Organopolysiloxanes and a method of setting hair using the same

BACKGROUND OF THE INVENTION

Field of the Invention

:

0001The present invention relates to novel organopolysiloxanes and to a method of setting hair using the same. More particularly, the invention relates to organopolysiloxanes which are excellent in the hair setting performance and the hair set retentivity, which provide soft touch to the set hair, which have good removal-by-shampoo property, and which are useful as an effective component in hair setting compositions, and to a method of setting hair using the same.

Description of Related Art

:

0002People make their hair styles in different manners. Generally, hair styles are made by applying a hair setting agent to dry or towel-dried hair, then giving hair a desired form with or without drying the hair naturally or with a drier. Hair setting agents which are generally used in this method are in the forms of foam, spray, mist, lotion, cream, gel, etc. Another method of making a hair style is to apply a hair setting agent in a spray or mist form to the hair which has been given shape by curlers and the like, and to maintain the given shape. In both methods, hair setting agents are required to have a function that maintains the finished hair style over time. In addition, good sensation free from roughness and stickiness is desirable.

0003Conventional hair setting agents generally contain film-forming setting polymers, examples of which include polyvinylpyrrolidones, vinylpyrrolidone - vinyl acetate copolymers, acrylic ester - methacrylic ester - acrylic acid copolymers, methylvinyl ether - maleic anhydride copolymers and copolymers of methacrylic esters (compounds in which dialkylaminoethyl methacrylate and monochloroacetic acid are bonded to each other).

0004Hair setting agents containing these film-forming setting polymers have a drawback that the formed hair style collapses as time passes. Especially, when the humidity is high, the shape of the set hair is easily lost.

0005The main reason which explains the lost of shape is that the setting polymer which is bonded to hair fibers is deformed over time. In highly humid conditions, the polymer plasticizes by absorbing humidity and thus easily gets deformed to shorten the set retention.

0006Therefore, setting polymers having high elasticity have been conventionally used to avoid easy deformation. However, such polymers involve a drawback in that the hair treated with them results in a stiff and rough texture, which is undesirable. In order to improve the touch to the hair, hair setting agents generally contain a variety of sensation improvers such as silicone oils, modified silicones and oil agents, which in turn deteriorate the set retaining ability. Accordingly, there has been a difficulty in obtaining a good set retention and favorable touch to the hair at the same time.

0007The shape of set hair also is lost by external force, such as winds and hand touch. Generally speaking, polymers having a high elasticity is brittle, so impacts of external force easily break polymer films before they get deformed, which causes collapsing of the set shape.

0008In order to overcome these problems, polymers which exhibit flexible and rubber-elastic properties without causing plastic deformation are required. Polymers which are free from plastic deformation include those having a intramolecular/intermolecular cross-linking such as in vulcanized rubbers. Cross-linked polymers are not suitable for the practical use because they generally have an extremely low solubility in solvents such as water and alcohols. Japanese Patent Application Laid-open (kokai) No. 4-139116 discloses a hair setting agent containing a polymer which is obtained by allowing a polyalkylene oxide and polycarboxylic acid or diisocyanate to react each other. This polymer forms a flexible film but is inferior to silicone derivatives with regard to the smoothness of the hair fibers.

0009In an attempt to impart favorable touch to hair fibers, silicone derivatives have been incorporated in hair cosmetic compositions. For example, Japanese Patent Application Laid-open (kokai) No. 61-158914 and Japanese Patent Application Laid-open (kokai) No. 61-161214 disclose hair cosmetic compositions which contain partially cross-linked organic silicone resins. These resins, however, are cross-linked by covalent bonds, which render the resulting compositions to have a very low solubility and poor removal-by-shampoo property which mar the appearance of the hair.

0010Japanese Patent Application Laid-open (kokai) No. 4-261113 discloses a composition for protecting the hair which contains a silicone polymer having a cross-linkable functional group, and a cross linking agent. A characteristic feature of this composition is that when the composition is exposed to the air, cross-linking takes place to exhibit properties like an elastomer. In order to give set retention property to a hair cosmetic composition, a certain extent of cross-linked structure must be present therein. But in the case of the composition according to this publication, if the degree of cross-linking is elevated to such an extent that set-retention property is evident, removal-by-shampoo property in turn deteriorates, that is, the composition cannot completely be removed by shampooing, which means that the hair style cannot be easily altered. This is because the cross-linking is based on covalent bonding.

0011Japanese Patent Application Laid-open (kokai) No. 63-2918 discloses a hair styling mousse which contains a hydroxylated polyorganosiloxane emulsion capable of forming an elastomer. The silicone elastomer disclosed in this publication is similar to that disclosed in U.S. patent No. 4,221,688, and forms an elastomer by cross-linking based on covalent bonding as in the above-mentioned Japanese Patent Application Laid-open (kokai) No. 4-261113. Accordingly, the elastomer involves the same disadvantage as mentioned above.

0012Japanese Patent Application Laid-open (kokai) No. 63-22010 discloses a hair styling composition which contains a hard type silicone polymer and a volatile carrier therefor. Examples of the polymer include, for example, filler reinforcing polydimethylpolysiloxane gums which encompass those having a terminal hydroxyl group, cross-linked siloxanes such as organic substituted silicone elastomers, organic substituted siloxane gums which encompass those having a terminal hydroxyl group, resin-reinforced siloxanes and cross-linked siloxane polymers.

0013However, organopolysiloxanes which are characterized only by a high molecular weight, or which merely contain a filler are vulnerable to plastic deformation and do not have good setting performance. Those which have a terminal hydroxyl group and which are cross-linked with fillers have an irreversible property. That is, if cross-linking proceeds until the setting property is evident, solubility and removal-by-shampoo property after application are extremely lowered. The organic substituted silicone elastomers are, like those described in the afore-mentioned Japanese Patent Application Laid-open (kokai) No. 63-2918, similar to those disclosed in U.S. patent No. 4,221,688, and involve the same disadvantage as mentioned above.

0014Moreover, Japanese Patent Application Laid-open (kokai) No. 60-68820, Japanese Patent Application Laid-open (kokai) No. 2-276824 and Japanese Patent Application Laid-open (kokai) No. 4-85334 disclose silicones which have been modified with a saccharide residue or poly(N-acylalkyleneimine). The silicones disclosed in these publications are low molecular weight silicones, and therefore, they are either liquid at room temperature or brittle even when they are solid. Thus, they are not suitable as components of hair setting compositions.

0015Japanese Patent Publication (Kokoku) No. 60-240732 disclose silicones which have been modified with betaine groups. The silicones disclosed in the publication are low molecular weight silicones and therefore, they are liquid at room temperature. Thus, they are not suitable as components of hair setting compositions.

0016EP-A-524 612 discloses a hair cosmetic comprising a poly(N-acylalkyleneimine)-modified silicone having a poly(N-acylalkyleneimine) segment and an organopolysiloxane segment at a weight ratio of said poly(N-acylalkyleneimine) segment to said organopolysiloxane segment of from 1/20 to 20/1, and having a molecular weight of from 500 to 500,000, and a film-forming polymer. The same content is reflected in JP-A-4-85334.

0017GB-A-1 097 453 refers to organosilicon compounds of the formula: <chemistry id="chem0001" num="0001"><img file="EP0640643B1_D0001.tif" /></chemistry> that are useful in sizing agent and elastomeric materials.

0018Finally, EP-0 489 303 A1 discloses a hair treating composition comprising a mixture of a film-forming material and a solvent for the film-forming material, the film-forming material being an amino-functional silicone resin which is the reaction product of a cyclic silyl amine and a silicone resin.

0019In view of the foregoing, the present invention is to provide a method of setting hair in which excellent hair setting effect and prolonged set retention can be obtained, favorable soft touch is imparted to the hair after it has undergone a setting treatment, and the shape given by the setting treatment can be easily restored to the original shape by ordinary shampooing, and also to provide a novel organopolysiloxane which is used in this method.

SUMMARY OF THE INVENTION

0020Applicants have disclosed that organopolysiloxanes having specifically defined properties exhibit excellent hair-set retentivity, impart soft sensation to the hair, and are easily removed by shampooing.

0021Accordingly, an object of the present invention is to provide an organopolysiloxane as defined in present claim 1 which generates intramolecular or intermolecular cross-linking based on dipole-dipole interaction, hydrogen-bonding or ion bonding, and which is not ruptured or plastically deformed before the extension ratio reaches a value of 15% at a temperature of 20°C under relative humidity of 65%.

0022Another object of the present invention is to provide a method of setting hair by applying a composition which comprises the organopolysiloxane to the hair and then removing a solvent present in the composition.

0023A further object of the present invention is to provide a hair setting composition which contains the defined organopolysiloxane.

0024A still further object of the present invention is to provide for a use of the organopolysiloxane in setting hair.

0025The hair which is set by the method or the composition according to the present invention retains the given shape over time, and imparts a soft touch to the hair without roughening the hair. In addition, the shape given by the setting treatment can be easily restored to the original shape by ordinary shampooing.

0026The above and other objects, features and advantages of the present invention will become apparent from the following description.

DETAILED DESCRIPTION OF THE INVENTION AND PREFERRED EMBODIMENTS

0027The organopolysiloxane according to the present invention undergoes intramolecular and intermolecular cross-linking based on a bonding mechanism other than the covalent bonding. This phenomenon takes place in a solvent-free system or in a solution system of high concentration. Since the cross-linking is on a non-covalent bond basis, it is easily cleaved in a dilute solution. The presence of this cross-linking can be confirmed under transmission electron microscope (TEM) to check whether a micro phase separation is observed.

0028The organopolysiloxane according to the present invention has a weight-average molecular weight of at least 50,000, and is in a solid state at normal ambient temperatures and under normal pressure (Generally, -10 to 40°C, 1 atm). Moreover, the organopolysiloxane is soluble or completely dispersible in water or in lower alcohols, so that the cross-linking is easily cleaved in water or in lower alcohols. The lower alcohols are C1 to C6 alcohols.

0029The bonding mechanism according to the present invention is dipole-dipole interaction, hydrogen bonding or ion bonding and must be easily cleaved in water or lower alcohols. The organopolysiloxane according to the present invention has one or more functional groups which permits formation of the above bonds.

0030The organopolysiloxane according to the present invention is not ruptured or plastically deformed before the extension ratio reaches a value of 15% at 20°C under relative humidity of 65%. Generally speaking, deformed polymers can easily restore their original shape if the deformation degree is small, but when the deformation degree is significant, they do not. This phenomenon in which the original shape is not recovered is called plastic deformation. If a polymer is hard and brittle, it may rupture before plastic deformation takes place. In either case of rupture or plastic deformation, the original shape cannot be restored, and therefore, polymers which cause them are not suitable as hair setting polymers. Accordingly, the above-mentioned property possessed by the organopolysiloxane according to the present invention is a so-called rubber-elasticity, and it is a very important property for imparting a strong set retentivity and improving the touch to the hair which has undergone a setting treatment.

0031Whether plastic deformation takes place or not at a 15% extension can be confirmed by a simple test. A test piece having a thickness of about 0.2 mm, a length of about 20 mm and a width of about 5 mm is extended by 3 mm (15%) at a crosshead speed of 20 mm/min while the stress-strain curve is recorded at a temperature of 20°C and under relative humidity of 65%. Immediately thereafter, the crosshead is returned to the original position at the same speed. After 10 minutes, the test piece is extended again. If the stress-strain curve recorded in the second test is identical to the curve recorded in the first test, the test piece is completely restored without causing any plastic deformation. By contrast, if plastic deformation takes place, the test piece has been lengthened after the reciprocating movement in the first test, the stress is imposed on the test piece with a time lag in the second test, and as a result, the stress-strain curve becomes different from the curve in the first test.

0032In order to generate intramolecular and intermolecular cross-linkings based on dipole-dipole interaction, hydrogen bonding or ion bonding, a polar functional group must be present in a side chain or at a terminal of an organopolysiloxane segment. Such polar functional groups include a group having dipole-dipole interaction, a group having hydrogen bonds, and a group having ionic bonds. The groups having dipole-dipole interaction include N-acylalkyleneimine and pyrrolidon. The groups having hydrogen bonds include: a group having hydroxide group, such as a sugar and polyvinylalcohol; a group having amide groups, such as, poly-N-morpholin(meth)acrylamide, poly-N-vinylvinylpyrrolidone, poly-N-vinylacetoamide, polyaminoacid, and C_1-4 mono- or di-alkyl(meth)acrylamide polymer including poly(meth)acrylamide, polydimethylacrylamide and polydiethylacrylamide. The groups having ionic bonds include an amphoteric ionomer and an amineoxide. The amphoteric ionomer is for example a betaine polymer such as carbobetaine, sulfobetaine and phosphobetaine; a copolymer of an anionic monomer such as acryl acid, and a cationic monomer such as N,N-dimetylaminoethyl(meth)acrylate and N,N-dimethylaminopropyl(meth)acrylamide.

0033Examples of the organopolysiloxanes according to the present invention include the following (A), (B), (C) and (D). <ul id="ul0001" list-style="none" compact="compact"><li>(A): Organopolysiloxanes in which at least one silicon atom in a side chain or at a terminal of an organopolysiloxane segment is bonded, through an alkylene group having a hetero atom, to poly(N-acylalkyleneimine) constituted by a recurring unit represented by the following general formula (1): <chemistry id="chem0002" num="0002"><img file="EP0640643B1_D0002.tif" /></chemistry> wherein R¹ represents hydrogen, C1-C22 alkyl, cycloalkyl, aralkyl or aryl, and n represents a number of 2 or 3. In these organopolysiloxanes (A), the ratio by weight between the organopolysiloxane segment and the poly(N-acylalkyleneimine) segment is from 98/2 to 40/60. More preferably, the ratio is from 94/6 to 60/40 and the weight-average molecular weight of the organopolysiloxane is from 50,000 to 500,000, preferably from 100,000 to 300,000. If the ratio by weight between an organopolysiloxane segment and a poly(N-acylalkyleneimine) segment is over 98/2 or under 40/60, or the weight average molecular weight of the organopolysiloxane is less than 50,000, rupture or plastic deformation tend to occur before the extension ratio reaches 15%. On the other hand, if the weight average molecular weight exceeds 500,000, production of organopolysiloxane becomes difficult. Examples of the alkylene group which has a hetero atom and which is present between an organopolysiloxane segment and a poly(N-acylalkyleneimine) segment for bonding them include a C2-C20 alkylene which contains 1 to 3 nitrogen atoms, oxygen atoms and/or sulfur atoms. Specific examples include the following: <chemistry id="chem0003" num="0003"><img file="EP0640643B1_D0003.tif" /></chemistry> wherein X^- represents a counter ion of a quaternary ammonium salt. In the organopolysiloxanes (A), the cycloalkyl group represented by R¹ are those having 3 to 6 carbon atoms. Examples of the aralkyl group include phenylalkyl and naphthylalkyl. Examples of aryl group include phenyl, naphthyl and alkyl-substituted phenyl. The organopolysiloxanes (A) are prepared by allowing the organopolysiloxane represented by the following formula (2): <chemistry id="chem0004" num="0004"><img file="EP0640643B1_D0004.tif" /></chemistry> wherein the substituents R² are the same or different from each other and independently represent C1-C22 saturated alkyl or phenyl; R³ and R⁴, independently, are the same as R² or, independently represent the following groups: <chemistry id="chem0005" num="0005"><img file="EP0640643B1_D0005.tif" /></chemistry> R⁵ represents the following groups, <chemistry id="chem0006" num="0006"><img file="EP0640643B1_D0006.tif" /></chemistry> p¹ represents an integer of 100 to 400 and q¹ represents an integer of 1 to 300, to react with a terminal reactive poly(N-acylalkyleneimine) obtained by a ring-opening polymerization of a cyclic iminoether represented by the following formula (3): <chemistry id="chem0007" num="0007"><img file="EP0640643B1_D0007.tif" /></chemistry> wherein n represents a number of 2 or 3 and R¹ has the same meaning as above. The ring-opening polymerization of the cyclic iminoether (3) is carried out by the use of compounds having strong electrophilic reactivity, such as methyl, ethyl, 3-propenyl or benzyl esters of strong acids, for example, benzenesulfonic acid, p-toluenesulfonic acid, trifluoromethane sulfonic acid, trifluoroacetic acid, or sulfuric acid as an initiator. If 2-substituted-2-oxazoline is used for the cyclic iminoether (3), poly(N-acylethyleneimine) (compound of formula (1), in which n=2) is obtained. Alternatively, if 2-substituted-2-oxazine is used, poly(N-acylpropyleneimine) (compound of formula (1), in which n=3) is obtained. In order to link the above-mentioned poly(N-acylethyleneimine) chain to a silicone chain, a variety of reactions may be employed, which include an ester forming reaction based on the condensation between a carboxyl group and a hydroxyl group; an amide forming reaction based on the condensation of a carboxyl group and an amino group; a secondary, tertiary or quaternary ammonium forming reaction between a halogenized alkyl group and a primary, secondary or tertiary amino group; and a beta-hydroxylamine forming reaction utilizing an epoxy group and an amino group. Japanese Patent Application Laid-open (kokai) 2-276824, Japanese Patent Application Laid-open (kokai) 4-85334, Japanese Patent Application Laid-open (kokai) 4-85335, Japanese Patent Application Laid-open (kokai) 4-96933, for instance, describe a method in which a terminal reactive poly(N-acylalkyleneimine) obtained by a cationic ring-opening polymerization of a cyclic iminoether reacts with an organopolysiloxane represented by formula (2), i.e., a modified organopolysiloxane having side chains substituted by the aforementioned groups. This method is advisable in view of its simplicity and efficiency. </li><li>(B): Organopolysiloxanes in which at least one silicon atom in a side chain or at a terminal of an organopolysiloxane segment is bonded to the group represented by the following formula (4): <chemistry id="chem0008" num="0008"><img file="EP0640643B1_D0008.tif" /></chemistry> wherein m represents a number of 1 to 8. In these organopolysiloxanes (B), the number of the silicon atoms bonded to the group represented by formula (4) occupies 10 to 90%, preferably 40 to 80%, of the total number of the silicon atoms in the molecule. The weight-average molecular weight is from 50,000 to 300,000, and preferably from 100,000 to 200,000. If the weight-average molecular weight of the organopolysiloxanes (B) is less than 50,000, rupture or plastic deformation tend to occur before the extension ratio reaches 15%. On the other hand, if the weight-average molecular weight exceeds 300,000, production of organopolysiloxanes becomes difficult. If the number of the silicon atoms bonded to the group represented by formula (4) occupies less than 10%, sufficient cross-linking cannot occur, and therefore, the organopolysiloxanes (B) tend to rupture or deform before the extension ratio reaches 15%. On the other hand, if the number exceeds 90%, favorable sensation which is a characteristic feature of silicones is not obtained to any significant degree. In order to obtain organopolysiloxanes (B), a so-called hydrosilyl reaction may be used, in which an organohydrogenpolysiloxane represented by the formula (5) below is used as a precursor and is allowed to react with N-alkylenepyrrolidone. This hydrosilyl reaction is carried out in a solvent of a halogen series such as dichloromethane, chloroform, or 1,2-dichloroethane, or in an aliphatic ether such as tetrahydrofuran, diisopropylether or dibutylether at a temperature between room temperature and 100°C using a transition metal complex such as platinum chloride as a catalyst. <chemistry id="chem0009" num="0009"><img file="EP0640643B1_D0009.tif" /></chemistry> wherein p² represents an integer of 30 to 3,000, q² represents an integer of 60 to 1,500, and R², R³, R⁴ and m have the same meaning as defined above. Japanese Patent Application Laid-open (kokai) 5-32784 discloses compounds which are analogous to the above-described organopolysiloxanes (B) as well as methods of preparing them. However, this publication is silent on the molecular weight of the disclosed organopolysiloxane compounds. Moreover, the elastomeric property in which rupture or deformation are not caused until the extension ratio reaches 15% is not disclosed at all. Furthermore, examples of this publication only contain such compounds which rupture or deform before the extension ratio reaches 15% are illustrated. </li><li>(C): Organopolysiloxanes in which at least one silicon atom in a side chain or at a terminal of an organopolysiloxane segment is bonded to a saccharide residue. In these organopolysiloxanes (C), examples of the saccharide residue include a sugar lactone amidealkyl group (a group composed of a sugar lactone compound and an aminoalkyl group bonded thereto by an amide bond). The organopolysiloxanes (C) preferably have 40 to 97% by weight, more preferably 50 to 85% by weight, of silicone chains. The weight-average molecular weight of the organopolysiloxanes (C) ranges from 50,000 to 500,000, and preferably from 100,000 to 300,000. If the proportion of the silicone chains is less than 40% by weight, rupture or plastic deformation tend to occur before the extension ratio reaches 15%, and thus rubber-elasticity is not obtained to any significant degree. On the other hand, if the proportion exceeds 97% by weight, cross-linking is insufficient, thereby resulting in a paste like material. The rubber-elasticity also is not obtained in this case. If the weight-average molecular weight of the organopolysiloxanes (C) is less than 50,000, rupture or plastic deformation tend to occur before the extension ratio reaches 15%, and if it exceeds 500,000, production of organopolysiloxanes becomes difficult. In order to obtain the organopolysiloxanes (C), an organopolysiloxane having at least one aminoalkyl group is allowed to react with a sugar lactone compound (a compound which is obtained by subjecting aldonic acid or uronic acid to an intramolecular cyclodehydration) to generate amide bonds. The aminoalkyl groups are those having 1 to 20, more preferably 1 to 8, carbon atoms. Examples of the lactone compounds which are obtained from the intramolecular cyclodehydration of aldonic acid or uronic acid include lactones of aldonic acid derived from a reducing monosaccharide such as D-glucose, D-galactose D-allose, D-aldose, D-mannose, D-gulose, D-idose, and D-talose; lactones of aldonic acid derived from a reducing disaccharide such as maltose, cellobiose, lactose, xylobiose, isomaltose, nigerose, and kojibiose; lactones of aldonic acid derived from a reducing trisaccharide such as maltotriose, banose, panose, and isomaltotriose; lactones of aldonic acid derived from a reducing oligosaccharide containing more than four simple sugars; and lactones of an uronic acid such as D-glucuronic acid, L-iduronic acid and mannuronic aid. These are used singly or in combination. The reaction between an organopolysiloxane precursor having an aminoalkyl group and a sugar lactone is carried out using, preferably, 1.0 to 1.3 mol fold of a sugar lactone based on the amino group of an organopolysiloxane precursor. The precursor and the sugar lactone are mixed in a solvent, and then stirred for 3 to 20 hours while refluxing with heat at the solution concentration of 5 to 30% by weight. Suitable solvents in this step are lower alcohols such as methanol, ethanol, 1-propanol and 2-propanol. </li><li>(D): Organopolysiloxanes in which at least one silicon atom in a side chain or at a terminal of an organopolysiloxane segment is bonded, through an alkylene group containing a hetero atom, to a poly(N-propylene carbobetaine) segment containing a recurring unit represented by the following formula (7): <chemistry id="chem0010" num="0010"><img file="EP0640643B1_D0010.tif" /></chemistry> wherein R⁶ represents hydrogen, C1-C22 alkyl, cycloalkyl, aralkyl, aryl or alkoxycarbonylalkyl, and r represents a number from 1 to 5.</li></ul>

0034These organopolysiloxanes (D) preferably have a ratio by weight of the organopolysiloxane segment and the poly(N-propylene carbobetaine) segment of from 98/2 to 40/60 (more preferably from 90/10 to 60/40), and a weight-average molecular weight of from 50,000 to 500,000 (preferably from 100,000 to 300,000). If the ratio by weight of the organopolysiloxane segment and the poly(N-propylene carbobetaine) segment exceeds 98/2 or below 40/60, or the weight-average molecular weight is less than 50,000, rupture or plastic deformation tend to occur before the extension ratio reaches 15%. On the other hand, if the weight-average molecular weight exceeds 500,000, production of organopolysiloxanes becomes difficult.

0035Examples of the alkylene group containing a hetero atom which intervenes in the linkage of an organopolysiloxane segment and a poly(N-propylene carbobetaine) segment include a C2-C20 alkylene group containing 1 to 3 nitrogen atoms, oxygen atoms, and/or sulfur atoms. More specifically, the compounds which are represented by the following formulae may be mentioned: <chemistry id="chem0011" num="0011"><img file="EP0640643B1_D0011.tif" /></chemistry> wherein X^- is a counter ion of a quaternary ammonium salt. Among the groups represented by R⁶, the cycloalkyl group has 3 to 6 carbon atoms, the aralkyl group includes phenylalkyl, naphthylalkyl; and the aryl group includes phenyl, naphthyl and alkyl-substituted phenyl.

0036The above-described organopolysiloxanes (D) are prepared as follows. First, an organopolysiloxane of formula (2) is allowed to react with terminal reactive poly(N-propyleneimine) obtained by a ring-opening polymerization of a cyclic amine represented by the following formula (8): <chemistry id="chem0012" num="0012"><img file="EP0640643B1_D0012.tif" /></chemistry> wherein R⁶ has the same meaning as described above, to prepare an organopolysiloxane to which poly(N-propylene imine) is bonded. Then, the obtained product is allowed to react with sodium chloroacetate, β-propiolactone, γ-butyrolactone, ε-caprolactone to obtain organopolysiloxanes (D) which contain a poly(N-propylene carbobetaine) segment.

0037Alternatively, the organopolysiloxanes (D) may be prepared by quaternarizing, by the use of a C1-C22 alkyl halide, cycloalkyl halide or an aryl halide, an organopolysiloxane to which a poly(N-propylene imine) segment is bonded, and subsequently bringing the alkoxycarbonylethyl or alkoxycarbonylmethyl group to a hydrolizing reaction under basic conditions.

0038The ring-opening polymerization of a cyclic amine is performed using, as a polymerization initiator, Lewis acid, protonic acid, or alkylating agents such as triethyloxonium tetrafluoroborate, benzyl chloride, benzyl bromide, benzyl iodide, methyl bromide, methyl iodide, ethyl bromide, ethyl iodide, dimethyl sulfate, diethyl sulfate, trifluoromethane sulfonic acid, methyl trifluoromethane sulfonate, ethyl trifluoromethane sulfonate, benzene sulfonic acid, methyl benzene sulfonate, ethyl benzene sulfonate, p-toluenesulfonic acid, methyl p-toluenesulfonate, and ethyl p-toluenesulfonate.

0039If N-substituted azetidine is used as a cyclic amine, poly(N-substituted propylene carbobetaine) is obtained.

0040Examples of a solvent which may be used in the ring-opening polymerization of a cyclic amine or in the manufacture of the copolymers of the present invention include acetic esters such as ethyl acetate and propyl acetate; ethers such as diethylether, diisopropylether, dioxane and tetrahydrofuran; ketones such as acetone and methylethyl ketone; halogen solvents such as chloroform and methylene chloride; nitrile solvents such as acetonitrile and benzonitrile; and non-protonic polar solvents such as N,N-dimethylformamide, N,N-dimethylacetamide and dimethylsulfoxide.

0041The poly(N-propylene imine) chain is linked to a silicone chain in a similar manner that the above-mentioned poly(N-acylalkylene imine) chain is linked to a silicone chain.

0042In order to set hair fibers using the organopolysiloxane according to the present invention, a composition containing the organopolysiloxane is first applied to the hair fibers and then the solvent present in the composition is removed. It is preferred that the organopolysiloxane be incorporated in the composition in a proportion of 0.05 to 20% by weight, more preferably 0.1 to 10% by weight, of the composition.

0043The composition may further contain optional ingredients including solvents such as water and ethanol, and a variety of ingredients which are ordinarily incorporated in hair setting compositions such as surfactants, oils, polyols, medicinal ingredients, preservatives, perfumes, according to the purpose, use, intended form of the composition. Examples of the surfactants include linear or branched alkylbenzenesulfonates, ethylene oxide and/or propylene oxide-added alkyl- or alkenyl- ether sulfates, olefinsulfonates, alkanesulfonates, saturated or unsaturated fatty acid salts, ethylene oxide and/or propylene oxide-added alkyl- or alkenyl- ether carboxylates, esters of alpha-sulfofatty acid salts, amino acid-type surfactants, phosphate-type surfactants, sulfosuccinic acid-type surfactants, sulfonic acid-type amphoteric surfactants, betaine-type amphoteric surfactants, alkylene amine oxides, cationic surfactants such as linear and/or branched alkyl- or alkenyl- quaternary ammonium salts, polyoxyalkylene alkyl- or alkenyl- ethers, polyoxyalkylene alkylphenylethers, addition products of higher fatty acid alkanolamides or alkylene oxides, esters of polyols and fatty acids, esters of sorbitol and fatty acids, esters of sucrose and fatty acids, and esters of higher alcohols and saccharides. The amount of surfactants to be incorporated into the composition is preferably from 0 to 10% by weight, and particularly preferably from 0 to 5% by weight.

0044Examples of the oils include higher fatty acids such as stearic acid, higher alcohols such as cetanol, cholesterol, Vaseline, cholesteryl isostearate, solid fats such as sphingolipids, squalene, jojoba oil, other liquid fats of silicone derivatives. Examples of the polyols include glycerol, 1,3-butylene glycol, propylene glycol, dipropylene glycol, polyethylene glycol, polyglycerol, sorbitol. Examples of the solvents other than water and ethanol include benzyl alcohol, 2-benzyloxyethanol, N-alkylpyrrolidone, diethylene glycol monoethylether. Other ingredients include pearl-hue imparting agents, perfumes, colorants, UV absorbers, antioxidants, bacteriostats such as triclosan and triclocarban, antiinflammatory agents such as potassium glycyrrhizate and tocopherol acetate, antidandruff agents such as zinc pyrithione and Octopirox, preservatives such as methylparaben and butylparaben, and pH modifiers such as lactic acid and citric acid. These optional ingredients may be arbitrarily incorporated into the compositions as long as the effects of the invention are not impeded.

0045In order to obtain more enhanced effects, i.e., strong setting power which effectively retains the hair style made by blow setting or combing even under highly humid conditions, and soft and smooth touch without inviting rough or sticky hair, it is preferred that dimethylpolysiloxane having a polymerization degree of not less than 5,000, preferably not less than 10,000, especially preferably not less than 15,000 be incorporated into the compositions.

0046The compositions can be processed into a variety of forms including sprays, mists, lotions, tonics, blows, creams, post-foaming gels, according to conventional methods. When the compositions are prepared into aerosols, injection gases including volatile hydrocarbons such as butane, isobutane, pentane and isopentane; hydrocarbon halides such as dichlorofluoromethane and dichlorotetrafluoroethane; dimethylether; carbon dioxide; nitrogen; and air can be incorporated therein.

0047When a film-forming polymer is incorporated into the compositions, set retention power is even further enhanced, and excellent smooth touch to the hair is obtained.

0048Examples of the film-forming polymer include the following (1) to (8) compounds. <ul id="ul0002" list-style="none" compact="compact"><li>(1) Polymers of a polyvinylpyrrolidone series: <ul id="ul0003" list-style="none" compact="compact"><li><u>Polyvinylpyrrolidone</u>: Luviskol K12, K30 (by BASF), PVP K15, K30 (by GAF) are commercially obtainable.</li><li><u>Polyvinylpyrrolidone/vinyl acetate copolymers</u>: Luviskol VA28, VA73 (by BASF), PVP/VA E-735, S-630 (by GAF) are commercially obtainable.</li><li><u>Polyvinylpyrrolidone/vinyl acetate/vinyl propyonate ternary copolymers</u>: Luviskol VAP343 (by BASF) are commercially obtainable.</li><li><u>Polyvinylpyrrolidone/alkylamino acrylate copolymers</u>: Luviflex (by BASF), Copolymer 845, 937 and 958 (by GAF) are commercially obtainable.</li><li><u>Polyvinylpyrrolidone/acrylate/(meth)acrylic acid copolymers</u>: Luviflex VBM35 (by BASF) are commercially obtainable.</li><li><u>Polyvinylpyrrolidone/alkylamino acrylate/vinyl caprolactam copolymers</u>: Copolymer VC-713 (by GAF) are commercially obtainable.</li></ul></li><li>(2) Polymers of an acidic vinyl ether series: <ul id="ul0004" list-style="none" compact="compact"><li><u>Methylvinyl ether/maleic anhydride alkyl half ester copolymers</u>: Gantrez ES-225, ES-425, SP-215 (by GAF) are commercially obtainable.</li></ul></li><li>(3) Polymers of an acidic polyvinyl acetate series: <ul id="ul0005" list-style="none" compact="compact"><li><u>Vinyl acetate/crotonic acid copolymers</u>: Resin 28-1310 (by National Starch), Luviset CA66 (by BASF) are commercially obtainable.</li><li><u>Vinyl acetate/crotonic acid/vinyl neodecanoate copolymers</u>: Resin 28-2930 (by National Starch) are commercially obtainable.</li><li><u>Vinyl acetate/crotonic acid/vinyl propionate copolymers</u>: Luviset CAP (by BASF) are commercially obtainable.</li></ul></li><li>(4) Polymers of an acidic acrylic series: <ul id="ul0006" list-style="none" compact="compact"><li><u>(Meth)acrylic acid/(meth)acrylic ester copolymers</u>: Plascize L53P (by Goo Chemical), Diahold (by Mitsubishi Petrochemical) are commercially obtainable.</li><li><u>Acrylic acid/acrylic acid alkyl ester/alkyl acrylamide copolymers</u>: Ultrahold 8 (by BASF), Amphomer V-42 (by National Starch) are commercially obtainable.</li></ul></li><li>(5) Polymers of an amphoteric acrylic series: <ul id="ul0007" list-style="none" compact="compact"><li><u>(Meth)acrylethyl betaine/(meth)acrylic acid alkyl ester copolymers</u>: Polymers of this type include copolymer of N-methacryloyloxyethyl-N,N-dimethylammonium -α-N-methylcarboxybetaine and alkyl (meth)acrylate, and commercial products include Yukaformer M-75, SM (by Mitsubishi Petrochemical).</li><li><u>Acrylic acid alkyl ester/butylaminoethyl methacrylate/octylamide acrylate copolymers</u>: Polymers of this type include octylacrylamide/acrylate/butylaminoethyl methacrylate polymers, and commercial products include Unformer 28-4910 (by National Starch).</li></ul></li><li>(6) Polymers of a basic acrylic series: <ul id="ul0008" list-style="none" compact="compact"><li><u>Acrylamide/acryl ester quaternary system copolymers</u>: Polymers described in Japanese Patent Application Laid-open (kokai) 2-180911 are mentioned.</li></ul></li><li>(7) Cellulose derivatives: <ul id="ul0009" list-style="none" compact="compact"><li><u>Cationic cellulose derivatives</u>: Celquat H-100, L-200 (by National Starch) are commercially obtainable.</li></ul></li><li>(8) Chitin/chitosan derivatives: <ul id="ul0010" list-style="none" compact="compact"><li><u>Hydroxypropyl chitosan</u>: Chitofilmer (by Ichimaru-Pharcos) are commercially obtainable.</li><li><u>Carboxymethyl chitin, carboxymethyl chitosan, salts of chitosan and a monovalent acid such as pyrrolidone carboxylic acid, lactic acid, and glycolic acid, or of</u><u>chitosan and a divalent acid such as adipic acid and succinic acid</u>: Chitomer PC (pyrrolidone carboxylic acid salt), Chitomer L (lactic acid salt), both by Union Carbide are commercially obtainable.</li></ul></li></ul>

0049Among the above-described film-forming polymers, (math)acrylic polymers, amphoteric acrylic polymers, poryvinylpyrrolidone polymers, polymers having a sugar skeleton and salts of chitosan are especially preferred.

0050The amount of these film-forming polymers to be incorporated into the afore-mentioned compositions is preferably from 0.05 to 20%, and particularly preferably from 0.1 to 10% by weight.

0051The above-described compositions are applied to the hair in various manners according to the forms of the compositions. Generally, spraying, applications by hands and combinations of the them are employed. The removal of solvents is preferably performed by natural drying or drying with heat. When the hair fibers are set to have a desired shape, shape is preferably given after application and before drying. Generally, the hair is set by the use of a hair brush or curlers.

EXAMPLES

0052The present invention will further be described by way of examples, which should not be construed as limiting the invention thereto.

0053In the following examples, the %content of a silicone segment was obtained by quantitatively determining Si atoms by plasma emission analysis. The weight-average molecular weight in the examples is that of polystyrene equivalent calculated based on the results of gel permeation liquid chromatography using chloroform as a developer.

Synthesis Example 1:

Organopolysiloxane A-1:

0054Diethyl sulfate (21.4 g; 0.139 mol) and 2-ethyl-2-oxazoline (331 g; 3.33 mol) were dissolved in dehydrated ethyl acetate (700 g). The solution was refluxed with heat for 5 hours in the atmosphere of nitrogen to synthesize a terminal reactive poly(N-propionylethyleneimine). To this, side-chain primary aminopropyl-modified polydimethylsiloxane (molecular weight: 110,000, amine equivalent: 4840) (560 g; amino group equivalent = 0.116 mol) in ethyl acetate (50% solution) was added at a time and refluxed with heat over 10 hours. The reaction mixture was condensed under reduced pressure. An N-propionylethyleneimine-dimethylsiloxane copolymer was obtained as a pale yellow rubber-like solid (885 g; yield = 97%). The weight-average molecular weight was 109,000. When a neutralization titration was performed using HCl in methanol, no residual amino groups were found.

Comparative Synthesis Example 1:

Organopolysiloxane a:

0055Diethyl sulfate (21.4 g; 0.139 mol) and 2-ethyl-2-oxazoline (331 g; 3.33 mol) were dissolved in dehydrated ethyl acetate (700 g). The solution was refluxed with heat for 5 hours in the atmosphere of nitrogen to synthesize a terminal reactive poly(N-propionylethyleneimine). To this, side-chain primary aminopropyl-modified polydimethylsiloxane (molecular weight: 24,000, amine equivalent: 4810) (560 g; amino group equivalent = 0.116 mol) in ethyl acetate (50% solution) was added at a time and refluxed with heat over 10 hours. The reaction mixture was condensed under reduced pressure. A N-propionylethyleneimine-dimethylsiloxane copolymer was obtained as a pale yellow rubber-like solid (867 g; yield = 95%). The weight-average molecular weight was 25,800. When a neutralization titration was performed using HCl in methanol, no residual amino groups were found.

Synthesis Example 2:

Organopolysiloxane A-2:

0056Diethyl sulfate (30.6 g; 0.199 mol) and 2-ethyl-2-oxazoline (945 g; 9.53 mol) were dissolved in dehydrated ethyl acetate (1,950 g). The solution was refluxed with heat for 8 hours in an atmosphere of nitrogen to synthesize a terminal reactive poly(N-propionylethyleneimine). To this, a side-chain primary aminopropyl-modified polydimethylsiloxane (molecular weight: 110,000, amine equivalent: 4840) (800 g; amino group equivalent = 0.165 mol) in ethyl acetate (50% solution) was added at a time and refluxed with heat over 12 hours. The reaction mixture was condensed under reduced pressure. A N-propionylethyleneimine-dimethylsiloxane copolymer was obtained as a pale yellow rubber-like solid (1,720g; yield = 97%). The weight-average molecular weight was 122,000. When a neutralization titration was performed using HCl in methanol, no residual amino groups were found.

Synthesis Example 3:

Organopolysiloxane A-3:

0057Diethyl sulfate (3.56 g; 0.0230 mol) and 2-ethyl-2-oxazoline (27.5 g; 0.277 mol) were dissolved in dehydrated ethyl acetate (60 g). The solution was refluxed with heat for 4 hours in an atmosphere of nitrogen to synthesize a terminal reactive poly(N-propionylethyleneimine). To this, side-chain primary aminopropyl-modified polydimethylsiloxane (molecular weight: 110,000, amine equivalent: 20800) (400 g; amino group equivalent = 0.0192 mol) in ethyl acetate (50% solution) was added at a time and refluxed with heat over 8 hours. The reaction mixture was condensed under reduced pressure. A N-propionylethyleneimine-dimethylsiloxane copolymer was obtained as a pale yellow rubber-like solid (428 g; yield = 99%). The weight-average molecular weight was 115,000. When a neutralization titration was performed using HCl in methanol, no residual amino groups were found.

Synthesis Example 4:

Organopolysiloxane B-1:

00582.0 g of a 5% isopropylalcohol solution of chloroplatinic acid was added to methylhydrogen polysiloxane (500 g; 2.91 mol as SiH; weight-average MW = 100,000; SiH equivalent = 172), and stirred in the atmosphere of nitrogen. N-(3-propenyl)pyrrolidone (382 g; 3.06 mol) was added dropwise to the mixture obtained at such a speed that the temperature of the reaction system did not exceed 60°C. After completion of the addition, the temperature of the system was maintained at 65°C, and the mixture was stirred for further 3 hours. Thereafter, the temperature was returned to room temperature. To this, ethanol (3530 g) was added to make a uniform solution. Activated carbon powder (10 g) was added to the uniform solution, and the solution was stirred for 30 minutes at room temperature. Subsequently, the activated carbon was removed by filtration. The solution so obtained was concentrated under reduced pressure. Ethanol and unreacted N-(3-propenyl)pyrrolidone were distilled off. Methylpolysiloxane (847 g; yield = 98%) having an alkylpyrrolidone group as a side chain was obtained as a colorless transparent rubber-like solid. The weight-average molecular weight was 155,000. In the FT-IR spectrum, absorption of Si-H stretching vibration (2125 cm^-1) was not observed.

Comparative Synthesis Example 2:

Organopolysiloxane b:

00592.0 g of a 5% isopropylalcohol solution of chloroplatinic acid was added to methylhydrogen polysiloxane (500 g; 2.97 mol as SiH; weight-average MW = 4,300; SiH equivalent = 168), and stirred in an atmosphere of nitrogen. N-(3-propenyl)pyrrolidone (390 g; 3.12 mol) was added dropwise to the obtained mixture at such a speed that the temperature of the reaction system did not exceed 60°C. After completion of the addition, the temperature of the system was maintained at 65°C, and the mixture was stirred for further 3 hours. Thereafter, the temperature was returned to room temperature. To this, ethanol (3600 g) was added to make a uniform solution. Activated carbon powder (10 g) was added to the uniform solution, and the solution was stirred for 30 minutes at room temperature. Subsequently, the activated carbon was removed by filtration. The solution so obtained was concentrated under reduced pressure. Ethanol and unreacted N-(3-propenyl)pyrrolidone were distilled off. Methylpolysiloxane (819 g; yield = 94%) having an alkylpyrrolidone group as a side chain was obtained as a colorless transparent rubber-like solid. The weight-average molecular weight was 7,100. In the FT-IR spectrum, absorption of Si-H stretching vibration (2125 cm^-1) was not observed.

Synthesis Example 5:

Organopolysiloxane A-4:

0060Diethyl sulfate (3.75 g; 0.0244 mol) and 2-ethyl-2-oxazoline (58.6 g; 0.591 mol) were dissolved in dehydrated ethyl acetate (125 g). The solution was refluxed with heat for 5 hours in an atmosphere of nitrogen to synthesize a terminal reactive poly(N-propionylethyleneimine). To this, a side-chain primary aminopropyl-modified polydimethylsiloxane (molecular weight: 110,000, amine equivalent: 9840) (200 g; amino group equivalent = 0.0203 mol) in ethyl acetate (50% solution) was added at a time and refluxed with heat over 8 hours. The reaction mixture was condensed under reduced pressure. A N-propionylethyleneimine-dimethylsiloxane copolymer was obtained as a pale yellow rubber-like solid (257 g; yield = 98%). The %content of silicone segments was 76%, and the weight-average molecular weight was 118,000. When a neutralization titration was performed using HCl in methanol, no residual amino groups were found.

Synthesis Example 6:

Organopolysiloxane A-5:

0061Diethyl sulfate (29.7 g; 0.193 mol) and 2-ethyl-2-oxazoline (153 g; 1.54 mol) were dissolved in dehydrated ethyl acetate (370 g). The solution was refluxed with heat for 3 hours in the atmosphere of nitrogen to synthesize a terminal reactive poly(N-propionylethyleneimine). To this, side-chain primary aminopropyl-modified polydimethylsiloxane (molecular weight: 90,000, amine equivalent: 1870) (300 g; amino group equivalent = 0.160 mol) in ethyl acetate (50% solution) was added at a time and refluxed with heat over 12 hours. The reaction mixture was condensed under reduced pressure. A N-propionylethyleneimine-dimethylsiloxane copolymer was obtained as a pale yellow rubber-like solid (468 g; yield = 97%). The %content of silicone segments was 61%, and the weight-average molecular weight was 102,000. When a neutralization titration was performed using HCl in methanol, no residual amino groups were found.

Synthesis Example 7:

Organopolysiloxane A-6:

0062Diethyl sulfate (3.75 g; 0.0243 mol) and 2-ethyl-2-oxazoline (49.8 g; 0.585 mol) were dissolved in dehydrated ethyl acetate (107 g). The solution was refluxed with heat for 5 hours in an atmosphere of nitrogen to synthesize a terminal reactive poly(N-acetylethyleneimine). To this, a side-chain primary aminopropyl-modified polydimethylsiloxane (molecular weight: 110,000, amine equivalent: 9840) (400 g; amino group equivalent = 0.0407 mol) in ethyl acetate (50% solution) was added at a time and refluxed with heat over 13 hours. The reaction mixture was condensed under reduced pressure. A N-acetylethyleneimine-dimethylsiloxane copolymer was obtained as a pale yellow rubber-like solid (444 g; yield = 98%). The %content of silicone segments was 88%, and the weight-average molecular weight was 137,000. When a neutralization titration was performed using HCl in methanol, no residual amino groups were found.

Synthesis Example 8:

Organopolysiloxane C-1:

0063Gamma-aminopropyl-modified dimethylpolysiloxane (200 g; 0.493 mol as converted to amino groups) which has an amine equivalent of 406 and a weight-average molecular weight of 36,000, maltobionolactone (201 g; 0.591 mol) and ethanol (800 g) were mixed. The mixture was refluxed with heat for 9 hours under vigorous agitation in an atmosphere of nitrogen. The resultant solution was vigorously agitated at room temperature, to which hexane (1000 g) was added. The sedimented pellet was removed by filtration, and the filtrate was condensed under reduced pressure. Dimethylpolysiloxane containing a saccharide residue was obtained as a colorless transparent elastic solid (342 g; yield = 93%). When a neutralization titration was performed using HCl in methanol, no residual amino groups were found. The %content of silicone segments was 54%.

Synthesis Example 9:

Organopolysiloxane C-2:

0064Gamma-aminopropyl-modified dimethylpolysiloxane (200 g; 0.201 mol as converted to amino groups) which has an amine equivalent of 996 and a weight-average molecular weight of 108,000, delta-glucolactone (39.3 g; 0.221 mol) and methanol (200 g) were mixed. The mixture was refluxed with heat for 8 hours under vigorous agitation in an atmosphere of nitrogen. The resultant solution was diluted in three fold with methanol, and was added to water (10 l) dropwise under vigorous agitation. Subsequently, agitation was stopped, and a pellet was collected by filtration. It was washed with water and then dried under reduced pressure. As a result, dimethylpolysiloxane containing saccharide residues was obtained as a colorless transparent elastic solid (204 g; yield = 86%). When a neutralization titration was performed using HCl in methanol, no residual amino groups were found. The %content of silicone segments was 86%.

Synthesis Example 10:

Organopolysiloxane C-3:

0065Gamma-aminopropyl-modified dimethylpolysiloxane (200 g; 0.0201 mol as converted to amino groups) which has an amine equivalent of 9,940 and a weight-average molecular weight of 128,000, maltobionolactone (8.22 g; 0.0241 mol) and ethanol (300 g) were mixed. The mixture was refluxed with heat for 9 hours under vigorous agitation in an atmosphere of nitrogen. The resultant solution was diluted in 2.5 fold with ethanol, and was added to water (10 l) dropwise under vigorous agitation. Subsequently, agitation was stopped, and pellet was collected by filtration. It was washed with water and then dried under reduced pressure. As a result, a dimethylpolysiloxane containing saccharide residues was obtained as a colorless transparent elastic solid (206 g; yield = 92%). When a neutralization titration was performed using HCl in methanol, no residual amino groups were found. The %content of silicone segments was 97%.

Comparative Synthesis Example 3:

0066Organopolysiloxane c containing a saccharide residue was prepared by the following method.

0067A mixture of 50 g (0.0694 mol by a primary amino group conversion) of 6-amino-4-azahexyl-modified dimethylpolysiloxane (product of Shin'estu Kagaku Kogyo, KF393) having an amine equivalent of 360 and a weight-average molecular weight of 3,800, 13 g of glucono-delta-lactone and 200 ml of methanol was refluxed for 6 hours. Methanol was distilled off under reduced pressure. The residue was dissolved in water. An aqueous solution of the reaction mixture was placed in a transparent cellophane tube, and dialyzed to remove gluconic acid originated from unreacted glucono-delta-lactone. The resultant material was freeze-dried, to obtain 60 g of 6-gluconamide-4-azahexyl-modified organopolysiloxane c as a white solid (yield: 95%). When a neutralization titration was performed using HCl in methanol, no residual amino groups were found. The %content of silicone segments was 70%.

Synthesis Example 11:

Organopolysiloxane D-1:

0068Diethyl sulfate (30.6 g; 0.198 mol) and 1-(2-carboethoxyethyl)azetidine (1498.2 g; 9.53 mol) were dissolved in dehydrated ethyl acetate (3058 g), and refluxed with heat for 15 hours in an atmosphere of nitrogen to synthesize a terminal reactive poly(N-propylene imine). To this, a side-chain primary aminopropyl-modified polydimethylsiloxane (molecular weight: 110,000, amine equivalent: 4840) (800 g; amino group equivalent = 0.165 mol) in ethyl acetate (50% solution) was added at a time and refluxed with heat over 12 hours. The reaction mixture was condensed under reduced pressure. A N-propyleneimine-dimethylsiloxane copolymer was obtained as a pale yellow solid (2212 g; yield = 95%). The resultant reaction product was dispersed in methanol (5000 g), to which sodium chloroacetate (1665.6 g; 14.3 mol) was added. The mixture was allowed to react for 24 hours while refluxing with heat. The reaction solution was cooled to room temperature, and sodium chloride was filtered off. The obtained solution was condensed under reduced pressure to obtain an N-propylene carbobetaine-dimethylsiloxane copolymer as a pale yellow solid.

Synthesis Example 12:

Organopolysiloxane D-2:

0069Diethyl sulfate (3.56 g; 0.023 mol) and 1-(2-carboethoxyethyl)azetidine (43.5 g; 0.277 mol) were dissolved in dehydrated ethyl acetate (94.2 g), and refluxed with heat for 6 hours in an atmosphere of nitrogen to synthesize a terminal reactive poly(N-propylene imine). To this, a side-chain primary aminopropyl-modified polydimethylsiloxane (molecular weight: 110,000, amine equivalent: 20800) (400 g; amino group equivalent = 0.0192 mol) in ethyl acetate (50% solution) was added at a time and refluxed with heat over 12 hours. The reaction mixture was condensed under reduced pressure. A N-propyleneimine-dimethylsiloxane copolymer was obtained as a pale yellow solid (425 g; yield = 95%). The resultant reaction product was dispersed in methanol (1000 g), to which sodium chloroacetate (46.6 g; 0.4 mol) was added. The mixture was allowed to react for 24 hours while refluxing with heat. The reaction solution was cooled to room temperature, and sodium chloride was filtered off. The obtained solution was condensed under reduced pressure to obtain an N-propylene carbobetaine-dimethylsiloxane copolymer as a pale yellow solid.

Synthesis Example 13:

Organopolysiloxane D-3:

0070Diethyl sulfate (30.6 g; 0.198 mol) and 1-(2-carboethoxyethyl)azetidine (1498.2 g; 9.53 mol) were dissolved in dehydrated ethyl acetate (3058 g), and refluxed with heat for 15 hours in an atmosphere of nitrogen to synthesize a terminal reactive poly(N-propylene imine). To this, a side-chain primary aminopropyl-modified polydimethylsiloxane (molecular weight: 110,000, amine equivalent: 4840) (800 g; amino group equivalent = 0.165 mol) in ethyl acetate (50% solution) was added at a time and refluxed with heat over 12 hours. The reaction mixture was condensed under reduced pressure. A N-propyleneimine-dimethylsiloxane copolymer was obtained as a pale yellow solid (2212 g; yield = 95%). The resultant reaction product was dispersed in diethylether (5000 g), to which β-propiolactone (824 g; 11.4 mol) was added at room temperature. The mixture was allowed to react for a day and night at room temperature. The obtained mixture was condensed under reduced pressure to obtain an N-propylene carbobetaine-dimethylsiloxane copolymer as a pale yellow solid.

Synthesis Example 14:

Organopolysiloxane D-4:

0071Diethyl sulfate (3.56 g; 0.023 mol) and 1-(2-carboethoxyethyl)azetidine (43.5 g; 0.277 mol) were dissolved in dehydrated ethyl acetate (94.2 g), and refluxed with heat for 6 hours in an atmosphere of nitrogen to synthesize a terminal reactive poly(N-propylene imine). To this, a side-chain primary aminopropyl-modified polydimethylsiloxane (molecular weight: 110,000, amine equivalent: 20800) (400 g; amino group equivalent = 0.0192 mol) in ethyl acetate (50% solution) was added at a time and refluxed with heat over 12 hours. The reaction mixture was condensed under reduced pressure. A N-propyleneimine-dimethylsiloxane copolymer was obtained as a pale yellow solid (425 g; yield = 95%). The resultant reaction mixture was dissolved in diethylether (1000 g), to which β-propiolactone (23.95 g; 0.332 mol) was added at room temperature. The mixture was allowed to react for a day and night at room temperature. The obtained mixture was condensed under reduced pressure to obtain an N-propylene carbobetaine-dimethylsiloxane copolymer as a pale yellow solid.

Synthesis Example 15:

Organopolysiloxane D-5:

0072Triethyloxonium tetrafluoroborate (37.6 g; 0.198 mol) and 1-(2-carboethoxyethyl)azetidine (1498.2 g; 9.53 mol) were dissolved in dehydrated tetrahydrofuran (3058 g), and refluxed with heat for 15 hours in an atmosphere of nitrogen to synthesize a terminal reactive poly(N-propylene imine). To this, a side-chain primary aminopropyl-modified polydimethylsiloxane (molecular weight: 110,000, amine equivalent: 4840) (800 g; amino group equivalent = 0.165 mol) in tetrahydrofuran (50% solution) was added at a time and refluxed with heat over 12 hours. The reaction mixture was condensed under reduced pressure. A N-propyleneimine-dimethylsiloxane copolymer was obtained as a pale yellow solid (2212 g; yield = 95%). The obtained reaction mixture was dissolved in diethylether (5000 g), to which γ-butyrolactone (981.4 g; 11.4 mol) was added at room temperature. The mixture was allowed to react for a day and night at room temperature. The obtained solution was condensed under reduced pressure to obtain an N-propylene carbobetaine-dimethylsiloxane copolymer as a pale yellow solid.

Synthesis Example 16:

Organopolysiloxane D-6:

0073Trifluoromethanesulfonic acid (3.45 g; 0.023 mol) and 1-(2-carboethoxyethyl)azetidine (43.5 g; 0.277 mol) were dissolved in dehydrated diisopropyl ether (94.2 g), and refluxed with heat for 6 hours in an atmosphere of nitrogen to synthesize a terminal reactive poly(N-propylene imine). To this, a side-chain primary aminopropyl-modified polydimethylsiloxane (molecular weight: 110,000, amine equivalent: 20800) (400 g; amino group equivalent = 0.0192 mol) in diisopropyl ether (50% solution) was added at a time and refluxed with heat over 12 hours. The reaction mixture was condensed under reduced pressure. A N-propyleneimine-dimethylsiloxane copolymer was obtained as a pale yellow solid (425 g; yield = 95%). The resultant reaction mixture was dissolved in diethylether (1000 g), to which ε-caprolactone (37.9 g; 0.332 mol) was added at room temperature. The mixture was allowed to react for a day and night at room temperature. The obtained mixture was condensed under reduced pressure to obtain an N-propylene carbobetaine-dimethylsiloxane copolymer as a pale yellow solid.

Synthesis Example 17:

Organopolysiloxane D-7:

0074Diethyl sulfate (30.6 g; 0.198 mol) and 1-(2-carboethoxyethyl)azetidine (1498.2 g; 9.53 mol) were dissolved in dehydrated ethyl acetate (3058 g), and refluxed with heat for 15 hours in an atmosphere of nitrogen to synthesize a terminal reactive poly(N-propylene imine). To this, a side-chain primary aminopropyl-modified polydimethylsiloxane (molecular weight: 110,000, amine equivalent: 4840) (800 g; amino group equivalent = 0.165 mol) in ethyl acetate (50% solution) was added at a time and refluxed with heat over 12 hours. The reaction mixture was condensed under reduced pressure. A N-propyleneimine-dimethylsiloxane copolymer was obtained as a pale yellow solid (2212 g; yield = 95%). The resultant reaction mixture was dissolved in acetone (5000 g), to which ethyl bromide (1246.2 g; 11.44 mol) was added. The mixture was allowed to react for 24 hours while refluxing with heat. The reaction mixture was condensed under reduced pressure, and dispersed in methanol (5000 g). 2N potassium hydroxide in methanol (5000 g) was added thereto, and then heated at 80°C for 6 hours. The obtained solution was condensed under reduced pressure, dissolved in chloroform, washed with water, and condensed under reduced pressure again to obtain an N-propylene carbobetaine-dimethylsiloxane copolymer as a pale yellow solid.

Synthesis Example 18:

Organopolysiloxane D-8:

0075Diethyl sulfate (3.56 g; 0.023 mol) and 1-(2-carboethoxyethyl)azetidine (43.5 g; 0.277 mol) were dissolved in dehydrated ethyl acetate (94.2 g), and refluxed with heat for 6 hours in an atmosphere of nitrogen to synthesize a terminal reactive poly(N-propylene imine). To this, a side-chain primary aminopropyl-modified polydimethylsiloxane (molecular weight: 110,000, amine equivalent: 20800) (400 g; amino group equivalent = 0.0192 mol) in ethyl acetate (50% solution) was added at a time and refluxed with heat over 12 hours. The reaction mixture was condensed under reduced pressure. A N-propyleneimine-dimethylsiloxane copolymer was obtained as a pale yellow solid (425 g; yield = 95%). The resultant reaction product was dissolved in acetone (1000 g), to which ethyl bromide (25.2 g; 0.231 mol) was added. The mixture was allowed to react for 24 hours while refluxing with heat. The reaction mixture was condensed under reduced pressure, and dispersed in methanol (1000 g). 2N potassium hydroxide in methanol (150 g) was added thereto, and then heated at 80°C for 6 hours. The obtained solution was condensed under reduced pressure, dissolved in chloroform, washed with water, and condensed under reduced pressure again to obtain an N-propylene carbobetaine-dimethylsiloxane copolymer as a pale yellow solid.

Synthesis Example 19:

Organopolysiloxane D-9:

0076Diethyl sulfate (30.6 g; 0.198 mol) and 1-(2-carboethoxyethyl)azetidine (1498.2 g; 9.53 mol) were dissolved in dehydrated ethyl acetate (3058 g), and refluxed with heat for 15 hours in an atmosphere of nitrogen to synthesize a terminal reactive poly(N-propylene imine). To this, a side-chain primary aminopropyl-modified polydimethylsiloxane (molecular weight: 110,000, amine equivalent: 4840) (800 g; amino group equivalent = 0.165 mol) in ethyl acetate (50% solution) was added at a time and refluxed with heat over 12 hours. The reaction mixture was condensed under reduced pressure. A N-propyleneimine-dimethylsiloxane copolymer was obtained as a pale yellow solid (2212 g; yield = 95%). The resultant reaction mixture was dissolved in acetone (5000 g), to which hexyl bromide (1888.5 g; 11.44 mol) was added. The mixture was allowed to react for 24 hours while refluxing with heat. The reaction mixture was condensed under reduced pressure, and dispersed in methanol (5000 g). 2N potassium hydroxide in methanol (5000 g) was added thereto, and then heated at 80°C for 6 hours. The obtained solution was condensed under reduced pressure, dissolved in chloroform, washed with water, and condensed under reduced pressure again to obtain an N-propylene carbobetaine-dimethylsiloxane copolymer as a pale yellow solid.

Synthesis Example 20:

Organopolysiloxane D-10:

0077Diethyl sulfate (3.56 g; 0.023 mol) and 1-(2-carboethoxyethyl)azetidine (43.5 g; 0.277 mol) were dissolved in dehydrated ethyl acetate (94.2 g), and refluxed with heat for 6 hours in an atmosphere of nitrogen to synthesize a terminal reactive poly(N-propylene imine). To this, a side-chain primary aminopropyl-modified polydimethylsiloxane (molecular weight: 110,000, amine equivalent: 20800) (400 g; amino group equivalent = 0.192 mol) in ethyl acetate (50% solution) was added at a time and refluxed with heat over 12 hours. The reaction mixture was condensed under reduced pressure. A N-propyleneimine-dimethylsiloxane copolymer was obtained as a pale yellow solid (425 g; yield = 95%). The resultant reaction mixture was dissolved in acetone (1000 g), to which hexyl bromide (38.1 g; 0.231 mol) was added. The mixture was allowed to react for 24 hours while refluxing with heat. The reaction mixture was condensed under reduced pressure, and dispersed in methanol (1000 g). 2N potassium hydroxide in methanol (150 g) was added thereto, and then heated at 80°C for 6 hours. The obtained solution was condensed under reduced pressure, dissolved in chloroform, washed with water, and condensed under reduced pressure again to obtain an N-propylene carbobetaine-dimethylsiloxane copolymer as a pale yellow solid.

Reference Example 1:

0078The organopolysiloxanes according to the present invention which were obtained in Synthesis Examples 1 to 20, low-molecular weight organopolysiloxanes obtained in Comparative Synthesis Examples 1 to 3, and the below-described commercially obtained set polymers d and e were evaluated in terms of the film-forming property in the method described below. The results follow the description of the method. <dl id="dl0001" compact="compact"><dt>d:</dt><dd>Yukaformer M-75 (by Mitsubishi Petrochemical)</dd><dt>e:</dt><dd>Gantrez ES 225 (by GAF)</dd></dl>

Evaluation Method

:

0079Each polymer was made into a 10% ethanol solution. Ethanol was spontaneously evaporated to form a film having a thickness of about 0.2 to 0.3 mm. A sample having a length of 20 mm and a width of 5 mm was cut out from this film. The sample was attached to a tension meter placed in a room of 65% relative humidity. The stress-strain curve was recorded, during which the sample was stretched by 3 mm at a cross head speed of 20 mm/min. Immediately thereafter, the cross head was returned to its original position at the same speed. After 10 minutes, the sample was stretched again, and the stress-strain curve was recorded.

Results

:

0080When the organopolysiloxanes according to present invention were stretched, the stress-strain curves of the first and the second times were identical. This means that no plastic deformation was caused by the first stretching. By contrast, when the commercially obtained set polymer d was stretched, it ruptured at the first stretching. In the cases of the organopolysiloxanes a nd c obtained in Comparative Synthesis Examples 1 and 3, respectively, and the commercially obtained set polymer e, the second stress-strain curve was not identical to the first curve, which indicates that plastic deformation was caused by the first stretching. When the films formed with the organopolysiloxanes according to the present invention were observed under transmission electron microscope (TEM), it was found that all of them were cross-linked and had a micro phase separation structure.

Reference Example 2:

0081The solubility of the organopolysiloxanes according to present invention obtained in Synthesis Examples 1 to 20 was determined in ethanol and in an aqueous 20% ethanol solution. In both cases, the compounds were either uniformly dissolved to form a transparent solution or uniformly dispersed to form a translucent dispersion at a concentration of 2 wt%. By contrast, room temperature-setting type Silicone Elastomer SH 9585 (by Shin'etsu Kagaku Kogyo) and Silicone Elastomer KE-10 (covalent bond cross-linking type) were neither dissolved nor dispersed at the same concentration.

Examples 1 to 6 and Comparative Examples 1 to 5:

0082The organopolysiloxanes according to the present invention which were obtained in Synthetic Examples 1 to 5, the organopolysiloxanes a - c obtained in Comparative Synthesis Examples 1 - 3, and the above-mentioned commercially obtained polymers d and e were used to prepare hair set mists formulated as shown in Table 1. Hair fibers were treated with the obtained mists, and were tested with regard to the evaluation items described below. The results are also shown in Table 1.

(a) Set retentivity:

0083A hair tress (18 cm, 1.5 g) was wet with water, and then towel-dried. Mist (2 g) was applied thereto and wound on a rod having a diameter of 2 cm, then spontaneously dried. After being dried, the curled hair was removed from the rod, and suspended in a highly humid chamber (20°C, 98%RH) for 30 minutes. The shape of the curl was observed. The set retentivity was determined based on the following:

Evaluation Standard

:

0084<dl id="dl0002" compact="compact"><dt>A:</dt><dd>Very much superior to untreated hair</dd><dt>B:</dt><dd>Superior to untreated hair</dd><dt>C:</dt><dd>Comparable to untreated hair</dd><dt>D:</dt><dd>Inferior to untreated hair</dd></dl>

(b) Sensory Evaluation:

0085A hair tress (18 cm, 10 g) was wet with water, and then towel-dried. Mist (2 g) was applied thereto and wound on a rod having a diameter of 2 cm, then spontaneously dried. Five expert panelists evaluated the touch to the hair.

Evaluation Standard

:

0086<dl id="dl0003" compact="compact"><dt>A:</dt><dd>Very much superior to untreated hair</dd><dt>B:</dt><dd>Superior to untreated hair</dd><dt>C:</dt><dd>Comparable to untreated hair</dd><dt>D:</dt><dd>Inferior to untreated hair</dd><dt>E:</dt><dd>Very much inferior to untreated hair</dd></dl>

(c) Elasticity of curls:

0087Curls were formed by a similar method described in (a) above. Five expert panelists evaluated the elasticity of curls.

Evaluation Standard

:

0088<dl id="dl0004" compact="compact"><dt>A:</dt><dd>More elastic than untreated hair</dd><dt>B:</dt><dd>Slightly more elastic than untreated hair</dd><dt>C:</dt><dd>Comparable to untreated hair</dd><dt>D:</dt><dd>Stiff and rough compared to untreated hair</dd></dl><tables id="tabl0001" num="0001"><img file="EP0640643B1_D0013.tif" /></tables>

0089As shown in Table 1, the products according to the present invention are all superior to the comparative products in terms of the set retentivity, touch to the hair and elasticity of curls. In addition, the products according to the present invention exhibited excellent removal-by-shampoo property. Although not shown in Table 1, the organopolysiloxanes according to the present invention obtained in Synthesis Examples 5 to 7, 9, 10 and 12 to 20 also exhibit excellent set retentivity, and touch to the hair, and the curls had elasticity.

Example 7:

0090Organopolysiloxanes according to the present invention and a film-forming polymer were used, and the mists shown in Table 2 were prepared.

0091The mists were applied to the hair, and were evaluated with regard to the set retentivity and smoothness of the hair by testing them as described below. Evaluation was made based on the following criteria. The results are also shown in Table 2.

(a) Set retentivity:

0092A hair tress (18 cm, 1.5 g) was wet with water, and then towel-dried. Mist (2 g) was applied thereto and wound on a rod having a diameter of 2 cm, then spontaneously dried. After being dried, the curled hair was removed from the rod, and suspended in a thermostat chamber (20°C, 98%RH) for 30 minutes. The shape of the curl was observed. The set retentivity was determined based on the following criteria:

Evaluation Standard

:

0093<dl id="dl0005" compact="compact"><dt>A:</dt><dd>Excellent</dd><dt>B:</dt><dd>Good</dd><dt>C:</dt><dd>Ordinary</dd><dt>D:</dt><dd>Slightly poor</dd><dt>E:</dt><dd>Poor</dd></dl>

(b) Smoothness:

0094A hair tress (18 cm, 10 g) was wet with water, and then towel-dried. Mist (0.2 g) was applied thereto and then spontaneously dried. Smoothness of the hair was evaluated based on the following criteria:

Evaluation Standard

:

0095<dl id="dl0006" compact="compact"><dt>A:</dt><dd>Excellent</dd><dt>B:</dt><dd>Good</dd><dt>C:</dt><dd>Ordinary</dd><dt>D:</dt><dd>Slightly poor</dd><dt>E:</dt><dd>Poor</dd></dl><tables id="tabl0002" num="0002"><img file="EP0640643B1_D0014.tif" /></tables>

0096As shown in Table 2, the products according to the present invention are all superior to the comparative products in terms of the set retentivity and smoothness of the hair. Although not shown in Table 2, the compositions containing the organopolysiloxanes obtained in Synthesis Examples 1 - 3, 5, 6, 11 and 13 - 20 and an amphoteric polymer also exhibit excellent set retentivity, and impart excellent smoothness to the hair after treatment.

0097The comparative products I, J and K, which contain an organopolysiloxane which does not meet the requirements of the present invention, have poor set retentivity, though they exhibit good performance with regard to the smoothness of the set hair.

Example 8:

0098A foam agent was prepared by blending the following components. <tables id="tabl0003" num="0003"><table frame="all"><tgroup cols="2" colsep="1" rowsep="0"><colspec colnum="1" colname="col1" colwidth="78.75mm" /><colspec colnum="2" colname="col2" colwidth="78.75mm" /><thead valign="top"><row rowsep="1"><entry namest="col1" nameend="col1" align="left">(Components)</entry><entry namest="col2" nameend="col2" align="center">(wt.%)</entry></row></thead><tbody valign="top"><row><entry namest="col1" nameend="col1" align="left">Organopolysiloxane A-1</entry><entry namest="col2" nameend="col2" align="right">3.0</entry></row><row><entry namest="col1" nameend="col1" align="left">Coconut oil fatty acid diethanolamide</entry><entry namest="col2" nameend="col2" align="right">0.5</entry></row><row><entry namest="col1" nameend="col1" align="left">Ethanol</entry><entry namest="col2" nameend="col2" align="right">20.0</entry></row><row><entry namest="col1" nameend="col1" align="left">Perfume</entry><entry namest="col2" nameend="col2" align="right">trace</entry></row><row><entry namest="col1" nameend="col1" align="left">Purified water</entry><entry namest="col2" nameend="col2" align="right">balance</entry></row><row rowsep="1"><entry namest="col1" nameend="col1" align="left">Liquefied petroleum gas</entry><entry namest="col2" nameend="col2" align="right">10.0</entry></row><row rowsep="1"><entry namest="col1" nameend="col1" align="left">Total</entry><entry namest="col2" nameend="col2" align="right">100.0</entry></row></tbody></tgroup></table></tables>

Example 9:

0099A foam agent was prepared by blending the following components. <tables id="tabl0004" num="0004"><table frame="all"><tgroup cols="2" colsep="1" rowsep="0"><colspec colnum="1" colname="col1" colwidth="78.75mm" /><colspec colnum="2" colname="col2" colwidth="78.75mm" /><thead valign="top"><row rowsep="1"><entry namest="col1" nameend="col1" align="left">(Components)</entry><entry namest="col2" nameend="col2" align="center">(wt.%)</entry></row></thead><tbody valign="top"><row><entry namest="col1" nameend="col1" align="left">Organopolysiloxane A-3</entry><entry namest="col2" nameend="col2" align="right">1.0</entry></row><row><entry namest="col1" nameend="col1" align="left">Commercially available setting polymer (GANTREZ ES 225, product of GAF)</entry><entry namest="col2" nameend="col2" align="right">2.0</entry></row><row><entry namest="col1" nameend="col1" align="left">Cetyltrimethyl ammonium chloride solution (25%)</entry><entry namest="col2" nameend="col2" align="right">0.5</entry></row><row><entry namest="col1" nameend="col1" align="left">Ethanol</entry><entry namest="col2" nameend="col2" align="right">15.0</entry></row><row><entry namest="col1" nameend="col1" align="left">Perfume</entry><entry namest="col2" nameend="col2" align="right">trace</entry></row><row><entry namest="col1" nameend="col1" align="left">Purified water</entry><entry namest="col2" nameend="col2" align="right">balance</entry></row><row rowsep="1"><entry namest="col1" nameend="col1" align="left">Liquefied petroleum gas</entry><entry namest="col2" nameend="col2" align="right">10.0</entry></row><row rowsep="1"><entry namest="col1" nameend="col1" align="left">Total</entry><entry namest="col2" nameend="col2" align="right">100.0</entry></row></tbody></tgroup></table></tables>

0100The foam agents obtained in Examples 8 and 9 all exhibit excellent set retentivity and favorable touch to the hair and the curls have elasticity.

Example 10:

0101A mist agent was prepared by blending the following components. <tables id="tabl0005" num="0005"><table frame="all"><tgroup cols="2" colsep="1" rowsep="0"><colspec colnum="1" colname="col1" colwidth="78.75mm" /><colspec colnum="2" colname="col2" colwidth="78.75mm" /><thead valign="top"><row rowsep="1"><entry namest="col1" nameend="col1" align="left">(Components)</entry><entry namest="col2" nameend="col2" align="center">(wt.%)</entry></row></thead><tbody valign="top"><row><entry namest="col1" nameend="col1" align="left">Organopolysiloxane A-1</entry><entry namest="col2" nameend="col2" align="right">2.0</entry></row><row><entry namest="col1" nameend="col1" align="left">Ethanol</entry><entry namest="col2" nameend="col2" align="right">30.0</entry></row><row><entry namest="col1" nameend="col1" align="left">Perfume</entry><entry namest="col2" nameend="col2" align="right">trace</entry></row><row rowsep="1"><entry namest="col1" nameend="col1" align="left">Purified water</entry><entry namest="col2" nameend="col2" align="right">balance</entry></row><row rowsep="1"><entry namest="col1" nameend="col1" align="left">Total</entry><entry namest="col2" nameend="col2" align="right">100.0</entry></row></tbody></tgroup></table></tables>

Example 11:

0102A hair set lotion was prepared by blending the following components. <tables id="tabl0006" num="0006"><table frame="all"><tgroup cols="2" colsep="1" rowsep="0"><colspec colnum="1" colname="col1" colwidth="78.75mm" /><colspec colnum="2" colname="col2" colwidth="78.75mm" /><thead valign="top"><row rowsep="1"><entry namest="col1" nameend="col1" align="left">(Components)</entry><entry namest="col2" nameend="col2" align="center">(wt.%)</entry></row></thead><tbody valign="top"><row><entry namest="col1" nameend="col1" align="left">Organopolysiloxane A-1</entry><entry namest="col2" nameend="col2" align="right">1.0</entry></row><row><entry namest="col1" nameend="col1" align="left">Ethanol</entry><entry namest="col2" nameend="col2" align="right">balance</entry></row><row><entry namest="col1" nameend="col1" align="left">Perfume</entry><entry namest="col2" nameend="col2" align="right">trace</entry></row><row rowsep="1"><entry namest="col1" nameend="col1" align="left">Purified water</entry><entry namest="col2" nameend="col2" align="right">10.0</entry></row><row rowsep="1"><entry namest="col1" nameend="col1" align="left">Total</entry><entry namest="col2" nameend="col2" align="right">100.0</entry></row></tbody></tgroup></table></tables>

Example 12:

0103A hair spray was prepared by blending the following components. <tables id="tabl0007" num="0007"><table frame="all"><tgroup cols="2" colsep="1" rowsep="0"><colspec colnum="1" colname="col1" colwidth="78.75mm" /><colspec colnum="2" colname="col2" colwidth="78.75mm" /><thead valign="top"><row rowsep="1"><entry namest="col1" nameend="col1" align="left">(components)</entry><entry namest="col2" nameend="col2" align="center">(wt.%)</entry></row></thead><tbody valign="top"><row><entry namest="col1" nameend="col1" align="left">Organopolysiloxane B-1</entry><entry namest="col2" nameend="col2" align="right">5.0</entry></row><row><entry namest="col1" nameend="col1" align="left">Ethanol</entry><entry namest="col2" nameend="col2" align="right">balance</entry></row><row><entry namest="col1" nameend="col1" align="left">Perfume</entry><entry namest="col2" nameend="col2" align="right">trace</entry></row><row rowsep="1"><entry namest="col1" nameend="col1" align="left">Liquefied petroleum gas</entry><entry namest="col2" nameend="col2" align="right">50.0</entry></row><row rowsep="1"><entry namest="col1" nameend="col1" align="left">Total</entry><entry namest="col2" nameend="col2" align="right">100.0</entry></row></tbody></tgroup></table></tables>

0104The hair cosmetic compositions obtained in Examples 8 to 10 exhibit excellent set retentivity and favorable touch to the hair, and the curls have elasticity. In addition, the removal-by-shampoo property was not impeded.

Example 13:

0105A blow agent containing the following components was prepared in accordance with a conventional method. <tables id="tabl0008" num="0008"><table frame="all"><tgroup cols="2" colsep="1" rowsep="0"><colspec colnum="1" colname="col1" colwidth="78.75mm" /><colspec colnum="2" colname="col2" colwidth="78.75mm" /><thead valign="top"><row rowsep="1"><entry namest="col1" nameend="col1" align="left">(Components)</entry><entry namest="col2" nameend="col2" align="center">(wt.%)</entry></row></thead><tbody valign="top"><row><entry namest="col1" nameend="col1" align="left">Organopolysiloxane C-1</entry><entry namest="col2" nameend="col2" align="right">0.5</entry></row><row><entry namest="col1" nameend="col1" align="left">Amphoteric polymer (Yukaformer M-75)</entry><entry namest="col2" nameend="col2" align="right">0.5</entry></row><row><entry namest="col1" nameend="col1" align="left">Perfume</entry><entry namest="col2" nameend="col2" align="right">trace</entry></row><row><entry namest="col1" nameend="col1" align="left">Ethanol</entry><entry namest="col2" nameend="col2" align="right">30.0</entry></row><row rowsep="1"><entry namest="col1" nameend="col1" align="left">Purified water</entry><entry namest="col2" nameend="col2" align="right">suitable amount</entry></row><row rowsep="1"><entry namest="col1" nameend="col1" align="left">Total</entry><entry namest="col2" nameend="col2" align="right">100.0</entry></row></tbody></tgroup></table></tables>

Example 14:

0106A foam agent containing the following components was prepared in accordance with a conventional method. <tables id="tabl0009" num="0009"><table frame="all"><tgroup cols="2" colsep="1" rowsep="0"><colspec colnum="1" colname="col1" colwidth="78.75mm" /><colspec colnum="2" colname="col2" colwidth="78.75mm" /><thead valign="top"><row rowsep="1"><entry namest="col1" nameend="col1" align="left">(Components)</entry><entry namest="col2" nameend="col2" align="center">(wt.%)</entry></row></thead><tbody valign="top"><row><entry namest="col1" nameend="col1" align="left">Organopolysiloxane C-1</entry><entry namest="col2" nameend="col2" align="right">1.0</entry></row><row><entry namest="col1" nameend="col1" align="left">Chitin liquid (product of Ichimaru-Pharcos)</entry><entry namest="col2" nameend="col2" align="right">5.0</entry></row><row><entry namest="col1" nameend="col1" align="left">Nonionic surfactant (Softanol 90, product of Nihon Shokubai)</entry><entry namest="col2" nameend="col2" align="right">1.0</entry></row><row><entry namest="col1" nameend="col1" align="left">Perfume</entry><entry namest="col2" nameend="col2" align="right">trace</entry></row><row><entry namest="col1" nameend="col1" align="left">Purified water</entry><entry namest="col2" nameend="col2" align="right">balance</entry></row><row rowsep="1"><entry namest="col1" nameend="col1" align="left">Liquefied petroleum gas</entry><entry namest="col2" nameend="col2" align="right">10.0</entry></row><row rowsep="1"><entry namest="col1" nameend="col1" align="left">Total</entry><entry namest="col2" nameend="col2" align="right">100.0</entry></row></tbody></tgroup></table></tables>

Example 15:

0107A hair spray containing the following components was prepared in accordance with a conventional method. <tables id="tabl0010" num="0010"><table frame="all"><tgroup cols="2" colsep="1" rowsep="0"><colspec colnum="1" colname="col1" colwidth="78.75mm" /><colspec colnum="2" colname="col2" colwidth="78.75mm" /><thead valign="top"><row rowsep="1"><entry namest="col1" nameend="col1" align="left">(Components)</entry><entry namest="col2" nameend="col2" align="center">(wt.%)</entry></row></thead><tbody valign="top"><row><entry namest="col1" nameend="col1" align="left">Organopolysiloxane C-3</entry><entry namest="col2" nameend="col2" align="right">1.5</entry></row><row><entry namest="col1" nameend="col1" align="left">Nonionic polymer (Luviskol VA37, product of BASF)</entry><entry namest="col2" nameend="col2" align="right">5.0</entry></row><row><entry namest="col1" nameend="col1" align="left">Perfume</entry><entry namest="col2" nameend="col2" align="right">trace</entry></row><row><entry namest="col1" nameend="col1" align="left">Ethanol</entry><entry namest="col2" nameend="col2" align="right">balance</entry></row><row rowsep="1"><entry namest="col1" nameend="col1" align="left">Liquefied petroleum gas</entry><entry namest="col2" nameend="col2" align="right">50.0</entry></row><row rowsep="1"><entry namest="col1" nameend="col1" align="left">Total</entry><entry namest="col2" nameend="col2" align="right">100.0</entry></row></tbody></tgroup></table></tables>

Example 16:

0108A hair set lotion containing the following components was prepared in accordance with an ordinary manner. <tables id="tabl0011" num="0011"><table frame="all"><tgroup cols="2" colsep="1" rowsep="0"><colspec colnum="1" colname="col1" colwidth="78.75mm" /><colspec colnum="2" colname="col2" colwidth="78.75mm" /><thead valign="top"><row rowsep="1"><entry namest="col1" nameend="col1" align="left">(Components)</entry><entry namest="col2" nameend="col2" align="center">(wt.%)</entry></row></thead><tbody valign="top"><row><entry namest="col1" nameend="col1" align="left">Organopolysiloxane C-2</entry><entry namest="col2" nameend="col2" align="right">1.0</entry></row><row><entry namest="col1" nameend="col1" align="left">Amphoteric polymer (Yukaformer M-75)</entry><entry namest="col2" nameend="col2" align="right">2.0</entry></row><row><entry namest="col1" nameend="col1" align="left">Ethanol</entry><entry namest="col2" nameend="col2" align="right">balance</entry></row><row><entry namest="col1" nameend="col1" align="left">Purified water</entry><entry namest="col2" nameend="col2" align="right">10.0</entry></row><row rowsep="1"><entry namest="col1" nameend="col1" align="left">Perfume</entry><entry namest="col2" nameend="col2" align="right">trace</entry></row><row rowsep="1"><entry namest="col1" nameend="col1" align="left">Total</entry><entry namest="col2" nameend="col2" align="right">100.0</entry></row></tbody></tgroup></table></tables>

0109The hair setting agents obtained in Examples 13 to 16 are all excellent in terms of set retentivity, smoothness, natural gloss, softness, elasticity, easy combing and water repellency.

Example 17:

0110A foam agent was obtained by blending the following components. <tables id="tabl0012" num="0012"><table frame="all"><tgroup cols="2" colsep="1" rowsep="0"><colspec colnum="1" colname="col1" colwidth="78.75mm" /><colspec colnum="2" colname="col2" colwidth="78.75mm" /><thead valign="top"><row rowsep="1"><entry namest="col1" nameend="col1" align="left">(Components)</entry><entry namest="col2" nameend="col2" align="center">(wt.%)</entry></row></thead><tbody valign="top"><row><entry namest="col1" nameend="col1" align="left">Organopolysiloxane D-1</entry><entry namest="col2" nameend="col2" align="char" char=".">3.0</entry></row><row><entry namest="col1" nameend="col1" align="left">Polyoxyethylene(9)tetradecyl ether</entry><entry namest="col2" nameend="col2" align="char" char=".">0.5</entry></row><row><entry namest="col1" nameend="col1" align="left">Ethanol</entry><entry namest="col2" nameend="col2" align="char" char=".">10.0</entry></row><row><entry namest="col1" nameend="col1" align="left">Perfume</entry><entry namest="col2" nameend="col2" align="char" char=".">0.10</entry></row><row><entry namest="col1" nameend="col1" align="left">Liquefied petroleum gas</entry><entry namest="col2" nameend="col2" align="char" char=".">10.0</entry></row><row rowsep="1"><entry namest="col1" nameend="col1" align="left">Purified water</entry><entry namest="col2" nameend="col2" align="left">balance</entry></row><row rowsep="1"><entry namest="col1" nameend="col1" align="left">Total</entry><entry namest="col2" nameend="col2" align="char" char=".">100.0</entry></row></tbody></tgroup></table></tables>

Example 18:

0111A hair spray was obtained by blending the following components. <tables id="tabl0013" num="0013"><table frame="all"><tgroup cols="2" colsep="1" rowsep="0"><colspec colnum="1" colname="col1" colwidth="78.75mm" /><colspec colnum="2" colname="col2" colwidth="78.75mm" /><thead valign="top"><row rowsep="1"><entry namest="col1" nameend="col1" align="left">(Components)</entry><entry namest="col2" nameend="col2" align="center">(wt.%)</entry></row></thead><tbody valign="top"><row><entry namest="col1" nameend="col1" align="left">Organopolysiloxane D-5</entry><entry namest="col2" nameend="col2" align="char" char=".">3.0</entry></row><row><entry namest="col1" nameend="col1" align="left">Squalane</entry><entry namest="col2" nameend="col2" align="char" char=".">0.1</entry></row><row><entry namest="col1" nameend="col1" align="left">Methylphenyl polysiloxane (KF-53 by Shin'etsu)</entry><entry namest="col2" nameend="col2" align="char" char=".">0.15</entry></row><row><entry namest="col1" nameend="col1" align="left">Perfume</entry><entry namest="col2" nameend="col2" align="char" char=".">0.10</entry></row><row><entry namest="col1" nameend="col1" align="left">Liquefied petroleum gas</entry><entry namest="col2" nameend="col2" align="char" char=".">25.0</entry></row><row><entry namest="col1" nameend="col1" align="left">Dimethylether</entry><entry namest="col2" nameend="col2" align="char" char=".">25.0</entry></row><row rowsep="1"><entry namest="col1" nameend="col1" align="left">Ethanol</entry><entry namest="col2" nameend="col2" align="left">balance</entry></row><row rowsep="1"><entry namest="col1" nameend="col1" align="left">Total</entry><entry namest="col2" nameend="col2" align="char" char=".">100.0</entry></row></tbody></tgroup></table></tables>

Example 19:

0112A foam agent was obtained by blending the following components. <tables id="tabl0014" num="0014"><table frame="all"><tgroup cols="2" colsep="1" rowsep="0"><colspec colnum="1" colname="col1" colwidth="78.75mm" /><colspec colnum="2" colname="col2" colwidth="78.75mm" /><thead valign="top"><row rowsep="1"><entry namest="col1" nameend="col1" align="left">(Components)</entry><entry namest="col2" nameend="col2" align="center">(wt.%)</entry></row></thead><tbody valign="top"><row><entry namest="col1" nameend="col1" align="left">Organopolysiloxane D-8</entry><entry namest="col2" nameend="col2" align="char" char=".">1.0</entry></row><row><entry namest="col1" nameend="col1" align="left">Anionic polymer (Gantrey ES 225 by GAF)</entry><entry namest="col2" nameend="col2" align="char" char=".">1.5</entry></row><row><entry namest="col1" nameend="col1" align="left">Polyoxyethylene(9)tetradecyl ether</entry><entry namest="col2" nameend="col2" align="char" char=".">0.5</entry></row><row><entry namest="col1" nameend="col1" align="left">Ethanol</entry><entry namest="col2" nameend="col2" align="char" char=".">10.0</entry></row><row><entry namest="col1" nameend="col1" align="left">Perfume</entry><entry namest="col2" nameend="col2" align="char" char=".">0.10</entry></row><row><entry namest="col1" nameend="col1" align="left">Liquefied petroleum gas</entry><entry namest="col2" nameend="col2" align="char" char=".">10.0</entry></row><row rowsep="1"><entry namest="col1" nameend="col1" align="left">Purified water</entry><entry namest="col2" nameend="col2" align="left">balance</entry></row><row rowsep="1"><entry namest="col1" nameend="col1" align="left">Total</entry><entry namest="col2" nameend="col2" align="char" char=".">100.0</entry></row></tbody></tgroup></table></tables>

0113The hair setting agents obtained in Examples 17 - 19 all exhibited excellent set retentivity and favorable touch to the hair and the curls had elasticity.

Example 20:

0114A foam agent was prepared by blending the following components. <tables id="tabl0015" num="0015"><table frame="all"><tgroup cols="2" colsep="1" rowsep="0"><colspec colnum="1" colname="col1" colwidth="78.75mm" /><colspec colnum="2" colname="col2" colwidth="78.75mm" /><thead valign="top"><row rowsep="1"><entry namest="col1" nameend="col1" align="left">(Components)</entry><entry namest="col2" nameend="col2" align="center">(wt.%)</entry></row></thead><tbody valign="top"><row><entry namest="col1" nameend="col1" align="left">Organopolysiloxane A-2</entry><entry namest="col2" nameend="col2" align="char" char=".">2.70</entry></row><row><entry namest="col1" nameend="col1" align="left">Salf of Chitosan (Chitomer PC, product of Union Carbide)</entry><entry namest="col2" nameend="col2" align="char" char=".">0.30</entry></row><row><entry namest="col1" nameend="col1" align="left">Ethanol</entry><entry namest="col2" nameend="col2" align="char" char=".">15.0</entry></row><row><entry namest="col1" nameend="col1" align="left">Coconut oil fathy acid diethanolamide</entry><entry namest="col2" nameend="col2" align="char" char=".">0.4</entry></row><row><entry namest="col1" nameend="col1" align="left">Cationic polymer (Polymer JR400, product of Union Carbide)</entry><entry namest="col2" nameend="col2" align="char" char=".">0.1</entry></row><row><entry namest="col1" nameend="col1" align="left">Perfume</entry><entry namest="col2" nameend="col2" align="left">trace</entry></row><row><entry namest="col1" nameend="col1" align="left">Purified water</entry><entry namest="col2" nameend="col2" align="left">balance</entry></row><row rowsep="1"><entry namest="col1" nameend="col1" align="left">Liquefied petroleum gas</entry><entry namest="col2" nameend="col2" align="char" char=".">10.0</entry></row><row rowsep="1"><entry namest="col1" nameend="col1" /><entry namest="col2" nameend="col2" align="char" char=".">100.0</entry></row></tbody></tgroup></table></tables>

0115The foam agent obtained in Examples 20 exhibited exellent set retentivity and favorable touch to the hair and curls had elasticity.

Example 21:

0116A blow agent containing the following components was prepared in accordance with a conventional method. <tables id="tabl0016" num="0016"><table frame="all"><tgroup cols="2" colsep="1" rowsep="0"><colspec colnum="1" colname="col1" colwidth="78.75mm" /><colspec colnum="2" colname="col2" colwidth="78.75mm" /><thead valign="top"><row rowsep="1"><entry namest="col1" nameend="col1" align="left">(Components)</entry><entry namest="col2" nameend="col2" align="center">(wt.%)</entry></row></thead><tbody valign="top"><row><entry namest="col1" nameend="col1" align="left">Organopolysiloxane A-2</entry><entry namest="col2" nameend="col2" align="char" char=".">2.0</entry></row><row><entry namest="col1" nameend="col1" align="left">Dimethylpolysiloxane emulsion (L-13, product of Toray Dow Corning Silicone)</entry><entry namest="col2" nameend="col2" align="char" char=".">1.0</entry></row><row><entry namest="col1" nameend="col1" align="left">Cetyltrimethyl ammonium chloride</entry><entry namest="col2" nameend="col2" align="char" char=".">0.1</entry></row><row><entry namest="col1" nameend="col1" align="left">Ethanol</entry><entry namest="col2" nameend="col2" align="char" char=".">20.0</entry></row><row><entry namest="col1" nameend="col1" align="left">Perfume</entry><entry namest="col2" nameend="col2" align="left">trace</entry></row><row rowsep="1"><entry namest="col1" nameend="col1" align="left">Purified water</entry><entry namest="col2" nameend="col2" align="left">balance</entry></row><row rowsep="1"><entry namest="col1" nameend="col1" /><entry namest="col2" nameend="col2" align="char" char=".">100.0</entry></row></tbody></tgroup></table></tables>

0117The blow agent ogtained in Example 21 exhibited excellent blow setting effect and soft and smooth touch to the hair.