Single-substrate multi-layer optical disk for read-only storage and phase change rewritable storage

BACKGROUND OF THE INVENTION

Field of the Invention

0001The present invention relates to an optical disk, and more particularly, to a single-substrate multi-layer optical disk for read-only storage media and phase change rewritable storage media.

Description of the Related Art

0002Optical disks suitable for large capacity are classified as a read-only type, a write-once type and a rewritable type.

0003The read-only type optical disks are used as compact-disk read-only memories (CD-ROM) in personal fields and image compressing technology such as Moving Picture Image Coding Experts Group Phase 2 (MPEG2). Also, the read-only type optical disks are used as laser disks for high definition television (HDTV). The read-only type optical disks are needed to be more integrated with increased capacity.

0004The write-once type optical disks can be written to by users. The write-once type optical disks are used, for example as external memories for computers, document files and image files. The write-once type optical disks are also needed to be more integrated with increased capacity.

0005The rewritable type optical disks can be written to and erased repeatedly by users. Also the rewritable type optical disks are used, for example, as external memories of computers, document files and image files. The rewritable type optical disks are further divided into phase change rewritable optical disks using a phase change of a recording layer and magneto-optical disks using a change of magnetization direction of a magnetic layer. The rewritable type optical disks are also needed to be more integrated with increased capacity.

0006Generally, the read-only type optical disk includes a grooved substrate and a reflecting metal layer made of aluminum alloy formed thereon. The write-once optical disk includes a low melting temperature metal layer made of metal alloy of Te, Bi, Se or Sn, or a dye active layer having an absorption characteristic coated on a substrate. The phase change rewritable optical disk includes a recording layer made of GeSbTe, InSbTe, InSe, InTe, AsTeGe, TeOx-GeSn, TeSeSn, SbSeBi or BiSeGe. The magneto-optical disk includes a metal alloy of rare earth metal such as Tb, Gd, Dy or Ho and a transition metal such as Fe, Co or Ni sandwiched by transparent passivation layers made of SiN or the like. The layers used herein are deposited by a resistance heating vacuum evaporation method, an electron beam vacuum evaporation method, a sputtering method, or a spin coating method.

0007In order to increase the integration and capacity of optical disks, a prior art single-substrate single-layer optical disk, which is called a partial read-only memory (ROM) disk, was known in which a substrate of the disk is divided into three areas: a read-only area, a write-once area and a rewritable area (see; "Erasable Optical Disc", Trikeps Co. Ltd., pp. 249, 1993).

0008In the above-mentioned prior art single-substrate single-layer optical disk, since the three areas are arranged two-dimensionally in the substrate, it is actually impossible to increase the integration and capacity.

0009A prior art dual-substrate dual-layer optical disk includes two substrates each having a recording layer formed thereon.

0010In the above-mentioned prior art dual-substrate dual-layer multi-optical disk, however, the disk has to be read from both sides, which requires separate disk drive units. This also increases the manufacturing cost and makes the control complex.

0011A first prior art single-substrate multi-layer optical disk includes a plurality of read-only type recording layers capable of being read from a single side (see: Kurt A. Rubin et al., "Multilevel Volumetric Optical Storage", SPIE Vol. 2338, pp. 247-253, 1994).

0012The above-mentioned first prior art single-substrate multi-layer optical disk, however, is only for read-only storage.

0013A second prior art single-substrate multi-layer optical disk includes a read-only type recording layer and a phase change rewritable recording layer (see: K. Nishiuchi et al., "Dual-Layer Optical Disk with Phase Change Rewritable and Read only Layers", Extended Abstract of JSAP, pp. 959, 1995).

0014In the above-mentioned second prior art single-substrate multi-layer optical disk, however, since the read-only type recording layer is formed over a substrate, and the phase change rewritable recording layer is formed over the read-only type recording layer, a reflecting layer for the read-only type recording layer needs to be transparent, so that data detection from the read-only type recording layer is unreliable. Also, it is difficult to form the phase change rewritable recording layer after the formation of the read-only type recording layer.

SUMMARY OF THE INVENTION

0015It is an object of the present invention to provide a reliable single-substrate multi-layer optical disk for read-only storage and phase change rewritable storage.

0016According to the present invention, an optical disk includes a transparent rigid substrate, a phase change rewritable optical recording medium formed on the transparent rigid substrate, a transparent spacer formed on the phase change rewritable optical recording medium and having a grooved surface for storing information, and a reflecting layer formed on the grooved surface of the transparent spacer. The grooved surface of the transparent spacer and the reflecting layer form a read-only optical recording medium.

0017Since the reflecting layer does not need to be transparent, the reflecting layer can be made of metal in the same way as the conventional CD-ROM, so that the data detection of the read-only optical recording medium can be reliable. Also, since the read-only recording medium can be formed after the formation of the phase-change rewritable optical medium, it is easy to manufacture the optical disk.

BRIEF DESCRIPTION OF THE DRAWINGS

0018The present invention will be more clearly understood from the description as set forth below, with reference to the accompanying drawings, wherein: <ul id="ul0001" list-style="none" compact="compact"><li>Fig. 1 is a cross-sectional view illustrating an embodiment of the optical disk according to the present invention;</li><li>Fig. 2 is a detailed cross-sectional view of the phase change rewritable recording medium of Fig. 1; and</li><li>Fig. 3 is a cross-sectional view illustrating an optical disk to which the optical disk of Fig. 1 is applied.</li></ul>

DESCRIPTION OF THE PREFERRED EMBODIMENTS

0019In Fig. 1, which illustrates an embodiment of the present invention, reference numeral 1 designates a transparent rigid substrate made of polycarbonate which is about 130 mm in diameter, about 1.2 mm thick and has a track pitch of about 1.0 µm. Also, a phase change rewritable recording medium 2 is formed on the substrate 1. The phase change rewritable recording medium 2 will be explained later in detail. Note that the substrate 1 can be made of transparent resin or glass.

0020A transparent spacer 3 made of about 25 µ m thick ultravioletsetting resin is formed on the phase change rewritable medium 2 by a spin coating method. That is, the ultravioletsetting resin is coated on the phase change rewlitable medium 2, and read-only information is transferred by a transparent stamper (not shown) to the ultravioletsetting resin, so that grooves (pits) 4 corresponding to the read-only information are formed on the surface of the ultravioletsetting resin. Then, the ultravioletsetting resin is hardened by ultraviolet radiation, and the transparent stamper is removed therefrom.

0021Further, a reflecting layer 5 made of about 150 nm thick Al alloy is formed on the grooved surface of the transparent spacer 3.

0022In addition, an overcoat layer 6 made of about 10 µm thick ultravioletsetting resin is coated on the reflecting layer 5.

0023An about 690 nm wavelength laser beam 7 or 7' is focused by a 0.55 numerical aperture objective lens 8 or 8' at the phase change rewritable recording medium 2 or at the read-only recording medium formed by the pits 4 and the reflecting layer 5. Note that, although the objective lenses 8 and 8' are illustrated, a single objective lens is actually provided, so that the single object lens is moved to different locations as occasion demands, to realize the objective lenses 8 and 8'.

0024Also, although the thickness of the substrate 1 is so designed as to obtain a certain rigidity of the substrate 1, the thickness of the substrate 1 is changed in accordance with the position and focal length of the objective lens 8. In addition, the thickness of the substrate 1 can be other values than the thickness of 1.2 µm of the conventional compact disks.

0025The phase change rewritable optical recording medium 2 is explained in detail next with reference to Fig. 2.

0026A transparent lower passivation layer 21 made of about 230 nm thick ZnS-SiO₂, a phase change recording layer 22 made of about 10 nm thick Ge₂Sb₂Te₅, a transparent upper passivation layer 23 made of about 18 nm thick ZnS-SiO₂, a transparent reflecting layer 24, and a transparent interference layer 25 made of about 120 µm thick ZnS-SiO₂ are deposited sequentially on the substrate 1 by a sputtering method.

0027The transparent reflecting layer 24 can be made of about 60 nm thick silicon (Si) by a sputtering method using a silicon target in an argon atmosphere. Also, the transparent reflecting layer 24 can be made of about 75 nm thick germanium (Ge) by a sputtering method using a germanium target in an argon atmosphere.

0028Further, the transparent reflecting layer 24 can be made of about 120 nm thick silicon oxide (SiO) by a reactive sputtering method using a silicon target in an argon/oxygen atmosphere. Or, the transparent reflecting layer 24 can be made of about 110 nm thick silicon nitride (SiN) by a reactive sputtering method using a silicon target in an argon/nitrogen atmosphere.

0029In addition, the transparent reflecting layer 24 can be made of about 100 nm thick germanium oxide (GeO) by a reactive sputtering method using a germanium target in an argon/oxygen atmosphere. Or, the transparent reflecting layer 24 can be made of about 95 nm thick germanium nitride (GeN) by a reactive sputtering method using a germanium target in an argon/nitrogen atmosphere.

0030In the above-constructed phase change rewritable optical recording medium 2, when the phase change recording layer 22 is crystal, the transmission of 690 nm laser light is about 30 percent, while, when the phase change recording layer 22 is noncrystal, the transmission of 690 nm laser light is about 52 percent.

0031The inventors have performed a writing operation, an overwritting (erasing) operation and a reproducing operation upon the optical disk of Fig. 1.

0032First, the laser beam is focused by at the phase change rewritable optical medium 2 by a focus servo circuit (not shown) (see the reference numerals 7 and 8 of Fig. 1). Then, the phase change rewritable optical recording medium 2 was initialized. Then, the optical disk of Fig. 1 was rotated at a speed of 3600 rpm, and a signal having a frequency of 8.4 MHz and a duty ratio of 50 percent was written onto a track at a radius of 30 nm of the optical disk of Fig. 1. Then, a signal having a frequency of 2.2 MHz and a duty ratio of 50 percent was overwritten onto the same track. In this case, in order to minimize the secondary harmonic distortion, the writing laser power was 12 mW, 11 mW, 11.5 mW, 11.5 mW, 10 mW and 10.8 mW for the phase change rewritable optical recording medium 2 using Si, Ge, SiO, SiN, GeO and GeN, respectively, as the transparent reflecting layer 24, and also, the overwriting (erasing) laser power was 6 mW, 5.5 mW, 6 mW, 6 mW, 5 mW and 5.4 mW for the phase change rewritable optical recording medium 2 using Si, Ge, SiO, SiN, GeO and GeN, respectively, as the transparent reflecting layer 24. Finally, this track was produced, thus obtaining a reliable detection signal.

0033Next, the laser beam was focused at the read-only recording medium (4, 5) by the focus servo circuit. Then, the optical disk of Fig. 1 was rotated at a speed of 3600 rpm to reproduce data on the read-only recording medium. In this case, the reproducing laser power was 0.8 mW, thus obtaining a reliable detection signal.

0034In the above-constructed phase change rewritable optical recording medium 2, it is preferable that the transmission of laser light be about 30 to 60 Percent. That is, when the phase change recording layer 22 is made thick, for example, 15 nm thick, the transmission of laser light is reduced. In this case, when the phase change recording layer 22 is crystal, the transmission Of 690 nm laser light is about 22 percent, while, when the phase change recording layer 22 is amorphous, the transmission of 690 nm laser light is about 40 percent.

0035Also, the inventors have performed a writing operation, an overwriting (erasing) operation and a reproducing operation upon the optical disk of Fig. 1, where the phase change recording layer 22 was 15 nm thick.

0036First, the laser beam is focused at the phase change rewritable optical medium 2 by the focus servo circuit (see the reference numerals 7 and 8 of Fig. 1). Then, the phase change rewritable optical recording medium 2 was initialized. Then, the optical disk of Fig. 1 was rotated at a speed of 3600 rpm, a signal having a frequency of 8.4 MHz and a duty ratio of 50 percent was written onto a track at a radius of 30 nm of the optical disk of Fig. 1. Then, a signal having a frequency of 2.2 MHz and a duty ratio of 50 percent was overwritten onto the same track. In this case, in order to minimize the secondary harmonic distortion, the writing laser power was 12 mW, 11 mW, 11.5 mW, 11.5 mW, 10 mW and 10.8 mW for the phase change rewritable optical recording medium 2 using Si, Ge, SiO, SiN, GeO and GeN, respectively, as the transparent reflecting layer 24, and also, the over writing (erasing) laser power was 6 mW, 5.5 mW, 6 mW, 6 mW, 5 mW and 5.4 mW for the phase change rewritable optical recording medium 2 using Si, Ge, SiO, SiN, GeO and GeN, respectively, as the transparent reflecting layer 24. Finally, this track was reproduced, thus obtaining a reliable detection signal.

0037Next, the laser beam was focused at the read-only recording medium (4, 5) by the focus servo circuit (see the reference numerals 7' and 8' of Fig. 1). Then, the optical disk of Fig. 1 was rotated at a speed of 3600 rpm to reproduce data on the read-only recording medium. In this case, the reproducing laser power was 0.8 mW, however, a reliable detection signal could not be obtained.

0038The above-constructed transparent spacer 3 is preferably approximately 5 to 50 µm thick, in view of the focal length of the objective lens 9'. For example, if the transparent spacer 3 is 2 µm thick, when a reproducing operation is performed upon the read-only recording medium (4, 5), a reproducing operation may be performed upon the phase change rewritable optical recording medium 2. As a result, a reliable detection signal cannot be obtained. On the other hand, if the transparent spacer 3 is 60 µm thick, when a reproducing operation is performed upon the read-only recording medium (4, 5), the laser beam 8' is focused at a location within the transparent spacer 3 apart from the read-only recording medium (4, 5). As a result, a reliable detection signal cannot be obtained.

0039In Fig. 3, which illustrates a modification to which the optical disk of Fig. 1 is applied, two disk portions A and B, each having the same configuration, are adhered by an adhesive layer 9. In this case, the overcoat layer 6 of the disk portion A is adhered by the adhesive layer 10 to the overcoat layer 6' of the disk portion B.

0040A writing, overwriting (erasing) or reproducing operation is performed upon the disk portion A by a laser beam incident from the substrate 1. On the other hand, a writing, overwriting (erasing) or reproducing operation is performed upon the disk portion B by a laser beam incident from the substrate 1'.

0041As explained hereinabove, according to the present invention, since the reflecting layer does not need to be transparent, the reflecting layer can be made of metal in the same way as the conventional CD-ROM, so that the data detection of the read-only optical recording medium can be reliable. Also, since the read-only recording medium can be formed after the formation of the phase-change rewritable optical medium, it is easy to manufacture the optical disk.