A suspending medium for water soluble polymer.

Background of the Invention

0001This invention relates to preparing stable suspensions of water soluble polymers.

0002Water soluble polymers suspensions are commonly used for oil field drilling fluids and cementing applications.

0003The industry goal has been, and still is, to improve on the process of making and using these suspensions, and also to improve on their intrinsic efficiency. By the term intrinsic efficiency is meant to eliminate or substantially minimize the formation of agglomerates that do not hydrate easily.

0004Attempts to meet the above stated goals are known in the art. Such efforts have employed a wide variety of methods and agents inclusive of organophyllic clay, water, surfactants, fatty acids, and a specially prepared controlled moisture content polymer. Although these methods and/or compositions individually and collectively have improved on the art, the ultimate goal of providing an ideal suspension i.e. one which is easy to manufacture, remains stable and is useable over a wide temperature range, remains to be met.

Summary of the Invention

0005It is a general object of this invention, to provide a superior suspension of a water soluble polymer.

0006It is also another object of this invention to provide a stable liquid suspension of a water soluble polymer.

0007It is a further object of this invention to provide stable liquid suspensions of water soluble polymers that are useable over a wide temperature range.

0008It is also another object of this invention to provide a process for making an improved composition of a stable liquid suspension of a water soluble polymer.

0009It is a further object of this invention to provide a process which is easier to practice than prior art processes.

0010In accordance with the present invention a stable liquid suspension of a water soluble polymer is provided comprising an oil, an oil soluble resin, and a water soluble polymer.

0011In a preferred embodiment the composition also includes silica.

Detailed Description of the Invention

0012The ingredients useful in carrying out this invention comprise oils, resins, polymers, and silica. Generally speaking, the practice of this invention consists of mixing a suitable oil, suitable resin, suitable polymer, and preferably suitable silica in appropriate quantities in order to form the new composition of the invention - a stable liquid suspension of water soluble polymer. The new composition so formed does not generally require additional processing in order to be used. Because of its exceptional stability the liquid suspension of the invention can be prepared and shipped to customers ready to use and do not need to be prepared in the field.

0013The oils useful in the practice of this invention broadly include all hydrocarbon oils. Examples of such oils are vegetble oils, crude oil, diesel, kerosene, pentane, decane, soybean oil, corn oil and the like.

0014However, the preferred oils for purposes of this invention are kerosene, light diesel oil, heating oil, mineral oil, diesel, and iso-paraffins. Most particularly preferred are the iso-paraffins. Examples of distinctly preferred iso-paraffins include but are not limited to tetradecane, hexadecane, dodecane, mixed iso-paraffins, mixed C₁₃-C₁₄ iso-paraffins, C₁₄ iso-paraffin, and C₁₆ iso-paraffin.

0015Generally, all oil soluble resins are useful in the practice of this invention. Examples of such oil soluble resins include styrene isoprene copolymer, styrene ethylene/propylene block copolymer, styrene isobutylene copolymer, styrene butadiene copolymer, polybutylene, polystyrene, polyethylene-propylene copolymer, and like compounds.

0016Preferred, however, are block copolymers, examples of which include but are not limited to styrene ethylene/propylene block copolymer, hydrogenated styrene-isoprene block copolymers and styrene butadiene copolymer. Most particularly preferred are hydrogenated styrene-isoprene block copolymers, examples of which include but are not limited to materials sold under the trademarks "BARARESIN VIS" (trademark of Baroid Corporation), "SHELLVIS 40" and "SHELLVIS 50" (both trademarks of Shell Chemical Company).

0017All water soluble polymers are useful in the practice of this invention. Examples of such polymers and the methods for producing and/or obtaining them are disclosed in Bishop U.S. Patent 4,735,659, which is incorporated herein by reference for all purposes. (See in particular column 1, line 45 to column 2, line 60.) Particularly preferred is carboxymethyl cellulose (CMC). Also useful are water soluble Xanthanthin gum biopolymers, polyacrylamides, and carboxymethylhydroxyethylcellulose.

0018The silica useful for the practice of this invention generally includes fumed silicas, colloidal silicas, and precipitated silicas. Preferred, however, are fumed silicas, hydrophyllic fumed silica, and hydrophobic fumed silica. Distinctly preferred is hydrophobic fumed silica. Examples of this class of silica, method for making it, and other pertinent information relating to its useage is disclosed in Bishop U.S. Patent 4,735,659 incorporated herein by reference. (See in particular column 2, lines 61-68.)

0019The ranges of the ingredients listed above useful in the practice of this invention are as shown in Table 1 below. <tables id="tabl0001" num="0001"><img file="EP0454057A2_D0001.tif" /></tables>

0020The reaction conditions for carrying out the practice of the invention are as follows: The temperature is generally in the range of about -10°C to about 200°C, with a preferred range of about 0°C to about 150°C, and a most preferred range of about 60°C to about 70°C. The reaction time is generally in the broad range of about 0.05 hours to about 200 hours, with a preferred range of about 0.25 hours to about 20 hours, and a most preferred range of about 1 hour to about 2 hours. It is noted that the reaction time is generally inversely proportional to the reaction temperature i.e., the lower the temperature the more time is required.

0021In one embodiment, the process of this invention comprises introducing a suitable oil into a suitable mixing device and adding a suitable resin to the oil in the mixing device. The oil-resin mixture is then mixed for about 30-45 minutes at a temperature range of about 60°C to about 70°C. To this oil-resin mixture is then added a polymer blend comprising about 98 weight percent of a water soluble polymer and 2 weight percent hydrophobic fumed silica. The end product of this process comprising a stable liquid suspension of a water soluble polymer can then be collected by any technique known in the art. While the order of mixing is not a critical aspect of this invention, it is preferred to add the oil first and the polymer last.

0022The addition of an anitoxidant, a surfactant, a biocide, or even a minimal amount of an organophyllic clay to these basic ingredients is an option which will be frequently exercised by those of skill in the art.

0023The product of this invention normally has a gel strength that is capable of suspending particulate matter. Additionally, this gel strength develops very rapidly or almost immediately and is of the type referred to in the art as flat gels. By this is meant that unlike normal gels, its gel strength stays constant or increases only slightly with time and that it has desirable fragile properties evidenced by the ease with which it pours.

0024The product of this invention is primarily tested by observation for syneresis, pour point, and stability over a wide temperature range. Syneresis can be measured by means of a ruler or other such graduated device. This can be accomplished by inserting the ruler or graduated device through the clear liquid portion of the suspension until it contacts the interface that separates this portion, from the layer containing suspended solids. The thickness of the clear liquid layer, the measure of syneresis, can then be determined directly on the ruler or graduated device.

0025The following examples further illustrate the various aspects of this invention.

Inventive Composition 1

0026This example includes the following components: <tables id="tabl0002" num="0002"><img file="EP0454057A2_D0002.tif" /></tables><ul id="ul0001" list-style="none"><li>(1) Available under the name "SOLTROL 145" (0.8g/ml) a trademark of Phillips Petroleum Company.</li><li>(2) Available under the name "BARARESIN VIS" a trademark of Baroid Corporation.</li><li>(3) Availabe under the name "DRISPAC REGULAR" a trademark of Phillips Petroleum Company.</li></ul>

0027The oil soluble resin was sheared into the light isoparrafin oil with a Ross mixer at a setting of 5 until the temperature reached 140°F (60°C). The mixer was then shut off and the mixture allowed to cool to near room temperature. Shearing was then continued until all of the oil soluble resin was incorporated (visual observation). The carboxymethyl cellulose (CMC) was then blended into the mixture.

0028The sample was then split into three (3) 1-pint units. Unit 1 was then vibrated for three (3) days to simulate transport. Very slight syneresis was noted but no settling was observed. Unit 2 was placed in a freezer at -20°F (-29°C) until the temperature stabilized. No syneresis or settling was observed and the sample remained pourable. Unit 3 was placed in an oven at 120°F (49°C) and static aged for six months. About 1/8" syneresis was observed but no hard settling was observed.

0029This demonstrates that a stable liquid suspension of a water soluble polymer is obtained. While some syneresis occurred, no precipitation occurred. This composition has better stability than presently commercially available suspensions of water soluble polymers.

Inventive Composition 2

0030This composition comprises the following components: <tables id="tabl0003" num="0003"><img file="EP0454057A2_D0003.tif" /></tables><ul id="ul0002" list-style="none"><li>(1) Available under the name "SOLTROL 170" a trademark of Phillips Petroleum Company.</li><li>(2) Available under the name "BARARESIN VIS" a trademark of Baroid Corporation.</li><li>(3) Available under the name Liquid "DRISPAC PLUS" a trademark of Phillips Petroleum Company. This essentially consists of CMC dusted with 2 weight percent hydrophobic fumed silica.</li></ul>

0031The oil soluble resin was added to the isoparrafin oil and mixed on a Ross mixer until the mixture temperature reached 62°C (143.6°F). The mixture of water soluble polymer and silica was then added to the oil/resin mixture and blended well. Three 1-pint samples were then taken from the mixture. Sample No. 1 of these three samples was vibrated for three (3) days to simulate transport. No syneresis or settling was observed after a six month period. A portion of Sample No. 1 was also heat aged at 120°F (49°C) for six months with no syneresis or settling observed. The temperature was then increased to 150°F (66°C) and no syneresis or settling was observed after a two month period. Sample No. 2 of these three samples was placed in a freezer at -20°F (-29°C) until the temperature stabilized. No syneresis or settling was observed and the sample remained pourable during the six month period of the tests. The third sample was static shelf aged for 6 months with no syneresis or settling observed.

0032This demonstrates that the addition of silica to the basic inventive composition is a desirable and useful improvement. This results in a suspension of even greater stability and better properties than the basic inventive composition as shown in Inventive Composition 1.

Inventive Composition 3

0033This composition was made identical to Inventive Composition 2 above, except for the omission of silica. Three 1 pint samples were also collected and subjected to the same respective conditions as with those of Inventive Composition 2.

0034No hard settling was observed in any of these samples. However, about 1/8" syneresis was observed in the samples that were heat aged and/or static shelf aged for six months.

0035This demonstrates that this composition although stable, is less so than the composition containing silica.

Inventive Composition 4

0036This composition comprises the following components: <tables id="tabl0004" num="0004"><img file="EP0454057A2_D0004.tif" /></tables><ul id="ul0003" list-style="none"><li>(1) Available under the name "SOLTROL 170" a trademark of Phillips Petroleum Company.</li><li>(2) Available under the name "BARBARESIN VIS" a trademark of Baroid Corporation.</li><li>(3) Available under the name "KELZAN" a trademark of Kelco Division, Merck and Company. This is a xanthan gum biopolymer. The xanthan gum biopolymer was predusted with a 2 wt% hydrophobic fumed silica.</li></ul>

0037The light isoparrafin oil was blended with the oil soluble resin on a high shear Ross mixer until all the resin predusted with the silica, was incorporated and the temperature stabilized at 62°C (143.6°F). A split of the sample was taken and placed in a freezer at -20°F (-29°C) for test of pour point. It poured at -20°F (-29°C) and remained pourable after 6 months.

0038A split of the sample was taken and placed in an oven at a temperature of 120°F (49°C) for six months. No syneresis or settling was observed. After 6 months, the oven temperature was increased to 150°F (66°C). No increase in syneresis and no settling was observed eight weeks later.

0039This demonstrates that stable liquid suspensions of xanthan gum biopolymers can be made by employing the method and components of this invention.

Inventive Composition 5

0040This formulation was made identical to that of Inventive Composition 4 except for the substitution of the xanthan gum biopolymer with a polyacrylamide. The samples were tested under similar conditions as in Inventive Composition 4. Results obtained were similar to those of Inventive Composition 4.

0041This example further demonstrates that another kind of water soluble polymer is useful in the practice of this invention.

Inventive Composition 6

0042This formulation was made identical to that of Inventive Composition 4 except for the substitution of the xanthan gum biopolymer with carboxymethyl hydroxyethyl cellulose. The samples were likewise tested under similar conditions as those of Inventive Composition 4. Similar results were obtained.

0043This example additionally demonstrates that all water soluble polymers are useful in the practice of this invention.

0044While this invention has been described in detail for the purpose of illustration, it is not to be construed as limited thereby but is intended to cover all changes and modifications within the spirit and scope thereof.