Packaging of high power semiconductor lasers

Background of the Invention

0001This invention relates to packaged high power semiconductor lasers and a method and package therefor.

0002Maintaining laser stability and prolonging laser life may require control of the laser operating environment, especially temperature, humidity and atmosphere, which is relatively inert with respect to the semiconductor laser materials, the art teaching that an oxygen free atmosphere extends laser life. Also a dry atmosphere is preferred to prevent reaction with the laser materials and to preserve the integrity of the miniature electric circuitry associated with the laser operation. For a further discussion of appropriate microcircuit packaging see, "Considerations in the Hermetic Packaging of Hybrid Microcircuits", Byrnes et al., <u>Solid State Technology</u>, 1984. For example, an atmosphere of dry nitrogen with a helium tracer provides a favorable laser operating environment. The term dry, as used in this document, in general refers to a gaseous medium having a water content less than about 5000 ppm. However, as semiconductor laser facet power has increased to 50 mW and higher, these generally accepted strategies for stable, long term laser operation have provided inadequate. For a laser having a facet size of about 2 microns by 1 micron, a power output of 50 mW translates into an average power density at the facet of the order to 1 megawatt/cm². Laser ends facets, which essentially delimit the lasing cavity, can change in reflectivity and can even be destroyed when a high power laser is operated in a dry helium/nitrogen atmosphere. Materials which can contaminate the container include solder flux, oils, epoxies and cleaning agents used in the process of producing high powered semiconductor laser devices, resulting in particulate and gaseous contamination reaching the surface of the facet coatings, and producing impurity deposits thereon. Such deposits can change the facet reflectivity, reducing transmitted power, and increasing absorptivity at the facet which causes facet heating and eventual laser failure. Therefore, new strategies are needed to meet those laser applications which require high power together with assurance of laser stability and longevity.

0003JP A 60186076 discloses that the presence of <u>oxygen</u> in hermetically sealed packages containing InGaAsP/InP lasers, having an operating optical power of 3-5 mW, reduces the leakage current.

Brief Description of the Invention

0004The invention is disclosed in claims 1, 6 and 7. Various embodiments of the invention are disclosed in the dependent claims.

0005The present invention meets the need for stable, long term, continuous operation of a high power semiconductor laser by providing an environment which is protective of the laser materials, "high power semiconductor laser" referring to a semiconductor laser having a front facet power of at least 50 mW. Because the front facet of the laser is very small, an equivalent definition of high power may be expressed as a front facet power density of the order of 1 megawatt/cm² or higher.

0006In a basic aspect of the invention a packaged high power semiconductor laser comprises a laser with an InGaAs active layer, and optionally a getter, surrounded by a hermetically sealed container filled with a gaseous medium containing at least 100 ppm oxygen. Further advantageous aspects and developments of the invention will be found in the claims. Surprisingly, the incorporation of oxygen in the container's gaseous medium significantly reduces the potential of damage to the laser's facets arising from residual organic impurities present in the container at the time of sealing. Although such an atmosphere substantially increases the useful life of high power semiconductor lasers, even further increases are achieved through the combination of an oxygen-containing atmosphere and a getter material which is capable of adsorbing or absorbing (trapping) organic materials. Such increased life is especially important for high power semiconductor lasers used in the filed of telecommunications where life expectancies of ten years or more are required. The oxygen may act to substantially remove deposits from the laser facet structure or to react with impurities prior to deposition on the facet structure and so prevent deposits from forming thereon, thereby avoiding damage to the laser facet structure. Because of the deleterious effects of water on microcircuits, very lower water content, less than 1000 ppm, is preferred.

0007The use of materials, such as metals, having a low hydrogen content to form the walls of the laser's container provide the important advantage of minimizing water formation within the container as a result of reaction between hydrogen released from the walls of the container and the oxygen included in the container for impurity control. A preferred method for achieving the desired low hydrogen levels is to bake the container materials at an elevated temperature, e.g., about 150°C, for an extended period of time, e.g., about 200 hours, prior to the assembly of the complete container.

Brief Description of the Drawings

0008Fig. 1 is an exploded illustration of a semiconductor laser.

0009Figs. 2 &amp; 3 are charts illustrative of back facet power measured over time for semiconductor lasers packaged in a dry inert environment compared to lasers packaged in air.

0010Fig. 4 is a side view, cut-away illustration of a laser device mounted within a container.

Detailed Description of the Invention

0011Fig. 1 illustrates the structure of a semiconductor laser, familiar to those skilled in the art. The front and back facets, 10 and 12 respectively, of laser body 3 are cleaved surfaces substantially parallel to one another. These facets are protected by passivation layers 5 which may be a layer of silicon. The passivation layer serves to protect the laser facet from contamination and erosion. The passivation layer also protects the laser facet from oxidation. The front facet mirror 9 is a coating of thickness approximately one quarter of the laser wavelength. The back facet mirror 7 is comprised of successive layers of reflective material, wherein adjacent layers are generally of different materials. The number, composition and thickness of the layers forming mirror 7 are chosen to give a target ratio of front facet to back facet transmitted power. A typical front to back facet power ratio is about 40:1.

0012A possible mechanism for failure of a semiconductor laser of the general type illustrated in Fig. 1 is as follows.

0013The emitting area at the laser facet may be of the order of 10 square microns or less. Thus when power levels reach or exceed about 50 mW, the number of photons crossing a unit area (photon flux) of a facet is comparatively large. The probability of a photon interacting with a trace impurity in the laser enclosure rises in proportion to the photon flux. Hence the probability increases for photon breakdown of impurity molecules on or near the facet mirror. Alternatively, the photon flux may excite labile or volatile impurity molecules on or near the facet mirror, thereby increasing the reactivity of the impurities, and possibly resulting in depositions on the facet mirror. Also, since high power semiconductor lasers are generally operated continuously, especially in telecommunications applications, once impurity molecules are deposited on the facet mirrors, the problem escalates rapidly through local heating as a result of absorption of the continuously impinging laser light at the location of the impurity.

0014The impurity molecules may originate from residues of soldering flux, epoxies, or cleaning materials, viz., isopropyl alcohol or OPTICLEAR (a brand name cleaning agent for optical materials) used in the fabricating process. With regard to epoxies, extended curing of this material helps reduce, but does not eliminate, impurity generation. Examples or organic chemicals found in these materials are propene, terpene and abietic acid. The action of the infrared photons on such carbon chains may be to strip off water, leaving a reactive carbon chain fragment which can bind to an atom in the material which makes up the facet mirror. Another mechanism is that the photons can strip hydrogen from the carbon chains thereby producing a reactive carbon chain fragment. Alumina and silicon nitride are examples of mirror materials. The presence of free oxygen in the laser container may protect the facet mirrors by binding to the reactive fragments before the fragments bond to the facet mirror. Or the oxygen may serve to quench excited states of reactive species thereby protecting the facet mirrors. An alternative possibility is that the free oxygen molecules break the "mirror-atom"-"carbon-chain-fragment" bond and thus remove the reactive fragment from the facet mirror. The oxygen thus may effectively act as a getter for impurity molecules.

0015In the above scenario, the amount of oxygen required to protect the facet mirror or facet structure would depend upon the number of impurity molecules as well as upon the number of other reactive sites present in the container which could bind to oxygen. The amount of oxygen required would also depend upon the kind of impurity molecules. Hence, the determination of the proper amount of oxygen to add to the gaseous medium filling the container would, in general, be experimental. Because of the known deleterious effects of oxygen, i.e., the reaction with hydrogen to form water which may undermine microcircuit integrity, the preferred amount of oxygen to add to the gaseous medium within the container is an amount just sufficient to maintain constant the properties of the facet structure.

0016The posited phenomena of impurity breakdown by photons would be most likely to occur at the higher power (higher photon flux) front facet. In the absence of free oxygen, the photo-reaction products could bind to or produce deposits on the facet structures, especially the mirror of the front facet. The deposits could change the reflectivity or absorptivity of the facet mirror. Increased absorptivity could increase the temperature at the facet to the melting point of the facet materials thereby destroying the facet. Also, increase temperature at the facet could cause junction migration in the bulk laser material, thereby destroying the laser. Thus, trace impurities which are essentially inconsequential at lower power levels, may become significant as the power level and associated photon flux increases. A successful strategy for realizing maximum laser life for lower photon flux lasers may become ineffective for higher photon flux lasers.

0017Assuming a photo-reaction is taking place, it is believed that a reactive gas, such as oxygen, present near a facet, binds to the reactive products of the photo-reaction, as described above, thereby preventing these reactive products from precipitating onto the facet mirror or removing the reactive products already bound to the facet mirror. Oxygen thus becomes a protective element of the laser atmosphere as opposed to a potential factor in shortening the life of microcircuit as taught in prior art.

0018It will be understood that the validity of the mechanism described immediately above is not essential to the invention nor is the mechanism put forward as necessary to the function of the invention.

0019It was found, as will be explained in the examples below, that a standard procedure, for example MIL-STD-1772A, for laser packaging which includes cleaning the inside of the container with a substance such as isopropyl alcohol, filling the container with a dry inert gas, and hermetically sealing the laser container, produced unacceptably short laser life, of the order of several tens of hours, for high power lasers, i.e., lasers producing a front facet power of at least 50 mW.

0020Lasers packaged per the standard procedure, except that dry air was introduced into the laser enclosure atmosphere, showed acceptable life. Furthermore, certain lasers which had begun to degrade in power when operated in a dry inert atmosphere, were found to recover when an environment of air was introduced.

0021As discussed above, the atmosphere used to fill the laser enclosure preferably contains at least 100 ppm oxygen and less than about 1000 ppm of water. Commercially available "reconstituted air" is a suitable source for the atmosphere. For example, air produce number 00.1 sold by Airco Gas Inc. of Portland, Oregon, can be used in the packaging of lasers in accordance with the invention. As reported by the manufacturer, this product has the following composition: -20% 0₂ (typical value); -80% N₂ (typical value); 0.2 ppm CO (typical value); &lt;0.1 ppm CO₂ (typical value); &lt;0.1 ppm NO_x (typical value); &lt;0.1 ppm total hydrocarbons (guaranteed value); and &lt;3 ppm H₂O (guaranteed value).

0022In addition to packaging the laser in oxygen, an adsorptive or absorptive getter is also preferably included within the laser enclosure. Various getter materials can be used for this purpose. The material should have the following properties: 1) it should have a substantial adsorptive or absorptive capacity for organic impurities and preferably a substantial specific adsorptive or absorptive capacity so that only a limited amount of the material need be included in the laser enclosure; 2) its adsorptive or absorptive capacity should remain sufficient to protect the laser and its circuitry over the operating temperature range of the enclosure (e.g., over the range from about -40°C to about 85°C), so that substantial amounts of adsorbed or absorbed impurities are not released as the getter's temperature changes during use; 3) it should exhibit substantial physical integrity during shipping, handling and use, e.g., the material should release minimal dust or particulates that could adhere to the facet mirrors; and 4) organic contaminants should be readily removable from the material prior to introduction of the material into the container, i.e., the material should be purgable prior to use.

0023The amount of getter used for a particular laser enclosure will at least in part involve an empirical determination based on the specific properties of the getter material chosen for the laser package, the nominal amount of organic impurities within the enclosure at the time of sealing, and the volume of the enclosure. In general terms, for a getter material having a high specific surface area, e.g., a surface area on the order to 100 square meters per gram and an interconnected pore size distribution able to accommodate a substantial volume of organic compounds, approximately 0.1 grams of getter should be used for each cm³ of enclosure.

0024Preferably, the getter material is used in block form to facilitate its incorporation in the laser enclosure. For example, a block of getter material can be mounted on the inside surface of the cover for the enclosure. In general, such mounting should not employ organic materials, e.g., epoxies or glues, but rather should be by mechanical means. For example, wire or spring clip or screw mounting can be used. Similarly, a mechanical solder attachment can be employed wherein, for example, through-holes are formed in the block of getter material, the getter is placed on the inside surface of the enclosure's cover, and the getter is soldered to the cover by pouring molten solder through the through-holes. Other means of attachment can, of course, be used if desired.

0025Examples of getter materials suitable for use in the practice of the invention include various porous silicas, such as the VYCOR brand porous silica sold by Corning Incorporated (Corning, New York) under product number 7930, and various zeolites, such as the Na-Al-Si zeolite sold by W.R. Grace &amp; Company under product number 10A. Mixtures of getter materials can be used in the practice of the invention if desired.

0026As discussed above, the oxygen within the packaging atmosphere serves the important function of minimizing laser damage by organic impurities. There is, however, a downside to using oxygen, namely, that it can react with hydrogen to form water within the laser enclosure. The water, in turn, can adversely affect the overall operation of the electronic components within the enclosure, including the semiconductor laser, by, for example, creating a short circuit between the conductors which interconnect the components. The use of a getter material which adsorbs or absorbs water in addition to organic impurities, such as the VYCOR material referred to above, can help to minimize this problem.

0027In accordance with the invention, the water problem is also addressed by reducing the amount of hydrocarbon available within the enclosure for reaction with the oxygen of the oxygen-containing atmosphere. The metals used to form the walls of the container are the main source of hydrogen within the enclosure. For example, a common material for use in constructing electronic enclosures is Kovar (an alloy of nickel and cobalt) electroplated with nickel and gold. During its manufacture, Kovar is normally annealed in hydrogen. Similarly, during the electroplating process, hydrogen is generated, which becomes absorbed in the metal. Over time, the hydrogen is released from the metal, reacts with the oxygen in the enclosure, and forms water. Accordingly, the hydrogen problem does not normally present itself initially, but rather develops as the semiconductor laser device ages after sealing in an atmosphere containing oxygen.

0028The invention addresses the hydrogen problem by pretreating the materials used to form the container. Specifically, the materials are baked at an elevated temperature and for an extended period of time in order to substantially reduce the amount of hydrogen adsorbed or absorbed therein. For example, in the case of Kovar plated with nickel and gold, the baking can take place at a temperature of about 150°C for a period of about 200 hours. Further hydrogen reduction can be achieved by increasing the baking temperature to about 350°C, although in general such higher temperature processing is not required. The temperatures and times used for plated Kovar are also generally applicable to other materials known in the art for constructing sealed enclosures.

Comparative Example 1

0029A 980 nm InGaAs semiconductor laser was obtained from the IBM research facility in Zurich, Switzerland, with a structure substantially as shown in Fig. 1. The laser mirrors were configured to deliver 90% of total power through the front facet and 10% through the back facet. The laser was operated at a drive current of 195 mA which produced a front facet power of 150 mW. The laser was enclosed in a hermetically sealed container filled with a mixture of He/N in the ratio 1:9. Prior to sealing, the container was cleaned with isopropyl alcohol and with OPTICLEAR. Water content of the atmosphere surrounding the laser was &lt;1000 ppm.

0030A semiconductor photodiode sensitive to the 980 nm wavelength was used to continuously monitor back facet power over time. Because of the front to back facet power ratio chosen for the laser, a small increase in front mirror reflectivity which produces only a small decrease in front facet power produces a proportionately larger increase in back facet power. Hence the back facet monitor is sensitive to small changes in front facet reflectivity. Fig. 4 is a cut away illustration of laser 21 and back facet photodiode 23 mounted on platform 25. The arrangement is sealed inside container 27.

0031Referring to Fig. 2, line 13 shows the back facet power increase observed during approximately 45 hours of testing of the device of Comparative Example 1 with a He/N atmosphere. The sharp upward trend is indicative of an increase in front facet reflectivity and thus a premature laser failure.

Comparative Example 2

0032Line 11 of Fig. 2 shows the back facet power measured for a laser, essentially identical to the laser of Comparative Example 1, packaged using the same procedure as for the Example 1 laser except that the dry He/N mixture is replaced by air. After 264 hours the back facet power curve is normal, indicative of a normal laser life expectancy.

Comparative Example 3

0033A 980 nm InGaAs laser was packaged in a dry inert atmosphere as described in Example 1. Again drive current was about 195 mA and initial front facet power was about 150 mW. Referring to Fig. 3, line 15 shows a monotonic increase in back facet power. The data is predictive of premature laser failure. The testing was stopped at about 100 hours, before failure of the laser.

Comparative Example 4

0034The laser container of Example 3 was punctured in ambient air, breaking the hermetic seal of the container to allow ingress of the ambient air. The laser drive current was reapplied and back facet power monitoring was resumed. Line 17 shows the back facet power decreasing to nominal level and then continuing with a normal aging slope. A normal aging slope is about 5% decrease in back facet power in 500 hours. That is, the laser back facet power decreases about 5% in the first 500 hours of operation.

0035Repeated tests of lasers in dry air showed the superiority of that atmosphere over the atmosphere of the dry He/N mixture.

0036It is believed that oxygen levels as low as 100 ppm may be sufficient to maintain the integrity of the laser facet mirror since thorough cleaning of the container can reduce vapor impurities to very low levels. In general, organic impurities may be minimized by cleaning. Conversely, if vapor impurity levels are relatively higher, oxygen levels should be increased to stoichiometrically react with the impurity molecules present. Preferably the oxygen concentration is such that the reaction to form the non-harmful oxidized products of the organic impurities is strongly favored thermodynamically. In this case the amount of oxygen would be greater than the stoichiometric amount.

0037The other elemental and compound gases, which in addition to oxygen make up air, are not believed to be preferred in preserving the integrity of the high power laser facet structure. Thus a mixture of oxygen with numerous commonly known gases would serve as a suitable gaseous medium for a high power semiconductor laser. For example a mixture of argon, helium or nitrogen and oxygen would constitute a suitable atmosphere for the laser.

0038Optical waveguide amplifier fiber 19 in Fig. 4 is shown coupled to the front facet of laser 21 and passing through the wall of container 27. This configuration is typical of a pump laser providing power to an amplifier fiber.

Example 5

0039A 980 nm InGaAs semiconductor laser of the type described in Example 1, along with other components for using the laser to provide power to an amplifier fiber, are packaged along with a VYCOR glass getter (product number 7930) in a low-hydrogen Kovar container filled with an oxygen-containing atmosphere as follows.

0040The container for the laser is fabricated from Kovar plated with gold and nickel in two sections -- a body section for holding the laser and other components and a cover for carrying the VYCOR getter. The two sections are baked in a N₂ purged oven at 150°C for 200 hours. The internal volume of the container is approximately 5 cm³.

0041The VYCOR getter is baked at 650°C for at least 0.5 hours to activate the material and to remove previously adsorbed or absorbed organics. A section of the material having a weight of approximately 0.75 grams is attached to the previously baked cover using through-holes formed in the getter as described above.

0042The semiconductor laser and other components are mounted in the body section of the container. That section along with the cover section with its attached getter are then vacuum baked for 12 hours at 100°C. Finally, the two sections are sealed together in an atmosphere of the 00.1 air product referred to above. The sealing is performed by fluxless, electro-resistance heating.

0043The semiconductor laser is found to operate successfully over an extended period of time, i.e., for over 5000 hours, with minimal free water in the package, i.e., a water concentration in the package atmosphere of less than 5000 ppm at the end of the test period. The packaged high power semiconductor laser is thus suitable for use in providing power to an amplifier fiber in a telecommunications system.