A dispenser form for sustainedly releasing sex pheromone of insects.

BACKGROUND OF THE INVENTION

0001The present invention relates to a dispenser form for sustainedly releasing a sex pheromone of insects or, more particularly, to a dispenser body capable of sustainedly releasing a sex pheromone compound of a species of insects at a constant rate over a long period of time into the atmosphere with an object to control population of the species of insectan pest.

0002Along with the progress of the technoloqy for controlling the population of insectan pest by utilizing the sex pheromone compound of the particular species of insects, various attempts and proposals have been hitherto made to obtain a constant or controlled rate of pheromone emission into the atmosphere of the field over a length of time during which an effective concentration of the pheromone compound in the atmosphere should desirably be maintained. For example, it is already practiced to prepare a dispenser form containing the pheromone compound and a large number of such dispenser forms are distributed over the field so as to emit the pheromone compound in the form of vapor at a controlled rate therefrom. It is highly desirable in order to effectively and economically utilize the sex pheromone compound with expensiveness that the rate of pheromone emission from the dispensers should be controlled at such a rate that the concentration of the compound in the atmosphere should be maintained to exhibit the desired effect over a desired length of time under varied environmental or, in particular, meteorological conditions such as temperature, humidity, wind velocity and the like. Notwithstanding such a desirable condition of uniform rate of pheromone emission, use of dispenser forms is unavoidably accompanied by a problem that the rate of pheromone emission therefrom is too large at one time and too small at the other, especially, when the pheromone compound should be released by permeating barrier walls made of a single kind of a polymeric material.

0003When the rate of pheromone emission is too large, the serviceable life of the dispenser forms would consequently expire too early before the end of the term of the desired length. When the rate of pheromone emission is too small, on the other hand, a considerable portion of the pheromone compound initially contained in the dispenser forms remains unutilized to cause a great economical disadvantage.

0004When the serviceable life of the pheromone dispensers is unduly short, it would be necessary that the dispenser forms must be distributed over the field several times in a season taking a large amount of the labor cost therefor in addition to the problem that the rate of pheromone emission from the dispensers may be unduly decreased in the latest stage of the serviceable life so that the desired effect can no longer be obtained. While it is highly desirable that a single round of the work for the distribution of dispensers over the field in a season is sufficient to sustain the necessary amount of the released pheromone compound and that the necessary minimum number of the dispenser forms to be distributed over the field should desirably be as small as possible per unit area of the field provided that the effect by the sex pheromone compound is not unduly reduced, a generally encountered difficulty when a single dispenser form contains an increased amount of the sex pheromone compound is that the rate of pheromone emission steadily decreases from the beginning to the end of the serviceable life of the dispenser with a considerably large difference in the rate of pheromone emission therebetween.

0005U.S. Patent No. 4,600,146 discloses a type of pheromone dispenser which is a tubular body made of a polymeric resin such as polyethylene or a copolymer of ethylene and vinyl acetate containing the sex pheromone compound in the capillary bore. The results of the field tests using such dispensers, however, indicated that the rate of pheromone emission therefrom was unavoidably somewhat decreased in the latter half of the serviceable life as is reported in Journal of Economic Entomology, volume 78, No. 6, pages 1431-1436 (1985).

0006On the other hand, it would not be an easy matter to sustainedly release a sex pheromone compound having a relatively large vapor pressure over a long period of time and no effective proposals have yet been made in this regard.

0007The inventors have continued extensive investigations with an object to develop a means, in a dispenser form in which a sex pheromone compound is enclosed in barrier walls, for solving the problem in the prior art dispensers that the rate of pheromone emis-ion steadily decreases, especially, in the latter half of the serviceable life of the dispenser and to provide a means for sustainedly releasing a sex pheromone compound having a relatively large vapor pressure over a long period of time leading to completion of the present invention.

SUMMARY OF THE INVENTION

0008Thus, the present invention provides a novel dispenser form free from the above described problems and disadvantages in the prior art dispensers and capable of sustainedly releasing a sex pheromone compound of insects at a constant rate over a period of 1 to 6 months.

0009The invention provides an improvement that, in a dispenser of tubular form for containing a sex pheromone compound of insects in which the pheromone compound permeates through a barrier wall made of a polyolefin or a copolymeric resin of vinyl acetate and an olefin and is released from the surface of the barrier wall, a part of the outer surface of the barrier wall is coated with a material which is impermeable or hardly permeable to the sex pheromone compound.

BRIEF DESCRIPTION OF THE DRAWING

0010<ul id="ul0001" list-style="none"><li>FIGURES la and 1b are each an axial cross sectional view of a dispenser form of the invention for sustainedly releasing a sex pheromone compound.</li><li>FIGURES 2 and 3 are each a graphic showing of the amount of the pheromone compound remaining in the dispenser as a function of days of exposure determined in the experiments in Examples 1 and 2, respectively.</li></ul>

DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS

0011As is illustrated in FIGURES la and Ib, the dispenser form of the present invention for sustainedly releasing a sex pheromone compound of insects is a tubular body having a barrier wall 1 made of a polymeric material and containing a sex pheromone compound 2 therein. The sex pheromone compound 2 enclosed in the tubular body permeates through the barrier wall 1 and is emitted to the outside atmosphere from the outer surface of the barrier wall 1. Different from conventional dispenser forms of such a type, the outer surface of the barrier wall 1 is partly coated with a material 3 which is impermeable or hardly permeable to the sex pheromone compound, which is referred to as the coating material hereinbelow. The sex pheromone compound is emitted naturally only from the uncoated portion of the outer surface of the barrier walls 1 and not from the coated portion.

0012The barrier wall 1 of the inventive dispenser form is made of a polyolefm or a copolymeric resin of vinyl acetate and an olefin. In particular, the barrier wall 1 should be made of a polyethylene or a copolymer of vinyl acetate and ethylene of which the content of the vinyl acetate moiety is 20% by weight or smaller. The configuration of the inventive dispenser is not particularly limitative including spherical, ellipsoidal, cylindrical and plate-like ones having a hollow space surrounded by the walls to serve as the barrier walls and containing the sex pheromone compound in the hollow space. A particularly preferable configuration of the dispenser form is a tube having an inner diameter in the range from 0.5 to 4 mm and a length in the range from 50 to 1000 mm with both ends tightly sealed after introduction of the sex pheromone compound into the capillary bore. The outer surface of the barrier walls 1 should be partly coated with a coating layer 3 of the coating material which should have an equilibrium swelling not exceeding 1% by weight or, preferably, not exceeding 0.5% by weight at 20 °C with the sex pheromone compound enclosed in the dispenser body. Suitable coating materials are exemplified by polymeric materials including polyvinylidene chloride, polyvinylidene fluoride, polyacrylonitrile, polysulfone, polycarbonate, polyamides, e. g. nylon, polymers of acrylic esters, e. g. polymethyl methacrylate, cellulose esters, e. g. cellulose acetate, regenerated cellulose, polyvinyl alcohol, polyurethane and the like. Metal foils may also be used.

0013The coating layer 3 of the coating material may be formed by any known method without particular limitations. For example, the outer surface of the barrier wall 1 is coated with a coating composition containing the coating material or a film of the coating material is adhesively bonded or welded to the outer surface of the barrier wall 1. it is sometimes sufficient to merely put a sheath or cap made of the coating material on to the barrier wall 1. When the dispenser body is in a long tubular form, the covering sheath of the coating material should have a length somewhat smaller than the dispenser body so that the end portions of the dispenser body are left uncovered when the covering sheath is put on the dispenser body and the sex pheromone compound is released from the uncovered portions of the tubular body. The covering sheath of the coating material should not be too long because the surface area of the barrier walls left uncovered and available for the emission of the sex pheromone compound is unduly decreased so that the rate of pheromone emission is decreased to have a considerably large portion of the pheromone compound initially contained left unutilized.

0014It is usually preferable that the coating layer of the coating material occupies from 30% to 90% of the whole outer surface of the barrier walls. The value of the equilibrium swelling of the coating material by the sex pheromone compound can be determined by immersing a chip of the coating material in the sex pheromone compound at the specified temperature and measuring the weight increase of the chip after a sufficiently long time of immersion.

0015The dispenser form of the invention may contain a single sex pheromone compound or a mixture of two kinds or more of such sex pheromone compounds. When the sex pheromone compound is susceptible to photochemical decomposition, it is advantageous that the polymeric material forming the barrier walls is admixed with an ultraviolet absorber or a coloring agent such as dyes and pigments and, simultaneously or alternatively, the sex pheromone compound contained in the dispenser form is also admixed with an antioxidant, ultraviolet absorber and the like dissolved therein. It is also optional that the sex pheromone compound is admixed with other known additives including fillers, solvents and so on.

0016As is understood from the above given description, the dispenser form of the invention is very advantageous in respect of the extremely uniform rate of pheromone emission over the whole period of the serviceable life. This advantage of constant rate of pheromone emission can be obtained over a long period of time even when the amount of the sex pheromone compound contained in each of the dispenser forms exceeds 70 mg. Moreover, the dispenser form of the invention is applicable even to a sex pheromone compound having a relatively high vapor pressure and such a sex pheromone compound contained in the dispenser form can be sustainedly released by substantially extending the serviceable life of the dispenser while maintaining a uniform rate of pheromone emission.

0017In the following, the dispenser form of the present invention for sustainedly releasing a sex pheromone compound is described in more detail by way of examples.

Example 1.

0018A dispenser form, which is referred to as the dispenser A hereinbelow, was prepared by introducing 75 mg of E-5-decenyl acetate into a capillary tube made of a high-density polyethylene and having an inner diameter of 0.8 mm and an outer diameter of 1.5 mm followed by weld-sealing and cutting of the tube in a length of 20 cm. Three more dispenser forms were prepared each in the same manner as in the dispenser A and were coated with a latex of polyvinylidene chloride over 30%, 60% and 80% of the whole outer surface area in a coating thickness of about 10 µm as dried leaving uncoated surface areas at both ends of the tubular forms. These partially coated dispenser forms are referred to as the dispensers B, C and D, respectively. Furthermore, one more dispenser form was prepared in the same manner as above except that the whole outer surface was coated with the polyvinylidene chloride latex in the same thickness. This entirely coated dispenser form is referred to as the dispenser E hereinbelow.

0019These five dispenser forms A to E were kept standing at 30 °C under a stream of air of 1.5 meters/second velocity and decrease of weight of each dispenser was determined periodically over a period of 70 days to calculate the percentage of the amount of the sex pheromone compound remaining in the dispenser. The results are shown in FIGURE 2 by the curves A to E for the dispensers A to E, respectively.

0020As is seen in this figure, the rate of pheromone emission from the uncoated dispenser A was remarkably large with a great difference between the rates at the initial and latest stages of the testing period while the rate of pheromone emission form the dispenser E was unduly small to leave a considerably large amount of the initially introduced pheromone compound unreleased. On the contrary, the rates of pheromone emission were adequate and quite uniform over the testing period from the partially coated dispensers B, C and D to ensure sufficiently long serviceable lives.

0021The equilibrium swelling of the polyvinylidene chloride in the sex pheromone compound was determined by immersing a chip of the resin of 20 mm by 20 mm by 1 mm dimensions in E-5- decenyl acetate at 20 °C and determining the weight increase after a sufficient length of time to find a value of 0.2% by weight.

Example 2.

0022A dispenser form, which is referred to as the dispenser F hereinbelow, was prepared by introducing 90 mg of 14-methyl-l-octadecene into a capillary tube made of a copolymer of 94% by weight ethylene and 6% by weight of vinyl acetate and having an inner diameter of 1.5 mm and an outer diameter of 2.2 mm followed by weld-sealing and cutting of the tube in a length of 10 cm. Another dispenser form was prepared in just the same manner as above and coated on 70% area of the outer surface thereof with a solution of cellulose diacetate in a coating thickness of about 8 pm as dfried leaving 30% area of the outer surface uncoated at one end of the tubular form. This partially coated dispenser form is referred to as the dispenser G hereinbelow.

0023These uncoated and partially coated dispenser forms F and G were subjected to the determination of the rate of pheromone emission therefrom in the same manner as in Example 1 to give the results shown in FIGURE 3 by the curves F and G, respectively. As is seen in this figure, the rate of pheromone emission from the dispenser F was too large with a great difference in the rates between the first and second halves of the testing period while the rate of pheromone emissiion was adequate and quite uniform from the partially coated dispenser G.

0024The equilibrium swelling of the polyvinylidene chloride in the sex pheromone compound was determined by immersing a chip of the resin of 20 mm by 20 mm by 1 mm dimensions in 14-methyl-1-octadecene at 20 °C and determining the weight increase after a sufficient length of time to find a value of 0.5% by weight.