Tough heat-shrinkable multilayer film

BACKGROUND OF THE INVENTION

0001Heat shrinkable polymer films have gained substantial acceptance for such uses as the packaging of meats and other articles of food. This description will detail the usage of films for packaging meat; it being understood that these films are also suitable for packaging other products such as frozen foods and cheeses. Some of the films embodying this invention are normally used as heat shrinkable bags supplied to the meat packer with one open end, to be closed and sealed-after insertion or the meat After the product is inserted, air is normally evacuated, the open end of the bag is closed, such as by heat sealing, or applying a metal clip, and finally heat is applied, such as by hot water, to initiate film shrinkage about the meat.

0002In subsequent processing of the meat, the bag may be opened and the meat removed for further cutting of the meat into user cuts, for retail sale, for example, or for institutional use.

0003Successful shrink bags must satisfy a multiplicity of requirements imposed by both the bag producer and the bag user. Of primary importance to the bag user is the capability of the bag to survive physically intact the process of being filled, evacuated, sealed closed, and heat shrunk. The bag must also be strong enough to survive the material handling involved in moving the contained meat, which may weigh 45.4 kg (100 pounds) or more, along the distribution system to the next processor, or to the user. Frequently, the meat will have protruding bones that will puncture shrink bags that are not sufficiently strong. Thus, the bag must be strong enough to physically protect the meat.

0004It is also highly desirable to the bag user that the bag serve as a barrier to infusion of gaseous material from the surrounding environment. Of particular importance is provision of an effective barrier to infusion of oxygen, since oxygen is well known to cause spoilage of meat.

0005The bag producer requires a product which can be produced competitively while meeting the performance requirements of the user. Thus, the bag material should be readily extrudable, and susceptible to cross-linking by irradiation, with sufficient leeway in process parameters as to allow for efficient film production. The process should also be susceptible to efficient extended production operations. In the irradiation process, the film produced must have improved strength while the inner layer maintains sufficient sealability.

0006It is important to users of shrink bags that once the meat or other food article is placed in the bag, the bag can be heat sealed to form an air tight bond. Generally, the heat seal is formed by applying heat and pressure to the opposing sides of the bag mouth until the opposing inner layers of the film have fused together.

0007One of the problems encountered when heat sealing bags made from multiple layer films is that the sealing process causes the film to become deformed in the area where the heat is applied..A solution to this problem known in the art has been to cross-link the film layers by irradiation prior to heat sealing. Cross-linking the film provides improved toughness and increases the heat seal temperature range.

0008However, cross-linked thermoplastic films are more difficult to melt and produce weaker seals than unirradiated films when heat sealed. Users require that the seals maintain their integrotu when the bag containing meat or other food article is immersed in hot water to shrink the film. A bag with weak heat seals that rupture when the bag is shrunk, is of no use. Thus, there is a need for an irradiated multiple layer film which can be made into a bag that will have strong seals when heat sealed.

0009It is known that heat shrinkable bags for food packaging may be made from multiple layer films in which individual layers have different degrees of cross-linking. Such multiple layer films have been fabricated by forming and irradiating the layers individually and then laminating or extrusion coating the layers to form the multiple layer film. These multiple step fabrication methods produce a more costly film.

0010<patcit id="pcit0001" dnum="CA1125229"><text>Canadian Patent, 1,125,229</text></patcit> discloses a film structure having a heat sealable inner layer and an outer layer wherein the outer layer is cross-linked to a larger extent then the heat sealable layer. The differential cross-linking is achieved by adding a cross-linking enhancer compound to the outer layer, forming the structure, and then irradiating. The irradiation enhancer allows the irradiation dosage to be lowered to a point where the heat sealable inner layer is not adversely affected in its heat sealing characteristics by the radiation. However, the lower irradiation dosage does not produce a bag with the strength and toughness required by users.

0011<patcit id="pcit0002" dnum="US4724176A"><text>U.S. Patent No. 4,724,176</text></patcit> to Sun discloses a heat shrinkable container having an unirradiated inner layer, a barrier layer and an irradiated outer layer. This film is coextruded and the outer layer is irradiated by precisely controlling the depth of material that the electron beam irradiation penetrates. This invention limits the crosslinking to the outer layer and therefore, does not improve the strength of the inner layer by cross-linking.

0012<patcit id="pcit0003" dnum="US5055328A"><text>U.S. Patent No. 5,055,328</text></patcit> to Evert discloses a multiple layer film in which the inner layer contains an antioxidant cross-linking inhibitor to control the degree of cross-linking.

0013<patcit id="pcit0004" dnum="US4894107A"><text>U.S. Patent No. 4,894,107</text></patcit> to Tse discloses oriented or unoriented multiple layerfilms with barrier layers that are irradiated for cross-linking. This invention does not teach the selection of polymers for individual layers with different degrees of cross-linking when irradiated.

0014<patcit id="pcit0005" dnum="US4734327A"><text>US 4,734,327 (Vicik</text></patcit>) describes an irradiated three layer heat shrinkable plastic film comprising an EVOH-Nylon core layer as an oxygen barrier, a fast outer layer comprising a blend of EVA and C₆-C₈ olefin type LLDPE and a second outer layer comprising EVA.

0015<patcit id="pcit0006" dnum="US4985188A"><text>US 4,985,188</text></patcit> (Ishio <i>et al</i>) describes a process for producing a cross laminated film by forming a laminate comprising a polyolefin resin, an oxygen barrier, an adhesive shrinkable resin layer and a sealing resin layer, Irradiating the laminate so as the polyolefin resin has specified gel fraction levels at various portions, and stretching the cross linked laminate.

0016<patcit id="pcit0007" dnum="DE2925205"><text>DE 2925205 (Bayer</text></patcit>) describes a hot sealable foil obtained by irradiating one side of a cross linkable polymer foil of such an intensity that the foil is cross linked on the irradiated side of the foil and not cross linked on the non-irradiated side.

0017<patcit id="pcit0008" dnum="US4724176A"><text>US 4,724,176 (Sun</text></patcit>) describes a process for manufacturing a container by coextruding a middle tube of material having a low oxygen transmission rate between outer and inner tubes of olefin polymers from a multilayered tube.

0018Many of the multilayer heat shrinkable films with an uncross-linked inner layer and a cross-linked outer layer previously known in the art were made by extruding the outer layer separately from the inner layer. After the outer layer was extruded and irradiated, it would be laminated with the inner layer and any other additional layers to form the multilayer film. In the present invention, the additional expense of separately extruding the irradiated and unirradiated layers and then laminating the layers together is avoided. All of the layers of the films in the present invention can be coextruded and the entire film structure can be exposed to EB radiation. Such films would be widely accepted by those skilled in the art and meet with substantial commercial success.

0019It is an object of this invention to provide multiple layer cross-linked films with improved sealability and toughness. It is a further object of this invention to provide a coextruded multiple layer cross-linked film having these improvements after subjecting the fabricated multiple layer film structure to a single dose of irradiation. Another object of this invention is to provide a meat or food article packaging bag that will maintain the integrity of heat seals when it is shrunk wrapped.

0020It should be understood that the objectives stated in or inferred from this specification do not limit the invention as defined in the claims.

0021Irradiation of polymers causes the formation of covalent bonds between different polymer chains. This process is called "cross-linking". The overall effect of cross-linking is that the molecular weight of the polymer steadily increases with dose, leading to branched chains, until ultimately a tri-dimensional network is formed. This three dimensional network is referred to as the "gel fraction". The gel fractions disclosed herein have been determinea in accoraance with ASTM D2765. The gel fraction molecules are insoluble while the unlinked molecules remain soluble and are referred to as the "sol fraction". These molecules are separated from the network although they may be highly branched and can be extracted from the bulk polymer by a process that uses a proper solvent. Thus, the gel fraction can be easily measured to determine the extent of cross-linking for various radiation doses.

0022It has been known in the art that irradiation of polymeric multiple layer films cross-links the layers and produces a film with improved toughness and strength. However, cross-linking also raises the normal melting temperature of a polymer and consequently reduces the heat sealability. Surprisingly, it has been found in the practice of this invention that by the selection of different polymers for the various layers of a multiple layer film, it is possible to have extensive cross-linking in one layer and a minimum amount of cross-linking in another layer when the film is irradiated. This allows the outer layer of a multiple layer film to be cross-linked to provide increased strength and toughness while the inner layer is not cross-linked and retains its heat sealability characteristics.

SUMMARY OF THE INVENTION

0023The multiple layer films in the invention have inner heat sealant layers and outer protective layers that have different degrees of cross-linking when subjected to electron beam irradiation. More significantly, these films experience incipient cross-linking at different levels of irradiation doses. Thus, by the selection of the materials for the protective and heat sealant layers as taught by this invention, it is possible to form an irradiated multiple layer film having a protective layer with significant crosslinking and a heat sealant layer with only minimal cross-linking.

0024The irradiation serves at least two significant purposes. First, it enhances the heat resistance of the protective layer of the film. This is evidenced by reduced failure rates in packages which have been heat shrunk or heat sealed. Second, the timing of the irradiation, treatment being after the formation of the multiple layer film, substantial freedom is available in selecting the process for fabricating the multiple layer film. Thus the processes which tend to yield higher interfacial adhesion, such as coextrusion, are preferred. Because more desirable formation processes can be used, the resulting films may have substantially improved interfacial adhesion over similar films made by less desirable processes.

0025The amount of cross-linking in the protective and heat sealant layers is measured by the gel fraction of the material after irradiation. The higher the gel fraction, the greater the amount of cross-linking. Irradiation doses of from about 2 MR to about 10 MR are usea to cross-link the films of this invention. The most preferred irradiation dose for the invention is from about 4 MR to about 6 MR. Within this range, the protective layer undergoes significant cross-linking that makes the film tougher and gives it added strength, while the heat sealant layer undergoes an insignificant amount of cross-linking and maintains its heat sealability.

0026A substantial end use for the films of the invention is in the fabrication of heat sealable shrink bags that are particularly useful in the packaging of meat, especially meat having bony projections or large cavities. Bags made according to this invention find particular utility in forming packages which are subjected to high temperature shrinking processes.

0027The bags produced from the films in this invention have the following advantages over bags known to the art: 1) the bags are tougher and exhibit superior puncture resistance; 2) the bags have a higher heat seal strength: 3) the bags have a higher burst value; and 4) the increased toughness and higher heat seal strength allow the bag machines to be operated at faster speeds.

BRIEF DESCRIPTION OF THE DRAWINGS

0028<ul id="ul0001" list-style="none" compact="compact"><li><figref idref="f0001">FIG. 1</figref> is a cross-sectional view of a three-layer film of the present invention.</li><li><figref idref="f0001">FIG. 2</figref> is a cross-sectional view of a five-layer film of the present invention.</li><li><figref idref="f0002">FIG. 3</figref> is a plan view of a bag made according to the invention.</li><li><figref idref="f0002">FIG. 4</figref> is a cross-sectional view of the bag of <figref idref="f0002">FIG. 3</figref> taken at 2-2 of <figref idref="f0002">FIG. 3</figref>.</li><li><figref idref="f0002">FIG. 5</figref> is a cross-sectional view of the bag of <figref idref="f0002">FIG. 3</figref> taken at 2-2 of <figref idref="f0002">FIG. 3</figref>, except the film is a 5 layer structure.</li><li><figref idref="f0003">FIG. 6</figref> is a graph of gel fraction versus radiation dose for EVA and ULDPE.</li></ul>

DETAILED DESCRIPTION OF THE INVENTION

0029According to the present invention, it has been found that good heat sealability can be obtained in a multilayer film that has been irradiated. In one embodiment of the invention, a material in the inner heat sealant layer, such as ultra low density polyethylene (ULDPE), low density polyethylene (LDPE), linear low density polyethylene (LLDPE), very low density polyethylene (VLDPE), or ionomers, such as Surlyn, having incipient cross-linking at a higher radiation dose level than the material in the outer protective layer, produces an irradiated film with superior heat sealability. The inner sealant layer is comprised of a copolymer of at least 50% ULDPE, LDPE, LLDPE, VLDPE or ionomers. The ULDPE is commercially available from Dow Chemical Company under the trade name Dow 4201 and the EVA resin is commercially available from Exxon as XV-97.06, LD-306.09, LD-318.92 or LD-701.06 and DuPont as ELVAX 3129. Interposed between the inner and outer layers is a gas barrier layer.

0030In this invention, the outer layer comprises at least 80% to 90% EVA resin.

0031The multiple layer films of this invention are subjected to electron beam (EB) radiation with preferred doses in the range of from about 2 megarads to about 10 megarads (MR).

0032In another preferred embodiment of this invention, the films are subjected to EB radiation doses of from about 2 MR to about 6 MR.

0033In a particularly preferred embodiment of this invention, the films are subjected to EB radiation doses of from about 4 to about 6 MR.

0034The multiple layer films of this invention are comprised of at least two layers. In a more preferred embodiment, the film is provided with an oxygen or flavor barrier core layer. The oxygen or flavor barrier layer is preferably a vinylidene chloride copolymer such as methylacrylate - polyvinylidene chloride (MA-PVdC) or ethylene vinyl alcohol (EVOH). However, it is not limited to these materials. There may also be present in the film an oxygen absorbing or oxygen scavenging material. Examples of such materials are disclosed in <patcit id="pcit0009" dnum="US4536409A"><text>U.S. Patent Nos. 4,536,409</text></patcit> and <patcit id="pcit0010" dnum="US4702966A"><text>4,702,966</text></patcit> to Farrell, <patcit id="pcit0011" dnum="US4856650A"><text>U.S. Patent No. 4,856,650</text></patcit> to Inoure, <patcit id="pcit0012" dnum="US4919984A"><text>U.S. Patent No. 4,919,984</text></patcit> to Maruhashi, <patcit id="pcit0013" dnum="US5021515A"><text>U.S. Patent No. 5,021,515</text></patcit> to Cochran, and <patcit id="pcit0014" dnum="US4877664A"><text>U.S. Patent No. 4,877,664</text></patcit> to Maeda and <patcit id="pcit0015" dnum="US761490A" dnum-type="L"><text>U.S. Patent Application Serial No. 07/761,490</text></patcit> by Kim, In addition to the oxygen or flavor barrier layer and inner and outer layers, the film can also be comprised of adhesive layers and additional layers to improve the strength and toughness of the films.

0035The multiple layer films in the invention can be fabricated by conventional processes known in the art. These films can be either oriented or unoriented. A preferred process includes the steps of coextrusion of the layers to be oriented, followed by orientation in one of the conventional processes such as blown tubular orientation or stretch orientation in the form of a continuous sheet; both being molecular orientation processes. Once the multiple layer film has been formed and oriented, it is subjected to electron beam irradiation.

0036One of the advantages of the films of the present invention is that they can be coextruded and there is no need to laminate layers. Similar films known In the prior art were produced by extruding the outer layer and cross-linking it by irradiation before laminating it onto the Inner layer which had been extruded separately. Thus, the ability to coextrude the inner and outer layers of the films of the present invention and expose the entire film structure to EB radiation provides the user with a significant cost savings.

0037The amount of electron beam irradiation Is adjusted, depending on the make-up of the specific film to be treated and the end use requirements. While virtually any amount of irradiation will induce some cross-linking, a minimum level of at least 1.5 megarads is usually preferred in order to achieve desired levels of enhancement of the hot strength of the film and to expand the range of temperatures at which satisfactory heat seals may be formed. While treatment up to about 50 megarads can be tolerated, there is usually no need to use more than 10 meaarads, so this is a preferred upper level of treatment; a preferred dosage being from about 2 megarads to about 6 megarads and the most preferred dosage being from about 4 megarads to about 6 megarads.

0038The film is subjected to electron beam irradiation only after the multiple layer film has been formed, and after molecular orientation, in those embodiments where the film is molecularly oriented. It should be noted that, in the irradiation step, all of the layers in the film are exposed simultaneously to the irradiation source, such that irradiation of all the layers of the film takes place simultaneously.

0039<figref idref="f0001">FIG. 1</figref> shows a three layer coextruded film made according to the invention. Layer 14 is a barrier layer which minimizes the transmission of oxygen through the film. The preferred barrier material is MA-PVdC, EVOH, nylon or a VdC-VC copolymer. Layer 16 is the heat sealant layer and it is composed of a polymer having a low degree of cross-linking when subjected to irradiation. A preferred material for the heat sealant layer is ULDPE sold by Dow Chemical Company as Dow 4201. However, other copolymers, polymers and blends thereof with high dosage incipient cross-linking characteristics may be used (for example Exxon's Exact polymer and Mitsui's TAFMER). Layer 18 is the outer protective layer composed of a blend of at least from about 80% to about 90% EVA and from about 10% to about 20% ULDPE, VLDPE, LDPE, LLDPE or ionomers. The EVA in these blends can be comprised of one or more different types of EVA. One preferred blend is comprised of Exxon's LD-701.06 EVA or DuPont's ELVAX 3129 EVA, Dow Chemical's ATTANE 4201 ULDPE and Exxon's LD-318.92.

0040<figref idref="f0001">FIG. 2</figref> shows a five layer coextruded film made according to the invention. Layer 114 is a barrier layer similar to layer 14. Layer 116 is a neat sealant layer similar to layer 16. Layer 118 is an outer protective layer similar to layer 18. Layer 120 is a first protective-adhesive layer composed of a blend of an EVA copolymer, preferably an EVA resin with 10% VA. Layer 122 is a second protective-adhesive layer comprising a polyethylene copolymer, preferably ULDPE, VLDPE, LDPE, LLDPE or ionomers such as Surlyn. The additional layers in the five layer film structure provide added adhesion, strength, heat resistance and toughness.

0041Preferred EVA's are those having 6% to 12% vinyl acetate (VA) content and having incipient cross-linking occur at about 1 to 2 MR and a gel fraction of at least 0.15 at 6 MR. Most preferred EVA's are EVA's having a vinyl acetate content of about 10%.

0042Preferred materials for the heat sealant layer are those having incipient cross-linking occur at about 5 MR or higher.

0043<figref idref="f0002">FIG. 3</figref> shows a bag 10 made according to the invention. The empty bag shown is a collapsed, biaxially oriented tube with one end closed by a heat seal 12 across the one end of the tube. The other end of the bag is open for insertion of meat or other food article, and it is normally closed and sealed when the meat or food article is put into the bag.

0044The cross-section of the bag in <figref idref="f0002">FIG. 4</figref> shows a typical structure where the bag 10 is made from a three-layer coextruded plastic film. The heat seal 12 is formed by the application of heat and pressure to fuse the heat sealant layers 16 of the two multiple layer films that form the opposing walls of the bag 10.

0045The cross-section of the bag in <figref idref="f0002">FIG. 5</figref> shows a typical structure where the bag 110 is made from a five-layer coextruded film. The heat seal 112 is formed by the application of heat and pressure to fuse the heat sealant layers 116 of the two multiple layer films that form the opposing walls of the bag 110.

0046The overall thickness of films of this invention is nominally the same as the thickness of conventional films. Films are generally about 0.051 mm (2.0 mils) thick with a normal range of 0.025 mm to 0.102 mm (1.0 to 4.0 mils.) Films thinner than 0.025 mm (1.0 mils) tend to be too weak to perform all required functions. Films thicker than 0.102 mm (4.0 mils) are economically unable to compete with thinner competitive films.

0047Table A shows the structure of typical 3-layer films of this invention. <tables id="tabl0001" num="0001"><table frame="all"><title>TABLE A</title><tgroup cols="4"><colspec colnum="1" colname="col1" colwidth="26mm" /><colspec colnum="2" colname="col2" colwidth="31mm" /><colspec colnum="3" colname="col3" colwidth="30mm" /><colspec colnum="4" colname="col4" colwidth="22mm" /><thead><row><entry namest="col1" nameend="col4" align="center" valign="top">THICKNESS AND STRUCTURE OF TYPICAL THREE LAYER FILMS</entry></row><row><entry valign="top">1. LAYER</entry><entry valign="top">MATERIAL</entry><entry align="center" valign="top">THICKNESS mm</entry><entry align="center" valign="top">(x 10^-2 Mils)</entry></row></thead><tbody><row rowsep="0"><entry>Sealant</entry><entry>ULDPE</entry><entry align="center">0.0279</entry><entry align="center">110</entry></row><row rowsep="0"><entry>Barrier</entry><entry>MA-PVdC</entry><entry align="center">0.0076</entry><entry align="center">30</entry></row><row rowsep="0"><entry>Protective</entry><entry>EVA/ULDPE</entry><entry rowsep="1" align="center">0.020</entry><entry rowsep="1" align="center">80</entry></row><row><entry /><entry /><entry align="center">0.056</entry><entry align="center">220</entry></row></tbody></tgroup><tgroup cols="4"><colspec colnum="1" colname="col1" colwidth="26mm" /><colspec colnum="2" colname="col2" colwidth="31mm" /><colspec colnum="3" colname="col3" colwidth="30mm" /><colspec colnum="4" colname="col4" colwidth="22mm" /><thead><row><entry valign="top">2. LAYER</entry><entry valign="top">MATERIAL</entry><entry align="center" valign="top">THICKNESS mm</entry><entry align="center" valign="top">(x 10^-2 Mils)</entry></row></thead><tbody><row rowsep="0"><entry>Sealant</entry><entry>ULDPE</entry><entry align="center">0.025</entry><entry align="center">100</entry></row><row rowsep="0"><entry>Barrier</entry><entry>EVOH</entry><entry align="center">0.0076</entry><entry align="center">30</entry></row><row rowsep="0"><entry>Protective</entry><entry>EVA/ULDPE</entry><entry rowsep="1" align="center">0.025</entry><entry rowsep="1" align="center">100</entry></row><row><entry /><entry /><entry align="center">0.058</entry><entry align="center">230</entry></row></tbody></tgroup><tgroup cols="4"><colspec colnum="1" colname="col1" colwidth="26mm" /><colspec colnum="2" colname="col2" colwidth="31mm" /><colspec colnum="3" colname="col3" colwidth="30mm" /><colspec colnum="4" colname="col4" colwidth="22mm" /><thead><row><entry valign="top">3. LAYER</entry><entry valign="top">MATERIAL</entry><entry align="center" valign="top">THICKNESS mm</entry><entry align="center" valign="top">(x 10^-2 Mils)</entry></row></thead><tbody><row rowsep="0"><entry>Sealant</entry><entry>ULDPE/EVA</entry><entry align="center">0.020</entry><entry align="center">80</entry></row><row rowsep="0"><entry>Barrier</entry><entry>MA-PVdC</entry><entry align="center">0.0076</entry><entry align="center">30</entry></row><row rowsep="0"><entry>Protective</entry><entry>EVA/ULDPE/EVA</entry><entry rowsep="1" align="center">0.020</entry><entry rowsep="1" align="center">80</entry></row><row><entry /><entry /><entry align="center">0.048</entry><entry align="center">190</entry></row></tbody></tgroup><tgroup cols="4"><colspec colnum="1" colname="col1" colwidth="26mm" /><colspec colnum="2" colname="col2" colwidth="31mm" /><colspec colnum="3" colname="col3" colwidth="30mm" /><colspec colnum="4" colname="col4" colwidth="22mm" /><thead><row><entry valign="top">4. LAYER</entry><entry valign="top">MATERIAL</entry><entry align="center" valign="top">THICKNESS mm</entry><entry align="center" valign="top">(x 10^-2 Mils)</entry></row></thead><tbody><row rowsep="0"><entry>Sealant</entry><entry>ULDPE/EVA</entry><entry align="center">0.0023</entry><entry align="center">90</entry></row><row rowsep="0"><entry>Barrier</entry><entry>EVOH</entry><entry align="center">0.0076</entry><entry align="center">30</entry></row><row rowsep="0"><entry>Protective</entry><entry>EVA/ULDPE/EVA</entry><entry rowsep="1" align="center">0.015</entry><entry rowsep="1" align="center">60</entry></row><row><entry /><entry /><entry align="center">0.046</entry><entry align="center">180</entry></row></tbody></tgroup></table></tables>

0048Table B shows the structure of typical 5-layer films of this invention. <tables id="tabl0002" num="0002"><table frame="all"><title>TABLE B</title><tgroup cols="4"><colspec colnum="1" colname="col1" colwidth="30mm" /><colspec colnum="2" colname="col2" colwidth="30mm" /><colspec colnum="3" colname="col3" colwidth="29mm" /><colspec colnum="4" colname="col4" colwidth="21mm" /><thead><row><entry namest="col1" nameend="col4" align="center" valign="top">THICKNESS AND STRUCTURE OF TYPICAL FIVE LAYER FILMS</entry></row><row><entry valign="top">1. LAYER</entry><entry valign="top">MATERIAL</entry><entry align="center" valign="top">THICKNESS mm</entry><entry align="center" valign="top">(x 10^-2 Mils)</entry></row></thead><tbody><row rowsep="0"><entry>Sealant</entry><entry>ULDPE</entry><entry align="center">0.0076</entry><entry align="center">30</entry></row><row rowsep="0"><entry>Second Protective</entry><entry>EVA</entry><entry align="center">0.0279</entry><entry align="center">110</entry></row><row rowsep="0"><entry>Barrier</entry><entry>MA-PVdC</entry><entry align="center">0.0076</entry><entry align="center">30</entry></row><row rowsep="0"><entry>Adhesive</entry><entry>ULDPE</entry><entry align="center">0.0076</entry><entry align="center">30</entry></row><row rowsep="0"><entry>First Protective</entry><entry>EVA/ULDPE</entry><entry rowsep="1" align="center">0.0076</entry><entry rowsep="1" align="center">30</entry></row><row><entry /><entry /><entry align="center">0.058</entry><entry align="center">230</entry></row></tbody></tgroup><tgroup cols="4"><colspec colnum="1" colname="col1" colwidth="30mm" /><colspec colnum="2" colname="col2" colwidth="30mm" /><colspec colnum="3" colname="col3" colwidth="29mm" /><colspec colnum="4" colname="col4" colwidth="21mm" /><thead><row><entry valign="top">2. LAYER</entry><entry valign="top">MATERIAL</entry><entry align="center" valign="top">THICKNESS mm</entry><entry align="center" valign="top">(x 10^-2 Mils)</entry></row></thead><tbody><row rowsep="0"><entry>Sealant</entry><entry>ULDPE</entry><entry align="center">0.020</entry><entry align="center">80</entry></row><row rowsep="0"><entry>Second Protective</entry><entry>EVA/ULDPE</entry><entry align="center">0.0076</entry><entry align="center">30</entry></row><row rowsep="0"><entry>Barrier</entry><entry>MA-PVdC</entry><entry align="center">0.0076</entry><entry align="center">30</entry></row><row rowsep="0"><entry>Adhesive</entry><entry>ULDPE</entry><entry align="center">0.0076</entry><entry align="center">30</entry></row><row rowsep="0"><entry>First Protective</entry><entry>EVA/ULDPE/EVA</entry><entry rowsep="1" align="center">0.015</entry><entry rowsep="1" align="center">60</entry></row><row><entry /><entry /><entry align="center">0.058</entry><entry align="center">230</entry></row></tbody></tgroup><tgroup cols="4"><colspec colnum="1" colname="col1" colwidth="30mm" /><colspec colnum="2" colname="col2" colwidth="30mm" /><colspec colnum="3" colname="col3" colwidth="29mm" /><colspec colnum="4" colname="col4" colwidth="21mm" /><thead><row><entry valign="top">3. LAYER</entry><entry valign="top">MATERIAL</entry><entry align="center" valign="top">THICKNESS mm</entry><entry align="center" valign="top">(x 10^-2 Mils)</entry></row></thead><tbody><row rowsep="0"><entry>Sealant</entry><entry>ULDPE/EVA</entry><entry align="center">0.015</entry><entry align="center">60</entry></row><row rowsep="0"><entry>Second Protective</entry><entry>EVA/ULDPE/EVA</entry><entry align="center">0.0076</entry><entry align="center">30</entry></row><row rowsep="0"><entry>Barrier</entry><entry>EVOH</entry><entry align="center">0.010</entry><entry align="center">40</entry></row><row rowsep="0"><entry>Adhesive</entry><entry>ULDPE/EVA</entry><entry align="center">0.0076</entry><entry align="center">30</entry></row><row rowsep="0"><entry>First Protective</entry><entry>EVA/ULDPE/EVA</entry><entry rowsep="1" align="center">0.015</entry><entry rowsep="1" align="center">60</entry></row><row><entry /><entry /><entry align="center">0.056</entry><entry align="center">220</entry></row></tbody></tgroup><tgroup cols="4"><colspec colnum="1" colname="col1" colwidth="30mm" /><colspec colnum="2" colname="col2" colwidth="30mm" /><colspec colnum="3" colname="col3" colwidth="29mm" /><colspec colnum="4" colname="col4" colwidth="21mm" /><thead><row><entry valign="top">4. LAYER</entry><entry valign="top">MATERIAL</entry><entry align="center" valign="top">THICKNESS mm</entry><entry align="center" valign="top">(x 10^-2 Mils)</entry></row></thead><tbody><row rowsep="0"><entry>Sealant</entry><entry>ULDPE/EVA</entry><entry align="center">0.020</entry><entry align="center">80</entry></row><row rowsep="0"><entry>Second Protective</entry><entry>EVA/ULDPE</entry><entry align="center">0.015</entry><entry align="center">60</entry></row><row rowsep="0"><entry>Barrier</entry><entry>EVOH</entry><entry align="center">0.0051</entry><entry align="center">20</entry></row><row rowsep="0"><entry>Adhesive</entry><entry>ULDPE/EVA</entry><entry align="center">0.0076</entry><entry align="center">30</entry></row><row rowsep="0"><entry>First Protective</entry><entry>EVA/ULDPE/EVA</entry><entry rowsep="1" align="center">0.670</entry><entry rowsep="1" align="center">80</entry></row><row><entry /><entry /><entry align="center">0.068</entry><entry align="center">270</entry></row></tbody></tgroup></table></tables>

0049Table C shows the gel fractions for ULDPE and EVA at various irradiation doses. These results are plotted on a graph as shown in <figref idref="f0003">FIG. 6</figref>. <tables id="tabl0003" num="0003"><table frame="all"><title>TABLE C</title><tgroup cols="3"><colspec colnum="1" colname="col1" colwidth="52mm" /><colspec colnum="2" colname="col2" colwidth="16mm" /><colspec colnum="3" colname="col3" colwidth="14mm" /><thead><row><entry align="center" valign="top">IRRADIATION EB, DOSE, MRAD</entry><entry namest="col2" nameend="col3" align="left" valign="top">GEL FRACTION</entry></row><row><entry align="center" valign="top" /><entry align="center" valign="top">ULDPE</entry><entry align="center" valign="top">EVA</entry></row></thead><tbody><row rowsep="0"><entry align="right">2</entry><entry align="char" char=".">0.03</entry><entry align="char" char="." charoff="14">0.18</entry></row><row rowsep="0"><entry align="right">3</entry><entry align="char" char=".">0.03</entry><entry align="char" char="." charoff="14">0.42</entry></row><row rowsep="0"><entry align="right">4</entry><entry align="char" char=".">0.02</entry><entry align="char" char="." charoff="14">0.38</entry></row><row rowsep="0"><entry align="right">5</entry><entry align="char" char=".">0.03</entry><entry align="char" char="." charoff="14">0.50</entry></row><row rowsep="0"><entry align="right">6</entry><entry align="char" char=".">0.04</entry><entry align="char" char="." charoff="14">0.50</entry></row><row rowsep="0"><entry align="right">8</entry><entry align="char" char=".">0.35</entry><entry align="char" char="." charoff="14">0.62</entry></row><row rowsep="0"><entry align="right">10</entry><entry align="char" char=".">0.41</entry><entry align="char" char="." charoff="14">0.66</entry></row><row><entry align="right">15</entry><entry align="char" char=".">0.56</entry><entry align="char" char="." charoff="14">0.75</entry></row></tbody></tgroup></table></tables>

0050It is to be understood that the films and the materials disclosed above as well as other films and materials which are apparent in view of this specification are not to be considered a limitation of the present invention, the scope of which is defined by the claims.

THE EXAMPLES

0051To determine the physical properties of various five layer film structures, twelve films were fabricated. These twelve films are listed in Table D and the materials of the individual layers and the irradiation dosage they were exposed to are shown for each. (Note films 1 B, 2B, 6B and 8B are not listed because good heat seals could not be formed for these structures.) Also, listed as sample number nine is a three layer film known in the prior art that was used as a control for comparing the test results of the five layer films.

0052The twelve five layer films and the three layer control film were tested to determine tear strength, percent haze, gloss, puncture resistance, minimum sealing temperature, seal durability and impact strength. Film samples 4A, 4B, 7A and 7B represent film structures of the present invention with 7A and 7B being preferred structures. <tables id="tabl0004" num="0004"><table frame="all"><title>TABLE D</title><tgroup cols="7"><colspec colnum="1" colname="col1" colwidth="23mm" /><colspec colnum="2" colname="col2" colwidth="25mm" /><colspec colnum="3" colname="col3" colwidth="23mm" /><colspec colnum="4" colname="col4" colwidth="24mm" /><colspec colnum="5" colname="col5" colwidth="24mm" /><colspec colnum="6" colname="col6" colwidth="24mm" /><colspec colnum="7" colname="col7" colwidth="25mm" /><thead><row><entry namest="col1" nameend="col7" align="center" valign="top">COMPOSITION OF SAMPLE MULTILAYER FILMS</entry></row><row><entry align="center" valign="top">SAMPLE NO.</entry><entry align="center" valign="top">OUTER PROTECTIVE LAYER</entry><entry align="center" valign="top">OUTER TIE LAYER</entry><entry align="center" valign="top">OXYGEN BARRIER LAYER</entry><entry align="center" valign="top">INNER TIE LAYER</entry><entry align="center" valign="top">INNER SEALANT LAYER</entry><entry align="center" valign="top">IRRADIATION (DOSAGE)</entry></row></thead><tbody><row rowsep="0"><entry align="center">1A</entry><entry align="center">3651</entry><entry align="center">3651</entry><entry align="center">3649</entry><entry align="center">3651</entry><entry align="center">XV-97.06</entry><entry>Medium</entry></row><row rowsep="0"><entry align="center">2A</entry><entry align="center">3651</entry><entry align="center">3651</entry><entry align="center">3649</entry><entry align="center">3651</entry><entry align="center">306.09</entry><entry>Medium</entry></row><row rowsep="0"><entry align="center">3A</entry><entry align="center">3651</entry><entry align="center">3651</entry><entry align="center">3649</entry><entry align="center">3651</entry><entry align="center">318.92</entry><entry>Medium</entry></row><row rowsep="0"><entry align="center">3B</entry><entry align="center">3651</entry><entry align="center">3651</entry><entry align="center">3649</entry><entry align="center">3651</entry><entry align="center">318.92</entry><entry>High</entry></row><row rowsep="0"><entry align="center">4A</entry><entry align="center">3651</entry><entry align="center">3651</entry><entry align="center">3649</entry><entry align="center">3651</entry><entry align="center">4201</entry><entry>Medium</entry></row><row rowsep="0"><entry align="center">4B</entry><entry align="center">3651</entry><entry align="center">3651</entry><entry align="center">3649</entry><entry align="center">3651</entry><entry align="center">4201</entry><entry>High</entry></row><row rowsep="0"><entry align="center">5A</entry><entry align="center">3651</entry><entry align="center">4201</entry><entry align="center">3649</entry><entry align="center">XV-97.06</entry><entry align="center">306.09</entry><entry>Medium</entry></row><row rowsep="0"><entry align="center">5B</entry><entry align="center">3651</entry><entry align="center">4201</entry><entry align="center">3649</entry><entry align="center">XV-97.06</entry><entry align="center">306.09</entry><entry>High</entry></row><row rowsep="0"><entry align="center">6A</entry><entry align="center">3651</entry><entry align="center">4201</entry><entry align="center">3649</entry><entry align="center">XV-97.06</entry><entry align="center">318.92</entry><entry>Medium</entry></row><row rowsep="0"><entry align="center">7A</entry><entry align="center">3651</entry><entry align="center">4201</entry><entry align="center">3649</entry><entry align="center">XV-97.06</entry><entry align="center">4201</entry><entry>Medium</entry></row><row rowsep="0"><entry align="center">7B</entry><entry align="center">3651</entry><entry align="center">4201</entry><entry align="center">3649</entry><entry align="center">XV-97.06</entry><entry align="center">4201</entry><entry>High</entry></row><row rowsep="0"><entry align="center">8A</entry><entry align="center">3651</entry><entry align="center">4201</entry><entry align="center">3649</entry><entry align="center">XV-97.06</entry><entry align="center">XV-97.06</entry><entry>Medium</entry></row><row><entry align="center">9</entry><entry align="center">3651</entry><entry align="center">-</entry><entry align="center">3649</entry><entry align="center">-</entry><entry align="center">3651</entry><entry>Medium</entry></row><row rowsep="0"><entry namest="col1" nameend="col7" align="left">WHERE:</entry></row><row rowsep="0"><entry namest="col1" nameend="col7" align="left">Medium irradiation dosage is between 4 and 5.5 megarads and high irradiation dosage is between 5.5 and 6.5 megarads.</entry></row><row rowsep="0"><entry namest="col1" nameend="col7" align="left">3651 - is an EVA1/ULDPE/EVA2 blend. EVA1 is an EVA copolymer such as Exxon LD-701.06, XV-97.06, 318.92 or DuPont ELVAX 3129: ULDPE is a ULDPE copolymer such as Dow ATTANE 4201 and EVA2 is an EVA copolymer such as Exxon LD-318.92, LD-701.06, XV-97.06 or DuPont ELVAX 3129.</entry></row><row rowsep="0"><entry namest="col1" nameend="col7" align="left">4201 - is an ethylene alpha-olefin copolymer manufactured by Dow Chemical Company and sold as ATTANE 4201. XV-97.06 - is an EVA copolymer manufactured by Exxon Chemical Co. with 10% vinyl acetate (VA) and a melt index of 0.3.</entry></row><row rowsep="0"><entry namest="col1" nameend="col7" align="left">LD-306.09 - is an EVA copolymer manufactured by Exxon Chemical Co. with 5.8% VA and a melt index of 2.0. LD-318.92 - is an EVA copolymer manufactured by Exxon Chemical Co. with 9.0% VA and a melt index of 2.2. 3649 - is a Saran comprised of a mehtylacrylate - polyvinylidene chloride copolymer.</entry></row><row><entry namest="col1" nameend="col7" align="left">ELVAX 3129 - is an EVA copolymer manufactured by DuPont having 10% VA and a melt index of 0.35 g/10 min. LD-701.06 - is an EVA copolymer manufactured by Exxon having 10% VA and a melt index of 0.19 g/10 min.</entry></row></tbody></tgroup></table></tables>

TEAR STRENGTH TEST

0053The comparative tear strengths of the films was measured using an Elmendorf DigiTear Tester, Model No. 65-200, available from Thwing-Albert Instrument Company, Philadelphia, Pennsylvania.

0054The test consisted of; 1) preparing seven representative samples of each film; 2) clamping a test specimen in the TAIR clamps of the tester; 3) slitting the film with a razor blade to initiate a slit: 4) releasing the pendulum of the tester which exerts a force on the opposing sides of the slit; and 5) recording the digital readout values of the tester. The digital readout value is the amount of force required to tear the film and it is measured in grams.

0055Table E below shows the results of the tear strength tests for seven specimens of each of the twelve five layer films and the three-layer control film. Each of the specimens was tested for tear strength in the machine direction (MD) and the cross-machine direction (CMD) and the results were averaged. The results indicate that the film structures of the present invention (samples 4A, 4B, 7A and 7B) have above average tear strengths, especially in the machine direction. <tables id="tabl0005" num="0005"><table frame="none"><title><u style="single">TABLE E</u></title><tgroup cols="7" colsep="0"><colspec colnum="1" colname="col1" colwidth="26mm" /><colspec colnum="2" colname="col2" colwidth="11mm" /><colspec colnum="3" colname="col3" colwidth="13mm" /><colspec colnum="4" colname="col4" colwidth="11mm" /><colspec colnum="5" colname="col5" colwidth="13mm" /><colspec colnum="6" colname="col6" colwidth="11mm" /><colspec colnum="7" colname="col7" colwidth="13mm" /><thead><row><entry namest="col1" nameend="col7" align="center" valign="top"><b>TEAR STRENGTH TEST</b></entry></row><row rowsep="0"><entry namest="col1" nameend="col7" align="left" valign="top">Tear strength is measured in grams.</entry></row><row><entry namest="col1" nameend="col7" rowsep="0" align="left" valign="top" /></row><row rowsep="0"><entry align="center" valign="top"><b>SAMPLE NO:</b></entry><entry namest="col2" nameend="col3" rowsep="1" align="center" valign="top"><b>1A</b></entry><entry namest="col4" nameend="col5" rowsep="1" align="center" valign="top"><b>2A</b></entry><entry namest="col6" nameend="col7" rowsep="1" align="center" valign="top"><b>3A</b></entry></row><row rowsep="0"><entry align="center" valign="top" /><entry rowsep="1" align="center" valign="top"><b>MD</b></entry><entry rowsep="1" align="center" valign="top"><b>CMD</b></entry><entry rowsep="1" align="center" valign="top"><b>MD</b></entry><entry rowsep="1" align="center" valign="top"><b>CMD</b></entry><entry rowsep="1" align="center" valign="top"><b>MD</b></entry><entry rowsep="1" align="center" valign="top"><b>CMD</b></entry></row></thead><tbody><row rowsep="0"><entry /><entry align="right">128</entry><entry align="right">96</entry><entry align="right">112</entry><entry align="right">112</entry><entry align="right">128</entry><entry align="right">128</entry></row><row rowsep="0"><entry /><entry align="right">96</entry><entry align="right">128</entry><entry align="right">112</entry><entry align="right">48</entry><entry align="right">112</entry><entry align="right">128</entry></row><row rowsep="0"><entry /><entry align="right">112</entry><entry align="right">144</entry><entry align="right">112</entry><entry align="right">48</entry><entry align="right">112</entry><entry align="right">112</entry></row><row rowsep="0"><entry /><entry align="right">112</entry><entry align="right">112</entry><entry align="right">112</entry><entry align="right">96</entry><entry align="right">128</entry><entry align="right">144</entry></row><row rowsep="0"><entry /><entry align="right">128</entry><entry align="right">128</entry><entry align="right">112</entry><entry align="right">80</entry><entry align="right">112</entry><entry align="right">112</entry></row><row rowsep="0"><entry /><entry align="right">112</entry><entry align="right">128</entry><entry align="right">96</entry><entry align="right">112</entry><entry align="right">112</entry><entry align="right">96</entry></row><row rowsep="0"><entry /><entry rowsep="1" align="right">112</entry><entry rowsep="1" align="right">144</entry><entry rowsep="1" align="right">96</entry><entry rowsep="1" align="right">112</entry><entry rowsep="1" align="right">96</entry><entry rowsep="1" align="right">128</entry></row><row rowsep="0"><entry><b>AVERAGE:</b></entry><entry align="right">114</entry><entry align="right">126</entry><entry align="right">107</entry><entry align="right">87</entry><entry align="right">114</entry><entry align="right">121</entry></row><row rowsep="0"><entry /><entry align="right" /><entry align="right" /><entry align="right" /><entry align="right" /><entry align="right" /><entry align="right" /></row></tbody></tgroup><tgroup cols="7" colsep="0"><colspec colnum="1" colname="col1" colwidth="26mm" /><colspec colnum="2" colname="col2" colwidth="11mm" /><colspec colnum="3" colname="col3" colwidth="13mm" /><colspec colnum="4" colname="col4" colwidth="11mm" /><colspec colnum="5" colname="col5" colwidth="13mm" /><colspec colnum="6" colname="col6" colwidth="11mm" /><colspec colnum="7" colname="col7" colwidth="13mm" /><thead><row><entry rowsep="0" valign="top"><b>SAMPLE NO:</b></entry><entry namest="col2" nameend="col3" align="center" valign="top"><b>3B</b></entry><entry namest="col4" nameend="col5" align="center" valign="top"><b>4A</b></entry><entry namest="col6" nameend="col7" align="center" valign="top"><b>4B</b></entry></row><row><entry rowsep="0" valign="top" /><entry align="center" valign="top"><b>MD</b></entry><entry align="center" valign="top"><b>CMD</b></entry><entry align="center" valign="top"><b>MD</b></entry><entry align="center" valign="top"><b>CMD</b></entry><entry align="center" valign="top"><b>MD</b></entry><entry align="center" valign="top"><b>CMD</b></entry></row></thead><tbody><row rowsep="0"><entry /><entry align="right">116</entry><entry align="right">132</entry><entry align="right">152</entry><entry align="right">64</entry><entry align="right">160</entry><entry align="right">184</entry></row><row rowsep="0"><entry /><entry align="right">128</entry><entry align="right">100</entry><entry align="right">148</entry><entry align="right">140</entry><entry align="right">176</entry><entry align="right">72</entry></row><row rowsep="0"><entry /><entry align="right">120</entry><entry align="right">104</entry><entry align="right">156</entry><entry align="right">64</entry><entry align="right">160</entry><entry align="right">172</entry></row><row rowsep="0"><entry /><entry align="right">112</entry><entry align="right">128</entry><entry align="right">180</entry><entry align="right">132</entry><entry align="right">148</entry><entry align="right">120</entry></row><row rowsep="0"><entry /><entry align="right">120</entry><entry align="right">100</entry><entry align="right">184</entry><entry align="right">76</entry><entry align="right">172</entry><entry align="right">76</entry></row><row rowsep="0"><entry /><entry align="right">120</entry><entry align="right">104</entry><entry align="right">156</entry><entry align="right">96</entry><entry align="right">152</entry><entry align="right">152</entry></row><row rowsep="0"><entry /><entry rowsep="1" align="right">124</entry><entry rowsep="1" align="right">124</entry><entry rowsep="1" align="right">172</entry><entry rowsep="1" align="right">120</entry><entry rowsep="1" align="right">176</entry><entry rowsep="1" align="right">56</entry></row><row rowsep="0"><entry><b>AVERAGE:</b></entry><entry align="right">120</entry><entry align="right">113</entry><entry align="right">164</entry><entry align="right">99</entry><entry align="right">163</entry><entry align="right">119</entry></row><row rowsep="0"><entry /><entry align="right" /><entry align="right" /><entry align="right" /><entry align="right" /><entry align="right" /><entry align="right" /></row></tbody></tgroup><tgroup cols="7" colsep="0"><colspec colnum="1" colname="col1" colwidth="26mm" /><colspec colnum="2" colname="col2" colwidth="11mm" /><colspec colnum="3" colname="col3" colwidth="13mm" /><colspec colnum="4" colname="col4" colwidth="11mm" /><colspec colnum="5" colname="col5" colwidth="13mm" /><colspec colnum="6" colname="col6" colwidth="11mm" /><colspec colnum="7" colname="col7" colwidth="13mm" /><thead><row><entry rowsep="0" valign="top"><b>SAMPLE NO :</b></entry><entry namest="col2" nameend="col3" align="center" valign="top"><b>5A</b></entry><entry namest="col4" nameend="col5" align="center" valign="top"><b>5B</b></entry><entry namest="col6" nameend="col7" align="center" valign="top"><b>6A</b></entry></row><row><entry rowsep="0" valign="top" /><entry align="center" valign="top"><b>MD</b></entry><entry align="center" valign="top"><b>CMD</b></entry><entry align="center" valign="top"><b>MD</b></entry><entry align="center" valign="top"><b>CMD</b></entry><entry align="center" valign="top"><b>MD</b></entry><entry align="center" valign="top"><b>CMD</b></entry></row></thead><tbody><row rowsep="0"><entry /><entry align="right">120</entry><entry align="right">544</entry><entry align="right">104</entry><entry align="right">480</entry><entry align="right">96</entry><entry align="right">272</entry></row><row rowsep="0"><entry /><entry align="right">104</entry><entry align="right">368</entry><entry align="right">116</entry><entry align="right">192</entry><entry align="right">176</entry><entry align="right">256</entry></row><row rowsep="0"><entry /><entry align="right">108</entry><entry align="right">288</entry><entry align="right">108</entry><entry align="right">592</entry><entry align="right">96</entry><entry align="right">256</entry></row><row rowsep="0"><entry /><entry align="right">128</entry><entry align="right">304</entry><entry align="right">112</entry><entry align="right">400</entry><entry align="right">128</entry><entry align="right">224</entry></row><row rowsep="0"><entry /><entry align="right">128</entry><entry align="right">416</entry><entry align="right">120</entry><entry align="right">448</entry><entry align="right">112</entry><entry align="right">208</entry></row><row rowsep="0"><entry /><entry align="right">124</entry><entry align="right">192</entry><entry align="right">108</entry><entry align="right">432</entry><entry align="right">112</entry><entry align="right">368</entry></row><row rowsep="0"><entry /><entry rowsep="1" align="right">124</entry><entry rowsep="1" align="right">528</entry><entry rowsep="1" align="right">124</entry><entry rowsep="1" align="right">416</entry><entry rowsep="1" align="right">112</entry><entry rowsep="1" align="right">336</entry></row><row rowsep="0"><entry><b>AVERAGE:</b></entry><entry align="right">119</entry><entry align="right">377</entry><entry align="right">113</entry><entry align="right">423</entry><entry align="right">119</entry><entry align="right">274</entry></row></tbody></tgroup><tgroup cols="7" colsep="0" rowsep="0"><colspec colnum="1" colname="col1" colwidth="26mm" /><colspec colnum="2" colname="col2" colwidth="11mm" /><colspec colnum="3" colname="col3" colwidth="13mm" /><colspec colnum="4" colname="col4" colwidth="11mm" /><colspec colnum="5" colname="col5" colwidth="13mm" /><colspec colnum="6" colname="col6" colwidth="11mm" /><colspec colnum="7" colname="col7" colwidth="13mm" /><thead><row><entry valign="top"><b>SAMPLE NO:</b></entry><entry namest="col2" nameend="col3" rowsep="1" align="center" valign="top"><b>7A</b></entry><entry namest="col4" nameend="col5" rowsep="1" align="center" valign="top"><b>7B</b></entry><entry namest="col6" nameend="col7" rowsep="1" align="center" valign="top"><b>8A</b></entry></row><row><entry valign="top" /><entry rowsep="1" align="center" valign="top"><b>MD</b></entry><entry rowsep="1" align="center" valign="top"><b>CMD</b></entry><entry rowsep="1" align="center" valign="top"><b>MD</b></entry><entry rowsep="1" align="center" valign="top"><b>CMD</b></entry><entry rowsep="1" align="center" valign="top"><b>MD</b></entry><entry rowsep="1" align="center" valign="top"><b>CMD</b></entry></row></thead><tbody><row><entry /><entry align="right">128</entry><entry align="right">176</entry><entry align="right">132</entry><entry align="right">236</entry><entry align="right">96</entry><entry align="right">480</entry></row><row><entry /><entry align="right">148</entry><entry align="right">220</entry><entry align="right">148</entry><entry align="right">140</entry><entry align="right">104</entry><entry align="right">288</entry></row><row><entry /><entry align="right">152</entry><entry align="right">192</entry><entry align="right">156</entry><entry align="right">172</entry><entry align="right">156</entry><entry align="right">448</entry></row><row><entry /><entry align="right">168</entry><entry align="right">116</entry><entry align="right">156</entry><entry align="right">176</entry><entry align="right">112</entry><entry align="right">304</entry></row><row><entry /><entry align="right">172</entry><entry align="right">108</entry><entry align="right">160</entry><entry align="right">104</entry><entry align="right">100</entry><entry align="right">432</entry></row><row><entry /><entry align="right">144</entry><entry align="right">228</entry><entry align="right">180</entry><entry align="right">124</entry><entry align="right">104</entry><entry align="right">320</entry></row><row><entry /><entry rowsep="1" align="right">148</entry><entry rowsep="1" align="right">180</entry><entry rowsep="1" align="right">184</entry><entry rowsep="1" align="right">132</entry><entry rowsep="1" align="right">160</entry><entry rowsep="1" align="right">352</entry></row><row><entry><b>AVERAGE:</b></entry><entry align="right">151</entry><entry align="right">174</entry><entry align="right">159</entry><entry align="right">155</entry><entry align="right">119</entry><entry align="right">375</entry></row><row><entry /><entry align="right" /><entry align="right" /><entry align="right" /><entry align="right" /><entry align="right" /><entry align="right" /></row></tbody></tgroup><tgroup cols="7" colsep="0" rowsep="0"><colspec colnum="1" colname="col1" colwidth="26mm" /><colspec colnum="2" colname="col2" colwidth="11mm" /><colspec colnum="3" colname="col3" colwidth="13mm" /><colspec colnum="4" colname="col4" colwidth="11mm" /><colspec colnum="5" colname="col5" colwidth="13mm" /><colspec colnum="6" colname="col6" colwidth="11mm" /><colspec colnum="7" colname="col7" colwidth="13mm" /><thead><row><entry valign="top"><b>SAMPLE NO:</b></entry><entry namest="col2" nameend="col3" rowsep="1" align="center" valign="top"><b>9</b></entry><entry valign="top" /><entry valign="top" /><entry valign="top" /><entry valign="top" /></row><row><entry valign="top" /><entry rowsep="1" align="center" valign="top"><b>MD</b></entry><entry rowsep="1" align="center" valign="top"><b>CMD</b></entry><entry valign="top" /><entry valign="top" /><entry valign="top" /><entry valign="top" /></row></thead><tbody><row><entry /><entry align="right">88</entry><entry align="right">212</entry><entry /><entry /><entry /><entry /></row><row><entry /><entry align="right">104</entry><entry align="right">176</entry><entry /><entry /><entry /><entry /></row><row><entry /><entry align="right">220</entry><entry align="right">304</entry><entry /><entry /><entry /><entry /></row><row><entry /><entry align="right">128</entry><entry align="right">256</entry><entry /><entry /><entry /><entry /></row><row><entry /><entry align="right">240</entry><entry align="right">256</entry><entry /><entry /><entry /><entry /></row><row><entry /><entry align="right">140</entry><entry align="right">208</entry><entry /><entry /><entry /><entry /></row><row><entry /><entry rowsep="1" align="right">220</entry><entry rowsep="1" align="right">208</entry><entry /><entry /><entry /><entry /></row><row><entry><b>AVERAGE:</b></entry><entry align="right">163</entry><entry align="right">231</entry><entry /><entry /><entry /><entry /></row></tbody></tgroup></table></tables>

PUNCTURE TEST

0056The puncture strengths of the twelve five layer films and the three layer control film were measured using a compression tester manufactured by Instron Corp. of Canton, Ma. The puncture test measures the amount of force needed to rupture a film. This test allows various films to be rated as to their resistance to being punctured by the contents of a package or by objects outside the package.

0057The test procedure consisted of the following: 1) preparing five 76 mm square (3" square) representative film samples without delaminations; 2) driving a hemispherical-faced probe having a 6 mm diameter through a film sample being held in a circular clamp with the probe in contact with the inner sealant layer of the film; 3) attaching a crosshead to the end of the probe that is opposite to the end that is in contact with the film; 4) positioning the probe, crosshead and sample holder on the Instron compression cell, 5) compressing the crosshead and the sample holder until the probe punctures the sample film, and 6) recording the compression force (measured in pounds) required to puncture the sample film.

0058The puncture strengths of each of the five samples of the five-layer films and the three-layer control film are measured and an average puncture strength calculated for each film. The test results are listed below in Table F. The results indicate that the films of the invention (samples 4A, 4B, 7A and 7B) have excellent puncture strengths as compared to the other films tested. <tables id="tabl0006" num="0006"><table frame="all"><title>TABLE F</title><tgroup cols="7"><colspec colnum="1" colname="col1" colwidth="26mm" /><colspec colnum="2" colname="col2" colwidth="12mm" /><colspec colnum="3" colname="col3" colwidth="12mm" /><colspec colnum="4" colname="col4" colwidth="12mm" /><colspec colnum="5" colname="col5" colwidth="12mm" /><colspec colnum="6" colname="col6" colwidth="12mm" /><colspec colnum="7" colname="col7" colwidth="12mm" /><thead><row><entry namest="col1" nameend="col7" align="center" valign="top">Puncture resistance measured in pounds per square inch. (1 pound per square inch = 6.895 kPa)</entry></row><row><entry align="center" valign="top"><b>SAMPLE NO:</b></entry><entry align="center" valign="top">1A</entry><entry align="center" valign="top">2A</entry><entry align="center" valign="top">3A</entry><entry align="center" valign="top">3B</entry><entry align="center" valign="top">4A</entry><entry align="center" valign="top">4B</entry></row></thead><tbody><row rowsep="0"><entry morerows="5" rowsep="1" align="center" valign="bottom"><b>AVERAGE:</b></entry><entry align="center">14.9</entry><entry align="center">14.6</entry><entry align="center">15.1</entry><entry align="center">14.5</entry><entry align="center">15.5</entry><entry align="center">16.3</entry></row><row rowsep="0"><entry align="center">14.9</entry><entry align="center">14.7</entry><entry align="center">15.5</entry><entry align="center">14.6</entry><entry align="center">16.5</entry><entry align="center">15.5</entry></row><row rowsep="0"><entry align="center">15.2</entry><entry align="center">14.2</entry><entry align="center">15.8</entry><entry align="center">14.0</entry><entry align="center">15.4</entry><entry align="center">16.0</entry></row><row rowsep="0"><entry align="center">15.7</entry><entry align="center">14.3</entry><entry align="center">16.0</entry><entry align="center">14.2</entry><entry align="center">16.4</entry><entry align="center">14.9</entry></row><row rowsep="0"><entry rowsep="1" align="center">15.9</entry><entry rowsep="1" align="center">14.1</entry><entry rowsep="1" align="center">15.2</entry><entry rowsep="1" align="center">13.8</entry><entry rowsep="1" align="center">16.8</entry><entry rowsep="1" align="center">17.0</entry></row><row><entry align="center">15.3</entry><entry align="center">14.4</entry><entry align="center">15.5</entry><entry align="center">14.2</entry><entry align="center">16.1</entry><entry align="center">15.9</entry></row></tbody></tgroup><tgroup cols="7"><colspec colnum="1" colname="col1" colwidth="26mm" /><colspec colnum="2" colname="col2" colwidth="12mm" /><colspec colnum="3" colname="col3" colwidth="12mm" /><colspec colnum="4" colname="col4" colwidth="12mm" /><colspec colnum="5" colname="col5" colwidth="12mm" /><colspec colnum="6" colname="col6" colwidth="12mm" /><colspec colnum="7" colname="col7" colwidth="12mm" /><thead><row><entry align="center" valign="top"><b>SAMPLE No:</b></entry><entry align="center" valign="top">5A</entry><entry align="center" valign="top">5B</entry><entry align="center" valign="top">6A</entry><entry align="center" valign="top">7A</entry><entry align="center" valign="top">7B</entry><entry align="center" valign="top">8A</entry></row></thead><tbody><row rowsep="0"><entry morerows="5" rowsep="1" align="center" valign="bottom"><b>AVERAGE:</b></entry><entry align="center">15.4</entry><entry align="center">16.3</entry><entry align="center">15.8</entry><entry align="center">18.3</entry><entry align="center">18.5</entry><entry align="center">16.3</entry></row><row rowsep="0"><entry align="center">15.6</entry><entry align="center">15.3</entry><entry align="center">15.5</entry><entry align="center">18.5</entry><entry align="center">19.0</entry><entry align="center">15.7</entry></row><row rowsep="0"><entry align="center">15.9</entry><entry align="center">15.8</entry><entry align="center">15.5</entry><entry align="center">18.8</entry><entry align="center">17.9</entry><entry align="center">16.3</entry></row><row rowsep="0"><entry align="center">15.8</entry><entry align="center">16.5</entry><entry align="center">15.1</entry><entry align="center">16.8</entry><entry align="center">18.3</entry><entry align="center">16.0</entry></row><row rowsep="0"><entry rowsep="1" align="center">15.2</entry><entry rowsep="1" align="center">15.0</entry><entry rowsep="1" align="center">15.6</entry><entry rowsep="1" align="center">17.7</entry><entry rowsep="1" align="center">19.1</entry><entry rowsep="1" align="center">16.5</entry></row><row><entry align="center">15.6</entry><entry align="center">15.8</entry><entry align="center">15.5</entry><entry align="center">18.0</entry><entry align="center">18.6</entry><entry align="center">16.2</entry></row></tbody></tgroup><tgroup cols="7"><colspec colnum="1" colname="col1" colwidth="26mm" /><colspec colnum="2" colname="col2" colwidth="12mm" /><colspec colnum="3" colname="col3" colwidth="12mm" /><colspec colnum="4" colname="col4" colwidth="12mm" /><colspec colnum="5" colname="col5" colwidth="12mm" /><colspec colnum="6" colname="col6" colwidth="12mm" /><colspec colnum="7" colname="col7" colwidth="12mm" /><thead><row><entry align="center" valign="top"><b>SAMPLE NO:</b></entry><entry valign="top">9</entry><entry align="center" valign="top" /><entry align="center" valign="top" /><entry align="center" valign="top" /><entry align="center" valign="top" /><entry align="center" valign="top" /></row></thead><tbody><row rowsep="0"><entry morerows="5" rowsep="1" align="center" valign="bottom"><b>AVERAGE:</b></entry><entry align="center">16.3</entry><entry align="center" /><entry align="center" /><entry align="center" /><entry align="center" /><entry align="center" /></row><row rowsep="0"><entry align="center">14.8</entry><entry align="center" /><entry align="center" /><entry align="center" /><entry align="center" /><entry align="center" /></row><row rowsep="0"><entry align="center">15.1</entry><entry align="center" /><entry align="center" /><entry align="center" /><entry align="center" /><entry align="center" /></row><row rowsep="0"><entry align="center">15.7</entry><entry align="center" /><entry align="center" /><entry align="center" /><entry align="center" /><entry align="center" /></row><row rowsep="0"><entry rowsep="1" align="center">16.1</entry><entry align="center" /><entry align="center" /><entry align="center" /><entry align="center" /><entry align="center" /></row><row><entry align="center">15.6</entry><entry align="center" /><entry align="center" /><entry align="center" /><entry align="center" /><entry align="center" /></row></tbody></tgroup></table></tables>

MINIMUM SEAL TEMPERATURE TEST

0059The minimum seal temperature (MST) is the lowest temperature at which a weld seal can be achieved for making packaging seals. This test measures the effect of the cross-linking caused by irradiation on the heat seal temperature. Irradiation is known to elevate the heat seal temperature and make it more difficult to from a seal. The MST for the twelve five layer films and the three layer control film were measured in accordance with ASTM F-88 using a Sentinel Sealer.

0060The test was performed as follows: 1) two one inch widths of the sample film were cut in either the machine direction or the cross-machine direction into strips; 2) the two strips were placed one on top of the other with the sealant layers of the opposing films face to face; 3) the two strips of film were positioned in the Sentinel Sealer and a pressure of 50 psig for a dwell time of 1 second at an initial seal temperature of 93.3°C (200 °F); 4) the seal was inspected to determine if an adequate seal had been formed; 5) if an adequate seal was not achieved, steps 1 through 4 were repeated at a seal temperature 3°C (5 °F) higher than the previous test until an adequate seal was achieved; 6) the test was repeated at least four more times at the seal temperature that was found to be adequate to confirm the result; and 6) the minimum seal temperature was recorded for the sample film.

0061The results for the films tested are listed below in Table G. <tables id="tabl0007" num="0007"><table frame="all"><title>TABLE G</title><tgroup cols="3"><colspec colnum="1" colname="col1" colwidth="33mm" /><colspec colnum="2" colname="col2" colwidth="26mm" /><colspec colnum="3" colname="col3" colwidth="51mm" /><thead><row><entry namest="col1" nameend="col3" align="center" valign="top">Minimum Seal Temperature Test (MST) Minimum sealing temperature is measured in degrees Celsius (°F)</entry></row><row><entry align="center" valign="top"><b>SAMPLE NO.</b></entry><entry namest="col2" nameend="col3" align="center" valign="top"><b>MST</b></entry></row><row><entry align="center" valign="top" /><entry align="center" valign="top">C°</entry><entry align="center" valign="top">F</entry></row></thead><tbody><row rowsep="0"><entry align="center">1A</entry><entry align="center">121</entry><entry>(250)</entry></row><row rowsep="0"><entry align="center">2A</entry><entry align="center">188</entry><entry>(370) (film degradation observed)</entry></row><row rowsep="0"><entry align="center">3A</entry><entry align="center">118</entry><entry>(245</entry></row><row rowsep="0"><entry align="center">3B</entry><entry align="center">118</entry><entry>(245)</entry></row><row rowsep="0"><entry align="center">4A</entry><entry align="center">132</entry><entry>(270)</entry></row><row rowsep="0"><entry align="center">4B</entry><entry align="center">138</entry><entry>(280)</entry></row><row rowsep="0"><entry align="center">5A</entry><entry align="center">127</entry><entry>(260)</entry></row><row rowsep="0"><entry align="center">5B</entry><entry align="center">138</entry><entry>(280)</entry></row><row rowsep="0"><entry align="center">6A</entry><entry align="center">121</entry><entry>(250)</entry></row><row rowsep="0"><entry align="center">7A</entry><entry align="center">132</entry><entry>(270)</entry></row><row rowsep="0"><entry align="center">7B</entry><entry align="center">132</entry><entry>(270)</entry></row><row rowsep="0"><entry align="center">8A</entry><entry align="center">132</entry><entry>(270)</entry></row><row><entry align="center">9</entry><entry align="center">118</entry><entry>(245)</entry></row></tbody></tgroup></table></tables>

SEAL DURABILITY TEST

0062The seal durability test is used to determine the level of cross-linking in a thermoplastic film resulting from electron beam (EB) radiation. This information is helpful in determining the suitability of a film for use with particular seal equipment.

0063The seal durability test used the Vertrod impulse Heat Sealer with a motorized strain gauge and consisted of the following: 1) preparing six samples of each of the twelve five-layer films and the three-layer control film by cutting strips 8 inches in length in the machine direction and 1 inch wide in the cross-machine direction; 2) folding the sample strip in half along the cross-machine axis so that the sealant layers are on the inside; 3) clamping a strip of sample film in place between the sealing jaws of the Vertrod Heat Sealer and attaching one end to the strain gauge; 4) heat sealing the sample film by actuating the heater element ana applying 20.65 kPa (30 psig) pressure for a dwell time of 0.7 seconds; 5) activating the strain gauge motor as the seal bar raises; 6) measuring the seal durability as the motorized strain gauge stretches the heat seal and determining the peak force required to stretch the film at the heat seal; 7) visually examining the seal for burn through and/or stretching; and 8) recording the maximum value measured by the strain gauge.

0064The results of the seal durability test are listed below in Table H. The results indicate that the films of the invention (samples 4A, 4B, 7A and 78) have average seal durability but are less likely to peel than most of the other films tested. ' <tables id="tabl0008" num="0008"><table frame="all"><title>TABLE H</title><tgroup cols="7"><colspec colnum="1" colname="col1" colwidth="25mm" /><colspec colnum="2" colname="col2" colwidth="16mm" /><colspec colnum="3" colname="col3" colwidth="16mm" /><colspec colnum="4" colname="col4" colwidth="16mm" /><colspec colnum="5" colname="col5" colwidth="16mm" /><colspec colnum="6" colname="col6" colwidth="16mm" /><colspec colnum="7" colname="col7" colwidth="16mm" /><thead><row><entry namest="col1" nameend="col7" align="center" valign="top">Seal Durability Test Seal Durability Is measured In ounces (1 ounce = 28.35 g)</entry></row><row><entry valign="top">SAMPLE NO:</entry><entry valign="top">1A</entry><entry valign="top">2A</entry><entry valign="top">3A</entry><entry valign="top">3B</entry><entry valign="top">4A</entry><entry valign="top">4B</entry></row></thead><tbody><row rowsep="0"><entry morerows="6" rowsep="1" align="center" valign="bottom">AVERAGE:</entry><entry>16.5NB</entry><entry>12.5 NB</entry><entry>15.0 NB</entry><entry>15.0 NB</entry><entry>15.0 NB</entry><entry>17.0 NB</entry></row><row rowsep="0"><entry>15.0 NB</entry><entry>12.0 NB</entry><entry>13.0 NB</entry><entry>15.0 NB</entry><entry>13.5NB</entry><entry>16.0 NB</entry></row><row rowsep="0"><entry>9.5P</entry><entry>10.5NB</entry><entry>12.0 NB</entry><entry>11.0 NB</entry><entry>13.0 NB</entry><entry>15.0 NB</entry></row><row rowsep="0"><entry>14.0P</entry><entry>13.0 NB</entry><entry>13.5NB</entry><entry>15.0NB</entry><entry>15.5NB</entry><entry>16.0NB</entry></row><row rowsep="0"><entry>13.0 P</entry><entry>10.5 NB</entry><entry>14.0 NB</entry><entry>14.0 NB</entry><entry>14.0 NB</entry><entry>14.5 NB</entry></row><row rowsep="0"><entry rowsep="1">11.5P</entry><entry rowsep="1">11.0 NB</entry><entry rowsep="1">12.5 NB</entry><entry rowsep="1">15.5 NB</entry><entry rowsep="1">14.0 NB</entry><entry rowsep="1">14.5 NB</entry></row><row><entry>13.2</entry><entry>11.6</entry><entry>13.3</entry><entry>13.3</entry><entry>14.2</entry><entry>15.5</entry></row></tbody></tgroup><tgroup cols="7"><colspec colnum="1" colname="col1" colwidth="25mm" /><colspec colnum="2" colname="col2" colwidth="16mm" /><colspec colnum="3" colname="col3" colwidth="16mm" /><colspec colnum="4" colname="col4" colwidth="16mm" /><colspec colnum="5" colname="col5" colwidth="16mm" /><colspec colnum="6" colname="col6" colwidth="16mm" /><colspec colnum="7" colname="col7" colwidth="16mm" /><thead><row><entry align="center" valign="top">SAMPLE NO:</entry><entry valign="top">5A</entry><entry valign="top">5B</entry><entry valign="top">6A</entry><entry valign="top">7A</entry><entry valign="top">7B</entry><entry valign="top">8A</entry></row></thead><tbody><row rowsep="0"><entry morerows="6" rowsep="1" align="center" valign="bottom">AVERAGE:</entry><entry>15.0 P</entry><entry>15.0 P</entry><entry>12.0 P</entry><entry>11.0 NB</entry><entry>13.0 NB</entry><entry>13.5 P</entry></row><row rowsep="0"><entry>150NB</entry><entry>11.0 P</entry><entry>14.5P</entry><entry>13.0 NB</entry><entry>11.5 NB</entry><entry>15.0 NB</entry></row><row rowsep="0"><entry>12.0 P</entry><entry>16.0 P</entry><entry>16.5NB</entry><entry>12.5 NB</entry><entry>13.5 NB</entry><entry>14.0 P</entry></row><row rowsep="0"><entry>10.5 P</entry><entry>17.5 NB</entry><entry>15.5 P</entry><entry>14.0 NB</entry><entry>13.0 NB</entry><entry>12.0 NB</entry></row><row rowsep="0"><entry>10.0 NB</entry><entry>15.0 P</entry><entry>16.0 P</entry><entry>10.0 NB</entry><entry>15.0 NB</entry><entry>25.0 P</entry></row><row rowsep="0"><entry rowsep="1">16.0 NB</entry><entry rowsep="1">17.0 NB</entry><entry rowsep="1">12.0 P</entry><entry rowsep="1">10.0 NB</entry><entry rowsep="1">10.5 NB</entry><entry rowsep="1">22.0 P</entry></row><row><entry>13.1</entry><entry>15.2</entry><entry>14.4</entry><entry>11.7</entry><entry>12.7</entry><entry>16.9</entry></row></tbody></tgroup><tgroup cols="7"><colspec colnum="1" colname="col1" colwidth="25mm" /><colspec colnum="2" colname="col2" colwidth="16mm" /><colspec colnum="3" colname="col3" colwidth="16mm" /><colspec colnum="4" colname="col4" colwidth="16mm" /><colspec colnum="5" colname="col5" colwidth="16mm" /><colspec colnum="6" colname="col6" colwidth="16mm" /><colspec colnum="7" colname="col7" colwidth="16mm" /><thead><row><entry align="center" valign="top">SAMPLE NO:</entry><entry valign="top">9</entry><entry valign="top" /><entry valign="top" /><entry valign="top" /><entry valign="top" /><entry valign="top" /></row></thead><tbody><row rowsep="0"><entry morerows="6" rowsep="1" align="center" valign="bottom">AVERAGE:</entry><entry>12.0 NB</entry><entry /><entry /><entry /><entry /><entry /></row><row rowsep="0"><entry>12.0 NB</entry><entry /><entry /><entry /><entry /><entry /></row><row rowsep="0"><entry>10.0 NB</entry><entry /><entry /><entry /><entry /><entry /></row><row rowsep="0"><entry>11.5 NB</entry><entry /><entry /><entry /><entry /><entry /></row><row rowsep="0"><entry>11.0 NB</entry><entry /><entry /><entry /><entry /><entry /></row><row rowsep="0"><entry rowsep="1">7.0 NB</entry><entry /><entry /><entry /><entry /><entry /></row><row><entry>10.6</entry><entry /><entry /><entry /><entry /><entry /></row><row rowsep="0"><entry namest="col1" nameend="col7" align="left">NB = No break after peak force.</entry></row><row><entry namest="col1" nameend="col7" align="left">P = Peeling of the layers was observed.</entry></row></tbody></tgroup></table></tables>

HAZE TEST

0065Haze is a basic measure of film clarity. Haze is defined as the amount of light that is scattered as light passes through a film.

0066The haze test was performed in accordance with ASTM D-1003 using a Pacific Scientific XL-211 Hazegard System. The test was performed on the twelve five layer sample films and the three-layer control film and consisted of: 1) preparing samples for each film by cutting the films into five 10 cm (4 inch) square specimens; 2) positioning a sample on the Hazegard System; 3) measuring the percent haze using an integrating sphere to collect light scattered by the sample film; and 4) recording the percent haze.

0067The results of the haze test are recorded below in Table I. <tables id="tabl0009" num="0009"><table frame="all"><title>TABLE I</title><tgroup cols="7"><colspec colnum="1" colname="col1" colwidth="25mm" /><colspec colnum="2" colname="col2" colwidth="13mm" /><colspec colnum="3" colname="col3" colwidth="12mm" /><colspec colnum="4" colname="col4" colwidth="12mm" /><colspec colnum="5" colname="col5" colwidth="12mm" /><colspec colnum="6" colname="col6" colwidth="12mm" /><colspec colnum="7" colname="col7" colwidth="12mm" /><thead><row><entry namest="col1" nameend="col7" align="center" valign="top">Haze Test Haze is measured as the percentage of scattered light.</entry></row><row><entry align="center" valign="top"><b>SAMPLE No:</b></entry><entry valign="top">1 A</entry><entry valign="top">2A</entry><entry valign="top">3A</entry><entry valign="top">3B</entry><entry valign="top">4A</entry><entry valign="top">4B</entry></row></thead><tbody><row rowsep="0"><entry morerows="6" rowsep="1" align="center" valign="bottom">AVERAGE:</entry><entry>14.2</entry><entry>13.1</entry><entry>14.4</entry><entry>13.3</entry><entry>10.0</entry><entry>9.66</entry></row><row rowsep="0"><entry>13.7</entry><entry>12.9</entry><entry>14.3</entry><entry>12.4</entry><entry>10.7</entry><entry>10.5</entry></row><row rowsep="0"><entry>14.7</entry><entry>11.7</entry><entry>14.8</entry><entry>13.8</entry><entry>11.0</entry><entry>12.1</entry></row><row rowsep="0"><entry>11.9</entry><entry>11.1</entry><entry>11.7</entry><entry>13.8</entry><entry>10.9</entry><entry>12.4</entry></row><row rowsep="0"><entry>12.5</entry><entry>13.8</entry><entry>13.0</entry><entry>14.3</entry><entry>12.2</entry><entry>10.7</entry></row><row rowsep="0"><entry rowsep="1">12.0</entry><entry rowsep="1">13.3</entry><entry rowsep="1">12.2</entry><entry rowsep="1">13.0</entry><entry rowsep="1">9.24</entry><entry rowsep="1">10.1</entry></row><row><entry>13.2</entry><entry>12.6</entry><entry>13.4</entry><entry>13.4</entry><entry>10.7</entry><entry>10.9</entry></row></tbody></tgroup><tgroup cols="7"><colspec colnum="1" colname="col1" colwidth="25mm" /><colspec colnum="2" colname="col2" colwidth="13mm" /><colspec colnum="3" colname="col3" colwidth="12mm" /><colspec colnum="4" colname="col4" colwidth="12mm" /><colspec colnum="5" colname="col5" colwidth="12mm" /><colspec colnum="6" colname="col6" colwidth="12mm" /><colspec colnum="7" colname="col7" colwidth="12mm" /><thead><row><entry align="center" valign="top"><b>SAMPLE NO:</b></entry><entry valign="top">5A</entry><entry valign="top">5B</entry><entry valign="top">6A</entry><entry valign="top">7A</entry><entry valign="top">78</entry><entry valign="top">8A</entry></row></thead><tbody><row rowsep="0"><entry morerows="6" rowsep="1" align="center" valign="bottom">AVERAGE:</entry><entry>10.6</entry><entry>10.9</entry><entry>11.2</entry><entry>9.37</entry><entry>13.5</entry><entry>9.35</entry></row><row rowsep="0"><entry>13.2</entry><entry>10.9</entry><entry>11.5</entry><entry>10.3</entry><entry>11.6</entry><entry>11.2</entry></row><row rowsep="0"><entry>12.5</entry><entry>11.8</entry><entry>12.6</entry><entry>11.5</entry><entry>12.7</entry><entry>11.2</entry></row><row rowsep="0"><entry>12.0</entry><entry>13.6</entry><entry>10.3</entry><entry>11.8</entry><entry>10.5</entry><entry>11.7</entry></row><row rowsep="0"><entry>12.4</entry><entry>11.8</entry><entry>10.5</entry><entry>10.8</entry><entry>9.87</entry><entry>11.5</entry></row><row rowsep="0"><entry rowsep="1">12.1</entry><entry rowsep="1">13.7</entry><entry rowsep="1">10.2</entry><entry rowsep="1">11.2</entry><entry rowsep="1">12.3</entry><entry rowsep="1">13.0</entry></row><row><entry>12.1</entry><entry>12.1</entry><entry>11.0</entry><entry>10.8</entry><entry>11.7</entry><entry>11.3</entry></row></tbody></tgroup><tgroup cols="7"><colspec colnum="1" colname="col1" colwidth="25mm" /><colspec colnum="2" colname="col2" colwidth="13mm" /><colspec colnum="3" colname="col3" colwidth="12mm" /><colspec colnum="4" colname="col4" colwidth="12mm" /><colspec colnum="5" colname="col5" colwidth="12mm" /><colspec colnum="6" colname="col6" colwidth="12mm" /><colspec colnum="7" colname="col7" colwidth="12mm" /><thead><row><entry align="center" valign="top"><b>SAMPLE No:</b></entry><entry valign="top">9</entry><entry valign="top" /><entry valign="top" /><entry valign="top" /><entry valign="top" /><entry valign="top" /></row></thead><tbody><row rowsep="0"><entry morerows="6" rowsep="1" align="center" valign="bottom">AVERAGE:</entry><entry>8.98</entry><entry /><entry /><entry /><entry /><entry /></row><row rowsep="0"><entry>11.10</entry><entry /><entry /><entry /><entry /><entry /></row><row rowsep="0"><entry>9.81</entry><entry /><entry /><entry /><entry /><entry /></row><row rowsep="0"><entry>8.34</entry><entry /><entry /><entry /><entry /><entry /></row><row rowsep="0"><entry>8.52</entry><entry /><entry /><entry /><entry /><entry /></row><row rowsep="0"><entry rowsep="1">8.71</entry><entry /><entry /><entry /><entry /><entry /></row><row><entry>9.2</entry><entry /><entry /><entry /><entry /><entry /></row></tbody></tgroup></table></tables>

GLOSS TEST

0068Gloss is a surface optical property of a film relating to the deflection of light. Gloss is measured as the percentage of light secularly reflected from the surface of the film. The Macbeth Lab-Gloss instrument was used to measure the gloss of the twelve five-layer sample films and the three-layer control film.

0069The gloss test consisted of the following: 1) preparing samples for each of the films by cutting the films Into 10 cm (4 inch) square specimens; 2) positioning a sample on the Macbeth Lab-Gloss instrument; 3) reflecting a beam of light from a light Source onto the surface of the film sample at a 45 degree angle; 4) measuring the percentage or light reflecting from the surface; and 5) recording the results.

0070The gloss test results were recorded in Table J below. <tables id="tabl0010" num="0010"><table frame="all"><title>TABLE J</title><tgroup cols="7"><colspec colnum="1" colname="col1" colwidth="26mm" /><colspec colnum="2" colname="col2" colwidth="12mm" /><colspec colnum="3" colname="col3" colwidth="12mm" /><colspec colnum="4" colname="col4" colwidth="12mm" /><colspec colnum="5" colname="col5" colwidth="12mm" /><colspec colnum="6" colname="col6" colwidth="12mm" /><colspec colnum="7" colname="col7" colwidth="12mm" /><thead><row><entry namest="col1" nameend="col7" align="center" valign="top">Gloss Test Gloss is measured as the percentage of light reflected when a light strikes the surface at a 45 degree angle.</entry></row><row><entry align="center" valign="top"><b>SAMPLE NO:</b></entry><entry valign="top">1A</entry><entry valign="top">2A</entry><entry valign="top">3A</entry><entry valign="top">3B</entry><entry valign="top">4A</entry><entry valign="top">4B</entry></row></thead><tbody><row rowsep="0"><entry morerows="6" rowsep="1" align="center" valign="bottom">AVERAGE:</entry><entry>65.3</entry><entry>62.5</entry><entry>62.6</entry><entry>61.5</entry><entry>68.5</entry><entry>69.0</entry></row><row rowsep="0"><entry>65.4</entry><entry>63.9</entry><entry>64.5</entry><entry>63.8</entry><entry>70.4</entry><entry>68.3</entry></row><row rowsep="0"><entry>63.8</entry><entry>65.6</entry><entry>60.4</entry><entry>65.0</entry><entry>67.7</entry><entry>66.8</entry></row><row rowsep="0"><entry>61.9</entry><entry>67.1</entry><entry>65.9</entry><entry>64.1</entry><entry>67.7</entry><entry>63.7</entry></row><row rowsep="0"><entry>65.9</entry><entry>67.4</entry><entry>64.8</entry><entry>63.4</entry><entry>67.4</entry><entry>69.3</entry></row><row rowsep="0"><entry rowsep="1">66.8</entry><entry rowsep="1">65.8</entry><entry rowsep="1">66.5</entry><entry rowsep="1">62.8</entry><entry rowsep="1">69.4</entry><entry rowsep="1">68.0</entry></row><row><entry>64.8</entry><entry>65.3</entry><entry>64.1</entry><entry>63.4</entry><entry>68.5</entry><entry>67.5</entry></row></tbody></tgroup><tgroup cols="7"><colspec colnum="1" colname="col1" colwidth="26mm" /><colspec colnum="2" colname="col2" colwidth="12mm" /><colspec colnum="3" colname="col3" colwidth="12mm" /><colspec colnum="4" colname="col4" colwidth="12mm" /><colspec colnum="5" colname="col5" colwidth="12mm" /><colspec colnum="6" colname="col6" colwidth="12mm" /><colspec colnum="7" colname="col7" colwidth="12mm" /><thead><row><entry valign="top"><b>SAMPLE NO:</b></entry><entry valign="top">5A</entry><entry valign="top">5B</entry><entry valign="top">6A</entry><entry valign="top">7A</entry><entry valign="top">7B</entry><entry valign="top">8A</entry></row></thead><tbody><row rowsep="0"><entry morerows="6" rowsep="1" align="center" valign="bottom">AVERAGE:</entry><entry>69.3</entry><entry>67.4</entry><entry>68.3</entry><entry>64.8</entry><entry>61.0</entry><entry>67.9</entry></row><row rowsep="0"><entry>69.9</entry><entry>69.3</entry><entry>65.0</entry><entry>68.6</entry><entry>63.8</entry><entry>68.9</entry></row><row rowsep="0"><entry>65.2</entry><entry>66.2</entry><entry>69.1</entry><entry>64.7</entry><entry>63.2</entry><entry>68.1</entry></row><row rowsep="0"><entry>64.3</entry><entry>68.8</entry><entry>68.3</entry><entry>62.8</entry><entry>60.9</entry><entry>68.3</entry></row><row rowsep="0"><entry>64.0</entry><entry>69.3</entry><entry>70.0</entry><entry>67.2</entry><entry>64.4</entry><entry>68.6</entry></row><row rowsep="0"><entry rowsep="1">68.0</entry><entry rowsep="1">68.1</entry><entry rowsep="1">68.7</entry><entry rowsep="1">67.5</entry><entry rowsep="1">61.5</entry><entry rowsep="1">69.5</entry></row><row><entry>66.7</entry><entry>68.1</entry><entry>68.2</entry><entry>65.9</entry><entry>62.4</entry><entry>68.5</entry></row></tbody></tgroup><tgroup cols="7"><colspec colnum="1" colname="col1" colwidth="26mm" /><colspec colnum="2" colname="col2" colwidth="12mm" /><colspec colnum="3" colname="col3" colwidth="12mm" /><colspec colnum="4" colname="col4" colwidth="12mm" /><colspec colnum="5" colname="col5" colwidth="12mm" /><colspec colnum="6" colname="col6" colwidth="12mm" /><colspec colnum="7" colname="col7" colwidth="12mm" /><thead><row><entry valign="top"><b>SAMPLE NO.:</b></entry><entry valign="top">9</entry><entry valign="top" /><entry valign="top" /><entry valign="top" /><entry valign="top" /><entry valign="top" /></row></thead><tbody><row rowsep="0"><entry morerows="6" rowsep="1" align="center" valign="bottom">AVERAGE:</entry><entry>68.2</entry><entry /><entry /><entry /><entry /><entry /></row><row rowsep="0"><entry>68.9</entry><entry /><entry /><entry /><entry /><entry /></row><row rowsep="0"><entry>67.2</entry><entry /><entry /><entry /><entry /><entry /></row><row rowsep="0"><entry>68.5</entry><entry /><entry /><entry /><entry /><entry /></row><row rowsep="0"><entry>63.9</entry><entry /><entry /><entry /><entry /><entry /></row><row rowsep="0"><entry rowsep="1">68.7</entry><entry /><entry /><entry /><entry /><entry /></row><row><entry>67.5</entry><entry /><entry /><entry /><entry /><entry /></row></tbody></tgroup></table></tables>

IMPACT STRENGTH TEST

0071The impact strength test is used to determine the total energy impact strength of a film structure by measuring the kinetic energy lost by a free-falling dart that passes through the film. This test is useful in predicting the performance of a film used for packaging. The test simulates the action encountered in applications where moderate velocity blunt impacts occur in relatively small areas of the film.

0072The impact strength test uses a Kayeness Energy Absorption Impact Tester (EAIT) and consists of the following: <ol id="ol0001" compact="compact" ol-style=""><li>1) preparing samples for each of the twelve five-layer films and the three-layer control film by cutting the films into five 20.3 cm (8-inch) square specimens; 2) positioning a sample films on the EAIT; 3) dropping a 15.9 kg (35 pound) probe having a 3.8 cm (1 1/2 inch) diameter tip through the sample film: 4) measuring the force of the probe as it strikes a load cell positioned below the sample film; 5) determining the impact strength of the sample film by calculating the kinetic energy that is lost when the probe passes through the film; and 6) recording the test results.</li></ol>

0073The test results are listed in Table K below. The results indicate that the films of the invention (samples 4A, 4B, 7A and 7B) have above average impact strengths. <tables id="tabl0011" num="0011"><table frame="all"><title>TABLE K</title><tgroup cols="5"><colspec colnum="1" colname="col1" colwidth="25mm" /><colspec colnum="2" colname="col2" colwidth="13mm" /><colspec colnum="3" colname="col3" colwidth="15mm" /><colspec colnum="4" colname="col4" colwidth="15mm" /><colspec colnum="5" colname="col5" colwidth="13mm" /><thead><row><entry namest="col1" nameend="col5" align="center" valign="top">Impact Strength Test The impact energy is measured in foot-pounds (1 foot- pound = 1.355 J.)</entry></row><row><entry align="center" valign="top"><b>SAMPLE NO.</b></entry><entry align="center" valign="top"><b>1A</b></entry><entry align="center" valign="top"><b>2A</b></entry><entry align="center" valign="top"><b>3A</b></entry><entry align="center" valign="top"><b>3B</b></entry></row></thead><tbody><row rowsep="0"><entry morerows="6" rowsep="1" align="center" valign="bottom"><b>AVERAGE:</b></entry><entry align="center">5.96</entry><entry align="center">5.25</entry><entry align="center">6.05</entry><entry align="center">4.83</entry></row><row rowsep="0"><entry align="center">5.49</entry><entry align="center">5.95</entry><entry align="center">6.33</entry><entry align="center">5.76</entry></row><row rowsep="0"><entry align="center">5.45</entry><entry align="center">5.84</entry><entry align="center">6.33</entry><entry align="center">4.79</entry></row><row rowsep="0"><entry align="center" /><entry align="center">5.47</entry><entry align="center">6.07</entry><entry align="center">4.92</entry></row><row rowsep="0"><entry align="center" /><entry align="center">5.56</entry><entry align="center">6.07</entry><entry align="center">6.00</entry></row><row rowsep="0"><entry rowsep="1" align="center" /><entry rowsep="1" align="center" /><entry rowsep="1" align="center" /><entry rowsep="1" align="center">5.83</entry></row><row><entry align="center"><b>5.64</b></entry><entry align="center"><b>5.61</b></entry><entry align="center"><b>6.17</b></entry><entry align="center"><b>5.35</b></entry></row></tbody></tgroup><tgroup cols="5"><colspec colnum="1" colname="col1" colwidth="25mm" /><colspec colnum="2" colname="col2" colwidth="13mm" /><colspec colnum="3" colname="col3" colwidth="15mm" /><colspec colnum="4" colname="col4" colwidth="15mm" /><colspec colnum="5" colname="col5" colwidth="13mm" /><thead><row><entry align="center" valign="top"><b>SAMPLE NO.</b></entry><entry align="center" valign="top"><b>4A</b></entry><entry align="center" valign="top"><b>4B</b></entry><entry align="center" valign="top"><b>5A</b></entry><entry align="center" valign="top"><b>5B</b></entry></row></thead><tbody><row rowsep="0"><entry morerows="6" rowsep="1" align="center" valign="bottom">AVERAGE:</entry><entry align="center">8.42</entry><entry align="center">9.45</entry><entry align="center">6.10</entry><entry align="center">6.83</entry></row><row rowsep="0"><entry align="center">9.44</entry><entry align="center">9.41</entry><entry align="center">6.52</entry><entry align="center">6.89</entry></row><row rowsep="0"><entry align="center">6.20</entry><entry align="center">7.81</entry><entry align="center">7.66</entry><entry align="center">6.42</entry></row><row rowsep="0"><entry align="center">7.90</entry><entry align="center">8.51</entry><entry align="center">7.31</entry><entry align="center">7.17</entry></row><row rowsep="0"><entry align="center">8.30</entry><entry align="center">8.30</entry><entry align="center">6.48</entry><entry align="center">6.29</entry></row><row rowsep="0"><entry rowsep="1" align="center" /><entry rowsep="1" align="center">9.14</entry><entry rowsep="1" align="center">6.98</entry><entry rowsep="1" align="center" /></row><row><entry align="center"><b>8.05</b></entry><entry align="center"><b>8.77</b></entry><entry align="center"><b>6.84</b></entry><entry align="center"><b>6.72</b></entry></row></tbody></tgroup><tgroup cols="5"><colspec colnum="1" colname="col1" colwidth="25mm" /><colspec colnum="2" colname="col2" colwidth="13mm" /><colspec colnum="3" colname="col3" colwidth="15mm" /><colspec colnum="4" colname="col4" colwidth="15mm" /><colspec colnum="5" colname="col5" colwidth="13mm" /><thead><row><entry align="center" valign="top"><b>SAMPLE NO.</b></entry><entry align="center" valign="top"><b>6A</b></entry><entry align="center" valign="top"><b>7A</b></entry><entry align="center" valign="top"><b>7B</b></entry><entry align="center" valign="top"><b>8A</b></entry></row></thead><tbody><row rowsep="0"><entry morerows="6" rowsep="1" align="center" valign="bottom">AVERAGE:</entry><entry align="center">6.83</entry><entry align="center">7.79</entry><entry align="center">9.89</entry><entry align="center">6.21</entry></row><row rowsep="0"><entry align="center">7.00</entry><entry align="center">10.00</entry><entry align="center">11.25</entry><entry align="center">6.98</entry></row><row rowsep="0"><entry align="center">5.81</entry><entry align="center">11.27</entry><entry align="center">12.11</entry><entry align="center">7.11</entry></row><row rowsep="0"><entry align="center">6.08</entry><entry align="center">10.29</entry><entry align="center">11.19</entry><entry align="center">7.04</entry></row><row rowsep="0"><entry align="center">5.42</entry><entry align="center">9.35</entry><entry align="center">11.02</entry><entry align="center">7.09</entry></row><row rowsep="0"><entry align="center">6.92</entry><entry align="center">8.60</entry><entry align="center">13.24</entry><entry align="center">7.44</entry></row><row><entry align="center"><b>6.34</b></entry><entry align="center"><b>9.55</b></entry><entry align="center"><b>11.45</b></entry><entry align="center"><b>6.98</b></entry></row></tbody></tgroup><tgroup cols="5"><colspec colnum="1" colname="col1" colwidth="25mm" /><colspec colnum="2" colname="col2" colwidth="13mm" /><colspec colnum="3" colname="col3" colwidth="15mm" /><colspec colnum="4" colname="col4" colwidth="15mm" /><colspec colnum="5" colname="col5" colwidth="13mm" /><thead><row><entry align="center" valign="top"><b>SAMPLE NO.</b></entry><entry align="center" valign="top"><b>9</b></entry><entry align="center" valign="top" /><entry align="center" valign="top" /><entry align="center" valign="top" /></row></thead><tbody><row rowsep="0"><entry morerows="6" rowsep="1" align="center" valign="bottom"><b>AVERAGE:</b></entry><entry align="center">8.40</entry><entry align="center" /><entry align="center" /><entry align="center" /></row><row rowsep="0"><entry align="center">7.14</entry><entry align="center" /><entry align="center" /><entry align="center" /></row><row rowsep="0"><entry align="center">7.95</entry><entry align="center" /><entry align="center" /><entry align="center" /></row><row rowsep="0"><entry align="center">6.87</entry><entry align="center" /><entry align="center" /><entry align="center" /></row><row rowsep="0"><entry align="center">7.57</entry><entry align="center" /><entry align="center" /><entry align="center" /></row><row rowsep="0"><entry rowsep="1" align="center">7.86</entry><entry align="center" /><entry align="center" /><entry align="center" /></row><row><entry align="center"><b>7.63</b></entry><entry align="center" /><entry align="center" /><entry align="center" /></row></tbody></tgroup></table></tables>