Wound dressing

The present invention relates to wound dressings.

It is known from United Kingdom Patent Specifications

Nos. 1417962 and 1450201 to provide a wound dressing comprising a pad of polyurethane material one surface layer of which has been modified to render it hydrophilic and the remainder of which is hydrophobic. Such wound dressings are used by placing the pad over the wound with the hydrophilic surface of the pad in contact with the wound and then securing the pad in place by adhesive strapping or by bandaging thereover. It is also known from United States Patent No. 4730611 to provide a wound dressing comprising a foamed polyurethane as aforesaid positioned on a porous non-woven fibrous sheet of a larger selected size and having an adhesive on the side contacting the hydrophobic side of said pad so that the dressing presents the hydrophilic side and the adhesive for use in contact with a wound and the area surrounding the wound.

With wound dressings of the kind aforesaid it is desirable that the hydrophilic surface of the pad remain in close contact with the wound to remove exudates and to promote healing. With the known wound dressings this is difficult to achieve, particularly where the wound dressing is applied to an area subject to considerable movement such as an elbow joint or a knee joint, since conventional adhesive strapping and conventional

94024-64 SJD:jy bandaging either do not hold the pad in close contact with the wound over an extended period of time or can quickly work loose. The wound dressing comprising a polyurethane pad positioned on a porous non-woven fibrous sheet in accordance with the aforesaid United States patent has little elasticity and therefore does not readily conform for any extended period of time to difficult areas such as elbow joints and knee joints.

It is also desirable that a wound dressing should be impervious to water to enable a patient to bathe or shower without wetting or contaminating the wound but at the same time should be sufficiently porous to enable moisture to evaporate therethrough to maintain an environment under the dressing which will promote rapid healing of a wound. These requirements are not met by the known wound dressings.

The present invention therefore has as its object to provide a wound dressing which will overcome the limitations of the known wound dressings, which is highly -X conformable even to difficult areas of the body such as elbow joints or knee joints, which is water impermeable and which will allow moisture to evaporate therethrough.

A wound dressing comprising a pad of soft-polyurethane foam one surface layer of which is hydrophillic and a backing layer of which is hydrophobic and a sheet or strip of a soft conformable polyetherurethane foam having an adhesive on one surface thereof, the surface of said pad opposite said hydrophillic layer being secured to said sheet or strip by said adhesive and said sheet or strip overlapping said pad to enable said pad to be secured in position with said hydrophillic layer in contact with a wound by means of said adhesive, wherein the polyetherurethane foam is a predominantly closed cell foam having a pore size of 0.1 to 0.6 mm, such that the dressing is waterproof but water vapour permeable.

Said sheet or strip may overlap said pad on two opposite sides thereof although it is preferrred that the sheet or strip overlap said pad around the whole of the periphery thereof.

A release paper or film may be applied over said adhesive, said release paper or film being removable prior to application of the wound dressing over a wound.

Said pad may have a thickness from 3 to 10 mm, preferably from 4 to 6 mm.

94024-64 SJDzjy

Said pad may be compressed around the periphery. Preferably, the compressed region extends inwardly for 5 mm to 10 mm from the edge, suitably 6 mm to 8 mm from the edge.

Preferably, the periphery is compressed to have a thickness of from 0.1 mm to 1.0 mm, suitably from 0.2 mm to 0.6 mm.

Said sheet or strip may be formed from a high density polyetherurethane foam, preferably a predominantly closed cell blocked toluene di-isocyanate polyetherurethane foam. Said polyetherurethane foam may have a pore size of 0.1 to 0.6 mm. The sheet or strip may have an elongation of 200% to 300%, preferably 240% to 270%. The sheet or strip may have a thickness of 0.2 to 1.0 mm, preferably 0.4 to 0.8 mm.

The said adhesive is preferably an acrylic adhesive but may be any of the other adhesives approved for medical use.

If desired, said pad may comprise at or adjacent said opposite surface thereof a layer impregnated with activated carbon for adsorbing organic odours. Thus, said impregnated layer may comprise a layer of non-woven viscose fibres on to which activated carbon granules have been sprayed. Said impregnated layer may be sandwiched between said sheet or strip and the hydrophobic backing layer of the pad or between two layers of hydrophobic polyurethane foam. Dressings comprising

X

94024-64 SJDîjy

2017633 such an impregnated layer are useful when dressing wounds which give off an offensive odour as is the case, for example, with certain leg ulcers.

The wound dressing of the present invention may, in conventional manner, be sterile and be packaged in a sterile pack. For example said dressing and said pack may have been sterilised by gamma irradiation after packaging of the dressing in said pack.

The invention will be more particularly described with reference to the accompanying drawings, in which

Figure 1 is an isometric view of a wound dressing according to the present invention,

Figure 2 is a fragmentary sectional elevation on an enlarged scale of the wound dressing of Figure 1,

Figure 3 is a fragmentary sectional elevation on an enlarged scale of a modified wound dressing according to the present invention,

Figure 4 is a fragmentary sectional elevation of another modification of a wound dressing according to the invention, and

X

94024-64 SJD:jy

Figure 5 is a fragmentary sectional elevation of a further embodiment of a wound dressing according to the invention.

Referring to Figure 1 and 2 of the drawings it will be seen that the wound dressing illustrated therein comprises a pad 1 of soft polyurethane foam one surface layer 2 of which is hydrophilic and the remainder of which is hydrophobic and forms a backing layer 3 and a sheet or strip 4 of a soft conformable polyether foam having an adhesive 5 on one surface thereof, the surface of the hydrophobic layer 3 being secured to the sheet or strip 4 by said adhesive 5 and the sheet or strip 4 overlapping the pad 1 as shown at 6 to enable the pad 1 to be secured in position with the hydrophilic layer 2 in contact with a wound means of the adhesive 5. As will be seen from Figure 1, the sheet or strip 4 overlaps the pad 1 around the whole of the periphery thereof. A release paper or release film 7, indicated by broken lines in Figure 1, is applied over the adhesive 5 and

<td> over the</td><td> pad</td><td> 1 and is removable prior</td><td> to</td><td> application</td><td> of</td><td> the</td>

<td> dressing</td><td> over</td><td> a wound.</td><td></td><td></td><td></td><td></td>

<td></td><td> The</td><td> pad 1 has a thickness</td><td> of</td><td> from 3 to</td><td> 10</td><td> mm,</td>

<td colspan="2"> preferably 4</td><td> to 6 mm.</td><td></td><td></td><td></td><td></td>

<td></td><td colspan="3"> Referring to the embodiment shown</td><td> in Figure 5,</td><td> the</td><td> pad</td>

is preferably compressed around its periphery. The compressed region 9 may extend inwardly for 5 mm to 10 mm from the edge,

X

94024-64 SJD:jy suitably 6 mm to 8 mm from the edge. Preferably, the periphery is compressed to have a thickness of from 0.1 to 1.0 mm, suitably from 0.2 to 0.6 mm.

Compressing the periphery of the pad 1 increases the effective border width without increasing overall dimensions or reducing the pad 1 area, to enable a more secure fixation of the wound dressing on the patient. Further, the release papers 7 thereby sits flat across the full width of the adhesive surfaces.

The compression of the periphery of the pad 1 is achieved prior to assembly of the wound dressing. The pad 1 is placed, with the hydrophilic surface layer 2 uppermost, centrally onto a forming tray with a cut out 14 mm smaller in all dimensions. The forming.tray and wound dressing are then placed onto the lower, unheated, platen of a heat press. The lower 2 platen is raised at a pressure in the range of 50 to 5000N/m , 2 preferably 500 to 1500N/m , against the upper platen which is heated to a temperature of 140°C to 250°C, preferably 180°C to 200°C. After a period of time, preferably between 10 seconds and 90 seconds - suitably about 20 seconds - the pressure is released and the bottom platen lowered. The wound dressing so produced will have a periphery reduced in thickness.

The sheet or strip 4 in either embodiment is formed from a high density predominantly closed cell blocked toluene di-isocyanate polyetherurethane foam.

Preferably, the

94024-64 SJD;jy polyetherurethane foam from which the sheet or strip 4 is formed has a pore size of 0.1 to 0.6 mm and an elongation of 200% to 300%, preferably to 240% to 270%. The sheet or strip 4 may have a thickness of from 0.2 to 1.0 mm, preferably from 0.4 to 0.8 mm. The corners of the sheet or strip 4 are preferably rounded, to prevent them from lifting up when the wound dressing is in use.

The adhesive 5 is an acrylic adhesive although other adhesives approved for medical use may be used if desired.

The wound dressing illustrated in Figures 1 and 2 is highly conformable to different parts of the body, even to difficult parts such as elbow joints or knee joints, is waterproof so that a patient wearing the dressing can bathe or shower without danger of wetting or contaminating a wound and

<td> is sufficiently therethrough.</td><td> porous to</td><td> enable</td><td> moisture to</td><td> evaporate</td>

<td> As shown</td><td> in Figures</td><td> 3 and 4,</td><td> in which like</td><td> parts have</td>

<td> been given like</td><td> reference</td><td> numerals,</td><td> the pad 1</td><td> in either</td>

embodiment may include a layer 8 of non-woven fibres, e.g., viscose fibres, impregnated with granules of activated carbon. Thus, as shown in Figure 3, the layer 8 may be provided between the hydrophobic layer 3 and the layer of adhesive 5 or, as shown in Figure 4, the layer 8 may be sandwiched between hydrophobic layers 3a, 3b of the pad 1. A dressing incorporating the layer 8 is particularly useful for dressing wounds which give off an

X

2017633

94024-64 SJD:jy offensive odour, as is the case, for example, with certain leg ulcers and other wounds.