Coated cemented carbide endmill having hard-materials-coated-layers excellent in adhesion

BACKGROUND OF THE INVENTION

1. Field of the Invention

The present invention relates to a coated cemented carbide endmill exhibiting excellent wear resistance for a long period of time because even if the endmill is used in high speed cutting, the hard-material-coated-layers of the endmill are not exfoliated due to the excellent adhesion thereof.

2. Description of the Related Art

Conventionally, there is known coated cemented carbide endmills composed of a tungsten carbide (hereinafter, shown by WC) based cemented carbide substrate (hereinafter, simply referred to as a cemented carbide substrate) having a surface portion to which formed, in an average layer thickness of 0.5 - 5 µm, are hard-material-coated-layers composed of a Ti compound layer which is composed of one or more layers of a Titanium carbide (TiC), Titanium nitride (TiN), Titanium carbide-nitride (TiCN), Titanium oxy-carbide (TiCO), Titanium oxy-nitride (TiNO) and Titanium oxy-carbo-nitride (TiCNO), each of the hard-material-coated-layers being formed by medium temperature chemical vapor deposition (a method generally referred to as MT-CVD by which vapor deposition is performed at 700 - 980°C which is relatively lower than the vapor deposition temperature 1000 - 1150°C employed by ordinary high temperature chemical vapor deposition (hereinafter, referred to as HT-CVD)), as shown in, for example, Japanese Unexamined Patent Publication No. 62-88509.

Recently, since labor and energy are greatly saved in a cutting process, there is a tendency that a cutting speed as one of cutting conditions is further more increased accordingly. When the conventional coated cemented carbide endmills are used under such high speed condition, the hard-material-coated layers are liable to be exfoliated due to their insufficient adhesion, by which the endmills are remarkably worn and their life is ended in a relatively short time.

To cope with this problem, the inventors directed attention to the conventional coated cemented carbide endmills from the above point of view and made studies to improve the adhesion of the hard-material-coated layers constituting the endmills. As a result, the inventors have obtained a conclusion that when a coated cemented carbide endmill is arranged as shown in the following items (a), (b) and (c), the adhesion of the Ti compound layer to the surface of the cemented carbide substrate of the endmill is greatly improved by a surface layer which is formed to the surface portion thereof by being heated at a high temperature and thus the hard-material-coated layer of the coated cemented carbide endmill is not exfoliated even if the endmill is used in high speed cutting and the endmill exhibits excellent wear resistance for a long time: <ul id="ul0001" list-style="none" compact="compact"><li>(a) the cemented carbide substrate has a composition of 5 - 20 wt% of Co (hereinafter, % shows wt%) as a binder phase forming component, further when necessary, 0.1 - 2% of one kind or two kinds of Cr and V as the binder phase forming component, further when necessary, 0.1 - 5% of one kind or more kinds of carbides, nitrides and carbonitrides of Ti, Ta, Nb and Zr (hereinafter, shown as TiC, TiN, TiCN, TaC, TaN, TaCN, NbC, NbN, NbCN, ZrC, ZrN and ZrCN, respectively) as well as two or more kinds of solid solutions thereof (hereinafter, they are shown as (Ti, Ta, Nb, Zr) C·N as a whole) as a dispersed phase forming component and the balance being WC as the dispersed phase forming component and inevitable impurities, wherein the WC has a refined particle structure having an average particle size of 0.1 - 1.5 µm;</li><li>(b) when the cemented carbide substrate shown in (a) is heated at a high temperature in a hydrogen atmosphere in which a carbon dioxide gas or titanium tetrachloride is blended under conditions that the atmosphere is set to a pressure of 50 - 550 torr and the substrate is held at a temperature of 900 - 1000°C for 1 - 15 minutes, a surface layer created by the reaction of composite carbides of Co and W (hereinafter, shown by Co_mW_nC) is formed to the surface portion of the base substance over a predetermined depth from the uppermost surface at the cutting edge thereof.</li><li>(c) hard-material-coated layers composed of a Ti compound layer and, when necessary, an aluminum oxide (hereinafter, shown by Al₂O₃) layer are formed to the surface of the substrate having the surface layer which is formed by being heated at the high temperature and in which the reaction-created Co_mW_nC shown in (b) is distributed, wherein the Ti compound layer is composed of one or more layers of a Tic, TiN, TiCN, TiCO, TiNO and TiCNO using MT-CVD and the aluminum oxide layer is formed using MT-CVD or HT-CVD.</li></ul>

SUMMARY OF THE INVENTION

The present invention achieved based on the result of the above studies is characterized in a coated cemented carbide endmill having hard-material-coated layers excellent in an adhesion, the endmill comprising a tungsten carbide based cemented carbide substrate having a composition of 5 - 20 wt% of Co as a binder phase forming component, further when necessary, 0.1 - 2% of one kind or two kinds of Cr and V as the binder phase forming component, further when necessary, 0.1 - 5% of one kind or more kinds of (Ti, Ta, Nb, Zr) C·N as a dispersed phase forming component and the balance being WC as the dispersed phase forming component and inevitable impurities, wherein the WC has a refined particle structure having an average particle size of 0.1 - 1.5 µm, the cemented carbide substrate has a surface layer formed to the surface portion thereof which is formed by being heated at a high temperature and in which reaction-created Co_mW_nC is distributed over a depth of 0.1 - 2 µm from the uppermost surface at the cutting edge thereof and further the substrate has coated layers composed of a Ti compound layer and, further when necessary, an Al₂O₃ layer formed thereto in an average layer thickness of 0.5 - 4.5 µm, the Ti compound layer being composed of one or more layers of a TiC, TiN, TiCN, TiCO, TiNO and TiCNO using MT-CVD and the Al₂O₃ layer being formed using MT-CVD or HT-CVD.

Next, reasons why the compositions of the cemented carbide substrate constituting the coated cemented carbide endmill of the present invention, the average particle size of WC particles and the distributed depth of Co_mW_nC and the average layer thickness of the hard-material-coated layers are limited as described above will be described.

(a) Co content

Co has an action for improving a sinterability and thereby improving the toughness of the cemented carbide substrate. When a Co content is less than 5%, however, a desired toughness improving effect cannot be obtained, whereas when the Co content is larger than 20%, not only the wear resistance of the cemented carbide substrate itself is lowered but also the cemented carbide substrate is deformed by the heat generated in high speed cutting. Thus, the Co content is set to 5 - 20% and preferably to 8 - 12%.

(b) Cr and V

Cr and V are contained in a necessary amount because they are dissolved in solid in Co as the binder phase forming component to thereby strengthen it as well as contribute to refine the WC particles and further have an action for promoting the formation of the reaction-created Co_mW_nC which is distributed in the surface layer formed by being heated at the high temperature to thereby improve the adhesion of the hard-material-coated layers achieved by the reaction-created Co_mW_nC. When their content is less than 0.1%, however, it cannot be expected that the above action achieves a desired effect, whereas when their content is larger than 2%, the above action is saturated and an improving effect cannot be further enhanced. Thus, their content is set to 0.1 - 2% and preferably to 4 - 0.8%.

When the coated cemented carbide endmill is made, it is preferable that Cr and V as the binder phase forming component are used in the form of carbides, nitrides and oxides of Cr and V (hereinafter, shown as Cr₃C₂, CrN, Cr₂O₃, VC, VN and V₂O₅ and further shown as (Cr, V) C·N·O as a whole) as material powders. Since these material powders are dissolved in solid in Co as the binder phase forming component when sintering is carried out and form a binder phase, a precipitate containing Cr and V as one of components cannot be observed by an optical microscope or a scanning electron microscope.

(c) (Ti, Ta, Nb, Sr) C·N

Since these components have an action for improving the wear resistance of the cemented carbide substrate, they are contained in a necessary amount. When their content is less than 0.1%, however, a desired wear resistance improving effect cannot be obtained, whereas when it is larger than 5%, toughness is lowered. Thus, their content is set to 0.1 - 5% and preferably 1 - 2.5%.

(d) Average particle size of WC

It is intended to improve the strength of the cemented carbide substrate by the refined particle structure of WC particles and the refined particle structure is obtained by setting the particle size of WC powder used as material powder to 1.5 µm or less. Accordingly, when the average particle size of the material powder is larger than 1.5 µm, a desired strength improving effect cannot be obtained, whereas when it is less than 0.1 µm, wear resistance is lowered. Thus, the average particle size of the WC powder is set to 0.1 - 1.5 µm and preferably to 0.6 - 1.0 µm.

(e) Average distributed depth of Co

m

W

n

C

Since the portion of the endmill which contributes to cutting is a cutting edge and the portion of the endmill which is far from the cutting edge does not contribute to the cutting, the average distributed depth of Co_mW_nC is important at the portion of the cutting edge. Thus, the average distributed depth will be prescribed here. When the average distributed depth of Co_mW_nC is less than 0.1 µm, the ratio of it distributed in the surface layer formed by being heated at the high temperature is too small for the Co_mW_nC to secure a desired excellent adhesion to the hard-material-coated layers, whereas when the average distributed depth thereof is larger than 2 µm, since ratio of the average distributed depth of the Co_mW_nC in the uppermost surface portion of the cemented carbide substrate is made excessively large, chipping is liable to be caused to a cutting edge. Thus, the average distributed depth is set to 0.1 - 2 µm and preferably to 0.5 - 1.5 µm.

(f) Average layer thickness of the hard-material-coated layers

When the average layer thickness of the hard-material-coated layers is less than 0.5 µm, desired excellent wear resistance cannot be obtained, whereas when the average layer thickness is larger than 4.5 µm, chipping is liable to be caused to the cutting edge. Thus, the average layer thickness is set to 0.5 - 4.5 µm and preferably to 1.5 - 2.5 µm.

DESCRIPTION OF THE PREFERRED EMBODIMENTS

A coated cemented carbide endmill of the present invention will be specifically described with reference to embodiments.

(Embodiment 1)

WC powder having a predetermined average particle size within the range of 0.1 - 1.5 µm, various carbide powder, nitride powder and carbo-nitride powder each having the average particle size of 0.5 µm as shown in Table 1 and Table 2 and constituting (Ti, Ta, Nb, Zr) C·N and Co powder having the average particle size of 0.5 µm were prepared as material powders. These material powders were blended to the composition shown in Table 1 and Table 2 likewise, wet mixed in a ball mill for 72 hours and dried and thereafter pressed to green compact at the pressure of 1 ton/cm² and the green compact was vacuum sintered under conditions that it was held for one hour in the vacuum of 1 × 10^-3 torr at a predetermined temperature within the range of 1350 - 1500°C and cemented carbide substrates a - z which had compositions substantially similar to the above blended compositions and comprised WC particles having the average particle sizes shown in Table 1 and Table 2 were formed.

Further, cemented carbide substrates A - Z were made by forming a surface layer formed by being heated at a high temperature to the surface portion of each of the cemented carbide substrates a - z under the conditions shown in Table 3 and Table 4, the surface having Co_mW_nC distributed therein over the average depths shown in Table 3 and Table 4.

Subsequently, hard-material-coated layers having the compositions and the average layer thicknesses shown in Table 6 and Table 7 were formed under the conditions shown in Table 5 to the surface of each of the cemented carbide substrates A - Z and coated cemented carbide ball-nose endmills of the present invention (hereinafter, referred to as coated endmills of the present invention) 1 - 26 were made. The endmills were composed of a shank portion and a two-flute portion and had a ball-nose radius of 5 mm and a nelix angle of 30°.

For the purpose of comparison, comparative coated cemented carbide endmills (hereinafter, referred to as comparative coated endmill) 1 - 26 were made, respectively under conditions similar to the above conditions except that cemented carbide substrates a - z, to which the surface layer formed by being heated at the high temperature was not formed, were used in place of the cemented carbide substrates A - Z having the above surface layer as shown in Table. 8.

Next, high speed copy milling was carried out, by means of the resultant coated endmills 1 - 26 of the present invention and the resultant comparative coated endmills 1 - 26, to alloy steel in a dry state by alternately effecting down-cut and up-cut milling under the following conditions and the worn width of the maximum flank face of the cutting edge of each of the endmills was measured. <ul id="ul0002" list-style="none" compact="compact"><li>material to be cut SKD61 (hardness: H<img file="EP0900860A2_D0001.tif" />C 53)</li><li>cutting speed: 800 m/min</li><li>feed per tooth: 0.1 mm/cutting edge</li><li>depth of cut: 0.5 mm</li><li>width of cut: 0.5 mm</li><li>length of cut: 250 m</li></ul> Since the comparative coated endmills 1 - 26 were worn at a high speed, the cutting operation of them was interrupted when the width of the maximum flank wear of the cutting edge reached 0.3 mm and the cut length up to that time was measured. Table 6 - Table 8 show the result of measurement, respectively.

(Embodiment 2)

WC powder having a predetermined average particle size within the range of 0.1 - 1.5 µm, Cr₃C₂ powder having the average particle size of 0.5 µm, VC powder having the average particle size of 0.5 µm and Co powder having the average particle size of 0.5 µm were prepared as material powders. These material powders were blended at a predetermined blend ratio, wet mixed in a ball mill for 72 hours and dried and thereafter pressed to green compact at the pressure of 1 ton/cm² and the green compact was vacuum sintered under conditions that it was held for one hour in the vacuum of 1 × 10^-3 torr at a predetermined temperature within the range of 1350 - 1500°C and cemented carbide substrates a - t which had the compositions shown in Table 9 and comprised WC having the average particle sizes shown in Table 9 were formed.

Further, cemented carbide substrates A - T were made by forming a surface layer formed by being heated at a high temperature to the surface portion of each of the cemented carbide substrates a - z under the conditions shown in Table 10, the surface layer having Co_mW_nC distributed therein over the average depths shown in Table 10.

Subsequently, hard-material-coated layers having the compositions and the average layer thicknesses shown in Table 12 were formed under the conditions shown in Table 11 to the surface of each of the cemented carbide substrates A - T and coated cemented carbide ball-nose endmills of the present invention (hereinafter, referred to as coated endmills of the present invention) 1 - 20 were made, respectively. The endmills were composed of a shank portion and a two-flute portion and had a ball-nose radius of 5 mm and a helix angle of 30°.

For the purpose of comparison, comparative coated cemented carbide endmills (hereinafter, referred to as comparative coated endmills) 1 - 20 were made, respectively under conditions similar to the above conditions except that cemented carbide substrates a - t, to which the surface layer formed by being heated at the high temperature was not formed, were used in place of the cemented carbide substrates A - T having the above surface layer as shown in Table. 13.

Next, high speed copy milling was carried out, by means of the resultant coated endmills 1 - 20 of the present invention and the resultant comparative coated endmills 1 - 20, to alloy steel in a dry state by alternately effecting down-cut and up-cut milling under the following conditions and the worn width of the maximum flank face of the cutting edge of each of the endmills was measured. <ul id="ul0003" list-style="none" compact="compact"><li>material to be cut: SKD61 (hardness: H<img file="EP0900860A2_D0001.tif" />C 53)</li><li>cutting speed: 500 m/min</li><li>feed per tooth: 0.1 mm/cutting edge</li><li>depth of cut: 0.5 mm</li><li>width of cut: 0.5 mm</li><li>length of cut: 350 m</li></ul> Table 12 and Table 13 show the result of measurement, respectively.

(Embodiment 3)

WC powder having a predetermined average particle size within the range of 0.1 - 1.5 µm, various carbide powder, nitride powder, oxide powder and carbo-nitride powder each having the average particle size of 0.5 µm and constituting (Ti,Ta, Nb, Zr) C·N and (Cr, V) C·N·O, Co powder having the average particle size of 0.5 µm and carbon powder for adjusting an amount of carbon were prepared as material powders. These material powders were blended to a predetermined composition, wet mixed in a ball mill for 72 hours and dried and thereafter pressed to green compact at the pressure of 1 ton/cm² and the green compact was vacuum sintered under conditions that it was held for one hour in the vacuum of 1 × 10^-3 torr at a predetermined temperature in the range of 1350 - 1500°C and cemented carbide substrates a - s which had the compositions shown in Table. 14 and comprised WC particles having the average particle sizes shown in Table 14 were formed.

Further, cemented carbide substrates A - S were made by forming a surface layer formed by being heated at a high temperature to the surface portion of each of the cemented carbide substrates a - s under the conditions shown in Table 15, the surface layer having Co_mW_nC distributed therein over the average depths shown in Table 15.

Subsequently, hard-material-coated layers having the compositions and the average layer thicknesses shown in Table 17 were formed under the conditions shown in Table 16 to the surface of each of the cemented carbide substrates A - S and coated carbide ball-nose endmills of the present invention (hereinafter, referred to as coated endmills of the present invention) 1 - 19 were made. The endmills were composed of a shank portion and a two-flute portion and had a ball-nose radius of 5 mm and a helix angle of 30°.

For the purpose of comparison, comparative coated cemented carbide endmills (hereinafter, referred to comparative coated endmills) 1 - 19 were made, respectively under conditions similar to the above conditions except that cemented carbide substrates a - s, to which the surface layer formed by being heated at the high temperature was not formed, were used in place of the cemented carbide substrates A - S having the above surface layer as shown in Table. 18.

Next, high speed copy milling was carried out, by means of the resultant coated endmills 1 - 19 of the present invention and the resultant comparative coated endmills 1 - 19, to alloy steel in a dry state by alternately effecting down-cut and up-cut milling, under the following conditions and the width of the maximum flank wear of the cutting edge of each of the endmills was measured. <ul id="ul0004" list-style="none" compact="compact"><li>material to be cut: SKD61 (hardness: H<img file="EP0900860A2_D0001.tif" />C 53)</li><li>cutting speed: 650 m/min</li><li>feed per tooth: 0.1 mm/cutting edge</li><li>depth of cut: 0.5 mm</li><li>width of cut: 0.5 mm</li><li>time of cut: 50 min</li></ul> Table 17 and Table 18 show the result of measurement, respectively.

It is apparent from the results shown in Tables 6 - 8, 12, 13, 17 and 18 that the hard-material-coated layers of the coated endmills of the present invention were not exfoliated and the endmills thereby exhibited excellent wear resistance, whereas the hard-material-coated layers of the comparative coated endmills were exfoliated in the midway of cutting and the endmills were greatly worn by the exfoliation and their life was ended in a relatively short time.

In the coated carbide endmills of the present invention, since the adhesion of the hard-material-coated layers to the surface of the cemented carbide substrate is greatly improved by the ComWnC distributed in the surface layer formed to the surface portion of the base substance by being heated at the high temperature as described above, the hard-material-coated layers are not exfoliated not only when the endmills are used under usual cutting conditions but also even if they are used in high speed cutting. Accordingly, the coated cemented carbide endmills of the present invention exhibit excellent wear resistance for a long period of time. <tables id="tabl0001" num="0001"><table frame="all"><title>Table 1</title><tgroup cols="4" colsep="1" rowsep="1"><colspec colnum="1" colname="col1" colwidth="39.37mm" /><colspec colnum="2" colname="col2" colwidth="39.37mm" /><colspec colnum="3" colname="col3" colwidth="39.37mm" /><colspec colnum="4" colname="col4" colwidth="39.37mm" /><thead valign="top"><row><entry namest="col1" nameend="col2" align="center">Type</entry><entry namest="col3" nameend="col3" align="center">Composition (wt%)</entry><entry namest="col4" nameend="col4" align="center">Average grain size of WC (µm)</entry></row></thead><tbody valign="top"><row><entry namest="col1" nameend="col1" morerows="13" align="center">Cemented carbide substrate</entry><entry namest="col2" nameend="col2" align="left">a</entry><entry namest="col3" nameend="col3" align="left">Co: 5, WC + impurities: balance</entry><entry namest="col4" nameend="col4" align="char" char=".">1.2</entry></row><row><entry namest="col2" nameend="col2" align="left">b</entry><entry namest="col3" nameend="col3" align="left">Co: 8, WC + impurities: balance</entry><entry namest="col4" nameend="col4" align="char" char=".">0.8</entry></row><row><entry namest="col2" nameend="col2" align="left">c</entry><entry namest="col3" nameend="col3" align="left">Co: 10, WC + impurities: balance</entry><entry namest="col4" nameend="col4" align="char" char=".">1.0</entry></row><row><entry namest="col2" nameend="col2" align="left">d</entry><entry namest="col3" nameend="col3" align="left">Co: 12, WC + impurities: balance</entry><entry namest="col4" nameend="col4" align="char" char=".">1.2</entry></row><row><entry namest="col2" nameend="col2" align="left">e</entry><entry namest="col3" nameend="col3" align="left">Co: 15, WC + impurities: balance</entry><entry namest="col4" nameend="col4" align="char" char=".">0.6</entry></row><row><entry namest="col2" nameend="col2" align="left">f</entry><entry namest="col3" nameend="col3" align="left">Co: 20, WC + impurities: balance</entry><entry namest="col4" nameend="col4" align="char" char=".">0.4</entry></row><row><entry namest="col2" nameend="col2" align="left">g</entry><entry namest="col3" nameend="col3" align="left">Co: 13, TiN: 2.5, WC + impurities: balance</entry><entry namest="col4" nameend="col4" align="char" char=".">0.4</entry></row><row><entry namest="col2" nameend="col2" align="left">h</entry><entry namest="col3" nameend="col3" align="left">Co: 10, TaC: 2, WC + impurities: balance</entry><entry namest="col4" nameend="col4" align="char" char=".">0.8</entry></row><row><entry namest="col2" nameend="col2" align="left">i</entry><entry namest="col3" nameend="col3" align="left">Co: 6, NbC: 0.5, WC + impurities: balance</entry><entry namest="col4" nameend="col4" align="char" char=".">1.2</entry></row><row><entry namest="col2" nameend="col2" align="left">j</entry><entry namest="col3" nameend="col3" align="left">Co: 5, ZrCN: 0.1, WC + impurities: balance</entry><entry namest="col4" nameend="col4" align="char" char=".">1.5</entry></row><row><entry namest="col2" nameend="col2" align="left">k</entry><entry namest="col3" nameend="col3" align="left">Co: 7, (Ti, Ta) N: 0.8, WC + impurities: balance</entry><entry namest="col4" nameend="col4" align="char" char=".">1.0</entry></row><row><entry namest="col2" nameend="col2" align="left">l</entry><entry namest="col3" nameend="col3" align="left">Co: 15, (Ti, Nb) CN: 3.5, NbCN: 0.5, WC + impurities: balance</entry><entry namest="col4" nameend="col4" align="char" char=".">0.5</entry></row><row><entry namest="col2" nameend="col2" align="left">m</entry><entry namest="col3" nameend="col3" align="left">Co: 8, (Ti, Zr) CN: 1, WC + impurities: balance</entry><entry namest="col4" nameend="col4" align="char" char=".">0.6</entry></row><row rowsep="1"><entry namest="col2" nameend="col2" align="left">n</entry><entry namest="col3" nameend="col3" align="left">Co: 8, (Ta, Nb) C: 1.5, WC + impurities: balance</entry><entry namest="col4" nameend="col4" align="char" char=".">1.0</entry></row></tbody></tgroup></table></tables><tables id="tabl0002" num="0002"><table frame="all"><title>Table 2</title><tgroup cols="4" colsep="1" rowsep="1"><colspec colnum="1" colname="col1" colwidth="39.37mm" /><colspec colnum="2" colname="col2" colwidth="39.37mm" /><colspec colnum="3" colname="col3" colwidth="39.37mm" /><colspec colnum="4" colname="col4" colwidth="39.37mm" /><thead valign="top"><row><entry namest="col1" nameend="col2" align="center">Type</entry><entry namest="col3" nameend="col3" align="center">Composition (wt%)</entry><entry namest="col4" nameend="col4" align="center">Average grain size of WC (µm)</entry></row></thead><tbody valign="top"><row><entry namest="col1" nameend="col1" morerows="11" align="center">Cemented carbide substrate</entry><entry namest="col2" nameend="col2" align="left">o</entry><entry namest="col3" nameend="col3" align="left">Co: 12, (Ta, Zr) C: 2, WC + impurities: balance</entry><entry namest="col4" nameend="col4" align="char" char=".">0.6</entry></row><row><entry namest="col2" nameend="col2" align="left">p</entry><entry namest="col3" nameend="col3" align="left">Co: 6, (Zr, Nb) N: 1.2, NbN: 0.3, WC + impurities: balance</entry><entry namest="col4" nameend="col4" align="char" char=".">1.2</entry></row><row><entry namest="col2" nameend="col2" align="left">q</entry><entry namest="col3" nameend="col3" align="left">Co: 10, (Ti, Ta, Nb) C: 2.2, WC + impurities: balance</entry><entry namest="col4" nameend="col4" align="char" char=".">0.8</entry></row><row><entry namest="col2" nameend="col2" align="left">r</entry><entry namest="col3" nameend="col3" align="left">Co: 20, (Ti, Ta, Zr) N: 5, WC + impurities: balance</entry><entry namest="col4" nameend="col4" align="char" char=".">0.1</entry></row><row><entry namest="col2" nameend="col2" align="left">s</entry><entry namest="col3" nameend="col3" align="left">Co: 12, (Ti, Zr, Nb) CN: 2.5, WC + impurities: balance</entry><entry namest="col4" nameend="col4" align="char" char=".">0.6</entry></row><row><entry namest="col2" nameend="col2" align="left">t</entry><entry namest="col3" nameend="col3" align="left">Co: 8, (Ta, Nb, Zr) C: 1, TiCN: 0.5, WC + impurities: balance</entry><entry namest="col4" nameend="col4" align="char" char=".">1.2</entry></row><row><entry namest="col2" nameend="col2" align="left">u</entry><entry namest="col3" nameend="col3" align="left">Co: 6, (Ti, Ta, Zr, Nb) C: 1, WC + impurities: balance</entry><entry namest="col4" nameend="col4" align="char" char=".">0.8</entry></row><row><entry namest="col2" nameend="col2" align="left">v</entry><entry namest="col3" nameend="col3" align="left">Co: 10, TaN: 1.5, TiC: 0.5, WC + impurities: balance</entry><entry namest="col4" nameend="col4" align="char" char=".">1.2</entry></row><row><entry namest="col2" nameend="col2" align="left">w</entry><entry namest="col3" nameend="col3" align="left">CO: 7, (Ti, Zr) C: 0.4, ZrN: 0.1, WC + impurities: balance</entry><entry namest="col4" nameend="col4" align="char" char=".">0.8</entry></row><row><entry namest="col2" nameend="col2" align="left">x</entry><entry namest="col3" nameend="col3" align="left">Co: 17, (Ti, Zr) N: 1, (Ti, Ta, Zr) C: 3, TaCN: 0.6, WC + impurities: balance</entry><entry namest="col4" nameend="col4" align="char" char=".">1.5</entry></row><row><entry namest="col2" nameend="col2" align="left">y</entry><entry namest="col3" nameend="col3" align="left">Co: 12, TiC: 0.2, ZrC: 0.8, (Ta, Nb) C: 1, WC + impurities: balance</entry><entry namest="col4" nameend="col4" align="char" char=".">1.0</entry></row><row rowsep="1"><entry namest="col2" nameend="col2" align="left">z</entry><entry namest="col3" nameend="col3" align="left">Co: 15, TiN: 0.5, TaC: 1, ZrCN: 1, NbC: 0.5, WC + impurities: balance</entry><entry namest="col4" nameend="col4" align="char" char=".">0.4</entry></row></tbody></tgroup></table></tables><tables id="tabl0003" num="0003"><table frame="all"><title>Table 3</title><tgroup cols="8" colsep="1" rowsep="1"><colspec colnum="1" colname="col1" colwidth="19.68mm" /><colspec colnum="2" colname="col2" colwidth="19.68mm" /><colspec colnum="3" colname="col3" colwidth="19.68mm" /><colspec colnum="4" colname="col4" colwidth="19.68mm" /><colspec colnum="5" colname="col5" colwidth="19.68mm" /><colspec colnum="6" colname="col6" colwidth="19.68mm" /><colspec colnum="7" colname="col7" colwidth="19.68mm" /><colspec colnum="8" colname="col8" colwidth="19.68mm" /><thead valign="top"><row><entry namest="col1" nameend="col2" rowsep="0" align="center">Type</entry><entry namest="col3" nameend="col3" rowsep="0" align="center">Symbol of substrate</entry><entry namest="col4" nameend="col8" align="center">Surface layer formed by being heated at high temperature</entry></row><row><entry namest="col1" nameend="col2" rowsep="0" /><entry namest="col3" nameend="col3" rowsep="0" /><entry namest="col4" nameend="col7" align="center">Forming conditions</entry><entry namest="col8" nameend="col8" rowsep="0" align="center">Average distributed depth of Co_mW_nC (µm)</entry></row><row><entry namest="col1" nameend="col2" rowsep="0" /><entry namest="col3" nameend="col3" rowsep="0" /><entry namest="col4" nameend="col5" align="center">Atmosphere</entry><entry namest="col6" nameend="col6" rowsep="0" align="center">Temperature (°C)</entry><entry namest="col7" nameend="col7" rowsep="0" align="center">Holding time (min.)</entry><entry namest="col8" nameend="col8" rowsep="0" /></row><row><entry namest="col1" nameend="col2" /><entry namest="col3" nameend="col3" /><entry namest="col4" nameend="col4" align="center">Ratio of composition blended to H₂ (vol%)</entry><entry namest="col5" nameend="col5" align="center">Pressure (torr)</entry><entry namest="col6" nameend="col6" /><entry namest="col7" nameend="col7" /><entry namest="col8" nameend="col8" /></row></thead><tbody valign="top"><row><entry namest="col1" nameend="col1" morerows="12" align="center">Cemented carbide substrate</entry><entry namest="col2" nameend="col2" align="left">A</entry><entry namest="col3" nameend="col3" align="left">a</entry><entry namest="col4" nameend="col4" align="left">CO₂: 11</entry><entry namest="col5" nameend="col5" align="center">250</entry><entry namest="col6" nameend="col6" align="center">950</entry><entry namest="col7" nameend="col7" align="center">6</entry><entry namest="col8" nameend="col8" align="char" char=".">1.64</entry></row><row><entry namest="col2" nameend="col2" align="left">B</entry><entry namest="col3" nameend="col3" align="left">b</entry><entry namest="col4" nameend="col4" align="left">TiCl₄: 2</entry><entry namest="col5" nameend="col5" align="center">550</entry><entry namest="col6" nameend="col6" align="center">900</entry><entry namest="col7" nameend="col7" align="center">11</entry><entry namest="col8" nameend="col8" align="char" char=".">0.83</entry></row><row><entry namest="col2" nameend="col2" align="left">C</entry><entry namest="col3" nameend="col3" align="left">c</entry><entry namest="col4" nameend="col4" align="left">CO₂: 10</entry><entry namest="col5" nameend="col5" align="center">300</entry><entry namest="col6" nameend="col6" align="center">950</entry><entry namest="col7" nameend="col7" align="center">10</entry><entry namest="col8" nameend="col8" align="char" char=".">1.27</entry></row><row><entry namest="col2" nameend="col2" align="left">D</entry><entry namest="col3" nameend="col3" align="left">d</entry><entry namest="col4" nameend="col4" align="left">TiCl₄: 3</entry><entry namest="col5" nameend="col5" align="center">400</entry><entry namest="col6" nameend="col6" align="center">920</entry><entry namest="col7" nameend="col7" align="center">7</entry><entry namest="col8" nameend="col8" align="char" char=".">0.80</entry></row><row><entry namest="col2" nameend="col2" align="left">E</entry><entry namest="col3" nameend="col3" align="left">e</entry><entry namest="col4" nameend="col4" align="left">CO₂: 10</entry><entry namest="col5" nameend="col5" align="center">50</entry><entry namest="col6" nameend="col6" align="center">900</entry><entry namest="col7" nameend="col7" align="center">5</entry><entry namest="col8" nameend="col8" align="char" char=".">0.24</entry></row><row><entry namest="col2" nameend="col2" align="left">F</entry><entry namest="col3" nameend="col3" align="left">f</entry><entry namest="col4" nameend="col4" align="left">TiCl₄: 2</entry><entry namest="col5" nameend="col5" align="center">150</entry><entry namest="col6" nameend="col6" align="center">900</entry><entry namest="col7" nameend="col7" align="center">5</entry><entry namest="col8" nameend="col8" align="char" char=".">0.41</entry></row><row><entry namest="col2" nameend="col2" align="left">G</entry><entry namest="col3" nameend="col3" align="left">g</entry><entry namest="col4" nameend="col4" align="left">TiCl₄: 2</entry><entry namest="col5" nameend="col5" align="center">450</entry><entry namest="col6" nameend="col6" align="center">900</entry><entry namest="col7" nameend="col7" align="center">10</entry><entry namest="col8" nameend="col8" align="char" char=".">1.73</entry></row><row><entry namest="col2" nameend="col2" align="left">H</entry><entry namest="col3" nameend="col3" align="left">h</entry><entry namest="col4" nameend="col4" align="left">CO₂: 11</entry><entry namest="col5" nameend="col5" align="center">350</entry><entry namest="col6" nameend="col6" align="center">950</entry><entry namest="col7" nameend="col7" align="center">12</entry><entry namest="col8" nameend="col8" align="char" char=".">1.48</entry></row><row><entry namest="col2" nameend="col2" align="left">I</entry><entry namest="col3" nameend="col3" align="left">i</entry><entry namest="col4" nameend="col4" align="left">CO₂: 9</entry><entry namest="col5" nameend="col5" align="center">550</entry><entry namest="col6" nameend="col6" align="center">1000</entry><entry namest="col7" nameend="col7" align="center">15</entry><entry namest="col8" nameend="col8" align="char" char=".">2.00</entry></row><row><entry namest="col2" nameend="col2" align="left">J</entry><entry namest="col3" nameend="col3" align="left">j</entry><entry namest="col4" nameend="col4" align="left">TiCl₄: 1</entry><entry namest="col5" nameend="col5" align="center">300</entry><entry namest="col6" nameend="col6" align="center">950</entry><entry namest="col7" nameend="col7" align="center">10</entry><entry namest="col8" nameend="col8" align="char" char=".">0.99</entry></row><row><entry namest="col2" nameend="col2" align="left">K</entry><entry namest="col3" nameend="col3" align="left">k</entry><entry namest="col4" nameend="col4" align="left">TiCl₄: 3</entry><entry namest="col5" nameend="col5" align="center">50</entry><entry namest="col6" nameend="col6" align="center">1000</entry><entry namest="col7" nameend="col7" align="center">5</entry><entry namest="col8" nameend="col8" align="char" char=".">0.45</entry></row><row><entry namest="col2" nameend="col2" align="left">L</entry><entry namest="col3" nameend="col3" align="left">1</entry><entry namest="col4" nameend="col4" align="left">CO₂: 11</entry><entry namest="col5" nameend="col5" align="center">200</entry><entry namest="col6" nameend="col6" align="center">950</entry><entry namest="col7" nameend="col7" align="center">5</entry><entry namest="col8" nameend="col8" align="char" char=".">1.28</entry></row><row rowsep="1"><entry namest="col2" nameend="col2" align="left">M</entry><entry namest="col3" nameend="col3" align="left">m</entry><entry namest="col4" nameend="col4" align="left">CO₂: 9</entry><entry namest="col5" nameend="col5" align="center">80</entry><entry namest="col6" nameend="col6" align="center">900</entry><entry namest="col7" nameend="col7" align="center">6</entry><entry namest="col8" nameend="col8" align="char" char=".">0.31</entry></row></tbody></tgroup></table></tables><tables id="tabl0004" num="0004"><table frame="all"><title>Table 4</title><tgroup cols="8" colsep="1" rowsep="1"><colspec colnum="1" colname="col1" colwidth="19.68mm" /><colspec colnum="2" colname="col2" colwidth="19.68mm" /><colspec colnum="3" colname="col3" colwidth="19.68mm" /><colspec colnum="4" colname="col4" colwidth="19.68mm" /><colspec colnum="5" colname="col5" colwidth="19.68mm" /><colspec colnum="6" colname="col6" colwidth="19.68mm" /><colspec colnum="7" colname="col7" colwidth="19.68mm" /><colspec colnum="8" colname="col8" colwidth="19.68mm" /><thead valign="top"><row><entry namest="col1" nameend="col2" rowsep="0" align="center">Type</entry><entry namest="col3" nameend="col3" rowsep="0" align="center">Symbol of substrate</entry><entry namest="col4" nameend="col8" align="center">Surface layer formed by being heated at high temperature</entry></row><row><entry namest="col1" nameend="col2" rowsep="0" /><entry namest="col3" nameend="col3" rowsep="0" /><entry namest="col4" nameend="col7" align="center">Forming conditions</entry><entry namest="col8" nameend="col8" rowsep="0" align="center">Average distributed depth of Co_mW_nC (µm)</entry></row><row><entry namest="col1" nameend="col2" rowsep="0" /><entry namest="col3" nameend="col3" rowsep="0" /><entry namest="col4" nameend="col5" align="center">Atmosphere</entry><entry namest="col6" nameend="col6" rowsep="0" align="center">Temperature (°C)</entry><entry namest="col7" nameend="col7" rowsep="0" align="center">Holding time (min.)</entry><entry namest="col8" nameend="col8" rowsep="0" /></row><row><entry namest="col1" nameend="col2" /><entry namest="col3" nameend="col3" /><entry namest="col4" nameend="col4" align="center">Ratio of composiblended to H₂ (vol%)</entry><entry namest="col5" nameend="col5" align="center">Pressure (torr)</entry><entry namest="col6" nameend="col6" /><entry namest="col7" nameend="col7" /><entry namest="col8" nameend="col8" /></row></thead><tbody valign="top"><row><entry namest="col1" nameend="col1" morerows="12" align="center">Cemented carbide substrate</entry><entry namest="col2" nameend="col2" align="left">N</entry><entry namest="col3" nameend="col3" align="left">n</entry><entry namest="col4" nameend="col4" align="left">TiCl₄: 1</entry><entry namest="col5" nameend="col5" align="center">250</entry><entry namest="col6" nameend="col6" align="center">900</entry><entry namest="col7" nameend="col7" align="center">13</entry><entry namest="col8" nameend="col8" align="char" char=".">1.02</entry></row><row><entry namest="col2" nameend="col2" align="left">O</entry><entry namest="col3" nameend="col3" align="left">o</entry><entry namest="col4" nameend="col4" align="left">TiCl₄: 3</entry><entry namest="col5" nameend="col5" align="center">450</entry><entry namest="col6" nameend="col6" align="center">950</entry><entry namest="col7" nameend="col7" align="center">11</entry><entry namest="col8" nameend="col8" align="char" char=".">0.56</entry></row><row><entry namest="col2" nameend="col2" align="left">P</entry><entry namest="col3" nameend="col3" align="left">p</entry><entry namest="col4" nameend="col4" align="left">Co₂: 9</entry><entry namest="col5" nameend="col5" align="center">300</entry><entry namest="col6" nameend="col6" align="center">1000</entry><entry namest="col7" nameend="col7" align="center">13</entry><entry namest="col8" nameend="col8" align="char" char=".">1.52</entry></row><row><entry namest="col2" nameend="col2" align="left">Q</entry><entry namest="col3" nameend="col3" align="left">q</entry><entry namest="col4" nameend="col4" align="left">CO₂: 10</entry><entry namest="col5" nameend="col5" align="center">500</entry><entry namest="col6" nameend="col6" align="center">950</entry><entry namest="col7" nameend="col7" align="center">15</entry><entry namest="col8" nameend="col8" align="char" char=".">1.80</entry></row><row><entry namest="col2" nameend="col2" align="left">R</entry><entry namest="col3" nameend="col3" align="left">r</entry><entry namest="col4" nameend="col4" align="left">TiCl₄: 1</entry><entry namest="col5" nameend="col5" align="center">100</entry><entry namest="col6" nameend="col6" align="center">900</entry><entry namest="col7" nameend="col7" align="center">6</entry><entry namest="col8" nameend="col8" align="char" char=".">0.53</entry></row><row><entry namest="col2" nameend="col2" align="left">S</entry><entry namest="col3" nameend="col3" align="left">s</entry><entry namest="col4" nameend="col4" align="left">TiCl₄: 3</entry><entry namest="col5" nameend="col5" align="center">450</entry><entry namest="col6" nameend="col6" align="center">1000</entry><entry namest="col7" nameend="col7" align="center">14</entry><entry namest="col8" nameend="col8" align="char" char=".">1.45</entry></row><row><entry namest="col2" nameend="col2" align="left">T</entry><entry namest="col3" nameend="col3" align="left">t</entry><entry namest="col4" nameend="col4" align="left">CO₂: 11</entry><entry namest="col5" nameend="col5" align="center">500</entry><entry namest="col6" nameend="col6" align="center">1000</entry><entry namest="col7" nameend="col7" align="center">15</entry><entry namest="col8" nameend="col8" align="char" char=".">1.82</entry></row><row><entry namest="col2" nameend="col2" align="left">U</entry><entry namest="col3" nameend="col3" align="left">u</entry><entry namest="col4" nameend="col4" align="left">TiCl₄: 1</entry><entry namest="col5" nameend="col5" align="center">50</entry><entry namest="col6" nameend="col6" align="center">900</entry><entry namest="col7" nameend="col7" align="center">5</entry><entry namest="col8" nameend="col8" align="char" char=".">0.11</entry></row><row><entry namest="col2" nameend="col2" align="left">V</entry><entry namest="col3" nameend="col3" align="left">v</entry><entry namest="col4" nameend="col4" align="left">TiCl₄: 3</entry><entry namest="col5" nameend="col5" align="center">100</entry><entry namest="col6" nameend="col6" align="center">900</entry><entry namest="col7" nameend="col7" align="center">7</entry><entry namest="col8" nameend="col8" align="char" char=".">0.36</entry></row><row><entry namest="col2" nameend="col2" align="left">W</entry><entry namest="col3" nameend="col3" align="left">w</entry><entry namest="col4" nameend="col4" align="left">CO₂: 9</entry><entry namest="col5" nameend="col5" align="center">300</entry><entry namest="col6" nameend="col6" align="center">950</entry><entry namest="col7" nameend="col7" align="center">9</entry><entry namest="col8" nameend="col8" align="char" char=".">1.01</entry></row><row><entry namest="col2" nameend="col2" align="left">X</entry><entry namest="col3" nameend="col3" align="left">x</entry><entry namest="col4" nameend="col4" align="left">TiCl₄: 2</entry><entry namest="col5" nameend="col5" align="center">450</entry><entry namest="col6" nameend="col6" align="center">900</entry><entry namest="col7" nameend="col7" align="center">10</entry><entry namest="col8" nameend="col8" align="char" char=".">1.98</entry></row><row><entry namest="col2" nameend="col2" align="left">Y</entry><entry namest="col3" nameend="col3" align="left">y</entry><entry namest="col4" nameend="col4" align="left">CO₂: 11</entry><entry namest="col5" nameend="col5" align="center">100</entry><entry namest="col6" nameend="col6" align="center">900</entry><entry namest="col7" nameend="col7" align="center">6</entry><entry namest="col8" nameend="col8" align="char" char=".">0.33</entry></row><row rowsep="1"><entry namest="col2" nameend="col2" align="left">Z</entry><entry namest="col3" nameend="col3" align="left">z</entry><entry namest="col4" nameend="col4" align="left">TiCl₄: 2</entry><entry namest="col5" nameend="col5" align="center">400</entry><entry namest="col6" nameend="col6" align="center">950</entry><entry namest="col7" nameend="col7" align="center">8</entry><entry namest="col8" nameend="col8" align="char" char=".">1.01</entry></row></tbody></tgroup></table></tables><tables id="tabl0005" num="0005"><table frame="all"><title>Table 5</title><tgroup cols="4" colsep="1" rowsep="1"><colspec colnum="1" colname="col1" colwidth="39.37mm" /><colspec colnum="2" colname="col2" colwidth="39.37mm" /><colspec colnum="3" colname="col3" colwidth="39.37mm" /><colspec colnum="4" colname="col4" colwidth="39.37mm" /><thead valign="top"><row><entry namest="col1" nameend="col1" rowsep="0" align="center">Type of hard-material-coated-layer</entry><entry namest="col2" nameend="col4" align="center">Hard-material-coated-layer forming conditions</entry></row><row><entry namest="col1" nameend="col1" rowsep="0" /><entry namest="col2" nameend="col2" rowsep="0" align="center">Composition of reaction gas (vol%)</entry><entry namest="col3" nameend="col4" align="center">Reaction atmosphere</entry></row><row><entry namest="col1" nameend="col1" /><entry namest="col2" nameend="col2" /><entry namest="col3" nameend="col3" align="center">Pressure (torr)</entry><entry namest="col4" nameend="col4" align="center">Temperature (°C)</entry></row></thead><tbody valign="top"><row><entry namest="col1" nameend="col1" align="left">Al₂O₃ *</entry><entry namest="col2" nameend="col2" align="left">Al₂₁Cl₃:4, CO₂: 10, H₂S: 0.2. HCl: 2, H₁: balance</entry><entry namest="col3" nameend="col3" align="center">50</entry><entry namest="col4" nameend="col4" align="center">1020</entry></row><row><entry namest="col1" nameend="col1" align="left">Al₂O₃</entry><entry namest="col2" nameend="col2" align="left">Al[OCH(CH₃)₂]₃: 0.3, H₂: balance</entry><entry namest="col3" nameend="col3" align="center">50</entry><entry namest="col4" nameend="col4" align="center">900</entry></row><row><entry namest="col1" nameend="col1" align="left">TiC</entry><entry namest="col2" nameend="col2" align="left">TiCl₄: 2, C₃H₈: 5, H₂: balance</entry><entry namest="col3" nameend="col3" align="center">100</entry><entry namest="col4" nameend="col4" align="center">900</entry></row><row><entry namest="col1" nameend="col1" align="left">TiN</entry><entry namest="col2" nameend="col2" align="left">TiCl₄: 2, N : 30, H : balance</entry><entry namest="col3" nameend="col3" align="center">100</entry><entry namest="col4" nameend="col4" align="center">850</entry></row><row><entry namest="col1" nameend="col1" align="left">TiCN</entry><entry namest="col2" nameend="col2" align="left">TiCl₄: 2, N₂: 10, CH₃CN: 0.8, H₂: balance</entry><entry namest="col3" nameend="col3" align="center">70</entry><entry namest="col4" nameend="col4" align="center">900</entry></row><row><entry namest="col1" nameend="col1" align="left">TiCO</entry><entry namest="col2" nameend="col2" align="left">TiCl₄: 3, CO: 2, H₂: balance</entry><entry namest="col3" nameend="col3" align="center">100</entry><entry namest="col4" nameend="col4" align="center">900</entry></row><row><entry namest="col1" nameend="col1" align="left">TiNO</entry><entry namest="col2" nameend="col2" align="left">TiCl₄: 3, CO: 1, N₂: 15, H₂: balance</entry><entry namest="col3" nameend="col3" align="center">50</entry><entry namest="col4" nameend="col4" align="center">900</entry></row><row><entry namest="col1" nameend="col1" align="left">TiCNO</entry><entry namest="col2" nameend="col2" align="left">TiCl₄: 3. CO: 2, N₂: 15, H₂: balance</entry><entry namest="col3" nameend="col3" align="center">50</entry><entry namest="col4" nameend="col4" align="center">900</entry></row><row rowsep="1"><entry namest="col1" nameend="col4" align="justify">[In Table 5, item with * shows high temperature chemical vapor deposition (HT-CVD) and items without * show medium temperature chemical vapor deposition (MT-CVD).]</entry></row></tbody></tgroup></table></tables><tables id="tabl0006" num="0006"><img file="EP0900860A2_D0002.tif" /></tables><tables id="tabl0007" num="0007"><img file="EP0900860A2_D0003.tif" /></tables><tables id="tabl0008" num="0008"><img file="EP0900860A2_D0004.tif" /></tables><tables id="tabl0009" num="0009"><table frame="all"><title>Table 9</title><tgroup cols="7" colsep="1" rowsep="1"><colspec colnum="1" colname="col1" colwidth="22.50mm" /><colspec colnum="2" colname="col2" colwidth="22.50mm" /><colspec colnum="3" colname="col3" colwidth="22.50mm" /><colspec colnum="4" colname="col4" colwidth="22.50mm" /><colspec colnum="5" colname="col5" colwidth="22.50mm" /><colspec colnum="6" colname="col6" colwidth="22.50mm" /><colspec colnum="7" colname="col7" colwidth="22.50mm" /><thead valign="top"><row><entry namest="col1" nameend="col2" rowsep="0" align="center">Type</entry><entry namest="col3" nameend="col6" align="center">Composition (wt%)</entry><entry namest="col7" nameend="col7" rowsep="0" align="center">Average grain size of WC (µm)</entry></row><row><entry namest="col1" nameend="col2" /><entry namest="col3" nameend="col3" align="center">Co</entry><entry namest="col4" nameend="col4" align="center">Cr</entry><entry namest="col5" nameend="col5" align="center">V</entry><entry namest="col6" nameend="col6" align="center">WC + impurities</entry><entry namest="col7" nameend="col7" /></row></thead><tbody valign="top"><row><entry namest="col1" nameend="col1" morerows="19" align="center">Cemented carbide substrate</entry><entry namest="col2" nameend="col2" align="left">a</entry><entry namest="col3" nameend="col3" align="char" char=".">8.1</entry><entry namest="col4" nameend="col4" align="center">0.52</entry><entry namest="col5" nameend="col5" align="center">0.10</entry><entry namest="col6" nameend="col6" align="left">balance</entry><entry namest="col7" nameend="col7" align="char" char=".">0.52</entry></row><row><entry namest="col2" nameend="col2" align="left">b</entry><entry namest="col3" nameend="col3" align="center">9.8</entry><entry namest="col4" nameend="col4" align="char" char=".">0.40</entry><entry namest="col5" nameend="col5" align="char" char=".">0.21</entry><entry namest="col6" nameend="col6" align="left">balance</entry><entry namest="col7" nameend="col7" align="char" char=".">0.76</entry></row><row><entry namest="col2" nameend="col2" align="left">c</entry><entry namest="col3" nameend="col3" align="center">7.8</entry><entry namest="col4" nameend="col4" align="char" char=".">0.28</entry><entry namest="col5" nameend="col5" align="char" char=".">0.12</entry><entry namest="col6" nameend="col6" align="left">balance</entry><entry namest="col7" nameend="col7" align="char" char=".">0.95</entry></row><row><entry namest="col2" nameend="col2" align="left">d</entry><entry namest="col3" nameend="col3" align="center">10.3</entry><entry namest="col4" nameend="col4" align="char" char=".">0.11</entry><entry namest="col5" nameend="col5" align="char" char=".">0.30</entry><entry namest="col6" nameend="col6" align="left">balance</entry><entry namest="col7" nameend="col7" align="char" char=".">0.03</entry></row><row><entry namest="col2" nameend="col2" align="left">e</entry><entry namest="col3" nameend="col3" align="center">12.4</entry><entry namest="col4" nameend="col4" align="char" char=".">0.23</entry><entry namest="col5" nameend="col5" align="char" char=".">0.45</entry><entry namest="col6" nameend="col6" align="left">balance</entry><entry namest="col7" nameend="col7" align="char" char=".">0.51</entry></row><row><entry namest="col2" nameend="col2" align="left">f</entry><entry namest="col3" nameend="col3" align="center">11.6</entry><entry namest="col4" nameend="col4" align="char" char=".">0.78</entry><entry namest="col5" nameend="col5" align="char" char=".">0.22</entry><entry namest="col6" nameend="col6" align="left">balance</entry><entry namest="col7" nameend="col7" align="char" char=".">0.80</entry></row><row><entry namest="col2" nameend="col2" align="left">g</entry><entry namest="col3" nameend="col3" align="center">19.7</entry><entry namest="col4" nameend="col4" align="char" char=".">1.71</entry><entry namest="col5" nameend="col5" align="char" char=".">0.31</entry><entry namest="col6" nameend="col6" align="left">balance</entry><entry namest="col7" nameend="col7" align="char" char=".">0.11</entry></row><row><entry namest="col2" nameend="col2" align="left">h</entry><entry namest="col3" nameend="col3" align="center">15.1</entry><entry namest="col4" nameend="col4" align="char" char=".">0.13</entry><entry namest="col5" nameend="col5" align="char" char=".">0.08</entry><entry namest="col6" nameend="col6" align="left">balance</entry><entry namest="col7" nameend="col7" align="char" char=".">1.23</entry></row><row><entry namest="col2" nameend="col2" align="left">i</entry><entry namest="col3" nameend="col3" align="center">10.2</entry><entry namest="col4" nameend="col4" align="char" char=".">-</entry><entry namest="col5" nameend="col5" align="char" char=".">1.52</entry><entry namest="col6" nameend="col6" align="left">balance</entry><entry namest="col7" nameend="col7" align="char" char=".">0.30</entry></row><row><entry namest="col2" nameend="col2" align="left">j</entry><entry namest="col3" nameend="col3" align="center">7.9</entry><entry namest="col4" nameend="col4" align="char" char=".">-</entry><entry namest="col5" nameend="col5" align="char" char=".">0.61</entry><entry namest="col6" nameend="col6" align="left">balance</entry><entry namest="col7" nameend="col7" align="char" char=".">1.17</entry></row><row><entry namest="col2" nameend="col2" align="left">k</entry><entry namest="col3" nameend="col3" align="center">5.0</entry><entry namest="col4" nameend="col4" align="char" char=".">-</entry><entry namest="col5" nameend="col5" align="char" char=".">0.11</entry><entry namest="col6" nameend="col6" align="left">balance</entry><entry namest="col7" nameend="col7" align="char" char=".">1.50</entry></row><row><entry namest="col2" nameend="col2" align="left">l</entry><entry namest="col3" nameend="col3" align="center">9.6</entry><entry namest="col4" nameend="col4" align="char" char=".">-</entry><entry namest="col5" nameend="col5" align="char" char=".">0.48</entry><entry namest="col6" nameend="col6" align="left">balance</entry><entry namest="col7" nameend="col7" align="char" char=".">0.82</entry></row><row><entry namest="col2" nameend="col2" align="left">m</entry><entry namest="col3" nameend="col3" align="center">6.3</entry><entry namest="col4" nameend="col4" align="char" char=".">-</entry><entry namest="col5" nameend="col5" align="char" char=".">0.29</entry><entry namest="col6" nameend="col6" align="left">balance</entry><entry namest="col7" nameend="col7" align="char" char=".">0.12</entry></row><row><entry namest="col2" nameend="col2" align="left">n</entry><entry namest="col3" nameend="col3" align="center">19.8</entry><entry namest="col4" nameend="col4" align="char" char=".">-</entry><entry namest="col5" nameend="col5" align="char" char=".">0.13</entry><entry namest="col6" nameend="col6" align="left">balance</entry><entry namest="col7" nameend="col7" align="char" char=".">1.54</entry></row><row><entry namest="col2" nameend="col2" align="left">o</entry><entry namest="col3" nameend="col3" align="center">10.1</entry><entry namest="col4" nameend="col4" align="char" char=".">0.82</entry><entry namest="col5" nameend="col5" align="char" char=".">-</entry><entry namest="col6" nameend="col6" align="left">balance</entry><entry namest="col7" nameend="col7" align="char" char=".">1.04</entry></row><row><entry namest="col2" nameend="col2" align="left">p</entry><entry namest="col3" nameend="col3" align="center">8.0</entry><entry namest="col4" nameend="col4" align="char" char=".">0.55</entry><entry namest="col5" nameend="col5" align="char" char=".">-</entry><entry namest="col6" nameend="col6" align="left">balance</entry><entry namest="col7" nameend="col7" align="char" char=".">0.51</entry></row><row><entry namest="col2" nameend="col2" align="left">q</entry><entry namest="col3" nameend="col3" align="center">6.1</entry><entry namest="col4" nameend="col4" align="char" char=".">0.32</entry><entry namest="col5" nameend="col5" align="char" char=".">-</entry><entry namest="col6" nameend="col6" align="left">balance</entry><entry namest="col7" nameend="col7" align="char" char=".">1.47</entry></row><row><entry namest="col2" nameend="col2" align="left">r</entry><entry namest="col3" nameend="col3" align="center">17.8</entry><entry namest="col4" nameend="col4" align="char" char=".">1.54</entry><entry namest="col5" nameend="col5" align="char" char=".">-</entry><entry namest="col6" nameend="col6" align="left">balance</entry><entry namest="col7" nameend="col7" align="char" char=".">0.33</entry></row><row><entry namest="col2" nameend="col2" align="left">s</entry><entry namest="col3" nameend="col3" align="center">15.2</entry><entry namest="col4" nameend="col4" align="char" char=".">0.96</entry><entry namest="col5" nameend="col5" align="char" char=".">-</entry><entry namest="col6" nameend="col6" align="left">balance</entry><entry namest="col7" nameend="col7" align="char" char=".">0.80</entry></row><row rowsep="1"><entry namest="col2" nameend="col2" align="left">t</entry><entry namest="col3" nameend="col3" align="center">12.0</entry><entry namest="col4" nameend="col4" align="char" char=".">1.03</entry><entry namest="col5" nameend="col5" align="char" char=".">-</entry><entry namest="col6" nameend="col6" align="left">balance</entry><entry namest="col7" nameend="col7" align="char" char=".">0.49</entry></row></tbody></tgroup></table></tables><tables id="tabl0010" num="0010"><table frame="all"><title>Table 10</title><tgroup cols="8" colsep="1" rowsep="1"><colspec colnum="1" colname="col1" colwidth="19.68mm" /><colspec colnum="2" colname="col2" colwidth="19.68mm" /><colspec colnum="3" colname="col3" colwidth="19.68mm" /><colspec colnum="4" colname="col4" colwidth="19.68mm" /><colspec colnum="5" colname="col5" colwidth="19.68mm" /><colspec colnum="6" colname="col6" colwidth="19.68mm" /><colspec colnum="7" colname="col7" colwidth="19.68mm" /><colspec colnum="8" colname="col8" colwidth="19.68mm" /><thead valign="top"><row><entry namest="col1" nameend="col2" rowsep="0" align="center">Type</entry><entry namest="col3" nameend="col3" rowsep="0" align="center">Symbol of substrate</entry><entry namest="col4" nameend="col8" align="center">Surface layer formed by being heated at high temperature</entry></row><row><entry namest="col1" nameend="col2" rowsep="0" /><entry namest="col3" nameend="col3" rowsep="0" /><entry namest="col4" nameend="col7" align="center">Forming conditions</entry><entry namest="col8" nameend="col8" rowsep="0" align="center">Average distributed depth of Co_mW_nC (µm)</entry></row><row><entry namest="col1" nameend="col2" rowsep="0" /><entry namest="col3" nameend="col3" rowsep="0" /><entry namest="col4" nameend="col5" align="center">Atmosphere</entry><entry namest="col6" nameend="col6" rowsep="0" align="center">Temperature (°C)</entry><entry namest="col7" nameend="col7" rowsep="0" align="center">Holding time (min.)</entry><entry namest="col8" nameend="col8" rowsep="0" /></row><row><entry namest="col1" nameend="col2" /><entry namest="col3" nameend="col3" /><entry namest="col4" nameend="col4" align="center">Ratio of composition blended to H₂ (vol%)</entry><entry namest="col5" nameend="col5" align="center">Pressure (torr)</entry><entry namest="col6" nameend="col6" /><entry namest="col7" nameend="col7" /><entry namest="col8" nameend="col8" /></row></thead><tbody valign="top"><row><entry namest="col1" nameend="col1" morerows="19" align="center">Cemented carbide substrate</entry><entry namest="col2" nameend="col2" align="left">A</entry><entry namest="col3" nameend="col3" align="left">a</entry><entry namest="col4" nameend="col4" align="left">CO₂: 11</entry><entry namest="col5" nameend="col5" align="right">250</entry><entry namest="col6" nameend="col6" align="center">1000</entry><entry namest="col7" nameend="col7" align="center">5</entry><entry namest="col8" nameend="col8" align="char" char=".">0.96</entry></row><row><entry namest="col2" nameend="col2" align="left">B</entry><entry namest="col3" nameend="col3" align="left">b</entry><entry namest="col4" nameend="col4" align="left">TiCl₄: 2</entry><entry namest="col5" nameend="col5" align="center">450</entry><entry namest="col6" nameend="col6" align="center">950</entry><entry namest="col7" nameend="col7" align="center">1</entry><entry namest="col8" nameend="col8" align="char" char=".">0.52</entry></row><row><entry namest="col2" nameend="col2" align="left">C</entry><entry namest="col3" nameend="col3" align="left">c</entry><entry namest="col4" nameend="col4" align="left">CO₂: 9</entry><entry namest="col5" nameend="col5" align="center">350</entry><entry namest="col6" nameend="col6" align="center">1000</entry><entry namest="col7" nameend="col7" align="center">10</entry><entry namest="col8" nameend="col8" align="char" char=".">1.52</entry></row><row><entry namest="col2" nameend="col2" align="left">D</entry><entry namest="col3" nameend="col3" align="left">d</entry><entry namest="col4" nameend="col4" align="left">TiCl₄: 2</entry><entry namest="col5" nameend="col5" align="center">550</entry><entry namest="col6" nameend="col6" align="center">900</entry><entry namest="col7" nameend="col7" align="center">7</entry><entry namest="col8" nameend="col8" align="char" char=".">1.04</entry></row><row><entry namest="col2" nameend="col2" align="left">E</entry><entry namest="col3" nameend="col3" align="left">e</entry><entry namest="col4" nameend="col4" align="left">TiCl₄: 3</entry><entry namest="col5" nameend="col5" align="center">500</entry><entry namest="col6" nameend="col6" align="center">1000</entry><entry namest="col7" nameend="col7" align="center">7</entry><entry namest="col8" nameend="col8" align="char" char=".">1.50</entry></row><row><entry namest="col2" nameend="col2" align="left">F</entry><entry namest="col3" nameend="col3" align="left">f</entry><entry namest="col4" nameend="col4" align="left">TiCl₄: 1</entry><entry namest="col5" nameend="col5" align="center">300</entry><entry namest="col6" nameend="col6" align="center">900</entry><entry namest="col7" nameend="col7" align="center">7</entry><entry namest="col8" nameend="col8" align="char" char=".">0.48</entry></row><row><entry namest="col2" nameend="col2" align="left">G</entry><entry namest="col3" nameend="col3" align="left">g</entry><entry namest="col4" nameend="col4" align="left">TiCl₄: 2</entry><entry namest="col5" nameend="col5" align="center">50</entry><entry namest="col6" nameend="col6" align="center">900</entry><entry namest="col7" nameend="col7" align="center">1</entry><entry namest="col8" nameend="col8" align="char" char=".">0.12</entry></row><row><entry namest="col2" nameend="col2" align="left">H</entry><entry namest="col3" nameend="col3" align="left">h</entry><entry namest="col4" nameend="col4" align="left">CO₂: 9</entry><entry namest="col5" nameend="col5" align="center">200</entry><entry namest="col6" nameend="col6" align="center">950</entry><entry namest="col7" nameend="col7" align="center">3</entry><entry namest="col8" nameend="col8" align="char" char=".">0.31</entry></row><row><entry namest="col2" nameend="col2" align="left">I</entry><entry namest="col3" nameend="col3" align="left">i</entry><entry namest="col4" nameend="col4" align="left">TiCl₄: 1</entry><entry namest="col5" nameend="col5" align="center">400</entry><entry namest="col6" nameend="col6" align="center">950</entry><entry namest="col7" nameend="col7" align="center">7</entry><entry namest="col8" nameend="col8" align="char" char=".">1.06</entry></row><row><entry namest="col2" nameend="col2" align="left">J</entry><entry namest="col3" nameend="col3" align="left">j</entry><entry namest="col4" nameend="col4" align="left">TiCl₄: 2</entry><entry namest="col5" nameend="col5" align="center">450</entry><entry namest="col6" nameend="col6" align="center">950</entry><entry namest="col7" nameend="col7" align="center">7</entry><entry namest="col8" nameend="col8" align="char" char=".">1.33</entry></row><row><entry namest="col2" nameend="col2" align="left">K</entry><entry namest="col3" nameend="col3" align="left">k</entry><entry namest="col4" nameend="col4" align="left">CO₂: 10</entry><entry namest="col5" nameend="col5" align="center">550</entry><entry namest="col6" nameend="col6" align="center">1000</entry><entry namest="col7" nameend="col7" align="center">10</entry><entry namest="col8" nameend="col8" align="char" char=".">1.95</entry></row><row><entry namest="col2" nameend="col2" align="left">L</entry><entry namest="col3" nameend="col3" align="left">l</entry><entry namest="col4" nameend="col4" align="left">CO₂: 9</entry><entry namest="col5" nameend="col5" align="center">250</entry><entry namest="col6" nameend="col6" align="center">950</entry><entry namest="col7" nameend="col7" align="center">5</entry><entry namest="col8" nameend="col8" align="char" char=".">0.51</entry></row><row><entry namest="col2" nameend="col2" align="left">M</entry><entry namest="col3" nameend="col3" align="left">m</entry><entry namest="col4" nameend="col4" align="left">TiCl₄: 3</entry><entry namest="col5" nameend="col5" align="center">550</entry><entry namest="col6" nameend="col6" align="center">1000</entry><entry namest="col7" nameend="col7" align="center">7</entry><entry namest="col8" nameend="col8" align="char" char=".">1.80</entry></row><row><entry namest="col2" nameend="col2" align="left">N</entry><entry namest="col3" nameend="col3" align="left">n</entry><entry namest="col4" nameend="col4" align="left">CO₂: 9</entry><entry namest="col5" nameend="col5" align="center">500</entry><entry namest="col6" nameend="col6" align="center">1000</entry><entry namest="col7" nameend="col7" align="center">16</entry><entry namest="col8" nameend="col8" align="char" char=".">1.76</entry></row><row><entry namest="col2" nameend="col2" align="left">O</entry><entry namest="col3" nameend="col3" align="left">o</entry><entry namest="col4" nameend="col4" align="left">TiCl₄: 2</entry><entry namest="col5" nameend="col5" align="center">400</entry><entry namest="col6" nameend="col6" align="center">950</entry><entry namest="col7" nameend="col7" align="center">5</entry><entry namest="col8" nameend="col8" align="char" char=".">0.97</entry></row><row><entry namest="col2" nameend="col2" align="left">P</entry><entry namest="col3" nameend="col3" align="left">p</entry><entry namest="col4" nameend="col4" align="left">TiCl₄: 2</entry><entry namest="col5" nameend="col5" align="center">500</entry><entry namest="col6" nameend="col6" align="center">950</entry><entry namest="col7" nameend="col7" align="center">16</entry><entry namest="col8" nameend="col8" align="char" char=".">1.46</entry></row><row><entry namest="col2" nameend="col2" align="left">Q</entry><entry namest="col3" nameend="col3" align="left">q</entry><entry namest="col4" nameend="col4" align="left">TiCl₄: 3</entry><entry namest="col5" nameend="col5" align="center">200</entry><entry namest="col6" nameend="col6" align="center">900</entry><entry namest="col7" nameend="col7" align="center">3</entry><entry namest="col8" nameend="col8" align="char" char=".">0.30</entry></row><row><entry namest="col2" nameend="col2" align="left">R</entry><entry namest="col3" nameend="col3" align="left">r</entry><entry namest="col4" nameend="col4" align="left">TiCl₄: 1</entry><entry namest="col5" nameend="col5" align="center">550</entry><entry namest="col6" nameend="col6" align="center">950</entry><entry namest="col7" nameend="col7" align="center">10</entry><entry namest="col8" nameend="col8" align="char" char=".">1.89</entry></row><row><entry namest="col2" nameend="col2" align="left">S</entry><entry namest="col3" nameend="col3" align="left">s</entry><entry namest="col4" nameend="col4" align="left">CO₂: 10</entry><entry namest="col5" nameend="col5" align="center">100</entry><entry namest="col6" nameend="col6" align="center">900</entry><entry namest="col7" nameend="col7" align="center">1</entry><entry namest="col8" nameend="col8" align="char" char=".">0.28</entry></row><row rowsep="1"><entry namest="col2" nameend="col2" align="left">T</entry><entry namest="col3" nameend="col3" align="left">t</entry><entry namest="col4" nameend="col4" align="left">CO₂: 11</entry><entry namest="col5" nameend="col5" align="center">200</entry><entry namest="col6" nameend="col6" align="center">950</entry><entry namest="col7" nameend="col7" align="center">3</entry><entry namest="col8" nameend="col8" align="char" char=".">0.47</entry></row></tbody></tgroup></table></tables><tables id="tabl0011" num="0011"><table frame="all"><title>Table 11</title><tgroup cols="4" colsep="1" rowsep="1"><colspec colnum="1" colname="col1" colwidth="39.37mm" /><colspec colnum="2" colname="col2" colwidth="39.37mm" /><colspec colnum="3" colname="col3" colwidth="39.37mm" /><colspec colnum="4" colname="col4" colwidth="39.37mm" /><thead valign="top"><row><entry namest="col1" nameend="col1" rowsep="0" align="center">Type of hard-material-coated-layer</entry><entry namest="col2" nameend="col4" align="center">Hard-material-coated-layer forming conditions</entry></row><row><entry namest="col1" nameend="col1" rowsep="0" /><entry namest="col2" nameend="col2" rowsep="0" align="center">Composition of reaction gas (vol%)</entry><entry namest="col3" nameend="col4" align="center">Reaction atmosphere</entry></row><row><entry namest="col1" nameend="col1" /><entry namest="col2" nameend="col2" /><entry namest="col3" nameend="col3" align="center">Pressure (torr)</entry><entry namest="col4" nameend="col4" align="center">Temperature (°C)</entry></row></thead><tbody valign="top"><row><entry namest="col1" nameend="col1" align="left">Al,O₃ *</entry><entry namest="col2" nameend="col2" align="left">Al₂Cl₃: 4, CO₂: 10, H₂S: 0.2, HCl: 2, H₂: balance</entry><entry namest="col3" nameend="col3" align="center">50</entry><entry namest="col4" nameend="col4" align="center">1020</entry></row><row><entry namest="col1" nameend="col1" align="left">Al₂O₃</entry><entry namest="col2" nameend="col2" align="left">Al[OCH(CH₃)₂]₃: 0.3, H₂: balance</entry><entry namest="col3" nameend="col3" align="center">50</entry><entry namest="col4" nameend="col4" align="center">900</entry></row><row><entry namest="col1" nameend="col1" align="left">TiC</entry><entry namest="col2" nameend="col2" align="left">TiCl₄: 2, C₃H₈: 5, H₂: balance</entry><entry namest="col3" nameend="col3" align="center">100</entry><entry namest="col4" nameend="col4" align="center">900</entry></row><row><entry namest="col1" nameend="col1" align="left">TiN</entry><entry namest="col2" nameend="col2" align="left">TiCl₄: 2, N₂: 30, H₂: balance</entry><entry namest="col3" nameend="col3" align="center">100</entry><entry namest="col4" nameend="col4" align="center">850</entry></row><row><entry namest="col1" nameend="col1" align="left">TiCN</entry><entry namest="col2" nameend="col2" align="left">TiCl₄: 2, N₂: 10, CH₃CN: 0.8, H₂: balance</entry><entry namest="col3" nameend="col3" align="center">70</entry><entry namest="col4" nameend="col4" align="center">900</entry></row><row><entry namest="col1" nameend="col1" align="left">TiCO</entry><entry namest="col2" nameend="col2" align="left">TiCl₄: 3, CO: 2, H₂: balance</entry><entry namest="col3" nameend="col3" align="center">100</entry><entry namest="col4" nameend="col4" align="center">900</entry></row><row><entry namest="col1" nameend="col1" align="left">TiNO</entry><entry namest="col2" nameend="col2" align="left">TiCl₄: 3, CO: 1, N₂: 15, H₂: balance</entry><entry namest="col3" nameend="col3" align="center">50</entry><entry namest="col4" nameend="col4" align="center">900</entry></row><row><entry namest="col1" nameend="col1" align="left">TiCNO</entry><entry namest="col2" nameend="col2" align="left">TiCl₄: 3, CO: 2, N₂: 15, H₂: balance</entry><entry namest="col3" nameend="col3" align="center">50</entry><entry namest="col4" nameend="col4" align="center">900</entry></row><row rowsep="1"><entry namest="col1" nameend="col4" align="justify">[In Table 11, item with * shows high temperature chemical vapor deposition (HT-CVD) and items without * show medium temperature chemical vapor deposition (MT-CVD).]</entry></row></tbody></tgroup></table></tables><tables id="tabl0012" num="0012"><img file="EP0900860A2_D0005.tif" /></tables><tables id="tabl0013" num="0013"><img file="EP0900860A2_D0006.tif" /></tables><tables id="tabl0014" num="0014"><table frame="all"><title>Table 14</title><tgroup cols="8" colsep="1" rowsep="1"><colspec colnum="1" colname="col1" colwidth="19.68mm" /><colspec colnum="2" colname="col2" colwidth="19.68mm" /><colspec colnum="3" colname="col3" colwidth="19.68mm" /><colspec colnum="4" colname="col4" colwidth="19.68mm" /><colspec colnum="5" colname="col5" colwidth="19.68mm" /><colspec colnum="6" colname="col6" colwidth="19.68mm" /><colspec colnum="7" colname="col7" colwidth="19.68mm" /><colspec colnum="8" colname="col8" colwidth="19.68mm" /><thead valign="top"><row><entry namest="col1" nameend="col2" rowsep="0" align="center">Type</entry><entry namest="col3" nameend="col7" align="center">Composition (wt%)</entry><entry namest="col8" nameend="col8" rowsep="0" align="center">Average grain size of WC (µm)</entry></row><row><entry namest="col1" nameend="col2" /><entry namest="col3" nameend="col3" align="center">Co</entry><entry namest="col4" nameend="col4" align="center">Cr</entry><entry namest="col5" nameend="col5" align="center">V</entry><entry namest="col6" nameend="col6" align="center">(Ti, Ta, Nb, Zr) C · N</entry><entry namest="col7" nameend="col7" align="center">WC + impurities</entry><entry namest="col8" nameend="col8" /></row></thead><tbody valign="top"><row><entry namest="col1" nameend="col1" morerows="19" align="center">Cemented carbide substrate</entry><entry namest="col2" nameend="col2" align="left">a</entry><entry namest="col3" nameend="col3" align="center">12.0</entry><entry namest="col4" nameend="col4" align="char" char=".">0.48</entry><entry namest="col5" nameend="col5" align="center">0.50</entry><entry namest="col6" nameend="col6" align="left">TiC: 1.9</entry><entry namest="col7" nameend="col7" align="left">balance</entry><entry namest="col8" nameend="col8" align="char" char=".">0.9</entry></row><row><entry namest="col2" nameend="col2" align="left">b</entry><entry namest="col3" nameend="col3" align="center">7.9</entry><entry namest="col4" nameend="col4" align="char" char=".">0.23</entry><entry namest="col5" nameend="col5" align="char" char=".">1.02</entry><entry namest="col6" nameend="col6" align="left">TaN: 0.5</entry><entry namest="col7" nameend="col7" align="left">balance</entry><entry namest="col8" nameend="col8" align="char" char=".">1.2</entry></row><row><entry namest="col2" nameend="col2" align="left">c</entry><entry namest="col3" nameend="col3" align="center">14.8</entry><entry namest="col4" nameend="col4" align="char" char=".">1.41</entry><entry namest="col5" nameend="col5" align="char" char=".">-</entry><entry namest="col6" nameend="col6" align="left">TaCN:1.5</entry><entry namest="col7" nameend="col7" align="left">balance</entry><entry namest="col8" nameend="col8" align="char" char=".">0.4</entry></row><row><entry namest="col2" nameend="col2" align="left">d</entry><entry namest="col3" nameend="col3" align="center">10.1</entry><entry namest="col4" nameend="col4" align="char" char=".">1.42</entry><entry namest="col5" nameend="col5" align="char" char=".">0.51</entry><entry namest="col6" nameend="col6" align="left">NbN: 1.3</entry><entry namest="col7" nameend="col7" align="left">balance</entry><entry namest="col8" nameend="col8" align="char" char=".">0.5</entry></row><row><entry namest="col2" nameend="col2" align="left">e</entry><entry namest="col3" nameend="col3" align="center">17.8</entry><entry namest="col4" nameend="col4" align="char" char=".">-</entry><entry namest="col5" nameend="col5" align="char" char=".">1.55</entry><entry namest="col6" nameend="col6" align="left">NbCN: 3.3</entry><entry namest="col7" nameend="col7" align="left">balance</entry><entry namest="col8" nameend="col8" align="char" char=".">0.2</entry></row><row><entry namest="col2" nameend="col2" align="left">f</entry><entry namest="col3" nameend="col3" align="center">5.3</entry><entry namest="col4" nameend="col4" align="char" char=".">-</entry><entry namest="col5" nameend="col5" align="char" char=".">0.10</entry><entry namest="col6" nameend="col6" align="left">ZrCN: 0.9</entry><entry namest="col7" nameend="col7" align="left">balance</entry><entry namest="col8" nameend="col8" align="char" char=".">1.3</entry></row><row><entry namest="col2" nameend="col2" align="left">g</entry><entry namest="col3" nameend="col3" align="center">9.8</entry><entry namest="col4" nameend="col4" align="char" char=".">0.52</entry><entry namest="col5" nameend="col5" align="char" char=".">-</entry><entry namest="col6" nameend="col6" align="left">TaC: 1.0</entry><entry namest="col7" nameend="col7" align="left">balance</entry><entry namest="col8" nameend="col8" align="char" char=".">1.0</entry></row><row><entry namest="col2" nameend="col2" align="left">h</entry><entry namest="col3" nameend="col3" align="center">12.1</entry><entry namest="col4" nameend="col4" align="char" char=".">-</entry><entry namest="col5" nameend="col5" align="char" char=".">0.16</entry><entry namest="col6" nameend="col6" align="left">NbC: 3.0</entry><entry namest="col7" nameend="col7" align="left">balance</entry><entry namest="col8" nameend="col8" align="char" char=".">0.5</entry></row><row><entry namest="col2" nameend="col2" align="left">i</entry><entry namest="col3" nameend="col3" align="center">7.8</entry><entry namest="col4" nameend="col4" align="char" char=".">0.39</entry><entry namest="col5" nameend="col5" align="char" char=".">-</entry><entry namest="col6" nameend="col6" align="left">ZrN: 1.2</entry><entry namest="col7" nameend="col7" align="left">balance</entry><entry namest="col8" nameend="col8" align="char" char=".">1.5</entry></row><row><entry namest="col2" nameend="col2" align="left">j</entry><entry namest="col3" nameend="col3" align="center">14.7</entry><entry namest="col4" nameend="col4" align="char" char=".">-</entry><entry namest="col5" nameend="col5" align="char" char=".">1.21</entry><entry namest="col6" nameend="col6" align="left">TiCN: 4.1</entry><entry namest="col7" nameend="col7" align="left">balance</entry><entry namest="col8" nameend="col8" align="char" char=".">1.0</entry></row><row><entry namest="col2" nameend="col2" align="left">k</entry><entry namest="col3" nameend="col3" align="center">5.0</entry><entry namest="col4" nameend="col4" align="char" char=".">0.20</entry><entry namest="col5" nameend="col5" align="char" char=".">-</entry><entry namest="col6" nameend="col6" align="left">TiN: 0.5</entry><entry namest="col7" nameend="col7" align="left">balance</entry><entry namest="col8" nameend="col8" align="char" char=".">1.0</entry></row><row><entry namest="col2" nameend="col2" align="left">l</entry><entry namest="col3" nameend="col3" align="center">15.2</entry><entry namest="col4" nameend="col4" align="char" char=".">1.23</entry><entry namest="col5" nameend="col5" align="char" char=".">-</entry><entry namest="col6" nameend="col6" align="left">ZrC: 2.3</entry><entry namest="col7" nameend="col7" align="left">balance</entry><entry namest="col8" nameend="col8" align="char" char=".">0.3</entry></row><row><entry namest="col2" nameend="col2" align="left">m</entry><entry namest="col3" nameend="col3" align="center">11.9</entry><entry namest="col4" nameend="col4" align="char" char=".">1.04</entry><entry namest="col5" nameend="col5" align="char" char=".">-</entry><entry namest="col6" nameend="col6" align="left">(Ta, Nb) C: 1.5</entry><entry namest="col7" nameend="col7" align="left">balance</entry><entry namest="col8" nameend="col8" align="char" char=".">0.5</entry></row><row><entry namest="col2" nameend="col2" align="left">n</entry><entry namest="col3" nameend="col3" align="center">10.2</entry><entry namest="col4" nameend="col4" align="char" char=".">0.79</entry><entry namest="col5" nameend="col5" align="char" char=".">-</entry><entry namest="col6" nameend="col6" align="left">TaC: 0.5, ZrN: 0.5</entry><entry namest="col7" nameend="col7" align="left">balance</entry><entry namest="col8" nameend="col8" align="char" char=".">0.8</entry></row><row><entry namest="col2" nameend="col2" align="left">o</entry><entry namest="col3" nameend="col3" align="center">5.3</entry><entry namest="col4" nameend="col4" align="char" char=".">-</entry><entry namest="col5" nameend="col5" align="char" char=".">0.17</entry><entry namest="col6" nameend="col6" align="left">(Ti, Ta, Zr) C: 0.1</entry><entry namest="col7" nameend="col7" align="left">balance</entry><entry namest="col8" nameend="col8" align="char" char=".">1.5</entry></row><row><entry namest="col2" nameend="col2" align="left">p</entry><entry namest="col3" nameend="col3" align="center">19.8</entry><entry namest="col4" nameend="col4" align="char" char=".">0.87</entry><entry namest="col5" nameend="col5" align="char" char=".">0.97</entry><entry namest="col6" nameend="col6" align="left">(Ti, Ta, Nb, Zr) C: 5.0</entry><entry namest="col7" nameend="col7" align="left">balance</entry><entry namest="col8" nameend="col8" align="char" char=".">0.1</entry></row><row><entry namest="col2" nameend="col2" align="left">q</entry><entry namest="col3" nameend="col3" align="center">8.1</entry><entry namest="col4" nameend="col4" align="char" char=".">-</entry><entry namest="col5" nameend="col5" align="char" char=".">0.39</entry><entry namest="col6" nameend="col6" align="left">(Ti, Zr) C: 1.0, NbC: 0.1</entry><entry namest="col7" nameend="col7" align="left">balance</entry><entry namest="col8" nameend="col8" align="char" char=".">1.2</entry></row><row><entry namest="col2" nameend="col2" align="left">r</entry><entry namest="col3" nameend="col3" align="center">16.9</entry><entry namest="col4" nameend="col4" align="char" char=".">-</entry><entry namest="col5" nameend="col5" align="char" char=".">1.98</entry><entry namest="col6" nameend="col6" align="left">(Ta, Nb) C: 0.5, TaC: 1.0</entry><entry namest="col7" nameend="col7" align="left">balance</entry><entry namest="col8" nameend="col8" align="char" char=".">0.5</entry></row><row rowsep="0"><entry namest="col2" nameend="col2" morerows="1" rowsep="1" align="left">s</entry><entry namest="col3" nameend="col3" morerows="1" rowsep="1" align="center">9.8</entry><entry namest="col4" nameend="col4" morerows="1" rowsep="1" align="char" char=".">0.89</entry><entry namest="col5" nameend="col5" morerows="1" rowsep="1" align="char" char=".">-</entry><entry namest="col6" nameend="col6" align="left">Tic: 0.2, TaN: 0.8</entry><entry namest="col7" nameend="col7" morerows="1" rowsep="1" align="left">balance</entry><entry namest="col8" nameend="col8" morerows="1" rowsep="1" align="char" char=".">0.5</entry></row><row rowsep="1"><entry namest="col6" nameend="col6" align="left">NbC: 0.2, ZrCN: 1.6</entry></row></tbody></tgroup></table></tables><tables id="tabl0015" num="0015"><table frame="all"><title>Table 15</title><tgroup cols="8" colsep="1" rowsep="1"><colspec colnum="1" colname="col1" colwidth="19.68mm" /><colspec colnum="2" colname="col2" colwidth="19.68mm" /><colspec colnum="3" colname="col3" colwidth="19.68mm" /><colspec colnum="4" colname="col4" colwidth="19.68mm" /><colspec colnum="5" colname="col5" colwidth="19.68mm" /><colspec colnum="6" colname="col6" colwidth="19.68mm" /><colspec colnum="7" colname="col7" colwidth="19.68mm" /><colspec colnum="8" colname="col8" colwidth="19.68mm" /><thead valign="top"><row><entry namest="col1" nameend="col2" rowsep="0" align="center">Type</entry><entry namest="col3" nameend="col3" rowsep="0" align="center">Symbol of substrate</entry><entry namest="col4" nameend="col8" align="center">Surface layer formed by being heated at high temperature</entry></row><row><entry namest="col1" nameend="col2" rowsep="0" /><entry namest="col3" nameend="col3" rowsep="0" /><entry namest="col4" nameend="col7" align="center">Forming conditions</entry><entry namest="col8" nameend="col8" rowsep="0" align="center">Average distributed depth of Co_mW_nC (µm)</entry></row><row><entry namest="col1" nameend="col2" rowsep="0" /><entry namest="col3" nameend="col3" rowsep="0" /><entry namest="col4" nameend="col5" align="center">Atmosphere</entry><entry namest="col6" nameend="col6" rowsep="0" align="center">Temperature (°C)</entry><entry namest="col7" nameend="col7" rowsep="0" align="center">Holding time (min.)</entry><entry namest="col8" nameend="col8" rowsep="0" /></row><row><entry namest="col1" nameend="col2" /><entry namest="col3" nameend="col3" /><entry namest="col4" nameend="col4" align="center">Ratio of composition blended to H₂ (vol%)</entry><entry namest="col5" nameend="col5" align="center">Pressure (torr)</entry><entry namest="col6" nameend="col6" /><entry namest="col7" nameend="col7" /><entry namest="col8" nameend="col8" /></row></thead><tbody valign="top"><row><entry namest="col1" nameend="col1" morerows="18" align="center">Cemented carbide substrate</entry><entry namest="col2" nameend="col2" align="left">A</entry><entry namest="col3" nameend="col3" align="left">a</entry><entry namest="col4" nameend="col4" align="left">CO₂: 9</entry><entry namest="col5" nameend="col5" align="center">500</entry><entry namest="col6" nameend="col6" align="center">950</entry><entry namest="col7" nameend="col7" align="center">13</entry><entry namest="col8" nameend="col8" align="char" char=".">1.22</entry></row><row><entry namest="col2" nameend="col2" align="left">B</entry><entry namest="col3" nameend="col3" align="left">b</entry><entry namest="col4" nameend="col4" align="left">TiCl₄: 3</entry><entry namest="col5" nameend="col5" align="center">350</entry><entry namest="col6" nameend="col6" align="center">950</entry><entry namest="col7" nameend="col7" align="center">8</entry><entry namest="col8" nameend="col8" align="char" char=".">0.54</entry></row><row><entry namest="col2" nameend="col2" align="left">C</entry><entry namest="col3" nameend="col3" align="left">c</entry><entry namest="col4" nameend="col4" align="left">CO₂: 11</entry><entry namest="col5" nameend="col5" align="center">400</entry><entry namest="col6" nameend="col6" align="center">900</entry><entry namest="col7" nameend="col7" align="center">15</entry><entry namest="col8" nameend="col8" align="char" char=".">1.01</entry></row><row><entry namest="col2" nameend="col2" align="left">D</entry><entry namest="col3" nameend="col3" align="left">d</entry><entry namest="col4" nameend="col4" align="left">TiCl₄: 2</entry><entry namest="col5" nameend="col5" align="center">250</entry><entry namest="col6" nameend="col6" align="center">950</entry><entry namest="col7" nameend="col7" align="center">6</entry><entry namest="col8" nameend="col8" align="char" char=".">0.87</entry></row><row><entry namest="col2" nameend="col2" align="left">E</entry><entry namest="col3" nameend="col3" align="left">e</entry><entry namest="col4" nameend="col4" align="left">CO₂: 10</entry><entry namest="col5" nameend="col5" align="center">150</entry><entry namest="col6" nameend="col6" align="center">950</entry><entry namest="col7" nameend="col7" align="center">2</entry><entry namest="col8" nameend="col8" align="char" char=".">0.30</entry></row><row><entry namest="col2" nameend="col2" align="left">F</entry><entry namest="col3" nameend="col3" align="left">f</entry><entry namest="col4" nameend="col4" align="left">TiCl₄: 1</entry><entry namest="col5" nameend="col5" align="center">400</entry><entry namest="col6" nameend="col6" align="center">1000</entry><entry namest="col7" nameend="col7" align="center">8</entry><entry namest="col8" nameend="col8" align="char" char=".">1.13</entry></row><row><entry namest="col2" nameend="col2" align="left">G</entry><entry namest="col3" nameend="col3" align="left">g</entry><entry namest="col4" nameend="col4" align="left">CO₂: 11</entry><entry namest="col5" nameend="col5" align="center">350</entry><entry namest="col6" nameend="col6" align="center">900</entry><entry namest="col7" nameend="col7" align="center">5</entry><entry namest="col8" nameend="col8" align="char" char=".">0.42</entry></row><row><entry namest="col2" nameend="col2" align="left">H</entry><entry namest="col3" nameend="col3" align="left">h</entry><entry namest="col4" nameend="col4" align="left">TiCl₄: 2</entry><entry namest="col5" nameend="col5" align="center">350</entry><entry namest="col6" nameend="col6" align="center">950</entry><entry namest="col7" nameend="col7" align="center">10</entry><entry namest="col8" nameend="col8" align="char" char=".">1.04</entry></row><row><entry namest="col2" nameend="col2" align="left">I</entry><entry namest="col3" nameend="col3" align="left">i</entry><entry namest="col4" nameend="col4" align="left">CO₂: 10</entry><entry namest="col5" nameend="col5" align="center">400</entry><entry namest="col6" nameend="col6" align="center">1000</entry><entry namest="col7" nameend="col7" align="center">15</entry><entry namest="col8" nameend="col8" align="char" char=".">1.53</entry></row><row><entry namest="col2" nameend="col2" align="left">J</entry><entry namest="col3" nameend="col3" align="left">j</entry><entry namest="col4" nameend="col4" align="left">TiCl₄: 3</entry><entry namest="col5" nameend="col5" align="center">450</entry><entry namest="col6" nameend="col6" align="center">900</entry><entry namest="col7" nameend="col7" align="center">13</entry><entry namest="col8" nameend="col8" align="char" char=".">1.31</entry></row><row><entry namest="col2" nameend="col2" align="left">K</entry><entry namest="col3" nameend="col3" align="left">k</entry><entry namest="col4" nameend="col4" align="left">TiCl₄: 3</entry><entry namest="col5" nameend="col5" align="center">550</entry><entry namest="col6" nameend="col6" align="center">1000</entry><entry namest="col7" nameend="col7" align="center">15</entry><entry namest="col8" nameend="col8" align="char" char=".">1.94</entry></row><row><entry namest="col2" nameend="col2" align="left">L</entry><entry namest="col3" nameend="col3" align="left">l</entry><entry namest="col4" nameend="col4" align="left">CO₂: 9</entry><entry namest="col5" nameend="col5" align="center">500</entry><entry namest="col6" nameend="col6" align="center">950</entry><entry namest="col7" nameend="col7" align="center">10</entry><entry namest="col8" nameend="col8" align="char" char=".">0.87</entry></row><row><entry namest="col2" nameend="col2" align="left">M</entry><entry namest="col3" nameend="col3" align="left">m</entry><entry namest="col4" nameend="col4" align="left">TiCl₄: 2</entry><entry namest="col5" nameend="col5" align="center">350</entry><entry namest="col6" nameend="col6" align="center">950</entry><entry namest="col7" nameend="col7" align="center">6</entry><entry namest="col8" nameend="col8" align="char" char=".">0.45</entry></row><row><entry namest="col2" nameend="col2" align="left">N</entry><entry namest="col3" nameend="col3" align="left">n</entry><entry namest="col4" nameend="col4" align="left">CO₂: 10</entry><entry namest="col5" nameend="col5" align="center">400</entry><entry namest="col6" nameend="col6" align="center">920</entry><entry namest="col7" nameend="col7" align="center">8</entry><entry namest="col8" nameend="col8" align="char" char=".">0.51</entry></row><row><entry namest="col2" nameend="col2" align="left">O</entry><entry namest="col3" nameend="col3" align="left">o</entry><entry namest="col4" nameend="col4" align="left">CO₂: 11</entry><entry namest="col5" nameend="col5" align="center">200</entry><entry namest="col6" nameend="col6" align="center">900</entry><entry namest="col7" nameend="col7" align="center">4</entry><entry namest="col8" nameend="col8" align="char" char=".">0.34</entry></row><row><entry namest="col2" nameend="col2" align="left">P</entry><entry namest="col3" nameend="col3" align="left">p</entry><entry namest="col4" nameend="col4" align="left">CO₂: 9</entry><entry namest="col5" nameend="col5" align="center">50</entry><entry namest="col6" nameend="col6" align="center">900</entry><entry namest="col7" nameend="col7" align="center">2</entry><entry namest="col8" nameend="col8" align="char" char=".">0.11</entry></row><row><entry namest="col2" nameend="col2" align="left">Q</entry><entry namest="col3" nameend="col3" align="left">q</entry><entry namest="col4" nameend="col4" align="left">TiCl₄: 1</entry><entry namest="col5" nameend="col5" align="center">300</entry><entry namest="col6" nameend="col6" align="center">1000</entry><entry namest="col7" nameend="col7" align="center">3</entry><entry namest="col8" nameend="col8" align="char" char=".">0.80</entry></row><row><entry namest="col2" nameend="col2" align="left">R</entry><entry namest="col3" nameend="col3" align="left">r</entry><entry namest="col4" nameend="col4" align="left">TiCl₄: 1</entry><entry namest="col5" nameend="col5" align="center">150</entry><entry namest="col6" nameend="col6" align="center">950</entry><entry namest="col7" nameend="col7" align="center">7</entry><entry namest="col8" nameend="col8" align="char" char=".">0.23</entry></row><row rowsep="1"><entry namest="col2" nameend="col2" align="left">S</entry><entry namest="col3" nameend="col3" align="left">s</entry><entry namest="col4" nameend="col4" align="left">TiCl₄: 2</entry><entry namest="col5" nameend="col5" align="center">100</entry><entry namest="col6" nameend="col6" align="center">900</entry><entry namest="col7" nameend="col7" align="center">5</entry><entry namest="col8" nameend="col8" align="char" char=".">0.17</entry></row></tbody></tgroup></table></tables><tables id="tabl0016" num="0016"><table frame="all"><title>Table 16</title><tgroup cols="4" colsep="1" rowsep="1"><colspec colnum="1" colname="col1" colwidth="39.37mm" /><colspec colnum="2" colname="col2" colwidth="39.37mm" /><colspec colnum="3" colname="col3" colwidth="39.37mm" /><colspec colnum="4" colname="col4" colwidth="39.37mm" /><thead valign="top"><row><entry namest="col1" nameend="col1" rowsep="0" align="center">Type of hard-material-coated-layer</entry><entry namest="col2" nameend="col4" align="center">Hard-material-coated-layer forming conditions</entry></row><row><entry namest="col1" nameend="col1" rowsep="0" /><entry namest="col2" nameend="col2" rowsep="0" align="center">Composition of reaction gas (vol%)</entry><entry namest="col3" nameend="col4" align="center">Reaction atmosphere</entry></row><row><entry namest="col1" nameend="col1" /><entry namest="col2" nameend="col2" /><entry namest="col3" nameend="col3" align="center">Pressure (torr)</entry><entry namest="col4" nameend="col4" align="center">Temperature (°C)</entry></row></thead><tbody valign="top"><row><entry namest="col1" nameend="col1" align="left">Al₂O₃ *</entry><entry namest="col2" nameend="col2" align="left">Al₂Cl₃: 4, CO₂: 10, H₂S: 0.2, HCl: 2, H₂: balance</entry><entry namest="col3" nameend="col3" align="center">50</entry><entry namest="col4" nameend="col4" align="center">1020</entry></row><row><entry namest="col1" nameend="col1" align="left">Al₂O₃</entry><entry namest="col2" nameend="col2" align="left">Al[OCH(CH₃)₂]₃: 0.3, H₂: balance</entry><entry namest="col3" nameend="col3" align="center">50</entry><entry namest="col4" nameend="col4" align="center">900</entry></row><row><entry namest="col1" nameend="col1" align="left">TiC</entry><entry namest="col2" nameend="col2" align="left">TiCl₄: 2, C₃H₈: 5, H₂: balance</entry><entry namest="col3" nameend="col3" align="center">100</entry><entry namest="col4" nameend="col4" align="center">900</entry></row><row><entry namest="col1" nameend="col1" align="left">TiN</entry><entry namest="col2" nameend="col2" align="left">TiCl₄: 2, N₂: 30, H₂: balance</entry><entry namest="col3" nameend="col3" align="center">100</entry><entry namest="col4" nameend="col4" align="center">850</entry></row><row><entry namest="col1" nameend="col1" align="left">TiCN</entry><entry namest="col2" nameend="col2" align="left">TiCl₄: 2, N₂: 10, CH₃CN: 0.8, H₂: balance</entry><entry namest="col3" nameend="col3" align="center">70</entry><entry namest="col4" nameend="col4" align="center">900</entry></row><row><entry namest="col1" nameend="col1" align="left">TiCO</entry><entry namest="col2" nameend="col2" align="left">TiCl₄: 3, CO: 2, H₂: balance</entry><entry namest="col3" nameend="col3" align="center">100</entry><entry namest="col4" nameend="col4" align="center">900</entry></row><row><entry namest="col1" nameend="col1" align="left">TiNO</entry><entry namest="col2" nameend="col2" align="left">TiCl₄: 3, CO: 1, N₂: 15, H₂: balance</entry><entry namest="col3" nameend="col3" align="center">50</entry><entry namest="col4" nameend="col4" align="center">900</entry></row><row><entry namest="col1" nameend="col1" align="left">TiCNO</entry><entry namest="col2" nameend="col2" align="left">TiCl₄: 3, CO: 2, N₂: 15, H₂: balance</entry><entry namest="col3" nameend="col3" align="center">50</entry><entry namest="col4" nameend="col4" align="center">900</entry></row><row rowsep="1"><entry namest="col1" nameend="col4" align="justify">[In Table 16, item with * shows high temperature chemical vapor deposition (HT-CVD) and items without * show medium temperature chemical vapor deposition (MT-CVD).]</entry></row></tbody></tgroup></table></tables><tables id="tabl0017" num="0017"><img file="EP0900860A2_D0007.tif" /></tables><tables id="tabl0018" num="0018"><table frame="all"><title>Table 18</title><tgroup cols="5" colsep="1" rowsep="1"><colspec colnum="1" colname="col1" colwidth="31.50mm" /><colspec colnum="2" colname="col2" colwidth="31.50mm" /><colspec colnum="3" colname="col3" colwidth="31.50mm" /><colspec colnum="4" colname="col4" colwidth="31.50mm" /><colspec colnum="5" colname="col5" colwidth="31.50mm" /><thead valign="top"><row><entry namest="col1" nameend="col2" align="center">Type</entry><entry namest="col3" nameend="col3" align="center">Symbol of substrate</entry><entry namest="col4" nameend="col4" align="center">Hard-material-coated-layer</entry><entry namest="col5" nameend="col5" align="center">Result of cutting test</entry></row></thead><tbody valign="top"><row><entry namest="col1" nameend="col1" morerows="18" align="center">Comparative coated carbide endmill</entry><entry namest="col2" nameend="col2" align="center">1</entry><entry namest="col3" nameend="col3" align="left">a</entry><entry namest="col4" nameend="col4" align="center">similar to coated carbide endmill 1 of the present invention</entry><entry namest="col5" nameend="col5" align="left">life ended in 40 min</entry></row><row><entry namest="col2" nameend="col2" align="center">2</entry><entry namest="col3" nameend="col3" align="left">b</entry><entry namest="col4" nameend="col4" align="center">similar to coated carbide endmill 2 of the present invention</entry><entry namest="col5" nameend="col5" align="left">life ended in 40 min</entry></row><row><entry namest="col2" nameend="col2" align="center">3</entry><entry namest="col3" nameend="col3" align="left">c</entry><entry namest="col4" nameend="col4" align="center">similar to coated carbide endmill 3 of the present invention</entry><entry namest="col5" nameend="col5" align="left">life ended in 35 min</entry></row><row><entry namest="col2" nameend="col2" align="center">4</entry><entry namest="col3" nameend="col3" align="left">d</entry><entry namest="col4" nameend="col4" align="center">similar to coated carbide endmill 4 of the present invention</entry><entry namest="col5" nameend="col5" align="left">life ended in 45 min</entry></row><row><entry namest="col2" nameend="col2" align="center">5</entry><entry namest="col3" nameend="col3" align="left">e</entry><entry namest="col4" nameend="col4" align="center">similar to coated carbide endmill 5 of the present invention</entry><entry namest="col5" nameend="col5" align="left">life ended in 20 min</entry></row><row><entry namest="col2" nameend="col2" align="center">6</entry><entry namest="col3" nameend="col3" align="left">f</entry><entry namest="col4" nameend="col4" align="center">similar to coated carbide endmill 6 of the present invention</entry><entry namest="col5" nameend="col5" align="left">life ended in 45 min</entry></row><row><entry namest="col2" nameend="col2" align="center">7</entry><entry namest="col3" nameend="col3" align="left">g</entry><entry namest="col4" nameend="col4" align="center">similar to coated carbide endmill 7 of the present invention</entry><entry namest="col5" nameend="col5" align="left">life ended in 45 min</entry></row><row><entry namest="col2" nameend="col2" align="center">8</entry><entry namest="col3" nameend="col3" align="left">h</entry><entry namest="col4" nameend="col4" align="center">similar to coated carbide endmill 8 of the present invention</entry><entry namest="col5" nameend="col5" align="left">life ended in 20 min</entry></row><row><entry namest="col2" nameend="col2" align="center">9</entry><entry namest="col3" nameend="col3" align="left">i</entry><entry namest="col4" nameend="col4" align="center">similar to coated carbide endmill 9 of the present invention</entry><entry namest="col5" nameend="col5" align="left">life ended in 20 min</entry></row><row><entry namest="col2" nameend="col2" align="center">10</entry><entry namest="col3" nameend="col3" align="left">j</entry><entry namest="col4" nameend="col4" align="center">similar to coated carbide endmill 10 of the present invention</entry><entry namest="col5" nameend="col5" align="left">life ended in 25 min</entry></row><row><entry namest="col2" nameend="col2" align="center">11</entry><entry namest="col3" nameend="col3" align="left">k</entry><entry namest="col4" nameend="col4" align="center">similar to coated carbide endmill 11 of the present invention</entry><entry namest="col5" nameend="col5" align="left">life ended in 20 min</entry></row><row><entry namest="col2" nameend="col2" align="center">12</entry><entry namest="col3" nameend="col3" align="left">l</entry><entry namest="col4" nameend="col4" align="center">similar to coated carbide endmill 12 of the present invention</entry><entry namest="col5" nameend="col5" align="left">life ended in 30 min</entry></row><row><entry namest="col2" nameend="col2" align="center">13</entry><entry namest="col3" nameend="col3" align="left">m</entry><entry namest="col4" nameend="col4" align="center">similar to coated carbide endmill 13 of the present invention</entry><entry namest="col5" nameend="col5" align="left">life ended in 45 min</entry></row><row><entry namest="col2" nameend="col2" align="center">14</entry><entry namest="col3" nameend="col3" align="left">n</entry><entry namest="col4" nameend="col4" align="center">similar to coated carbide endmill 14 of the present invention</entry><entry namest="col5" nameend="col5" align="left">life ended in 45 min</entry></row><row><entry namest="col2" nameend="col2" align="center">15</entry><entry namest="col3" nameend="col3" align="left">o</entry><entry namest="col4" nameend="col4" align="center">similar to coated carbide endmill 15 of the present invention</entry><entry namest="col5" nameend="col5" align="left">life ended in 40 min</entry></row><row><entry namest="col2" nameend="col2" align="center">16</entry><entry namest="col3" nameend="col3" align="left">p</entry><entry namest="col4" nameend="col4" align="center">similar to coated carbide endmill 16 of the present invention</entry><entry namest="col5" nameend="col5" align="left">life ended in 30 min</entry></row><row><entry namest="col2" nameend="col2" align="center">17</entry><entry namest="col3" nameend="col3" align="left">q</entry><entry namest="col4" nameend="col4" align="center">similar to coated carbide endmill 17 of the present invention</entry><entry namest="col5" nameend="col5" align="left">life ended in 35 min</entry></row><row><entry namest="col2" nameend="col2" align="center">18</entry><entry namest="col3" nameend="col3" align="left">r</entry><entry namest="col4" nameend="col4" align="center">similar to coated carbide endmill 18 of the present invention</entry><entry namest="col5" nameend="col5" align="left">life ended in 45 min</entry></row><row rowsep="1"><entry namest="col2" nameend="col2" align="center">19</entry><entry namest="col3" nameend="col3" align="left">s</entry><entry namest="col4" nameend="col4" align="center">similar to coated carbide endmill 19 of the present invention</entry><entry namest="col5" nameend="col5" align="left">life ended in 40 min (life is ended by exfoliation of hard-material-coated-layer in any case)</entry></row></tbody></tgroup></table></tables>