Thermal dye transfer sheet and method for thermal dye transfer recording

0001The present invention relates to a thermal transfer sheet used for a color hard copy by thermal transfer recording system, and particularly relates to a thermal dye transfer sheet used by thermal dye transfer recording system.

0002Recently, as a system for developing an image on a display such as CRT or the like as a hard copy, there is widely used a thermal dye transfer recording system which comprises heating a thermal dye transfer sheet with a thermal head, the heat generation of which can be controlled by an electric signal, transferring a dye only in a dye layer of the thermal dye transfer sheet and forming the transferred image on an image-receiving sheet. Generally, this system employs a thermal dye transfer sheet having a dye layer comprising a dye and a binder resin coated on a substrate. A full color image can be formed by overlapping a yellow image from a yellow dye layer, a magenta image from a magenta dye layer and a cyan image from a cyan dye layer.

0003Examples of a thermal transfer recording system include a melting dye transfer recording system which comprises melting a dye layer which contains a dye and a wax, on a substrate by heating and transferring the melted dye and wax to a dye-receiving material and a thermal dye transfer recording system which comprises transferring a dye only from a dye layer to an image-receiving material. The thermal dye transfer recording system is suitable for obtaining a full color print having a density gradation expression and also suitable for obtaining a precise image since it can control an amount of a dye to be transferred by controlling an amount of heat.

0004An important point of a thermal dye transfer recording system is to form an image having satisfactory color reproducibility, sensitivity, coloring density and fastness such as light-resistance. Thus, the thermal dye transfer sheet is demanded to achieve a faithful color reproducibility of an original image, to provide a sufficient color-developing property (high sensitivity) and a sufficient coloring density (high optical density) by a small heat energy, and to form an image having a satisfactory fastness, and also demanded to have a satisfactory shelf life.

0005However, a conventional thermal dye transfer sheet does not always satisfy all of these demanded properties.

0006The present invention has been made to solve the above-mentioned conventional problems. Thus, an object of the present invention is to provide a thermal dye transfer sheet, particularly excellent in thermal yellow color dye transfer recording, which forms an image having a faithful color reproducibility of an original image and also having a high fastness such as a high light-resistance, and which achieves a sufficient color-developing property (high color-developing sensitivity) and a sufficient coloring density by a small heat energy, and also which has satisfactory shelf life.

0007In order to solve the above-mentioned problem, the present invention provide a thermal dye transfer sheet having a dye layer comprising at least one dye and a binder resin provided on a substrate sheet, characterized in that the dye layer contains at least one pyrazolonemethine type dye of the following formula (1) <chemistry id="chem0001" num="0001"><img file="EP0802065A2_D0001.tif" /></chemistry> wherein R¹ and R² can be respectively independently selected and are a lower alkyl group which may be substituted, a lower alkenyl group which may be substituted or an aryl group which may be substituted; and    R³ and R⁴ can be respectively independently selected and are a lower alkyl group which may be substituted, a dialkylamino group, a -COOR⁵ group or a -CONR⁶R⁷ group, in which R⁵ is a lower alkyl group which may be substituted, a lower alkenyl group which may be substituted or an aryl group which may be substituted, and R⁶ and R⁷ can be respectively independently selected and are a hydrogen atom, a lower alkyl group which may be substituted, a lower alkenyl group which may be substituted or an aryl group which may be substituted.

0008Another object of the present invention is to provide a thermal dye transfer sheet, characterized by containing a pyrazolonemethine type dye of the formula (1) and a pyrazoloneazo type dye.

0009Other object of the present invention is to provide a thermal dye transfer sheet, characterized by containing a pyrazolonemethine type dye of the formula (1) and a quinophthalone type dye.

0010Still other object of the present invention is to provide a thermal dye transfer sheet, characterized in that a plurality of dye layers are provided on one side of a substrate and at least one of the dye layers contains the pyrazolonemethine type yellow dye and at least one other dye layer contains an indoaniline type cyan dye.

0011As a result of various studies and experiments, the present inventors have found that an image recording having a faithful color reproducibility of an original image, achieving a satisfactory coloring (high sensitivity) and a high coloring density by a low heat energy and having a satisfactory fastness, can be achieved by using a dye layer for thermal dye transfer recording, which contains at least one of (1) a pyrazolonemethine type dye having the above-mentioned specific chemical structure, (2) a mixture of a pyrazolonemethine type dye and a pyrazoloneazo type dye, and (3) a mixture of a pyrazolonemethine type dye and a quinophthalone type dye.

0012The thermal dye transfer sheet of the present invention comprises a substrate and a dye layer provided at least one side of the substrate. If necessary, the heat-resistant layer may be provided on the opposite side of the dye layer side of the substrate.

0013The substrate is selected in view of mechanical strength, easy handling or convenience for formation of a dye layer, examples of which include paper such as condenser paper, polyethylene terephthalate film, polyamide film, polyaramide film, polyimide film, polycarbonate film, polyphenylene sulfide film, polysulfone film, cellophane, triacetate film, polypropylene film, and the like. Among them, polyethylene terephthalate film is preferable in view of mechanical strength, size stability, heat-resistance, price and the like, a biaxially oriented polyethylene terephthalate film is particularly preferable. These substrates have a thickness of generally from 1 to 30 µm, preferably from 2 to 10 µm.

0014In order to improve adhesiveness of a dye layer to a substrate, the surface of a substrate may be subjected to corona-treatment, or may be provided with an anchor coat of polyester type resin, cellulose type resin, polyvinyl alcohol type resin, urethane resin, polyvinylidene chloride type resin or the like.

0015A dye contained in a dye layer is preferably at least one of (1) a pyrazolonemethine type dye of the formula (1) <chemistry id="chem0002" num="0002"><img file="EP0802065A2_D0002.tif" /></chemistry> wherein R¹ and R² can be respectively independently selected and are a lower alkyl group which may be substituted, a lower alkenyl group which may be substituted or an aryl group which may be substituted; and    R³ and R⁴ can be respectively independently selected and are a lower alkyl group which may be substituted, a dialkylamino group, a -COOR⁵ group or a -CONR⁶R⁷ group, in which R⁵ is a lower alkyl group which may be substituted, a lower alkenyl group which may be substituted or an aryl group which may be substituted and R⁶ and R⁷ can be respectively independently selected and are a hydrogen atom, a lower alkyl group which may be substituted, a lower alkenyl group which may be substituted or an aryl group which may be substituted; <ul id="ul0001" list-style="none" compact="compact"><li>(2) a mixture of the above pyrazolonemethine type dye and a pyrazoloneazo type dye; and</li><li>(3) a mixture of the above pyrazolonemethine type dye and a quinophthalone type dye.</li></ul>

0016In the substituents of the pyrazolonemethine type dye of the formula (1), the term "lower" means "C₁-C₈" (number of carbon atoms = from 1 to 8).

0017R¹ and R² are respectively independently selected, and are a lower alkyl group which may be substituted, a lower alkenyl group which may be substituted or an aryl group which may be substituted; and R³ and R⁴ are respectively independently selected, and are a lower alkyl group which may be substituted, a dialkylamino group, a -COOR⁵ group or a -CONR⁶R⁷ group, in which R⁵ is a lower alkyl group which may be substituted, a lower alkenyl group which may be substituted or an aryl group which may be substituted, and R⁶ and R⁷ are respectively independently selected and are a hydrogen atom, a lower alkyl group which may be substituted, a lower alkenyl group which may be substituted or an aryl group which may be substituted.

0018Preferably, R¹ and R² are respectively independently selected, and are a lower alkyl group, a phenyl group which may be substituted or an aralkyl group, and R³ and R⁴ are respectively independently selected, and are a lower alkyl group or a -COOR⁵ group in which R⁵ is a lower alkyl group, a phenyl group which may be substituted or an aralkyl group.

0019More preferably, R¹ and R² are respectively independently selected, and are a lower alkyl group, a phenyl group which may be substituted with a methyl group, methyl groups, a halogen atom, halogen atoms or a benzyl group, and R³ and R⁴ are respectively independently selected and are a lower alkyl group or a -COOR⁵ in which R⁵ is a lower alkyl group, a phenyl group which may be substituted with a methyl group or a halogen atom, or a benzyl group.

0020Still more preferably, R¹ and R² are respectively independently selected, and are a phenyl group or a tolyl group, and R³ and R⁴ are methyl groups.

0021The pyrazolonemethine type dye of the formula (1) wherein R¹ and R² are phenyl groups and R³ and R⁴ are methyl groups, is known as C.I. Solvent Yellow 93, and is most preferable among the dyes used in the present invention for yellow recording by thermal sublimable dye transfer recording.

0022The pyrazoloneazo type dye is preferably a pyrazoloneazo type dye of the following formula (2): <chemistry id="chem0003" num="0003"><img file="EP0802065A2_D0003.tif" /></chemistry> wherein A is a phenyl group which may be substituted, R⁸ is a lower alkyl group which may be substituted, a lower alkenyl group which may be substituted or an aryl group which may be substituted, and R⁹ is a lower alkyl group which may be substituted or -COOR¹⁰ group in which R¹⁰ is a lower alkyl group which may be substituted, a lower alkenyl group which may be substituted or an aryl group which may be substituted. In these substituents, the term "lower" means "C₁-C₈".

0023Preferably, a substituent for A is respectively independently selected, and is a hydrogen atom, a fluorine atom, a chlorine atom, a bromine atom, a nitro group, a cyano group or a methyl group and they may be plurally present, and R⁸ is a lower alkyl group or a phenyl group which may be substituted with a halogen atom, halogen atoms, a methyl group or methyl groups, and R⁹ is a methyl group.

0024The pyrazoloneazo type dye of the formula (2) wherein A is a phenyl group, R⁸ is a phenyl group and R⁹ is a methyl group, is known to be as C.I. Solvent Yellow 16, and is most preferable among the dyes used in the present invention, as a pyrazoloneazo type dye to be contained in a dye layer, together with a pyrazolonemethine type dye of the formula (1).

0025The most preferable combination of a pyrazolonemethine type dye and a pyrazoloneazo type dye used in the present invention is a combination of a pyrazolonemethine type dye of the formula (1) wherein R¹ and R² are respectively independently a phenyl group or a tolyl group and R³ and R⁴ are methyl groups and a pyrazoloneazo type dye of the formula (2) wherein a substituent for A is selected from the group consisting of a hydrogen atom, a chlorine atom and a methyl group and they may be plurally present, and R⁸ is a C₃-C₈ alkyl group, a phenyl group or a tolyl group, and R⁹ is a methyl group. Most preferably, a combination of C.I. Solvent Yellow 93 and C.I. Solvent Yellow 16.

0026With regard to a quinophthalone type dye used in combination with a pyrazolonemethine type dye of the present invention, any dye may be usable as far as it satisfies the aimed object of the present invention.

0027Particularly, a quinophthalone type dye of the following formula (3) is preferable. <chemistry id="chem0004" num="0004"><img file="EP0802065A2_D0004.tif" /></chemistry>

0028In the above formula, R¹¹ is a hydrogen atom, a lower alkyl group which may be substituted, a halogen atom, an alkoxy group or an alkoxycarbonyl group, R¹² is a hydrogen atom, a halogen atom, an alkoxy group or a phenoxy group which may be substituted, and R¹³ is halogen atom, a -COOR¹⁴ group or a -CONR¹⁵R¹⁶ group, in which R¹⁴ is an alkyl group which may be substituted, a lower alkenyl group which may be substituted or an aryl group which may be substituted, and R¹⁵ and R¹⁶ are respectively a hydrogen atom, a lower alkyl group which may be substituted, a lower alkenyl group which may be substituted or an aryl group which may be substituted, provided that R¹⁵ and R¹⁶ are not hydrogen atoms at the same time. In the above definition, the term "lower" means" "C₁-C₈".

0029A preferable dye of the formula (3) is a quinophthalone type dye of the following formula (4) wherein R¹¹ is a hydrogen atom or a C₁-C₄ alkyl group, R¹² is a hydrogen atom or a halogen atom, and R¹³ is a -COOR¹⁴ group or a -CONR¹⁵R¹⁶ group, in which R¹⁴ is a C₃-C₁₂ alkyl group which may be substituted or a phenyl group which may be substituted, and R¹⁵ and R¹⁶ are independently a lower alkyl group which may be substituted or an aryl group which may be substituted. <chemistry id="chem0005" num="0005"><img file="EP0802065A2_D0005.tif" /></chemistry>

0030More preferably, in the above formula (4), R¹¹ is a hydrogen atom or C₁-C₄ alkyl group, R¹² is a hydrogen atom or a bromine atom, and R¹³ is a -COOR¹⁴ group or a -CONR¹⁵R¹⁶ group, in which R¹⁴ is a C₃-C₈ alkyl group or a C₃-C₈ alkoxyalkyl group, and R¹⁵ and R¹⁶ are independently a lower alkyl group.

0031A quinophthalone type dye is poor in solubility because it contains a plurality of a hydroxyl group, a carbonyl bond and an aromatic ring in its molecule. For example, in the formula (4), when R¹³ is a hydrogen atom, R¹⁴ is a hydrogen atom and R¹⁵ and R¹⁶ are also hydrogen atoms at the same time, it tends to be poor in solubility.

0032When the above substituents are evaluated from the point of solubility, it is preferable that R¹¹ is an alkyl group, R¹² is a bromine atom, and R¹³ is preferably a -CONR¹⁵R¹⁶ group rather than a -COOR¹⁴ group, in which R¹⁴ of the -COOR¹⁴ group is preferably an alkyl group having a carbon number of at least 4 or an alkoxyalkyl group having a total carbon number of at least 6, and a larger carbon number is more preferable, and R¹⁵ and R¹⁶ of the -CONR¹⁵R¹⁶ are preferably an alkyl group having a carbon number of at least 2, and a larger carbon number is more preferable. When R¹¹ is an alkyl group, it works favorable in respect of solubility, but is unfavorable in respect to a cost since it requires a complicated synthesis route of many steps as compared with the case where R¹¹ is hydrogen.

0033A preferable combination example of a pyrazolonemethine type dye and a quinophthalone type dye includes a pyrazolonemethine type dye of the formula (1) wherein R¹ and R² are independently a lower alkyl group, a phenyl group which may be substituted with a methyl group or a halogen atom, or a benzyl group, and R³ and R⁴ are independently a lower alkyl group or a -COOR⁵ group in which R⁵ is a lower alkyl group, a phenyl group which may be substituted with a methyl group or a halogen atom, or a a benzyl group, and a quinophthalone type dye of the formula (4) wherein R¹¹ is a hydrogen atom or a C₁-C₄ alkyl group, R¹² is a hydrogen atom or a halogen atom, and R¹³ is a -COOR¹⁴ group or a -CONR¹⁵R¹⁶ group, in which R¹⁴ is a C₃-C₁₂ alkyl group which may be substituted or a phenyl group which may be substituted, and R¹⁵ and R¹⁶ are independently a lower alkyl group which may be substituted or an aryl group which may be substituted.

0034The most preferable combination is a pyrazolonemethine type dye of the formula (1) wherein R¹ and R² are a methyl group, an ethyl group, a propyl group, a butyl group, a phenyl group or a tolyl group, and R³ and R⁴ are independently a methyl group or a -COOR⁵ group in which R⁵ is an ethyl group, a propyl group or a butyl group, and a quinophthalone type dye of the formula (4) wherein R¹¹ is a hydrogen atom or a C₁-C₄ alkyl group, R¹² is a hydrogen atom or a bromine atom, R¹³ is a -COOR¹⁴ group or a -CONR¹⁵R¹⁶ group, in which R¹⁴ is a C₃-C₈ alkyl group or a C₃-C₈ alkoxyethyl group, and R¹⁵ and R¹⁶ are independently a C₂-C₈ alkyl group.

0035It is known from JP-A-60-53565 and JP-A-63-182193 that a quinophthalone type dye of the formula (3) of the present invention is usable for thermal dye transfer recording system.

0036An ordinary color print is expressed by the three primary colors of yellow, magenta and cyan, and a thermal dye transfer sheet used for thermal dye transfer recording system usually has three dye layers of yellow, magenta and cyan disposed in order on a substrate. In some cases, four dye layers including a black dye layer in addition to yellow, magenta and cyan dye layers, are disposed on a substrate.

0037When the above yellow dye layer of the present invention is used for full color image formation, preferable examples of a magenta dye used for a magenta dye layer favorably used in combination with the above yellow dye layer, include C.I. Disperse Red 60, C.I. Disperse Violet 26, C.I. Solvent Red 27, C.I. Solvent Red 19, an anthraquinone type dye, an imidazoleazo dye, a thiadiazoleazo type dye and the like.

0038Preferable examples of a cyan dye used for a cyan dye layer favorably used in combination with the above yellow dye layer, include an indoaniline type cyan dye. The indoaniline type cyan dye is preferable because of a high sensitivity and a high weather resistance, but it has a disadvantage that it is weak to catalytic fading phenomenon.

0039The catalytic fading phenomenon is a phenomenon of light-fading caused depending on a combination of dyes, and it is particularly remarkable in the combination of a cyan dye and a yellow dye. More particularly, it has been known that this phenomenon is liable to be caused when using an indoaniline type dye useful as a cyan dye. Depending on a yellow dye used to be combined, regardless of its light-resistance, a yellow dye remarkably fades an indoaniline type dye color used in combination therewith when they are exposed to light. Thus, among conventional yellow dyes usually used for thermal dye transfer recording, there has been no yellow dye which gives a high density and does not cause catalytic fading phenomenon when used in combination with an indoaniline type dye. It was therefore very difficult to provide a mixed color, i.e. green color (yellow color + cyan color) or black color (yellow + magenta + cyan), which has an excellent high-light resistance and gives a high density recording.

0040As a result of the study, the present inventors have found that a pyrazolonemethine type yellow dye not only provides a high optical density recording but also does not cause a catalytic fading phenomenon of an indoaniline type cyan used in combination therewith. Thus, it has been made possible by the present invention that a combination use of an indoaniline type cyan dye and a pyrazolonemethine type dye provides an image having a high optical density and a high light-resistance.

0041Accordingly, in the present invention, any of indoaniline type dyes can be used and a plurality of dyes can be blended as far as they satisfy the aimed object of the present invention.

0042Preferable examples of an indoaniline type dye include a dye of the following formula (5): <chemistry id="chem0006" num="0006"><img file="EP0802065A2_D0006.tif" /></chemistry> wherein -B- is -CONH-, -NHCO-, -NHCOO- or -NHSO₂-, R¹⁷ is a lower alkyl group which may be substituted, a lower alkenyl group which may be substituted, an aryl group which may be substituted, an aralkyl group which may be substituted or a heterocyclic ring which may be substituted with an alkyl group or a halogen atom, R¹⁸ and R¹⁹ are independently a lower alkyl group which may be substituted, R²⁰ is a hydrogen atom or a halogen atom, R²¹ is a hydrogen atom or an alkyl group which may be substituted or an acylamino group, R²² is a hydrogen atom, a methyl group, an acylamino group, an alkoxycarbonylamino group or an alkylsulfonylamino group, R²³ is a hydrogen atom or a methyl group, and R²⁰ and R²¹ may be connected to form a 6-membered aromatic ring which may contain a hetero atom.

0043More preferably, an indoaniline type dye of the above formula (5) is a dye of the following formula (6): <chemistry id="chem0007" num="0007"><img file="EP0802065A2_D0007.tif" /></chemistry> wherein -B- is -NHCO- or -NHCOO-, R¹⁷ is a lower alkyl group which may be substituted, a lower alkenyl group which may be substituted, an aryl group which may be substituted, an aralkyl group which may be substituted or a heterocyclic ring which may be substituted with an alkyl group or a halogen atom, R¹⁸ and R¹⁹ are independently a lower alkyl group which may be substituted, R²⁰ is a hydrogen atom or a halogen atom, R²¹ is a methyl group or an ethyl group, and R²² is a hydrogen atom or a methyl group.

0044In the above definition of substituents of the formula (5) and (6), the term "lower" means "C₁-C₈", and an aryl group and aralkyl group usually have a carbon number of from 6 to 10.

0045Preferably, R¹⁷ is an alkyl group, a lower alkenyl group, an aralkyl group, an aryl group, a halogeno-lower alkyl group, a hydroxy-lower alkyl group, a cyan-lower alkyl group, an ether bond-containing alkyl group, a heterocyclic ring-substituted alkyl group or a heterocyclic ring, R¹⁸ is a lower alkyl group, R¹⁹ is a lower alkyl group, a halogeno-lower alkyl group, a hydroxy-lower alkyl group, an amino-lower alkyl group, an ether bond containing alkyl group, an amino bond-containing alkyl group or a sulfonylamino bond-containing alkyl group, R²¹ is a methyl group or an ethyl group, R²² is a hydrogen atom or a methyl group, and R²⁰ is a hydrogen atom, a chlorine atom or a bromine atom.

0046More preferably, R¹⁷ is a lower alkyl group, a lower alkenyl group, a C₇-C₁₀ aralkyl group, a C₆-C₁₀ aryl group, a chloroethyl group, a lower alkoxyalkyl group, a tetrahydrofurfuryl group, a C₉-C₁₂ aralkyloxyethyl group, a C₈-C₁₂ aryloxyethyl group, a lower alkenyloxyethyl group or a heterocyclic ring having O, N or S as a hetero atom, R¹⁸ is a methyl group or an ethyl group, R¹⁹ is a lower alkyl group, a chloroethyl group, a hydroxyethyl group, a lower alkoxyethyl group, a C₉-C₁₂ aralkyloxyethyl group or a C₈-C₁₂ aryloxyethyl group, R²¹ is a methyl group or an ethyl group, R²² is a hydrogen atom or a methyl group, and R²⁰ is a hydrogen atom or a chlorine atom.

0047Still more preferably, R¹⁷ is a lower alkyl group, a lower alkenyl group, a phenyl group, a tolyl group, a benzyl group, a tetrahydrofurfuryl group, a lower alkoxy lower alkyl group, furan, pyridine or thiophene, R¹⁸ and R¹⁹ are ethyl groups, R²¹ is a methyl group or an ethyl group, R²² is a hydrogen atom or a methyl group, and R²⁰ is a hydrogen atom or a chlorine atom.

0048When R²⁰ is a chlorine atom, R¹⁷ preferably has at least 2 carbon atoms since it improves the solubility of a dye.

0049Preferable combination examples of a pyrazolonemethine type dye and an indoaniline type dye to be used in a mixture, include a pyrazolonemethine type dye of the formula (1) wherein R¹ and R² are independently a lower alkyl group, an aryl group which may be substituted or an aralkyl group, and R³ and R⁴ are a lower alkyl group or a -COOR⁵ group in which R⁵ is a lower alkyl group, an aryl group which may be substituted or an aralkyl group, and an indoaniline type dye of the formula (6) wherein -B- is -NHCO- or -NHCOO-, R¹⁷ is a lower alkyl group, a lower alkenyl group, a C₇-C₁₀ aralkyl group, a C₆-C₁₀ aryl group, a chloroethyl group, a lower alkoxy lower alkyl group, a tetrahydrofurfuryl group, a C₉-C₁₂ aralkyloxyethyl group, a C₈-C₁₂ aryloxyethyl group, a lower alkenyloxyethyl group, a tetrahydrofurfuryloxyethyl group or a heterocyclic ring containing O, N or S as a hetero atom, R¹⁸ and R¹⁹ are a methyl group or an ethyl group, R²⁰ is a hydrogen atom or a chlorine atom, R²¹ is a methyl group or an ethyl group, and R²² is a hydrogen atom or a methyl group.

0050More preferable combination examples include a pyrazolonemethine type dye of the formula (1) wherein R¹ and R² are independently a methyl group, an ethyl group, a propyl group, a butyl group, a phenyl group or a tolyl group, and R³ and R⁴ are independently a methyl group or a -COOR⁵ group in which R⁵ is an ethyl group, a propyl group or a butyl group, and an indoaniline type dye of the formula (6) wherein -B- is -NHCO-, R¹⁷ is a lower alkyl group, a lower alkenyl group, a phenyl group, a tolyl group,a benzyl group, a tetrahydrofurfuryl group, a lower alkoxy lower alkyl group, furan, pyridine or thiophene, R¹⁸ and R¹⁹ are ethyl groups, R²⁰ is a hydrogen atom or a chlorine atom, R²¹ is a methyl group or an ethyl group, and R²² is a hydrogen atom or a methyl group.

0051It is known from JP-A-61-31292 and JP-A-61-35994 that a part of the indoaniline type dye of the formula (6) of the present invention is usable for thermal dye transfer recording system.

0052The main component contained in a dye layer other than a dye is a binder resin. Preferable examples of the binder resin include a cellulose type resin such as ethylcellulose, hydroxyethylcellulose, ethylhydroxycellulose, hydroxypropylcellulose, methylcellulose, cellulose acetate or the like, a butyral resin, an acetal resin, a phenoxy resin, a polycarbonate resin, a vinyl chloride-vinyl acetate resin, an acrylonitrile-styrene resin, a polyester resin, and the like.

0053A preferable ratio of a dye and a binder in a dye layer is dye/resin = from 10/100 to 300/100. If the dye/resin ratio is lower than 10/100, an amount of a dye is too small to provide a satisfactory coloring sensitivity and a satisfactory thermal dye transfer image can not be obtained. On the contrary, if the dye/resin ratio exceeds 300/100, a dye becomes too poor in solubility to a binder resin, and therefore a dye layer of a thermal dye transfer sheet obtained therefrom becomes too poor in shelf stability (that is, a dye is liable to precipitate).

0054In order to avoid the above-mentioned problems, a more preferable dye/resin ratio in the present invention is dye/resin = from 40/100 to 200/100, most preferably from 66/100 to 150/100.

0055When taking these points into consideration, it is preferable to use a binder resin having a higher compatibility with a dye and causing no problem when containing a dye at a high concentration. Thus, among the above-mentioned binder resins, it is preferable to use a resin having a Tg value of at least 50°C, such as a phenoxy resin, a polyvinyl butyral resin, a vinyl chloride-vinyl acetate resin and an acryl-styrene resin. Particularly, a phenoxy resin and a polyvinyl butyral resin are preferable since they can contain a dye at a high concentration.

0056The dye layer of the thermal dye transfer sheet of the present invention are made basically from the above-mentioned materials, but it is preferable for avoiding a fusing between the thermal dye transfer sheet and an image-receiving material to incorporate a release agent into the dye layer by taking compatibility of the thermal dye transfer sheet with the image-receiving material into consideration, if necessary.

0057Preferable examples of the release agent include a silicone oil, a silicone resin and the like, and it is more preferable to employ a silicone-modified resin having the main chain modified with silicone for imparting a higher shelf stability to the thermal dye transfer sheet.

0058Examples of the main chain used for such a release agent include an acrylic type resin, a cellulose type resin, a vinyl type resin or a polyester type resin, but particularly preferable examples include an acrylic type resin or a polyester type resin. When a film is formed from an ink for a dye layer containing such a release agent, the silicone part is bleeded on the surface (due to low compatibility to the dye layer ink), thereby achieving a satisfactory release property during heating.

0059The release agent is incorporated preferably in an amount of from 0.01% to 10% to the solid content of the dye layer ink. If the amount of the release agent is lower than 0.01%, a satisfactory release property can not be achieved. On the other hand, if the amount of the release agent exceeds 10%, it becomes difficult to form a satisfactory dye layer on a substrate sheet or the bleeded amount of silicone on the surface of the dye layer becomes so large that an image-receiving layer tends to be easily polluted.

0060The dye layer is formed by preparing a dye layer ink having the above-mentioned dye, a binder resin and other additives dissolved or dispersed in an appropriate solvent, coating the dye layer ink on the above-mentioned substrate sheet and drying.

0061Examples of a solvent used for the ink include aromatic type solvents such as toluene and xylene; ketone type solvents such as methyl ethyl ketone, methyl isobutyl ketone and cyclohexanone; ester type solvents such as ethyl acetate and butyl acetate; alcohol type solvents such as isopropanol, butanol and methyl cellosolve, ether type solvents such as dioxane and heterohydrofuran; and amide type solvents such as dimethylformamide and N-methylpyrrolidone. In addition to the above-mentioned components, the ink may further contain organic or inorganic non-sublimable particles, a dispersing agent, an antistatic agent, an anti-blocking agent, a defoaming agent, an antioxidant, a viscosity regulator and other additives, if necessary. Further, an infrared ray-absorbing agent or carbon black may be added to be used for sublimable dye transfer system using a laser light. A means for providing a dye layer by coating the above-mentioned ink is not specially limited, but a gravier printing machine, a reverse roll coater or the like may be used. A coating film thickness is appropriately from 0.1 to 5 µm, preferably from 0.4 to 3 µm, more preferably from 0.5 to 2 µm on the basis of a dry film thickness. A coating amount is from 0.3 to 1.5 g/m².

0062If the thickness of the dye layer is smaller than 0.2 µm, a satisfactory coloring density can not be achieved. On the other hand, if the thickness exceeds 5 µm, a coloring sensitivity becomes poor.

0063As mentioned above, in order to improve the heat-resistance and lubricating property of a thermal dye transfer sheet, it is sometimes preferable to provide a heat-resistant layer on the opposite side of a dye layer of a substrate sheet.

0064The heat-resistant layer is not specially limited, but it is known to use a cured resin of a UV ray-cured resin or a thermoplastic resin having a high Tg value. Since the heat-resistant layer requires not only a heat-resistance to the heat of a thermal head but also a lubricating property to the thermal head, it is general for the heat-resistant layer to contain such a lubricating agent as a silicone oil.

0065Generally, in order to carry out thermal dye transfer recording, a dye layer of a thermal dye transfer sheet is brought into contact with an image-receiving layer of an image-receiving sheet provided on one side of a substrate, and heat is applied depending on an image signal by using a heat source such as a line type thermal head on the opposite side of a dye layer of the thermal transfer sheet, thereby transferring a dye in the dye layer to the image-receiving layer. In accordance with the heat amount applied, a dye amount to be transferred can be controlled, thereby achieving light and shade expressions and obtaining precise images. With regard to three colors of yellow, magenta and cyan or four colors additionally including black, the same operation as mentioned above is repeated, thereby obtaining a photograph-tone image.

0066As a thermal dye transfer sheet for obtaining a color image, there is a system of employing a plurality of respectively separate thermal dye transfer sheets of each color or a system of employing a thermal dye transfer sheet having a plurality of dye layers provided on the same single sheet. Either system may be employed, but the single thermal dye transfer sheet having a plurality of dye layers provided on the same sheet is preferable since a color image can be formed by only one thermal dye transfer sheet and a device for carrying out the thermal dye transfer recording is simple.

0067As a heat source for carrying out the transferring of a dye, there are generally known a line type thermal head and a laser light. In the case of using a laser light, a light-heat conversion material is required to transfer the laser light into heat, and an infrared ray-absorbing agent and carbon black may be incorporated in a dye layer of a thermal dye transfer sheet, between the dye layer and a substrate or the opposite side of the dye layer.

0068An image-receiving sheet used for forming an image by means of the above-mentioned thermal dye transfer sheet, may be any type of image-receiving sheet as far as its recording phase has an image-receiving property to the above-mentioned dye. Thus, any type of image-receiving sheet may be used as far as its recording phase is an image-receiving material. An image-receiving layer is generally provided on at least one side of a substrate. Examples of the substrate include a synthetic paper, a cellulose paper, a cast coat paper, and a substrate having synthetic papers attached to both sides of a film or cellulose paper. The surface of the substrate is preferably smooth so that a satisfactory intimate contact with a dye layer can be made at the time of recording, thereby achieving a satisfactory uniform transferring of a dye. Thus, if possible, it is preferable to use a substrate having a beck smoothness of at least 10,000 seconds. From this point of view, it is preferable to use a synthetic paper or film as a substrate.

0069An image-receiving layer is a layer comprising a resin as the main component, and has a function of forming an image by receiving a dye. Thus, it is preferable to use a resin easily dyeable with a dye, examples of which include polyolefin type resins such as polyethylene or polypropylene, acetal resin, polyvinyl chloride resin, vinyl chloride-vinyl acetate copolymer resin, polyester resin, polystyrene resin, a copolymer resin of an olefin and other vinyl monomer, ionomer, cellulose type resin, polycarbonate resin, and the like. These resins may be used in combination. It is not preferable to use a resin, the glass transition point of each is too low, since an image blurs during storing. Thus, it is preferable to use an image-receiving layer having a glass transition temperature of at least 35°C as an image-receiving layer.

0070If necessary, an image-receiving layer may further contain additives in addition to a resin. Examples of the additives include a curing agent such as isocyanate for curing a resin, a release agent such as silicone to be added for preventing a fusing between the image-receiving layer and a dye layer during thermal dye transferring, a UV ray-absorbing agent to improve light-resistance, an antioxidant to improve weather-resistance, and the like, but the additives to be added are not limited thereto.

0071With regard to a thickness of an image-receiving layer, if the thickness is too small, a satisfactory coloring density can not be obtained.

0072When the recording surface does not have an image-receiving property (such as paper, metal, glass, a resin having no dye-receiving property, and the like), an image-receiving layer (comprising a dye-receiving material) is provided on the recording surface having no dye-receiving property, thereby forming a dye-receiving layer, and an image from a thermal dye transfer sheet may be formed thereon. Alternatively, an image from a thermal dye transfer sheet is formed on a separate image-receiving layer, and the image-receiving layer having the image thus formed may be attached to a recording surface having no dye-receiving property.

(EXAMPLES)

0073Now, the present invention will be described in further detail with reference to Examples. However, it should be understood that the present invention is by no means restricted to such specific Examples. In the present specification, "part" means part by weight and "%" means % by weight.

EXAMPLE 1

0074A thermal dye transfer sheet of the present invention was obtained by preparing an ink composition of the following composition for a dye layer and coating and drying the ink composition in a polyethyleneterephthalate film of a thickness of 5.4 µm provided with a heat-resistant layer on its backside in such a manner as to provide a dry coating thickness of 1.5 µm.

(Ink for dye layer)

0075<tables id="tabl0001" num="0001"><table frame="all"><tgroup cols="2" colsep="1" rowsep="0"><colspec colnum="1" colname="col1" colwidth="78.75mm" /><colspec colnum="2" colname="col2" colwidth="78.75mm" /><tbody valign="top"><row><entry namest="col1" nameend="col1" align="left">C.I Solvent Yellow 93</entry><entry namest="col2" nameend="col2" align="left">4.0 parts</entry></row><row><entry namest="col1" nameend="col1" align="left">Butyral resin</entry><entry namest="col2" nameend="col2" align="left">5.0 parts</entry></row><row><entry namest="col1" nameend="col1" align="left">Methyl ethyl ketone</entry><entry namest="col2" nameend="col2" align="left">60.0 parts</entry></row><row rowsep="1"><entry namest="col1" nameend="col1" align="left">Toluene</entry><entry namest="col2" nameend="col2" align="left">31.0 parts</entry></row></tbody></tgroup></table></tables>

0076The above C.I. Solvent Yellow 93 is a pyrazolonemethine type dye of the formula (1) wherein R¹ and R² are a phenyl group and R³ and R⁴ are a methyl group.

0077Thereafter, an image-receiving sheet was prepared by coating an ink of the following composition for an image-receiving layer on one side of a layered structure sheet of foamed polypropylene film (thickness 50 µm)/adhesive resin layer/coated paper (108 g/m²)/adhesive resin layer/foamed polypropylene film (thickness 50 µm) as a substrate sheet so as to provide a dry coating thickness of 4 µm, drying the coated film and then subjecting the coated film to aging at 45°C for one week.

(Ink for image-receiving layer)

0078<tables id="tabl0002" num="0002"><table frame="all"><tgroup cols="2" colsep="1" rowsep="0"><colspec colnum="1" colname="col1" colwidth="78.75mm" /><colspec colnum="2" colname="col2" colwidth="78.75mm" /><tbody valign="top"><row><entry namest="col1" nameend="col1" align="left">Acetal resin</entry><entry namest="col2" nameend="col2" align="left">10.0 parts</entry></row><row><entry namest="col1" nameend="col1" align="left">Vinyl chloride-vinyl acetate copolymer resin</entry><entry namest="col2" nameend="col2" align="left">10.0 parts</entry></row><row><entry namest="col1" nameend="col1" align="left">Silicone oil</entry><entry namest="col2" nameend="col2" align="left">2.0 parts</entry></row><row><entry namest="col1" nameend="col1" align="left">Isocyanate resin</entry><entry namest="col2" nameend="col2" align="left">3.0 parts</entry></row><row><entry namest="col1" nameend="col1" align="left">Methyl ethyl ketone</entry><entry namest="col2" nameend="col2" align="left">50.0 parts</entry></row><row rowsep="1"><entry namest="col1" nameend="col1" align="left">Toluene</entry><entry namest="col2" nameend="col2" align="left">25.0 parts</entry></row></tbody></tgroup></table></tables>

0079The dye layer side of the above-obtained thermal dye transfer sheet was brought into contact with the dye-receiving layer of the above prepared image-receiving sheet, and the dye was transferred by using a thermal head under the following conditions to form an image.

(Printing conditions)

0080<dl id="dl0001" compact="compact"><dt>Printer:</dt><dd>Simulator manufactured by SIP Co. (300 dots/mm Head)</dd><dt>Printing pattern:</dt><dd>16 tone pattern</dd><dt>Printing energy:</dt><dd>0.6 mJ/dot at 16th tone</dd></dl>

0081The image thus formed was evaluated in the following manner.

(Evaluation items)

0082Coloring density: a reflective density at the 16th tone was measured by Macbeth RD-918.

0083Heat tranfer-resistance: density reduction rate at the 16th tone after 8 hours at 70°C.

0084Light-resistance: density reduction rate at the 16th tone after irradiating with a xenon fade meter for 80 hours.

0085Evaluation results with regard to the above items were satisfactory as shown below. Also, a color reproducibility of yellow color was satisfactory.

0086Under the above printing conditions, the following coloring density could be obtained, and its coloring sensitivity was also satisfactory.

(Evaluation results)

0087<dl id="dl0002" compact="compact"><dt>Coloring density :</dt><dd>2.4</dd><dt>Heat transfer-resistance:</dt><dd>at most 5%</dd><dt>Light-resistance:</dt><dd>at most 3%</dd></dl>

EXAMPLE 2

0088A thermal dye transfer sheet was obtained in the same manner as in Example 1, except that an ink composition of the following composition for a dye layer was used.

(Ink for dye layer)

0089<tables id="tabl0003" num="0003"><table frame="all"><tgroup cols="2" colsep="1" rowsep="0"><colspec colnum="1" colname="col1" colwidth="78.75mm" /><colspec colnum="2" colname="col2" colwidth="78.75mm" /><tbody valign="top"><row><entry namest="col1" nameend="col1" align="left">C.I. Solvent Yellow 93</entry><entry namest="col2" nameend="col2" align="left">3.0 parts</entry></row><row><entry namest="col1" nameend="col1" align="left">C.I. Solvent Yellow 16</entry><entry namest="col2" nameend="col2" align="left">1.0 parts</entry></row><row><entry namest="col1" nameend="col1" align="left">Butyral resin</entry><entry namest="col2" nameend="col2" align="left">5.0 parts</entry></row><row><entry namest="col1" nameend="col1" align="left">Methyl ethyl ketone</entry><entry namest="col2" nameend="col2" align="left">60.0 parts</entry></row><row rowsep="1"><entry namest="col1" nameend="col1" align="left">Toluene</entry><entry namest="col2" nameend="col2" align="left">31.0 parts</entry></row></tbody></tgroup></table></tables>

0090The above C.I. Solvent Yellow 16 is a pyrazoloneazo type dye of the formula (2), wherein A is a phenyl group, R⁸ is a phenyl group, and R⁹ is a methyl group.

0091The obtained thermal dye transfer sheet was placed on an image-receiving sheet obtained in the same manner as in Example 1, and an image was formed and evaluated in the same manner as in Example 1. The evaluation results are shown below.

0092Under the above printing conditions, the following coloring density could be obtained, and its coloring sensitivity was also satisfactory.

(Evaluation results)

0093<dl id="dl0003" compact="compact"><dt>Coloring density:</dt><dd>2.4</dd><dt>Heat tranfer-resistance:</dt><dd>at most 5%</dd><dt>Light-resistance:</dt><dd>at most 3%</dd></dl>

0094Also, a color reproducibility of yellow color was evaluated to be satisfactory.

EXAMPLE 3

0095A thermal dye transfer sheet was obtained in the same manner as in Example 1, except that an ink composition of the following composition for a dye layer was used.

(Ink for dye layer)

0096<tables id="tabl0004" num="0004"><table frame="all"><tgroup cols="2" colsep="1" rowsep="0"><colspec colnum="1" colname="col1" colwidth="78.75mm" /><colspec colnum="2" colname="col2" colwidth="78.75mm" /><tbody valign="top"><row><entry namest="col1" nameend="col1" align="left">C.I. Solvent Yellow 93</entry><entry namest="col2" nameend="col2" align="left">3.0 parts</entry></row><row><entry namest="col1" nameend="col1" align="left">C.I. Solvent Yellow 16</entry><entry namest="col2" nameend="col2" align="left">1.0 parts</entry></row><row><entry namest="col1" nameend="col1" align="left">Phenoxy resin</entry><entry namest="col2" nameend="col2" align="left">3.0 parts</entry></row><row><entry namest="col1" nameend="col1" align="left">Butyral resin</entry><entry namest="col2" nameend="col2" align="left">2.0 parts</entry></row><row><entry namest="col1" nameend="col1" align="left">Methyl ethyl ketone</entry><entry namest="col2" nameend="col2" align="left">60.0 parts</entry></row><row rowsep="1"><entry namest="col1" nameend="col1" align="left">Toluene</entry><entry namest="col2" nameend="col2" align="left">31.0 parts</entry></row></tbody></tgroup></table></tables>

0097The obtained thermal dye transfer sheet was placed on an image-receiving sheet obtained in the same manner as in Example 1, and an image was formed and evaluated in the same manner as in Example 1. The evaluation results are shown below.

0098Under the above printing conditions, the following coloring density could be obtained, and its coloring sensitivity was also satisfactory.

(Evaluation results)

0099<dl id="dl0004" compact="compact"><dt>Coloring density:</dt><dd>2.3</dd><dt>Heat tranfer-resistance:</dt><dd>at most 5%</dd><dt>Light-resistance:</dt><dd>at most 3%</dd></dl>

0100Also, a color reproducibility of yellow color was evaluated to be satisfactory.

EXAMPLE 4

0101A thermal dye transfer sheet was obtained in the same manner as in Example 1, except that an ink composition of the following composition for a dye layer was used.

(Ink for dye layer)

0102<tables id="tabl0005" num="0005"><table frame="all"><tgroup cols="2" colsep="1" rowsep="0"><colspec colnum="1" colname="col1" colwidth="78.75mm" /><colspec colnum="2" colname="col2" colwidth="78.75mm" /><tbody valign="top"><row><entry namest="col1" nameend="col1" align="left">C.I. Solvent Yellow 93</entry><entry namest="col2" nameend="col2" align="left">3.0 parts</entry></row><row><entry namest="col1" nameend="col1" align="left">C.I. Solvent Yellow 16</entry><entry namest="col2" nameend="col2" align="left">1.0 parts</entry></row><row><entry namest="col1" nameend="col1" align="left">Phenoxy resin</entry><entry namest="col2" nameend="col2" align="left">5.0 parts</entry></row><row><entry namest="col1" nameend="col1" align="left">Silicone-modified resin</entry><entry namest="col2" nameend="col2" align="left">0.05 part</entry></row><row><entry namest="col1" nameend="col1" align="left">Methyl ethyl ketone</entry><entry namest="col2" nameend="col2" align="left">60.0 parts</entry></row><row rowsep="1"><entry namest="col1" nameend="col1" align="left">Toluene</entry><entry namest="col2" nameend="col2" align="left">31.0 parts</entry></row></tbody></tgroup></table></tables>

0103The obtained thermal dye transfer sheet was placed on an image-receiving sheet obtained in the same manner as in Example 1, and an image was formed and evaluated in the same manner as in Example 1. The evaluation results are shown below.

0104Under the above printing conditions, the following coloring density could be obtained, and its coloring sensitivity was also satisfactory.

(Evaluation results)

0105<dl id="dl0005" compact="compact"><dt>Coloring density:</dt><dd>2.4</dd><dt>Heat tranfer-resistance:</dt><dd>at most 5%</dd><dt>Light-resistance:</dt><dd>at most 3%</dd></dl>

0106Also, a color reproducibility of yellow color was evaluated to be satisfactory.

EXAMPLE 5

0107A thermal dye transfer sheet was obtained in the same manner as in Example 1, except that Dye 1-2 (compound of the formula (1) wherein R¹ and R² are an o-tolyl group and R³ and R⁴ are a methyl group) was used in placed of C.I. Solvent Yellow 93. An image was formed by using the above obtained thermal dye transfer sheet and was evaluated in the same manner as in Example 1. The evaluation results are shown below.

0108Under the above printing conditions, the following coloring density could be obtained, and its coloring sensitivity was also satisfactory.

(Evaluation results)

0109<dl id="dl0006" compact="compact"><dt>Coloring density:</dt><dd>2.4</dd><dt>Heat tranfer-resistance:</dt><dd>at most 5%</dd><dt>Light-resistance:</dt><dd>at most 3%</dd></dl>

0110Also, a color reproducibility of yellow color was evaluated to be satisfactory.

EXAMPLE 6

0111A thermal dye transfer sheet was obtained in the same manner as in Example 1, except that Dye 1-3 (compound of the formula (1) wherein R¹ is a phenyl group, R² is an o-tolyl group, and R³ and R⁴ are a methyl group) was used in placed of C.I. Solvent Yellow 93. An image was formed by using the above obtained thermal dye transfer sheet and was evaluated in the same manner as in Example 1. The evaluation results are shown below.

0112Under the above printing conditions, the following coloring density could be obtained, and its coloring sensitivity was also satisfactory.

(Evaluation results)

0113<dl id="dl0007" compact="compact"><dt>Coloring density:</dt><dd>2.4</dd><dt>Heat tranfer-resistance:</dt><dd>at most 5%</dd><dt>Light-resistance:</dt><dd>at most 3%</dd></dl>

0114Also, a color reproducibility of yellow color was evaluated to be satisfactory.

EXAMPLE 7

0115A thermal dye transfer sheet was obtained in the same manner as in Example 2, except that Dye 2-2 (compound of the formula (2) wherein A is a m-chlorophenyl group, and R⁸ is a m-tolyl group, and R⁹ is a methyl group) was used in placed of C.I. Solvent Yellow 16. An image was formed by using the above prepared thermal dye transfer sheet and was evaluated in the same manner as in Example 2. The evaluation results are shown below.

0116Under the above printing conditions, the following coloring density could be obtained, and its coloring sensitivity was also satisfactory.

(Evaluation results)

0117<dl id="dl0008" compact="compact"><dt>Coloring density:</dt><dd>2.4</dd><dt>Heat tranfer-resistance:</dt><dd>at most 5%</dd><dt>Light-resistance:</dt><dd>at most 3%</dd></dl>

0118Also, a color reproducibility of yellow color was evaluated to be satisfactory.

Effects of Examples 1 to 7

0119As mentioned above, according to the present invention, by using a pyrazolonemethine type dye of the formula (1) or a combination of a pyrazolonemethine type dye of the formula (1) and a pyrazoloneazo type of the formula (2) in the same dye layer for a thermal sublimable dye transfer recording system employing a thermal head or a laser as a heat source, it is possible to provide an image having a faithful color reproducibility of an original image and a satisfactory fastness (heat transfer-resistance and dye-resistance), and also possible to provide a satisfactory coloring property (high coloring sensitivity) and a satisfactory coloring density by a small heat energy.

0120Further, by incorporating a silicone type release agent into the dye layer, it is possible to prevent fusing of a dye-receiving layer during thermal dye transfer recording, and also possible to largely wide a range of a choice of a satisfactory material to be used in the dye-receiving layer. Thus, the incorporation of a silicone type release agent achieves excellent performances in these respects.

0121Generally, according to the present invention, a thermal dye transfer sheet achieving the above-mentioned excellent performances can be provided particularly with regard to thermal dye transfer recording system of yellow color.

EXAMPLE 8

(a) Preparation of thermal dye transfer sheet

0122An ink obtained by mixing and stirring 50 parts of Dye 1-1 (Solvent Yellow 93, i.e. a dye of the formula (1) wherein R¹ and R² are a phenyl group and R³ and R⁴ are a methyl group), 50 parts of Dye 3-1 (a dye of the formula (4) wherein R¹¹ is a hydrogen atom, R¹² is a bromine atom, and R¹³ is CONR¹⁵R¹⁶, in which R¹⁵ and R¹⁶ are a propyl group), 100 parts of phenoxy resin (tradename: PKHH manufactured by Union Carbide Co.), 125 parts of methyl ethyl ketone, 450 parts of toluene and 300 parts of tetrahydrofuran (THF), was coated and dried on a polyester film of 6 µm by a bar coater so as to provide a dry film thickness of 1 µm.

0123On the back side of the above obtained polyester film, was coated a mixture solution of 10 parts by weight of acrylic resin (tradename: BR-80 manufactured by Mitsubishi Rayon K.K.), 1 part by weight of amino-modified silicone oil (tradename: KF 393 manufactured by Shin-Etsu Kagaku K.K.) and 89 parts by weight of toluene by a bar coater to provide a dry film thickness of 1 µm and dried to provide a heat-resistant layer.

(b) Preparation of image-receiving layer

0124A solution obtained by mixing and stirring 46 parts of polyvinylphenylacetal resin, 20 parts of vinyl chloride/vinyl acetate/vinyl alcohol copolymer resin (tradename: VAGD manufactured by Union Carbide Co.), 30 parts of silicone varnish (tradename: KR 311 (non-volatile content 60%) manufactured by Toshiba Silicone K.K.), 6 parts of polyoxyethylenealkylphenyl ether (tradename: OP-10 manufactured by Nikko Chemicals K.K.), 1 part of amino-modified silicone oil (tradename: KF 393 manufactured by Shin-Etsu Kagaku Kogyo K.K.), 12 parts of hexamethylenediisocyanate type polyfunctional isocyanate compound (tradename: Mytec NY-710A (solid content concentration 75%) manufactured by Mitsubishi Chemical Co.), 200 parts of methyl ethyl ketone and 200 parts of toluene, was coated on a polypropylene-made synthetic paper of a thickness of 150 µm (tradename: Yupo FPG 150 manufactured by Oji Yuka Goseishi K.K.) by a wire bar and dried (dry film thickness about 5 µm), and was further heat-treated in an oven at 80°C for 12 hours to obtain an image-receiving sheet.

0125The above polyvinylphenylacetal resin is obtained by acetalizing polyvinyl alcohol (saponification value: 99 mol%, polymerization degree: 1,700) with phenylacetaldehyde, and has the following structure formula (7) <chemistry id="chem0008" num="0008"><img file="EP0802065A2_D0008.tif" /></chemistry>

(c) Print recording

0126The dye layer of the thermal dye transfer sheet obtained in the above paragraph (a) was brought into contact with the resin coating surface of the image-receiving sheet obtained in the above paragraph (b), printing was carried out by using a partly glace type line thermal head having a density of 5.6 dots/mm under conditions of a conveying speed of 6 lines (dots)/mm in the conveying direction, a printing speed of 16.6 ms/line and an applied electric power of 0.20 W/dot. The time applied to the head per line was made 12 ms, thereby providing a deep color printing.

(d) Measurement of density

0127The density of the printed matter printed as mentioned in the above paragraph (c) was measured by a refractive densitometer (tradename: Macbeth RD-920 containing a filter having a SPI spectral sensitivity manufactured by Macbeth Co.). As this result, a density was 1.9.

(e) Light-resistance test 1

0128A deep color sample of the printed matter printed as described in the above paragraph (c) was subjected to a light-resistance test for 72 hours at an illuminance of 3.5 kg/m² by using a xenon lamp light-resistance tester (tradename: Atlas Ci35A weatherometer manufactured by Toyo Seiki Seisakusho K.K.). A chrominance of the printed matter was measured before and after the light-resistance test by using a chrominance-meter having an optical system in accordance with JIS Z-8722 (tradename: Spectral Chrominance-meter SZ-Σ80 manufactured by Nihon Denshoku Kogyo K.K.) under conditions of a C-light source and a visual field angle of 2°. As this result, the color difference in the CIELAB color system (ΔEab*) was small and its value was 6.0.

(f) Light-resistance test 2

0129A thermal dye transfer sheet was prepared in the same manner as described in the above paragraph (a), except that 60 parts of an indophenol type dye of the following structural formula was used. By using the thermal dye transfer sheet thus prepared, a cyan color printed matter was obtained by conducting thermal dye transfer recording on the image-receiving sheet obtained in the above paragraph (b) under the same printing conditions as described in the above paragraph (c). On the cyan color printed matter, thermal dye transfer recording was conducted by using the thermal dye transfer sheet obtained in the above paragraph (a) under the same printing conditions as described in the above paragraph (c) to obtain a green color printed matter. The green color printed matter thus obtained was subjected to a light-resistance test under the same conditions as described in the above paragraph (e), and a chrominance was measured before and after the light-resistance test by using the same chrominance-meter under the same color difference in conditions as mentioned above. As this result, the color difference in CIELAB color system was small and its measured value was 12.0. Also, a printed matter printed by cyan color only was subjected to the same light-resistance test under the same conditions, and at this result, the color differences in CIELAB color system was small and its measured value (ΔEab*) was 8.0. <chemistry id="chem0009" num="0009"><img file="EP0802065A2_D0009.tif" /></chemistry>

(g) Shelf stability test

0130The thermal dye transfer sheet obtained in the above paragraph (a) was stored for one week under conditions of 40°C and a relative humidity of 80%, and was subjected to the printing test in the above paragraph (c). Thereafter, a density change of the printed matter before and after storing was measured, and was expressed by %. As this result, the density change was -5% and was proved to be very small.

EXAMPLES 9 TO 14

0131The same procedure as in Example 8 was repeated, except that such combinations of dyes as shown in the following Table 1 were used, and their results are shown in the following Table 2. Any of these Examples shows a satisfactorily high density and a satisfactory light-resistance. <tables id="tabl0006" num="0006"><table frame="all"><title>Table 1</title><tgroup cols="5" colsep="1" rowsep="1"><colspec colnum="1" colname="col1" colwidth="31.50mm" /><colspec colnum="2" colname="col2" colwidth="31.50mm" /><colspec colnum="3" colname="col3" colwidth="31.50mm" /><colspec colnum="4" colname="col4" colwidth="31.50mm" /><colspec colnum="5" colname="col5" colwidth="31.50mm" /><thead valign="top"><row><entry namest="col1" nameend="col1" /><entry namest="col2" nameend="col3" align="center">Pyrazolonemethine type dye</entry><entry namest="col4" nameend="col5" align="center">Quinophthalone type dye</entry></row></thead><tbody valign="top"><row><entry namest="col1" nameend="col1" align="left">Example 8</entry><entry namest="col2" nameend="col2" align="left">Dye No. 1-1</entry><entry namest="col3" nameend="col3" align="right">50 parts</entry><entry namest="col4" nameend="col4" align="left">Dye No. 3-1</entry><entry namest="col5" nameend="col5" align="right">50 parts</entry></row><row><entry namest="col1" nameend="col1" align="left">Example 9</entry><entry namest="col2" nameend="col2" align="left">Dye No. 1-2</entry><entry namest="col3" nameend="col3" align="right">60 parts</entry><entry namest="col4" nameend="col4" align="left">Dye No. 3-2</entry><entry namest="col5" nameend="col5" align="right">40 parts</entry></row><row><entry namest="col1" nameend="col1" align="left">Example 10</entry><entry namest="col2" nameend="col2" align="left">Dye No. 1-6</entry><entry namest="col3" nameend="col3" align="right">50 parts</entry><entry namest="col4" nameend="col4" align="left">Dye No. 3-3</entry><entry namest="col5" nameend="col5" align="right">40 parts</entry></row><row><entry namest="col1" nameend="col1" align="left">Example 11</entry><entry namest="col2" nameend="col2" align="left">Dye No. 1-4</entry><entry namest="col3" nameend="col3" align="right">60 parts</entry><entry namest="col4" nameend="col4" align="left">Dye No. 3-4</entry><entry namest="col5" nameend="col5" align="right">30 parts</entry></row><row><entry namest="col1" nameend="col1" align="left">Example 12</entry><entry namest="col2" nameend="col2" align="left">Dye No. 1-5</entry><entry namest="col3" nameend="col3" align="right">45 parts</entry><entry namest="col4" nameend="col4" align="left">Dye No. 3-5</entry><entry namest="col5" nameend="col5" align="right">45 parts</entry></row><row rowsep="0"><entry namest="col1" nameend="col1" morerows="1" rowsep="1" align="left">Example 13</entry><entry namest="col2" nameend="col2" morerows="1" rowsep="1" align="left">Dye No. 1-3</entry><entry namest="col3" nameend="col3" morerows="1" rowsep="1" align="right">35 parts</entry><entry namest="col4" nameend="col4" align="left">Dye No. 3-6</entry><entry namest="col5" nameend="col5" align="right">20 parts</entry></row><row><entry namest="col4" nameend="col4" align="left">Dye No. 3-7</entry><entry namest="col5" nameend="col5" align="right">30 parts</entry></row><row rowsep="0"><entry namest="col1" nameend="col1" morerows="1" rowsep="1" align="left">Example 14</entry><entry namest="col2" nameend="col2" morerows="1" rowsep="1" align="left">Dye No. 1-7</entry><entry namest="col3" nameend="col3" morerows="1" rowsep="1" align="right">40 parts</entry><entry namest="col4" nameend="col4" align="left">Dye No. 3-8</entry><entry namest="col5" nameend="col5" align="right">35 parts</entry></row><row rowsep="1"><entry namest="col4" nameend="col4" align="left">Dye No. 3-9</entry><entry namest="col5" nameend="col5" align="right">35 parts</entry></row></tbody></tgroup></table></tables>

0132Dyes 1-1 to 1-7 used in respective Examples are pyrazolonemethine type dyes having the following structural formulas, and Dyes 3-1 to 3-9 are quinophthalone type dyes having the following structural formulas. <chemistry id="chem0010" num="0010"><img file="EP0802065A2_D0010.tif" /></chemistry><chemistry id="chem0011" num="0011"><img file="EP0802065A2_D0011.tif" /></chemistry><chemistry id="chem0012" num="0012"><img file="EP0802065A2_D0012.tif" /></chemistry><chemistry id="chem0013" num="0013"><img file="EP0802065A2_D0013.tif" /></chemistry>

EXAMPLES 15 TO 17

0133The same procedure as in Example 8 was repeated (light-resistance test was omitted), except that the phenoxy resin (tradename: PKHH manufactured by Union Carbide Co.) used as a binder resin in the dye layer of Example 8 was replaced by the following resins. The results are shown in the following Table 2. <ul id="ul0002" list-style="none" compact="compact"><li>Example 15: Polyvinylbutyral resin (tradename: BX-1 manufactured by Sekisui Kagaku K.K.)</li><li>Example 16: Vinylchloride-vinylacetate resin (tradename: VYHD manufactured by Union Carbide Co.)</li><li>Example 17: AS resin (tradename: SEBIAN-N020 manufactured by Disel Kagaku Kogyo K.K.)</li></ul>

COMPARATIVE EXAMPLE 1

0134The same procedure as in Example 8 was repeated, except that 0 part of Dye 1-1 and 90 parts of Dye 3-1 were used. Since a coating solution for a dye layer becomes heterogeneous due to poor solubility of the dye, a solvent amount was 1.5 times increased for coating. The dried dye layer thus coated was opaque, and was proved to have many crystals of Dye 3-1 precipitated according to observation by a microscope. An optical density was low and its measured value was 1.4. From this result, it was proved to be difficult to improve a density by increasing the dye content of Dye 3-1 in the dye layer. With regard to a light-resistance, a measured color difference (ΔEab*) of monocolor was 5.0 and a color difference (ΔEab*) of mixed color (green) was 12.0, which proved satisfactory results. These results are shown in the following Table 2.

COMPARATIVE EXAMPLE 2

0135The same procedure as in Example 8 was repeated, except that 0 part of Dye 1-1 and 50 parts of Dye 3-1 were used. The dried dye layer thus obtained was transparent. According to observation by a microscope, there was no crystal of Dye 3-1. An optical density was 1.2 and was low and unsatisfactory. The light-resistance result was satisfactory. Judging from Comparative Examples 1 and 2, it was proved to be difficult to maintain both a high density and a high shelf stability in the case of using a quinophthalone type dye alone. The results are shown in the following Table 2.

COMPARATIVE EXAMPLE 3

0136The same procedure as in Example 8 was repeated, except that 100 parts of Dye 1-1 and 0 part of Dye 3-1 were used. An optical density was 1.9. With regard to the light-resistance, a chrominance value of monocolor was 7.0 and a chrominance value of mixed color (green) was 16.0, thus providing satisfactory results. The shelf stability was -20%, and was proved to be unsatisfactory. This is probably due to unsatisfactory solubility of Dye 1-1 since there were observed many crystals of Dye 1-1 in the dye layer by a microscope. The results are shown in the following Table 2.

COMPARATIVE EXAMPLE 4

0137The same procedure as in Example 8 was repeated, except that 60 parts of Dye 1-1 and 0 part of Dye 3-1 were used. An optical density was 1.5. With regard to the light-resistance, a chrominance value of monocolor was 7.0 and a chrominance value of mixed color (green) was 16.0, thus providing satisfactory results. The shelf stability was -5%, and was proved to be satisfactory. Judging from Comparative Examples 3 and 4, it was proved to be difficult to maintain both a high density and a satisfactory shelf stability by using a pyrazolonemethine type dye alone. The results are shown in the following Table 2.

COMPARATIVE EXAMPLE 5

0138The same procedure as in Example 8 was repeated, except that 50 parts of Dye 3-1 and 50 parts of pyridone type dye of the following structural formula were used. An optical density was 1.9, and was proved to be satisfactory. With regard to the light-resistance, a measured color difference (ΔEab*) of monocolor was 16.0 and a measured color difference (ΔEab*) of mixed color (green) was 30.0, thus providing unsatisfactory results. This is not only due to the unsatisfactory light-resistance of monocolor but also due to the degradation of the light-resistance of green color by catalytic fading phenomenon. The results are shown in the following Table 2. <chemistry id="chem0014" num="0014"><img file="EP0802065A2_D0014.tif" /></chemistry>

COMPARATIVE EXAMPLE 6

0139The same procedure as in Example 8 was repeated, except that 50 parts of a quinophthalone type dye of the following structural formula which corresponds to a dye of the formula (4) wherein all of R¹¹, R¹² and R¹³ are hydrogen atoms and 50 parts of the pyridone type dye used in Comparative Example 5, were used. An optical density was 1.5, and was proved to be unsatisfactory. With regard to the light-resistance, a measured color difference (ΔEab*) of monocolor was 16.0, and a measured color difference (ΔEab*) of mixed color (green) was 30.0, thus providing unsatisfactory results. This is not only due to the unsatisfactory light-resistance of monocolor but also due to the degradation of the light-resistance of green color by catalytic fading phenomenon. The shelf stability was -15%. The results are shown in the following Table 2. <chemistry id="chem0015" num="0015"><img file="EP0802065A2_D0015.tif" /></chemistry>

COMPARATIVE EXAMPLE 7

0140The same procedure as in Example 8 was repeated, except that 50 parts of Dye 3-2 and 50 parts of a styryl type dye of the following structural formula were used. An optical density was 2.3, and was satisfactory. With regard to the light-resistance, a measured color difference (ΔEab*) of monocolor was 20.0, and a measured color difference (ΔEab*) of mixed color (green) was 45.0, thus providing unsatisfactory results. This is not only due to the unsatisfactory light-resistance of monocolor but also due to the degradation of the light-resistance of green color by catalytic fading phenomenon. The shelf stability was -5%. The results are shown in the following Table 2. <chemistry id="chem0016" num="0016"><img file="EP0802065A2_D0016.tif" /></chemistry>

COMPARATIVE EXAMPLE 8

0141The same procedure as in Example 8 was repeated, except that 50 parts of Dye 1-1 and 50 parts of a pyridone type dye used in Comparative Example 5 were used. An optical density was 1.5, and was proved to be unsatisfactory. With regard to the light-resistance, a measured color difference (ΔEab*) of monocolor was 12.0, and a measured color difference (ΔEab*) of mixed color (green) was 24.0, thus providing unsatisfactory results. This is not only due to the unsatisfactory light-resistance of monocolor but also due to the degradation of the light-resistance of green color by catalytic fading phenomenon. The shelf stability was -5%. The results are shown in the following Table 2.

COMPARATIVE EXAMPLE 9

0142The same procedure as in Example 8 was repeated, except that 50 parts of Dye 3-2 and 50 parts of a pyrazoloneazo type dye having the following structural formula were used. An optical density was 1.9, and was proved to be satisfactory. With regard to the light-resistance, a color difference (ΔEab*) of monocolor was 15.0, and a color difference (ΔEab*) of mixed color (green) was 30.0, thus providing unsatisfactory results. This is not only due to the unsatisfactory light-resistance of monocolor but also due to the degradation of the light-resistance of green color by catalytic fading phenomenon. The shelf stability was -5%. The results are shown in the following Table 2. <chemistry id="chem0017" num="0017"><img file="EP0802065A2_D0017.tif" /></chemistry><tables id="tabl0007" num="0007"><table frame="all"><title>Table 2</title><tgroup cols="5" colsep="1" rowsep="0"><colspec colnum="1" colname="col1" colwidth="31.50mm" /><colspec colnum="2" colname="col2" colwidth="31.50mm" /><colspec colnum="3" colname="col3" colwidth="31.50mm" /><colspec colnum="4" colname="col4" colwidth="31.50mm" /><colspec colnum="5" colname="col5" colwidth="31.50mm" /><thead valign="top"><row rowsep="1"><entry namest="col1" nameend="col1" /><entry namest="col2" nameend="col2" align="center">Optical Density</entry><entry namest="col3" nameend="col3" align="center">Light-resistance (yellow) (ΔEab*)</entry><entry namest="col4" nameend="col4" align="center">Light-resistance (green) (ΔEab*)</entry><entry namest="col5" nameend="col5" align="center">Shelf stability</entry></row></thead><tbody valign="top"><row><entry namest="col1" nameend="col1" align="left">Example 8</entry><entry namest="col2" nameend="col2" align="char" char=".">1.9</entry><entry namest="col3" nameend="col3" align="center">6.0</entry><entry namest="col4" nameend="col4" align="char" char=".">13.0</entry><entry namest="col5" nameend="col5" align="center">-5%</entry></row><row><entry namest="col1" nameend="col1" align="left">Example 9</entry><entry namest="col2" nameend="col2" align="char" char=".">1.9</entry><entry namest="col3" nameend="col3" align="center">6.5</entry><entry namest="col4" nameend="col4" align="char" char=".">14.0</entry><entry namest="col5" nameend="col5" align="center">-5%</entry></row><row><entry namest="col1" nameend="col1" align="left">Example 10</entry><entry namest="col2" nameend="col2" align="char" char=".">1.7</entry><entry namest="col3" nameend="col3" align="center">6.0</entry><entry namest="col4" nameend="col4" align="char" char=".">13.0</entry><entry namest="col5" nameend="col5" align="center">-5%</entry></row><row><entry namest="col1" nameend="col1" align="left">Example 11</entry><entry namest="col2" nameend="col2" align="char" char=".">1.7</entry><entry namest="col3" nameend="col3" align="center">7.0</entry><entry namest="col4" nameend="col4" align="char" char=".">15.0</entry><entry namest="col5" nameend="col5" align="center">-10%</entry></row><row><entry namest="col1" nameend="col1" align="left">Example 12</entry><entry namest="col2" nameend="col2" align="char" char=".">1.6</entry><entry namest="col3" nameend="col3" align="center">6.0</entry><entry namest="col4" nameend="col4" align="char" char=".">13.0</entry><entry namest="col5" nameend="col5" align="center">-5%</entry></row><row><entry namest="col1" nameend="col1" align="left">Example 13</entry><entry namest="col2" nameend="col2" align="char" char=".">1.9</entry><entry namest="col3" nameend="col3" align="center">5.5</entry><entry namest="col4" nameend="col4" align="char" char=".">13.0</entry><entry namest="col5" nameend="col5" align="center">-5%</entry></row><row><entry namest="col1" nameend="col1" align="left">Example 14</entry><entry namest="col2" nameend="col2" align="char" char=".">1.7</entry><entry namest="col3" nameend="col3" align="center">5.5</entry><entry namest="col4" nameend="col4" align="char" char=".">13.0</entry><entry namest="col5" nameend="col5" align="center">-5%</entry></row><row><entry namest="col1" nameend="col1" align="left">Example 15</entry><entry namest="col2" nameend="col2" align="char" char=".">1.9</entry><entry namest="col3" nameend="col3" align="center">-</entry><entry namest="col4" nameend="col4" align="char" char=".">-</entry><entry namest="col5" nameend="col5" align="center">-5%</entry></row><row><entry namest="col1" nameend="col1" align="left">Example 16</entry><entry namest="col2" nameend="col2" align="char" char=".">1.8</entry><entry namest="col3" nameend="col3" align="center">-</entry><entry namest="col4" nameend="col4" align="char" char=".">-</entry><entry namest="col5" nameend="col5" align="center">-5%</entry></row><row><entry namest="col1" nameend="col1" align="left">Example 17</entry><entry namest="col2" nameend="col2" align="char" char=".">1.7</entry><entry namest="col3" nameend="col3" align="center">-</entry><entry namest="col4" nameend="col4" align="char" char=".">-</entry><entry namest="col5" nameend="col5" align="center">-5%</entry></row><row><entry namest="col1" nameend="col1" align="left">Comparative Example 1</entry><entry namest="col2" nameend="col2" align="char" char=".">1.4</entry><entry namest="col3" nameend="col3" align="center">5.0</entry><entry namest="col4" nameend="col4" align="char" char=".">12.0</entry><entry namest="col5" nameend="col5" align="center">-30%</entry></row><row><entry namest="col1" nameend="col1" align="left">Comparative Example 2</entry><entry namest="col2" nameend="col2" align="char" char=".">1.2</entry><entry namest="col3" nameend="col3" align="center">4.5</entry><entry namest="col4" nameend="col4" align="char" char=".">11.0</entry><entry namest="col5" nameend="col5" align="center">-5%</entry></row><row><entry namest="col1" nameend="col1" align="left">Comparative Example 3</entry><entry namest="col2" nameend="col2" align="char" char=".">1.9</entry><entry namest="col3" nameend="col3" align="center">7.0</entry><entry namest="col4" nameend="col4" align="char" char=".">17.0</entry><entry namest="col5" nameend="col5" align="center">-20%</entry></row><row><entry namest="col1" nameend="col1" align="left">Comparative Example 4</entry><entry namest="col2" nameend="col2" align="char" char=".">1.5</entry><entry namest="col3" nameend="col3" align="center">7.0</entry><entry namest="col4" nameend="col4" align="char" char=".">17.0</entry><entry namest="col5" nameend="col5" align="center">-5%</entry></row><row><entry namest="col1" nameend="col1" align="left">Comparative Example 5</entry><entry namest="col2" nameend="col2" align="char" char=".">1.9</entry><entry namest="col3" nameend="col3" align="center">16.0</entry><entry namest="col4" nameend="col4" align="char" char=".">30.0</entry><entry namest="col5" nameend="col5" align="center">-5%</entry></row><row><entry namest="col1" nameend="col1" align="left">Comparative Example 6</entry><entry namest="col2" nameend="col2" align="char" char=".">1.5</entry><entry namest="col3" nameend="col3" align="center">16.0</entry><entry namest="col4" nameend="col4" align="char" char=".">30.0</entry><entry namest="col5" nameend="col5" align="center">-15%</entry></row><row><entry namest="col1" nameend="col1" align="left">Comparative Example 7</entry><entry namest="col2" nameend="col2" align="char" char=".">2.3</entry><entry namest="col3" nameend="col3" align="center">20.0</entry><entry namest="col4" nameend="col4" align="char" char=".">45.0</entry><entry namest="col5" nameend="col5" align="center">-5%</entry></row><row><entry namest="col1" nameend="col1" align="left">Comparative Example 8</entry><entry namest="col2" nameend="col2" align="char" char=".">2.0</entry><entry namest="col3" nameend="col3" align="center">12.0</entry><entry namest="col4" nameend="col4" align="char" char=".">24.0</entry><entry namest="col5" nameend="col5" align="center">-5%</entry></row><row rowsep="1"><entry namest="col1" nameend="col1" align="left">Comparative Example 9</entry><entry namest="col2" nameend="col2" align="char" char=".">1.9</entry><entry namest="col3" nameend="col3" align="center">15.0</entry><entry namest="col4" nameend="col4" align="char" char=".">30.0</entry><entry namest="col5" nameend="col5" align="center">-5%</entry></row></tbody></tgroup></table></tables>

EXAMPLE 18

(a) Preparation of thermal cyan dye transfer sheet

0143An ink obtained by mixing and stirring 80 parts of Dye 4-1 (dye of the formula (6) wherein -B- is -COO-, and R¹⁷ , R¹⁸ and R¹⁹ are ethyl groups, and R²⁰ is a chlorine atom, and R²¹ and R²² are methyl groups), 100 parts of phenoxy resin (tradename: PKHH manufactured by Union Carbide Co.), 125 parts of methyl ethyl ketone, 450 parts of toluene and 300 parts of tetrahydrofuran (THF), was coated and dried on a polyester film of 6 µm by a bar coater so as to provide a dry film thickness of 1 µm, thereby forming a cyan dye layer.

0144On the back side of the sheet thus obtained, was coated a mixture solution of 10 parts by weight of acrylic resin (tradename: BR-100 manufactured by Mitsubishi Rayon K.K.), 1 part by weight of amino-modified silicone oil (tradename: KF 393 manufactured by Shin-Etsu Kagaku K.K.) and 89 parts by weight of toluene by a bar coater to provide a dry film thickness of 1 µm, thus providing a heat-resistant layer.

(b) Preparation of thermal yellow dye transfer sheet

0145An ink obtained by mixing and stirring 90 parts of Dye 1-1 (dye of the formula (1) wherein R¹ and R² are phenyl groups and R³ and R⁴ are methyl groups), 100 parts of phenoxy resin (tradename: PKHH manufactured by Union Carbide Co.), 125 parts of methyl ethyl ketone, 450 parts of toluene and 300 parts of tetrahydrofuran (THF), was coated on a polyester film of 6 µm by a bar coater, and dried so as to provide a dry film thickness of 1 µm, thereby forming a yellow dye layer.

0146In the same manner as in the above paragraph (a), on the back side of the sheet thus obtained, was coated a mixture solution of 10 parts by weight of acrylic resin (tradename: BR-100 manufactured by Mitsubishi Rayon K.K.), 1 part by weight of amino-modified silicone oil (tradename: KF 393 manufactured by Shin-Etsu Kagaku K.K.) and 89 parts by weight of toluene by a bar coater, so as to provide a dry film thickness of 1 µm, thus providing a heat-resistant lubricating layer.

(c) Preparation of image-receiving sheet

0147A solution obtained by mixing and stirring 70 parts of polyvinylphenylacetal resin, 25 parts of vinylchloride/vinyl acetate/vinyl alcohol copolymer resin (tradename: Esrec A manufactured by Sekisui Kagaku K.K.), 40 parts of modified silicone varnish (tradename: TSR-160 (solid content concentration 60%) manufactured by Toshiba Silicone K.K.), 3 parts of amino-modified silicone oil (tradename: KF 393 manufactured by Shin-Etsu Kagaku K.K.), 10 parts of a hexamethylene diisocyanate type polyfunctional isocyanate compound (tradename: Mitech NY-710A (solid content concentration 75%) manufactured by Mitsubishi Chemical Co.), 500 parts of methyl ethyl ketone and 500 parts of toluene, was coated on a polypropylene-made synthetic paper of a thickness of 150 µm (tradename: Yupo FPG150 manufactured by Oji Yuka Goseishi K.K.) by a wire bar, and dried (dry film thickness about 5 µm), and was further heat-treated in an oven at 80°C for 12 hours to obtain an image-receiving sheet.

0148The above polyvinylphenylacetal resin was obtained by acetalizing polyvinyl alcohol (saponification value 99 mol%, polymerization degree: 1,700) with phenylacetaldehyde, and had a structure of the above-mentioned structural formula (1).

(d) Print recording

0149The dye layer of each of the thermal dye transfer sheets prepared as described in the above paragraphs (a) and (b) was brought into contact with the resin coating surface of the image-receiving sheet prepared as described in the above paragraph (c), and printing was made by using a part glaze type line thermal head having a density of 5.6 dots/mm under conditions of a conveying speed of 6 lines (dots)/mm in the conveying direction, a printing speed of 16.6 ms/line and an applied electric power of 0.20 W/dot. The time applied to the head per line for printing was 12 ms. By this method, a cyan-printed matter and a yellow-printed matter were obtained, and a green color-printed matter was obtained by over printing a cyan color on a yellow-printed matter.

(e) Measurement of density and color

0150A deep color density of the printed matter printed as described in the above paragraph (d) was measured by a reflective densitometer (tradename: Macbeth RD-920 type containing a filter having a SPI spectral sensitivity, manufactured by Macbeth Co.). As this result, an optical density of the cyan-printed matter was 2.0 and an optical density of the yellow-printed matter was 1.6.

0151Further, a chrominance value of each color was measured by using a chrominance-meter having an optical system in accordance with JIS Z-8722 (tradename: Spectral chrominance-meter SZ-Σ80 manufactured by Nihon Denshi Kogyo K.K.) under conditions of a C-light source and a visual field angle of 2°, and the measured value was expressed by CIELAB color system.

(f) Weather-resistance test

0152A deep color sample of the printed matter printed as described in the above paragraph (d) was subjected to a light-resistance test for 48 hours at an illuminance of 3.5 kw/m² by using a xenon lamp light-resistance tester (tradename: Atlas Ci35A Weatherometer manufactured by Toyo Seiki Seisakusho K.K.). A chrominance value of the printed matter was measured before and after the light-resistance test by using the same chrominance-meter under the same conditions as used in the above paragraph (e). A color difference (ΔEab*) in CIELAB color system was 8.0 with regard to the cyan color, 5.0 with regard to the yellow color and 11.0 with regard to the green color. Thus, the measured color differences were satisfactorily small.

EXAMPLES 19 TO 25

0153The same test as in Example 18 was repeated, except that such combinations of dyes as shown in the following Table 3 were used in place of the combination of dyes used in Example 18. The results are shown in the following Table 4. It was proved from these results that the density was satisfactorily high and the light-resistance was also satisfactory. <tables id="tabl0008" num="0008"><table frame="all"><title>Table 3</title><tgroup cols="5" colsep="1" rowsep="0"><colspec colnum="1" colname="col1" colwidth="31.50mm" /><colspec colnum="2" colname="col2" colwidth="31.50mm" /><colspec colnum="3" colname="col3" colwidth="31.50mm" /><colspec colnum="4" colname="col4" colwidth="31.50mm" /><colspec colnum="5" colname="col5" colwidth="31.50mm" /><thead valign="top"><row rowsep="1"><entry namest="col1" nameend="col1" /><entry namest="col2" nameend="col3" align="center">Pyrazolonemethine type dye</entry><entry namest="col4" nameend="col5" align="center">Indoaniline type dye</entry></row></thead><tbody valign="top"><row><entry namest="col1" nameend="col1" align="left">Example 18</entry><entry namest="col2" nameend="col2" align="left">Dye No. 1-1</entry><entry namest="col3" nameend="col3" align="right">90 parts</entry><entry namest="col4" nameend="col4" align="left">Dye No. 4-1</entry><entry namest="col5" nameend="col5" align="right">80 parts</entry></row><row><entry namest="col1" nameend="col1" align="left">Example 19</entry><entry namest="col2" nameend="col2" align="left">Dye No. 1-2</entry><entry namest="col3" nameend="col3" align="right">80 parts</entry><entry namest="col4" nameend="col4" align="left">Dye No. 4-2</entry><entry namest="col5" nameend="col5" align="right">80 parts</entry></row><row><entry namest="col1" nameend="col1" align="left">Example 20</entry><entry namest="col2" nameend="col2" align="left">Dye No. 1-5</entry><entry namest="col3" nameend="col3" align="right">90 parts</entry><entry namest="col4" nameend="col4" align="left">Dye No. 4-3</entry><entry namest="col5" nameend="col5" align="right">80 parts</entry></row><row><entry namest="col1" nameend="col1" align="left">Example 21</entry><entry namest="col2" nameend="col2" align="left">Dye No. 1-7</entry><entry namest="col3" nameend="col3" align="right">80 parts</entry><entry namest="col4" nameend="col4" align="left">Dye No. 4-4</entry><entry namest="col5" nameend="col5" align="right">90 parts</entry></row><row><entry namest="col1" nameend="col1" align="left">Example 22</entry><entry namest="col2" nameend="col2" align="left">Dye No. 1-3</entry><entry namest="col3" nameend="col3" align="right">100 parts</entry><entry namest="col4" nameend="col4" align="left">Dye No. 4-5</entry><entry namest="col5" nameend="col5" align="right">70 parts</entry></row><row><entry namest="col1" nameend="col1" align="left">Example 23</entry><entry namest="col2" nameend="col2" align="left">Dye No. 1-6</entry><entry namest="col3" nameend="col3" align="right">80 parts</entry><entry namest="col4" nameend="col4" align="left">Dye No. 4-6</entry><entry namest="col5" nameend="col5" align="right">80 parts</entry></row><row><entry namest="col1" nameend="col1" align="left">Example 24</entry><entry namest="col2" nameend="col2" align="left">Dye No. 1-4</entry><entry namest="col3" nameend="col3" align="right">90 parts</entry><entry namest="col4" nameend="col4" align="left">Dye No. 4-7</entry><entry namest="col5" nameend="col5" align="right">90 parts</entry></row><row rowsep="1"><entry namest="col1" nameend="col1" align="left">Example 25</entry><entry namest="col2" nameend="col2" align="left">Dye No. 1-1</entry><entry namest="col3" nameend="col3" align="right">90 parts</entry><entry namest="col4" nameend="col4" align="left">Dye No. 4-8</entry><entry namest="col5" nameend="col5" align="right">80 parts</entry></row></tbody></tgroup></table></tables>

0154Dyes 4-1 to 4-8 used in respective Examples are indoaniline type dyes having the following structural formulas. <chemistry id="chem0018" num="0018"><img file="EP0802065A2_D0018.tif" /></chemistry><chemistry id="chem0019" num="0019"><img file="EP0802065A2_D0019.tif" /></chemistry>

COMPARATIVE EXAMPLE 10

0155The same test as in Example 18 was repeated, except that an anthraquinone type cyan dye of the following structural formula was used in place of Dye 4-1 used in the paragraph (a) of Example 18. An optical density was 1.5 and was proved to be unsatisfactorily low. The light-resistance was also unsatisfactory. The results are shown in the following Table 4. <chemistry id="chem0020" num="0020"><img file="EP0802065A2_D0020.tif" /></chemistry>

Comparative Example 11

0156The same test as in Example 18 was repeated, except that 70 parts of a styryl type dye of the following structural formula was used in place of Dye 1-1 used in the paragraph (b) of Example 18. The transferred density of yellow color was satisfactorily high, but the light-resistance, particularly the light-resistance of green color was unsatisfactory. This is considered to be due to the influence by catalytic fading phenomenon. The results are shown in the following Table 4. <chemistry id="chem0021" num="0021"><img file="EP0802065A2_D0021.tif" /></chemistry>

COMPARATIVE EXAMPLE 12

0157The same test as in Example 18 was repeated, except that a quinophthalone type yellow dye of the following structural formula was used in place of Dye 1-1 used in the paragraph (b) of Example 18. At this time, since it was proved that a solubility of the dye in a coating solution for a dye layer was insufficient, a solvent was added and the transparent coating solution thus prepared was coated to form a dye layer. The dye layer thus formed was opaque and precipitation of the dye was recognized. The transferred yellow density was unsatisfactory. The results are shown in the following Table 4. <chemistry id="chem0022" num="0022"><img file="EP0802065A2_D0022.tif" /></chemistry>

COMPARATIVE EXAMPLE 13

0158The same test as in Example 18 was repeated, except that Dye 4-1 used in the paragraph (a) of Example 18 was replaced by an indoaniline type dye of the formula (6) (-B- is -CO-, R¹⁷ is a pentyl group, R¹⁸ and R¹⁹ are ethyl groups, R²⁰ is a chlorine atom, R²¹ is a methyl group and R²² is a hydrogen atom) and Dye 1-1 used in the above paragraph (b) was replaced by a quinophthalone type yellow dye of the following structural formula. In the cyan dye layer, the dye was slightly precipitated. Since the quinophthalone type yellow dye was proved to be poor in solubility in a dye layer coating solution, a solvent was added thereto to prepare a transparent coating solution which was then coated to form a dye layer. The dye layer thus formed was opaque, and precipitation of the dye was recognized. The transferred yellow density was unsatisfactory. The results are shown in the following Table 4.

0159This combination of the dyes is the same combination as used in Example 1-4 of JP-A-63-71393. <chemistry id="chem0023" num="0023"><img file="EP0802065A2_D0023.tif" /></chemistry>

COMPARATIVE EXAMPLE 14

0160The same test as in Example 18 was repeated, except that a pyridone azo type yellow dye of the following structural formula was used in place of Dye 1-1 used in the paragraph (b) of Example 18. The yellow density was 2.1 and was proved to be satisfactorily high. With regard to the light-resistance, a measured color difference (ΔEab*) of mixed color (green) was 24.0, thus providing an unsatisfactory result. It is considered that this is not only due to the unsatisfactory light-resistance of monocolor but also due to the degradation of the light-resistance of green color by catalytic fading phenomenon. <chemistry id="chem0024" num="0024"><img file="EP0802065A2_D0024.tif" /></chemistry><tables id="tabl0009" num="0009"><table frame="all"><title>Table 4</title><tgroup cols="6" colsep="1" rowsep="0"><colspec colnum="1" colname="col1" colwidth="26.25mm" /><colspec colnum="2" colname="col2" colwidth="26.25mm" /><colspec colnum="3" colname="col3" colwidth="26.25mm" /><colspec colnum="4" colname="col4" colwidth="26.25mm" /><colspec colnum="5" colname="col5" colwidth="26.25mm" /><colspec colnum="6" colname="col6" colwidth="26.25mm" /><thead valign="top"><row rowsep="1"><entry namest="col1" nameend="col3" align="center">Density (OD)</entry><entry namest="col4" nameend="col6" align="center">Light-resistance (ΔE)</entry></row><row rowsep="1"><entry namest="col1" nameend="col1" /><entry namest="col2" nameend="col2" align="center">Cyan</entry><entry namest="col3" nameend="col3" align="center">Yellow</entry><entry namest="col4" nameend="col4" align="center">Cyan</entry><entry namest="col5" nameend="col5" align="center">Yellow</entry><entry namest="col6" nameend="col6" align="center">Green</entry></row></thead><tbody valign="top"><row><entry namest="col1" nameend="col1" align="left">Example 18</entry><entry namest="col2" nameend="col2" align="char" char=".">2.0</entry><entry namest="col3" nameend="col3" align="char" char=".">1.7</entry><entry namest="col4" nameend="col4" align="center">8.0</entry><entry namest="col5" nameend="col5" align="center">5.0</entry><entry namest="col6" nameend="col6" align="char" char=".">11.0</entry></row><row><entry namest="col1" nameend="col1" align="left">Example 19</entry><entry namest="col2" nameend="col2" align="char" char=".">2.1</entry><entry namest="col3" nameend="col3" align="char" char=".">1.8</entry><entry namest="col4" nameend="col4" align="center">8.0</entry><entry namest="col5" nameend="col5" align="center">5.0</entry><entry namest="col6" nameend="col6" align="char" char=".">10.0</entry></row><row><entry namest="col1" nameend="col1" align="left">Example 20</entry><entry namest="col2" nameend="col2" align="char" char=".">1.8</entry><entry namest="col3" nameend="col3" align="char" char=".">1.6</entry><entry namest="col4" nameend="col4" align="center">9.0</entry><entry namest="col5" nameend="col5" align="center">5.0</entry><entry namest="col6" nameend="col6" align="char" char=".">12.0</entry></row><row><entry namest="col1" nameend="col1" align="left">Example 21</entry><entry namest="col2" nameend="col2" align="char" char=".">2.2</entry><entry namest="col3" nameend="col3" align="char" char=".">1.6</entry><entry namest="col4" nameend="col4" align="center">9.0</entry><entry namest="col5" nameend="col5" align="center">6.0</entry><entry namest="col6" nameend="col6" align="char" char=".">12.0</entry></row><row><entry namest="col1" nameend="col1" align="left">Example 22</entry><entry namest="col2" nameend="col2" align="char" char=".">2.2</entry><entry namest="col3" nameend="col3" align="char" char=".">1.8</entry><entry namest="col4" nameend="col4" align="center">7.0</entry><entry namest="col5" nameend="col5" align="center">7.0</entry><entry namest="col6" nameend="col6" align="char" char=".">11.0</entry></row><row><entry namest="col1" nameend="col1" align="left">Example 23</entry><entry namest="col2" nameend="col2" align="char" char=".">2.4</entry><entry namest="col3" nameend="col3" align="char" char=".">1.6</entry><entry namest="col4" nameend="col4" align="center">7.0</entry><entry namest="col5" nameend="col5" align="center">5.0</entry><entry namest="col6" nameend="col6" align="char" char=".">10.0</entry></row><row><entry namest="col1" nameend="col1" align="left">Example 24</entry><entry namest="col2" nameend="col2" align="char" char=".">2.2</entry><entry namest="col3" nameend="col3" align="char" char=".">1.8</entry><entry namest="col4" nameend="col4" align="center">8.0</entry><entry namest="col5" nameend="col5" align="center">5.0</entry><entry namest="col6" nameend="col6" align="char" char=".">10.0</entry></row><row><entry namest="col1" nameend="col1" align="left">Example 25</entry><entry namest="col2" nameend="col2" align="char" char=".">1.5</entry><entry namest="col3" nameend="col3" align="char" char=".">1.7</entry><entry namest="col4" nameend="col4" align="center">11.0</entry><entry namest="col5" nameend="col5" align="center">5.0</entry><entry namest="col6" nameend="col6" align="char" char=".">15.0</entry></row><row><entry namest="col1" nameend="col1" align="left">Comparative Example 10</entry><entry namest="col2" nameend="col2" align="char" char=".">1.5</entry><entry namest="col3" nameend="col3" align="char" char=".">1.7</entry><entry namest="col4" nameend="col4" align="center">15.0</entry><entry namest="col5" nameend="col5" align="center">5.0</entry><entry namest="col6" nameend="col6" align="char" char=".">20.0</entry></row><row><entry namest="col1" nameend="col1" align="left">Comparative Example 11</entry><entry namest="col2" nameend="col2" align="char" char=".">2.0</entry><entry namest="col3" nameend="col3" align="char" char=".">2.4</entry><entry namest="col4" nameend="col4" align="center">8.0</entry><entry namest="col5" nameend="col5" align="center">20.0</entry><entry namest="col6" nameend="col6" align="char" char=".">40.0</entry></row><row><entry namest="col1" nameend="col1" align="left">Comparative Example 12</entry><entry namest="col2" nameend="col2" align="char" char=".">2.0</entry><entry namest="col3" nameend="col3" align="char" char=".">1.4</entry><entry namest="col4" nameend="col4" align="center">8.0</entry><entry namest="col5" nameend="col5" align="center">3.0</entry><entry namest="col6" nameend="col6" align="char" char=".">10.0</entry></row><row><entry namest="col1" nameend="col1" align="left">Comparative Example 13</entry><entry namest="col2" nameend="col2" align="char" char=".">1.8</entry><entry namest="col3" nameend="col3" align="char" char=".">1.1</entry><entry namest="col4" nameend="col4" align="center">8.0</entry><entry namest="col5" nameend="col5" align="center">3.0</entry><entry namest="col6" nameend="col6" align="char" char=".">10.0</entry></row><row rowsep="1"><entry namest="col1" nameend="col1" align="left">Comparative Example 14</entry><entry namest="col2" nameend="col2" align="char" char=".">2.0</entry><entry namest="col3" nameend="col3" align="char" char=".">2.1</entry><entry namest="col4" nameend="col4" align="center">8.0</entry><entry namest="col5" nameend="col5" align="center">12.0</entry><entry namest="col6" nameend="col6" align="char" char=".">24.0</entry></row></tbody></tgroup></table></tables>

0161As mentioned above, according to the present invention, a thermal dye transfer sheet having a yellow dye layer excellent in sensitivity, fastness such as light-resistance, shelf stability, coloring density and color reproducibility can be provided.