Partially crosslinked thermoplastic resin composition.

Background of the Invention

0001The present invention relates to a useful thermoplastic resin composition and more particularly to a thermoplastic resin composition prepared by dynamically heat-treating a thermoplastic resin using a carbon radical inducing agent and well-balanced in rigidity, impact resistance, flexibility and moldability.

0002Thermoplastic resins are used in various industrial fields as materials superior in moldability. The utilization field of thermoplastic resins has been expanded by blending them for modification with heterogeneous or homogeneous resins or fillers having various properties. Further, various attempts have been made for attaining effects of such blending, e.g. improvement of impact resistance and heat resistance, by heat-treating the resulting mixtures dynamically. As an example, there is known a process of heat-treating a thermoplastic resin dynamically using an organic peroxide.

0003However, the composition obtained by such process using an organic peroxide is desired to be remedied in the following points although it has advantages. For example, as shown in U.S. Patent No. 3,806,558, a free radical forming agent typified by organic peroxides is used, so in the case where the thermoplastic resin used is an organic peroxide non-crosslinked type resin such as, for example, a polypropylene resin, although the resulting composition will exhibit good fluidity during injection molding, the organic peroxide remaining in the composition will cause deterioration of the thermal stability and weathering resistance and there will occur a thermal decomposition of the organic peroxide rapidly, resulting in that a molecular cutting reaction is unavoidable, thus leading to deterioration of mechanical characteristics such as yield tensile strength, bending strength and flexural modulus.

0004Besides, if the said composition is used in extrusion or blow molding, there will arise such problems as deteriorated anti-drawdown property, surface roughening of parison and deficient elongation. It has also been pointed out that when the composition is used in injection molding, the gloss of the resulting molded product deteriorates, thus affecting the beauty of the product as commodity.

0005On the other hand, in the case where the thermoplastic resin used is an organic peroxide crosslinked type resin such as a polyethylene resin, it becomes difficult to perform molding because the fluidity of the resulting composition is reduced markedly, so it is required that the amount of an organic peroxide used be extremely small. In this case, it is difficult to handle such trace amount of an organic peroxide. Further, in the use of an organic peroxide there inevitably arise problems in point of stability and safety during storage and dynamic heat treatment of a free radical forming agent, as well as thermal decomposition loss caused by the deposition on the inner wall of a processing machine. Therefore, it has been desired to solve these problems.

0006The following processes are known as processes for crosslinking a thermoplastic resin containing rubber and having a carbon-carbon unsaturated bond.

0007As the first process, the use of a sulfur-based crosslinking agent is proposed in U.S. Patent No. 4,130,535. However, when such thermoplastic resin is dynamically heat-treated in the presence of a sulfur-based crosslinking agent, which causes the formation of sulfur radical, not only is a very offensive odor emmited at an ordinary kneading temperature, but also the resulting composition emits an offensive odor. This offensive odor of the composition is emitted again in a plasticizing step during molding, thus reducing the commercial value markedly. Moreover, since this composition is colored yellowish red, the coloring freedom of the composition is restricted. Further, during use over a long period, there may occur discoloration due to bleeding of the sulfur compound and hence the application field is restricted.

0008As the second process, it is proposed in U.S. Patent No. 4,311,628 and Japanese Patent Publication No. 19421/1979 to use a crosslinking agent comprising a halogenated phenolic resin or a phenol-formaldehyde resin with a halide incorporated therein. However, since the active halogen is liberated during crosslinking reaction, the resulting composition is discolored to black and thus the coloring freedom is lost. Besides, the fluidity of the composition is not good.

0009As the third process, in the above Japanese Patent Publication No. 19421/1979 it is proposed to use a quinone dioxime compound for crosslinking. However, since quinone dioximes are dark purple, the coloring freedom of the resulting composition is greatly restricted, and a pungent odor is emitted during dynamic heat treatment. Also as to the composition obtained by this process, it cannot be said that the fluidity thereof during molding is good.

0010As the fourth process, in U.S. Patent Nos. 4,104,210 and 4,130,535 there is shown an example of using a bismaleimide compound or a combined use thereof with a thiazole compound. In the former, N,N'-m-phenylene bismaleimide is used for a highly unsaturated diene rubber, but it must be used in a large amount for attaining a predetermined crosslinking effect, thus giving rise to problems such as coloration of the resulting composition and bleeding of unreacted portion. In the latter, N,N'-m-phenylene bismaleimide is also used in polypropylene/EPDM system, but as to the effect of modification by dynamic heat treatment, extremely unsatisfactory results have been reported. Further, since bismaleimide compounds are generally expensive, the use thereof in a large amount causes an increase of cost.

0011Thus, although various crosslinking processes are known, it is desired to develop a more efficient process.

0012Having made extensive studies in view of the above-mentioned points, the present inventors have found a crosslinking reaction using a carbon radical inducing agent which avoids the reckless and excessive crosslinking reaction which is a drawback of organic peroxides in the prior art. It is the object of the invention to provide a thermoplastic resin composition prepared by such crosslinking reaction of a thermoplastic resin using a carbon radical inducing agent and free of the drawbacks of the conventional processes.

Summary of the Invention

0013As a result of having made studies earnestly along the above-mentioned object, the present inventors have found out that a partially crosslinked thermoplastic resin composition obtained by dynamically heat-treating a thermoplastic resin in the presence of a carbon radical inducing agent could afford remarkably excellent results in comparison with the use of a conventional crosslinking agent.

0014More specifically, the present invention resides in a partially crosslinked thermoplastic resin composition prepared by dynamically heat-treating a thermoplastic resin (A) in the presence of a carbon radical inducing agent (B) which is formed from a material containing a charge transfer complex or a material containing both a hydrogen donating compound and a hydrogen accepting compound.

Detailed Description of the Invention

0015The present invention will be described in detail hereinunder.

0016As examples of the thermoplastic resin(s) used in the present invention there are mentioned substantially crystalline polyolefin resins such as crystalline polypropylene, propylene-a-olefin random block copolymers, high and medium density polyethylenes, polybutene-1, poly-4-methylpentene-1, high pressure process low-density polyethylenes, linear low-density polyethylenes, very low density polyethylenes, ethylene-unsaturated carboxylate copolymers, and ethylene-carboxylic acid unsaturated ester copolymers; as well as polystyrene resins, polyacrylonitrile resins, poly(meth)acrylate resins, polyamide resins, polyester resins, polycarbonate resins, polyphenylene resins, polyphenylene ether resins, polyphenylene sulfide resins, polyphenylene sulfone resins, polyacetal resins, and mixtures thereof.

0017The thermoplastic resin used in the invention may contain a rubbery substance. Examples of such rubbery substance include ethylene-a-olefin copolymer rubbers such as ethylene-propylene random copolymer rubber and ethylene-propylene-diene random copolymer rubber, 1,2-polybutadiene, styrene-butadiene-styrene block copolymer rubber, styrene-isoprene-styrene block copolymer rubber, natural rubber, nitrile rubber, and isobutylene rubber. These may be used each alone or as mixtures. Particularly, ethylene-propylene random copolymer rubber and ethylene-propylene-diene random copolymer rubber are preferred. These two rubbers, as compared with the other rubbery substances, are superior in thermoplasticity and can be easily dispersed by melt kneading. Besides, they do not have any peculiar odor in comparison with SBR, isoprene rubber, nitrile rubber and butadiene rubber. Further, the two rubbers in question are available as pellets so are easy to weigh and handle in the mixing operation, and also as to the type of the composition manufacturing apparatus, they have a high degree of freedom in selection. Thus, they have advantages in operation.

0018As the diene component in the above ethylene-propylene-diene random copolymer rubber there may be used any of known dienes, including ethylidene norbornene, 1,4-hexadiene and dicyclopentadiene.

0019In the present invention, a wide variety of crosslinked thermoplastic resin compositions having various characteristics can be obtained by changing the kind and proportion of the thermoplastic resin used. The thermoplastic resin to be used can be selected optionally from among those exemplified above. For example, a combination of a polyolefin resin and a heterogeneous thermoplastic resin, a combination of polyolefins with each other, or a combination of a polyolefin resin and a rubbery substance, can be selected. In this case, since the heterogeneous thermoplastic resin is melt-kneaded with a polyolefin resin or a rubbery substance, it is preferable that the heterogeneous thermoplastic resin be selected from among thermoplastic resins which are relatively close in melting point or softening point to the polyolefin resin or the rubbery substance.

0020In the case of combining polyolefin resins with each other, a combination of polypropylene and ethylene (co)polymer is a preferable combination because it is superior in the balance of physical properties and can be obtained inexpensively. Polypropylenes are superior in heat resistance and rigidity, and ethylene (co)polymers are widely available, ranging from those rich in flexibility up to those rich in rigidity, typical of which are high pressure process low-density polyethylenes, high density polyethylenes, linear low-density polyethylenes, very low density polyethylenes, ethylene-unsaturated carboxylate copolymers, and ethylenecarboxylic acid unsaturated ester copolymers. Compositions obtained using these polyolefin resins alone can satisfy a wide range of physical properties.

0021A combination of a polyolefin resin just exemplified above and a rubbery substance is also a preferable combination, which can satisfy a wider range of physical properties than in the combination of only polyolefin resins. For example, the low-temperature impact resistance can be improved remarkably.

0022As to a concrete blending ratio, it is preferable that the proportion of the polyolefin resin be in the range of 20 to 100 wt% and that of the rubbery substance 0 to 80 wt%. An amount of the rubbery substance exceeding 80 wt% is not desirable because it becomes difficult to effect processing.

0023In the present invention, a softening agent may be used during and/or after the heat treatment. As the softening agent there may be used an oil commonly called extender oil which is used mainly for the improvement of processability in rubber processing, for attaining an extending effect, orfor improving the dispersibility of filler. Such extender oils are high-boiling petroleum components, which are classified into paraffinic, naphthenic and aromatic components. In addition to these petroleum distillates, synthetic oils such as liquid polyisobutene, are also employable.

0024The carbon radical inducing agent used as an essential component in the dynamic heat treatment comprises a charge transfer complex or a combination of a hydrogen donating compound and a hydrogen accepting compound.

0025The charge transfer complex is used as a combination of compounds. In this combination, upon formation of the complex, an electric charge is transferred from one compound to the other for radical cleavage of unsaturated bond. Various known combinations are employable for this purpose provided there is a difference in the electron density of unsaturated bond. As preferred examples of compounds which are low in the electron density of an unsaturated bond there are mentioned maleimide compounds (e.g. N,N'-m-phenylene bismaleimide and N,N'-ethylene bismaleimide) and unsaturated carboxylic acid derivatives (e.g. maleic anhydride and ethylene glycol dimethacrylate). Bismaleimide compounds are preferred because even if there remains a compound which has not participated in the radical formation, it functions as an ordinary crosslinking aid. In the case of unsaturated carboxylic acid derivatives, a compound which has not been concerned in the radical formation reacts graftwise with the thermoplastic resin and creates the action as an adhesive or as a compatibil izing agent. Therefore, when it is desired to attain such effect, the use of an unsaturated carboxylic acid derivative is par- ticulady preferred. As the compound which forms a charge transfer complex together with such unsaturated carboxylic acid derivative there is used a compound which is high in the electron density of unsaturated bond. Examples are a-methylstyrene, transstilbene, vinylferrocene, 4-vinylpyridine, 2-isopropenylnaphthalene, N-vinylcarbazole, N-vinylindole, and indole. Also, there are mentioned cyclic vinyl ethers typified by furan, 3,4-dihydro-2-pyran and 4H-chromene; furan derivatives typified by furfuryl alcohol, furfuryl aldehyde, benzofuran and furfuryl acetate; straight-chain vinyl ether compounds typified by n-octadecyl vinyl ether and ethyl vinyl ether; enol ethers and enol esters of carbonyl compounds such as ketones, esters, lactones, aldehydes, amides and lactams typified ketene acetal, isopropenyl acetate and 1-amino-1-methoxyethylene; alkenyl acetate, 1,2-dimethoxyethylene, p-dioxene, 2-chloroethyl vinyl ether, 2-phenylalkenyl ether, heptafluoroisopropyl alkenyl ether, ethyl vinyl sulfide, styrylalkenyl thioether, p-oxadiene, cyclopentene, cyclohexene, divinyl ether, butadiene, isoprene, 1,3-pentadiene, 1,4-pentadiene, and dimethyldivinylsilane.

0026It is preferable that the said complex be present as radical without forming an alternating copolymer.

0027Next, the combination of a hydrogen donating compound and a hydrogen accepting compound indicates a combination wherein hydrogen atom is transferred from the former to the latter and both are radicalized. The hydrogen donating compound indicates a compound which per se can be stabilized resonantly even after the release of hydrogen radical. When viewed from the standpoint of characteristics, this compound indicates a compound which when reacted at 350°C, 50 atm. (in a nitrogen gas atmosphere), for 30 minutes in the absence of catalyst, exhibits an amount of hydrogen transfer from this compound to anthracene as a hydrogen acceptor of at least 0.1 (hydrogen atom/mol anthracene). Examples are octahydrophenanthrene, tetralin, indene, tetrahydrofuran, 2,3-dihydrobenzofuran, and fluorene. Particularly, octahydrophenanthrene, octahyd- roanthracene, tetralin, indene and fluorene are superior in that they are available easily and do not decompose esters and amides and in that the resulting compositions are not colored. The hydrogen accepting compound is a compound which is not so highly stabilized resonantly as radical after the addition of hydrogen radical thereto. Usually there is employed a compound which is used as a crosslinking aid in the crosslinking of rubber using a peroxide. As examples there are mentioned polyfunctional vinyl monomers typified by trimethylolpropane trimethacrylate, ethylene glycol di(meth)acrylate, triallyl (iso)cyanurate, and diallyl phthalate. However, in view of the high reactivity as radical, it is desirable to use maleimide compounds (e.g. N,N'-m-phenylene bismaleimide) and unsaturated carboxylic acid derivatives (e.g. maleic anhydride and ethylene glycol dimethacrylate). These inducing agents may be used each alone or in combination.

0028A particularly preferred combination comprises (B1) a compound having an unsaturated bond of a high electron density or a hydrogen donating compound and (B2) a compound having an unsaturated bond of a low electron density or a hydrogen accepting compound. A combination comprising a compound as (B1) selected from (a) ether compounds, (p) tetrahydroaromatic compounds and (y) cyclopentane compounds and a compound as (B2) selected from (8) bismaleimide compounds and (s) polyol unsaturated ester compounds is high in activity and particularly preferred.

0029The ether compounds (a) may be straight-chained or cyclic and may contain a substituent group. Examples are cyclic ethers such as 1,3-dioxolane and 1,4-dioxane; straight-chain ethers such as ethyl ether and isopropyl ether; non-aromatic cyclic vinyl ethers typified by 3,4-dihydro-2-pyran and 4H-chromene; furan derivatives typified by furfuryl alcohol, furfuryl aldehyde, benzofuran and furfuryl acetate; straight-chain vinyl ether compounds typified by n-octadecyl vinyl ether and ethyl vinyl ether; enol ethers and enol esters of carbonyl compounds such as esters, lactones, aldehydes, amides and lactams typified by ketene acetal, isopropenyl acetate, vinyl acetate and 1-amino-1-methoxyethylene. These compounds may contain substituent groups. Alkyl-substituted compounds as well as derivatives substituted with various elements and functional groups are employable. And these compounds may be used each alone or as mixtures. Particularly, vinyl or alkenyl ethers are preferred.

0030The tetrahydroaromatic compounds (β) indicate compounds containing one or more aromatic rings, at least one of which is tetrahydrogenated. The aromatic ring as referred to herein indicates a ring structure having 4n + 2 (n is an integer) of Tc-electrons shown in the definition of aromaticity [see, for example, "Yuki Kagaku-no Kiso," Tokyo Kagaku Dojin K.K. (1976), translated by Toshio Goto, pp. 105-106, (Richard S. Mon-son & John C. Shelton, "Fundamentals of Organic Chemistry," MacGraw-Hill, Inc. (1974)]. Benzene and naphthalene are included as examples, while pyran is excluded. Therefore, examples of the tetrahydroaromatic compounds employable in the present invention include tetrahydro derivatives of naphthalene. Further, the tetrahydroaromatic compounds employable in the invention may contain substituent groups. Alkyl-substituted compounds, as well as derivatives substituted with various elements and functional groups, are also employable.

0031The tetrahydroaromatic compounds employable in the invention can be prepared by a known chemical reaction. Examples of those available at present are 1,2,3,4-tetrahydronaphthalene, tetrahydrobenzene, and tetrahydrofuran. Polymers of these compounds are also employable.

0032The cyclopentane compounds (y) indicate compounds containing at least one cyclopentane, cyclopentene or cyclopentadiene skeleton. That is, the cyclopentane compounds (y) are compounds of a five-membered ring which is constituted by only carbon atoms. Examples are cyclopentane, cyclopentene, cyclopentadiene, dicyclopentadiene, indene, indane, and fluorene. Of course, these compounds may contain substituent groups. Alkyl-substituted compounds and derivatives substituted with various elements and functional groups are employable. And these compounds may be used each alone or as mixtures.

0033Preferred examples of the bismaleimide compounds (8) are ethylene bismaleimide and N,N'-m-phenylene bismaleimide.

0034As examples of the polyol unsaturated ester compounds (s) there are mentioned higher esters of methacrylic acid, typical of which are trimethylolpropane methacrylate and ethylene glycol dimethacrylate.

0035In addition to the components (8) and (s) exemplified above there also are employable polyfunctional vinyl monomers, typical of which are divinylbenzene, triallyl isocyanurate, and diallyl phthalate. These compounds may be used in combination.

0036In the present invention, a mixture comprising components obtained as above is subjected to a dynamic heat treatment to afford a resin composition. The dynamic heat treatment as referred to herein means increasing the value of boiling xylene insolubles content in the composition after melt-kneading of the mixture in comparison with the value before the melt-kneading. The effects of the present invention are attained by this heat treatment. Generally, the higher the boiling xylene insolubles content, the more remarkable the improvement of various effects, including that of impact resistance.

0037The temperature of the dynamic heat treatment should be not lower than the melting point or softening point of the thermoplastic resin used and below the decomposition point of the resin. Preferably, the melt kneading is performed using a mixing machine which affords a high shear rate to facilitate the formation of radicals in the mixture.

0038The boiling xylene insolubles content is increased mainly by adjusting the amount of the carbon radical inducing agent used, which amount can be selected optionally. An appropriate amount is adopted on the basis of the kind of the carbon radical inducing agent used, the type of the melt-kneading apparatus used and conditions for the melt kneading. If the carbon radical inducing agent is used in an excessive amount, there will occur bleeding of the components added, coloration of the resulting composition, or increase of cost. Therefore, the amount of the carbon radical inducing agent to be used may be restricted in consideration of these points. A practical amount is usually in the range of 0.01 to 7, preferably 0.05 to 5, parts by weight based on 100 parts by weight of the resin used.

0039The dynamic heat treatment can be carried out using any known melt-kneading apparatus, including open type mixing rolls, non-open type Bumbury's mixer, extruder, kneader, and twin-screw extruder. In the composition described above the dynamic heat treatment is preferably conducted at a kneading temperature of 120° to 350°C and for 20 seconds to 20 minutes as a heat treatment time. Further, this treatment may be conducted in a solvent.

0040If necessary, in the composition of the present invention there may be incorporated stabilizer, anti-oxidant, ultraviolet ray absorber, lubricant, foaming agent, antistatic agent, dye, pigment, glass fiber, carbon fiber, inorganic filler, flame retardant, etc.

0041According to the present invention, as described above, an excessive crosslinking reaction which is a drawback involved in the use of a conventional crosslinking agent can be suppressed by dynamically heat-treating a thermoplastic resin using a carbon radical inducing agent. By using such a dynamically heat-treated thermoplastic resin it is made possible to obtain a composition which is crosslinked partially to a desired extent in the range from a very slightly crosslinked state up to a greatly crosslinked state. Besides, physical properties could be improved remarkably.

[Examples and Comparative Examples]

0042The present invention will be described below concretely using working and comparative examples, but it is to be understood that the invention is not limited thereto.

Examples 1-21 and Comparative Examples 1-21

0043As thermoplastic resins (A) there were used polypropylene resin, low density polyethylene resin, high density polyethylene resin, linear low-density polyethylene resin, very low density polyethylene resin, ethylene-propylene random copolymer rubber, ethylene-ethyl acrylate copolymer, and polyamide resin.

How to Prepare Composition

00443 parts by weight of a carbon radical inducing agent (B1) selected from (a), (β), (y) and 2 parts by weight of a carbon radical inducing agent (B2) selected from (8), (s) were mixed with 100 parts by weight of a thermoplastic resin (A) referred to above (various combinations were used as set forth in Table 1). The resulting mixture was melt-kneaded in a Plastomill (20R200, a product of Toyo Seiki K K.) under the conditions of reaction temperature 230°C, reaction time 5 minutes and 60 r.p.m. In the melt-kneading operation, torque was observed. After the reaction, boiling xylene insolubles content was determined.

0045The resulting composition was formed into a 30 µ thick film using a 40 mm-dia. extruder (L/D = 20) under the conditions of spiral die diameter 125 mm and lip 2 mm, blow ratio 1.8 and processing temperature 200°C. Then, physical properties of the film were measured.

0046The results obtained are asshown in Table 2, in which the results of Comparative Examples were obtained by kneading without using a carbon radical inducing agent and in which the "Torque" is represented in terms of rise (t) or unchanged (-+).

Testing and Measuring Methods

0047(Yield Tensile Strength)

0048According to ASTM D882.

0049(Boiling Xylene Insolubles Content)

0050A 20 mm x 50 mm x 0.2 mm film formed by pressing was put on a 120-mesh wire gauze and immersed in boiling xylene for 5 hours. Then, the weight of the film before the immersion and that after the immersion were measured, and a boiling xylene insolubles content was determined from the following equation:<maths id="math0001" num=""><img file="EP0457550A2_D0001.tif" /></maths>

Examples 22-46 and Comparative Examples 22-49

0051Mixtures of components selected from polypropylene resin, high density polyethylene resin, linear low-density polyethylene resin, polystyrene resin, polyamide resin, polyester resin and ethylene-propylene random copolymer rubber were used. Test pieces were prepared by subjecting injection-molded products to an annealing treatment unless otherwise described.

0052The following are how to prepare compositions, conditions for preparing test pieces by injection molding and testing methods.

How to Prepare Composition

0053<ul id="ul0001" list-style="none"><li>1) The above thermoplastic resins were mixed in predetermined proportions using a Henschel mixer.</li><li>2) Predetermined amounts of carbon radical inducing agents (B1) and (B2) were added to the mixtures obtained above, followed by melt-kneading for dynamic heat treatment at resin temperatures of 180-260°C and a revolution of 200 r.p.m., using a continuous twin-screw kneader/extruder (diameter 30 mm, a product of Plastic Kogaku Kenkyu-Sho K.K.).</li></ul>

Conditions for Injection Molding

0054<ul id="ul0002" list-style="none"><li>Molding Machine : IS-90B (a product of Toshiba Machine Co., Ltd</li><li>Injection Pressure 1,000 kg/cm²</li><li>Molding Temperature 180-260°C</li><li>Mold temperature : 50°C</li></ul>

Testing and Measuring Methods

(MFR)

0056According to JIS K6760, K6758 and K7210.

0057(Ultimate Tensile Strength) and (Ultimate Elongation Length)

0058According to JIS K6760, K6758, K7113, and ASTM D882.

0059(Flexural Modulus)

0060According to JIS K6758 and K7203.

0061(Vicat Softening Temperature)

0062According to JIS K6760, K6758 and K7206.

0063(Izod Impact Value)

0064According to JIS K6758 and K7110.

0065(Crystallization Temperature)

0066Crystallization temperature was measured as an index of cycle time in injection molding. Since the higher the crystallization temperature, the higher the crystallizing speed, it can be considered that the cycle time in injection molding can be shortened. Using a differential scanning calorimeter (SSC/580, a product of Seiko Den- shi Kogyo K.K.), about 10 mg of a sample was held at 210°C for 5 minutes, then cooled at a rate of 10°C/min, and the temperature exhibiting a peak in the resulting exotherm curve was used as a crystallization temperature.

0067The results obtained are as shown in Tables 3 to 5, in which the proportions of carbon radical inducing agents are based on 100 parts by weight of the thermoplastic resins (this also applies to the tables which follow those tables).

Examples 47-54 and Comparative Examples 50-56

0068As thermoplastic resins there were used 70-90 wt% of very low density polyethylenes. Test pieces were prepared by forming a flat plate of 100 mm x 200 mm x 2 mm by injection molding and then punching the flat plate into a predetermined size. The composition preparing process was the same as above, except that in the melt-kneading step 2) there were used resin temperatures in range of 150° to 220°C, and where required, a mineral oil- or synthetic oil-based softening agent was added from a reciprocating fixed displacement pump connected to a vent hole.

0069The following testing methods were used.

Testing and Measuring Methods

0070(High Load MFR)

0071According to JIS K7210, at a temperature of 230°C and a load of 10 kg.

0072(Ultimate Tensile Strength) and (Ultimate Elongation Length)

0073According to JIS K6301, at a pulling rate of 200 mmlmin.

0074(Durometer Hardness, H_DA)

0075According to ISO 868.

0076(Permanent Elongation)

0077According to JIS K6301, 100% elongation, using No. 3 dumbbell.

0078(Vicat Softening Temperature)

0079According to JIS K7206, at a load of 250 g.

0080(Bnttle Temperature)

0081According to JIS K6760 and K7216.

0082(Abrasion Resistance)

0083According to JIS K7204 (using a Taber abrasion tester), at a load of 1,000 g and continuous 1,000 revolutions.

0084The results obtained are as shown in Table 6. The proportion of the softening agent in Table 6 is based on 100 parts by weight of the total resin weight (also in Table 7).

Examples 55-62 and Comparative Examples 57, 58

0085Mixtures of components selected from polypropylene resin, low density polyethylene resin, very low density polyethylene resin, ethylene-ethyl acrylate copolymer resin and ethylene-propylene random copolymer rubber were used. How to prepare compositions and test pieces and conditions for injection molding to prepare test pieces are the same as in Examples 47-54.

0086Testing methods are as follows.

Testing and Measuring Methods

0087(Spiral Flow)

0088A sample was prepared by injection molding using a mold having a cavity of a certain spiral and under the following molding conditions. Then, the length of the spiral thus formed was measured to check the melt flow property of the sample.

Conditions for Injection Molding

0089<ul id="ul0003" list-style="none"><li>Molding Machine : IS-90B (a product of Toshiba Machine Co., Ltd.)</li><li>Injection Pressure 1,000 kg/cm²</li><li>Molding Temperature : 230°C</li><li>Stroke : 25 mm</li><li>Injection Time : 15 sec</li><li>Curing Time : 10 sec</li><li>Interval Time : sec</li><li>Mold : Archimedes type, Temperature 50°C</li></ul>

0090(Bending Strength)

0091According to JIS K6758 and K7203.

0092(Durometer Hardness, H_DD)

0093According to JIS K6760 and K7215.

0094(Surface Roughening and Elongation of Parison)

0095Parison was formed in the same manner as above, using an extruder for blow molding, and then visually checked and evaluated for the state of its surface and elongation. The evaluation was made in the following three stages: <ul id="ul0004" list-style="none"><li>Ⓞ: Very Good, O : Good, ×: Bad</li></ul>

0096The results obtained are as shown in Table 7.

0097The following are the thermoplastic resins, carbon radical inducing agents, etc. used in the above Examples and Comparative Examples.

Thermoplastic Resin (A)

0098<ul id="ul0005" list-style="none"><li>A1. Very low density polyethylene, Nisseki Softrex D9010, d = 0.900 g/cm³, MFR 0.9, a product of Nippon Petrochemicals Co.. Ltd.</li><li>A2. Very low density polyethylene, Nisseki Softrex D9005, d = 0.900 g/cm³, MFR 0.5, a product of Nippon Petrochemicals Co., Ltd.</li><li>A3. Very low density polyethylene, Nisseki Softrex D9550, d = 0.905 g/cm³, MFR 5.0, a product of Nippon Petrochemicals Co., Ltd.</li><li>A4. Polypropylene, Nisseki Polypro J120G, MFR 1.5, a product of Nippon Petrochemicals Co., Ltd.</li><li>A5. Polypropylene, Nisseki Polypro J130G, MFR 4.0, a product of Nippon Petrochemicals Co., Ltd.</li><li>A6. Polypropylene, Nisseki Polypro J150G, MFR 8.0, a product of Nippon Petrochemicals Co., Ltd.</li><li>A7. Polypropylene, Nisseki Polypro J160G, MFR 14, a product of Nippon Petrochemicals Co., Ltd.</li><li>A8. Polypropylene, Nisseki Polypro J170G, MFR 30, a product of Nippon Petrochemicals Co., Ltd.</li><li>A9. Polypropylene, Nisseki Polypro J420G, MFR 1.5, a product of Nippon Petrochemicals Co., Ltd.</li><li>A10. Polypropylene, Nisseki Polypro J630G, MFR 4.0, a product of Nippon Petrochemicals Co., Ltd.</li><li>A11. Polypropylene, Nisseki Polypro J650G, MFR 8.0, a product of Nippon Petrochemicals Co., Ltd.</li><li>A12. Polypropylene, Nisseki Polypro J871 M, MFR 23, a product of Nippon Petrochemicals Co., Ltd.</li><li>A13. Polypropylene, Nisseki Polypro J880G, MFR 40, a product of Nippon Petrochemicals Co., Ltd.</li><li>A14. Linear low-density polyethylene, Nisseki Linirex AF121 0, d = 0.920 glcm³, MFR 0.8, a product of Nippon Petrochemicals Co., Ltd.</li><li>A15. Linear low-density polyethylene, Nisseki Linirex AJ5610, d = 0.934 g/cm³, MFR 10, a product of Nippon Petrochemicals Co., Ltd.</li><li>A16. Linear low-density polyethylene, Nisseki Linirex AJ6820, d = 0.942 glcm³, MFR 30, a product of Nippon Petrochemicals Co., Ltd.</li><li>A17. Linear low-density polyethylene, Nisseki Linirex AJ6285, d = 0.916 g/cm³, MFR 32, a product of Nippon Petrochemicals Co., Ltd.</li><li>A18. Low density polyethylene, Nisseki Rexlon F102, d = 0.922 g/cm³, MFR 0.25, a product of Nippon Petrochemicals Co., Ltd.</li><li>A19. Low density polyethylene, Nisseki Rexlon F22, d = 0.924 g/cm³, MFR 1.0, a product of Nippon Petrochemicals Co., Ltd.</li><li>A20. Low density polyethylene, Nisseki Rexlon F312, d = 0.925 glcm³, MFR 2.0, a product of Nippon Petrochemicals Co., Ltd.</li><li>A21. Low density polyethylene, Nisseki Rexlon F504, d = 0.917 g/cm³, MFR 9.5, a product of Nippon Petrochemicals Co., Ltd.</li><li>A22. Ethylene-Ethyl acrylate copolymer, Nisseki Rexlon EEA A3050, MFR 3.0, EA content 5 wt%, a product of Nippon Petrochemicals Co., Ltd.</li><li>A23. Ethylene-Ethyl acrylate copolymer, Nisseki Rexlon EEA A3100, MFR 3.0, EA content 10 wt%, a product of Nippon Petrochemicals Co., Ltd.</li><li>A24. Ethylene-Ethyl acrylate copolymer, Nisseki Rexlon EEA A3150, MFR 3.0, EA content 15 wt%, a product of Nippon Petrochemicals Co., Ltd.</li><li>A25. Ethylene-Ethyl acrylate copolymer, Nisseki Rexlon EEA A4250, MFR 5.0, EA content 25 wt%, a product of Nippon Petrochemicals Co., Ltd.</li><li>A26. High density polyethylene, Nisseki Staflene E809(M), d = 0.950 glcm³, MFR 0.9, a product of Nippon Petrochemicals Co., Ltd.</li><li>A27. High density polyethylene, Nisseki Staflene E750 (C), d = 0.963 g/cm³, MFR 5.3, a product of Nippon Petrochemicals Co., Ltd.</li><li>A28. High density polyethylene, Nisseki Staflene E807 (F), d = 0.950 g/cm³, MFR 0.6, a product of Nippon Petrochemicals Co., Ltd.</li><li>A29. Ethylene-Propylene random copolymer ru bber, EP02P, ML₁₊₄= 4, a product of Japan Synthetic Rubber Co., Ltd.</li><li>A30. Ethylene-Propylene random copolymer rubber, EP07P, ML₁₊₄=70, a product of Japan Synthetic Rubber Co., Ltd.</li><li>A31. Ethylene-Propylene-Diene random copolymer rubber, EP57P, ML₁₊₄=88, a product of Japan Synthetic Rubber Co., Ltd.</li><li>A32. 6-Nylon, CM1021, a product of Toray Industries Inc.</li><li>A33. Polystyrene, Toporex 525, a product of Mitsui Toatsu Chemicals, Inc.</li><li>A34. Polybutylene terephthalate, PBT310, a product of Toray Industries Inc.</li></ul>

Carbon Radical Inducing Agent

0099(B1, a compound having an unsaturated bond of a high electron density or a hydrogen donating compound) <ul id="ul0006" list-style="none"><li>a. Ether Compounds</li><li>a-1. Dihydropyran, a product of Tokyo Kasei K.K.</li><li>a-2. Isopropenyl acetate, a product of Tokyo Kasei K.K.</li><li>β. Tetrahydroaromatic Compounds</li><li>β-1. 1,2,3,4-Tetrahydronaphthalene, a product of Tokyo Kasei K.K.</li><li>β-2. Tetrahydrobenzene, a product of Tokyo Kasei K.K.</li><li>β-3. Tetrahydrofuran, a product of Tokyo Kasei K.K.</li><li>γ. Cyclopentane Compound</li><li>y-1. Indene</li></ul>

Carbon Radical Inducing Agent

0100(B2, a compound having an unsaturated bond of a low electron density or a hydrogen accepting compound) <ul id="ul0007" list-style="none"><li>8. Bismaleimide Compound</li><li>8-1. N,N_'-m-phenylene bismaleimide, Vulnoc PM. a product of Ohuchi Shinko Kagaku K.K.</li><li>ε. Polyol Unsaturated Ester Compound</li><li>ε-1. Ethylene glycol dimethacrylate, a product of Tokyo Kasei K.K.</li><li>Softening Agent (C)</li><li>Super Oil C, a product of Nippon Oil Co., Ltd.</li><li>Organic Peroxide (D)</li><li>a,a'-Bis-(t-butylperoxy)-m-diisopropylbenzene, Perbutyl P, a product of Nippon Oils &amp; Fats Co., Ltd.<img file="EP0457550A2_D0002.tif" /><img file="EP0457550A2_D0003.tif" /><img file="EP0457550A2_D0004.tif" /><img file="EP0457550A2_D0005.tif" /><img file="EP0457550A2_D0006.tif" /><img file="EP0457550A2_D0007.tif" /><img file="EP0457550A2_D0008.tif" /><img file="EP0457550A2_D0009.tif" /><img file="EP0457550A2_D0010.tif" /><img file="EP0457550A2_D0011.tif" /><img file="EP0457550A2_D0012.tif" /><img file="EP0457550A2_D0013.tif" /></li></ul>