Urea-modified copolymers as dispersants for pigments in coating compositions.

FIELD OF THE INVENTION

0001The present invention is directed to a modified copolymer. More specifically, the present invention is directed to a modified copolymer pigment dispersant for aqueous coating compositions.

BACKGROUND OF THE INVENTION

0002Colorant compositions for use in coating compositions are disclosed in EP 0 462 557 A2. This composition contains a pigment component and a liquid vehicle for the pigment component. The liquid vehicle includes a urea-containing component. In the preferred embodiment the urea-containing component is 1-(2-hydroxyethyl)-2-imidizolidinone, commonly called 2-hydroxyethylethylene urea.

0003Aqueous coating compositions are known and described for example in U.S. Patent Nos. 4,794,147; 4,791,168; 4,518,724; and 4,403,055.

0004These aqueous coating compositions comprise a principal resin, and may contain a crosslinker, pigments dispersed in a grind resin and other additives such as solvents, control agents, fillers and the like.

0005Many pigments, especially organics, used in coating compositions for the automotive industry are hydrophobic. These pigments, when used in aqueous coating systems require the use of specialized grind resins with the additions of dispersing agents and solvents to overcome their incompatibility with water and poor ability to grind.

0006Pigment pastes are usually prepared by dispersing a pigment in a grinding resin in the presence of plasticizers, wetting agents, surfactants or other ingredients in a ball mill, sand mill or continuous mill, until the pigment has been reduced to the desired particle size and is wetted by the resin or dispersed in it.

0007One disadvantage of pigment pastes is that the pastes often require a large amount of resin relative to pigment, and the resulting pigment pastes are not very concentrated. In addition, pastes made with conventional resins often do not have optimum color development.

0008The present invention is directed to a pigment dispersant for an aqueous coating composition that provides stable aqueous pigment pastes or pigment dispersions. By using the dispersant of the present invention, dispersions with a high concentration of pigments can be made. The present invention is also directed to an aqueous coating composition containing the pigment dispersants and an article coated with the coating composition.

SUMMARY OF THE INVENTION

0009The present invention is a polymeric dispersant for pigments. The dispersant includes a) a copolymer functionalized with isocyanate, anhydride or epoxy functionalities, b) a polyalkylene glycol homopolymer or copolymer, to impart water-soluble character to the polymeric backbone and c) a urea-containing pigment-interactive substituent, which enhances pigment dispersion in solution.

0010The copolymer (a) includes (i) an ethylenically unsaturated monomer having a reactive functionality from which grafting may take place, where said functionality is an isocyanate functionality, an anhydride functionality or an epoxy functionality; and (ii) at least one ethylenically unsaturated monomer having no functional group that reacts with the reactive functionality of monomer (i). The copolymer may also include an additional monomer (iii) that is an ethylenically functional aromatic compound.

0011The dispersant also includes at least one polyalkylene glycol compound that is a polyalkylene glycol homopolymer, copolymer, or mixture thereof, to react with the reactive functionality of monomer (i) to impart water soluble character to the polymer. When the reactive functionality of monomer (i) is an isocyanate functionality or an anhydride, the polyalkylene glycol compound reacts with the isocyanate or anhydride reactive functionality to form a sidechain. When the reactive functionality of monomer (i) is an epoxy functionality, the polyalkylene glycol compound must first be reacted with anhydride to form an acid functional polyalkylene glycol compound.

0012Useful polyalkylene glycol compounds include polyalkylene glycol monoalkyl ethers and mixtures thereof.

0013The copolymer is also reacted with a pigment interactive substituent that is a urea-containing compound having the formula: <chemistry id="chem0001" num="0001"><img file="EP0589340A1_D0001.tif" /></chemistry> and mixtures thereof, wherein each R is independently selected from the group consisting of H, saturated and unsaturated aliphatic and alicyclic compounds that may be substituted or unsubstituted, substituted and unsubstituted aromatic compounds and divalent radicals including but not limited to - NH-, oxygen and sulfur, and wherein one R group contains a functional group which can react with the reactive functionality on monomer (i).

0014If any isocyanate functionality provided by monomer (i) remains after reaction with monomer (ii) or monomers (ii) and (iii), it may be capped by the addition of a compound having an amine or hydroxy functionality which reacts with the isocyanate. These amine and hydroxy containing compounds are selected from the group consisting of mono or dialkyl amines, mono or dicycloalkyl amines, aromatic amines, aryl aliphatic amines, mono and di alkanolamines, cyclic alkanolamines and primary and secondary ether alcohols.

DETAILED DESCRIPTION OF THE INVENTION

0015The present invention is directed to a polymeric pigment dispersant, coating composition containing the dispersant, and articles coated with the dispersant-containing coating. The pigment dispersant includes a functionalized copolymer, a polyalkylene glycol homopolymer or copolymer to impart water soluble character to the functionalized copolymer, and a pigment interactive substituent, which enhances pigment dispersion in solution.

0016The functionalized copolymer is the reaction product of (i) an ethylenically unsaturated monomer containing a reactive functionality selected from the group consisting of isocyanate, anhydride, and epoxy functionalities; and (ii) at least one ethylenically unsaturated monomer that has no functional groups capable of reacting with the reactive functionality of monomer (i). The functionalized copolymer may also include an additional monomer (iii) which is an ethylenically functional aromatic compound.

0017The ethylenically unsaturated monomer (i) is present in an amount between about 5% to about 50% by weight, preferably from about 20% to about 40% by weight based on total monomer weight. Suitable ethylenically unsaturated monomers containing an isocyanate functionality include dimethyl-meta-isopropenylbenzyl isocyanate, vinylisocyanate, isocyanatoethyl acrylate and isocyanato ethyl methacrylate, isopropenyl isocyanate, and mixtures thereof. Preferred is 1-(1-isocyanato-1-methyl ethyl)-3-(1-methyl ethenyl)benzene, also referred to as TMI®, available from American Cyanamid Co. Wayne, NJ 076470.

0018Suitable ethylenically unsaturated monomers containing an anhydride functionality include aliphatic and cycloaliphatic anhydrides, olefinic and cycloolefinic anhydrides and aromatic anhydrides. The aromatic anhydrides include aliphatic and aromatic substituted anhydrides, provided that the substituents do not adversely affect the reactivity of the anhydride or the properties of the resultant polymer. Examples of these substituents include chloro, alkyl and alkoxy substituents.

0019Examples of specific anhydrides include succinic anhydride, methylsuccinic anhydride, dodecenyl succinic anhydride, octadecenylsuccinic anhydride, phthalic anhydride, tetrahydrophthalic anhydride, methyltetrahydrophthalic anhydride, hexahydrophthalic anhydride, alkyl hexahydrophthalic anhydrides such as methylhexahydrophthalic anhydride, tetrachlorophthalic anhydride, endomethylene tetrahydrophthalic anhydride, chlorendic anhydride, itaconic anhydride, citraconic anhydride and maleic anhydride.

0020Preferred monomers containing the anhydride functionality are itaconic anhydride and maleic anhydride. Suitable ethylenically unsaturated monomers containing an epoxy functionality include glycidyl acrylate, glycidyl methacrylate, and allyl glycidyl ether. The preferred monomer containing the epoxy functionality is glycidyl methacrylate.

0021The ethylenically unsaturated monomers (ii), are present in an amount from about 10% to about 90% by weight, preferably from about 40% to about 70% by weight based on total monomer weight. Suitable monomers having no functionality that reacts with the reactive functionality of monomer (i), include acrylic and methacrylic alkyl, aryl, aryl alkyl and alkoxyalkyl esters. The alkyl esters of acrylic and methacrylic acid are derived from alcohols having from 1 to about 20 carbon atoms, from phenols or from vinyl monomers.

0022Preferred are the esters of acrylic and methacrylic acid such as methyl, ethyl, propyl, n-butyl, isobutyl, tert-butyl, cyclohexyl, and 2-ethylhexyl acrylates and methacrylates and mixtures thereof.

0023Also suitable are vinyl chloride, acrylamide and methacrylamide, acrylonitrile, methacrylonitrile, N-alkyl maleimides, N-aryl malemides and acrolein. Maleic acid and fumaric acid dialkyl esters in which the alkyl groups have 1 to 20 carbon atoms may also be used.

0024The ethylenically functional aromatic substituted monomer (iii), when included, is present in an amount from about 5% to about 40% by weight, preferably from about 10% to about 20% by weight, based on total monomer weight. Suitable monomers include styrene, alpha-methyl styrene, para-hydroxy styrene, tert-butyl styrene and vinyl toluene and halogenated vinyl benzenes such as chloro-styrene. Also useful are acrylic and methacrylic esters such as para-tolyl acrylate, phenylethyl acrylate, naphthyl acrylate, phenyl methacrylate, naphthyl methacrylate, 3-phenylpropyl methacrylate, phenoxyethyl methacrylate. Additional useful monomers are aromatic-containing acrylamides and methacrylamides such as N-phenylacrylamide and mixtures of acrylamides. The preferred ethylenically unsaturated aromatic substituted monomers are styrene and phenyl methacrylate.

0025All weight percentages for the monomers (i)-(iii) reflect a variance of ± 5%.

0026The dispersant also includes at least one polyalkylene glycol compound that is a polyalkylene glycol homopolymer, copolymer, or mixture thereof, to react with the reactive functionality of monomer (i) to impart water soluble character to the polymer. The polyalkylene glycol compound is present in an amount between about 20% and about 60% by weight, preferably between about 30% and about 40% by weight, based on total non-volatile content of the dispersant. The weight percentages reflect a variance of ±5%.

0027Useful compounds for this purpose are polyalkylene glycol monoalkyl ethers and mixtures thereof. Examples of these include polyalkylene glycol monoalkyl ethers formed from monoalcohol initiated polymerization of ethylene oxide, propylene oxide and mixtures thereof with up to 30% by weight propylene oxide. Starting monoalcohols are C₁-C₁₈ alcohols such as methanol, ethanol, n-propanol, iso-propanol, hexanol, decanol, undecanol and ether alcohols such as methoxyethanol, butoxyethanol and the like. The preferred monoalkyl ethers are polyethylene glycol monoalkyl ethers, and polyethylene glycol ethers in mixture with other polyalkylene glycol monoalkyl ethers.

0028The polyalkylene glycol compound reacts with the reactive functionality on monomer (i) to form a side chain. When the reactive functionality of monomer (i) is an isocyanate or an anhydride, the polyalkylene glycol compound reacts with the isocyanate or anhydride reactive functionality. The polyalkylene glycol compound can be reacted with monomer (i) before the addition polymerization reaction between monomers (i), (ii) and (iii). Alternatively, the polyalkylene glycol compound can be reacted with the functionalized copolymer after the polymerization of monomers (i)-(iii).

0029When the reactive functionality of monomer (i) is an epoxy functionality, the polyalkylene glycol must first be reacted with anhydride to form an acid functional polyalkylene glycol. The acid functional polyalkylene glycol can be reacted with the epoxy functional monomer before the polymerization reaction or with the functionalized copolymer after polymerization of monomers (i) and (ii) or (i)-(iii).

0030The dispersant also includes a pigment interactive substituent that is a urea-containing compound having the formula: <chemistry id="chem0002" num="0002"><img file="EP0589340A1_D0002.tif" /></chemistry> and mixtures thereof, wherein each R is independently selected from the group consisting of H, saturated and unsaturated aliphatic and alicyclic compounds that may be substituted or unsubstituted, substituted and unsubstituted aromatic compounds and divalent radicals such as, but not limited to - NH-, oxygen and sulfur, and wherein one R group has a functional group which can react with the reactive functionality on monomer (i). The R group having the reactive functional group is selected from the group consisting of monovalent alkyl radicals substituted with hydroxy and amino substituents, and ethylenically unsaturated groups substituted with amino, amide, carbonyl, carboxyl, epoxy, hydroxy, ether, ketone, aldehyde and ester functionalities and mixtures thereof.

0031In one embodiment, the R groups of the urea-containing compound are individually selected from the group consisting of H, alkyl and alkylene, and R'OH where R' is an alkylene group having from 1 to 4 carbon atoms and another R is a bond in this alkylene or is another alkylene radical.

0032In a preferred embodiment, the urea-containing compounds are omega hydroxy alkyl alkylene ureas and omega amino alkyl alkylene ureas. One such compound is 1-(2-hydroxyethyl)-2-imidazolidinone, also known as 2-hydroxyethyl ethylene urea. This compound has the formula: <chemistry id="chem0003" num="0003"><img file="EP0589340A1_D0003.tif" /></chemistry>    The urea-containing compound is present in an amount between about 1.0 and about 7.0 percent by weight, preferably between about 3.0 and about 5.0 percent by weight, based on total non volatile content of the dispersant. Weight percentages reflect a variance of ± 0.5 percent.

0033The method for adding the urea-containing compound to the reaction mixture is determined by the functional group on R that reacts with the reactive functionality on monomer (i). If the functional group on R is polymerizable across an ethylenically unsaturated double bond, the urea-containing compound is combined with monomers (i) and (ii) or (i)-(iii) and polymerized as described hereinafter. If the functional group on R that reacts with monomer (i) is not polymerizable, the urea-containing compound is added to the flask containing the copolymer, after completion of polymerization.

0034When the urea-containing compound is to be reacted with a monomer having an epoxy functionality, described above as monomer (i), or a copolymer having an epoxy functionality, formed by the polymerization of monomers (i) and (ii) or (i)-(iii), the urea must be acid functional. As described above, the polyalkylene glycol compound must also be acid functional to react with these epoxy functional monomers or polymers. The preferred method of the present invention is to form both the acid functional urea and the acid functional polyalkylene glycol in one reaction. This is accomplished by combining the polyalkylene glycol, urea and anhydride, which forms both acid functional polyalkylene glycol and urea. This mixture is then reacted with the epoxy functional monomer or epoxy functional copolymer.

0035The copolymer is formed by copolymerization using conventional techniques such as heating the monomers in the presence of a polymerization initiating agent and optionally chain transfer agents. The copolymerization may be carried out in bulk or solution. For the present invention it is preferred to form the copolymer by means of a free radical solution polymerization reaction. Solvents for solution polymerization should not have functional groups capable of reacting with the reactive functionalities on monomer (i).

0036Suitable solvents include ketones, such as methyl ethyl ketone, methyl propyl ketone and acetone; esters, such as butyl acetate and pentyl propionate; ethers, such as diethylene glycol dimethyl ether, dioxane, tetrahydrofuran; N-methyl pyrrolidone, ketoesters, aromatic hydrocarbons, alkanes, cyclic alkanes and mixtures thereof.

0037Typically initiators are peroxides such as dialkyl peroxides, peroxyesters, peroxydicarbonates, diacyl peroxides, hydroperoxides, and peroxyketals and azo compounds such as 2_,2'-azobis(2-methylbutanenitrile) and 1,1'-azobis (cyclohexanecarbonitrile).

0038Typical chain transfer agents are mercaptans such as octyl mercaptan, n- or tert- dodecyl mercaptan; halogenated compounds; thiosalicylic acid, mercaptoacetic acid, mercaptoethanol, buten-1-ol and dimeric alpha-methyl styrene. Mercaptans are preferred.

0039The reaction is usually carried out at temperatures from about 20°C to about 200°C. The reaction may conveniently be done at the temperature at which the solvent or solvent mixture refluxes, although with proper control a temperature below the reflux may be maintained. The initiator should be chosen to match the temperature at which the reaction is carried out, so that the half-life of the initiator at that temperature should preferably be between one minute and thirty minutes.

0040The solvent or solvent mixture is generally heated to the reaction temperature and the monomers and initiator(s) are added at a controlled rate over a period of time, usually between 2 and 6 hours. A chain transfer agent or additional solvent may also be fed in at a controlled rate during this time. The temperature of the mixture is then maintained for a period of time to complete the reaction. Optionally, additional initiator may be added to ensure complete conversion.

0041The NCO number of a copolymer formed from monomer (i) containing an isocyanate reactive functionality and monomer (ii) is from about 0.3 meq/g NV to 2.0 meq/g NV, preferably from about 0.9 meq/g NV to about 1.4 meq/g NV. The copolymer has a weight average molecular weight determined by GPC versus polystyrene standards of from about 3,000 to about 25,000, preferably from about 4,000 to about 10,000.

0042The polyalkylene glycol compound may be added before or after the polymerization of monomers (i) and (ii) or (i)-(iii). If the compound is added before the polymerization reaction, it is combined with monomer (i) and reacts with the reactive functionality on monomer (i). Monomer (i) is then polymerized with monomers (ii) and (iii). This is usually done by an addition polymerization reaction.

0043The polyalkylene glycol compound also may be added after the polymerization of monomers has occurred. In this case the polyalkylene glycol compound reacts with the reactive functionality on the copolymer to form a sidechain on the copolymer.

0044As described above, if non-polymerizable urea-containing compound is used, it is added to the flask containing the copolymer after polymerization is complete. If any unreacted isocyanate functionality remains after polymerization, the unreacted isocyanate may be capped by the addition of a compound having an amine or hydroxy group that reacts with the isocyanate.

0045The amine or hydroxy containing compound useful for capping the isocyanate is selected from the group consisting of mono or dialkyl amines, such as n-propyl amine, isopropyl amine, n-hexyl amine, 2-ethyl hexyl amine, n-decyl amine, stearyl amine; C₄-C₁₈ mono or dicycloalkyl amines, such as cyclopentyl amine, cyclohexyl amine, dicyclohexyl amine; heterocyclic C₄-C₁₈ amines, such as pyrrolidine, piperidine, and morpholine; aromatic C₆-C₁₈ amines, such as aniline, p-toluidine, o-toluidine, diphenyl amine, indole and indoline; araliphatic C₇-C₁₈ amines, such as benzyl amine, dibenzylamine and 2-phenyl ethylamine; C₂-C₃₆ mono and di alkanolamines, such as ethanol amine, diethanol amine, isopropanol amine, n-hexanol amine, n-undecanol amine. 3-aminopropanol, aminocyclohexanol, 2-(2-aminoethoxy) ethanol; C₁-C₃₆ ether alcohols, such as methoxyethanol, butoxyethanol, 1-butoxy-2-propanol, (butoxyethoxy) ethanol and solketal.

0046The amine or alcohol may be reacted in a stepwise reaction or simultaneously with the reactive functionality on the copolymer. The stepwise reaction is preferred. The reaction is usually carried out at temperatures of from about 50°C to about 130°C. The reaction may be carried out in the presence of the same organic solvents which have been used in the polymerization reaction and in the presence of a catalyst such as organic tin compounds and/or tertiary amine.

0047The final copolymers have a weight average molecular weight of from about 3,000 to about 25,000, preferably from about 5,000 to about 12,000. The molar ratio of hydrogen functionality on the amino or hydroxy containing compound to the reactive functionality on the copolymer is from about 0.8 to about 1.3 and preferably from about 0.8 to about 1.3.

0048Pigment pastes are prepared by dispersing pigments or dyestuffs in a solution of the copolymer in water with optional cosolvent and grinding in a ball mill, sand mill, cowlesmill, attritor, or continuous mill.

0049The pigment dispersant may be used with both inorganic or organic dye stuffs or pigments. Examples of these include graphite, carbon black, zinc chromate, strontium chromate, barium chromate, lead chromate, lead cyanide, titanium dioxide, zinc oxide, iron oxide, aluminum flakes, mica flakes, zinc sulfide, isoindolinones, phthalocyanine complexes, napthol red, carbazole violet, perylene reds, quinacridones, indanthrone, diketopyrrolopyrrole, and halogenated thioindigo pigments. The invention is a particularly useful dispersant for organic pigments.

0050For the preparation of pigment paste, the pigments or dyestuffs are dispersed in a solution of the copolymer in water with optional cosolvent, and ground in a ball mill or other mill. The pigment paste has a concentration of from about 10 to about 60% by weight of pigments based on the total weight of the pigment paste.

0051The pigment paste of the present invention is added to water dispersible film forming resin such as those described in Patent No. 4,794,147; 4,791,168; 4,518,724; and 4,403,085. These patents also describe the principle resin. Preferred principle resins are described in U.S. Patent Nos. 4,794,147 and 4,791,168.

0052The concentration of the pigment paste in the aqueous coating composition is from about 3 to about 25% by weight based on the total weight of the aqueous coating composition.

0053Coating compositions of the present invention are formulated by mixing the pigment dispersions of the present invention, along with other components, into water dispersible basecoat compositions. Examples of the water dispersible basecoat compositions include, but are not limited to, water dispersible film forming resins such as a water dispersible non-ionic polyurethane resin of the type disclosed in U.S. Patent 4,794,147, a water dispersible anionic polyurethane resin of the type of the type disclosed in U.S. Patent 4,791,168, or a water dispersible acrylic resin of the type disclosed in U.S. Patents 4,403,085 and 4,518,724. The resin is mixed with an aminoplast resin, polyisocyanate, or other suitable cross-linking agent, one or more rheology control agents if desired, water and a small amount of organic solvent if needed. Other agents may be included such as various fillers, surfactants, plasticizers, wetting agents, defoamers, adhesion promoters and catalysts in minor amounts.

0054Other additives may be used, such as organic solvents, catalysts, wetting agents, conditioning agents, thickeners, rheology control agents, antioxidants, surfactants, leveling agents and mixtures thereof.

0055The basecoat compositions containing the pigment dispersions of the present invention are applied to a metal or plastic substrate in one or more coats. The coating composition may be sprayed or electrostatically deposited onto metal or plastic substrates such as, for example, automotive vehicle bodies. Application may be made, for example, by an air atomizer (Binks Model 62 spray gun, available from the Binks manufacturing Corporation, Franklin Park, IL), or by using other conventional spray methods known in the art.

0056After being deposited, the basecoat compositions may be flash dried at a temperature sufficient to remove a portion of the solvent, but below that sufficient to cure the applied coating. Typically temperatures range from room temperature to about 145°F (63°C). After the first basecoat is deposited, a second basecoat and subsequent layer of basecoat, if needed or desired can be deposited over the first layer, either with or without flash drying. A clear, transparent top coat layer is then subsequently applied over the last basecoat layer. Any known unpigmented or transparently pigmented coating agent is, in principle, suitable for use as the topcoat material.

0057After the clear coat is applied over the basecoat layer(s), the multi-layer coating is then baked to cross-link and cure the polymeric materials and to drive the small amount of residual water and/or solvent from the coating layer(s). This baking step generally involves the heating of the coated substrate for periods of from about 10 to about 60 minutes and temperatures ranging between about 150°F (66°C) and about 300°F (149°C). The baking step cures the multi-layer coating to a hard, durable film.

0058The invention provides new urea-modified copolymers as dispersant for pigments in coating compositions. These copolymers stabilize dispersions of pigments in aqueous systems. These dispersants allow organic pigments to be more readily dispersed in pigment grinds. Without being bound to any theory, improved pigment dispersibility is believed to result from the increased potential of the polymeric resin to hydrogen bond to the pigment surface. The resulting dispersions provide increased formulating latitude and color styling potential in coating compositions.

0059Although certain embodiments of the invention have been selected for description in the examples, the examples are merely illustrative and do not in any way limit the scope of the invention as defined in the attached claims.

EXAMPLES

Example 1

Preparation of Isocyanate Functional Acrylic Copolymer 1

0060231.3 g (2.02 mol) of methyl amyl ketone was charged to a reaction vessel fitted with stirrer and condenser. The solvent was heated to reflux temperature and maintained at reflux for the duration of the reaction. A blend consisting of 94.8 g (0.91 mol) styrene, 160.7 g (1.13 mol) butyl methacrylate, 144.8 g (1.13 mol) butyl acrylate and 271.7 g (1.35 mol) 1-(1-isocyanato-1-methylethyl)-3-(1-methylethenyl) benzene, hereafter referred to as TMI®, available from American Cyanamid Co., Wayne, NJ 07470 , was slowly added over a period of three hours. 67.2 g of 50% active tert-butyl peracetate was added to the monomer blend to initiate the vinyl polymerization. 33.6 g of initiator along with 58.0 g of methyl amyl ketone were added one half hour after the addition of monomer was complete. The mixture was heated for an additional 1.5 hours and then cooled and collected for further modification.

Example 2

Preparation of Epoxy Functional Acrylic Copolymer 2

0061222.0 g (1.94 mol) of methyl amyl ketone was charged to a reaction vessel fitted with stirrer and condenser. The solvent was heated to reflux temperature and maintained at reflux for the duration of the reaction. A blend of 104.2 g (1.00 mol) styrene, 210.5 g (1.48 mol) butyl methacrylate, 131.0 g (1.02 mol) butyl acrylate, 72.1 g (0.50 mol) hydroxypropyl methacrylate and 142.2 g (1.00 mol) glycidyl methacrylate, was slowly added over a period of three hours. 66.0 g of 50% active tert-butyl peroxy acetate was added to the monomer blend to initiate the vinyl polymerization. 33.0 g of 50% active initiator along with 55.0 g methyl amyl ketone were added one half hour after the addition of monomer was complete. The mixture was heated for an additional 1.5 hours and then cooled and collected for further modification.

Example 3

Preparation of Anhydride Functional Acrylic Copolymer 3

0062A solvent blend of 110.0 g (0.96 mol) methyl amyl ketone and 20.0 g methyl propyl ketone was charged to a reaction vessel fitted with stirrer, water trap and condenser. The solvent blend was heated to reflux temperature and maintained at reflux for the duration of the reaction. A monomer blend of 65.4 g (0.63 mol) styrene, 111.6 g (0.78 mol) butyl methacrylate, and 100.6 g (0.78 mol) butyl acrylate, was slowly added over a period of three hours. 40.0 g of 50% active tert-butyl peroxy acetate was added to the monomer blend to initiate the vinyl polymerization. 122.4 g (0.94 mol) itaconic acid was added simultaneously with the monomer blend into the reaction vessel at 7.5 minute increment shots of solid itaconic acid, followed by washings of methyl amyl ketone (47.0 g total). 20.0 g of initiator and 30.0 g of methyl amyl ketone were added one half hour after the addition of monomer was complete. The mixture was heated for an additional 1.5 hours until 14-16 g of water were removed and then cooled and collected for further modification.

Example 4

Preparation of Isocyanate Functional Acrylic Copolymer 4

0063219.6 g (1.92 mol) methyl amyl ketone was charged to a reaction vessel fitted with stirrer and condenser. The solvent was heated to reflux temperature and maintained at reflux for the duration of the reaction. A blend consisting of 248.9 g (1.75 mol) butyl methacrylate, 224.3 g (1.75 mol) butyl acrylate, and 301.9 g (1.50 mol) TMI® was slowly added over a period of three hours. 77.5 g of 50% active tert-butyl peroxy acetate was added to the monomer blend to initiate the vinyl polymerization. 38.8 g of initiator and 58.4 g of methyl amyl ketone were added one half hour after the addition of monomer was complete. The mixture was heated for an additional 1.5 hours and then cooled and collected for further modification.

Example 5

Preparation of Modified Copolymer (Grind Resin) 1

0064112.0 g (0.56 mol), average molecular weight of 2000) methoxy polyethylene glycol, 16.5 g (0.13 mol) hydroxyethyl ethylene urea, 4.0 g of a 1% solution of dibutyltin dilaurate in methyl propyl ketone, and 300.0 g isocyanate-functional acrylic prepared in accordance with Example 1 were charged to a reaction vessel fitted with a stirrer and condenser. The mixture was heated to 120°C and maintained at that temperature for not more than two hours. At the end of this time, the mixture was titrated and the result indicated that all of the methoxy polyethylene glycol and hydroxyethyl ethylene urea had reacted with the isocyanate groups. The remainder of the isocyanate functionality was capped with 7.5 g (0.12 mol) monoethanolamine which was added over a period of 5-10 minutes while the mixture was stirred and the temperature was approximately 90°C. The temperature then rose to 100°C and then subsided. When the exothermic reaction had ceased, the mixture was titrated. Titration revealed no remaining isocyanate functionality. The material was subsequently dispersed with 10.0 g (0.55 mol) of deionized water.

Example 6

Preparation of Modified Copolymer (Grind Resin)2

006568.8 g (0.34 mol), average molecular weight of 2000) methoxy polyethylene glycol, 3.7 g of a 1% solution of dibutyltin dilaurate in methyl propyl ketone, and 300.0 g isocyanate-functional acrylic prepared in accordance with Example 1 were charged to a reaction vessel fitted with a stirrer and condenser. The mixture was heated to reflux and maintained at reflux for not more than one hour. At the end of this time, the mixture was titrated and the result indicated that all of the methoxy polyethylene glycol had reacted with the isocyanate groups. After the mixture had cooled to approximately 45°C, 16.5 g (0.13 mol) aminoethyl ethylene urea was added. The temperature then rose to 58°C and then subsided. The mixture was titrated and the result indicated that all of the aminoethyl ethylene urea had reacted with the isocyanate groups. The remainder of the isocyanate functionality was capped with 8.6 g (0.14 mol) monoethanolamine which was added over a period of 5-10 minutes while the mixture was stirred and the temperature was approximately 35°C. The temperature rose to 48°C and then subsided. When the exothermic reaction had ceased, the mixture was titrated. Titration revealed no remaining isocyanate functionality. The material was subsequently dispersed with 10.0 (0.55 mol) of deionized water.

Example 7

Red Pigment Paste 1

0066A red pigment paste was prepared by adding 22.50 parts by weight quinacridone pigment (C.I. Pigment Violet 19) to a stirred mixture of 3.22 parts by weight grind resin 1 prepared in accordance with Example 5 given above, 67.60 parts by weight deionized water, and 6.68 parts by weight ethylene glycol monobutyl ether. The resultant mixture was stirred on cowles for about thirty minutes and milled in an attritor for one and a half hours.

Example 8

Red Pigment Paste 2 (Control)

0067A red pigment paste was prepared by mixing 8.0 parts by weight quinacridone pigment (C.I. Pigment Violet 19) and 55.0 parts by weight nonionic polyurethane grind resin. After stirring this mixture for thirty minutes, 30.0 parts by weight nonionic polyurethane grind resin and 7.0 parts by weight deionized water were added and the resultant mixture milled on the attritor for two hours.

0068The nonionic polyurethane resin was prepared according to the teachings of United States Patent 4,794,147, the contents of which are incorporated herein by reference.

Example 9

Red Pigment Paste 3

0069A red pigment paste was prepared by adding 24.19 parts by weight diketopyrrolopyrrole pigment (C.I. Pigment Red 254) to a stirred mixture of 1.04 parts by weight grind resin 1, prepared in accordance with Example 5 given above, 68.04 parts by weight deionized water, and 6.73 parts by weight ethylene glycol monobutyl ether. The resultant mixture was stirred on cowles for about 30 minutes and milled on an attritor for one hour.

Example 10

Red Pigment Paste 4 (Control)

0070A red pigment paste was prepared by mixing 22.02 parts by weight diketopyrrolopyrrole pigment (C.I. Pigment Red 254) and 53.11 parts by weight nonionic polyurethane grind resin. After stirring this mixture for 30 minutes, 20.72 parts by weight nonionic polyurethane grind resin and 4.15 parts by weight deionized water were added and the resultant mixture milled on an attritor for two hours.

0071The nonionic polyurethane resin was prepared according to the teachings of United States Patent 4,794,147, the contents of which are incorporated herein by reference.

Example 11

Fumed Silica Paste

0072A fumed silica paste was prepared by mixing together 12.16 parts by weight Aerosil® R-972 fumed silica (Degussa Corporation, 2 Penn Plaza New York, NY), 31.36 parts by weight isopropanol, 17.10 parts by weight monobutyl ethylene glycol ether, and 5.90 parts by weight Resimene®, 747 methylated melamine formaldehyde resin, available from Monsanto Corp. 800 N. Lindbergh Blvd., St. Louis MO 63167. The resultant mixture was stirred on cowles for approximately thirty minutes after which 33.48 parts by weight nonionic polyurethane grind resin was added. The mixture was then run through a sand mill for two passes.

0073The nonionic polyurethane resin was prepared according to the teachings of United States Patent 4,794,147, the contents of which are incorporated herein by reference.

Example 12

Red Iron Oxide Tint Paste

0074A red iron oxide pigment paste was prepared by mixing 35.86 parts by weight nonionic polyurethane resin, 10.11 parts by weight deionized water, and 37.99 parts by weight RO-3097 iron oxide pigment (Pfizer Inc., 235 E. 42nd St. New York, NY). The resultant mixture was stirred on cowles for about thirty minutes and milled in an attritor for four hours.

0075The nonionic polyurethane resin was prepared according to the teachings of United States Patent 4,794,147, the contents of which are incorporated herein by reference.

Example 13

Coating Composition 1

0076A coating composition was prepared that contained dispersant-stabilized diketopyrrolopyrrole and quinacridone pigments prepared in accordance with the present invention above. <tables id="tabl0001" num="0001"><img file="EP0589340A1_D0004.tif" /></tables><tables id="tabl0002" num="0002"><img file="EP0589340A1_D0005.tif" /></tables>

0077Components 2 and 3 were premixed, then added to component 1 with rapid stirring. To this mixture were then added, successively with rapid stirring, components 4-9. After mixing of all components, stirring was continued for about one hour, after which the coating was filtered into a container and capped for later use.

Example 14

Coating Composition 2 (Control)

0078A coating composition was prepared having the same pigment concentrations as in Example 13, but the diketopyrrolopyrrole and quinacridone pigment grind was prepared using the nonionic polyurethane grind resin according to Examples 10 and 8 respectively. The procedure for the preparation of this coating composition is as described in Example 13. <tables id="tabl0003" num="0003"><table frame="all"><tgroup cols="2" colsep="1" rowsep="0"><colspec colnum="1" colname="col1" colwidth="78.75mm" /><colspec colnum="2" colname="col2" colwidth="78.75mm" /><thead valign="top"><row><entry namest="col1" nameend="col2" align="left">Coating Composition 2</entry></row><row><entry namest="col1" nameend="col1" align="center">Ingredient</entry><entry namest="col2" nameend="col2" align="center">Parts by weight</entry></row></thead><tbody valign="top"><row><entry namest="col1" nameend="col1" align="left">1. 3% Pluricol P-1010¹ and 3% Laponite RD² dispersion in water</entry><entry namest="col2" nameend="col2" align="char" char=".">19.62</entry></row><row><entry namest="col1" nameend="col1" align="left">2. Resimene® 747 methylated melamine formaldehyde resin³</entry><entry namest="col2" nameend="col2" align="char" char=".">9.92</entry></row><row><entry namest="col1" nameend="col1" align="left">3. Ethylene glycol monobutyl ether</entry><entry namest="col2" nameend="col2" align="char" char=".">2.48</entry></row><row><entry namest="col1" nameend="col1" align="left">4. Nonionic polyurethane resin dispersion⁴</entry><entry namest="col2" nameend="col2" align="char" char=".">15.02</entry></row><row><entry namest="col1" nameend="col1" align="left">5. Fumed silica dispersion (Example 11)</entry><entry namest="col2" nameend="col2" align="char" char=".">11.50</entry></row><row><entry namest="col1" nameend="col1" align="left">6. Red pigment paste 4(Example 10)</entry><entry namest="col2" nameend="col2" align="char" char=".">28.95</entry></row><row><entry namest="col1" nameend="col1" align="left">7. Red pigment paste 2 (Example 8)</entry><entry namest="col2" nameend="col2" align="char" char=".">9.46</entry></row><row><entry namest="col1" nameend="col1" align="left">8. Iron oxide tint (Example 12)</entry><entry namest="col2" nameend="col2" align="char" char=".">0.35</entry></row><row><entry namest="col1" nameend="col1" align="left">9. Nacure® 2500 blocked acid catalyst⁵</entry><entry namest="col2" nameend="col2" align="char" char=".">2.70</entry></row><row rowsep="1"><entry namest="col1" nameend="col1" /><entry namest="col2" nameend="col2" align="char" char="."><maths id="math0001" num=""><math display="inline"><mrow><mover accent="true"><mrow><mtext>100.00</mtext></mrow><mo>¯</mo></mover></mrow></math><img file="EP0589340A1_D0006.tif" /></maths></entry></row></tbody></tgroup><tgroup cols="2" colsep="0" rowsep="0"><colspec colnum="1" colname="col1" colwidth="78.75mm" /><colspec colnum="2" colname="col2" colwidth="78.75mm" /><tbody valign="top"><row><entry namest="col1" nameend="col2" align="justify">1Surfactant from BASF Corporation, 1419 Biddle, Wyandotte, MI 48192.</entry></row><row><entry namest="col1" nameend="col2" align="justify">²Synthetic bentonite clay from Laporte, Incorporated, Park 80 West, Plaza 11, Saddle Brook, NJ 07662.</entry></row><row><entry namest="col1" nameend="col2" align="justify">³Melamine crosslinker from Monsanto Corporation, 800 North Lindbergh Boulevard, St. Louis, MO 63167.</entry></row><row><entry namest="col1" nameend="col2" align="justify">⁴The nonionic polyurethane resin was prepared in accordance with the teachings of United States Patent 4,794,147.</entry></row><row><entry namest="col1" nameend="col2" align="justify">⁵Blocked Acid Catalyst from King Industries, P.O. Box 588, Science Road, Norwalk, CT 06852.</entry></row></tbody></tgroup></table></tables>