Method for rendering non-ferrous metals corrosion resistant

Non-ferrous metal substrates such as aluminium are coated with a composition consisting essentially of a dispersion of colloidal titania particles in a water/polar organic solvent medium of a partial condensate formed by hydrolyzing a silane such as methyltrimethoxysilane in the presence of the colloidal titania particles and in the presence of a sufficient amount of an acid such as acetic acid to provide a pH in the range of from 2 to 6. Optionally, the composition can contain up to 20 weight percent of colloidal silica and/or up to 5 weight percent of other types of monoorganosilsesquioxanes based upon the total weight of solids in the composition. The coated substrates are heated until the coating cures, preferably at 50 °C to 150 °C, to form a transparent coating which renders the substrate more resistant to corrosion induced by acids or salts such as road salt or ocean spray.