Improved process for the production of perfluoropolyethers substantially comprising perfluorooxyethylene and perfluorooxypropylene units.

The present invention relates to the production of perfluoropolyethers predominantly composed of units of the formulae -CF₂CF₂0-and <chemistry id="chem0001" num="0001"><img file="EP0344547A2_D0001.tif" /></chemistry>and terminal perfluoroalkyl groups,which products show an optimum combination of chemical and physical properties.

The process for producing said perfluoropolyethers is based on the low-temperature photo-oxidation of a mixture of perfluoropropene and tetrafluoroethylene, the subsequent decomposition of the peroxide groups contained in the resulting products and the fluorination of the end groups in order to convert them to perfluoroalkyl groups, and the optional regulation of the molecular weight in case the latter is too high for the intended use of the end product.

The various steps of the present process are based on wellknown techniques. However, the products obtained according to the present invention are the result of the application of specific working conditions which allow to prepare them at economically favourable costs and with high yields with respect to the starting perfluoroolefins.

The photo-oxidation of C₂F₄/C₃F₆ mixtures is known from USA 3,442,942; 3,665,041 and 3,770,792 as well as from DE-A-18 17 826.

In said publications the specific operating conditions which, according to the present invention, are essential for obtaining the above products in high yields and high conversions with respect to the perfluoroolefins used as the starting material have not been taken into consideration. Particularly, the products disclosed in the examples of the above publications show a rather low ratio of C₂ to C₃ units.

According to the present invention, by adopting specific working conditions in the photo-oxidation of the C₂F₄ C₃F₆ mixture and by subsequent decomposition of the peroxy groups and conversion of the terminal groups to perfluoroalkyl end groups by means of special methods, perfluoropolyethers may be obtained, which have the general formula: <chemistry id="chem0002" num="0002"><img file="EP0344547A2_D0002.tif" /></chemistry>wherein: <ul id="ul0001" list-style="none"><li>R, and R the same or different from each other, are terminal perfluoroalkyl groups selected from: -CF₃, -C₂F₃ and -C₃F₇; and</li><li>m,n,p and q which represent average values for the products which are generally composed of mixtures of individual compounds within the scope of the above formula, meet the following conditions:</li><li>- the sum (m + n + p + q) is within the range of from 2 to 200;</li><li>- the ratio (p + q)i(m + n + p + q) is smaller than or equal to 10/100, and preferably ranges from 0.5/100 to 4100:</li><li>- the ratio nim is in the range of from 0.2 to 6, and preferably of from 0.5 to 3.</li></ul>

m, n, p and q are the same or different from each other. Both m and n preferably range from 1 to 100 (most preferred from 1 to 80) whereas both p and q preferably range from 0 to 80 (most preferred from 0 to 50).

As compared to the products known from the prior art, the products obtainable according to the present invention are characterized by the following properties: <ul id="ul0002" list-style="none"><li>- a very low content of -CF₂0- units, which are known to constitute breakage points of the perfluoropolyether chain: as a consequence, they have a high stability to catalytic breakdown;</li><li>- a high value of the ratio n/m, which involves a higher content of C₃ units, and a decidedly lower viscosity, with the molecular weight being the same; therefore the products have a low viscosity also at very low temperatures, and at the same time have an extremely low vapour pressure due to their high molecular weight; furthermore, their pour point is lower, with the molecular weight being the same, which means that low-pour-point, low-volatility products are available through the process of the present invention.</li></ul>

Furthermore, with the process according to the present invention it is unexpectedly possible to obtain C2F4 conversions which are much higher than those of the prior art, and are generally of the order of 90%.

Particularly, it can be observed that the products according to the present invention, as compared to the perfluoropolyethers obtained by means of the photooxidation of only C2F4 alone (and thus not containing C₃ units, e.g. Fomblin -@ Z), show a much smaller content of -CF₂0- groups, and therefore a much higher stability.

Furthermore, the present process is easier to carry out from a technical point of view and less expensive in that it does not require the use of solvents, which are needed, on the contrary, in the case of photo-oxidation of only C₂F₄.

From US-A-3,770,792 to Sianesi, it is known to prepare PFPE products containing both -CF₂CF₂0- and-CF(CF₃)CF₂0- units by means of the simultaneous photochemical oxidation of C₂F4 and C₃F₆. Under the operating conditions stated or suggested in the above patent and in particular, in the examples thereof, very high conversions and yields of useful products cannot be obtained, however. The highest yields given in the examples are 70% based on C2F4 and 60% based on C₃F₆, while the maximum conversions are 60% for C₂F₄. and 15% for C₃F₆.

In particular, as regards the U.V. light, which is a key factor of the process, the above patent suggests to work under conditions such that the irradiation index I, as defined below, is at least 2, and preferably at least 3, and up to 50 in order to obtain a product not containing an excessively large amount of peroxy oxygen. Said index is represented by the formula:<maths id="math0001" num=""><img file="EP0344547A2_D0003.tif" /></maths>wherein: <ul id="ul0003" list-style="none"><li>E = U.V. energy at a wavelength of ≦ 330 nm in watts,</li><li>S = the surface area through which the energy E penetrates the system, in cm², and</li><li>V = the volume, in cm³, of the reaction system.</li></ul>

From the examples reported in the patent values of I of around 6 may be calculated; in example 9 it is shown that a low value of I (1.4) results in a high content of peroxy oxygen.

It has now surprisingly been found that compared to the results reported in the above patent yields and conversions can considerably be improved and that yields of more than 90% based on C₂F₄ and contemporaneously of approximately 90% based on C₃F₆ and conversions higher than 60% for C₂F₄ and of the order of 15%, and even higher, for C₃F₆, can be achieved.

These results may be obtained by adopting optimum working conditions, which are characterized, in particular, by specific values of the U.V. light intensity with respect to the volume of the liquid reaction phase and the flow rate of the gaseous reactants (0₂, C₂F₄, C₃F₆) which are fed as continuous stream.

As regards the radiation energy E suitable for the photochemical effects in the reaction, said energy corresponding to radiation having a wavelength of 5300 nm, it was found that the intensity of said radiation, with respect to both the volume of the liquid reaction phase (V_liq) and the flow rate (Fg)of the continuously fed gaseous reactants (0₂, C₂F₄., and, possibly, C₃F_s) must meet the following conditions: <ul id="ul0004" list-style="none"><li>a) E,V_liq is within the range of from 15 to 150, and preferably of from 20 to 100, E being expressed in watts and V_liq being expressed in dm³;</li><li>b) E/F_g ranges from 0.15 to 1.55, Fg being expressed as litres/hour (1/h) of C₂F₄ + O₂ (+C₃F₆</li></ul>

Another important parameter is the value of the gas flow rate Fg with respect to the volume of the liquid phase of the reaction (V_liq): said value is interdependent with the above parameters (a) and (b), and should be such that: c) V_liq/ Fg is from 10.10-³ to 25.10^-3, and preferably from 10.10-³ to 17.10^-3.

It is evident that the operating conditions of the process according to the present invention are considerably different from those of the process disclosed and exemplified by the above US patent, due to a considerably higher intensity of radiation with respect to the reaction volume (liquid phase) and the flow rate of the gaseous reactants. Furthermore, the flow rate of the gaseous reactants with respect to the reaction volume (liquid phase) is maintained at lower values.

It was not foreseeable that by employing a specific radiation intensity with respect to both the volume of the reactant liquid phase and the flow rate of the gaseous reactants, which is much higher than the ones generally used in the processes of the prior art, not only the conversions but also the yields of useful products can be improved substantially.

The liquid reaction phase, contained in the reactor, is exposed to U.V. radiation emitted by a lamp of known type, with a wavelength within the range of from 200 to 600 nm.

The other operating conditions of the process according to the present invention fall within the scope of the processes known from the above patent to Sianesi and still other patents of the applicant.

The reaction is carried out at a temperature of from -30 to -100 C by passing the gaseous reactants 0₂ and C₂F₄ and possibly also C₃F₆, through the reaction liquid initially composed of only liquified C₃Fs and, subsequently of a mixture of said C₃F₆ and the liquid products formed during the reaction.

The gaseous mixture of O₂+C₂F₄ is introduced continuously. and the molar ratio of O₂/C₂F₄ is kept within the range of from 1 to 10, preferably of from 3 to 9.

The reactant mixture is maintained at a temperature of from -30° C to -100° C, preferably of from -40 to -80 C.

The reaction can be carried out under atmospheric, subatmospheric and superatmospheric pressures. The product of the photo-oxidation, containing peroxy groups and having a very high molecular weight (i.e., a high viscosity) in consideration of the usual applications of the end product, is subjected to a thermal or photochemical treatment for the elimination of the peroxy groups according to methods known from, e.g., GB-A 1,226,566. The fluorination of the end groups is (then) carried out with fluorine gas thermally at temperatures of from 100° to 250 °C or in the presence of U.V. light at temperatures of from 50° to 120°C, see US-A-4,664,766.

The liquid reaction phase, contained in the reactor, is exposed to U.V. radiation emitted by a lamp of known type, with a wavelength within the range of from 200 to 600 nm.

The other operating conditions of the process according to the present invention fall within the scope of the processes known from the above patent to Sianesi and still other patents of the applicant.

The reaction is carried out at a temperature of from -30 to -100 C by passing the gaseous reactants O₂ and C₂F₄ and possibly also C₃F₆ through the reaction liquid initially composed of only liquified C₃F₆ and, subsequently of a mixture of said C₃Fs and the liquid products formed during the reaction.

The gaseous mixture of O₂+C₂F₄ is introduced continuously, and the molar ratio of 02/C2F4 is kept within the range of from 1 to 10, preferably of from 3 to 9.

The reactant mixture is maintained at a temperature of from -30° C to -100 C, preferably of from -40 to -80 C.

The reaction can be carried out under atmospheric, subatmospheric and superatmospheric pressures. The product of the photo-oxidation, containing peroxy groups and having a very high molecular weight (i.e., a high viscosity) in consideration of the usual applications of the end product, is subjected to a thermal or photochemical treatment for the elimination of the peroxy groups according to methods known from, e.g., GB-A 1,226,566. The fluorination of the end groups is (then) carried out with fluorine gas thermally at temperatures of from 100° to 250 °C or in the presence of U.V. light at temperatures of from 50° to 120° C, see US-A-4,664,766.

The thermal decomposition of the peroxide groups may be only partial, the residual peroxy oxygen being eliminated during the subsequent fluorination step (see US-A-4,664,766), a controlled reduction of the molecular weight being thus achieved, as disclosed in US-A-4,668,357.

The regulation of the molecular weight can be further accomplished by means of a catalytic thermal cracking treatment at a temperature of from 150° to 380°C, in the presence of AIF₃ or any other catalytically active fluorides, oxyfluorides or oxides, as disclosed in EP-A 167,258, 224,201 and 223,238, followed by the fluorination with fluorine gas as described above in order to convert the oxygen-containing terminal groups into neutral perfluoroalkyl groups.

The catalytic thermal cracking treatment furthermore decreases the content of -CF₂0- units present in the product, whereby an end product which contains a minimum number of such units can be obtained.

The peroxy product from the photo-oxidation can optionally be directly subjected to the above catalytic thermal cracking treatment.

The following examples are given only for illustrative purposes.

Example 1

At a temperature of -60° C, 800 g of C₃F₆ were placed into a cylindrical glass reactor (volume 500 ml, optical path 1 cm), equipped with an internal coaxial quartz sheath, a dipping tube for the introduction of gases, a sheath with a thermocouple for determining the internal temperature and a reflux condenser maintained at a temperature of -80° C. Through the dipping tube a gaseous mixture consisting of 27 I/h of 0₂ and 9 1/h of C₂F₄ was introduced in the reactor. By means of a cooling bath placed around the reactor the temperature of the liquid reactant phase was maintained at -60 C throughout the whole experiment.

After introducing an U.V.-lamp (HANAU TQ 150 type; emitting 47 W of U.V. light having a wavelength in the range of from 200 to 600 nm and 12 W of energy corresponding to radiation of ≦300 nm)into the quartz sheath, said lamp was turned on, and irradiation and introduction of the reactant gases were continued for 5 hours.

After 5 hours of irradiation, the lamp was turned off, the reactor was vented, and from the reactor the unreacted C₃F₆ was recovered by evaporation at room temperature. Thus 420 g of oily polymeric residue were obtained. Said residue had a content of active (peroxy) oxygen of 2.75%, based on iodometric titration. The ¹⁹F-NMR spectrum revealed polyetherpolyperoxy chains, wherein the total C₃F₆/C₂F₄ ratio was 0.85 and the ratio CF₂/C₃F₆+C₂F₄ was 0.019. The average number molecular weight was 6,630 and the viscosity of the product was 983 cSt at 20°C, as determined with an OSTWALD-FENSKE viscometer. The yield with respect to C2F4 in the obtained oil was 93%.

The results of Examples 1-8 are summarized in Table 1.

Example 2

By using the same equipment as in Example 1, a photooxidation was carried out under the same conditions, as regards temperature and intensity of irradiation, as in Example 1, but the flow rate of C₂F₄ was changed. In this case, 3 I/h of TFE were employed. After 5 hours of reaction, 213 g of a polymer with a content of active oxygen of 0.7% (based on iodometric titration) were isolated from the reactor . According to ¹⁹F-NMR the polymer was composed of polyether-polyperoxy chains, wherein the ratio C₃F₆/C₃F₄. was 2.11, the ratio CF₂/C₃F₆ +C₂F₄ was 0.063, and the average number molecular weight was 5,700.

The viscosity of the product was 955 cSt at 20° C.

Example 3

By using the same equipment as in Example 1, a photooxidation was carried out under the same conditions of temperature, flow rate of 0₂ and flow rate of C₂F₄ as in Example 2, but the intensity of the lamp was reduced. In this case 33W of U.V. radiation within the range of from 200 to 600 nm and 8.5 W of U.V. radiation of ≦300 nm were used.

After 5 hours of reaction, 147 g of a polymer were recovered from the reactor, which polymer, as revealed by ¹⁹F-NMR,was composed of polyether-polyperoxy chains wherein the ratio C₃F₆/C₂F₄ was 0.74, the ratio CF₂/C₃F₆ +C₂F₄ was 0.0112, and the average number molecular weight was 12,000.

According to iodometric analysis, the product had a content of active oxygen of 3.86% and showed a viscosity of 5,330 cSt at 20° C.

Example 4

By using the same equipment as in Example 1, a photooxidation was carried out under the same conditions of temperature and intensity of irradiation as in Example 1, but the flow rate of the reactants was changed. In this case, 5 I/h of C₂F₄ and 31 I/h of 0₂ were introduced. After 5 hours of reaction, 338 g of a polymer were recovered from the reactor. According to iodometric analysis, said polymer showed a content of active oxygen of 1.9%.

The viscosity of the product was 637 cSt at 20° C.

The ¹⁹F-NMR analysis showed that the polymer was composed of polyether-polyperoxy chains wherein the ratio C₃F₆/C₂F₄ was 1.18, the ratio CF₂/C₃F₆ + C₂F₄ was 0.027, and the average number molecular weight was 5,200.

Example 5

By using the same equipment as in Example 1, a photooxidation was carried out under the same conditions as in Example 1, but at a temperature of -40 C. In this case, after 5 hours of reaction, 488 g of a polymer were recovered from the reactor. According to iodometric analysis, said polymer showed a content of active oxygen of 1.9%.

The viscosity of the product was 210 cSt at 20° C.

¹⁹F-NMR analysis showed the polymer to be composed of polyether-polyperoxy chains wherein the ratio C₃F₆/C₂F₄ was 1.17, the ratio CF₂/C₃Fs +C₂F₄ was 0.032, and the average number molecular weight was 3,000.

The yield of C₂F₄ in the obtained oil was 89%.

Example 6

By using the same equipment as in Example 1, a photooxidation was carried out under the same conditions as in Example 2, but at a temperature of -40° C. After 5 hours of reaction, 479 g of a polymer were isolated from the reactor. According to iodometric analysis, said polymer showed a content of active oxygen of 0.92%.

The viscosity of the product was 188 cSt at 20 C.

The ¹⁹-NMR analysis showed the polymer to be composed of polyether-polyperoxy chains wherein the ratio C₃F₆/C₂F₄ was 1.91, the ratio CF₂/C₃F₆ +C₂F₄ was 0.038, and the average number molecular weight was 3,300.

Example 7

By using the same equipment as in Example 1, a photooxidation was carried out under the same conditions as in Example 3, but at a temperature of -40 C.

The radiation energy at a wavelength of ≦300 nm was 8.5 W.

After 5 hours of reaction, 265 g of a polymer were recovered from the reactor. According to iodometric analysis the polymer had a content of active oxygen of 1.47%.

The viscosity of the product was 504 cSt at 20° C.

¹⁹F-NMR analysis showed the polymer to be composed of polyether-polyperoxy chains wherein the ratio C₃F₆/C₂F₄ was 1.47, the ratio CF₂/C₃F₆ +C₂F₄ was 0.021, and the average number molecular weight was 4,200.

Example 8

By using the same equipment as in Example 1, a photooxidation was carried out under the same conditions as in Example 4, but at a temperature of -40° C.

After 5 hours of reaction, 453 g of a polymer were discharged from the reactor. According to the iodometric analysis the polymer had a content of active oxygen of 1.26%.

The viscosity of the product was 226 cSt at 20 C.

¹⁹F-NMR analysis showed the polymer to be composed of polyether-polyperoxy chains, wherein the ratio C₃F₆/C₂F₄ was 0.024, and the average number molecular weight was 3,400.

Example 9

A stainless-steel cylindrical reactor was used, which reactor was equipped with a coaxial quartz sheath. The ratio E/V_liq was 80, the ratio E/Fg was 0.88, and the ratio V_liq/F_g was 11x10^-3.

The reaction was started with an initial charge of liquid C₃F_s in the reactor. During the reaction, a flow rate of the reactant gases was maintained which was 2,730 I/h for 0₂ and 1,344 I/h for C₂F₄.

The reaction was carried out for 42 hours. The reaction product was continuously discharged, and C₃F₆ was replenished in a way such as to maintain a constant concentration of the oil in the reactor.

The relevant operating conditions are reported in Table 1. In the same table, the data reported in the Examples of the above cited US-A-3,770,792 are given for comparative purposes.

Example 10

The product obtained in Example 4 was placed in a photochemical reactor and was subjected to a photoreduction at a temperature of 40° C in order to eliminate the peroxy power (P.O.). After 12 hours, 321 g of polymer were discharged, placed into a photochemical reactor and subjected to a photo-assisted fluorination at a temperature of 50° C (5 1/h of fluorine and 5 1/h of nitrogen). After 10 hours, 314 g of neutral product were obtained (yield 95%). By distillation of the neutral product under vacuum four fractions, A, B, C and D, were obtained, which showed the characteristics reported in Table 2.

The ratios C₃F₆O/C₂Fa₄O were, respectively: <ul id="ul0005" list-style="none"><li>for A = 1.13; for B = 1.42; for C = 1.32; for D = 1.20; the ratios C₃F₆O/CF₂O were:</li><li>for A = 14.2; for B = 15.5; for C = 14.0; for D = 11.9; the ratios C₂F₄O/CF₂O were:</li><li>for A = 12.5; for B = 10.9; for C = 10.2; for D = 9.8.</li><li>From this data, one can calculate the ratio:<maths id="math0002" num=""><img file="EP0344547A2_D0004.tif" /></maths>which was:</li><li>for A = 3.74%; for B = 3.79%; for C = 4.22%;and for D = 4.64%.</li></ul>

In Table 3 the characteristics of Fomblin ® Y and Z (commercial products) are given for comparative purposes. <tables id="tabl0001" num="0001"><img file="EP0344547A2_D0005.tif" /></tables><tables id="tabl0002" num="0002"><img file="EP0344547A2_D0006.tif" /></tables><tables id="tabl0003" num="0003"><img file="EP0344547A2_D0007.tif" /></tables><tables id="tabl0004" num="0004"><img file="EP0344547A2_D0008.tif" /></tables>