Ultrasonic method and apparatus for evaluating spot weld zone

CA 02579671 2007-02-28

- 1 DESCRIPTION

ULTRASONIC METHOD AND APPARATUS FOR EVALUATING SPOT WELD ZONE

Technical Field

The present invention relates to a method and apparatus for ultrasonic nondestructive inspection of a diameter and soundness of a welded metal portion (also referred to as a weld solidified structure or a nugget hereinafter) formed by spot welding.

Background Art

For example, in plants for manufacturing automobile bodies, a spot weld inspection method which can be easily carried out has been recently desired for inspecting spot weld zones with high efficiency on site.

Since an automobile body is assembled by spot welding at thousands of points, quality of spot welding directly influences the strength and durability of the body, and thus it is very important to inspect whether or not spot welding is properly performed. As a method of inspecting spot weld zones, chisel inspection has been carried out for deciding the quality by confirming whether or not a spot weld zone is separated by a cold chisel inserted between spot-welded metal sheets. However, in the chisel inspection, spot weld zones may be broken, and thus it is difficult to precisely determine the quality of spot welding by the chisel inspection. Also, members each having a spot weld

CA 02579671 2007-02-28

- 2 zone broken by the chisel inspection cannot be used for products, and there is thus the problem of increasing the cost.

Therefore, various apparatuses and methods have been recently proposed for ultrasonic nondestructive inspection of the quality of spot welding.

For example, Japanese Unexamined Patent Application Publication Nos. 2000-146928, 2002-131297, 11-2627, and 6-265529 disclose methods and apparatuses in each of which an ultrasonic wave is vertically incident onto a sheet surface to detect a reflected wave, for evaluating the quality of a spot weld zone formed by welding two stacked sheets . Japanese Unexamined Patent Application Publication No. 62-52456 discloses an ultrasonic flaw detector based on local immersion method in which a pair of immersion probes disposed on and below a test piece to be opposed to each other with the test object disposed therebetween, and the test object is horizontally moved so that a spot weld zone of the test object is scanned by an ultrasonic beam transmitted from the transmitting probe and the presence of a flaw in the spot weld zone is determined on the basis of a signal received by the receiving probe.

In the above-mentioned prior art, an ultrasonic wave is sent and received vertically to the plate-shaped test object. Therefore, in an inclined surface 102 formed around each dimple 102b formed in a spot weld zone 102 of a test object illustrated in Fig. 10, an ultrasonic beam cannot be efficiently incident

CA 02579671 2007-02-28

- 3 onto the test object. There is thus the problem of difficulty in precisely detecting the size of a nugget 102a formed in the spot weld zone 102.

In other words, as shown in Fig. 10, when an upper sheet 101a and a lower sheet 101b are stacked and welded together by spot welding, a weld solidified structure 102a referred to as a nugget is formed in the spot weld zone 102 at a joint between the upper and lower sheets 101a and 101b. In spot welding, the upper and lower sheets 101a and 101b are strongly pressed by electrode tips not shown in the drawing to form the dimples 102b corresponding to the shapes of the electrode tips in the surfaces of the upper and lower sheets 101a and 101b.

Furthermore, the conical inclined surfaces 102c are formed between the bottoms of the dimples 102b and the surfaces of the upper and lower sheets 101a and 101b. In normal welding, the diameter of the nugget 102a is slightly larger than or substantially the same as the diameter of the electrode tips used for welding. Since the electrode tips have a chamfered cylindrical tip shape, the inner diameter of the dimples 102b is slightly smaller than the diameter of the cylindrical portions of the electrode tips. Therefore, the inner diameter of the dimples 102b is generally slightly smaller than the diameter of the nugget 102a. In abnormal welding, the diameter of the nugget is smaller than that in normal welding, thereby causing abnormality such as lack of strength. In Fig. 10, symbol S

CA 02579671 2007-02-28

- 4 represents the toe of the nugget 102a. The toe refers to a point of intersection between the front or back surface of the upper sheet 101a or the lower sheet 101b and the boundary of a weld metal.

As described above, in the spot weld zone 102, the conical inclined surfaces 102c are formed between the bottoms of the respective dimples 102b and the surfaces of the upper and lower sheets 101a and 101b. Therefore, an ultrasonic wave is reflected by the inclined surfaces 102c and little transmitted into the test object, thereby obtaining substantially no signal from a portion to be inspected by use of an ultrasonic inspection apparatus of the prior art in which an ultrasonic beam is sent and received vertically to the surfaces of the upper and lower sheets 101a and 101b of a test object. As described above, the size of the nugget 102a is slightly larger than or substantially the same as the diameter of the electrode tips, and thus the toe S of the nugget 102a substantially overlaps the inclined surfaces 102c formed in the test object. Therefore, as an ultrasonic wave is reflected by one of the inclined surfaces 102c, a correct signal cannot be obtained from a portion near the nugget toe S, thereby causing difficulty in precisely determining the nugget diameter and deciding whether or not a defect such as a crack or the like is present.

In Japanese Unexamined Patent Application Publication No. 2004-163210, the inventor of the present invention has already

CA 02579671 2007-02-28

- 5 proposed an ultrasonic method of evaluating a spot weld zone formed by welding a plurality of stacked metal sheets, in which a Lamb wave is excited in the metal sheets outside the spot weld zone toward a weld metal, and the Lamb wave is transmitted through the weld metal and then received after the transmission to evaluate soundness of the spot weld zone. In this method, evaluation of the spot weld zone was succeeded without being influenced by the inclined surfaces formed around the dimples formed in the spot weld zone. However, in Japanese Unexamined Patent Application Publication No. 2004-163210, it was found that a deviation of the positional relation between the two Lamb wave probes and the spot weld zone from a predetermined positional relation, which may happen in disposing two Lamb wave probes opposite to each other with the spot weld zone disposed therebetween, causes a deviation of the Lamb wave propagation path from the center of the spot weld zone, thereby failing to correctly evaluate the soundness of the spot weld zone. This problem significantly occurs when the relative positional relation between the Lamb wave probes and the spot weld zone cannot be sufficiently controlled because the measurement time is limited to a short time.

The Lamb wave is also referred to as a plate wave and is produced by oblique incidence of an ultrasonic wave onto a thin plate (a metal sheet or a non-metal sheet) at a specified angle of incidence. Obliquely traveling longitudinal and

CA 02579671 2007-02-28

- 6 transverse waves generated in a thin plate from oblique incidence refraction propagate and interfere with each other while repeating reflection followed by mode conversion at the front and back surfaces of the thin plate, thereby producing a traveling wave displaced symmetrically or asymmetrically with respect to the center of the thin plate in the thickness direction. This traveling wave is the Lamb wave (refer to Joseph L. Rose, Ultrasonic waves in solid media, pp. 101-126, Cambridge Univ. Press, Cambridge, 1999). A Lamb wave probe is an ultrasonic probe for making an ultrasonic wave incident on a thin plate at a specified angle of incidence in order to excite a Lamb wave in the thin plate. The Lamb wave probe can also be used for receiving Lamb waves.

It was further found that in evaluating the soundness of a spot weld zone using the method disclosed in Japanese Unexamined Patent Application Publication No. 2004-163210, the soundness of a spot weld zone cannot be precisely evaluated in some cases because the amplitude of a transmitted Lamb wave may be changed depanding on a change in the coupling condition between two Lamb wave probes and a metal sheet unless a method of detecting the amplitudes Ai and A₂ of transmitted Lamb waves at two frequencies f_x and f₂ (fi < f₂) shown in claim 3 of Japanese Unexamined Patent Application Publication No. 2004-163210 and determining the ratio (A₂/Ai) is used. This problem significantly occurs when the coupling condition between two Lamb wave probes and a metal

CA 02579671 2007-02-28

- Ί sheet cannot be sufficiently stabilized because the measurement time is limited to a short time. In order to use Lamb waves at two frequencies, it is necessary to arrange two piezoelectric elements in a line in a Lamb wave probe because of the need for the Lamb waves to have the same passage path. Therefore, a Lamb wave probe is inevitably increased in size, thereby causing the problem of difficulty in evaluating a spot weld zone in a narrow portion.

The present invention has been achieved for solving the problems of the prior art, and an object of the invention is to evaluate the soundness (the presence of a nugget, the nugget diameter, and weld cracking) of a spot weld zone with high reliability within a short measurement time (for example, 5 seconds or less per spot) without the influence of a deviation between the positions of an ultrasonic probe and the spot weld zone and a coupling condition between an ultrasonic probe and a metal sheet.

Disclosure of Invention

In order to achieve the object, the present invention provides an ultrasonic method for evaluating a spot weld zone formed by welding two or more stacked metal sheets, wherein provided that an ultrasonic wave propagating in a sectional plane which has one axis parallel to the surface of the metal sheets or the spot weld zone and has the other axis parallel to the

CA 02579671 2007-02-28

- 8 thickness direction is referred to as an ultrasonic wave propagating along the surface of a test object, ultrasonic waves propagating along the surface of a test object are transmitted in a plurality of directions from a plurality of wave sending positions outside the spot weld zone in the metal sheets, and ultrasonic waves propagating along the surface of the test object with propagation paths not including the spot weld zone and ultrasonic waves propagating along the surface of the test object with propagation paths including the spot weld zone are received at a plurality of wave receiving positions outside the spot weld zone to evaluate the soundness of the spot weld zone on the basis of the ultrasonic waves received at the plurality of wave receiving positions.

The amplitudes of the received ultrasonic waves (also referred to as the heights of transmitted waves) are detected to measure the diameter of a nugget of the spot weld zone.

In order to achieve the object, the present invention also provides an ultrasonic apparatus for evaluating a spot weld zone formed by welding two or more stacked metal sheets, wherein provided that an ultrasonic wave propagating in a sectional plane which has one axis parallel to the surface of the metal sheets or the spot weld zone and has the other axis parallel to the thickness direction is referred to as an ultrasonic wave propagating along the surface of a test object, the apparatus includes means for transmitting ultrasonic waves propagating

CA 02579671 2007-02-28

- 9 along the surface of a test object in a plurality of directions from a plurality of wave sending positions outside the spot weld zone in the metal sheets, means for receiving ultrasonic waves propagating along the surface of the test object with propagation paths not including the spot weld zone and ultrasonic waves propagating along the surface of the test object with propagation paths including the spot weld zone at a plurality of wave receiving positions outside the spot weld zone, and means for evaluating the soundness of the spot weld zone on the basis of the ultrasonic waves received at the plurality of wave receiving positions.

The amplitudes of the received ultrasonic waves are detected to measure the diameter of a nugget of the spot weld zone.

The apparatus further includes display means for displaying the amplitudes of the signals transmitted from the respective wave sending positions and received at the respective wave receiving positions in a two-dimensional matrix in which the wave sending positions are related to the respective wave receiving positions.

The positional relation between the spot weld zone and the means for transmitting ultrasonic waves and the means for receiving ultrasonic waves is aligned on the basis of the display results of the display means so that the influence of a positional deviation between an ultrasonic probe and the spot weld zone can be removed to permit the high-reliability evaluation of

CA 02579671 2007-02-28

- 10 soundness.

The amplification gains of signals of the received ultrasonic waves are controlled on the basis of the amplitudes of the ultrasonic waves propagating along the surface of the test object with the propagation paths not including the spot weld zone so that the influence of a coupling condition between ultrasonic probes and the metal sheets can be removed to permit the high-reliability evaluation of soundness.

The means for transmitting ultrasonic waves propagating along the surface of a test object in a plurality of directions from a plurality of wave sending positions includes an ultrasonic probe provided with a piezoelectric element array.

The means for receiving ultrasonic waves at a plurality of wave receiving positions includes an ultrasonic probe provided with a piezoelectric element array.

Furthermore, a flexibly deformable member is attached to the contact surface of the ultrasonic probe provided with the piezoelectric element array.

Brief Description of the Drawings

Fig. 1 is a perspective view showing a constitution according to an embodiment of the present invention.

Fig. 2 is a sectional view showing an ultrasonic wave propagation path, for explaining the principle of the present invention.

CA 02579671 2007-02-28

- 11 Fig. 3 is a plan view showing ultrasonic wave propagation paths, for explaining the principle of the present invention.

Fig. 4 is a sectional view showing a spot weld zone.

Fig. 5 is a diagram illustrating an example of a matrix display in which the relative position between ultrasonic probes and a spot weld zone is optimum.

Figs. 6A to 6D are drawings each illustrating an example of a matrix display in which the relative position between ultrasonic probes and a spot weld zone is deviated.

Fig. 7 is a perspective view including a block diagram showing an example of an apparatus for carrying out the present invention.

Fig. 8 is a graph showing an interpolation curve of amplitudes of received ultrasonic waves.

Fig. 9A and 9B are graphs showing comparison of accuracy between the measurement results obtained by a conventional method and a method of the present invention.

Fig. 10 is a sectional view for explaining a spot weld zone.

Fig. 11 is a perspective view including a block diagram showing another example of an apparatus for carrying out the present invention.

Fig. 12 is a plan view showing a constitution according to another embodiment of the present invention.

Fig. 13 is a sectional view showing the measurement of a curved surface through a flexible member.

CA 02579671 2007-02-28

- 12 Figs. 14A and 14B are diagrams showing a comparison between an example of a matrix display having a crack and a matrix display without a crack.

(Reference Numerals) la, 101a ... upper sheet lb, 101b ... lower sheet

2, 102 ... spot weld zone

2a, 102a ... nugget

2b ... weld solidified structure (weld metal)

10, 20 ... ultrasonic probe

11, 21 ... piezoelectric element array

12, 22 ... resin wedge

... silicone rubber

... ultrasonic probe for transmitting waves

... ultrasonic probe for receiving waves

25, 26 ... switching circuit

... ultrasonic pulser/receiver

31, 131 ... gating means

32, 132 ... peak detecting means

... processing unit

... display

111 ... ultrasonic transmitter

121 ... ultrasonic receiver

Best Mode for Carrying Out the Invention

CA 02579671 2007-02-28

- 13 An embodiment of the present invention will be described in detail below with reference to the drawings.

The evaluation of a spot weld zone formed by bonding two metal sheets will be described as an example. Of the two sheets, a sheet on the upper side is referred to as an upper sheet, and a sheet on the lower side is referred to as a lower sheet. In the present invention, as shown in Fig. 1, an ultrasonic probe 10 provided with a piezoelectric element array 11 and an ultrasonic probe 20 provided with a piezoelectric element array 21 are brought into contact with the upper sheet la to be opposed to each other with a spot weld zone 2 disposed therebetween. A proper coupling medium is interposed between the upper sheet la and each of the ultrasonic probes 10 and 20. For example, as the coupling medium, glycerin, glycerin paste, machine oil, alcohol, or water can be used.

In addition, ultrasonic waves are transmitted to the upper sheet la from a plurality of positions using the ultrasonic probe 10 provided with the piezoelectric element array 11. The ultrasonic probe 10 has a structure in which the piezoelectric element array 11 is attached to a resin wedge 12. Each of the ultrasonic waves transmitted from the piezoelectric element array 11 reach obliquely onto the upper sheet la. As shown in Fig. 2, as a result of the oblique incidence of an ultrasonic wave, an obliquely traveling ultrasonic wave with respect to the surface of the upper sheet la is transmitted in the upper sheet

CA 02579671 2007-02-28

- 14 la. The obliquely traveling ultrasonic wave includes a longitudinal wave and a transverse wave and propagates in the upper sheet la while repeating reflection accompanied by mode conversion at the bottom and at the surface of the upper sheet la. In Fig. 2, the transverse wave is shown by a solid line, and the longitudinal wave is shown by a broken line. When the angle of incidence of an ultrasonic wave on the upper sheet la is an appropriate value, an ultrasonic wave propagating while repeating the reflection becomes a wave called a Lamb wave. The propagating ultrasonic wave is received by the ultrasonic probe 20 provided with the piezoelectric element array 21. The ultrasonic probe 20 has a structure in which the piezoelectric element array 21 is attached to a resin wedge 22. As the resin wedges 12 and 22, a polystyrol (polystyrene) resin, an acrylic resin, or a polyimide resin can be used. When a polystyrol (polystyrene) resin and glycerin paste are used as the resin wedges 12 and 22 and the coupling medium, respectively, the influence of the surface roughness and curvature of the metal sheets on ultrasonic transmission between an ultrasonic probe and a test object can be minimized. Therefore, this combination is preferred.

Furthermore, gentle unevenness may be formed in the surface of a metal sheet around a spot weld zone of an automobile or the like. In this case, when a flexibly deformable member of rubber or the like is attached to the contact surface between each of

CA 02579671 2007-02-28

- 15 the ultrasonic probes 10 and 20 and the test object, coupling between each of the ultrasonic probes 10 and 20 and the metal sheet surface is easily stabilized, thereby causing a practical effect. As the flexibly deformable member, a soft member with an international rubber hardness IRHD of 30 or less based on ISO 48:1994 is preferred. Examples of such a member include silicone rubber, natural rubber, and ethylene-propylene rubber.

By using the ultrasonic probe 10 provided with the piezoelectric element array 11 and the ultrasonic probe 20 provided with the piezoelectric element array 21, ultrasonic waves propagating in the planar paths (paths in a top view of the metal sheets) shown in Fig. 3 can be received. The respective piezoelectric elements in the piezoelectric element array 11 of the ultrasonic probe 10 are represented by Hi to 11_N, and the respective piezoelectric elements in the piezoelectric element array 21 of the ultrasonic probe 20 are represented by 21i to 21_n. For example, N is 4 to 256. N may not be an even number and N of receiving piezoelectric elements need not be the same as N of sending piezoelectric elements . In Fig. 3, N is 8 . Since ultrasonic waves transmitted from the piezoelectric elements Hi to 11_N in the piezoelectric element array have spatial divergence (For example, assuming that the dimension of each piezoelectric element in the array direction is 1.5 mm, and the nominal frequency of each piezoelectric element is 5 MHz, the divergence of ultrasonic waves represented by a beam angle of divergence

CA 02579671 2007-02-28

- 16 between first zero pressure points is 24 to 45° in a plane parallel to the metal sheet surface. This value varies depending on the propagation mode of ultrasonic waves used in measurement.), ultrasonic waves can be transmitted along the planar paths shown in Fig. 3 from the probes Hi to 11_N.

The ultrasonic wave transmitted from the piezoelectric element lli of the ultrasonic probe 10 is received by the piezoelectric elements 21i to 21_N of the ultrasonic probe 20. Next, the ultrasonic wave transmitted from the piezoelectric element 11₂ of the ultrasonic probe 10 is received by the piezoelectric element 21χ to 21_N of the ultrasonic probe 20. This process is performed by sequentially changing the piezoelectric element ll_n (n = 1, 2, ..., N) for wave transmission until the ultrasonic waves transmitted from the piezoelectric element 11_Nof the ultrasonic probe 10 are received by the piezoelectric elements 21i to 21_N of the ultrasonic probe 20. As a result, ultrasonic waves transmitted from a plurality of positions and propagating in a plurality of directions can be received by the piezoelectric element 21i to 21_N of the ultrasonic probe 20.

As shown in Fig. 4, the nugget 2a formed in the spot weld zone 2 has a weld solidified structure 2b having directivity substantially parallel to the thickness direction (vertical to the rolling direction of the sheets). The weld solidified structure 2b corresponds to a weld metal of the present invention. In addition, the weld solidified structure 2b is referred to as

CA 02579671 2007-02-28

- 17 a dendrite structure, and includes a collection of coarse crystals extending in one direction. Therefore, the weld solidified structure 2b has a property of low transmission of ultrasonic waves (large attenuation) as compared with a metal structure of a steel sheet. Thus, ultrasonic waves propagating along the surface of the test object are attenuated depending on the length (also referred to as the nugget diameter) of the weld solidified structure 2b parallel to the sheet surface. As a result, when the paths of the ultrasonic waves include the weld solidified structure 2b, the ultrasonic waves propagating along the paths shown in Fig. 3 are attenuated according to the length of the weld solidified structure 2b present in the paths and then received by the ultrasonic probe 20.

Although, in the above description, the present invention is applied to a weld inspection of metal sheets, the application of the present invention is not limited to this. Also, the number of metal sheets to be welded is not limited to 2, and when the number is 3, 4, or 5, the same measurement as with the number of 2 can be performed.

The ultrasonic waves propagating along the surface of the test object used in the present invention may be any of Lamb waves (for example, Ao mode, So mode, AoSo mode, A2 mode, or S2 mode, for details, refer to Joseph L. Rose, Ultrasonic waves in solid media, pp. 101-126, Cambridge Univ. Press, Cambridge, 1999), longitudinal waves, transverse waves, or a mixture of

CA 02579671 2007-02-28

- 18 longitudinal and transverse waves.

When the whole width of each of the piezoelectric element array lli to 11_N and the piezoelectric element array 21i to 21_Nin the array direction is 1.1 to 2.0 times the maximum of the nugget diameter to be measured, the positional relation between the spot weld zone and the piezoelectric element arrays is controlled so that the spot weld zone is near the center of piezoelectric element array in the array direction. In this case, ultrasonic waves propagating along the surface of the test object with the propagation paths not including the spot weld zone and ultrasonic waves propagating along the surface of the test object with the propagation paths including the spot weld zone can be received.

Furthermore, by making the piezoelectric element size in the array direction smaller, the measurement accuracy can be increased. In this connection, the number N of the piezoelectric elements in the piezoelectric element arrays lli to 11_N and 21i to 21_N increases. The number of the piezoelectric elements in each of the piezoelectric element arrays lli to 11_N and 21i to 21_n in the array direction may be determined according to the required measurement accuracy. For example, the width of the probes need not be smaller than the required measurement accuracy. When a measurement accuracy of about ±0.5 mm is required, the width of the probes is 0.5 mm or more.

Fig. 5 shows a matrix display of the results obtained by

CA 02579671 2007-02-28

- 19 a process in which, by using an apparatus with the constitution shown in Fig. 7, the ultrasonic probes 10 and 20 opposed to each other with a spot weld zone 2 disposed therebetween are put into contact with a sample,prepared by spot welding two steel sheets having a thickness of 2.6 mm (welding conditions: passing a current of 5 kA and 15 Hz in frequency), and ultrasonic waves propagating along the 64 (=8x8) paths shown in Fig. 3 are received to detect the amplitudes thereof. The ultrasonic probe 10 includes the piezoelectric element array 11 attached to the resin wedge 12 made of a polystyrol resin, the piezoelectric element array 11 including piezoelectric elements with a width of 1.5 mm in the array direction, a length of 8 mm in the direction perpendicular to the array direction, and a elements spacing of 0.1 mm in the array direction. As the piezoelectric material, a piezo-composite element with a nominal frequency of 5 MHz is used. In addition, the inclined surface of the resin wedge 12 is formed so that the angle of incidence (angle of incidence 0° equals the normal direction to the sheet) is 34.7°. The specifications of the ultrasonic probe 20 are the same as the ultrasonic probe 10. In Fig. 5, the amplitudes of the ultrasonic waves in the 64 paths are shown by hatching in 5 shading steps (practically, representation using brightness modulation or representation using gray scale is used.), and a black portion shows that the received ultrasonic wave had a low amplitude. Furthermore, in Fig. 5, numerals 1 to 8 in the longitudinal

CA 02579671 2007-02-28

- 20 direction represent the respective piezoelectric elements Hi to llg of the piezoelectric element array of the ultrasonic probe 10 used for sending ultrasonic waves, and numerals 1 to 8 in the transverse direction represent the respective piezoelectric elements 21χ to 21g of the piezoelectric element array of the ultrasonic probe 20 used for receiving ultrasonic waves. In the matrix shown in Fig. 5, the amplitudes of received waves with the propagating paths including the weld solidified structure 2b are displayed along a diagonally right-up direction at 45°. Thereinafter, a black portion is referred to as an attenuation band. The width W (length in the diagonally right-down direction at 45°) of the attenuation band is proportional to the size of the weld solidified structure 2b, i.e., the nugget diameter, as viewed from a direction vertical to the sheet surface The example shown in Fig. 5 indicates that the positional relation between the ultrasonic probes 10 and 20 and the spot weld zone is optimum.

The method described above, in which the ultrasonic waves transmitted from a plurality of positions and propagating in a plurality of directions are received by the piezoelectric elements 21i to 21_N of the ultrasonic probe 20 and the amplitudes of the received ultrasonic waves are shown in the matrix display, has the following advantage: Figs. 6A and 6B each show the case in which the positional relation between the ultrasonic probes 10 and 20 and the spot weld zone 2 is deviated in the piezoelectric

CA 02579671 2007-02-28

- 21 element array direction (longitudinal direction of the drawing) , and Figs. 6C and 6D each show the case in which the positional relation between the ultrasonic probes 10 and 20 and the spot weld zone 2 is deviated in the direction (lateral direction of the drawing) perpendicular to the piezoelectric element array direction. In each of Figs. 6, planar paths of ultrasonic waves are shown by broken lines. As shown in Figs. 6A and 6B, when the positional relation between the ultrasonic probes 10 and 20 and the spot weld zone 2 is deviated in the array direction, the attenuation band is moved to the upper left (Fig. 6A) or the lower right (Fig. 6B) in the matrix display in comparison to Fig. 5. As shown in Figs. 6C and 6D, when the positional relation between the ultrasonic probes 10 and 20 and the spot weld zone 2 is deviated in the direction perpendicular to the piezoelectric element array direction, bright displays which show low attenuation of ultrasonic waves appear at the upper and lower ends (Fig. 6C) or the right and left ends (Fig. 6D) of the matrix display.

Therefore, whether or not the positional relation between the ultrasonic probes 10 and 20 and the spot weld zone 2 is deviated can be determined from the contents of the matrix display. On -the other hand, Fig. 5 shows the example in which the positional relation between the ultrasonic probes 10 and 20 and the spot weld zone 2 is optimum because the attenuation band clearly positions on a diagonal line of the matrix display.

According to the present invention, the positional

CA 02579671 2007-02-28

- 22 relation between the ultrasonic probes 10 and 20 and the spot weld zone 2 can be controlled by using the matrix display. Therefore, since the positional relation between the ultrasonic probes 10 and 20 and the spot weld zone 2 is always kept constant, the soundness (the presence of a nugget, nugget diameter, and the presence of weld cracks) of the spot weld zone can be evaluated with high reliability.

Furthermore, since ultrasonic waves transmitted from a plurality of positions using the piezoelectric element array Hi to 11_N of the ultrasonic probe 10 and propagating in a plurality of directions are received by the piezoelectric element array 211 to 21_n of the ultrasonic probe 20, ultrasonic waves propagating in the paths not containing the weld solidified structure 2b can be received. These ultrasonic waves are shown in white in the matrix displays of Figs. 5 and 6. By controlling the amplification gains so that the amplitudes of these ultrasonic waves get constant, changes in the amplitudes of the received ultrasonic waves caused by changes in the coupling condition between the ultrasonic probes 10 and 20 and the metal sheet (la) can be compensated. Therefore, according to the present invention, it is possible to remove the influence of changes in the coupling condition between the ultrasonic probes and the metal sheet on the amplitudes of the received ultrasonic waves, thereby permitting the soundness evaluation of a spot weld zone with high reliability.

CA 02579671 2007-02-28

- 23 Fig. 7 shows an example of an apparatus for carrying out the present invention. The apparatus includes the ultrasonic probe 10 provided with the piezoelectric element array lli to Ils used for transmitting ultrasonic waves, the ultrasonic probe 20 provided with the piezoelectric element array 21i to 21_a used for receiving ultrasonic waves, an ultrasonic pulser/receiver for supplying electric pulses used for transmitting ultrasonic waves from the piezoelectric elements of the piezoelectric element array lli to Ils and amplifying signals of the ultrasonic waves received by the piezoelectric element array 21χ to 21s, a switching circuit 25 interposed between the ultrasonic pulser/receiver 30 and the piezoelectric element array lli to Ils in order to switch the connections between the piezoelectric elements in the piezoelectric element array ll_x to Ils and the ultrasonic pulser/receiver 30, a switching circuit 26 interposed between the ultrasonic pulser/receiver 30 and the piezoelectric element array 21i to 21θ in order to switch the connections between the piezoelectric elements in the piezoelectric element array 211 to 21g and the ultrasonic pulser/receiver 30, gating means for extracting the signals of the ultrasonic waves propagating along the surface of the test object among the signals amplified by the ultrasonic pulser/receiver 30, peak detecting means 32 for detecting the amplitudes of the signals extracted by the gating means, and a processing unit 33 for receiving the amplitudes of the received ultrasonic waves detected by the peak

CA 02579671 2007-02-28

- 24 detecting means 32 to perform a matrix display of the amplitudes of the received ultrasonic waves in a display 34. The gating means 31 and the peak detecting means 32 may be substitued for a means with which the signals amplified by the ultrasonic pulser/receiver 30 are subjected to A/D conversion, and the amplitudes of the signals of the ultrasonic waves propagating along the surface of the test object are detected from the digital signals using a software.

Fig. 11 shows another example of an apparatus for carrying out the present invention. The apparatus includes the ultrasonic probe 10 provided with the piezoelectric element array Hi to llg used for transmitting ultrasonic waves, the ultrasonic probe 20 provided with the piezoelectric element array 21i to 21₈ used for receiving ultrasonic waves, ultrasonic pulsers Illi to 111₈for supplying electric pulses used for transmitting ultrasonic waves from the probes of the piezoelectric element array Hi to 11₈, ultrasonic receivers 121i to 121₈ for amplifying signals of the ultrasonic waves received by the piezoelectric element array 211 to 21₈, gating means 131i to 131₈ for extracting the signals of the ultrasonic waves propagating along the surface of the test object among the signals amplified by the ultrasonic receivers 1211 to 121s, peak detecting means 132i to 132₈ for detecting the amplitudes of the signals extracted by the gating means, and a processing unit 33 for receiving the amplitudes of the received ultrasonic waves detected by the peak detecting means 132i to

CA 02579671 2007-02-28

- 25 132g to perform a matrix display of the amplitudes of the received ultrasonic waves in a display 34. The gating means 131i to 131s and the peak detecting means 132i to 132₈ may be substitued for a means with which the signals amplified by the ultrasonic receivers 121i to 121g are subjected to A/D conversion, and the amplitudes of the signals of the ultrasonic waves propagating along the surface of the test object are detected from the digital signals using a software.

In this embodiment, ultrasonic probes each provided with a piezoelectric element array are used on both the sending side and the receiving side, and thus the configuration is simplified. However, a plurality of probes may be arranged in parallel on one or both of the sending side and the receiving side, or an ultrasonic probe 15 for transmitting waves and an ultrasonic probe 18 for receiving waves each including a single probe may be scanned opposite to each other as shown in Fig. 12.

Examples

A spot weld zone 2 was measured using the apparatus shown in Fig. 7 in which the wedge materials 12 and 22 of the ultrasonic probes 10 and 20 were made of polystyrol, the piezoelectric element arrays lli to lie and 21i and 21g each included piezo-composite elements having a nominal frequency of 5 MHz, a width of 1.5 mm in the array direction, a length of 8 mm in the direction perpendicular to the array direction, and a

CA 02579671 2007-02-28

- 26 elements spacing of 0.1 mm in the array direction, and the angle of incidence onto the surface of the upper sheet la was 34.7°. In addition, glycerin paste was interposed as a coupling medium between each of the ultrasonic probes 10 and 20 and the upper sheet la. As measurement objects, 30 samples each prepared by spot welding (welding condition: passing a current of 2 to 10 kA and 15Hz in frequency) of two steel sheets having a thickness of 2.6 mm were used. In this measurement, the relative position between the ultrasonic probes 10 and 20 and the spot weld zone 2 was controlled so that the centerline of the attenuation band coincided a right-up diagonal in a matrix display of the amplitudes of the received ultrasonic waves, as shown in Fig.

5. As shown in Fig. 8, in the measurement of the width W of the attenuation band, an amplitude profile (height of transmitted wave) of the received ultrasonic waves in the array direction was determined by interpolation using the amplitudes of the ultrasonic waves transmitted by the piezoelectric element lln of the piezoelectric element array and then received by the piezoelectric element 21n of the piezoelectric element array (n = 1, 2, ..., 8), and the width of a portion where the amplitude profile was lower than a predetermined threshold value was determined. The width W of the attenuation band was regarded as the nugget diameter. The threshold value was determined as follows : As a result of comparison between the amplitude profile and the results of microscopic observation of a sectioned surface

CA 02579671 2007-02-28

- 27 (referred to as a section test) using several samples, it was found that by setting the threshold value at about - 6 dB for the amplitudes of ultrasonic waves propagating along the surface of the test object in the propagation paths not including the spot weld zone, the nugget diameter determined by microscopic examination coincides with the nugget diameter determined according to the present invention. Therefore, the threshold value was determined to -6 dB. The threshold value (-6 dB) is an example, and practically, the threshold value is preferably determined on the basis of experimental values for each measurement object.

For the purpose of comparison to the prior art, measurement was performed using the above-described measurement method and the method disclosed in Japanese Unexamined Patent Application Publication No. 2004-163210 under the condition in which the measurement time was limited within 5 seconds after an ultrasonic probe (the Lamb wave probe disclosed in Japanese Unexamined Patent Application Publication No. 2004-163210 is also referred to as an ultrasonic probe ) was brought into contact with a sample In the measurement, as for the method disclosed in Japanese Unexamined Patent Application Publication No. 2004-163210, an ultrasonic probe having the specifications including a nominal frequency of 5 MHz, a probe size of 10 x 10 mm, a wedge material composed of an acrylic resin, and an angle of 65.9° of incidence onto a sample from a wedge was used. In Fig. 9B, the results

CA 02579671 2007-02-28

- 28 of measurement using the apparatus shown in Fig. Ί (according to the present invention) are shown by plots of . Fig. 9A shows the results of measurement by the method disclosed in Japanese Unexamined Patent Application Publication No. 2004-163210.

Each of Figs. 9A and 9B is a scatter graph in which the nugget diameters determined by a section test (also referred to as section microscopic examination in which an etched section is observed through a microscope) are shown as abscissa, and the nugget diameters determined by each of the methods are shown as ordinate. Plots of □ , Δ, A, and O in Fig. 9B will be described below. In the method disclosed in Japanese Unexamined Patent Application Publication No. 2004-163210, the nugget diameter is underestimated due to the fact that the ultrasonic probes cannot be aligned with the weld solidified structure within a short time, and the nugget diameter is overestimated due to the fact that the coupling condition between the ultrasonic probes and the sample is not sufficiently stabilized within a short time and the fact that there is no means for compensating a change in the coupling condition. On the other hand, as a result of measurement according to the present invention, all measured values fall in the range of ±0.5 mm, and it is thus found that measurement results with high reliability can be rapidly obtained. This is due to the fact that the alignment between the ultrasonic probes and the spot weld zone (weld solidified structure) can be easily performed by a matrix display of amplitudes of received

CA 02579671 2007-02-28

- 29 ultrasonic waves, and sensitivity is controlled so that the amplitudes of the received ultrasonic waves propagating along the paths not containing the weld solidified structure is constant, thereby compensating a change in amplitudes of the received ultrasonic waves with a change in the coupling condition between the ultrasonic probes and the metal sheet.

The nugget diameter can also be determined using the method disclosed in Japanese Unexamined Patent Application Publication No. 2004-163210 in which the ratios of the minimum amplitude of received ultrasonic waves to the amplitudes of received ultrasonic waves with the paths not containing the weld solidified structure are determined using the amplitude profile of received ultrasonic waves in the array direction shown in Fig.

8.

Fig. 13 is a sectional view showing the state in which the ultrasonic probe 10 with a contact surface to which a silicone rubber film of 0.5 mm in thickness is attached is pressed on a gently curved surface 5. The same silicone rubber is attached to the ultrasonic probe 20. These ultrasonic probes 10 and 20 were used for measuring a nugget diameter of a spot weld sample made by spot welding (welding conditions: passing a current of 4 to 8 kA and 15Hz in frequency) of two steel sheets having a thickness of 2.6 mm and a radius of curvature of 100 mm, and the measured nugget diameters were compared with the nugget diameters determined by the section test. The results are shown by □ plots

CA 02579671 2007-02-28

- 30 in Fig. 9B. Even for a spot weld zone of metal sheets with curvature, a nugget diameter can be correctly measured using the method and apparatus of the present invention.

In Fig. 9B, Δ plots show the results of comparison between the nugget diameters measured using the apparatus shown in Fig. 7 (according to the present invention) and the nugget diameters measured by the section test using samples formed as a measurement object by spot welding (welding conditions: passing a current of 10 kA and 26 Hz in frequency) of three steel sheets having thicknesses of 0.8 mm, 2.0 mm, and 2.6 mm. In Fig. 9B, A plots show the results of comparison between the nugget diameters measured using the apparatus shown in Fig. 7 (according to the present invention) and the nugget diameters measured by the section test using samples made as a measurement object by spot welding (welding conditions: passing a current of 11 kA and 24 Hz in frequency) of four steel sheets having thicknesses of 0.8 mm, 0.8 mm, 1.2 mm, and 2.3 mm. In Fig. 9B, O plots show the results of comparison between the nugget diameters measured using the apparatus shown in Fig. 7 (according to the present invention) and the nugget diameters measured by the section test using samples made as a measurement object by spot welding (welding conditions: passing a current of 12 kA and 22 Hz in frequency) of five steel sheets having thicknesses of 0.8 mm, 0.8 mm, 0.8 mm, 1.2 mm, and 1.6 mm. These results show that even when the number of metal sheets to be welded is 3 to 5, the nugget diameter

CA 02579671 2007-02-28

- 31 can be correctly measured using the method and apparatus of the present invention.

The evaluation of soundness of a spot welt zone is not limited to the measurement of only the nugget diameter. For example, Fig. 14A shows a matrix display in measurement of a spot weld zone with a weld crack using the apparatus shown in Fig. 7. For comparison, Fig. 14B shows a matrix display in measurement of a spot weld zone with no weld crack made under equivalent welding conditions. Since the density of the attenuation band or brightness in the pattern of a matrix display significantly changes asymmetrically with respect to a right-up diagonal due to the presence of a welding crack, a welding crack can be detected by observing a matrix display.

Industrial Applicability

According to the present invention, a spot weld zone can be precisely evaluated by a nondestructive method without being influenced by an inclined surface formed around a dimple formed in the spot weld zone. In addition, even in measurement in which the measurement time is limited to a short time, the soundness of a spot weld zone can be evaluated with high reliability without being influenced by a positional deviation between an ultrasonic probe and the spot weld zone and the coupling condition between an ultrasonic probe and a metal sheet.