Liquid star polymers having terminal hydroxyl groups.

This invention relates to diene based star polymers suitable for crosslinking and to adhesive, sealant, and coating compositions made from the star polymers.

Diene based polymers having low viscosity can be used without solvents to make coatings and related compositions as disclosed in several United States Patents. For unsaturated 1,3-butadiene polymers it is known that high 1,4-addition obtains low viscosity as taught in U.S. Patents 4,518,753 and 3,652,732. However, when the polymers described in these patents are hydrogenated the products are crystalline solids. Such a crystalline hydrogenated diene polymer having terminal hydroxyl groups is available from Mitsubishi and is designated POLYTAIL H polymer which has a melting point of 72°C.

The hydrogenated butadiene polymers are non-crystalline when the 1,4-addition of butadiene is below 70% as stated in United States Patent No. 4,020,125. The non-crystalline hydrogenated butadiene polymers are viscous liquids at low molecular weights as described in United States Patents Nos. 4,866,120 and 4,020,125. POLYTAIL HA polymer produced by Mitsubishi and NISSO GI-2000 polymer produced by Nippon Soda are commercial examples of low molecular weight hydrogenated butadiene polymers which have terminal hydroxyl groups and 1,4-addition of about 16%.

Star polymers having three or more polymeric arms of a diene connected to a central nucleus are known in the art as described in Canadian Patent No. 716,645 and United States Patent No. 3,985,830. The star polymers are also useful as low viscosity components for coatings as evidenced by the fact that several diene polymers described in Example 3 of United States Patent 3,652,732 are inherently mixtures of star diene polymers and linear diene polymers. The star diene polymers facilitate crosslinking of the diene polymers. However, the diene polymers have at least 80% 1,4-addition and are crystalline solids after hydrogenation.

The termination of living anionic polymers to form functional end groups useful for adhesives, sealants, and coatings is described in United States Patents 4,417,029, 4,518,753, and 4,753,991. Capping of anionic polymers with hydroxyl, carboxyl, amine, epoxy, and phenolic groups is known. Of particular interest for the present invention are diene polymers having terminal functional groups for production of coatings.

It is an object of the present invention to provide star diene polymers having terminal functional groups and low viscosity at room temperature. It is also an object of the invention to use the low viscosity polymers to make coatings and other high molecular weight polymers.

The polymers of the invention comprise blocks or segments of a conjugated diene that are connected in a star structure with at least two terminal hydroxyl groups per molecule, wherein the peak molecular weight of each diene block is from 400 to 40,000 as measured by Gel Permeation Chromatography (GPC), and the peak molecular weight of the star molecules is at least 30,000 as measured by light scattering.

The polymers are produced by addition of hydroxyl groups to living star polymer structures containing anionically polymerized conjugated diene blocks or segments having terminal lithium groups. The living star polymers have the following generic formula: <chemistry id="chem0001" num="0001"><img file="EP0632075A2_D0001.tif" /></chemistry> wherein each A is a block or segment comprising a preponderance of a polymerised conjugated diene, q is from 2 to 30 and represents the number of polymeric arms having terminal lithium groups, and (Li―)_s ―Y―(―B)_r is the residue of a polylithium initiator wherein B is the residue of a monolithium polymer having the general structure B-Li, Y is a crosslinked core comprising a compound having at least two independently polymerized vinyl groups, r &gt; q, and s = (r-q).

Each A block or segment in the structure of Formula I preferably comprises at least 90% by weight of the polymerized conjugated alkadiene. Most preferably, the A segments or blocks are homopolymeric. The conjugated alkadienes preferably have up to 8 carbon atoms. Illustrative of such conjugated alkadienes are 1,3-butadiene (butadiene), 2-methyl-1,3-butadiene (isoprene), 1,3-pentadiene (piperylene), 1,3-octadiene, and 2-methyl-1,3-pentadiene. Preferred conjugated alkadienes are butadiene and isoprene, particularly butadiene.

The anionic polymerisation of the conjugated diene hydrocarbons is typically controlled with structure modifiers such as diethylether or glyme (1,2-diethoxyethane) when the polymer is to be hydrogenated to improve thermal stability. As described in Re 27,145, the level of 1,2-addition of a butadiene polymer or copolymer can greatly affect elastomeric properties after hydrogenation.

The 1,2-addition of 1,3-butadiene polymers having terminal functional groups influences the viscosity of the polymers as described in more detail below. A 1,2-addition of 40% is achieved during polymerization at 50°C with 6% by volume of diethylether or 1000 ppm of glyme.

Monolithium polymers having the structure B-Li are generally prepared by anionic polymerization of an alkenyl aromatic hydrocarbon, a conjugated diene, or an alkyl methacrylate with a monolithium compound to produce living polymers having a peak molecular weight from 1,500 to 15,000. Preferably, the monolithium polymer is a conjugated diene polymer having a peak molecular weight from 3,000 to 7,000, as measured by GPC.

Monolithium compounds for making the structure B-Li are preferably alkyllithiums having from 4 to 6 carbon atoms. Most preferably the monolithium compound is sec-butyllithium.

The alkenyl aromatic hydrocarbons used to prepare the monolithium polymers, or possibly included in the A blocks or segments, are hydrocarbon compounds of up to 18 carbon atoms having an alkenyl group of up to 6 carbon atoms attached to a ring carbon atom of an aromatic ring system of up to 2 aromatic rings. The preferred alkenyl aromatic compounds have an alkenyl group of up to 3 carbon atoms attached to a benzene ring as exemplified by styrene and styrene homologs such as styrene, α-methylstyrene, and p-methylstyrene. Styrene and α-methylstyrene are particularly preferred alkenyl aromatic compounds, especially styrene.

The alkyl methacrylates used to prepare the monolithium oligomers or monolithium polymers have from 4 to 8 carbon atoms in the alkyl groups. The preferred alkyl methacrylate is t-butyl methacrylate which is anionically polymerized as described in U.S. Patent 5,002,676.

Monolithium compounds, oligomers and polymers form a polylithium initiator by crosslinking the core Y which comprises a compound having at least two independently polymerized vinyl groups. Examples of compounds having two or more vinyl groups that independently polymerize include divinylsilane, divinylbenzene, trivinylbenzene, and tetravinylsilane. Compounds having one vinyl group, such as styrene, or two conjugated vinyl groups, such as butadiene and isoprene, may be polymerized with or prior to the compound having two or more independent vinyl groups as long as the compounds crosslink into a core Y having at least three active lithium sites.

The living star polymers are preferably terminated with hydroxyl groups by reaction with ethylene oxide, a protected hydroxystyrene monomer, or ethylene oxide followed by addition of epichlorohydrin. Termination with ethylene oxide is most preferred and results in addition of aliphatic hydroxyl groups at the lithium sites and release of fine particles after neutralization as described in U.S. Patent No. 5,166,277. The fine particles interfere with hydrogenation of the polymer and preferably are removed prior to hydrogenation.

Hydrogenation of at least 90%, preferably at least 95%, of the unsaturation in the A blocks or segments is achieved with nickel catalysts as described in U.S. Patents Nos. Re. 27,145, 4,970,254, and 5,166,277. The preferred nickel catalyst is a mixture of nickel 2-ethylhexanoate and triethylaluminium described in more detail below.

Following addition of hydroxyl groups, the polymers of the invention have the following structure: <chemistry id="chem0002" num="0002"><img file="EP0632075A2_D0002.tif" /></chemistry> wherein each A is a hydrogenated or unsaturated block or segment comprising a preponderance of a polymerized conjugated diene having a peak molecular weight from 400 to 40,000 as measured by GPC, t is from 2 to 30 and represents the number of polymeric arms having terminal hydroxyl groups, and (HO―)_u―Y-(―B)_r is the residue of a polylithium initiator wherein B is the hydrogenated or unsaturated residue of a monolithium conjugated diene polymer having a peak molecular weight from 1,500 to 15,000, Y is a crosslinked core comprising a compound having at least two independently polymerized vinyl groups, r &gt; t, and 0 &lt; u &lt; (r-t).

Star polymers having two or more terminal hydroxyl groups can be used with a minimum amount of solvents at room temperature when the viscosity of the polymer is less than 5,000 poise. The hydroxyl groups capping arms grown from the core unexpectedly do not exhibit significant atomic attractions that would gel the star polymers. Hydrogenated butadiene polymers having a lower viscosity than 5,000 poise are produced by limiting the peak molecular weight to a range from 1,000 to 10,000 and by limiting the 1,2-addition to an amount between 40% to 60%.

The polymers of the present invention are useful in making adhesives (including pressure sensitive adhesives, contact adhesives, laminating adhesives and assembly adhesives), sealants, coatings, films (such as those requiring heat and solvent resistance), printing plates, fibres, and as modifiers for polyesters, polyurethanes, polyethers and polyamides. The polymers are also useful in asphalt modification. In addition to the star polymers and conventional curing aids or agents, products formulated to meet performance requirements for particular applications may include various combinations of ingredients including adhesion promoting or tackifying resins, plasticizers, fillers, solvents, and stabilizers.

Generally, if a hydrogenation step is used, sufficient improvement of the chemical and heat stability of the final product should be achieved to justify the extra expense and effort involved. For greatest heat stability, all of the olefinic double bonds (ODB), anyplace in the polymer, should be removed so that less than 1 Meq of ODB per gram of polymer remain, more preferably less than 0.6 Meq/g, and most preferably less than about 0.3 Meq/g of polymer.

Molecular weights of linear polydienes are conveniently measured by Gel Permeation Chromatography (GPC), where the GPC system has been appropriately calibrated. Polymers of known molecular weight are used to calibrate and these must be of the same molecular structure and chemical composition as the unknown linear polymers or segments that are to be measured. For anionically polymerized linear polymers, the polymer is essentially monodisperse and it is both convenient and adequately descriptive to report the "peak" molecular weight of the narrow molecular weight distribution observed. Measurement of the true molecular weight of the final coupled star polymer is not as straightforward or as easy to make using GPC. This is because the star shaped molecules do not separate and elute through the packed GPC columns in the same manner as do the linear polymers used for the calibration, and, hence, the time of arrival at a UV or refractive index detector is not a good indicator of the molecular weight. A good analytical method to use for a star polymer is to measure the weight average molecular weight by light scattering techniques. The sample is dissolved in a suitable solvent at a concentration less than 1.0 gram of sample per 100 millilitres of solvent and filtered using a syringe and porous membrane filters of less than 0.5 microns pore size directly into the light scattering cell. The light scattering measurements are performed as a function of scattering angle and of polymer concentration using standard procedures. The differential refractive index (DRI) of the sample is measured at the same wavelength and in the same solvent used for the light scattering.

The polymers of the invention preferably comprise homopolymer blocks of hydrogenated butadiene that have Structure II with an average of from 2 to 10 terminal hydroxyl groups per molecule, wherein the peak molecular weight of each hydrogenated block A is from 500 to 3,000, the peak molecular weight of each hydrogenated block B is from 3,000 to 7,000, and the peak molecular weight of the star molecules is from 30,000 to 150,000.

The peak molecular weights of the hydrogenated butadiene blocks are very important for obtaining a low viscosity polymer for ease of application. The ranges of 500 to 3,000 and 3,000 to 7,000 are preferred because arms in this range will be at or very near the absolute minimum in viscosity.

Example 1

A polymer was prepared having Structure II shown on page 5, where A and B were polybutadienes radiating from a divinylbenzene core (Y). We charged 1800 grams of cyclohexane into a clean, 1 gallon, stirred, stainless steel autoclave. In a glove box were weighed 120 grams of diethyl ether, .06 moles of sec-butyllithium, and 29.3 grams of an 80% divinylbenzene (DVB) solution (a mixture of meta and para isomers), into three separate pressure vessels. The ether and sec-butyllithium reagents were added to the autoclave under nitrogen pressure at 25-30°C. Then 300 grams of 1,3-butadiene was added to the reactor in three 100 gram increments. Each increment was allowed to polymerize until the exotherm had subsided before the next increment was added.

After all of the butadiene was added, a sample of the polybutadiene (Sample I), was collected into a nitrogen purged bottle which contained methanol. The temperature of the reactor was increased to 50-55°C. The divinylbenzene reagent was added under nitrogen pressure to the reactor. The coupling reaction was allowed to proceed for one hour. At this point, the solution was a bright orange-red. Another sample (Sample II), the DVB-coupled star polymer, was removed into a nitrogen-purged bottle containing methanol. After one hour of DVB reaction, 500 ppm of 1,2-diethoxy-ethane was added from a pressure vessel under nitrogen to the reactor, followed by 60 grams of butadiene. We allowed the final increment of butadiene to react 1.25 hours. A sample (Sample III), the "inside-out" star polymer, was taken into a nitrogen-purged bottle containing methanol. Dry ethylene oxide (65 grams, 1.47 mol), was added to the reactor from a lecture bottle. This mixture was allowed to stir several hours. We then added 5-10 ml of methanol to the reactor from a pressure vessel. A final sample of the polymer solution (Sample IV), the "inside/out" star polyol, was taken. Samples I-IV were retained for analysis for hydroxyl content and molecular weight by ¹³C NMR and gel permeation chromatography, respectively.

The peak molecular weight of Sample I was 4,300. The peak molecular weight of Sample II was 31,000, which indicates that the initial star polymer had approximately seven arms. The peak molecular weight of Sample III was 34,000 and analysis by ¹³C NMR showed 87% of the polybutadiene arms which coupled grew back out of the core in the second polymerization step. In other words, there were 87% of the still active lithium sites in the coupled divinyl-benzene core which were available to initiate butadiene. Of the arms which grew back out, NMR analysis showed approximately 98% of those arms had a hydroxyl end group.

For hydrogenation, 2,000 grams of the star polyol cement were heated, in a 1 gallon, stainless steel autoclave, to 40°C, and briefly sparged with high pressure hydrogen. The reactor was sealed and pressured with high pressure hydrogen. An aliquot of preformed nickel/aluminium catalyst (2:1 Al/Ni) prepared from the reaction of nickel 2-ethylhexanoate and triethylaluminium, containing approximately 7,000 ppm nickel, was added to the reactor. The catalyst was prepared in a cyclohexane solution and 16 cc was added to the reactor. The reaction exothermed rapidly to 50°C. The pressure of hydrogen in the reactor was 6.5 bar (800 psig). The pressure began to drop noticeably during the reaction. The experiment was continued by the addition, at regular intervals, of 16 cc aliquots of the nickel/aluminium catalyst. Each increment of catalyst added approximately 45 ppm of nickel to the reaction solution, and a total of 900 ppm nickel was added to the reaction solution. The reaction was continued for a total of five hours.

The maximum temperature of the reactor was 89°C. After five hours the heat was turned off, and the reactor was allowed to sit overnight under 3.7-5.1 bar (500-600 psig) of hydrogen. The reactor was then heated to 63°C and we added 180 ppm more nickel. The maximum temperature of the reactor was 85.6°C, and we allowed the reaction to proceed for 7 hours.

After allowing the solution to cool, we placed it into a stirred glass vessel and contacted the solution with 1% aqueous sulphuric acid. Several washes were necessary to remove the black colour from the polymer solution. A check of the polymer solution with test strips specific for Ni(2+) did not indicate the presence of nickel. The polymer solution was stripped of solvent and dried thoroughly. An analysis of the polymer using an ozonolysis technique revealed that the polymer contained 1.89 meq/g of residual unsaturation. This number corresponds to 90% saturation of the double bonds in the molecule. Analysis by ¹³C NMR revealed only 5% remaining unsaturation. Results are listed in Table 1.

Example 2

An unsaturated star diol was made in a similar fashion to Example 1, using the same amounts of all reagents, except that a portion of the monolithium initiator was found to be inactive. Samples I-IV were taken during the experiment as in Example 1. The samples were analyzed for hydroxyl content and molecular weight by ¹³C NMR and gel permeation chromatography respectively, prior to hydrogenation.

The peak molecular weight (Mp) of Sample I was 13,000. The Mp of Sample II was 238,500, and the Mp of Sample III was 337,000. The star had approximately 18 arms, and ¹³C NMR showed that 17% of the lithium sites in the core initiated butadiene growth. Of the arms which grew out, 67% contained an hydroxyl end-group. Results are shown in Table 1.

This polymer could be hydrogenated using the same procedures described in Example 1 to give a saturated star diol.

Example 3 (Comparison)

This example compares the results of the present invention to a star polyol which is produced in accordance with European Patent Application No. 0516.203.

The comparison radial polymer has the following structure    Y-(A¹-eI)_n where Y is a divinylbenzene core, A¹ is polyethylene/butylene (hydrogenated polybutadiene), eI is epoxidized polyisoprene and n is 15-20. The arm molecular weight is approximately 3,900. The arm consists of a hydrogenated butadiene polymer attached to the DVB core on one end and attached to a 370 MW polyisoprene block on the other end. The overall molecular weight of the star polymer is approximately 85,000.

This polymer was made by making a star polymer with butadiene-isoprene arms, partially hydrogenating the polymer as described in European application No. 0516.203 to fully hydrogenate the butadiene segments and partially hydrogenate the isoprene segments, and then epoxidizing the polymer as described in the European application No. 0516.203 to produce the above polymer which has 0.6 meq of epoxy groups in the isoprene segments. The polymer was reacted with alcohol and boron trifluoride diethyl etherate as follows:    The 25 grams of polymer was dissolved to 10% by weight in a mixture of 55% toluene, 30% cyclohexane, and 15% Solketal, the reactor was purged with nitrogen and a solution of boron trifluoride diethyl etherate in 15 millilitres of toluene was added dropwise at room temperature. Exotherms of 3 to 4°C were observed. The solution was stirred at room temperature. The solution was then washed with an excess (150 volume percent) of aqueous sodium carbonate and then water, precipitated in isopropanol and then dried at 35-50°C under vacuum. Titrations for residual epoxy and ¹H NMR analysis were performed. The catalyst (in the solvent) was added dropwise to the polymer and Solketal solution at room temperature. Fifteen minutes after all of the catalyst was added, the polymer cement was washed with dilute aqueous base and then water. The majority of the solvent was removed by evaporation in a hood and the polymer was further dried under vacuum.

The epoxidized star polymer was initially reacted under the conditions that had been most effective, namely 10% solids and 85:15 cyclohexane/toluene:Solketal at room temperature using boron trifluoride diethyl etherate as the catalyst. As expected, the analytical results were consistent with substantial conversion of epoxy groups to the ether-triol. Derivatization could also be accomplished by adding Solketal and catalyst to the washed cement (epoxidized polymer in the solvent in which it was epoxidized, usually cyclohexane). The dibutyl etherate was used as the catalyst since the diethyl etherate was insoluble in cyclohexane. There was no evidence of the residual water in the cement interfering with the reaction in any way.

Titration, ¹H NMR, FTIR and GPC were performed as described previously. Spectroscopic results consistent with conversion to the ether- triol were obtained. Only 10-20% dimer is formed and little, if any, higher coupled products as determined by GPC. The extent of reaction indicates that about 1.3-2 derivatized repeat units (DE) are present per arm (25-37 per molecule), that is 4-6 hydroxyl groups per arm (75-112 per molecule), at least 1/3 of which are primary. Analytical results are shown in Table 1. <tables id="tabl0001" num="0001"><table frame="all"><title>Table 1</title><tgroup cols="4" colsep="1" rowsep="0"><colspec colnum="1" colname="col1" colwidth="39.37mm" /><colspec colnum="2" colname="col2" colwidth="39.37mm" /><colspec colnum="3" colname="col3" colwidth="39.37mm" /><colspec colnum="4" colname="col4" colwidth="39.37mm" /><thead valign="top"><row><entry namest="col1" nameend="col4" align="center">Viscosity of Hydroxylated Star Polymers</entry></row><row><entry namest="col1" nameend="col1" align="left">Example</entry><entry namest="col2" nameend="col2" align="center">1</entry><entry namest="col3" nameend="col3" align="center">2</entry><entry namest="col4" nameend="col4" align="center">3 (Comp.)</entry></row><row><entry namest="col1" nameend="col1" align="left">Peak Molecular Weights</entry><entry namest="col2" nameend="col2" /><entry namest="col3" nameend="col3" /><entry namest="col4" nameend="col4" /></row></thead><tbody valign="top"><row><entry namest="col1" nameend="col1" align="left">Uncoupled Arms (Sample 1)</entry><entry namest="col2" nameend="col2" align="right">4,300</entry><entry namest="col3" nameend="col3" align="char" char=",">13,000</entry><entry namest="col4" nameend="col4" align="char" char=",">3,900</entry></row><row><entry namest="col1" nameend="col1" align="left">Unsaturated Star (Sample 3)</entry><entry namest="col2" nameend="col2" align="right">34,000</entry><entry namest="col3" nameend="col3" align="char" char=",">337,000</entry><entry namest="col4" nameend="col4" align="char" char=",">--</entry></row><row><entry namest="col1" nameend="col1" align="left">Partial Saturated Star</entry><entry namest="col2" nameend="col2" align="right">--</entry><entry namest="col3" nameend="col3" align="char" char=",">--</entry><entry namest="col4" nameend="col4" align="char" char=",">85,000</entry></row></tbody></tgroup><tgroup cols="4" colsep="1" rowsep="0"><colspec colnum="1" colname="col1" colwidth="39.37mm" /><colspec colnum="2" colname="col2" colwidth="39.37mm" /><colspec colnum="3" colname="col3" colwidth="39.37mm" /><colspec colnum="4" colname="col4" colwidth="39.37mm" /><thead valign="top"><row><entry namest="col1" nameend="col1" align="left">Viscosity, Poise</entry><entry namest="col2" nameend="col2" /><entry namest="col3" nameend="col3" /><entry namest="col4" nameend="col4" /></row></thead><tbody valign="top"><row><entry namest="col1" nameend="col1" align="left">Unsaturated Star (Sample 3)</entry><entry namest="col2" nameend="col2" align="right">849</entry><entry namest="col3" nameend="col3" align="char" char=",">32,500</entry><entry namest="col4" nameend="col4" align="char" char=",">--</entry></row><row><entry namest="col1" nameend="col1" align="left">Unsaturated Polyol/Diol (Sample 4)</entry><entry namest="col2" nameend="col2" align="right">766</entry><entry namest="col3" nameend="col3" align="char" char=",">8,900</entry><entry namest="col4" nameend="col4" align="char" char=",">--</entry></row><row><entry namest="col1" nameend="col1" align="left">Partial Saturated Star</entry><entry namest="col2" nameend="col2" align="right">--</entry><entry namest="col3" nameend="col3" align="char" char=",">--</entry><entry namest="col4" nameend="col4" align="char" char=",">5,700</entry></row><row><entry namest="col1" nameend="col1" align="left">Saturated Star Epoxy</entry><entry namest="col2" nameend="col2" align="right">--</entry><entry namest="col3" nameend="col3" align="char" char=",">--</entry><entry namest="col4" nameend="col4" align="char" char=",">6,100</entry></row><row rowsep="1"><entry namest="col1" nameend="col1" align="left">Saturated Star Polyol</entry><entry namest="col2" nameend="col2" align="right">10,000</entry><entry namest="col3" nameend="col3" align="char" char=",">--</entry><entry namest="col4" nameend="col4" align="char" char=",">27,700</entry></row></tbody></tgroup></table></tables> It is well known that the addition of hydroxyl groups to hydro-carbon small molecules and polymers increases their viscosity through hydrogen bonding as shown in Comparative Example 3. The greater the number of hydroxyls per molecular weight, the greater the viscosity, e.g. ethylene glycol is much more viscous than ethanol which is much more viscous than ethane. In Comparative Example 3, the addition of non-hydrogen bonding epoxy groups to a typical star polymer increases the viscosity by only 5%. However the modification of the epoxy groups to form hydroxyl groups increases the viscosity by almost a factor of five as expected. Surprisingly, the addition of hydroxyl groups to the base star polymers in Examples 1 and 2 does not result in increased viscosity. In Example 2 there is a substantial reduction in the viscosity after the addition of hydroxyl groups. This unexpected result is apparently due to placement of hydroxyl groups on the cores of the star polymer molecules which promote intramolecular association of the hydroxyl groups on the ends of the polymeric arms. The special placement of the hydroxyls in polymers of Examples 1 and 2 therefore, gives them advantages both in their synthesis and in lower viscosity in the final product over typical star polymers containing hydroxyl groups such as Comparative Example 3.

Example 4

A clear, elastomeric, two-component, ambient temperature curing, polyurethane coating was prepared with the star polyol of Example 1 as follows. MONDUR MR (MONDUR is a trade mark) (from Miles, Inc.) is an aromatic polyisocyanate having an NCO equivalent weight of 197. The hydroxyl equivalent weight of the star polyol was assumed to be 6,000. <tables id="tabl0002" num="0002"><table frame="all"><tgroup cols="2" colsep="1" rowsep="0"><colspec colnum="1" colname="col1" colwidth="78.75mm" /><colspec colnum="2" colname="col2" colwidth="78.75mm" /><thead valign="top"><row><entry namest="col1" nameend="col1" align="left">Composition, pbw</entry><entry namest="col2" nameend="col2" align="center">1</entry></row></thead><tbody valign="top"><row><entry namest="col1" nameend="col1" align="left">Star Polyol of Example 1</entry><entry namest="col2" nameend="col2" align="right">6,000</entry></row><row><entry namest="col1" nameend="col1" align="left">MONDUR MR</entry><entry namest="col2" nameend="col2" align="right">197</entry></row><row rowsep="1"><entry namest="col1" nameend="col1" align="left">Toluene</entry><entry namest="col2" nameend="col2" align="right">429</entry></row></tbody></tgroup></table></tables>

First 6,000 parts by weight (pbw) of the star polyol were dissolved in toluene. Then, 197 pbw of MONDUR MR was added and the coating was immediately applied onto steel panels (QD412 panels from Q-Panel Corp.). The solution gelled about 1 hour after adding the isocyanate. The coated panels were dried/cured 1 week at room temperature before testing. The dry film thickness of the coatings was 50 microns. The composition gave a clear, soft, elastomeric coating having low adhesion. Composition 1 had the slight yellow colour characteristic of aromatic isocyanates.

Example 5

Clear, elastomeric coatings are prepared with the star polyol of Example 1 cured with a melamine resin in a bake-cured formulation as follows. <tables id="tabl0003" num="0003"><table frame="all"><tgroup cols="4" colsep="1" rowsep="0"><colspec colnum="1" colname="col1" colwidth="39.37mm" /><colspec colnum="2" colname="col2" colwidth="39.37mm" /><colspec colnum="3" colname="col3" colwidth="39.37mm" /><colspec colnum="4" colname="col4" colwidth="39.37mm" /><thead valign="top"><row><entry namest="col1" nameend="col1" align="left">Composition, %w</entry><entry namest="col2" nameend="col2" align="right">1</entry><entry namest="col3" nameend="col3" align="center">2</entry><entry namest="col4" nameend="col4" align="center">3</entry></row></thead><tbody valign="top"><row><entry namest="col1" nameend="col1" align="left">Star Polyol of Example 1</entry><entry namest="col2" nameend="col2" align="right">90</entry><entry namest="col3" nameend="col3" align="right">80</entry><entry namest="col4" nameend="col4" align="right">70</entry></row><row><entry namest="col1" nameend="col1" align="left">CYMEL 303</entry><entry namest="col2" nameend="col2" align="right">9</entry><entry namest="col3" nameend="col3" align="right">18</entry><entry namest="col4" nameend="col4" align="right">27</entry></row><row rowsep="1"><entry namest="col1" nameend="col1" align="left">CYCAT 600</entry><entry namest="col2" nameend="col2" align="right">1</entry><entry namest="col3" nameend="col3" align="right">2</entry><entry namest="col4" nameend="col4" align="right">3</entry></row></tbody></tgroup></table></tables> The compositions are prepared at 65%w solids content in a solvent blend containing 90%w xylene and 10%w n-butyl alcohol. The coatings are applied onto steel panels (QD412 panels from Q-Panel Corp) and are dried/cured for 20 minutes at 175°C. The following properties were measured. <tables id="tabl0004" num="0004"><table frame="all"><tgroup cols="4" colsep="1" rowsep="0"><colspec colnum="1" colname="col1" colwidth="39.37mm" /><colspec colnum="2" colname="col2" colwidth="39.37mm" /><colspec colnum="3" colname="col3" colwidth="39.37mm" /><colspec colnum="4" colname="col4" colwidth="39.37mm" /><thead valign="top"><row><entry namest="col1" nameend="col1" align="left">Property</entry><entry namest="col2" nameend="col2" align="right">1</entry><entry namest="col3" nameend="col3" align="right">2</entry><entry namest="col4" nameend="col4" align="right">3</entry></row></thead><tbody valign="top"><row><entry namest="col1" nameend="col1" align="left">Thickness, mil</entry><entry namest="col2" nameend="col2" align="right">1.0</entry><entry namest="col3" nameend="col3" align="right">1.0</entry><entry namest="col4" nameend="col4" align="right">1.0</entry></row><row><entry namest="col1" nameend="col1" align="left">Pencil Hardness</entry><entry namest="col2" nameend="col2" align="right">&lt;4B</entry><entry namest="col3" nameend="col3" align="right">3B</entry><entry namest="col4" nameend="col4" align="right">1B</entry></row><row><entry namest="col1" nameend="col1" align="left">MEK Double Rubs</entry><entry namest="col2" nameend="col2" align="right">60</entry><entry namest="col3" nameend="col3" align="right">40</entry><entry namest="col4" nameend="col4" align="right">30</entry></row><row><entry namest="col1" nameend="col1" align="left">Crosshatch Adhesion</entry><entry namest="col2" nameend="col2" align="right">5</entry><entry namest="col3" nameend="col3" align="right">5</entry><entry namest="col4" nameend="col4" align="right">3</entry></row><row><entry namest="col1" nameend="col1" align="left">Gloss</entry><entry namest="col2" nameend="col2" align="left">High</entry><entry namest="col3" nameend="col3" align="left">High</entry><entry namest="col4" nameend="col4" align="left">Fair</entry></row><row rowsep="1"><entry namest="col1" nameend="col1" align="left">Clarity</entry><entry namest="col2" nameend="col2" align="left">Clear</entry><entry namest="col3" nameend="col3" align="left">Opaque</entry><entry namest="col4" nameend="col4" align="left">Opaque</entry></row></tbody></tgroup></table></tables> Before baking, all coatings were very tacky, viscous liquids. After baking, all coatings were elastic solids having moderate MEK Double Rub Resistance, indicating that all coatings did indeed cure. Results show that the optimum level of melamine crosslinker is 10-20 %w. Below 10%w, the coating will be very soft (pencil hardness &lt;4B). Above 20%w, the coating will have limited adhesion (crosshatch adhesion &lt;3) and lower gloss.

Example 6

The star polyol of Example 1 is reacted into an isocyanate crosslinker and this is used to crosslink an acrylic polyol, a polyester polyol and a polyether polyol to give rubber toughened coatings. The equivalent weights used in calculating the appropriate compositions are the following. <tables id="tabl0005" num="0005"><table frame="all"><tgroup cols="2" colsep="1" rowsep="0"><colspec colnum="1" colname="col1" colwidth="78.75mm" /><colspec colnum="2" colname="col2" colwidth="78.75mm" /><thead valign="top"><row><entry namest="col1" nameend="col1" /><entry namest="col2" nameend="col2" align="center">Equivalent Weight</entry></row></thead><tbody valign="top"><row><entry namest="col1" nameend="col1" align="left">Star Polyol of Example 1</entry><entry namest="col2" nameend="col2" align="right">6,000</entry></row><row><entry namest="col1" nameend="col1" align="left">DESMODUR Z-4370</entry><entry namest="col2" nameend="col2" align="right">365</entry></row><row><entry namest="col1" nameend="col1" align="left">Acrylic Polyol</entry><entry namest="col2" nameend="col2" align="right">500</entry></row><row><entry namest="col1" nameend="col1" align="left">Polyester Polyol</entry><entry namest="col2" nameend="col2" align="right">500</entry></row><row rowsep="1"><entry namest="col1" nameend="col1" align="left">Polyether Polyol</entry><entry namest="col2" nameend="col2" align="right">500</entry></row></tbody></tgroup></table></tables> The following compositions are prepared. <tables id="tabl0006" num="0006"><table frame="all"><tgroup cols="4" colsep="1" rowsep="0"><colspec colnum="1" colname="col1" colwidth="39.37mm" /><colspec colnum="2" colname="col2" colwidth="39.37mm" /><colspec colnum="3" colname="col3" colwidth="39.37mm" /><colspec colnum="4" colname="col4" colwidth="39.37mm" /><thead valign="top"><row><entry namest="col1" nameend="col1" align="left">Composition, %w</entry><entry namest="col2" nameend="col2" align="center">1</entry><entry namest="col3" nameend="col3" align="center">2</entry><entry namest="col4" nameend="col4" align="center">3</entry></row></thead><tbody valign="top"><row><entry namest="col1" nameend="col1" align="left">Star Polyol of Example 1</entry><entry namest="col2" nameend="col2" align="char" char=".">6.5</entry><entry namest="col3" nameend="col3" align="char" char=".">6.5</entry><entry namest="col4" nameend="col4" align="char" char=".">6.5</entry></row><row><entry namest="col1" nameend="col1" align="left">DESMODUR Z-4370</entry><entry namest="col2" nameend="col2" align="char" char=".">39.3</entry><entry namest="col3" nameend="col3" align="char" char=".">39.3</entry><entry namest="col4" nameend="col4" align="char" char=".">39.3</entry></row><row><entry namest="col1" nameend="col1" align="left">DBTDL</entry><entry namest="col2" nameend="col2" align="char" char=".">0.2</entry><entry namest="col3" nameend="col3" align="char" char=".">0.2</entry><entry namest="col4" nameend="col4" align="char" char=".">0.2</entry></row><row><entry namest="col1" nameend="col1" align="left">Acrylic Polyol</entry><entry namest="col2" nameend="col2" align="char" char=".">54.0</entry><entry namest="col3" nameend="col3" /><entry namest="col4" nameend="col4" /></row><row><entry namest="col1" nameend="col1" align="left">Polyester Polyol</entry><entry namest="col2" nameend="col2" /><entry namest="col3" nameend="col3" align="char" char=".">54.0</entry><entry namest="col4" nameend="col4" /></row><row rowsep="1"><entry namest="col1" nameend="col1" align="left">Polyether Polyol</entry><entry namest="col2" nameend="col2" /><entry namest="col3" nameend="col3" /><entry namest="col4" nameend="col4" align="char" char=".">54.0</entry></row></tbody></tgroup></table></tables> First, 6.5 pbw of the star polyol of Example 1 are combined with 39.3 pbw of DESMODUR Z-4370 (DESMODUR is trade mark) (from Miles, Inc.) and 0.2 pbw dibutyl tin dilaurate (DBTDL) catalyst in a jar. This is mixed on a roller for several days to prepare the rubber modified, isocyanate crosslinker. The NCO/OH ratio in the rubber modified crosslinker was 100/1. Coatings are then prepared by adding 54 pbw of the acrylic polyol, the polyester polyol or the polyether polyol to the rubber modified, isocyanate crosslinker. The NCO/OH ratio in these coatings is 1/1. These two-component, clear coatings must be applied to the substrate fairly soon after combining the rubber modified crosslinker and the polyol since the pot life of the coating will be only several hours. The coatings will cure on the substrate to give hazy, rubber toughened, impact resistant coatings.

Example 7

A flexible crosslinker is prepared by reaction of the star polyol of Example 1 with isophorone diisocyanate (IPDI). This is then used to crosslink a polybutadiene diol (Bd-diol) or a hydrogenated polybutadiene diol (EB-diol) to give a polyurethane for use in sealants and binders. The equivalent weights used for the star polyol, IPDI and the Bd-diol or EB-diol are 6,000, 111, and 1,000, respectively.

The flexible crosslinker is prepared by combining 63.5 pbw of the star polyol of Example 1, 4.7 pbw of IPDI (from Hüls, Inc.) and .02 pbw of DBTDL in a resin kettle, heating at 80°C and stirring for 4 hours under a dry nitrogen purge. IPDI is used at a 4/1 NCO/OH excess to prevent gellation during the reaction. The flexible crosslinker is then cooled to 50°C and 31.8 pbw of either the Bd-diol or the EB-diol is added. After 5 minutes of mixing, the mixture is pumped into place where it cures to give an elastomeric sealant or binder. Other formulating ingredients (such as tackifying resins, plasticizers, fillers, stabilizers, propellants, etc.) can be added to the flexible crosslinker or to the diol prior to mixing of the two reactants.

Example 8

A moisture curing, clear, elastomeric coating is made from the star polyol of Example 1 terminated with hexane diisocyanate (HDI). The isocyanate terminated prepolymer is prepared by combining 94.7 pbw of the star polyol of Example 1 with 5.3 pbw of HDI (from Miles, Inc.) and 0.02 pbw of DBTDL in a resin kettle, heating to 80°C and stirring for 4 hours under a dry nitrogen purge. HDI is used at a 4/1 NCO/OH excess to prevent gellation during the reaction. Unreacted excess HDI is removed by vacuum stripping to give the isocyanate terminated prepolymer. This prepolymer is diluted with 20 pbw of xylene and applied to aluminium. After aging at ambient conditions for 1 month, the prepolymer cures via ambient moisture to give a clear, elastomeric coating.

Example 9

A moisture curing, elastomeric formulation is prepared from the isocyanate terminated prepolymer of Example 8 as follows. The composition is made by mixing 100 pbw of the prepolymer of Example 8, 50 pbw toluene, 100 pbw of WINGTACK 95 hydrocarbon tackifying resin (from Goodyear) and 100 pbw of ATOMITE calcium carbonate (from Thompson Weiman) in a sigma blade mixer under a dry nitrogen blanket. It is required that the material be packaged with critical exclusion of moisture until the package is opened for use. The material is useful as a moisture curable, polyurethane/urea sealant, caulk or coating.

Example 10

An acrylate terminated prepolymer is prepared from the isocyanate terminated prepolymer of Example 8 as follows. 98.1 pbw of the prepolymer of Example 8, 1.9 pbw of hydroxy ethyl acrylate and 0.01 pbw of DBTDL are combined in a resin kettle, heated to 80°C and stirred for 4 hours under a dry nitrogen purge to give the acrylate terminated polymer. This prepolymer is useful in coatings, sealants and adhesives which are cured by free radical processes, initiated for example by peroxides or radiation.