Thermoset adhesive films
Abstract
This invention is a film adhesive prepared from an adhesive composition comprising a polymer system, a film forming rubber compound, and curing agents for the polymeric system. The polymer system comprises a base polymer and electron donor and electron acceptor functionality.

Term
Term ended
Projected expiry passed 12 May 2023, 3.4 years ago.
- Priority
- Filed
- Published
- Projected expiry
- Today
32 claims: 4 independent, 28 dependent
- 1A film adhesive prepared from materials comprising (i) a polymer containing no electron donor or acceptor functionality having a molecular weight in the range of 2,000 to 1,000,000, (ii) an independent electron donor compound and (iii) an independent electron acceptor compound.
- 9A film adhesive prepared from (i) a polymer substituted with pendant electron acceptor functionality having a molecular weight in the range of 2,000 to 1,000,000, (ii) an independent electron donor compound, and optionally (iii) an independent electron acceptor compound
- 17A film adhesive prepared from (i) a polymer having pendant electron donor functionality having a molecular weight in the range of 2,000 to 1,000,000, (ii) an independent electron acceptor compound and optionally (iii) an independent electron donor compound;
- 25A film adhesive prepared from (i) a polymer having pendant electron donor and electron acceptor functionality and having a molecular weight in the range of 2,000 to 1,000,000, or a combination of a polymer having pendant electron donor functionality and having a molecular weight in the range of 2,000 to 1,000,000, and a polymer having pendant electron acceptor functionality and having a molecular weight in the range of 2,000 to 1,000,000;optionally (ii) an independent electron donor compound;and optionally (III) an independent electron acceptor compound.
Independent claims4
71 paragraphs in 8 sections, as filed
FIELD OF THE INVENTION
0001This invention relates to film adhesives, and particularly film adhesives for use In semiconductor packaging.
BACKGROUND OF THE INVENTION
0002A common mode of electronics packaging involves affixing semiconductor devices onto substrates by means of an adhesive tape. Epoxy compounds and resins currently are among the most commonly used materials for current film based adhesive applications, such as die attach, in which a semiconductor die is attached to a substrate. In a typical embodiment, a film-forming rubber polymer is blended with epoxy resins and a hardening agent. These compositions can then be cured upon application of heat, which results in the development of a thermoset network. One drawback to epoxy adhesives is their ultimate latency. Typically, these materials must be stored at low temperature to avoid premature advancement of the adhesive. Moreover, the speed of cure for these compositions is relatively slow making the die-attach operation the least efficient step in the total assembly manufacturing process for wirebonded integrated circuit packages. This creates a need for a film adhesive that can be rapidly cured compared to the conventional thermoset film adhesives, and particularly to films containing no epoxy.
SUMMARY OF THE INVENTION
0003This invention is a film adhesive prepared from an adhesive composition comprising a polymer system, a film forming rubber compound, and curing agents for the polymeric system. In a preferred embodiment the polymer system contains no epoxy functionality. The polymer system comprises a base polymer and electron donor and electron acceptor functionality. The electron donor and electron acceptor functionality can be pendant from the base polymer, or can be interdispersed with the base polymer as independent compounds. In some cases, the base polymer can function as a film-forming rubber compound. The film can be prepared directly as a monolayer from the adhesive composition, or from coating the adhesive composition onto both sides of a thermal resistant tape substrate.
DETAILED DESCRIPTION OF THE INVENTION
0004The polymer system for preparing the film adhesives will contain a base polymer (hereinafter "polymer" or "base polymer") and electron donor and electron acceptor functionality. The system can be segregated into several classes: (1) an unsubstituted base polymer blended with an independent electron donor compound and an independent electron acceptor compound; (2) a base polymer substituted with pendant electron acceptor functionality, blended with an independent electron donor compound, and optionally an independent electron acceptor compound; (3) a base polymer substituted with pendant electron donor functionality, blended with an independent electron acceptor compound and optionally an independent electron donor compound; (4) a base polymer substituted with pendant electron donor and electron acceptor functionality, or a combination of a base polymer substituted with pendant electron donor functionality and a base polymer substituted with pendant electron acceptor functionality, optionally blended with an independent electron donor compound, or an independent electron acceptor compound, or both.
0005Preferably, there will be a 1:1 molar ratio of electron donor to electron acceptor, however, the molar ratio can range from 0.01 - 1.0 : 1.0 - 0.01.
0006A suitable base polymer in the polymer system of the inventive film adhesive is prepared from acrylic and/or vinyl monomers using standard polymerization techniques. The acrylic monomers that may be used to form the base polymer include α,β-unsaturated mono and dicarboxylic acids having three to five carbon atoms and acrylate ester monomers (alkyl esters of acrylic and methacrylic acid in which the alkyl groups contain one to fourteen carbon atoms). Examples are methyl acryate, methyl methacrylate, n-octyl acrylate, n-nonyl methacrylate, and their corresponding branched isomers, such as, 2-ethylhexyl acrylate. The vinyl monomers that may be used to form the base polymer include vinyl esters, vinyl ethers, vinyl halides, vinylidene halides, and nitriles of ethylenically unsaturated hydrocarbons. Examples are vinyl acetate, acrylamide, 1-octyl acrylamide, acrylic acid, vinyl ethyl ether, vinyl chloride, vinylidene chloride, acrylonitrile, maleic anhydride, and styrene.
0007Another suitable base polymer in the polymer system of the inventive film adhesive is prepared from conjugated diene and/or vinyl monomers using standard polymerization techniques. The conjugated diene monomers that may be used to form the polymer base include butadiene-1,3, 2-chlorobutadiene-1/3, isoprene, piperylene and conjugated hexadienes. The vinyl monomers that may be used to form the base polymer include styrene, α-methylstyrene, divinylbenzene, vinyl chloride, vinyl acetate, vinylidene chloride, methyl methacrylate, ethyl acrylate, vinylpyridine, acrylonitrile, methacrylonltrlle, methacrylic acid, itaconic acid and acrylic acid.
0008Alternatively, the base polymer can be purchased commercially. Suitable commercially available polymers include acrylonitrile-butadiene rubbers from Zeon Chemicals and styrene-acrylic copolymers from Johnson Polymer.
0009In those systems in which the base polymer is substituted with electron donor and/or electron acceptor functionality, the degree of substitution can be varied to suit the specific requirements for cross-link density in the final applications. Suitable substitution levels range from 6 to 500, preferably from 10 to 200.
0010The base polymer, whether substituted or unsubstituted will have a molecular weight range of 2,000 to 1,000,000. The glass transition temperature (Tg) will vary depending on the specific base polymer. For example, the Tg for butadiene polymers ranges from -100°C to 25°C, and for modified acrylic polymers, from 15°C to 50°C.
0011Suitable electron donor functionality includes vinyl ether groups, vinyl silane groups, and carbon to carbon double bonds external to an aromatic ring and conjugated with the unsaturation in the aromatic ring. Suitable electron acceptor groups include maleimides, acrylates, fumarates and maleates.
0012Examples of suitable starting materials for reacting with complementary functionality on the base polymer in order to add the electron donor or electron acceptor functionality pendant to the base polymer include: for electron donor functionality, hydroxybutyl vinyl ether, cinnamyl alcohol, 1,4-cyclohexane-dimethanol monovinyl ether, 3-isopropenyl- α,α-dimethylbenzyl isocyanate, isoeugenol, and the derivatives of the aforementioned compounds; for electron acceptor functionality, dioctyl maleate, dibutyl maleate, dioctyl fumarate, dibutyl fumarate, N-(6-hydroxyhexyl) maleimide, 6-maleimidocaproic acid, and 3-maleimidopropionic acid.
0013Independent electron donor compounds for blending with the base polymer include compounds having at least two vinyl ether groups, or having at least two carbon to carbon double bonds external to aromatic rings and conjugated with the unsaturation in the aromatic ring. Suitable divinyl ether examples include compounds such as bis[4-(vinyloxy)butyl]tere- phthalate, bis[4-(vinyloxy)butyl] (4-methyl-1,3-phenylene)biscarbamate, bis[4-(vinyloxy) butyl] 1,6-hexanediylbiscarbamate, 4-(vinyloxy)butyl stearate, and bis[4-(vinyloxy)butyl] (methylenedi-4,1-phenylene)biscarbamate (sold under the trade name Vectomer from Morflex, Inc). Exemplary compounds having at least two carbon to carbon double bonds external to aromatic rings and conjugated with the unsaturation in the aromatic ring include; the adduct of tricyclodecane-dimethanol and 3-isopropenyl-α,α-dimethylbenzyl isocyanate (m-TMI) having the structure <chemistry id="chem0001" num="0001"><img file="EP1362901A2_D0001.tif" /></chemistry> the adduct of 2-hydroxyethyl disulfide and m-TMI having the structure <chemistry id="chem0002" num="0002"><img file="EP1362901A2_D0002.tif" /></chemistry> the adduct of cyanurate/trlfunctional isocyanate and cinnamyl alcohol having the structure <chemistry id="chem0003" num="0003"><img file="EP1362901A2_D0003.tif" /></chemistry> the adduct of 1,3-propanediol and m-TMI having the structure <chemistry id="chem0004" num="0004"><img file="EP1362901A2_D0004.tif" /></chemistry> the adduct of 1,4-butanediol and m-TMI having the structure <chemistry id="chem0005" num="0005"><img file="EP1362901A2_D0005.tif" /></chemistry> and the adduct of cinnamyl alcohol and 1,6-diisocyanatohexane having the structure <chemistry id="chem0006" num="0006"><img file="EP1362901A2_D0006.tif" /></chemistry> These compounds can be prepared by standard synthetic methods known to those skilled in the art without undue experimentation.
0014Independent electron acceptor compounds for blending with the base polymer include resins having at least two intramolecular maleimide, acrylate, fumarate or maleate groups. Examples of bismaleimides include: N,N'-ethylene-bis-maleimide, N,N'-butylene-bis-maleimide, N,N'-phenylene-bis-maleimide, N,N'-hexamethylene-bis-maleimide, N,N'-4,4'-diphenyl methane-bis-maleimide, N,N'-4,4'-diphenyl ether-bis-maleimide, N,N'-4,4'-diphenyl sulfone-bis-maleimide, N,N'-4,4'-dicyclohexyl methane-bis-maleimide, N,N'-xylylene-bis-maleimide, N,N'-diphenyl cyclohexane-bis-maleimide and the like.
0015Suitable film forming resins or compounds include acrylic polymers (sold under the trade name TEISAN RESIN from Nagase ChemteX Corporation) and acrylonitrile-butadiene elastomers (sold under the trade name NIPOL from Zeon Chemicals). These materials, in general, will be present in the adhesive composition from which the film will be prepared, in an amount ranging from 10% to 70%. preferably 15% to 50%, by weight of the adhesive formulation. Other levels may be suitable depending on the end use application, and optimal levels can be determined without undue experimentation on the part of the formulator.
0016Suitable curing agents for the polymer system are thermal initiators and photoinitiators, present in an amount of 0.1% to 10%, preferably 0.1% to 5.0%, by weight of the polymer system. Preferred thermal initiators include peroxides, such as butyl peroctoates and dicumyl peroxide, and azo compounds, such as 2,2'-azobis(2-methyl-propanenitrile) and 2,2'-azobis(2-methyl-butanenitrile). A preferred series of photoinitiators is one sold under the trademark Irgacure by Ciba Specialty Chemicals. In some formulations, both thermal initiation and photoinitiation may be desirable; for example, the curing process can be started by irradiation, and in a later processing step curing can be completed by the application of heat to accomplish the thermal cure. In general, these compositions will cure within a temperature range of 70°C to 250°C, and curing will be effected at a temperature within the range of ten seconds to three hours. The time and temperature curing profile of each formulation will vary with the specific electron donor compound and the other components of the formulation, but the parameters of a curing profile can be determined by a practitioner skilled in the art without undue experimentation.
0017In some cases, it may be an advantage to add an epoxy compound or resin to the adhesive composition. Suitable epoxy compounds or resins include bifunctional and polyfinctional epoxy resins such as bisphenol A-type epoxy, cresol novolak epoxy, or phenol novolak epoxy. Another suitable epoxy resin is a multifunctional epoxy resin from Dainippon Ink and Chemicals, Ino. (sold under the product number HP-7200). When added to the formulation, the epoxy will be present in an amount up to 80% by weight.
0018If an epoxy compound is added, the formulation will need to contain a curing or hardening agent for the epoxy. Suitable curing agents include amines, polyamides, acid anhydrides, polysulfides, trifluoroboron, and bisphenol A, bisphenol F and bisphenol S, which are compounds having at least two phenolic hydroxyl groups in one molecule. A curing accelerator may also be used in combination with the curing agent. Suitable curing accelerators include imidazoles, such as 2-methylimidazole, 2-ethyl-4-methylimidazole, 4-methyl-2-phenylimidazole, and 1-cyanoethyl-2-phenylimidazolium trimellitate. The curing agents and accelerators are used in standard amounts known to those skilled in the art.
0019Other materials, such as adhesion promoters (epoxides, sllanes), dyes, pigments, and rheology modifiers, may be added as desired for modification of final properties. Such materials and the amounts needed are within the expertise of those skilled in the art.
0020Filler particles that enhance the mechanical, electrical conductivity, or thermal conductivity may also be added. Suitable conductive filters are carbon black, graphite, gold, silver, copper, platinum, palladium, nickel, aluminum, silicon carbide, boron nitride, diamond, and alumina. Suitable nonconductive fillers are particles of vermiculite, mica, wollastonite, calcium carbonate, titania, sand, glass, fused silica, fumed silica, barium sulfate, and halogenated ethylene polymers, such as tetrafluoroethylene, trifluoroethylene, vinylidene fluoride, vinyl fluoride, vinylidene chloride, and vinyl chloride. When present, fillers will be in amounts of 0.1% to 90%, preferably from 5% to 90%, by weight of the formulation.
POLYMER SYNTHETIC EXAMPLES
0021EXAMPLE 1. This example discloses a butadiene/acrylo-nitrile base polymer containing pendant acrylate (electron acceptor) functionality. <chemistry id="chem0007" num="0007"><img file="EP1362901A2_D0007.tif" /></chemistry> where x = 50, y = 5, n = 310, p = 678, and q = 59, based on GPC and NMR analysis (one skilled in the art will recognize that these values may vary slightly due to the polymeric character of the material).
0022Carboxylated butadiene/acrylonitrile polymer (50.6 g) (Nipol 1072 from Zeon Chemicals) was solvated in 4-methyl-2-pentanone (MIBK, 250 mL) in a 500mL four-necked flask equipped with a mechanical stirrer, condenser and drying tube. Glycidyl methacrylate (9.78 g) and tetrabutylphosphonium acetate solution (0.58 g) (TBPAAC, catalyst, 70% by weight of tetrabutylphosphonium acid acetate in methanol from Morton International, Inc.) were added to the mixture with stirring. The mixture was heated to 110°C and held at that temperature for approximately twelve hours. The final product has a viscosity of 4870 mPa.s at ambient temperature and according to titration results of the residual carbpxylic acid of the modified Nipol rubber, the carboxyl conversion is about 90%. According to GPC analysis, the weight average molecular weight and the number average molecular weight of the modified Nipol polymer are 430,500 g/mol and 60,900 g/mol, respectively.
0023EXAMPLE 2. This example discloses a butadiene/acrylonitrile base polymer with pendant styrenic (electron donor) functionality, <chemistry id="chem0008" num="0008"><img file="EP1362901A2_D0008.tif" /></chemistry> where x = 56, y = 16, n = 401, p = 877, and q = 76 based on GPC and NMR analysis (one skilled in the art will recognize that these values may vary slightly due to the polymeric character of the material).
0024Carboxylated butadiene/acrylonitrile polymer (38.0 g) (Nipol 1072 from Zeon Chemicals) was solvated in 4-methyl-2-pentanone (MIBK, 255 mL) in a 500mL four-necked flask equipped with a mechanical stirrer, condenser and drying tube. Isoeugenol glycidyl ether (11.43 g) and tetrabutyl-phosphonium acetate solution (0.62 g) (TBPAAC, catalyst, 70% by wetight of tetrabutylphosphonium acid acetate in methanol from Morton International, Inc.) were added into the mixture with stirring. The mixture was heated to 110°C and held at that temperature for approximately fourteen hours. According to titration results of the residual carboxylic acid of the modified Nipol rubber, the carboxyl conversion is about 87%. The product was purified by precipitation in methanol three times. According to GPC analysis, the weight average molecular weight and the number average molecular weight of the modified Nipol polymer are 554,400 g/mol and 89,100 g/mol, respectively.
0025EXAMPLE 3. This example discloses a butadiene/acrylonitrile base polymer with pendant styrenic (electron donor) functionality, <chemistry id="chem0009" num="0009"><img file="EP1362901A2_D0009.tif" /></chemistry> where x = 49, y = 7, n = 310, p = 739, and q = 59 based on GPC and NMR analysis (one skilled in the art will recognize that these values may vary slightly due to the polymeric character of the material)..
0026Carboxylated butadiene/acrylonitrile polymer (53.8 g) (Nipol 1072 from Zeon Chemicals) was solvated in 4-methyl-2-pentanone (MIBK, 360 mL) in a 1L four-necked flask equipped with a mechanical stirrer, condenser and drying tube. Glycidyl N-(3-isopropenyl-α,α-dimethylbenzyl) carbamate (14.8g) and tetrabutylphosphonium acetate solution (0.54 g) (TBPAAC, catalyst) were added into the mixture with stirring. The mixture was heated to 105°C and held at that temperature for approximately fifteen hours. The final product has a viscosity of 2000 mPa.s at ambient temperature and according to titration results, the carboxyl conversion is about 88%. According to GPC analysis, the weight average molecular weight and the number average molecular weight of the modified Nipol polymer are 666,000 g/mol and 75,600 g/mol, respectively.
0027EXAMPLE 4. This example discloses a butadiene/ acrylonitrile base polymer with pendant cinnamyl (electron donor) functionality, <chemistry id="chem0010" num="0010"><img file="EP1362901A2_D0010.tif" /></chemistry><chemistry id="chem0011" num="0011"><img file="EP1362901A2_D0011.tif" /></chemistry>
0028A solution of carboxylated butadiene/acrylonitrile polymer (one molar equivalent based on the carboxylic acid) in toluene is reacted with excess thionyl chloride at 50°C for approximately fourteen hours. The excess thionyl chloride and the solvent are removed under reduced pressure to afford the butadiene/acrylonitrile polymer with pendant acid chloride.
0029One molar equivalent of cinnamyl alcohol and one molar equivalent of triethylamine are mixed in dry toluene at 0°C, to which is added the butadiene/acrylonitrile polymer with pendant acid chloride dissolved in dry toluene (one molar equivalent based on the acid chloride). The mixture is allowed to react overnight. The product is purified by precipitation in methanol three times.
0030EXAMPLE 5. This example discloses a butadiene/ acrylonitrile base polymer with pendant cinnamyl (electron donor) functionality, <chemistry id="chem0012" num="0012"><img file="EP1362901A2_D0012.tif" /></chemistry>
0031One molar equivalent of cinnamyl amine and one molar equivalent of triethylamine are mixed in dry toluene at 0°C, to which is added the butadiene/acrylonitrile polymer with pendant acid chloride dissolved in dry toluene (one molar equivalent based on the acid chloride). The mixture is allowed to react overnight. The product is purified by precipitation in methanol three times.
0032EXAMPLE 6. This example discloses a butadiene/ acrylonitrile base polymer with pendant styrenic (electron donor) functionality, <chemistry id="chem0013" num="0013"><img file="EP1362901A2_D0013.tif" /></chemistry><chemistry id="chem0014" num="0014"><img file="EP1362901A2_D0014.tif" /></chemistry>
0033One molar equivalent of isoeugenol and one molar equivalent of triethylamine are mixed in dry toluene at 0°C, to which is added the butadiene/acrylonitrile polymer with pendant acid chloride dissolved in dry toluene (one molar equivalent based on the acid chloride) The mixture is allowed to react overnight. The product is purified by precipitation in methanol three times.
0034EXAMPLE 7. This example discloses a butadiene/ acrylonitrile base polymer with pendant styrenic (electron donor) functionality, <chemistry id="chem0015" num="0015"><img file="EP1362901A2_D0015.tif" /></chemistry>
0035One molar equivalent of 4-vinyl benzyl amine and one molar equivalent of triethylamine are mixed in dry toluene at 0°C, to which is added the butadiene/acrylonitrile polymer with pendant acid chloride dissolved in dry toluene (one molar equivalent based on the acid chloride). The mixture is allowed to react overnight. The product is purified by precipitation in methanol three times.
0036EXAMPLE 8. This example discloses a butadiene/ acrylonitrile base polymer with pendant vinyl ether (electron donor) functionality. <chemistry id="chem0016" num="0016"><img file="EP1362901A2_D0016.tif" /></chemistry>
0037One molar equivalent of 4-hydroxybutyl vinyl ether and one molar equivalent of triethylamine are mixed in dry toluene at 0°C, to which is added the butadienelacrylonitrile polymer with pendant acid chloride dissolved in dry toluene (one molar equivalent based on the acid chloride). The mixture is allowed to react overnight. The product is purified by precipitation in methanol three times.
0038EXAMPLE 9. This example discloses a butadiene/ acrylonitrile base polymer with pendant vinyl ether (electron donor) functionality, <chemistry id="chem0017" num="0017"><img file="EP1362901A2_D0017.tif" /></chemistry>
0039One molar equivalent of 2-aminoethyl vinyl ether and one molar equivalent of triethylamine are mixed in dry toluene at 0°C, to which is added the butadiene/acrylonitrile polymer with pendant acid chloride dissolved in dry toluene (one molar equivalent based on the acid chloride). The mixture is allowed to react overnight. The product is purified by precipitation in methanol three times.
0040EXAMPLE 10. This example discloses a hydroxylated styrene/butadiene base polymer with pendant styrenic (electron donor) functionality, <chemistry id="chem0018" num="0018"><img file="EP1362901A2_D0018.tif" /></chemistry><chemistry id="chem0019" num="0019"><img file="EP1362901A2_D0019.tif" /></chemistry>
0041One molar equivalent (based on hydroxyl function) of hydroxylated styrene/butadiene polymer is solvated in dry toluene at 90°C under nitrogen, followed by the addition of one molar equivalent of 3-isopropenyl-α,α-dimethylbenzyl isocyanate (m-TMI) together with 0.07% of dibutyltin dilaurate (catalyst) based on the total amount of reactants. The resulting mixture is heated for an additional twenty-four hours under nitrogen. After removal of the solvent under reduced pressure, the product is obtained in almost quantitative yield.
0042EXAMPLE 11. This example discloses a hydroxylated styrene/butadiene base polymer having pendant styrenic (electron donor) functionality, <chemistry id="chem0020" num="0020"><img file="EP1362901A2_D0020.tif" /></chemistry>
0043One molar equivalent of butadiene/styrene polymer based on the 1,2-vinyl bonds is solvated in dry toluene under nitrogen and 0.3 molar equivalent of 2-mercaptoethanol is added into the mixture, followed by heating to 75°C. A solution of azodiisobutyronitrile (AIBN) in toluene is then added to the mixture. The mixture is stirred at 75°C for 7 hours. The product is purified by precipitation in methanol three times.
0044One molar equivalent (based on hydroxyl function) of hydroxylated styrene/butadiene polymer prepared as above is solvated in dry toluene at 90°C under nitrogen, followed by the addition of one molar equivalent of 3-isopropenyl-α,α-dimethylbenzyl isocyanate (m-TMI) together with 0.07% of dibutyltin dilaurate (catalyst) based on the total amount of reactants. The resulting mixture is heated for an additional twenty-four hours under nitrogen. After removal of the solvent under reduced pressure, the product is obtained in almost quantitative yield.
0045EXAMPLE 12. This example discloses a hydroxylated styrene/butadiene base polymer having pendant maleimide (electron acceptor) functionality, <chemistry id="chem0021" num="0021"><img file="EP1362901A2_D0021.tif" /></chemistry>
0046One molar equivalent (based on hydroxyl function) of hydroxylated styrene/butadiene polymer prepared as in Example 11 is solvated in dry toluene at 90°C under nitrogen, followed by the addition of one molar equivalent of 6-maleimidocaproic acid in toluene. Catalytic amount of sulfuric acid is then introduced into the mixture. The mixture is heated to reflux and water generated during the reaction is removed by azeotrope. The reaction is run overnight. The product is purified by precipitation in methanol three times.
0047EXAMPLE 13. This example discloses a polybutadiene base polymer with pendant styrenic (electron donor) functionality, <chemistry id="chem0022" num="0022"><img file="EP1362901A2_D0022.tif" /></chemistry>
0048One molar equivalent (based on anhydride function) of polybutadiene adducted with maleic anhydride (trade name: Ricon 131MA20, produced by Sartomer Company) is solvated in acetone, followed by the dropwise addition of one molar equivalent of cinnamyl amine. The reaction mixture is stirred for 6 hours. After acetone is removed by reduced pressure, the polymer is solvated in toluene and the product is purified by precipitation in methanol three times.
0049EXAMPLE 14. This example discloses a styrene/acrylic base polymer with pendant acrylate (electron acceptor) functionality. <chemistry id="chem0023" num="0023"><img file="EP1362901A2_D0023.tif" /></chemistry> where m = 11 based on GPC and NMR analysis (one skilled in the art will recognize that this value may vary slightly due to the polymeric character of the material).
0050In a 500mL four-necked flask equipped with a mechanical stirrer, condenser, addition funnel and a N<sub>2</sub> inlet, was charged with 45.02 g of a styrene-acrylic polymer (Joncryl 587 from Johnson Polymer) in methylene chloride (100 mL). After the polymer was solvated under nitrogen at room temperature, the solution was cooled to 0°C and 6.83 g of triethylamine was added to the mixture. To this resulting mixture was added dropwise 6.11 g of acryloyl chloride. The mixture was allowed to react for an additional 6 hours. After washing with aqueous solutions several times until the aqueous phase is neutral, the resulting organic layer was dried over Mg<sub>2</sub>SO<sub>4</sub> and silica gel. After the solvents were removed under reduced pressure, a white solid was obtained.
0051EXAMPLE 15. This example discloses a styrene/acrylic base polymer with pendant styrenic (electron donor) functionality, <chemistry id="chem0024" num="0024"><img file="EP1362901A2_D0024.tif" /></chemistry> where m = 11 based on GPC and NMR analysis (one skilled in the art will recognize that this value may vary slightly due to the polymeric character of the material).
0052In a 1L four-necked flask equipped with a mechanical stirrer, condenser, addition funnel and a N<sub>3</sub> inlet, was charged with 126.7 g of a styrene acrylic polymer (Joncryl 587 from Johnson Polymer) in methyl ethyl ketone (620 mL). After the polymer was solvated at the refluxing temperature of the solvent under nitrogen, 40,58 g of 3-isopropenyl-α,α-dimethylbenzyl isocyanate (m-TMI) was added to the mixture together with 0.12 g of dibutyltin dilaurate (catalyst). The resulting mixture was heated for an additional twenty-four hours under nitrogen. After removal of the solvent under reduced pressure, a white solid was obtained in almost quantitative yield. According to GPC analysis, the weight average molecular weight and the number average molecular weight of the modified styrene-acrylic polymer are 15,600 g/mol and 8,400 g/mol, respectively. According to DSC analysis, the glass transition temperature of the modified styrene-acrylic polymer is approximately 40°C.
ADHESIVE FILM EXAMPLES
0053EXAMPLE 16. An adhesive film was prepared from a polymer system comprising an unsubstituted acrylic/rubber base polymer, an independent electron acceptor resin, an independent electron donor resin, and an epoxy resin, which components and parts by weight used are identified in Table 1. The film formulation also contained a radical initiator, hardeners for the epoxy, a filler and adhesion promoters. <tables id="tabl0001" num="0001"><table frame="all"><title>Table 1</title><tgroup cols="3" colsep="1" rowsep="1"><colspec colnum="1" colname="col1" colwidth="52.50mm" /><colspec colnum="2" colname="col2" colwidth="52.50mm" /><colspec colnum="3" colname="col3" colwidth="52.50mm" /><thead valign="top"><row><entry namest="col1" nameend="col1" align="left">Component Chemical Class or Function</entry><entry namest="col2" nameend="col2" align="left">Source</entry><entry namest="col3" nameend="col3" align="left">Parts by wt.</entry></row></thead><tbody valign="top"><row><entry namest="col1" nameend="col1" align="left">Base polymer Acrylic rubber</entry><entry namest="col2" nameend="col2" align="left">SG-80DR Nagase ChemteX Corp.</entry><entry namest="col3" nameend="col3" align="left">5</entry></row><row><entry namest="col1" nameend="col1" align="left">Electron acceptor Bismaleimide</entry><entry namest="col2" nameend="col2" align="left">Matrimid 5292A Ciba Specialty Chemicals Corporation</entry><entry namest="col3" nameend="col3" align="left">3</entry></row><row><entry namest="col1" nameend="col1" align="left">Electron donor Structure I</entry><entry namest="col2" nameend="col2" align="left">Adduct of tricyclodecane-dimethanol/m-TMI</entry><entry namest="col3" nameend="col3" align="left">2.5</entry></row><row rowsep="1"><entry namest="col1" nameend="col1" align="left">Epoxy</entry><entry namest="col2" nameend="col2" align="left">HP-7200H Dainippon Ink and Chemicals, Inc.</entry><entry namest="col3" nameend="col3" align="left">3.5</entry></row></tbody></tgroup></table></tables>
0054The electron donor had the following structure: <chemistry id="chem0025" num="0025"><img file="EP1362901A2_D0025.tif" /></chemistry>
0055The film formulation was prepared by mixing the components in methyl ethyl ketone with stirring, followed by vacuum degassing. The varnish obtained was coated to a thickness of 2 mil onto a 5 mil thick silicone-treated release-liner and then dried by heating at 100°C for 10 minutes to form a partially cured adhesive film with a thickness of 1mil.
0056EXAMPLE 17. An adhesive film was prepared from a polymer system comprising a poly(butadiene) base polymer substituted with pendant electron acceptor functionality, an independent electron acceptor resin, an independent electron donor resin, and an epoxy resin, which components and parts by weight used are identified in Table 2. The film formulation also contained a radical initiator, hardeners for the epoxy, and adhesion promoters. <tables id="tabl0002" num="0002"><table frame="all"><title>Table 2</title><tgroup cols="3" colsep="1" rowsep="1"><colspec colnum="1" colname="col1" colwidth="52.50mm" /><colspec colnum="2" colname="col2" colwidth="52.50mm" /><colspec colnum="3" colname="col3" colwidth="52.50mm" /><thead valign="top"><row><entry namest="col1" nameend="col1" align="left">Component Chemical Class or Function</entry><entry namest="col2" nameend="col2" align="left">Source</entry><entry namest="col3" nameend="col3" align="left">Parts by wt.</entry></row></thead><tbody valign="top"><row><entry namest="col1" nameend="col1" align="left">Butadiene base polymer substituted with pendant electron acceptor functionality</entry><entry namest="col2" nameend="col2" align="left">Polymer from Example 1.</entry><entry namest="col3" nameend="col3" align="left">2</entry></row><row><entry namest="col1" nameend="col1" align="left">Electron acceptor Bismaleimide</entry><entry namest="col2" nameend="col2" align="left">Matrimid 5292A Ciba Specialty Chemicals Corporation</entry><entry namest="col3" nameend="col3" align="left">1</entry></row><row><entry namest="col1" nameend="col1" align="left">Electron donor Structure I</entry><entry namest="col2" nameend="col2" align="left">Adduct of tricyclodecane-dimethanol/m-TMI</entry><entry namest="col3" nameend="col3" align="left">2.5</entry></row><row rowsep="1"><entry namest="col1" nameend="col1" align="left">Epoxy</entry><entry namest="col2" nameend="col2" align="left">HP-7200H Dainippon Ink and Chemicals, Inc.</entry><entry namest="col3" nameend="col3" align="left">3.5</entry></row></tbody></tgroup></table></tables>
0057The film formulation was prepared by mixing the components in methyl ethyl ketone with stirring, followed by vacuum degassing. The varnish obtained was coated to a thickness of 2 mil onto a 5 mil thick silicone-treated release-liner and then dried by heating at 100°C for 10 minutes to form a partially cured adhesive film with a thickness of 1mil.
0058EXAMPLE 18. An adhesive film was prepared from a polymer system comprising a styrene/acrylic base polymer substituted with pendant electron donor functionality, an independent electron acceptor resin, an independent electron donor resin, and an acrylonitrile/butadiene rubber, which components and parts by weight used are identified in Table 3. The film formulation also contained a radical initiator and adhesion promoters. <tables id="tabl0003" num="0003"><table frame="all"><title>Table 3</title><tgroup cols="3" colsep="1" rowsep="1"><colspec colnum="1" colname="col1" colwidth="52.50mm" /><colspec colnum="2" colname="col2" colwidth="52.50mm" /><colspec colnum="3" colname="col3" colwidth="52.50mm" /><thead valign="top"><row><entry namest="col1" nameend="col1" align="left">Component Chemical Class or Function</entry><entry namest="col2" nameend="col2" align="left">Source</entry><entry namest="col3" nameend="col3" align="left">Parts by wt.</entry></row></thead><tbody valign="top"><row><entry namest="col1" nameend="col1" align="left">Sytrene/acrylic base polymer substituted with pendant electron donor functionality</entry><entry namest="col2" nameend="col2" align="left">Polymer from Example 15</entry><entry namest="col3" nameend="col3" align="left">2</entry></row><row><entry namest="col1" nameend="col1" align="left">Electron acceptor Bismaleimide</entry><entry namest="col2" nameend="col2" align="left">Matrimid 5292A Ciba Specialty Chemicals Corporation</entry><entry namest="col3" nameend="col3" align="left">5</entry></row><row><entry namest="col1" nameend="col1" align="left">Electron donor Structure I</entry><entry namest="col2" nameend="col2" align="left">Adduct of tricyclodecane-dimethanol/m-TMI</entry><entry namest="col3" nameend="col3" align="left">1.75</entry></row><row rowsep="1"><entry namest="col1" nameend="col1" align="left">Acrylonitrile/butadiene rubber</entry><entry namest="col2" nameend="col3" align="left">Zeon Chemicals 4</entry></row></tbody></tgroup></table></tables>
0059The film formulation was prepared by mixing the components in methyl ethyl ketone with stirring, followed by vacuum degassing. The varnish obtained was coated to a thickness of 2 mil onto a 5 mil thick silicone-treated release-liner and then dried by heating at 100°C for 10 minutes to form a partially cured adhesive film with a thickness of 1mil.
0060EXAMPLE 19. An adhesive film was prepared from a polymer system comprising a styrene/acrylic base polymer substituted with pendant electron donor functionality, an acrylonitrile/butadiene base polymer substituted with pendant electron donor functionality, an independent electron acceptor resin, an independent electron donor resin, which components and parts by weight used are identified in Table 4. The film formulation also contained a radical initiator, filler, and adhesion promoters. <tables id="tabl0004" num="0004"><table frame="all"><title>Table 4</title><tgroup cols="3" colsep="1" rowsep="1"><colspec colnum="1" colname="col1" colwidth="52.50mm" /><colspec colnum="2" colname="col2" colwidth="52.50mm" /><colspec colnum="3" colname="col3" colwidth="52.50mm" /><thead valign="top"><row><entry namest="col1" nameend="col1" align="left">Component Chemical Class or Function</entry><entry namest="col2" nameend="col2" align="left">Source</entry><entry namest="col3" nameend="col3" align="left">Parts by wt.</entry></row></thead><tbody valign="top"><row><entry namest="col1" nameend="col1" align="left">Sytrene/acrylic base polymer substituted with pendant electron donor functionality</entry><entry namest="col2" nameend="col2" align="left">Polymer from Example 15</entry><entry namest="col3" nameend="col3" align="left">2</entry></row><row><entry namest="col1" nameend="col1" align="left">Acrylonitrile/butadiene base polymer substituted with pendant electron donor functionallty</entry><entry namest="col2" nameend="col2" align="left">Polymer from Example 2</entry><entry namest="col3" nameend="col3" align="left">4</entry></row><row><entry namest="col1" nameend="col1" align="left">Electron acceptor Bismaleimide</entry><entry namest="col2" nameend="col2" align="left">Matrimid 5292A Ciba Specialty Chemicals Corporation</entry><entry namest="col3" nameend="col3" align="left">5</entry></row><row rowsep="1"><entry namest="col1" nameend="col1" align="left">Electron donor Structure I</entry><entry namest="col2" nameend="col2" align="left">Adduct of tricyclodecane-dimethanol/m-TMI</entry><entry namest="col3" nameend="col3" align="left">1.8</entry></row></tbody></tgroup></table></tables>
0061The film formulation was prepared by mixing the components in methyl ethyl ketone with stirring, followed by vacuum degassing. The varnish obtained was coated to a thickness of 2 mil onto a 5 mil thick sillcone-treated release-liner and then dried by heating at 100°C for 10 minutes to form a partially cured adhesive film with a thickness of 1mil.
0062EXAMPLE 20. An adhesive film was prepared from a polymer system comprising a acrylonitrile/butadiene base polymer substituted with pendant electron donor functionality, an independent electron acceptor resin, an independent electron donor resin, and an epoxy, which components and parts by weight used are identified in Table 5. The film formulation also contained a radical initiator, hardeners for the epoxy, filler, and adhesion promoters. <tables id="tabl0005" num="0005"><table frame="all"><title>Table 5</title><tgroup cols="3" colsep="1" rowsep="1"><colspec colnum="1" colname="col1" colwidth="52.50mm" /><colspec colnum="2" colname="col2" colwidth="52.50mm" /><colspec colnum="3" colname="col3" colwidth="52.50mm" /><thead valign="top"><row><entry namest="col1" nameend="col1" align="left">Component Chemical Class or Function</entry><entry namest="col2" nameend="col2" align="left">Source</entry><entry namest="col3" nameend="col3" align="left">Parts by wt.</entry></row></thead><tbody valign="top"><row><entry namest="col1" nameend="col1" align="left">Acrylonitrile/butadiene base polymer substituted with pendant electron donor functionality</entry><entry namest="col2" nameend="col2" align="left">Polymer from Example 2</entry><entry namest="col3" nameend="col3" align="left">2.5</entry></row><row><entry namest="col1" nameend="col1" align="left">Electron acceptor Bismaleimide</entry><entry namest="col2" nameend="col2" align="left">Matrimid 5292A Ciba Specialty Chemicals Corporation</entry><entry namest="col3" nameend="col3" align="left">3</entry></row><row><entry namest="col1" nameend="col1" align="left">Electron donor Structure I</entry><entry namest="col2" nameend="col2" align="left">Adduct of tricyclodecane-dimethanol/m-TMI</entry><entry namest="col3" nameend="col3" align="left">2.5</entry></row><row rowsep="1"><entry namest="col1" nameend="col1" align="left">Epoxy</entry><entry namest="col2" nameend="col2" align="left">HP-7200H Dainippon Ink and Chemicals, Inc.</entry><entry namest="col3" nameend="col3" align="left">3.5</entry></row></tbody></tgroup></table></tables>
0063The film formulation was prepared by mixing the components in methyl ethyl ketone with stirring, followed by vacuum degassing. The varnish obtained was coated to a thickness of 2 mil onto a 5 mil thick silicone-treated release-liner and then dried by heating at 100°C for 10 minutes to form a partially cured adhesive film with a thickness of 1mil.
0064EXAMPLE 21. An adhesive film was prepared from a polymer system comprising a acrylonitrile/butadiene base polymer substituted with pendant electron donor functionality, an independent electron acceptor resin, an independent electron donor resin, and an epoxy, which components and parts by weight used are identified in Table 6. The film formulation also contained a radical initiator, hardeners for the epoxy, filler, and adhesion promoters. <tables id="tabl0006" num="0006"><table frame="all"><title>Table 6</title><tgroup cols="3" colsep="1" rowsep="1"><colspec colnum="1" colname="col1" colwidth="52.50mm" /><colspec colnum="2" colname="col2" colwidth="52.50mm" /><colspec colnum="3" colname="col3" colwidth="52.50mm" /><thead valign="top"><row><entry namest="col1" nameend="col1" align="left">Component Chemical Class or Function</entry><entry namest="col2" nameend="col2" align="left">Source</entry><entry namest="col3" nameend="col3" align="left">Parts by wt.</entry></row></thead><tbody valign="top"><row><entry namest="col1" nameend="col1" align="left">Acrylonitrile/butadiene base polymer substituted with pendant electron donor functionality</entry><entry namest="col2" nameend="col2" align="left">Polymer from Example 3</entry><entry namest="col3" nameend="col3" align="left">2.5</entry></row><row><entry namest="col1" nameend="col1" align="left">Electron acceptor Bismaleimide</entry><entry namest="col2" nameend="col2" align="left">Matrimid 5292A Ciba Specialty Chemicals Corporation</entry><entry namest="col3" nameend="col3" align="left">3</entry></row><row><entry namest="col1" nameend="col1" align="left">Electron donor Structure I</entry><entry namest="col2" nameend="col2" align="left">Adduct of trlcyclodecane-dimethanol/m-TMI</entry><entry namest="col3" nameend="col3" align="left">2.5</entry></row><row rowsep="1"><entry namest="col1" nameend="col1" align="left">Epoxy</entry><entry namest="col2" nameend="col2" align="left">HP-7200H Dainippon Ink and Chemicals, Inc.</entry><entry namest="col3" nameend="col3" align="left">3.5</entry></row></tbody></tgroup></table></tables>
0065The film formulation was prepared by mixing the components in methyl ethyl ketone with stirring, followed by vacuum degassing. The varnish obtained was coated to a thickness of 2 mil onto a 5 mil thick silicone-treated release-liner and then dried by heating at 100°C for 10 minutes to form a partially cured adhesive film with a thickness of 1mil.
0066EXAMPLE 22. An adhesive film was prepared from a polymer system comprising an acrylonitrile/butadiene base polymer substituted with pendant electron acceptor functionality, a styrene/acrylic base polymer substituted with pendant electron donor functionality, an independent electron acceptor resin, an independent electron donor resin, which components and parts by weight used are identified in Table 7. The film formulation also contained a radical initiator. <tables id="tabl0007" num="0007"><table frame="all"><title>Table 7</title><tgroup cols="3" colsep="1" rowsep="1"><colspec colnum="1" colname="col1" colwidth="52.50mm" /><colspec colnum="2" colname="col2" colwidth="52.50mm" /><colspec colnum="3" colname="col3" colwidth="52.50mm" /><thead valign="top"><row><entry namest="col1" nameend="col1" align="left">Component Chemical Class or Function</entry><entry namest="col2" nameend="col2" align="left">Source</entry><entry namest="col3" nameend="col3" align="left">Parts by wt.</entry></row></thead><tbody valign="top"><row><entry namest="col1" nameend="col1" align="left">Acrylonitrile/butadiene base polymer substituted with pendant electron donor functionality</entry><entry namest="col2" nameend="col2" align="left">Polymer from Example 1</entry><entry namest="col3" nameend="col3" align="left">2.5</entry></row><row><entry namest="col1" nameend="col1" align="left">Styrene/acrylic base polymer substituted with pendant electron donor functionality</entry><entry namest="col2" nameend="col2" align="left">Polymer from Example 15</entry><entry namest="col3" nameend="col3" align="left">3</entry></row><row><entry namest="col1" nameend="col1" align="left">Electron acceptor Bismaleimide</entry><entry namest="col2" nameend="col2" align="left">Matrimid 5292A Ciba Specialty Chemicals Corporation</entry><entry namest="col3" nameend="col3" align="left">5</entry></row><row rowsep="1"><entry namest="col1" nameend="col1" align="left">Electron donor Structure I</entry><entry namest="col2" nameend="col2" align="left">Adduct of tricyclodecane-dimethanol/m-TMI</entry><entry namest="col3" nameend="col3" align="left">1.8</entry></row></tbody></tgroup></table></tables>
0067The film formulation was prepared by mixing the components in methyl ethyl ketone with stirring, followed by vacuum degassing. The varnish obtained was coated to a thickness of 2 mil onto a 5 mil thick silicone-treated release-liner and then dried by heating at 100°C for 10 minutes to form a partially cured adhesive film with a thickness of 1mil.
COMPARATIVE ADHESIVE FILM EXAMPLE
0068EXAMPLE 23. This example discloses an adhesive film prepared with a polymeric system containing an acrylonitrile/butadiene base polymer, and epoxy resin, and no electron donor nor electron acceptor functionality. The formulation also contained a phenol novolak resin and curing agents. The formulation components and parts by weight are disclosed in Table 8. <tables id="tabl0008" num="0008"><table frame="all"><title>Table 8</title><tgroup cols="3" colsep="1" rowsep="1"><colspec colnum="1" colname="col1" colwidth="52.50mm" /><colspec colnum="2" colname="col2" colwidth="52.50mm" /><colspec colnum="3" colname="col3" colwidth="52.50mm" /><thead valign="top"><row><entry namest="col1" nameend="col1" align="left">Component Chemical Class or Function</entry><entry namest="col2" nameend="col2" align="left">Source</entry><entry namest="col3" nameend="col3" align="left">Parts by wt.</entry></row></thead><tbody valign="top"><row><entry namest="col1" nameend="col1" align="left">Acrylonitrile/butadiene rubber</entry><entry namest="col2" nameend="col2" align="left">Nipol 1072 Zeon Chemicals</entry><entry namest="col3" nameend="col3" align="left">2.7</entry></row><row><entry namest="col1" nameend="col1" align="left">Epoxy</entry><entry namest="col2" nameend="col2" align="left">HP-7200H Dainippon Ink and Chemicals, Inc.</entry><entry namest="col3" nameend="col3" align="left">3.5</entry></row><row rowsep="1"><entry namest="col1" nameend="col1" align="left">Phenol Novolak resin</entry><entry namest="col2" nameend="col2" align="left">HRJ-1166 Schenectady International Inc.</entry><entry namest="col3" nameend="col3" align="left">1</entry></row></tbody></tgroup></table></tables>
0069The film formulation was prepared by mixing the components in methyl ethyl ketone with stirring, followed by vacuum degassing. The varnish obtained was coated to a thickness of 2 mil onto a 5 mil thick silicone-treated release-liner and then dried by heating at 100°C for 10 minutes to form a partially cured adhesive film with a thickness of 1mil.
PERFORMANCE EXAMPLES
0070EXAMPLE 24. A sample of each film produced in Examples 16-22 and Comparative Example 23 was used to bond a 100 by 100 square mil silicon die to a PI flex substrate at 120°C in 5 seconds and cured at 180°C for one minute. The die shear strength of these bare packages was measured at 180°C on a Dage Series 4000 Bondtester.
0071The results are disclosed in Table 9 and demonstrate that the inventive films have superior adhesive strength. <tables id="tabl0009" num="0009"><table frame="all"><title>Table 9</title><tgroup cols="2" colsep="1" rowsep="1"><colspec colnum="1" colname="col1" colwidth="78.75mm" /><colspec colnum="2" colname="col2" colwidth="78.75mm" /><thead valign="top"><row><entry namest="col1" nameend="col2" align="center">DIE SHEAR STRENGTH in Kg Force @ 180°C</entry></row><row><entry namest="col1" nameend="col1" align="center">Cure condition</entry><entry namest="col2" nameend="col2" align="center">180°C/1 min</entry></row></thead><tbody valign="top"><row><entry namest="col1" nameend="col1" align="center">Die shear strength measure temperature</entry><entry namest="col2" nameend="col2" align="center">180°C</entry></row><row><entry namest="col1" nameend="col1" align="center">Example 16</entry><entry namest="col2" nameend="col2" align="center">1.86</entry></row><row><entry namest="col1" nameend="col1" align="center">Example 17</entry><entry namest="col2" nameend="col2" align="center">0.90</entry></row><row><entry namest="col1" nameend="col1" align="center">Example 18</entry><entry namest="col2" nameend="col2" align="center">2.22</entry></row><row><entry namest="col1" nameend="col1" align="center">Example 19</entry><entry namest="col2" nameend="col2" align="center">1.93</entry></row><row><entry namest="col1" nameend="col1" align="center">Example 20</entry><entry namest="col2" nameend="col2" align="center">2.78</entry></row><row><entry namest="col1" nameend="col1" align="center">Example 21</entry><entry namest="col2" nameend="col2" align="center">2.80</entry></row><row><entry namest="col1" nameend="col1" align="center">Example 22</entry><entry namest="col2" nameend="col2" align="center">3,00</entry></row><row rowsep="1"><entry namest="col1" nameend="col1" align="center">Comparative Example 23</entry><entry namest="col2" nameend="col2" align="center">0.26</entry></row></tbody></tgroup></table></tables>
Contents8
49 sheets
Sheet 1 Sheet 2 Sheet 3 Sheet 4 Sheet 5 Sheet 6 Sheet 7 Sheet 8 Sheet 9 Sheet 10 Sheet 11 Sheet 12 Sheet 13 Sheet 14 Sheet 15 Sheet 16 Sheet 17 Sheet 18 Sheet 19 Sheet 20 Sheet 21 Sheet 22 Sheet 23 Sheet 24 Sheet 25 Sheet 26 Sheet 27 Sheet 28 Sheet 29 Sheet 30 Sheet 31 Sheet 32 Sheet 33 Sheet 34 Sheet 35 Sheet 36 Sheet 37 Sheet 38 Sheet 39 Sheet 40 Sheet 41 Sheet 42 Sheet 43 Sheet 44 Sheet 45 Sheet 46 Sheet 47 Sheet 48 Sheet 49
Every citation, both ways
| Document | Relation | Office | Cited during |
|---|---|---|---|
| US7541406B2 | Cited by | United States of America | Applicant |
| US7674842B2 | Cited by | United States of America | Applicant |
| US7449515B2 | Cited by | United States of America | Applicant |
| EP1156034A2 | Cites | European Patent Office (EPO) | Search report |
| EP1156053A2 | Cites | European Patent Office (EPO) | Search report |
| EP1156068A1 | Cites | European Patent Office (EPO) | Search report |
| US6307001B1 | Cites | United States of America | Search report |
14 members in 6 offices; this record represents the family
Priority claims4
| Document | Office | Kind | Date |
|---|---|---|---|
| 146387 | United States of America | – | |
| 14638702 | United States of America | A | |
| US20020146387 | – | – | – |
| 146387 | – | – | – |
Members14
| Document | Office | Kind | |
|---|---|---|---|
| EP1362901A2This record | European Patent Office (EPO) | A2 | |
| US2003232926A1 | United States of America | A1 | |
| KR20040030203A | Republic of Korea | A | |
| TW200406477A | Taiwan Province of China | A | |
| EP1362901A3 | European Patent Office (EPO) | A3 | |
| JP2004161990A | Japan | A | |
| US2005137340A1 | United States of America | A1 | |
| US2006030672A1 | United States of America | A1 | |
| EP1362901B1 | European Patent Office (EPO) | B1 | |
| DE60303972D1 | Germany | D1 | |
| DE60303972T2 | Germany | T2 | |
| JP4028431B2 | Japan | B2 | |
| US7326754B2 | United States of America | B2 | |
| TWI296008B | Taiwan Province of China | B |
28 legal events, as 2 offices reported them to INPADOC
Over the term
Point at a mark for the eventEvents
| Event | Code | Office | |
|---|---|---|---|
| Lapsed in a contracting state [announced via postgrant information from national office to epo]LapsedPG25 | PG25 | EP | |
| Lapsed in a contracting state [announced via postgrant information from national office to epo]LapsedPG25 | PG25 | EP | |
| Lapsed in a contracting state [announced via postgrant information from national office to epo]LapsedPG25 | PG25 | EP | |
| Annual fee paid to national office [announced via postgrant information from national office to epo]GrantedPGFP | PGFP | EP | |
| Notification of lapseLapsedST | ST | FR | |
| Annual fee paid to national office [announced via postgrant information from national office to epo]GrantedPGFP | PGFP | EP | |
| Annual fee paid to national office [announced via postgrant information from national office to epo]GrantedPGFP | PGFP | EP | |
| No opposition filedOpposition26N | 26N | EP | |
| No opposition filed within time limitOppositionORIGINAL CODE: 0009261PLBE | PLBE | EP | |
| Information on the status of an ep patent application or granted ep patentGrantedSTATUS: NO OPPOSITION FILED WITHIN TIME LIMITSTAA | STAA | EP | |
| Fr: translation filedET | ET | EP | |
| Corresponds to:REF | REF | EP | |
| Designated contracting statesAK | AK | EP | |
| (expected) grantORIGINAL CODE: 0009210GRAA | GRAA | EP | |
| Grant fee paidORIGINAL CODE: EPIDOSNIGR3GRAS | GRAS | EP | |
| Despatch of communication of intention to grant a patentORIGINAL CODE: EPIDOSNIGR1GRAP | GRAP | EP | |
| Designated contracting states (corrected)RBV | RBV | EP | |
| First examination report despatched17Q | 17Q | EP | |
| Designation fees paidAKX | AKX | EP | |
| Request for examination filed17P | 17P | EP | |
| Designated contracting statesAK | AK | EP | |
| Request for extension of the european patentAX | AX | EP | |
| Information provided on ipc code assigned before grantRIC1 | RIC1 | EP | |
| Information provided on ipc code assigned before grantRIC1 | RIC1 | EP | |
| Search report despatchedORIGINAL CODE: 0009013PUAL | PUAL | EP | |
| Designated contracting statesAK | AK | EP | |
| Request for extension of the european patentAX | AX | EP | |
| Public reference made under article 153(3) epc to a published international application that has entered the european phaseORIGINAL CODE: 0009012PUAI | PUAI | EP |
Numbers
- Publication
- 1362901
- Publication, DOCDB
- 1362901
- Publication, EPODOC
- EP1362901
- Application
- 30098032
- Application, DOCDB
- 03009803
- Application, EPODOC
- EP20030009803
Titles3
- German
- Wärmehärtbare Klebefilme
- English
- Thermoset adhesive films
- French
- Films adhesifs thermodurcissables
Classification
- CPC, 15
- C08F267/10
- C09J11/06
- C08L25/00
- C08L33/00
- C08L55/00
- C09J5/10
- C09J2301/414
- C09J2425/00
- C09J2433/00
- C09J2455/00
- C09J109/02
- C09J125/08
- C09J133/20
- C09J157/00
- C09J201/00
- IPC, 13
- C09J7 00
- C08L25 00
- C08L33 00
- C08L55 00
- C09J5 10
- C09J11 06
- C09J109 02
- C09J125 08
- C09J133 00
- C09J133 20
- C09J157 00
- C09J201 00
- C09J201 02
Designated states3
- Contracting states, 2
- Türkiye
- Italy
- Extension states, 1
- North Macedonia