Alkali-free glass substrate

BACKGROUND OF THE INVENTION

FIELD OF THE INVENTION

0001The present invention relates to an alkali-free glass substrate, more particularly to an alkali-free glass substrate useful as a transparent glass substrate for displays and others.

DESCRIPTION OF RELATED ART

0002Conventionally, an alkali-free glass has been used as a transparent glass for liquid crystal displays. The alkali-free glass particularly for display application is required to be free of bubbles that result in display defects, as well as having satisfactory heat resistance and chemical durability.

0003For such an alkali-free glass, various types of glasses have been proposed. For example, Japanese Patent Kokai No. Hei 6-263473 and Japanese Patent Kohyo No. 2001-500098 disclose alkali-free aluminosilicate glasses.

0004If a bubble-free glass is to be obtained, a gas produced during a batch decomposition must be expelled from a glass melt by a fining gas. In addition, the remaining minute bubbles must be removed during homogenization melting by the reproduced fining gas which renders them larger in sizes and thereby causes them to float in the melt.

0005For the alkali-free glass, particularly for use as a glass substrate for liquid crystal displays, a glass melt has a high viscosity and its melting is carried out at higher temperatures compared to alkali-containing glasses.

0006For this type of alkali-free glass, a batch decomposition occurs generally at 1,300 - 1,500 °C. Accordingly, fining and homogenization are carried out at 1,500 °C or higher temperatures. Under such conditions, As₂O₃ has been widely used as a fining agent which can release a fining gas over a wide temperature range (approximate range of 1,300 - 1,700 °C).

0007However, As₂O₃ is very toxic in nature and possibly causes environmental pollution during glass manufacturing processes or waste glass treatments. For this reason, its use is being increasingly limited.

0008US-A-4 605 632 relates to the production of transparent, high silica glass envelopes for tungsten-halogen lamps consiting essentially, by weight, of 1-2.5% Al₂O₃, 0.25-1% CaO, 0.1-0.25 Na₂O and/or K₂O, 2.5-3.5% B₂O₃, 0.15-0.3% F, and the remainder SiO₂.

SUMMARY OF THE INVENTION

0009It is an object of the present invention to provide an alkali-free glass substrate rendered free of bubbles resulting in display defects without using As₂O₃ as a fining agent.

0010After conduction of various experiments, the inventors of this application have found that the above object can be achieved by using Sb₂O₃ or SnO₂ as a fining agent and controlling a water content in the glass at at least a specific level.

0011That is, the alkali-free glass substrate of the present invention is characterized as comprising a glass which has a β-OH value of 0.5 to 0.65/mm and contains SnO₂ and/or Sb₂O₃.

0012The alkali-free glass substrate comprises a glass containing, by mass percent, 50 - 70 % SiO₂, 10 - 25% Al₂O₃, 5 - 20 % B₂O₃, 0 - 7% MgO, 0 - 10 % CaO, 0 - 10 % BaO, 0 - 10 % SrO and 0 - 5 % ZnO.

0013An As₂O₃ content is preferably 0.4 % or less by mass. The SnO₂ content is preferably 0.05 - 1 % by mass. The Sb₂O₃ content is preferably 0.05 - 3 % by mass. A Cl₂ content is preferably 0.1 % or less by mass.

0014The glass substrate preferably has an area of at least 0.5 m².

0015The alkali-free glass substrate of the present invention is suitable for use as a transparent glass substrate of a liquid crystal display.

0016Because the alkali-free glass substrate of the present invention comprises a glass rendered free of bubbles resulting in display defects without use of As₂O₃, it can be suitably used as a transparent glass substrate for displays. Particularly, this alkali-free glass substrate becomes very advantageous when used in a large size, because such use increases a percentage of non-defectives.

0017Also, the increased β-OH value enables reduction of the amount of B₂O₃ and improves chemical durability.

BEST MODE FOR CARRYING OUT THE INVENTION

0018Japanese Patent Kohyo No. 2001-500098 discloses that if the β-OH value is maintained below 0.5/mm, preferably below 0.45/mm, formation of bubbles at a platinum interface can be prevented. However, clearing of bubbles produced during an initial stage of melting (e.g., during a batch decomposition), what is called, a fineness improvement is not considered at all in Japanese Patent Kohyo No. 2001-500098. The β-OH value disclosed in Japanese Patent Kohyo No. 2001-500098 indicates a water content level obtained under normal melting conditions. In other words, the disclosed β-OH level is comparable to those for conventional alkali-free glasses.

0019Surprisingly, it has been clearly shown that the glass is better fined if the β-OH value is increased to at least a specific value. In this invention, the water content in the glass is adjusted to a high level which is difficult to be attained under normal melting conditions. This contemplates to compensate for the deficiency in fining ability that results from the use of SnO₂ or Sb₂O₃ as an alternative fining agent of As₂O₃. The water present in the glass acts to lower viscosity of the glass and, if contained in a large amount, facilitates melting and fining of the glass. Also, the water itself serves as one fining gas to diffuse into bubbles, increase bubble sizes and allow them to float up.

0020Specifically, Sb₂O₃ releases a fining gas in a lower temperature range compared to As₂O₃, and accordingly use of Sb₂O₃ in a high temperature range (e.g., homogenization melting temperature range) brings a slight shortage of the fining gas. In order to counter such a shortage, the present invention contemplates to allow the glass to contain a large amount of water. The water, if present in a large amount, serves as a fining gas to diffuse into bubbles in the temperature range, thereby compensating for the shortage in volume of the fining gas. On the other hand, SnO₂ releases a fining gas in a higher temperature range compared to As₂O₃, and accordingly use of SnO₂ in a low temperature range (e.g., a batch decomposition temperature range) brings a slight shortage of the fining gas. However, the water, if present in a large amount, lowers viscosity of the glass and facilitates melting thereof in the low temperature range. As a result, the glass is better fined.

0021The water content in the glass, as indicated by the β-OH value, is at 0.5 to 0.65/mm, preferably at 0.51 to 0.65/mm. As the water content in the glass increases, the glass viscosity decreases, while the amount of the water diffusing into bubbles increases. As a result, the glass is better fined.

0022The higher the β-OH value, the better the glass is melted. On the other hand, as the β-OH value increases, the strain point tends to decrease. For such reasons, it is desirable that the β-OH value does not exceed 0.65/mm, particularly 0.6/mm.

0023The β-OH value, indicative of the water content in the glass, can be calculated from the following equation: <maths id="math0001" num=""><math display="block"><mi mathvariant="normal">B</mi><mo mathvariant="normal">-</mo><mi>OH</mi><mo mathvariant="normal">=</mo><mfenced separators=""><mn mathvariant="normal">1</mn><mo mathvariant="normal">/</mo><mi mathvariant="normal">X</mi></mfenced><mo>⁢</mo><msub><mi>LOG</mi><mn mathvariant="normal">10</mn></msub><mfenced separators=""><msub><mi mathvariant="normal">T</mi><mn mathvariant="normal">1</mn></msub><mo mathvariant="normal">/</mo><msub><mi mathvariant="normal">T</mi><mn mathvariant="normal">2</mn></msub></mfenced></math><img file="EP1512671B1_D0001.tif" /></maths> where, <ul id="ul0001" list-style="none" compact="compact"><li>X = glass thickness (mm);</li><li>T₁ = transmittance (%) at the reference wavelength 3,846 cm^-1 (2,600 nm); and</li><li>T₂ = minimum transmittance (%) at and near the hydroxyl absorption wavelength 3,600 cm^-1 (2,800 nm).</li></ul>

0024The glass substrate of the present invention preferably comprises an aluminosilicate glass. More specifically, it desirably comprises an alkali-free glass having a basic composition containing, by mass percentage, 50 - 70 % SiO₂, 10 - 25 % Al₂O₃, 5 - 20 % B₂O₃, 0 - 7 % MgO, 0 - 10 % CaO, 0 - 10 % BaO, 0 - 10 % SrO and 0 - 5 % ZnO. By "alkali-free", as used in the present invention, it is meant that an alkaline metal oxide (Li₂O, Na₂O, K₂O) content is up to 0.2 % by mass.

0025The reasons why the composition of the alkali-free glass substrate should be brought within the above-specified range are given below.

0026SiO₂ is a network component of the glass. Its content is 50 - 70 %, preferably 55 - 70 %, more preferably 55 - 65 %. If the SiO₂ content is below 50 %, the chemical resistance of the glass is lowered. Also, its strain point is lowered so that the heat resistance of the glass deteriorates. The SiO₂ content of exceeding 70 % increases the high-temperature viscosity of the glass so that its melting ability is lowered, as well as increasing the tendency of cristobalite to precipitate via devitrification.

0027Al₂O₃ is a component which improves heat resistance and devitrification tendency of the glass. Its content is 10 - 25 %, preferably 10 - 20 %, more preferably 13 - 18 %. If the Al₂O₃ content is less than 10 %, a devitrification temperature is markedly elevated to result in the increased occurrence of devitrification in the glass. If the content exceeds 25 %, the acid resistance, particularly the resistance to buffered hydrofluoric acid, is lowered to result in the increased occurrence of haze at a surface of the glass substrate.

0028B₂O₃ is a component which acts as a flux to lower the viscosity and thereby facilitate melting of the glass. Its content is 5 - 20 %, preferably 5 - 15 %, more preferably 8.5 - 12 %. If the B₂O₃ content is less than 5 %, its effect as a flux becomes insufficient. On the other hand, the higher B₂O₃ content tends to lower the acid resistance. Particularly when the B₂O₃ content is greater than 15 %, the resistance of the glass decreases against hydrochloric acid and its strain point drops so that the heat resistance is lowered.

0029As described above, B₂O₃ is a component which affects the acid resistance of the glass. The reduction of its content improves the acid durability of the glass. A metal film or an ITO film is formed on a surface of a transparent glass substrate for use in liquid crystal displays. Since such a film is patterned by acid etching, the glass must have a high degree of acid resistance. It is accordingly desirable to reduce the B₂O₃ content in the glass. Since boron (B) is a chemical substance designated in the PRTR Act, the reduction of the B₂O₃ content is also desirable from an environmental point of view. However, simple reduction of the B₂O₃ content may in turn raise other problems, including deterioration of the melting ability and increase of bubbles. In the present invention, the β-OH value of the glass is maintained at a high level. This restrains elevation of glass viscosity that occurs when the B₂O₃ content is reduced. It is believed that as the β-OH value increases, the glass viscosity decreases to thereby facilitate reduction of the B₂O₃ content.

0030MgO is a component which lowers the high-temperature viscosity of the glass without a drop of the strain point and thereby facilitates melting of the glass. Its content is 0 - 7 %, preferably 0 - 3.5 %. If the MgO content is greater than 10 %, the glass exhibits a marked reduction in resistance to buffered hydrofluoric acid.

0031CaO functions in a manner similar to MgO. Its content is 0 - 10 %. If the CaO content is greater than 15 %, the glass exhibits a marked reduction in resistance to buffered hydrofluoric acid.

0032BaO is a component which improves not only the chemical durability but also devitrification tendency of the glass. Its content is 0 - 10 %, preferably 0 - 7 %. If the BaO content is greater than 10 %, a strain point drops to deteriorate the heat resistance of the glass.

0033SrO affects in a manner similar to BaO. Its content is 0 - 10 %, preferably 0 - 7 %, more preferably 0.1 - 7 %. If the SrO content exceeds 10 %, the occurrence of devitrification undesirably increases.

0034For portable devices such as portable telephones and notebook computers, the lightweight device designs have been required to increase handiness during carriage. In order to achieve such lightweight designs, a glass substrate for use therein must be reduced in density. Preferably, this type of glass substrate exhibits a low thermal expansion coefficient as approximate to that (about 30 - 33 x 10^-7/°C) of a thin-film transistor (TFT) material, specifically a thermal expansion coefficient of 28 - 40 x 10^-7/°C, because a large difference in thermal expansion coefficient between the glass substrate and the TFT material results in the occurrence of warp. BaO and SrO are the glass components which also affect the density and thermal expansion coefficient of the glass. In order to obtain a low-density and low-expansion glass, their total content must be controlled not to exceed 15 %, preferably 10 %.

0035ZnO is a component which improves resistance to buffered hydrofluoric acid as well as divitrification resistance. Its content is 0 - 10 %, preferably 0 - 5 %. If the ZnO content exceeds 10 %, the occurrence of devitrification of the glass increases. Also, a strain point drops to result in the failure to obtain sufficient heat resistance.

0036The glass contains at least one of SnO₂ and Sb₂O₃ as an essential fining component. The SnO₂ content is between 0.05 and 1 %, with 0.05 - 0.5 % being particularly preferred. The Sb₂O₃ content is 0.05 - 3 %, with 0.05 - 2 % being particularly preferred. SnO₂ shows a tendency to precipitate in the glass when its content exceeds 1 %. If the Sb₂O₃ content exceeds 3 %, the density of the glass increases. Also, the strain point of the glass is dropped to deteriorate its heat resistance. If the SnO₂ or Sb₂O₃ content is below 0.05 %, it becomes difficult to obtain a sufficient fining effect.

0037From an environmental point of view, the As₂O₃ content should be maintained at as low a level as possible, preferably within 0.4 %, more preferably within 0.1 %, further preferably within 0.05 %.

0038Besides the aforementioned components, the glass in the present invention may further contain ZrO₂, TiO₂, Fe₂O₃, P₂O₅, Y₂O₃, Nb₂O₃ and La₂O₃ in the total amount of up to 5 %, for example. CeO₂, MnO₂, WO₃, Ta₂O₅, Nb₇O₅, SO₃, chlorides and fluorides can also be used as a fining agent. However, the present invention finds chlorides as being inferior to the others, because they cause a marked reduction of the water content in the glass. The use amount of a chloride is limited to 0.1 % or below, particularly to 0.04 % or below, in terms of a Cl₂ content calculated from a chlorine component remaining in the glass. It would be advisable to exclude the chloride, if possible.

0039A method of producing the alkali-free glass substrate of the present invention is below described.

0040First, a glass batch is prepared such that a glass having a desired composition results.

0041Then, the prepared glass batch is melted.

0042Thereafter, the molten glass is formed into a desired shape to obtain a glass substrate. For display applications, the molten glass may be formed into a thin sheet using an overflow downdraw method, a slot downdraw method, or a float method. Use of the overflowdowndrawmethod is particularly preferred because it results in obtaining a glass sheet having a very superior surface quality.

0043In the above production process, the β-OH value of an alkali-free aluminosilicate glass having the above composition does not exceed 0.485/mm, particularly 0.5/mm, unless a proper measure is positively devised to increase a water content.

0044For this reason, in the production of the alkali-free glass of the present invention, various measures should be devised to increase the water content. For example, one or more of the following measures may be adopted selectively: (1) a high water-content batch material (e.g., a hydroxide material) is selected; (2) water is added to the batch; (3) a component (e.g., chlorine) which lowers the water content in the glass, if used, is reduced in amount or excluded; (4) oxygen combustion is carried out during melting of the glass, or a water vapor is introduced directly into a melting furnace to thereby increase the water content in an atmosphere inside the furnace; (5) a water vapor bubbling is carried out through the molten glass; and (6) a large-scale melting furnace is employed, or a flow rate of the molten glass is slowed down to thereby allow the molten glass to stay for an extended period in a melting furnace under the atmosphere controlled at a high water content.

0045The thus-produced, alkali-free glass substrate of the present invention is characterized as including a very small number of bubbles. In general, a percentage of non-defectives drops dramatically owing to bubbles in glass if a substrate is rendered larger in size. Hence, the reduction in number of bubbles is very advantageous for a large-scale substrate such as having an area of 0.5 m² or larger (specifically 630 mm x 830 mm or larger), particularly 1.0 m² or larger (specifically 950 mm x 1,150 mm or larger), further 2. 5 m² or larger (specifically 1,450 mm x 1,750 mm or larger). The suitable number of bubbles is within the range that does not exceed 0.2/kg, preferably 0.1/kg, more preferably 0.05/kg.

DESCRIPTION OF PREFERRED EXAMPLES

0046The following example illustrates the alkali-free glass substrate of the present invention. <tables id="tabl0001" num="0001"><table frame="all"><title>Table 1</title><tgroup cols="7"><colspec colnum="1" colname="col1" colwidth="27mm" colsep="0" /><colspec colnum="2" colname="col2" colwidth="20mm" /><colspec colnum="3" colname="col3" colwidth="24mm" /><colspec colnum="4" colname="col4" colwidth="13mm" /><colspec colnum="5" colname="col5" colwidth="24mm" /><colspec colnum="6" colname="col6" colwidth="24mm" /><colspec colnum="7" colname="col7" colwidth="24mm" /><thead><row><entry namest="col1" nameend="col2" align="left" valign="top">Sample No.</entry><entry align="center" valign="middle">1</entry><entry align="center" valign="middle">2</entry><entry align="center" valign="middle">3</entry><entry align="center" valign="middle">4</entry><entry align="center" valign="middle">5</entry></row><row rowsep="0"><entry namest="col1" nameend="col2" align="left" valign="top">Glass Composition</entry><entry align="center" valign="middle" /><entry align="center" valign="middle" /><entry align="center" valign="middle" /><entry align="center" valign="middle" /><entry align="center" valign="middle" /></row></thead><tbody><row rowsep="0"><entry>SiO₂</entry><entry /><entry align="center" valign="middle">59.5</entry><entry align="center" valign="middle">59.4</entry><entry align="center" valign="middle">59.4</entry><entry align="center" valign="middle">59.6</entry><entry align="center" valign="middle">59.4</entry></row><row rowsep="0"><entry>Al₂O₃</entry><entry /><entry align="center" valign="middle">15.3</entry><entry align="center" valign="middle">15.2</entry><entry align="center" valign="middle">15.4</entry><entry align="center" valign="middle">14.8</entry><entry align="center" valign="middle">15.3</entry></row><row rowsep="0"><entry>B₂O₃</entry><entry /><entry align="center" valign="middle">9.9</entry><entry align="center" valign="middle">9.6</entry><entry align="center" valign="middle">9.9</entry><entry align="center" valign="middle">9.8</entry><entry align="center" valign="middle">9.8</entry></row><row rowsep="0"><entry>MgO</entry><entry /><entry align="center" valign="middle">0.02</entry><entry align="center" valign="middle">0.02</entry><entry align="center" valign="middle">0.02</entry><entry align="center" valign="middle">0.01</entry><entry align="center" valign="middle">0.01</entry></row><row rowsep="0"><entry>CaO</entry><entry /><entry align="center" valign="middle">5.40</entry><entry align="center" valign="middle">5.36</entry><entry align="center" valign="middle">5.50</entry><entry align="center" valign="middle">5.44</entry><entry align="center" valign="middle">5.45</entry></row><row rowsep="0"><entry>SrO</entry><entry /><entry align="center" valign="middle">6.10</entry><entry align="center" valign="middle">6.09</entry><entry align="center" valign="middle">6.07</entry><entry align="center" valign="middle">6.07</entry><entry align="center" valign="middle">6.01</entry></row><row rowsep="0"><entry>BaO</entry><entry /><entry align="center" valign="middle">2.20</entry><entry align="center" valign="middle">2.19</entry><entry align="center" valign="middle">2.19</entry><entry align="center" valign="middle">2.21</entry><entry align="center" valign="middle">2.19</entry></row><row rowsep="0"><entry>ZnO</entry><entry /><entry align="center" valign="middle">0.40</entry><entry align="center" valign="middle">0.42</entry><entry align="center" valign="middle">0.40</entry><entry align="center" valign="middle">0.48</entry><entry align="center" valign="middle">0.48</entry></row><row rowsep="0"><entry>ZrO₂</entry><entry /><entry align="center" valign="middle">0.10</entry><entry align="center" valign="middle">0.15</entry><entry align="center" valign="middle">0.10</entry><entry align="center" valign="middle">0.05</entry><entry align="center" valign="middle">0.08</entry></row><row rowsep="0"><entry>As₂O₃</entry><entry /><entry align="center" valign="middle">0.02</entry><entry align="center" valign="middle">0.33</entry><entry align="center" valign="middle">0.70</entry><entry align="center" valign="middle">0.06</entry><entry align="center" valign="middle">0.03</entry></row><row rowsep="0"><entry>Sb₂O₃</entry><entry /><entry align="center" valign="middle">0.92</entry><entry align="center" valign="middle">0.77</entry><entry align="center" valign="middle">0.36</entry><entry align="center" valign="middle">0.90</entry><entry align="center" valign="middle">0.94</entry></row><row rowsep="0"><entry>SnO₂</entry><entry /><entry align="center" valign="middle">0.18</entry><entry align="center" valign="middle">0.13</entry><entry align="center" valign="middle">0.01</entry><entry align="center" valign="middle">0.18</entry><entry align="center" valign="middle">0.06</entry></row><row><entry>Cl₂</entry><entry /><entry align="center" valign="middle"><0.01</entry><entry align="center" valign="middle">0.01</entry><entry align="center" valign="middle">0.05</entry><entry align="center" valign="middle">0.13</entry><entry align="center" valign="middle">0.23</entry></row><row><entry>β-OH</entry><entry align="right">(/mm)</entry><entry align="center" valign="middle">0.540</entry><entry align="center" valign="middle">0.512</entry><entry align="center" valign="middle">0.419</entry><entry align="center" valign="middle">0.292</entry><entry align="center" valign="middle">0.241</entry></row><row rowsep="0"><entry namest="col1" nameend="col2" align="left">Number of Bubbles</entry><entry morerows="1" rowsep="1" align="center" valign="middle">0.10</entry><entry morerows="1" rowsep="1" align="center" valign="middle">0.08</entry><entry morerows="1" rowsep="1" align="center" valign="middle">0.03</entry><entry morerows="1" rowsep="1" align="center" valign="middle">0.85</entry><entry morerows="1" rowsep="1" align="center" valign="middle">35.6</entry></row><row><entry /><entry align="right">(/kg)</entry></row><row><entry>Density</entry><entry align="right">(g/cm²)</entry><entry align="center" valign="middle">Unmeasured</entry><entry align="center" valign="middle">2.502</entry><entry align="center" valign="middle">Unmeasured</entry><entry align="center" valign="middle">Unmeasured</entry><entry align="center" valign="middle">Unmeasured</entry></row><row rowsep="0"><entry namest="col1" nameend="col2" align="left">Expansion Coefficient</entry><entry align="center" valign="middle">Unmeasured</entry><entry align="center" valign="middle">37.3</entry><entry align="center" valign="middle">Unmeasured</entry><entry align="center" valign="middle">Unmeasured</entry><entry align="center" valign="middle">Unmeasured</entry></row><row><entry /><entry align="right">(×10^-7/°C)</entry><entry align="center" valign="middle" /><entry align="center" valign="middle" /><entry align="center" valign="middle" /><entry align="center" valign="middle" /><entry align="center" valign="middle" /></row><row rowsep="0"><entry>Strain Point</entry><entry align="right">(°C)</entry><entry align="center" valign="middle" /><entry align="center" valign="middle">652</entry><entry align="center" valign="middle" /><entry align="center" valign="middle" /><entry align="center" valign="middle" /></row><row rowsep="0"><entry>Annealing Point</entry><entry align="right">(°C)</entry><entry align="center" valign="middle" /><entry align="center" valign="middle">708</entry><entry align="center" valign="middle" /><entry align="center" valign="middle" /><entry align="center" valign="middle" /></row><row rowsep="0"><entry>Softening Point</entry><entry align="right">(°C)</entry><entry morerows="1" align="center" valign="middle">Unmeasured</entry><entry align="center" valign="middle">955</entry><entry morerows="1" align="center" valign="middle">Unmeasured</entry><entry morerows="1" align="center" valign="middle">Unmeasured</entry><entry morerows="1" align="center" valign="middle">Unmeasured</entry></row><row rowsep="0"><entry>10⁴</entry><entry align="right">(°C)</entry><entry align="center" valign="middle">1291</entry></row><row rowsep="0"><entry>10³</entry><entry align="right">(°C)</entry><entry align="center" valign="middle" /><entry align="center" valign="middle">1459</entry><entry align="center" valign="middle" /><entry align="center" valign="middle" /><entry align="center" valign="middle" /></row><row><entry>10^2.5</entry><entry align="right">(°C)</entry><entry align="center" valign="middle" /><entry align="center" valign="middle">1570</entry><entry align="center" valign="middle" /><entry align="center" valign="middle" /><entry align="center" valign="middle" /></row></tbody></tgroup></table></tables>

0047Each sample shown in the Table was fabricated in accordance with the following procedure.

0048First, a glass batch having the composition specified in the Table was prepared, mixed and then melted in a continuous melting furnace at a maximum temperature of 1,650 °C. The molten glass was formed into a sheet by an overflow downdraw method and then cut to obtain an alkali-free substrate sample having a size of 1,000 x 1,200 x 0.7 mm for various evaluations. In the fabrication of the sample No. 1, a water content in an atmosphere inside the melting furnace was increased to increase a water content of the resulting glass. In the fabrication of the sample No. 2, a high water-content batchmaterial was selected to increase a water content of the resulting glass.

0049The β-OH value of each glass was determined by measuring its light transmittance using FT-IR and making a calculation using the following equation: <maths id="math0002" num=""><math display="block"><mi mathvariant="normal">B</mi><mo mathvariant="normal">-</mo><mi>OH value</mi><mo mathvariant="normal">=</mo><mfenced separators=""><mn mathvariant="normal">1</mn><mo mathvariant="normal">/</mo><mi mathvariant="normal">X</mi></mfenced><mo>⁢</mo><msub><mi>LOG</mi><mn mathvariant="normal">10</mn></msub><mfenced separators=""><msub><mi mathvariant="normal">T</mi><mn mathvariant="normal">1</mn></msub><mo mathvariant="normal">/</mo><msub><mi mathvariant="normal">T</mi><mn mathvariant="normal">2</mn></msub></mfenced></math><img file="EP1512671B1_D0002.tif" /></maths> where, <ul id="ul0002" list-style="none" compact="compact"><li>X = glass thickness (mm);</li><li>T₁ = transmittance (%) at the reference wavelength 3,846 cm^-1; and</li><li>T₂ = minimum transmittance (%) at and near the hydroxyl absorption wavelength 3,600 cm^-1.</li></ul>

0050The fineness was evaluated by counting the number of 100 µm and larger size bubbles present in the glass and reducing the result to the number of bubbles per kg of the glass. The density was determined by a well-known Archimedes' method. The thermal expansion coefficient was given in terms of a mean thermal expansion coefficient measured over the 30 - 380 °C temperature range using a dilatometer. The strain point and annealing point were measured according to the method specified in ASTM C336-71. The softening point was measured according to the method specified in ASTM C338-73. A platinum ball pull-up method was utilized to measure temperatures which correspond to viscosities at 10⁴, 10³ and 10^2.5.

UTILITY IN INDUSTRY

0051The alkali-free glass substrate of the present invention has application on liquid crystal displays and others. For example, it can be used as a glass substrate for flat displays such as electroluminescent displays; as a cover glass for image sensors such as charge-coupled devices, equimultiple solid-state image pickup proximity sensors and CMOS image sensors; and as a glass substrate for hard disks and filters.