Improved coextrudable adhesive for polystyrene, and products therefrom

BACKGROUND OF THE INVENTION

0001The invention relates to an extrudable adhesive composition of ethylene vinyl acetate copolymer, modified ethylene vinyl acetate copolymer (EVA), and styrene homopolymer, useful for bonding polystyrene to gas barrier polymers.

0002Laminates of polystyrene and a gas barrier resin, using adhesives containing EVA modified with ethylenically unsaturated carboxylic acid or anhydride are known in the art. For example, U.S. patent 4,576,995, to Nakabayashi et al., discloses an adhesive for bonding ethylene/vinyl alcohol copolymer and polystyrene, which comprises a modified ethylene/vinyl acetate copolymer obtained by graft-copolymerizing a styrenic vinyl monomer and an alpha, beta-unsaturated carboxylic acid to an ethylene/vinyl acetate copolymer. Laminates prepared therefrom are valuable as a deep draw forming material with enhanced gas barrier properties.

0003Japanese application 53018653 (reported as Derwent Abstract 26079A/14) describes a low temperature heat sealing adhesive consisting of 100 parts carboxylated ethylene vinyl acetate copolymer and 3-100 parts styrene resin of molecular weight 500-1000.

0004Japanese application 54057582 (reported as Derwent Abstract 46260B/25) discloses a resin laminate of a polystyrene resin layer, a layer of ethylene-vinyl acetate copolymer saponification product, and a layer of a styrene/butadiene block copolymer containing 60% butadiene, ethylene vinyl acetate copolymer (6 mol % VA), and a maleic anhydride-ethylene vinyl acetate graft copolymer (3 mol % VA).

0005Japanese application 58203043 (reported as Derwent Abstract 84-008480/02) discloses a similar laminate, in which the adhesive layer is a blend of polystyrene, ethylene-vinyl acetate copolymer (5-50 % VA), and a polyolefin grafted with e.g. maleic anhydride.

0006Japanese application 59055743 discloses a process for production of resin laminates characterized by melt coextrusion of a styrene group resin layer, a gas barrier resin layer such as saponified ethylene-vinyl acetate copolymer, and a bonding layer of (a)ethylene- vinyl acetate copolymer graft-modified with unsaturated carboxylic acid or anhydride, and (b) ethylene-vinyl acetate copolymer which is graft-modified with e.g. styrene, or further (c) unmodified ethylene-vinyl acetate copolymer.

SUMMARY OF THE INVENTION

0007The present invention provides an extrudable bonding resin composition consisting essentially of: <ul id="ul0001" list-style="none"><li>(a) 55 to 80 percent by weight of an ethylene vinyl acetate copolymer portion consisting essentially of <ul id="ul0002" list-style="none"><li>(i) 0 to 99 percent by weight of a copolymer of 60 to 87 weight percent ethylene and 13 to 40 weight percent vinyl acetate comonomer, and</li><li>(ii) 1 to 100 percent by weight of a copolymer of at least 50 weight percent ethylene; 3 to 50 weight percent vinyl acetate comonomer, the amount of said vinyl acetate comonomer being within 10 percent of the amount of vinyl acetate comonomer in copolymer (i), if present; and a grafted comonomer containing pendant carboxylic acid or carboxylic acid derivative functionality, wherein the amount of said grafted comonomer comprises 0.03 to 0.5 percent by weight of the total composition and the total amount of copolymerized vinyl acetate of (i) and (ii) exceeds 13.5 percent by weight of the total composition; and</li></ul></li><li>(b) 20 to 45 percent by weight of an impact modified polystyrene having a molecular weight of greater than 50,000.</li></ul>

0008The present invention further provides a laminated structure comprising at least one structural layer, at least one barrier layer, and at least one layer of the above resin composition used as a bonding layer. Such structures exhibit desirable combinations of structural strength and barrier properties, with excellent adhesion between the layers.

DETAILED DESCRIPTION OF THE INVENTION

0009The extrudable bonding resin of the present invention comprises a blend of 55 to 80 percent by weight of an ethylene vinyl acetate (EVA) component and 20 to 45 weight percent of a polystyrene component. The EVA component comprises an EVA copolymer grafted with pendant acid or acid derivative functionality. This grafted copolymer may be blended, if desired, with additional ungrafted EVA. Such blending may be desirable in order to minimize the amount of the relatively more expensive grafted EVA material, while maintaining the excellent adhesive properties of the composition.

0010The ungrafted EVA copolymer is present in amounts of 0 to 99, and preferably 50 to 97 percent by weight of the EVA portion of the composition. This component is a copolymer containing 13 to 40, and preferably 25 to 35 weight percent copolymerized vinyl acetate. The balance of the copolymer is substantially copolymerized ethylene. The melt index of the copolymer, as measured by ASTM D1238 Condition "E", should be 0.5 to 40. Outside of these ranges, processing becomes more difficult, and flow instabilities may result.

0011The other polymer of the EVA component is an EVA copolymer similar to that described above, onto which has been grafted a comonomer containing pendant carboxylic acid or carboxylic acid derivative functionality. The amount of vinyl acetate comonomer present in the graft copolymer should be between 3 and 50 weight percent, preferably between 15 and 35 weight percent. In order to achieve good peel strength in laminates prepared from the present adhesive, the amount of copolymerized vinyl acetate in the grafted EVA copolymer should be within 10 percent of the amount of copolymerized vinyl acetate in the nongrafted EVA copolymer, if present. That is to say that the percentage of copolymerized vinyl acetate in the grafted EVA copolymer should be within 10 absolute percentage points of the amount in the ungrafted material. Thus if the ungrafted EVA contains 28% copolymerized vinyl acetate, the grafted material should contain between 18 and 38% copolymerized vinyl acetate. Furthermore, the total amount of copolymerized vinyl acetate in the adhesive, from both the grafted and ungrafted EVA copolymers, should exceed 13.5 weight percent of the adhesive. If the total amount of copolymerized vinyl acetate is below 13.5 weight percent, the adhesion of the composition to polystyrene is impaired. The melt index of this copolymer should also be 0.5 to 40.

0012The grafting monomer is selected from the group consisting of ethylenically unsaturated mono-, di-, or polycarboxylic acids and ethylenically unsaturated carboxylic acid anhydrides, including derivatives of such acids or anhydrides. Examples of the acids and anhydrides include acrylic acid, methacrylic acid, maleic acid, fumaric acid, itaconic acid, crotonic acid, itaconic anhydride, maleic anhydride, and dimethyl maleic anhydride. Examples of suitable derivatives includes salts, amides, imides, and esters of such acids or anhydrides, for example, mono- and disodium maleate and diethyl fumarate. Among the acids and anhydrides that are particularly useful are maleic anhydride and maleic acid.

0013The method for grafting of the comonomer onto the EVA copolymer can be any of the processes which are well known in the art. For example, grafting can be carried out in the melt without a solvent, as disclosed in copending U.S. Patent Application 07/122,359, filed November 18, 1987, or in solution or dispersion. Melt grafting can be done using a heated extruder, a Brabender™ or Banbury™ mixer or other internal mixers or kneading machines, roll mills, and the like. The grafting may be carried out in the presence of a radical initiator such as a suitable organic peroxide, organic perester, or organic hydroperoxide. The graft copolymers are recovered by any method which separates or utilizes the graft polymer that is formed. Thus the graft copolymer can be recovered in the form of precipitated fluff, pellets, powders, and the like.

0014The amount of monomer grafted onto the EVA copolymer is not particularly limiting, and may be as low as 0.03 weight percent or as much as 5 percent or even more, based on the weight of the grafted EVA copolymer. The total amount of graft polymer in the total adhesive composition, however, is important, and should be between 0.03 and 0.5 weight percent of the total composition, in order to obtain superior adhesive and bonding properties.

0015The third component of the extrudable bonding resin composition is an impact modified polystyrene. This polystyrene component makes up 20 to 45, and preferably 30 to 45 weight percent of the composition. The polymer is impact modified by an elastomer such a polybutadiene elastomer or polybutadiene-styrene elastomer. It can be prepared by polymerizing styrene monomer in the presence of polybutadiene or styrene-butadiene elastomer, so that there arises both a physical blend as well as a graft copolymer. The polystyrene is a high molecular weight polymer, having a molecular weight greater than 50,000.

0016In addition to the above mentioned components, the adhesive resin may contain small amounts of other materials commonly used and known in the art, such as antioxidants, stabilizers, and fillers.

0017The adhesive resin composition is prepared by blending the above described components by any suitable means, such as melt blending, extruding, etc. The composition provides excellent adhesion in a composite structure containing a structural layer of a styrene-type resin layer, a vinyl chloride resin layer, or a polycarbonate resin layer, and a barrier layer such as polyamide or ethylene vinyl alcohol copolymer. Structures containing styrene-type resins show excellent extrudability and good forming processability over a wide range of temperatures. The combination of processability and barrier properties provided by such composite structures make them useful in applications such as packaging, disposable containers, etc.

EXAMPLES

0018Adhesive blends were prepared by dry blending the ingredients in a polyethylene bag and subsequently melt blending at 220 to 230°C in a 28 or 30 mm twin screw extruder with a vacuum port. Each of the blends, listed in Table I, also contained 0.10 weight percent Irganox™ 1010 hindered polyphenol stabilizer (not separately reported in the Table).

0019Each of the blends was coextruded from a 25 mm single screw extruder operated at 4 to 6 r.p.m., through a coextrusion die. On one side of the blend was extruded a layer of high impact polystyrene (HIPS) from a 38 mm extruder at 8 to 12 r.p.m, and on the other side was extruded a layer of ethylene vinyl alcohol copolymer containing 33 mole percent ethylene from a 38 mm extruder at 30 to 45 r.p.m. The barrel temperature of each extruder was set at 230°C; the chill rolls over which the extrudate was passed were maintained at 100°C. The take-up speed for the extruded sheet was about 1.5 m/min. The thickness of the layers is indicated in the Table.

0020The laminates thus prepared were evaluated by measuring their peel strength. Peel strength was measured by ASTM D 1876-72, modified in that the test was run at 305 mm/min, rather than 254 mm/min, and 3 to 6 duplicates of each sample were measured, rather than 10. Results from this test, in a "T" configuration, are indicated in the Table by "T." For some samples an additional measurement of peel strength was made in a similar way but using a configuration in which one of the tabs was turned back so that it was parallel to the laminate. These tests are indicated in the Table by "180."

0021The results in the Table show the superiority of the adhesive compositions within the scope of the present invention. Examples 1-19 represent laminates made using the adhesive of the present invention. The "T" peel strength for such laminates is at least 280 N/m, typically at least 300 N/m. Laminates prepared outside the scope of the present invention are represented in Comparative Example C1-C23. For these laminates the "T" peel strength is typically less than 250 N/m, often much less. Comparative Example C1 has a low peel strength because the total vinyl acetate content of the EVA copolymers used in the blend was below 13.5%. Comparative Example C3 has low peel strength because the difference in the vinyl acetate level of the grafted and the ungrafted EVA copolymers is greater than 10%. Comparative Examples C4 and C5 show poor results because the grafted polymer is a modified polyethylene or a modified EPDM, rather than a modified EVA copolymer. Comparative Example C6 has poor peel strength because of the difference in the vinyl acetate content of the grafted and ungrafted EVA is greater than 10 percent, and the level of polystyrene is below 20%. Comparative Examples C7 through C9 have poor peel strengths because the blends contain less than 20% polystyrene as a component. Comparative Examples C10 through C17, on the other hand, have poor or variable peel strengths because the polystyrene component is greater than 45% of the blend. Comparative Examples C18 through C24 give low peel strengths because impact-modified polystyrene is not used: in Comparative Examples C18 and C19, unmodified or crystalline polystyrene is used; in Comparative Examples C19 through C21, styrene hydrogenated butadiene triblock copolymer with 70% butadiene is used; and in Comparative Examples C22 and C23 a styrene butadiene copolymer with 30% butadiene is used. <tables id="tabl0001" num="0001"><img file="EP0345069B1_D0001.tif" /></tables><tables id="tabl0002" num="0002"><img file="EP0345069B1_D0002.tif" /></tables>