Organic electroluminescence device

0001This application claims the benefit of the Korean Patent Application No. 10-2004-0000624, filed on January 6, 2004, which is hereby incorporated by reference as if fully set forth herein.

<u>BACKGROUND OF THE INVENTION</u>

<u>Field of the Invention</u>

0002The present invention relates to an organic electroluminescence device.

<u>Background of the Related Art</u>

0003With the recent trend of a display device' s growing in size, the need for a flat display device occupying a small space is increasing. As one of such flat display devices, the technology of organic electroluminescence device, known as an organic light emitting diode (OLED), has been developed rapidly, and a variety of sample products have been already released.

0004An organic electroluminescence device includes an organic film which is formed between an electron injecting electrode(cathode) and a hole injecting electrode(anode), and emits light generated upon extinction after electrons and holes are paired. The device can be formed on a flexible transparent substrate, such as plastic, can be driven at a lower voltage (below 10V) than a plasma display panel or inorganic electroluminescence(EL) display is, has relatively low power consumption, and has a superior color sense. Further, the organic electroluminescence(EL) device can represent three colors of green, blue and red, and thus is drawing a great deal of attention as a next-generation full-color display device.

0005Here, the procedure of fabricating an organic electroluminescence device will be described briefly.

0006(1) Firstly, an anode material is coated on a transparent substrate. Indium tin oxide(ITO) is often used as the anode material.

0007(2) A hole injecting layer(HIL) is coated thereon. Copper phthalocyanine(CuPC)is mainly used as the hole injecting layer at a thickness of 10 to 30nm.

0008(3) Then, a hole transport layer(HTL) is coated. 4.4' -bis[N-(1-naphthyl)-N-phentylamino]-biphenyl(NPB) is deposited and coated at 30 to 60nm as the hole transport layer.

0009(4) An organic emitting layer is formed thereon. At this moment, a dopant is added thereto as needed. In case of green luminescence, tris(8-hydroxy-quinolate)aluminum(Alq3) is deposited at a thickness of 30 to 60nm as the organic emitting layer, and MQD(N-methyl quinacridone) is commonly used as the dopant.

0010(5) An electron transport layer(ETL) or electron injecting layer(EIL) are consecutively coated thereon, or an electron injecting transport layer is formed thereon. In case of green luminescence, Alq3 of the above (4) has a good electron transport capability, and thus it is often the case that no electron injecting/transport layer is used.

0011(6) Next, a cathode is coated, and finally a protecting layer is coated.

0012In the above structure, blue, green and red light emitting devices each can be realized depending on how a light emitting layer is formed.

0013The organic electroluminescence device forms excitons by the combination of holes from the hole transport layer and electrons from the electron transport layer. At this time, the excitons are protons that conduct heat without being accompanied by the movement of an electric charge in a semiconductor or insulating body.

0014The excitons thus generated are dispersed a relatively long distance before extinction, and thus increases the possibility of some parts of the excitons being dispersed out of the light emitting layer. In some cases, the excitons are dispersed and quenched by the anode. To reduce this phenomenon, a hole blocking layer is used which can disperse electrons, substantially support the dispersion of excitons, and substantially prevent the dispersion of holes.

0015However, the hole blocking layer according to the prior art is low in stability, and thus is unable to prevent the quenching of the exictons to a satisfying level.

<u>SUMMARY OF THE INVENTION</u>

0016Accordingly, the present invention is directed to an organic electroluminescence device that substantially obviates one or more problems due to limitations and disadvantages of the related art.

0017An object of the present invention is to provide an organic electroluminescence device which is suitable for phosphorescence and excellent in luminance and driving characteristics by comprising a hole blocking layer having an excellent stability disposed between an electron injecting electrode (cathode) and a hole injecting electrode (anode).

0018The organic electroluminescence device of the present invention comprises an anode, a hole injecting layer, a hole transport layer, an emitting layer, a hole blocking layer, an electron transport layer, an electron injecting layer and a cathode, the material for the hole blocking layer is expressed by the following chemical formula 1: <chemistry id="chem0001" num="0001"><img file="EP1553155A1_D0001.tif" /></chemistry>

<u>DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS</u>

0019Additional advantages, objects, and features of the invention will be set forth in part in the description which follows and in part will become apparent to those having ordinary skill in the art upon examination of the following or may be learned from practice of the invention.

0020The organic electroluminescence device of the present invention comprises an anode, a hole injecting layer, a hole transport layer, an emitting layer, a hole blocking layer, an electron transport layer, an electron injecting layer and a cathode, the material for the hole blocking layer is expressed by the following chemical formula 1: <chemistry id="chem0002" num="0002"><img file="EP1553155A1_D0002.tif" /></chemistry> wherein A is selected from the group consisting of a substituted or non-substituted aromatic group, a hetero ring group, a substituted or non-substituted phenyl, biphenyl, pyridyl, bipyridyl, naphthyl, binaphthyl, quinoline, isoquinoline, anthracene, phenanthraene and the like. The substituent on the substituted aromatic group or hetero ring group is selected from the group consisting of alkyl, allyl, alkoxy, halogene, cyano and the like, or the group consisting of methyl, ethyl, isopropyl, phenyl, naphtyl, methoxy, ethoxy, fluoro, chloro, cyano and the like.

0021A is expressed by one of the following chemical formulae 2: <chemistry id="chem0003" num="0003"><img file="EP1553155A1_D0003.tif" /></chemistry><chemistry id="chem0004" num="0004"><img file="EP1553155A1_D0004.tif" /></chemistry><chemistry id="chem0005" num="0005"><img file="EP1553155A1_D0005.tif" /></chemistry><chemistry id="chem0006" num="0006"><img file="EP1553155A1_D0006.tif" /></chemistry><chemistry id="chem0007" num="0007"><img file="EP1553155A1_D0007.tif" /></chemistry><chemistry id="chem0008" num="0008"><img file="EP1553155A1_D0008.tif" /></chemistry> and the material for the hole blocking layer is expressed by one of the following chemical formulae 3: <chemistry id="chem0009" num="0009"><img file="EP1553155A1_D0009.tif" /></chemistry><chemistry id="chem0010" num="0010"><img file="EP1553155A1_D0010.tif" /></chemistry><chemistry id="chem0011" num="0011"><img file="EP1553155A1_D0011.tif" /></chemistry><chemistry id="chem0012" num="0012"><img file="EP1553155A1_D0012.tif" /></chemistry><chemistry id="chem0013" num="0013"><img file="EP1553155A1_D0013.tif" /></chemistry><chemistry id="chem0014" num="0014"><img file="EP1553155A1_D0014.tif" /></chemistry><chemistry id="chem0015" num="0015"><img file="EP1553155A1_D0015.tif" /></chemistry><chemistry id="chem0016" num="0016"><img file="EP1553155A1_D0016.tif" /></chemistry><chemistry id="chem0017" num="0017"><img file="EP1553155A1_D0017.tif" /></chemistry><chemistry id="chem0018" num="0018"><img file="EP1553155A1_D0018.tif" /></chemistry><chemistry id="chem0019" num="0019"><img file="EP1553155A1_D0019.tif" /></chemistry><chemistry id="chem0020" num="0020"><img file="EP1553155A1_D0020.tif" /></chemistry><chemistry id="chem0021" num="0021"><img file="EP1553155A1_D0021.tif" /></chemistry>

0022At this time, the method of synthesis of some parts (BL-1, BL-25) of the hole blocking material as shown in formulae 3 will be described.

00231. Synthesis of Phenanthryl Boronic Acid <chemistry id="chem0022" num="0022"><img file="EP1553155A1_D0022.tif" /></chemistry>    In a well-dried three-neck round bottom flask, 9-bromophnanthrene (2.57g, 0.01mol) was dissolved in 100ml of anhydrous diethyl ether, and a -78°C container was disposed. To this mixture, n-BuLi (2.5M in hexane, 4mL, 0.01mol) was slowly added for 10 minutes, and stirred for 30 minutes at a room temperature. Next, a -78°C container was disposed againand trimethylborate (1.59ml, 0.014mol) was slowly added to the mixture. After addition, the mixture was stirred at the room temperature for 12 hours. After reaction, a -0°C container was disposed again, 10% hydrochloric acid was slowly added to the mixture to have a pH of 2 or 3. Next, the reaction was extracted using diethyl ether, and then the solvent was distilled under vacuum and precipitates were filtered off using petroleum ether, thereby obtaining a white solid (1.93g, 87%), i.e., phenathryl boronic acid.

00242. Synthesis of 1,4-Diphenanthrylbenzene (BL-01) <chemistry id="chem0023" num="0023"><img file="EP1553155A1_D0023.tif" /></chemistry>    In a two-neck round bottom flask, phenanthryl boronic acid (6.3g, 0.028mol),1,4-dibromo benzene (2.68g, 0.011mol), Tetrakis(triphenylphosphine)palladium(0)(0.19g, 0.05eq), and potassium carbonate (6.21g, 0.045mol) were dissolved in toluene (80ml), THF(50mL) and water(50mL), and stirred for 24 hours in a 100°C container. After reaction, THF and toluene were removed, and the reaction was extracted using dichloromethane and water, distilled under vacuum, and purified through silica gel column chromatography. Then, the solvent was distilled under vacuum and recrystallized using dichloromethane and methanol and filtered off, thereby obtaining a product, i.e., a white solid of 1,4-diphenanthrylbenzene (3.57g, 73%).

00253. Synthesis of 1.4-diphenathrylquinoline (BL-25) <chemistry id="chem0024" num="0024"><img file="EP1553155A1_D0024.tif" /></chemistry>    In a two-neck round bottom flask, phenanthryl boronic acid (3.25g, 0.015mol),1,4-dibromo benzene (1.4g, 0.005mol), Tetrakis(triphenylphosphine)palladium(0)(0.1g, 0.05eq), and potassium carbonate (3.36g, 0.025mol) were dissolved in toluene (40ml), THF(20mL) and water(20mL), and stirred for 24 hours in a 100°C container. After reaction, THF and toluene were removed, and the reaction was extracted using dichloromethane and water, distilled under vacuum, and purified through silica gel column chromatography. Then, the solvent was distilled under vacuum and recrystallized using dichloromethane and methanol and filtered off, thereby obtaining a product, i.e., a white solid of 1,4-diphenanthrylbenzene (1.61g, 69%).

0026Hereinafter, examples of the organic electroluminescence according to the present invention and the corresponding driving voltage and luminescence characteristics will be described below.

<Examples of the present invention>

Example 1

0027An ITO glass was patterned to have a luminescence area of 3mm X 3mm, and then washed.

0028Then, the substrate is mounted to a vacuum chamber, the base pressure was set to 1 × 10^-6 Torr, and then organic materials were deposited on the ITO in the order of HIL(600Å)/NPD(300Å)/CBP+1r(ppy)₃(8%)(200Å)BL-01(100Å)(hole blocking layer)/Alq₃(300Å)/LiF(5Å)/Al(1000Å).

0029The luminescence showed 2,625cd/m² (8.16V) at 1mA, where x and y are 0.286 and 0.628, respectively, on CIE chromaticity diagram.

Example 2

0030An ITO glass was patterned to have a luminescence area of 3mm × 3mm, and then washed.

0031Then, the substrate is mounted to a vacuum chamber, the base pressure was set to 1 × 10^-6 Torr, and then organic materials were deposited on the ITO in the order of HIL(600Å)/NPD(300Å)/CBP+1r(ppy)₃(8%)(200Å)/BL-25(100Å)(hole blocking layer)/Alq₃(300Å)/LiF(5Å)/Al(1000Å).

0032The luminescence showed 3,209cd/m² (8.18V) at 1mA, where x and y are 0.287 and 0.627, respectively, on CIE chromaticity diagram.

0033Comparative Example

0034An ITO glass was patterned to have a luminescence area of 3mm × 3mm, and then washed.

0035Then, the substrate is mounted to a vacuum chamber, the base pressure was set to 1 × 10^-6 Torr, and then organic materials were deposited on the ITO in the order of HIL(600Å)/NPD(300Å)/CBP+1r(ppy)₃(8%)(200Å)/BAlq(100Å)(hole blocking layer)/Alq₃(300Å)/LiF(5Å)/Al(1000Å).

0036The luminescence showed 2,893cd/m² (9.73V) at 1mA, where x and y are 0.318 and 0.617, respectively, on CIE chromaticity diagram. The structural formula of CuPC, NPB, CBP, Ir(ppy)₃, BAlq and Alq₃ was expressed below. <chemistry id="chem0025" num="0025"><img file="EP1553155A1_D0025.tif" /></chemistry><chemistry id="chem0026" num="0026"><img file="EP1553155A1_D0026.tif" /></chemistry><chemistry id="chem0027" num="0027"><img file="EP1553155A1_D0027.tif" /></chemistry>

0037At this time, in Examples 1 and 2 according to the present invention, BL-1 and BL-25 were used as the hole blocking layer, respectively. In the prior art illustrated by way of Comparative Example, BAlq was used as the hole blocking layer. It can be known that Examples of the present invention are superior in luminescence and driving characteristics than Comparative Example.

0038Accordingly, the organic electroluminescence device according to the present invention can solve the prior art extinction problem completely and improve the luminescence and driving characteristics by forming a hole blocking layer of a material having an excellent stability, as shown in the aforementioned chemical formulae 3, between an electron injecting electrode and a hole injecting electrode.

0039The forgoing embodiments are merely exemplary and are not to be construed as limiting the present invention. The present teachings can be readily applied to other types of apparatuses. The description of the present invention is intended to be illustrative, and not to limit the scope of the claims. Many alternatives, modifications, and variations will be apparent to those skilled in the art.

0040The claims refer to examples of preferred embodiments of the invention. However, the invention also refers to the use of any single feature and subcombination of features which are disclosed in the claims and the description.