Improved fluoropolymer fiber reinforced integral composite cable jacket and tubing

0001This invention relates to the field of reinforced cable jackets and tubing. More particularly, the present invention provides an improved elastomer and fluoropolymer fiber reinforced composite for use as cable jacket or tubing.

0002Cable jackets are often comprised of elastomeric materials that provide protection from corrosive chemical and/or high temperature environments. Despite these jackets exhibiting satisfactory flexibility in some applications, the handling of a jacketed cable imposes axial forces thereupon which cause elastomeric jackets to stretch or elongate over a cable core. Such axial forces are particularly problematic in low modulus homogeneous elastomeric jacket materials.

0003Conventional elastomeric jackets generally do not uniformly return to a relaxed state, from an elongated state, because the jacket sticks to the cable core. This causes localized regions where the jacket wall thickness is reduced. Typically, these localized regions are sites of mechanical failure. Additionally, jacket wall thickness reduction during normal cable use degrades cut-through resistance of the jacket.

0004A need exists for a cable that does not allow significant jacket wall thickness reduction during handling. Such a cable would be particularly useful in phaco emulsification surgery, autoclave sterilizable devices, interventional magnetic resonance imaging devices which require a non-metal reinforcement, high flex robotic applications, and pharmaceutical and food processing, particularly when biotoxicity is of concern. Additionally, this cable would not introduce the electrical and/or health hazards associated with broken ends of fatigued metallic wire penetrating to either the inside or outside of the cable.

0005The foregoing illustrates limitations known to exist in present cable jackets and tubing. Thus, it is apparent that it would be advantageous to provide an improved cable jacket and tubing directed to overcoming one of more of the limitations set forth above. Accordingly, a suitable alternative is provided including features more fully disclosed hereinafter.

0006Accordingly, it is a primary purpose of the present invention to provide an improved cable jacket to reduce cable strain without significantly increasing cable bending stiffness.

0007It is another purpose of the present invention to provide an improved cable jacket having a fiber array disposed within an elastomer layer to prevent jacket wall thickness reduction during handling of the cable.

0008It is yet another purpose of the present invention to provide an improved cable jacket having a fiber array that is resistant to chemicals and heat which are employed in sterilization procedures.

0009Yet another purpose of the present invention is to provide an improved cable jacket or tubing which is resistant to temperatures in excess of 204,4°C (400°F), chemical attack, and water absorption.

0010According to the present invention there is provided a composite tubing comprising: <ul id="ul0001" list-style="none" compact="compact"><li>a first tubular shaped elastomer material;</li><li>a fiber array disposed about said first tubular shaped elastomer material, wherein the fiber array is defined by at least two fluoropolymer fibers, and wherein the fiber array defines predetermined open regions; and</li><li>a second tubular shaped elastomer material disposed about the fiber array, wherein the first and second tubular shaped elastomer materials are bonded together at the predetermined open regions to form an integral composite tube.</li></ul>

0011According to a further aspect of the present invention there is provided a signal cable assembly having a signal transmission core with a longitudinal central axis; and a jacket surrounding said core, said jacket comprising a composite tubing comprising: <ul id="ul0002" list-style="none" compact="compact"><li>a first tubular shaped elastomer material;</li><li>a fiber array disposed about said first tubular shaped elastomer material, wherein the fiber array is defined by at least two fluoropolymer fibers, and wherein the fiber array defines predetermined open regions; and</li><li>a second tubular shaped elastomer material disposed about the fiber array, wherein the first and second tubular shaped elastomer materials are bonded together at the predetermined open regions to form an integral composite tube.</li></ul>

0012Preferably, the first and second elastomer materials are formed of silicone and the fiber array is formed from individual high modulous fibers comprised at least in part of polytetrafluoroethylene. The fiber array may comprise a plurality of configurations, such as but not limited to a braided configuration or served configuration, for example.

0013Embodiments of the present invention will now be described by way of example, with reference to the accompanying drawings in which:- <ul id="ul0003" list-style="none" compact="compact"><li>Figure 1 is a partial perspective view of one embodiment of an improved fluoropolymer fiber reinforced composite cable jacket of the present invention, wherein a fluoropolymer fiber array is disposed in a braided configuration which forms equiangular open portions in the array;</li><li>Figure 2 is a partial perspective view of an alternative embodiment of the present invention, wherein the fiber array is braided in two directions at unequal angles to a centerline of the cable;</li><li>Figure 3 is a partial perspective view of an alternative embodiment of the present invention, wherein the fiber array is arranged in a helical served configuration over longitudinally disposed fibers; and</li><li>Figure 4 is a diagram illustrating typical mechanical forces which may be exerted upon a cable jacket during use.</li></ul>

0014Referring to the drawings, wherein similar reference characters designate corresponding parts throughout several views, the improved cable jacket of the present invention is generally illustrated at 10 in Figures 1-3. The improved cable jacket 10 includes a signal transmission core 12, a first inner elastomer jacket layer 16, individual fluoropolymer fibers 14 which form a fiber array 18, and a second outer elastomer jacket layer 20. As the term is used herein, "fiber" is intended to mean any strand of a fluoropolymer material whether a single thread, or multiple threads, braided, twisted or otherwise. In a preferred embodiment of the present invention, the fluoropolymer fibers are comprised of tetrafluoroethylene (TFE) based polymers of various degrees of density and porosity such as porous polytetrafluoroethylene (PTFE), for example. They may be sized, treated, coated, or imbibed with agents to augment processing and/or adhesion. For example, the fibers may be etched with a suitable etchant, which may be obtained from W. L. Gore &amp; Associates, Inc., under the tradename TETRA-ETCH®, to improve adhesion between the fluoropolymers 14 and the first and second elastomer jacket layers 16 and 20, respectively.

0015The bending stiffness of the cable or tubing is not significantly altered by the presence of the fluoropolymer fiber. The fluoropolymer fibe is highly anisotropic and sustains tensile loads, but not compressive loads. Under compressive loads, the fiber collapses on itself without increasing cross-sectional area. As the cable bends, the fibers in tension do not undergo significant elongation; the neutral axis shifts towards the region of the cable cross-section in tension.

0016As the term is used herein, "porous polytetrafluoroethylene" (PTFE) shall mean PTFE which may be prepared by any number of known processes, for example, by stretching or drawing processes, by papermaking processes, by processes in which filler materials are incorporated with the PTFE resin and which are subsequently removed to leave a porous structure, or by powder sintering processes. Preferably, the porous polytetrafluoroethylene is porous expanded polytetrafluoroethylene having a microstructure of interconnected nodes and fibrils, as described in U.S. Patent Nos. 3,953,566; 4,187,390; and 4,110,392, and which fully describe the preterred material and processes for making them. The porous polytetrafluoroethylene may have a thickness in a range from about 3 to about 1,000 micrometers, preferably in a range of from about 5 to about 100 micrometers, and a pore volume in a range from about 20 to about 98 percent.

0017The signal transmission core 12 may be comprised of any suitable elements useful in the transmission of electromagnetic and/or optical signals and/or power. For example, the signal transmission core 12 may be comprised of electrical conductor elements, flexible tubular conduit or fiber optic elements for transmitting data and/or providing power to a system (not shown) and interstitial fillers for providing radial compressive support. The signal transmission core 12 may also be wrapped or covered with a layer of porous polytetrafluoroethylene.

0018The signal transmission core 12 is jacketed or coated with the first elastomeric jacket layer 16, which may be comprised of any suitable material such as silicones, fluorosilicones, fluororubbers, polyurethane, hydronated nitrite rubber or ethylene propylene diene monomer (EPDM), for example. The first elastomeric jacket layer 16 may be applied by any suitable process, such as by a conventional extrusion process, for example.

0019A preferred fiber 14 is a fluoropolymer fiber comprised of polytetrafluoroethylene. One example of such a fiber has the following characteristics: a round or flat TFE based polymer, having both a porous and a non-porous surface, with an average diameter of .003", a denier of 200, a tenacity >3, and a high service temperature of >260°C.

0020The fibers 14 are disposed about the first jacket 16 in a predetermined orientation to form the array 18. As best illustrated in Figure 1, in one embodiment, the fibers 14 are disposed in a braided configuration such that equiangular open portions are defined in the array. By contrast, Figure 2 displays a fiber array 18 wherein at least some of the fibers 14 are disposed substantially parallel to a longitudinal centerline of the cable core 12 with other fibers 14 being interwoven therewith. Figure 3 illustrates a fiber array 18 having a plurality of helically served fibers which are disposed about a plurality of fibers 14 disposed substantially parallel to the longitudinal centerline of the cable core 12. Each fiber array 18, illustrated in Figures 1-3, define open spaces 22 that permit the first inner elastomer jacket layer 16 to bond with the second outer elastomer jacket layer 20.

0021In a preferred embodiment, the second outer elastomer jacket layer 20 may be comprised of any suitable material such as silicones, fluorosilicones, fluororubbers, polyurethane, hydronated nitrite rubber or EPDM, for example.

0022The cable jacket of the present invention may be formed by first extruding and curing the first inner elastomer jacket layer 16 over the cable core 12. The fluoropolymer fiber 14 is then arranged about the first inner jacket layer 16. The second outer elastomer jacket layer 20 is then extruded over the fiber array 18 and cured. During this extrusion process, the material of the second elastomer jacket layer 20 flows through the open portions 22 to contact and bond with the first inner jacket 16. The first and second jackets 16, 20 fuse or bond together to form a homogeneous structure having the fiber array 18 disposed therein.

0023Tubing may also be formed in accordance with the teachings of the present invention by first extruding a first tubular shaped elastomer material over a removable circular core or mandrel. Then the first tubular shaped elastomer is cured or vulcanized. The application of a fiber array and the application of a second tubular shaped elastomer material is the same as described hereinabove. The method just described may also be conducted without a removable core or mandrel, such as by applying air pressure to the inner diameter of the tube during each process step. The above-outlined process steps can be done as individual processes, or as a co-extrusion wherein all steps are performed in line or in a continuous process in which the final tubular article is cured in one step. Compression molding techniques may also be used.

0024Without intending to limit the scope of the present invention, the apparatus and method of production of the present invention may be better understood by referring to the following examples:

Example 1

0025A cable having a fluoropolyer fiber reinforced integral composite cable jacket was manufactured using the following steps and materials. Electrical wires were twisted together or cabled to form a core. The twisted wires were then helically wrapped, covering them completely, with a 50 µm (0.002 inch) thick tape of porous PTFE to an outer diameter of 0,19 cm (0.076 inches). A primary silicone jacket (Dow Corning Q7-4750) was extruded, at a thickness of 0,25 mm (0.010 inches), over the core and cured at 148,9°C (300°F). A braid was arrayed over the core using 16 ends of a 200 denier high strength porous expanded PTFE fiber. This was done using a braid angle of 20° and a tension of approximately 85,04 g (3 ounces) per fiber. A final 0.027 inch thick silicone jacket (Dow Corning Q7-4750) was extruded over the braided core, and then cured at 148,9°C (300°F).

Example 2

0026A tube may be made using the same methods described in Example 1, except the core is substituted by a mandrel of a suitable size. Upon completion of the final extrusion, the mandrel is removed from the core leaving a tube.

0027Various tests were performed to determine the material properties (tensile strength, elongation, modulus_100%, flex and cut-through capacity) of a cable, manufactured in accordance with the techniques herein, after exposure to increasing numbers of autoclave cycles. Also, capacitance was monitored to determine if any shift occurred as a result of the autoclave cycling Approximately 15,2 m (50 feet) of cable was placed into an autoclave at 135°C (275°F). At predetermined cycle counts, a test specimen was removed and the following tests were performed.

0028The test data is presented in Table 2 and Table 3. The tensile and elongation data is divided into two data points, namely, the peak break point tensile strength and elongation for the porous PTFE re-enforcement fiber and the silicone peak break point tensile strength and elongation. The modulus_100% is of the silicone material. Cut-through is in pounds force (lbf) and is a relative reading. Taber stiffness is in gm-cm and also is a relative reading. The capacitance was recorded in ρF/1,83 m (ρF/72 inches).

Autoclave Tests

0029Autoclave testing was accomplished cyclically as provided in Table 1. Test samples were placed in the autoclave and exposed to temperatures between 132,2 - 134,4°C (270-274°F) and pressures between 2,07-2,62 bar (30-38 psi) for time periods of 5 minutes.

Tensile and Elongation and Modulus

100%

Tests

0030Tensile strength, elongation and modulus_100% were determined using a method which follows ASTM D412 (reference straight specimen, Section 11.2) with bench marks for elongation determination. The modulus_100% was chosen as a convenient reference. Test specimens were taken from the autoclave at predetermined cycle counts, as shown in Table 1 and tested. An Instron 4201 Universal Tester, Part No. 10-00030 was employed using the following setup parameters: 1) Crosshead speed 12,7 cm/min (5 in./min); 2) Chart speed, 1 in./min; 3) Chart Range 0 - 222,4 N (0 to 50 lbf); and 4) Embossed steel grips were used.

Flex Tests

0031Test specimens of the complete cable were taken from the autoclave at predetermined cycle counts, as shown in Table 1, and flexed in a variety of motions to 100,000 cycles. The test specimens were electrically monitored for center conductor failures. After the flexing, tensile and elongation and modulus_100% tests were performed on the re-enforced silicone jacket, with the core removed, to evaluate any change of the material properties in the flexed area.

Cut-Through Tests

0032Test specimens were taken from the autoclave at predetermined cycle counts, as shown in Table 1, and cut-through tests were performed on the re-enforced silicone jacket with the core removed to evaluate any change of the material properties as a result of the autoclave cycles.

Taber Stiffness Tests

0033Test specimens were taken from the autoclave at predetermined cycle counts, as shown in Table 1, and taber stiffness tests were performed on the complete cable to evaluate any change of the material properties as a result of the autoclave cycles.

Capacitance Tests

0034Test specimens were taken from the autoclave at predetermined cycle counts, as shown in Table 1, and capacitance tests were performed to evaluate any change of the electrical properties as a result of the autoclave cycles. Initial data points were 0 and 200 cycles, but the decision was made to continue data collection to the completion of the autoclave cycle. <tables id="tabl0001" num="0001"><table frame="all"><title>Table 1</title><tgroup cols="6" colsep="1" rowsep="1"><colspec colnum="1" colname="col1" colwidth="26.25mm" /><colspec colnum="2" colname="col2" colwidth="26.25mm" /><colspec colnum="3" colname="col3" colwidth="26.25mm" /><colspec colnum="4" colname="col4" colwidth="26.25mm" /><colspec colnum="5" colname="col5" colwidth="26.25mm" /><colspec colnum="6" colname="col6" colwidth="26.25mm" /><tbody valign="top"><row><entry namest="col1" nameend="col1" /></row></tbody></tgroup><tgroup cols="6" colsep="1" rowsep="1"><colspec colnum="1" colname="col1" colwidth="26.25mm" /><colspec colnum="2" colname="col2" colwidth="26.25mm" /><colspec colnum="3" colname="col3" colwidth="26.25mm" /><colspec colnum="4" colname="col4" colwidth="26.25mm" /><colspec colnum="5" colname="col5" colwidth="26.25mm" /><colspec colnum="6" colname="col6" colwidth="26.25mm" /><thead valign="top"><row><entry namest="col1" nameend="col1" align="center">Autoclave Cycles</entry><entry namest="col2" nameend="col2" align="center">Tensile and Elongation</entry><entry namest="col3" nameend="col3" align="center">Flex to 100,000 Cycles</entry><entry namest="col4" nameend="col4" align="center">Cut-</entry><entry namest="col5" nameend="col5" align="center">Taber Stiffness</entry><entry namest="col6" nameend="col6" align="center">Capacitance</entry></row></thead><tbody valign="top"><row><entry namest="col1" nameend="col1" align="center">0</entry><entry namest="col2" nameend="col2" align="center">X</entry><entry namest="col3" nameend="col3" align="center">X</entry><entry namest="col4" nameend="col4" align="center">X</entry><entry namest="col5" nameend="col5" align="center">X</entry><entry namest="col6" nameend="col6" align="center">X</entry></row><row><entry namest="col1" nameend="col1" align="center">100</entry><entry namest="col2" nameend="col2" align="center">X</entry><entry namest="col3" nameend="col3" align="center">X</entry><entry namest="col4" nameend="col4" align="center">X</entry><entry namest="col5" nameend="col5" align="center">X</entry><entry namest="col6" nameend="col6" /></row><row><entry namest="col1" nameend="col1" align="center">500</entry><entry namest="col2" nameend="col2" align="center">X</entry><entry namest="col3" nameend="col3" /><entry namest="col4" nameend="col4" /><entry namest="col5" nameend="col5" /><entry namest="col6" nameend="col6" align="center">X (200)</entry></row><row><entry namest="col1" nameend="col1" align="center">750</entry><entry namest="col2" nameend="col2" align="center">X</entry><entry namest="col3" nameend="col3" /><entry namest="col4" nameend="col4" /><entry namest="col5" nameend="col5" align="center">X</entry><entry namest="col6" nameend="col6" /></row><row><entry namest="col1" nameend="col1" align="center">1000</entry><entry namest="col2" nameend="col2" align="center">X</entry><entry namest="col3" nameend="col3" align="center">X</entry><entry namest="col4" nameend="col4" /><entry namest="col5" nameend="col5" /><entry namest="col6" nameend="col6" align="center">X</entry></row><row rowsep="1"><entry namest="col1" nameend="col1" align="center">1500</entry><entry namest="col2" nameend="col2" align="center">X</entry><entry namest="col3" nameend="col3" align="center">X</entry><entry namest="col4" nameend="col4" align="center">X</entry><entry namest="col5" nameend="col5" align="center">X</entry><entry namest="col6" nameend="col6" align="center">X</entry></row></tbody></tgroup></table></tables><tables id="tabl0002" num="0002"><table frame="all"><title>Table 2</title><tgroup cols="11" colsep="1" rowsep="1"><colspec colnum="1" colname="col1" colwidth="14.31mm" /><colspec colnum="2" colname="col2" colwidth="14.31mm" /><colspec colnum="3" colname="col3" colwidth="14.31mm" /><colspec colnum="4" colname="col4" colwidth="14.31mm" /><colspec colnum="5" colname="col5" colwidth="14.31mm" /><colspec colnum="6" colname="col6" colwidth="14.31mm" /><colspec colnum="7" colname="col7" colwidth="14.31mm" /><colspec colnum="8" colname="col8" colwidth="14.31mm" /><colspec colnum="9" colname="col9" colwidth="14.31mm" /><colspec colnum="10" colname="col10" colwidth="14.31mm" /><colspec colnum="11" colname="col11" colwidth="14.31mm" /><thead valign="top"><row><entry namest="col1" nameend="col11" align="center">Tensile Strength and Elongation (psi &amp; %)</entry></row><row><entry namest="col1" nameend="col1" /><entry namest="col2" nameend="col6" align="center">Non-Flexed</entry><entry namest="col7" nameend="col11" align="center">Flexed</entry></row><row><entry namest="col1" nameend="col1" rowsep="0" align="center">Autoclave Cycle Count</entry><entry namest="col2" nameend="col3" align="center">Fiber Reinforced Silicone</entry><entry namest="col4" nameend="col6" align="center">Silicone</entry><entry namest="col7" nameend="col8" align="center">Fiber Reinforced Silicone</entry><entry namest="col9" nameend="col11" align="center">Silicone</entry></row><row><entry namest="col1" nameend="col1" /><entry namest="col2" nameend="col2" align="center">Tensile Strength (psi)</entry><entry namest="col3" nameend="col3" align="center">El. (%)</entry><entry namest="col4" nameend="col4" align="center">Tensile Strength (psi)</entry><entry namest="col5" nameend="col5" align="center">El. (%)</entry><entry namest="col6" nameend="col6" align="center">Modulus_100% (psi)</entry><entry namest="col7" nameend="col7" align="center">Tensile Strength (psi)</entry><entry namest="col8" nameend="col8" align="center">El.(psi)</entry><entry namest="col9" nameend="col9" align="center">Tensile Strength (psi)</entry><entry namest="col10" nameend="col10" align="center">El. (%)</entry><entry namest="col11" nameend="col11" align="center">Modulus_100% (psi)</entry></row></thead><tbody valign="top"><row><entry namest="col1" nameend="col1" align="center">0*</entry><entry namest="col2" nameend="col2" align="center">N/A</entry><entry namest="col3" nameend="col3" align="center">N/A</entry><entry namest="col4" nameend="col4" align="center">1118.2</entry><entry namest="col5" nameend="col5" align="center">914</entry><entry namest="col6" nameend="col6" align="center">218.0</entry><entry namest="col7" nameend="col7" align="center">N/A</entry><entry namest="col8" nameend="col8" align="center">N/A</entry><entry namest="col9" nameend="col9" align="center">N/A</entry><entry namest="col10" nameend="col10" align="center">N/A</entry><entry namest="col11" nameend="col11" align="center">N/A</entry></row><row><entry namest="col1" nameend="col1" align="center">0</entry><entry namest="col2" nameend="col2" align="center">2504.0</entry><entry namest="col3" nameend="col3" align="center">50</entry><entry namest="col4" nameend="col4" align="center">1004.0</entry><entry namest="col5" nameend="col5" align="center">687</entry><entry namest="col6" nameend="col6" align="center">222.1</entry><entry namest="col7" nameend="col7" align="center">1894.4</entry><entry namest="col8" nameend="col8" align="center">39</entry><entry namest="col9" nameend="col9" align="center">1070.9</entry><entry namest="col10" nameend="col10" align="center">709</entry><entry namest="col11" nameend="col11" align="center">232.5</entry></row><row><entry namest="col1" nameend="col1" align="center">100</entry><entry namest="col2" nameend="col2" align="center">2401.9</entry><entry namest="col3" nameend="col3" align="center">47</entry><entry namest="col4" nameend="col4" align="center">973.1</entry><entry namest="col5" nameend="col5" align="center">641</entry><entry namest="col6" nameend="col6" align="center">212.2</entry><entry namest="col7" nameend="col7" align="center">1693.4</entry><entry namest="col8" nameend="col8" align="center">35</entry><entry namest="col9" nameend="col9" align="center">1137.9</entry><entry namest="col10" nameend="col10" align="center">650</entry><entry namest="col11" nameend="col11" align="center">293.8</entry></row><row><entry namest="col1" nameend="col1" align="center">500</entry><entry namest="col2" nameend="col2" align="center">2543.5</entry><entry namest="col3" nameend="col3" align="center">49</entry><entry namest="col4" nameend="col4" align="center">1078.9</entry><entry namest="col5" nameend="col5" align="center">634</entry><entry namest="col6" nameend="col6" align="center">317.8</entry><entry namest="col7" nameend="col7" align="center">N/A</entry><entry namest="col8" nameend="col8" align="center">N/A</entry><entry namest="col9" nameend="col9" align="center">N/A</entry><entry namest="col10" nameend="col10" align="center">N/A</entry><entry namest="col11" nameend="col11" align="center">N/A</entry></row><row><entry namest="col1" nameend="col1" align="center">750</entry><entry namest="col2" nameend="col2" align="center">2480.5</entry><entry namest="col3" nameend="col3" align="center">48</entry><entry namest="col4" nameend="col4" align="center">1037.8</entry><entry namest="col5" nameend="col5" align="center">648</entry><entry namest="col6" nameend="col6" align="center">294.7</entry><entry namest="col7" nameend="col7" align="center">1935.3</entry><entry namest="col8" nameend="col8" align="center">36</entry><entry namest="col9" nameend="col9" align="center">1167.6</entry><entry namest="col10" nameend="col10" align="center">663</entry><entry namest="col11" nameend="col11" align="center">320.2</entry></row><row><entry namest="col1" nameend="col1" align="center">1000</entry><entry namest="col2" nameend="col2" align="center">2491.9</entry><entry namest="col3" nameend="col3" align="center">47</entry><entry namest="col4" nameend="col4" align="center">998.3</entry><entry namest="col5" nameend="col5" align="center">637</entry><entry namest="col6" nameend="col6" align="center">291.4</entry><entry namest="col7" nameend="col7" align="center">N/A</entry><entry namest="col8" nameend="col8" align="center">N/A</entry><entry namest="col9" nameend="col9" align="center">N/A</entry><entry namest="col10" nameend="col10" align="center">N/A</entry><entry namest="col11" nameend="col11" align="center">N/A</entry></row><row rowsep="1"><entry namest="col1" nameend="col1" align="center">1500</entry><entry namest="col2" nameend="col2" align="center">2549.1</entry><entry namest="col3" nameend="col3" align="center">49</entry><entry namest="col4" nameend="col4" align="center">893.5</entry><entry namest="col5" nameend="col5" align="center">629</entry><entry namest="col6" nameend="col6" align="center">199.9</entry><entry namest="col7" nameend="col7" align="center">1984.8</entry><entry namest="col8" nameend="col8" align="center">36</entry><entry namest="col9" nameend="col9" align="center">913.0</entry><entry namest="col10" nameend="col10" align="center">643</entry><entry namest="col11" nameend="col11" align="center">226.0</entry></row></tbody></tgroup><tgroup cols="11" colsep="0" rowsep="0"><colspec colnum="1" colname="col1" colwidth="14.31mm" /><colspec colnum="2" colname="col2" colwidth="14.31mm" /><colspec colnum="3" colname="col3" colwidth="14.31mm" /><colspec colnum="4" colname="col4" colwidth="14.31mm" /><colspec colnum="5" colname="col5" colwidth="14.31mm" /><colspec colnum="6" colname="col6" colwidth="14.31mm" /><colspec colnum="7" colname="col7" colwidth="14.31mm" /><colspec colnum="8" colname="col8" colwidth="14.31mm" /><colspec colnum="9" colname="col9" colwidth="14.31mm" /><colspec colnum="10" colname="col10" colwidth="14.31mm" /><colspec colnum="11" colname="col11" colwidth="14.31mm" /><tbody valign="top"><row><entry namest="col1" nameend="col11" align="justify">* Homogeneous silicone without fiber reinforcement. ** All silicone is Dow Corning type Q74750. 1 psi corresponds to 0,069 bar</entry></row></tbody></tgroup></table></tables><tables id="tabl0003" num="0003"><table frame="all"><title>Table 3</title><tgroup cols="8" colsep="1" rowsep="1"><colspec colnum="1" colname="col1" colwidth="19.68mm" /><colspec colnum="2" colname="col2" colwidth="19.68mm" /><colspec colnum="3" colname="col3" colwidth="19.68mm" /><colspec colnum="4" colname="col4" colwidth="19.68mm" /><colspec colnum="5" colname="col5" colwidth="19.68mm" /><colspec colnum="6" colname="col6" colwidth="19.68mm" /><colspec colnum="7" colname="col7" colwidth="19.68mm" /><colspec colnum="8" colname="col8" colwidth="19.68mm" /><thead valign="top"><row><entry namest="col1" nameend="col1" rowsep="0" align="center">Autoclave Cycle count</entry><entry namest="col2" nameend="col3" align="center">Cut-Through</entry><entry namest="col4" nameend="col5" align="center">Taber Stiffness</entry><entry namest="col6" nameend="col8" align="center">Capacitance</entry></row><row><entry namest="col1" nameend="col1" /><entry namest="col2" nameend="col2" align="center">Average (lbf)</entry><entry namest="col3" nameend="col3" align="center">Std Dev (lbf)</entry><entry namest="col4" nameend="col4" align="center">Resilience (%)</entry><entry namest="col5" nameend="col5" align="center">Initial Stiffness (gm-cm)</entry><entry namest="col6" nameend="col6" align="center">Red/Drains (ρF/72 in.)</entry><entry namest="col7" nameend="col7" align="center">Red/Brown (ρF/72 in.)</entry><entry namest="col8" nameend="col8" align="center">Red/Blue (ρF/72 in.)</entry></row></thead><tbody valign="top"><row><entry namest="col1" nameend="col1" align="center">0*</entry><entry namest="col2" nameend="col2" align="center">24.5</entry><entry namest="col3" nameend="col3" align="center">1.16</entry><entry namest="col4" nameend="col4" align="center">N/A</entry><entry namest="col5" nameend="col5" align="center">34</entry><entry namest="col6" nameend="col6" align="center">220.5</entry><entry namest="col7" nameend="col7" align="center">89.1</entry><entry namest="col8" nameend="col8" align="center">89.1</entry></row><row><entry namest="col1" nameend="col1" align="center">0</entry><entry namest="col2" nameend="col2" align="center">32.32</entry><entry namest="col3" nameend="col3" align="center">2.83</entry><entry namest="col4" nameend="col4" align="center">65.6</entry><entry namest="col5" nameend="col5" align="center">41.2</entry><entry namest="col6" nameend="col6" align="center">221.3</entry><entry namest="col7" nameend="col7" align="center">89.22</entry><entry namest="col8" nameend="col8" align="center">86.57</entry></row><row><entry namest="col1" nameend="col1" align="center">100</entry><entry namest="col2" nameend="col2" align="center">32.24</entry><entry namest="col3" nameend="col3" align="center">1.39</entry><entry namest="col4" nameend="col4" align="center">63.1</entry><entry namest="col5" nameend="col5" align="center">48.1</entry><entry namest="col6" nameend="col6" align="center">N/A</entry><entry namest="col7" nameend="col7" align="center">N/A</entry><entry namest="col8" nameend="col8" align="center">N/A</entry></row><row><entry namest="col1" nameend="col1" align="center">200</entry><entry namest="col2" nameend="col2" align="center">N/A</entry><entry namest="col3" nameend="col3" align="center">N/A</entry><entry namest="col4" nameend="col4" align="center">N/A</entry><entry namest="col5" nameend="col5" align="center">N/A</entry><entry namest="col6" nameend="col6" align="center">229.35</entry><entry namest="col7" nameend="col7" align="center">91.5</entry><entry namest="col8" nameend="col8" align="center">89.25</entry></row><row><entry namest="col1" nameend="col1" align="center">500</entry><entry namest="col2" nameend="col2" align="center">N/A</entry><entry namest="col3" nameend="col3" align="center">N/A</entry><entry namest="col4" nameend="col4" align="center">N/A</entry><entry namest="col5" nameend="col5" align="center">N/A</entry><entry namest="col6" nameend="col6" align="center">N/A</entry><entry namest="col7" nameend="col7" align="center">N/A</entry><entry namest="col8" nameend="col8" align="center">N/A</entry></row><row><entry namest="col1" nameend="col1" align="center">750</entry><entry namest="col2" nameend="col2" align="center">N/A</entry><entry namest="col3" nameend="col3" align="center">N/A</entry><entry namest="col4" nameend="col4" align="center">64.8</entry><entry namest="col5" nameend="col5" align="center">61.3</entry><entry namest="col6" nameend="col6" align="center">N/A</entry><entry namest="col7" nameend="col7" align="center">N/A</entry><entry namest="col8" nameend="col8" align="center">N/A</entry></row><row><entry namest="col1" nameend="col1" align="center">1000</entry><entry namest="col2" nameend="col2" align="center">N/A</entry><entry namest="col3" nameend="col3" align="center">N/A</entry><entry namest="col4" nameend="col4" align="center">59.7</entry><entry namest="col5" nameend="col5" align="center">44.3</entry><entry namest="col6" nameend="col6" align="center">226.08</entry><entry namest="col7" nameend="col7" align="center">89.45</entry><entry namest="col8" nameend="col8" align="center">89.51</entry></row><row rowsep="1"><entry namest="col1" nameend="col1" align="center">1500</entry><entry namest="col2" nameend="col2" align="center">30.17</entry><entry namest="col3" nameend="col3" align="center">4.89</entry><entry namest="col4" nameend="col4" align="center">68</entry><entry namest="col5" nameend="col5" align="center">58.3</entry><entry namest="col6" nameend="col6" align="center">225.8</entry><entry namest="col7" nameend="col7" align="center">88.16</entry><entry namest="col8" nameend="col8" align="center">88.18</entry></row></tbody></tgroup><tgroup cols="8" colsep="0" rowsep="0"><colspec colnum="1" colname="col1" colwidth="19.68mm" /><colspec colnum="2" colname="col2" colwidth="19.68mm" /><colspec colnum="3" colname="col3" colwidth="19.68mm" /><colspec colnum="4" colname="col4" colwidth="19.68mm" /><colspec colnum="5" colname="col5" colwidth="19.68mm" /><colspec colnum="6" colname="col6" colwidth="19.68mm" /><colspec colnum="7" colname="col7" colwidth="19.68mm" /><colspec colnum="8" colname="col8" colwidth="19.68mm" /><tbody valign="top"><row><entry namest="col1" nameend="col8" align="justify"><u>* Homogeneous silicone without fiber reinforcement.</u> 1 lbf corresponds to 4,45 N; 1ρF/72 in corresponds to 1 ρF/1,83m</entry></row></tbody></tgroup></table></tables>

0035Although a few exemplary embodiments of the present invention have been described in detail above, including exemplary jacket constructions and fiber array configurations, those skilled in the art readily appreciate that many modifications are possible without materially departing from the novel teachings and advantages which are described herein. Accordingly, all such modifications are intended to be included within the scope of the present invention, as defined by the following claims.