection surface 204 on the sidewall of recess 205.
0028A light-emitting chip 206 is mounted at a central portion of nearly circular bottom of the recess 205 by silver paste, etc. As for the light-emitting chip 206, it is possible to employ, for example, a light-emitting diode, a laser diode, etc. Alternatively, it is also possible to employ those which are capable of emitting ultraviolet rays. Namely, there is not any particular limitation with respect to the kinds of the light-emitting chip 206. Thus, it is possible to employ, other than the ultraviolet-ray-emitting chip, a chip which is capable of emitting blue, bluish purple, or near-ultraviolet light. For example, it is possible to employ a semiconductor light-emitting element such as GaN, etc. The electrodes (not shown) of the light-emitting chip 206 are electrically connected, through bonding wires 207 and 208 made of gold, etc., with the lead 201 and the lead 202, respectively. It should be noted that the arrangement of these leads 201 and 202 can be optionally modified.
0029A luminous layer 209 is placed in the recess 205 of resin part 203. This luminous layer 209 can be formed by dispersing or sedimenting a luminescent material 210 according to one embodiment in a resin layer 211 made of silicone resin for example at a concentration ranging from 5 to 50% by weight. In the luminescent material according to this embodiment, a nitride which is high in covalent boding property is employed as a matrix. Because of this, the luminescent material is rendered hydrophobic and hence very excellent in affinity with the resin. Therefore, it is possible to effectively suppress the scattering of light at the interface of resin and luminescent material, and the light extraction efficiency is improved.
0030As the light-emitting chip 206, it is possible to employ a flip-chip where an n-type electrode and a p-type electrode are positioned on the same plane. In this case, it is possible to overcome the problems originating from wire such as the cut-off or peeling of wire and the absorption of light by the wire, thus making it possible to obtain a semiconductor light-emitting device which is high in reliability and also high in luminance. Further, it is also possible to employ an n-type substrate for the light-emitting chip 206 to fabricate the following structure. More specifically, an n-type electrode is formed on the rear face of an n-type substrate, a p-type electrode is formed on the upper face of a semiconductor layer formed on the substrate, and the n-type electrode or the p-type electrode is mounted on one of leads. The rest of the p-type electrode and the n-type electrode are electrically connected through a wire with the other lead. The size of the light-emitting chip 206, the dimension and configuration of the recess 205 may be optionally modified.
0031It should be noted that the kinds of light-emitting device to which the luminescent material of this embodiment is applicable can be optionally changed. More specifically, even to a bombshell-type LED and a surface-mounted type LED, the luminescent material of this embodiment can be applied while securing the same effects as described above.
0032Next, the present invention will be explained in detail with reference to examples and comparative examples. These examples however are not intended to limit the present invention.
(Reference Example 1)
0033SrCO<sub>3</sub>, AlN, Si<sub>3</sub>N<sub>4</sub> and Eu<sub>2</sub>O<sub>3</sub> were prepared as starting materials, and these starting materials were weighed to obtain 25.687, 8.198, 46.770 and 4.575g, respectively. Then, these starting materials were mixed together with dehydrated isopropanol (IPA) for 24 hours in a ball mill. After IPA was volatilized and removed by drying at room temperature, the mixture was allowed to dry overnight in air atmosphere and at a temperature of 120°C. The resultant mixture was ground in a mortar and then charged in a carbon crucible. The mixture in the crucible was then subjected to sintering in a nitrogen atmosphere of 7.5 atm. for eight hours at a temperature of 1900°C to synthesize a luminescent material of this reference example.
0034This luminescent material thus sintered was formed of a mixture of two kinds of sintered powder differing in body colors, and a white sintered powder and a red sintered powder were confirmed. When this luminescent material was excited by black light, a blue emission from the white powder and a red emission from the red powder were observed.
(Reference Example 2)
0035A luminescent material was synthesized in this reference example by following the same procedures as described in Reference Example 1 except that the loading of SrCO<sub>3</sub> was changed to 25.097g and the loading of Eu<sub>2</sub>O<sub>3</sub> was changed to 5.279g.
0036This luminescent material thus sintered was formed of a mixture of two kinds of sintered powder differing in body color, thus confirming existence of a white sintered powder and a red sintered powder. When this luminescent material was excited by black light, a blue emission from the white powder and a red emission from the red powder were observed.
(Reference Example 3)
0037A luminescent material was synthesized in this reference example by following the same procedures as described in Reference Example 1 except that the loading of SrCO<sub>3</sub> was changed to 24.506g and the loading of Eu<sub>2</sub>O<sub>3</sub> was changed to 5.983g.
0038This luminescent material thus sintered was formed of a mixture of two kinds of sintered powder differing in body color, thus confirming existence of a white sintered powder and a red sintered powder. When this luminescent material was excited by black light, a blue emission from the white powder and a red emission from the red powder were observed.
(Reference Example 4)
0039A luminescent material was synthesized in this reference example by following the same procedures as described in Reference Example 1 except that the loading of SrCO<sub>3</sub> was changed to 7.012g and the loading of Eu<sub>2</sub>O<sub>3</sub> was changed to 0.440g.
0040This luminescent material thus sintered was formed of a mixture of two kinds of sintered powder differing in body color, thus confirming existence of a white sintered powder and a red sintered powder. When this luminescent material was excited by black light, a blue emission from the white powder and a red emission from the red powder were observed.
0041The red powder of Reference Example 1 was taken out of the crucible and ground in a mortar. This red powder was excited by an emission diode exhibiting a peak wavelength of 457 nm to observe the emission spectrum of the red powder. The red powders of Reference Examples 2 to 4 were also respectively taken out and ground in the same manner as the red powder of Reference Example 1 and excited using light having a peak wavelength of 457 nm to observe the emission spectrum of each of the red powders of Reference Examples 2 to 4.
0042The results thus obtained are shown in <figref idref="f0002">FIG. 3</figref>. In <figref idref="f0002">FIG. 3</figref>, the bands each exhibiting a peak at 457 nm were derived from the reflection of exciting beam. From every red powders, a single-band emission exhibiting a peak at a wavelength ranging from 620 to 640 nm was obtained. By the expression "single-band", it is intended to indicate an emission which appears as if the peak wavelength where the emission intensity becomes maximal is only one.
(Reference Example 5)
0043A luminescent material was synthesized in this reference example under the same conditions as described in Reference Example 1 except that the sintering temperature was changed to 1950°C.
0044This luminescent material thus sintered was formed of a mixture of two kinds of sintered powder differing in body color, thus confirming existence of a white sintered powder and a red sintered powder. When this luminescent material was excited by black light, a blue emission from the white powder and a red emission from the red powder were observed.
(Reference Example 6)
0045A luminescent material was synthesized in this reference example under the same conditions as described in Reference Example 2 except that the sintering temperature was changed to 1950°C.
0046This luminescent material thus sintered was formed of a mixture of two kinds of sintered powder differing in body color, thus confirming existence of a white sintered powder and a red sintered powder. When this luminescent material was excited by black light, a blue emission from the white powder and a red emission from the red powder were observed.
(Reference Example 7)
0047A luminescent material was synthesized in this reference example under the same conditions as described in Reference Example 3 except that the sintering temperature was changed to 1950°C.
0048This luminescent material thus sintered was formed of a mixture of two kinds of sintered powder differing in body color, thus confirming existence of a white sintered powder and a red sintered powder. When this luminescent material was excited by black light, a blue emission from the white powder and a red emission from the red powder were observed.
(Reference Example 8)
0049A luminescent material was synthesized in this reference example under the same conditions as described in Reference Example 4 except that the sintering temperature was changed to 1950°C.
0050This luminescent material thus sintered was formed of a mixture of two kinds of sintered powder differing in body color, thus confirming existence of a white sintered powder and a red sintered powder. When this luminescent material was excited by black light, a blue emission from the white powder and a red emission from the red powder were observed.
0051The red powders of Reference Examples 5 to 8 were respectively taken out of the crucible and ground in a mortar in the same manner as described above. Then, the red powders were respectively excited by an emission diode exhibiting a peak wavelength of 457 nm. The emission spectrums thus obtained are shown in <figref idref="f0002">FIG. 4</figref>. In <figref idref="f0002">FIG. 4</figref>, the bands each exhibiting a peak at 457 nm were derived from the reflection of exciting beam. From every red powders, a single-band emission exhibiting a peak at a wavelength ranging from 620 to 640 nm was obtained.
0052The red powders of Reference Examples 1-4, 7 and 8 were subjected to X-ray diffraction measurement employing CuKα characteristic X-rays (wavelength: 1.54056Å). The profiles thus obtained are shown in <figref idref="f0003">FIG. 5</figref>. As shown in <figref idref="f0003">FIG. 5</figref>, since the profiles shown therein contained a large number of peaks, these red powders were assumed as having a relatively complicated structure.
0053It will be recognized that every red powders concurrently indicate diffraction peaks at diffraction angles (2θ) of 8.60-8.64, 11.16-11.20 and 18.26-18.30°. It was suggested that the peaks on the lower angle side were relatively large in unit lattice.
0054When this profile was collated with the JPCDS cards, there were no JPCDS cards data on existing substances which were identical with this profile. It should be noted that the JPCDS cards are a data book in which the peak profiles of various kinds of substances as obtained by X-ray diffraction are summarized.
0055It was found as a result of index numbering of peaks of the profile of red powder of Reference Example 1 that the lattice size of the red powder was quite identical with the space group Pnma, Pnc2 (rhombic system) of 11.7×4.96×21.4Å. Further, as a result of the index numbering of peaks of the profile of red powder of Reference Example 2, it was found that the lattice size of the red powder was quite identical with the space group Pnma (rhombic system) P21/c (monoclinic system) of 11.7×4.96×21.4Å. It will be recognized from these results that these luminescent materials were at least formed of rhombic system and the lattice size thereof was around 12×5×21Å.
(Reference Example 9)
0056A luminescent material was synthesized in this reference example under the same conditions as described in Reference Example 2 except that the sintering temperature was changed to 1850°C.
0057This luminescent material thus sintered was formed of a mixture of three kinds of sintered powder differing in body color, thus confirming existence of a white sintered powder, a red sintered powder and a yellowish green powder. When this luminescent material was excited by black light, a blue emission from the white powder, a red emission from the red powder, and a yellowish green emission from the yellowish green powder were observed.
(Reference Example 10)
0058A luminescent material was synthesized in this reference example under the same conditions as described in Reference Example 3 except that the sintering temperature was changed to 1850°C.
0059This luminescent material thus sintered was formed of a mixture of three kinds of sintered powder differing in body color, thus confirming existence of a white sintered powder, a red sintered powder and a yellowish green powder. When this luminescent material was excited by black light, a blue emission from the white powder, a red emission from the red powder, and a yellowish green emission from the yellowish green powder were observed.
(Reference Example 11)
0060A luminescent material was synthesized in this reference example under the same conditions as described in Reference Example 4 except that the sintering temperature was changed to 1850°C.
0061This luminescent material thus sintered was formed of a mixture of three kinds of sintered powder differing in body color, thus confirming existence of a white sintered powder, a red sintered powder and a yellowish green powder. When this luminescent material was excited by black light, a blue emission from the white powder, a red emission from the red powder, and a yellowish green emission from the yellowish green powder were observed.
0062The red powders of Reference Examples 9 to 11 were respectively taken out of the crucible and ground in a mortar in the same manner as described above. Then, the red powders were respectively excited by an emission diode exhibiting a peak wavelength of 457 nm. The emission spectrums thus obtained are shown in <figref idref="f0003">FIG. 6</figref>. In <figref idref="f0003">FIG. 6</figref>, the bands each exhibiting a peak at 457 nm were derived from the reflection of exciting beam. From every red powders, a single-band emission exhibiting a peak at a wavelength ranging from 610 to 620 nm was obtained.
(Reference Example 12)
0063A luminescent material was synthesized in this reference example by following the same procedures as described in Reference Example 1 except that the loading of SrCO<sub>3</sub> was changed to 13.287g and the loading of Eu<sub>2</sub>O<sub>3</sub> was changed to 1.760g.
0064This luminescent material thus sintered was formed of a mixture of two kinds of sintered powder differing in body color, thus confirming existence of a white sintered powder and a red sintered powder. When this luminescent material was excited by black light, a blue emission from the white powder and a red emission from the red powder were observed.
(Reference Example 13)
0065A luminescent material was synthesized in this reference example under the same conditions as described in Reference Example 12 except that the sintering temperature was changed to 1800°C.
0066This luminescent material thus sintered was formed of a mixture of three kinds of sintered powder differing in body color, thus confirming existence of a white sintered powder, a red sintered powder and a yellowish green powder. When this luminescent material was excited by black light, a blue emission from the white powder, a red emission from the red powder, and a yellowish green emission from the yellowish green powder were observed.
(Reference Example 14)
0067A luminescent material was synthesized in this reference example under the same conditions as described in Reference Example 2 except that the sintering temperature was changed to 1800°C.
0068This luminescent material thus sintered was formed of a mixture of three kinds of sintered powder differing in body color, thus confirming existence of a white sintered powder, a red sintered powder and a yellowish green powder. When this luminescent material was excited by black light, a blue emission from the white powder, a red emission from the red powder, and a yellowish green emission from the yellowish green powder were observed.
(Reference Example 15)
0069A luminescent material was synthesized in this reference example under the same conditions as described in Reference Example 4 except that the sintering temperature was changed to 1800°C.
0070This luminescent material thus sintered was formed of a mixture of three kinds of sintered powder differing in body color, thus confirming existence of a white sintered powder, a red sintered powder and a yellowish green powder. When this luminescent material was excited by black light, a blue emission from the white powder, a red emission from the red powder, and a yellowish green emission from the yellowish green powder were observed.
(Reference Example 16)
0071A luminescent material was synthesized in this reference example by following the same procedures as described in Reference Example 14 except that the crucible was changed to a boron nitride crucible.
0072This luminescent material thus sintered was formed of a mixture of two kinds of sintered powder differing in body color, thus confirming existence of a red sintered powder and a yellowish green sintered powder. When this luminescent material was excited by black light, a red emission from the red powder and a yellowish green emission from the yellowish green powder were observed.
0073The red powders of Reference Examples 12 to 16 were respectively taken out of the crucible and ground in a mortar in the same manner as described above. Then, the red powders were respectively excited by an emission diode exhibiting a peak wavelength of 457 nm. The emission spectrums thus obtained are shown in <figref idref="f0004">FIG. 7</figref>. In <figref idref="f0004">FIG. 7</figref>, the bands each exhibiting a peak at 457 nm were derived from the reflection of exciting beam. From every red powders, a single-band emission exhibiting a peak at a wavelength ranging from 600 to 630 nm was obtained.
(Reference Example 17)
0074A luminescent material was synthesized in this reference example by following the same procedures as described in Reference Example 2 except that the sintering time period was changed to 16 hours.
0075This luminescent material thus sintered was formed of a mixture of two kinds of sintered powder differing in body color, thus confirming existence of a white sintered powder and a red sintered powder. When this luminescent material was excited by black light, a blue emission from the white powder and a red emission from the red powder were observed.
(Reference Example 18)
007631.371g of SrCO<sub>3</sub>, 12.296g of AlN, 46.770g of Si<sub>3</sub>N<sub>4</sub> and 6.599g of Eu<sub>2</sub>O<sub>3</sub> were prepared as starting materials. Then, a luminescent material of this reference example was synthesized by following the same procedures as described in Reference Example 1 except that the sintering conditions thereof were changed to 1750°C in temperature and 20 hours in sintering time.
0077This luminescent material thus sintered was formed of a mixture of two kinds of sintered powder differing in body color, thus confirming existence of a red sintered powder and a yellowish green sintered powder. When this luminescent material was excited by black light, a red emission from the red powder and a yellowish green emission from the yellowish green powder were observed.
(Reference Example 19)
0078A luminescent material of this reference example was synthesized by following the same procedures as described in Reference Example 1 except that the sintering conditions thereof were changed to 1850°C in temperature and 16 hours in sintering time.
0079This luminescent material thus sintered was formed of a mixture of two kinds of sintered powder differing in body color, thus confirming existence of a red sintered powder and a yellowish green sintered powder. When this luminescent material was excited by black light, a red emission from the red powder and a yellowish green emission from the yellowish green powder were observed.
(Reference Example 20)
0080A luminescent material of this reference example was synthesized by following the same procedures as described in Reference Example 2 except that the sintering conditions thereof were changed to 1850°C in temperature and 16 hours in sintering time.
0081This luminescent material thus sintered was formed of a mixture of three kinds of sintered powder differing in body color, thus confirming existence of a white sintered powder, a red sintered powder and a yellowish green powder. When this luminescent material was excited by black light, a blue emission from the white powder, a red emission from the red powder, and a yellowish green emission from the yellowish green powder were observed.
0082The red powders of Reference Examples 17 to 20 were respectively taken out of the crucible and ground in a mortar in the same manner as described above. Then, the red powders were respectively excited by an emission diode exhibiting a peak wavelength of 457 nm. The emission spectrums thus obtained are shown in <figref idref="f0004">FIG. 8</figref>. In <figref idref="f0004">FIG. 8</figref>, the bands each exhibiting a peak at 457 nm were derived from the reflection of exciting beam. From every red powders, a single-band emission exhibiting a peak at a wavelength ranging from 616 to 618 nm was obtained.
0083The red powders of Reference Examples 1 to 4, 7, 8 and 17 were sorted out to perform the chemical analysis thereof, the results being summarized in the following Table 1. In this Table 1, there are shown the values of "a", "b", "c" and "d" in the aforementioned general formula (B). <tables id="tabl0001" num="0001"><table frame="all"><title>Table 1</title><tgroup cols="5"><colspec colnum="1" colname="col1" colwidth="20mm" /><colspec colnum="2" colname="col2" colwidth="13mm" /><colspec colnum="3" colname="col3" colwidth="12mm" /><colspec colnum="4" colname="col4" colwidth="13mm" /><colspec colnum="5" colname="col5" colwidth="12mm" /><thead><row><entry align="center" valign="top" /><entry align="center" valign="top">a</entry><entry align="center" valign="top">b</entry><entry align="center" valign="top">c</entry><entry align="center" valign="top">d</entry></row></thead><tbody><row><entry>Ref. Ex.1</entry><entry>0.858</entry><entry>3.34</entry><entry>0.350</entry><entry>4.92</entry></row><row><entry>Ref. Ex.2</entry><entry>0.935</entry><entry>3.41</entry><entry>0.418</entry><entry>5.18</entry></row><row><entry>Ref. Ex.3</entry><entry>0.868</entry><entry>3.58</entry><entry>0.270</entry><entry>5.42</entry></row><row><entry>Ref. Ex.4</entry><entry>0.911</entry><entry>3.70</entry><entry>0.272</entry><entry>5.63</entry></row><row><entry>Ref. Ex.7</entry><entry>0.839</entry><entry>3.37</entry><entry>0.283</entry><entry>5.18</entry></row><row><entry>Ref. Ex.8</entry><entry>0.845</entry><entry>3.34</entry><entry>0.281</entry><entry>5.14</entry></row><row><entry>Ref. Ex.17</entry><entry>0.680</entry><entry>2.54</entry><entry>0.332</entry><entry>4.29</entry></row></tbody></tgroup></table></tables>
(Reference Example 21)
0084A luminescent material of this reference example was synthesized by following the same procedures as described in Reference Example 12 except that the sintering conditions thereof were changed to 1800°C in temperature and 16 hours in sintering time.
0085This luminescent material thus sintered was formed of a mixture of two kinds of sintered powder differing in body color, thus confirming existence of a red sintered powder and a yellowish green sintered powder. When this luminescent material was excited by black light, a red emission from the red powder and a yellowish green emission from the yellowish green powder were observed.
(Reference Example 22)
0086A luminescent material of this reference example was synthesized by following the same procedures as described in Reference Example 1 except that the sintering conditions thereof were changed to 1800°C in temperature and 16 hours in sintering time.
0087This luminescent material thus sintered was formed of a mixture of two kinds of sintered powder differing in body color, thus confirming existence of a red sintered powder and a yellowish green sintered powder. When this luminescent material was excited by black light, a red emission from the red powder and a yellowish green emission from the yellowish green powder were observed.
(Reference Example 23)
0088A luminescent material of this reference example was synthesized by following the same procedures as described in Reference Example 3 except that the sintering conditions thereof were changed to 1800°C in temperature and 16 hours in sintering time.
0089This luminescent material thus sintered was formed of a mixture of two kinds of sintered powder differing in body color, thus confirming existence of a red sintered powder and a yellowish green sintered powder. When this luminescent material was excited by black light, a red emission from the red powder and a yellowish green emission from the yellowish green powder were observed.
0090The red powders of Reference Examples 21 to 23 were respectively taken out of the crucible and ground in a mortar in the same manner as described above. Then, the red powders were respectively excited by an emission diode exhibiting a peak wavelength of 457 nm. The emission spectrums thus obtained are shown in <figref idref="f0005">FIG. 9</figref>. In <figref idref="f0005">FIG. 9</figref>, the bands each exhibiting a peak at 457 nm were derived from the reflection of exciting beam. From every red powders, a single-band emission exhibiting a peak at a wavelength ranging from 615 to 645 nm was obtained.
(Reference Example 24)
0091A raw material powder that had been mixed, dried and ground in the same manner as that of Reference Example 1 was placed in a boron nitride crucible. Thereafter, the raw material powder was sintered for 24 hours at a temperature of 1900°C in a nitrogen atmosphere of 7.5 atm. Then, the sintering of the raw material powder was continued for 64 hours at a temperature of 1800°C, thereby synthesizing the luminescent material of this reference example.
0092This luminescent material thus sintered was formed of a mixture of two kinds of sintered powder differing in body color, thus confirming existence of a red sintered powder and a yellowish green sintered powder. When this luminescent material was excited by black light, a red emission from the red powder and a yellowish green emission from the yellowish green powder were observed.
(Reference Example 25)
0093A raw material powder that had been mixed, dried and ground in the same manner as that of Reference Example 2 was placed in a boron nitride crucible. Thereafter, the raw material powder was sintered for 24 hours at a temperature of 1900°C in a nitrogen atmosphere of 7.5 atm. Then, the sintering of the raw material powder was continued for 64 hours at a temperature of 1800°C, thereby synthesizing the luminescent material of this reference example.
0094This luminescent material thus sintered was formed of a mixture of three kinds of sintered powder differing in body color, thus confirming existence of a white sintered powder, a red sintered powder and a yellowish green powder. When this luminescent material was excited by black light, a blue emission from the white powder, a red emission from the red powder, and a yellowish green emission from the yellowish green powder were observed.
(Reference Example 26)
0095A raw material powder that had been mixed, dried and ground in the same manner as that of Reference Example 3 was placed in a boron nitride crucible. Thereafter, the raw material powder was sintered for 24 hours at a temperature of 1900°C in a nitrogen atmosphere of 7.5 atm. Then, the sintering of the raw material powder was continued for 64 hours at a temperature of 1800°C, thereby synthesizing the luminescent material of this reference example.
0096This luminescent material thus sintered was formed of a mixture of three kinds of sintered powder differing in body color, thus confirming existence of a white sintered powder, a red sintered powder and a yellowish green powder. When this luminescent material was excited by black light, a blue emission from the white powder, a red emission from the red powder, and a yellowish green emission from the yellowish green powder were observed.
0097The red powders of Reference Examples 24 to 26 were respectively taken out of the crucible and ground in a mortar in the same manner as described above. Then, the red powders were respectively excited by an emission diode exhibiting a peak wavelength of 457 nm. The emission spectrums thus obtained are shown in <figref idref="f0005">FIG. 10</figref>. In <figref idref="f0005">FIG. 10</figref>, the bands each exhibiting a peak at 457 nm were derived from the reflection of exciting beam. From every red powders, a single-band emission exhibiting a peak at a wavelength ranging from 580 to 610 nm was obtained.
(Reference Example 27)
0098SrCO<sub>3</sub>, AlN, Si<sub>3</sub>N<sub>4</sub> and Eu<sub>2</sub>O<sub>3</sub> were employed as starting materials, and these starting materials were weighed to obtain 0.664, 0.410, 0.702 and 0.088g, respectively. Then, these starting materials were sufficiently mixed together in a mortar and then charged in a carbon crucible. The mixture in the crucible was then subjected to sintering in a nitrogen atmosphere of 7.5 atm. for four hours at a temperature of 1800°C, thereby synthesizing a luminescent material of this reference example.
0099This luminescent material thus sintered was formed of a mixture of three kinds of sintered powder differing in body color, thus confirming existence of a white sintered powder, a red sintered powder and an orange sintered powder. When this luminescent material was excited by black light, a blue emission from the white powder, a red emission from the red powder and an orange emission from the orange powder were observed.
(Reference Example 28)
0100SrCO<sub>3</sub>, AlN, Si<sub>3</sub>N<sub>4</sub> and Eu<sub>2</sub>O<sub>3</sub> were prepared as starting materials, and these starting materials were weighed to obtain 1.417, 0.820, 1.403 and 0.070g, respectively. Then, these starting materials were sufficiently mixed together in a mortar and then charged in a carbon crucible. The mixture in the crucible was then subjected to sintering in a nitrogen atmosphere of 7.5 atm. for ten hours at a temperature of 1800°C, thereby synthesizing a luminescent material of this reference example.
0101This luminescent material thus sintered was formed of a mixture of three kinds of sintered powder differing in body color, thus confirming existence of a white sintered powder, a red sintered powder and an orange sintered powder. When this luminescent material was excited by black light, a blue emission from the white powder, a red emission from the red powder and an orange emission from the orange powder were observed.
(Reference Example 29)
0102SrCO<sub>3</sub>, AlN, Si<sub>3</sub>N<sub>4</sub> and Eu<sub>2</sub>O<sub>3</sub> were prepared as starting materials, and these starting materials were weighed to obtain 1.402, 0.820, 1.403 and 0.088g, respectively. Then, these starting materials were sufficiently mixed together in a mortar and then charged in a carbon crucible. The mixture in the crucible was then subjected to sintering in a nitrogen atmosphere of 7.5 atm. for ten hours at a temperature of 1800°C, thereby synthesizing a luminescent material of this reference example.
0103This luminescent material thus sintered was formed of a mixture of three kinds of sintered powder differing in body color, thus confirming existence of a white sintered powder, a red sintered powder and an orange sintered powder. When this luminescent material was excited by black light, a blue emission from the white powder, a red emission from the red powder and an orange emission from the orange powder were observed.
0104The orange powders of Reference Examples 27 to 29 were respectively taken out of the crucible and ground in a mortar in the same manner as described above. Then, the orange powders were respectively excited by an emission diode exhibiting a peak wavelength of 457 nm. The emission spectrums thus obtained are shown in <figref idref="f0006">FIG. 11</figref>. In <figref idref="f0006">FIG. 11</figref>, the bands each exhibiting a peak at 457 nm were derived from the reflection of exciting beam. From every orange powder, a single-band emission exhibiting a peak at a wavelength ranging from 587 to 606 nm was obtained.
(Reference Example 30)
0105A luminescent material of this reference example was synthesized by following the same procedures as described in Reference Example 18 except that the sintering conditions thereof were changed to 1800°C in temperature and 16 hours in sintering time.
0106This luminescent material thus sintered was formed of a mixture of three kinds of sintered powder differing in body color, thus confirming existence of a white sintered powder, a red sintered powder and an orange sintered powder. When this luminescent material was excited by black light, a blue emission from the white powder, a red emission from the red powder and an orange emission from the orange powder were observed.
0107The red powder of Reference Example 30 was taken out of the crucible and ground in a mortar in the same manner as described above. Then, the red powder was excited by an emission diode exhibiting a peak wavelength of 457 nm. The emission spectrum thus obtained is shown in <figref idref="f0006">FIG. 12</figref>. In <figref idref="f0006">FIG. 12</figref>, the band exhibiting a peak at 457 nm was derived from the reflection of exciting beam. <figref idref="f0006">FIG. 12</figref> clearly indicates a single-band emission exhibiting a peak at a wavelength of 611 nm.
0108The values of absorption coefficient, quantum yield and luminous efficiency of the red powders of Reference Examples 1-26, the orange powders of Reference Examples 27-29 and the red powder of Reference Example 30 are summarized in the following Table 2. <tables id="tabl0002" num="0002"><table frame="all"><title>Table 2</title><tgroup cols="5"><colspec colnum="1" colname="col1" colwidth="20mm" /><colspec colnum="2" colname="col2" colwidth="36mm" /><colspec colnum="3" colname="col3" colwidth="35mm" /><colspec colnum="4" colname="col4" colwidth="33mm" /><colspec colnum="5" colname="col5" colwidth="40mm" /><thead><row><entry align="center" valign="middle" /><entry align="center" valign="middle">Peak wavelength (nm)</entry><entry align="center" valign="middle">Absorption coefficient</entry><entry align="center" valign="middle">Quantum efficiency</entry><entry align="center" valign="middle">Luminescence efficiency</entry></row></thead><tbody><row><entry>Ref. Ex.1</entry><entry align="center">622</entry><entry align="center">0.83</entry><entry align="center">0.23</entry><entry align="center">0.19</entry></row><row><entry>Ref. Ex.2</entry><entry align="center">631</entry><entry align="center">0.85</entry><entry align="center">0.22</entry><entry align="center">0.19</entry></row><row><entry>Ref. Ex.3</entry><entry align="center">633</entry><entry align="center">0.87</entry><entry align="center">0.17</entry><entry align="center">0.15</entry></row><row><entry>Ref. Ex.4</entry><entry align="center">642</entry><entry align="center">0.93</entry><entry align="center">0.12</entry><entry align="center">0.11</entry></row><row><entry>Ref. Ex.5</entry><entry align="center">630</entry><entry align="center">0.79</entry><entry align="center">0.22</entry><entry align="center">0.18</entry></row><row><entry>Ref. Ex.6</entry><entry align="center">628</entry><entry align="center">0.81</entry><entry align="center">0.17</entry><entry align="center">0.14</entry></row><row><entry>Ref. Ex.7</entry><entry align="center">630</entry><entry align="center">0.85</entry><entry align="center">0.16</entry><entry align="center">0.14</entry></row><row><entry>Ref. Ex.8</entry><entry align="center">640</entry><entry align="center">0.85</entry><entry align="center">0.13</entry><entry align="center">0.11</entry></row><row><entry>Ref. Ex.9</entry><entry align="center">614</entry><entry align="center">0.79</entry><entry align="center">0.33</entry><entry align="center">0.26</entry></row><row><entry>Ref. Ex.10</entry><entry align="center">617</entry><entry align="center">0.81</entry><entry align="center">0.32</entry><entry align="center">0.26</entry></row><row><entry>Ref. Ex.11</entry><entry align="center">621</entry><entry align="center">0.88</entry><entry align="center">0.25</entry><entry align="center">0.22</entry></row><row><entry>Ref. Ex.12</entry><entry align="center">626</entry><entry align="center">0.74</entry><entry align="center">0.29</entry><entry align="center">0.21</entry></row><row><entry>Ref. Ex.13</entry><entry align="center">602</entry><entry align="center">0.78</entry><entry align="center">0.32</entry><entry align="center">0.25</entry></row><row><entry>Ref. Ex.14</entry><entry align="center">619</entry><entry align="center">0.78</entry><entry align="center">0.38</entry><entry align="center">0.29</entry></row><row><entry>Ref. Ex.15</entry><entry align="center">629</entry><entry align="center">0.85</entry><entry align="center">0.29</entry><entry align="center">0.25</entry></row><row><entry>Ref. Ex.16</entry><entry align="center">628</entry><entry align="center">0.85</entry><entry align="center">0.42</entry><entry align="center">0.36</entry></row><row><entry>Ref. Ex.17</entry><entry align="center">616</entry><entry align="center">0.82</entry><entry align="center">0.37</entry><entry align="center">0.30</entry></row><row><entry>Ref. Ex.18</entry><entry align="center">618</entry><entry align="center">0.88</entry><entry align="center">0.32</entry><entry align="center">0.28</entry></row><row><entry>Ref. Ex.19</entry><entry align="center">618</entry><entry align="center">0.86</entry><entry align="center">0.22</entry><entry align="center">0.19</entry></row><row><entry>Ref. Ex.20</entry><entry align="center">617</entry><entry align="center">0.88</entry><entry align="center">0.24</entry><entry align="center">0.21</entry></row><row><entry>Ref. Ex.21</entry><entry align="center">616</entry><entry align="center">0.90</entry><entry align="center">0.16</entry><entry align="center">0.15</entry></row><row><entry>Ref. Ex.22</entry><entry align="center">627</entry><entry align="center">0.91</entry><entry align="center">0.20</entry><entry align="center">0.18</entry></row><row><entry>Ref. Ex.23</entry><entry align="center">645</entry><entry align="center">0.91</entry><entry align="center">0.21</entry><entry align="center">0.19</entry></row><row><entry>Ref. Ex.24</entry><entry align="center">614</entry><entry align="center">0.71</entry><entry align="center">0.44</entry><entry align="center">0.31</entry></row><row><entry>Ref. Ex.25</entry><entry align="center">647</entry><entry align="center">0.72</entry><entry align="center">0.37</entry><entry align="center">0.27</entry></row><row><entry>Ref. Ex.26</entry><entry align="center">646</entry><entry align="center">0.77</entry><entry align="center">0.34</entry><entry align="center">0.26</entry></row><row><entry>Ref. Ex.27</entry><entry align="center">604</entry><entry align="center">0.77</entry><entry align="center">0.32</entry><entry align="center">0.24</entry></row><row><entry>Ref. Ex.28</entry><entry align="center">587</entry><entry align="center">0.53</entry><entry align="center">0.35</entry><entry align="center">0.19</entry></row><row><entry>Ref. Ex.29</entry><entry align="center">587</entry><entry align="center">0.53</entry><entry align="center">0.35</entry><entry align="center">0.19</entry></row><row><entry>Ref. Ex.30</entry><entry align="center">587</entry><entry align="center">0.53</entry><entry align="center">0.35</entry><entry align="center">0.19</entry></row></tbody></tgroup></table></tables>
0109As shown in Table 2, all of the red powders of Reference Examples 1-26, the orange powders of Reference Examples 27-29 and the red powder of Reference Example 30 were capable of exhibiting an emission wavelength falling within the range of 580 to 700 nm as they were excited by the light having a wavelength ranging from 250 to 500 nm. The absorption coefficient, quantum yield and luminous efficiency of these luminescent materials were by no means inferior to the conventional red-type luminescent materials such for example as Sr<sub>2</sub>Si<sub>5</sub>N<sub>8</sub>Eu, etc.
0110It should be noted that, even if the exciting wavelength was changed to 254, 365, 390 or 460 nm, it was possible to confirm the emission having a peak in the aforementioned wavelength range. Because of the facts that if the exciting wavelength is too short, the loss due to Stokes shift would become prominent and that if the exciting wavelength is too long, the excitation efficiency would be deteriorated, the exciting wavelength should preferably be confined within the range of 380 to 460 nm. Further, the peak wavelength of emission should desirably be confined to 670 nm or less.
0111With respect to the compositions of red powders of Reference Examples 1-4, 7, 8 and 17, they are already shown in Table 1. The red powders and orange powders of other Reference Examples were also chemically analyzed to investigate the values of "a", "b", "c" and "d" in the aforementioned general formula (B).
0112As a result, it was found out that, in the cases of the red powders of Reference Examples 1-26, the orange powders of Reference Examples 27-29 and the red powder of Reference Example 30, the upper limit of the value of "a" was 0.948 and the lower limit thereof was 0.605. With respect to the upper limit and the lower limit of the value of "b", they were 3.88 and 2.10, respectively. With respect to the upper limit and the lower limit of the value of "c", they were 0.446 and 0.253, respectively. Further, with respect to the upper limit and the lower limit of the value of "d", they were 5.68 and 4.05, respectively.
0113Based on these results, the compositions of red powders of Reference Examples 1-26, the orange powders of Reference Examples 27-29 and the red powder of Reference Example 30 were found definable by the following general formula (1). (M<sub>1-x</sub>R<sub>x</sub>)<sub>al</sub>AlSi<sub>bl</sub>O<sub>c1</sub>N<sub>d1</sub> (1)
0114In the general formula (1), M is at least one metallic element excluding Si and Al; R is a luminescence center element; and x, a1, b1, c1 and d1 satisfy following relationships: <maths id="math0007"><math display="block"><mn mathvariant="normal">0</mn><mo mathvariant="normal"><</mo><mi mathvariant="normal">x</mi><mo mathvariant="normal">≤</mo><mn mathvariant="normal">1</mn><mo mathvariant="normal">,</mo><mspace width="2em" /><mn mathvariant="normal">0.6</mn><mo><</mo><mi mathvariant="normal">a</mi><mo></mo><mn mathvariant="normal">1</mn><mo mathvariant="normal"><</mo><mn mathvariant="normal">0.95</mn><mo mathvariant="normal">,</mo><mspace width="1em" /><mn mathvariant="normal">2</mn><mo mathvariant="normal"><</mo><mi mathvariant="normal">b</mi><mo></mo><mn mathvariant="normal">1</mn><mo mathvariant="normal"><</mo><mn mathvariant="normal">3.9</mn></math><img file="EP2003183A1_D0007.tif" /></maths><maths id="math0008"><math display="block"><mn mathvariant="normal">0.25</mn><mo mathvariant="normal"><</mo><mi mathvariant="normal">c</mi><mo></mo><mn mathvariant="normal">1</mn><mo mathvariant="normal"><</mo><mn mathvariant="normal">0.45</mn><mo mathvariant="normal">,</mo><mspace width="5em" /><mn mathvariant="normal">4</mn><mo mathvariant="normal"><</mo><mi mathvariant="normal">d</mi><mo></mo><mn mathvariant="normal">1</mn><mo mathvariant="normal"><</mo><mn mathvariant="normal">5.7</mn></math><img file="EP2003183A1_D0008.tif" /></maths>
0115When all of the compositions of red powders of Reference Examples 1-26, the orange powders of Reference Examples 27-29 and the red powder of Reference Example 30 were subjected to X-ray diffraction measurement employing CuKα characteristic X-rays (wavelength: 1.54056Å), they exhibited concurrently diffraction peaks at least at diffraction angles (2θ) of 8.60-8.64, 11.16-11.20 and 18.26-18.30°.
(Example 1)
0116A luminescent material was synthesized in this example by following the same procedures as described in Reference Example 21 except that the sintering conditions thereof were changed to 1800°C in temperature and 72 hours in sintering time.
0117This luminescent material thus sintered was formed of a mixture of two kinds of sintered powder differing in body color, thus confirming existence of a yellowish green sintered powder and an orange sintered powder. When this luminescent material was excited by black light, a yellowish green emission from the yellowish green powder and an orange emission from the orange powder were observed.
(Example 2)
0118A luminescent material was synthesized in this example by following the same procedures as described in Reference Example 22 except that the sintering conditions thereof were changed to 1800°C in temperature and 72 hours in sintering time.
0119This luminescent material thus sintered was formed of a mixture of two kinds of sintered powder differing in body color, thus confirming existence of a yellowish green sintered powder and an orange sintered powder. When this luminescent material was excited by black light, a yellowish green emission from the yellowish green powder and an orange emission from the orange powder were observed.
(Example 3)
0120A luminescent material was synthesized in this example by following the same procedures as described in Reference Example 23 except that the sintering conditions thereof were changed to 1800°C in temperature and 72 hours in sintering time.
0121This luminescent material thus sintered was formed of a mixture of two kinds of sintered powder differing in body color, thus confirming existence of a yellowish green sintered powder and an orange sintered powder. When this luminescent material was excited by black light, a yellowish green emission from the yellowish green powder and an orange emission from the orange powder were observed.
0122When this yellowish green powder was subjected to X-ray diffraction measurement employing CuKα characteristic X-rays (wavelength: 1.54056Å), it exhibited concurrently diffraction peaks at diffraction angles (2θ) of 11.831, 15.361, 20.451 and 23.840°.
(Example 4)
0123A luminescent material was synthesized in this example by following the same procedures as described in Reference Example 24 except that the sintering conditions thereof were changed to 1800°C in temperature and 72 hours in sintering time.
0124This luminescent material thus sintered was formed of a mixture of two kinds of sintered powder differing in body color, thus confirming existence of a yellowish green sintered powder and an orange sintered powder. When this luminescent material was excited by black light, a yellowish green emission from the yellowish green powder and an orange emission from the orange powder were observed.
0125The yellowish green powders of Examples 1 to 4 were respectively taken out of the crucible and ground in a mortar in the same manner as described above. Then, the yellowish green powders were respectively excited by an emission diode exhibiting a peak wavelength of 457 nm. The emission spectrums thus obtained are shown in <figref idref="f0007">FIG. 13</figref>. In <figref idref="f0007">FIG. 13</figref>, the bands each exhibiting a peak at 457 nm were derived from the reflection of exciting beam. From every yellowish green powders, a single-band emission exhibiting a peak at a wavelength ranging from 522 to 524 nm was obtained.
0126The yellowish green powder of Example 3 was sorted out from the crucible to perform the chemical analysis thereof, the results being indicated in the following Table 3. In this Table 3, there are shown the values of "a", "b", "c" and "d" in the aforementioned general formula (B). <tables id="tabl0003" num="0003"><table frame="all"><title>Table 3</title><tgroup cols="5"><colspec colnum="1" colname="col1" colwidth="12mm" /><colspec colnum="2" colname="col2" colwidth="13mm" /><colspec colnum="3" colname="col3" colwidth="12mm" /><colspec colnum="4" colname="col4" colwidth="12mm" /><colspec colnum="5" colname="col5" colwidth="12mm" /><thead><row><entry valign="top" /><entry align="center" valign="top">a</entry><entry align="center">b</entry><entry align="center">c</entry><entry align="center">d</entry></row></thead><tbody><row><entry>Ex.3</entry><entry>0.940</entry><entry>4.15</entry><entry>0.63</entry><entry>6.30</entry></row></tbody></tgroup></table></tables>
0127The values of absorption coefficient, quantum yield and luminous efficiency of the yellowish green powders of Examples 1-4 as they were excited by the light having a wavelength of 457 nm are summarized in the following Table 4. <tables id="tabl0004" num="0004"><table frame="all"><title>Table 4</title><tgroup cols="5"><colspec colnum="1" colname="col1" colwidth="12mm" /><colspec colnum="2" colname="col2" colwidth="36mm" /><colspec colnum="3" colname="col3" colwidth="35mm" /><colspec colnum="4" colname="col4" colwidth="33mm" /><colspec colnum="5" colname="col5" colwidth="40mm" /><thead><row><entry align="center" valign="middle" /><entry align="center" valign="middle">Peak wavelength (nm)</entry><entry align="center" valign="middle">Absorption coefficient</entry><entry align="center" valign="middle">Quantum efficiency</entry><entry align="center" valign="middle">Luminescence efficiency</entry></row></thead><tbody><row><entry>Ex.1</entry><entry align="center">522</entry><entry align="center">0.84</entry><entry align="center">0.48</entry><entry align="center">0.40</entry></row><row><entry>Ex.2</entry><entry align="center">522</entry><entry align="center">0.85</entry><entry align="center">0.48</entry><entry align="center">0.40</entry></row><row><entry>Ex.3</entry><entry align="center">524</entry><entry align="center">0.83</entry><entry align="center">0.45</entry><entry align="center">0.38</entry></row><row><entry>Ex.4</entry><entry align="center">524</entry><entry align="center">0.80</entry><entry align="center">0.45</entry><entry align="center">0.36</entry></row></tbody></tgroup></table></tables>
0128As shown in Table 4, all of the yellowish green powders of Examples 1-4 were capable of exhibiting an emission wavelength falling within the range of 490 to 580 nm as they were excited by the light having a wavelength ranging from 250 to 500 nm. The absorption coefficient, quantum yield and luminous efficiency of these luminescent materials were by no means inferior to the conventional yellowish green luminescent materials such for example as (Ba,Sr)<sub>2</sub>SiO<sub>4</sub>:Eu, etc.
0129Further, the emission characteristics of the luminescent material of Example 2 as it was excited by the light having a wavelength of 450 nm were 87% in absorption coefficient, 48% in internal quantum yield and 42% in luminous efficiency. These results indicates that, as far as the yellowish green luminescent material of this embodiment is concerned, it has such emission characteristics that the excitation thereof using a wavelength of 450 nm is more advantageous in obtaining higher luminous efficiency than the excitation thereof using a wavelength of 460 nm.
0130It should be noted that <nplcit id="ncit0001" npl-type="b"><text>N. Hirosaki et al., Extended Abstracts (53rd Spring Meeting), The Japan Society of Applied Physics and Related Societies, 25p-ZR-11 (2006</text></nplcit>), describes that the emission characteristics of Eu-activated β salon as it was excited by the light having a wavelength of 450 nm were 65% in absorption coefficient, 53% in internal quantum yield and 35% in luminous efficiency. <patcit id="pcit0001" dnum="JP2005255895A"><text>JP-A 2005-255895</text></patcit> (KOKAI) is a Patent Gazette related to the aforementioned Eu-activated β sialon. It will be recognized from the comparison between the luminous efficiency of this conventional luminescent material and the luminous efficiency of the luminescent material of this embodiment under the same condition with respect to the excitation wavelength that the yellowish green luminescent material of this embodiment is more excellent than the aforementioned conventional luminescent material.
0131Even if the exciting wavelength was changed to 254, 365, 390 or 460 nm, it was possible to confirm the emission having a peak in almost the same wavelength range as described above. Because of the facts that if the exciting wavelength is too short, the loss due to Stokes shift would become prominent and that if the exciting wavelength is too long, the excitation efficiency would be deteriorated, the exciting wavelength should preferably be confined within the range of 380 to 460 nm. Further, the peak wavelength of emission should desirably be confined to 560 nm or less. Additionally, the peak wavelength of emission should desirably be confined to 500 nm or more.
(Example 5)
0132SrCO<sub>3</sub>, AlN, Si<sub>3</sub>N<sub>4</sub> and Eu<sub>2</sub>O<sub>3</sub> were prepared as starting materials, and these starting materials were weighed to obtain 16.027, 4.837, 27.594 and 1.661g, respectively. Then, these starting materials were mixed together with dehydrated isopropanol (IPA) for 2 hours in a ball mill. IPA was volatilized and removed by drying using mantle heater. Thereafter, the resultant mixture was passed through a sieve having an aperture of 300 µm to prepare a raw material powder. The raw material powder thus obtained was allowed to naturally drop from sieve having an aperture of 500-1000 µm, thereby enabling a boron nitride crucible to be filled with the raw material powder. The raw material powder in the crucible was then subjected to sintering in a nitrogen atmosphere of 7 atm. for 12 hours at a temperature of 1800°C to synthesize a luminescent material of this reference example.
0133This luminescent material thus sintered was formed of a mixture of two kinds of sintered powder differing in body color, thus confirming existence of a white sintered powder and a yellowish green sintered powder. When this luminescent material was excited by black light, a blue emission from the white powder and a yellowish green emission from the yellowish green powder were observed.
(Example 6)
0134A luminescent material was synthesized in this example by following the same procedures as described in Example 5 except that the loading of SrCO<sub>3</sub>, AlN, Si<sub>3</sub>N<sub>4</sub> and Eu<sub>2</sub>O<sub>3</sub> was changed to 16.298, 4.919, 25.256 and 1.689g, respectively. The raw material powder thus obtained was sintered for 6 hours at a temperature of 1850°C to synthesize a luminescent material of this reference example.
0135This luminescent material thus sintered was formed of a mixture of three kinds of sintered powder differing in body color, thus confirming existence of a white sintered powder, a red sintered powder and a yellowish green sintered powder. When this luminescent material was excited by black light, a blue emission from the white powder, a red emission from the red powder and a yellowish green emission from the yellowish green powder were observed.
(Example 7)
0136A luminescent material was synthesized in this example by following the same procedures as described in Example 6 except that the loading of Si<sub>3</sub>N<sub>4</sub> was changed to 26.659g.
0137This luminescent material thus sintered was formed of a mixture of three kinds of sintered powder differing in body color, thus confirming existence of a white sintered powder, a red sintered powder and a yellowish green sintered powder. When this luminescent material was excited by black light, a blue emission from the white powder, a red emission from the red powder and a yellowish green emission from the yellowish green powder were observed.
(Example 8)
0138A luminescent material was synthesized in this example by following the same procedures as described in Example 7 except that the sintering conditions thereof were changed to 1800°Cin temperature and 16 hours in sintering time.
0139This luminescent material thus sintered was formed of a mixture of three kinds of sintered powder differing in body color, thus confirming existence of a white sintered powder, a red sintered powder and a yellowish green sintered powder. When this luminescent material was excited by black light, a blue emission from the white powder, a red emission from the red powder and a yellowish green emission from the yellowish green powder were observed.
(Example 9)
0140A luminescent material was synthesized in this example by following the same procedures as described in Example 5 except that the sintering time period thereof were changed to 16 hours.
0141This luminescent material thus sintered was formed of a mixture of three kinds of sintered powder differing in body color, thus confirming existence of a white sintered powder, a red sintered powder and a yellowish green sintered powder. When this luminescent material was excited by black light, a blue emission from the white powder, a red emission from the red powder and a yellowish green emission from the yellowish green powder were observed.
(Example 10)
0142A luminescent material was synthesized in this example by following the same procedures as described in Example 9 except that the loading of Si<sub>3</sub>N<sub>4</sub> was changed to 29.465g.
0143This luminescent material thus sintered was formed of a mixture of two kinds of sintered powder differing in body color, thus confirming existence of a white sintered powder and a yellowish green sintered powder. When this luminescent material was excited by black light, a blue emission from the white powder and a yellowish green emission from the yellowish green powder were observed.
0144When this yellowish green powder was subjected to X-ray diffraction measurement employing CuKα characteristic X-rays (wavelength: 1.54056Å), it exhibited concurrently diffraction peaks at diffraction angles (2θ) of 11.870, 15.39, 20.47 and 23.79°.
(Example 11)
0145A luminescent material was synthesized in this example by following the same procedures as described in Example 9 except that the loading of Si<sub>3</sub>N<sub>4</sub> was changed to 30.868g.
0146This luminescent material thus sintered was formed of a mixture of two kinds of sintered powder differing in body color, thus confirming existence of a white sintered powder and a yellowish green sintered powder. When this luminescent material was excited by black light, a blue emission from the white powder and a yellowish green emission from the yellowish green powder were observed.
(Example 12)
0147A luminescent material was synthesized in this example by following the same procedures as described in Example 6 except that the loading of Si<sub>3</sub>N<sub>4</sub> was changed to 29.465g and the sintering time period was changed to 10 hours. This luminescent material thus sintered was formed of a sintered powder exhibiting a body color of yellowish green. When this luminescent material was excited by black light, a yellowish green emission was observed.
(Example 13)
0148A luminescent material was synthesized in this example by following the same procedures as described in Example 5 except that the loading of SrCO<sub>3</sub> was changed to 16.550g and the loading of Eu<sub>2</sub>O<sub>3</sub> was changed to 1.038g. This luminescent material thus sintered was formed of a sintered powder exhibiting a body color of yellowish green. When this luminescent material was excited by black light, a yellowish green emission was observed.
(Example 14)
0149A luminescent material was synthesized in this example by following the same procedures as described in Example 12. This luminescent material thus sintered was formed of a sintered powder exhibiting a body color of yellowish green. When this luminescent material was excited by black light, a yellowish green emission was observed.
0150When this yellowish green powder was subjected to X-ray diffraction measurement employing CuKα characteristic X-rays (wavelength: 1.54056Å), it exhibited concurrently diffraction peaks at diffraction angles (2θ) of 11.87, 15.39, 20.47 and 23.85°.
0151The yellowish green powder of Example 5 was excited by an emission diode exhibiting a peak wavelength of 461 nm. The emission spectrum thus obtained is shown in <figref idref="f0007">FIG. 14</figref>. In <figref idref="f0007">FIG. 14</figref>, the band exhibiting a peak at 461 nm was derived from the reflection of exciting beam. From this yellowish green powder, a single-band emission exhibiting a peak wavelength falling within the range of 514 to 518 nm was obtained.
0152The yellowish green powders of Examples 6 and 7 were respectively excited by an emission diode exhibiting a peak wavelength of 461 nm. The emission spectrums thus obtained are shown in <figref idref="f0008">FIG. 15</figref>. In <figref idref="f0008">FIG. 15</figref>, the band exhibiting a peak at 461 nm was derived from the reflection of exciting beam. From these yellowish green powders, a single-band emission exhibiting a peak wavelength at 517 nm was obtained.
0153The yellowish green powders of Examples 8 to 11 were respectively excited by an emission diode exhibiting a peak wavelength of 461 nm. The emission spectrums thus obtained are shown in <figref idref="f0008">FIG. 16</figref>. In <figref idref="f0008">FIG. 16</figref>, the band exhibiting a peak at 461 nm was derived from the reflection of exciting beam. From these yellowish green powders, a single-band emission exhibiting a peak wavelength falling within the range of 517 to 520 nm was obtained.
0154The yellowish green powders of Examples 12 to 14 were respectively excited by an emission diode exhibiting a peak wavelength of 461 nm. The emission spectrums thus obtained are shown in <figref idref="f0009">FIG. 17</figref>. In <figref idref="f0009">FIG. 17</figref>, the band exhibiting a peak at 461 nm was derived from the reflection of exciting beam. From these yellowish green powders, a single-band emission exhibiting a peak wavelength falling within the range of 517 to 520 nm was obtained.
0155The yellowish green luminescent materials of Examples 5, 7, and 10-14 were respectively sorted out from the crucible to perform the chemical analysis thereof, the results being summarized in the following Table 5. In this Table 5, there are shown the values of "a", "b", "c" and "d" in the aforementioned general formula (B). <tables id="tabl0005" num="0005"><table frame="all"><title>Table 5</title><tgroup cols="5"><colspec colnum="1" colname="col1" colwidth="14mm" /><colspec colnum="2" colname="col2" colwidth="13mm" /><colspec colnum="3" colname="col3" colwidth="12mm" /><colspec colnum="4" colname="col4" colwidth="12mm" /><colspec colnum="5" colname="col5" colwidth="10mm" /><thead><row><entry align="center" valign="top" /><entry align="center" valign="top">a</entry><entry align="center" valign="top">b</entry><entry align="center" valign="top">c</entry><entry align="center" valign="top">d</entry></row></thead><tbody><row><entry>Ex.5</entry><entry>0.940</entry><entry>4.12</entry><entry>0.71</entry><entry>6.7</entry></row><row><entry>Ex.7</entry><entry>0.950</entry><entry>4.41</entry><entry>0.82</entry><entry>8.8</entry></row><row><entry>Ex.10</entry><entry>0.963</entry><entry>4.28</entry><entry>0.64</entry><entry>6.9</entry></row><row><entry>Ex.11</entry><entry>1.09</entry><entry>5.73</entry><entry>0.68</entry><entry>9.7</entry></row><row><entry>Ex.12</entry><entry>1.30</entry><entry>5.70</entry><entry>0.85</entry><entry>11</entry></row><row><entry>Ex.13</entry><entry>1.06</entry><entry>4.78</entry><entry>0.71</entry><entry>7.3</entry></row><row><entry>Ex.14</entry><entry>1.03</entry><entry>4.61</entry><entry>0.74</entry><entry>7.4</entry></row></tbody></tgroup></table></tables>
0156The values of absorption coefficient, quantum yield and luminous efficiency of the yellowish green powders of Examples 5-14 are summarized in the following Table 6. <tables id="tabl0006" num="0006"><table frame="all"><title>Table 6</title><tgroup cols="5"><colspec colnum="1" colname="col1" colwidth="14mm" /><colspec colnum="2" colname="col2" colwidth="36mm" /><colspec colnum="3" colname="col3" colwidth="35mm" /><colspec colnum="4" colname="col4" colwidth="33mm" /><colspec colnum="5" colname="col5" colwidth="40mm" /><thead><row><entry valign="top" /><entry align="center" valign="top">Peak wavelength (nm)</entry><entry align="center" valign="middle">Absorption coefficient</entry><entry align="center" valign="middle">Quantum efficiency</entry><entry align="center" valign="middle">Luminescence efficiency</entry></row></thead><tbody><row><entry>Ex.5</entry><entry align="center">518</entry><entry align="center">0.79</entry><entry align="center">0.58</entry><entry align="center">0.46</entry></row><row><entry>Ex.6</entry><entry align="center">514</entry><entry align="center">0.84</entry><entry align="center">0.55</entry><entry align="center">0.46</entry></row><row><entry>Ex.7</entry><entry align="center">517</entry><entry align="center">0.91</entry><entry align="center">0.56</entry><entry align="center">0.51</entry></row><row><entry>Ex.8</entry><entry align="center">517</entry><entry align="center">0.84</entry><entry align="center">0.53</entry><entry align="center">0.45</entry></row><row><entry>Ex.9</entry><entry align="center">518</entry><entry align="center">0.81</entry><entry align="center">0.54</entry><entry align="center">0.44</entry></row><row><entry>Ex.10</entry><entry align="center">520</entry><entry align="center">0.80</entry><entry align="center">0.55</entry><entry align="center">0.44</entry></row><row><entry>Ex.11</entry><entry align="center">520</entry><entry align="center">0.75</entry><entry align="center">0.54</entry><entry align="center">0.41</entry></row><row><entry>Ex.12</entry><entry align="center">514</entry><entry align="center">0.64</entry><entry align="center">0.62</entry><entry align="center">0.40</entry></row><row><entry>Ex.13</entry><entry align="center">511</entry><entry align="center">0.72</entry><entry align="center">0.59</entry><entry align="center">0.43</entry></row><row><entry>Ex.14</entry><entry align="center">516</entry><entry align="center">0.80</entry><entry align="center">0.59</entry><entry align="center">0.48</entry></row></tbody></tgroup></table></tables>
0157As shown in Table 6, all of the yellowish green powders of Examples 5-14 were capable of exhibiting an emission wavelength falling within the range of 490 to 580 nm as they were excited by the light having a wavelength ranging from 250 to 500 nm. The absorption coefficient, quantum yield and luminous efficiency of these luminescent materials were by no means inferior to the conventional yellowish green luminescent materials such for example as (Ba,Sr)<sub>2</sub>SiO<sub>4</sub>:Eu, etc.
0158With respect to the compositions of yellowish green powders of Examples 3, 5, 7, and 10-14, they are already shown in Table 1. The yellowish green powders of other Examples were also chemically analyzed to investigate the values of "a", "b", "c" and "d" in the aforementioned general formula (B).
0159As a result, it was found out that, in the cases of the yellowish green powders of Reference Examples 1-14, the upper limit of the value of "a" was 1.30 and the lower limit thereof was 0.940. With respect to the upper limit and the lower limit of the value of "b", they were 5.73 and 4.12, respectively. With respect to the upper limit and the lower limit of the value of "c", they were 0.85 and 0.63, respectively. Further, with respect to the upper limit and the lower limit of the value of "d", they were 11 and 6.3, respectively.
0160Based on these results, the compositions of yellowish green powders of Examples 1-14 were found definable by the following general formula (2). (M<sub>1-x</sub>R<sub>x</sub>)<sub>a2</sub>AlSi<sub>b2</sub>O<sub>c2</sub>N<sub>d2</sub> (2)
0161In the general formula (2), M is at least one kind of metallic element excluding Si and Al; R is a luminescence center element; and x, a2, b2, c2 and d2 satisfy the following relationship: <maths id="math0009"><math display="block"><mn mathvariant="normal">0</mn><mo mathvariant="normal"><</mo><mi mathvariant="normal">x</mi><mo mathvariant="normal">≤</mo><mn mathvariant="normal">1</mn><mo mathvariant="normal">,</mo><mspace width="2em" /><mn mathvariant="normal">0.93</mn><mo><</mo><mi mathvariant="normal">a</mi><mo></mo><mn mathvariant="normal">2</mn><mo mathvariant="normal"><</mo><mn mathvariant="normal">1.3</mn><mo mathvariant="normal">,</mo><mspace width="1em" /><mn mathvariant="normal">4.0</mn><mo mathvariant="normal"><</mo><mi mathvariant="normal">b</mi><mo></mo><mn mathvariant="normal">2</mn><mo mathvariant="normal"><</mo><mn mathvariant="normal">5.8</mn></math><img file="EP2003183A1_D0009.tif" /></maths><maths id="math0010"><math display="block"><mn mathvariant="normal">0.6</mn><mo mathvariant="normal"><</mo><mi mathvariant="normal">c</mi><mo></mo><mn mathvariant="normal">2</mn><mo mathvariant="normal"><</mo><mn mathvariant="normal">1</mn><mo mathvariant="normal">,</mo><mspace width="3em" /><mi>and</mi><mspace width="1em" /><mn mathvariant="normal">6</mn><mo mathvariant="normal"><</mo><mi mathvariant="normal">d</mi><mo></mo><mn mathvariant="normal">2</mn><mo mathvariant="normal"><</mo><mn mathvariant="normal">11</mn><mn mathvariant="normal">.</mn></math><img file="EP2003183A1_D0010.tif" /></maths>
0162The yellowish green luminescent materials of Examples 5-8 and 14 were found capable of exhibiting a luminous efficiency of 45% or more, thus indicating excellent luminous efficiency. The compositions of yellowish green powders of Examples 1-14 which were especially excellent in luminous efficiency can be defined by the general formula (2) wherein a2, b2, c2 and d2 satisfy the following relationships: <maths id="math0011"><math display="block"><mn mathvariant="normal">0.94</mn><mo mathvariant="normal"><</mo><mi mathvariant="normal">a</mi><mo></mo><mn mathvariant="normal">2</mn><mo mathvariant="normal"><</mo><mn mathvariant="normal">1.1</mn><mo mathvariant="normal">,</mo><mspace width="3em" /><mn mathvariant="normal">4.1</mn><mo mathvariant="normal"><</mo><mi mathvariant="normal">b</mi><mo></mo><mn mathvariant="normal">2</mn><mo mathvariant="normal"><</mo><mn mathvariant="normal">4.7</mn></math><img file="EP2003183A1_D0011.tif" /></maths><maths id="math0012"><math display="block"><mn mathvariant="normal">0.7</mn><mo mathvariant="normal"><</mo><mi mathvariant="normal">c</mi><mo></mo><mn mathvariant="normal">2</mn><mo mathvariant="normal"><</mo><mn mathvariant="normal">0.85</mn><mo mathvariant="normal">,</mo><mspace width="5em" /><mn mathvariant="normal">7</mn><mo mathvariant="normal"><</mo><mi mathvariant="normal">d</mi><mo></mo><mn mathvariant="normal">2</mn><mo mathvariant="normal"><</mo><mn mathvariant="normal">9</mn><mn mathvariant="normal">.</mn></math><img file="EP2003183A1_D0012.tif" /></maths>
0163When all of the yellowish green powders of Examples 1-14 were subjected to X-ray diffraction measurement employing CuKα characteristic X-rays (wavelength: 1.54056Å), they exhibited concurrently diffraction peaks at least at diffraction angles (2θ) of 11.81-11.85, 15.34-15.38, 20.40-20.47 and 23.74-23.86°.
(Reference Example 31)
0164SrCO<sub>3</sub>, AlN, Si<sub>3</sub>N<sub>4</sub> and Eu<sub>2</sub>O<sub>3</sub> were prepared as starting materials, and these starting materials were weighed to obtain 29.378, 16.395, 28.062 and 0.176g, respectively. Then, these starting materials were mixed together with dehydrated isopropanol (IPA) for 24 hours in a ball mill. After IPA was volatilized and removed by room temperature drying, the mixture was allowed to dry overnight in air atmosphere and at a temperature of 120°C. The resultant mixture was ground in a mortar and then charged in a carbon crucible. Finally, the mixture in the crucible was subjected to sintering in a nitrogen atmosphere of 7.5 atm. for 60 hours at a temperature of 1800°C to synthesize a luminescent material, wherein this sintering was repeated twice under the same conditions.
0165This luminescent material thus sintered was formed of a mixture of sintered powders differing in body color, i.e., a white sintered powder, a minute amount of orange sintered powder and a minute amount of red sintered powder. When this luminescent material was excited by black light, a blue emission from the white powder, an orange emission from the minute amount of orange sintered powder and a red emission from the minute amount of red powder were observed.
0166This red powder was dispensed and subjected to X-ray diffraction measurement employing CuKα characteristic X-rays (wavelength: 1.54056Å). As a result, it exhibited concurrently diffraction peaks at diffraction angles (2θ) of 13.10, 18.62, 20.22, 26.40 and 28.04°.
0167When this red powder was subjected to chemical analysis, it was possible to confirm a composition represented by (M<sub>0.991</sub>R<sub>0.009</sub>)<sub>2.23</sub>AlSi<sub>4.75</sub>O<sub>0.80</sub>N<sub>7.88</sub>. The red powder of this reference example can be defined, by the values of a, b, c and d in the aforementioned general formula (B), such that the value of (1+b)/a is 2.58 and the value of (c+d)/a is 3.93.
(Reference Example 32)
0168A luminescent material was synthesized in this example under the same conditions as described in Reference Example 31 except that the loading of SrCO<sub>3</sub> was changed to 29.231g and the loading of Eu<sub>2</sub>O<sub>3</sub> was changed to 0.352g.
0169This luminescent material thus sintered was formed of a mixture of sintered powders differing in body color, i.e., a white sintered powder, a minute amount of orange sintered powder and a minute amount of red sintered powder. When this luminescent material was excited by black light, a blue emission from the white powder, an orange emission from the minute amount of orange sintered powder and a red emission from the minute amount of red powder were observed.
(Reference Example 33)
0170A luminescent material was synthesized in this example under the same conditions as described in Reference Example 31 except that the loading of SrCO<sub>3</sub> was changed to 28.935g and the loading of Eu<sub>2</sub>O<sub>3</sub> was changed to 0.704g.
0171This luminescent material thus sintered was formed of a mixture of sintered powders differing in body color, i.e., a white sintered powder, a minute amount of orange sintered powder and a minute amount of red sintered powder. When this luminescent material was excited by black light, a blue emission from the white powder, an orange emission from the minute amount of orange sintered powder and a red emission from the minute amount of red powder were observed.
0172This red powder was dispensed and subjected to X-ray diffraction measurement employing CuKα characteristic X-rays (wavelength: 1.54056Å). As a result, it exhibited concurrently diffraction peaks at diffraction angles (2θ) of 13.08, 18.62, 20.18, 26.38 and 28.02°.
(Reference Example 34)
0173A luminescent material was synthesized in this example under the same conditions as described in Reference Example 31 except that the loading of SrCO<sub>3</sub> was changed to 28.640g and the loading of Eu<sub>2</sub>O<sub>3</sub> was changed to 1.056g.
0174This luminescent material thus sintered was formed of a mixture of sintered powders differing in body color, i.e., a white sintered powder, a minute amount of orange sintered powder and a minute amount of red sintered powder. When this luminescent material was excited by black light, a blue emission from the white powder, an orange emission from the minute amount of orange sintered powder and a red emission from the minute amount of red powder were observed.
0175This red powder was dispensed and subjected to X-ray diffraction measurement employing CuKα characteristic X-rays (wavelength: 1.54056Å). As a result, it exhibited concurrently diffraction peaks at diffraction angles (2θ) of 13.10, 18.60, 20.20, 26.38 and 28.03°.
0176The red powders of Reference Examples 31-34 were respectively taken out of the crucible and ground in a mortar in the same manner as described above. Then, the red powders were respectively excited by an emission diode exhibiting a peak wavelength of 457 nm. The emission spectrums thus obtained are shown in <figref idref="f0009">FIG. 18</figref>. In <figref idref="f0009">FIG. 18</figref>, the band exhibiting a peak at 457 nm was derived from the reflection of exciting beam. A single-band emission exhibiting a peak at a wavelength ranging from 620 to 640 nm was obtained from all of these red powders.
(Reference Example 35)
0177The same kind of raw material as that of Reference Example 31 was placed in a carbon crucible. Thereafter, the raw material was sintered for 60 hours at a temperature of 1800°C in a nitrogen atmosphere of 7.5 atm., thereby synthesizing the luminescent material of this reference example.
0178This luminescent material thus sintered was formed of a mixture of two kinds of sintered powder differing in body color, thus confirming existence of a white sintered powder and a red sintered powder. When this luminescent material was excited by black light, a blue emission from the white powder, and a red emission from the red powder were observed.
0179This red powder was then subjected to X-ray diffraction measurement employing CuKα characteristic X-rays (wavelength: 1.54056Å). As a result, it exhibited concurrently diffraction peaks at diffraction angles (2θ) of 13.12, 18.64, 20.22, 26.40 and 28.04°.
(Reference Example 36)
0180The same kind of raw material as that of Reference Example 32 was placed in a carbon crucible. Thereafter, the raw material was sintered for 60 hours at a temperature of 1800°C in a nitrogen atmosphere of 7.5 atm., thereby synthesizing the luminescent material of this reference example.
0181This luminescent material thus sintered was formed of a mixture of two kinds of sintered powder differing in body color, thus confirming existence of a white sintered powder and a red sintered powder. When this luminescent material was excited by black light, a blue emission from the white powder, and a red emission from the red powder were observed.
(Reference Example 37)
0182The same kind of raw material as that of Reference Example 33 was placed in a carbon crucible. Thereafter, the raw material was sintered for 60 hours at a temperature of 1800°C in a nitrogen atmosphere of 7.5 atm., thereby synthesizing the luminescent material of this reference example.
0183This luminescent material thus sintered was formed of a mixture of two kinds of sintered powder differing in body color, thus confirming existence of a white sintered powder and a red sintered powder. When this luminescent material was excited by black light, a blue emission from the white powder, and a red emission from the red powder were observed.
(Reference Example 38)
0184The same kind of raw material as that of Reference Example 34 was placed in a carbon crucible. Thereafter, the raw material was sintered for 60 hours at a temperature of 1800°C in a nitrogen atmosphere of 7.5 atm., thereby synthesizing the luminescent material of this reference example.
0185This luminescent material thus sintered was formed of a mixture of two kinds of sintered powder differing in body color, thus confirming existence of a white sintered powder and a red sintered powder. When this luminescent material was excited by black light, a blue emission from the white powder, and a red emission from the red powder were observed.
0186The red powders of Reference Examples 35-38 were respectively taken out of the crucible and ground in a mortar in the same manner as described above. Then, the red powders were respectively excited by an emission diode exhibiting a peak wavelength of 457 nm. The emission spectrums thus obtained are shown in <figref idref="f0010">FIG. 19</figref>. In <figref idref="f0010">FIG. 19</figref>, the band exhibiting a peak at 457 nm was derived from the reflection of exciting beam. A single-band emission exhibiting a peak at a wavelength ranging from 610 to 640 nm was obtained from all of these red powders.
(Reference Example 39)
0187SrCO<sub>3</sub>, AlN, Si<sub>3</sub>N<sub>4</sub> and Eu<sub>2</sub>O<sub>3</sub> were prepared as starting materials, and these starting materials were weighed to obtain 2.923, 1.640, 2.806 and 0.035g, respectively. Then, these starting materials were mixed together in a mortar for 20 minutes and then placed in a carbon crucible. The mixture in the crucible was then subjected to sintering in a nitrogen atmosphere of 7.5 atm. for four hours at a temperature of 1800°C, thereby synthesizing a luminescent material of this reference example.
0188This luminescent material thus sintered was formed of a mixture of sintered powders differing in body color, i.e., a white sintered powder, a minute amount of orange sintered powder and a minute amount of red sintered powder. When this luminescent material was excited by black light, a blue emission from the white powder, an orange emission from the minute amount of orange sintered powder and a red emission from the minute amount of red powder were observed.
0189The red powder of Reference Example 39 was taken out of the crucible and ground in a mortar in the same manner as described above. Then, the red powder was excited by an emission diode exhibiting a peak wavelength of 457 nm. The emission spectrum thus obtained is shown in <figref idref="f0010">FIG. 20</figref>. In <figref idref="f0010">FIG. 20</figref>, the band exhibiting a peak at 457 nm was derived from the reflection of exciting beam. A single-band emission exhibiting a peak at a wavelength ranging from 610 to 640 nm was obtained from the red powder.
0190The values of absorption coefficient, quantum yield and luminous efficiency of the yellowish green powders of Reference Examples 31-39 are summarized in the following Table 7. <tables id="tabl0007" num="0007"><table frame="all"><title>Table 7</title><tgroup cols="5"><colspec colnum="1" colname="col1" colwidth="20mm" /><colspec colnum="2" colname="col2" colwidth="36mm" /><colspec colnum="3" colname="col3" colwidth="35mm" /><colspec colnum="4" colname="col4" colwidth="33mm" /><colspec colnum="5" colname="col5" colwidth="40mm" /><thead><row><entry align="center" valign="top" /><entry align="center" valign="top">Peak wavelength (nm)</entry><entry align="center" valign="middle">Absorption coefficient</entry><entry align="center" valign="middle">Quantum efficiency</entry><entry align="center" valign="middle">Luminescence efficiency</entry></row></thead><tbody><row><entry>Ref. Ex.31</entry><entry align="center">621</entry><entry align="center">0.63</entry><entry align="center">0.52</entry><entry align="center">0.33</entry></row><row><entry>Ref. Ex.32</entry><entry align="center">625</entry><entry align="center">0.77</entry><entry align="center">0.53</entry><entry align="center">0.41</entry></row><row><entry>Ref. Ex.33</entry><entry align="center">626</entry><entry align="center">0.79</entry><entry align="center">0.53</entry><entry align="center">0.42</entry></row><row><entry>Ref. Ex.34</entry><entry align="center">646</entry><entry align="center">0.83</entry><entry align="center">0.49</entry><entry align="center">0.41</entry></row><row><entry>Ref. Ex.35</entry><entry align="center">616</entry><entry align="center">0.62</entry><entry align="center">0.40</entry><entry align="center">0.25</entry></row><row><entry>Ref. Ex.36</entry><entry align="center">623</entry><entry align="center">0.64</entry><entry align="center">0.42</entry><entry align="center">0.27</entry></row><row><entry>Ref. Ex.37</entry><entry align="center">624</entry><entry align="center">0.69</entry><entry align="center">0.44</entry><entry align="center">0.30</entry></row><row><entry>Ref. Ex.38</entry><entry align="center">637</entry><entry align="center">0.74</entry><entry align="center">0.47</entry><entry align="center">0.35</entry></row><row><entry>Ref. Ex.39</entry><entry align="center">633</entry><entry align="center">0.75</entry><entry align="center">0.46</entry><entry align="center">0.35</entry></row></tbody></tgroup></table></tables>
0191As shown in Table 7, all of the yellowish green powders of Reference Examples 31-39 were capable of exhibiting an emission wavelength falling within the range of 580 to 700 nm as they were excited by the light having a wavelength ranging from 250 to 500 nm. The absorption coefficient, quantum yield and luminous efficiency of these luminescent materials were by no means inferior to the conventional yellowish green luminescent materials such for example as Sr<sub>2</sub>Si<sub>5</sub>N<sub>8</sub>:Eu, etc.
0192Even if the exciting wavelength was changed to 254, 365, 390 or 460 nm, it was possible to confirm the emission having a peak in almost the same wavelength range as described above. Because of the facts that if the exciting wavelength is too short, the loss due to Stokes shift would become prominent and that if the exciting wavelength is too long, the excitation efficiency would be deteriorated, the exciting wavelength should preferably be confined within the range of 380 to 460 nm. Further, the peak wavelength of emission should desirably be confined to 670 nm or less.
0193With respect to the composition of red powder of Reference Example 31, it is already explained above. The red powders of other Reference Examples were also chemically analyzed to investigate the values of "a", "b", "c" and "d" in the aforementioned composition formula (B). As a result, it was found out that, in the cases of the red powders of Reference Examples 31-39, the lower limit and the upper limit of the value of (1+b)/a was 2.41 and 2.58, respectively. Further, the lower limit and the upper limit of the value of (c+d)/a was 3.48 and 4.17, respectively.
0194Based on these results, the compositions of yellowish green powders of Reference Examples 31-39 were found definable by the following general formula (3). (M<sub>1-x</sub>R<sub>x</sub>)<sub>a3</sub>AlSi<sub>b3</sub>O<sub>c3</sub>N<sub>d3</sub> (3)
0195In the general formula (3), M is at least one metallic element excluding Si and Al; R is a luminescence center element; and x, a3, b3, c3 and d3 satisfy the following relationships: <maths id="math0013"><math display="block"><mn mathvariant="normal">0</mn><mo mathvariant="normal"><</mo><mi mathvariant="normal">x</mi><mo mathvariant="normal">≤</mo><mn mathvariant="normal">1</mn><mo mathvariant="normal">,</mo><mspace width="2em" /><mn mathvariant="normal">2.4</mn><mo mathvariant="normal"><</mo><mfenced><mn mathvariant="normal">1</mn><mo mathvariant="normal">+</mo><mi mathvariant="normal">b</mi><mo></mo><mn mathvariant="normal">3</mn></mfenced><mo mathvariant="normal">/</mo><mi mathvariant="normal">a</mi><mo></mo><mn mathvariant="normal">3</mn><mo mathvariant="normal"><</mo><mn mathvariant="normal">2.6</mn></math><img file="EP2003183A1_D0013.tif" /></maths><maths id="math0014"><math display="block"><mn mathvariant="normal">3.4</mn><mo mathvariant="normal"><</mo><mfenced><mi mathvariant="normal">c</mi><mo></mo><mn mathvariant="normal">3</mn><mo mathvariant="normal">+</mo><mi mathvariant="normal">d</mi><mo></mo><mn mathvariant="normal">3</mn></mfenced><mo mathvariant="normal">/</mo><mi mathvariant="normal">a</mi><mo></mo><mn mathvariant="normal">3</mn><mo mathvariant="normal"><</mo><mn mathvariant="normal">4.2.</mn></math><img file="EP2003183A1_D0014.tif" /></maths>
0196When all of the compositions of red powders of Reference Examples 31-39 were subjected to X-ray diffraction measurement employing CuKα characteristic X-rays (wavelength: 1.54056Å), they exhibited concurrently diffraction peaks at least at diffraction angles (2θ) of 13.06-13.16, 18.58-18.68, 20.14-20.24, 26.32-26.46 and 27.98-28.10°.
(Comparative Example 1)
019726.573g of SrCO<sub>3</sub>, 23.385g of Si<sub>3</sub>N<sub>4</sub> and 3.519g of Eu<sub>2</sub>O<sub>3</sub> were prepared as starting materials, and these starting materials were mixed together in a ball mill. The resultant mixture was placed in a carbon crucible and then subjected to sintering in a nitrogen atmosphere of 7 atm. for 8 hours at a temperature of 1650°C to synthesize a luminescent material of this comparative example.
0198As a result of chemical analysis, the luminescent material of this comparative example was confirmed as having a composition represented by (Sr<sub>0.9</sub>Eu<sub>0.1</sub>)<sub>2</sub>Si<sub>5</sub>N<sub>8</sub>. The luminescent material thus obtained was a vermilion sintered body and when it was excited by black light, a red emission was observed.
(Comparative Example 2)
0199148g of SrCO<sub>3</sub> and 0.176g of Eu<sub>2</sub>O<sub>3</sub> were prepared as starting materials, and these starting materials were mixed together in a mortar. The resultant mixed powder was placed in a quartz crucible and then subjected to sintering in a H<sub>2</sub>S atmosphere of 1 atm. for one hour at a temperature of 1100°C. The sintered mixture was further powdered and blended with 2g of NH<sub>4</sub>Cl. The resultant mixture was further mixed in a mortar and sealed in a quartz tube. Thereafter, the mixture was sintered for one hour at a temperature of 1100°C in a nitrogen atmosphere of 1 atm., thereby synthesizing the luminescent material of this comparative example.
0200As a result of chemical analysis, the luminescent material of this comparative example was confirmed as having a composition represented by (Sr<sub>0.999</sub>Eu<sub>0.001</sub>)<sub>2</sub>S. The luminescent material thus obtained was a pink sintered body and when it was excited by black light, a red emission exhibiting a peak wavelength of 620 nm was observed.
(Comparative Example 3)
020117.066g of SrCO<sub>3</sub>, 8.198g of AlN, 23.759g of Si<sub>3</sub>N<sub>4</sub> and 3.590g of Eu<sub>2</sub>O<sub>3</sub> were prepared as starting materials. These starting materials were mixed, dried and ground in the same manner as Example 1. After being placed in a carbon crucible, the resultant mixture was sintered using a hot press for two hours at a press pressure of 350 MPa and a temperature of 1800°C in a nitrogen atmosphere of 3.5 atm. The sample thus sintered was formed of a sintered body having a gray-yellowish green body color and when it was excited by black light, a weak yellowish green emission was observed.
(Comparative Example 4)
0202A luminescent material was synthesized in this comparative example in the same manner as in Comparative Example 3 except that 17.693g of SrCO<sub>3</sub>, 6.148g of AlN, 29.114g of Si<sub>3</sub>N<sub>4</sub> and 3.722g of Eu<sub>2</sub>O<sub>3</sub> were employed as starting materials. The sample thus sintered was formed of a sintered body having a gray-yellowish green body color and when it was excited by black light, a weak yellowish green emission was observed.
(Comparative Example 5)
0203A raw material that had been weighed and mixed in the same manner as in Reference Example 1 was placed in a carbon crucible and sintered in the same manner as in Comparative Example 3, thereby synthesizing a luminescent material of this comparative example. The sample thus sintered was formed of a sintered body having a gray-yellowish green body color and when it was excited by black light, a weak yellowish green emission was observed.
(Comparative Example 6)
020494.27g of SrCO<sub>3</sub> powder, 7.12g of BaCO<sub>3</sub> powder, 22.835g of SiO<sub>2</sub> powder and 4.460g of Eu<sub>2</sub>O<sub>3</sub> powder were prepared as starting materials. To these starting materials, 1.8g of NH<sub>4</sub>Cl was added as a crystal growth-promoting agent. Then, these starting materials were mixed together in a ball mill.
0205The mixed raw materials thus obtained were charged into a sintering vessel and sintered under the following sintering conditions. First of all, the mixed raw materials were sintered for 3-7 hours in a reducing atmosphere of nitrogen/hydrogen at a temperature ranging from 1000 to 1600°C to prepare an Sr<sub>1.9</sub>Ba<sub>0.1</sub>SiO<sub>4</sub>:Eu luminescent material of this comparative example. The luminescent material thus sintered was formed of a sintered body having a yellow body color and when it was excited by black light, a yellow emission was observed.
0206The luminescent materials of Comparative Examples 3-5 were respectively chemically analyzed, the results being summarized in the following Table 8. In this Table 6, there are shown the values of "a", "b", "c" and "d" in the aforementioned general formula (B). <tables id="tabl0008" num="0008"><table frame="all"><title>Table 8</title><tgroup cols="5"><colspec colnum="1" colname="col1" colwidth="22mm" /><colspec colnum="2" colname="col2" colwidth="12mm" /><colspec colnum="3" colname="col3" colwidth="12mm" /><colspec colnum="4" colname="col4" colwidth="12mm" /><colspec colnum="5" colname="col5" colwidth="12mm" /><thead><row><entry align="center" valign="top" /><entry align="center" valign="top">a</entry><entry align="center" valign="top">b</entry><entry align="center" valign="top">c</entry><entry align="center" valign="top">d</entry></row></thead><tbody><row><entry>Comp. Ex.3</entry><entry>0.68</entry><entry>2.59</entry><entry>1.12</entry><entry>3.78</entry></row><row><entry>Comp. Ex.4</entry><entry>0.95</entry><entry>4.25</entry><entry>1.68</entry><entry>5.59</entry></row><row><entry>Comp. Ex.5</entry><entry>0.99</entry><entry>5.03</entry><entry>1.75</entry><entry>6.48</entry></row></tbody></tgroup></table></tables>
0207Although the luminescent materials of Comparative Examples 3-5 all comprise, as a matrix, a sialon-based compound, they fail to meet any of the conditions defined by the general formulas (1), (2) and (3). Therefore, it will be seen that these luminescent materials were all falling outside the scope of composition of luminescent material as defined by the embodiment of the present invention. It should be noted that the luminescent materials of Comparative Examples 1, 2 and 6 were all different from those comprising a sialon-based compound as a matrix.
0208The luminescent materials of Comparative Examples 3-5 were subjected to X-ray diffraction measurement employing CuKα characteristic X-rays (wavelength: 1.54056Å), the results being illustrated in <figref idref="f0011">FIG. 21</figref>. In this <figref idref="f0011">FIG. 21</figref>, the results of X-ray diffraction measurement performed on the luminescent materials of Reference Example 20 and of Example 2 are also illustrated. As shown in <figref idref="f0011">FIG. 21</figref>, since the compositions of the luminescent materials of Comparative Examples 3-5 were not confined within the aforementioned prescribed range, the luminescent materials of Comparative Examples 3-5 exhibited XRD profiles which were different from that of Reference Example 20 or of Example 2. For this reason, the luminescent materials of Comparative Examples 3-5 were supposed that they were respectively formed of a different structure from that of the luminescent material of Example 2. The structure of each of the luminescent materials of Comparative Examples 3-5 was almost identical with the pattern of S phase (JCPDS card #53-0636) shown in <figref idref="f0011">FIG. 21</figref>.
0209The luminescent materials of Comparative Examples 3-5 were respectively excited by an emission diode exhibiting a peak wavelength of 390 nm. The emission spectrums thus obtained are shown in <figref idref="f0011">FIG. 22. FIG. 22</figref> also shows the results obtained from the red powder of Reference Example 20 and from the yellowish green powder of Example 2. In <figref idref="f0011">FIG. 22</figref>, the bands each exhibiting a peak at 390 nm were derived from the reflection of exciting beam. The luminescent materials of Comparative Examples 3-5 were all very low in emission intensity.
0210As seen from the results described above, any kinds of luminescent material whose compositions fall outside the composition range of luminescent material as defined by this embodiment would have a different structure from those of the luminescent materials of this embodiment, thus failing to obtain desired emission characteristics.
0211The red powders of Reference Examples 20 and 39 were excited while increasing the temperature of these samples from room temperature to 200°C by a heater to measure any changes in emission spectrum. In this excitation, an emission diode exhibiting a peak wavelength of 458 nm was employed. <figref idref="f0012">FIG. 23</figref> shows the temperature dependency of the peak emission intensity in emission spectrum at each temperature.
0212For the purpose of comparison, the temperature dependency of the peak emission intensity of Sr<sub>2</sub>Si<sub>5</sub>N<sub>8</sub>:Eu luminescent material of Comparative Example 1 and the temperature dependency of CaS:Eu luminescent material of Comparative Example 2 are also shown in <figref idref="f0012">FIG. 23</figref>. The y-axis in <figref idref="f0012">FIG. 23</figref> represents values which were normalized on the basis of emission intensity of each of luminescent materials at room temperature, the value of which being set to one.
0213The graph of <figref idref="f0012">FIG. 23</figref> indicates that, in the cases of luminescent materials of Reference Examples 20 and 39, even under high temperature conditions of as high as 200°C, the deterioration of emission intensity thereof was minimal. It will be recognized from these results that the luminescent material according to this embodiment was excellent in temperature characteristics as compared with CaS:Eu luminescent material and also with Sr<sub>2</sub>Si<sub>5</sub>N<sub>8</sub>:Eu luminescent material which was constituted by the same nitride matrix as that of the luminescent material of this embodiment. In the graph of <figref idref="f0012">FIG. 23</figref>, only the results obtained from the luminescent materials of Reference Examples 20 and 39 are shown. However, even in the cases of luminescent materials of other examples, it was also possible to obtain more excellent temperature characteristics than those of comparative examples.
0214In the same manner as described above, the red powders of Comparative Examples 3 to 5 were also excited while increasing the temperature of these samples to measure any changes in emission spectrum. As a result, under high temperature conditions of as high as 200°C, all of these luminescent materials were deteriorated in emission intensity, thus indicating almost the same tendency as that of Comparative Example 1 or Comparative Example 2.
0215Further, the yellowish green powder of Example 1 was excited while increasing the temperature of this sample from room temperature to 200°C by a heater to measure any changes in emission spectrum. In this excitation, an emission diode exhibiting a peak wavelength of 458 nm was employed. <figref idref="f0012">FIG. 24</figref> shows the temperature dependency of the peak emission intensity in emission spectrum at each temperature.
0216For the purpose of comparison, the temperature dependency of the peak emission intensity of Sr<sub>1.9</sub>Ba<sub>0.1</sub>SiO<sub>4</sub>:Eu luminescent material of Comparative Example 6 is also shown in <figref idref="f0012">FIG. 24</figref>. The y-axis in <figref idref="f0012">FIG. 24</figref> represents values which were normalized on the basis of emission intensity of each of luminescent materials at room temperature, the value of which being set to one.
0217The graph of <figref idref="f0012">FIG. 24</figref> indicates that the luminescent material of Example 1 was minimal in deterioration of emission intensity even under high temperature condition of as high as 200°C. It will be recognized from the result thus obtained that the luminescent material of this embodiment was excellent in temperature characteristics as compared with Sr<sub>1.9</sub>Ba<sub>0.1</sub>SiO<sub>4</sub>:Eu luminescent material.
0218Further, using the luminescent material of Example 1, a light-emitting device was manufactured as shown in <figref idref="f0001">FIG. 2</figref>. When the light-emitting device thus obtained was actuated at a temperature ranging from room temperature to 150°C to measure the changes in emission efficiency with temperature, almost no deterioration in emission efficiency was caused to occur within this range of temperature. From this fact, it was confirmed that the light-emitting device according to this embodiment was provided with excellent temperature characteristics.
0219When the luminescent material of Comparative Example 3 was employed to manufacture a light-emitting device which was similar in structure as described above and the light-emitting device was tested in the same manner as described above. As a result, the emission efficiency thereof was prominently deteriorated in the aforementioned range of temperature. Even when the luminescent materials of Comparative Examples 4 and 5 were employed, almost the same result as that of the luminescent material of Comparative Example 3 was obtained. It was confirmed that even in the case of sialon-based compounds comprising an emission center element, it was impossible to secure excellent temperature characteristics unless the composition thereof was not confined to fall within the aforementioned prescribed range.
0220According to the present invention, it is possible to provide a luminescent material excellent in temperature characteristics and a light-emitting device wherein this luminescent material is employed.
32 sheets
Sheet 1 Sheet 2 Sheet 3 Sheet 4 Sheet 5 Sheet 6 Sheet 7 Sheet 8 Sheet 9 Sheet 10 Sheet 11 Sheet 12 Sheet 13 Sheet 14 Sheet 15 Sheet 16 Sheet 17 Sheet 18 Sheet 19 Sheet 20 Sheet 21 Sheet 22 Sheet 23 Sheet 24 Sheet 25 Sheet 26 Sheet 27 Sheet 28 Sheet 29 Sheet 30 Sheet 31 Sheet 32
Every citation, both ways
| Document | Relation | Office | Cited during |
|---|---|---|---|
| CN104164235A | Cited by | China | Search report |
| US9068116B2 | Cited by | United States of America | Applicant |
| CN103113883A | Cited by | China | Search report |
| US8921878B2 | Cited by | United States of America | Applicant |
| EP2426745A2 | Cited by | European Patent Office (EPO) | Search report |
| CN104080884A | Cited by | China | Search report |
| CN102952541A | Cited by | China | Search report |
| EP2597131A1 | Cited by | European Patent Office (EPO) | Search report |
| EP2727976A1 | Cited by | European Patent Office (EPO) | Search report |
| CN104204134A | Cited by | China | Search report |
| EP2562231A1 | Cited by | European Patent Office (EPO) | Search report |
| EP2597131A1 | Cited by | European Patent Office (EPO) | Search report |
| EP2426745A3 | Cited by | European Patent Office (EPO) | Search report |
| US8569943B2 | Cited by | United States of America | Applicant |
| CN103827260A | Cited by | China | Search report |
| US2003094893A1 | Cites | United States of America | Search report |
| WO2005049763A1 | Cites | World Intellectual Property Organization (WIPO) | Search report |
| US2005230689A1 | Cites | United States of America | Search report |
| WO2006003961A1 | Cites | World Intellectual Property Organization (WIPO) | Search report |
| WO2006033417A1 | Cites | World Intellectual Property Organization (WIPO) | Search report |
| WO2006033418A1 | Cites | World Intellectual Property Organization (WIPO) | Search report |
| WO2006050232A1 | Cites | World Intellectual Property Organization (WIPO) | Search report |
| WO2006072918A1 | Cites | World Intellectual Property Organization (WIPO) | Search report |
| WO2006073141A1 | Cites | World Intellectual Property Organization (WIPO) | Search report |
| WO2006080539A1 | Cites | World Intellectual Property Organization (WIPO) | Search report |
| WO2006126567A1 | Cites | World Intellectual Property Organization (WIPO) | Search report |
37 members in 4 offices; this record represents the family
Priority claims3
| Document | Office | Kind | Date |
|---|---|---|---|
| 2006065603 | Japan | – | |
| 2006065603 | Japan | A | |
| 2007054676 | Japan | W |
Members37
| Document | Office | Kind | |
|---|---|---|---|
| WO2007105631A1 | World Intellectual Property Organization (WIPO) | A1 | |
| WO2007105631A1 | World Intellectual Property Organization (WIPO) | A1 | |
| EP2003183A1This record | European Patent Office (EPO) | A1 | |
| US2009096361A1 | United States of America | A1 | |
| JPWO2007105631A1 | Japan | A1 | |
| EP2003183A4 | European Patent Office (EPO) | A4 | |
| US2011057149A1 | United States of America | A1 | |
| US2011058582A1 | United States of America | A1 | |
| US2011058583A1 | United States of America | A1 | |
| EP2308946A2 | European Patent Office (EPO) | A2 | |
| JP2011080068A | Japan | A | |
| JP2011082529A | Japan | A | |
| JP2011084741A | Japan | A | |
| JP2011116994A | Japan | A | |
| JP4719309B2 | Japan | B2 | |
| EP2308946A3 | European Patent Office (EPO) | A3 | |
| JP4762248B2 | Japan | B2 | |
| JP2011246733A | Japan | A | |
| JP2012001731A | Japan | A | |
| JP2012070014A | Japan | A | |
| JP2012109592A | Japan | A | |
| EP2003183B1 | European Patent Office (EPO) | B1 | |
| JP5058365B2 | Japan | B2 | |
| EP2518129A2 | European Patent Office (EPO) | A2 | |
| EP2518129A3 | European Patent Office (EPO) | A3 | |
| US8450923B2 | United States of America | B2 | |
| US8475680B2 | United States of America | B2 | |
| US8482192B2 | United States of America | B2 | |
| US8491817B2 | United States of America | B2 | |
| EP2308946B1 | European Patent Office (EPO) | B1 | |
| JP5319645B2 | Japan | B2 | |
| JP5323216B2 | Japan | B2 | |
| JP5337130B2 | Japan | B2 | |
| JP5454965B2 | Japan | B2 | |
| EP2518129B1 | European Patent Office (EPO) | B1 | |
| JP5586499B2 | Japan | B2 | |
| JP5696013B2 | Japan | B2 |
28 legal events, as 4 offices reported them to INPADOC
Over the term
Point at a mark for the eventEvents
| Event | Code | Office | |
|---|---|---|---|
| Annual fee paid to national office [announced via postgrant information from national office to epo]GrantedPGFP | PGFP | EP | |
| Annual fee paid to national office [announced via postgrant information from national office to epo]GrantedPGFP | PGFP | EP | |
| Annual fee paid to national office [announced via postgrant information from national office to epo]GrantedPGFP | PGFP | EP | |
| Annual fee paid to national office [announced via postgrant information from national office to epo]GrantedPGFP | PGFP | EP | |
| Fee paymentPLFP | PLFP | FR | |
| Fee paymentPLFP | PLFP | FR | |
| Fee paymentPLFP | PLFP | FR | |
| No opposition filed against granted patent, or epo opposition proceedings concluded without decisionGrantedR097 | R097 | DE | |
| No opposition filedOpposition26N | 26N | EP | |
| No opposition filed within time limitOppositionORIGINAL CODE: 0009261PLBE | PLBE | EP | |
| Information on the status of an ep patent application or granted ep patentGrantedSTATUS: NO OPPOSITION FILED WITHIN TIME LIMITSTAA | STAA | EP | |
| Dpma publication of mentioned ep patent grantGrantedR096 | R096 | DE | |
| Designated contracting statesAK | AK | EP | |
| European patent grantedGrantedFG4D | FG4D | GB | |
| Request for extension of the european patent (deleted)DAX | DAX | EP | |
| (expected) grantORIGINAL CODE: 0009210GRAA | GRAA | EP | |
| Grant fee paidORIGINAL CODE: EPIDOSNIGR3GRAS | GRAS | EP | |
| Despatch of communication of intention to grant a patentORIGINAL CODE: EPIDOSNIGR1GRAP | GRAP | EP | |
| Information provided on ipc code assigned before grantRIC1 | RIC1 | EP | |
| Information provided on ipc code assigned before grantRIC1 | RIC1 | EP | |
| Amendment of ipc main classPREVIOUS MAIN CLASS: C09K0011640000R079 | R079 | DE | |
| First examination report despatched17Q | 17Q | EP | |
| Supplementary search report drawn up and despatchedA4 | A4 | EP | |
| Party data changed (applicant data changed or rights of an application transferred)RAP1 | RAP1 | EP | |
| Designated contracting states (corrected)RBV | RBV | EP | |
| Request for examination filed17P | 17P | EP | |
| Designated contracting statesAK | AK | EP | |
| Public reference made under article 153(3) epc to a published international application that has entered the european phaseORIGINAL CODE: 0009012PUAI | PUAI | EP |
Numbers
- Publication
- 2003183
- Application
- 77381614
Titles3
- German
- LEUCHTSTOFF UND LEUCHTVORRICHTUNG
- English
- PHOSPHOR AND LIGHT-EMITTING DEVICE
- French
- PHOSPHORE ET DISPOSITIF LUMINESCENT
Classification
- CPC, 3
- C09K11/0883
- C09K11/77348
- H10H20/8512
- IPC, 3
- C09K11 64
- C09K11 08
- C09K11 77
Designated states3
- Contracting states, 3
- Germany
- France
- United Kingdom