SLIP-LAYERED CATHETER B.ALLOON

CROSS REFERENCE TO RELATED .APPLICATIONS This application is a continuation-in-part of commonly assigned, co-pending U. S. Patent Applications Serial Nos. 08/017,763, filed February 16, 1993 by J. Wang, and

08/082,594, filed June 25, 1993 by J.E. Abele et al. Appli¬ cations 08/017,763 and 08/082,594 are hereby incorporated herein by reference.

BACKGROUND OF THE INVENTION

The present invention relates to balloons for medical catheter applications, wherein a catheter with a balloon at the proximal end is positioned within a bodily conduit and inflated to expand the conduit, and to methods of fabrica- tion of such balloons.

Typical balloon catheters have a balloon fastened around the exterior of a hollow catheter tube or shaft, with the balloon in fluid flow relation with the interior of the shaft. The shaft provides a fluid supply for inflating the balloon.

Examples of such balloon catheters are catheters for prostate therapy, TTS endoscopic catheters for gastrointes¬ tinal use, and PTA and PTCA catheters for angioplasty. For example, coronary angioplasty can involve the insertion of a PTCA (percutaneous transluminal coronary angioplasty) cathe¬ ter through a patient's artery to an arterial stenosis, and injecting a suitable fluid into the balloon to inflate it. The inflation expands the stenosis radially outwardly and compresses it against the artery wall to increase the cross- sectional area of the artery so that the artery has an acceptable blood flow rate.

Some known catheter balloons are fabricated from non- compliant materials such as polyethylene terephthalate (PET) or Nylon. Non-compliant balloons present the advantages of high burst strength and predetermined maximum diameter. These balloons can prevent damage to tissues due to over- inflation, since they do not increase in diameter signifi- cantly beyond the point of full inflation. Their disadvan¬ tages, however, include stiffness and poor foldability. Further, on deflation these balloons can present sharp edges and corners which can cause trauma to bodily tissues as the catheters are withdrawn. Other known balloons are fabricated from compliant materials such as polyethylene (PE) or ethylene vinyl ace¬ tate (EVA) . The diameter of these balloons is dependent on the pressure of the inflation fluid. The compliant balloons are easily folded, and are softer than the non-compliant balloon, thus are less likely to cause trauma during their passage through the body. However, the variable diameter of the non-compliant balloons must be carefully monitored to prevent tissue damage and catastrophic failure of the bal¬ loon during inflation. They can also present the disadvan- tages of lower tensile strength than the non-compliant balloons. Increasing the wall thickness to offset the lower tensile strength can present an undesirably large profile in the folded balloon.

It would be desirable to have a medical catheter bal- loon which combines the best properties of the compliant and non-compliant balloons, with low compliance, high burst strength, low folded profile, softness, and pliability. The invention described herein was developed to address that need.

SUMMARY OF THE INVENTION In a first aspect, the invention is a slip-layered balloon for use with a medical catheter device. The balloon includes a wall defining a chamber, the wall including at least two layers of a polymeric medical balloon material. Between the layers is a low-friction substance imparting a low coefficient of friction between facing surfaces of the layers, so that the layers become slip-layers which readily slide with respect to one another as the balloon is inflated and deflated. A typical configuration for the balloon wall is a generally cylindrical central portion between tapered proximal and distal end portions.

In a narrower aspect, the balloon wall is unitary, with layers joined to one another at a plurality of ridges, each extending the length of the wall. Each ridge is separated from other ridges by slip-layered segments in which the layers become slip-layers which readily slide with respect to one another as the balloon is inflated and deflated.

In another narrower aspect, the balloon further in¬ cludes an elastic sleeve surrounding and coextensive with the wall. The low-friction substance in such a sleeved balloon can also be disposed between the elastic sleeve and the outermost layer, so that a low coefficient of friction is imparted between facing surfaces of the elastic sleeve and the outermost layer and such that the elastic sleeve and the outermost layer also become slip-layers which readily slide with respect to one another as the balloon is inflated and deflated.

In another aspect, the invention is a catheter for insertion into a bodily conduit. The catheter includes a shaft with a lumen for delivery of fluid inflation media, a balloon having a wall concentric with the shaft and defining a chamber. The chamber is in fluid communication with the lumen for inflation of the balloon. The balloon wall in¬ cludes at least two non-adhering layers of a polymeric medical balloon material. Between the layers is a low- friction substance imparting a low coefficient of friction between facing surfaces of the layers, so that the layers become slip-layers which readily slide with respect to one another as the balloon is inflated and deflated. In yet another aspect, the invention is a method for fabricating a slip-layered balloon for use with a medical catheter device. The method involves providing on a first layer of a medical balloon material at least one additional layer to form a balloon wall including at least two layers of a medical balloon material. The wall defines a chamber. A low-friction substance is disposed between said layers imparting a low coefficient of friction between facing surfaces of the layers, so that the layers become slip- layers which readily slide with respect to one another as the balloon is inflated and deflated. In a narrower aspect of this method, the additional layer on said first layer is provided by extruding the medical balloon material to form the first layer and the additional layer of the balloon wall. In a preferred method, a polymeric medical balloon material and a second polymeric material are coextruded so that the medical bal¬ loon material forms a continuous phase providing a generally tubular balloon blank and the second material forms a dis¬ crete phase. The discrete phase is surrounded by the con¬ tinuous phase and provides strands extending lengthwise within the blank. The strands are then removed from the blank and the strand-removed blank is shaped to form a balloon including a unitary wall defining a chamber. The balloon wall includes at least two layers of a the medical balloon material joined to one another at a plurality of ridges, each of the ridges extending the length of the wall and being separated from other ridges by layered segments of the wall. A low-friction substance is disposed between the layers of the segments, imparting a low coefficient of friction between facing surfaces of the layers, so that the layers become slip-layers which readily slide with respect to one another as the balloon is inflated and deflated. In a most preferred method, the second material is softer than the medical balloon material, and the strands are removed by scoring the balloon blank to form a score-line in the circumferential direction along the outermost surface of the medical balloon material near an end of the blank, without affecting the second material. The medical balloon material is then broken at the score-line to separate the medical balloon material of the end of the blank from the remainder of the medical balloon material. The separated medical balloon material is removed from the blank by pulling the separated medical balloon material off of the strands, thereby exposing an end of each strand. The strand ends are then gripped and pulled to remove the strands from the blank.

BRIEF DESCRIPTION OF THE DRAWINGS Figure 1 is a cross-sectional view of a balloon cathe¬ ter in an inflated condition in accordance with one embodi¬ ment of the present invention. Figure 2 is a cross-sectional view of the balloon shown in Figure 1, taken along the line 2-2.

Figure 3 is a cross-sectional view of a coextruded balloon blank for fabricating a balloon in accordance with an alternate embodiment of the present invention. Figure 4 is an elevation view of the balloon blank of

Figure 3, illustrating the withdrawal of the second phase strands to leave open channels in the balloon blank.

Figure 5 is a cross-sectional view of a portion of the balloon fabricated from the balloon blank of Figures 3 and 4.

Figure 6 is a cross-sectional view of a portion of a balloon in accordance with another alternate embodiment of the present invention.

DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS

An exemplary embodiment of the balloon in accordance with the invention utilizes a non-compliant balloon in which the balloon wall encloses a chamber. The balloon has two or more concentric thin layers of high strength medical balloon material, with provision made to overcome the normally occurring high coefficient of friction existing between the interfacial surfaces of the balloon layers. That is, a sufficiently low coefficient of friction between the layers exists for the layers to be very slippery against each other. The number of layers in the balloon wall typically is 2 to about 10 layers, preferably 3 - 5 layers, with provision made for a low coefficient of friction between adjacent pairs of layers.

This slip-layered balloon deforms easily, since little force is necessary to cause the layers to slide against (move relative to) one another. This sliding movement is principally in the circumferential direction, and may be likened to the sliding against one another of the pages of a paperback booklet when the booklet is bent into a curve. Although the booklet may be the same thickness as a similar sized piece of paperboard, it is softer and more flexible. Similarly, even if each individual layer is stiff and strong, the slip-layered balloon described herein feels soft and pliable, and folds down easily. This improvement in properties is achieved even in a balloon having a total thickness greater than is normally used for a particular medical purpose.

The balloon layers may be fabricated from any high strength material known to be suitable for medical balloons, and preferably from a non-compliant material. Examples of preferred non-compliant materials suitable for fabrication of the balloon are polyethylene terephthalate (PET) , most preferably biaxially oriented PET, Nylon, polypropylene (PP) , and other non-compliant engineering resins known to be suitable for medical balloon applications. Suitable compli- ant materials are polyethylene (PE) , particularly biaxially oriented PE (irradiated) , polyvinyl chloride (PVC) , and other compliant polymers known to be suitable for medical balloons.

The low coefficient of friction between layers may be provided by coating the interfacial surfaces of the balloon layers with a low-friction substance, or otherwise inserting a low-friction substance between the layers. Examples of such a low-friction substance include silicone, silicone oil, fluorocarbons, and other lubricants known to be suit¬ able for medical uses. The softness, pliability, and foldability of such a slip-layered balloon is significantly greater than that of a single layer balloon of the same total thickness, and even than that of a multi-layered balloon of the same total thickness without the low-friction substance between the layers. The coextensive layers of the slip-layered balloon described herein may be fabricated by separately forming (e.g., by extrusion) tubular balloon blanks, either formed with or stretched to progressively larger diameters, and sliding progressively larger tubes over the smaller tubes to assemble the individual layers into a multi-layered balloon blank. If necessary, the larger tubes may be shrink-fitted over the smaller diameter tubes. In a preferred alterna¬ tive, however, the layers are extruded simultaneously (co- extruded) to form the balloon blank. If desired, the inner- most and/or outermost layers of a multi-layered balloon may be thicker than the intermediate layer(s) for improved abrasion resistance. The balloon blank may then be shaped by conventional means to form the balloon. In one exemplary shaping process, the blank is heated and inflated to form, e«g., a cylindrical balloon body with tapered portions between the body and the balloon proximal and distal ends. As part of such a shaping process, the blank may be stretched to orient the material and/or to form thinner layers and/or ends. The low-friction substance may be coated on or other¬ wise inserted between the layers by any one of several means. For example, separately fabricated layers may be coated with the low-friction substance, e.g., by dipping, wiping, or spraying with the substance alone or in solution before assembling the layers to form the balloon blank.

Alternatively, the assembled or commonly extruded layers of the blank may be coated, e.g., by soaking the blank in a solution of the substance or by forcing the substance or its solution between the layers under pressure. One example of a suitable solution of a low friction substance is a solu- tion of about 2% - 10% silicone oil in Freon. The blank may then be shaped by conventional methods to form a medical balloon for use with a catheter. Preferably, the low fric¬ tion substance is applied before shaping to prevent adhering of the layers together during the shaping process. Most preferably, the low-friction material is applied both before and after shaping.

A catheter utilizing the herein-described slip-layered balloon may be similar to any conventional balloon catheter assembly, with the herein-described novel balloon substitut- ed for the conventional balloon. The catheter includes a shaft, and the proximal end of the slip-layered balloon typically is joined to the shaft at the shaft distal end. The length of the catheter is sufficient to be threaded through the bodily cavity or cavities to the area to be treated with a sufficient length remaining outside the body to permit manipulation of the catheter. The shaft includes at least one internal lumen for inflating the balloon with a fluid inflation medium. Typically, a guidewire extends through the balloon, and may extend distally from the bal- loon. Alternatively, a wire may extend proximally through the shaft (via an additional lumen) to provide greater stiffness and strength to the shaft.

The catheter may be fabricated by conventional means, except for the fabrication of the novel slip-layered bal- loon, described above, and the joining of the balloon to the catheter at the balloon's proximal and distal ends. The proximal joint may be accomplished by adhering the layers to one another at the balloon ends and adhering the innermost layer to the shaft. Alternatively, the layers may be trimmed to overlap one another and successively adhered to the shaft, or only the innermost and outermost layers may be adhered. Heat sealing and/or adhesive are suitable for this joining process. An improved seal may be achieved by adher¬ ing the innermost layer to the shaft, slipping a flexible polymeric sleeve cover over the shaft with its distal end overlapping the balloon end, then adhering the sleeve cover to both the outermost layer and the shaft. Similar joining methods may be used to anchor the proximal end of the bal¬ loon to, e.g., the guidewire. Optionally, the outer surface of the balloon or the entire catheter may be further coated with a conventional slip coating, for example silicone or a hydrophilic coating, to ease passage of the catheter through the body.

In a particularly preferred embodiment of the slip- layered balloon, a unitary balloon wall is fabricated in which regions of slip-layered wall extend lengthwise between "ridges", i.e. long, narrow regions in which the layers of the balloon are joined to one another through the thickness of the balloon, the joined regions normally visible as ridges or stripes on the outside surface of the balloon wall. The unitary nature of the ridged slip-layered balloon provides better quality control and simplifies joining of the balloon ends to the catheter, since the layers are already fixed to one another at the ridges.

The ridged design also results in differential stiff- ness about the circumference of the balloon, encouraging regular, multiple-fold collapse of the balloon during defla¬ tion and ensuring a smaller diameter for the collapsed balloon. On deflation, multiple folds form in a regular pattern about the circumference of the balloon wall as the balloon wall collapses. The regular fold pattern, in turn, provides a smaller collapsed profile than is usual with the prior art balloons, especially the stiffer non-compliant balloons. This smaller profile can ease passage of the deflated balloon through the arteries during withdrawal of the catheter.

The ridged slip-layered balloon may be fabricated by heat-sealing or otherwise joining together the separate layers of the above described multi-layered balloons along the ridges, leaving layered segments between the ridges. (Preferably, each heat-sealed ridge is continuous along the length of the balloon.) However, the preferred method of fabricating such a ridged slip-layered balloon is to extrude a balloon blank with open channels extending lengthwise through the wall of the blank to divide regions of the wall into multi-layered segments. For example, the wall of a blank for a ridged two-layered balloon is fabricated with a single cylindrical array of a plurality of radially dis¬ posed, axially extending channels within the thickness of the wall. The channels are separated by ridges formed by the non-channeled portions of the wall. After shaping of the balloon from the blank, the channels effectively divide the single balloon wall into inner and outer walls in the regions between the ridges. The channels and ridges may extend in a straight line parallel to the balloon axis, or they may be "wrapped" in a helical pattern about the balloon axis.

A balloon with more than two layers in the layered segments between ridges is similarly fabricated, except that at least one additional array of channels is formed, each array at a different radial position within the wall of the balloon blank. The channels of each array preferably are superimposed over one another to provide multi-layered segments sharing a common ridge between each pair of adja¬ cent segments. The surfaces enclosing each channel are coated with the low-friction substance described above to provide a slip-layered balloon, but with the advantages of unitary construction, as described below.

In a most preferred method, a blank for the ridged slip-layered balloon is fabricated by coextruding a hollow tube of two or more dissimilar polymeric materials using conventional extrusion techniques. A discrete phase, that is a phase which serves as the precursor of the channels (and which dictates their location and shape) is formed of, for example, high density polyethylene, Nylon, low density polyethylene, or polyethylene copolymers. A continuous phase, that is the phase that will form the balloon blank with the discrete phase enclosed within the walls thereof, can be formed of polyethylene terephthalate or high or low density polyethylene. High density polyethylene, low densi¬ ty polyethylene and polyethylene copolymers can be extruded within polyethylene terephthalate. Nylon can be extruded within a high or low density polyethylene. Typically, the material of the continuous phase is harder and more brittle than the softer, more pliable discrete phase material. Normally, the strands of all arrays are formed of the same second-phase material. However, arrays of different strand materials as well as strands of different materials in the same array are within the scope of the invention.

After the phases are coextruded, the discrete phase is withdrawn from the continuous phase to leave open channels internal to the continuous phase, as described above. Coextrusion of two polymeric materials is well known, and conventional techniques are used for this process. Criteria for matching of two polymeric materials for the above-de¬ scribed coextrusion are that they not adhere to each other after extrusion and that the discrete phase can be withdrawn from the continuous phase leaving channels therein.

In one method for removing the strands from the co¬ extruded balloon blank, the material of the continuous phase of the balloon blank is harder and more brittle than that of the discrete phase strands. A notch is scratched into the outer surface of the blank, extending in a circumferential direction. (The notch need not extend about the entire circumference of the balloon wall.) The blank then can be fractured cross-sectionally by exerting tensile stress at the notch (for example, by bending the balloon blank) with- out breaking the strands, and the fractured continuous phase is separated from the blank. The discrete phase strands then can be withdrawn from the continuous phase, forming a tubular balloon blank of, e.g., polyethylene terephthalate with a plurality of open channels within its wall. The shape, number, and arrange- ent of the channels can be varied as desired by the opera¬ tor by varying the design of the extrusion die. For exam¬ ple, the strands described above may be round, ovoid, square, rectangular, etc. in cross-section. Also, any number of arrays between 1 and about 10, preferably about 3 - 7, is possible through the total thickness of the bal¬ loon, n-1 arrays producing n layers in each shaped, ridged, slip-layered balloon. Any number of channels in each array between 1 and about 24 is possible, preferably about 3 - 10. Normally, the ridges are of a circumferential width smaller than that of the slip-layered segments.

The open channel balloon blank is then shaped by con¬ ventional means, e.g. heating and inflation, to form a ridged balloon. During the shaping process, the chamber enclosed by the inner surface of the heated balloon is inflated, but the channels within the wall itself are not pressurized. Thus, the layers formed by the inner and outer walls of the channels are stretched to a greater extent than the walls joining the channels in each array, creating a plurality of layered wall segments separated by ridges. If desired, the innermost and/or outermost layers may be thick¬ er than any intermediate layers present, providing increased toughness and strength. The channels are coated with sili¬ cone oil or other low-friction substance such that the layered segments are slip-layered segments which readily slide relative to one another, as described above. This ridged balloon is a strong, soft medical balloon in which ridges and slip-layered segments provide differential stiff¬ ness about the circumference of the balloon for improved foldability. Additionally, the ridges anchor the layers to one another providing easier joining of the balloon to the catheter. While coextrusion is generally the preferred method for forming the ridged balloons, it is also possible to extrude tubes having the channels already formed therein using a known type of extrusion die. However, the thickness of the channels within the blank is extremely small, typically about 0.025 - 0.5 mm within a tubular balloon blank having a total wall thickness between about 0.07 and 1.0 mm and outside diameter between about 0.25 and 5.0 mm. Therefore, extrusion with the desired preformed channels can be more difficult than coextrusion, and coextrusion is generally preferred.

The foldability and surface characteristics of any of the balloons described herein, and particularly of the ridged balloons, may be improved by providing an elastomeric or elastic sleeve surrounding the balloon wall. The sleeve may be fabricated of such materials as silicone rubber, polyurethane elastomer, polya ide elastomer, polyolefin elastomer, thermoplastic elastomers (e.g., an engineering thermoplastic elastomer) , or any elastomer considered suit- able for use in medical catheters.

The elastic sleeve is of a size, thickness, and elastic modulus such that it fits closely around the slip-layered balloon wall in its completely deflated or collapsed state, expands with the balloon wall as the balloon is inflated to its maximum diameter, and contracts as the pressure in the balloon is decreased during deflation, collapsing the slip- layered balloon wall into a tight, compact, generally cylin¬ drical bundle. A typical thickness for the elastic sleeve is about 0.003" - 0.020". To further encourage the collapse of the balloon wall, as well as to permit more even expan¬ sion of the elastic sleeve, a coating of silicone oil or other low-friction substance may be disposed between the slip-layered balloon wall and the elastic sleeve. The elastic sleeve and low-friction coating cooperate with the slip layers, and in the ridged balloon with the ridges to refold the balloon in, e.g., a helical wrap about the axis of the balloon. Ridges in the sleeved balloon assure that the folding will occur along predetermined lines along the length of the balloon. The sleeve is fabricated, applied to the balloon, and joined to the catheter by known means. Referring now to Figures 1 and 2, catheter 10, not drawn to scale, includes slip-layered balloon 11, shown in its inflated state, in which slip-layered balloon wall 12 encloses chamber 13. Balloon wall 12 includes inner layer 14 and outer layer 15. Layers 14 and 15 are coextensive, and are disposed with interfacial surfaces 16 and 17, re¬ spectively, facing one another. Surface 16 and/or surface 17 are coated with silicone oil 18, and layer 15 is heat treated to shrink-fit layer 15 over inflated layer 14 such that no air bubbles are enclosed between surfaces 16 and 17. Thus, silicone oil coating 18 causes layers 14 and 15 to slide with respect to one another, such that slip-layered balloon 11 is softer and more pliable than prior art bal¬ loons. In Figures 1 and 2, balloon wall 12 is shown with two layers with a silicone oil coating between the two layers. Alternatively, the balloon wall may have up to about 10 layers, with silicone oil or other low-friction substance between facing surfaces of the layers.

Balloon 11 is shown in Figure 1 with its proximal end 19 fixed to distal end 20 of shaft 21 by sleeve cover 22 and adhesive (not shown) . Balloon distal end 23 is fixed to wire 24 in a similar manner by sleeve cover 25. Balloon chamber 13 is in communication via lumens 26 with a source (not shown) of an inflation medium for inflation of balloon 11. In the embodiment of Figure 1, wire 24 extends proxi- mally through balloon chamber 13 and through lumen 27 of catheter 10.

Inflation of chamber 13 causes balloon wall 12 to expand from a folded arrangement around wire 24 to being spaced therefrom. This expansion causes proximal and distal ends 19 and 23 to assume generally conical shapes and allow for an increase in the diameter of balloon 11 and for press- ing of balloon wall 12 against the lesion being addressed.

A typical balloon diameter when the balloon chamber is fully inflated is about 0.04 - 2 in. The thickness of each of layers 14 and 15 typically is about 0.0001 - 0.004 in, with 0.0003 - 0.002 in being preferred. The deflated pro¬ file of balloon 11 typically is about 0.03 - 0.25 in.

Figures 3 and 4 illustrate coextruded balloon blank 30, from which an alternate embodiment of the balloon described herein is fabricated. In Figures 3 and 4, like features to those shown in Figures 1 and 2 are indicated by the same reference numerals.

In Figure 3, balloon blank 30 has continuous phase balloon wall 12a of non-compliant polyethylene terephthalate balloon material. Balloon wall 12a includes channels 31 filled by discrete phase strands 32 of a high density poly¬ ethylene. Channels 31 are disposed in inner and outer cylindrical arrays 33 and 34, respectively, around an axis, not shown, which can be similar to wire 24. Each of chan¬ nels 31 share a common "connector" wall, wall 35 or 36, with the next adjacent of channels 31 in array 35 or 36, respec¬ tively. Thus, in this embodiment, innermost layer 14a, outermost layer 15a, and intermediate layer 37 are each present as segments joined by connector walls 35 and 36.

After coextrusion, strands 32 are removed from balloon blank 30 by withdrawing the strands from channels 31, as illustrated in Figure 4. A notch or groove (not shown) is scratched into the outer surface of continuous phase balloon wall 12a at 38, the notch extending in a short circumferential arc about the balloon wall. The hard, brittle continuous phase balloon wall 12a is fractured cross-sectionally by bending the balloon blank to exert tensile stress at the notch. The soft, pliable strands remain unbroken during this process. The fractured continu¬ ous phase 12a may then be separated into portions 30a and 30b. Shorter portion 30a is pulled away from longer portion 30b, permitting part of each strand 32 to be withdrawn from channels 31 in shorter portion 30a, and to extend from cross-sectional surface 39 of longer portion 30b. The exposed parts of strands 32 are then gripped and pulled, withdrawing strands 32 from channels 31 in longer portion 30b to form a balloon blank with open channels. The open channels of the balloon blank are then coated with, e.g., silicone oil, as described above, and the balloon blank is shaped by conventional means, e.g. heating and inflation, to form a ridged balloon, described in more detail below. The coextruded balloon blank of Figures 3 and 4, as mentioned above, is fabricated from two dissimilar materi¬ als, the harder, more brittle polyethylene terephthalate continuous phase forming the balloon wall and the softer, more pliable high density polyethylene discrete phase form- ing the removable strands. However, other dissimilar mate¬ rial combinations may be used, as described above.

As the discrete phase is withdrawn from the continuous phase, a tubular balloon blank is formed having a plurality of open channels within its wall. For the balloon blank of Figures 3 and 4, the discrete phase is extruded such that the channels within the shaped balloon are disposed to define two cylindrical arrays, as shown in Figure 5. The shape and arrangement of the channels can be varied as desired by the operator by varying the design of the extru- sion die.

Figure 5 illustrates in cross-section a portion of ridged balloon 30c. In Figure 5, like features to those shown in Figures 1-4 are indicated by the same reference numerals. Balloon 30c is fabricated from coextruded balloon blank portion 30b of Figure 4 (after withdrawal of strands 32 from channels 31) by heating and inflation of balloon blank portion 30b, in a conventional manner, to form a balloon similar in shape to balloon 11 of Figure 1. (The cross-section shown in Figure 5 is taken at a position on the balloon similar to cross-section 2-2 of Figure 1.) During the shaping process, layers 14a, 37, and 15a of balloon wall 12a (Figure 3) are stretched to a greater extent than connecting walls 35 and 36 (Figure 3) , creating a plurality of layered wall segments 40 (of shaped balloon wall 12b) separated by ridges 41. Each layered segment 40 is made up of innermost thin balloon wall layer 14b, outer¬ most thin balloon wall layer 15b, and intermediate thin balloon wall layer 37a. In the embodiment shown in Figure 5, intermediate layer 37a is thinner than either of layers 14b and 15b. Layers 14b and 37a and layers 37a and 15b are separated by channels 31, which have been coated with sili¬ cone oil 42 such that segments 40 are slip-layered segments which readily slide relative to one another, as described above. Thus, balloon 30c is a strong, soft, ridged medical balloon in which ridges 41 and slip-layered segments 40 provide differential stiffness about the circumference of the balloon for improved foldability. Additionally, ridges 41 anchor the layers to one another providing easier joining of the balloon to the catheter.

Figure 6 illustrates in cross-section a portion of yet another embodiment of the balloon described herein. In

Figure 6, like features to those shown in Figures 1-5 are indicated by the same reference numerals.

Ridged balloon 50 of Figure 6 includes non-compliant balloon wall 12c made up of slip-layered segments 40a sepa- rated by ridges 41. Segments 40a include channels 31 ar¬ ranged in single cylindrical array 33a. Channels 31 sepa¬ rate inner layer 14c and outer layer 15c, and are coated with silicone oil 42 as described above. Surrounding bal¬ loon wall 12c is elastomeric sleeve or elastic sleeve 51, fabricated of silicone rubber. Elastic sleeve 51 is of a size, thickness, and elastic modulus such that it fits closely around slip-layered balloon wall 12c in its com¬ pletely deflated or collapsed state, expands with balloon wall 12c as balloon 50 is inflated to its maximum diameter, and contracts as the pressure in balloon 50 is decreased during deflation, collapsing slip-layered balloon wall 12c into a tight, compact, generally cylindrical bundle. To further encourage the collapse of balloon wall 12c, as well as to permit more even expansion of elastic sleeve 51, coating 52 of silicone oil or other low-friction substance is disposed between sleeve 51 and balloon wall 12c. Elastic sleeve 51 and silicone oil coating 52 cooperate with slip layered segments 40a and ridges 41 to refold balloon 50 in a helical wrap about its axis.

Balloon wall 12c is fabricated by a process similar to that described above for balloon wall 12b. Elastic sleeve 51 may be applied to balloon wall 12c by, for example, prefabricating tubular elastic sleeve 51 by known means, e.g., extrusion, then swelling sleeve 51 by immersing in, e.g., Freon. Prefabricated balloon wall 12c may then be inserted into the enlarged sleeve, and the Freon evaporated to shrink sleeve 51 about balloon wall 12c.

Elastic sleeve 51 is shown in Figure 6 surrounding a ridged, non-compliant balloon wall having a single array of channels filled with a low-friction substance. However, a similar elastic sleeve may be utilized as part of any com¬ pliant or non-compliant slip-layered balloon embodiment in accordance with the present invention. The elastic sleeve of Figure 6 is described as silicone rubber. Other suitable materials for the sleeve are polyurethane elastomer, polyam- ide elastomer, polyolefin elastomer, thermoplastic elasto¬ mers (e.g., an engineering thermoplastic elastomer), or any elastomer considered suitable for use in medical catheters, as described above.

The slip-layered balloons described herein and the catheters made therefrom present many advantages over those of the prior art. For example, the balloons can combine small folded profiles, high burst pressures, and, optional¬ ly, low compliance with improved foldability, pliability, and softness, and high tensile strength. In particular, the ridged slip-layered balloon presents the advantages of fabrication by simple, commercially viable techniques, further improved foldability, and easier joining without significantly sacrificing softness and pliability. Also, the addition of the elastic sleeve described herein even further improves foldability and minimizes folded profile while eliminating sharp folded edges and adding considerable abrasion resistance to the balloon.