Foam collar and boat incorporating same

BACKGROUND OF THE INVENTION

1.

Field of the Invention

0001The present invention relates to a foam collar system for boats which is affixed to the external surface of the boat hull.

2.

Description of the Prior Art

0002The present invention is directed to solving the problem of providing an external fender system for protecting the hull of a boat. The fender system must not interfere with the normal operation of the boat while providing sufficient protection for the hull of the boat when mooring the boat or bringing the boat along side another boat for boarding. The fender system must also be aesthetically pleasing.

0003Several constructions for fenders and/or auxiliary flotation for boats are known from the prior art. For example, U.S. Patent No. 5,205,235 (Hodges) relates to a system of elongate rails installed on the exterior hull surfaces of boats and projecting externally from the exterior hull surfaces. These elongate rails include a skin made from a woven fabric material and an interior made of polyethylene foam. These rails are for the purpose of deflecting spray, reducing the tendency of the bow to go under in choppy or turbulent seas, reducing heel and side-slipping while turning, contributing lift, acting as fenders to protect the hull, providing accessible hand-holds and footsteps, reducing the rocking motion of the boat and adding flotation to the boat.

0004U.S. Patent No. 4,060,865 (Woolworth) relates to a small boat comprising a flotation chamber located at the gunwale. The flotation chamber is defined by a first member integral with the sides of the hull extending upwardly and defining an upper end portion and a second member or cover secured at its bottom portion to the hull. A connecting device resiliently engages the upper end portion with the second member to secure a flotation material in the form of a block of expanded polystyrene or the like within the flotation chamber. A rub rail is defined at the upper end of the flotation chamber and can be formed either by a separate connecting member or by a portion of one of the other members. The flotation means of this patent serves both to provide flotation and to act as a rub rail to protect the boat from damage.

0005U.S. Patent No. 4,807,556 relates to a rigid inflatable boat including a hull with an inflatable buoyancy collar. The collar comprises a number of separate inflatable members each of which has an axially extending bore so that it may be securely attached to mountings on the hull straps passing through it. Since the inflatable members are separate, rupture of one does not seriously effect either the pressure in the other members or the load capability of the craft.

0006U.S. Patent No. 4,520,746 relates to an inflated flotation collar formed by positioning a longitudinal inflatable member along at least part of the length of both the port and starboard sides of the hull. The terminal portions of the member are secured so that the linear length of the gunwale over which the member extends is substantially fixed and so that the member is held substantially at gunwale level on the hull by securing devices passing around and over but not under the hull. This device is provided mainly for flotation and is designed to minimize localized stresses on the hull.

0007U.S. Patent No. 4,625,674 (Covington) discloses an aluminum boat including laterally outwardly bowed gunnels. Each of the gunnels is provided with an outer tubular aluminum flotation member extending therealong which is bowed to conform to and is welded to the outer surface of the gunnel. The aluminum tubes are filled with flotation material and have for their primary purpose to provide additional flotation to the boat should it become swamped.

0008U.S. Patent No. 4,287,624 (Lowther) discloses auxiliary flotation gear for fishing boats. The flotation gear comprises two float wings of substantially triangular contoured construction which conform to the hull of the boat and are securely affixed to the exterior stern of a fishing boat above the waterline. The float wings may be constructed of a closed cell, rigid foam. The foam is preferably covered with a fabric such as nylon reinforced vinyl or another suitable durable fabric. The float wings are provided to aid flotation and stability should the boat become swamped.

0009U.S. Patent No. 5,282,436 (Hansen) relates to a foam stabilized watercraft. The high performance boat of this patent is stabilized through the use of foam stabilizing members mounted on the sides of the hull above the chine and extending from the transom along the length of the boat. The sides of the boat also include an upper and lower flange extending outwardly from the sides of the boat adjacent to the upper and lower edges of the stabilizing members at the location where the stabilizing members attach to the sides of the hull. The lower flange helps to ensure that water is not forced between the sides of the boat and the stabilizing members. The stabilizing members are attached to the sides of the hull without use of holes extending from the exterior to the interior of the hull thereby preventing water from seeping into the hull of the boat.

0010Although the foregoing patents provide numerous alternatives for ensuring additional flotation for boats as well as some fender means, none of the prior art references teaches a fender means which is inexpensive to manufacture, aesthetically pleasing, and durable. Accordingly, the present invention is directed to overcoming these disadvantages of the prior art fender means.

SUMMARY OF THE INVENTION

0011The present invention relates, in a first aspect, to a method for the manufacture of a foam collar for use on a boat. The method includes the steps of molding a polymeric foam material by application of heat and pressure to form the foam material into a predetermined shape, removing the foam material from the mold, applying a surface coating to at least a portion of the inner surface of a mold, curing the surface coating in the mold to form a cured surface coating, applying a reinforcement coating in the mold, curing the reinforcement coating to form a cured reinforcement coating, applying adhesives to the cured reinforcement coating, placing the molded foam material into the mold with its outer surface against the adhesive, applying a vacuum over the molded foam material in the mold until the adhesive cures and removing the resultant foam collar from the mold.

0012In a second aspect, the present invention relates to a foam collar made by the above-described process and which includes a polymeric foam material molded to a predetermined shape, a reinforcement coating on a portion of the outer surface of the polymeric foam material and a surface coating on at least part of the reinforcement coating.

0013In a third aspect, the present invention relates to a boat comprising a hull having an outer surface and the above-described foam collar attached to the outer surface of the hull of the boat at a point high enough on the hull to ensure that the foam collar is completely above the static waterline of the boat.

0014The present invention provides a durable, highly attractive foam fender system which can be used on high speed boats with planing hulls. It is considered that this foam collar represents an improvement over prior boats since it does not require inflation, it can be fabricated in an aesthetically pleasing manner, it is durable and it is inexpensive to make and maintain.

0015The present invention will be described in greater detail in the detailed description which follows.

BRIEF DESCRIPTION OF THE DRAWINGS

0016<ul id="ul0001" list-style="none" compact="compact"><li>Fig. 1 is a top view of a boat including the foam collar.</li><li>Fig. 2 is a side view of a boat including the foam collar.</li><li>Fig. 3 is a cross-sectional view of the foam collar and the section of the hull of a boat along line III-III of Fig. 2.</li><li>Fig. 4 is a detail of the circled section of Fig. 3.</li></ul>

DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS

0017Referring to the drawings where like numerals indicate like elements throughout several views, Figure 1 shows a boat 10 including a hull 11 and a foam collar 12. The boat shown in Fig. 1 also includes a bow box 13, a console 14, a bolster 15 and an engine 16.

0018From Figure 1 it can be seen that the preferred embodiment of the boat of the present invention includes four foam collar sections 12 which together form the foam collar of the present invention. The foam collar sections 12 extend around the periphery of the hull 11.

0019Referring to Fig. 2, there is shown a side view of the boat 10 of the present invention. From Fig. 2 it can be seen that the foam collar sections 12 are located on the hull 11 of the boat 10 at a point where the foam collar sections 12 are above the static waterline of the boat. Preferably, the bottom of the foam collar section 12 is 5-50 centimeters above the static waterline so that during normal operation of the boat, the foam collar remains above the surface of the water. Also shown in Fig. 2 is the surface coating 20 of the foam collar sections 12 upon which may be printed, for example, stripes 21, a logo 22 and/or any other design which may be desirable.

0020Referring now to Fig. 3, there is shown a cross-sectional view of the foam collar section 12 along the line III-III of Fig. 2. In the preferred embodiment, the foam collar section 12 is made up of a laminate 24 of first, second and third layers 31, 32, 33, respectively, of foam material. The laminate 24 of foam material layers 31-33 is molded preferably to the shape shown in Fig. 3.

0021On the outer surface of the laminate 24 is a layer of a surface coating 20 and a reinforcement coating 23 which, together are adhered to the laminate 24 by an adhesive layer 25. Laminate 24 is molded so as to have mating surfaces 35, 36 which mate with portions of the hull 11 of boat 10. However, the entire inner surface of the molded laminate 24 need not mate with the hull 11 in the preferred embodiment and thus a gap 34 is formed between the foam collar section 12 and the hull 11 as shown in Fig. 3.

0022The foam collar sections 12 are attached to the hull of the boat by one or more attachment means 30, one of which is shown in the detail of Fig. 4. More specifically, the preferred attachment means 30 includes an attachment flange 40 which is formed integrally with and extends from the foam collar section 12. Attachment flange 40 includes a lip 42 at the distal end thereof. A flat bar, 41, preferably made from aluminum, is used to attach attachment flange 40 to hull 11 by virtue of a first fastening means such as a pin 44. The fastening means may be any other suitable conventional fastener such as a screw 45, bolt, nail or bracket. Nylon scrim 43 can be used to reinforce attachment flange 40 to thereby provide additional strength to bear the load of foam collar sections 12.

0023The molded laminate 24 of the foam collar section 12 of the present invention is preferably made from a copolymer closed cell foam. In particular, three sheets of copolymer are heat fused together to form the foam laminate 24 and the formed foam laminate 24 is molded under heating pressure in a mold to produce the desired shape. A preferred material for the copolymer foam is cross-linked polyethylene-ethylene vinyl acetate copolymer. However, other conventional closed cell polymeric foams can be employed to fabricate the foam collar sections 12 of the present invention.

0024The closed-cell polymer foams useful for for making foam collar sections 12 are chosen based on their density, water absorption characteristics and compressive strength. Preferred foams have a density of from about 1.5 lb/ft³ to about 5 lb/ft³ and, more preferably, from about 2 lb/ft³ to about 5 lb/ft³. Water absorption of the foam is preferably less than 0.1 lb/ft² using ASTM-D3575-84L. Preferred foams have a compressive strength from about 5-9 psi at 25% (ASTM-D3575-91D).

0025The reinforcement coating 23 of the present invention has for its purpose to impart strength to the foam laminate 24 and the attachment flanges 40. Accordingly, the materials used for the reinforcement coating 23 may be conventional materials known to provide strength. One preferred material for use as the reinforcement coating is polyurethane. The reinforcement coating is applied to a thickness of from about 40 to about 70 mils of dry film thickness. More preferably, the reinforcement coating is 50-60 mils thick in dry film thickness. Nylon scrim 43 may be placed along the attachment flanges 40 and sprayed over with the reinforcement coating 23 as shown in Figs. 3-4 in order to provide additional strength to attachment flanges 40.

0026The reinforcement coating 23 is made from materials having good abrasive resistance and elongation. Preferred materials have an abrasive resistance of less than about 1 mg. lost (ASTM (501) and an elongation of at least about 200% (ASTM D412). A preferred material for the reinforcement coating is an abrasive resistant urethane elastomer.

0027The surface coating 20 is used primarily to provide a pleasing aesthetic feel and appearance for the foam collar sections 12. A preferred material for the surface coating is a two-component polyurethane system which is pigmented to the desired color of the foam collar sections 12. The surface coating 20 is preferably sufficiently thick to cover the entire outer surface of foam collar sections 12 to thereby provide a pleasing aesthetic effect for the foam collar sections 12 when viewed from outside of the boat 10. The surface coating 20, coating thickness and foam density may also be chosen to be smooth and soft to the touch. This is useful for persons getting into and out of the boat who will touch the foam collar sections 12. In addition, the surface coating 20 may be chosen to impart abrasion resistance to the outer surface of the foam collar sections 12 such that when boarding other craft or when docked at a waterfront the foam collar will not be damaged by abrasion.

0028Optionally, detailing can be provided on the outer surface of the surface coating 20 of the foam collar sections 12. An example of such detailing is shown in Fig. 2 where stripes 21 and a logo 22 are included on the outer surface 20 of the foam collar sections 12. This option provides an additional means of rendering the foam collar sections 12 aesthetically pleasing and can be used to strongly influence the overall aesthetic impact of the boat 10.

0029Another aspect of the present invention is a method for making the foam collar. In the first step of the method, a polymeric foam material is molded using a mold by application of heat and pressure using conventional molding techniques in order to provide a polymeric foam of a predetermined shape such as the shape shown in Fig. 3 which includes a convex outer surface. The polymeric foam is then removed from the mold and trimmed to remove flash and any other defects and provide a polymeric foam material of the desired shape.

0030The next step in the process is to provide the surface coating onto the interior of a mold. The surface coating may be sprayed or brushed onto the interior surface of the mold. Once the surface coating is applied to the interior surface of the mold, it is cured to a dry film thickness of from about 3 mils to about 20 mils thick. The thickness of the surface coating 20 is primarily a function of the desired color and/or surface characteristics for the foam collar sections 12.

0031After curing the surface coating, a reinforcement coating 23 is applied to the mold atop the surface coating 20. The reinforcement coating 23 may also be sprayed, brushed or applied by any conventional means onto the interior surface of the mold atop the surface coating 20. The reinforcement coating 23 is then cured to a dry film thickness of from about 20 to about 70 mils to form a cured reinforcement coating 23. Optionally, reinforcement mesh, which may be nylon scrim 43, is placed along the areas where the attachment flanges 40 will fit in the mold and the strength reinforcement coating 23 is sprayed over the reinforcement mesh 43 so as to include the reinforcement mesh 43 inside of the reinforcement coating 23 and thereby provide additional strength to attachment flange 40.

0032Once the reinforcement coating 23 has been fully cured to a dry film, an adhesive layer 25 is placed on the cured surface of the reinforcement coating 23 and on the molded surface of the copolymer foam laminate 24. The copolymer foam laminate 24 is then placed in the mold against the adhesion layer 25 and a vacuum is applied over the entire surface of the mold until the adhesive layer 25 cures thereby securing the reinforcement coating 23 directly to the surface of the molded foam laminate 24. Optionally, a flexible polyurethane foam can be applied to fill voids at the mold ends. The application of the flexible polyurethane foam can be by spraying, brushing or any other suitable conventional means. Finally, the completed foam collar section 12 is removed from the mold and trimmed to remove flash or any other defects.

0033The foam collar sections 12 are preferably designed to key into the molded glass reinforced plastic surface of the hull 11 as shown in Fig. 3. In other words, the mating surfaces 35, 36 are molded to fit closely with the outer surface of the hull 11 as shown in Fig. 3. The foam collar sections could also fit onto an aluminum hull with a similar shape as the glass reinforced plastic hull. The foam collar sections 12 are mechanically attached to the hull 11 by any suitable attachment means. An example of the attachment means are aluminum flat bars 41 which key into a molded lip 42 around the perimeter of the molded surface on the attachment flanges 40. The foam collar sections 12 may then be glued together and the seams between the foam collar sections 12 can be reinforced using a polyvinyl chloride seam tape which is glued into place. In this manner, water can be prevented from entering between the foam collar sections 12. The mating surfaces 35, 36 which key into the hull 11 also help prevent water from coming between foam collar sections 12 and hull 11.

0034The foam collar of the present invention provides several advantages over prior art constructions which may be used for the same purpose. First, the foam collar of the present invention allows an increase in the inside space of the boat due to the placement of the foam collar on the outside of the hull 11 and above the static waterline of the boat 10. Further, the foam collar of the present invention provides a soft fendering effect which is useful when boarding other boats or mooring the boat since it will prevent damage to the hull of the boat when it comes into contact with other boats or docks.

0035The foam collar of the present invention may be fabricated to be aesthetically pleasing since it includes a surface coating 20 which can be of a selected color and because the surface coating 20 can be chosen to allow the application of designs and/or logos on the surface coating 20. Further, designs can be molded into the foam collar sections 12 of the present invention in order to provide a three-dimensional textured effect on the outer surface of the foam collar sections 12.

0036Finally, the foam collar sections 12 of the present invention can be made smooth and soft to the touch, are abrasion resistant and require little or no maintenance since they are not inflatable. Finally, the foam collar of the present invention can be fabricated by the relatively inexpensive molding process described above.

0037The foregoing description of the invention has been provided for the purposes of illustration and description only. The scope of the invention is to be determined from the claims appended hereto.