Process for preparing low density porous crosslinked polymeric materials

0001This invention relates to the preparation of low density, porous, crosslinked, polymeric materials. In one aspect, the invention relates to reducing curing time in a high internal phase emulsion polymerization process to manufacture low density porous crosslinked polymeric materials.

0002Open-cell polymeric foams can be used as a matrix to contain various liquids and gases and they are capable of commercial applications such as diapers and ion exchange resins. High absorption capacity, low density, porous polymer blocks can be prepared by polymerizing a specific type of water-in-oil emulsion known as a high internal phase emulsion (HIPE) having relatively small amounts of a continuous oil phase and relatively greater amounts of an internal water phase.

0003Such high absorption capacity, low density foams are prepared in US-A-4,522,953 by polymerizing the monomers in the oil phase of a high internal phase water-in-oil emulsion with a water-soluble polymerization initiator such as potassium persulfate. It has been found that, in order to obtain foams by this method with high absorption properties and low unreacted monomer content, curing must be conducted for 16 hours or longer at a temperature of 60°C. It would be desirable to reduce the curing time without significantly affecting the resulting foam properties.

0004Further, it is desirable to incorporate volatile monomers such as butadiene and isoprene as mentioned in US-A-5,149,720. However, such monomers are difficult to incorporate and tend to volatilize during the preparation and cure of the water-in-oil emulsion.

0005US-A-5210104 describes a process for the production of a porous crosslinked polymeric material which process comprises a) providing an aqueous stream comprising water and an electrolyte; b) providing a monomer stream comprising a mixture of polymerizable monomers including at least one vinyl monomer and a difunctional unsaturated crosslinking monomer, c) providing a surfactant to either of the above streams, d) mixing the streams of produce a water-in-oil high internal phase emulsion; e) polymerizing the emulsion in the presence of a catalyst.

0006DE-A-166779 describes the prepolymerisation of monomers in HIPE emulsion polymerisation.

0007It is therefore an object of the invention to provide a high internal phase water-in-oil emulsion polymerization process with short curing times. It is another object of the invention to provide an improved method to incorporate volatile monomers in a low density crosslinked polymeric material produced by the high internal phase water-in-oil emulsion process.

0008According to the invention, a process for the production of a porous crosslinked polymeric material is provided, comprising the steps of: <ul id="ul0001" list-style="none" compact="compact"><li>(a) providing an aqueous mixture comprising water and an electrolyte;</li><li>(b) mixing one or more vinyl monomers which volatilise at the temperature used in step (f) in the presence of an effective amount of an initiator, subjecting said monomer(s) to a free-radical-producing radiation source, so as to produce a monomer component having a Brookfield viscosity ratio of the treated monomer component to the untreated monomer component of greater than 1.00 at -78°C;</li><li>(c) adding one or more multifunctional unsaturated crosslinking monomers (i) to the one or more vinyl monomers prior to step (b), (ii) to the treated monomer component prior to emulsion forming step (e), or to both (i) and (ii) to form a treated monomer mixture;</li><li>(d) providing a surfactant to the aqueous mixture, the vinyl monomer, the treated monomer component, the treated monomer mixture, or any combinations of the aqueous mixture, vinyl monomer, treated monomer component and treated monomer mixture;</li><li>(e) combining and mixing said aqueous mixture and said treated monomer mixture in a mixing vessel under conditions effective to produce a water-in-oil emulsion having at least 90 weight percent, based on the emulsion, of water as the internal phase; and</li><li>(f) heating the emulsion at a temperature of at least about 25°C to polymerize and crosslink the treated monomers. A process in which a treated monomer component is added to a water-in-oil high internal phase emulsion is also provided.</li></ul>

0009Further, a process in which a branched peroxide is used as the polymerization initiator or an initiator is provided to produce a porous crosslinked polymeric material.

0010The time necessary for curing the emulsion is reduced without significantly affecting the resulting foam properties by treating the monomers prior to forming a water-in-oil high internal phase emulsion.

0011It has been found that a low density porous crosslinked polymeric material (hereinafter "foam") with high absorption capacity and low monomer content can be prepared in a shorter curing time (less than about 8 hours) by first treating (partially polymerizing) the monomers prior to formation of a water-in-oil high internal phase emulsion. Further, it has been now found that desirable open-cell isoprene or butadiene incorporated foams can be produced by the process of the invention.

0012Many monomers which are gaseous at room temperature (e.g., allene, methyl allene, 1,3-butadiene, vinyl chloride, vinyl fluoride) or low boiling liquids (e.g., isoprene, piperylene, chloroallenes, polyfluoro-olefins) may be useful in foam material prepared by a high internal phase water-in-oil emulsion method. However, their volatility introduces processing problems which are addressed by treating the monomers according to the inventive process.

0013In one embodiment of the inventive process, a foam is produced by treating at least a portion of a monomer mixture containing at least one vinyl monomer and a multifunctional unsaturated crosslinking monomer in the presence of an initiator or by a free-radical-producing radiation source, thereby producing a treated monomer mixture, then forming a water-in-oil high internal phase emulsion containing such treated monomer mixture, water as the internal phase and a surfactant and curing the treated monomers and monomers in such water-in-oil high internal phase emulsion.

0014In another embodiment, one or more vinyl monomers are treated in the presence of an effective amount of an initiator or by a free-radical-producing radiation source to produce a treated monomer component and the multifunctional unsaturated crosslinking monomer is added to the vinyl monomer prior to treating, to the treated monomer component prior to emulsion forming, or to both the vinyl monomer and treated monomer component to form a treated monomer mixture. Then, a curable high internal phase water-in-oil emulsion is formed containing the treated monomer mixture, optionally additional vinyl monomers, surfactant, and aqueous solution as the internal phase. Then the treated monomers and any monomers in the curable emulsion are cured.

0015In another embodiment, one or more vinyl monomers are treated in the presence of an effective amount of an initiator or by a free-radical-producing radation source to produce a treated monomer component. The treated monomer component is then added and mixed to a water-in-oil high internal phase emulsion containing, in the continuous phase of the emulsion, a monomer component containing one or more vinyl monomers, one or more multifunctional unsaturated crosslinking monomers, or a combination of these monomers to form a treated monomer emulsion. The water-in-oil high internal phase emulsion can be formed in a conventional manner such as those prepared in United States Patent Nos. 4,522,953, 5,149,720 and 5,189,070. Optionally additional vinyl monomers and additional multifunctional unsaturated crosslinking monomers can be added to the treated monomer component, to the emulsion, to the treated monomer emulsion, or to any combination of these. Multifunctional unsaturated crosslinking monomers can be added to one or more vinyl monomers to be treated and treated along with the vinyl monomers to form the treated monomer component. If only vinyl monomers are present in the emulsion, one or more multifunctional unsaturated crosslinking monomers can be added to one or more monomers to be treated, treated monomer component, to the emulsion, to the treated monomer emulsion, or to any combination of these in an effective amount to crosslink the monomers to form a foam. Then the treated monomers and any monomers in the treated monomer emulsion are cured.

0016The present invention provides a process for the production of a porous crosslinked polymeric material comprising polymerizing and crosslinking monomers in a water-in-oil high internal phase emulsion comprising a) a mixture of polymerizable monomers comprising at least one vinyl monomer which volatilises at the polymerization temperature and from 2 to 70 weight percent, based on the mixture, of at least one multifunctional unsaturated crosslinking monomer, b) at least 90 weight percent, based on the emulsion, of water as the internal phase, c) a surfactant, and d) a polymerization initiator which is an alkylperoxycarbonate branched at the 1-carbon position or an alkylperoxycarboxylate branched at at least one of the α-carbon or 1-carbon positions.

0017The term "treatment" or "treated" includes any oligomerization or partial polymerization of some of or all of the monomers. The treated monomers thus generally contain a mixture of monomers, and various oligomers/polymers.

0018The treatment may be carried out, for example, by mixing the entire monomer mixture together with an initiator, warming to an effective temperature for polymerization and oligomerizing the mixture, or a single component or selected components may be treated and then blended with the rest of the monomers desired in the continuous phase of the emulsion or blended into a water-in-oil high internal phase emulsion containing the rest of the monomers. Which approach is followed will be determined by the objectives desired, since the final molecular structure of the foam will be affected by which route is chosen, and the molecular structure achieved will affect resulting foam properties.

0019Various monomers may be used in the preparation of the foams, provided the monomers can volatilise at the temperature used in step (f) and can be dispersed in or form an oil phase of a water-in-oil high internal phase emulsion and have a polymerizable vinyl group. Suitable vinyl monomers include, for example, monoalkenyl arene monomers such as styrene, α-methylstyrene, chloromethylstyrene, vinylethylbenzene and vinyl toluene; acrylate or methacrylate esters such as 2-ethylhexyl acrylate, n-butyl acrylate, isobutyl acrylate, t-butyl acrylate, hexyl acrylate, n-butyl methacrylate, lauryl methacrylate , and isodecyl methacylate; conjugated diolefins such as butadiene, isoprene and piperylene; allenes such as allene, methyl allene and chloroallene; olefin halides such as vinyl chloride, vinyl fluoride and polyfluoro-olefins; and mixtures thereof.

0020Suitable crosslinking agents can be any multifunctional unsaturated monomers capable of reacting with the vinyl monomers. Multifunctional unsaturated crosslinking monomers include, for example, difunctional unsaturated crosslinking monomers such as divinyl benzene, diethylene glycol dimethacrylate, 1,3-butanediol dimethacrylate, and allyl methacrylate; tri-, tetra- and penta-functional unsaturated crosslinking monomers such as trimethylolpropane trimethacrylate, pentaerythritol tetramethacrylate, trimethylolpropane triacrylate, pentaerythritol tetraacrylate, glucose pentaacrylate, glucose diethylmercaptal pentaacrylate, and sorbitan triacrylate; and poly-functional unsaturated crosslinking monomers such as polyacrylates (eg. sucrose per(meth)acrylate and cellulose (meth)acrylate). Crosslinking monomers are typically present in an amount of from about 2 weight percent to about 70 weight percent, preferably from about 5 weight percent to about 40 weight percent based on the total monomer mixture. Some of these crosslinking monomers can be incorporated as a non-crosslinked monomer as long as at least about 2 weight percent of the crosslinking monomers are crosslinked.

0021Suitable initiators are monomer-soluble free radical polymerization initiators. Monomer-soluble (oil soluble) free radical polymerization initiators include, for example, azo compounds such as azobisisobutyronitrile (AIBN) and peroxides such as benzoyl peroxide, methyl ethyl ketone peroxides, di-2-ethylhexyl peroxydicarbonate and other alkylperoxycarbonates and alkylperoxycarboxylates including branched peroxides listed below. The initiator should be present in at least an amount effective to partially polymerize or oligomerise the monomers, but can also be in an amount effective to completely polymerize and crosslink the monomers. Typically the initiator can be present from 0.005 to 20 weight percent, preferably from 0.1 to 4 weight percent based on the monomers. The initiator is added to the monomer mixture containing one or more vinyl monomers with or without the crosslinking monomer and optionally a surfactant.

0022Preferably the monomer mixture is treated provide a ratio of viscosity of monomer mixture to water within the range of from 1000:1 to 1:2, more preferably from 50:1 to 1.5:2. Generally, the ratio of viscosity for a untreated monomer to water is about 1:2. The viscosity of the treated monomer mixture will vary depending on the monomer used.

0023The viscosity of the advanced monomer will be higher than the viscosity of the unadvanced monomer mixture. The viscosity is also dependent on temperature, and is quite low at ambient temperature, typically about 0.4 cp for the untreated monomer mixture, and up to about 100 cp for the treated monomer mixture. The viscosity will be expressed as a ratio between the viscosity of the monomer mixture and that of the treated monomer mixture, or the viscosity of the treated monomer mixture plus surfactant and the unadvanced mixture plus surfactant, because the absolute viscosity values are a function of temperature and whether or not the surfactant has been added to the mixture (normally addition of the surfactant raises the viscosity several-fold). If the treated mixture is in the numerator, and the untreated (fresh) in the denominator, then the ratio should be greater than 1.00. Preferably, the ratio is within the range from 1.03 to 50, more preferably from 1.07 to 30, most preferably from 1.15 to 15.

0024Since the viscosities are generally low, it is convenient to measure them at -78°C. Thus, the viscosity of a 1:1:3 weight percent mixture of styrene: divinyl benzene: 2-ethylhexyl acrylate is about 300 cp at -78°C. When 12 parts per 100 parts of weight of monomer mixture of a sorbitan monolaurate surfactant is added to the monomer mixture, the viscosity at -78°C increases to about 2900 cp. On treating the monomer/surfactant mixture the viscosity increases with time of treatment as described in the illustrative embodiment described below. The level of treatment preferred will depend on the particular mixture of monomers and the relative importance of rapid cure, volatility and properties.

0025To obtain the treated monomer mixture, the monomer mixture is heated in the presence of the initiator at a temperature above about 25°C, preferably at a temperature within the range of 25°C to 150°C, more preferably within the range of 50°C to 100°C for a time effective to form the treated monomer mixture with a desired viscosity, or irradiated by a free-radical-producing radiation source, such as gamma rays, electron beams, neutrons or ultra-violet light, for a time effective to form the treated monomer mixture with a desired viscosity. Such time is preferably within the range of about 5% to about 95% of the time necessary to form a solid mixture. The mixture is solid when the mixture no longer visibly deforms. The time necessary to form a solid mixture can be conveniently measured by a Solidity Test described below. More preferably, the treatment is done for a time within the range of 10% to 90%, most preferably from 35% to 88% of the time necessary to form a solid mixture. The treated monomer mixture which is preferred is one which forms a stable emulsion, cures rapidly, and yields a good porous polymeric product relative to the treated monomer mixture.

0026Treatment of the monomer mixture has various advantages besides the acceleration of cure time of the emulsion described above; among these is the ability to use comonomers which are not effective when used directly in the conventional emulsion system such as isoprene and butadiene, the reduction of volatiles from the emulsion curing line, the reduction of soluble organics in recycle water, the elimination of odors, and the use of low boiling monomer mixtures at atmospheric pressure.

0027To aid in the determination of level of treatment, the level of unsaturation in a mixture of monomers containing double bonds may be assessed by various means, such as infrared determination of the C=C stretching frequency, NMR examination of the vinylic carbons or protons, ultraviolet absorption measurements, dielectric constant, average molecular weight by HPLC, or other means of measuring molecular weight or unsaturation. One of the simplest and most direct measures is the reaction of halogen with olefinic bonds. Such tests result in determination of Bromine or Iodine number corresponding to the number of grams of halogen reacted with a certain amount (normally 100g) of the sample.

0028In one embodiment, if it is desirable to incorporate vinyl chloride for example, into a HIPE foam material, but toxicity concerns limit the amount of gas phase monomer tolerable in the process, the monomer can be mixed with comonomers, such as styrene, divinylbenzene, acrylates, and/or the like, in the presence of an initiator in a sealed reaction vessel, and the reaction vessel warmed to a temperature effective to begin an oligomerization and/or polymerization reaction. After the desired level of reaction has occurred, the vessel may be vented and depressured or evacuated, to remove unreacted vinyl chloride monomer, and leave a polymerizable liquid "treated monomer" mixture containing vinyl chloride molecules incorporated into larger molecular structures. This treated monomer then can be polymerized with less potential health hazard of handling vinyl chloride in the mixture, but with the property benefits of the final vinyl chloride containing polymer structure.

0029In another embodiment, low boiling monomers such as butadiene or isoprene can be readily incorporated in the HIPE foam material either by a monomer mix approach in which a mixture of one or more low boiling monomers, optionally other vinyl monomers, and a crosslinker is treated preferably until up to about 1/3 of the monomer is used, or the low boiling component itself can be treated and then blended with the higher boiling components.

0030For example, to incorporate butadiene in the porous polymeric product, an autoclave or a pressure reactor ("reaction vessel") can be charged with liquid butadiene, and purged of air by venting some of the butadiene, or alternatively, by chilling the butadiene in liquid nitrogen or in dry ice, and evacuating the gas cap of permanent gases. Optionally other vinyl monomers and crosslinkers can be added. Before charging the butadiene, an effective amount of a suitable initiator such as t-butyl peroxyisobutyrate to treat the butadiene is charged to the reaction vessel. The reaction vessel is then warmed to about 80°C-85°C to allow butadiene to react for a time sufficient to lower the butadiene partial pressure. The treatment reaction for low boiling monomers is preferably carried out until the absolute pressure in the reaction vessel at room temperature is less than about 14.7 psia (or below boiling) at atmospheric pressure. For example, if pressure of less than 14.7 psia is required at around 27°C (80°F) to be able to handle the monomers at 27°C (80°F) without having it boil, the absolute pressure in the reaction vessel should be reduced to a pressure at most of about 60 psia at 82°C to indicate a level of reaction just sufficient to prevent boiling at 27°C (80°F). Once the desired pressure range is reached at the reaction temperature, the treated monomer mixture can be optionally blended with other monomer components to further lower the vapor pressure of the monomer mixture and make the emulsification and curing process simpler. A wide range of temperature may be used to perform the treatment depending on the initiator and the monomer used. For example, for 1,3-butadiene, higher or lower temperatures than about 80°C-85°C may be used, but the temperature should be below about 152°C, the critical temperature of butadiene, so that the monomer may remain in the liquid instead of the supercritical gas state. In addition, the temperature should be below the ceiling temperature of the oligomers formed to allow polymerization to occur. On the low temperature side, the temperature should be high enough to give a satisfactory rate with whatever initiator system is used. As a practical matter, that means that for many low boiling volatile monomers, the temperature preferred for the treatment reaction will be within the range from room temperature to 150°C, more preferably from 50°C to 100°C.

0031For the inventive process, it is also desirable to use a fast curing initiator to reduce the cure time. It has been found that the known oil-soluble initiators reported in the literature such as benzoyl peroxide and AIBN are generally slower than the water-soluble potassium persulfate initiator and provide incomplete curing of the resulting foams without addition of additional polymerization initiators after the formation of the emulsion or in the aqueous mixture. Therefore, it was desirable to develop a faster curing monomer-soluble polymerization initiator.

0032It has been found that branched alkyl carbonate peroxides branched at the 1-carbon position or branched alkyl carboxylate peroxides branched at the α-carbon position and/or 1-carbon position (hereinafter "branched peroxides") cure faster than the conventional oil-soluble initiator such as benzoyl peroxide. This branching at the 1-carbon position and/or α-carbon position can be secondary or tertiary.

0033The preferred branched alkyl carbonate peroxide can be represented by the formula: where R¹ is independently C₁ to C₁₆ hydrocarbon groups or hydrogen in which at least two of the R¹ are hydrocarbon groups. Hydrocarbon groups can be alkyl, alkenyl or aryl <chemistry id="chem0001" num="0001"><img file="EP0712425B1_D0001.tif" /></chemistry> groups.

0034The preferred branched alkyl carboxylate peroxide can be represented by the formula: <chemistry id="chem0002" num="0002"><img file="EP0712425B1_D0002.tif" /></chemistry> where R¹ and R² are independently C₁ to C₁₆ hydrocarbon groups or hydrogen in which at least two of the R¹ or R² are hydrocarbon groups. Preferably at least two of both R¹ and R² are hydrocarbon groups. Hydrocarbon groups can be alkyl, alkenyl or aryl groups.

0035Examples of the branched peroxides include t-butyl peroxyisobutyrate, t-butyl peroxycrotonate, t-butyl peroxypivalate, di-isobutyryl peroxide, di-t-butyl diperoxyphthalate, t-butyl perbenzoate, cumylperoxy neodecanoate, 2,5-dimethyl-2,5-bis(benzoylperoxy)hexane, 2,5-dimethyl-2,5-bis(2-ethylhexanoylperoxy)hexane, t-butyl peroctoate, 1,1,3,3-tetramethylbutylperoxy-2-ethyl hexanoate, dicyclohexyl peroxydicarbonate, di(sec-butyl) peroxydicarbonate, diisopropyl peroxydicarbonate, and t-butyl peroxyisopropylcarbonate. Commercial examples of the branched peroxide include Lupersol™ 11, Lupersol™ 80, Lupersol™ 118M75, Lupersol™ 225, Lupersol™ 227, Lupersol™ 229, Lupersol™ 256, Lupersol™ 259, Lupersol™ KBD, Lupersol™ TBIC, Luperox™ 118, Luperox™ 229, and Luperox™ IPP (from Atochem North America). The most preferred advancement and/or polymerization initiator is t-butyl peroxyisobutyrate.

0036These branched peroxide initiators also improve the conventional water-in-oil high internal phase polymerization processes such as those described in U.S. Patent No. 4,522,953 where no treatment takes place prior to the formation of an emulsion. Further these branched peroxide initiators are also useful when the initiator is added after the formation of the emulsion as described in U.S. Patent No. 5,210,104, issued May 11, 1993.

0037When initiators such as benzoyl peroxide, AIBN and methyl ethyl ketone peroxide are used, additional polymerization initiator should be added in the aqueous mixture or in the emulsion. When such polymerization initiator is added to the emulsion, the polymerization initiators can be, for example, oil-soluble (monomer-soluble) initiators such as branched peroxides listed above or water-soluble initiators such as potassium or sodium persulfate and various redox systems such as ammonium persulfate together with sodium metabisulfite. When such a polymerization initiator is added to the aqueous mixture, the polymerization initiators can be any of the water-soluble initiators mentioned above.

0038When the additional polymerization initiator is added to the emulsion, it can optionally be blended into the emulsion by any blending technique such as, for example, a static mixer or a pin mixer at a low shear rate, to form a curable water-in-oil high internal phase emulsion. The rate of shear must be high enough to blend the initiator but low enough not to allow the emulsion to coalesce or liquify.

0039The surfactant used in making the high internal phase emulsion can be added to the aqueous phase or monomer phase (monomer mixture) depending on the solubility of the surfactant used. Suitable surfactants include, for example, nonionic surfactants such as sorbitan esters (eg., sorbitan monooleate and sorbitan monolaurate), glycerol esters (eg. glycerol monooleate and glycerol monoricinoleate), PEG 200 dioleate, partial fatty acid esters of polyglycerol, and castor oil 5-10 EO; cationic surfactants such as ammonium salts (eg., distearyl dimethyl ammonium chloride and dioleyl dimethyl ammonium chloride); and anionic surfactants such as bis-tridecyl sulfosuccinic acid salt. Commercially available surfactants include, for example, SPAN@ emulsifying agents 20, 40, 60, 65, 80 and 85 (from Fluka Chemical Corp. or Aldrich Chemical Co.), EMSORB 2502 (from Henkel) and ALKAMULS® sorbitan esters SML, SMO, SMS, STO and ALKAMULS® sorbitan ester ethoxylates PMSL-20 and PSMO-20 (from Alkaril Chemicals Ltd.) among others. The surfactant is present in an amount effective to form a water-in-oil high internal phase emulsion (HIPE). Preferably, the surfactant is present from about 2 to about 40% by weight, more preferably about 5 to about 25% by weight based on the monomers.

0040To form a polymeric foam product with suitable density and high absorption capacity, the water-in-oil high internal phase emulsion (HIPE) typically contains, as the internal phase, at least about 90 weight percent, based on the emulsion, of water, corresponding to a water to oil weight ratio of at least about 9:1, more preferably at least about 95 weight percent of water, most preferably at least about 97 weight percent of water, corresponding to a water to oil weight ratio of at least about 33:1.

0041The internal aqueous phase can preferably contain a water-soluble electrolyte to stabilize the HIPE and to make the foam more water wettable. Suitable electrolytes include inorganic salts (monovalent, divalent, trivalent or mixtures thereof), for example, alkali metal salts, alkaline earth metal salts and heavy metal salts such as halides, sulfates, carbonates, phosphates and mixtures thereof. Such electrolyte includes, for example, sodium chloride, sodium sulfate, potassium chloride, potassium sulfate, lithium chloride, magnesium chloride, calcium chloride, magnesium sulfate, aluminum chloride and mixtures thereof. Mono- or di-valent salts with monovalent anions such as halides are preferred.

0042The curable water-in-oil high internal phase emulsions (curable HIPE) can be cured in a batch process or in a continuous process. In a batch process, the curable HIPE is collected in a suitable container with the desired shape and cured at a temperature of at least about 25°C for a time effective to polymerize and to cure the monomers. The HIPE is preferably polymerized and crosslinked (cured) at a temperature within the range of about 25°C to about 90°C, as long as the emulsion is stable at the curing temperature.

0043Alternatively, a multiple-step process as described in a United States Patent No. 5,189,070 can also be used, the disclosure of which is herein incorporated by reference. In the multi-step process the emulsion is precured at a temperature of less than about 65°C until the emulsion has a Rheometrics dynamic shear modulus of greater than about 500 pascal, (lightly gelled, having a consistency like a jelly or a gelatin referred to as "gel"), then cured at a temperature of above about 70°C for a time effective to cure the gel. The cure temperature can be as high as about 175°C under suitable pressure to prevent water from boiling.

0044The emulsions can be heated, for example, by hot water, hot air, steam, IR, RF, microwave or ohmic heating. The HIPE should be cured until the desired properties are obtained. Typically, to obtain a cured foam, the emulsions should be cured for at least about 4 hours at 60°C or at least about 1/2 hour at 60°C then 3 hours at a temperature of above about 70°C. Generally, the extent of reaction after curing is at least about 85% of the monomers, preferably at least about 90%, more preferably at least about 95% (i.e., less than about 5% of free monomers), most preferably at least about 99% (i.e., less than about 1% of free monomers) in order to obtain good properties.

0045These foams can be post-cured to improve the foam properties. Better properties such as, for example, increased free swell (i.e., amount of liquid a foam can initially absorb), and/or good resistance to compression deflection (i.e., retention of liquid under load) can be obtained depending on the monomer formulation by post-curing the foam at a temperature of above about 75°C, preferably greater than 90°C, by steam, hot air or other heating source. Such heating may be performed initially in a heat exchanger, oven, over heated rollers or by other means.

0046When the temperature is near or above the boiling point of water, pressure is preferably applied to keep the water in the liquid phase and to obtain better properties. If desired, the pressure may be lowered to boil some of the water, but in normal practice the water will be maintained in the liquid state to stabilize the monomer. The use of pressure to maintain the aqueous phase and oil phase in the liquid state allows very rapid curing of emulsions at very high temperatures, provided the emulsions are stable at the high temperatures used. Pressure can be applied to the emulsion, if desired, at a pressure generally from above atmospheric pressure, typically within the range of about atmospheric pressure to about 1.03 MPa (150 psig). When the temperature is about 100°C, a pressure from about 7 to 70 kPa gauge (about 1 to 10 psig) is sufficient; when the temperature is about 130°C, a pressure from about 210 to 480 kPa gauge (about 30 psig to 70 psig) is preferred.

0047Once the curing and/or post-curing process is completed, the water incorporated in the foam may be squeezed out, dried by heat or flashed by lowering the pressure to a suitable level to evaporate the remaining liquid to give the desired degree of dryness in the product foam. These drying techniques will preferably be used after the desired state of cure is developed in the foam material.

0048These foams prepared by the inventive process may be washed prior to, after or between drying stages to yield an absorbent block which is especially useful for the absorption of liquids. Typically, these foams are washed to reduce the electrolyte content of the foam with a solvent such as, for example, an alcohol, a low concentration electrolyte solution (lower concentration than the water phase) such as 1% calcium chloride solution or deionized water. The washed foams can be conveniently dried by squeezing the water and/or solvent out of the foams and air or heat drying.

0049The foams produced by the inventive process possess high absorption capacities and good uniform properties especially suitable for use as liquid absorbent articles.

Illustrative Embodiment

0050The following illustrative embodiments describe the process of the invention and are provided for illustrative purposes and are not meant as limiting the invention.

Washing and Drying Method

0051The following washing and drying method was used for all of the examples below: After the foam blocks were cured, the blocks were sliced to 0.35 inches (0.89 cm) thickness. Then, each individual slice was placed on a 0.04 inch (0.1 cm) mesh screen between a 9" X 6.75" (22.9 cm X 17.1 cm) stainless steel plate that allowed the slice to be squeezed to a 0.045 inch (1.14 mm) thickness. The squeezed slices were placed in an Arbor-press made by DAKE and the calcium chloride solution was squeezed out. The slices were then washed and squeezed twice by soaking the slices in 7.6 liters (2 US gallons) of 1% calcium chloride solution and placing in the Arbor-press. Then, after the slices were squeezed, a paper towel was placed on both sides of the washed slices which were squeezed again to remove excess water from the slices. The slices were then placed in an oven at a temperature of 60°C for 4 hours to dry. The washed and dried foam slices were analyzed for physical properties as discussed below.

TESTING METHODS

Solidity Test:

0052A flat-tipped probe of about 6 mm diameter is placed on top of a treated monomer mixture to create a pressure at the flat-tip of about 2.1 kPa (0.3 psi). The ease and penetration of the object into the gel was measured. The monomer mixture is considered solid when the object no longer penetrates or penetrates less than about 1 mm.

Viscosity:

0053At selected times, aliquots of approx. 5 ml are removed and placed in 8 dram vials. If the aliquots are above ambient temperature, the aliquots are then quickly cooled in wet ice to ambient temperature (approx. 24 °C). The aliquots are chilled in acetone/dry ice slush bath for approx. 10 minutes to a temperature of approx. -78°C. The warm aliquots may be chilled immediately to approx. -78°C. While the aliquots are kept cold, the viscosity is run using Brookfield Viscometer, Model RVTD equipped with a #6 Spindle (manufactured by Brookfield Engineering Lab, Stoughton, Massachusetts).

Bromine Test:

0054Determination of bromine numbers is done potentiometrically using a "bromine number solvent" consisting of acetic acid, trichloroethylene, methanol with 1% sulfuric acid and 1/5% water from Ricca Company. Alternatively, a suitable solvent is 1400 ml of acetic acid, 268 ml of methylene chloride, 268 ml of methanol, and 36 ml of a 1:5 mixture of sulfuric acid and water. 100 Milligrams of sample is dissolved in 100 ml of the solvent and then titrated with 0.5N bromine/bromate titrant in a Kyoto AT310 potentiometric titrator. The titration is done in a sealed cell kept between 0°C to 5°C, using a platinum double ring electrode. The level of saturation of the solution with bromine is followed potentiometrically, and the bromine number values are reported as grams of bromine reacted per 100 grams of sample.

Free Swell ("FS")/Dry Thickness ("DT")/Foam Density ("FD")/Percent Strain/Resistance to Compression Deflection ("RTCD"):

0055A 2"x 2" (5.08 x 5.08 cm) square is cut from a foam slice. The thickness of the foam sample is measured while it is dry ("dry thickness") using a dead weight thickness gage (a digital linear gage model EG-225 made by Ono Sokki) exerting 50 grams force applied to a 1.60" diameter disk. This thickness is called the "caliper." The foam square is soaked in warm 88°F (31°C) Syn-Urine from Jayco for 17 minutes. From the 2" x 2" (5.08 x 5.08 cm) square, a circle of 1.129" (2.868 cm) diameter is cut. This disk is re-equilibrated in the Syn-Urine for 5 minutes. The wet disk is then weighed ("initial wet weight").

0056The thickness of the wet sample is measured using the same load gage ("initial wet caliper"). The disk is then placed under a 5.1 kPa (0.74 psi) stress where stress is the total dead weight applied to the gage divided by the cross-sectional area. The thickness of the disk is measured under this stress after 15 minutes ("wet caliper"). After 15 minutes, the specimen disk is weighed to measure the retained fluid.

0057The excess urine is squeezed from the disk and the remainder of the square from which it was cut. The foam is placed in boiling deionized water for 15 minutes. The foam is washed this way several times to remove inorganics. The foam is then removed, blotted dry, then placed in a vacuum oven at 60-70 °C and dried until the foam has fully expanded. The weight of the dry disk sample is then determined in grams ("final dry weight").

0058The following values were calculated from the above measurements. <ul id="ul0002" list-style="none" compact="compact"><li>Free swell= initial wet weight/final dry weight</li><li>Resistance to Compression Deflection (RTCD)= wet weight after load at 15 minutes/final dry weight</li><li>Foam Volume (cm³)=<maths id="math0001" num=""><math display="block"><mrow><mtext>%</mtext><mtext mathvariant="italic">Strain</mtext><mtext>= </mtext><mfrac><mrow><mtext mathvariant="italic">initial wet caliper - wet caliper</mtext></mrow><mrow><mtext mathvariant="italic">initial wet caliper</mtext></mrow></mfrac><mtext></mtext><mtext mathvariant="italic">X</mtext><mtext> 100</mtext></mrow></math><img file="EP0712425B1_D0003.tif" /></maths> (diameter/2)² x 3.142 x initial wet caliper    based on a 1.129" diameter circle cut (in cm)</li><li>Foam Density (mg/cm³)= final dry weight x 1000/Foam Volume</li></ul>

Vertical Wicking Time ("VWT"):

0059From a foam slice, cut at 0.35 inches (0.89 cm) thickness, a 1 to 2 cm wide strip is cut, greater than 5 cm in length. The strip of foam is clamped or taped to a metal ruler, with the bottom of the foam strip flush with the 0 mark on the ruler. The ruler and foam are placed in a container of approximately 100 ml Syn-Urine from Jayco, in an incubator at 99°F (37°C) so the bottom of the strip (0 mark) is barely touching the surface of the Syn-Urine (less than lmm). The Syn-Urine is dyed with food coloring to more easily monitor its absorption and rise in the foam. A stopwatch is used to measure the time required for the liquid level to reach 5 cm vertical height in the foam sample.

Percent Free Liquid:

0060The amount of unabsorbed water was measured by decanting fluid from the foam in the container after pre-curing or curing stage and weighing the decanted fluid.

EXAMPLE 1

0061This example demonstrates the change in viscosity as measured at -78°C as the monomer mixture is advanced according to the invention.

0062A 1:1:3 weight ratio of styrene: divinyl benzene: 2-ethylhexyl acrylate was mixed to produce a monomer mixture and viscosity was measured at -78°C. (Commercial divinyl benzene containing 55% divinyl benzene from Aldrich Chemical Co. was used.) To this monomer mixture, 12 parts by weight for 100 parts by weight of the monomer mixture of a sorbitan monolaurate surfactant (SPAN® 20 emulsifying agent from Fluka Chemical Corp. or Aldrich Chemical Co.) was added and viscosity was measured at -78°C. To this mixture 1 part by weight for 100 parts by weight of the monomer mixture of Lupersol™ 80 initiator (t-butyl peroxyisobutyrate from Atochem North America) was added. The resulting mixture was treated at 75°C and viscosity was measured at -78°C periodically as listed in Table 1 below. The viscosities were measured as described above. <tables id="tabl0001" num="0001"><table frame="all"><title>TABLE 1</title><tgroup cols="3" colsep="1" rowsep="0"><colspec colnum="1" colname="col1" colwidth="52.50mm" /><colspec colnum="2" colname="col2" colwidth="52.50mm" /><colspec colnum="3" colname="col3" colwidth="52.50mm" /><thead valign="top"><row rowsep="1"><entry namest="col1" nameend="col1" align="left">mixture</entry><entry namest="col2" nameend="col2" align="left">Time of treatment (min)</entry><entry namest="col3" nameend="col3" align="left">Viscosity (cp)</entry></row></thead><tbody valign="top"><row><entry namest="col1" nameend="col1" align="left">Monomer</entry><entry namest="col2" nameend="col2" align="right">--</entry><entry namest="col3" nameend="col3" align="center">300</entry></row><row><entry namest="col1" nameend="col1" align="left">Monomer/surfactant</entry><entry namest="col2" nameend="col2" align="right">0</entry><entry namest="col3" nameend="col3" align="center">2900</entry></row><row><entry namest="col1" nameend="col1" align="left">Monomer/surfactant</entry><entry namest="col2" nameend="col2" align="right">16</entry><entry namest="col3" nameend="col3" align="center">3060</entry></row><row><entry namest="col1" nameend="col1" align="left">Monomer/surfactant</entry><entry namest="col2" nameend="col2" align="right">41</entry><entry namest="col3" nameend="col3" align="center">3260</entry></row><row><entry namest="col1" nameend="col1" align="left">Monomer/surfactant</entry><entry namest="col2" nameend="col2" align="right">72</entry><entry namest="col3" nameend="col3" align="center">3930</entry></row><row><entry namest="col1" nameend="col1" align="left">Monomer/surfactant</entry><entry namest="col2" nameend="col2" align="right">84</entry><entry namest="col3" nameend="col3" align="center">5600</entry></row><row rowsep="1"><entry namest="col1" nameend="col1" align="left">Monomer/surfactant</entry><entry namest="col2" nameend="col2" align="right">120</entry><entry namest="col3" nameend="col3" align="center">infinite</entry></row></tbody></tgroup></table></tables>

Example 2

0063This example demonstrates the change in bromine numbers as the monomer mixture is advanced according to the invention.

0064A 1:1:3 weight ratio of styrene: divinyl benzene: 2-ethylhexyl acrylate was mixed to produce a monomer mixture. (Commercial divinyl benzene containing 55% divinyl benzene from Aldrich Chemical Co. was used.) To this monomer mixture, 12 parts by weight for 100 parts by weight of the monomer mixture of a sorbitan monolaurate surfactant (SPAN® 20 emulsifying agent from Fluka Chemical Corp. or Aldrich Chemical Co.) was added and bromine number was measured as described above. To this mixture 1 part by weight for 100 parts by weight of the monomer mixture of Lupersol™ 80 initiator (t-butyl peroxyisobutyrate from Atochem North America) was added. The resulting mixture was treated at 72°C and bromine number was measured at 20 minute intervals as described above. The bromine numbers are shown in Table 2 below. <tables id="tabl0002" num="0002"><table frame="all"><title>TABLE 2</title><tgroup cols="2" colsep="1" rowsep="0"><colspec colnum="1" colname="col1" colwidth="78.75mm" /><colspec colnum="2" colname="col2" colwidth="78.75mm" /><thead valign="top"><row rowsep="1"><entry namest="col1" nameend="col1" align="center">Time of treatment (min)</entry><entry namest="col2" nameend="col2" align="center">Bromine Number</entry></row></thead><tbody valign="top"><row><entry namest="col1" nameend="col1" align="center">--</entry><entry namest="col2" nameend="col2" align="center">49^a</entry></row><row><entry namest="col1" nameend="col1" align="center">20</entry><entry namest="col2" nameend="col2" align="center">50</entry></row><row><entry namest="col1" nameend="col1" align="center">40</entry><entry namest="col2" nameend="col2" align="center">48</entry></row><row><entry namest="col1" nameend="col1" align="center">80</entry><entry namest="col2" nameend="col2" align="center">46</entry></row><row><entry namest="col1" nameend="col1" align="center">100</entry><entry namest="col2" nameend="col2" align="center">45</entry></row><row rowsep="1"><entry namest="col1" nameend="col1" align="center">120</entry><entry namest="col2" nameend="col2" align="center">43</entry></row></tbody></tgroup><tgroup cols="2" colsep="0" rowsep="0"><colspec colnum="1" colname="col1" colwidth="78.75mm" /><colspec colnum="2" colname="col2" colwidth="78.75mm" /><tbody valign="top"><row><entry namest="col1" nameend="col2" align="justify">^a Numbers are +/- 2.</entry></row></tbody></tgroup></table></tables>

0065As seen from the above table, the available double bonds have decreased 14% over the treatment time. The particular test used did not give a reliable indication for acrylate double bonds, which reacted more slowly than the styrenic double bonds. Thus, the bromine numbers are low relative to the theoretical numbers for the monomer mixture. However, the data show a clear drop in number of reactive double bonds with time of treatment which can be used to monitor the degree of treatment.

Example 3

0066This example demonstrates the change in bromine numbers as the monomer mixture containing a volatile monomer is treated according to the invention.

00673:2 weight ratio of isoprene:divinyl benzene were mixed to produce monomer mixtures. (Commercial divinyl benzene containing 55% divinyl benzene from Aldrich Chemical Co. was used.) To these monomer mixtures, 12 parts by weight for 100 parts by weight of the monomer mixtures of a sorbitan monolaurate surfactant (SPAN@ 20 emulsifying agent from Fluka Chemical Corp. or Aldrich Chemical Co.) was added. Bromine number of the untreated mixture was measured as described above. To these mixtures 1 weight percent for 100 weight percent of the monomer mixtures of Lupersol™ 225 initiator (di(sec-butyl) peroxydicarbonate), Lupersol™ 80 initiator (t-butyl peroxyisobutyrate), Lupersol™ 223 initiator as comparative example (di(2-ethylhexyl) peroxydicarbonate), and Lupersol™ 188M75 initiator (alpha-cumyl peroxyneodecanoate) all from Atochem North America, were added as listed below. The resulting mixture was treated at the temperatures listed below and bromine numbers were measured as described above. The high temperature treatment runs were performed in an autoclave blanketed with nitrogen under pressures up to 400 psig. The bromine numbers are shown in Table 3 below. <tables id="tabl0003" num="0003"><table frame="all"><title>TABLE 3</title><tgroup cols="4" colsep="1" rowsep="0"><colspec colnum="1" colname="col1" colwidth="39.37mm" /><colspec colnum="2" colname="col2" colwidth="39.37mm" /><colspec colnum="3" colname="col3" colwidth="39.37mm" /><colspec colnum="4" colname="col4" colwidth="39.37mm" /><thead valign="top"><row rowsep="1"><entry namest="col1" nameend="col1" align="left">Initiator Number</entry><entry namest="col2" nameend="col2" align="center">Temperature (°C)</entry><entry namest="col3" nameend="col3" align="center">Time (min)</entry><entry namest="col4" nameend="col4" align="center">Bromine</entry></row></thead><tbody valign="top"><row><entry namest="col1" nameend="col1" align="left">   --</entry><entry namest="col2" nameend="col2" /><entry namest="col3" nameend="col3" /><entry namest="col4" nameend="col4" align="right">176^a</entry></row><row><entry namest="col1" nameend="col1" align="left">Lupersol™ 225</entry><entry namest="col2" nameend="col2" align="center">74 - 78</entry><entry namest="col3" nameend="col3" align="center">244</entry><entry namest="col4" nameend="col4" align="right">140</entry></row><row><entry namest="col1" nameend="col1" align="left">   "</entry><entry namest="col2" nameend="col2" align="center">80 - 87</entry><entry namest="col3" nameend="col3" align="center">244</entry><entry namest="col4" nameend="col4" align="right">160</entry></row><row><entry namest="col1" nameend="col1" align="left">Lupersol™ 80</entry><entry namest="col2" nameend="col2" align="center">80 - 87</entry><entry namest="col3" nameend="col3" align="center">120</entry><entry namest="col4" nameend="col4" align="right">148</entry></row><row><entry namest="col1" nameend="col1" align="left">   "</entry><entry namest="col2" nameend="col2" align="center">80 - 88</entry><entry namest="col3" nameend="col3" align="center">252</entry><entry namest="col4" nameend="col4" align="right">solid</entry></row><row><entry namest="col1" nameend="col1" align="left">Lupersol™ 223</entry><entry namest="col2" nameend="col2" align="center">80 - 86</entry><entry namest="col3" nameend="col3" align="center">180</entry><entry namest="col4" nameend="col4" align="right">176</entry></row><row rowsep="1"><entry namest="col1" nameend="col1" align="left">Lupersol™ 188M75</entry><entry namest="col2" nameend="col2" align="center">80 - 86</entry><entry namest="col3" nameend="col3" align="center">240</entry><entry namest="col4" nameend="col4" align="right">172</entry></row></tbody></tgroup><tgroup cols="4" colsep="0" rowsep="0"><colspec colnum="1" colname="col1" colwidth="39.37mm" /><colspec colnum="2" colname="col2" colwidth="39.37mm" /><colspec colnum="3" colname="col3" colwidth="39.37mm" /><colspec colnum="4" colname="col4" colwidth="39.37mm" /><tbody valign="top"><row><entry namest="col1" nameend="col4" align="justify">^aNumbers are +/- 5.</entry></row></tbody></tgroup></table></tables>

0068As seen from the above table, the available bromine double bonds have decreased about 21% over the treatment time. Since the isoprene polymers mostly retain a reactive double bond for each isoprene unit, the 21% observed decrease in double bonds represents from 21% to 42% of complete polymerization cure (depending on whether the monomer has both or only one bond reacted).

0069As can be seen from the table, Lupersol™ 80 initiator gives a greater degree of treatment at a shorter time when held at 80 to 87°C although the Self Accelerating Decomposition Temperature (SADT) of Lupersol™ 80 initiator is higher than for Lupersol™ 225, 223 or 188M75 initiators (80°C versus 0°C, 0°C and 15°C respectively). The amount of treatment is not just a function of the amount of peroxide decomposed but the matching of the rate of decomposition to the rate of polymerization. (The half life at 80°C of Lupersol™ 80 initiator (L80) is ca.7.5 hrs, while Lupersol™ 223 initiator (L223) is 10 min, Lupersol™ 225 initiator (L225) is 13 min, and Lupersol™ 188M75 initiator (L188M75) is ca. 1 hr; at 60°C, the half lives are roughly L80 =110 hrs, L223 = 0.83 hrs, L225 = 1.4 hrs, and L188M75 = ca 12.5 hrs, Lucidol Pennwalt, "Evaluation of Organic Peroxides from Half-Life Data", Lucidol Div. of Pennwalt, 1740 Military Road, Buffalo, New York 142140) However, even assuming roughly the same rates of decomposition, the 1-position or α-position branched peroxides such as di(sec-butyl) peroxydicarbonate, t-butyl peroxyisobutyrate and alpa-cumyl peroxyneodecanoate are clearly more effective at treating the monomers than peroxides not branched at the 1-position or α-position such as di(2-ethylhexyl) peroxydicarbonate.

Example 4

0070This example demonstrates the reduction in cure time with increased treatment time according to the invention.

0071A 1:1:3 weight ratio of styrene: divinyl benzene: 2-ethylhexyl acrylate were mixed to produce a monomer mixture. (Commercial divinyl benzene containing 55% divinyl benzene from Aldrich Chemical Co. was used.) To this monomer mixture, 12 parts by weight for 100 parts by weight of the monomer mixture of a sorbitan monolaurate surfactant (SPAN® 20 emulsifying agent from Fluka Chemical Corp. or Aldrich Chemical Co.) was added and bromine number was measured as described above. To this mixture 1 part by weight for 100 parts by weight of the monomer mixture of Lupersol™ 80 initiator (t-butyl peroxyisobutyrate from Atochem North America) was added. The resulting mixture was treated at 80°C for a specified time as listed below. A 30:1 water-in-oil emulsion was made by mixing a 70°C aqueous solution of 10% CaCl₂ and 0.14% potassium persulfate into the treated monomer mixtures with an air motor and a paint mixer. Each emulsion was cured in a 60°C water bath in a 118 cm³ (4 fluid oz.) bottle. Cure Time was determined by determining the time necessary for the emulsion to support a 2.1 kPa (0.3 psi) flat tipped probe at the surface of the emulsion and listed below in Table 4. <tables id="tabl0004" num="0004"><table frame="all"><title>TABLE 4</title><tgroup cols="2" colsep="1" rowsep="0"><colspec colnum="1" colname="col1" colwidth="78.75mm" /><colspec colnum="2" colname="col2" colwidth="78.75mm" /><thead valign="top"><row rowsep="1"><entry namest="col1" nameend="col1" align="center">treatment Time (min)</entry><entry namest="col2" nameend="col2" align="center">Cure Time (min)</entry></row></thead><tbody valign="top"><row><entry namest="col1" nameend="col1" align="right">0</entry><entry namest="col2" nameend="col2" align="right">144</entry></row><row><entry namest="col1" nameend="col1" align="right">16</entry><entry namest="col2" nameend="col2" align="right">136</entry></row><row><entry namest="col1" nameend="col1" align="right">29</entry><entry namest="col2" nameend="col2" align="right">121</entry></row><row><entry namest="col1" nameend="col1" align="right">41</entry><entry namest="col2" nameend="col2" align="right">112</entry></row><row><entry namest="col1" nameend="col1" align="right">53</entry><entry namest="col2" nameend="col2" align="right">94</entry></row><row><entry namest="col1" nameend="col1" align="right">111</entry><entry namest="col2" nameend="col2" align="right">61</entry></row><row rowsep="1"><entry namest="col1" nameend="col1" align="right">125</entry><entry namest="col2" nameend="col2" align="right">Solid during advancement</entry></row></tbody></tgroup></table></tables>

Example 5

0072This example demonstrates preparation of a low density crosslinked polymeric material by treating the monomer mixture according to the invention.

0073In a container, 100.09 g of a monomer mixture (19.11 wt% styrene, 20.63 wt% divinyl benzene and 60.26 wt% of 2-ethyl hexyl acrylate) is mixed with 1.06 g of t-butyl peroxyisobutyrate (Lupersol™ 80 from Atochem North America) . For divinyl benzene, commercial divinyl benzene containing 55% divinyl benzene from Aldrich Chemical Co. was used. To 80.03 g of the initiator-containing monomer mixture which has been heated for 12 minutes in a 80°C water bath, 10 g of Span ® 20 emulsifying agent (sorbitan monolaurate from Fluka Chemical Corp. or Aldrich Chemical Co.) was added to give a 12.35% surfactant-containing mixture ("mixture-A" 12 minutes aging).

0074While stirring with a paint stirrer (model 06200 PM-70 made by SHUR-LINE® Inc.) attached to an air motor (#C-1712 1/2hp motor made by Arrow Engineering Co.), 600 cc of aqueous 10 wt% CaCl₂ and 0.15 wt% potassium persulfate solution was slowly added to 20.03 g of mixture-A which had been heated at 80°C for 16 minutes. A water-in-oil high internal phase emulsion formed with a desired 30:1 water-to-oil ratio. 60.87 g of the resulting emulsion was poured into a 118 cm³ (4 fluid oz.) jar and labeled B1. The remaining emulsion (521.41 g) was poured into a 1.4 liter (3 US pint) tub and labeled B2. The emulsion was cured by placing this jar B1 in a 60°C water bath and periodically tested with a flat-tipped probe of about 6 mm diameter which creates a pressure at the flat-top of about 0.3 psi ("the probe") by placing the probe on top of the emulsion. After 136 minutes, the probe sat on top of the foam and did not sink. The emulsion in the tub was cured by heating the tub B2 in a 60°C incubator for 24 hours. 3.13 % of free water was poured off from the resulting foam.

0075While stirring in a similar manner to above, 600 cc of aqueous 10 wt% CaCl₂ and 0.15 wt% potassium persulfate solution was slowly added to 20.29 g of mixture-A which had been heated at 80°C for 29 minutes. 59.78 g of the resulting emulsion was poured into a 118 cm³ (4 fluid oz.) jar and labeled C1. The remaining emulsion (558.0 g) was poured into a 1.4 liter (3 US pint) tub and labeled C2. The emulsion was cured by placing this jar C1 in a 60°C water bath and periodically tested by placing the probe described above on top of the emulsion. After 121 minutes, the probe sat on top of the foam and did not sink. The emulsion in the tub was cured by heating the tub C2 in a 60°C incubator for 24 hours. 1.74 % of free water was poured off from the resulting foam.

0076While stirring in a similar manner to above, 600 cc of aqueous 10 wt% CaCl₂ and 0.15 wt% potassium persulfate solution was slowly added to 20.32 g of mixture-A which had been heated at 80°C for 41 minutes. 62.18 g of the resulting emulsion was poured into a 118 cm³ (4 fluid oz.) jar and labeled D1. The remaining emulsion (552.48 g) was poured into a 1.4 liter (3 US pint) tub and labeled D2. The emulsion was cured by placing this jar D1 in a 60°C water bath and periodically tested by placing the probe described above on top of the emulsion. After 112 minutes, the probe sat on top of the foam and did not sink. The emulsion in the tub was cured by heating the tub D2 in a 60°C incubator for 24 hours. 2.08 % of free water was poured off from the resulting foam.

0077While stirring in a similar manner to above, 600 cc of aqueous 10 wt% CaCl₂ and 0.15 wt% potassium persulfate solution was slowly added to 20.2 g of mixture-A which had been heated at 80°C for 53 minutes. 61.94 g of the resulting emulsion was poured into a 118 cm³ (4 fluid oz.) jar and labeled E1. The remaining emulsion (543.82 g) was poured into a 1.4 liter (3 US pint) tub and labeled E2. The emulsion was cured by placing this jar E1 in a 60°C water bath and periodically tested by placing the probe described above on top of the emulsion. After 94 minutes, the probe sat on top of the foam and did not sink. The emulsion in the tub was cured by heating the tub E2 in a 60°C incubator for 23 hours. 1.77 % of free water was poured off from the resulting foam.

0078In a container, 99.77 g of a monomer mixture (19.11 wt% styrene, 20.63 wt% divinyl benzene and 60.26 wt% of 2-ethyl hexyl acrylate) was mixed with 1.19 g of t-butyl peroxyisobutyrate (Lupersol™ 80 from Atochem, North America) and 11.98g of Span® 20 emulsifying agent (sorbitan monolaurate from Fluka Chemical Corp. or Aldrich Chemical Co.) ("mixture-F"). For divinyl benzene, commercial divinyl benzene containing 55% divinyl benzene from Aldrich Chemical Co. was used.

0079While stirring in a similar manner to above, 600 cc of aqueous 10 wt% CaCl₂ and 0.15 wt% potassium persulfate solution was slowly added to 20.07 g of mixture-F which had been heated at 80°C for 60 minutes. 62.99 g of the resulting emulsion was poured into a 118 cm³ (4 fluid oz.) jar and labeled H1. The remaining emulsion (538.63 g) was poured into a 1.4 liter (3 US pint) tub and labeled G2. The emulsion was cured by placing this jar G1 in a 60°C water bath and periodically tested by placing the probe described above on top of the emulsion. After 134 minutes, the probe sat on top of the foam and did not sink. The emulsion in the tub was cured by heating the tub G2 in a 60°C incubator for 22 hours. 4.94 % of free water was poured off from the resulting foam.

0080While stirring in a similar manner to above, 600 cc of aqueous 10 wt% CaCl₂ and 0.15 wt% potassium persulfate solution was slowly added to 20.27 g of mixture-F which had been heated at 80°C for 72 minutes. 61.08 g of the resulting emulsion was poured into a 118 cm³ (4 fluid oz.) jar and labeled H1. The remaining emulsion (557.67 g) was poured into a 1.4 liter (3 US pint) tub and labeled H2. The emulsion was cured by placing this jar H1 in a 60°C water bath and periodically tested by placing the probe described above on top of the emulsion. After 132 minutes, the probe sat on top of the foam and did not sink. The emulsion in the tub was cured by heating the tub H2 in a 60°C incubator for 21 hours. 6.8 % of free water was poured off from the resulting foam.

0081While stirring in a similar manner to above, 600 cc of aqueous 10 wt% CaCl₂ and 0.15 wt% potassium persulfate solution was slowly added to 20.21 g of mixture-F which had been heated at 80°C for 84 minutes. 59.22 g of the resulting emulsion was poured into a 118 cm³ (4 fluid oz.) jar and labeled I1. The remaining emulsion (551.61 g) was poured into a 1.4 liter (3 US pint) tub and labeled I2. The emulsion was cured by placing this jar I1 in a 60°C water bath and periodically tested by placing the probe described above on top of the emulsion. After 119 minutes, the probe sat on top of the foam and did not sink. The emulsion in the tub was cured by heating the tub I2 in a 60°C incubator for 20.33 hours. 1.6 % of free water was poured off from the resulting foam.

0082While stirring in a similar manner to above, 600 cc of aqueous 10 wt% CaCl₂ and 0.15 wt% potassium persulfate solution was slowly added to 19.98 g of mixture-F which had been heated at 80°C for 97 minutes. 63.78 g of the resulting emulsion was poured into a 118 cm³ (4 fluid oz.) jar and labeled J1. The remaining emulsion (524.59 g) was poured into a 1.4 liter (3 US pint) tub and labeled J2. The emulsion was cured by placing this jar J1 in a 60°C water bath and periodically tested by placing the probe described above on top of the emulsion. After 110 minutes, the probe sat on top of the foam and did not sink. The emulsion in the tub was cured by heating the tub J2 in a 60°C incubator for 19 hours. 2.21 % of free water was poured off from the resulting foam.

0083While stirring in a similar manner to above, 600 cc of aqueous 10 wt% CaCl₂ and 0.15 wt% potassium persulfate solution was slowly added to 20.06 g of mixture-F which had been heated at 80°C for 111 minutes. 69.02 g of the resulting emulsion was poured into a 118 cm³ (4 fluid oz.) and labeled K1. The remaining emulsion (552.48 g) was poured into a 1.4 liter (3 US pint) tub and labeled K2. The emulsion was cured by placing this jar K1 in a 60°C water bath and periodically tested by placing the probe described above on top of the emulsion. After 61 minutes, the probe sat on top of the foam and did not sink. The emulsion in the tub was cured by heating the tub K2 in a 60°C incubator for 18.25 hours. 6.65 % of free water was poured off from the resulting foam.

0084After 125 minutes, the remaining mixture-F was solid as tested by the above solidity test.

0085The properties of #2, tub samples are listed in Table 5.

Example 6

0086This example demonstrates another preparation of a low density crosslinked polymeric material by treating the monomer mixture according to the invention and comparison run N.

0087A mixture-M was prepared in a similar manner to Example 5, except 100.23 g of monomer mixture (20.26 wt% styrene, 19.91 wt% divinyl benzene and 60.06 wt% of 2-ethyl hexyl acrylate) was mixed with 1.14 g of t-butyl peroxyisobutyrate (Lupersol™ 80 from Atochem, North America) and 12.34g of Span® 20 emulsifying agent (sorbitan monolaurate from Fluka Chemical Corp. or Aldrich Chemical Co.).

0088To 20.03 g of mixture-M, 600 cc of aqueous 10 wt% CaCl₂ and 0.15 wt% potassium persulfate solution was slowly added as in Example 5. 60.03 g of the resulting emulsion was poured into a 118 cm³ (4 fluid oz.) jar and labeled N1. The remaining emulsion (540.28 g) was poured into a 1.4 liter (3 US pint) tub and labeled N2. The emulsion was cured by placing this jar N1 in a 60°C water bath and periodically tested by placing the probe described in Example 5 on top of the emulsion. After 127 minutes, the probe sat on top of the foam and did not sink. The emulsion in the tub was cured by heating the tub N2 in a 60°C incubator for 23 hours. 2.81 % of free water was poured off from the resulting foam.

0089In a similar manner to above, 600 cc of aqueous 10 wt% CaCl₂ and 0.15 wt% potassium persulfate solution was slowly added to 19.91 g of mixture-M which had been heated at 80°C for 12 minutes. 59.03 g of the resulting emulsion was poured into a 118 cm³ (4 fluid oz.) jar and labeled O1. The remaining emulsion (531.0 g) was poured into a 1.4 liter (3 US pint) tub and labeled O2. The emulsion was cured by placing this jar O1 in a 60°C water bath and periodically tested by placing the probe described above on top of the emulsion. After 114 minutes, the probe sat on top of the foam and did not sink. The emulsion in the tub was cured by heating the tub O2 in a 60°C incubator for 22.75 hours. 6.02 % of free water was poured off from the resulting foam.

0090In a similar manner to above, 600 cc of aqueous 10 wt% CaCl₂ and 0.15 wt% potassium persulfate solution was slowly added to 20.1 g of mixture-M which had been heated at 80°C for 26 minutes. 62.88 g of the resulting emulsion was poured into a 118 cm³ (4 fluid oz.) and labeled P1. The remaining emulsion (519.21 g) was poured into a 1.4 liter (3 US pint) tub and labeled P2. The emulsion was cured by placing this jar P1 in a 60°C water bath and periodically tested by placing the probe described above on top of the emulsion. After 89 minutes, the probe sat on top of the foam and did not sink. The emulsion in the tub was cured by heating the tub P2 in a 60°C incubator for 22.5 hours. 0 % of free water was poured off from the resulting foam.

0091In a similar manner to above, 600 cc of aqueous 10 wt% CaCl₂ and 0.15 wt% potassium persulfate solution was slowly added to 20.12 g of mixture-N which had been heated at 80°C for 37 minutes. 65.75 g of the resulting emulsion was poured into a 118 cm³ (4 fluid oz.) jar and labeled Q1. The remaining emulsion (531.74 g) was poured into a 1.4 liter (3 US pint) tub and labeled Q2. The emulsion was cured by placing this jar Q1 in a 60°C water bath and periodically tested by placing the probe described above on top of the emulsion. After 78 minutes, the probe sat on top of the foam and did not sink. The emulsion in the tub was cured by heating the tub Q2 in a 60°C incubator for 22.25 hours. 4.36 % of free water was poured off from the resulting foam.

0092In a similar manner to above, 600 cc of aqueous 10 wt% CaCl₂ and 0.15 wt% potassium persulfate solution was slowly added to 19.99 g of mixture-N which had been heated at 80°C for 48 minutes. 64.74 g of the resulting emulsion was poured into a 118 cm³ (4 fluid oz.) jar and labeled R1. The remaining emulsion (620.61 g) was poured into a 1.4 liter (3 US pint) tub and labeled R2. The emulsion was cured by placing this jar R1 in a 60°C water bath and periodically tested by placing the probe described above on top of the emulsion. After 82 minutes, the probe sat on top of the foam and did not sink. The emulsion in the tub was cured by heating the tub R2 in a 60°C incubator for 22 hours. 17.03 % of free water was poured off from the resulting foam.

0093The properties of #2, tub samples, are listed in Table 5 below. <tables id="tabl0005" num="0005"><table frame="all"><title>TABLE 5</title><tgroup cols="7" colsep="1" rowsep="0"><colspec colnum="1" colname="col1" colwidth="22.50mm" /><colspec colnum="2" colname="col2" colwidth="22.50mm" /><colspec colnum="3" colname="col3" colwidth="22.50mm" /><colspec colnum="4" colname="col4" colwidth="22.50mm" /><colspec colnum="5" colname="col5" colwidth="22.50mm" /><colspec colnum="6" colname="col6" colwidth="22.50mm" /><colspec colnum="7" colname="col7" colwidth="22.50mm" /><thead valign="top"><row rowsep="1"><entry namest="col1" nameend="col1" align="left">Sample</entry><entry namest="col2" nameend="col2" align="left">% Strain</entry><entry namest="col3" nameend="col3" align="left">RTCD</entry><entry namest="col4" nameend="col4" align="left">FD</entry><entry namest="col5" nameend="col5" align="left">FS</entry><entry namest="col6" nameend="col6" align="left">DT</entry><entry namest="col7" nameend="col7" align="left">VWT</entry></row></thead><tbody valign="top"><row><entry namest="col1" nameend="col1" align="left">B2</entry><entry namest="col2" nameend="col2" align="left">17.4</entry><entry namest="col3" nameend="col3" align="left">17.3</entry><entry namest="col4" nameend="col4" align="left">34.4</entry><entry namest="col5" nameend="col5" align="left">19.9</entry><entry namest="col6" nameend="col6" align="left">.447</entry><entry namest="col7" nameend="col7" align="left">71S</entry></row><row><entry namest="col1" nameend="col1" align="left">C2</entry><entry namest="col2" nameend="col2" align="left">11.9</entry><entry namest="col3" nameend="col3" align="left">15.0</entry><entry namest="col4" nameend="col4" align="left">37.2</entry><entry namest="col5" nameend="col5" align="left">15.8</entry><entry namest="col6" nameend="col6" align="left">.386</entry><entry namest="col7" nameend="col7" align="left">145S</entry></row><row><entry namest="col1" nameend="col1" align="left">D2</entry><entry namest="col2" nameend="col2" align="left">19.8</entry><entry namest="col3" nameend="col3" align="left">21.1</entry><entry namest="col4" nameend="col4" align="left">34.4</entry><entry namest="col5" nameend="col5" align="left">24.3</entry><entry namest="col6" nameend="col6" align="left">.342</entry><entry namest="col7" nameend="col7" align="left">90S</entry></row><row><entry namest="col1" nameend="col1" align="left">E2</entry><entry namest="col2" nameend="col2" align="left">22.4</entry><entry namest="col3" nameend="col3" align="left">10.7</entry><entry namest="col4" nameend="col4" align="left">32.6</entry><entry namest="col5" nameend="col5" align="left">21.1</entry><entry namest="col6" nameend="col6" align="left">.396</entry><entry namest="col7" nameend="col7" align="left">67S</entry></row><row><entry namest="col1" nameend="col1" align="left">G2</entry><entry namest="col2" nameend="col2" align="left">56.4</entry><entry namest="col3" nameend="col3" align="left">17.5</entry><entry namest="col4" nameend="col4" align="left">27.2</entry><entry namest="col5" nameend="col5" align="left">34.9</entry><entry namest="col6" nameend="col6" align="left">.344</entry><entry namest="col7" nameend="col7" align="left">70S</entry></row><row><entry namest="col1" nameend="col1" align="left">H2</entry><entry namest="col2" nameend="col2" align="left">37.0</entry><entry namest="col3" nameend="col3" align="left">15.8</entry><entry namest="col4" nameend="col4" align="left">35.9</entry><entry namest="col5" nameend="col5" align="left">19.1</entry><entry namest="col6" nameend="col6" align="left">.366</entry><entry namest="col7" nameend="col7" align="left">58S</entry></row><row><entry namest="col1" nameend="col1" align="left">I2</entry><entry namest="col2" nameend="col2" align="left">21.4</entry><entry namest="col3" nameend="col3" align="left">15.8</entry><entry namest="col4" nameend="col4" align="left">35.9</entry><entry namest="col5" nameend="col5" align="left">19.1</entry><entry namest="col6" nameend="col6" align="left">.366</entry><entry namest="col7" nameend="col7" align="left">68S</entry></row><row><entry namest="col1" nameend="col1" align="left">J2</entry><entry namest="col2" nameend="col2" align="left">28.6</entry><entry namest="col3" nameend="col3" align="left">19.4</entry><entry namest="col4" nameend="col4" align="left">33.8</entry><entry namest="col5" nameend="col5" align="left">23.9</entry><entry namest="col6" nameend="col6" align="left">.380</entry><entry namest="col7" nameend="col7" align="left">76S</entry></row><row><entry namest="col1" nameend="col1" align="left">K2</entry><entry namest="col2" nameend="col2" align="left">17.9</entry><entry namest="col3" nameend="col3" align="left">18.9</entry><entry namest="col4" nameend="col4" align="left">39.7</entry><entry namest="col5" nameend="col5" align="left">20.9</entry><entry namest="col6" nameend="col6" align="left">.391</entry><entry namest="col7" nameend="col7" align="left">161S</entry></row><row><entry namest="col1" nameend="col1" align="left">N2</entry><entry namest="col2" nameend="col2" align="left">28.4</entry><entry namest="col3" nameend="col3" align="left">18.7</entry><entry namest="col4" nameend="col4" align="left">33.1</entry><entry namest="col5" nameend="col5" align="left">23.8</entry><entry namest="col6" nameend="col6" align="left">.110</entry><entry namest="col7" nameend="col7" align="left">92S</entry></row><row><entry namest="col1" nameend="col1" align="left">O2</entry><entry namest="col2" nameend="col2" align="left">14.2</entry><entry namest="col3" nameend="col3" align="left">15.7</entry><entry namest="col4" nameend="col4" align="left">34.9</entry><entry namest="col5" nameend="col5" align="left">17.3</entry><entry namest="col6" nameend="col6" align="left">.379</entry><entry namest="col7" nameend="col7" align="left">91S</entry></row><row><entry namest="col1" nameend="col1" align="left">P2</entry><entry namest="col2" nameend="col2" align="left">9.5</entry><entry namest="col3" nameend="col3" align="left">16.5</entry><entry namest="col4" nameend="col4" align="left">36.8</entry><entry namest="col5" nameend="col5" align="left">17.2</entry><entry namest="col6" nameend="col6" align="left">.411</entry><entry namest="col7" nameend="col7" align="left">148S</entry></row><row><entry namest="col1" nameend="col1" align="left">Q2</entry><entry namest="col2" nameend="col2" align="left">10.5</entry><entry namest="col3" nameend="col3" align="left">14.4</entry><entry namest="col4" nameend="col4" align="left">37.3</entry><entry namest="col5" nameend="col5" align="left">15.0</entry><entry namest="col6" nameend="col6" align="left">.388</entry><entry namest="col7" nameend="col7" align="left">128S</entry></row><row rowsep="1"><entry namest="col1" nameend="col1" align="left">R2</entry><entry namest="col2" nameend="col2" align="left">12.3</entry><entry namest="col3" nameend="col3" align="left">15.9</entry><entry namest="col4" nameend="col4" align="left">46.8</entry><entry namest="col5" nameend="col5" align="left">16.8</entry><entry namest="col6" nameend="col6" align="left">.313</entry><entry namest="col7" nameend="col7" align="left">128S</entry></row></tbody></tgroup></table></tables>

0094As can be seen from Table 5, the foams produced according to the process of the invention (obtained from the advanced monomer mixture) have comparable or better foam properties compared with an unadvanced conventionally prepared material of N2.

Example 7

0095This example demonstrates the treatment of the process of the invention for volatile monomers.

0096A 3:2 weight ratio of isoprene: divinyl benzene were mixed to produce a monomer mixture. (Commercial divinyl benzene containing 55% divinyl benzene from Aldrich Chemical Co. was used.) To this monomer mixture, 12 parts by weight for 100 parts by weight of the monomer mixture of a sorbitan monolaurate surfactant (SPAN® 20 emulsifying agent from Fluka Chemical Corp. or Aldrich Chemical Co.) was added. To this mixture 1 part by weight for 100 parts by weight of the monomer mixture of Lupersol™ 225 initiator (di(sec-butyl) peroxydicarbonate) from Atochem North America was added. The resulting mixture was treated at the temperatures listed below. The high temperature treatment runs were performed in an autoclave blanketed with nitrogen under pressures up to 400 psig.

0097The mixtures were treated for the times indicated below. To each treated mixture an aqueous phase containing 10% CaCl₂ was added slowly to the treated monomer mixture while stirring as in Example 5 to form a water-in-oil emulsion. The emulsion was poured into a 118 cm³ (4 fluid oz.) jar and cured for a time and temperature as indicated in Table 6 below. Cure Time was determined by determining the time necessary for the emulsion to support a 2.1 kPa (0.3 psi) flat tipped probe at the surface of the emulsion. <tables id="tabl0006" num="0006"><table frame="all"><title>TABLE 6</title><tgroup cols="5" colsep="1" rowsep="0"><colspec colnum="1" colname="col1" colwidth="31.50mm" /><colspec colnum="2" colname="col2" colwidth="31.50mm" /><colspec colnum="3" colname="col3" colwidth="31.50mm" /><colspec colnum="4" colname="col4" colwidth="31.50mm" /><colspec colnum="5" colname="col5" colwidth="31.50mm" /><thead valign="top"><row rowsep="1"><entry namest="col1" nameend="col2" align="left">Treatment</entry><entry namest="col3" nameend="col3" rowsep="0" align="left">Bromine No.</entry><entry namest="col4" nameend="col4" rowsep="0" align="left">Cure Time</entry><entry namest="col5" nameend="col5" rowsep="0" align="left">Foam Properties</entry></row><row rowsep="1"><entry namest="col1" nameend="col1" align="center">Time</entry><entry namest="col2" nameend="col2" align="center">Temp.</entry><entry namest="col3" nameend="col3" /><entry namest="col4" nameend="col4" /><entry namest="col5" nameend="col5" /></row></thead><tbody valign="top"><row><entry namest="col1" nameend="col1" align="left">0 Cell</entry><entry namest="col2" nameend="col2" /><entry namest="col3" nameend="col3" align="left">175+</entry><entry namest="col4" nameend="col4" align="right">>400 min.</entry><entry namest="col5" nameend="col5" align="left">Poor, Closed Many Voids</entry></row><row><entry namest="col1" nameend="col1" align="left">250 min</entry><entry namest="col2" nameend="col2" align="left">60-80°C</entry><entry namest="col3" nameend="col3" align="left">144</entry><entry namest="col4" nameend="col4" align="right">260 min.</entry><entry namest="col5" nameend="col5" align="left">Normal to Poor</entry></row><row><entry namest="col1" nameend="col1" align="left">260 min</entry><entry namest="col2" nameend="col2" align="left">74-78°C</entry><entry namest="col3" nameend="col3" align="left">140</entry><entry namest="col4" nameend="col4" align="right">200 min.</entry><entry namest="col5" nameend="col5" align="left">Normal to Good</entry></row><row rowsep="1"><entry namest="col1" nameend="col1" align="left">244 min</entry><entry namest="col2" nameend="col2" align="left">80-87°C</entry><entry namest="col3" nameend="col3" align="left">160</entry><entry namest="col4" nameend="col4" align="right">183 min.</entry><entry namest="col5" nameend="col5" align="left">Normal</entry></row></tbody></tgroup></table></tables>

0098As seen from the Table above, the effect of curing the emulsion containing a high mole fraction of isoprene as shown above at 60°C without treatment produces formation of closed cell foams, and broken, cracked, and disintegrated foam chuncks. At the curing temperature without treatment, emulsions containing such high mole fractions of isoprene forms pockets of gas, giving a "Swiss Cheese" appearance with many large voids when sliced. However, with the inventive process using treatment steps an open celled foam with good properties can be produced.

Example 8

0099This example further demonstrates the process of the invention.

01001:1:3 Weight ratio of styrene: divinyl benzene:2-ethylhexyl acrylate were mixed to produce monomer mixtures. (Commercial divinyl benzene containing 55% divinyl benzene from Aldrich Chemical Co. was used.) To these monomer mixtures, 12 parts by weight for 100 parts by weight of the monomer mixture of a sorbitan monolaurate surfactant (SPAN® 20 emulsifying agent from Fluka Chemical Corp. or Aldrich Chemical Co.) was added. To these mixtures 1 part by weight for 100 parts by weight of the monomer mixture of the treatment initiators listed below were added. The resulting mixtures were treated at the temperatures listed below and for the time listed below in Table 7.

0101To these advanced mixtures an aqueous phase containing 10% CaCl₂ was added slowly to the treated monomer mixtures while stirring as in Example 5 to form a water-in-oil emulsion. In some batches as indicated in the Table below, 1 part by weight for 100 parts by weight of the monomer mixture of peroxide polymerization initiators or 0.14 part by weight for 100 parts by weight of the monomer mixture of potassium persulfate ("KPS") were added to the emulsion and mixed. The emulsions were poured into a 118 cm³ (4 fluid oz.) jar and cured at 60°C. Cure Time was determined by determining the time necessary for the emulsion to support a 2.1 kPa (0.3 psi) flat tipped probe at the surface of the emulsion and listed below in Table 7. <tables id="tabl0007" num="0007"><table frame="all"><title>TABLE 7</title><tgroup cols="5" colsep="1" rowsep="0"><colspec colnum="1" colname="col1" colwidth="31.50mm" /><colspec colnum="2" colname="col2" colwidth="31.50mm" /><colspec colnum="3" colname="col3" colwidth="31.50mm" /><colspec colnum="4" colname="col4" colwidth="31.50mm" /><colspec colnum="5" colname="col5" colwidth="31.50mm" /><thead valign="top"><row rowsep="1"><entry namest="col1" nameend="col2" align="center">Treatment</entry><entry namest="col3" nameend="col3" /><entry namest="col4" nameend="col5" /></row><row rowsep="1"><entry namest="col1" nameend="col1" align="left">Time Time(min.)</entry><entry namest="col2" nameend="col2" align="center">Temp.</entry><entry namest="col3" nameend="col3" align="center">Initiator</entry><entry namest="col4" nameend="col5" align="center">Cure Initiator</entry></row></thead><tbody valign="top"><row><entry namest="col1" nameend="col1" align="right">0 min</entry><entry namest="col2" nameend="col2" /><entry namest="col3" nameend="col3" align="left">--</entry><entry namest="col4" nameend="col4" align="left">Benzoyl peroxide</entry><entry namest="col5" nameend="col5" align="left">Would not cure</entry></row><row><entry namest="col1" nameend="col1" align="right">0 min</entry><entry namest="col2" nameend="col2" /><entry namest="col3" nameend="col3" /><entry namest="col4" nameend="col4" align="left">Lupersol™ 80^a</entry><entry namest="col5" nameend="col5" align="left">212</entry></row><row><entry namest="col1" nameend="col1" align="right">24 min</entry><entry namest="col2" nameend="col2" align="left">75°C</entry><entry namest="col3" nameend="col3" align="left">Lupersol 80</entry><entry namest="col4" nameend="col4" align="left">--</entry><entry namest="col5" nameend="col5" align="left">190</entry></row><row><entry namest="col1" nameend="col1" align="right">24 min</entry><entry namest="col2" nameend="col2" align="left">75°C</entry><entry namest="col3" nameend="col3" align="left">Lupersol 80</entry><entry namest="col4" nameend="col4" align="left">KPS</entry><entry namest="col5" nameend="col5" align="left">190</entry></row><row><entry namest="col1" nameend="col1" align="right">36 min</entry><entry namest="col2" nameend="col2" align="left">75°C</entry><entry namest="col3" nameend="col3" align="left">Lupersol 80</entry><entry namest="col4" nameend="col4" align="left">KPS</entry><entry namest="col5" nameend="col5" align="left">179</entry></row><row><entry namest="col1" nameend="col1" align="right">60 min</entry><entry namest="col2" nameend="col2" align="left">75°C</entry><entry namest="col3" nameend="col3" align="left">Lupersol 80</entry><entry namest="col4" nameend="col5" align="left">Solidified during advancement</entry></row><row><entry namest="col1" nameend="col1" align="right">0 min</entry><entry namest="col2" nameend="col2" /><entry namest="col3" nameend="col3" align="left">Benzoyl peroxide</entry><entry namest="col4" nameend="col4" align="left">Lupersol 80</entry><entry namest="col5" nameend="col5" align="left">95</entry></row><row><entry namest="col1" nameend="col1" align="right">12 min</entry><entry namest="col2" nameend="col2" align="left">75°C</entry><entry namest="col3" nameend="col3" align="left">Benzoyl peroxide</entry><entry namest="col4" nameend="col4" align="left">Lupersol 80</entry><entry namest="col5" nameend="col5" align="left">100</entry></row><row><entry namest="col1" nameend="col1" align="right">24 min</entry><entry namest="col2" nameend="col2" align="left">75°C</entry><entry namest="col3" nameend="col3" align="left">Benzoyl peroxide</entry><entry namest="col4" nameend="col4" align="left">Lupersol 80</entry><entry namest="col5" nameend="col5" align="left">95</entry></row><row><entry namest="col1" nameend="col1" align="right">0 min</entry><entry namest="col2" nameend="col2" /><entry namest="col3" nameend="col3" align="left">Lupersol 80</entry><entry namest="col4" nameend="col4" align="left">Benzoyl peroxide</entry><entry namest="col5" nameend="col5" align="left">173</entry></row><row><entry namest="col1" nameend="col1" align="right">12 min</entry><entry namest="col2" nameend="col2" align="left">75°C</entry><entry namest="col3" nameend="col3" align="left">Lupersol 80</entry><entry namest="col4" nameend="col4" align="left">Benzoyl peroxide</entry><entry namest="col5" nameend="col5" align="left">177</entry></row><row><entry namest="col1" nameend="col1" align="right">24 min</entry><entry namest="col2" nameend="col2" align="left">75°C</entry><entry namest="col3" nameend="col3" align="left">Lupersol 80</entry><entry namest="col4" nameend="col4" align="left">Benzoyl peroxide</entry><entry namest="col5" nameend="col5" align="left">173</entry></row><row><entry namest="col1" nameend="col1" align="right">48 min</entry><entry namest="col2" nameend="col2" align="left">75°C</entry><entry namest="col3" nameend="col3" align="left">Lupersol 80</entry><entry namest="col4" nameend="col4" align="left">Benzoyl peroxide</entry><entry namest="col5" nameend="col5" align="left">154</entry></row><row><entry namest="col1" nameend="col1" align="right">60 min</entry><entry namest="col2" nameend="col2" align="left">60°C</entry><entry namest="col3" nameend="col3" align="left">Benzoyl peroxide</entry><entry namest="col4" nameend="col4" align="left">--</entry><entry namest="col5" nameend="col5" align="left">158</entry></row><row rowsep="1"><entry namest="col1" nameend="col1" align="right">60 min</entry><entry namest="col2" nameend="col2" align="left">60°C</entry><entry namest="col3" nameend="col3" align="left">Benzoyl peroxide</entry><entry namest="col4" nameend="col4" align="left">KPS</entry><entry namest="col5" nameend="col5" align="left">98</entry></row></tbody></tgroup><tgroup cols="5" colsep="0" rowsep="0"><colspec colnum="1" colname="col1" colwidth="31.50mm" /><colspec colnum="2" colname="col2" colwidth="31.50mm" /><colspec colnum="3" colname="col3" colwidth="31.50mm" /><colspec colnum="4" colname="col4" colwidth="31.50mm" /><colspec colnum="5" colname="col5" colwidth="31.50mm" /><tbody valign="top"><row><entry namest="col1" nameend="col5" align="justify">^a t-butyl peroxyisobutyrate from Atochem North America.</entry></row></tbody></tgroup></table></tables>

0102As seen from the Table above, the emulsion did not cure properly using benzoyl peroxide as the polymerization initiator without treatment. The emulsion cured to form a foam when benzoyl peroxide was used as an initiator in the oil phase before formation of the emulsion.

Example 9

0103This example demonstrates another preparation of a low density crosslinked polymeric material by treating the monomer mixture according to the invention.

0104A 1:1:3 weight ratio of styrene: divinyl benzene:2-ethylhexyl acrylate were mixed to produce a monomer mixture. (Commercial divinyl benzene containing 55% divinyl benzene from Aldrich Chemical Co. was used.) To this monomer mixture, 12 parts by weight for 100 parts by weight of the monomer mixture of a sorbitan monolaurate surfactant (SPAN® 20 emulsifying agent from Fluka Chemical Corp. or Aldrich Chemical Co.) was added. To this mixture 1 part by weight for 100 parts by weight of the monomer mixture of Lupersol™ 80 (t-butyl peroxyisobutyrate from Atochem North America) was added. The resulting mixture was treated at 75°C for approximately 20 minutes.

0105To this treated mixture an aqueous phase containing 10% CaCl₂ was added slowly to the treated monomer mixture while stirring as in Example 5 to form a water-in-oil emulsion. No additional polymerization initiator was added. The emulsion was poured into a 1.5 liter (3 US pint) tub and cured at 60°C for 16 hours. The properties of the foam are shown in Table 8 below.

Example 10

0106This example demonstrates another preparation of a low density crosslinked polymeric material by treating the monomer mixture according to the invention.

01071:1:3 Weight ratio of styrene: divinyl benzene:2-ethylhexyl acrylate were mixed to produce monomer mixtures. (Commercial divinyl benzene containing 55% divinyl benzene from Aldrich Chemical Co. was used.) To these monomer mixtures, 12 parts by weight for 100 parts by weight of the monomer mixture of a sorbitan monolaurate surfactant (SPAN® 20 emulsifying agent from Fluka Chemical Corp. or Aldrich Chemical Co.) was added. To these mixtures 1 part by weight for 100 parts by weight of the monomer mixture of Lupersol™ 80 (t-butyl peroxyisobutyrate from Atochem North America) for Example 10A and benzoyl peroxide (from Aldrich Chemical Co.) for Example 10B were added. The resulting mixtures were treated at 75°C for 12 minutes.

0108To these treated mixture an aqueous phase containing 10% CaCl₂ was added slowly to the treated monomer mixtures while stirring as in Example 5 to form water-in-oil emulsions. To these emulsions, 1 part by weight for 100 parts by weight of the monomers of benzoyl peroxide for Example 10A and Lupersol™ 80 for Example 10B were added and mixed. The emulsions were poured into a 1.5 liter (3 US pint) tub and cured at 60°C for 16 hours. The properties of the foams are shown in Table 8 below. <tables id="tabl0008" num="0008"><table frame="all"><title>TABLE 8</title><tgroup cols="7" colsep="1" rowsep="0"><colspec colnum="1" colname="col1" colwidth="22.50mm" /><colspec colnum="2" colname="col2" colwidth="22.50mm" /><colspec colnum="3" colname="col3" colwidth="22.50mm" /><colspec colnum="4" colname="col4" colwidth="22.50mm" /><colspec colnum="5" colname="col5" colwidth="22.50mm" /><colspec colnum="6" colname="col6" colwidth="22.50mm" /><colspec colnum="7" colname="col7" colwidth="22.50mm" /><thead valign="top"><row rowsep="1"><entry namest="col1" nameend="col1" align="left">Example</entry><entry namest="col2" nameend="col2" align="left">% Strain</entry><entry namest="col3" nameend="col3" align="left">RTCD</entry><entry namest="col4" nameend="col4" align="left">FD</entry><entry namest="col5" nameend="col5" align="left">FS</entry><entry namest="col6" nameend="col6" align="left">DT</entry><entry namest="col7" nameend="col7" align="left">VWT</entry></row></thead><tbody valign="top"><row><entry namest="col1" nameend="col1" align="left">9</entry><entry namest="col2" nameend="col2" align="left">26.7</entry><entry namest="col3" nameend="col3" align="left">19.3</entry><entry namest="col4" nameend="col4" align="left">34.1</entry><entry namest="col5" nameend="col5" align="left">24.4</entry><entry namest="col6" nameend="col6" align="left">.129</entry><entry namest="col7" nameend="col7" align="left">126</entry></row><row><entry namest="col1" nameend="col1" align="left">10A</entry><entry namest="col2" nameend="col2" align="left">35.6</entry><entry namest="col3" nameend="col3" align="left">28.1</entry><entry namest="col4" nameend="col4" align="left">32.5</entry><entry namest="col5" nameend="col5" align="left">26.4</entry><entry namest="col6" nameend="col6" align="left">.363</entry><entry namest="col7" nameend="col7" align="left">70</entry></row><row rowsep="1"><entry namest="col1" nameend="col1" align="left">10B</entry><entry namest="col2" nameend="col2" align="left">46</entry><entry namest="col3" nameend="col3" align="left">16.8</entry><entry namest="col4" nameend="col4" align="left">32.6</entry><entry namest="col5" nameend="col5" align="left">28.5</entry><entry namest="col6" nameend="col6" align="left">0.129</entry><entry namest="col7" nameend="col7" align="left">168</entry></row></tbody></tgroup></table></tables>

0109As can be seen from Table 8, the foams produced by the treatment process of the invention have comparable to superior properties compared with the comparative example, Example 6, N2, particularly in foam absorption capacity such as Free Swell.