2-cyanoacrylate composition

TECHNICAL FIELD

0001The present invention relates to a 2-cyanoacrylate composition, particularly to a 2-cyanoacrylate composition that has an excellent adhesiveness to poorly adherent materials and porous materials and a good light stability, and the composition is useful especially as an instantaneous adhesive.

BACKGROUND ART

0002Cyanoacrylate adhesives which contain a 2-cyanoacrylate as a main ingredient are widely used as instantaneous adhesives in various industrial fields such as electronic, electric and automotive fields and in leisure and household applications since they are polymerized and hardened in a short time by anionic species such as moisture on an adherend surface or in the air thanks to their high anionic polymerizability, thereby bonding various materials to each other.

0003However, they have been disadvantageous in that they are insufficient in speed of adhesion to poorly adherent materials such as polyacetals, FRPs, chrome platings and EPDM rubbers, and porous materials such as leathers, wood and paper.

0004As a method for solving the above problems, it has been proposed that crown ethers as described in Patent Document 1, polyethylene glycol derivatives as described in Patent Document 2 or the like should be incorporated as hardening accelerators in 2-cyanoacrylates. Thus, adhesive compositions having an adhesion speed high enough for the above materials have been obtained.

0005However, the adhesive compositions which contain such hardening accelerators are disadvantageous in that they are ease to thicken and gel when left at a window exposed to sunlight or under a fluorescent lamp for a long period.

0006As a result of investigating the cause, the present inventors have presumed that the following phenomenon occurs. Hydroquinone is commonly used as a radical stabilizer in cyanoacrylate adhesives. When radicals are generated in the system by the action of light, hydroquinone may capture the radical to form a phenoxy radical. Since the phenoxy radical is unstable, it may abstract hydrogen from a crown ether or a polyethylene glycol. The resulting radical may react with oxygen in the system to generate a peroxide. Cleavage of the peroxide may induce radical chain reactions, thereby finally leading to radical polymerization of 2-cyanoacrylates.

0007On the other hand, an example using another radical stabilizer instead of hydroquinone is disclosed in Patent Document 3 in which a phenolic antioxidant is used. This avoids generation of benzoquinone which is toxic and medically undesirable, when a medical-grade 2-cyanoacrylate composition is irradiated with γ-ray for sterilization. This neither improves light stability in ordinary use, nor discloses that a hardening accelerator is used together. <ul id="ul0001" list-style="none"><li>Patent Document 1: Japanese Patent Laid-Open (Kokai) No. <patcit id="pcit0001" dnum="JP53129231A"><text>53-129231</text></patcit></li><li>Patent Document 2: Japanese Patent Laid-Open (Kokai) No. <patcit id="pcit0002" dnum="JP54028342A"><text>54-28342</text></patcit></li><li>Patent Document 3: Japanese Patent Laid-Open (Kokai) No. <patcit id="pcit0003" dnum="JP7252455A"><text>7-252455</text></patcit></li></ul>

DISCLOSURE OF THE INVENTION

PROBLEMS TO BE SOLVED BY THE INVENTION

0008It is an object of the present invention to solve the above-mentioned problems, that is, to provide a 2-cyanoacrylate composition useful as cyanoacrylate adhesives, which maintain a high speed of adhesion to poorly adherent materials and porous materials, and have an improved light stability.

MEANS FOR SOLVING THE PROBLEMS

0009As a result of intensive studies on methods for improving the light stability of the 2-cyanoacrylate composition, the present inventors have found that incorporation of a hindered phenol compound having a specific structure (hereinafter, referred to as "a specific hindered phenol compound") as a radical stabilizer can solve the problems. Thus, the present invention has the following constitution. <ol id="ol0001" compact="compact"><li>1) A 2-cyanoacrylate composition which comprises:a 2-cyanoacrylate;(1) a hindered phenol compound represented by the following general formula (1): <chemistry id="chem0001" num="0001"><img file="EP1908786B1_D0001.tif" /></chemistry> wherein R₁ is a linear or branched alkylene group having 1 to 4 carbon atoms; R₂ and R₃ are each independently a linear, branched or cyclic alkyl group having 1 to 10 carbon atoms; R₄ and R₅ are each independently a linear or branched alkyl group having 1 to 4 carbon atoms; and R₆ is a hydrogen atom, an alkyl group having 1 to 20 carbon atoms, an alkenyl group having 2 to 20 carbon atoms or an acyl group having 2 to 20 carbon atoms; and (2) a compound having a clathrating ability.</li><li><smallcaps>2)</smallcaps> The 2-cyanoacrylate composition according to the above item 1), <b>characterized in that</b> the compound having a clathrating ability is a crown ether, a polyalkylene glycol or a derivative of these.</li><li>3) The 2-cyanoacrylate composition according to the above item 2), in which the compound having a clathrating ability is 15-crown-5.</li><li>4) The 2-cyanoacrylate composition according to any one of the above items 1) to 3), in which the hindered phenol compound is 2,2'-methylene-bis-(4-methyl-6-t-butylphenol).</li></ol>

EFFECTS OF THE INVENTION

0010The 2-cyanoacrylate composition of the present invention has advantages of maintaining a high speed of adhesion to poorly adherent materials and porous materials and having a good light stability. This is presumably because radicals from the specific hindered phenol compound are more stable than phenoxy radicals generated from hydroquinone, and thus hardly cause hydrogen abstraction from crown ethers or polyethylene glycols.

BEST MODE FOR CARRYING OUT THE INVENTION

00112-Cyanoacrylates used in the present invention include methyl-2-cyanoacrylate, ethyl-2-cyanoacrylate, propyl-2-cyanoacrylate, isopropyl-2-cyanoacrylate, butyl-2-cyanoacrylate, isobutyl-2-cyanoacrylate, amyl-2-cyanoacrylate, hexyl-2-cyanoacrylate, cyclohexyl-2-cyanoacrylate, octyl-2-cyanoacrylate, 2-ethylhexyl-2-cyanoacrylate, allyl-2-cyanoacrylate, benzyl-2-cyanoacrylate, methoxyethyl-2-cyanoacrylate, ethoxyethyl-2-cyanoacrylate, methoxypropyl-2-cyanoacrylate, tetrahydrofurfuryl-2-cyanoacrylate, and the like. These 2-cyanoacrylates may be used not only singly but also as a mixture of two or more.

0012Among them, methyl-2-cyanoacrylate, ethyl-2-cyanoacrylate and isopropyl-2-cyanoacrylate are preferable ones for making cyanoacrylate adhesives.

0013The specific hindered phenol compound used in the present invention is represented by the above general formula (1).

0014As to R₁ of the general formula (1), the linear or branched alkylene groups having 1 to 4 carbon atoms include methylene, ethylene, ethylidene, propylene, butylidnen, butylene, and the like; R₁ is preferably methylene.

0015As to R₂ and R₃ of the general formula (1), the linear, branched or cyclic alkyl groups having 1 to 10 carbon atoms include methyl, ethyl, n-propyl, t-butyl, t-pentyl, cyclohexyl, methylcyclohexyl, and the like; R₂ and R₃ are each preferably a t-butyl group.

0016As to R₄ and R₅ of the general formula (1), the linear or branched alkyl groups having 1 to 4 carbon atoms include methyl, ethyl, n-propyl, t-butyl, and the like; R₄ and R₅ are each preferably a methyl group.

0017As to R₆ of the general formula (1), the alkyl groups having 1 to 20 carbon atoms include methyl, ethyl, n-propyl, n-butyl, n-pentyl, n-hexyl, n-heptyl, n-octyl n-nonyl, and the like; the alkenyl groups having 2 to 20 carbon atoms include vinyl, allyl, acryl, and the like; the acyl groups having 2 to 20 carbon atoms include acetyl, benzoyl, and the like; R₆ is preferably a hydrogen atom.

0018Specific examples of the specific hindered phenol compound used in the present invention include, for example, 2,2'-methylene-bis-(4-methyl-6-t-butylphenol), 2,2'-methylene-bis-(4-ethyl-6-t-butylphenol), 2,2'-methylene-bis-(4-methyl-6-cyclohexylphenol), 2,2'-methylene-bis-(6-1-methylcyclohexyl)-p-cresol, 2,2'-ethylidene-bis-(2,4-methyl-6-t-butylphenol), 2,2'-butylidene-bis-(2-t-butyl-4-methylphenol), 2-t-butyl-6-(3'-t-butyl-5'-methyl-2'-hydroxybenzyl)-4-methylphenyl acrylate, and the like. These specific hindered phenol compounds may be used singly or as a mixture of two or more. Among them, 2,2'-methylene-bis-(4-methyl-6-t-butylphenol), 2,2'-methylene-bis-(4-ethyl-6-t-butylphenol), 2,2'-methylene-bis-(4-methyl-6-cyclohexylphenol) and 2-t-butyl-6-(3'-t-butyl-5'-methyl-2'-hydroxybenzyl)-4-methylphenyl acrylate are preferable because these have an excellent light stabilizing property in 2-cyanoacrylate compositions; 2,2'-methylene-bis-(4-methyl-6-t-butylphenol) is further preferable.

0019Hydroquinone, hydroquinone monomethyl ether, catechol, pyrogallol or the like, which has been conventionally used as a radical polymerization inhibitor, may be used together.

0020The amount of the specific hindered phenol compound used in the present invention is 100 to 10,000 ppm by mass, preferably 500 to 5,000 ppm by mass relative to the 2-cyanoacrylate. When the amount is less than 100 ppm by mass, sufficient light stability cannot be obtained; and when the amount exceeds 10,000 ppm by mass, curing rate may be lowered.

0021The compound having a clathrating ability includes polyalkylene oxides, crown ethers, silacrown ethers, Calixarenes, cyclodextrins, pyrogallolic cyclic compounds, or the like. Crown ethers, polyalkylene glycols or derivatives of these are preferable because these have an excellent hardening acceleration effect. Among the polyalkylene glycols, polyethylene glycols are preferable. Specifically, crown ethers include, for example, 18-crown-6, 15-crown-5, 12-crown-4, benzo-18-crown-6, dibenzo-18-crown-6, dicyclohexano-24-crown-8, 2-hydroxymethyl-18-crown-6, benzo-15-crown-5, and the like. Polyethylene glycols and their derivatives include, for example, polyethylene glycols, polyethylene glycol monoacrylates, polyethylene glycol diacrylates, polyethylene glycol monomethacrylates, polyethylene glycol dimethacrylates, monomethoxy polyethylene glycol monomethacrylates, dimethoxy polyethylene glycols, and the like. Among these compounds having a clathrating ability, 12-crown-4, 15-crown-5 and 18-crown-6 are preferable because these have a great hardening acceleration effect; 15-crown-5 is further preferable. These compounds having a clathrating ability may be used singly or as a mixture of two or more.

0022The amount of the compound having a clathrating ability is preferably 50 ppm by mass to 5.0 % by mass, further preferably 100 ppm by mass to 2.0 % by mass relative to the 2-cyanoacrylate. When the amount is less than 50 ppm by mass, a sufficient speed of adhesion to poorly adherent materials and porous materials cannot be obtained. When the amount exceeds 5.0 % by mass, storage stability may be remarkably deteriorated.

0023The 2-cyanoacrylate composition of the present invention may be supplemented, for the purpose of improving the storage stability, with an anionic polymerization inhibitor such as sulfur dioxide, p-toluenesulfonic acid, methanesulfonic acid, propanesultone and a boron trifluoride complex in an arbitrary amount. Further, according to the purpose, a thickener, plasticizer, thixotropic agent, adhesion promoter, crosslinking agent, dye, perfume or the like may be added.

EXAMPLES

0024Hereinafter, the present invention will be further described in detail by way of examples and comparative examples, but the present invention is not limited thereto. Evaluation method for light stability was as follows: a polyethylene vessel was charged with 2 g of an adhesive composition obtained in each of the examples and comparative examples, which was then irradiated with a solar light lamp (Daiwa Lighting Corporation; Sun Ream Light TDL-150) at an illuminance of 0.2 mW/cm² (405 nm) under a temperature of 23°C and a humidity of 50%. The number of days until gelation occurred was counted. Speed of adhesion to acid paper was measured according to JIS-K-6861. Herein, three drops of an adhesive sample were dropped on acid paper of 0.3 mm in thickness as a test piece; a second test piece was bonded thereto whilst stood upright; and the time required till the second test piece came not to fall was measured with a stopwatch.

Examples 1 to 10 and Comparative Examples 1 to 12

0025To ethyl-2-cyanoacrylate, were added 20 ppm by weight of sulfur dioxide as an anionic polymerization inhibitor, and a hindered phenol compound and a compound having a clathrating ability which were compounds shown in Table 1 or 2 together with addition amounts thereof, to prepare each adhesive composition. The results of the evaluation described above are shown in Tables 1 and 2. A to D in the Tables denote as follows. A: 15-crown-5 B: 12-crown-4 C: monomethacrylate of polyethylene glycol (400) monoethyl ether D: polyethylene glycol (1,000) dimethacrylate <tables id="tabl0001" num="0001"><table frame="all"><title>Table 1</title><tgroup cols="7"><colspec colnum="1" colname="col1" colwidth="12mm" /><colspec colnum="2" colname="col2" colwidth="31mm" /><colspec colnum="3" colname="col3" colwidth="25mm" /><colspec colnum="4" colname="col4" colwidth="24mm" /><colspec colnum="5" colname="col5" colwidth="24mm" /><colspec colnum="6" colname="col6" colwidth="27mm" /><colspec colnum="7" colname="col7" colwidth="26mm" /><thead><row><entry valign="top" /><entry valign="top">Hindered phenol compound or hydroquinone</entry><entry valign="top">Content (ppm by mass) of the hindered phenol compound or hydroquinone</entry><entry valign="top">Compound having clathrating ability</entry><entry valign="top">Content (ppm by mass) of the compound having clathrating ability</entry><entry valign="top">Light stability (gelling days)</entry><entry valign="top">Adhesion speed (sec)</entry></row></thead><tbody><row><entry>Ex. 1</entry><entry>2,2'-methylene-bis-(4-methyl-6-t-butylphenol)</entry><entry align="right">780</entry><entry align="right">A</entry><entry align="right">1000</entry><entry align="right">12</entry><entry align="right">15</entry></row><row><entry>Ex. 2</entry><entry>same as above</entry><entry align="right">3100</entry><entry align="right">A</entry><entry align="right">1000</entry><entry align="right">27</entry><entry align="right">15</entry></row><row><entry>Ex. 3</entry><entry>2-t-butyl-6-(3'-t-butyl-5'-methyl-2'-hydroxybenzyl)-4-methylphenyl acrylate</entry><entry align="right">3600</entry><entry align="right">A</entry><entry align="right">1000</entry><entry align="right">22</entry><entry align="right">15</entry></row><row><entry>Ex. 4</entry><entry>2,2'-methylene-bis-(4-ethyl-6-t-butylphenol)</entry><entry align="right">840</entry><entry align="right">A</entry><entry align="right">1000</entry><entry align="right">8</entry><entry align="right">15</entry></row><row><entry>Ex. 5</entry><entry>2,2'-methylene-bis-(4-methyl-6-cyclohexylphenol)</entry><entry align="right">3500</entry><entry align="right">A</entry><entry align="right">1000</entry><entry align="right">8</entry><entry align="right">15</entry></row><row><entry>Ex. 6</entry><entry>2,2'-methylene-bis-(4-methyl-6-t-butylphenol)</entry><entry align="right">780</entry><entry align="right">B</entry><entry align="right">5000</entry><entry align="right">13</entry><entry align="right">10</entry></row><row><entry>Ex. 7</entry><entry>same as above</entry><entry align="right">780</entry><entry align="right">C</entry><entry align="right">5000</entry><entry align="right">17</entry><entry align="right">45</entry></row><row><entry>Ex. 8</entry><entry>same as above</entry><entry align="right">780</entry><entry align="right">D</entry><entry align="right">5000</entry><entry align="right">16</entry><entry align="right">15</entry></row></tbody></tgroup><tgroup cols="7" rowsep="0"><colspec colnum="1" colname="col1" colwidth="12mm" /><colspec colnum="2" colname="col2" colwidth="31mm" /><colspec colnum="3" colname="col3" colwidth="25mm" /><colspec colnum="4" colname="col4" colwidth="24mm" /><colspec colnum="5" colname="col5" colwidth="24mm" /><colspec colnum="6" colname="col6" colwidth="27mm" /><colspec colnum="7" colname="col7" colwidth="26mm" /><tbody><row><entry namest="col1" nameend="col7" align="justify">Note: "Ex." means Example.</entry></row></tbody></tgroup></table></tables><tables id="tabl0002" num="0002"><table frame="all"><title>Table 2</title><tgroup cols="7"><colspec colnum="1" colname="col1" colwidth="22mm" /><colspec colnum="2" colname="col2" colwidth="35mm" /><colspec colnum="3" colname="col3" colwidth="25mm" /><colspec colnum="4" colname="col4" colwidth="21mm" /><colspec colnum="5" colname="col5" colwidth="22mm" /><colspec colnum="6" colname="col6" colwidth="21mm" /><colspec colnum="7" colname="col7" colwidth="23mm" /><thead><row><entry valign="top" /><entry valign="top">Hindered phenol compound or hydroquinone</entry><entry valign="top">Content (ppm by mass) of the hindered phenol compound or hydroquinone</entry><entry valign="top">Compound having clathrating ability</entry><entry valign="top">Content (ppm by mass) of the compound having clathrating ability</entry><entry valign="top">Light stability (gelling days)</entry><entry valign="top">Adhesion speed (sec)</entry></row></thead><tbody><row><entry>Comp. Ex. 1</entry><entry>Hydroquinone</entry><entry align="right">500</entry><entry align="right">A</entry><entry align="right">1000</entry><entry align="right">3</entry><entry align="right">15</entry></row><row><entry>Comp. Ex. 2</entry><entry>Hydroquinone</entry><entry align="right">500</entry><entry align="right">B</entry><entry align="right">5000</entry><entry align="right">4</entry><entry align="right">10</entry></row><row><entry>Comp. Ex. 3</entry><entry>Hydroquinone</entry><entry align="right">500</entry><entry align="right">C</entry><entry align="right">5000</entry><entry align="right">5</entry><entry align="right">45</entry></row><row><entry>Comp. Ex. 4</entry><entry>Hydroquinone</entry><entry align="right">500</entry><entry align="right">D</entry><entry align="right">5000</entry><entry align="right">5</entry><entry align="right">15</entry></row><row><entry>Comp. Ex. 5</entry><entry>2,6'-di-t-butyl-4-methylphenol</entry><entry align="right">1000</entry><entry align="right">A</entry><entry align="right">1000</entry><entry align="right">3</entry><entry align="right">15</entry></row><row><entry>Comp. Ex. 6</entry><entry>Tetrakis-[methylene-3-(3',5'-di-t-butyl-4'-hydroxyphenyl)propionate]-methane</entry><entry align="right">1300</entry><entry align="right">A</entry><entry align="right">1000</entry><entry align="right">2</entry><entry align="right">15</entry></row><row><entry>Comp. Ex. 7</entry><entry>4,4'-butylidene-bis-(3-methyl-6-t-butylphenol)</entry><entry align="right">780</entry><entry align="right">A</entry><entry align="right">1000</entry><entry align="right">2</entry><entry align="right">15</entry></row><row><entry>Comp. Ex. 8</entry><entry>4,4'-methylene-bis-(2,6-di-t-butylphenol)</entry><entry align="right">960</entry><entry align="right">A</entry><entry align="right">1000</entry><entry align="right">2</entry><entry align="right">15</entry></row><row><entry>Comp. Ex. 9</entry><entry>2,2'-methylene-bis-(4-methylphenol)</entry><entry align="right">1000</entry><entry align="right">A</entry><entry align="right">1000</entry><entry align="right">2</entry><entry align="right">15</entry></row><row><entry>Comp. Ex. 10</entry><entry>Hydroquinone</entry><entry align="right">500</entry><entry align="right">none</entry><entry align="right" /><entry align="right">8</entry><entry align="right">120 or more</entry></row><row><entry>Comp. Ex. 11</entry><entry>2,2'-methylene-bis-(4-methyl-6-t-butylphenol)</entry><entry align="right">780</entry><entry align="right">none</entry><entry align="right" /><entry align="right">25</entry><entry align="right">120 or more</entry></row><row><entry>Comp. Ex. 12</entry><entry>none</entry><entry align="right" /><entry align="right">A</entry><entry align="right">1000</entry><entry align="right">1</entry><entry align="right">15</entry></row><row><entry>Ex. 9</entry><entry>2,2'-methylene-bis-(4-methyl-6-t-butylphenol)</entry><entry align="right">50</entry><entry align="right">A</entry><entry align="right">1000</entry><entry align="right">3</entry><entry align="right">15</entry></row><row><entry>Ex. 10</entry><entry>same as above</entry><entry align="right">12000</entry><entry align="right">A</entry><entry align="right">1000</entry><entry align="right">50</entry><entry align="right">120</entry></row></tbody></tgroup><tgroup cols="7" rowsep="0"><colspec colnum="1" colname="col1" colwidth="22mm" /><colspec colnum="2" colname="col2" colwidth="35mm" /><colspec colnum="3" colname="col3" colwidth="25mm" /><colspec colnum="4" colname="col4" colwidth="21mm" /><colspec colnum="5" colname="col5" colwidth="22mm" /><colspec colnum="6" colname="col6" colwidth="21mm" /><colspec colnum="7" colname="col7" colwidth="23mm" /><tbody><row><entry namest="col1" nameend="col7" align="justify">Note: "Comp. Ex." means Comparative Example, and "Ex." means Example.</entry></row></tbody></tgroup></table></tables>

Examples 11 to 15

0026Adhesive compositions were prepared under the same conditions as in Example 1, except that the addition amounts of the compounds A to D having a clathrating ability were all 1,000 ppm. The results of adhesion tests described before are shown in Table 3. <tables id="tabl0003" num="0003"><table frame="all"><title>Table 3</title><tgroup cols="6"><colspec colnum="1" colname="col1" colwidth="14mm" /><colspec colnum="2" colname="col2" colwidth="30mm" /><colspec colnum="3" colname="col3" colwidth="31mm" /><colspec colnum="4" colname="col4" colwidth="32mm" /><colspec colnum="5" colname="col5" colwidth="31mm" /><colspec colnum="6" colname="col6" colwidth="31mm" /><thead><row><entry valign="top" /><entry valign="top">Hindered phenol compound</entry><entry valign="top">Content (ppm by mass) of the hindered phenol compound</entry><entry valign="top">Compound having clathrating ability</entry><entry valign="top">Content (ppm by mass) of the compound having clathrating ability</entry><entry valign="top">Adhesion speed (sec))</entry></row></thead><tbody><row><entry>Ex. 11</entry><entry>2,2'-methylene-bis-(4-methyl-6-t-butylphenol)</entry><entry align="right">780</entry><entry align="right">A</entry><entry align="right">1000</entry><entry align="right">15</entry></row><row><entry>Ex. 12</entry><entry>same as above</entry><entry align="right">same as above</entry><entry align="right">B</entry><entry align="right">1000</entry><entry align="right">20</entry></row><row><entry>Ex. 13</entry><entry>same as above</entry><entry align="right">same as above</entry><entry align="right">C</entry><entry align="right">1000</entry><entry align="right">120</entry></row><row><entry>Ex. 14</entry><entry>same as above</entry><entry align="right">same as above</entry><entry align="right">D</entry><entry align="right">1000</entry><entry align="right">45</entry></row></tbody></tgroup></table></tables>

0027As is clear from Table 2, the adhesive compositions containing hydroquinone as a radical stabilizer exhibit an improved adhesiveness but become poor in light stability, when the compositions contain a compound having a clathrating ability together (Comparative Examples 1 to 4 and 10).

0028When the adhesive compositions contain, instead of hydroquinone, compounds other than the specific hindered phenol compounds of the present invention, namely, when hindered phenol compounds having one aromatic ring such as 2,6'-di-t-butyl-4-methylphenol are used (Comparative Examples 5 and 6), when hindered phenol compounds in which two aromatic rings are bonded together at para-positions relative to the phenolic hydroxyl groups thereof are used (Comparative Examples 7 and 8), and also when a compound in which non-hindered phenolic hydroxyl-containing aromatic rings are bonded together at ortho-positions relative to the hydroxyl groups thereof are used (Comparative Example 9), light stability is not improved.

0029By contrast, when the specific hindered phenol compounds of the present invention are used (Examples 1 to 8), light stability is greatly improved.

0030However, when the concentration of the specific hindered phenol compound is less than 100 ppm by weight, a sufficient light stability cannot be obtained (Example 9); and when the concentration of the specific hindered phenol compound exceeds 10,000 ppm by weight, a good light stability is obtained, but adhesiveness was lowered (Example 10).

0031The present invention has been described in detail referring to specified embodiments, but it will be obvious to those skilled in the art that various changes and modifications may be made without departing from the spirit and the scope of the present invention.

0032The present application is based on a Japanese Patent Application (Japanese Patent Application No. <patcit id="pcit0004" dnum="JP2005156636A"><text>2005-156636</text></patcit>) filed on May 30, 2005, the content of which is incorporated herein by reference.

INDUSTRIAL APPLICABILITY

0033Since the 2-cyanoacrylate compositions provided by the present invention have an excellent adhesiveness to poorly adherent materials and porous materials, and have a good light stability, they can be used as instantaneous adhesives and fillers having adhesiveness and storage stability that have not conventionally been available.