Improved composition and process for making poly(arylene sulfide) resins reinfored with glass fibers.

Background of the Invention

0001The present invention relates to fiber reinforced thermoplastic materials.

0002The production of thermoplastic material of poly(arylene sulfide) resins reinforced with unidirectional glass fibers by pultrusion has been disclosed. See, for example, U.S. Patent 4,680,224. At least one fiber strand of continuous filaments is contacted with a poly(arylene sulfide) resin in the form of a powder or a slurry. The impregnated strand or strands are then pulled through a temperature controlled die for producing a composite which can have the form of, for example, a tape, a rod or a sheet.

0003The glass fiber reinforced pre-preg tapes produced in this manner are useful for such applications as structural members, aircraft parts, doctor blades, and the like.

0004For some applications the continuous fiber reinforced thermoplastic pre-preg tape will be more useful with improved transverse tensile strength and improved hydrolytic stability. For example, doctor blades used to process aqueous-based materials require materials of construction that have good hydrolytic stability and good transverse tensile strength. Likewise, structural members subjected to multi-directional high loads require materials of construction with, among other properties, good transverse tensile strength. Good transverse tensile strength also helps to eliminate continuous fiber composite microcracking, mitigates the propagation of microcracking under loaded conditions and improves resistance to fatique.

0005Properties such as transverse tensile strength and hydrolytic stability in thermoplastic material of poly(arylene sulfide) reinforced with glass fibers have been improved by use of silanes. When the silanes are mixed with the poly(arylene sulfide) prior to application on the glass fiber it is important that the silanes are maintained at consistent concentrations in the poly(arylene sulfide)s during treatment of the glass fibers and that coating of the glass fibers be uniform.

Summary of the Invention

0006It is an object of this invention to provide a method for preparing a thermoplastic resin and silane mixture suitable for use in preparing glass reinforced thermoplastic composites. It is also an object to provide this mixture, which will be useful in making thermoplastic composites with improved properties.

0007It is an object of this invention to provide a method for producing continuous fiber reinforced thermoplastic material in which the fibers are treated with a silane and thermoplastic mixture.

Brief Description of the Drawing

0008Figure 1 illustrates silane adsorption on poly(phenylene sulfide) as a function of time.

Detailed Description

0009In accordance with this invention mixtures of polysulfide organosilanes and poly(arylene sulfides) are aged to allow adsorption of the silanes onto the poly(arylene sulfides) and these mixtures are provided.

0010In accordance with another embodiment of the present invention an aged mixture of at least one polysulfide organosilane and poly(arylene sulfide) is used in a method of making glass reinforced composites.

0011In accordance with yet another embodiment of the present invention, glass fiber reinforced poly(arylene sulfide) pre-preg tapes are prepared by passing single end glass roving through a slurry containing an aged mixture of the poly(arylene sulfide) matrix material and a polysulfide organosilane.

0012The silane and thermoplastic compositions of this invention are useful for improving the process for making glass reinforced thermoplastic composites. When silanes and thermoplastic resins are mixed in a slurry bath for pultrusion of glass reinforcing fibers the concentration of silane in the slurry must be kept consistent over time and throughout the slurry mix. This has been done by constant monitoring and adjustment of feeds to the slurry bath. To avoid inconsistencies in silane concentration and to eliminate the necessity of frequent monitoring and feed adjustment during the pultrustion process, this invention provides for aging a polysulfide silane and thermoplastic mixture before introduction of the mixture into the slurry bath. This surprisingly gives continued even distribution of the silane throughout the thermoplastic matrix material, thus permitting improved contact of the silane and thermoplastic mixture with the glass reinforcing material.

0013Examples of poly(arylene sulfide) resins contemplated as useful in making the compositions of this invention include those described in U.S Patent No. 3,354,129 issued to Edmonds and Hill on November 21, 1967, and those described in U.S. Patent No. 3,919,177, issued to Campbell on November 11, 1977, the disclosures of which are hereby incorporated by reference. The presently preferred polymer is poly(phenylene sulfide).

0014The term poly(arylene sulfide) includes homopolymers and the normally solid arylene sulfide copolymers, terpolymers and the like having melting or softening points of at least about 150°C, and more preferably from about 200°C to about 400°C. Other examples of poly(arylene sulfide) materials are poly(4,4-biphenylene sulfide), poly(2,4-tolylene sulfide), and a copolymer from p-dichlorobenzene, 2,4-dichlorotoluene and sodium sulfide and the like.

0015The term poly(phenylene sulfide) includes homopolymers and copolymers containing ortho-, meta- and/or para-phenylene linkages on aryl groups in the polymer chain. Also included are aryl-substituted derviatives of these materials. Also included are poly(arylene sulfide sulfone), poly(arylene sulfide ketone) and poly(arylene sulfide diketone).

0016The organosilanes contemplated as useful in making the compositions of this invention include aromatic polysulfide silanes within the formula: <chemistry id="chem0001" num="0001"><img file="EP0448043A1_D0001.tif" /></chemistry>

0017The number of sulfur atoms (S) linking the two aromatic groups is determined by the value of n which represents a positive integer and ranges from 1 to 30. A subgenus within the scope of this invention is represented by formula I wherein n ranges from 1 to 10. The preferred value for n is from 1 to 5.

0018Each of R₁ and R₂ is H or an alkyl group having from 1 to 30 carbon atoms. Each of R₅, R₆, R₇, R₈, R₉, and R₁₀ is an alkyl group having from 1 to 30 carbon atoms. The alkyl groups associated with R₁, R₂, R₅, R₆, R₇, R₈, R₉, and R₁₀ can be linear (e.g. n-propyl) or branched (e.g. tert-butyl). Examples of alkyl groups within the scope of this invention include, but are not limited to, the following:         ―CH₃         ―CH₂CH₃         ―CH₂CH₂CH₃         ―CH₂CH₂CH₂CH₃ <chemistry id="chem0002" num="0002"><img file="EP0448043A1_D0002.tif" /></chemistry>

0019A subgenus within the scope of this invention is represented by formula I wherein each of R₁ and R₂ is H or an alkyl group having from 1 to 10 carbon atoms and each of R₅, R₆, R₇, R₈, R₉, and R₁₀ is an alkyl group having from 1 to 10 carbon atoms. Preferably, each of R₁ and R₂ is H or an alkyl group having from 1 to 5 carbon atoms and each of R₅, R₆, R₇, R₈, R₉, and R₁₀ is an alkyl group having from 1 to 5 carbon atoms. In an embodiment of this invention each of R₁, and R₂ represents a methyl group (-CH₃) and each of R₅, R₆, R₇, R₈, R₉ and R₁₀ represents an ethyl group (-CH₂CH₃).

0020Each of the letters x and y represents either 1 or 0. When x = 0, R, is absent from formula I and the Si bond extends to a carbon member of the corresponding aromatic ring. When x = 1, R₃ is as defined below. In a similar manner when y = 0, R₄ is absent from formula I and the Si bond extends to a carbon member of the corresponding aromatic ring. When y = 1, R₄, is as defined below.

0021Each of R₃ and R₄, when present (i.e. when x = 1, y = 1), is an alkylene group having from 1 to 30 carbon atoms. The alkylene group can be linear or branched. Examples of alkylene groups within the scope of this invention include, but are not limited to, the following:         ―CH₂―         ―CH₂CH₂―         ―CH₂CH₂CH₂―         ―CH₂CH₂CH₂CH₂― <chemistry id="chem0003" num="0003"><img file="EP0448043A1_D0003.tif" /></chemistry>

0022A subgenus within the scope of this invention is represented by formula I wherein each of R₃ and R₄ (when present) is an alkylene group having from 1 to 10 carbon atoms. Preferably, each of R₃ and R₄ (when present) is an alkylene group having from 1 to 5 carbon atoms. In an embodiment of this invention each of R₃ and R₄ is present (i.e. x = 1 and y = 1) and represents an ethylene group (i.e. ―CH₂H₂―).

0023R₁ and R₃ (or Si when x = 0) can be bonded to any available carbon atom of the corresponding aromatic ring, with the understanding that they cannot both be bonded to the same ring atom or to the ring atom to which the sulfur is bonded. The position of R₁ with respect to the sulfur substituent can be ortho, meta or para. The position of R₃ (or Si when x = 0) with respect to the sulfur substituent can be ortho, meta or para. In a similar manner R₂ and R₄ (or Si when y = 0) can be bonded to any available carbon atom of the corresponding aromatic ring, with the understanding that they cannot both be bonded to the same ring atom or to the ring atom to which the sulfur is bonded. The position of R₂ with respect to the sulfur substituent can be ortho, meta or para. The position of R₄ (or Si when y = 0) with respect to the sulfur substituent can be ortho, meta or para. Examples of various orientations within the scope of this invention include, but are not limited to, the following: <chemistry id="chem0004" num="0004"><img file="EP0448043A1_D0004.tif" /></chemistry>

0024The preferred silane compounds of this invention are defined by the following chemical formula: <chemistry id="chem0005" num="0005"><img file="EP0448043A1_D0005.tif" /></chemistry> where n is an integer from 1 to 5. Included are all positional isomers of the above. Examples include, but are not limited to, the following: <chemistry id="chem0006" num="0006"><img file="EP0448043A1_D0006.tif" /></chemistry>

0025The composition can contain more than one silane within the scope of formulas I through IX. By way of non-limiting example the poly(arylene sulfide) composition can contain the compounds VII, VIII and IX above. In one embodiment of this invention the poly(arylene sulfide) composition contains two or more silanes defined by <chemistry id="chem0007" num="0007"><img file="EP0448043A1_D0007.tif" /></chemistry> wherein the average value of n for the mixture is about 2 to about 4 and preferably about 2.8.

0026Presently preferred is a silane having the formula above wherein R₁ and R₂ are ―CH₃; wherein R₁ and R₄ are ―CH₂CH₂―; wherein R₅, R₆, R₇, R₈, R₉ and R₁₀ are ―CH₂CH₃; wherein x = 1 and y = 1; wherein the average value of n is about 2.8. This material is commercially available from Union Carbide Corporation under the product name Ucarsil^TM RC-2 or as Y-9194.

0027The fiber reinforced pultruded thermoplastics produced in accordance with this invention are basically comprised of poly(arylene sulfide) resin, glass reinforcing material, and at least one polysulfide organosilane.

0028The presently preferred composition of matter comprises substantially linear poly(phenylene sulfide) having a melt flow within the range of about 1 to about 800 grams per 10 minutes, unidirectionally aligned continuous glass fiber reinforcements, a silane content of from about 0.01 to about 5.0 weight percent based on weight of the glass or, more preferably, from about 0.05 to about 0.5 weight percent based on weight of the glass, and demonstrates improved transverse tensile strength.

0029The weight ratio of the poly(arylene sulfide) to the polysulfide organosilane in the silane and thermoplastic mixture of this invention is greater than about 2 to 1 and less than about 5,000 to 1. The scope of this invention encompasses a broad range and requires only that an amount of silane sufficient to increase the transverse tensile strength or to improve the hydrolytic stability of the resulting composition be used.

0030The silane and thermoplastic mixtures presently preferred have been aged sufficiently to allow enough adsorption of the polysulfide silane onto the poly(arylene sulfide) to significantly reduce the need for constant monitoring and feed adjusting in a thermoplastic pultrusion process.

0031The poly(arylene sulfide) resin is present in the pultruded composite in an amount in the range of from about 20 % to about 90% by weight of the composition, preferably in the range of from about 25 % to about 60% by weight, and most preferably in the range of from about 25 % to about 35% by weight.

0032The glass reinforcing material is present in the pultruded composite in an amount in the range of from about 80% to about 10% by weight of the total composition, preferably from about 40% to about 75% by weight, and most preferably from about 65% to about 75% by weight.

0033Continuous unidirectionally aligned glass fibers arranged In single end rovings are contemplated as a suitable reinforcement material. The glass fibers are available commercially. Examples include Certainteed 70C sized E glass and Certainteed 70D-11, with the latter being presently preferred. However, fiber contemplated as useful in this invention is not limited to single end roving, but may also be a conventional or assembled roving. Also, these examples are not to be construed as constraints on the diameter of fiber contemplated as useful in this invention.

0034It is also within the scope of this invention to make a glass reinforced thermoplastic composite by pultruding a woven glass fabric through a slurry of the polysulfide silane and thermoplastic mixture.

0035Diluents contemplated as useful include but are not limited to water, alcohols and mixtures thereof.

0036The diluent is typically water or an aqueous mixture containing one or more alcohols. In addition to diluent, the thermoplastic and resin mixture may contain additives such as acid to adjust the pH of the mixture, lubricants, surfactants and wetting agents.

0037The inventive method for producing the unidirectional fiber reinforced thermoplastic material comprises the following steps: <ul id="ul0001" list-style="none"><li>(1) preparing a slurry or emulsion comprising a thermoplastic resin, one or more of the chosen silanes and optionally other additives as needed;</li><li>(2) allowing the thermoplastic resin/silane mixture to age long enough to significantly increase adsorption of the silane onto the thermoplastic resin;</li><li>(3) passing the continuous glass fibers through the slurry of step (1);</li><li>(4) passing the treated and impregnated glass fibers through an oven;</li><li>(5) giving the composite final shaping in a heated die. Alternatively, after allowing the thermoplastic resin/silane mixture to age (step 2), the mixture could be dried, then used in a second slurry for step (3).</li></ul>

0038Preferably the oven will maintain the temperature of the poly(arylene sulfide) at least as high as the melting point of the poly(arylene sulfide).

0039The slurry or emulsion is prepared by any suitable procedure. One method is to mix the silane and surfactant, add the silane/surfactant mixture to the water and then add the poly(arylene sulfide) powder. Agitation of the components during the preparation and aging of the mixture is advantageous. Any suitable temperature, usually 20-50°C, may be used during aging of the mixture and for the bath temperature.

0040Having a mixture of the thermoplastic resin and silane in which the silane is substantially completely adsorbed onto the thermoplastic prior to use of the mixture as a slurry for pultrusion allows for running the pultrusion process without frequent monitoring of the slurry bath for consistency of the concentration of silane in the slurry.

0041Adsorption significantly increases during the first approximately 20 hours and exhibits a slower adsorption rate from about 20 hours to about 35 hours of aging. Thereafter the increase in adsorption is significantly slowed. After about 48 hours of aging, there does not appear to be any appreciable increase in the amount of silane adsorbed onto the thermoplastic resin. Presently preferred is from about 1 hour to about 100 hours of aging. More preferred is from about 6 hours to about 75 hours; most preferred is from about 12 hours to about 48 hours.

0042The rate of adsorption of the silane onto the poly(arylene sulfide) depends upon such factors as bath temperature, silane concentration, poly(arylene sulfide) surface area, and agitation.

0043Commerical objectives in production of fiber reinforced thermoplastic materials may not require maximum adsorption of the polysulfide silane onto the poly(arylene sulfide) because of the benefits obtainable with use of shorter aging periods.

Example I

0044This example demonstrates the difference in behavior of the polysulfide silanes which are used in this invention and an epoxy silane in an aqueous bath with polyphenylene sulfide (PPS). An air milled PPS with a mean particle size of 17 microns was combined with aqueous solutions of the silanes (0.5 weight percent silane based on the PPS weight). The mixtures, about 3000 g, containing 15 weight percent PPS were stirred with magnetic stirring bars at 28°C At various time intervals a 100 mL sample of each slurry was collected and analyzed. Each sample slurry was centrifuged and the liquid removed for analysis of the silicon content by inductively coupled plasma. The PPS solid was collected by filtering on a Buchner funnel, washed with water, dried for a minimum of 15 minutes at 110°C, and analyzed for silicon content by neutron activation. Calculations involving Ucarsil^TM RC-2 assume that the molecular weight is 652 g/mole, the alkyl groups on the aromatic rings are methyl, and that there are 2.8 sulfur atoms per molecule.

0045The results of the control run using Ucarsil^TM TC-100 epoxy silane (3-glycidoxypropyltrimethoxysilane) from Union Carbide are summarized in Table I. The TC-100 remains predominantly in the aqueous solution during the test and very little silicon was detected on the PPS over the time period of the test. Figure 1 shows the concentration of silicon on the PPS during the test.

0046In sharp contrast with the above results with TC-100, the run with the Ucarsil^TM RC-2 polysulfide silane from Union Carbide (Table II) shows that the RC-2 silane adheres to the PPS. About 83 weight percent of the RC-2 initially present in the solution was found on the PPS after about 24 hours and about 88 weight percent of the RC-2 was on the PPS after 48 hours. The silicon levels in the liquid phase are believed to be low due to difficulties in asperating the relatively insoluble silane to the plasma torch with the existing equipment. The results of this run are also shown in Figure 1 with the upper line representing the calculated maximum possible level of silicon on PPS. These curves in Figure 1 clearly show the difference In behavior between the epoxy silane and the polysulfide silane in an aqueous mixture with PPS. <tables id="tabl0001" num="0001"><img file="EP0448043A1_D0008.tif" /></tables>

Example II

0047This example demonstrates the preparation and properties of unidirectional continuous glass fiber reinforced poly(phenylene sulfide) (PPS) composites where a polysulfide silane is contacted with the PPS resin and aged before the prepreg operation. Several other silanes were used for composite preparation for comparison.

0048All compounds were made using techniques disclosed in U.S. Patent 4,680,224, modified to include a curtain sprayer in the slurry bath and rolling redirect bars at any point the glass is wet. All composites were made using Certainteed 70-C sized E glass, 20 micron diameter, 250 yield, 1.0 weight percent of the indicated silane in the slurry bath (based on the weight of resin in the slurry bath), and a poly(phenylene sulfide) with a melt flow of approximately 50-150 g/10 min. (ASTM D1238-79, Procedure B, Condition 315/5.0, modified to use a 5 minute preheat time rather than the 6 minute minimum stated in the test method). Techniques disclosed in U.S. Patent 3,919,177; U.S. Patents 4,801,664 and/or 4,414,729 were used for preparation of the poly(phenylene sulfide) for the test.

0049The slurry concentration and amount of slurry needed for producing the composite will depend on such factors as the size of bath or baths, the line speed and properties of the fiber to be impregnated. This was determined empirically so as to produce a slurry which would result in a composite having 30 ± 2 weight percent resin and 70 ± 2 weight percent glass.

0050In these examples, the main bath was 20.5 weight percent PPS resin and the add bath was 30 weight percent PPS. The surfactant was Neodol^TM 91-6 at a concentration of 0.26 weight percent based on the PPS weight. Ucarsil^TM RC-2, a polysulfide aliphatic silane from Union Carbide, was used in a run with prolonged contact of the PPS with the silane before the pultrusion. Several other silanes were used in other runs without extended contact with the PPS. Emulsions were formed when RC-2, T2905, and B2494 were used. DSC-18 was a solid and A-1160 was water soluble.

0051In the slurry formation, the appropriate amount of water was weighed in a large container and the pH was adjusted to approximately 4 by using acetic acid. The appropriate amount of surfactant was weighed and added to the silane and stirred by hand until the mixture was uniform. Then, the silane/surfactant mixture was added to the water with very rigorous continuous mixing. After all of the silane/surfactant mixture was added to the water, less vigorous stirring was continued for four hours. It is not necessary to stir rigorously after the emulsion has formed.

0052Then the PPS resin was added to the water/silane/surfactant mixture. The resulting slurry was very thick and was not used for 48 hours after it had been blended in order to allow the silane to adsorb onto the PPS resin. The mixture was stirred two or three times daily until use.

0053While this invention has been described in detail for the purpose of illustration, it is not to be construed as limited thereby. This patent is intended to cover all changes and modifications within the spirit and scope thereof.