EP0657477A2

Process for producing olefin polymers, olefin-polymerizing catalyst and polypropylene for biaxially oriented film produced with said catalyst.

Abstract

An olefin polymerizing catalyst consisting of (A) a solid catalyst component containing magnesium, titanium, halogen and electron donative compound as essential components, (B) an organoaluminum compound and (C) at least two electron donative compounds including electron donative compounds (α) and (β), provided that the pentad stereoirregularity index (mmrr/mmmm) of 105°C xylene-insoluble fraction of a homopolypropyelene obtained by carrying out polymerization by the use of electron donative compound (α) together with the above-mentioned solid catalyst component (A) and organoaluminum compound (B) satisfies the following condition:0 ≦ mmrr/mmmm ≦ 0.0068 and the pentad stereoirregularity index (mmrr/mmmm) of 105°C xylene-insoluble fraction of a homopolypropylene obtained by carrying out polymerization by the use of electron donative compound (α) together with the above-mentioned solid catalyst component (A) and organoaluminum compound (B) satisfies the following condition:0.0068 < mmrr/mmmm ≦ 0.0320; a process for producing an olefin polymer using the catalyst; a polypropylene for use in production of a biaxially oriented film, the polypropylene being obtained by carrying out polymerization by the use of the polymerizing catalyst wherein: (1) 23°C decalin-soluble fraction content of the polypropylene is in the range of from 3.0 to 10.0% by weight,(2) the temperature at which the polypropylene shows a complex elastic modulus of 1.0 × 10⁹ dynes/cm² when a vibration of 110 Hz is applied to the polypropylene is in the range of from 134 to 152°C, and(3) melt flow rate (MFR) of the polypropylene at 230°C is in the range of from 0.5 to 10.0 g/10 minutes; and a biaxially oriented film obtained by subjecting the polypropylene to a stretching processing.

EP0657477A2, drawing sheet 1 — Sheet 1 of 25

Term

Term ended

Projected expiry passed 28 November 2014, 11.8 years ago.

7 claims: 2 independent, 5 dependent

1
A process for producing an olefin polymer which comprises homopolymerizing or copolymerizing an olefin by the use of an olefin polymerizing catalyst consisting of:(A) a solid catalyst component containing magnesium, titanium, halogen and electron donative compound as essential components, (B) an organoaluminum compound, and (C) at least two electron donative compounds including electron donative compound (α) and electron donative compound (β), provided that the pentad stereoirregularity index (mmrr/mmmm) of 105°C xylene-insoluble fraction of a homopolypropylene obtained by carrying out polymerization by the use of electron donative compound (α) together with the above-mentioned solid catalyst component (A) and organoaluminum compound (B) satisfies the following condition: 0 ≦ mmrr/mmmm ≦ 0.0068 and the pentad stereoirregularity index (mmrr/mmmm) of 105°C xylene-insoluble fraction of a homopolypropylene obtained by carrying out polymerization by the use of electron donative compound (-) together with the above-mentioned solid catalyst component (A) and organoaluminum compound (B) satisfies the following condition: 0.0068 mmrr/mmmm ≦ 0.0320.
2
An olefin-polymerizing catalyst consisting of:(A) a solid catalyst component containing magnesium, titanium, halogen and electron donative compound as essential components, (B) an organoaluminum compound, and (C) at least two electron donative compounds including electron donative compound (α) and electron donative compound (β), provided that the pentad stereoirregularity index (mmrr/mmmm) of 105°C xylene-insoluble fraction of a homopolypropyelene obtained by carrying out polymerization by the use of electron donative compound (α) together with the above-mentioned solid catalyst component (A) and organoaluminum compound (B) satisfies the following condition: 0 ≦ mmrr/mmmm ≦ 0.0068 and the pentad stereoirregularity index (mmrr/mmmm) of 105°C xylene-insoluble fraction of a homopolypropylene obtained by carrying out polymerization by the use of electron donative compound (β) together with the above-mentioned solid catalyst component (A) and organoaluminum compound (B) satisfies the following condition: 0.0068 mmrr/mmmm ≦ 0.0320.

Independent claims2

175 paragraphs in 5 sections, as filed

BACKGROUND OF THE INVENTION

Field of the Invention

The present invention relates to an olefin-polymerizing catalyst capable of forming in one polymerization system two homopolyolefins, each of said homopolyolefins being an isotactic polyolefin in which the disorder of monomer units alignment is in respective specified range. The present invention further relates to a process for producing an olefin polymer using said catalyst and a polypropylene produced by said process which is useful for production of a biaxially oriented film. More particularly, the present invention relates to a process for producing an olefin polymer excellent in stiffness and stretchability and successfully usable for formation of films, fibers, blow-molded articles, extrusion-molded articles, etc., an olefin-polymerizing catalyst used for production of such a polymer, a polypropylene for use in the production of a biaxially oriented film which can give a biaxially oriented film excellent in transparency and stiffness while retaining a particularly excellent stretchability, and a biaxially oriented film produced from said polypropylene.

Biaxially oriented films are extensively used as packaging materials because of their excellence in transparency, gloss, stiffness and water vapor barrier property. With the aim of improving the film properties, such as stiffness, of biaxially oriented film, highly crystalline homopolymers of propylene obtained with a high-stereospecificity catalyst have conventionally been used. However, such highly crystalline homopolymers of propylene have a fault that they are inferior in stretchability and apt to make troubles such as film breaking in the course of stretching. Thus, a variety of methods have so far been proposed for improving the stretchability of highly crystalline polypropylene. As one example of such proposals, copolymerization of propylene with a small amount of ethylene is known. Concretely speaking, JP-B-46-11027 has proposed a process for producing a polypropylene for use in production of films which comprises polymerizing propylene together with a very small amount of ethylene in the presence of a coordination catalyst and a hydrocarbon, hydrogen chloride or chlorinated hydrocarbon solvent so that one mole of the monomer unit in the resulting polymer becomes containing 0.01 mole or less of ethylene unit. Further, in JP-B-64-6211, there is proposed a process for producing a polypropylene improved in stretchability which comprises feeding propylene together with a small amount of ethylene into polymerization system using a catalyst consisting of an organoaluminum compound and titanium trichloride prepared by reducing titanium tetrachloride with an organoaluminum compound and further activating the reduced product by a treatment using a complex-forming agent, a treatment using an organoaluminum compound, a treatment using titanium tetrachloride or a combination thereof so that the resulting polymer comes to have an ethylene content of 0.1-1.0% by weight. Further, in JP-B-3-4371, there is proposed a process for producing a biaxially oriented polypropylene film excellent in transparency, stiffness and impact resistance by using a polypropylene of which ethylene content is 0.1-2% by mole and isotacticity is in a specified range. Any of these processes, however, have been unsatisfactory as a method for obtaining a polypropylene for a biaxially oriented film simultaneously having an excellent transparency and a high stiffness while retaining a good stretchability.

SUMMARY OF THE INVENTION

The object of the present invention is to provide an olefin-polymerizing catalyst capable of forming in one polymerization system two homopolyolefins, each of said homopolyolefins being an isotactic polyolefin in which stereoirregularity of monomer units is in respective specified range, a process for producing an olefin polymer using said catalyst, and a propylene for use in the production of a biaxially oriented film excellent in stretchability and having high transparency and stiffness.

In view of the above-mentioned state of things, the present inventors have conducted extensive studies to find that a polyolefin in which the stereoirregularity is in a specified range can be obtained by using a specified catalyst system, and that a biaxially oriented film simultaneously having high transparency and stiffness while retaining an excellent stretchability can be obtained from a polypropylene obtained by the use of said catalyst system which has a cold decalin-soluble fraction (23°C decalin-soluble fraction) content falling in a specified range, shows a specified complex elastic molulus in a specified temperature range, and has a melt flow rate (referred to as MFR, too) falling in a specified range. Based on this finding, the present invention has been accomplished.

Thus, the present invention relates to a process for producing an olefin polymer which comprises homo- or co-polymerizing an olefin by the use of a olefin-polymerizing catalyst consisting of: <ul id="ul0001" list-style="none"><li>(A) a solid catalyst component containing magnesium, titanium, halogen and an electron donative compound as essential components,</li><li>(B) an organoaluminum compound, and</li><li>(C) at least two electron donative compounds including electron donative compound (α) and electron donative compound (β), provided that 105°C xylene-insoluble fraction of a homopolypropylene obtained by carrying out a polymerization using the electron donative compound (α) together with the solid catalyst component and the organoaluminum compound shows a pentad stereoirregularity index (mmrr/mmmm) satisfying the following formula: <maths id="math0001" num=""><math display="inline"><mrow><mtext>0 ≦ mmrr/mmmm ≦ 0.0068</mtext></mrow></math><img file="EP0657477A2_D0001.tif" /></maths> and 105°C xylene-insoluble fraction of a homopolypropylene obtained by carrying out a polymerization using the electron donative compound (β) together with the solid catalyst component and the organoaluminum compound shows a pentad stereoirregularity index satisfying the following formula: <maths id="math0002" num=""><math display="inline"><mrow><mtext>0.0068 ≦ mmrr/mmmm ≦ 0.0320;</mtext></mrow></math><img file="EP0657477A2_D0002.tif" /></maths> an olefin-polymerizing catalyst consisting of: <ul id="ul0002" list-style="none"><li>(A) a solid catalyst component containing magnesium, titanium, halogen and an electron donative compound as essential components,</li><li>(B) an organoaluminum compound, and</li><li>(C) at least two electron donative compounds including electron donative compound (α) and electron donative compound (β), provided that 105°C xylene-insoluble fraction of a homopolypropylene obtained by carrying out a polymerization using the electron donative compound (α) together with the solid catalyst component and the organoaluminum compound shows a pentad stereoirregularity index (mmrr/mmmm) satisfying the following formula: <maths id="math0003" num=""><math display="inline"><mrow><mtext>0 ≦ mmrr/mmmm ≦ 0.0068</mtext></mrow></math><img file="EP0657477A2_D0003.tif" /></maths> and 105°C xylene-insoluble fraction of a homopolypropylene obtained by carrying out a polymerization using the electron donative compound (β) together with the solid catalyst component and the organoaluminum compound shows a pentad stereoirregularity index satisfying the following formula: <maths id="math0004" num=""><math display="inline"><mrow><mtext>0.0068 ≦ mmrr/mmmm ≦ 0.0320;</mtext></mrow></math><img file="EP0657477A2_D0004.tif" /></maths> and a polypropylene for use in the production of a biaxially oriented film obtained by carrying out a polymerization using said catalyst system, wherein: <ul id="ul0003" list-style="none"><li>(1) the content of 23°C decalin-soluble fraction of the polypropylene is in the range of from 3.0 to 10.0% by weight,</li><li>(2) when a vibration of 110 Hz is applied to the polypropylene, the polypropylene shows a complex elastic modulus of 1.0 × 10⁹ dynes/cm² at a temperature falling in the range of from 134°C to 152°C, and</li><li>(3) melt flow rate (MFR) of the polypropylene at 230°C is in the range of from 0.5 to 10.0 g/10 minutes.</li></ul></li></ul></li></ul>

Further, the present invention relates also to a biaxially oriented film obtained by subjecting said polypropylene for use in the production of biaxially oriented film to a stretching processing.

Next, the present invention is explained below in more detail.

The catalyst system used for production of the polyolefin of the present invention consists of (A) a solid catalyst component containing magnesium, titanium, halogen and electron donative component as essential components, (B) an organoaluminum compound and (C) an electron donative component.

(a) Solid catalyst component (A)

As the solid catalyst component (A) of the present invention containing magnesium, titanium, halogen and an electron donative compound as essential components, those generally called titanium-magnesium complex catalysts can be used. Such solid catalyst component (A) can be obtained by contacting the following magnesium compound, titanium compound and electron donative compound mutually.

As the titanium compound used for the synthesis of solid catalyst component (A), for example, the titanium compounds represented by the following general formula: Ti(OR¹)<sub>a</sub>X<sub>4-a</sub> wherein R¹ represents a hydrocarbon group having 1-20 carbon atoms, X represents a halogen atom, and a represents a number satisfying 0 ≦ a ≦ 4, can be referred to. More specifically, titanium tetrahalide compounds such as titanium tetrachloride, titanium tetrabromide, titanium tetraiodide and the like, alkoxytitanium trihalide compounds such as methoxytitanium trichloride, ethoxytitanium trichloride, butoxytitanium trichloride, phenoxytitanium trichloride, ethoxytitanium tribromide and the like, dialkoxytitanium dihalide compounds such as dimethoxytitanium dichloride, diethoxytitanium dichloride, dibutoxytitanium dichloride, diphenoxytitanium dichloride, diethoxytitanium dibromide and the like, trialkoxytitanium halide compounds such as trimethoxytitanium chloride, triethoxytitanium chloride, tributoxytitanium chloride, triphenoxytitanium chloride, triethoxytitanium bromide and the like, and tetraalkoxytitanium compounds such as tetramethoxytitanium, tetraethoxytitanium, tetrabutoxytitanium, tetraphenoxytitanium and the like can be referred to. These titanium compounds may be used either in the form of a single compound or in the form of a mixture of two or more compounds. Further, if desired, these titanium compounds may be used after dilution with a hydrocarbon or halogenated hydrocarbon compound or the like.

As the magnesium compound used in the synthesis of solid catalyst component (A), reductive magnesium compounds having a magnesium-carbon bond or a magnesium-hydrogen bond and non-reductive magnesium compounds can be used. Specific examples of the reductive magnesium compound include dimethylmagnesium, diethylmagnesium, dipropylmagnesium, dibutylmagnesium, dihexylmagnesium, butylethylmagnesium, ethylmagnesium chloride, butylmagnesium chloride, hexylmagnesium chloride, butylethoxymagnesium, butylmagnesium hydride and the like. If desired, these reductive magnesium compounds may be used in the form of a complex compound with an organoaluminum compound. On the other hand, specific examples of the non-reductive magnesium compounds include magnesium dihalide compounds such as magnesium dichloride, magnesium dibromide, magnesium diiodide and the like; alkoxymagnesium halide compounds such as methoxymagnesium chloride, ethoxymagnesium chloride, butoxymagnesium chloride, isopropoxymagnesium chloride, phenoxymagnesium chloride and the like; dialkoxymagnesium compounds such as diethoxymagnesium, dibutoxymagnesium, diisopropoxymagnesium, diphenoxymagnesium and the like; and magnesium carboxylates such as magnesium laurate, magnesium stearate and the like. If desired, said non-reductive magnesium compound may be a compound synthesized from a reductive magnesium compound according to a known method either previously or at the time of preparation of the solid catalyst component.

As the electron donative compound used in the synthesis of solid catalyst component (A), oxygen-containing electron donative compounds such as alcohols, phenols, ketones, aldehydes, carboxylic acids, esters of organic and inorganic acids, ethers, acid amides, acid anhydrides and the like; nitrogen-containing electron donative compounds such as ammonia, amines, nitriles, isocyanates and the like; etc. can be referred to. Of these electron donative compounds, esters of organic and inorganic acids and ethers are preferred.

As the ester of organic acid, esters of mono-and poly-carboxylic acids can be used preferably, of which examples include esters of aliphatic carboxylic acids, esters of olefinic carboxylic acids, esters of alicyclic carboxylic acids and esters of aromatic carboxylic acids. Specific examples thereof are methyl acetate, ethyl acetate, phenyl acetate, methyl propionate, ethyl propionate, ethyl butyrate, ethyl valerate, methyl acrylate, ethyl acrylate, methyl methacrylate, ethyl benzoate, butyl benzoate, methyl toluate, ethyl toluate, ethyl anisate, diethyl succinate, dibutyl succinate, diethyl malonate, dibutyl malonate, dimethyl maleate, dibutyl maleate, diethyl itaconate, dibutyl itaconate, monoethyl phthalate, dimethyl phthalate, methyl ethyl phthalate, diethyl phthalate, di-n-propyl phthalate, diisopropyl phthalate, di-n-butyl phthalate, diisobutyl phthalate, di-n-octyl phthalate, diphenyl phthalate and the like.

As the esters of inorganic acid, the silicon compounds represented by the following general formula: R²<sub>n</sub>Si(OR³)<sub>4-n</sub> wherein R² represents a hydrocarbon group having 1-20 carbon atoms or a hydrogen atom, R³ represents a hydrocarbon group having 1-20 carbon atoms, and n represents a number satisfying 0 ≦ n ≦ 4, can be used preferably. Specific examples of said silicon compound include tetramethoxysilane, tetraethoxysilane, tetrabutoxysilane, tetraphenoxysilane, methyltrimethoxysilane, ethyltrimethoxysilane, butyltrimethoxysilane, isobutyltrimethoxysilane, t-butyltrimethoxysilane, isopropyltrimethoxysilane, cyclohexyltrimethoxysilane, phenyltrimethoxysilane, vinyltrimethoxysilane, dimethyldimethoxysilane, diethyldimethoxysilane, dipropyldimethoxysilane, propylmethyldimethoxysilane, diisopropyldimethoxysilane, dibutyldimethoxysilane, diisobutyldimethoxysilane, di-t-butyldimethoxysilane, butylmethyldimethoxysilane, butylethyldimethoxysilane, t-butylmethyldimethoxysilane, hexylmethyldimethoxysilane, hexylethyldimethoxysilane, dodecylmethyldimethoxysilane, dicyclopentyldimethoxysilane, cyclopentylmethyldimethoxysilane, cyclopentylethyldimethoxysilane, cyclopentylisopropyldimethoxysilane, cyclopentylisobutyl-dimethoxysilane, cyclopentyl-t-butyldimethoxysilane, dicyclohexyldimethoxysilane, cyclohexylmethyldimethoxysilane, cyclohexylethyldimethoxysilane, cyclohexylisopropyldimethoxy-silane, cyclohexylisobutyldimethoxysilane, cyclohexyl-t-butyldimethoxysilane, diphenyldimethoxysilane, phenylmethyldimethoxysilane, vinylmethyldimethoxysilane, methyltriethoxysilane, ethyltriethoxysilane, butyltriethoxysilane, isobutyltriethoxysilane, t-butyltriethoxysilane, isopropyltriethoxysilane, cyclohexyltriethoxysilane, phenyltriethoxysilane, vinyltriethoxysilane, dimethyldiethoxysilane, diethyldiethoxysilane, dipropyldiethoxysilane, propylmethyldiethoxysilane, diisopropyldiethoxysilane, dibutyldiethoxysilane, diisobutyldiethoxysilane, di-t-butyldiethoxysilane, butylmethyldiethoxysilane, butylethyldiethoxysilane, t-butylmethyldiethoxysilane, hexylmethyldiethoxysilane, hexylethyldiethoxysilane, dodecylmethyldiethoxysilane, dicyclopentyldiethoxysilane, dicyclohexyldiethoxysilane, cyclohexylmethyldiethoxysilane, cyclohexylethyldiethoxysilane, diphenyldiethoxysilane, phenylmethyldiethoxysilane, vinylmethyldiethoxysilane, ethyltriisopropoxysilane, vinyltributoxysilane, phenyltri-t-butoxysilane, 2-norbornanetrimethoxysilane, 2-norbornanetriethoxysilane, 2-norbornanemethyldimethoxysilane, trimethylphenoxysilane, methyltriallyloxysilane, and the like.

As the ethers, the dialkyl ether compounds such as those represented by the following general formula: <chemistry id="chem0001" num="0001"><img file="EP0657477A2_D0005.tif" /></chemistry> wherein R⁴ to R⁷ each represents linear or branched alkyl group having 1-20 carbon atoms, alicyclic group, aryl group, alkylaryl group or arylalkyl group, provided that R⁴ to R⁷ may be identical with or different from one another and each of R⁴ and R⁵ may also be a hydrogen atom, can be referred to. Specific examples of the ether compound include diethyl ether, dipropyl ether, diisopropyl ether, dibutyl ether, diamyl ether, diisoamyl ether, dineopentyl ether, dihexyl ether, dioctyl ether, methyl butyl ether, methyl isoamyl ether, ethyl isobutyl ether, 2,2-diisobutyl-1,3-dimethoxypropane, 2-isopropyl-2-isopentyl-1,3-dimethoxypropane, 2,2-bis(cyclohexylmethyl)-1,3-dimethoxypropane, 2-isopropyl-2-3,7-dimethyloctyl-1,3-dimethoxypropane, 2,2-diisopropyl-1,3-dimethoxypropane, 2-isopropyl-2-cyclohexylmethyl-1,3-dimethoxypropane, 2,2-dicyclohexyl-1,3-dimethoxypropane, 2-isopropyl-2-isobutyl-1,3-dimethoxypropane, 2,2-diisopropyl-1,3-dimethoxypropane, 2,2-dipropyl-1,3-dimethoxypropane, 2-isopropyl-2-cyclohexyl-1,3-dimethoxypropane, 2-isopropyl-2-cyclopentyl-1,3-dimethoxypropane, 2,2-dicyclopentyl-1,3-dimethoxypropane, 2-heptyl-2-pentyl-1,3-dimethoxypropane and the like.

Among these electron donative compounds, the ester compounds are particularly preferred.

As the method for producing such solid catalyst component, for example, the methods disclosed in JP-B-52-39431, JP-B-52-36786, JP-A-54-94590, JP-A-55-36203, JP-A-56-41206, JP-A-57-63310, JP-A-57-59916, JP-A-58-83006, JP-A-61-218606, JP-A-1-319508, JP-A-3-706, etc. can be referred to.

These methods can be exemplified by the following: <ul id="ul0004" list-style="none"><li>(1) a method of reacting a liquid magnesium compound or a complex compound consisting of a magnesium compound and an electron donative compound with a depositing agent and thereafter treating the reaction product with a titanium compound or a combination of titanium compound and electron donative compound;</li><li>(2) a method of treating a solid magnesium compound or a complex compound consisting of a solid magnesium compound and an electron donative compound with a titanium compound or a combination of titanium compound and electron donative compound;</li><li>(3) a method of reacting a liquid magnesium compound with a liquid titanium compound in the presence of an electron donative compound and thereby depositing a solid titanium composite compound;</li><li>(4) a method of further treating the reaction product obtained by (1), (2) or (3) with a titanium compound or a combination of electron donative compound and titanium compound;</li><li>(5) a method of reducing an alkoxytitanium compound with an organomagnesium compound such as Grignard reagent or the like in the presence of an organic silicon compound having a Si-O bond to obtain a solid product, followed by treating said solid product with an ester compound, an ether compound and titanium tetrachloride;</li><li>(6) a method of mutually contacting and reacting a metal oxide, dihydrocarbylmagnesium and a halogen-containing alcohol to obtain a product, followed by treating or not treating the product with a halogenating agent and then contacting the product with an electron donative compound and a titanium compound;</li><li>(7) a method of treating or not treating a magnesium compound such as a magnesium salt of organic acid, alkoxymagnesium or the like with a halogenating agent followed by contacting the magnesium compound with an electron donative compound and a titanium compound; and</li><li>(8) a method of treating the compound obtained in (1) to (7) with any one of halogen, halogen compound and aromatic hydrocarbon.</li></ul>

Among these methods for synthesizing a solid catalyst, the methods (1) to (5) are preferred, and the method (5) is particularly preferred.

Although such solid catalyst component (A) can be used in itself alone, it may also be used after impregnation into a porous material such as inorganic oxides, organic polymers and the like, if desired. As said porous inorganic oxide, SiO₂, Al₂O₃, MgO, TiO₂, ZrO₂, SiO₂-Al₂O₃ composite oxide, MgO-Al₂O₃ composite oxide, MgO-SiO₂-Al₂O₃ composite oxide and the like can be referred to. As said porous organic polymer, polystyrene type, polyacrylic ester type, polyacrylonitrile type, polyvinyl chloride type, and polyolefin type of polymers can be referred to, of which specific examples include polystyrene, styrene-divinylbenzene copolymer, styrene-n,n'-alkylenedimethacrylamide copolymer, styrene-ethylene glycol dimethyl methacrylate copolymer, polyethyl acrylate, methyl acrylate-divinylbenzene copolymer, ethyl acrylate-divinylbenzene copolymer, polymethyl methacrylate, methyl methacrylate-divinylbenzene copolymer, polyethyleneglycol dimethyl methacrylate, polyacrylonitrile, acrylonitrile-divinylbenzene copolymer, polyvinyl chloride, polyvinylpyrrolidine, polyvinylpyridine, ethylvinylbenzene-divinylbenzene copolymer, polyethylene, ethylene-methyl acrylate copolymer, polypropylene and the like.

Of these porous materials, SiO₂, Al₂O₃ and styrene-divinylbenzene copolymer are preferred.

(b) Organoaluminum compound (B)

The organoaluminum compounds which can be used as component (B) of the present invention are those having at least one Al-carbon bond in one molecule.

Typical organoaluminum compounds of the present invention are represented by the following general formulas: R⁸<sub>m</sub>AlY<sub>3-m</sub> R⁹R¹⁰Al-O-AlR¹¹R¹² wherein R⁸ to R¹² each represents a hydrocarbon group having 1-8 carbon atoms, provided that R⁸ to R¹² may be identical with or different from one another, Y represents halogen, hydrogen or alkoxy group, and m represents a number satisfying 2 ≦ m ≦ 3. Specific examples of such organoaluminum compound include trialkylaluminums such as triethylaluminum, triisobutylaluminum, trihexylaluminum and the like, dialkylaluminum hydrides such as diethylaluminum hydride, diisobutylaluminum hydride and the like, mixtures of a trialkylaluminum and a dialkylaluminum halide such as mixture of triethylaluminum and diethylaluminum chloride, and alkylalumoxanes such as tetraethyldialumoxane, tetrabutyldialumoxane and the like.

Of these organoaluminum compounds, preferred are trialkylaluminums, mixtures of a trialkylaluminum and a dialkylaluminum halide and alkylalumoxanes, and particularly preferred are triethylaluminum, triisobutylauminum, mixture of triethylaluminum and diethylaluminum chloride, and tetraethyldialumoxane.

As the electron donative compound (C) of the present invention, at least two electron donative compounds including electron donative compound (α) and electron donative compound (β) are used, wherein said electron donative compounds (α) and (β) satisfy the following conditions. Thus, 105°C xylene-insoluble fraction of a homopolypropylene obtained by carrying out polymerization using electron donative compound (α) together with the above-mentioned solid catalyst component (A) and organoaluminum compound (B) shows a pentad stereoirregularity index (mmrr/mmmm) satisfying the following condition: <maths id="math0005" num=""><math display="inline"><mrow><mtext>0 ≦ mmrr/mmmm ≦ 0.0068,</mtext></mrow></math><img file="EP0657477A2_D0006.tif" /></maths> preferably the following condition: <maths id="math0006" num=""><math display="inline"><mrow><mtext>0.0004 ≦ mmrr/mmmm ≦ 0.0068,</mtext></mrow></math><img file="EP0657477A2_D0007.tif" /></maths> and further preferably the following condition: <maths id="math0007" num=""><math display="inline"><mrow><mtext>0.0004 ≦ mmrr/mmmm ≦ 0.0060,</mtext></mrow></math><img file="EP0657477A2_D0008.tif" /></maths> and 105°C xylene-insoluble fraction of a homopolypropylene obtained by carrying out polymerization using electron donative compound (β) together with the above-mentioned solid catalyst component (A) and organoaluminum compound (B) shows a pentad stereoirregularity index satisfying the following condition: <maths id="math0008" num=""><math display="inline"><mrow><mtext>0.0068 < mmrr/mmmm ≦ 0.0320,</mtext></mrow></math><img file="EP0657477A2_D0009.tif" /></maths> preferably the following condition: <maths id="math0009" num=""><math display="inline"><mrow><mtext>0.0068 < mmrr/mmmm ≦ 0.0200,</mtext></mrow></math><img file="EP0657477A2_D0010.tif" /></maths> and further preferably the following condition: <maths id="math0010" num=""><math display="inline"><mrow><mtext>0.0072 ≦ mmrr/mmmm ≦ 0.0140.</mtext></mrow></math><img file="EP0657477A2_D0011.tif" /></maths> As used in the present invention, the term "105°C xylene-insoluble fraction" means the weight (%) of a fraction measured according to the method of Kakugo et al. [Macromolecules, <u>21</u>, 314-319 (1988)], namely by dissolving a polypropylene in xylene at 130°C, throwing sea sand into the resulting solution, cooling the mixture to 20°C, again heating the mixture, and measuring the weight (%) of a fraction which is not extracted at 105°C and extracted in the temperature range exceeding 105°C and not exceeding 130°C. On the other hand, the term "pentad stereoirregularity index" means peak intensity ratio of the pentad fraction mmrr (the peak appears at about 21.01 ppm when TMS standard is used) to the pentad fraction mmmm (the peak appears at about 21.78 ppm when TMS standard is used) in the pentamer unit of a polypropylene molecular chain as measured at 135°C, at 270 MHz, on a solution of polymer in o-dichlorobenzene containing 10% by weight of C₆D₆ (concentration of polymer = 150 mg/3 ml) by means of ¹³C-NMR (EX-270, manufactured by Nippon Denshi K. K.) according to the paper of A. Zambelli et al. [Macromolecules, <u>13</u>, 687-689 (1975)].

In the present invention, as the electron donative compound used for preparation of electron donative catalyst component (C), the same electron donative compounds as used in the preparation of solid catalyst component (A) can be used. Preferably, electron donative compound (α) and electron donative compound (β) are independently selected from the organic silicon compounds mentioned below.

As such organic silicon compounds, those represented by the following general formula: R²<sub>n</sub>Si(OR³)<sub>4-n</sub> wherein R² represents a hydrocarbon group having 1-20 carbon atoms or a hydrogen atom, R³ represents a hydrocarbon group having 1-20 carbon atoms, and n represents a number satisfying 0 ≦ n < 4, can be referred to. Specific examples of such organic silicon compound include the following: tetramethoxysilane, tetraethoxysilane, tetrabutoxysilane, tetraphenoxysilane, methyltrimethoxysilane, ethyltrimethoxysilane, butyltrimethyoxysilane, isobutyltrimethoxysilane, t-butyltrimethoxysilane, isopropyltrimethoxysilane, cyclohexyltrimethoxysilane, phenyltrimethoxysilane, vinyltrimethoxysilane, dimethyldimethoxysilane, diethyldimethoxysilane, dipropyldimethoxysilane, propylmethyldimethoxysilane, diisopropyldimethoxysilane, dibutyldimethoxysilane, diisobutyldimethoxysilane, di-t-butyldimethoxysilane, butylmethyldimethoxysilane, butylethyldimethoxysilane, t-butylmethyldimethoxysilane, isobutylisopropyldimethoxysilane, t-butylisopropyldimethoxysilane, hexylmethyldimethoxysilane, hexylethyldimethoxysilane, dodecylmethyldimethoxysilane, dicyclopentyldimethoxysilane, cyclopentylmethyldimethoxysilane, cyclopentylethyldimethoxysilane, cyclopentylisopropyldimethoxysilane, cyclopentylisobutyl-dimethoxysilane, cyclopentyl-t-butyldimethoxysilane, dicyclohexyldimethoxysilane, cyclohexylmethyldimethoxysilane, cyclohexylethyldimethoxysilane, cyclohexylisopropyldimethoxy-silane, cyclohexylisobutyldimethoxysilane, cyclohexyl-t-butyldimethoxysilane, cyclohexylcyclopentyldimethoxysilane, cyclohexylphenyldimethoxysilane, diphenyldimethoxysilane, phenylmethyldimethoxysilane, phenylisopropyldimethoxysilane, phenylisobutyldimethoxysilane, phenyl-t-butyldimethoxysilane, phenylcyclopentyldimethoxysilane, vinylmethyldimethoxysilane, methyltriethoxysilane, ethyltriethoxysilane, butyltriethoxysilane, isobutyltriethoxysilane, t-butyltriethoxysilane, isopropyltriethoxysilane, cyclohexyltriethoxysilane, phenyltriethoxysilane, vinyltriethoxysilane, dimethyldiethoxysilane, diethyldiethoxysilane, dipropyldiethoxysilane, propylmethyldiethoxysilane, diisopropyldiethoxysilane, dibutyldiethoxysilane, diisobutyldiethoxysilane, di-t-butyldiethoxysilane, butylmethyldiethoxysilane, butylethyldiethoxysilane, t-butylmethyldiethoxysilane, hexylmethyldiethoxysilane, hexylethyldiethoxysilane, dodecylmethyldiethoxysilane, dicyclopentyldiethoxysilane, dicyclohexyldiethoxysilane, cyclohexylmethyldiethoxysilane, cyclohexylethyldiethoxysilane, diphenyldiethoxysilane, phenylmethyldiethoxysilane, vinylmethyldiethoxysilane, ethyltriisopropoxysilane, vinyltributoxysilane, phenyltri-t-butoxysilane, 2-norbornanetrimethoxysilane, 2-norbornanetriethoxysilane, 2-norbornanemethyldimethoxysilane, trimethylphenoxysilane, methyltriallyloxysilane, and the like.

Among the organic silicon compounds mentioned above, those preferably usable as electron donative compound (α) are, for example, organic silicon compounds represented by the following general formula: R¹³R¹⁴Si(OR¹⁵)₂ . In this general formula, R¹³ represents C₃-C₂₀ hydrocarbon group in which the carbon atom adjacent to Si is a secondary or tertiary carbon atom, and specific examples thereof include branched chain alkyl groups such as isopropyl, sec-butyl, t-butyl, t-amyl and the like, cycloalkyl groups such as cyclopentyl, cyclohexyl and the like, cycloalkenyl groups such as cyclopentenyl and the like, and aryl groups such as phenyl, tolyl and the like. In the general formula, R¹⁴ represents C₁-C₂₀ hydrocarbon group, of which specific examples include straight chain alkyl groups such as methyl, ethyl, propyl, butyl, pentyl and the like, branched chain alkyl groups such as isopropyl, sec-butyl, t-butyl, t-amyl and the like, cycloalkyl groups such as cyclopentyl, cyclohexyl and the like, cycloalkenyl groups such as cyclopentenyl and the like, and aryl groups such as phenyl, tolyl and the like. In the general formula, R¹⁵ represents C₁-C₂₀ hydrocarbon group, and preferably C₁-C₅ hydrocarbon group.

Specific examples of the organic silicon compound which can be used as such electron donative compound include the following: diisopropyldimethoxysilane, diisobutyldimethoxysilane, di-t-butyldimethoxysilane, t-butylmethyldimethoxysilane, isobutylisopropyldimethoxysilane, t-butylisopropyl-dimethoxysilane, dicyclopentyldimethoxysilane, cyclopentyl-isopropyldimethoxysilane, cyclopentylisobutyldimethoxysilane, cyclopentyl-t-butyldimethoxysilane, dicyclohexyldimethoxysilane, cyclohexylmethyldimethoxysilane, cyclohexylethyldimethoxysilane, cyclohexylisopropyldimethoxysilane, cyclohexylisobutyldimethoxysilane, cyclohexyl-t-butyldimethoxysilane, cyclohexylcyclopentyldimethoxysilane, cyclohexylphenyldimethoxysilane, diphenyldimethoxysilane, phenylmethyldimethoxysilane, phenylisopropyldimethoxysilane, phenylisobutyldimethoxysilane, phenyl-t-butyldimethoxysilane, phenylcyclopentyldimethoxysilane, diisopropyldiethoxysilane, diisobutyldiethoxysilane, di-t-butyldiethoxysilane, t-butylmethyldiethoxysilane, dicyclopentyldiethoxysilane, dicyclohexyldiethoxysilane, cyclohexylmethyldiethoxysilane, cyclohexylethyldiethoxysilane, diphenyldiethoxysilane, phenylmethyldiethoxysilane, 2-norbornanemethyldimethoxysilane and the like.

Among the organic silicon compounds mentioned above, those preferably usable as electron donative compound (β) are, for example, organic silicon compounds represented by the following general formula: R¹⁶R¹⁷Si(OR¹⁸)₂ wherein R¹⁶ represents a C₁-C₂₀ hydrocarbon group and particularly preferably a straight chain alkyl group such as methyl, ethyl, propyl, butyl, pentyl and the like; R¹⁷ represents a C₁-C₅ hydrocarbon group and particularly a hydrocarbon group having one carbon atom; and R¹⁸ represents a C₁-C₂₀ hydrocarbon group and preferably a C₁-C₅ hydrocarbon group.

Specific examples of such organic silicon compound which can be used as electron donative compound (β) include the following: dimethyldimethoxysilane, ethylmethyldimethoxysilane, propylmethyldimethoxysilane, butylmethyldimethoxysilane, pentylmethyldimethoxysilane, hexylmethyldimethoxysilane, heptylmethyldimethoxysilane, octylmethyldimethoxysilane, dodecylmethyldimethoxysilane and the like.

In the process for producing a polyolefin of the present invention, the method for feeding the catalyst components to a polymerization reactor is not particularly limited, so far as the catalyst components are fed in a moisture-free state in an inert gas such as nitrogen gas, argon gas or the like.

According to the polymerization process of the present invention, an olefin is polymerized in the presence of a catalyst consisting of a solid catalyst component (A), an organoaluminum compound (B) and an electron donative component comprising at least two electron donative compounds including electron donative compound (α) and electron donative compound (β). In this polymerization reaction, there is no particular limitation except that mmrr/mmmm of a homopolypropylene obtained by carrying out the polymerization in the presence of a catalyst consisting of (A), (B) and a single component (α) must satisfy the following condition: <maths id="math0011" num=""><math display="inline"><mrow><mtext>0 ≦ mmrr/mmmm ≦ 0.0068</mtext></mrow></math><img file="EP0657477A2_D0012.tif" /></maths> and mmrr/mmmm of a homopolypropylene obtained by carrying out the polymerization in the presence of a catalyst consisting of (A), (B) and a single component (β) must satisfy the following condition: <maths id="math0012" num=""><math display="inline"><mrow><mtext>0.0068 ≦ mmrr/mmmm ≦ 0.0320.</mtext></mrow></math><img file="EP0657477A2_D0013.tif" /></maths>

In the polymerization process of the present invention, an olefin is polymerized in the presence of the above-mentioned catalyst. If desired, a preliminary polymerization may be carried out before carrying out the main polymerization process. The preliminary polymerization is effected, for example, by feeding a small amount of olefin in the presence of solid catalyst component (A) and organoaluminum compound (B), and it is preferably carried out in the state of a slurry. As the solvent used for preparing the slurry, inert hydrocarbons such as propane, butane, isobutane, pentane, isopentane, hexane, heptane, octane, cyclohexane, benzene or toluene can be referred to. In preparing the slurry, a liquid olefin may be used, if desired, in place of a part or the whole of the inert hydrocarbon solvent.

In carrying out the preliminary polymerization, the amount of organoaluminum compound may be selected from such a wide range as from 0.5 to 700 moles per mole of titanium atom in the solid catalyst component. The amount of organoaluminum compound is preferably from 0.8 mole to 500 moles, and particularly preferably from 1 mole to 200 moles, both on the same basis as above.

The amount of olefin consumed in the preliminary polymerization is from 0.01 to 1,000 g, preferably from 0.05 to 500 g, and particularly preferably from 0.1 to 200 g, per gram of the solid catalyst component.

In carrying out the preliminary polymerization, the concentration of slurry is preferably from 1 to 500 g of solid catalyst component per liter of solvent, and particularly preferably from 3 to 300 g solid catalyst component per liter of solvent. The temperature of preliminary polymerization is preferably from -20°C to 100°C, and particularly preferably from 0°C to 80°C. In the process of the preliminary polymerization, the partial pressure of propylene in the gas phase is preferably from 0.01 to 20 kg/cm² and particularly preferably from 0.1 to 10 kg/cm², provided that this condition is not applicable to propylene which is in a liquid state at the pressure and temperature of preliminary polymerization. Although the period of time of the preliminary polymerization is not critical, it is usually from 2 minutes to 15 hours.

In carrying out the preliminary polymerization, the method for feeding solid catalyst component, organoaluminum compound and olefin may be any of a method of contacting a solid catalyst component with an organoaluminum compound and thereafter feeding olefin and a method of contacting a solid catalyst component with olefin and thereafter feeding an organoaluminum compound. The method for feeding olefin may be any of a method of portionwise feeding olefin while keeping the inner atmosphere of polymerization reactor at a prescribed pressure and a method of wholly feeding a prescribed quantity of olefin at the beginning. It is also possible to add a chain transfer agent such as hydrogen or the like in order to regulate molecular weight of the polymer formed.

In subjecting the solid catalyst component to a preliminary polymerization with a small amount of olefin in the presence of an organoaluminum compound, the preliminary polymerization may be carried out in the presence of an electron donative compound, if desired. The electron donative compound used for this purpose is a part or the whole of the above-mentioned electron donative catalyst component (C). Its amount is 0.01-400 moles, preferably 0.02-200 moles and particularly preferably 0.03-100 moles per mole of titanium atom present in the solid catalyst component, and is 0.003-5 moles, preferably 0.005-3 moles and particularly preferably 0.01-2 moles per mole of the organoaluminum compound.

In carrying out the preliminary polymerization, the method for feeding the electron donative compound is not particularly limited. Thus, an electron donative compound may be fed independently of an organoaluminum compound, or after a previous contact with an organoaluminum compound. The olefin used in the preliminary polymerization may be identical with or different from the olefin used in the main polymerization step which will be mentioned later.

After carrying out a preliminary polymerization in the above-mentioned manner or without carrying out the preliminary polymerization, a main polymerization of olefin can be effected in the presence of a polymerization catalyst consisting of the above-mentioned solid catalyst component (A), organoaluminum compound (B) and electron donative catalyst component (C).

The solid catalyst component, organoaluminum compound and electron donative catalyst component consisting of at least two electron donative compounds may be fed either independently of one another or after mutually contacting any two of them. Regarding the electron donative compounds (α) and (β) as the electron donative catalyst components, it is allowable to use both of them at the time of preliminary polymerization or it is also allowable to use one of them in the preliminary polymerization and to use the other in the main polymerization or it is also allowable to use both of them firstly in the main polymerization.

In the main polymerization, the amount of the organoaluminum compound may be selected from such a wide range as from 1 mole to 1,000 moles per mole of titanium atom in the solid catalyst component. Particularly preferably, however, the amount of the organoaluminum compound is in the range of from 5 to 600 moles on the same basis as above.

In the main polymerization, the total amount of the electron donative catalyst component (C) is from 0.1 to 2,000 moles, preferably from 0.3 to 1,000 moles and particularly preferably from 0.5 to 800 moles per mole of titanium atom present in the solid catalyst component. The total amount of electron donative component (C) is from 0.001 to 5 moles, preferably from 0.005 to 3 moles and particularly preferably from 0.01 to 1 mole per mole of the organoaluminum compound.

The main polymerization can be effected at a temperature ranging from -30°C to 300°C and preferably from 20°C to 180°C. Although there is no limitation upon the polymerization pressure, a pressure of from ordinary pressure to 100 kg/cm² and preferably from about 2 to about 50 kg/cm² is usually adopted from the viewpoint of industrial and economical practicabilities. As the mode of polymerization, batch process and continuous process can both be adopted. A slurry polymerization process or a solution polymerization process using an inert hydrocarbon solvent such as propane, butane, isobutane, pentane, hexane, heptane, octane and the like, a bulk polymerization process using propylene keeping liquid at the polymerization temperature as a medium, and a gas phase polymerization process can also be practiced.

At the time of main polymerization, a chain transfer agent such as hydrogen and the like may be added for the purpose of regulating molecular weight of the formed polymer.

The olefins which can be used in the main polymerization are those having 3 or more carbon atoms. Specific examples of the olefin include propylene, butene-1, pentene-1, hexene-1, 3-methyl-butene-1, 3-methyl-pentene-1, 4-methyl-pentene-1, octene-1, decene-1, dodecene-1, cyclohexene and the like. Of these olefins, propylene and butene-1 are preferabe for use in homopolymerization, and mixed olefins consisting mainly of propylene or butene-1 are preferable for use in copolymerization. Of these olefin monomers, propylene is particularly preferred. In the copolymerization of the present invention, two or more kinds of olefin compounds selected from ethylene and the above-mentioned olefin compounds may be used in the form of a mixture. Compounds having a plurality of unsaturated bonds such as conjugated dienes and non-conjugated dienes can also be used in the copolymerization.

The first characteristic feature of the polypropylene used for production of the biaxially oriented film of the present invention consists in that it exhibits a good stretchability in the process of film-making. Further, the second characteristic feature thereof consists in that a biaxially oriented film obtained by biaxially stretching said polypropylene is excellent in transparency and stiffness.

The polypropylene produced according to the process of the present invention contains a specified quantity of 23°C decalin-soluble fraction. The content of 23°C decalin-soluble fraction in said polypropylene is in the range of from 3.0 to 10.0% by weight, preferably from 3.0 to 9.0% by weight and particularly preferably from 3.5 to 8.5% by weight. If the content of 23°C decalin-soluble fraction in said polypropylene exceeds the above-specified upper limit, the biaxially oriented film prepared therefrom is insufficient in stiffness. If the content of 23°C decalin-soluble fraction in said polypropylene is lower than the above-specified lower limit, the biaxially oriented film obtained therefrom is insufficient in stretchability.

The temperature at which the polypropylene of the present invention exhibits a complex elastic modulus of 1 × 10⁹ dynes/cm² when a vibration of 110 Hz is applied to the polypropylene is in the range of from 134 to 152°C and preferably from 137 to 149°C. If said temperature is higher than the above-specified upper limit, stretchability is insufficient. If said temperature is lower than the above-specified lower limit, stiffness of the biaxially oriented film is insufficient.

Melt flow rate (MFR) of the polypropylene of the present invention at 230°C is in the range of from 0.5 to 10.0 g/10 minutes and preferably from 1.0 to 8.0 g/10 minutes. MFR is a parameter representing the average molecular weight of a polymer, and its greater value means a lower average molecular weight. If MFR of said polypropylene is higher than the above-specified upper limit, stretchability is not good. If MFR of the polypropylene is lower than the above-specified lower limit, flow property at the time of extrusion is not good to bring about undesirable results.

Into the polypropylene of the present invention, ethylene and α-olefins having 4 or more carbon atoms may be copolymerized unless the object of the present invention is damaged by their copolymerization.

Into the polypropylene of the present invention, a stabilizer, a slipper, an antistatic agent, an anti-blocking agent and the like may be incorporated, unless the object of the present invention is damaged by adding these additives. A variety of inorganic and organic fillers may also be added, unless the object of the present invention is damaged by their addition.

The polypropylene of the present invention is made into a film and subjected to a stretching processing usually in the following manner to give a biaxially oriented film. Thus, the propylene is melted in an extruder, and thereafter extruded from a T die and cooled and solidified by means of cooling rolls to give a sheet-form material. Subsequently, the sheet thus obtained is pre-heated and stretched in the longitudinal direction by means of a number of heating rolls, and then laterally stretched by means of a heating oven consisting of a pre-heating part, a stretching part and a heat-treating part, after which it is subjected to a corona treatment if desired, and finally wound up. Although the melting temperature of the polypropylene varies depending on molecular weight, the above treatment is usually carried out at a temperature of from 230°C to 290°C. The temperature of longitudinal stretching is from 130°C to 150°C, and the draw ratio in the longitudinal direction is usually from 4 to 6. The temperature of lateral stretching is from 150°C to 165°C, and the draw ratio in the lateral direction is usually from 8 to 10.

The biaxially oriented polypropylene film produced in the above-mentioned manner is superior to prior biaxially oriented films in transparency and stiffness, while retaining a good stretchability.

BRIEF DESCRIPTION OF THE DRAWING

Figure 1 is a flow chart for facilitating understanding of the present invention. This flow chart is a typical example of the embodiments of the present invention, and the present invention is by no means limited thereby.

DESCRIPTION OF THE PREFERRED EMBODIMENTS

Next, the present invention is explained in more detail with reference to the following examples. The invention is by no means limited by these examples, unless essentiality of the invention is exceeded. The characteristic properties referred to in the examples and comparative examples were measured in the following manner.

(1) 20°C xylene-soluble fraction (referred to as CXS) content:

One gram of polymer powder was dissolved in 200 ml of boiling xylene, slowly cooled to 50°C, immersed in ice water and cooled with stirring to 20°C and allowed to stand at 20°C for 3 hours. The deposited polymer was filtered off. Xylene was evaporated off from the filtrate, the residue was dried at 60°C under a reduced pressure, and the fraction soluble in 20°C was recovered.

(2) Boiling heptane-insoluble fraction (referred to as II) content:

By means of Soxhlet extractor, 3 g of polymer powder was subjected to an extraction treatment with 100 ml heptane for 6 hours. After vaporizing off the heptane from the extract solution, the residue was dried under reduced pressure and the fraction soluble in boiling heptane was recovered.

(3) Intrinsic viscosity (referred to as [η]):

Measured in tetralin solvent at 135°C.

(4) Bulk density (referred to as BD):

Measured according to ASTM D-1865.

(5) Pentad stereoirregularity index (mmrr/mmmm) of 105°C xylene-insoluble fraction:

Measured according to the method mentioned in the specification of the present invention.

(6) 23°C decalin-soluble fraction content (% by weight)

Two grams of polypropylene was completely dissolved in 100 ml of boiling decalin, cooled to 23°C and allowed to stand for more than 4 hours. The resulting mixture was separated into deposited matter and filtrate by filtration. The filtrate was evaporated to dryness, and the residue was dried at 120°C under a reduced pressure and weighed.

(7) Temperature at which sample polymer shows a complex elastic modulus of 1 × 10⁹ dynes/cm² when a vibration of 110 Hz is applied (Tl) (unit: °C)

According to JIS K6758-81, a polypropylene was formed into a press sheet having a thickness of 0.25 mm, from which test pieces having a length of 40 mm, a width of 2 mm and a thickness of 0.25 mm were cut out. While applying a vibration of 110 Hz to the test piece with Automatic Dynamic Viscoelasticity Measuring Machine (RHEOBIBRON DV-II-EA, manufactured by Orientec Co., Ltd.), the temperature at which a complex elastic modulus of 1 × 10⁹ dynes/cm² was shown was measured.

(8) Melt flow rate (MFR) (unit: g/10 minutes)

Measured according to JIS K7210, condition 14.

(9) Haze (unit: %)

Measured according to ASTM D1003.

(10) Young's modulus (unit: Kg/cm²)

Test pieces having a width of 20 mm were cut out in the longitudinal direction (MD) on the one hand and in the lateral direction (TD) on the other hand. S-S curve was pictured by means of a tensile tester at a chuck distance of 60 mm and a tensile speed of 5 mm/minute, from which initial elastic modulus was determined.

(11) Stretchability

According to JIS K6758-81, a polypropylene was formed into a press sheet having a thickness of 500 µ, from which a sample of 90 mm × 90 mm was cut out. The sample was biaxially oriented under the following conditions. A case that no good film was obtained due to uneven stretching or stretching cracking was expressed by defective stretchability (X) and a case that a good film was obtained was expressed by good stretchability (○). Stretching machine: Biaxial Stretching Tester manufactured by Toyo Seiki Co. Temperature: 135°C Thermal inertia time: 3 minutes Draw ratio: 5 × 5 Stretching speed: 5 m/minute.

Example 1

(a) Synthesis of organomagnesium compound

After replacing the inner atmosphere of a 1,000 ml flask equipped with a stirrer, a reflux condenser, a dropping funnel and a thermometer with argon gas, 32.0 g of sliced metallic magnesium for Grignard reaction was thrown into the flask. The dropping funnel was charged with 120 g of butyl chloride and 500 ml of dibutyl ether, and about 30 ml of the mixture was dropped onto the magnesium in the flask to start a reaction. After starting the reaction, the mixture was continuously dropped for 4 hours at 50°C. After the dropping, the reaction was continued for an additional one hour at 60°C. Then, the content of the flask was cooled to room temperature, and the solid matter was filtered off. A part of the reacted solution was sampled out, the butylmagnesium chloride present in the solution was hydrolyzed with 1N sulfuric acid, and the excessive sulfuric acid was back titrated with 1N aqueous solution of sodium hydroxide to determine the concentration of butylmagnesium chloride, using phenolphthalein as an indicator. As the result, the concentration was 2.1 moles/liter.

(b) Synthesis of solid product

After replacing the inner atmosphere of a 500 ml flask equipped with a stirrer and a dropping funnel with argon gas, 290 ml of hexane, 7.7 g (23 mmoles) of tetrabutoxy-titanium and 75.0 g (360 mmoles) of tetraethoxysilane were thrown into the flask to prepare a homogeneous solution. Then, 181 ml of the solution of organomagnesium compound synthesized in (a) was slowly dropped into the flask from the dropping funnel over a period of 3.5 hours, while keeping the inner temperature of the flask at 5°C. After completing the dropping, the content of the flask was stirred at room temperature for an additional one hour and then separated into solid and liquid phases. The solid product was three times washed with each 300 ml portion of hexane and then three times with each 300 ml portion of toluene, after which 300 ml of toluene was added thereto.

A part of the solid product slurry was sampled out and its composition was analyzed to reveal that the solid product contained 2.1% by weight of titanium atom, 36.2% by weight of ethoxy group and 3.8% by weight of butoxy group. Concentration of the slurry was 0.125 g/ml.

The supernatant of the slurry (125 ml) was withdrawn, 45.8 ml (171 mmoles) of diisobutyl phthalate was added thereto and reacted at 95°C for 30 minutes. After the reaction, the solid matter was separated from the liquid phase and twice washed with each 287 ml portion of toluene.

(d) Synthesis of solid catalyst component (activating treatment)

After completing the washing treatment of (c), 74.5 ml of toluene, 2.9 ml (11 mmoles) of diisobutyl phthalate, 6.3 ml (37 mmoles) of butyl ether and 99 ml (0.90 mole) of titanium tetrachloride were introduced into the flask and reacted at 100°C for 3 hours. After the reaction, the solid matter was separated from liquid phase and twice washed each 287 ml portion of toluene at the same temperature as above. Then, 74.5 ml of toluene, 6.3 ml (37 mmoles) of butyl ether and 50 ml (0.45 mole) of titanium tetrachloride were added and reacted at 100°C for one hour. After the reaction, the solid matter was separated from liquid phase at that temperature, four times washed with each 287 ml portion of toluene, three times washed with each 287 ml portion of hexane, and dried under reduced pressure to obtain 46 g of a solid catalyst component.

The solid catalyst component thus obtained contained 2.2% by weight of titanium atom, 10.7% by weight of phthalic ester, 0.7% by weight of ethoxy group and 0.3% by weight of butoxy group.

(e) Polymerization of propylene

After replacing the inner atmosphere of a stainless steel-made autoclave equipped with a stirrer and having a capacity of 3 liters with argon gas, 2.6 mmoles of triethylaluminum, 0.065 mmole of cyclohexylethyldimethoxysilane, 0.065 mmole of n-propylmethyldimethoxysilane and 8.7 mg of the solid catalyst component synthesized in (d) were charged, to which was fed hydrogen gas up to a partial pressure of 0.33 kg/cm². Then, after feeding 780 g of liquefied propylene, temperature of the autoclave was elevated to 80°C and a polymerization was carried out at 80°C for one hour. After the polymerization, the unreacted monomer was purged and the polymer formed was dried at 60°C for 2 hours under a reduced pressure. Thus, 254 g of a polypropylene powder was obtained.

This means that the yield of polypropylene per gram of solid catalyst component (hereinafter, referred to as PP/Cat) was 29,200 (g/g). The proportion of 20°C xylene-soluble fraction (CXS) was 1.6% by weight, and the proportion of boiling heptane-insoluble fraction (II) was 99.1% by weight, both based on total yield of the polymer. Intrinsic viscosity ([η]) of the polymer was 1.77, and bulk density of the polymer (BD) was 0.41 (g/ml). The content of 105°C xylene-insoluble fraction was 78.5% by weight, and pentad stereoirregularity index (mmrr/mmmm) of the 105°C xylene-insoluble fraction was 0.0060. The conditions and results of the polymerization are summarized in Table 1.

Example 2

(a) Polymerization of propylene

Propylene was polymerized in the same manner as in Example 1 (e), except that n-butylmethyldimethoxysilane was used in place of the n-propylmethyldimethoxysilane.