Multilayered articles and method of manufacture thereof

0001This disclosure relates to multilayered articles and methods of manufacture. In particular this disclosure relates to multilayered sheets for absorption of IR radiation and methods of manufacture thereof.

0002Absorption of excessive amounts of solar radiation by the interior surfaces of a vehicle, residential home or office building can result in elevated interior temperatures, reduced comfort for the occupants, accelerated degradation of interior materials, and an increase in the requirement for larger air conditioning units. In vehicles especially, under high static-soak conditions, which can occur in vehicles parked in the hot summer sun, especially in a desert climate, surface temperature within a closed car can reach over 100°C, and the entire thermal mass of the car can be raised to high temperatures.

0003Increasing the cooling load of the air conditioning unit in a vehicle to ameliorate heat discomfort would go against the trend currently prevailing in the automobile industry. Automobile engines are being downsized to reduce weight and improve fuel efficiency and are less able to handle the power drain of the larger air conditioners. A recent concern to industry and Government is the role played by automotive air conditioners as a source of chlorofluorocarbons (CFC) released into the atmosphere, increased cooling load will lead to even larger air conditioning units, which will exacerbate this problem. Thus, there is a need for new technologies and passive design solutions, which would lead to reduced solar heat loads in automobiles as well as for residential and office buildings.

0004<patcit id="pcit0001" dnum="US4895904A"><text>US-A-4895904</text></patcit> discloses polymer sheets or films for use in greenhouses. The polymer sheets or films contain components which absorb or reflect in the near I.R. (NIR) i.e. in the 0.7 to 2.0µ region, and which transmit at least 75 percent in the photosynthesis active radiation (PAR) region, which is essentially the 0.4µ to 0.7µ region of the solar spectrum. The compositions of the invention contain UV radiation stabilizers. The NIR absorbers and reflectors in the films are certain specific oxides or metals in a very fine particle size, in the submicron or micron range.

0005<patcit id="pcit0002" dnum="EP0943587A"><text>EP-A-0943587</text></patcit> discloses a film for cutting off heat rays, the film having a high transmittance and a low reflectivity of visible light, a low transmittance and a high reflectivity of near infrared radiation and a surface resistivity of at least about 106 ohms/square. The film is easy to form at a low cost by coating a surface with a coating liquid and heating it. The coating liquid is a dispersion containing fine particles of borides having an average diameter no exceeding 100 nm. The dispersion may further contain fine particles of at least one ruthenium or iridium oxide having an average diameter not exceeding 100 nm.

0006<patcit id="pcit0003" dnum="US20020086926A1"><text>US-A1-2002/0086926</text></patcit> discloses a polyvinyl butryal composition which is comprised of polyvinyl butryal resin containing an IR absorbing effective amount of lanthanum hexaboride or a mixture of lanthanum hexaboride and at least one of tin oxide and antimony tin oxide. The lanthanum hexaboride and any indium tin oxide and/or antimony tin oxide are present as fine particles with a particle size that does not interfere with the visual transmission through a sheet comprised of such an IR absorbing polyvinyl butryal.

0007According to one aspect of the present invention, there is provided a multilayered sheet comprising a core layer comprising a thermoplastic polymer and an IR absorbing additive; a first cap layer comprising a thermoplastic polymer and an electromagnetic radiation absorbing additive; wherein a surface of the first cap layer is disposed upon and in intimate contact with a surface of the core layer.

0008According to another aspect of the invention, there is provided a method for manufacturing a multilayered sheet comprising melt blending a composition comprising a thermoplastic polymer and an IR absorbing additive to produce a core layer; melt blending a composition comprising a thermoplastic polymer and an ultraviolet radiation absorber to produce a first cap layer; combining the core layer with the first cap layer in such a manner that the cap layer is disposed upon and in intimate contact with a surface of the core layer.

0009Disclosed herein is a method for manufacturing a multilayered sheet comprising co-extruding a core layer comprising a thermoplastic polymer and an IR absorbing additive with a first cap layer comprising a thermoplastic polymer and an ultraviolet radiation absorber.

0010Disclosed herein too are articles comprising the multilayered sheet detailed above.

0011Embodiments of the invention will now be described, by way of example, with reference to the accompanying drawings, in which: <ul id="ul0001" list-style="none"><li><figref idref="f0001">Figure 1</figref> is a schematic depicting a core layer disposed between two cap layers in accordance with the invention;</li><li><figref idref="f0001">Figure 2</figref> is a schematic depicting a core layer disposed upon and in intimate contact with a single cap layer;</li><li><figref idref="f0002">Figure 3</figref> is a schematic depiction of a multiwall sheet wherein the respective sheets are separated by brackets and having air pockets in between the brackets;</li><li><figref idref="f0003">Figure 4</figref> are photographs of an object taken through two multilayer sheets, one multilayer sheet contained LaB₆ in the core layer, while the other had LaB₆ in the cap layer; and</li><li><figref idref="f0004">Figure 5</figref> shows a device over which thermoforming experiments were performed.</li></ul>

0012The IR absorbing additives are generally used in amounts of about 0.001 gram/square meter (g/m²) to about 2.0 g/m². In one embodiment, the IR absorbing additive may be used in amounts of about 0.03 to about 1.0 g/m². In another embodiment, the IR absorbing additive may be used in amounts of about 0.05 to about 0.75 g/m², In yet another embodiment, the IR absorbing additive may be used in amounts of about 0.09 to about 0.36 g/m².

0013The IR absorbing additives are generally used in amounts of about 0.02 ppm to about 3000 ppm based on the total weight of the core layer. In one embodiment, the IR absorbing additive may be used in amounts of about 1 ppm to about 1500 ppm, based on the total weight of the core layer. In another embodiment, the IR absorbing additive may be used in amounts of about 1.5 ppm to about 1250 ppm based on the total weight of the core layer. In yet another embodiment the IR absorbing additive may be used in amounts of about 2.5 ppm to about 600 ppm , based on the total weight of the core layer and depending on the thickness of the sheet. In one embodiment, the core layer may contain thermal stabilizers to compensate for the increase in temperature brought on by the interaction of the IR light with the IR absorbing additives. Additionally the addition of thermal stabilizers protects the material during processing operations such as melt blending. In general, a layer of polycarbonate containing the IR absorbing additives may experience an increase in temperature of up to about 20°C, upon exposure to light. The addition of thermal stabilizers to the core layer improves the long term aging characteristics and increases the life cycle of the multilayer sheet. In another embodiment, UV stabilizers may also be optionally added to the core layer to prevent against UV degradation. Suitable thermal stabilizers include phosphites, phosphonites, phosphines, hindered amines, hydroxyl amines, phenols, acryloyl modified phenols, hydroperoxide decomposers, benzofuranone derivatives, or the like, or combinations comprising at least one of the foregoing thermal stabilizers Suitable thermal stabilizers that are commercially available are IRGAPHOS 168 (CIBA SPECIALTY CHEMICALS CORPORATION), DOVERPHOS S-9228 (DOVER CHEMICAL CORPORATION), ULTRANOX 641(CHEMTURA CORPORATION), while suitable commercially available UV stabilizers are TINUVIN 329 (CIBA SPECIALTY CHEMICALS CORPORATION) , TINUVIN 234, TINUVIN 350 (CIBA SPECIALTY CHEMICALS CORPORATION), TINUVIN 360 (CIBA SPECIALTY CHEMICALS CORPORATION) or UVINOL 3030 (BASF). If desirable, an optional costabilizer such as a cyclo aliphatic epoxy polymer or IRGANOX 1076 (CIBA SPECIALTY CHEMICALS CORPORATION) may also be

0014As stated above, both, the core and the cap layer comprise thermoplastic resins. Thermoplastic polymers that may be used are oligomers, polymers, ionomers, dendrimers, copolymers such as block copolymers, graft copolymers, star block copolymers, random copolymers, and the like, as well as combinations comprising at least one of the foregoing polymers. Suitable examples of thermoplastic polymers that can be used as the core and cap layer are polyacetals, polyacrylics, polycarbonates polystyrenes, polyesters, polyamides, polyamideimides, polyarylates, polyarylsulfones, polyethersulfones, polyphenylene sulfides, polyvinyl chlorides, polysulfones, polyimides, polyetherimides, polytetrafluoroethylenes, polyetherketones, polyether etherketones, polyether ketone ketones, polybenzoxazoles, polyoxadiazoles, polybenzothiazinophenothiazines, polybenzothiazoles, polypyrazinoquinoxalines, polypyromellitimides, polyquinoxalines, polybenzimidazoles, polyoxindoles, polyoxoisoindolines, polydioxoisoindolines, polytriazines, polypyridazines, polypiperazines, polypyridines, polypiperidines, polytriazoles, polypyrazoles, polypyrrolidines, polycarboranes, polyoxabicyclononanes, polydibenzofurans, polyphthalides, polyacetals, polyanhydrides, polyvinyl ethers, polyvinyl thioethers, polyvinyl alcohols, polyvinyl ketones, polyvinyl halides, polyvinyl nitriles, polyvinyl esters, polysulfonates, polysulfides, polythioesters, polysulfones, polysulfonamides, polyureas, polyphosphazenes, polysilazanes, or the like, or combinations comprising at least one of the foregoing thermoplastic polymers. The preferred thermoplastic polymers for use in the core layer are polycarbonates or copolymers of polycarbonate and polysiloxane. The preferred thermoplastic polymers for use in the cap layer are polycarbonate, copolyestercarbonates, or blends of polyesters with polycarbonates.

0015As stated above, the core layer may be a single sheet of a thermoplastic polymer or multiple sheets of a thermoplastic polymer. It is preferred for the thermoplastic polymer to be transparent to light in the optical wavelength region of the electromagnetic spectrum. The core layer generally comprises a polycarbonate and an IR absorbing additive. As used herein, the terms "polycarbonate", "polycarbonate composition", and "composition comprising aromatic carbonate chain units" includes compositions having structural units of the formula (I): <chemistry id="chem0001" num="0001"><img file="EP1529632B1_D0001.tif" /></chemistry> in which greater than or equal to about 60 percent of the total number of R¹ groups are aromatic organic radicals and the balance thereof are aliphatic, alicyclic, or aromatic radicals. Preferably, R¹ is an aromatic organic radical and, more preferably, a radical of the formula (II): <chemistry id="chem0002" num="0002"><img file="EP1529632B1_D0002.tif" /></chemistry> wherein each of A¹ and A² is a monocyclic divalent aryl radical and Y¹ is a bridging radical having zero, one, or two atoms which separate A¹ from A². In an exemplary embodiment, one atom separates A¹ from A². Illustrative examples of the Y¹ radicals are -O-, -S-, -S(O)-, -S(O)₂-, -C(O)-, methylene, cyclohexyl-methylene, 2-[2,2,1]-bicycloheptylidene, ethylidene, isopropylidene, neopentylidene, cyclohexylidene, cyclopentadecylidene, cyclododecylidene, adamantylidene, or the like. In another embodiment, zero atoms separate A¹ from A², with an illustrative example being biphenyl. The bridging radical Y¹ can be a saturated hydrocarbon group such as methylene, cyclohexylidene or isopropylidene.

0016Polycarbonates may be produced by the Schotten-Bauman interfacial reaction of the carbonate precursor with dihydroxy compounds. Typically, an aqueous base such as sodium hydroxide, potassium hydroxide, calcium hydroxide, or the like, is mixed with an organic, water immiscible solvent such as benzene, toluene, carbon disulfide, or dichloromethane, which contains the dihydroxy compound. A phase transfer agent is generally used to facilitate the reaction. Molecular weight regulators may be added either singly or in admixture to the reactant mixture. Branching agents, described forthwith may also be added singly or in admixture.

0017Polycarbonates can be produced by the interfacial reaction of dihydroxy compounds in which only one atom separates A¹ and A². As used herein, the term "dihydroxy compound" includes, for example, bisphenol compounds having general formula (III) as follows: <chemistry id="chem0003" num="0003"><img file="EP1529632B1_D0003.tif" /></chemistry> wherein R^a and R^b each independently represent hydrogen, a halogen atom, preferably bromine, or a monovalent hydrocarbon group, p and q are each independently integers from 0 to 4, and X^a represents one of the groups of formula (IV): <chemistry id="chem0004" num="0004"><img file="EP1529632B1_D0004.tif" /></chemistry> wherein R^c and R^d each independently represent a hydrogen atom or a monovalent linear or cyclic hydrocarbon group, and R^e is a divalent hydrocarbon group, oxygen, or sulfur.

0018Examples of the types of bisphenol compounds that may be represented by formula (III) include the bis(hydroxyaryl)alkane series such as, 1,1-bis(4-hydroxyphenyl)methane, 1,1-bis(4-hydroxyphenyl)ethane, 2,2-bis(4-hydroxyphenyl)propane (or bisphenol-A), 2,2-bis(4-hydroxyphenyl)butane, 2,2-bis(4-hydroxyphenyl)octane, 1,1-bis(4-hydroxyphenyl)propane, 1,1-bis(4-hydroxyphenyl)n-butane, bis(4-hydroxyphenyl)phenylmethane, 2,2-bis(4-hydroxy-1-methylphenyl)propane, 1,1-bis(4-hydroxy-t-butylphenyl)propane, 2,2-bis(4-hydroxy-3-bromophenyl)propane, or the like; bis(hydroxyaryl)cycloalkane series such as, 1,1-bis(4-hydroxyphenyl)cyclopentane, 1,1-bis(4-hydroxyphenyl)cyclohexane, or the like, or combinations comprising at least one of the foregoing bisphenol compounds.

0019Other bisphenol compounds that may be represented by formula (III) include those where X is -O-, -S-, -SO- or -S(O)₂-. Some examples of such bisphenol compounds are bis(hydroxyaryl)ethers such as 4,4'-dihydroxy diphenylether, 4,4'-dihydroxy-3,3'-dimethylphenyl ether, or the like; bis(hydroxy diaryl)sulfides, such as 4,4'-dihydroxy diphenyl sulfide, 4,4'-dihydroxy-3,3'-dimethyl diphenyl sulfide, or the like; bis(hydroxy diaryl) sulfoxides, such as, 4,4'-dihydroxy diphenyl sulfoxides, 4,4'-dihydroxy-3,3'-dimethyl diphenyl sulfoxides, or the like; bis(hydroxy diaryl)sulfones, such as 4,4'-dihydroxy diphenyl sulfone, 4,4'-dihydroxy-3,3'-dimethyl diphenyl sulfone, or the like; or combinations comprising at least one of the foregoing bisphenol compounds.

0020Other bisphenol compounds that may be utilized in the polycondensation of polycarbonate are represented by the formula (V) <chemistry id="chem0005" num="0005"><img file="EP1529632B1_D0005.tif" /></chemistry> wherein, R^f, is a halogen atom of a hydrocarbon group having 1 to 10 carbon atoms or a halogen substituted hydrocarbon group; n is a value from 0 to 4. When n is at least 2, R^f may be the same or different. Examples of bisphenol compounds that may be represented by the formula (V), are resorcinol, substituted resorcinol compounds such as 5-methyl resorcin, 5-ethyl resorcin, 5-propyl resorcin, 5-butyl resorcin, 5-t-butyl resorcin, 5-phenyl resorcin, 5-cumyl resorcin, or the like; catechol, hydroquinone, substituted hydroquinones, such as 3-methyl hydroquinone, 3-ethyl hydroquinone, 3-propyl hydroquinone, 3-butyl hydroquinone, 3-t-butyl hydroquinone, 3-phenyl hydroquinone, 3-cumyl hydroquinone, or the like; or combinations comprising at least one of the foregoing bisphenol compounds.

0021Bisphenol compounds such as 2,2, 2', 2'- tetrahydro-3, 3, 3', 3'- tetramethyl-1, 1'-spirobi-[IH-indene]-6, 6'- diol represented by the following formula (VI) may also be used. <chemistry id="chem0006" num="0006"><img file="EP1529632B1_D0006.tif" /></chemistry>

0022Suitable polycarbonates further include those derived from bisphenols containing alkyl cyclohexane units. Such polycarbonates have structural units corresponding to the formula (VII) <chemistry id="chem0007" num="0007"><img file="EP1529632B1_D0007.tif" /></chemistry> wherein R^a-R^d are each independently hydrogen, C₁-C₁₂ hydrocarbyl, or halogen; and R^e-Rⁱ are each independently hydrogen, C₁-C₁₂ hydrocarbyl. As used herein, "hydrocarbyl" refers to a residue that contains only carbon and hydrogen. The residue may be aliphatic or aromatic, straight-chain, cyclic, bicyclic, branched, saturated, or unsaturated. The hydrocarbyl residue may contain heteroatoms over and above the carbon and hydrogen members of the substituent residue. Thus, when specifically noted as containing such heteroatoms, the hydrocarbyl residue may also contain carbonyl groups, amino groups, hydroxyl groups, or the like, or it may contain heteroatoms within the backbone of the hydrocarbyl residue. Alkyl cyclohexane containing bisphenols, for example the reaction product of two moles of a phenol with one mole of a hydrogenated isophorone, are useful for making polycarbonate polymer s with high glass transition temperatures and high heat distortion temperatures. Such isophorone bisphenol-containing polycarbonates have structural units corresponding to the formula (VIII) <chemistry id="chem0008" num="0008"><img file="EP1529632B1_D0008.tif" /></chemistry> wherein R^a-R^d are as defined above. These isophorone bisphenol based polymer s, including polycarbonate copolymers made containing non-alkyl cyclohexane bisphenols and blends of alkyl cyclohexyl bisphenol containing polycarbonates with non-alkyl cyclohexyl bisphenol polycarbonates, are supplied by Bayer Co. under the APEC trade name. The preferred bisphenol compound is bisphenol A.

0023In one embodiment, the dihydroxy compound may be reacted with a hydroxyaryl-terminated poly(diorganosiloxane) to create a polycarbonate-polysiloxane copolymer. Preferably the polycarbonate-poly(diorganosiloxane) copolymers are made by introducing phosgene under interfacial reaction conditions into a mixture of a dihydroxy compound, such as BPA, and a hydroxyaryl-terminated poly(diorganosiloxane). The polymerization of the reactants can be facilitated by use of a tertiary amine catalyst or a phase transfer catalyst.

0024The hydroxyaryl-terminated poly(diorganosiloxane) can be made by effecting a platinum catalyzed addition between a siloxane hydride of the formula (IX), <chemistry id="chem0009" num="0009"><img file="EP1529632B1_D0009.tif" /></chemistry> and an aliphatically unsaturated monohydric phenol wherein R⁴ is, for example, C_(1-8) alkyl radicals, haloalkyl radicals such as trifluoropropyl and cyanoalkyl radicals; aryl radicals such as phenyl, chlorophenyl and tolyl. R⁴ is preferably methyl, or a mixture of methyl and trifluoropropyl, or a mixture of methyl and phenyl.

0025Some of the aliphatically unsaturated monohydric phenols, which can be used to make the hydroxyaryl-terminated poly(diorganosiloxane)s are, for example, eugenol, 2-alkylphenol, 4-allyl-2-methylphenol, 4-allyl-2-phenylphenol, 4-allyl-2-bromophenol, 4-allyl-2-t-butoxyphenol, 4-phenyl-2-phenylphenol, 2-methyl-4-propylphenol, 2-allyl-4,6-dimethylphenol, 2-allyl-4-bromo-6-methylphenol, 2-allyl-6-methoxy-4-methylphenol, 2-allyl-4,6-dimethylphenol, or the like, or a combination comprising at least one of the foregoing.

0026Typical carbonate precursors include the carbonyl halides, for example carbonyl chloride (phosgene), and carbonyl bromide; the bis-haloformates, for example the bis-haloformates of dihydric phenols such as bisphenol A, hydroquinone, or the like, and the bis-haloformates of glycols such as ethylene glycol and neopentyl glycol; and the diaryl carbonates, such as diphenyl carbonate, di(tolyl) carbonate, and di(naphthyl) carbonate. The preferred carbonate precursor for the interfacial reaction is carbonyl chloride.

0027It is also possible to employ polycarbonates resulting from the polymerization of two or more different dihydric phenols or a copolymer of a dihydric phenol with a glycol or with a hydroxy- or acid-terminated polyester or with a dibasic acid or with a hydroxy acid or with an aliphatic diacid in the event a carbonate copolymer rather than a homopolymer is desired for use. Generally, useful aliphatic diacids have about 2 to about 40 carbons. A preferred aliphatic diacid is dodecanedioic acid.

0028Branched polycarbonates, as well as blends of linear polycarbonate and a branched polycarbonate may also be used in the core layer. The branched polycarbonates may be prepared by adding a branching agent during polymerization. These branching agents may comprise polyfunctional organic compounds containing at least three functional groups, which may be hydroxyl, carboxyl, carboxylic anhydride, haloformyl, and combinations comprising at least one of the foregoing branching agents. Specific examples include trimellitic acid, trimellitic anhydride, trimellitic trichloride, tris-p-hydroxy phenyl ethane, isatin-bis-phenol, tris-phenol TC (1,3,5-tris((p-hydroxyphenyl)isopropyl)benzene), tris-phenol PA (4(4(1,1-bis(p-hydroxyphenyl)-ethyl) α,α-dimethyl benzyl)phenol), 4-chloroformyl phthalic anhydride, trimesic acid, benzophenone tetracarboxylic acid, or the like, or combinations comprising at least one of the foregoing branching agents. The branching agents may be added at a level of about 0.05 to about 4.0 weight percent (wt%), based upon the total weight of the polycarbonate in a given layer.

0029In one embodiment, the polycarbonate may be produced by a melt polycondensation reaction between a dihydroxy compound and a carbonic acid diester. Examples of the carbonic acid diesters that may be utilized to produce the polycarbonates are diphenyl carbonate, bis(2,4-dichlorophenyl)carbonate, bis(2,4,6-trichlorophenyl) carbonate, bis(2-cyanophenyl) carbonate, bis(o-nitrophenyl) carbonate, ditolyl carbonate, m-cresyl carbonate, dinaphthyl carbonate, bis(diphenyl) carbonate, diethyl carbonate, dimethyl carbonate, dibutyl carbonate, dicyclohexyl carbonate, bis(o-methoxycarbonylphenyl)carbonate, bis(o-ethoxycarbonylphenyl)carbonate, bis(o-propoxycarbonylphenyl)carbonate, bis-ortho methoxy phenyl carbonate, bis(o-butoxycarbonylphenyl)carbonate, bis(isobutoxycarbonylphenyl)carbonate, o-methoxycarbonylphenyl-o-ethoxycarbonylphenylcarbonate, bis o-(tert-butoxycarbonylphenyl)carbonate, o-ethylphenyl-o-methoxycarbonylphenyl carbonate, p-(tertbutylphenyl)-o-(tert-butoxycarbonylphenyl)carbonate, bis-methyl salicyl carbonate, bis-ethyl salicyl carbonate, bis-propyl salicyl carbonate, bis-butyl salicyl carbonate, bis- benzyl salicyl carbonate, bis-methyl 4-chlorosalicyl carbonate or the like, or combinations comprising at least one of the foregoing carbonic acid diesters. The preferred carbonic acid diester is diphenyl carbonate or bis-methyl salicyl carbonate.

0030Preferably, the weight average molecular weight of the polycarbonate is about 3,000 to about 1,000,000 grams/mole (g/mole). In one embodiment, the polycarbonate has a molecular weight of about 10,000 to about 100,000 g/mole. In another embodiment, the polycarbonate has a molecular weight of about 20,000 to about 50,000 g/mole. In yet another embodiment, the polycarbonate has a molecular weight of about 25,000 to about 35,000 g/mole.

0031The thermoplastic polymer is generally used in amounts of about 70 to about 99.9 weight percent (wt%) based upon the weight of the core layer. In one embodiment, the thermoplastic polymer is present in an amount of about 75 to about 99.7 wt%, based on the total weight of the core layer. In another embodiment, the thermoplastic polymer is present in an amount of about 80 to about 99.5 wt%, based on the total weight of the core layer. In yet another embodiment, the thermoplastic polymer is present in an amount of about 85 to about 97 wt%, based on the total weight of the core layer.

0032The IR absorbing additives are generally fine particles of a metal boride or a boride such as such as lanthanum boride (LaB₆), praseodymium boride (PrB₆), neodymium boride (NdB₆), cerium boride (CeB₆), gadolinium boride (GdB₆), terbium boride (TbB₆), dysprosium boride (DyB₆), holmium boride (HoB₆), yttrium boride (YB₆), samarium boride (SmB₆), europium boride (EuB₆), erbium boride (ErB₆), thulium boride (TmB₆), ytterbium boride (YbB₆), lutetium boride (LuB₆), strontium boride (SrB₆), calcium boride (CaB₆), titanium boride (TiB₂), zirconium boride (ZrB₂), hafnium boride (HfB₂), vanadium boride (VB₂), tantalum boride (TaB₂), chromium borides (CrB and CrB₂), molybdenum borides (MoB₂, Mo₂B₅ and MoB), tungsten boride (W₂B₅), or the like, or combinations comprising at least one of the foregoing borides.

0033It is desirable for the IR absorbing additives to be in the form of nanosized particles prior to the dispersion into the polycarbonate. There is no particular limitation to the shape of the particles, which may be for example, spherical, irregular, plate-like or whisker like. The nanosized particles may generally have average largest dimensions of less than or equal to about 200 nanometers (nm). In one embodiment, the particles may have average largest dimensions of less than or equal to about 150 nm. In another embodiment, the particles may have average largest dimensions of less than or equal to about 100 nm. In yet another embodiment, the particles may have average largest dimensions of less than or equal to about 75 nm. In yet another embodiment, the particles may have average largest dimensions of less than or equal to about 50 nm. As stated above, the nanosized particles may generally have average largest dimensions of less than or equal to about 200 nm. In one embodiment, more than 90% of the particles have average largest dimensions less than or equal to about 200 nm. In another embodiment, more than 95% of the particles have average largest dimensions less than or equal to about 200 nm. In yet another embodiment, more than 99% of the particles have average largest dimensions less than or equal to about 200 nm. Bimodal or higher particle size distributions may be used.

0034The IR absorbing additives are generally used in amounts of about 0.001 gram/square meter (g/m²) to about 2.0 g/m². In one embodiment, the IR absorbing additive may be used in amounts of about 0.03 to about 1.0 g/m². In another embodiment, the IR absorbing additive may be used in amounts of about 0.05 to about 0.75 g/m². In yet another embodiment, the IR absorbing additive may be used in amounts of about 0.09 to about 0.36 g/m².

0035The IR absorbing additives are generally used in amounts of about 0.02 ppm to about 3000 ppm based on the total weight of the core layer. In one embodiment, the IR absorbing additive may be used in amounts of about 1 ppm to about 1500 ppm, based on the total weight of the core layer. In another embodiment, the IR absorbing additive may be used in amounts of about 1.5 ppm to about 1250 ppm based on the total weight of the core layer. In yet another embodiment, the IR absorbing additive may be used in amounts of about 2.5 ppm to about 600 ppm , based on the total weight of the core layer and depending on the thickness of the sheet. In one embodiment, the core layer may contain thermal stabilizers to compensate for the increase in temperature brought on by the interaction of the IR light with the IR absorbing additives. Additionally the addition of thermal stabilizers protects the material during processing operations such as melt blending. In general, a layer of polycarbonate containing the IR absorbing additives may experience an increase in temperature of up to about 20°C, upon exposure to light. The addition of thermal stabilizers to the core layer improves the long term aging characteristics and increases the life cycle of the multilayer sheet. In another embodiment, UV stabilizers may also be optionally added to the core layer to prevent against UV degradation. Suitable thermal stabilizers include phosphites, phosphonites, phosphines, hindered amines, hydroxyl amines, phenols, acryloyl modified phenols, hydroperoxide decomposers, benzofuranone derivatives, or the like, or combinations comprising at least one of the foregoing thermal stabilizers. Suitable thermal stabilizers that are commercially available are IRGAPHOS 168, DOVERPHOS S-9228, ULTRANOX 641, while suitable commercially available UV stabilizers are TINUVIN 329, TINUVIN 234, TINUVIN 350, TINUVIN 360 or UVINOL 3030. If desirable, an optional co-stabilizer such as a cyclo aliphatic epoxy polymer or IRGANOX 1076 may also be added to improve thermal stability of the core layer. The preferred thermal stabilizers are phosphites.

0036It is generally desirable to add the thermal stabilizer in an amount of about 0.001 to about 3 wt%, based on the total weight of the core layer. In one embodiment, the thermal stabilizer may be added in amounts of about 0.002 to about 0.5 wt%, based on the total weight of the core layer. In another embodiment, the thermal stabilizer may be added in amounts of about 0.005 to about 0.2 wt%, based on the total weight of the core layer. In yet another embodiment, the thermal stabilizer may be added in amounts of about 0.01 to about 0.1 wt%, based on the total weight of the core layer. If a co-stabilizer is added, it is generally desirable to add it in amount of about 0.001 to about 2 wt%, based on the total weight of the core layer.

0037In addition to the thermal stabilizers and the UV stabilizer, other additives such as mold release agents, pigments, dyes, impact modifiers, lubricants, anti-oxidants, antimicrobials, flame retardants, visual effect additives, fibers such as carbon fibers, glass fibers, carbon nanotubes, or the like; antistatic agents, plasticizers, fillers such as fumed silica, aerogels, carbon black, or the like; can be added to both the core and the cap layers.

0038It is generally desirable for the core layer to have a thickness of about 0.5 to about 30 mm. In one embodiment, the core layer may have a thickness of about 0.75 to about 25 mm. In another embodiment, the core layer may have a thickness of about 0.85 to about 20 mm. In yet another embodiment, the core layer may have a thickness of about 1 to about 15 mm.

0039As stated above, the multilayered sheet may comprise a single cap layer disposed on an and in intimate contact with the core layer. Alternatively, the multilayered sheet may comprise two cap layers, one cap layer disposed on either surface of the core layer and in intimate contact with it. The cap layer also generally comprises a thermoplastic polymer. Suitable thermoplastic polymers are polycarbonate, copolyestercarbonates, or blends of polyesters with polycarbonates. The polyesters may be cycloaliphatic polyesters, polyarylates or a combination of cycloaliphatic polyesters with polyarylates.

0040Cycloaliphatic polyesters suitable for use in the cap layer are those that are characterized by optical transparency, improved weatherability, chemical resistance, and low water absorption. It is also generally desirable that the cycloaliphatic polyesters have good melt compatibility with the thermoplastic polymers used in the core layer. In an exemplary embodiment, it is preferred to use a cycloaliphatic polyester that displays good melt compatibility with the polycarbonate used in the core layer. Cycloaliphatic polyesters are generally prepared by reaction of a diol with a dibasic acid or derivative. The diols useful in the preparation of the cycloaliphatic polyester polymers for use as the high quality optical sheets are straight chain, branched, or cycloaliphatic, preferably straight chain or branched alkane diols, and may contain from 2 to 12 carbon atoms.

0041Suitable examples of diols include ethylene glycol, propylene glycol such as 1,2- and 1,3-propylene glycol, and the like; butane diol such as 1,3- and 1,4-butane diol, and the like; diethylene glycol, 2,2-dimethyl-1,3-propane diol, 2-ethyl, 2-methyl, 1,3-propane diol, 1,3- and 1,5-pentane diol, dipropylene glycol, 2-methyl-1,5-pentane diol, 1,6-hexane diol, 1,4- cyclohexane dimethanol and particularly its cis- and trans-isomers, triethylene glycol, 1,10-decane diol, and combinations comprising at least one of the foregoing diols. Particularly preferred is dimethanol bicyclo octane, dimethanol decalin, a cycloaliphatic diol or chemical equivalents thereof, and particularly 1,4-cyclohexane dimethanol or its chemical equivalents. If 1,4-cyclohexane dimethanol is to be used as the diol component, it is generally preferred to use a mixture of cis- to trans-isomes in ratios of about 1:4 to about 4:1. Within this range, it is generally desired to use a ratio of cis- to trans- isomers of about 1:3.

0042The diacids useful in the preparation of the cycloaliphatic polyester polymers are aliphatic diacids that include carboxylic acids having two carboxyl groups each of which are attached to a saturated carbon in a saturated ring. Suitable examples of cycloaliphatic acids include decahydro naphthalene dicarboxylic acid, norbornene dicarboxylic acids, bicyclo octane dicarboxylic acids. Preferred cycloaliphatic diacids are 1,4-cyclohexanedicarboxylic acid and trans-1, 4-cyclohexanedicarboxylic acids. Linear aliphatic diacids are also useful provided the polyester has at least one monomer containing a cycloaliphatic ring. Illustrative examples of linear aliphatic diacids are succinic acid, adipic acid, dimethyl succinic acid, and azelaic acid. Mixtures of diacid and diols may also be used to make the cycloaliphatic polyesters.

0043Cyclohexanedicarboxylic acids and their chemical equivalents can be prepared, for example, by the hydrogenation of cycloaromatic diacids and corresponding derivatives such as isophthalic acid, terephthalic acid or naphthalenic acid in a suitable solvent (e.g., water or acetic acid) at room temperature and at atmospheric pressure using catalysts such as rhodium supported on a carrier comprising carbon and alumina. They may also be prepared by the use of an inert liquid medium wherein an acid is at least partially soluble under reaction conditions and a catalyst of palladium or ruthenium in carbon or silica is used.

0044Generally, during hydrogenation, two or more isomers are obtained in which the carboxylic acid groups are in cis- or trans-positions. The cis- and trans-isomers can be separated by crystallization with or without a solvent, for example, n-heptane, or by distillation. The cis-isomer tends to be more miscible, however, the trans-isomer has higher melting and crystallization temperatures and is especially preferred. Mixtures of the cis- and trans-isomers may also be used, and preferably when such a mixture is used, the trans-isomer will preferably comprise at least about 75 wt% and the cis-isomer will comprise the remainder based on the total weight of cis- and trans-isomers combined. When a mixture of isomers or more than one diacid is used, a copolyester or a mixture of two polyesters may be used as the cycloaliphatic polyester polymer.

0045Chemical equivalents of these diacids including esters may also be used in the preparation of the cycloaliphatic polyesters. Suitable examples of the chemical equivalents of the diacids are alkyl esters, e.g., dialkyl esters, diaryl esters, anhydrides, acid chlorides, acid bromides, and the like, as well as combinations comprising at least one of the foregoing chemical equivalents. The preferred chemical equivalents comprise the dialkyl esters of the cycloaliphatic diacids, and the most preferred chemical equivalent comprises the dimethyl ester of the acid, particularly dimethyl-trans-1,4-cyclohexanedicarboxylate.

0046Dimethyl-1,4-cyclohexanedicarboxylate can be obtained by ring hydrogenation of dimethylterephthalate, and two isomers having the carboxylic acid groups in the cis- and trans-positions are obtained. The isomers can be separated, the trans-isomer being especially preferred. Mixtures of the isomers may also be used as detailed above.

0047The polyester polymers are generally obtained through the condensation or ester interchange polymerization of the diol or diol chemical equivalent component with the diacid or diacid chemical equivalent component and having recurring units of the formula (X): <chemistry id="chem0010" num="0010"><img file="EP1529632B1_D0010.tif" /></chemistry> wherein R³ represents an alkyl or cycloalkyl radical containing 2 to 12 carbon atoms and which is the residue of a straight chain, branched, or cycloaliphatic alkane diol having 2 to 12 carbon atoms or chemical equivalents thereof; and R⁴ is an alkyl or a cycloaliphatic radical which is the decarboxylated residue derived from a diacid, with the proviso that at least one of R³ or R⁴ is a cycloalkyl group.

0048A preferred cycloaliphatic polyester is poly(1,4-cyclohexane-dimethanol-1,4-cyclohexanedicarboxylate) (PCCD) having recurring units of formula (XI) <chemistry id="chem0011" num="0011"><img file="EP1529632B1_D0011.tif" /></chemistry> wherein in the formula (IX) R³ is a cyclohexane ring, and wherein R⁴ is a cyclohexane ring derived from cyclohexanedicarboxylate or a chemical equivalent thereof and is selected from the cis- or trans-isomer or a mixture of cis- and trans- isomers thereof.

0049Cycloaliphatic polyester polymers can be generally made in the presence of a suitable catalyst such as a tetra(2-ethyl hexyl)titanate, in a suitable amount, generally about 50 to 400 ppm of titanium based upon the total weight of the final product.

0050PCCD is generally completely miscible with the polycarbonate. It is generally desirable for a polycarbonate- PCCD mixture to have a melt volume rate of greater than or equal to about 5 cubic centimeters/10 minutes (cc/10 min or ml/10 min)to less than or equal to about 150 cubic centimeters/10 minutes when measured at 265°C, at a load of 2.16 kilograms and a four minute dwell time. Within this range, it is generally desirable to have a melt volume rate of greater than or equal to about 7, preferably greater than or equal to about 9, and more preferably greater than or equal to about 10 cc/10 min when measured at 265°C, at a load of 2.16 kilograms and a four minute dwell time. Also desirable within this range, is a melt volume rate of less than or equal to about 125, preferably less than or equal to about 110, and more preferably less than or equal to about 100 cc/10 minutes.

0051Other preferred cycloaliphatic polyesters that may be mixed with the polycarbonate are polyethelene terephthalate (PET), polybutylene terephthalate (PBT), poly(trimethylene terephthalate) ( PTT), poly(cyclohexanedimethanol-co-ethylene terephthalate) ( PETG), poly(ethylene naphthalate) (PEN), and poly(butylene naphthalate) (PBN).

0052Another preferred polyester that may be mixed with other polymers are polyarylates. Polyarylates generally refers to polyesters of aromatic dicarboxylic acids and bisphenols. Polyarylate copolymers that include carbonate linkages in addition to the aryl ester linkages, are termed polyester-carbonates, and may also be advantageously utilized in the mixtures. The polyarylates can be prepared in solution or by the melt polymerization of aromatic dicarboxylic acids or their ester forming derivatives with bisphenols or their derivatives.

0053In general, it is preferred for the polyarylates to comprise at least one diphenol residue in combination with at least one aromatic dicarboxylic acid residue. The preferred diphenol residue, illustrated in formula (XII), is derived from a 1,3-dihydroxybenzene moiety, referred to throughout this specification as resorcinol or resorcinol moiety. Resorcinol or resorcinol moieties include both unsubstituted 1,3-dihydroxybenzene and substituted 1,3-dihydroxybenzenes. <chemistry id="chem0012" num="0012"><img file="EP1529632B1_D0012.tif" /></chemistry>

0054In formula (X), R is at least one of C_1-12 alkyl or halogen, and n is 0 to 3. Suitable dicarboxylic acid residues include aromatic dicarboxylic acid residues derived from monocyclic moieties, preferably isophthalic acid, terephthalic acid, or mixtures of isophthalic and terephthalic acids, or from polycyclic moieties such as diphenyl dicarboxylic acid, diphenylether dicarboxylic acid, and naphthalene-2,6-dicarboxylic acid, and the like, as well as combinations comprising at least one of the foregoing polycyclic moieties. The preferred polycyclic moiety is naphthalene-2,6-dicarboxylic acid.

0055Preferably, the aromatic dicarboxylic acid residues are derived from mixtures of isophthalic and/or terephthalic acids as generally illustrated in formula (XIII). <chemistry id="chem0013" num="0013"><img file="EP1529632B1_D0013.tif" /></chemistry>

0056Therefore, in one embodiment the polyarylates comprise resorcinol arylate polyesters as illustrated in formula (XIV) wherein R and n are previously defined for formula (XI). <chemistry id="chem0014" num="0014"><img file="EP1529632B1_D0014.tif" /></chemistry> wherein R is at least one of C_1-12 alkyl or halogen, n is 0 to3, and m is at least about 8. It is preferred for R to be hydrogen. Preferably, n is zero and m is about 10 and about 300. The molar ratio of isophthalate to terephthalate is about 0.25:1 to about 4.0:1.

0057In another embodiment, the polyarylate comprises thermally stable resorcinol arylate polyesters that have polycyclic aromatic radicals as shown in formula (XV) <chemistry id="chem0015" num="0015"><img file="EP1529632B1_D0015.tif" /></chemistry> wherein R is at least one of C_1-12 alkyl or halogen, n is 0 to3, and m is at least about 8.

0058In another embodiment, the polyarylates are copolymerized to form block copolyestercarbonates, which comprise carbonate and arylate blocks. They include polymers comprising structural units of the formula (XVI) <chemistry id="chem0016" num="0016"><img file="EP1529632B1_D0016.tif" /></chemistry> wherein each R¹ is independently halogen or C_1-12 alkyl, m is at least 1, p is about 0 to about 3, each R² is independently a divalent organic radical, and n is at least about 4. Preferably n is at least about 10, more preferably at least about 20 and most preferably about 30 to about 150. Preferably m is at least about 3, more preferably at least about 10 and most preferably about 20 to about 200. In an exemplary embodiment m is present in an amount of about 20 and 50.

0059It is generally desirable for the weight average molecular weight of the polyester to be about 500 to about 1,000,000 grams/mole (g/mole). In one embodiment, the polyester has a weight average molecular weight of about 10,000 to about 200,000 g/mole. In another embodiment, the polyester has a weight average molecular weight of about 30,000 to about 150,000 g/mole. In yet another embodiment, the polyester has a weight average molecular weight of about 50,000 to about 120,000 g/mole. An exemplary molecular weight for the polyester utilized in the cap layer is 60,000 and 120,000 g/mole. These molecular weights are determined against a polystyrene standard.

0060In one embodiment, it is desirable to match the melt viscosity of the thermoplastic polymer used in the core layer with the melt viscosity of the thermoplastic polymer used in the cap layer during the formation of the multilayer sheet. In another embodiment, it is desirable for the melt viscosity of the thermoplastic polymer used in the cap layer to be equal to the melt viscosity of the thermoplastic polymer used in the core layer, at the point of initial contact of the two melts during the formation of the multilayer sheet. In yet another embodiment, it is desirable for the melt viscosity of the thermoplastic polymer used in the cap layer to be within 1% of the melt viscosity of the thermoplastic polymer used in the core layer, at the point of initial contact of the two melts during the formation of the multilayer sheet. In yet another embodiment, it is desirable for the melt viscosity of the thermoplastic polymer used in the cap layer to be within 5% of the melt viscosity of the thermoplastic polymer used in the core layer, at the point of initial contact of the two melts during the formation of the multilayer sheet. In yet another embodiment, it is desirable for the melt viscosity of the thermoplastic polymer used in the cap layer to be within 10% of the melt viscosity of the thermoplastic polymer used in the core layer, at the point of initial contact of the two melts during the formation of the multilayer sheet. In yet another embodiment, it is desirable for the melt viscosity of the thermoplastic polymer used in the cap layer to be within 20% of the melt viscosity of the thermoplastic polymer used in the core layer, at the point of initial contact of the two melts during the formation of the multilayer sheet.

0061The polyester and/or copolyestercarbonates are generally used in amounts of about 70 to about 99.9 weight percent (wt%) based upon the weight of the cap layer. Within this range, an amount of greater than or equal to about 75, preferably greater than or equal to about 80, and more preferably greater than or equal to about 85 wt% may be used, based upon the weight of the cap layer. Also desirable within this range, is an amount of greater than or equal to about 98, preferably greater than or equal to about 97, and more preferably greater than or equal to about 95 wt% may be used, based upon the weight of the cap layer.

0062The cap layer generally comprises a suitable UV absorber. Suitable UV absorbers are benzophenones such as 2,4 dihydroxybenzophenone, 2-hydroxy-4-methoxybenzophenone, 2-hydroxy-4-n-octoxybenzophenone, 4-dodecyloxy-2 hydroxybenzophenone, 2-hydroxy-4-octadecyloxybenzophenone, 2,2' dihydroxy- 4 methoxybenzophenone, 2,2' dihydroxy-4,4'dimethoxybenzophenone, 2,2' dihydroxy-4 methoxybenzophenone, 2,2', 4,4' tetra hydroxybenzophenone, 2-hydroxy-4-methoxy-5 sulfobenzophenone, 2-hydroxy-4-methoxy-2'-carboxybenzophenone, 2,2'dihydroxy-4,4'dimethoxy-5 sulfobenzophenone, 2-hydroxy-4-(2-hydroxy-3-methylaryloxy) propoxybenzophenone, 2-hydroxy-4 chlorobenzopheone, or the like; benzotriazoles such as 2,2'-(hydroxy-5-methyl phenyl) benzotriazole, 2,2'-(hydroxy-3',5'-ditert-butyl phenyl) benzotriazole, and 2,2'-(hydroxy-X-tert, butyl-5'-methyl-phenyl) benzotriazole, or the like; salicylates such as phenyl salicylate, carboxyphenyl salicylate, p-octylphenyl salicylate, strontium salicylate, p-tert butylphenyl salicylate, methyl salicylate, dodecyl salicylate, or the like; and also other ultraviolet absorbents such as resorcinol monobenzoate, 2'ethyl hexyl-2-cyano, 3-phenylcinnamate, 2- ethyl-hexyl-2-cyano-3,3-diphenyl acrylate, ethyl-2-cyano-3,3-diphenyl acrylate, [2-2'-thiobis(4-t-octylphenolate)-1-n-butylamine, or the like, or combinations comprising at least one of the foregoing UV absorbers. A preferred UV absorber for use in the cap layer is UVINUL 3030, commercially available from BASF.

0063The UV absorbers are generally used in amounts of about 5 wt% to about 15 wt%, based upon the weight of the cap layer. In one embodiment, the UV absorber may be used in an amount of 7 to about 14 wt%, based on the total weight of the cap layer. In yet another embodiment, the UV absorber may be used in an amount of 8 to about 12 wt%, based on the total weight of the cap layer. In one embodiment, the UV absorber may be used in an amount of 9 to about 11 wt%, based on the total weight of the cap layer.

0064It is generally desirable for the cap layer to have an average thickness of about 10 to about 120 micrometers. In one embodiment, the cap layer may have a thickness of about 15 to about 100 micrometers. In another embodiment, the cap layer may have a thickness of about 20 to about 90 micrometers. In yet another embodiment, the cap layer may have a thickness of about 25 to about 80 micrometers.

0065The multilayer sheet may generally be produced by extrusion followed by laminating the sheets in a roll mill or a roll stack. The extrusion of the individual layers of the multilayered sheet may be performed in a single screw extruder or in a twin screw extruder. It is desirable to extrude the layers in a single screw extruder and to laminate the layers in a roll mill. It is more desirable to co-extrude the layers in a single screw extruder or twin screw extruder and to optionally laminate the layers in a roll mill. The roll mill may be either a two roll or three roll mill, as is desired. Coextrusion of the layers by single screw extruders is generally desirable for the manufacturing of the multilayered sheet.

0066In one embodiment, in the extrusion of the core layer and the cap layer, the additives (e.g., IR absorbing additive and UV absorber) may be added to the extruder along with the thermoplastic polymer at the feed throat. In another embodiment, in the extrusion of the core layer and the cap layer, the additives may be added to the extruder in the form of a masterbatch. While the thermoplastic polymer is fed to the throat of the extruder, the masterbatch may be fed either at the throat of the extruder or downstream or the throat. In one exemplary embodiment, in the production of the core layer, the thermoplastic polymer is fed to the throat of a single screw extruder while the IR absorbing additive is added in masterbatch form downstream of the feed throat. In another exemplary embodiment, in the production of the cap layer, the thermoplastic polymer is fed to the throat of a single screw extruder while the UV absorber is added in masterbatch form downstream of the feed throat.

0067In one embodiment, the desired composition for the core layer and the cap layer may be separately precompounded prior to coextrusion. In this event, the precompounded materials may be first melt blended in a twin screw extruder, single screw extruder, buss kneader, roll mill, or the like, prior to being formed into a suitable shapes such as pellets, sheets, and the like, for further co-extrusion. The precompounded core and cap layer compositions may then be fed into the respective extruders for co-extrusion.

0068As stated above, it is desirable to co-extrude the cap and the core layer. In one embodiment, in one manner of co-extruding of the multilayered sheet, the melt streams (extrudates) from the various extruders are fed into a feed block die where the various melt streams are combined before entering the die. In another embodiment, the melt streams from the various extruders are fed into a multi-manifold internal combining die. The different melt streams enter the die separately and join just inside the final die orifice. In yet another embodiment, the melt streams from the various extruders are fed into a multi-manifold external combining die. The external combining dies have completely separate manifolds for the different melt streams as well as distinct orifices through which the streams leave the die separately, joining just beyond the die exit. The layers are combined while still molten and just downstream of the die. An exemplary die used in the production of the multilayered sheet is a feed block die. In an exemplary embodiment, the extruders used for the co-extrusion of the cap and core layers are single screw extruders respectively. The co-extruded sheet may optionally be calendared in a roll mill if desired. The multilayered sheet generally has a thickness of about 0.5 to about 35 millimeters.

0069It is desirable for the multilayered sheet to absorb an amount of greater than or equal to about 90% of all the IR radiation incident upon the surface of the sheet. In one embodiment, the multilayered sheet may absorb an amount of greater than or equal to about 60% of all the IR radiation incident upon the surface of the sheet. In another embodiment, the multilayered sheet may absorb an amount of greater than or equal to about 50% of all the IR radiation incident upon the surface of the sheet. In yet another embodiment, the multilayered sheet may absorb an amount of greater than or equal to about 40% of all the IR radiation incident upon the surface of the sheet. In yet another embodiment, the multilayered sheet may absorb an amount of greater than or equal to about 20% of all the IR radiation incident upon the surface of the sheet. In yet another embodiment, the multilayered sheet may absorb an amount of greater than or equal to about 5% of all the IR radiation incident upon the surface of the sheet.

0070It is desirable for the multilayered sheet to absorb an amount of greater than or equal to about 90% of all the UV radiation incident upon the surface of the sheet. In one embodiment, the multilayered sheet may absorb an amount of greater than or equal to about 60% of all the UV radiation incident upon the surface of the sheet. In another embodiment, the multilayered sheet may absorb an amount of greater than or equal to about 50% of all the UV radiation incident upon the surface of the sheet. In yet another embodiment, the multilayered sheet may absorb an amount of greater than or equal to about 40% of all the UV radiation incident upon the surface of the sheet. In yet another embodiment, the multilayered sheet may absorb an amount of greater than or equal to about 20% of all the UV radiation incident upon the surface of the sheet. In yet another embodiment, the multilayered sheet may absorb an amount of greater than or equal to about 5% of all the UV radiation incident upon the surface of the sheet.

0071While it is generally desirable for the multilayer sheet to absorb as much electromagnetic radiation as possible in the UV and IR regions of the electromagnetic spectrum, it is desirable for the multilayered sheet to be transparent to light in the visible region of the electromagnetic spectrum. The visible region of the electromagnetic spectrum generally has wavelengths of about 400 to about 700 nm. It is desirable for the sheet to have a transmissivity to light in the visible region of greater than or equal to about 20%. In one embodiment, it is desirable for the sheet to have a transmissivity to light in the visible region of greater than or equal to about 30%. In another embodiment, it is desirable for the sheet to have a transmissivity to light in the visible region of greater than or equal to about 40%. In yet another embodiment, it is desirable for the sheet for have a transmissivity of greater than or equal to about 50%.

0072It is also desirable for the multilayered sheet to have a haze of less than or equal to about 5%. In one embodiment, the haze may be less than or equal to about 2%. In another embodiment, the haze may be less than or equal to about 1.8%. In another embodiment, the haze may be less than or equal to about 1.6%.

0073If the resulting multilayer sheet is in the form of a multiwall sheet, it is generally desirable to have a haze of less than 25%. In one embodiment, the haze may be less than or equal to about 20%. In another embodiment, the haze may be less than or equal to about 15%. In another embodiment, the haze may be less than or equal to about 10%.

0074The multilayer sheet thus produced may be advantageously used in automobiles, residential and office buildings or other areas where heat produced by exposure to IR radiation is undesirable. In one embodiment, the sheets may be used as roofing or glazing materials, after being co-extruded as multiwall sheets with air channels in between the walls as shown in <figref idref="f0002">Figure 3. Figure 3</figref> is a schematic depiction of a multiwall sheet wherein the respective sheets are separated by brackets and having air pockets in between the brackets. The sheet thickness is also depicted in the <figref idref="f0002">Figure 3</figref> and encompasses the brackets as well as the individual multilayer sheets. The brackets may also be made of a thermoplastic polymer such as those described above. In one embodiment, the bracket may be manufactured from polycarbonate, polyester, or polyestercarbonate-polyester.

0075The multilayer sheet thus formed may also be subjected to additional processing such as thermoforming, vacuum molding, blow molding, shaping, and the like, to produce materials having different shapes and geometries.

0076The following examples, which are meant to be exemplary, not limiting, illustrate compositions and methods of manufacturing some of the various embodiments of the multilayered sheets using various materials and apparatus.

EXAMPLES

Comparative Example

0077This example along with the following Example 1 was undertaken to demonstrate the benefits of incorporating the IR absorbing additive in the core layer versus the cap layer. These examples were also undertaken to demonstrate the benefits of placing the cap layer (containing UV absorber) on the surface of the core layer (containing an IR absorbing additive) in such a manner that when the multilayer sheet is subjected to solar radiation, the radiation contacts the cap layer prior to contacting the core layer. In these examples, a 3 mm multilayered sheet having a cap layer (comprising polycarbonate with LaB₆ (IR absorbing additive) and a UV absorber) disposed upon a polycarbonate layer was compared with a multilayered sheet having the cap layer containing a UV absorber disposed upon a core layer containing an IR absorbing additive. The comparative example discusses the results of placing the IR absorbing additive (LaB₆) in the cap layer, while the following Example 1 discusses the beneficial results of placing the IR absorbing additive (LaB₆) in the core layer.

0078The cap layer thickness was about 60 micrometers, though thickness variations caused the cap layer thickness to vary from about 50 to about 80 micrometers. The composition and construction of the cap layer as well as the core layer are detailed below.

LaB

6

in the Cap Layer

0079Both the cap and the core layer have polycarbonate as the thermoplastic polymer. The polycarbonate was a linear bisphenol A polycarbonate having a weight average molecular weight of 30,000 g/mole.

0080The cap layer contains 0.18 g/m² of LaB₆, 10% Tinuvin 234 and 0.1% Irgafos 168, with the remainder being bisphenol a polycarbonate. The LaB₆ was obtained from a masterbatch containing 0.25 wt% LaB₆ in linear bisphenol A polycarbonate having a weight average molecular weight of 30,000 g/mole. The aforementioned ingredients were procompounded in a twin screw extruder to form a cap layer precompound.

0081The core layer was first precompounded in a twin screw extruder. The core layer contains 99.75 wt% linear bisphenol A polycarbonate having a weight average molecular weight of 30,000 g/mole, 0.1 wt% pentaerythritoltetrastearate, 0.1 wt% Tinuvin 234 (CIBA SPECIALTY CHEMICALS CORPORATION) and 0.05 wt% Irgafos 168 (CIBA SPECIALTY CHEMICALS CORPORATION). The core and cap layer precompounds were then co-extruded in the following manner to produce the multilayer sheet.

0082The extruder used for extruding the core layer was a Werner and Pfleiderer ZSK extruder 133 mm (twin screw extruder). The barrel temperatures were set at about 200 to 280°C respectively. The die temperature was 250°C and the screw speed was 85 rpm. Five barrels having temperatures of 250, 260, 260, 270, 280°C from feed throat to die respectively. The zone temperatures of the extruder used for making the cap layers (Macgi, Single Screw extruder having a 45 mm barrel diameter) were set between 200 and 280°C and the screw speed was 58 rpm. Six barrels were used in each of the single screw extruders with the barrel temperatures set at 245, 255, 230, 230, 270, 280°C respectively. The aforementioned barrel temperatures are, in order, from the feed throat to the feed block of the single screw extruder respectively. Some characteristics of the core layer are given in Table 1.

0083In the extrusion of the core and cap layers, pre-compounded pellets having the requisite compositions as detailed above, were fed to the extruder via the feed throat. The extrudate from the respective extruders was fed to a feed block die to form the co-extruded multilayer sheet. Light transmission and haze were measured according to ASTM D 1003, while the lab color was measured according to CIE lab DIN 5033. the results are shown in Table 1 below. <tables id="tabl0001" num="0001"><table frame="all"><title>Table 1</title><tgroup cols="6"><colspec colnum="1" colname="col1" colwidth="32mm" /><colspec colnum="2" colname="col2" colwidth="33mm" /><colspec colnum="3" colname="col3" colwidth="16mm" /><colspec colnum="4" colname="col4" colwidth="24mm" /><colspec colnum="5" colname="col5" colwidth="19mm" /><colspec colnum="6" colname="col6" colwidth="38mm" /><thead valign="top"><row valign="bottom"><entry align="center">Sample point</entry><entry align="center">Cap-layer-thickness</entry><entry /><entry /><entry /><entry /></row><row valign="bottom"><entry align="center">across width</entry><entry align="center">Top cap layer</entry><entry align="center">LT (%)</entry><entry align="center">b-value color</entry><entry align="center">Haze (%)</entry><entry align="center">Solar Transmission (%)</entry></row><row valign="bottom"><entry align="center">(mm)</entry><entry align="center">(micron)</entry><entry /><entry /><entry /><entry /></row></thead><tbody><row><entry align="center">25</entry><entry align="center">61.2</entry><entry align="center">59.8</entry><entry align="center">12.7</entry><entry align="center">7.6</entry><entry align="center">49.6</entry></row><row><entry align="center">75</entry><entry align="center">74.1</entry><entry align="center">55.6</entry><entry align="center">14.9</entry><entry align="center">8.4</entry><entry align="center">44.9</entry></row><row><entry align="center">125</entry><entry align="center">67.6</entry><entry align="center">57.7</entry><entry align="center">13.8</entry><entry align="center">8</entry><entry align="center">47.1</entry></row><row><entry align="center">175</entry><entry align="center">64.4</entry><entry align="center">58.7</entry><entry align="center">13.3</entry><entry align="center">7.8</entry><entry align="center">48</entry></row><row><entry align="center">225</entry><entry align="center">80.5</entry><entry align="center">53.4</entry><entry align="center">15.9</entry><entry align="center">8.7</entry><entry align="center">42.6</entry></row><row><entry align="center">275</entry><entry align="center">67.6</entry><entry align="center">57.7</entry><entry align="center">13.8</entry><entry align="center">8</entry><entry align="center">46</entry></row><row><entry align="center">325</entry><entry align="center">51.5</entry><entry align="center">63</entry><entry align="center">11.1</entry><entry align="center">7.1</entry><entry align="center">52.4</entry></row><row><entry align="center">375</entry><entry align="center">64.4</entry><entry align="center">58.7</entry><entry align="center">13.3</entry><entry align="center">7.8</entry><entry align="center">48.4</entry></row><row><entry align="center">425</entry><entry align="center">64.4</entry><entry align="center">58.7</entry><entry align="center">13.3</entry><entry align="center">7.8</entry><entry align="center">47.3</entry></row><row><entry align="center">475</entry><entry align="center">67.6</entry><entry align="center">57.7</entry><entry align="center">13.8</entry><entry align="center">8</entry><entry align="center">46.1</entry></row><row><entry align="center">525</entry><entry align="center">64.4</entry><entry align="center">58.7</entry><entry align="center">13.3</entry><entry align="center">7.8</entry><entry align="center">47.3</entry></row><row><entry align="center">575</entry><entry align="center">54.7</entry><entry align="center">61.9</entry><entry align="center">11.6</entry><entry align="center">7.3</entry><entry align="center">50.8</entry></row><row><entry align="center">625</entry><entry align="center">54.7</entry><entry align="center">61.9</entry><entry align="center">11.6</entry><entry align="center">7.3</entry><entry align="center">50.6</entry></row><row><entry align="center">675</entry><entry align="center">58</entry><entry align="center">60.9</entry><entry align="center">12.2</entry><entry align="center">7.5</entry><entry align="center">49.3</entry></row><row><entry align="center">725</entry><entry align="center">67.6</entry><entry align="center">57.7</entry><entry align="center">13.8</entry><entry align="center">8</entry><entry align="center">46.2</entry></row><row><entry align="center">775</entry><entry align="center">61.2</entry><entry align="center">59.8</entry><entry align="center">12.7</entry><entry align="center">7.6</entry><entry align="center">48.2</entry></row><row><entry align="center">825</entry><entry align="center">54.7</entry><entry align="center">61.9</entry><entry align="center">11.6</entry><entry align="center">7.3</entry><entry align="center">50.3</entry></row><row><entry align="center">850</entry><entry align="center">58</entry><entry align="center">60.9</entry><entry align="center">12.2</entry><entry align="center">7.5</entry><entry align="center">49.6</entry></row><row><entry>Variation</entry><entry align="center">51.5-80.5</entry><entry align="center">53.4-63</entry><entry align="center">11.1-15.9</entry><entry align="center">7.1-8.7</entry><entry align="center">42.6-52.4</entry></row><row><entry>Standard deviation</entry><entry align="center">7.3</entry><entry align="center">2.4</entry><entry align="center">1.2</entry><entry align="center">0.4</entry><entry align="center">2.4</entry></row></tbody></tgroup></table></tables>

0084From the above table it may be seen that there is a wide variation in the light transmission (LT) of about 53.4 to about 63%. Similarly placing the IR absorbing additive in the cap layer shows that the multilayer sheet has high levels of haze of greater than 7% and wide variations in the level of solar transmission.

Example 1

0085As stated above, this example demonstrates the efficacy of incorporating the LaB₆ in the core layer. A 3-layered multi layered sheet having its core layer containing the LaB₆ in the amount shown for Sample #1 in Table 1 was coextruded with a UV cap layer. The sheet contains two cap layers and one core layer. The core layer was disposed between the two cap layers.

0086The cap layer of the 3-layered sheet was made in the form of a pre-compound that contains 10 wt% UV absorber (Tinuvin 234 (CIBA SPECIALTY CHEMICALS CORPORATION)) , 0.1 wt% heat stabilizer (Irgafos 168 (CIBA SPECIALTY CHEMICALS CORPORATION)) and 89.9% linear bipshenol A polycarbonate.

0087The core layer was first precompounded by feeding and mixing the following product streams: 16 wt% of a LaB₆ masterbatch containing 0.032 wt% by weight of LaB₆, 0.05% Irgafos 168 (CIBA SPECIALTY CHEMICALS CORPORATION) and 99.918% linear polycarbonate having a weight average molecular weight of 30,000 to 31,000 g/mole. Secondly 5 wt% of a UV concentrate consisting of 97.5 wt% linear polycarbonate having a weight average molecular weight of 30,000 g/mole, 2 wt% Tinuvin 234 (CIBA SPECIALTY CHEMICALS CORPORATION) and 0.1 wt% Irgafos 168 (CIBA SPECIALTY CHEMICALS CORPORATION). The remainder was constituted by 79 wt % linear polycarbonate having a weight average molecular weight of 30,000 g/mole.

0088The respective pre-compounds were then fed to the respective extruders as detailed in the Comparative Example to produce the multilayer sheet. The results are shown in the Tables 2 and 3. Table 2 depicts some of the characteristics of the multilayer sheet containing the LaB₆ in the core layer. Table 3 shows the results obtained for the multilayered sheet having the UV absorbers in the cap layer and the IR absorbing additives in the core layer. In both cases, the cap layer was first contacted by the impinging radiation. <tables id="tabl0002" num="0002"><table frame="all"><title>Table 2</title><tgroup cols="10"><colspec colnum="1" colname="col1" colwidth="18mm" /><colspec colnum="2" colname="col2" colwidth="20mm" /><colspec colnum="3" colname="col3" colwidth="12mm" /><colspec colnum="4" colname="col4" colwidth="12mm" /><colspec colnum="5" colname="col5" colwidth="22mm" /><colspec colnum="6" colname="col6" colwidth="26mm" /><colspec colnum="7" colname="col7" colwidth="13mm" /><colspec colnum="8" colname="col8" colwidth="12mm" /><colspec colnum="9" colname="col9" colwidth="11mm" /><colspec colnum="10" colname="col10" colwidth="12mm" /><thead valign="top"><row valign="bottom"><entry align="center">Sample #</entry><entry align="center">LaB₆ conc.</entry><entry align="center">LT%</entry><entry align="center">ST%</entry><entry align="center">Solar factor</entry><entry align="center">Shading Coeff.</entry><entry align="center">Haze</entry><entry align="center">L</entry><entry>a</entry><entry>b</entry></row></thead><tbody><row valign="bottom"><entry align="center">1</entry><entry align="center">0.18 g/m²</entry><entry align="char" char="." charoff="31">62.0</entry><entry align="char" char="." charoff="30">50.8</entry><entry align="char" char="." charoff="9">1.21</entry><entry align="char" char="." charoff="7">0.58</entry><entry align="char" char="." charoff="15">1.4</entry><entry align="char" char="." charoff="32">82.3</entry><entry align="char" char="." charoff="28">-6.4</entry><entry align="char" char="." charoff="32">12.5</entry></row></tbody></tgroup><tgroup cols="10" rowsep="0"><colspec colnum="1" colname="col1" colwidth="18mm" /><colspec colnum="2" colname="col2" colwidth="20mm" /><colspec colnum="3" colname="col3" colwidth="12mm" /><colspec colnum="4" colname="col4" colwidth="12mm" /><colspec colnum="5" colname="col5" colwidth="22mm" /><colspec colnum="6" colname="col6" colwidth="26mm" /><colspec colnum="7" colname="col7" colwidth="13mm" /><colspec colnum="8" colname="col8" colwidth="12mm" /><colspec colnum="9" colname="col9" colwidth="11mm" /><colspec colnum="10" colname="col10" colwidth="12mm" /><tbody><row><entry namest="col1" nameend="col10" align="justify">LT% = light Transmission ST% = Total Solar Transmission Solar Factor = Light to Solar gain ratio = Total visible Light Transmission /Total Solar Transmission. Shading coefficient = total Solar Transmission /87</entry></row></tbody></tgroup></table></tables><tables id="tabl0003" num="0003"><table frame="all"><title>Table 3</title><tgroup cols="5"><colspec colnum="1" colname="col1" colwidth="32mm" /><colspec colnum="2" colname="col2" colwidth="19mm" /><colspec colnum="3" colname="col3" colwidth="22mm" /><colspec colnum="4" colname="col4" colwidth="19mm" /><colspec colnum="5" colname="col5" colwidth="38mm" /><thead valign="top"><row><entry align="center">Sample point</entry><entry /><entry /><entry /><entry /></row><row valign="bottom"><entry align="center">across width</entry><entry align="center">LT %</entry><entry align="center">b value color</entry><entry align="center">Haze (%)</entry><entry align="center">Solar Transmission (%)</entry></row><row><entry align="center">(mm)</entry><entry /><entry /><entry /><entry /></row></thead><tbody><row><entry align="center">25</entry><entry align="center">62.2</entry><entry align="center">12.5</entry><entry align="center">1.6</entry><entry align="center">50.8</entry></row><row><entry align="center">75</entry><entry align="center">62.1</entry><entry align="center">12.6</entry><entry align="center">1.5</entry><entry align="center">51</entry></row><row><entry align="center">125</entry><entry align="center">62.2</entry><entry align="center">12.5</entry><entry align="center">1.4</entry><entry align="center">51.1</entry></row><row><entry align="center">175</entry><entry align="center">62.1</entry><entry align="center">12.5</entry><entry align="center">1.4</entry><entry align="center">50.2</entry></row><row><entry align="center">225</entry><entry align="center">62.2</entry><entry align="center">12.6</entry><entry align="center">1.4</entry><entry align="center">51.2</entry></row><row><entry align="center">275</entry><entry align="center">62.2</entry><entry align="center">12.6</entry><entry align="center">1.4</entry><entry align="center">51</entry></row><row><entry align="center">325</entry><entry align="center">62.1</entry><entry align="center">12.6</entry><entry align="center">1.4</entry><entry align="center">51.1</entry></row><row><entry align="center">375</entry><entry align="center">62.1</entry><entry align="center">12.6</entry><entry align="center">1.4</entry><entry align="center">50.9</entry></row><row><entry align="center">425</entry><entry align="center">62.1</entry><entry align="center">12.6</entry><entry align="center">1.4</entry><entry align="center">50.8</entry></row><row><entry align="center">475</entry><entry align="center">62.1</entry><entry align="center">12.6</entry><entry align="center">1.5</entry><entry align="center">51</entry></row><row><entry align="center">525</entry><entry align="center">62</entry><entry align="center">12.6</entry><entry align="center">1.4</entry><entry align="center">50.8</entry></row><row><entry align="center">575</entry><entry align="center">62</entry><entry align="center">12.6</entry><entry align="center">1.4</entry><entry align="center">50.9</entry></row><row><entry align="center">625</entry><entry align="center">62</entry><entry align="center">12.6</entry><entry align="center">1.4</entry><entry align="center">50.8</entry></row><row><entry align="center">675</entry><entry align="center">62</entry><entry align="center">12.6</entry><entry align="center">1.4</entry><entry align="center">51.2</entry></row><row><entry align="center">725</entry><entry align="center">62</entry><entry align="center">12.6</entry><entry align="center">1.4</entry><entry align="center">51.1</entry></row><row><entry align="center">775</entry><entry align="center">61.9</entry><entry align="center">12.6</entry><entry align="center">1.4</entry><entry align="center">50.9</entry></row><row><entry align="center">825</entry><entry align="center">61.9</entry><entry align="center">12.6</entry><entry align="center">1.4</entry><entry align="center">50.9</entry></row><row><entry align="center">850</entry><entry align="center">61.9</entry><entry align="center">12.6</entry><entry align="center">1.5</entry><entry align="center">51</entry></row><row><entry align="center">Variation</entry><entry align="center">61.9-62.2</entry><entry align="center">12.5-12.6</entry><entry align="center">1.4-1.6</entry><entry align="center">50.8-51.2</entry></row><row><entry align="center">Standard deviation</entry><entry align="center">0.1</entry><entry align="center">0.06</entry><entry align="center">0.018</entry><entry align="center">0.2</entry></row></tbody></tgroup></table></tables>

0089From the Tables 1 (comparative example) and 3 (present example), it may be seen that having the IR absorbing additive, LaB₆, in the cap layer, causes a big variation in the percent light transmission (LT%), and the percent haze, when compared with the multilayered sheet having the IR absorbing additive in the core layer. From Table 3, it may also be seen that the variations in the percent light transmission, haze and color are smaller than those for the samples of Table 1. Since it is generally desirable to have the haze as low as possible, dispersing the IR absorbing additive in the core layer produces a superior product over a product where the IR absorbing additive is added to the cap layer. <figref idref="f0003">Figure 4</figref> represents photographs of an object taken through two multilayer sheets, one multilayer sheet contained LaB₆ in the core layer, while the other had LaB₆ in the cap layer. From this figure it may be clearly seen that while the object can be clearly seen through the multilayer sheet containing the LaB₆ in the core layer, it is barely visible through the multilayer sheet containing the LaB₆ in the cap layer. It clearly shows the visible variation in color when LaB₆ is used in the cap layer.

0090During this test several other observations were made. As noted above thickness variations of +/- 20 micrometers were observed in the thickness of the cap layer. In order to have an acceptable IR absorption, a target amount of 0.18 grams of LaB₆/m² of polycarbonate was utilized. When this amount of IR absorbing additive is added to a 60 micrometer cap layer rather than a 3 to 6 millimeter core layer, its concentration is much higher in the cap layer, thus leading to an unacceptable level of haze in the multilayer sheet. Additionally, to protect polycarbonate from UV aging, a UV protective coating or UV adsorber containing cap layer is used on the multi layered sheet. A certain concentration of UV absorbers is needed to reach an acceptable level for the UV protection of PC. One could envision reducing the problem of thickness variation of the cap layer and thereby the observed transmission variations by using a thicker cap layer, for example, a cap layer having a thickness of 500 micrometers (0.5 mm). However, apart from practical problems of making such a cap layer, the need for a high UV concentration throughout the cap layer would increase the cost of the entire multilayer sheet.

Example 2

0091This example was undertaken to study the effect of thermoforming the multilayer sheet, on the percent light transmission, solar factor, shading coefficient, and haze. Two 3 millimeter multilayer sheets having LaB₆ concentrations of 0.09 and 0.18 g/m² respectively were thermoformed over the device shown in <figref idref="f0004">Figure 5</figref>. Lab color measurements were made according CIE lab DIN 5033; solar transmission measurements were made according to ISO9050; haze and light transmission were measured according to ASTM D1003. Upon thermoforming the multilayer sheets over the device shown in the <figref idref="f0004">Figure 5</figref>, the sheet shows thickness variations of 1.15 to 2.4 millimeter. The cap layer thickness varies in an amount of about 23 to about 48 micrometers.

Example 3

0092This example describes the preferred range of LaB₆ in the polycarbonate core layer when the thickness of the core layer is 1 millimeter. Polycarbonate samples containing various amounts of LaB₆ and 500ppm Irgaphos168 (CIBA SPECIALTY CHEMICALS CORPORATION) were produced on a Werner and Pfleiderer 25mm twin screw extruder. 1 mm plaques were injection molded on an Engel 75T machine.

0093The percent of IR radiation that was transmitted was measured on a 'Hitachi U3410 UV-VIS-NIR'. The average of the IR transmission between 780nm - 1400 nm was calculated (IR-T%). Irradiation in this wavelength range is most responsible for heating. The results are shown in Table 4 <tables id="tabl0004" num="0004"><table frame="all"><title>Table 4</title><tgroup cols="5"><colspec colnum="1" colname="col1" colwidth="23mm" /><colspec colnum="2" colname="col2" colwidth="20mm" /><colspec colnum="3" colname="col3" colwidth="29mm" /><colspec colnum="4" colname="col4" colwidth="12mm" /><colspec colnum="5" colname="col5" colwidth="13mm" /><thead valign="top"><row valign="bottom"><entry align="center">%LaB6</entry><entry align="center">La B6 g/m²</entry><entry align="center">Average (IR-T%)</entry><entry align="center">LT%</entry><entry align="center">Haze</entry></row><row valign="bottom"><entry align="center">1mm plaque</entry><entry /><entry align="center">780-1400 nm</entry><entry /><entry /></row></thead><tbody><row><entry align="char" char="." charoff="8">0.0000</entry><entry align="char" char="." charoff="9">0.0000</entry><entry align="center">79</entry><entry align="char" char="." charoff="31">91.1</entry><entry align="char" char="." charoff="15">0.9</entry></row><row><entry align="char" char="." charoff="8">0.0016</entry><entry align="char" char="." charoff="9">0.0192</entry><entry align="center">67</entry><entry align="char" char="." charoff="31">87.9</entry><entry align="char" char="." charoff="15">0.78</entry></row><row><entry align="char" char="." charoff="8">0.0024</entry><entry align="char" char="." charoff="9">0.0288</entry><entry align="center">63</entry><entry align="char" char="." charoff="31">86.8</entry><entry align="char" char="." charoff="15">1.07</entry></row><row><entry align="char" char="." charoff="8">0.0032</entry><entry align="char" char="." charoff="9">0.0384</entry><entry align="center">56</entry><entry align="char" char="." charoff="31">84.8</entry><entry align="char" char="." charoff="15">1.12</entry></row><row><entry align="char" char="." charoff="8">0.0064</entry><entry align="char" char="." charoff="9">0.0768</entry><entry align="center">40</entry><entry align="char" char="." charoff="31">79.1</entry><entry align="char" char="." charoff="15">1.37</entry></row><row><entry align="char" char="." charoff="8">0.0160</entry><entry align="char" char="." charoff="9">0.1920</entry><entry align="center">15</entry><entry align="char" char="." charoff="31">63.2</entry><entry align="char" char="." charoff="15">2.16</entry></row><row><entry align="char" char="." charoff="8">0.0320</entry><entry align="char" char="." charoff="9">0.3840</entry><entry align="center">3</entry><entry align="char" char="." charoff="31">40.9</entry><entry align="char" char="." charoff="15">3.37</entry></row><row><entry align="char" char="." charoff="8">0.0640</entry><entry align="char" char="." charoff="9">0.7680</entry><entry align="center">0</entry><entry align="char" char="." charoff="31">21.3</entry><entry align="char" char="." charoff="15">5.29</entry></row></tbody></tgroup></table></tables>

0094The data show that no additional IR absorption effect was obtained when adding more than 0.77% LaB₆ to the polycarbonate core layer, when the thickness of the core layer was 1 millimeter.

0095From the above examples, it may be seen that it is advantageous to use a multilayered sheet, wherein the core layer contains the IR absorbing additive. This protects the IR absorbing additive from the effects of ambient moisture thereby increasing the life of the multilayer sheet. Further the results also demonstrate that there exists a synergy to combining a cap layer containing the UV absorber with a core layer containing the IR absorbing additive. The results clearly show that in the aforementioned configuration, there is improved transparency, lower haze and better color. These multilayered sheets may thus be effectively used in automobiles, residential and office housing.