;~QllO~ - 1 SOLDER ASSEMBLY OF COMPONENTS Back~round of the Invention This invention relates to solder assembly of components.

Soldering of components is often a critical operation in the fabrication 5 of circuits and devices since failure to form an effective solder joint can result in costly yield and reliability problems.

These problems are especially prevalent when an area array of solder joints is needed.

For example, in certain high performance connectors, a flexible printed circuit may be used to electrically connect a contact element to a rigid printed circuit board.

For high density applications, the flexible 10 circuit might preferably termin~te in an area array which must be electrically coupled to corresponding terrninations on the printed circuit board.

One technique for attachment involves the use of conductive pins inserted in holes formed in the corresponding terminations in the flexible circuit and circuit board. (See, for example, U.S.

Patent 4,806,107.) It would be more desirable to solder the flexible 15 circuit directly to the circuit board since that would provide for improved electrical performance of the circuits and elimin~te the need for extra piece parts.

Solder assembly of a flexible circuit to a rigid printed circuit board is typically done by solder plating the ends of the conductive lines on the flexible circuit and on the circuit board, and then using a hot ram to reflow the plating and 20 form a linear arrangement of solder joints between corresponding lines. A major problem is that solder joint formation is often not reliable, and many mis-formed joints would not be detectable until the final testing of the device since such joints would be hidden under the component.

It is, therefore, an object of the invention to provide a method of 25 soldering which results in readily inspectable and repairable solder joints.

Another concern in soldering of components is to provide just the right amount of solder to the pad arrays for forming an effective solder joint.

Inadequate amount of solder can lead to problems in forming reliable solder joints with high yield, and excessive solder can result in formation of solder bridges between 30 adjacent conducting elements and hence the need for repair.

Plating often does not deposit an adequate solder volume dependably.

Solder dipping is a possible approach to providing an enhanced solder coating on components, but the lack of control of solder volume leads to lack of control over the assembly process which produces assembly yield problems.

Another approach, which is often used for 35 surface mounted components, is to deposit the solder in the form of a paste through 2Q~10~)0 - 2 a~ Lules in a stencil.

Control of the deposited solder in such cases can become a problem depending on the ratio of the apel~ule width and thickness of the stencil.

This is because solder paste can cling to the stencil rather than deposit on the circuit board, and tacky deposits can build up on the walls of the a~ UlCS and in~elr~,lc S with solder deposition.

It is, therefore, a further object of the invention to provide a method and apparatus for depositing a well-controlled amount of solder in a desired location.

Summary of the Invention These and other objects are achieved in accordance with the invention 10 which, in one aspect, is a method for attaching a first component to a secondcomponent.

Metalized holes are provided in the pad areas of the first component to be attached to corresponding pad areas of the second component. A controlled amount of solder is deposited on the corresponding pad areas of the second component.

The first component is brought into contact with the solder on the 15 second component so that the holes are aligned with the corresponding pad areas.

The components are heated to melt the solder and to cause the solder to form fillets extending through the holes so that the fillets may be observed.

In accordance with a further aspect, the invention is a device comprising first and second components with pad areas on facing surfaces which are soldered20 together.

At least one of the components includes metalized holes in the pad areas which are soldered.

Solder fillets are formed between pad areas on the facing surfaces and extend through the holes to associated pad areas on the surface of said one component opposite to the facing surface so that the fillet can be inspected.

Brief Description of the Drawing These and other features of the invention are delineated in detail in the following description.

In the drawing:

FIG. 1 is a perspective view of portions of components which can be assembled in accordance with an embodiment of the invention;

FIG. 2 is a cross-sectional schematic view of apparatus for assembling 30 components in accordance with an embodiment of the invention;

FIGS. 3-5 are schematic illustrations of various stages of processing in accordance with the same embodiment;

FIG. 6 is a schematic illustration of the apparatus of FIG. 2 during a later stage in processing;

2Q~10~0 - 3 FIGS. 7-9 are cross-sectional schem~ti~ views of further stages of fabrication in accordance with the same embodiment; and FIG. 10 is a cross-sectional view of a portion of the assembled components in accordance with the same embodiment.

It will be appreciated that, for purposes of illustration, these figures are not necessarily drawn to scale.

Detailed Description FIG. 1 illustrates two components which can be bonded in accordance with the invention.

Component, 10, is a flexible printed circuit which is typically 10 made of a dielectric material such as polyimide and includes a plurality of conductive paths, 11, typically comprising copper.

Only three such paths are shown for illustrative purposes.

Each path terminates in an exterior conductive pad area, such as 12, which includes a metalized hole, 13, formed therethrough to connect to a corresponding interior pad area (as shown in FIG. 10).

The pads and holes form an 15 area array in the flexible circuit as indicated in FIG. 1.

Each such metallized hole and associated pad is to be bonded to a corresponding conductive pad area, such as 15, formed on the second component, 14, which is a standard printed circuit board.

The board is typically made of an epoxy-glass material and the conductive pads are typically copper.

The printed circuit board also usually includes a solder mask 20 material, which is shown as 16 in FIGS. 2-10, but is not shown in FIG. 1 for the sake of clarity.

This solder mask material covers essentially the entire printed circuit board except for the pads which will be soldered.

Similarly, the flexible circuit, 10, includes a cover layer which is shown as layers 17 and 18 in FIG. 10, on both surfaces of the circuit, but which is also not shown in FIG. 1 for clarity.

The solder 25 mask and cover layer act to provide control of the solder wettable areas of the two components.

The flexible circuit is typically approximately 0.2 mm thick, the paths are typically 0.2 mm wide and .05 mm thick; the conductive pad areas are usually0.8 mm in diameter, and the holes, 13, are typically .5 mm in diameter.

The printed 30 circuit board, 14, is usually 1.5 mm thick, with the pads, 15, measuring approximately 0.8 mm in diameter and a~?pl..xi~ tely .05 mm thick.

Of course, it will be appreciated that other types of components can be assembled according to the techniques described herein.

In order to bond the flexible circuit to the printed circuit board, precise 35 and predetermined amounts of solder should first be deposited on each printed circuit board pad, 15.

One method for accomplishing this is to individually deposit solder 2Q~l10~O spheres on each pad and heat the assembly in order to melt the solder and cause the spheres to adhere to each pad.

Such a process can be tedious and error prone, however.

Instead, in accordance with a feature of the invention, an element referred to as a shuttle element and illustrated as 20 in FIG. 2 was devised.

The shuttle5 element is made of a material such as molybdenum steel, lilaniulll, or aluminum which is not wettable by solder, but which is rea~on~hly conductive of heat and which is compatible with high temperatures and cl~ning operations.

The shuttle element also includes an array of cavities such as 21 in at least one major surface of the element.

The array of cavities matches the array of pads on the printed circuit 10 board.

The element can simply be a thin sheet of material with holes drilled therethrough and covered on one surface by a backing tape.

Such a construction is plerellt;d since the tape can be removed and the holes cleaned more easily.

In this example, the cavities were 1 mm in diameter, .2 mm deep, and filled with approximately 0.1 mm3 of solder paste.

The solder paste can be deposited in the 15 cavities by depositing the paste on the surface and then using a squeegee to smear the paste into the cavities.

After the cavities are filled with solder paste and dried, the shuttle, 20, is aligned with the printed circuit board, 14, as illustrated in FIG. 2 so that each cavity is above its corresponding pad.

Alignment can be effectuated with standard tooling 20 pins (not shown).

The solder will remain in the cavities due to its tacky consistency at room temperature.

The aligned shuttle and printed circuit board are positioned under a soldering head which comprises a hot ram, 22, and a spring-loaded holddown element, 23.

The hot ram includes a heater element, 24, to produce the desired ~em~eld~ule at the soldering surface.

The hot ram is typically formed from a block 25 of copper plated with nickel and the heater element is a conventional electrically resistive element.

The hold-down element, which is typically molybdenum steel acts as an interface between the hot ram and the soldering surface, as well as providing some pressure to hold the stencil, and, later, the flexible circuit, to the printed circuit board.

The apparatus further includes a cooling system to cool the surface of the 30 assembly after reflowing of the solder to below the melting point of the solder.

Cool air is supplied through nozzle, 40, so that air is directed to the surface of hold-down, 23.

The hot ram solder apparatus can be any coll~ ;ially available machine.

In the operation of the apparatus of FIG. 2, the soldering head is lowered until the hold-down, 23, makes contact with the shuttle, 20, as shown in FIG. 3.

The 35 hold-down is warmed by the hot ram to a temperature of about 100 degrees C.

Asufficient amount of heat, therefore, is transferred to the shuttle to warm the solder o~o - 5 paste and activate the flux in the paste.

The soldering head is further lowered until the hot ram, which is m~int~ined at 360 degrees C, makes physical contact with the hold-down as shown in FIG. 4.

This causes sufficient heat to be transferred to the hold-down/shuttle/circuit board assembly to cause the solder in the shuttle cavities to S reflow and wet the pads on the circuit board.

The hot ram is then moved upward out of contact with the hold-down, but the hold-down still applies pressure to the shuttle in the manner previously shown in FIG. 3.

At this point, air from nozzle, 40, isblown over the hold-down to cool the assembly and solidify the solder joints to the circuit board pads.

The soldering head and shuttle are then fully removed from the 10 printed circuit board.

This operation leaves unifo~ solder deposits such as 30 on all the circuit board pads as shown in FIG. 5.

The deposition and reflow operation usually takes approximately 30 seconds.

At this point, the solder fillets on the pads of the printed circuit board can be inspected to ensure good solder wetting and proper solder volume.

It is 15 generally desirable at this point that the solder wet the entire pad and project sufficiently above the plane of the solder mask to ensure a proper fillet in subsequent operations.

The printed circuit board, 14, is now ready to receive the flexible circuit, 10, for soldering thereto.

The flexible circuit is usually prepared by applying flux to 20 all of the holes, 13, and then drying to remove the volatiles in the flux. FM. 6 illustrates the placement of the flexible circuit, 10, in the appaldLus of FM. 2 for soldering to the printed circuit board, 14.

The flexible circuit is aligned with the board, again, by the use of standard tooling pins (not shown), so that the holes, such as 13, are positioned above and aligned with corresponding pads, such as 15, on the 25 board. A shuttle element, 20, can be used for this portion of the operation as a cover plate, with the cavities, 21, empty and aligned with their corresponding holes, 13, and pads, 15.

Use of relief in the cover plate allows the solder to flow up through the holes and out onto the exterior pad, 12, to form a rounded fillet with a free surface so as to permit the quality of the fillet to be inspected.

As before, the hold-down, 23, 30 contacts the shuttle to hold it (and the flexible circuit) in place while also preheating the solder surface (FIG. 7).

Note at this point the plated through holes, 13, just make contact with the solder deposits such as 30.

The hot ram, 22, is then pushed against the hold-down, 23, to heat the shuttle/flexible circuit/printed circuit board assembly.

This causes the previously-deposited solder to melt and flow up through the plated35 through holes, 13, and cover the pads, 12, forming fillet, 31, as well as closing thegap between the circuit, 10, and the layer, 16, on the circuit board, 14 (FIG. 8).

The hot ram is then removed leaving the hold-down in position to hold the shuttle and flexible circuit in place while the solder cools.

Air is blown over the surface of the hold-down to cool and solidify the solder joints as shown in FIG. 9.

The cover plate (shuttle) is then removed leaving a completed assembly.

S One of the solder joints formed in accordance with the invention is illustrated in the cross-sectional view of FIG. 10.

This figure shows in more detail the portion of the flexible circuit 10, including its cover layers, 17 and 18, and ground plane, 50, bonded to a pad, 15, on the printed circuit board.

As a result of choosing the appropliate amount of solder for each pad, the solder joint extends10 through the hole, 13, to the surface of the flexible circuit opposite to the surface which faces the printed circuit.

The penetration of the solder through the hole is sufficient to form a fillet, 31, on the conductive portion, 12, on the opposite surface.

Consequently, a simple visual inspection from above the assembly will verify which, if any, solder joints are defective and need repair.

It will also be realized that the 15 cover layers, 17 and 18, and solder mask, 16, also serve as solder dams to prevent solder from bridging to adjacent pads.

In order to carry out the solder assembly process with high yields and consistently produce reliable solder joints, it is preferable to observe severalimportant design constraints.

These "design-for-manufacturability" guidelines can 20 be stated in terms of a set of dimensional relationships which should be observed in the design of certain elements of the circuits which are to be joined.

For example, it is beneficial for the diameter of the hole in the flex circuit to be as small as is economically manufacturable and for the size (diameter) of the wettable pad areas on the flex circuit and the rigid circuit board to be a ,~ini,."l,~ of 2 times larger than the 25 diameter of the hole in the flex circuit.

Further, it is beneficial for the nominal separation of the associated pad areas on the flex circuit and printed wiring board after joint formation to be quite small (on the order of one tenth or less of the diameter of the pads).

These objectives together assure that the volume of solder selected to form the joint can meet the conditions that the solder fillet initially 30 formed on the pad of the rigid printed board completely spans that pad and forms a wetting angle which is indicative of the wettability of the printed circuit board pad, and that the solder fillet initially formed on the printed circuit pad has sufficient projection above any surrounding soldermask on the printed circuit board to facilitate good thermal contact and wetting to the associated pad and hole of the flex 35 circuit to which it is to be solder assembled during the solder reflow operation.

These dimensional relationships also ensure that there is sufficient solder volume in - 2Qll~O - 7 the final joint to completely occupy the total of the volume of space between the associated pads which are joined, the volume of the hole in the flex, and the volume of fillet spanning the exterior pad area so that the fillet forms a wetting angle to this exterior pad which is indicative of the wetting of the exterior pad and the quality of 5 the joint.

It is further beneficial that the aperture (opening) in the solder mask m:~teri~l and the cover layer m~teri~l surrounding the interior flex circuit pad and the printed circuit board pad be sufficiently large compared to the si~ of pads theysurround (typically 50% or more larger) to leave a free volume which is sufficiently large to accommodate any residual flux materials which are left upon completion of 10 the assembly process.

It will be appreciated that the inventive method can be applied simlllt~neously to two sides of the printed circuit board by also providing a shuttle, hold-down and hot ram on the underside of the board.

The solder llnll~rnP~th theboard will wet the pads as a result of the surface tension which causes the co~l~sce~l 15 solder from the paste to tend to form a sphere which protrudes from the shuttle cavities when the solder is melted.

Further, while the invention is most advantageous for bonding flexible circuits to printed circuit boards as described, it may be applied wherever it is desired to solder two components, especially when one component is flexible and the other is rigid.

It will also be appreciated that the 20 shuttle elements can be supplied on reels so that successive elements can be aligned with respective boards in an automated fashion.

Various additional modifications will become apparent to those skilled in the art.

All such variations which basically rely on the teachings through which the invention has advanced the art are ~lupt;lly considered within the scope of the 25 invention.