Method for reproducing paintings and the like

1308353 ! BACKGROUND OF THE INVENTION

1. Field Of The Invention

This invention relates generally to a new and · improved process for reproducing an original painting or the like, and more particularly, to an improved process for reproducing an oil or acrylic painting or the like, from the original artwork to produce a reproduction which has a relief surface and texture to it which is identical to the relief surface and texture of the original artwork and which maintains good colour integrity.

2. Description Of The Prior Art

Various methods have been prepared to copy or reproduce an oil or acrylic painting or the like, in order to produce a copy which is the same as or similar to the original.

Such copies generally fall within two categories. The first category includes copies of the

2Q artwork which lack surface texture or relief dimensions of the original. The second category includes copies which attempt to copy the relief dimensions or surface texture of the original artwork. It is to the second category to which this invention is directed.

*

<img file="CA1306353C_D0001.tif" />

' The first category includes such copies broadly classified as artistic polychrome prints, photographs and the like and while these may ba produced quite inexpensively, and while they exhibit good colour integrity, they lack the relief dimensions or surface texture of the original and thus are not as acceptable as would be a reproduction which duplicated faithfully the surface texture of the original.

The second category has in fact met with limited success although the quality of these copies in reproductions has not been high. The process for producing such copies generally involve the production of a type of plastic transparent layer which is given texture by using a mold made from an original painting (see patents DE-PS 494,894? FR-PS NO 1,521,466? DE-AS NO 2,019,699 and DE-OS NO 2,352,966).

With these processes, problems arose with colour fidelity and the effects created by the transparent relief layer. Attempts have been made to overcome these problems as shown in French patent 1,493,516? French patent .1,548,337 and Canadian patent 990,506 granted on June 8, 1976 to Dimension Weld Int. Corp, which shows the use of a thermoplastic transparent sheet.

More recently, a process was disclosed in U.S. patent 4,308,224 which issued on December 29, 1981 and which was developed to produce such reproductions of reasonable price and of acceptable fidelity.

This patent discloses a process which uses a relief’ mold taken from the original and a thermoplastic foil imprinted with the colour picture corresponding to the original. The foil, while being heated, was placed with its imprinted side down on the relief mold and a textile layer placed over the foil.

The combination was then heated causing the flowable component of the textile layer to flow into the relief surface of the mold, thus duplicating the texture of the original painting.

However, this process only partially duplicated the relief dimensions of the original artwork and also, after standing, the texture tended to reduce.

SUMMARY OF THE INVENTION

Accordingly, it is an object of the present invention to at least partially overcome these disadvantages by providing an improved process for reproducing, paintings and the like which-reproduces the artwork in colour integrity, relief surface and texture, and is quite cost effective.

It is a further object of his invention to provide an improved process for producing an reproduction of an painting and the like, which reproduction has a relief surface and texture faithful to the original artwork.

A further object of the invention is to provide a process for producing a reproduction of a painting and the like which produces good quality reproductions of consistent quality and which is susceptible to industrial application.

To this end, in one of its aspects, the invention provides a method for producing a reproduction of a painting or the· like, said reproduction having a relief surface imitating the relief surface of said painting or the like, said process comprising the steps of applying heat and pressure to an assembly consisting of a mold of said oil painting or the like, a coloured sheet for colouring said reproduction, a substrate to retain said reproduction, and then cooling said assembly.

BRIEF DESCRIPTION OF THE DRAWINGS

FIGURE 1 is a schematic drawing of the assembly used in the process of the present invention.

FIGURE 2 is a schematic drawing of an alternate assembly used in the process of the present invention.

FIGURE 3 is a sectional view of the reproduction and mold subsequent to the application of heat and pressure thereto.

DESCRIPTION OF THE PREFERRED EMBODIMENT

The first step of the process of the present invention is to make a suitable mold or negative from the original painting or the like. The mold is generally made of silicone rubber and is quite hard and acts as a negative for the production of the reproductions at a subsequent stage.

The mold may be made by any well known process. One example is as follows. Molten mold material is poured over an original painting and then allowed to set or harden and dry for about 48 hours. Since the mold is made from the original painting, it will retain all the surface texture of the original artwork to impart such surface texture to subsequently produced reproductions.

The mold may also be made of any suitable material. A preferred material is a two component RTV silicone rubber which uses silicone rubber as the base, and dibutyl tin dilaurate (DBT) as the catalyst. This material exhibits a viscosity of about 50,000 cps and has a specific gravity of about 1.47. Its hardness on the standard durometer of about 60 and a tensile strength of about 56/800 kg/cm^ allows it to withstand the pressures applied in the process. The material has an elongated percentage of about 130, a tear resistance of 7 to 140 kg/cm with a demonstrated wear shrinkage of about 0.2 to about 0.6. This provides good dimensional stability following multiple uses.

Colour separations are then prepared from the original painting using any well known method such as the Alexander method. A photograph of the painting is taken and a coloured positive transparently produced. The colour separation (using a four colour or a six colour or more, if required separation) is prepared using an offset process and then printed on a PVC coated sheet of about 300 microns in thickness.

Colour separations using a process camera, may also be made directly from the original artwork, without making a transparency, slide or the like. Basically, the original artwork is photographed using three filters, each of which lets through a preselected portion of light which is reflected from the image.

The red filter is used for cyan printing; the magenta filter is used for green printing; and the blue filter is used for yellow painting. Black is the fourth colour and is used to make the greys and shadows neutral. The separations off the camera are continuous tones and a half tone screen is used to print the image. Any corrections are made to the filter by reducing the size of the dots with chemicals (referred to as dot etching) and after the etching process is complete, cromalins and press proofs are made.

Referring now to figure 1, there is shown a schematic representative of the method of producing the reproductions, by the preferred embodiment.

A hydraulic press generally indicated as 22 is used to produce the actual reproductions. The press 22 basically comprises a table 4, a heating plate 14 and a cooling plate 18 (shown in phantom lines).

The press is capable of applying heat to the assembly by moving the heating plate 14 via pistons 16 affixed to housing 20, or could alternately, (as shown in figure 2), move table 4 upwardly to contact stationary heating plate 14. Heating plate 14 and cooling plate 18 are capable of moving laterally into or out of position to contact the assembly.

Preferably, a soft silicone mat 2 is placed over table 4. While not necessary, it is advisable as the soft silicone mat 2 will tend to equalize the applied pressure to produce a better quality product.

Mold 6 is then placed on top o£ the mat 2 with the relief side 8 of mold 6 in the up position.

The printed PVC coated sheet 10 which has been printed with the applicable colour separations as explained hereinbefore, is placed on the top of the relief side 8 of mold 6, in perfect registration which is of course essential in any reproductive process.

Sheet 10 may be of any suitable material and PVC is preferred. It is preferably from about 2 to about 300 microns in thickness. One particularly useful material is KLOCKNEL (trade mark) PR 278/09 0/200 which has a matte 4/3 of 12 gauge and is a rigid highly impact modified PVC/PVAC copolymer.

The inks used to colour the sheet 10 may be any well known type but should be of high quality. Preferred inks are those demonstrating high scuff resistance and these designed to run on offset lithographic presses allowing an open time on the press of about 45 minutes and a drying time on the substrate of about 24 to about 36 hours. In addition to the four process colours (cyan, magenta, yellow and black), special colours may be mixed as required. The inks must be heat resistant to prevent damage during the pressing operation and should be of the fast drying type.

1306333

A piece of canvas 12 to be used as the substrate for the reproduction is then placed on top of the sheet 10. It is preferred that the canvas be coated with a flexible PVC laminate with a cotton sheeting on the back. A suitable formulation of a canvas is about 23.0 oz/sq.yd. of total weight with about 16.0 oz/sq.yd. of vinyl coating and a fabric back of about 5.4 oz/sq.yd.

Once the assembly has been completed, heat and pressure are applied to the assembly by using the heat plate 14. It is possible to accomplish this by two different means. First, heat plate 14 can be moved downwardly by the action of pistons 16 in housing 20 to apply heat and pressure to the assembly and in this embodiment, table 4 is stationary. An alternative embodiment is for table 4 to rise up and compress the assembly between movable table 4 and stationary heat plate 14.

Heat is applied by heat plate 14 which applies heat to the top of the assembly, that is, the canvas at a temperature of from about 160°C to about 175°C. When these temperatures are applied, it has been found that the temperature of the sheet 10 reaches.

about 130°C.

<img file="CA1306353C_D0002.tif" />

It has been found that heat alone is not sufficient to produce the quality reproductions. Pressure must also be applied simultaneously with the heat and depending upon, the size and type of picture, the pressure will be from about 10 to about 90 tons per square inch. For the average size picture, application of heat and pressure for about 60 to about 180 seconds is sufficient.

Upon the application of heat and pressure, the sheet 10 melts as well as the PVC on the canvas substrate 12. The texture of the mold 6. is then imparted directly to the sheet and canvas which are now bonded and fused together. This type of lamination effectively transfers the relief surface of the mold to the reproduction as shown in figure 3.

Specifically, when heat is applied, the PVC coated sheet 10 and the PVC on the canvas substrate 12 become soft and flexible. As the pressure is applied, the backside of the PVC coated sheet 10 and the PVC on the canvas 12 are welded together and the thus bonded PVC coated sheet and canvas (as shown in figure 3) is pressed against the negative relief side of the mold 6. The PVC material covers and fills the negative hollows in the mold 6 which duplicate the surface texture and brush strokes of the original artwork.

-1306353 j The heat plate 14 is then removed from contact with the canvas 12. This is done by either moving the heat plate 14 upwardly away from canvas 12 by retracting piston 16 or by lowering the table 4.

The heat plate 14 is then moved laterally away and cooling plate 18 (shown in dotted lines) is moved into the same position occupied previously by heat plate

14. Cooling plate 18 is then brought into contact with the assembly either by moving the pistons 16 downwardly or raising table 4 upwardly. It moves in exactly the same manner as heat plate 14.

The assembly is then subjected to cooling by contact with the cooling plate 18 at about 0°C for about 30 to about 75 seconds. Subsequent to such ₁₅ contact, cooling plate 18 is moved away and the reproduction is removed and the mold is then cooled and is ready to be used again.

It has been found that the cooling step is an essential feature of the invention. If the assembly is

2q not subjected to a cooling step, the texture imparted to the reproduction, that is, the surface dimensions on the canvas, tend to be lost. The reproduction will go flat due to the rebound effect or the memory effect of the materials. By applying a deliberate cooling step, oh to shock the reproduction, such rebound has been effectively elminated and the surface texture remains permanently.

This cooling or shocking step is different than that disclosed in U.S. patent 4,308,224 as explained hereinafter. It has been found that by shocking the reproduction by cooling, the rebound effect or memory of the base material is not seen thus allowing for a reproduction which comes closed to duplicating the original artwork.

In order to demonstrate the improvements of the present process over the prior art, a comparison, study was made between a reproduction made in accordance with the process of U.S. patent 4,308,224 and the present process. The following parameters were applied.

STEPS PROCESS OP O.S. PATENT NEW PROCESS

4,308,224

1. Machine Temperature

2. Temperature Of Mold

3. Processing Time For Heat Plate

169°C-172°C

130°C-133°C sec.

169°C-172°C

13Q°C-133°C

180 sec.

Processing Time For Cooling Plate

5. Processing Temperature For none none sec.

-5°C

<td> 1</td><td> Cooling Plate</td><td></td>

<td></td><td> 6. Processing Pressure and Heat Plate</td><td> 30 tons</td>

<td> 5</td><td> 7. Processing Pressure and Cooling Plate</td><td> none</td>

tons tons

The texture height in the reproduction made in accordance with U.S. patent 4,308,224 including the height of the material measured 0.050 inches whereas thé texture height of the reproduction of the present process including the height of the material measured 0.075 inches. The texture height of the prior art reproduction not including the material measured 0.025 inches whenever the texture height of the reproduction of the present process without the material measured

0.050 inches. It is clear from the results that the present process produces a reproduction having about a 66-67% improvement in the texture height than in the prior art.

2o While the invention describes and illustrates a preferred embodiment of the invention, it is to be understood that it is not to restricted.