Uniform molecular weight polymers

TECHNICAL FIELD

0001This invention relates to processes for carrying out "living" polymerizations. More particularly, this invention relates to processes for preparing polymers having a relatively narrow molecular weight distribution. Specifically this invention relates to the synthesis oftelechelic polymers by a process capable of producing polymers whose ratio of weight average molecular weight, M_w, to number average molecular weight, M_n, approaches one.

BACKGROUND OF THE INVENTION

0002In co-pending European patent application 265 053 of some of the inventors herein, a new family of polymerization initiating systems is disclosed based on complexes formed from organic ethers, in conjunction with Lewis acids. Polymerizations conducted with such systems have been found to result in cationic polymerizations, sometimes termed "living" polymerizations, which polymerizations are termination less, and operate without chain transfer. Even though such polymerizations have produced polymers with fairly broad molecular weight distributions, the systems can be used to produce polymers of considerable commmercial importance.

0003It has now been found possible, however, to conduct such polymerizations in a way in which the M_wlM_n values of the polymers produced are relatively small, i.e., the molecular weight distribution of the resulting polymer molecules is particularly narrow. As is generally recognized, it is frequently desirable to prepare polymers having narrow molecular weight distributions for a variety of reasons, and polymers exhibiting such characteristics, for example, have been used as motor oil additives, as well as in paint formulations, to desirably improve the viscosity indices in such oils and paint. In addition, such polymers can be employed as calibration standards in connection with gel permeation chromatography, and in various other applications.

0004In the past techniques such as, for instance, fractionation of polymeric materials exhibiting a broad spectrum of molecular weights have been resorted to in preparing polymers having a narrow molecular weight distribution. Inevitably, however, such methods are both laborious and expensive, and thus are undesirable at least for those reasons.

0005In view of the foregoing, therefore, it is a first aspect of this invention to produce polymers having a relatively narrow range of molecular weight distribution.

0006A second aspect of this invention is to provide a process from preparing polymers in which the weight average molecular weight, to number average molecular weight, is less than 1.5.

0007Another aspect of this invention is to provide a method for producing polymers having a relatively narrow range of molecular weight distribution, without resort to polymer separation techniques.

0008An additional aspect of this invention is to conduct telechelic polymerizations in such a way that polymeric product falling within a relatively narrow molecular weight range is produced in the first instance.

0009A further aspect of this invention is to reduce undesirable reactions within the polymerization reaction mixture, thereby maximizing the reaction required to produce the desired polymeric material.

0010The foregoing and other aspects of the invention are provided by a process for producing polymers having a relatively narrow molecular weight distribution characterized in that a polymerization is initiated by combining an initiator component of the formula<maths id="math0001" num=""><img file="EP0341012B1_D0001.tif" /></maths>in which R_1' R₂ and R₃ are alkyl, aryl, or aralkyl groups, and can be the same or different, and X is an acetate, an etherate, a hydroxyl group, or a halogen, and i is a positive whole number less than 7; a Lewis acid component of the formula MX_n in which M is titanium, aluminum, boron, or tin, X is a halogen, and n is a positive whole number; an electron donor component having an electron donor number from at least 25 to no more than 50, a cationically polymerizable hydrocarbon monomer component selected from the group consisting of olefins, diolefins and substituted derivatives thereof; and a solvent for said components, wherein said components are combined in amounts such that the number of moles of the Lewis acid component present at least about equals the total number of moles of said initiator component and of moles of said electron donor component present; and at least about one mole of electron donor component is present for about every 10 moles of initiator component present; and wherein the reaction solution thus formed is maintained at a temperature below -10°C until the desired polymer has been formed, and wherein further, when the dielectric constant of said solvent is about equal to, or greater than 7, said donor number is from at least 30 to no more than 50, and when the said temperature is below -60°C, said donor number is from at least 25 to no more than 50.

0011The foregoing and other aspects of the invention are provided by a polymer produced by the process of the preceding paragraph wherein said polymer has a ratio of weight average molecular weight to number average molecular weight, of no more than 1.5.

0012The foregoing and still other aspects of the invention are provided by polyisobutylene in which the ratio of weight average molecular weight, to number average molecular weight, is no more than 1.15.

0013Polymerizations of the type contemplated herein are carried out by the polymerization of olefins and diolefins in the presence of a polymerization initiator complex prepared in a solvent system using procedures found to minimize decomposition of the active centers of the complex, as well as reduce side reactions which lead to the formation of undesirable products. The initiator complexes employed in the invention comprise certain initiator compounds in combination with various Lewis acids, together with particular electron donor components. Inasmuch as the unwanted side reactions are eliminated or greatly minimized, molecular weight control of the polymeric product can be accomplished simply by adjusting the relative amounts of monomer and initiator present in the reaction mixture. The polymer will continue to grow as long as monomer is available for reaction, and as long as the monomer is not prevented from reacting with the growing center of the polymer by precipitation of the polymer from the reaction mixture caused by insolubility of the polymeric product, or terminated by the deliberate destruction of the active centers.

0014In conducting cationic polymerizations an initiator compound of the general formula (A) is combined with a Lewis acid in a solvent, and monomer is added to the system, thereby initiating a living polymerization. In the reaction, a molecule of said initiator compound combines with a Lewis acid molecule to produce a carbocation and a counter-anion or "gegenion". The carbocation thus generated is an active site to which the monomer presents adds during the cationic polymerization process. While the mechanism described, is the primary reaction of the system, unfortunately, other reactions take place concurrently. For example, the carbocation has a tendency to split off one of its positively charged hydrogen atoms, forming a proton which creates a new polymerization reaction site. Such "protic" initiation also terminates the polymerization of the initial polymer chain. Both mechanisms give rise to unwanted variations in polymer molecular weight.

0015In other cases, the halogen originally attached to the gegenion returns to the carbocation, destroying the latter as a polymerization reaction site in a process referred to as irreversible termination. In still other cases, the growing carbocations have such a strong positive charge that they exhibit a pronounced affinity for the internal structure of the growing chain, leading to an internal reaction involving reaction of the end of the chain with the internal structure, referred to as "self-alkylation", a process, for example, producing unwanted indanyl groups. Polymers which have undergone self-alkylation not only interfere with formation of polymers having a uniform molecular weight, but the attachment of desirable functional endgroups, which require polymers with halogenated terminal ends, is prevented. Thus while cationic polymerizations may conveniently be used for the synthesis of polymers having molecular weights up to 100,000, and higher, unless the preceding competing reactions are avoided, the uniformity of the polymeric product produced is inferior, due to the different molecular weight polymer chains which result.

0016While not wishing to be bound by the theory, it is postulated that when electron pair donors exhibiting particular properties are added to the system, such donors share their electrons with the carbocations, thereby reducing their positive charge, as well as the positive charge of their terminal hydrogen atoms. This in turn, reduces the growing chain's latent tendency to split off protons, to react internally with themselves, or to accept reaction-terminating halogen atoms from the gegenions irreversibly.

0017A further advantage of moderating the reactivity of the growing chain and/or initiator compound by the addition of the electron donor compound is that the rate of polymer propagation is reduced relative to the rate of polymer initiation, favoring the formation of more uniform molecular weight distribution polymers.

0018A further disadvantage of carbocations having a high degree of reactivity stems from the fact that they tend to produce intermolecular alkylation in the case of diene polymerizations. Such side reactions cause the polymer chains to interact, forming highly branched, frequently insoluble polymers.

0019It is important that the electron donor be selected so that it has a sufficient donor strength to produce the action described, but one not so strong as to suppress the desired polymerization. In addition, it has been found that the strength of the donor is influenced by the temperature of the polymerization and the nature of the solvent in which the polymerization is conducted.

0020The tendency of, or "strength" of the electron pair donor to share its electrons with the initiator component has been referred to as its "donor number", DN, or sometimes its "donicity". The donor number is defined as the molar enthalpy value for the reaction of the donor with SbCI₅ as a reference acceptor in a 10-³M solution of dichloroethane. While the use of some compounds capable of exerting an electron donor effect have previously been used in polymerization systems, the desirable effect achieved through the use of electron donor compounds exhibiting the donor number values taught by the invention has not previously been appreciated. Consequently, the compounds used in the past have been substantially weaker than the compounds found to be valuable for the purposes of the invention taught herein.

0021Although the reqired donicity of the electron pair donors of the invention will depend upon other factors associated with the polymerization reaction, as will be further explained in the following, it has been found that the donor number of the electron pair donor should be at least 25 if the undesired reactions previously referred to are to be avoided, while it should not exceed a value of 50 in order that practical reaction rates can be achieved.

0022Among the numerous electron pair donors suitable for use with the invention may be mentioned dimethyl acetamide, dimethyl formamide, dimethyl sulfoxide, hexamethylphosphoric triamide, N-methyl-2-pyrrolidinone, tetramethylurea, and many others. Some typical electron pair donors and their donor numbers are listed by Viktor Gutman in "The Donor-Acceptor approach to Molecular Interactions", Plenum Press (1978).

0023It has also been found that both the temperature of the polymerization and the nature of the solvent selected for the reaction have a bearing on the nature of the electron pair donor required to produce the desired polymeric product. For example, it has been found that in order to produce polymers in which the M_w/M_n is maintained at about, or below 1.5, a relatively narrow molecular weight distribution, the polymerization should be conducted at a temperature below -10°C, and a preferred range is from -40°C to -80°C, although lower temperatures may be employed if desired. When the reaction is conducted over-60°C however, the donor number should be from at least 30 to no more than 50 if desirable molecular weight distributions are to be achieved.

0024As indicated, the nature of the solvent also has an influence on the nature of the reaction. In is regard it has been found that there is a correlation between the polarity of the solvent, or mixture of solvents employed in the reaction, reflected by their dielectric constant, and the donor number of the electron pair donor most suitable for the reaction. For example, when the dielectric constant of the solvent system is about equal to, or great- erthan 7, it is desirable that the electron donor number have a value of from 30 to 50, while below such dielectric constant value, the donor number should be from 25 to 50. In the case of mixed solvents the effective dielectric constant value for the mixture is determined on a weighted average basis. Suitable solvents include normal, branched, or cyclic hydrocarbons, including their halogen substituted derivatives, mixtures of such compounds, and others. Suitable solvents include, for instance, n-hexane, n-pentane, n-heptane, ethyl chloride, methylene chloride, n-butyl chloride, benzene, cyclohexane, isopentane, and mixtures of such compounds.

0025Initiator compounds of the type contemplated by the invention comprise compounds of the general formula (1) where R_1' R₂, and R₃ are selected from the group consisting of alkyl, aryl, or aralkyl groups, and can be the same or different, and X is an acetate, an etherate, hydroxyl group, or a halogen. Suitable compounds, include for example, cumyl, dicumyl and tricumyl halides, particularly the chlorides, i.e., 2-chloro-2-phenyl propane, i.e., cumylchloride; 1,4-di(2-chloro-2-propyl) benzene, i.e., di(cumylchloride); 1,3,5-tri(2-chloro-2-propyl)benzene, i.e., tri(cumylchloride); 2,4,4-trimethyl-2-chloro-pentane; 2-acetyl-2-phenyl-propane, i.e., cumyl acetate; 2-propionyl-2-phenyl-propane, i.e., cumyl propionate; 2-methoxy-2-phenyl propane, i.e., cumylmethyl ether; 1,4-di(2-methoxy-2-propyl) benzene, i.e., di(cumylmethyl ether); and 1,3,5-tri(2-methoxy-2-propyl) benzene, i.e.,tri(cumylmethyl ether).

0026Any of various Lewis acids of the general formula MX_n where M can be titanium, aluminum, boron, tin and others, X is a halogen, and n is a positive whole number, are suitable for purposes of the invention. Such compounds include, but are not limited to the titanium and boron halides, particularly titanium tetrachloride, boron trichloride, aluminum trichloride, antimony pentachloride, antimony pentafluoride, boron trifluoride, and others. Use of the titanium halides, is particularly preferred, however.

0027The amount of the Lewis acid present in the initiator system may vary; however, it is desirable that the number of moles of Lewis acid present at least be equal, preferably exceed the total number of moles of the initiator compound and moles of the electron donor compound present. Furthermore, at least one mole of donor compound should be present for every 10 moles of initiator compound present, and the use of about equal moles of such compounds is preferred.

0028The invention is suited for the carbocationic polymerization of hydrocarbon monomers selected from the group consisting of olefins, diolefins and substituted derivatives thereof. Normally said hydrocarbon monomers have from 2 to 20, but preferably from 4 to 8 carbon atoms. The process can be employed for the polymerization of such monomers to produce polymers of different, but uniform molecular weights, for example, from 300 to in excess of a 1,000,000. Such polymers can be low molecular weight liquids or viscous polymers having a molecular weight of from 200 to 10,000, or solid waxy to plastic substances, or elastomeric materials having molecular weights of from about a 100,000 to a 1,000,000, or more. Suitable monomeric materials include such compounds as isobutylene, styrene, beta pinene, isoprene, butadiene, sustituted compounds of the preceding types, and others. The use of isobutylene has been found to produce polymers having particularly narrow ranges of molecular weight, however, and the polymerization process of the invention is especially adapted to the use of that monomer.

0029In order to minimize the undesirable reactions referred to, it is necessary that the initiator compound and Lewis acid not be present together with the monomer, in the absence of the electron donor compound.

0030While uninterrupted growth can be maintained for an extended period, in instances where termination is desired in order to prepare a polymer having a particular molecular weight range, termination can be induced either by increasing the temperature of the polymerization system and thus decomposing the active growing complex, or can be achieved by adding a nucleophilic terminating agent such as methanol, pyridine, ammonia, an alkylamine, and others.

0031While not intended to be limiting in nature, the following examples, in which the volume measurements recited describe the undiluted amount of the component referred to, are illustrative of the invention.

Example 1

0032In this example a Lewis acid is combined with an initiator and an electron donor compound having a donor number of 17.1, lower than that required to produce the advantages of the initiator system contemplated by the invention. In the experiment, a 75 ml test tube has added thereto as a mixed solvent 15 ml of hexane and 10 ml of methyl chloride. Thereafter, 1.0 X 10-⁴ mole of cumyl chloride, the initiator compound, 1 X 10-⁴ mole of ethyl acetate, the electron donor with a DN of 17.1, and 1.3 X 10-² mole of isobutylene, the monomer, are added to the solution in the order recited, the solution being maintained at -40°C. Polymerization is initiated by the addition of 1.8 X 10-³ mole of titanium chloride, and is terminated after 30 minutes by the addition of 3 ml of prechilled methanol. Gel permeation chromatography of 0.33 gram of the product shows that only 72 percent by weight of the total product was formed by controlled initiation, while 28 percent by weight of polymer is produced by undersirable protic initiation.

Example 2

0033In a similar experiment, to a 75 ml test tube are added 25 ml of a solvent, methyl chloride, 1.0 X 10-4 mole of an initiator, cumyl chloride, 1 X 10-⁴ mole of an electron donor compound, ethyl acetate, and 1.3 X 10-² mole of isobutylene. The solution is maintained at -40°C, and the polymerization is initiated by the addition of 1.8 X 10-³ mole of titanium tetrachloride. The reaction is terminated after 10 minutes by the addition of 3 ml of prechilled methanol. Gel permeation chromatography of 0.68 grams of the product shows a broad high molecular weight peak equivalent to a M_n of 50,000 and a M_w/M_n of 2.26. The results are typical of a polymer produced to a substantial degree of a polymer produced to a substantial degree by undesirable protic initiation.

0034Both examples 1 and 2 demonstrate that ethyl acetate which has an electron donor number of only 17.1 is incapable of sufficiently modifying the carbocation, so that polymers which have poorly defined structures as a result of polymer initiation caused by protic impurities, which can include such materials as water, alcohol, amines, and the like are formed.

0035The following examples 3 and 4 illustrate that by the use of a stronger electron pair donor initiation by protic impurities can be completely eliminated, and polymers with well defined structures can be synthesized.

Example 3

0036In a further experiment, each of three 75 ml test tubes have added thereto a mixed solvent consisting of 15 ml of hexane mixed with 10 ml of methyl chloride. To the solvent are then added 1 X10-⁴ mole of a cumyl chloride initiator, 1 X 10-⁴ mole of dimethyl sulfoxide, the electron pair donor with a DN of 29.8 and 1.3 X 10-² mole of isobutylene monomer. The reaction, which is conducted at-40°C, is initiated by the addition of 1.8 X 10-³ mole of the Lewis acid titanium tetrachloride. The polymerization in the first test tube is terminated by the addition of prechilled methanol after 30 minutes. An additional 1.3 X 10-² mole of isobutylene monomer is then added to the two remaining test tubes, the reaction in the second being terminated after an additional 30 minutes by the addition of prechilled methanol. A still further addition of 1.3 X 10-³ mole of isobutylene is made to the third test-tube, following which the reaction is terminated after a further 30 minutes of reaction. Gel permeation chromatography analysis of the product shows the formation of a uniform polymer having a narrow molecular weight distribution, with no product present of the type formed by uncontrolled initiation.

0037Results are as follows: <tables id="tabl0001" num="0001"><img file="EP0341012B1_D0002.tif" /></tables>

0038The fact that the polymerizations proceeded as would be expected in the case of polymerizations experiencing no chain transfer or termination, in other words, as a "living" polymerization, is substantiated by the fact that the molecular weights obtained from the product in all three test tubes showed theoretical values, i.e. <ul id="ul0001" list-style="none"><li>_{Mn =} grams of polymer formed numberof initiator moles</li></ul> Ultraviolet and nuclear magnetic resonance analysis of the product demonstrates that the chains were terminated on one end with a cumyl group, and on the other end with a tertiary chlorine atom.

Example 4

0039In this example four 75 mm test tubes are prepared and the reactions are carried out at -40°C under conditions described in the following table 1. In each case, polymerization is initiated by the addition of 1.8 X 10-³ mole of the Lewis acid titanium tetrachloride. After 10 minutes the reactions are terminated by adding 3 ml of prechilled methanol. Analysis of the polymers produced by gel permeation chromatography indicates the following results, which indicate that only polymers with well defined structure were formed; no product indicating uncontrolled initiation being evident. Ultraviolet and nulclear magnetic resonance analysis of the product displays the cumyl and tertiary chlorine endings which would be expected in a living polymerization. <tables id="tabl0002" num="0002"><img file="EP0341012B1_D0003.tif" /></tables><tables id="tabl0003" num="0003"><img file="EP0341012B1_D0004.tif" /></tables>

Example 5

0040The following experiment is carried out to demonstrate the inhibiting effect which the presence of a strong electron pair donor, for example, dimethyl acetamide, or dimethyl sulfoxide, has on a reaction system which includes protogenic impurities such as water. The experiments are carried out according to the procedure of the preceding examples, with the exception that no initiator compound is included. Three samples are tested as shown in the following table. <tables id="tabl0004" num="0004"><img file="EP0341012B1_D0005.tif" /></tables>

0041Despite the presence of water, a protogenic impurity, no polymer is formed, due to the suppression of protic initiation by the presence of the electron pair donor.

0042However, in a set of duplicate experiments in which the electron pair donor, either dimethyl sulfoxide or dimethyl acetamide, was excluded, the water present initiated protic polymerization, 100 percent conversion of the monomer being achieved in the case of titanium tetrachloride, and 18 percent conversion in the case of boron trichloride. In otherwords, the experiment demonstrates that the presence of strong electron pair donors can totally suppress protic initiation, regardless of the relatively nonpolar nature of the solvent mixture employed, or the Lewis acid used. From a practical standpoint, the example shows that cationic polymerizations can be carried out according to the method of the invention without any necessity to carefully purify the reaction mixture components so as to exclude protogenic impurities, thereby avoiding any need for costly purification procedures. As previously pointed out, the extreme reactivity of living polymerization initiator systems has previously been disadvantageous due to the side reactions and by-products that tend to result. Heretofore, such high reactivity has necessitated the use of polymerization mediums of the highest purity, and the elimination of even trace impurities.

Example 6

0043Additional experiments are carried out involving a variety of initiator compounds in the following. The polymerizations are carried out at -40°C in 75 ml test tubes, as in the case of the preceding experiments. Three test tubes are prepared, each of which contains 1 X 10-⁴ mole of dimethyl sulfoxide, 15 ml of n-hexane solvent mixed with 10 ml of methyl chloride solvent, and the additional components listed in the following table. <tables id="tabl0005" num="0005"><img file="EP0341012B1_D0006.tif" /></tables>

0044Analysis of the resulting polymers gives following results: <tables id="tabl0006" num="0006"><img file="EP0341012B1_D0007.tif" /></tables>

0045Analysis by nulcear magnetic resonance shows the presence of tertiary chlorine groups on one end of the polymer chains and cumyl head group structures on the other end. The molecular weights are those theoretically expected, i.e., <ul id="ul0002" list-style="none"><li>_{Mn =} grams of polymer formed numberof initiator moles</li></ul>

0046It has previously been known that uncontrolled initiation, chain transfer, and inter and intra chain reactions can be reduced by carrying out the living polymerizations at lower temperatures. However, as can be seen from the above when the strong electron pair donors of the invention are included in the reaction mixtures, such undesirable side reactions can be completely eliminated, not simply reduced, thus providing the narrow molecular weight distributions which are one of the primary objectives of the invention. Furthermore, the use of such strong electron pair donors makes it unnecessary to resort to expensive cooling.

Example 7

0047In a further example which demonstrates the effect of the addition of strong electron pair donors, two 75 mm test tubes are charged with 1 X 10-⁴ mole of an initiator, cumyl chloride, a mixed solvent consisting of 15 ml of n-hexane combined with 10 ml of methyl chloride, and 1.37 x 10-² mole of isobutylene. The reaction is conducted at a temperature of -80°C. 1 X 10-⁴ mole of dimethyl sulfoxide is added to sample one, but not to sample two, and the polymerization is initiated by the addition of 1.8 X 10-³ mole of titanium tetrachloride to each of the samples. During the reaction, additional 1.37 X 10-² mole quantities of isobutylene are added to the samples, at 15 minute intervals, and after 75 minutes of reaction time the polymerization is terminated by the addition of prechilled methanol. The following results are obtained. <tables id="tabl0007" num="0007"><img file="EP0341012B1_D0008.tif" /></tables>

0048As can be seen, while the molecular weights in the case of both samples approached theoretical, sample one, in which the dimethylsulfoxide was present, showed a much more uniform structure, i.e., a significantly narrower molecular weight distribution. Polymers displaying broad molecular weight distributions are of limited usefulness due to the higher viscosities conferred by the presence of molecular chains having non-uniforms lengths.

Example 8

0049In a further experiment, two reactions are run under identical conditions with the exception that the first reaction is conducted at -40°C, while the other is carried out at -60°C. In both cases, the reaction is carried out in a 500 ml, 2-neck flask equipped with a stirrer. The flasks are charged with 1.16 grams (5 X 10-³ mole) of 1,4-bis(2-chloro-2-propyl)benzene, 0.7 ml of dimethyl sulfoxide, 200 ml of methyl chloride, and 15 ml of isobutylene. The polymerization is initiated by the addition of 8 ml of boron trichloride and allowed to continue for 2 hours. Polymerization is subsequently terminated by the addition of methanol. The following results are obtained. <tables id="tabl0008" num="0008"><img file="EP0341012B1_D0009.tif" /></tables>

0050Analysis by nuclear magnetic resonance shows that in both cases, the product produced is essentially pure bifunctional polymer, having tertiary chlorine end groups at each end of the polymer chains.

0051A subsequent experiment carried out at -40°C with identical ingredients except for the presence of the strong electron pair donor dimethylsulfoxide, leads to a polymeric product containing only about 40 percent by weight of the desired bifunctional polymer, which is contaminated by the presence of about 50 percent of the undesirable monofunctional polymer containing a tertiary chlorine end group on only one end of the polymer. The M_w/M_n value found is undesirably high at 2.0. The experiment clearly demonstrates that undesirable self-alkylation, leading to indanyl group formation, can be avoided by stabilizing the carbocation with the addition of a strong electron pair donor.

Example 9

0052In a still further experiment, two reactions are carried out in which the first contains the electron pair donor dimethyl sulfoxide, and the second a dimethyl acetamide electron pair donor. 1 X 10-⁴ mole of the electron pair donor is used in each case. The polymerizations are carried out in 75 ml test tubes to which has been added 15 ml of hexane, 10 ml of methyl chloride, 2 ml of the monomer isoprene, and 1 X 10-⁴ mole of an initiator compound cumyl chloride. The reaction, which is conducted at -40°C, is initiated by the addition of 1.8 X 10-³ mole of titanium tetrachloride, and is continued for 60 minutes. The following results are obtained. <tables id="tabl0009" num="0009"><img file="EP0341012B1_D0010.tif" /></tables>

0053In the case of both samples, the M_n is quite close to the theoretical value. Under similiar conditions, however, in the absence of an electron pair donor, the polymerization leads to highly branched product with a molecular weight distribution of greater than 10, indicating the presence of a substantial amount of microgel. In contrast, the products of samples 1 and 2 contain no gel, and are readily soluble in conventional solvents.

Example 10

0054Applicability of the invention to the formation of copolymers is demonstrated in the following experiment in which each of two test tubes is filled with 1 X 10-⁴ mole of cumyl chloride, a mixed solvent consisting of 15 ml of n-hexane combined with 10 ml of methyl chloride. and 4 ml of a mixture of isobutylene and isoprene which contains 3 percent isoprene and 97 percent isobutylene, on a volume basis. The test tube representing sample 1 is charged with 1 X 10-⁴ mole of dimethylsulfoxide, while sample 2 has 1 X 10-⁴ mole of dimethylacetamide added thereto. The polymerizations are initiated by the addition of 1.8 X 10-³ mole of titanium tetrachloride to each of the test tubes. The reaction is continued for 3 hours, after which it is terminated by the addition of prechilled methanol. The following results are obtained. <tables id="tabl0010" num="0010"><img file="EP0341012B1_D0011.tif" /></tables>

0055The molecular weights obtained are those theoretically expected, and the copolymers are found to contain 1.4 mole percent of the isoprene in trans 1,4 form.

0056The amount of solvent employed will depend upon the viscosity of the reaction solution desired, and may be varied within fairly broad limits. Typically, however, sufficient solvent will be added to provide a reaction solution having a solids contents of from 20 percent to 40 percent on a weight basis.